Oil and fat composition containing monovalent omega-7 unsaturated fatty acid and chocolate

Abstract

Fat bloom and graining can be suppressed if an oil and fat composition, which contains at least 40% by weight of a triglyceride (S2M) in which one monovalent unsaturated fatty acid and two saturated fatty acids are bonded and at least 4% by weight of a triglyceride (S2X) in which one monovalent ω7 unsaturated fatty acid and two saturated fatty acids are bonded, is added to a chocolate mainly composed of a triglyceride (S2O) in which one oleic acid and two saturated fatty acids are bonded.

Description

[Technical field]

[0001] The present invention relates to an oil and fat composition for chocolates and chocolates containing the oil and fat composition. [Background technology]

[0002] Chocolate is broadly divided into tempered and non-tempered types. The fats and oils used in tempered chocolate are mainly composed of symmetric disaturated monooleic triacylglycerol (hereinafter sometimes referred to as S2O). Symmetric S2O can take the stable polymorph V type by tempering. However, if this chocolate is stored for a long period of time, the crystal polymorphism changes to the more stable VI type, and as a result, the surface of the chocolate loses its luster when it is first produced, and furthermore, it turns white and discolored, known as fat bloom (hereinafter simply referred to as bloom), which can reduce its commercial value.

[0003] No-tempering chocolates are divided into trans acid type, lauric acid type, and type that uses fats and oils that are substantially free of trans acid and lauric acid, with the latter type of fats and oils that are substantially free of trans acid and lauric acid being mainly composed of symmetric and asymmetric S2O. Chocolate that uses this type of fat and oil is stable immediately after production in the form of unstable or metastable fat crystals, but the crystal polymorphism changes to a stable form during subsequent storage, which can cause deterioration in appearance (fat bloom) and texture (graining), which can impair the commercial value.

[0004] Tempering chocolates that are mainly composed of symmetric and / or asymmetric SO and chocolates that are substantially free of trans acids and lauric acid suffer from problems such as deterioration in appearance (fat bloom) and texture (graining) due to the polymorphic transition described above. Therefore, various methods have been proposed to solve these problems by suppressing the polymorphic transition.

[0005] Known examples of the above-mentioned methods include a method of adding a chemical substance other than triglycerides, such as sugar esters (Non-Patent Document 1) or sorbitan esters (Non-Patent Document 2), and a method of adding a specific triglyceride composition, for example, a triglyceride composition containing 20 to 60% saturated fatty acids having 22 carbon atoms as constituent fatty acids (Patent Document 1), a triglyceride composition containing 15 to 70% saturated fatty acids having 20 to 24 carbon atoms and 20 to 60% unsaturated fatty acids having 16 to 20 carbon atoms as constituent fatty acids (Patent Document 2), an oil and fat composition containing mono-U-di-S triglyceride (SSU) (Patent Document 3), and a high melting point fraction of milk fat (Non-Patent Document 3). [Prior art documents] [Patent documents]

[0006] [Patent Document 1] Japanese Patent Application Publication No. 58-198245 [Patent Document 2] Japanese Patent Application Publication No. 62-006635 [Patent Document 3] Japanese Patent Application Publication No. 2-138937 [Non-patent literature]

[0007] [Non-Patent Document 1] KATSURAGI, Toshiya; SATO, Kiyotaka. Effects of emulsifiers on fat bloom stability of cocoa butter. Journal of Oleo Science, 2001, 50.4: 243-248. [Non-Patent Document 2] BUSCATO, Monise Helen Masuchi, et al. Delaying fat bloom formation in dark chocolate by adding sorbitan monostearate or cocoa butter stearin. Food chemistry, 2018, 256: 390-396. [Non-Patent Document 3] LOHMAN, Myung H.; HARTEL, Richard W. Effect of milk fat fractions on fat bloom in dark chocolate. Journal of the American Oil Chemists' Society, 1994, 71.3: 267-276. Summary of the Invention [Problem to be solved by the invention]

[0008] An object of the present invention is to find an oil and fat composition that prevents fat bloom and graining in chocolate containing S2O as a main component without impairing meltability in the mouth and workability. [Means for solving the problem]

[0009] The present inventors have carried out various investigations to achieve the above-mentioned object.

[0010] In tempered and non-tempered chocolates that use fats and oils mainly composed of SO as described above, various measures have been taken to address the problem of deterioration in the appearance and texture of chocolate caused by the polymorphic transformation of the fats and oils.

[0011] One of the countermeasures is the use of additives such as food additives, but the use of chemical substances other than triglycerides may be subject to legal restrictions in some countries. The inventors have found that the other countermeasure, the addition of a specific triglyceride composition, may have the problem of impairing the meltability of the chocolate in the mouth or increasing the viscosity of the dough during tempering, thereby reducing workability, even if it has an effect of preventing blooming.

[0012] In the course of analyzing the characteristics of the crystal polymorphism of SO, the inventors conducted various investigations focusing on the differences in properties due to differences in the chain length and double bond position of the bound unsaturated fatty acid, and discovered for the first time that the polymorphic transition of SO is delayed by the coexistence of a mixed triglyceride of a saturated fatty acid and a monovalent ω7 unsaturated fatty acid.

