Abstract

To provide a die-bonding film and a dicing die-bonding film which can comparatively prevent a void from remaining between wiring boards.SOLUTION: A die-bonding film contains an acrylic resin, a phenolic resin and a filler, in which the filler has a specific surface area of 5 m2 / g or more and 100 m2 / g or less, and a content mass ratio of the filler to the acrylic resin is 0 or more and 1.50 or less.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to a die-bonding film and a dicing die-bonding film. [Background technology]

[0002] Conventionally, in the manufacture of semiconductor devices, in order to obtain a semiconductor chip for die bonding, The use of a dicing die bond film is known (for example, Patent Document 1). The dicing die bond film includes a dicing tape having a pressure-sensitive adhesive layer laminated on a base layer, and a die bond layer (die bond film) releasably laminated on the pressure-sensitive adhesive layer of the dicing tape.

[0003] As a method for obtaining a semiconductor chip (die) for die bonding using the dicing die bond film, Patent Document 1 discloses a method including a half-cut process in which a groove is formed in a semiconductor wafer to process the semiconductor wafer into a chip (die) by a fracturing process, a back-grind process in which the semiconductor wafer after the half-cut process is ground to reduce its thickness, a mounting process in which one surface (the surface opposite to the circuit surface) of the semiconductor wafer after the back-grind process is attached to a die-bonding layer and the semiconductor wafer is fixed to a dicing tape, an expanding process in which the space between the half-cut semiconductor chips is expanded, a kerf maintaining process in which the space between the semiconductor chips is maintained, and a pick-up process in which the die-bonding layer and the adhesive layer are peeled off to remove the semiconductor chip with the die-bonding layer attached.

[0004] In the pick-up process, the semiconductor chip with the die bond layer attached (hereinafter also referred to as the semiconductor chip with the die bond layer) taken out is bonded to a wiring board as an adherend. After being bonded to the wiring board, the semiconductor chip with the die bond layer is electrically connected to the wiring board at a predetermined temperature (e.g., 150°C) by wire bonding or the like. The semiconductor chip with the die bond layer and the wiring board are sealed (molded) with a sealing resin while electrically connected by wire bonding or the like, and the sealing resin is cured at a predetermined temperature (e.g., 175°C) to form a semiconductor package. The semiconductor package is then electrically connected to a motherboard by soldering at a predetermined temperature (for example, 260° C.) to form a semiconductor device.

[0005] In recent years, there has been an increasing demand for higher performance, thinner and smaller semiconductor devices and semiconductor packages. As a measure to meet this demand, a method has been developed in which the semiconductor chip with the die bond layer is thinned and the thinned semiconductor chip with the die bond layer is stacked in a stepped manner in multiple stages, that is, the thinned semiconductor chip with the die bond layer is mounted three-dimensionally, thereby achieving high density integration of the semiconductor package and therefore high density integration of the semiconductor device. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] JP 2019-9203 A Summary of the Invention [Problem to be solved by the invention]

[0007] However, gaps (voids) may occur between the surface of the wiring board and the surface of the die bond layer, or between the surface of the die bond layer and the surface of the semiconductor chip. Although the voids can be removed to a certain extent while the sealing resin is hardening at a predetermined temperature, if a relatively large number of voids are generated between the surface of the wiring board etc. and the surface of the die bond layer, it may not be possible to sufficiently remove the voids while the sealing resin is hardening. If the voids cannot be sufficiently removed, the voids contain not only air but also moisture in the air, resulting in a relatively large amount of moisture in the semiconductor package. In such a case, during soldering at a predetermined temperature (e.g., 260°C) for electrically connecting the semiconductor package to the motherboard, the degree of volume expansion due to evaporation of the moisture in the semiconductor package increases, and this large volume expansion causes a large increase in pressure in the semiconductor package. As a result, there is a risk of a phenomenon (so-called popcorn phenomenon) occurring in which the semiconductor package is destroyed by this large increase in pressure. However, it cannot be said that sufficient studies have been made yet on how to sufficiently prevent voids from remaining between the die bond layer (die bond film) and the wiring board or the like.

[0008] Therefore, an object of the present invention is to provide a die bond film that can relatively suppress the formation of voids between the die bond film and a wiring board or the like, and a dicing die bond film that includes the die bond film. [Means for solving the problem]

[0009] As a result of intensive research by the present inventors, it was found that the die bond film contains an acrylic resin, a phenolic resin, and a filler, and the specific surface area of ​​the filler is set to 5 m 2 / g or more 100m 2 / g or less, and the mass ratio of the filler to the acrylic resin is greater than 0 and not more than 1.50, it has been found that the occurrence of voids remaining between the wiring board, etc. can be relatively suppressed, which has led to the invention.

[0010] That is, the die bond film according to the present invention is A die bond film containing an acrylic resin, a phenolic resin, and a filler, The filler has a specific surface area of ​​5 m 2 / g or more 100m 2 / g or less, The mass ratio of the filler to the acrylic resin is greater than 0 and is 1.50 or less.

[0011] According to such a configuration, it is possible to relatively prevent voids from remaining between the wiring board and the like.

[0012] In the die bond film, The water absorption is preferably 0.22% by mass or less.

[0013] According to this configuration, it is possible to further prevent voids from remaining between the wiring board and the like.

[0014] In the die bond film, The ratio of the parallel ray transmittance at a wavelength of 1000 nm to the parallel ray transmittance at a wavelength of 250 nm is preferably 2100 or more and 4500 or less.

[0015] According to this configuration, it is possible to further prevent voids from remaining between the wiring board and the like.

[0016] In the die bond film, The ratio of the thickness of the die-bonding film to the average particle diameter of the filler is preferably 5 or more and 150 or less.

[0017] According to this configuration, it is possible to further prevent voids from remaining between the wiring board and the like.

[0018] The dicing die bond film according to this embodiment is a dicing tape having a pressure-sensitive adhesive layer laminated on a base layer; a die bond layer laminated on the pressure-sensitive adhesive layer of the dicing tape; The die-bonding layer is any one of the die-bonding films described above.

[0019] According to such a configuration, it is possible to relatively prevent voids from remaining between the wiring board and the like. Effect of the Invention

[0020] According to the present invention, it is possible to provide a die bond film that can relatively suppress the formation of voids between the die bond film and a wiring board or the like, and a dicing die bond film that includes the die bond film. [Brief description of the drawings]

[0021] [Figure 1] 1 is a cross-sectional view showing a configuration of a dicing die bond film according to one embodiment of the present invention. [Figure 2A] 1A to 1C are cross-sectional views each showing a schematic view of a half-cut process in a manufacturing method of a semiconductor integrated circuit. [Figure 2B] 1A to 1C are cross-sectional views each showing a schematic view of a half-cut process in a manufacturing method of a semiconductor integrated circuit. [Figure 2C] 1A to 1C are cross-sectional views each showing a schematic diagram of a back grinding process in a manufacturing method of a semiconductor integrated circuit. [Figure 2D] 1A to 1C are cross-sectional views each showing a schematic diagram of a back grinding process in a manufacturing method of a semiconductor integrated circuit. [Figure 3A] 1A to 1C are cross-sectional views each showing a schematic view of a mounting step in a manufacturing method of a semiconductor integrated circuit. [Figure 3B] 1A to 1C are cross-sectional views each showing a schematic view of a mounting step in a manufacturing method of a semiconductor integrated circuit. [Figure 4A] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step performed at a low temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 4B] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step performed at a low temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 4C] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step performed at a low temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 5A] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step at room temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 5B] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step at room temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 6] 1A to 1C are cross-sectional views each showing a kerf maintaining step in a method for manufacturing a semiconductor integrated circuit. [Figure 7] 1A to 1C are cross-sectional views each showing a pickup step in a method for manufacturing a semiconductor integrated circuit. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0022] Hereinafter, one embodiment of the present invention will be described.

[0023] [Die bond film] The die bond film according to the present embodiment contains an acrylic resin, a phenolic resin, and a filler. The die bond film of this embodiment preferably contains 40% by mass or more and 60% by mass or less of the acrylic resin, preferably contains 5% by mass or more and 7% by mass or less of the phenol resin, and preferably contains 40% by mass or more and 60% by mass or less of the filler.

[0024] In the die-bonding film according to the present embodiment, the content mass ratio of the filler to the acrylic resin is greater than 0 and equal to or less than 1.50.

