Method for producing toner for developing electrostatic images, and toner for developing electrostatic images

Abstract

To provide a method for manufacturing a toner for electrostatic charge image development which is excellent in color point occurrence suppressing property in an obtained image and fog suppressing property.SOLUTION: A method for manufacturing a toner for electrostatic charge image development includes an aggregation step of aggregating at least resin particles contained in a dispersion liquid using an aluminum-based aggregating agent, and forming aggregated particles, a fusion step of heating and fusing the aggregated particles, and forming fused particles, a cooling step of cooling the dispersion liquid containing the fused particles, and obtaining a toner particle dispersion liquid, and a pH adjustment step of adjusting the pH of the toner particle dispersion liquid to 8 or more and 11 or less.SELECTED DRAWING: Figure 1

Description

[Technical Field]

[0001] The present invention relates to a method for producing a toner for developing electrostatic images, and to a toner for developing electrostatic images. [Background technology]

[0002] Methods for visualizing image information, such as electrophotography, are currently used in a variety of fields. In electrophotography, an electrostatic image is formed as image information on the surface of an image carrier by charging and forming an electrostatic image. Then, a toner image is formed on the surface of the image carrier using a developer containing toner. This toner image is then transferred to a recording medium, and the toner image is then fixed to the recording medium. Through these steps, the image information is visualized as an image.

[0003] For example, Patent Document 1 discloses a method for producing a toner for developing an electrostatic latent image, which includes a step of preparing toner base particles containing at least a binder resin having a hydrophilic polar group, a colorant, and a release agent, and a washing step of washing the toner base particles, characterized in that at the end of the washing step, an alkaline aqueous solution is added to the toner base particles to adjust them to an alkaline state, and then an aqueous solution in which a monovalent metal salt is dissolved is added.

[0004] Patent Document 2 discloses a method for producing a toner for electrophotography, which includes the following steps (1) to (3). Step (1): A step of fusing the aggregated particles in an aqueous mixture containing a surfactant and resin particles (A) and agglomerated particles containing release agent particles after and / or while adjusting the pH of the aqueous mixture to 2.0 to 5.0 at 25°C. Step (2): A step of adjusting the pH of the fused particle dispersion liquid obtained in step (1) to 5.5 to 7.5 at 25°C. Step (3): A step of removing the liquid portion from the fused particle dispersion obtained in step (2) to obtain toner particles.

[0005] Patent Document 3 also discloses a method for producing a polymerized toner, which includes a step of forming colored resin particles by a polymerization method to obtain an aqueous dispersion of colored resin particles, a separation and washing step of separating and washing the colored resin particles in the aqueous dispersion of colored resin particles and redispersing them in ion-exchanged water to obtain a redispersion of colored resin particles, a by-product particle removing step of removing by-product fine particles from the redispersion of colored resin particles, a dehydration step of dehydrating the redispersion of colored resin particles to obtain wet colored resin particles, and a drying step of drying the wet colored resin particles, in which a belt filter is used as a device for separating and washing in the separation and washing step, and the colored resin particles obtained by separation and washing with the belt filter are redispersed in ion-exchanged water to prepare a redispersion of colored resin particles with a solids concentration of 20% by weight, and the redispersion is filtered. and then redispersing the colored resin particles in ion-exchange water to obtain a redispersion of colored resin particles having a predetermined solid content concentration; in the by-product fine particle removing step, adjusting the pH of the redispersion of colored resin particles having a predetermined solid content concentration to 9 to 12, removing the by-product fine particles from the pH-adjusted redispersion of colored resin particles, and then redispersing the colored resin particles in ion-exchange water to obtain a redispersion of colored resin particles having a predetermined solid content concentration; and in the dehydration step, adding an acid and / or a cationic polymer flocculant as an aggregating agent to the redispersion of colored resin particles having a predetermined solid content concentration to aggregate the colored resin particles, followed by dehydration. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] Japanese Patent Application Laid-Open No. 2012-83639 [Patent Document 2] Japanese Patent Application Laid-Open No. 2013-25093 [Patent Document 3] Japanese Patent Application Laid-Open No. 2009-109916 Summary of the Invention [Problem to be solved by the invention]

[0007] An object of the present invention is to provide a method for producing a toner for developing electrostatic images, the method comprising: an aggregation step of aggregating at least resin particles contained in a dispersion liquid using an aluminum-based aggregating agent to form aggregated particles; a fusion step of heating and fusing the aggregated particles to form fused particles; a cooling step of cooling the dispersion liquid containing the fused particles to obtain a toner particle dispersion liquid; and a pH adjustment step of adjusting the pH of the toner particle dispersion liquid, the method exhibiting excellent suppression of color spot generation and fogging in the resulting image compared to when the pH of the toner particle dispersion liquid is adjusted to less than 8 or more than 11 in the pH adjustment step. [Means for solving the problem]

[0008] Means for solving the above problems include the following aspects. <1> A method for producing a toner for developing electrostatic images, comprising: an aggregation step of aggregating at least resin particles contained in a dispersion liquid using an aluminum-based aggregating agent to form aggregated particles; a fusion step of heating and fusing the aggregated particles to form fused particles; a cooling step of cooling the dispersion liquid containing the fused particles to obtain a toner particle dispersion liquid; and a pH adjustment step of adjusting the pH of the toner particle dispersion liquid to 8 or more and 11 or less. <2> In the cooling step, the dispersion containing the fused particles is cooled to a temperature of 40° C. or less. <1> 10. A method for producing the toner for developing electrostatic images according to claim 9. <3> After the cooling step, the pH adjustment step is carried out within 60 minutes. <1> or <2> 10. A method for producing the toner for developing electrostatic images according to claim 9. <4> After the cooling step, the pH adjustment step is carried out within 30 minutes. <3> 10. A method for producing the toner for developing electrostatic images according to claim 9. <5> In the pH adjustment step, the pH of the toner particle dispersion is adjusted to 8.5 or more and 11.0 or less. <1> ~ <4> 10. A method for producing the toner for developing electrostatic images according to any one of claims 1 to 9. <6> In the pH adjustment step, the pH of the toner particle dispersion is adjusted to 9.0 or more and 10.0 or less. <5> 10. A method for producing the toner for developing electrostatic images according to claim 9. <7> In the aggregating step, at least the resin particles and the release agent particles are aggregated. <1> ~ <6> 10. A method for producing the toner for developing electrostatic images according to any one of claims 1 to 9. <8> In the pH adjustment step, the pH is adjusted with an alkali metal hydroxide. <1> ~ <7> 10. A method for producing the toner for developing electrostatic images according to any one of claims 1 to 9. <9> <1> ~ <8> 10. A toner for developing electrostatic images, which is produced by the method for producing a toner for developing electrostatic images according to any one of claims 1 to 9. [Effects of the Invention]