[0013] The present inventors, taking into consideration the above-mentioned polymorphic transition delay phenomenon, which was previously unknown, have found that fat bloom and graining can be suppressed by blending an oil and fat composition containing 40% by weight or more of a triglyceride (S2M) in which one monounsaturated fatty acid and two saturated fatty acids are bonded together, and 4% by weight or more of a triglyceride (S2X) in which one monounsaturated fatty acid and two saturated fatty acids are bonded together, with chocolates mainly composed of a triglyceride (S2O) in which one oleic acid and two saturated fatty acids are bonded together, thereby completing the present invention.

[0014] That is, the present invention (1) An oil and fat composition comprising 40% by weight or more of a triglyceride (S2M) having one monounsaturated fatty acid and two saturated fatty acids bound thereto, and 4% by weight or more of a triglyceride (S2X) having one monovalent ω7 unsaturated fatty acid and two saturated fatty acids bound thereto, where S is a saturated fatty acid having 16 to 22 carbon atoms, M is a monounsaturated fatty acid having 16 to 22 carbon atoms, and X is a monovalent ω7 unsaturated fatty acid; (2) The oil and fat composition according to (1), in which S2X in S2M is 5% or more; (3) The oil and fat composition according to (1) or (2), having a solid fat content (SFC) at 20°C of 30% or more; (4) The oil and fat composition according to (1) or (2) for use in chocolates; (5) Chocolates containing the fat or oil composition according to (1) or (2); (6) Chocolates according to (5) above in which fat bloom or graining has been suppressed; (7) Chocolates according to (5) in which the chocolate fat or oil contains 0.7% by weight or more of S2X; (8) Chocolates according to (7) which are tempered chocolates; (9) Chocolates according to (7) which are non-tempering type chocolates; (10) A method for producing chocolates, comprising: preparing a chocolate dough containing the oil-and-fat composition according to (1) or (2), in which the S2X content in the chocolate fat is 0.7% by weight or more; and subjecting the prepared dough to a tempering treatment or solidifying the dough without tempering; (11) An inhibitor of crystal transition of S2O triglyceride, comprising S2X as an active ingredient, where S is a saturated fatty acid having 16 to 22 carbon atoms, X is a monovalent ω7 unsaturated fatty acid, and O is oleic acid; (12) A method for suppressing fat bloom or graining in chocolates, comprising adding the oil or fat according to (1) or (2) to a chocolate dough. This is regarding. Effect of the Invention

[0015] The oil and fat composition of the present invention is advantageous in that when blended with tempering-type chocolates mainly composed of symmetrical S2O among chocolates mainly composed of S2O, fat bloom and graining can be suppressed without impairing the texture or tempering properties. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0016] The present invention will be specifically described below.

[0017] In this specification, chocolates are oil- and fat-processed foods in which oils and fats form a continuous phase, and include not only chocolate, semi-chocolate, and chocolate-based foods as defined by the National Chocolate Industry Fair Trade Council and the Chocolate-Based Food Fair Trade Council, but also products that contain any combination of ingredients such as oils and fats, milk powder, sugar, cacao ingredients (cacao mass, cocoa, cocoa butter), fruit juice powder, fruit powder, flavoring agents, emulsifiers, fragrances, coloring agents, etc., in any ratio.

[0018] In this specification, S means saturated fatty acid, more specifically, saturated fatty acid having 16 to 22 carbon atoms, M means monounsaturated fatty acid, more specifically, monounsaturated fatty acid having 16 to 22 carbon atoms, X means monovalent ω7 unsaturated fatty acid, St means stearic acid, P means palmitic acid, O means oleic acid, Po means palmitoleic acid, and V means cis-vaccenic acid. When expressing triglycerides as abbreviations, for example, SO means a triglyceride in which two saturated fatty acids and one oleic acid are bonded, SSO means a triglyceride in which saturated fatty acids are bonded at the 1st and 2nd positions and oleic acid is bonded at the 3rd position, and SOS means a triglyceride in which saturated fatty acids are bonded at the 1st and 3rd positions and oleic acid is bonded at the 2nd position.

[0019] (Oil composition) In one aspect, the present invention provides an oil and fat composition. The oil and fat composition of this aspect contains the oil and fat itself unless otherwise specified. In one embodiment, the oil and fat composition of this aspect does not contain the oil and fat itself, but contains other raw materials. The S2X content in the oil and fat composition of this aspect is 4.0% by weight or more, preferably 5.0 to 70% by weight, more preferably 7.0 to 60% by weight, even more preferably 10 to 50% by weight, and most preferably 13 to 40% by weight, and other preferred examples are 15 to 65% by weight, 20 to 55% by weight, and 25 to 45% by weight. The amount of the oil and fat composition added to chocolates that can be effective generally requires a smaller amount as the content of S2X, an active ingredient in the oil and fat composition, increases, and the lower the content, the larger the amount.

