Propylene-ethylene copolymer composition suitable for hot-fill packaging of food products

Abstract

To provide propylene-ethylene copolymer compositions that are particularly advantageous for use in hot filling packaging of foodstuffs, and methods for producing hot filling packaging containers.SOLUTION: Propylene-ethylene copolymers can be produced using a Ziegler-Natta catalyst and an alkoxysilane electron donor. The compositions can have propylene as a primary monomer with an ethylene content ranging from 2.0 to 6.0 wt.% with a xylene soluble content of less than 7.0 wt.%.SELECTED DRAWING: Figure 1

Description

[Technical Field]

[0001] (Related Applications) This application is based on and claims priority to U.S. Provisional Patent Application No. 62 / 683,113, filed June 11, 2018, which is incorporated herein by reference.

[0002] FIELD OF THE INVENTION FIELD OF THE DISCLOSURE The present disclosure relates to propylene-ethylene copolymer compositions and methods of making. The compositions of the disclosure are particularly well suited for hot fill packaging of food products. [Background technology]

[0003] Hot fill packaging is a method applied in both the food and beverage industries and is commonly used to package products including beverages, dips, and soups. Hot fill packaging is often used as part of a pasteurization process for products designed to have an extended shelf life lasting up to one year. Hot fill packaging faces various challenges because polymers tend to lose their packaging properties, including stiffness and strength, at high temperatures.

[0004] Because hot fill packaging comes into contact with products intended for human consumption, there are concerns that the properties of the hot fill packaging may deteriorate. For example, heating a polymer composition during the hot fill packaging process may result in unwanted degradation of the polymer or other components in the composition.

[0005] To date, polypropylene homopolymers with higher melting points have been used in hot-fill packaging applications to prevent distortion. However, polypropylene homopolymers have poor transparency properties. To improve transparency, polypropylene random copolymers have been proposed. However, polypropylene random copolymers do not have the heat resistance of polypropylene homopolymers, and furthermore, they cannot provide transparency over long periods of time.

[0006] In view of the above, there is currently a need for polymer compositions for producing hot fill packaging that not only have improved stiffness and heat resistance, but also have excellent clarity. Summary of the Invention

[0007] In general, the present disclosure is directed to propylene copolymers that have been found to have an excellent balance of properties. The polymers are particularly well suited for use in producing hot-fill packaging. In particular, the copolymers of the present disclosure have high stiffness, making them well suited for producing injection-molded articles. In addition, the polymer compositions of the present disclosure have very little extractables, exhibit blooming over time, and can be constructed to have higher heat deflection temperatures. In addition, the polymer compositions can also exhibit excellent haze properties. Of particular advantage, it has been found that the polymer compositions of the present disclosure can also maintain high haze properties even after thermal aging. In this regard, the polymer compositions of the present disclosure are well suited for producing a variety of different types of containers, particularly hot-fill packaging containers that may be subjected to numerous thermal cycles. According to the present disclosure, the containers not only have excellent physical properties but also long-lasting transparency properties.

[0008] In addition to hot fill packaging containers, the polymer compositions of the present disclosure can be used to produce a variety of other molded articles. For example, the polymer composition is well suited for producing a storage container. Such a storage container can be used to store goods in locations without air conditioning, such as attics, garages, warehouses, and other storage areas. The storage container can include a base defining a hollow interior space. The base can be made entirely from the polymer composition and can have excellent transparency properties. The container can also include a lid that cooperates with the base to form a seal.

[0009] The present disclosure includes a propylene-ethylene copolymer composition and a method for producing the propylene-ethylene copolymer composition. The composition can be a random copolymer particularly well suited for hot-fill packaging of food products. The copolymer composition can be produced using a Ziegler-Natta catalyst and an alkoxysilane electron donor. The composition can have propylene as the primary monomer with an ethylene content ranging from 2.0 to 5.0 weight percent. The composition can have a melt flow rate greater than 1 g / 10 min, such as greater than 10 g / 10 min, and a xylene solubles content less than 7.0 weight percent. In one embodiment, the composition has a ratio of xylene solubles weight percent to ethylene content weight percent of about 1.5 or less, such as less than about 1.4, such as less than about 1.3, such as less than about 1.2, such as less than about 1.1, or even 1 or less. Other features and aspects of the present disclosure are discussed in more detail below. [Brief explanation of the drawings]

[0010] A full and enabling disclosure of the present invention, including the best mode thereof, to one skilled in the art, is set forth more particularly in remaining portions of the specification, including reference to the accompanying drawings, in which:

[0011] [Figure 1] 1 is a graph of weight percent xylene soluble (XS) versus weight percent ethylene content (ethylene, ET) of propylene-ethylene copolymer samples according to the present disclosure. DETAILED DESCRIPTION OF THE INVENTION

[0012] The present disclosure includes a propylene-ethylene copolymer composition and a method for producing the propylene-ethylene copolymer composition. The composition can include a propylene-ethylene random copolymer. The propylene-ethylene copolymer composition can be particularly well suited for hot-fill packaging of food products. Specifically, the propylene-ethylene copolymer composition of the present disclosure can be used to form rigid hot-fill containers and films for packaging and sealing food and beverages. The composition of the present disclosure can be particularly beneficial for use with foods that must be pasteurized during packaging.

[0013] Advantages of the various propylene-ethylene copolymer compositions of the present disclosure include increased rigidity for use in containers. The compositions can also have reduced blooming and reduced haze, even under high temperature conditions and for long periods of time. The compositions of the present disclosure can have reduced extractable and xylene soluble content, making the polymer compositions safe for consumer use and more easily compliant with U.S. Food and Drug Administration (FDA) regulations. The propylene-ethylene copolymer compositions of the present disclosure can also be used in packaging designed for microwave reheating of stored foods.

[0014] A first embodiment of the present disclosure includes a propylene-ethylene random copolymer composition. The copolymer composition can be produced using a Ziegler-Natta catalyst and an alkoxysilane electron donor. The composition can have propylene as a primary monomer with an ethylene content ranging from 2.0 to 6.0 weight percent. The composition has a melt flow rate of 1 to 100 g / 10 min and an xylene content of less than 7.0 weight percent. The composition may have a soluble content. I. Definitions and Test Procedures

[0015] As used herein, the term "propylene-ethylene copolymer" refers to a copolymer containing a majority weight percent of propylene monomer with ethylene monomer as a secondary constituent. A "propylene-ethylene copolymer" (sometimes referred to as polypropylene random copolymer, PPR, PP-R, RCP, or RACO) is a polymer with individual repeat units of ethylene monomer present in a random or statistical distribution within the polymer chain.

[0016] As used herein, melt flow rate (MFR) is measured according to ASTM D 1238 test method using a 2.16 kg weight of propyne-based polymer at 230°C. The melt flow rate can be measured in pellet form or on reactor powder. When measuring reactor powder, a stabilization package can be added containing 2000 ppm CYANOX 2246 antioxidant (methylene bis(4-methyl-6-tert-butylphenol), 2000 ppm IRGAFOS 168 antioxidant (tris(2,4-di-tert-butylphenyl) phosphite), and 1000 ppm ZnO scavenger.

[0017] Xylene solubles (XS) are defined as the weight percent of resin remaining in solution after dissolving a sample of polypropylene random copolymer resin in hot xylene and allowing the solution to cool to 25°C. This is also referred to as the gravimetric XS method according to ASTM D5492-98, which uses a 90 minute settling time, and is also referred to herein as the "wet method." Xylene solubles are measured on the reactor powder without the addition of any other additives.