[0025] The die-bonding film according to the present embodiment preferably has thermosetting properties. That is, the die-bonding film according to the present embodiment preferably contains a resin having thermosetting properties and a curing agent for the resin having thermosetting properties.

[0026] Examples of the resin having thermosetting properties include a thermosetting resin and a thermoplastic resin having a thermosetting functional group.

[0027] Examples of the thermoplastic resin having a thermosetting functional group include a thermosetting functional group-containing acrylic resin (also called a thermosetting acrylic resin). That is, the acrylic resin may have thermosetting properties by including a thermosetting functional group. The acrylic resin in the thermosetting functional group-containing acrylic resin includes those containing monomer units derived from (meth)acrylic acid ester. In this specification, "(meth)acrylic" means at least one of "acrylic" and "methacrylic". The thermosetting functional group-containing acrylic resin may be used alone or in combination of two or more.

[0028] Examples of the (meth)acrylic acid ester include a hydrocarbon group-containing (meth)acrylic acid ester. Examples of the hydrocarbon group-containing (meth)acrylic acid ester include an alkyl (meth)acrylic acid ester, a cycloalkyl (meth)acrylic acid ester, and an aryl (meth)acrylic acid ester. The hydrocarbon group-containing (meth)acrylic acid ester may be used alone or in combination of two or more. In the die-bonding film, in order to appropriately exhibit basic properties such as adhesion due to the hydrocarbon group-containing (meth)acrylic acid ester, the mass ratio of the hydrocarbon group-containing (meth)acrylic acid ester in the total monomer components for forming the acrylic resin is preferably 40 mass% or more, more preferably 60 mass% or more.

[0029] The thermosetting functional group-containing acrylic resin preferably contains, as a constituent unit, a monomer containing an alkyl acrylate or a thermosetting functional group such as a glycidyl group, a carboxy group, a hydroxy group, an isocyanate group, etc. Among these, the monomer containing a thermosetting functional group preferably contains, as a constituent unit, a monomer containing a glycidyl group. Examples of the alkyl acrylate include ethyl acrylate, butyl acrylate, butyl methacrylate, hexyl acrylate, and lauryl acrylate. The monomer containing a glycidyl group includes a (meth)acrylic acid ester having a glycidyl group, etc. The (meth)acrylic acid ester having a glycidyl group includes glycidyl (meth)acrylate, etc. Examples of the monomer containing a carboxy group include acrylic acid, methacrylic acid, carboxyethyl (meth)acrylate, carboxypentyl (meth)acrylate, itaconic acid, maleic acid, fumaric acid, and crotonic acid. Examples of the monomer containing a hydroxy group include 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, 6-hydroxyhexyl (meth)acrylate, 8-hydroxyoctyl (meth)acrylate, 10-hydroxydecyl (meth)acrylate, 12-hydroxylauryl (meth)acrylate, and (4-hydroxymethylcyclohexyl)methyl (meth)acrylate. Examples of the monomer containing an isocyanate group include methacryloyl isocyanate, 2-methacryloyloxyethyl isocyanate (MOI), and m-isopropenyl-α,α-dimethylbenzoyl isocyanate. As the thermosetting functional group-containing acrylic resin, a copolymer of ethyl acrylate, butyl acrylate, acrylonitrile, and glycidyl methacrylate is particularly preferable. Furthermore, when the thermosetting functional group-containing acrylic resin contains a monomer containing a glycidyl group as a constituent unit, the equivalent ratio of the hydroxyl group of the phenol resin to the glycidyl group is preferably 0 or more and 3.0 or less, more preferably 1.0 or more and 2.0 or less, and particularly preferably 1.2 or more and 1.7 or less. The copolymer preferably has a mass average molecular weight of 600,000 to 1,600,000, more preferably 800,000 to 1,500,000, and particularly preferably 1,000,000 to 1,400,000. The copolymer preferably has a glass transition temperature Tg of -5°C to 25°C, more preferably 0°C to 20°C, and even more preferably 2°C to 18°C. The copolymer particularly preferably has a glass transition temperature Tg of 2°C to 6°C. The mass average molecular weight is a value converted by standard polystyrene by the GPC method. As the GPC main body, HLC-8120GPC manufactured by Tosoh Corporation was used, with a column temperature of 40°C, a pump flow rate of 0.5 mL / min, and a detector RI. Data processing can be performed using a calibration curve of standard polystyrene with a known molecular weight (a calibration curve was created using standard polystyrene with molecular weights of 20.6 million, 8.42 million, 4.48 million, 1.11 million, 707 million, 354 million, 189 million, 98.9 million, 37.2 million, 17.1 million, 9830, 5870, 2500, 1050, and 500), and the molecular weight can be obtained from the converted molecular weight. In addition, as the column, two TSKgel GMH-H(S) (manufactured by Tosoh Corporation) connected in series are used, tetrahydrofuran is used as the mobile phase, the injection amount is 100 μL, and the sample concentration is 1.0 g / L (the sample is dissolved in tetrahydrofuran). The glass transition temperature Tg means the midpoint glass transition temperature according to JIS K7121:2012.

[0030] Examples of the thermosetting resin include epoxy resin, phenol resin, amino resin, unsaturated polyester resin, polyurethane resin, silicone resin, and thermosetting polyimide resin, etc. The thermosetting resin may be used alone or in combination of two or more kinds. Of the various thermosetting resins mentioned above, it is preferable to use an epoxy resin.

[0031] Examples of epoxy resins include bisphenol A type, bisphenol F type, bisphenol S type, brominated bisphenol A type, hydrogenated bisphenol A type, bisphenol AF type, biphenyl type, naphthalene type, fluorene type, phenol novolac type, orthocresol novolac type, trishydroxyphenylmethane type, tetraphenylolethane type, hydantoin type, trisglycidyl isocyanurate type, and glycidylamine type epoxy resins.

[0032] The die bond film may contain a thermoplastic resin. The thermoplastic resin functions as a binder. Examples of the thermoplastic resin include natural rubber, butyl rubber, isoprene rubber, chloroprene rubber, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, ethylene-acrylic acid ester copolymer, polybutadiene resin, polycarbonate resin, thermoplastic polyimide resin, polyamide resin such as polyamide 6 and polyamide 6,6, phenoxy resin, acrylic resin, saturated polyester resin such as PET and PBT, polyamideimide resin, fluororesin, etc. That is, the acrylic resin may be included as a thermoplastic resin. The thermoplastic resin may be used alone or in combination of two or more. As the thermoplastic resin, an acrylic resin is preferable from the viewpoint that the connection reliability by the die bond film can be easily ensured since it contains little ionic impurities and has high heat resistance.

[0033] Examples of the acrylic resin as the thermoplastic resin include those containing monomer units derived from (meth)acrylic acid ester as described above. The acrylic resin as the thermoplastic resin may contain a structural unit derived from another monomer component copolymerizable with the hydrocarbon group-containing (meth)acrylic acid ester from the viewpoint of realizing high cohesive strength and high heat resistance in the die-bonding film. Examples of the other monomer component include an acid anhydride monomer, a sulfonic acid group-containing monomer, a phosphoric acid group-containing monomer, and a functional group-containing monomer such as acrylamide or acrylonitrile. Only one type of the other monomer component may be used, or two or more types may be used in combination. In the die bond film, in order to properly express the properties such as adhesion due to the hydrocarbon group-containing (meth)acrylic acid ester, the mass ratio of the other monomer components in the total monomer components for forming the acrylic resin is preferably 60 mass% or less, and more preferably 40 mass% or less.

[0034] The phenolic resin is a curing agent for the thermosetting resin. Examples of such phenolic resins include novolac-type phenolic resins, resol-type phenolic resins, and polyoxystyrenes such as polyparaoxystyrene. As the phenolic resin, it is preferable to use a biphenylaralkyl-type phenolic resin. An example of a commercially available biphenylaralkyl-type phenolic resin is the product name "MEH-7851SS" manufactured by Meiwa Kasei Co., Ltd.