[0020] The S2M content in the oil and fat composition of this embodiment is 40% by weight or more, preferably 45 to 95% by weight, more preferably 50 to 93% by weight, even more preferably 55 to 90% by weight, and most preferably 60 to 88% by weight. If this content is low, the product may tend to have a sticky texture.

[0021] In one embodiment, the S2X content in S2M is preferably 4.8% by weight or more, for example 5.0% by weight or more, more preferably 6.0 to 70% by weight, even more preferably 8.0 to 60% by weight, and most preferably 12 to 40% by weight, and other preferred examples are 9 to 65% by weight, 15 to 55% by weight, 20 to 50% by weight, and 25 to 45% by weight. In another embodiment, the S2O content in S2M is preferably 95% by weight or less, more preferably 50 to 90% by weight, and other preferred examples are 70 to 85% by weight.

[0022] If the S2X content or the S2X in S2M is low, the S2X in the chocolate cannot be increased efficiently, and the effect of the oil and fat composition added in a small amount may be poor. In addition, ingredients other than S2X may impair the quality of the chocolate.

[0023] In one embodiment, the amount of triglyceride (S3) in which three saturated fatty acids are bonded in the oil and fat composition is preferably 20% by weight or less, more preferably 15% by weight or less, and even more preferably 10% by weight or less, for example, 0.5 to 5% by weight, 1 to 3% by weight, 1.2 to 2.5% by weight, or 1.5 to 2.0% by weight. If the amount of S3 is high, the viscosity of the dough during tempering may increase, which may lead to a decrease in workability.

[0024] In one embodiment, the content of X in the constituent fatty acids of the oil or fat composition is preferably 1 to 30% by weight, more preferably 2 to 25% by weight, even more preferably 3 to 20% by weight, and most preferably 4 to 15% by weight.

[0025] In one embodiment, the X / M ratio (monovalent ω7 unsaturated fatty acid / monounsaturated fatty acid) in the constituent fatty acids of the oil or fat composition is preferably 4.5-55, more preferably 5-50, for example 5.5-55, 6-50, 10-40, or 15-30.

[0026] In one embodiment, the S (saturated fatty acid) content in the constituent fatty acids of the oil and fat composition is preferably 35 to 85 wt%, more preferably 40 to 80 wt%, even more preferably 45 to 75 wt%, and most preferably 50 to 70 wt%, for example, 63 to 67 wt%.

[0027] In one embodiment, the DHA and EPA contents of the oil composition are preferably low. More specifically, the DHA + EPA content of the oil composition is preferably less than 2%, for example, 0 to 1.5%, or 0.5 to 1.0%.

[0028] In one embodiment, the solid fat content (SFC) of the oil or fat composition at 10° C. is preferably 85% or more, more preferably 86 to 94%, for example 90 to 93%.

[0029] In one embodiment, the SFC of the oil or fat composition at 20° C. is preferably 30% or more, more preferably 40 to 90%, and even more preferably 50 to 80%, for example, 70 to 79%, or 75 to 78%.

[0030] In one embodiment, the SFC of the oil or fat composition at 25° C. is preferably 6.5% or more, for example 20% or more, more preferably 8 to 72%, and even more preferably 9 to 71%, for example 25 to 70%, 27 to 65%, 30 to 64%, or 35 to 62%.

[0031] In one embodiment, the SFC of the oil or fat composition at 30° C. is preferably 55% or less, for example 10% or less, more preferably 0 to 52%, and even more preferably 1 to 50%, for example 0 to 8%, 1 to 7%, or 1.5 to 4.5%.

[0032] (Monovalent omega-7 unsaturated fatty acids) ω7 unsaturated fatty acids are a classification of unsaturated fatty acids in which the unsaturated bond is located at the seventh carbon from the end of the carbon chain, and this embodiment focuses on monovalent ω7 unsaturated fatty acids. Examples of monovalent ω7 unsaturated fatty acids (sometimes referred to as X in the present specification) include cis-unsaturated fatty acids having 16 to 20 carbon atoms, more specifically, palmitoleic acid (cis-9 hexadecenoic acid, sometimes referred to as Po in the present specification) and cis-vaccenic acid (cis-11 octadecenoic acid, sometimes referred to as V in the present specification), but are not limited thereto. In a more specific embodiment, the monovalent ω7 unsaturated fatty acid is palmitoleic acid.

[0033] (Raw material for oil and fat composition) The raw material for the oil and fat composition of this embodiment is not particularly limited as long as it is an edible oil and fat containing monovalent ω7 unsaturated fatty acid, and examples thereof include various natural animal and vegetable oils such as marine oils and vegetable oils, and oils and fats obtained from microorganisms and algae. In addition, oils and fats obtained from plants, microorganisms, and algae whose fatty acid composition has been modified to contain monovalent ω7 unsaturated fatty acids using conventional breeding techniques that use natural and artificial mutants, or new breeding techniques such as recombinant gene technology and genome editing technology, can also be used.