[0018] The xylene soluble fraction was determined by a method adapted from ASTM D5492-06 and is sometimes referred to herein as the "wet method." The procedure consisted of weighing 2 g of sample and dissolving it in 200 mL of o-xylene in a 400 mL flask equipped with a 24 / 40 joint. The flask was connected to a water-cooled condenser, and the contents were stirred and heated to reflux under nitrogen (N2), then maintained at reflux for an additional 30 minutes. The solution was then cooled to 25°C in a temperature-controlled water bath for 90 minutes to crystallize the xylene-insoluble fraction. Once the solution had cooled and the insoluble fraction had precipitated from the solution, separation of the xylene-soluble fraction (XS) from the xylene-insoluble fraction (XI) was achieved by filtration through 25-micron filter paper. 100 mL of the filtrate was collected in a pre-weighed aluminum pan, and the o-xylene was evaporated from the 100 mL filtrate under a stream of nitrogen. Once the solvent has evaporated, place the pan and contents in a vacuum oven at 100°C for 30 minutes or until dry. The pan is then allowed to cool to room temperature and weighed. The xylene soluble portion is calculated as XS (wt%) = [(m3 - m2) * 2 / m1] * 100, where m1 is the initial weight of the sample used, m2 is the weight of the empty aluminum pan, and m3 is the weight of the pan and residue (asterisk, * , here and elsewhere in this disclosure indicate that the identified term or value is multiplied).

[0019] The term "tacticity" generally refers to the relative stereochemistry of adjacent chiral centers within a macromolecule or polymer. For example, in a propylene-based polymer, the chirality of adjacent monomers, such as two propylene monomers, can be of either like or opposite configuration. The term "dyad" is used to refer to two consecutive monomers, and three adjacent monomers are called a "triad." If the chirality of adjacent monomers is of the same relative configuration, the dyad is considered to be isotactic; if of opposite configuration, it is called syndiotactic. Another way of describing the configuration relationship is to call consecutive pairs of monomers with the same chirality meso (m) and those of opposite configuration racemic (r). ) is what is called.

[0020] The stereoregularity or stereochemistry of polymers in general, and of polypropylene or polypropylene random copolymers in particular, can be described or quantified by reference to triad concentration. An isotactic triad, typically identified by the abbreviated notation "mm," consists of two adjacent mesodiads with the same configuration; thus, the triad's stereoregularity is identified as "mm." If two adjacent monomers in a three-monomer sequence have the same chirality but differ from the relative configuration of the third unit, the triad has an "mr" stereoregularity. An "rr" triad has a middle monomer unit with an opposite configuration to either neighbor. The fraction of each type of triad in a polymer can be determined, and when multiplied by 100, indicates the percentage of that type found in the polymer. Herein, mm percentages are used to identify and characterize polymers.

[0021] The sequence distribution of the monomers in the polymer is 13 The carbon number can be determined by C-NMR, which also allows the positioning of the ethylene residue relative to the adjacent propylene residue. 13 C NMR can be used to measure ethylene content, Koenig B value, triad distribution, and triad assembly regularity, and is performed as follows.

[0022] Samples are prepared by adding approximately 2.7 g of a 50 / 50 mixture of tetrachloroethane-d2 / orthodichlorobenzene containing 0.025 M Cr(AcAc)3 to 0.20 g of sample in a Norell 1001-7 10 mm NMR tube. The sample is heated to 150°C using a heat block and heat gun to dissolve and homogenize the tube and its contents. Each sample is visually inspected to ensure homogeneity.

[0023] Data are collected using a Bruker 400 MHz spectrometer equipped with a Bruker Dual DUL high-temperature CryoProbe. The data are acquired using 320 transients per data file, a 6-second pulse repetition delay, a 90-degree flip angle, and inverse-gated decoupling at a sample temperature of 120°C. All measurements are performed on non-spinning samples in locked mode. Samples are allowed to thermally equilibrate for 7 minutes before data acquisition. The percent mm tacticity and wt% of ethylene are calculated according to methods commonly used in the art and are briefly summarized as follows:

[0024] For measuring the chemical shift of the resonance, the methyl group of the third unit in five consecutive propylene units consisting of head-to-tail bonds and having the same relative chirality is set to 21.83 ppm. The chemical shifts of the other carbon resonances are measured using the above values ​​as the reference. The spectrum for the methyl carbon region (17.0-23 ppm) can be divided into the first region (21.1-21.9 ppm), the second region (20.4-21.0 ppm), the third region (19.5-20.4 ppm), and the fourth region (17.0-17.5 ppm). Each peak in the spectrum is assigned with reference to literature sources such as T. Tsutsui et al., Polymer, Vol. 30, Issue 7 (1989) 1350-1356, and / or H.N. Cheng, Macromolecules, 17 (1984) 1950-1955, the contents of which are incorporated herein by reference.

[0025] The first region is occupied by the signal of the central methyl group in the PPP(mm) triad. The second region is occupied by the signal of the central methyl group in the PPP(mr) triad and the methyl group of the propylene unit (PPE-methyl group) whose adjacent units are propylene and ethylene units. The third region is occupied by the signal of the central methyl group in the PPP(rr) triad and the propylene unit (EPE-methyl group) whose adjacent units are ethylene units. The methyl group signal resonates.

[0026] PPP(mm), PPP(mr), and PPP(rr) each have the following three propylene unit chain structure with head-to-tail bonds, as shown in the Fischer projection below. [ka]

[0027] The three-assembly regularity (mm fraction) of the propylene random copolymer was calculated using the following formula: 13 It can be determined from the C-NMR spectrum.

number

[0028] The peak areas used in the above calculations are 13 The intensities of the mr and rr triads cannot be measured directly from the triplet region of the C-NMR spectrum. The areas due to the EPP and EPE sequences must be subtracted from them, respectively. The EPP area can be determined from the signal at 30.8 ppm after subtracting half the total area of ​​the signals from 26 to 27.2 ppm and the signal at 30.1 ppm. The area due to EPE can be determined from the signal at 33.2 ppm.

[0029] For convenience, the ethylene content can also be measured using the method described above. 13Measured using Fourier Transform Infrared method (FTIR), which correlates with ethylene values ​​determined using C NMR. Measurements performed using two methods The relationship and agreement between these two is described, for example, in J.R. Padson and J.C. Sandall, "Quantitative Measurement of Ethylene Incorporation into Propylene Copolymers by Carbon-13 Nuclear Magnetic Resonance and Infrared Spectroscopy," Analytical Chemistry, Vol. 50, No. 13, November 1978, pp. 1777-1780.

[0030] The "Koenig B value" or "B value" or chi statistic is a measure of randomness or blockiness in a propylene-ethylene random copolymer. A Koenig B value of 1.0 indicates a random copolymer, while a value of zero indicates a perfect block of monomers A and B, in this disclosure, propylene and ethylene. A Koenig B value of 2 indicates a perfect alternating copolymer (i.e., a polymer defined by the structure ABABAB). The Koenig B value can be calculated as B = [EP] / (2[P][E]), where [EP] is the total mole fraction of EP dimers (EP + PE or (EEP + PPE + PEP + EPE)), [E] is the mole fraction of ethylene, and [P] = 1 - [E]. For details on determining and calculating Koenig B values, see Koenig, Jack L., Spectroscopy of Polymers, 2nd Edition.

[0031] The Gardner impact test is measured according to ASTM Test No. D5420.

[0032] IZOD impact strength is measured according to ASTM Test No. D256 on specimens molded according to ASTM Test D4101.