[0035] The filler is contained in the die-bonding film in order to adjust the physical properties, such as the electrical conductivity, the thermal conductivity, and the elastic modulus, of the die-bonding film. As the filler, either an inorganic filler or an organic filler can be used, but it is preferable to use an inorganic filler. Examples of the inorganic filler include aluminum hydroxide, magnesium hydroxide, calcium carbonate, magnesium carbonate, calcium silicate, magnesium silicate, calcium oxide, magnesium oxide, aluminum oxide, titanium oxide, aluminum nitride, aluminum borate whisker, boron nitride, and silica (crystalline silica and amorphous silica), as well as simple metals such as aluminum, gold, silver, copper, and nickel, alloys, amorphous carbon black, and graphite. The filler may have various shapes such as a spherical shape, a needle shape, a flake shape, etc. The filler may be used alone or in combination of two or more kinds. Among the above inorganic fillers, it is preferable to use aluminum hydroxide, magnesium hydroxide, calcium oxide, magnesium oxide, aluminum oxide, titanium oxide, and silica (silicon (di)oxide), and it is particularly preferable to use silica.

[0036] In the die bond film according to this embodiment, the filler has a specific surface area of ​​5 m 2 / g or more 100m 2 / g or less. The specific surface area is 5 m 2 / g or more 60m 2 / g or less, and 2 / g or more 40m 2 / g or less is more preferable, and 2 / g or more 25m 2 It is more preferable that the molecular weight is not more than 1 / g. The specific surface area can be determined by a nitrogen adsorption method (JIS Z8830:2010).

[0037] The average particle size of the filler is preferably 40 nm or more and 600 nm or less, more preferably 60 nm or more and 500 nm or less, and particularly preferably 180 nm or more and 500 nm or less. By having the average particle size of the filler within the above numerical range, the specific surface area of ​​the filler can be set within the above numerical range (5 m 2 / g or more 100m 2 / g or less). The average particle size of the filler can be measured by dynamic light scattering (DLS). Specifically, the filler is dispersed in methyl ethyl ketone (MEK) so that the solid content concentration is 1% by mass or less to prepare a sample for particle size measurement, and the average particle size of the filler in the sample for particle size measurement is measured by a dynamic light scattering photometer (model number "ZEN3600": manufactured by Sysmex Corporation). The sample for particle size measurement may be treated with an ultrasonic homogenizer for 2 minutes before measurement.

[0038] The die bond film contains the acrylic resin, the phenol resin, and the filler, and the specific surface area of ​​the filler is set to 5 m 2 / g or more 100m 2 The inventors of the present invention surmise that the reason why the formation of voids between the printed wiring board and the like can be relatively suppressed by setting the filler content mass ratio to the acrylic resin at more than 0 and not more than 1.50 is as follows.

[0039] In general, when a filler and a resin are mixed uniformly, it is necessary to appropriately adjust parameters that contribute to polarity, such as surface tension and SP value (solubility parameter), to increase the affinity between the filler and the resin. When the affinity between the filler and the resin is increased, the resin is bound to the surface of the filler. In particular, as the particle size of the filler becomes smaller, the number of atoms present on the surface of the filler relative to the total number of atoms constituting the filler becomes larger, and therefore the force acting between the atoms present on the surface of the filler becomes smaller than that between the atoms present inside the filler. And, as the number of atoms present on the surface of the filler becomes relatively larger, the surface free energy of the filler becomes higher. In such a case, the filler becomes stable by reducing the surface free energy by attaching other substances to the surface.

[0040] In this situation, when the mass of the filler mixed with the resin is kept constant and the particle size of the filler is reduced, the ratio of the specific surface area of ​​the filler to the mass of the filler increases, and the amount of the resin bound to the surface of the filler also increases accordingly. That is, it is considered that the filler also functions to pseudo-crosslink the acrylic resin in the die bond film.

[0041] As described above, when the acrylic resin is restrained by the filler in the die bond film, it is considered that the gap (hereinafter also referred to as free volume) generated between the acrylic resin in the die bond film is reduced. And, it is considered that the more the portion in which the acrylic resin is restrained by the filler increases, the smaller the free volume in the die bond film is. And, as the free volume in the die bond film decreases, it is considered that when a void occurs between a printed wiring board or the like and the die bond film, it becomes difficult to move the air and moisture contained in the void into the die bond film. It is considered that such a problem becomes more significant when the acrylic resin is a resin having thermosetting properties, i.e., when the acrylic resin is a thermosetting group-containing acrylic resin (thermosetting acrylic resin), because in addition to crosslinking of the acrylic resin itself, pseudo crosslinking is also formed by the filler.

[0042] However, although the die bond film according to the present embodiment contains the acrylic resin and the filler, the specific surface area of ​​the filler is 100 m 2 / g or less, it is considered that the acrylic resin is prevented from being excessively constrained by the filler, and as a result, it is considered that the free volume in the die bond film is relatively prevented from being reduced to a level where it becomes difficult for the air and moisture contained in the voids to move into the die bond film. In addition, the mass ratio of the filler to the acrylic resin is greater than 0 and less than or equal to 1.50, that is, the mass ratio of the acrylic resin is sufficiently greater than the mass ratio of the filler. Therefore, even when it is considered that the acrylic resin is constrained by the filler, it is considered that a sufficient free volume can be secured in the die bond film. It is believed that this allows the air and moisture contained in the voids to be sufficiently transferred into the die bond film at the temperature (e.g., 175°C) when the sealing resin is cured when a semiconductor package is obtained, and as a result, it is believed that it is possible to relatively suppress the occurrence of voids remaining between the wiring board or the like and the die bond film. In addition, since the air and moisture that have moved into the die bond film can be sufficiently released into the atmosphere while the sealing resin is curing, the amount of moisture remaining in the semiconductor package can be relatively small in the state where the semiconductor package is formed. As a result, the so-called popcorn phenomenon can be suppressed from occurring during heating in a reflow furnace when obtaining a semiconductor device.

[0043] In the die bond film according to this embodiment, the lower limit of the surface area of ​​the filler is 5 m 2 / g, it is considered that the filler can be made to have a size capable of suppressing surface exposure from the die bond film.

[0044] The die bond film may contain a thermosetting catalyst (curing accelerator) from the viewpoint of sufficiently advancing the curing reaction of the resin component or increasing the curing reaction rate. Examples of the thermosetting catalyst include imidazole-based compounds, triphenylphosphine-based compounds, amine-based compounds, and trihalogen borane-based compounds.

[0045] The die-bonding film may contain one or more other components as necessary, such as a flame retardant, a silane coupling agent, and an ion trapping agent.

[0046] The thickness of the die bond film is not particularly limited, but is, for example, 0.5 μm or more and 200 μm or less. The thickness may be 1 μm or more and 50 μm or less, or 2 μm or more and 30 μm or less. The thickness of the die bond film can be determined, for example, by measuring the thickness at five randomly selected points using a dial gauge (manufactured by PEACOCK, model R-205) and calculating the arithmetic average of these thicknesses.

[0047] In the die-bonding film, the ratio of the thickness of the die-bonding film to the average particle diameter of the filler is preferably 5 or more and 150 or less. It is considered that by setting the ratio of the thickness of the die-bonding film to the average particle size of the filler to 5 or more, surface exposure of the filler from the die-bonding film can be suppressed. In addition, since the ratio of the thickness of the die bond film to the average particle diameter of the filler is 150 or less, the filler contained in the die bond film has a relatively large average particle diameter. As a result, the filler contained in the die bond film has a relatively small specific surface area, so that the acrylic resin can be further prevented from being excessively restrained by the filler. This makes it possible to further prevent voids from remaining between a printed wiring board or the like and the die bond film.

[0048] In the die-bonding film, the water absorption rate is preferably 0.22% by mass or less, more preferably 0.19% by mass or less, and further preferably 0.12% by mass or less. The water absorption rate can be measured by Karl Fischer moisture vaporization-coulometric titration method (JIS K 0113:2005). Specifically, a 10 mg sample taken from the die bond film is heated and vaporized at 150°C for 3 minutes using a Karl Fischer moisture meter (manufactured by Mitsubishi Chemical Corporation, a moisture vaporizer VA-07 connected to a trace moisture measuring device (coulometric titration type automatic moisture measuring device) CA-07 and an automatic moisture measuring device KF-07), and the amount of moisture generated is measured, and the ratio to the sample mass before heating can be calculated as the water absorption rate. Water absorption rate (mass%) = (water content measured by Karl Fischer / total mass of sample before measurement) x 100

[0049] When the water absorption rate in the die bond film is 0.22 mass% or less, it is possible to reduce the amount of water vapor generated in the die bond film when the die bond film is heated to 100° C. or more, thereby making it possible to further suppress the occurrence of voids remaining between a wiring board or the like and the die bond film.