[0034] In terms of purity and cost, the raw materials for the oil and fat composition of this embodiment are preferably sea buckthorn oil (seaberry fruit oil), vaccarifat, macadamia nut oil, hazelnut oil, seal oil, etc. Examples of raw materials containing palmitoleic acid and cis-vaccenic acid include sea buckthorn oil (seaberry fruit oil). Examples of raw materials containing palmitoleic acid include vaccarifat, macadamia nut oil, hazelnut oil, and seal oil. Sea buckthorn oil (seaberry fruit oil) and buckwheat fat inherently contain S2X triglycerides, and are particularly preferred because the oil composition of this embodiment can be obtained, for example, as an S2X triglyceride-enriched fraction by fractionation of these oils.

[0035] In addition, fats and oils containing S2X triglycerides can also be obtained by transesterification between the fats and oils rich in X and a raw material containing S. For example, the fats and oils can be used as they are or as an S2X triglyceride-enriched fraction obtained by fractionation of the fats and oils to obtain the fat and oil composition of the present invention. Examples of the S-containing raw material include fats and oils, fatty acids, and lower alcohol esters thereof.

[0036] In one embodiment, the present invention also provides a method for producing the oil and fat composition of the above embodiment by fractionating and / or interesterifying an oil or fat.

[0037] In this embodiment, the fats and oils to be subjected to fractionation and interesterification are as described above in (Raw materials for the fat and oil composition).

[0038] The oil and fat fractionation may be solvent fractionation or dry fractionation. Examples of the solvent in the case of solvent fractionation include acetone and hexane. When hexane is used, a charge mix with an oil content of 5 to 35% is prepared, and the oil and fat composition of the above embodiment can be obtained as a crystal portion after crystallization at -25°C to 0°C. When acetone is used, a charge mix with an oil content of 5 to 35% is prepared, and the oil and fat composition of the above embodiment can be obtained as a crystal portion after crystallization at -5°C to 10°C.

[0039] The transesterification may be a chemical random transesterification method using an alkali metal catalyst, or a 1,3-enzymatic transesterification method or a random transesterification method using an enzyme catalyst.

[0040] (Chocolate) In one embodiment, the present invention provides a chocolate comprising the fat composition of the above embodiment.

[0041] In one embodiment, the chocolate of this aspect is a tempering type chocolate. The chocolate of this embodiment preferably contains 35 to 90% by weight, more preferably 40 to 80% by weight, even more preferably 50 to 78.3% by weight, for example 70 to 78% by weight, 72 to 77% by weight, of S2O in the chocolate fat. It is also preferable that the chocolate contains 80% by weight or more of symmetric type (SOS) of S2O, more preferably 85 to 99% by weight, even more preferably 95 to 99.5% by weight.

[0042] The chocolate of this embodiment preferably contains 0.7% by weight or more, preferably 0.8 to 20% by weight, more preferably 1.1 to 15% by weight, even more preferably 1.5 to 10% by weight, and most preferably 2.2 to 5.5% by weight of S2X triglyceride in the chocolate fat or oil. If the S2X triglyceride content is low, it is not very effective in improving the bloom resistance of chocolates, and the higher the content, the greater the effect of improving the bloom resistance, but if the content is too high, it may cause difficulties in tempering and may result in a soft chew.

[0043] In another embodiment, the chocolate of this aspect is a non-tempering type chocolate. The chocolate of this embodiment preferably contains 35 to 90% by weight, more preferably 40 to 80% by weight, even more preferably 50 to 78.5% by weight, for example 65 to 78% by weight, 70 to 76% by weight, of S2O in the chocolate fat. It is also preferable that the symmetric type of S2O is contained in the chocolate fat in an amount of 33 to 70% by weight, more preferably 40 to 65% by weight, even more preferably 50 to 60% by weight.

[0044] The chocolate of this embodiment preferably contains 1.8% by weight or more, preferably 2.0 to 20% by weight, more preferably 2.5 to 15% by weight, even more preferably 3.0 to 10% by weight, and most preferably 4.5 to 7.5% by weight of S2X triglyceride in the chocolate fat or oil. If the S2X triglyceride content is low, the effect of improving the bloom resistance of chocolate is poor. The higher the content, the greater the effect of improving the bloom resistance, but if the content is too high, the chocolate may become soft when chewed.

[0045] In the case of chocolates of this embodiment, the fat composition of the present invention containing S2X triglyceride is dissolved together with other fat raw materials during the production of chocolates, but it may be used as is or as a fat raw material dissolved in other fats, such as cocoa butter or hard butter.

[0046] The amount of the oil and fat composition of the present invention blended in the chocolate of this embodiment is preferably 2 to 30% by weight, more preferably 3.5 to 25% by weight, even more preferably 5.0 to 20% by weight, and most preferably 7.0 to 15% by weight.