[0033] Flexural modulus is determined according to ASTM D790-10 Method A at 1.3 mm / min using Type 1 specimens according to ASTM 3641 and molded according to ASTM Test D4101. II. Propylene-ethylene random copolymer composition

[0034] The propylene-ethylene copolymer compositions of the present disclosure can comprise a majority weight percent of propylene monomer with ethylene monomer as a minor component. The ethylene content (ET) of the propylene-ethylene copolymer compositions of the present disclosure can be from about 2.0 up to about 5.0 weight percent of the copolymer, preferably from about 2.5 to about 5.0 weight percent, and more preferably from about 3.0 to about 5.0 weight percent.

[0035] The xylene soluble (XS) fraction of the (wet-laid) copolymer of the present invention may be 7.0 wt% or less, or ≦6.0 wt%, more preferably ≦5.0 wt%, even more preferably ≦4 wt%, e.g., ≦6.5 wt%, ≦5.5 wt%, ≦4.5 wt%, or ≦3.5 wt% of the copolymer. The xylene soluble (XS) fraction is preferably 2.0% to 7.0 wt%, 2.5% to 6.5 wt%, and more preferably 3.0% to 6.0 wt%. The MFR of the copolymer of the present disclosure may be in the range of 10 to 100 g / 10 min, more preferably 10 to 50 g / 10 min.

[0036] The weight ratio of xylene solubles (XS) to ethylene content (ET) is an important aspect of embodiments of the present disclosure and can be referred to as the xylene solubles to ethylene ratio, or XS / ET ratio. The XS / ET ratio of the propylene-ethylene copolymer compositions of the present disclosure can be less than or equal to 1.5, or less than 1.4, more preferably less than 1.2, even more preferably less than 1.0, e.g., less than 1.8, less than 1.4, less than 1.1, or less than 0.95. The XS / ET ratio can also be in the range of 0.5 to 1.51, 1.0 to 1.5, 1.1 to 1.4, or more preferably 1.15 to 1.35.

[0037] As shown in Figure 1, the xylene solubles weight percent (XS) and ethylene weight percent (ET) of the copolymer compositions of the present disclosure can be described by their location on a scatter plot of xylene solubles weight percent (XS) versus ethylene weight percent (ET). For example, the xylene solubles weight percent (XS) and ethylene weight percent (ET) of embodiments of the present disclosure can be calculated using the formula XS = 2.0e 0.297(ET) For example, the line XS=1.9e 0.297(ET) For example, the line XS=1.8e 0.297(ET) The weight percent xylene solubles (XS) and weight percent ethylene (ET) of embodiments of the present disclosure can also be calculated using the formula XS =1.1e 0.297(ET) For example, the line XS=1.3e 0.297(ET) For example, the line XS=1.4e 0.297(ET) For example, line XS=1.5e 0.297(ET) and for example, line XS=1.6e 0.297(ET) It can exceed.

[0038] In one embodiment, the polymer composition may contain a nucleating agent. For example, the nucleating agent may be an α-nucleating agent. Examples of nucleating agents and / or clarifying agents that can be used in the polymer composition include benzeneamide derivatives, sorbitol derivatives, nonitol derivatives, and mixtures thereof. Specific examples of nucleating agents include NA-11 nucleating agents sold by Adeka Palmarole SAS, such as sodium 2,2'-methylene-bis-(4,6-di-tert-butylphenyl)phosphate. Other nucleating agents that can be used include HPN nucleating agents sold by Milliken and Company of Spartanburg, South Carolina, including HPN-600ei. Other suitable clarifying agents from Milliken include Millad NX8000 and Millad 3988i.

[0039] The copolymers of the present disclosure generally have a relatively broad molecular weight distribution. For example, the molecular weight distribution (Mw / Mn) is generally greater than about 3.5, such as greater than about 3.8, for example greater than about 4, for example greater than about 4.3, for example greater than about 4.5, for example greater than about 4.8, for example greater than about 5, for example greater than about 5.2, for example greater than about 5.5, for example greater than about 5.7, for example greater than about 6, and generally less than about 10, for example less than about 8, for example less than about 7.5. The weight average molecular weight is determined by GPC. III. Formation of Propylene-Ethylene Random Copolymer

[0040] Embodiments of the present invention can be made by any method known in the art for polymerizing propylene-based polymers. This includes the UNIPOL® gas-phase process, which uses a supported Ziegler-Natta catalyst. Particularly preferred is the CONSISTA® catalyst available from W.R. Grace & Co., Columbia, Maryland. Suitable polypropylene random copolymers can be produced using a single reactor or multiple reactors to produce a multimodal product. For some embodiments, it is preferred to use a phthalate-free internal electron donor.

[0041] Processes and catalyst compositions for preparing useful PP-R copolymers are disclosed, for example, in WO 2011 / 084628, and others are generally described in U.S. Patent Nos. 7,381,779, 7,491,670, 7,678,868, 7,781,363, and 7,989,383. Propylene-ethylene random copolymers with high molecular weights and low MFRs have been produced using stereospecific catalysts, sometimes referred to as "sixth generation" Ziegler-Natta catalysts containing non-phthalate internal donors, as disclosed in U.S. Patent Nos. 8,288,585, 8,536,372, 8,778,826, U.S. Patent Application Publication No. 2013 / 0338321, and / or WO 2010 / 078494, among others. Also suitable are so-called "fourth generation" Ziegler-Natta catalysts, which typically contain an internal phthalate donor (e.g., diisobutyl phthalate (DIBP)). Each of the above-listed patents is incorporated herein by reference.

[0042] Suitable procatalyst compositions for use in producing random polypropylene (PP-R) copolymers include Ziegler-Natta procatalyst compositions. Any conventional Ziegler-Natta procatalyst, as generally known in the art, may be used in the present catalyst composition, provided that it is suitable for use in the production of the claimed PP-R copolymers. In one embodiment, the Ziegler-Natta procatalyst composition contains a titanium moiety, such as titanium chloride, a magnesium moiety, such as magnesium chloride, and an internal electron donor.

[0043] In one embodiment, the internal electron donor comprises a substituted phenylene aromatic diester. In one embodiment, a 1,2-phenylene aromatic diester is provided. The substituted 1,2-phenylene aromatic diester has the following structure (I): [ka]

[0044] In the formula, R1~R 14 are the same or different. 14 Each of R1 to R2 is selected from hydrogen, substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, heteroatoms, and combinations thereof. 14 At least one of the is not hydrogen.

[0045] As used herein, the terms "hydrocarbyl" and "hydrocarbon" refer to substituents containing only hydrogen and carbon atoms, including branched or unbranched, saturated or unsaturated, cyclic, polycyclic, fused, or acyclic species, and combinations thereof. Non-limiting examples of hydrocarbyl groups include alkyl, cycloalkyl, alkenyl, alkadienyl, cycloalkenyl, cycloalkadienyl, aryl, aralkyl, alkylaryl, and alkynyl groups.

[0046] As used herein, the terms "substituted hydrocarbyl" and "substituted hydrocarbon" refer to a hydrocarbyl group substituted with one or more non-hydrocarbyl substituents. A non-limiting example of a non-hydrocarbyl substituent is a heteroatom. As used herein, "heteroatom" refers to an atom other than carbon or hydrogen. A heteroatom can be a non-carbon atom belonging to Groups IV, V, VI, and VII of the periodic table. Non-limiting examples of heteroatoms include halogens (F, Cl, Br, I), N, O, P, B, S, and Si. Substituted hydrocarbyl groups also include halohydrocarbyl groups and silicon-containing hydrocarbyl groups. As used herein, the term "halohydrocarbyl" group refers to a hydrocarbyl group substituted with one or more halogen atoms. As used herein, the term "silicon-containing hydrocarbyl group" refers to a hydrocarbyl group substituted with one or more silicon atoms. The silicon atom(s) may or may not be in the carbon chain.