[0009] <1> or <7> According to the invention, there is provided a method for producing a toner for developing electrostatic images, which includes an aggregation step of aggregating at least resin particles contained in a dispersion liquid using an aluminum-based aggregating agent to form aggregated particles, a fusion step of heating and fusing the aggregated particles to form fused particles, a cooling step of cooling the dispersion liquid containing the fused particles to obtain a toner particle dispersion liquid, and a pH adjustment step of adjusting the pH of the toner particle dispersion liquid, and which is superior in terms of suppressing the occurrence of color spots and suppressing fogging in the resulting image compared to when the pH of the toner particle dispersion liquid is adjusted to less than 8 or more than 11 in the pH adjustment step. <2> According to the present invention, there is provided a method for producing a toner for developing electrostatic images, which is superior in terms of fogging suppression in the resulting image compared to a case in which the dispersion liquid containing the fused particles is cooled to a temperature of more than 40°C in the cooling step. <3> According to the present invention, a method for producing a toner for developing electrostatic images is provided which is superior in suppressing the occurrence of color spots in the resulting image compared to when the pH adjustment step is performed 60 minutes after the cooling step. <4> According to the present invention, a method for producing a toner for developing electrostatic images is provided which is superior in suppressing the occurrence of color spots in the resulting image compared to when the pH adjustment step is performed 30 minutes after the cooling step. <5> According to the invention related to the above, there is provided a method for producing a toner for developing electrostatic images, which is superior in suppressing the occurrence of color spots and fogging in the obtained image compared to when the pH of the toner particle dispersion is adjusted to less than 8.5 or more than 11.0 in the pH adjustment step. <6> According to the invention, there is provided a method for producing a toner for developing electrostatic images, which is superior in suppressing the occurrence of color spots and fogging in the obtained image compared to when the pH of the toner particle dispersion is adjusted to less than 9.0 or more than 10.0 in the pH adjustment step. <8> According to the invention, there is provided a method for producing a toner for developing electrostatic images, which is superior in suppressing the occurrence of color spots and fogging in the resulting image compared to when the pH is adjusted with ammonia in the pH adjustment step. <9> According to the invention, a method for producing a toner for developing electrostatic images, which includes an aggregation step of aggregating at least resin particles contained in a dispersion liquid using an aluminum-based aggregating agent to form aggregated particles, a fusion step of heating and fusing the aggregated particles to form fused particles, a cooling step of cooling the dispersion liquid containing the fused particles to obtain a toner particle dispersion, and a pH adjustment step of adjusting the pH of the toner particle dispersion, provides a toner for developing electrostatic images that is excellent in suppressing the occurrence of color spots and suppressing fogging in the resulting image, compared to when the pH of the toner particle dispersion is adjusted to less than 8 or more than 11 in the pH adjustment step. [Brief explanation of the drawings]

[0010] [Figure 1] 1 is a schematic configuration diagram illustrating an example of an image forming apparatus according to an embodiment of the present invention. [Figure 2] FIG. 2 is a schematic diagram illustrating an example of a process cartridge according to the present exemplary embodiment. DETAILED DESCRIPTION OF THE INVENTION

[0011] Hereinafter, an embodiment of the present invention will be described in detail. In addition, in numerical ranges described in stages, the upper limit or lower limit value described in a certain numerical range may be replaced with the upper limit or lower limit value of another numerical range described in stages. Furthermore, in a numerical range, the upper limit or lower limit value described in a certain numerical range may be replaced with a value shown in the examples. When a plurality of substances corresponding to each component are present in the composition, the amount of each component in the composition means the total amount of the plurality of substances present in the composition, unless otherwise specified. The term "process" includes not only an independent process but also a process that cannot be clearly distinguished from other processes as long as the intended purpose of the process is achieved.

[0012] (Method of manufacturing toner for developing electrostatic images) The method for producing a toner for developing electrostatic images according to this embodiment includes an aggregation step of aggregating at least resin particles contained in a dispersion liquid using an aluminum-based aggregating agent to form aggregated particles; a fusion step of heating and fusing the aggregated particles to form fused particles; a cooling step of cooling the dispersion liquid containing the fused particles to obtain a toner particle dispersion liquid; and a pH adjustment step of adjusting the pH of the toner particle dispersion liquid to a range of 8 to 11. The electrostatic image developing toner according to this embodiment is a toner produced by the method for producing the electrostatic image developing toner according to this embodiment.

[0013] One cause of color dots in the resulting image is that the charging characteristics change depending on the toner's cohesion, resulting in the toner adhering to locations unrelated to the output image. Patent Document 1 uses a photoreceptor with a photosensitive layer made of amorphous silicon, and uses fine particles containing quaternary ammonium salt functional groups as a charge control agent to stably charge the toner positively. However, these fine particles containing quaternary ammonium salt functional groups tend to aggregate instantaneously. Therefore, core particles containing a resin containing a quaternary ammonium salt functional group are coated with one or more resins selected from the group consisting of (meth)acrylic resins and styrene-(meth)acrylic resins to prevent aggregation of the charge control agent and maintain an appropriate charge level, thereby suppressing image defects such as color dots and fog. In addition, the causes of color dots are not limited to the above. When an aluminum-based coagulant is used in the production of toner by emulsion polymerization, a gel-like substance may be generated after the production of toner particles. Since the gel-like substance cannot be removed in the washing process, it is mixed into the toner particles and causes color dots.

[0014] As described above, in the conventional method, the toner particle dispersion liquid was sometimes kept as it was for a long time after the cleaning process, and the toner particle dispersion liquid that was left for a long time contained a large amount of gel-like substances. The present inventors have found that this gel-like substance is caused by aluminum hydroxide that is generated when a toner particle dispersion is left standing at a pH of less than 8 for several hours. First, aluminum ions present in the aqueous dispersion of toner particles after the cooling process combine with hydroxide ions in the aqueous dispersion to form aluminum hydroxide. This aluminum hydroxide gels when exposed to water for a long period of time, gradually increasing in size over time. Once formed, gel-like aluminum hydroxide cannot be completely removed by adjusting the pH, so pH adjustment is required before the gel forms to suppress its formation. While the formation of gel-like substances can be suppressed by adjusting the pH of the toner dispersion to 8 or higher after cooling, adding basic compounds to the toner particles has been difficult due to their significant impact on charge and surface properties. In fact, if the pH of the toner particle dispersion exceeds 11, chargeability decreases and fog occurs in the resulting image. The method for producing a toner for developing electrostatic images according to this embodiment includes a cooling step of cooling the dispersion containing the fused particles to obtain a toner particle dispersion, and a pH adjustment step of adjusting the pH of the toner particle dispersion to 8 or more and 11 or less. Therefore, even if an aluminum-based aggregating agent is used as the aggregating agent, it is estimated that the generation of aluminum hydroxide is suppressed, the generation of gel-like substances is suppressed, the generation of color spots in the resulting image is suppressed, the decrease in charging ability is suppressed, and the generation of fogging in the resulting image is also suppressed.

[0015] The method for producing the toner for developing electrostatic images according to this embodiment is a method for producing toner particles by an aggregation and coalescence method. Details of each step other than those described above will be explained below.

[0016] <Agglomeration process> The method for producing the toner for developing electrostatic images according to this embodiment includes an aggregation step in which at least resin particles contained in a dispersion liquid are aggregated using an aluminum-based aggregating agent to form aggregated particles. The dispersion liquid in the aggregation step contains at least resin particles, preferably at least resin particles and release agent particles, and may further contain colorant particles and the like, as necessary. The method for preparing the dispersion is not particularly limited, but it can be suitably prepared by mixing a resin particle dispersion and a release agent particle dispersion. Then, at least the resin particles are aggregated in the dispersion to prepare a dispersion containing aggregated particles.

[0017] Specifically, the aggregation is performed by adding an aggregating agent to the dispersion and adjusting the pH of the dispersion to an acidic value (for example, a pH of 2 or more and 5 or less), adding a dispersion stabilizer as needed, and then heating the dispersion to a temperature corresponding to the glass transition temperature of the resin particles (specifically, for example, the glass transition temperature of the resin particles minus 30°C or more and the glass transition temperature minus 10°C or less), thereby aggregating the particles dispersed in the dispersion to form aggregated particles. In the aggregation step, for example, the dispersion may be stirred with a rotary shear homogenizer, the aggregation agent may be added at room temperature (e.g., 25°C), the pH of the dispersion may be adjusted to an acidic value (e.g., a pH of 2 or more and 5 or less), a dispersion stabilizer may be added as needed, and then the heating may be carried out.