[0047] In chocolates that are mainly composed of SO, the specific components are St2O, PStO, and PO, but of these, PO, and even more so, the polymorphic transition of symmetric POP, is often problematic. (St stands for stearic acid, and P stands for palmitic acid.) That is, it is known that in tempering chocolate, POP undergoes a polymorphic transition from the most stable polymorph (β2) to the most stable polymorph (β1), while in oil-based foods that are not subjected to temperature control, such as no-tempering chocolate, the polymorphic transition of POP from the metastable polymorph (β'2 chain length structure) to the most stable polymorph (β3 chain length structure) is most degraded in texture and appearance, and it is considered most important to inhibit or delay this transition. Among S2X, which is the active ingredient in the oil and fat composition of one embodiment of the present invention, P2X in particular, and even more particularly symmetric P2X (PXP), are capable of effectively inhibiting such polymorphic transition of POP, and are therefore particularly effective in inhibiting deterioration in texture and appearance.

[0048] In one embodiment, the chocolates of this aspect have reduced fat bloom and graining.

[0049] In one embodiment, the present invention provides a method for producing chocolates of the above embodiment. As a specific example of the production method of this embodiment, the oil and fat composition of one embodiment of the present invention is mixed with other raw materials such as an oil and fat mainly composed of SO, a cacao component (cacao mass, cocoa powder, etc.), sugars (sugar, lactose, glucose, etc.), milk powder (whole milk powder, skim milk powder, etc.), and an emulsifier to prepare a chocolate dough, and the obtained dough is rolled and subjected to conching or the like to produce chocolates. When producing tempering type chocolates, a tempering step is included in the middle, and when producing non-tempering type chocolates, no tempering step is included. Examples of the tempering step include a method of cooling or heating the dough, or a method of adding a seed agent to the dough. The amount of the oil and fat composition added, the oil and fat composition of the dough, etc. are as described above.

[0050] When producing tempering type chocolates, tempering type fats can be used as the fats and oils mainly composed of S2O to be mixed into the chocolate dough. Here, tempering type fats and oils are fats and oils rich in SOS (triglycerides in which oleic acid is bonded at the 2-position and saturated fatty acids are bonded at the 1- and 3-positions), and typically contain cocoa butter. Specific examples of tempering type fats and oils include high oleic oil and 1- and 3-position enzyme transesterified oil of saturated fatty acids, shea fat, palm oil, monkey fat, mango kernel oil, kokum fat, illipe fat, and fractionated oils thereof.

[0051] When producing non-tempering type chocolates, non-tempering type fats can be used as the above-mentioned SO-based fats to be mixed into the chocolate dough. Here, non-tempering type fats refer to fats rich in SSO (triglycerides in which saturated fatty acids are bonded at the 2-position, and saturated fatty acids and oleic acid are bonded at the 1- and 3-positions). Specific examples of non-tempering type fats include fats obtained by random interesterification of a raw material fat mixture, and fractionated oils thereof. Examples of the raw material oils and fats include vegetable oils and fats such as palm oil, rapeseed oil, high erucic rapeseed oil, sunflower oil, high oleic sunflower oil, soybean oil, rice oil, corn oil, cottonseed oil, peanut oil, safflower oil, olive oil, sesame oil, shea butter, and monkey fat, animal oils and fats such as milk fat, beef tallow, lard, fish oil, and whale oil, as well as their hardened oils, fractionated oils, hardened fractionated oils, fractionated hardened oils, processed oils and fats that have been subjected to ester exchange or the like, and further mixed oils and fats thereof.

[0052] In one embodiment, the manufacturing method of this embodiment suppresses fat bloom or graining in chocolates. In a related embodiment, the present invention provides a method for suppressing fat bloom or graining in chocolates, comprising adding an oil and fat composition of one embodiment of the present invention containing S2X triglyceride to chocolate dough.

[0053] In one embodiment, the present invention provides a method for inhibiting crystal transition of S2O triglyceride using S2X triglyceride.

[0054] The method of this embodiment includes adding S2X triglyceride to a fat raw material containing S2O triglyceride. The amount of S2X triglyceride added is as described in the fat composition embodiment above. In one embodiment, the S2X triglyceride of this embodiment is added in the form of the fat composition described above.

[0055] In another aspect, the present invention provides an agent for inhibiting crystal transition of S2O triglyceride, comprising or consisting of the oil or fat composition of one aspect of the present invention containing S2X triglyceride. The "crystal transition inhibitor for SO triglycerides" in this embodiment refers to a novel use based on a previously unknown new attribute that, when added to chocolates mainly composed of SO triglycerides, can prevent fat bloom and graining without impairing meltability in the mouth or workability. The crystal transition inhibitor for SO triglycerides in this embodiment is particularly suitable for this use.

[0056] (Mechanism of action) This invention was made possible by the discovery of the phenomenon that the polymorphic transition of S2O (mixed triglyceride of saturated fatty acid and oleic acid) is delayed by the coexistence of S2X (mixed triglyceride of saturated fatty acid and monovalent ω7 unsaturated fatty acid). Although the crystallographic analysis is not sufficient, it is presumed that the delay in the polymorphic transition of S2O occurs due to the fact that, while saturated fatty acid lamellae are aligned in the crystal structure, in the unsaturated fatty acid lamellae where oleic acid and monovalent ω7 unsaturated fatty acid coexist, the two do not phase separate and can be compatible, but a slight misalignment occurs. EXAMPLES

[0057] Examples are described below, but the technical concept of the present invention is not limited to these examples. In the examples, parts and % are all by weight.