[0047] The procatalyst precursor comprises: (i) magnesium; (ii) a metal from Groups IV to VIII of the periodic table; (iii) halides, oxyhalides, and / or alkoxides of (i) and / or (ii), and (iv) combinations of (i), (ii), and (iii). Non-limiting examples of suitable procatalyst precursors include halides, oxyhalides, and alkoxides of magnesium, manganese, titanium, vanadium, chromium, molybdenum, zirconium, hafnium, and combinations thereof.

[0048] In one embodiment, the procatalyst precursor is a magnesium moiety compound (MagMo), a mixed magnesium titanium compound (MagTi), or a benzoate-containing magnesium chloride compound (BenMag). is a magnesium moiety ("MagMo") precursor. A "MagMo precursor" contains magnesium as the only metal component. A MagMo precursor comprises a magnesium moiety. Non-limiting examples of suitable magnesium moieties include anhydrous magnesium chloride and / or its alcohol adducts, magnesium alkoxides or aryloxides, mixed magnesium alkoxyhalides, and / or carboxylated magnesium dialkoxides or aryloxides. In embodiments, the MagMo precursor is a di(C 1~4 ) alkoxide. In a further embodiment, the MagMo precursor is diethoxymagnesium.

[0049] In an embodiment, the procatalyst precursor is a mixed magnesium / titanium compound (“MagTi”). A “MagTi precursor” is a compound of the formula Mg d Ti(OR e ) f X g wherein R eis an aliphatic or aromatic hydrocarbon radical having 1 to 14 carbon atoms or COR', where R' is an aliphatic or aromatic hydrocarbon radical having 1 to 14 carbon atoms, and each OR e The groups may be the same or different, X is independently chlorine, bromine, or iodine, preferably chlorine, d is 0.5 to 56, or 2 to 4, f is 2 to 116, or 5 to 15, and g is 0.5 to 116, or 1 to 3. The precursors are prepared by controlled precipitation through the removal of alcohol from the reaction mixture used in their preparation. In one embodiment, the reaction medium comprises a mixture of an aromatic liquid, particularly a chlorinated aromatic compound, especially chlorobenzene, with an alkanol, especially ethanol. Suitable halogenating agents include titanium tetrabromide, titanium tetrachloride, or titanium trichloride, especially titanium tetrachloride. Removal of the alkanol from the solution used in the halogenation results in the precipitation of a solid precursor having a particularly desirable morphology and surface area. Furthermore, the resulting precursor has a particularly uniform particle size.

[0050] The procatalyst composition can also include an internal electron donor. As used herein, an "internal electron donor" is a compound added during the formation of the procatalyst composition that donates a pair of electrons to one or more metals present in the resulting procatalyst composition. Without being bound by any particular theory, it is believed that the internal electron donor helps regulate the formation of active sites, thus enhancing catalytic stereoselectivity. In one embodiment, the internal electron donor comprises a substituted phenylene aromatic diester of structure (I) identified above.

[0051] In one embodiment, a procatalyst composition is provided that includes a combination of a magnesium moiety, a titanium moiety, and an internal electron donor. The internal electron donor includes a substituted phenylene aromatic diester. The procatalyst composition is produced by a halogenation procedure, detailed in U.S. Pat. No. 8,536,372, incorporated herein by reference, which converts a procatalyst precursor and a substituted phenylene aromatic diester donor into a combination of magnesium and titanium moieties into which the internal electron donor is incorporated. The procatalyst precursor from which the procatalyst composition is formed includes a magnesium moiety precursor, a mixed magnesium / titanium precursor, and a or a benzoate-containing magnesium chloride precursor.

[0052] In one embodiment, the magnesium moiety is a magnesium halide. In another embodiment, the magnesium halide is magnesium chloride or a magnesium chloride alcohol adduct. In one embodiment, the titanium moiety is a titanium halide, such as titanium chloride. In another embodiment, the titanium moiety is titanium tetrachloride. In another embodiment, the procatalyst composition comprises a magnesium chloride support onto which titanium chloride is deposited, at which point an internal electron donor is incorporated.

[0053] In one embodiment, the internal electron donor of the procatalyst composition comprises a substituted phenylene aromatic diester of structure (I) shown above, where R-R 14 are the same or different, and R1 to R 14 each of R to R is selected from hydrogen, substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, heteroatoms, and combinations thereof; 14 At least one of the is not hydrogen.

[0054] In embodiments, at least one (or two, or three, or four) R group(s) of R1 through R4 is selected from substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, heteroatoms, and combinations thereof.

[0055] In the embodiment, R to R 14 In another embodiment, at least one (or some or all) of the R groups is selected from the group consisting of substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, heteroatoms, and combinations thereof. 10 ~R 14 At least one of is selected from substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, heteroatoms, and combinations thereof.

[0056] In the embodiment, at least one of R1 to R4 and R5 to R 14 At least one of R1 through R4, at least one of R5 through R9, and R6 is selected from substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, heteroatoms, and combinations thereof. In another embodiment, at least one of R1 through R4, at least one of R5 through R9, and R 10 ~R 14 At least one of which is selected from substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, heteroatoms, and combinations thereof.

[0057] In embodiments, any consecutive R groups from R1 to R4, and / or any consecutive R groups from R5 to R9, and / or R 10 ~R 14Any consecutive R groups may be linked to form a cyclic or intracyclic structure. The cyclic / intercyclic structure may or may not be aromatic. In one embodiment, the cyclic / intercyclic structure is a C5 or C6 membered ring.

[0058] In embodiments, at least one of R1 through R4 is a hydrocarbyl group having 1 to 20 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, and combinations thereof. 14 At least one of R1 to R4, and / or R5 to R9, and / or R 10 ~R 14 may be linked to form cyclic or intracyclic structures. The cyclic and / or intracyclic structures may be aromatic. , or may not be aromatic.

[0059] In an embodiment, R1 to R4, and / or R5 to R9, and / or R 10 ~R 14 Any successive R groups may be members of a C5-C6 membered ring.

[0060] In one embodiment, structure (I) includes R1, R3, and R4 as hydrogen. R2 is selected from substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, and combinations thereof. R5 to R 14 are the same or different, and R5 to R 14 Each of is selected from hydrogen, substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, halogen, and combinations thereof.

[0061] In one embodiment, R2 is selected from a C1-C8 alkyl group, a C3-C6 cycloalkyl group, or a substituted C3-C6 cycloalkyl group. R2 can be a methyl group, an ethyl group, an n-propyl group, an isopropyl group, a t-butyl group, an isobutyl group, a sec-butyl group, a 2,4,4-trimethylpentan-2-yl group, a cyclopentyl group, and a cyclohexyl group.

[0062] In one embodiment, structure (I) includes R2 that is methyl, and R5 through R 14 is hydrogen. In one embodiment, structure (I) includes R2 that is ethyl, and R5 through R 14 is hydrogen. In one embodiment, structure (I) includes R2 that is t-butyl, and R5 through R 14 is hydrogen. In one embodiment, structure (I) includes R2 that is ethoxycarbonyl, and R5 through R 14 Each of is hydrogen.

[0063] In one embodiment, structure (I) includes R2, R3, and R4 each as hydrogen, and R1 is selected from substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, and combinations thereof. 14 are the same or different and each is selected from hydrogen, substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, halogen, and combinations thereof.

[0064] In one embodiment, structure (I) includes R1 which is methyl, and R5 through R 14 Each of is hydrogen.

[0065] In one embodiment, structure (I) includes R2 and R4 that are hydrogen, and R1 and R3 are the same or different. Each of R1 and R3 is selected from substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, and combinations thereof. R5 to R 14are the same or different, and R5 to R 14 Each of is selected from substituted hydrocarbyl groups having 1 to 20 carbon atoms, unsubstituted hydrocarbyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms, halogens, and combinations thereof.