[0050] In the die-bonding film, the ratio of the parallel ray transmittance at a wavelength of 1000 nm to the parallel ray transmittance at a wavelength of 250 nm is preferably 2100 or more and 4500 or less, and more preferably 2500 or more and 3500 or less. By having the ratio of the parallel ray transmittance at a wavelength of 1000 nm to the parallel ray transmittance at a wavelength of 250 nm within the above numerical range, voids can be further prevented from remaining between the wiring board or the like and the die bond film. As described above, by making the ratio of the parallel ray transmittance at a wavelength of 1000 nm to the parallel ray transmittance at a wavelength of 250 nm fall within the above-mentioned numerical range, it is considered that the curing reaction of the die bond film can be prevented from proceeding excessively due to the thermal history (the history of the amount of heat that contributes to the progress of the curing reaction and the history of the environmental temperature, etc.) during the period from when the die bond film (for example, the die bond film attached to one side of a semiconductor chip) is attached to a wiring board or the like until the wiring board to which the die bond film is attached is sealed (molded) using a sealing resin. For example, it is considered that the multiple factors (the amount of multiple organic components (for example, phenolic resin, acrylic resin, etc.) that contribute to the curing reaction of the die bond film, etc.) can be appropriately adjusted. As a result, the free volume in the die bond film can be more sufficiently secured, and the air and moisture contained in the voids can be more sufficiently moved within the die bond film, which is believed to further prevent the voids from remaining between a wiring board or the like and the die bond film. The present inventors believe that the above-mentioned reasons are factors that can further suppress the occurrence of voids between the wiring board or the like and the die bond film.

[0051] In the die bond film, the value of the parallel ray transmittance at a wavelength of 250 nm is preferably 0.01% or more and 0.05% or less, and more preferably 0.02% or more and 0.04% or less. In the die-bonding film, the value of the parallel ray transmittance at a wavelength of 1000 nm is preferably 60% or more and 100% or less, and more preferably 75% or more and 95% or less. The parallel ray transmittance at a wavelength of 250 nm and the parallel ray transmittance at a wavelength of 1000 nm of the die bond film can be measured using a spectrophotometer (manufactured by JASCO Corporation, product name "V-670"). The measurement wavelength can be in the range of 190 nm to 1400 nm. The measurement sample can be the die bond film prepared to have a thickness of about 20 μm.

[0052] [Dicing die bond film] As shown in Figure 1, the dicing die bond film 20 of this embodiment comprises a dicing tape 10 having an adhesive layer 2 laminated on a base layer 1, and a die bond layer 3 laminated on the adhesive layer 2 of the dicing tape 10. In the dicing die bond film 20 according to this embodiment, the die bond layer 3 is made of the die bond film described above. In the dicing die bond film 20 according to this embodiment, a semiconductor wafer is attached onto the die bond layer 3. When the semiconductor wafer is cut using the dicing die bond film 20, the die bond layer 3 is cut together with the semiconductor wafer. The die bond layer 3 is cut into pieces having sizes corresponding to the sizes of the individual semiconductor chips. This allows the semiconductor chips with the die bond layer 3 to be obtained.

[0053] The base layer 1 supports the pressure-sensitive adhesive layer 2. The base layer 1 is made of a resin film. Examples of resins contained in the resin film include polyolefin, polyester, polyurethane, polycarbonate, polyether ether ketone, polyimide, polyetherimide, polyamide, wholly aromatic polyamide, polyvinyl chloride, polyvinylidene chloride, polyphenyl sulfide, fluororesin, cellulose-based resin, and silicone resin.

[0054] As the polyolefin, polyester, polyurethane, polycarbonate, polyether ether ketone, polyimide, polyetherimide, polyamide, wholly aromatic polyamide, polyvinyl chloride, polyvinylidene chloride, polyphenyl sulfide, fluororesin, cellulose-based resin, and silicone resin, various known resins can be used.

[0055] The adhesive layer 2 contains an adhesive and adheres to the adhesive layer 2 to hold a semiconductor wafer to be diced into semiconductor chips.

[0056] The adhesive may be one whose adhesive strength can be reduced by an external action during use of the dicing tape 10 (hereinafter, referred to as a reduced-adhesion adhesive).

[0057] When a reduced-adhesion adhesive is used as the adhesive, the adhesive layer 2 can be used in a state where it exhibits a relatively high adhesive strength (hereinafter referred to as a high-adhesion state) and a state where it exhibits a relatively low adhesive strength (hereinafter referred to as a low-adhesion state) during the use of the dicing tape 10. For example, when a semiconductor wafer attached to the dicing tape 10 is subjected to cleavage, the high-adhesion state is used to prevent the multiple semiconductor chips separated by cleavage of the semiconductor wafer from lifting up or peeling off from the adhesive layer 2. On the other hand, in order to pick up the multiple semiconductor chips separated after cleavage of the semiconductor wafer, the low-adhesion state is used to make it easier to pick up the multiple semiconductor chips from the adhesive layer 2.

[0058] The reduced tack adhesive may be, for example, an adhesive that can be cured by exposure to radiation during use of the dicing tape 10 (hereinafter, referred to as a radiation-curable adhesive).

[0059] Examples of the radiation-curable adhesive include adhesives that are cured by irradiation with electron beams, ultraviolet rays, α rays, β rays, γ rays, or X-rays. Among these, it is preferable to use an adhesive that is cured by irradiation with ultraviolet rays (ultraviolet-curable adhesive).

[0060] Examples of the radiation-curable adhesive include additive-type radiation-curable adhesives that contain a base polymer as a main component and a radiation-polymerizable monomer component or a radiation-polymerizable oligomer component having a functional group such as a radiation-polymerizable carbon-carbon double bond. As the base polymer, an acrylic polymer is preferably used.

[0061] The acrylic polymer includes a monomer unit derived from a (meth)acrylic acid ester, such as an alkyl (meth)acrylate, a cycloalkyl (meth)acrylate, or an aryl (meth)acrylate. As the acrylic polymer, for example, 2-hydroxyethyl acrylate (HEA), ethyl acrylate (EA), butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), isononyl acrylate (INA), lauryl acrylate (LA), 4-acryloylmorpholine (AMCO), 2-isocyanatoethyl methacrylate (MOI), etc. are preferably used. These acrylic polymers may be used alone or in combination of two or more.

[0062] The pressure-sensitive adhesive layer 2 may contain an external crosslinking agent. Any external crosslinking agent can be used as long as it can react with a base polymer (e.g., an acrylic polymer) to form a crosslinked structure. Examples of such external crosslinking agents include polyisocyanate compounds, epoxy compounds, polyol compounds, aziridine compounds, and melamine-based crosslinking agents.

[0063] Examples of the radiation polymerizable monomer component include urethane (meth)acrylate, trimethylolpropane tri(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol monohydroxypenta(meth)acrylate, dipentaerythritol hexa(meth)acrylate, and 1,4-butanediol di(meth)acrylate. Examples of the radiation polymerizable oligomer component include various oligomers such as urethane-based, polyether-based, polyester-based, polycarbonate-based, and polybutadiene-based oligomers. The content of the radiation polymerizable monomer component or radiation polymerizable oligomer component in the radiation curable adhesive is selected within a range that appropriately reduces the adhesiveness of the adhesive layer 2.

[0064] The radiation-curable adhesive preferably contains a photopolymerization initiator, such as an α-ketol compound, an acetophenone compound, a benzoin ether compound, a ketal compound, an aromatic sulfonyl chloride compound, a photoactive oxime compound, a benzophenone compound, a thioxanthone compound, camphorquinone, a halogenated ketone, an acylphosphinoxide, or an acylphosphonate.

[0065] When the pressure-sensitive adhesive layer 2 contains an external crosslinking agent, the pressure-sensitive adhesive layer 2 preferably contains the external crosslinking agent in an amount of 0.1 parts by mass or more and 3 parts by mass or less. When the pressure-sensitive adhesive layer 2 contains a photopolymerization initiator, the pressure-sensitive adhesive layer 2 preferably contains 0.1 parts by mass or more and 10 parts by mass or less of the photopolymerization initiator.

[0066] The pressure-sensitive adhesive layer 2 may contain, in addition to the above-mentioned components, a crosslinking accelerator, a tackifier, an antiaging agent, a colorant such as a pigment or a dye, and the like.