[0058] (Experiment 1A) Verification of the effect of adding pure triglyceride P2Po containing palmitoleic acid Po POP triglyceride (commercially available product with a purity of 99% or more) and PPoP triglyceride (commercially available product with a purity of 99% or more) were mixed at POP / PPoP ratios of (A) 100 / 0, (B) 95 / 5, (C) 85 / 15, and (D) 80 / 20, respectively, and after complete melting at 80°C, 5μL was dropped onto an aluminum pan and immediately solidified at 5°C for 60 minutes. After solidification, samples were stored at 20°C from day 0 to day 14, at 25°C from day 15 to day 28, and at 28°C from day 29 to day 100. The samples were subjected to X-ray crystal structure analysis to follow the changes in the crystal polymorphism during storage.

[0059] The results obtained are summarized in Table 1. (A) In the case of 100% POP, the polymorphic form was β2 until the 21st day, but was clearly confirmed to have transitioned to β1 on the 28th day. On the other hand, in (B) and (C), no such polymorphic transition from β2 to β1 was observed even in the storage test over 100 days. This confirmed that PPoP can suppress the polymorphic transition of POP from β2 to β1 with the addition of a small amount of 5%.

[0060] Table 1A Polymorphic behavior of pure POP / PPoP [Table 1A] (The order of stable polymorphism is β', β2, β1)

[0061] (Experiment 1B) Verification of the effect of adding pure triglyceride P2V containing cis-vaccenic acid V POP triglyceride (commercially available product with a purity of 99% or more) and PVP triglyceride (commercially available product with a purity of 99% or more) were mixed at POP / PVP ratios of (E) 100 / 0, (F) 95 / 5, (G) 60 / 40, and (H) 50 / 50, respectively, and after complete melting at 80°C, 5μL was dropped onto an aluminum pan and immediately solidified at 5°C for 60 minutes. After solidification, samples were stored at 20°C from day 0 to day 14, at 25°C from day 15 to day 28, and at 28°C from day 29 to day 100. The samples were subjected to X-ray crystal structure analysis to follow the changes in the crystal polymorphism during storage.

[0062] The results obtained are summarized in Table 1B. (E) In the case of 100% POP, the polymorphic form was β2 until the 21st day, but was clearly transformed to β1 on the 28th day. On the other hand, in (F), no such transformation from β2 to β1 was observed even in the storage test over 100 days. This confirmed that PVP can suppress the transformation of POP from β2 to β1 with the addition of a small amount of PVP, only 5%.

[0063] Table 1B Polymorphism of pure POP / PVP [Table 1B] (The order of stable polymorphism is β', β2, β1)

[0064] (Experiment 2) Verification of the effect of adding S2Po Using high oleic sunflower oil or macadamia nut oil as raw oils and fats, 1,3-position enzymatic transesterification with ethyl palmitate was carried out, and the fatty acid ethyl ester fraction was distilled off by distillation. The obtained oil and fat fraction was subjected to multi-stage fractionation using a solvent to obtain oils and fats rich in P2O and oils and fats rich in P2Po. These obtained oils and fats were mixed to obtain oil and fat compositions of Examples 1 to 7 and Comparative Examples 1 and 2 having various S2Po contents. The triglyceride composition of each oil composition is shown in Table 2.

[0065] Table 2 Triglyceride composition of the oil composition [Table 2]

[0066] The results of measuring the SFC and fatty acid composition of each oil and fat composition are shown in Table 3. The SFC at 20°C was 30% or more for all of them.

[0067] Table 3 SFC and fatty acid composition of oil and fat composition [Table 3]

[0068] Each oil composition was subjected to X-ray crystal structure analysis, and the results of tracking the change in crystal polymorphism during storage are shown in Table 4. The cooling conditions were 80°C, after which the composition was completely melted, 5μL was dropped onto an aluminum pan, and immediately solidified at 5°C for 60 minutes. Samples stored at 20°C for 1 to 14 days after solidification, at 25°C for 15 to 28 days, and at 28°C for 29 to 100 days were subjected to X-ray crystal structure analysis, and the change in crystal polymorphism during storage was tracked. As a result, if the S2Po in the oil composition was 4% by weight or more and the S2Po in S2M was 5% or more, the most stable polymorph (β) did not appear at all for at least 100 days, and the crystal polymorph transition was suppressed.

[0069] Table 4. Polymorphic behavior of oil and fat compositions [Table 4] (The order of stable polymorphism is γ, β', β)

[0070] (Experiment 3) Verification of the effect of adding S2Po to tempering chocolate Chocolates were prepared using the oil and fat compositions of Examples 1 to 7 and Comparative Examples 1 and 2, and the effects of S2Po on the texture and bloom resistance were examined.

[0071] (Preparation of StOSt Fat) The 1,3-enzymatic transesterification of high oleic sunflower oil and ethyl stearate was carried out, and the fatty acid ethyl ester fraction was distilled off. The obtained oil fraction was subjected to multi-stage fractionation using a solvent to obtain StOSt fat with a StOSt content of 66.0% by weight.