[0066] In one embodiment, structure (I) comprises R1 and R3, which may be the same or different. Each of R1 and R3 is selected from a C1-C8 alkyl group, a C3-C6 cycloalkyl group, or a substituted C3-C6 cycloalkyl group. R5-R 14 are the same or different, and R5 to R 14 are each selected from hydrogen, a C1-C8 alkyl group, and halogen. Non-limiting examples of suitable C1-C8 alkyl groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, i-butyl, t-butyl, n-pentyl, i-pentyl, neopentyl, t-pentyl, n-hexyl, and 2,4,4-trimethylpentan-2-yl groups. Non-limiting examples of suitable C3-C6 cycloalkyl groups include cyclopentyl, In a further embodiment, R to R 14 At least one of them is a C1 to C8 alkyl group or a halogen.

[0067] In one embodiment, structure (I) comprises R1, which is a methyl group, and R3, which is a t-butyl group. 14 Each of is hydrogen.

[0068] In one embodiment, structure (I) includes R1 and R3 that are isopropyl groups. R2, R4 and R5 through R 14 Each of is hydrogen.

[0069] In one embodiment, structure (I) comprises R, R, and R as methyl groups. 10 and R3 is a t-butyl group. 11 ~R 14 Each of is hydrogen.

[0070] In one embodiment, structure (I) comprises R, R, and R as methyl groups. 12 and R3 is a t-butyl group. 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0071] In one embodiment, structure (I) includes R1 as a methyl group and R3 is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0072] In one embodiment, structure (I) is a methyl group having R, R, R, R, R 10 , R 12 , and R 14 and R3 is a t-butyl group. 11 and R 13 Each of is hydrogen.

[0073] In one embodiment, structure (I) includes R1 as a methyl group and R3 is a t-butyl group. 10 , R 12 and R 14 Each of R2, R4, R6, R8, R 11 and R 13 Each of is hydrogen.

[0074] In one embodiment, the substituted phenylene aromatic diester is a diester of R-R, as described in detail in U.S. Pat. No. 8,536,372, which is incorporated herein by reference. 14 has a structure selected from the group consisting of structures (II) to (V), including alternatives:

[0075] In one embodiment, structure (I) includes R1 that is a methyl group and R3 that is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0076] In one embodiment, structure (I) includes R1 that is a methyl group and R3 that is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0077] In one embodiment, structure (I) includes R1 that is a methyl group and R3 that is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0078] In one embodiment, structure (I) includes R1 that is a methyl group and R3 that is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0079] In one embodiment, structure (I) includes R1 being a methyl group and R3 being a t-butyl group. R7 and R 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0080] In one embodiment, structure (I) includes R1 being a methyl group and R3 being a t-butyl group. 11 and R 12 Each of R2, R4, R5, R8, R9, R 10 , R 13 , and R 14 Each of is hydrogen.

[0081] In one embodiment, structure (I) includes R1 being a methyl group and R3 being a t-butyl group. 11 and R 13 Each of R2, R4, R5, R7, R9, R 10 , R 12 , and R 14 Each of is hydrogen.

[0082] In one embodiment, structure (I) includes R1 which is a methyl group, and R3 is a t-butyl group. 14 Each of is a fluorine atom.

[0083] In one embodiment, structure (I) includes R1 that is a methyl group and R3 that is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0084] In one embodiment, structure (I) includes R1 that is a methyl group and R3 that is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0085] In an embodiment, R1 is a methyl group and R3 is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0086] In one embodiment, structure (I) includes R1 that is a methyl group and R3 that is a t-butyl group. 12 Each of R2, R4, R5, R6, R8, R9, R 10 , R 11 , R 13 , and R 14 Each of is hydrogen.

[0087] In one embodiment, structure (I) includes R1 which is a methyl group, and R3 is a 2,4,4-trimethylpentan-2-yl group. 14 Each of is hydrogen.

[0088] In one embodiment, structure (I) includes R1 and R3, each of which is a sec-butyl group. 14 Each of is hydrogen.

[0089] In one embodiment, structure (I) includes R1 and R4, each of which is a methyl group. R2, R3, R5-R9, and R 10 ~R 14 Each of is hydrogen.

[0090] In one embodiment, structure (I) includes R1, which is a methyl group. R4 is an i-propyl group. R2, R3, R5-R9, and R 10 ~R 14 Each of is hydrogen.

[0091] In one embodiment, structure (I) includes R1, R3, and R4, each of which is an i-propyl group. R2, R5-R9, and R 10 ~R 14Each of is hydrogen.

[0092] In one embodiment, another procatalyst composition is provided. The procatalyst composition includes a combination of a magnesium moiety, a titanium moiety, and a mixed internal electron donor. As used herein, a "mixed internal electron donor" refers to a combination of (i) a substituted phenylene aromatic diester, and (ii) an electron donor that donates a pair of electrons to one or more metals present in the resulting procatalyst composition. component, and (iii) optionally other components. In one embodiment, the electron donor component is a phthalate, a diether, a benzoate, and combinations thereof. Procatalyst compositions having mixed internal electron donors can be produced by the procatalyst production procedures disclosed in the previously issued patents and publications identified herein.

[0093] For example, a suitable catalyst composition may comprise a procatalyst composition, a cocatalyst, and an external electron donor or a mixed external electron donor (ME) of two or more different components. Suitable external donors include one or more activity limiting agents (ALA), one or more selectivity control agents (SCAs), or both ALA and SCAs. As used herein, an "external electron donor" is a component or composition comprising a mixture of components added independently of the procatalyst structure that modify catalyst performance. As used herein, an "activity limiting agent" is a composition that reduces catalyst activity when the polymerization temperature in the presence of the catalyst increases above a threshold temperature (e.g., above about 85°C). A "selectivity control agent" is a composition that improves polymer tacticity, where improved tacticity is generally understood to mean increased tacticity or reduced xylene solubles, or both. It should be understood that the above definitions are not mutually exclusive, and that a single compound may be classified, for example, as both an activity limiting agent and a selectivity control agent.

[0094] In one embodiment, the external electron donor comprises an alkoxysilane, which has the general formula: SiR m (OR') 4-m (I) wherein R, independently at each occurrence, is hydrogen or a hydrocarbyl or amino group optionally substituted with one or more substituents containing one or more Group 14, 15, 16, or 17 heteroatoms; R' contains up to 20 atoms other than hydrogen and halogen; R' is a C1-4 alkyl group; and m is 0, 1, 2, or 3. In one embodiment, R is C 6~12 Arylalkyl or aralkyl, C 3~12 Cycloalkyl, C 3~12 Branched alkyl, or C 3~12 A cyclic or acyclic amino group, and R' is C 1~4 alkyl, and m is 1 or 2.

[0095] Non-limiting examples of suitable silane compositions include dicyclopentyldimethoxysilane, di-tert-butyldimethoxysilane, methylcyclohexyldimethoxysilane, methylcyclohexyldiethoxysilane, ethylcyclohexyldimethoxysilane, diphenyldimethoxysilane, diisopropyldimethoxysilane, di-n-propyldimethoxysilane, diisobutyldimethoxysilane, diisobutyldiethoxysilane, isobutylpropyldimethoxysilane, di-n-butyldimethoxysilane, cyclopentyltrimethoxysilane, isopropyltrimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, ethyltriethoxysilane, tetramethoxysilane, tetraethoxysilane, diethylaminotriethoxysilane, cyclopentylpyrrolidinodimethoxysilane, bis(pyrrolidino)dimethoxysilane, bis(perhydroisoquinolino)dimethoxysilane, and dimethyldimethoxysilane. In one embodiment, the silane composition comprises dicyclopentyldimethoxysilane (DCPDMS), methylcyclohexyldimethoxysilane (McPDMS), MChDMS, or n-propyltrimethoxysilane (NPTMS), and any combination thereof.