[0018] As the flocculant, an aluminum-based flocculant is used. If necessary, an additive that forms a complex or a similar bond with the aluminum ions of the flocculant may be used, and a chelating agent is preferably used as this additive.

[0019] Examples of inorganic metal salts include aluminum salts such as aluminum chloride and aluminum sulfate, and inorganic aluminum salt polymers such as polyaluminum chloride and polyaluminum hydroxide. Among these, it is preferable to use aluminum sulfate as the flocculant. The amount of aluminum-based aggregating agent to be added is not particularly limited as long as it can aggregate the particles, but is preferably 0.01 parts by mass or more and 5.0 parts by mass or less, and more preferably 0.1 parts by mass or more and 3.0 parts by mass or less, per 100 parts by mass of resin particles.

[0020] The chelating agent may be a water-soluble chelating agent. Examples of the chelating agent include hydroxycarboxylic acids such as tartaric acid, citric acid, and gluconic acid, iminodiacetic acid (IDA), nitrilotriacetic acid (NTA), ethylenediaminetetraacetic acid (EDTA), and salts thereof. Among them, salts of nitrilotriacetic acid (NTA) or 3-hydroxy-2,2'-iminodisuccinic acid tetrasodium salt (HIDS) are preferably used as the chelating agent from the viewpoints of suppressing the occurrence of color spots and fogging in the resulting image. The amount of the chelating agent added is, for example, preferably 0.01 parts by mass or more and 5.0 parts by mass or less, and more preferably 0.1 parts by mass or more and less than 3.0 parts by mass, relative to 100 parts by mass of the resin particles.

[0021] The dispersion in the aggregation step is preferably an aqueous dispersion, and more preferably an aqueous dispersion. Examples of the dispersion medium used in the dispersion liquid in the aggregation step include an aqueous medium. Examples of aqueous media include water such as distilled water and ion-exchanged water, alcohols, etc. These may be used alone or in combination of two or more.

[0022] The dispersion liquid in the aggregation step preferably contains a surfactant. Examples of surfactants include anionic surfactants such as sulfate ester salts, sulfonate salts, phosphate esters, and soaps; cationic surfactants such as amine salts and quaternary ammonium salts; and nonionic surfactants such as polyethylene glycols, alkylphenol ethylene oxide adducts, and polyhydric alcohols. Among these, anionic surfactants and cationic surfactants are particularly preferred. Nonionic surfactants may be used in combination with anionic surfactants or cationic surfactants. The surfactants may be used alone or in combination of two or more.

[0023] The volume average particle size of the resin particles dispersed in the dispersion before aggregation is preferably 0.01 μm or more and 1 μm or less, more preferably 0.08 μm or more and 0.8 μm or less, and even more preferably 0.1 μm or more and 0.6 μm or less. The volume average particle size of the release agent particles dispersed in the dispersion before aggregation is preferably 0.01 μm or more and 1 μm or less, more preferably 0.08 μm or more and 0.8 μm or less, and even more preferably 0.1 μm or more and 0.6 μm or less. The volume average particle size of the resin particles and release agent particles is measured using a particle size distribution obtained by measurement with a laser diffraction particle size distribution analyzer (for example, LA-700 manufactured by Horiba, Ltd.), and the cumulative distribution for the volume of the divided particle size range (channel) is calculated from the small particle size side, and the particle size at which the cumulative percentage of all particles is 50% is measured as the volume average particle size D50v. The volume average particle sizes of particles in other dispersions are also measured in the same way.

[0024] The resin particles in the aggregation step preferably contain polyester resin particles, and more preferably are polyester resin particles, from the viewpoint of suppressing the occurrence of color spots and fogging in the resulting image. The resin particles in the aggregation step preferably include amorphous resin particles, and more preferably include amorphous resin particles and crystalline resin particles. As described above, the dispersion liquid may further contain colorant particles and the like used in the toner particles. The preferred volume average particle size of the colorant particles is the same as the preferred volume average particle size of the resin particles.

[0025] In the aggregation step, the solid content concentration of the dispersion is preferably 5% by mass or more and 30% by mass or less, more preferably 8% by mass or more and 25% by mass or less, and particularly preferably 11% by mass or more and 20% by mass or less, from the viewpoint of dispersibility of resin particles, release agent particles, etc.

[0026] The volume average particle size of the aggregated particles obtained in the aggregation step is not particularly limited, and can be appropriately selected depending on the volume average particle size of the desired toner particles. The aggregation can be stopped by a known method, such as by increasing the pH. A suitable method for increasing the pH is to add a basic compound. Suitable examples of the basic compound include the basic compounds described below in the pH adjustment step.

[0027] The preferred embodiments of the components contained in the toner particles, such as the binder resin, the release agent, and the colorant, will be described below.

[0028] <Fusion process> The method for producing the toner for developing electrostatic images according to this embodiment includes a fusing step of heating and fusing the aggregated particles to form fused particles. In the fusion step, the dispersion liquid in which the aggregated particles are dispersed is heated, for example, to a temperature equal to or higher than the glass transition temperature of the resin particles (for example, a temperature 30°C to 50°C higher than the glass transition temperature of the resin particles), to fuse and coalesce the aggregated particles and form fused particles. When the release agent particles are aggregated in the aggregation step, the resin and the release agent are in a fused state at a temperature equal to or higher than the glass transition temperature of the resin particles and the melting temperature of the release agent in the fusion step. Thereafter, the mixture is cooled to obtain toner particles.

[0029] <Cooling process> The method for producing a toner for developing electrostatic images according to this embodiment includes a cooling step of cooling the dispersion containing the fused particles to obtain a toner particle dispersion. In the cooling step, it is preferable to cool the temperature of the dispersion liquid containing the fused particles to 40°C or lower, more preferably to 0°C or higher and 35°C or lower, still more preferably to 10°C or higher and 30°C or lower, and particularly preferably to 15°C or higher and 25°C or lower, from the viewpoints of suppressing the generation of color dots in the obtained image and fog suppression. There are no particular restrictions on the cooling means in the cooling step, and known cooling means can be used.

[0030] The cooling rate of the dispersion liquid containing the fused particles in the cooling step is preferably 1°C / min or higher, more preferably 5°C / min or higher, still more preferably 10°C / min or higher and 100°C / min or lower, and particularly preferably 15°C / min or higher and 50°C / min or lower, from the viewpoints of suppressing the generation of aluminum hydroxide, suppressing the generation of color dots in the obtained image, and fog suppression.

[0031] <pH adjustment step> The method for producing an electrostatic charge image developing toner according to this embodiment includes a pH adjustment step of adjusting the pH of the toner particle dispersion liquid to 8 or higher and 11 or lower. From the viewpoints of suppressing the generation of aluminum hydroxide, suppressing the generation of color dots in the obtained image, and fog suppression, in the method for producing an electrostatic charge image developing toner according to this embodiment, it is preferable to perform the pH adjustment step within 60 minutes after the cooling step, more preferably within 30 minutes after the cooling step, and particularly preferably within 15 minutes after the cooling step.

[0032] In the pH adjustment step, from the viewpoints of suppressing the generation of aluminum hydroxide, suppressing the generation of color dots in the obtained image, and fog suppression, it is preferable to adjust the pH of the toner particle dispersion liquid to 8.5 or higher and 11.0 or lower, more preferably to 8.5 or higher and 10.5 or lower, and particularly preferably to 9.0 or higher and 10.0 or lower.

[0033] In addition, from the viewpoint of suppressing the occurrence of color spots and fogging in the resulting image, it is preferable that the pH of the toner particle dispersion after the pH adjustment step is higher than the pH of the toner particle dispersion before the pH adjustment step. In order to further exert the effects of the present embodiment, the pH of the toner particle dispersion before the pH adjustment step is preferably 6.0 or more and 9.5 or less, more preferably 7.0 or more and 9.2 or less, and particularly preferably 7.5 or more and 9.0 or less.