[0067] The thickness of the pressure-sensitive adhesive layer 2 is preferably from 1 μm to 50 μm, more preferably from 2 μm to 30 μm, and even more preferably from 5 μm to 25 μm. The thickness of the adhesive layer 2 can be determined, for example, by measuring the thickness at five randomly selected points using a dial gauge (manufactured by PEACOCK, model R-205) and calculating the arithmetic average of these thicknesses.

[0068] The dicing die bond film 20 according to this embodiment is used, for example, as an auxiliary tool for manufacturing a semiconductor integrated circuit. A specific example of the use of the dicing die bond film 20 will be described below. In the following, an example will be described in which a dicing die bond film 20 having a single base layer 1 is used.

[0069] The method for manufacturing a semiconductor integrated circuit includes a half-cut process in which a groove is formed in the semiconductor wafer to process the semiconductor wafer into chips (dies) by a fracturing process, a back-grind process in which the semiconductor wafer after the half-cut process is ground to reduce its thickness, a mounting process in which one surface (the surface opposite to the circuit surface) of the semiconductor wafer after the back-grind process is attached to a die-bonding layer 3 and the semiconductor wafer is fixed to a dicing tape 10, an expanding process in which the interval between the half-cut semiconductor chips is expanded, a kerf maintaining process in which the interval between the semiconductor chips is maintained, a pick-up process in which the die-bonding layer 3 is peeled off from the adhesive layer 2 to take out the semiconductor chip (die) with the die-bonding layer 3 attached, and a die-bonding process in which the semiconductor chip (die) with the die-bonding layer 3 attached is attached to an adherend. When these processes are carried out, the dicing die-bonding film 20 of this embodiment is used as a manufacturing auxiliary tool.

[0070] In the half-cut process, as shown in FIG. 2A and FIG. 2B, a half-cut process is performed to split the semiconductor wafer into small pieces (dies). More specifically, a wafer processing tape T is attached to the surface of the semiconductor wafer W opposite to the circuit surface (see FIG. 2A). A dicing ring R is attached to the wafer processing tape T (see FIG. 2A). With the wafer processing tape T attached, a groove for division is formed (see FIG. 2B). In the back-grind process, as shown in FIG. 2C and FIG. 2D, the semiconductor wafer is ground to reduce its thickness. More specifically, a back-grind tape G is attached to the surface where the groove is formed, while the wafer processing tape T attached initially is peeled off (see FIG. 2C). With the back-grind tape G attached, the semiconductor wafer W is ground until it reaches a predetermined thickness (see FIG. 2D).

[0071] 3A and 3B, in the mounting process, after a dicing ring R is attached to the adhesive layer 2 of the dicing tape 10, a half-cut semiconductor wafer W is attached to the exposed surface of the die bond layer 3 (see FIG. 3A). Then, the backgrind tape G is peeled off from the semiconductor wafer W (see FIG. 3B).

[0072] In the expanding step, as shown in Figs. 4A to 4C, the dicing ring R is fixed to a holder H of an expanding device. The dicing die bond film 20 is pushed up from below by a push-up member U provided in the expanding device, so that the dicing die bond film 20 is stretched so as to be expanded in the planar direction (see Fig. 4B). As a result, the half-cut semiconductor wafer W is cleaved under specific temperature conditions. The above temperature conditions are, for example, -15 to 40°C, preferably -15 to 10°C, and more preferably -15 to 0°C. The expanded state is released by lowering the push-up member U (see Fig. 4C). 5A and 5B, in the expanding step, the dicing tape 10 is stretched so as to expand its area under higher temperature conditions (for example, 15 to 60° C., preferably 20 to 40° C., and more preferably room temperature (23° C.)). This causes adjacent cleaved semiconductor chips to be separated in the planar direction of the film surface, further increasing the distance between them.

[0073] A series of steps from the half-cutting step to the expanding step may be referred to as a "DBG (Dicing Before Grinding) cleaving process." In addition, the half-cut process can be replaced with a modified region forming process in which a laser beam is irradiated to a planned dividing line in the semiconductor wafer to form a modified region, thereby making it possible to easily divide the semiconductor wafer at the planned dividing line. A series of processes from the modified region forming process to the expanding process is sometimes called an "SDBG (Stealth Dicing Before Grinding) cleaving process."

[0074] In the kerf maintaining process, as shown in FIG. 6, hot air (the setting value of the device generating the hot air is, for example, 200 to 250° C.) is applied to the dicing tape 10 to thermally shrink the dicing tape 10, and then the dicing tape 10 is cooled and solidified, thereby maintaining the distance (kerf) between adjacent cleaved semiconductor chips.

[0075] 7, in the pick-up process, the semiconductor chip with the die bond layer 3 attached (hereinafter also referred to as the semiconductor chip with the die bond layer) is peeled off from the adhesive layer 2 of the dicing tape 10. In detail, the pin member P is raised to push up the semiconductor chip with the die bond layer to be picked up through the dicing tape 10. The pushed-up semiconductor chip with the die bond layer is held by the suction jig J.

[0076] In the die bonding step, the semiconductor chip with the die bonding layer is bonded to an adherend (wiring board). In the dicing die bond film 20 according to this embodiment, since the die bond film described above is used as the die bond layer 3, the semiconductor chip with the die bond layer is adhered to the wiring board, the semiconductor chip with the die bond layer and the wiring board are electrically connected by wire bonding, and the semiconductor chip with the die bond layer and the wiring board that are wire bonded are sealed with a sealing resin, and then the sealing resin is cured at a temperature (for example, 175° C.) at which voids generated between the wiring board and the die bond layer 3 (die bond film) can be sufficiently removed. That is, the remaining of voids between the wiring board and the die bond layer 3 can be relatively suppressed. This makes it possible to obtain a semiconductor package in which voids remaining between the wiring board and the die bond layer 3 are relatively suppressed, and therefore, when obtaining a semiconductor device, it is possible to relatively suppress the occurrence of the popcorn phenomenon in the semiconductor package when the semiconductor package is heated in a reflow furnace to electrically connect the semiconductor package to a motherboard.

[0077] Moreover, the dicing die bond film 20 according to this embodiment is used as a constituent member of a semiconductor package, as described above. In a specific example, the dicing die bond film 20 according to this embodiment is used as the bonding film of a semiconductor package comprising a plurality of semiconductor chips, a wiring board having a mounting surface on which the semiconductor chips are mounted, a plurality of bonding films for adhering the semiconductor chips to the wiring board, and a sealing resin (mold resin) for sealing (molding) the wiring board so as to cover at least the mounting surface, in which a first bonding film of the plurality of bonding films is bonded to the mounting surface, and the semiconductor chips and the remaining bonding films are alternately stacked on the first bonding film to form a laminated structure of the plurality of bonding films and the plurality of semiconductor chips, and the laminated structure is embedded in the sealing resin.

[0078] When manufacturing the above-mentioned semiconductor package, the laminated structure is formed so as to be fixed to the mounting surface by the first bonding film, and the mounting surface is sealed so that the laminated structure is embedded in the sealing resin in a thermally molten state. Forming the laminated structure may include fabricating a laminated structure in which each bonding film has thermosetting properties. Fabricating the laminated structure may include wire bonding the semiconductor chip and the wiring board. Fabricating the laminated structure may include thermally curing each bonding film after die attach (die bonding) in the wire bonding. The sealing may include causing a thermosetting reaction in the bonding film by the heat of the molding resin in a molten state. In other words, in wire bonding, it is not necessary to perform thermosetting of the bonding film individually after die attach (die bonding). If the bonding film is not individually thermoset, even if a void (gas) occurs between the bonding film and the wiring board or the like in the sealing (molding), the void disappears. The reason is as follows. In the case of compressing the laminated structure under high temperature and high pressure (e.g., 175°C, pressing pressure of 8MPa) during encapsulation, the voids (gas) are also compressed. The compressed gas with a smaller volume (i.e., gas with a smaller particle size) is mixed with the resin with an increased contact area with the resin, so that the free energy in the system including the laminated structure is stabilized. As a result of the stabilization of the free energy in the system, the voids can be sufficiently eliminated at the temperature when encapsulation is performed. Furthermore, in the part where the voids have been eliminated, the resin comes into contact with the surface of the wiring board, and the resin comes into contact with the surface of the semiconductor chip, and an anchor effect is generated in this contact part, so that the contact state between the resin and the surface of the wiring board, and the resin and the surface of the semiconductor chip is more sufficiently maintained after molding. As described above, the die bond film of this embodiment can relatively prevent voids from remaining between the die bond film and the surface of the adherend (e.g., a wiring board). Therefore, even when bonded to the wiring board as a laminated structure as described above, voids can relatively be prevented from remaining between the surface of the die bond film and the surface of the wiring board, and between the surface of the die bond film and the surface of the semiconductor chip.