[0096] In one embodiment, the selectivity control agent component can be a mixture of two or more alkoxysilanes. In further embodiments, the mixture is dicyclopentyldimethoxysilane and methylcyclohexyldimethoxysilane, dicyclopentyldimethoxysilane and tetraethoxysilane, or dicyclopentyldimethoxysilane and n-propyltriethoxysilane. In one embodiment, the mixed external electron donor may include a benzoate, a succinate, and / or a diol ester. In one embodiment, the mixed external electron donor includes 2,2,6,6-tetramethylpiperidine as the SCA. In another embodiment, the mixed external electron donor includes a diether as both the SCA and the ALA.

[0097] The mixed external electron donor system can also include an activity limiting agent (ALA). ALA inhibits or otherwise prevents polymerization reactor upsets, ensuring the continuation of the polymerization process. Typically, the activity of Ziegler-Natta catalysts increases as the reactor temperature increases. Ziegler-Natta catalysts also typically maintain high activity at temperatures near the melting point of the produced polymer. Heat generated by exothermic polymerization reactions can cause polymer particle agglomerates to form, ultimately disrupting the polymer production process. ALA reduces catalyst activity at elevated temperatures, thereby preventing reactor upsets and reducing (or preventing) particle agglomeration, ensuring the continuation of the polymerization process.

[0098] The activity limiting agent can be a carboxylic acid ester, a diether, a poly(alkene glycol), a diol ester, or a combination thereof. The carboxylic acid ester can be an aliphatic or aromatic mono- or polycarboxylic acid ester. Non-limiting examples of suitable monocarboxylic acid esters include ethyl and methyl benzoate, ethyl p-methoxybenzoate, methyl p-ethoxybenzoate, ethyl p-ethoxybenzoate, ethyl p-isopropoxybenzoate, ethyl acrylate, methyl methacrylate, ethyl acetate, ethyl p-chlorobenzoate, hexyl p-aminobenzoate, isopropyl naphthenate, n-amyl toluate, ethyl cyclohexanoate, and propyl pivalate.

[0099] Non-limiting examples of suitable polycarboxylic acid esters include dimethyl phthalate, diethyl phthalate, di-n-propyl phthalate, diisopropyl phthalate, di-n-butyl phthalate, diisobutyl phthalate, di-tert-butyl phthalate, diisoamyl phthalate, di-tert-amyl phthalate, dineopentyl phthalate, di-2-ethylhexyl phthalate, di-2-ethyldecyl phthalate, diethyl terephthalate, dioctyl terephthalate, and bis[4-(vinyloxy)butyl]terephthalate.

[0100] Aliphatic carboxylic acid esters are C4 to C 30 It can be an aliphatic acid ester, can be a mono- or poly(two or more) ester, can be linear or branched, can be saturated or unsaturated, or any combination thereof. 30 The aliphatic acid esters may also be substituted with substituents containing one or more Group 14, 15, or 16 heteroatoms. 30 Non-limiting examples of fatty acid esters include aliphatic C 6~30 Ci of monocarboxylic acids -2 O alkyl ester, aliphatic C 8~20 Monocarboxylic acid C 1~20 Alkyl ester, aliphatic C 4~20 C of monocarboxylic and dicarboxylic acids 1~4 Allyl mono- and diesters, aliphatic C 8~20 Monocarboxylic acid C 1~4 Alkyl esters and dicarboxylic acids, and C 2~100 (Poly)glycol or C 2~100 (Poly)glycol ether C 6~20 In a further embodiment, the C6-C 30 Fatty acid esters include laurate, myristate, palmitate, stearate, oleate, sebacate, (poly)(alkylene glycol) mono- or di-acetate, (poly)(alkylene glycol) mono- or di-myristate, (poly)(alkylene glycol) mono- or di-laurate, (poly)(alkylene glycol) mono- or di-oleate, glyceryl tri(acetate), C 2~40 In a further embodiment, the glyceryl tri-esters of fatty acids may be C6-C8 glyceryl triesters of carboxylic acids, and mixtures thereof. 20 The aliphatic ester is isopropyl myristate or di-n-butyl sebacate.

[0101] In one embodiment, the activity limiting agent comprises a diether. The diether may be a 1,3-diether compound represented by the following structure (VI): [ka] wherein R1 to R4 are, independently of one another, alkyl, aryl, or aralkyl groups having up to 20 carbon atoms, which may optionally contain heteroatoms of Group 14, 15, 16, or 17; R i and R2 can be a hydrogen atom. The dialkyl ether can be linear or branched and can contain one or more of the following groups: alkyl, cycloaliphatic, aryl, alkylaryl, or arylalkyl radicals having 1 to 18 carbon atoms, and hydrogen. R1 and R2 can be linked to form a cyclic structure such as cyclopentadiene or fluorene.

[0102] In one embodiment, the activity limiting agent comprises a succinate composition having structure (VII): [ka] wherein R and R' can be the same or different, and R and / or R' comprise one or more of the following groups: hydrogen, straight or branched chain alkyl, alkenyl, cycloalkyl, aryl, arylalkyl, or alkylaryl groups, optionally containing heteroatoms. One or more ring structures can be formed through one or both of the 2- and 3-position carbon atoms.

[0103] In one embodiment, the activity limiting agent comprises a diol ester represented by the following structure (VIII): [ka] wherein n is an integer from 1 to 5. R1 and R2 can be the same or different and each can be selected from hydrogen, methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, t-butyl, allyl, phenyl, or halophenyl groups. R3, R4, R5, R6, R7, and R8 can be the same or different and each can be selected from hydrogen, halogen, and substituted or unsubstituted hydrocarbyl having 1 to 20 carbon atoms. The R1-R6 groups can optionally contain one or more heteroatoms replacing carbon, hydrogen, or both, where the heteroatoms are selected from nitrogen, oxygen, sulfur, silicon, phosphorus, and halogen. R7 and R8 can be the same or different and can be selected from the 2-, 3-, 4-, 6-, 7-, 8-, 9-, 10-, 11-, 12-, 13-, 14-, 15-, 16-, 17-, 18-, 19-, 20-, 21-, 22-, 23-, 24-, 25-, 26-, 27-, 28-, 29-, 30-, 31-, 32-, 33-, 34-, 35-, 36-, 37-, 38-, 39-, 40-, 41-, 42-, 43-, 44-, 45-, 46-, 47-, 48-, 49-, 50-, 51-, 52-, 53-, 54-, 55-, 56-, 57-, 58-, 59-, 60-, 61-, 62-, 63-, 64-, 65-, 66-, 67-, 68-, It can be bonded to any of the carbon atoms at the 5th and 6th positions.

[0104] The individual external electron donor components can be added separately to the reactor, or two or more can be premixed and then added to the reactor as a mixture. More than one selectivity control agent or more than one activity limiting agent can be used in the mixture. In one embodiment, the mixture is dicyclopentyldimethoxysilane and isopropyl myristate, diisopropyldimethoxysilane and isopropyl myristate, dicyclopentyldimethoxysilane and poly(ethylene glycol) laurate, dicyclopentyldimethoxysilane and isopropyl myristate and tri(ethylene glycol) dioleate, methylcyclohexyldimethoxysilane and isopropyl myristate, n-propyltrimethoxysilane and isopropyl myristate, dimethyldimethoxysilane and methylcyclohexyldimethoxysilane and isopropyl myristate, dicyclopentyldimethoxysilane and n-propyltriethoxysilane and isopropyl myristate, diisopropyldimethoxysilane and n-propyltriethoxysilane and isopropyl myristate, and dicyclopentyldimethoxysilane and tetraethoxysilane and isopropyl myristate, dicyclopentyldimethoxysilane and diisopropyldimethoxysilane and n-propyltriethoxysilane and isopropyl myristate, and combinations thereof.