[0034] In the pH adjustment step, it is preferable to adjust the pH by adding a basic compound. Specific examples of the basic compound include hydroxides of alkali metals such as lithium, sodium, and potassium, oxides or hydroxides of alkaline earth metals such as magnesium and calcium, ammonia, amine compounds, etc. Among these, from the viewpoints of suppressing the occurrence of color spots and fogging in the resulting image, hydroxides of alkali metals or alkaline earth metals are preferred, hydroxides of alkali metals are more preferred, potassium hydroxide or sodium hydroxide are even more preferred, and sodium hydroxide is particularly preferred. The basic compound is preferably added in the form of a solution of the basic compound in an aqueous medium, more preferably in the form of an aqueous solution of the basic compound. Examples of aqueous media include those described below.

[0035] Through the above steps, toner particles are obtained.

[0036] After the pH adjustment step is completed, the toner particles formed in the solution are subjected to a known washing step, a solid-liquid separation step, and a drying step to obtain dried toner particles. In the washing step, it is preferable to carry out sufficient replacement washing with ion-exchanged water from the viewpoint of electrostatic chargeability. Furthermore, the solid-liquid separation step is not particularly limited, but from the viewpoint of productivity, it is preferable to carry out suction filtration, pressure filtration, etc. Furthermore, in the drying step, there is no particular limitation on the method, but from the viewpoint of productivity, it is preferable to carry out freeze drying, flash drying, fluidized drying, vibration-type fluidized drying, etc.

[0037] The method for producing the toner for developing electrostatic images according to this exemplary embodiment preferably includes a step of externally adding an external additive to the obtained toner particles. The external addition may be carried out using, for example, a V blender, a Henschel mixer, a Loedige mixer, etc. Furthermore, if necessary, coarse particles of the toner may be removed using a vibrating sieve, an air sieve, etc.

[0038] <Resin particle dispersion preparation process> The method for producing the toner for developing electrostatic images according to this embodiment preferably includes a resin particle dispersion preparation step of preparing a resin particle dispersion. In addition to the resin particle dispersion liquid in which resin particles are dispersed, the method for producing the toner for developing electrostatic images according to the present embodiment preferably includes, for example, a step of preparing a colorant particle dispersion liquid in which colorant particles are dispersed, and a step of preparing a release agent particle dispersion liquid in which release agent particles are dispersed.

[0039] The resin particle dispersion is prepared, for example, by dispersing resin particles in a dispersion medium using a surfactant.

[0040] Examples of the dispersion medium used in the resin particle dispersion include aqueous media. Examples of aqueous media include water such as distilled water and ion-exchanged water, alcohols, etc. These may be used alone or in combination of two or more.

[0041] Examples of surfactants include anionic surfactants such as sulfate ester salts, sulfonate salts, phosphate esters, and soaps; cationic surfactants such as amine salts and quaternary ammonium salts; and nonionic surfactants such as polyethylene glycols, alkylphenol ethylene oxide adducts, and polyhydric alcohols. Among these, anionic surfactants and cationic surfactants are particularly preferred. Nonionic surfactants may be used in combination with anionic surfactants or cationic surfactants. The surfactants may be used alone or in combination of two or more.

[0042] In a resin particle dispersion, resin particles can be dispersed in a dispersion medium by common dispersion methods such as a rotary shear homogenizer, a ball mill with media, a sand mill, or a Dynomill. Depending on the type of resin particles, the resin particles may be dispersed in a dispersion medium by a phase inversion emulsification method. The phase inversion emulsification method involves dissolving the resin to be dispersed in a hydrophobic organic solvent in which the resin is soluble, neutralizing the organic continuous phase (O phase) by adding a base, and then introducing an aqueous medium (W phase) to invert the phase from W / O to O / W, thereby dispersing the resin in particulate form in the aqueous medium.

[0043] The volume average particle size of the resin particles dispersed in the resin particle dispersion is, for example, preferably from 0.01 μm to 1 μm, more preferably from 0.08 μm to 0.8 μm, and even more preferably from 0.1 μm to 0.6 μm.

[0044] The content of resin particles contained in the resin particle dispersion is preferably 5% by mass or more and 50% by mass or less, and more preferably 10% by mass or more and 40% by mass or less.

[0045] In the same manner as in the resin particle dispersion, for example, a colorant particle dispersion and a release agent particle dispersion are also prepared. That is, the volume average particle size, dispersion medium, dispersion method, and particle content of the particles in the resin particle dispersion are the same for the colorant particles dispersed in the colorant particle dispersion and the release agent particles dispersed in the release agent particle dispersion.

[0046] Furthermore, the method for producing a toner for developing electrostatic images according to this embodiment may further include, after the aggregation step and before the fusion step, a step of further mixing the dispersion containing the aggregated particles with a resin particle dispersion in which binder resin particles are dispersed, and aggregating the aggregated particles so that the binder resin particles adhere to the surfaces of the aggregated particles to form second aggregated particles. By undergoing the step of forming the second aggregated particles, toner particles having a core-shell structure are formed.

[0047] The method for producing the toner for developing electrostatic images according to this embodiment may include known steps other than those described above.

[0048] Each component contained in the toner for developing electrostatic images will be described in detail below. The toner particles preferably contain a binder resin, a release agent, and, if necessary, other components, and more preferably contain a binder resin, a release agent, and a colorant.

[0049] <Binder resin> The binder resin preferably contains an amorphous resin, and more preferably contains an amorphous resin and a crystalline resin from the viewpoints of image strength and suppression of density unevenness in the obtained image. That is, in the first aggregation step, it is more preferable that the resin particles contain amorphous resin particles and crystalline resin particles.

[0050] Here, the term "amorphous resin" refers to a resin that, in thermal analysis measurement using differential scanning calorimetry (DSC), does not show a clear endothermic peak but only a stepwise endothermic change, is solid at room temperature, and becomes thermoplastic at a temperature equal to or higher than the glass transition temperature. On the other hand, a crystalline resin is one that shows a clear endothermic peak rather than a stepwise change in endothermic amount in differential scanning calorimetry (DSC). Specifically, for example, a crystalline resin means a resin whose half-width of the endothermic peak when measured at a heating rate of 10°C / min is within 10°C, and an amorphous resin means a resin whose half-width exceeds 10°C or a resin in which no clear endothermic peak is observed.

[0051] The amorphous resin will be described. Examples of the amorphous resin include known amorphous resins such as amorphous polyester resin, amorphous vinyl resin (e.g., styrene-acrylic resin), epoxy resin, polycarbonate resin, polyurethane resin, etc. Among these, from the viewpoint of suppressing uneven density and white spots in the obtained image, amorphous polyester resin and amorphous vinyl resin (particularly styrene-acrylic resin) are preferred, and amorphous polyester resin is more preferred. In addition, it is also a preferred embodiment to use an amorphous polyester resin and a styrene-acrylic resin in combination as the amorphous resin.

[0052] The amorphous polyester resin may be, for example, a condensation polymer of a polycarboxylic acid and a polyhydric alcohol. As the amorphous polyester resin, a commercially available product or a synthesized product may be used.

[0053] Examples of polycarboxylic acids include aliphatic dicarboxylic acids (e.g., oxalic acid, malonic acid, maleic acid, fumaric acid, citraconic acid, itaconic acid, glutaconic acid, succinic acid, alkenylsuccinic acid, adipic acid, and sebacic acid), alicyclic dicarboxylic acids (e.g., cyclohexanedicarboxylic acid), aromatic dicarboxylic acids (e.g., terephthalic acid, isophthalic acid, phthalic acid, and naphthalenedicarboxylic acid), anhydrides thereof, and lower alkyl esters thereof (e.g., having 1 to 5 carbon atoms). Among these, aromatic dicarboxylic acids are preferred as polycarboxylic acids. The polycarboxylic acid may be a trivalent or higher carboxylic acid having a crosslinked or branched structure in combination with a dicarboxylic acid. Examples of the trivalent or higher carboxylic acid include trimellitic acid, pyromellitic acid, anhydrides thereof, and lower alkyl esters thereof (e.g., having 1 to 5 carbon atoms). The polycarboxylic acids may be used alone or in combination of two or more.