[0079] The dicing die bond film according to the present invention is not limited to the above embodiment. The dicing die bond film according to the present invention is not limited by the above-mentioned action and effect. The dicing die bond film according to the present invention can be modified in various ways without departing from the gist of the present invention. EXAMPLES

[0080] The present invention will now be described in more detail with reference to examples. The following examples are provided to further explain the present invention in detail, and are not intended to limit the scope of the present invention.

[0081] [Example 1] <Preparation of die bond film> Acrylic resin A (acrylic resin solution in which a copolymer of ethyl acrylate (EA), butyl acrylate (BA), acrylonitrile (AN) and glycidyl methacrylate (GMA) (mass average molecular weight is 1,200,000, glass transition temperature Tg is 4°C) is dissolved in methyl ethyl ketone (MEK)), phenolic resin (product name "MEH-7851ss", manufactured by Meiwa Kasei Co., Ltd.), and methyl ethyl ketone (MEK) were mixed to prepare solution A1a, and further, solution A1b in which spherical silica (product name "SO-E2", manufactured by Admatechs Co., Ltd., average particle size 500 nm) was dispersed in methyl ethyl ketone was added to the solution A1a to prepare adhesive composition A so that the solid content concentration was 18 mass%. In the adhesive composition A, the acrylic resin A, the phenolic resin, and the spherical silica were in the mass ratios shown in Table 1. Next, the adhesive composition A was applied to the silicone release-treated surface of a PET separator (thickness 50 μm) having a surface that had been subjected to silicone release treatment using an applicator to form a coating film, and the coating film was subjected to a solvent removal treatment for 2 minutes at 130° C. As a result, a die bond film (die bond film according to Example 1) having a thickness (average thickness) of 7 μm was produced on the PET separator.

[0082] The average particle size of the spherical silica was measured by dynamic light scattering (DLS). Specifically, the spherical silica was dispersed in methyl ethyl ketone (MEK) so that the solid content concentration was 1% by mass or less to prepare a sample for particle size measurement, and the average particle size of the spherical silica in the sample for particle size measurement was measured by a dynamic light scattering photometer (model number "ZEN3600": manufactured by Sysmex Corporation). The sample for particle size measurement was treated with an ultrasonic homogenizer for 2 minutes before the measurement. In addition, the thickness of the die bond film according to Example 1 was determined by measuring the thickness at five randomly selected points using a dial gauge (manufactured by PEACOCK, model R-205) and calculating the arithmetic average of these thicknesses.

[0083] [Example 2] <Preparation of die bond film> As the solution A1b, Admatechs' product name "SO-C1" and Admatechs' product name "YC100C" were dispersed in methyl ethyl ketone (MEK) at a mass ratio of 2:3, surface-treated with methacrylsilane, and a silica particle dispersion solution obtained by cutting coarse particles with a 1 μm filter was used (average particle diameter of spherical silica particles is 180 nm). Except for the above, acrylic resin A, phenolic resin, and spherical silica were prepared to have the mass ratios shown in Table 1 below. The adhesive composition B was prepared in the same manner as in Example 1, and the adhesive composition B was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a desolvation treatment at 130 ° C. for 2 minutes. As a result, a die bond film (die bond film according to Example 2) having a thickness (average thickness) of 5 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 2 were measured in the same manner as in Example 1.

[0084] [Example 3] <Preparation of die bond film> As the solution A1b, Admatechs' product name "SO-C1" and Admatechs' product name "YC100C" were dispersed in methyl ethyl ketone (MEK) at a mass ratio of 2:3, surface-treated with vinylsilane, and a silica particle dispersion solution obtained by cutting coarse particles with a 1 μm filter was used (average particle diameter of spherical silica particles is 180 nm). Except for the above, acrylic resin A, phenolic resin, and spherical silica were prepared to have the mass ratios shown in Table 1 below. The adhesive composition C was prepared in the same manner as in Example 1, and the adhesive composition C was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a desolvation treatment at 130 ° C. for 2 minutes. As a result, a die bond film (die bond film according to Example 3) having a thickness (average thickness) of 9 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 3 were measured in the same manner as in Example 1.

[0085] [Example 4] <Preparation of die bond film> As the solution A1b, Admatechs' product name "SO-C1" and Admatechs' product name "YC100C" were dispersed in methyl ethyl ketone (MEK) at a mass ratio of 2:3, surface-treated with alkylsilane, and coarse particles were removed with a 1 μm filter to obtain a silica particle dispersion solution (average particle diameter of spherical silica particles is 180 nm). Except for the above, acrylic resin A, phenolic resin, and spherical silica were prepared to have the mass ratios shown in Table 1 below. The adhesive composition D was prepared in the same manner as in Example 1, and the adhesive composition D was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a desolvation treatment at 130 ° C. for 2 minutes. As a result, a die bond film (die bond film according to Example 4) having a thickness (average thickness) of 7 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 4 were measured in the same manner as in Example 1.

[0086] [Example 5] <Preparation of die bond film> Except for preparing the acrylic resin A, the phenolic resin, and the spherical silica so as to have the mass ratio shown in Table 1 below, adhesive composition E was prepared in the same manner as in Example 1, and the adhesive composition E was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a solvent removal treatment at 130° C. for 2 minutes. As a result, a die-bonding film (die-bonding film according to Example 5) having a thickness (average thickness) of 3 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 5 were measured in the same manner as in Example 1.

[0087] [Example 6] <Preparation of die bond film> As the solution A1b, Admatechs' product name "SO-C1" and Admatechs' product name "YC100C" were dispersed in methyl ethyl ketone (MEK) at a mass ratio of 2:3, surface-treated with phenylsilane, and a silica particle dispersion solution obtained by cutting coarse particles with a 1 μm filter was used (average particle diameter of spherical silica particles is 180 nm). Except for the above, acrylic resin A, phenolic resin, and spherical silica were prepared to have the mass ratios shown in Table 1 below. The adhesive composition F was prepared in the same manner as in Example 1, and the adhesive composition F was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a desolvation treatment at 130 ° C. for 2 minutes. As a result, a die bond film (die bond film according to Example 6) having a thickness (average thickness) of 5 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 6 were measured in the same manner as in Example 1.

[0088] [Example 7] <Preparation of die bond film> Except for replacing the spherical silica with Nissan Chemical's trade name "MEK-EC-7150P (50%)" (average particle size 60 nm), and preparing the acrylic resin A, phenolic resin, and spherical silica to have the mass ratios shown in Table 1 below, adhesive composition G was prepared in the same manner as in Example 1, and the adhesive composition G was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and this coating film was subjected to a solvent removal treatment at 130°C for 2 minutes. As a result, a die bond film (die bond film according to Example 7) having a thickness (average thickness) of 5 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 7 were measured in the same manner as in Example 1.

[0089] [Example 8] <Preparation of die bond film> Except for replacing the spherical silica with Nissan Chemical's trade name "MEK-AC-4130Y (30%)" (average particle size 50 nm), and preparing the acrylic resin A, phenolic resin, and spherical silica to have the mass ratios shown in Table 1 below, adhesive composition H was prepared in the same manner as in Example 1, and adhesive composition H was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and this coating film was subjected to a solvent removal treatment at 130°C for 2 minutes. As a result, a die bond film (die bond film according to Example 8) having a thickness (average thickness) of 5 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 8 were measured in the same manner as in Example 1.

[0090] [Example 9] <Preparation of die bond film> As the solution A1b, Admatechs' product name "YA050C" was dispersed in methyl ethyl ketone (MEK), surface-treated with phenylsilane, and a silica particle dispersion solution obtained by cutting coarse particles with a 1 μm filter was used (the average particle diameter of the spherical silica particles was 50 nm). Except for the fact that the acrylic resin A, phenolic resin, and spherical silica were prepared so as to have the mass ratios shown in Table 1 below, an adhesive composition I was prepared in the same manner as in Example 1, and the adhesive composition I was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a solvent removal treatment at 130 ° C. for 2 minutes. As a result, a die bond film (die bond film according to Example 9) having a thickness (average thickness) of 3 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 9 were measured in the same manner as in Example 1.