[0072] (Preparation of chocolate) 40.4% by weight of cacao mass, 2.7% by weight of cocoa butter, 46.3% by weight of sugar, 0.6% by weight of lecithin, 4.7% by weight of StOSt fat, and 5.3% by weight of the fat composition of the examples or comparative examples were mixed, and chocolate doughs of Examples 1A to 7A and Comparative Examples 1A and 2A were prepared in a conventional manner. In addition, as a standard sample, chocolate doughs were prepared for comparison in which CBE (Cocoa Butter Equivalent) or cocoa butter was mixed in place of the fat composition. The total oil content was 35.1% by weight, and the triglyceride composition in each chocolate fat is as shown in Table 5 below.

[0073] The obtained chocolate dough was mixed well at 50°C until fully melted, then cooled to 32°C with stirring. Once the temperature reached 32°C, 0.2% by weight of StOSt seed agent (manufactured by Fuji Oil Co., Ltd. / product name "Chocolate Seed LT") was added based on the chocolate weight. The mixture was quickly and thoroughly mixed, poured into a mold, and cooled and solidified at 10°C for 30 minutes. The cooled chocolate was released from the mold and aged at 20°C for 7 days, after which the texture and bloom resistance were evaluated (Table 6). The texture evaluation was carried out by five well-trained panelists involved in the development work. Bloom resistance was evaluated in two cycle tests: 18°C ​​(12hr) - 30.5°C (12hr) and 20°C (12hr) - 32°C (12hr). The evaluation results were based on the following criteria. -: no bloom, +-: slightly cloudy surface, +: cloudy and whitish surface, ++: very cloudy and clearly turning white, +++: powdery texture and severe bloom The texture evaluation (chewing) was based on the following criteria. ◎ Very good snapping ability, very preferable, 〇 Has good snapping ability, preferable, △ Weak snapping ability, a little soft, × No snapping ability at all, not preferable The texture evaluation (melt in the mouth) was based on the following criteria. ◎ Melts very quickly and gives a strong cooling sensation, 〇 Melts quickly and gives a cooling sensation, △ Melts slowly and leaves a residue in the mouth, giving a weak cooling sensation, × Melts extremely slowly and leaves a strong residue in the mouth, giving no cooling sensation at all

[0074] Table 5. Triglyceride composition in chocolate fats and oils [Table 5]

[0075] Table 6 Chocolate texture and bloom resistance [Table 6]

[0076] It was confirmed that when the S2Po content in chocolate fats and oils is 0.9% by weight or more, good texture and bloom resistance can be achieved at the same time.

[0077] (Experiment 4) Verification of molding workability of tempering type chocolate An investigation was carried out on the workability during chocolate molding using the chocolate doughs of Examples 1A, 3A, 4A, 6A, and 7A prepared in Experiment 3. In addition, chocolate doughs containing CBE or cocoa butter instead of the fat and oil composition were used as standard samples for comparison.

[0078] (Experimental Method) After the chocolate was completely melted at 50°C, it was stirred and cooled to a temperature of 40°C. After reaching 40°C, it was cooled to 27°C at a cooling rate of 0.5°C / min while stirring at 100 rpm, and then maintained at 27°C while continuing to stir. The viscosity of chocolate increases as the fats and oils crystallize, and its tempering workability can be evaluated by comparing the time (min) to the inflection point of the viscosity increase and the rate of viscosity increase (the maximum value of the slope of the viscosity increase curve after the inflection point; centipoise / min).

[0079] Table 7. Chocolate tempering properties [Table 7]

[0080] The viscosity increase rate of all the Examples was lower than that of standard chocolate containing cocoa butter, meaning that a rapid viscosity increase during cooling was not considered to occur. The viscosity increase start time can be related to the time required for cooling, and the shorter the time, the better the workability. Compared to chocolates containing general CBE, the viscosity increase start time was equal to or shorter and better in all the Examples.

[0081] From the above, it was confirmed that the chocolate doughs of Examples 1A, 3A, 4A, 6A, and 7A have tempering workability that is equivalent to or better than that of chocolate doughs blended with CBE or cocoa butter.

[0082] (Experiment 5) Verification of the effect of adding S2Po to non-tempering chocolate (Preparation of chocolate) Chocolate dough of Examples 2B to 7B and Comparative Examples 1B and 2B was prepared by a conventional method using 40.4% by weight of cacao mass, 2.7% by weight of cocoa butter, 46.3% by weight of sugar, 0.6% by weight of lecithin, and 10.0% by weight of the fat composition of the Example or Comparative Example. The total fat content was 35.1% by weight, and the triglyceride composition of each chocolate fat is as shown in Table 8 below.