[0054] Examples of polyhydric alcohols include aliphatic diols (e.g., ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, butanediol, hexanediol, neopentyl glycol, etc.), alicyclic diols (e.g., cyclohexanediol, cyclohexanedimethanol, hydrogenated bisphenol A, etc.), and aromatic diols (e.g., ethylene oxide adducts of bisphenol A, propylene oxide adducts of bisphenol A, etc.). Among these, aromatic diols and alicyclic diols are preferred as polyhydric alcohols, and aromatic diols are more preferred. As the polyhydric alcohol, a trihydric or higher polyhydric alcohol having a crosslinked or branched structure may be used in combination with the diol. Examples of trihydric or higher polyhydric alcohols include glycerin, trimethylolpropane, and pentaerythritol. The polyhydric alcohols may be used alone or in combination of two or more.

[0055] Amorphous polyester resins can be obtained by known production methods. Specifically, for example, the polymerization temperature is set to 180°C or higher and 230°C or lower, and the reaction system is reduced in pressure as necessary, and the reaction is carried out while removing water and alcohol generated during condensation. If the raw material monomers are not soluble or compatible at the reaction temperature, a high-boiling solvent may be added as a solubilizer to dissolve them. In this case, the polycondensation reaction is carried out while distilling off the solubilizer. If a monomer with poor compatibility is present in the copolymerization reaction, it is recommended that the poorly compatible monomer be condensed in advance with the acid or alcohol to be polycondensed, and then polycondensed with the main component.

[0056] Examples of binder resins, particularly amorphous resins, include styrene-acrylic resins. Styrene-acrylic resins are copolymers obtained by copolymerizing at least a styrene-based monomer (a monomer having a styrene skeleton) and a (meth)acrylic-based monomer (a monomer having a (meth)acrylic group, preferably a monomer having a (meth)acryloxy group). The styrene-acrylic resins include, for example, copolymers of a styrene monomer and a (meth)acrylic acid ester monomer. The acrylic resin portion of the styrene-acrylic resin is a partial structure formed by polymerizing either an acrylic monomer or a methacrylic monomer, or both. Furthermore, the term "(meth)acrylic" includes both "acrylic" and "methacrylic."

[0057] Specific examples of styrene-based monomers include styrene, alkyl-substituted styrenes (e.g., α-methylstyrene, 2-methylstyrene, 3-methylstyrene, 4-methylstyrene, 2-ethylstyrene, 3-ethylstyrene, 4-ethylstyrene, etc.), halogen-substituted styrenes (e.g., 2-chlorostyrene, 3-chlorostyrene, 4-chlorostyrene, etc.), vinylnaphthalene, etc. The styrene-based monomers may be used alone or in combination of two or more. Of these, styrene is preferred as the styrene-based monomer in terms of ease of reaction, ease of reaction control, and availability.

[0058] Specific examples of (meth)acrylic monomers include (meth)acrylic acid and (meth)acrylic acid esters. Examples of (meth)acrylic acid esters include (meth)acrylic acid alkyl esters (e.g., methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, n-butyl (meth)acrylate, n-pentyl (meth)acrylate, n-hexyl acrylate, n-heptyl (meth)acrylate, n-octyl (meth)acrylate, n-decyl (meth)acrylate, n-dodecyl (meth)acrylate, n-lauryl (meth)acrylate, n-tetradecyl (meth)acrylate, n-hexadecyl (meth)acrylate, n-octadecyl (meth)acrylate, isopropyl (meth)acrylate, isobutyl (meth)acrylate, t-butyl (meth)acrylate, isopentyl (meth)acrylate, amyl (meth)acrylate, and (meth) Examples of the (meth)acrylic acid monomer include neopentyl acrylate, isohexyl (meth)acrylate, isoheptyl (meth)acrylate, isooctyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, cyclohexyl (meth)acrylate, t-butylcyclohexyl (meth)acrylate, etc.), aryl (meth)acrylate esters (e.g., phenyl (meth)acrylate, biphenyl (meth)acrylate, diphenylethyl (meth)acrylate, t-butylphenyl (meth)acrylate, terphenyl (meth)acrylate, etc.), dimethylaminoethyl (meth)acrylate, diethylaminoethyl (meth)acrylate, methoxyethyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, β-carboxyethyl (meth)acrylate, and (meth)acrylamide. The (meth)acrylic acid monomers may be used alone or in combination of two or more. Among these (meth)acrylic esters among the (meth)acrylic monomers, (meth)acrylic acid esters having an alkyl group with 2 to 14 carbon atoms (preferably 2 to 10 carbon atoms, more preferably 3 to 8 carbon atoms) are preferred from the viewpoint of fixability. Of these, n-butyl (meth)acrylate is preferred, and n-butyl acrylate is particularly preferred.

[0059] The copolymerization ratio of the styrene-based monomer to the (meth)acrylic monomer (based on mass, styrene-based monomer / (meth)acrylic monomer) is not particularly limited, but is preferably 85 / 15 to 70 / 30.

[0060] The styrene-acrylic resin may have a crosslinked structure. Preferred examples of the styrene-acrylic resin having a crosslinked structure include copolymers of at least a styrene-based monomer, a (meth)acrylic acid-based monomer, and a crosslinkable monomer.

[0061] Examples of the crosslinkable monomer include bifunctional or higher functional crosslinking agents. Examples of bifunctional crosslinking agents include divinylbenzene, divinylnaphthalene, di(meth)acrylate compounds (e.g., diethylene glycol di(meth)acrylate, methylene bis(meth)acrylamide, decanediol diacrylate, glycidyl (meth)acrylate, etc.), polyester-type di(meth)acrylate, 2-([1'-methylpropylideneamino]carboxyamino)ethyl methacrylate, etc. Examples of polyfunctional crosslinking agents include tri(meth)acrylate compounds (e.g., pentaerythritol tri(meth)acrylate, trimethylolethane tri(meth)acrylate, trimethylolpropane tri(meth)acrylate, etc.), tetra(meth)acrylate compounds (e.g., pentaerythritol tetra(meth)acrylate, oligoester (meth)acrylate, etc.), 2,2-bis(4-methacryloxy, polyethoxyphenyl)propane, diallyl phthalate, triallyl cyanurate, triallyl isocyanurate, triallyl trimellitate, diaryl chlorendate, etc. Among these, as the crosslinkable monomer, from the viewpoints of suppressing the occurrence of a decrease in image density and the occurrence of image density unevenness, and of fixability, a bifunctional or higher (meth)acrylate compound is preferred, a bifunctional (meth)acrylate compound is more preferred, a bifunctional (meth)acrylate compound having an alkylene group having from 6 to 20 carbon atoms is even more preferred, and a bifunctional (meth)acrylate compound having a linear alkylene group having from 6 to 20 carbon atoms is particularly preferred.

[0062] The copolymerization ratio of the crosslinkable monomer to the total monomers (based on mass, crosslinkable monomer / total monomers) is not particularly limited, but is preferably 2 / 1,000 to 20 / 1,000.

[0063] The method for producing the styrene-acrylic resin is not particularly limited, and various polymerization methods (e.g., solution polymerization, precipitation polymerization, suspension polymerization, bulk polymerization, emulsion polymerization, etc.) are applied. In addition, the polymerization reaction is carried out by a known operation (e.g., batchwise, semi-continuous, continuous, etc.).