[0091] [Example 10] <Preparation of die bond film> Except for replacing the spherical silica with Nissan Chemical's trade name "MEK-ST-L (30 wt%)" (average particle size 50 nm), and preparing the acrylic resin A, phenolic resin, and spherical silica to have the mass ratios shown in Table 1 below, adhesive composition J was prepared in the same manner as in Example 1, and the adhesive composition J was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a solvent removal treatment at 130°C for 2 minutes. As a result, a die bond film (die bond film according to Example 10) having a thickness (average thickness) of 9 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 10 were measured in the same manner as in Example 1.

[0092] [Example 11] Instead of acrylic resin A, acrylic resin B (a copolymer of ethyl acrylate (EA), butyl acrylate (BA), acrylonitrile (AN) and glycidyl methacrylate (GMA) (mass average molecular weight: 800,000, glass transition temperature: Tg: 15°C) dissolved in methyl ethyl ketone (MEK)) was used, and Admatechs' product name "SO-C1" and Admatechs' product name "YC100C" were dispersed in methyl ethyl ketone (MEK) in a mass ratio of 2:3 as the solution A1b. The adhesive composition X was prepared in the same manner as in Example 1, except that the adhesive composition X was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a solvent removal treatment at 130° C. for 2 minutes. As a result, a die-bonding film (die-bonding film according to Example 11) having a thickness (average thickness) of 9 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 11 were measured in the same manner as in Example 1.

[0093] [Example 12] Instead of acrylic resin A, acrylic resin C (a copolymer of ethyl acrylate (EA), butyl acrylate (BA), acrylonitrile (AN) and glycidyl methacrylate (GMA) (mass average molecular weight: 600,000, glass transition temperature Tg: 15°C) dissolved in methyl ethyl ketone (MEK)) was used, and Admatechs' product name "SO-C1" and Admatechs' product name "YC100C" were dispersed in methyl ethyl ketone (MEK) in a mass ratio of 2:3 as the solution A1b. The adhesive composition Y was prepared in the same manner as in Example 1, except that the adhesive composition Y was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a solvent removal treatment at 130° C. for 2 minutes. As a result, a die-bonding film (die-bonding film according to Example 12) having a thickness (average thickness) of 7 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Example 12 were measured in the same manner as in Example 1.

[0094] [Comparative Example 1] <Preparation of die bond film> As the solution A1b, Admatechs' product name "SO-C1" and Admatechs' product name "YC100C" were dispersed in methyl ethyl ketone (MEK) at a mass ratio of 2:3, surface-treated with phenylsilane, and a silica particle dispersion solution obtained by cutting coarse particles with a 1 μm filter was used (average particle diameter of spherical silica particles is 180 nm). Except for the above, acrylic resin A, phenolic resin, and spherical silica were prepared to have the mass ratios shown in Table 1 below. The adhesive composition K was prepared in the same manner as in Example 1, and the adhesive composition K was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a desolvation treatment at 130 ° C. for 2 minutes. As a result, a die bond film (die bond film according to Comparative Example 1) having a thickness (average thickness) of 9.5 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Comparative Example 1 were measured in the same manner as in Example 1.

[0095] [Comparative Example 2] <Preparation of die bond film> Except for replacing the spherical silica with Nissan Chemical's trade name "MEK-EC-2130Y (30 wt%)" (average particle size 15 nm), and adding acrylic resin A, phenolic resin, and spherical silica to methyl ethyl ketone so as to obtain the mass ratio in Table 1 below, adhesive composition L was prepared in the same manner as in Example 1, and adhesive composition L was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and this coating film was subjected to a solvent removal treatment at 130°C for 2 minutes. As a result, a die bond film (die bond film according to Comparative Example 2) having a thickness (average thickness) of 3 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Comparative Example 2 were measured in the same manner as in Example 1.

[0096] [Comparative Example 3] <Preparation of die bond film> As the solution A1b, Admatechs' product name "SO-C1" and Admatechs' product name "YC100C" were dispersed in methyl ethyl ketone (MEK) at a mass ratio of 2:3, surface-treated with phenylsilane, and a silica particle dispersion solution obtained by cutting coarse particles with a 1 μm filter was used (average particle diameter of spherical silica particles is 180 nm). The acrylic resin A was replaced with Nagase Chemitex's product name "SG-70L", and the acrylic resin (SG-70L), phenolic resin, and spherical silica were prepared so as to have the mass ratio in Table 1 below. Except for this, an adhesive composition M was prepared in the same manner as in Example 1, and the adhesive composition M was applied to the silicone release-treated surface of the PET separator using an applicator to form a coating film, and the coating film was subjected to a desolvation treatment at 130 ° C. for 2 minutes. As a result, a die bond film (die bond film according to Comparative Example 3) having a thickness (average thickness) of 5 μm was produced on the PET separator. The average particle size of the spherical silica and the thickness of the die-bonding film according to Comparative Example 3 were measured in the same manner as in Example 1.

[0097] (Effect of post-mold cure (PMC) conditions on heat resistance) The die bond film according to each example was evaluated for the effect of the post mold cure conditions on the heat resistance. The effect of the post mold cure conditions on the heat resistance was evaluated according to the following procedure. (1) The die bond film according to each example is attached to a mirror chip having a planar dimension of 10 mm x 10 mm and a thickness of 50 μm at a temperature of 70 ° C., and then the PET separator is peeled off to prepare a mirror chip with a die bond film. Nine mirror chips with the die bond film are prepared for each example. (2) Nine mirror chips with die bond films according to each example are bonded to each section of a BGA (Ball Grid Array) substrate partitioned into 3 rows and 3 columns (partitioned into 9 sections) at a temperature of 120°C, a pressure of 0.1 MPa, and for 1 second. (3) The BGA substrate is post-mold cured by heating it in a dryer at 150° C. for a predetermined time (0 h, 2 h, 4 h, or 6 h). (4) Using a molding machine (manual press Y-1, manufactured by TOWA Press Co., Ltd.) and sealing resin, the BGA substrate is subjected to a sealing process under the conditions of a molding temperature of 175° C., a clamp pressure of 184 kN, a transfer pressure of 5 kN, and a time of 120 seconds. (5) After the sealing process, the sealing resin is subjected to a heat curing process at 175° C. for 5 hours. (6) For the nine mirror chips with die bond film bonded to the BGA substrate, an ultrasonic microscope (manufactured by HITACHI, model FS200II) is used to shape an electric signal with a constant frequency of 50 MHz into a pulse in reflection mode, convert the pulse electric signal into ultrasonic waves, and irradiate the BGA substrate to observe whether peeling occurs between the surface of the BGA substrate and the surface of the die bond film. If peeling occurs between the surface of the BGA substrate and the surface of the die bond film in even one of the nine mirror chips with die bond film, the heat resistance is deemed insufficient and evaluated as ×, and if peeling does not occur in all of them, the heat resistance is deemed sufficient and evaluated as ◯. The state in which peeling occurs between the surface of the BGA substrate and the surface of the die bond film is believed to be caused by the large number of voids that occur between the surface of the BGA substrate and the surface of the die bond film. The effects of post-mold cure conditions on heat resistance were evaluated, and the results are shown in Table 1 below.

[0098] (Effect of reflow temperature on heat resistance) The die bond film according to each example was evaluated for the effect of the reflow temperature on the heat resistance. The effect of the reflow temperature on the heat resistance was evaluated according to the following procedure. (1) For the die bond film according to each example, the procedures (1) to (5) for evaluating the influence of the post-mold cure conditions on the heat resistance are carried out. (2) The BGA substrate according to each example after the encapsulation resin is cured is exposed to a high temperature and high humidity environment (temperature 85°C, humidity 85% RH) for 168 hours. That is, the BGA substrate according to each example after the encapsulation resin is cured is exposed to an environment in which voids are more likely to occur between the surface of the BGA substrate and the surface of the die bond film. (3) After exposure to the high temperature and humidity environment, the BGA substrate of each example is treated in an IR reflow furnace at a temperature of 260° C. for 10 seconds. (4) For the nine mirror chips with die bond film bonded to the BGA substrate, an ultrasonic microscope (manufactured by HITACHI, model FS200II) is used to shape an electric signal with a constant frequency of 50 MHz into a pulse in reflection mode, convert the pulse electric signal into ultrasonic waves, and irradiate the BGA substrate to observe whether peeling occurs between the surface of the BGA substrate and the surface of the die bond film. If peeling occurs between the surface of the BGA substrate and the surface of the die bond film in even one of the nine mirror chips with die bond film, the heat resistance is evaluated as insufficient and evaluated as ×, and if peeling does not occur in all of them, the heat resistance is evaluated as sufficient and evaluated as ◯. The state in which peeling occurs between the surface of the BGA substrate and the surface of the die bond film is believed to be caused by the large number of voids that occur between the surface of the BGA substrate and the surface of the die bond film. The results of evaluating the effect of reflow temperature on heat resistance are shown in Table 1 below.