[0105] The catalyst composition includes a cocatalyst. The cocatalyst for use with the Ziegler-Natta procatalyst composition can be an aluminum-containing composition. Non-limiting examples of suitable aluminum-containing compositions include organoaluminum compounds such as trialkylaluminums, dialkylaluminum hydrides, alkylaluminum dihydrides, dialkylaluminum halides, alkylaluminum dihalides, dialkylaluminum alkoxides, and alkylaluminum dialkoxide compounds containing 1 to 10 or 1 to 6 carbon atoms in each alkyl or alkoxide group. In one embodiment, the cocatalyst is a C alkylaluminum dialkoxide, such as triethylaluminum (TEA). 1~4 The catalyst composition comprises a molar ratio of aluminum (Al) to (SCA(s) + ALA(s)) of 0.5 to 25:1, or 1.0 to 20:1, or 1.5 to 15:1, or less than about 6.0, or less than about 5, or less than 4.5. In one embodiment, the molar ratio of Al to (SCA(s) + ALA(s)) is 0.5 to 4.0:1. The molar ratio of total SCA to ALA is 0.01 to 20:1, 0.10 to 5.00:1, 0.43 to 2.33:1, or 0.54 to 1.85:1, or 0.67 to 1.5:1. IV. Hot-fill packaging

[0106] In another embodiment, hot fill packaging can be produced using the propylene-ethylene copolymers discussed above. The hot fill packaging can be injection molded. Preferably, the resin used in the hot fill packaging comprises 100% of the propylene ethylene copolymer resin of the present invention, although up to 5%, 10%, 15%, or even 25% by weight of one or more additional resins other than the copolymers defined herein can be added.

[0107] The copolymer compositions used to make hot fill packaging preferably contain antioxidants and acid scavengers, and in some applications may also preferably contain other additives commonly used in PP, such as nucleating agents, clarifiers, mold release agents, antistatic agents, slip agents, UV stabilizers, and colorants (pigments).

[0108] In one embodiment, the copolymer composition may further contain a type of nucleating agent called a clarifying agent or clarifier. Clarifying agents may be added to further improve the transparency properties of the composition. Clarifying agents may, for example, create a gelling network within the composition. The compound may include a compound capable of

[0109] In one embodiment, the clarification agent may include a sorbitol compound, such as a sorbitol acetal derivative. In one embodiment, for example, the clarification agent may include benzyl sorbitol.

[0110] With respect to sorbitol acetal derivatives that can be used as additives in some embodiments, the sorbitol acetal derivatives are shown in formula (I): [ka] wherein R1 to R5 comprise the same or different moieties selected from hydrogen and C1 to C3 alkyl.

[0111] In some embodiments, R1-R5 are hydrogen, such that the sorbitol acetal derivative is 2,4-dibenzylidene sorbitol ("dibenzylidene sorbitol, DBS"). In some embodiments, R1, R4, and R5 are hydrogen, and R2 and R3 are methyl groups, such that the sorbitol acetal derivative is 1,3:2,4-di-p-methyldibenzylidene-D-sorbitol ("methyldibenzylidene-D-sorbitol, MDBS"). In some embodiments, R1-R4 are methyl groups, and R5 is hydrogen, such that the sorbitol acetal derivative is 1,3:2,4-bis(3,4-dimethylolbenzylidene)sorbitol ("dimethylobenzylideno)sorbitol, DMDBS"). In some embodiments, R2, R3, and R5 are propyl groups (-CH2-CH2-CH3) and R1 and R4 are hydrogen, such that the sorbitol acetal derivative is 1,2,3-trideoxy-4,6-:5,7-bis-O-(4-propylphenyl methylene)nonitol (TBPMN).

[0112] Other embodiments of clarifiers that can be used include: 1,3:2,4-dibenzylidene sorbitol, 1,3:2,4-bis(p-methylbenzylidene) sorbitol, Di(p-methylbenzylidene)sorbitol Di(p-ethylbenzylidene)sorbitol Bis(5',6',7',8'-tetrahydro-2-naphthylidene)sorbitol.

[0113] In one embodiment, the clarifying agent may also include a bisamide.The above clarifying agents may be used alone or in combination.

[0114] When present in the polymer composition, the one or more clarifiers are generally added in an amount greater than about 1500 ppm, such as greater than about 1800 ppm, for example, greater than about 2000 ppm, for example, greater than about 2200 ppm. The one or more clarifiers are generally present in an amount less than about 20,000 ppm, for example, less than about 15,000 ppm, for example, less than about 10,000 ppm, for example, less than about 8,000 ppm, for example, less than about 5,000 ppm. V. Working Examples Example 1

[0115] Following the procedures outlined above, samples of propylene-ethylene random copolymers were produced and their properties were tested. The properties and experimental results are summarized in Table 1. Figure 1 also includes a graph of xylene solubles versus ethylene content.

[0116] Propylene-ethylene random copolymers were produced using a stereospecific, sixth-generation Ziegler-Natta magnesium-supported / titanium-based catalyst. The catalyst contained a non-phthalate internal donor, which produced polymers with a broader molecular weight distribution than polymers made using metallocene catalysts. The process used to produce the polymers is described in the art as the UNIPOL gas-phase process. The catalyst used to produce the polymers contained a substituted phenylene aromatic diester internal electron donor. The catalyst used is available from W.R. Grace and Company and is sold under the trade name CONSISTA. All copolymers were made using triethylaluminum as a cocatalyst. [Table 1] Example 2

[0117] Other propylene-ethylene random copolymers were made according to the present disclosure using generally the same process as described above and compared to a control, all of which had an XS / ET ratio of 2. The propylene-ethylene random copolymers were injection molded into test plaques and tested for haze. Haze was tested initially and after heat aging. The propylene-ethylene random copolymers were as follows: [Table 2]

[0118] Haze is measured according to ASTM test D1003, procedure A, using the latest version of the test Haze was measured before and after 24 hours of heat aging at 55°C using a BYK Gardner Haze-Gard Plus 4725 instrument. Heat aging was performed by placing the plaque samples in an oven. Propylene polymer compositions tend to increase in haze during heat aging. Haze increases due to further crystallization within the polymer and / or the formation of a hazy surface layer, typically referred to as blooming.

[0119] In forming the test plaques, the propylene-ethylene random copolymer was compounded with various stabilizers. In particular, the polymer composition contained 500 ppm of a hindered phenolic antioxidant, namely, pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate. The phosphite stabilizer was added in an amount of 700 ppm. The phosphite stabilizer was tris(2,4-ditert-butylphenyl)phosphite. The acid scavenger was added at a concentration of 200 ppm. The acid scavenger used was hydrotalcite. The antistatic agent was added at a concentration of 500 ppm. The antistatic agent consisted of a distilled monoglyceride, specifically DIMODAN HS KA GMS90 sold by DuPont. A clarifier was also added to the composition at a concentration of 1800 ppm. The clarifier used was 1,2,3-tridethoxy-4,6:5,7-bis-O-[(4-propylphenyl)methylene]nonitol, specifically Milliken Millad It was the NX8000.