[0064] The proportion of the styrene acrylic resin in the total binder resin is preferably 0% by mass or more and 20% by mass or less, more preferably 1% by mass or more and 15% by mass or less, and even more preferably 2% by mass or more and 10% by mass or less.

[0065] The proportion of the amorphous resin in the total binder resin is preferably 60% by mass or more and 98% by mass or less, more preferably 65% ​​by mass or more and 95% by mass or less, and even more preferably 70% by mass or more and 90% by mass or less.

[0066] The characteristics of the amorphous resin will be explained. The glass transition temperature (Tg) of the amorphous resin is preferably 50°C or higher and 80°C or lower, and more preferably 50°C or higher and 65°C or lower. The glass transition temperature is determined from a DSC curve obtained by differential scanning calorimetry (DSC), more specifically, from the "extrapolated glass transition onset temperature" described in JIS K 7121-1987 "Method for measuring transition temperatures of plastics."

[0067] The weight average molecular weight (Mw) of the amorphous resin is preferably 5,000 or more and 1,000,000 or less, and more preferably 7,000 or more and 500,000 or less. The number average molecular weight (Mn) of the amorphous resin is preferably 2,000 or more and 100,000 or less. The molecular weight distribution Mw / Mn of the amorphous resin is preferably 1.5 or more and 100 or less, and more preferably 2 or more and 60 or less. The weight-average molecular weight and number-average molecular weight are measured by gel permeation chromatography (GPC). Molecular weight measurements by GPC are performed using a Tosoh GPC HLC-8120GPC measuring device and a Tosoh TSKgel SuperHM-M (15 cm) column in THF solvent. The weight-average molecular weight and number-average molecular weight are calculated from the measurement results using a molecular weight calibration curve prepared with monodisperse polystyrene standard samples.

[0068] The crystalline resin will now be described. Examples of the crystalline resin include known crystalline resins such as crystalline polyester resins and crystalline vinyl resins (e.g., polyalkylene resins, long-chain alkyl (meth)acrylate resins, etc.) Among these, crystalline polyester resins are preferred from the viewpoint of suppressing density unevenness and white spots in the resulting image.

[0069] Examples of the crystalline polyester resin include a polycondensate of a polycarboxylic acid and a polyhydric alcohol. As the crystalline polyester resin, a commercially available product or a synthesized product may be used. The crystalline polyester resin is preferably a polycondensate using a straight-chain aliphatic polymerizable monomer rather than a polymerizable monomer having an aromatic ring, since it easily forms a crystalline structure.

[0070] Examples of polycarboxylic acids include aliphatic dicarboxylic acids (e.g., oxalic acid, succinic acid, glutaric acid, adipic acid, suberic acid, azelaic acid, sebacic acid, 1,9-nonanedicarboxylic acid, 1,10-decanedicarboxylic acid, 1,12-dodecanedicarboxylic acid, 1,14-tetradecanedicarboxylic acid, 1,18-octadecanedicarboxylic acid, etc.), aromatic dicarboxylic acids (e.g., dibasic acids such as phthalic acid, isophthalic acid, terephthalic acid, and naphthalene-2,6-dicarboxylic acid), anhydrides thereof, and lower alkyl esters thereof (e.g., having 1 to 5 carbon atoms). The polycarboxylic acid may be a tricarboxylic or higher carboxylic acid having a crosslinked or branched structure in combination with a dicarboxylic acid. Examples of the tricarboxylic acid include aromatic carboxylic acids (e.g., 1,2,3-benzenetricarboxylic acid, 1,2,4-benzenetricarboxylic acid, 1,2,4-naphthalenetricarboxylic acid, etc.), anhydrides thereof, and lower alkyl esters thereof (e.g., having 1 to 5 carbon atoms). As the polycarboxylic acid, a dicarboxylic acid having a sulfonic acid group and a dicarboxylic acid having an ethylenic double bond may be used in combination with these dicarboxylic acids. The polycarboxylic acids may be used alone or in combination of two or more.

[0071] Examples of polyhydric alcohols include aliphatic diols (for example, straight-chain aliphatic diols having 7 to 20 carbon atoms in the main chain). Examples of aliphatic diols include ethylene glycol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, 1,10-decanediol, 1,11-undecanediol, 1,12-dodecanediol, 1,13-tridecanediol, 1,14-tetradecanediol, 1,18-octadecanediol, and 1,14-eicosanedecanediol. Among these, 1,8-octanediol, 1,9-nonanediol, and 1,10-decanediol are preferred as aliphatic diols. The polyhydric alcohol may be a trihydric or higher alcohol having a crosslinked or branched structure, such as glycerin, trimethylolethane, trimethylolpropane, or pentaerythritol, in combination with the diol. The polyhydric alcohols may be used alone or in combination of two or more.

[0072] The polyhydric alcohol may have an aliphatic diol content of 80 mol % or more, preferably 90 mol % or more.

[0073] The melting temperature of the crystalline polyester resin is preferably 50°C or higher and 100°C or lower, more preferably 55°C or higher and 90°C or lower, and even more preferably 60°C or higher and 85°C or lower. The melting temperature of the crystalline polyester resin is determined from a DSC curve obtained by differential scanning calorimetry (DSC) using the "melting peak temperature" described in the method for determining the melting temperature in JIS K7121:1987 "Method for measuring transition temperatures of plastics."

[0074] The weight average molecular weight (Mw) of the crystalline polyester resin is preferably 6,000 or more and 35,000 or less.

[0075] The crystalline polyester resin can be obtained by a known production method, for example, in the same manner as the amorphous polyester resin.

[0076] As the crystalline polyester resin, a polymer of an α,ω-linear aliphatic dicarboxylic acid and an α,ω-linear aliphatic diol is preferred from the viewpoint of easily forming a crystalline structure and having good compatibility with amorphous polyester resins, thereby improving image fixability.

[0077] The α,ω-linear aliphatic dicarboxylic acid is preferably an α,ω-linear aliphatic dicarboxylic acid in which the alkylene group connecting the two carboxy groups has 3 to 14 carbon atoms, more preferably 4 to 12 carbon atoms, and even more preferably 6 to 10 carbon atoms. Examples of the α,ω-linear aliphatic dicarboxylic acid include succinic acid, glutaric acid, adipic acid, 1,6-hexanedicarboxylic acid (commonly known as suberic acid), 1,7-heptanedicarboxylic acid (commonly known as azelaic acid), 1,8-octanedicarboxylic acid (commonly known as sebacic acid), 1,9-nonanedicarboxylic acid, 1,10-decanedicarboxylic acid, 1,12-dodecanedicarboxylic acid, 1,14-tetradecanedicarboxylic acid, and 1,18-octadecanedicarboxylic acid. Of these, 1,6-hexanedicarboxylic acid, 1,7-heptanedicarboxylic acid, 1,8-octanedicarboxylic acid, and 1,10-decanedicarboxylic acid are preferred. The α,ω-linear aliphatic dicarboxylic acids may be used alone or in combination of two or more.

[0078] The α,ω-linear aliphatic diol is preferably an α,ω-linear aliphatic diol in which the alkylene group connecting the two hydroxy groups has 3 to 14 carbon atoms, more preferably 4 to 12 carbon atoms, and even more preferably 6 to 10 carbon atoms. Examples of the α,ω-linear aliphatic diol include ethylene glycol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, 1,10-decanediol, 1,12-dodecanediol, 1,14-tetradecanediol, and 1,18-octadecanediol. Of these, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, and 1,10-decanediol are preferred. The α,ω-linear aliphatic diols may be used alone or in combination of two or more.