[0099] (parallel transmittance) For the die bond film according to each example, the parallel ray transmittance at a wavelength of 250 nm and the parallel ray transmittance at a wavelength of 1000 nm were measured using a spectrophotometer (manufactured by JASCO Corporation, product name "V-670"). The parallel ray transmittance was measured at a wavelength range of 190 nm to 1400 nm. Moreover, the measurement sample used was one in which the die bond film according to each example was laminated to a thickness of about 20 μm. The measurement results of the parallel ray transmittance at a wavelength of 250 nm and the parallel ray transmittance at a wavelength of 1000 nm, as well as the ratio of the parallel ray transmittance at a wavelength of 1000 nm to the parallel ray transmittance at a wavelength of 250 nm, are shown in Table 1 below.

[0100] (Water absorption rate) For the die bond film according to each example, the water absorption rate was measured by the Karl Fischer moisture evaporation-coulometric titration method (JIS K 0113:2005). Specifically, a 10 mg sample taken from the die-bonding film according to each example was measured for the amount of moisture generated by heating and vaporizing at 150°C for 3 minutes using a Karl Fischer moisture meter (manufactured by Mitsubishi Chemical Corporation, a moisture vaporizer VA-07 type connected to a trace moisture measuring device (coulometric titration type automatic moisture measuring device) CA-07 type and an automatic moisture measuring device KF-07 type), and the ratio to the sample mass before heating was calculated as the water absorption rate. Water absorption rate (mass%) = (water content measured by Karl Fischer / total mass of sample before measurement) x 100 The results of the water absorption measurements are shown in Table 1 below.

[0101] (Elasticity Modulus) For the die bond film according to each example, the tensile storage modulus at 150° C. was measured using a solid viscoelasticity measuring device (model RSA-G2, manufactured by Rheometric Scientific Co., Ltd.). Specifically, the die bond films according to each example were laminated to a thickness of 200 μm to obtain a laminate, and a rectangular test piece having a length of 50 mm (measurement length) x width of 10 mm was cut out from the laminate. The tensile storage modulus of the test piece was measured in the temperature range of 0 to 200°C using the solid viscoelasticity measuring device under the conditions of a frequency of 1 Hz, a strain amount of 0.1%, a heating rate of 10°C / min, and a chuck distance of 22.5 mm. At that time, the value at 150°C was read to determine the tensile storage modulus at 150°C. The measurement results of the tensile storage modulus at 150° C. are shown in Table 1 below.

[0102] [Table 1]

[0103] (Effect of post-mold cure (PMC) conditions on heat resistance) From Table 1, it can be seen that when no post-mold cure was performed (post-mold cure conditions were 150° C. and 0 hours), the results of evaluation using an ultrasonic microscope were ◯ in all examples. This is thought to be because the acrylic resin having a thermosetting functional group was not sufficiently crosslinked in the die bond film due to the lack of post-mold cure, and therefore sufficient free volume was secured in the die bond film. Furthermore, from Table 1, it can be seen that when the post-mold cure conditions were 150° C. for 2 hours, the results of evaluation using an ultrasonic microscope were such that only Comparative Example 2 was rated as "x", while all the other examples were rated as "good". The reason why the evaluation of Comparative Example 2 was negative was that the filler contained in the die bond film according to Comparative Example 2 had a specific surface area of ​​182 m 2 / g, which is extremely large, the acrylic resin is largely constrained by the filler, and in addition, crosslinking proceeds in the die bond film, so that it is considered that the cause is that a sufficient free volume cannot be secured in the die bond film. Furthermore, from Table 1, it can be seen that in Examples 1 to 11, even when the post-mold cure conditions were 150°C and 6 hours, the evaluation results using an ultrasonic microscope were all good (no problem with heat resistance), and in Example 12, when the post-mold cure conditions were 150°C and 4 hours, the evaluation result using an ultrasonic microscope was good (no problem with heat resistance), whereas in Comparative Examples 1 and 3, even when the post-mold cure conditions were 150°C and 4 hours, the evaluation result using an ultrasonic microscope was bad (problem with heat resistance), and in Comparative Example 2, in all cases where the post-mold cure conditions were 150°C and 2 hours or more, the evaluation result was bad (problem with heat resistance). (Effect of reflow temperature on heat resistance) From Table 1, it can be seen that when reflow was performed at 260° C. without post-mold curing, the evaluation results using an ultrasonic microscope were good in all cases. This is believed to be due to the same reason as described above. On the other hand, in Examples 1 to 11, even when post-mold cured at 150°C for 6 hours and then reflowed at 260°C, the evaluation results using an ultrasonic microscope were all good (no problem with heat resistance), and in Example 12, when post-mold cured at 150°C for 4 hours and then reflowed at 260°C, the evaluation result using an ultrasonic microscope was good (no problem with heat resistance). However, it can be seen that the evaluation results for Comparative Examples 1 to 3 using an ultrasonic microscope were all bad (problem with heat resistance) when post-mold cured at 150°C for 4 hours and then reflowed at 260°C. From the above results, it was found that the composition contains acrylic resin, phenolic resin, and filler, and the specific surface area of ​​the filler is 5 m 2 / g or more 100m 2 / g or less, and the mass ratio of the filler to the acrylic resin is greater than 0 and not more than 1.50, it can be seen that even when post-mold curing is performed for a relatively long time or reflow is performed at a temperature of 260°C, the die bond film is less likely to peel off from the printed wiring board, etc., and has high heat resistance, that is, it can be made so that voids are relatively less likely to remain between the die bond film and the surface of the printed wiring board, etc. In addition, one of the reasons why the evaluation result by ultrasonic microscope was ◯ under the conditions of 150°C x 0h in Table 1 is presumably that the spherical silica filler was not exposed from the surface of the die bond film (was not exposed on the surface). In this specification, surface exposure refers to a state in which, when a semiconductor chip with a bonding film is laminated onto a wiring board or the like by die attachment (die bonding), or when a laminated structure is produced from multiple bonding films and multiple semiconductor chips, the particle diameter of the coarse filler is larger than the thickness of the bonding film, and the surface of the coarse filler is exposed from the surface of the bonding film, resulting in the generation of voids. The voids thus generated can be confirmed by observation with an ultrasonic microscope. Furthermore, by checking the locations where voids have occurred by cross-sectional observation with an SEM, it is also possible to confirm the exposure of coarse fillers with particle sizes larger than the thickness of the film on the surface. [Explanation of symbols]

[0104] 1 Base material layer 2 Adhesive layer 3 Die bond layer 10 Dicing tape 20 Dicing die bond film G Backgrind Tape H Holder J suction jig P pin material R Dicing Ring T Wafer Processing Tape U Push-up member W Semiconductor wafer

Claims

1. A die bond film containing an acrylic resin, a phenolic resin, and a filler, The filler has a specific surface area of ​​5 m ２ / g or more 100m ２ / g or less, a mass ratio of the filler to the acrylic resin is greater than 0 and less than or equal to 1.50; The ratio of the parallel ray transmittance at a wavelength of 1000 nm to the parallel ray transmittance at a wavelength of 250 nm is 2100 or more and 4500 or less. Die bond film.

2. The water absorption rate is 0.22% by mass or less. The die-bonding film according to claim 1 .

3. The ratio of the thickness of the die bond film to the average particle diameter of the filler is 5 or more and 150 or less. The die-bonding film according to claim 1 or 2.

4. a dicing tape having a pressure-sensitive adhesive layer laminated on a base layer; a die bond layer laminated on the pressure-sensitive adhesive layer of the dicing tape; The die-bonding layer is the die-bonding film according to any one of claims 1 to 3. Dicing die bond film.