[0120] The polymer compositions were injection molded into plaques having three thicknesses: 40 mil, 80 mil, and 125 mil. The plaques were tested for haze before and after oven aging. The following results were obtained: [Table 3]

[0121] As shown above, the propylene-ethylene random copolymers of the present disclosure have unexpectedly good haze properties compared to similar conventional propylene-ethylene random copolymers. For example, one notable result is the absence of any visible blooming or smearing, even after heat treatment.

[0122] As noted above, polymer compositions made according to the present disclosure can exhibit a haze of less than about 15%, such as less than about 12%, for example less than about 11% at 40 mil. Additionally, after aging at 55°C for 24 hours, the increase in haze is less than about 15%, such as less than about 14%, for example less than about 13%, for example less than about 12%. When measuring an 80 mil sample, the initial haze is generally less than about 35%, such as less than about 30%, for example less than about 25%. After heat aging at 55°C for 24 hours, the increase in haze is generally less than about 12%, such as less than about 11%, for example less than about 10%, for example less than about 9%, for example less than about 8%, for example less than about 7.5%. When measuring a 125 mil sample, the initial haze is generally less than about 50%, such as less than about 46%, for example less than about 45%. After heat aging at 55° C. for 24 hours, the % increase in haze is generally less than about 10%, such as less than about 8%, such as less than about 6%, such as less than about 5%. Example 3

[0123] Propylene-ethylene random copolymer samples were prepared in the same manner as described in Example 1. The same procedure was used to produce the samples. The samples were tested for various physical properties. The following results were obtained: [Table 4]

[0124] As shown above, sample number 36 had improved stiffness relative to sample numbers 37 and 38.

[0125] These and other modifications and variations to the present invention may be practiced by those of ordinary skill in the art without departing from the spirit and scope of the present invention, which is more particularly set forth in the appended claims. Additionally, it should be understood that aspects of the various embodiments may be interchanged in whole or in part. Furthermore, those skilled in the art will appreciate that the foregoing description is by way of example only and is not intended to limit the invention as further set forth in such appended claims. The present invention includes the following aspects. [1] A propylene-ethylene copolymer, propylene as the primary monomer; an ethylene content (ET) of 2.0% to a maximum of 5% by weight; A melt flow rate of over 1g / 10min. a xylene soluble fraction (XS) of 2.0% to 7.0% by weight; and an XS / ET ratio of 1.51 or less. [2] 2. The propylene-ethylene copolymer according to 1, wherein the ethylene content is 3.0% by weight to 4.2% by weight. [3] 3. The propylene-ethylene copolymer according to any one of 1 or 2, wherein the melt flow rate is greater than 20 g / 10 min. [4] 4. The propylene-ethylene copolymer according to any one of 1 to 3, wherein the melt flow rate is greater than 10 g / 10 min and up to about 45 g / 10 min. [5] 5. The propylene-ethylene copolymer according to any one of 1 to 4, wherein the ratio of the xylene soluble matter to ethylene (XS / ET) is 0.90 to 1.50. [6] 6. The propylene-ethylene copolymer according to any one of 1 to 5, wherein the XS / ET ratio is less than 1.30. [7] 7. The propylene-ethylene copolymer according to any one of 1 to 6, wherein the XS / ET ratio is less than 1.00. [8] The xylene soluble fraction (XS) and the ethylene content (ET) are calculated using the formula XS=2.1e 0.297(ET) 8. The propylene-ethylene copolymer according to any one of 1 to 7, wherein the propylene-ethylene copolymer is below the line defined by [9] The xylene soluble fraction (XS) and the ethylene content (ET) are calculated using the formula XS=1.4e 0.297(ET) 9. The propylene-ethylene copolymer according to any one of 1 to 8, wherein the propylene-ethylene copolymer is above the line defined by

[10] 10. The propylene-ethylene copolymer according to any one of 1 to 9, wherein the copolymer is formed using a Ziegler-Natta catalyst and a dicyclopentyldimethoxysilane (DCPDMS) based donor.

[11] 11. The propylene-ethylene copolymer according to any one of 1 to 10, wherein the copolymer is formed using a Ziegler-Natta catalyst and an n-propyltrimethoxysilane (NPTMS) based donor.

[12] 12. The propylene-ethylene copolymer according to any one of 1 to 11, wherein the copolymer is produced without the use of a metallocene.

[13] 13. A polymer composition comprising a propylene-ethylene copolymer as defined in any one of 1 to 12, wherein the propylene-ethylene copolymer is present in the polymer composition in an amount greater than about 70 wt%, such as greater than about 80 wt%, such as greater than about 90 wt%, such as greater than about 95 wt%.

[14] 14. The polymer composition according to 13, further comprising a clarifier.

[15] 15. The polymer composition of claim 14, wherein the clarifying agent comprises dibenzyl sorbitol.

[16] 15. The polymer composition of claim 14, wherein the clarifying agent comprises nonitol.

[17] 16. The polymer composition of claim 14 or 15, wherein the polymer composition exhibits a haze of less than about 15% at 40 mil, and after heat aging at 55°C for 24 hours, the haze decreases by about 15% or less, such as about 14% or less, such as about 13% or less, such as about 12% or less.

[18] 18. An injection-molded article comprising the propylene-ethylene copolymer according to any one of 1 to 17.

[19] 13. The propylene-ethylene copolymer according to any of 1 to 12, wherein the copolymer has a molecular weight distribution (Mw / Mn) of greater than about 3.5.

[20] 20. A hot-fill packaging container comprising the propylene-ethylene copolymer according to any one of 1 to 19.

[21] 21. The hot fill packaging container of claim 20, wherein the container is formed by at least one of injection molding, blow molding, and thermoforming.

Claims

1. An injection-molded article comprising a polymer composition containing a propylene-ethylene copolymer, wherein the propylene-ethylene copolymer is present in the polymer composition in an amount greater than 95% by weight; The propylene-ethylene copolymer is propylene as the primary monomer; an ethylene content (ET) of 2.0 wt.% to a maximum of 5 wt.%; a melt flow rate of greater than 20 g / 10 min and up to 45 g / 10 min; 2.0 wt.% to 7.0 wt.% xylene soluble fraction (XS); Including, the XS / ET ratio is less than 1.30 or 1.15 to 1.35; The xylene soluble fraction (XS) and the ethylene content (ET) are determined by the formula: XS = 2.1e ０．２９７（ＥＴ） below the line defined by having a molecular weight distribution (Mw / Mn) greater than 5.5; The injection molded article.

2. 2. The injection molded article of claim 1, wherein the ethylene content is from 3.0% to 4.2% by weight.

3. 10. The injection-molded article of claim 1, wherein the XS / ET ratio is less than 1.

00.

4. The xylene soluble fraction (XS) and the ethylene content (ET) are determined by the formula: XS = 1.4e ０．２９７（ＥＴ） 3. The injection-molded article of claim 1, wherein the injection-molded article is above a line defined by

5. The injection molded article of claim 1 further comprising a clarifier.

6. 6. The injection molded article of claim 5, wherein the clarifier comprises dibenzyl sorbitol.

7. 6. The injection molded article of claim 5, wherein the clarifier comprises nonitol.

8. 7. The injection molded article of claim 5 or 6, wherein the polymer composition exhibits a haze of less than 15% at 40 mil, and after heat aging at 55°C for 24 hours, the haze increases by no more than 15%.

9. 9. The injection molded article of claim 8, wherein after heat aging at 55°C for 24 hours, the haze increases by no more than 14%.

10. 9. The injection molded article of claim 8, wherein the haze increases by no more than 13% after heat aging at 55°C for 24 hours.

11. 9. The injection molded article of claim 8, wherein the haze increases by no more than 12% after heat aging at 55°C for 24 hours.

Images