[0079] As the polymer of an α,ω-linear aliphatic dicarboxylic acid and an α,ω-linear aliphatic diol, from the viewpoint of easily forming a crystalline structure and having good compatibility with amorphous polyester resins, thereby improving image fixability, a polymer of at least one selected from the group consisting of 1,6-hexanedicarboxylic acid, 1,7-heptanedicarboxylic acid, 1,8-octanedicarboxylic acid, 1,9-nonanedicarboxylic acid, and 1,10-decanedicarboxylic acid and at least one selected from the group consisting of 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, and 1,10-decanediol is preferred, and among these, a polymer of 1,10-decanedicarboxylic acid and 1,6-hexanediol is more preferred.

[0080] The proportion of the crystalline resin in the total binder resin is preferably 1% by mass or more and 20% by mass or less, more preferably 2% by mass or more and 15% by mass or less, and even more preferably 3% by mass or more and 10% by mass or less.

[0081] Other binder resins Examples of binder resins include homopolymers of monomers such as ethylenically unsaturated nitriles (e.g., acrylonitrile, methacrylonitrile, etc.), vinyl ethers (e.g., vinyl methyl ether, vinyl isobutyl ether, etc.), vinyl ketones (e.g., vinyl methyl ketone, vinyl ethyl ketone, vinyl isopropenyl ketone, etc.), and olefins (e.g., ethylene, propylene, butadiene, etc.), and copolymers of two or more of these monomers in combination. Other examples of the binder resin include non-vinyl resins such as epoxy resins, polyurethane resins, polyamide resins, cellulose resins, polyether resins, and modified rosin, mixtures of these with the vinyl resins, and graft polymers obtained by polymerizing vinyl monomers in the presence of these. These binder resins may be used alone or in combination of two or more.

[0082] The content of the binder resin is preferably 40% by mass to 95% by mass, more preferably 50% by mass to 90% by mass, and even more preferably 60% by mass to 85% by mass, based on the total mass of the toner particles.

[0083] -Mold release agent- In the aggregation step, the dispersion preferably further contains release agent particles. Examples of release agents include hydrocarbon waxes, natural waxes such as carnauba wax, rice wax, and candelilla wax, synthetic or mineral / petroleum waxes such as montan wax, and ester waxes such as fatty acid esters and montanic acid esters, but are not limited thereto.

[0084] As the release agent, from the viewpoints of suppressing uneven density and white spots in the obtained image and having good compatibility with the amorphous polyester resin, thereby improving the fixability of the image, ester wax is preferred, and ester wax of a higher fatty acid having from 10 to 30 carbon atoms and a monovalent or polyvalent alcohol component having from 1 to 30 carbon atoms is more preferred.

[0085] The ester wax is a wax having an ester bond. The ester wax may be any of a monoester, diester, triester, and tetraester, and any known natural or synthetic ester wax can be used. Examples of ester waxes include ester compounds of higher fatty acids (such as fatty acids having 10 or more carbon atoms) and monohydric or polyhydric aliphatic alcohols (such as aliphatic alcohols having 8 or more carbon atoms), and have a melting temperature of 60°C or higher and 110°C or lower (preferably 65°C or higher and 100°C or lower, more preferably 70°C or higher and 95°C or lower). Examples of ester waxes include ester compounds of higher fatty acids (caprylic acid, capric acid, lauric acid, myristic acid, palmitic acid, stearic acid, arachidic acid, behenic acid, oleic acid, etc.) with alcohols (monohydric alcohols such as methanol, ethanol, propanol, isopropanol, butanol, capryl alcohol, lauryl alcohol, myristyl alcohol, cetyl alcohol, stearyl alcohol, and oleyl alcohol; and polyhydric alcohols such as glycerin, ethylene glycol, propylene glycol, sorbitol, and pentaerythritol). Specific examples include carnauba wax, rice wax, candelilla wax, jojoba oil, Japan wax, beeswax, privet wax, lanolin, and montan acid ester wax.

[0086] The melting temperature of the release agent is preferably 50°C or higher and 110°C or lower, and more preferably 60°C or higher and 100°C or lower. The melting temperature of the release agent is determined from a DSC curve obtained by differential scanning calorimetry (DSC) by using the "melting peak temperature" described in the method for determining the melting temperature in JIS K7121:1987 "Method for measuring transition temperatures of plastics."

[0087] The content of the release agent is preferably from 1% by mass to 20% by mass, and more preferably from 5% by mass to 15% by mass, based on the total mass of the toner particles.

[0088] -Coloring agent- In the aggregating step, the dispersion preferably further contains colorant particles. Examples of colorants include carbon black, chrome yellow, Hansa Yellow, benzidine yellow, threne yellow, quinoline yellow, pigment yellow, permanent orange GTR, pyrazolone orange, Balkan orange, watch young red, permanent red, brilliant carmine 3B, brilliant carmine 6B, DuPont oil red, pyrazolone red, lithol red, rhodamine B lake, lake red C, pigment red, rose bengal, aniline blue, ultramarine blue, and the like. Examples of the dye include various pigments such as phosphorus blue, chalco oil blue, methylene blue chloride, phthalocyanine blue, pigment blue, phthalocyanine green, and malachite green oxalate, and various dyes such as acridine-based, xanthene-based, azo-based, benzoquinone-based, azine-based, anthraquinone-based, thioindigo-based, dioxazine-based, thiazine-based, azomethine-based, indigo-based, phthalocyanine-based, aniline black-based, polymethine-based, triphenylmethane-based, diphenylmethane-based, and thiazole-based dyes. The colorant may be used alone or in combination of two or more kinds.

[0089] The colorant may be surface-treated as needed, or may be used in combination with a dispersant. Furthermore, a plurality of colorants may be used in combination.

[0090] The content of the colorant is, for example, preferably 1% by mass or more and 30% by mass or less, and more preferably 3% by mass or more and 15% by mass or less, based on the total mass of the toner particles.

[0091] -Other additives- Examples of other additives include well-known additives such as magnetic materials, charge control agents, inorganic powders, etc. These additives are contained in the toner particles as internal additives.

[0092] -Characteristics of toner particles, etc.- The toner particles may be toner particles having a single layer structure, or may be toner particles having a so-called core-shell structure (core-shell type particles) composed of a core (core particle) and a coating layer (shell layer) that coats the core. The toner particles having a core-shell structure are composed of, for example, a core containing a binder resin and, if necessary, a colorant and a release agent, and the like, and a coating layer containing a binder resin. Among these, the toner particles are preferably core-shell type particles from the viewpoints of low-temperature fixability and suppression of color streaks.

[0093] Volume average particle size of toner (D 50v ) is preferably 2 μm or more and 10 μm or less, and more preferably 4 μm or more and 8 μm or less.

[0094] The volume average particle size of the toner is measured using a Coulter Multisizer II (manufactured by Beckman Coulter), and the electrolyte is measured using an ISOTON-II (manufactured by Beckman Coulter). For the measurement, 0.5 mg to 50 mg of the measurement sample is added to 2 mL of a 5 mass % aqueous solution of a surfactant (preferably sodium alkylbenzene sulfonate) as a dispersant, and this is then added to 100 mL to 150 mL of the electrolyte. The electrolyte solution containing the suspended sample is dispersed in an ultrasonic disperser for 1 minute, and the particle size of each particle in the range of 2 μm to 60 μm is measured using a Coulter Multisizer II with an aperture diameter of 100 μm. The number of particles sampled is 50,000. The particle size measured is plotted from the smallest diameter side to the cumulative distribution on a volume basis, and the particle size at which the cumulative 50% is reached is called the volume average particle size D 50v It is defined as:

[0095] In this embodiment, the average circularity of the toner particles is not particularly limited, but from the viewpoint of improving the cleaning properties of the toner from the image carrier, it is preferably 0.91 or more and 0.98 or less, more preferably 0.94 or more and 0.98 or less, and even more preferably 0.95 or more and 0.97 or less.