[0083] Table 8. Triglyceride composition in chocolate fats and oils [Table 8]

[0084] The obtained chocolate dough was cooled to 40°C, poured into aluminum cups, and solidified at 20°C. It was then stored at 20°C and observed for blooming and graining. The results are shown in Table 9. When the S2Po content in the chocolate fat was 2.3% by weight or more, a blooming and graining inhibitory effect was observed. Blooming and graining were evaluated according to the following criteria. -: no bloom / graining, -+: slightly cloudy surface / slight signs of graining, +: cloudy and whitish surface / graining visible, ++: very cloudy and clearly turning white / graining clearly visible, +++: powdery texture with severe bloom / severe graining visible

[0085] Table 9 Bloom resistance of chocolate [Table 9]

[0086] (Experiment 6) Confirmation of the effect of adding S2Po to tempering chocolate Using high oleic sunflower oil or macadamia nut oil as the raw oil, a mixture of ethyl palmitate and ethyl stearate or ethyl stearate was subjected to 1,3-position enzymatic transesterification, and the fatty acid ethyl ester fraction was distilled off by distillation. The obtained oil fraction was subjected to multi-stage fractionation using a solvent to obtain oils rich in PPoSt and oils rich in St2Po. These oils were mixed with the above-mentioned StOSt fat and cocoa butter to obtain oil compositions of Examples 8 to 15 and Comparative Examples 3 to 4 having various S2Po contents. The triglyceride composition of each oil composition is shown in Table 10.

[0087] Table 10. Triglyceride composition of the oil composition [Table 10]

[0088] The results of measuring the SFC and fatty acid composition of each oil and fat composition are shown in Table 11.

[0089] Table 11. SFC and fatty acid composition of oil and fat composition [Table 11]

[0090] Chocolates were prepared using the oil and fat compositions of Examples 8 to 15 and Comparative Examples 3 and 4, and the effects of S2Po on the texture and bloom resistance were examined.

[0091] (Preparation of chocolate) In a similar manner to that of Experiment 3, 40.4% by weight of cacao mass, 2.7% by weight of cocoa butter, 46.3% by weight of sugar, 0.6% by weight of lecithin, 5.3% by weight of palm mid-melting point fraction Unilate P110N (manufactured by Fuji Oil Co., Ltd.), and 4.7% by weight of the fat and oil composition of the Examples or Comparative Examples were mixed and the chocolate doughs of Examples 8A to 15A and Comparative Examples 3A and 4A were prepared in a conventional manner. The total fat content was 35.1% by weight, and the triglyceride composition in each chocolate fat and oil is as shown in Table 12 below.

[0092] The obtained chocolate dough was molded as described in Experiment 3, and after maturing treatment at 20°C for 7 days, the texture and bloom resistance were evaluated in the same manner as in Experiment 3, and the results are shown in Table 13. Texture evaluation was performed by five well-trained panelists involved in the development work. The bloom resistance was evaluated under the same storage conditions as in Experiment 3, and the evaluation results were also based on the same criteria.

[0093] Table 12. Triglyceride composition in chocolate fats and oils [Table 12]

[0094] Table 13 Chocolate texture and bloom resistance [Table 13]

[0095] It was confirmed that if the chocolate fat contains 0.7% by weight or more of S2Po, good texture and bloom resistance can be achieved at the same time. [Industrial Applicability]

[0096] It was discovered that an oil and fat composition containing a specific amount of S2X can suppress fat bloom and graining in chocolates that are mainly composed of S2O, expanding the applications of X-rich oils and fats.

Claims

1. An oil and fat composition comprising 40% by weight or more of a triglyceride (S2M) having one monounsaturated fatty acid and two saturated fatty acids bonded thereto, and 4% by weight or more of a triglyceride (S2X) having one monovalent ω7 unsaturated fatty acid and two saturated fatty acids bonded thereto, wherein S is a saturated fatty acid having 16 to 22 carbon atoms, M is a monounsaturated fatty acid having 16 to 22 carbon atoms, and X is a monovalent ω7 unsaturated fatty acid.

2. 2. The oil composition according to claim 1, wherein the S2X content in the S2M is 5% or more.

3. 3. The oil and fat composition according to claim 1, having a solid fat content (SFC) at 20° C. of 30% or more.

4. 3. The oil and fat composition according to claim 1 or 2, which is for use in chocolates.

5. A chocolate product comprising the oil and fat composition according to claim 1 or 2.

6. The chocolate according to claim 5, which is inhibited from causing fat bloom or graining.

7. 6. The chocolate according to claim 5, wherein the chocolate fat contains 0.7% by weight or more of S2X.

8. The chocolate according to claim 7, which is a tempering type chocolate.

9. 8. The chocolate according to claim 7, which is a non-tempering type chocolate.

10. A method for producing chocolates, comprising: preparing a chocolate dough containing the oil-and-fat composition according to claim 1 or 2, and having an S2X content of 0.7% by weight or more in the chocolate oil-and-fat; and solidifying the prepared dough with or without tempering.

11. An inhibitor of crystal transition of S2O triglyceride containing S2X as an active ingredient, where S is a saturated fatty acid having 16 to 22 carbon atoms, X is a monovalent omega-7 unsaturated fatty acid, and O is oleic acid.

12. A method for suppressing fat bloom or graining in chocolate, comprising adding the oil or fat according to claim 1 or 2 to a chocolate dough.