[0096] In this embodiment, the circularity of a toner particle is (the perimeter of a circle having the same area as the projected image of the particle) divided by (the perimeter of the projected image of the particle), and the average circularity of a toner particle is the cumulative circularity that is 50% from the smallest side in the circularity distribution. The average circularity of a toner particle is determined by analyzing at least 3,000 toner particles using a flow-type particle image analyzer.

[0097] The average circularity of the toner particles can be controlled, for example, by adjusting the stirring speed of the dispersion, the temperature of the dispersion, or the retention time during the coalescence process.

[0098] <External additives> The toner produced by the method for producing a toner for developing electrostatic images according to this embodiment may contain an external additive, if necessary. The toner produced by the method for producing a toner for developing electrostatic images according to this embodiment may be toner particles that do not contain external additives, or toner particles to which external additives have been added. Examples of the external additive include inorganic particles, such as SiO2, TiO2, Al2O3, CuO, ZnO, SnO2, CeO2, Fe2O3, MgO, BaO, CaO, K2O, Na2O, ZrO2, CaO·SiO2, and K2O·(TiO2). n , Al2O3·2SiO2, CaCO3, MgCO3, BaSO4, MgSO4, etc.

[0099] The surfaces of inorganic particles as external additives are preferably subjected to a hydrophobic treatment. The hydrophobic treatment is carried out, for example, by immersing the inorganic particles in a hydrophobic treatment agent. The hydrophobic treatment agent is not particularly limited, and examples thereof include silane coupling agents, silicone oils, titanate coupling agents, and aluminum coupling agents. These may be used alone or in combination of two or more. The amount of the hydrophobic treatment agent is preferably, for example, 1 part by mass or more and 10 parts by mass or less per 100 parts by mass of the inorganic particles.

[0100] Examples of external additives include resin particles (resin particles such as polystyrene, polymethyl methacrylate (PMMA), and melamine resin), cleaning agents (for example, metal salts of higher fatty acids such as zinc stearate, and particles of fluorine-based polymers).

[0101] In the present embodiment, the external additive is preferably inorganic oxide particles, and specifically, particles of any one of titanium oxide (TiO2), silicon dioxide (SiO2), and alumina (Al2O3) are preferred.

[0102] The amount of the external additive added is, for example, preferably 0.01% by mass to 10% by mass, more preferably 0.01% by mass to 6% by mass, based on the toner particles.

[0103] <Electrostatic image developer> The electrostatic image developer according to this embodiment contains at least the toner produced by the method for producing the electrostatic image developing toner according to this embodiment. The electrostatic image developer according to the present embodiment may be a one-component developer containing only the toner produced by the method for producing a toner for developing electrostatic images according to the present embodiment, or may be a two-component developer containing a mixture of the toner and a carrier.

[0104] The carrier is not particularly limited, and examples thereof include known carriers, such as coated carriers in which the surface of a core material made of magnetic powder is coated with a coating resin, magnetic powder dispersion carriers in which magnetic powder is dispersed and blended in a matrix resin, and resin-impregnated carriers in which porous magnetic powder is impregnated with a resin. The magnetic powder dispersion type carrier and the resin impregnated type carrier may be a carrier in which the constituent particles of the carrier are used as a core material and are coated with a coating resin.

[0105] Examples of magnetic powder include magnetic metals such as iron, nickel, and cobalt, and magnetic oxides such as ferrite and magnetite.

[0106] Examples of coating resins and matrix resins include polyethylene, polypropylene, polystyrene, polyvinyl acetate, polyvinyl alcohol, polyvinyl butyral, polyvinyl chloride, polyvinyl ether, polyvinyl ketone, vinyl chloride-vinyl acetate copolymer, styrene-acrylic acid ester copolymer, straight silicone resins containing organosiloxane bonds or modified products thereof, fluororesins, polyesters, polycarbonates, phenolic resins, and epoxy resins. The coating resin and the matrix resin may contain other additives such as conductive particles. Examples of conductive particles include particles of metals such as gold, silver, and copper, carbon black, titanium oxide, zinc oxide, tin oxide, barium sulfate, aluminum borate, and potassium titanate.

[0107] Here, the method of coating the surface of the core material with a coating resin includes a method of coating with a solution for forming a coating layer in which the coating resin and, if necessary, various additives are dissolved in an appropriate solvent. The solvent is not particularly limited and may be selected taking into consideration the coating resin to be used, its applicability, etc. Specific resin coating methods include an immersion method in which the core material is immersed in a solution for forming a coating layer, a spray method in which the solution for forming a coating layer is sprayed onto the surface of the core material, a fluidized bed method in which the solution for forming a coating layer is sprayed onto the core material while it is suspended in flowing air, and a kneader coater method in which the core material of the carrier and the solution for forming a coating layer are mixed in a kneader coater and the solvent is removed.

[0108] In the two-component developer, the mixing ratio (mass ratio) of toner to carrier is preferably toner:carrier=1:100 to 30:100, and more preferably 3:100 to 20:100.

[0109] <Image forming device / image forming method> An image forming apparatus and an image forming method according to this embodiment will be described. The image forming apparatus according to the present embodiment includes an image carrier, a charging unit that charges the surface of the image carrier, an electrostatic image forming unit that forms an electrostatic image on the surface of the charged image carrier, a developing unit that contains an electrostatic image developer and develops the electrostatic image formed on the surface of the image carrier as a toner image using the electrostatic image developer, a transfer unit that transfers the toner image formed on the surface of the image carrier to the surface of a recording medium, and a fixing unit that fixes the toner image transferred to the surface of the recording medium. The electrostatic image developer according to the present embodiment is used as the electrostatic image developer.

[0110] The image forming apparatus according to this embodiment carries out an image forming method (the image forming method according to this embodiment) that includes a charging step of charging the surface of an image carrier, an electrostatic image forming step of forming an electrostatic image on the surface of the charged image carrier, a developing step of developing the electrostatic image formed on the surface of the image carrier as a toner image using the electrostatic image developer according to this embodiment, a transfer step of transferring the toner image formed on the surface of the image carrier to the surface of a recording medium, and a fixing step of fixing the toner image transferred to the surface of the recording medium.

[0111] The image forming apparatus according to the present embodiment may be any of known image forming apparatuses, such as a direct transfer type apparatus that directly transfers a toner image formed on the surface of an image carrier to a recording medium; an intermediate transfer type apparatus that primarily transfers a toner image formed on the surface of an image carrier to the surface of an intermediate transfer medium, and then secondarily transfers the toner image transferred to the surface of the intermediate transfer medium to the surface of a recording medium; an apparatus equipped with a cleaning means that cleans the surface of the image carrier after the transfer of the toner image but before charging; and an apparatus equipped with a discharging means that irradiates the surface of the image carrier with discharging light to discharge it after the transfer of the toner image but before charging. Among these, an image forming apparatus equipped with a cleaning means for cleaning the surface of the image carrier is preferred, and a cleaning blade is preferred as the cleaning means. In the case of an intermediate transfer type device, the transfer means is configured to have, for example, an intermediate transfer body onto whose surface a toner image is transferred, a primary transfer means which primarily transfers the toner image formed on the surface of the image carrier onto the surface of the intermediate transfer body, and a secondary transfer means which secondarily transfers the toner image transferred onto the surface of the intermediate transfer body onto the surface of the recording medium.

[0112] In the image forming apparatus according to the present embodiment, for example, a portion including the developing means may have a cartridge structure (process cartridge) that is detachably attached to the image forming apparatus. As the process cartridge, for example, a process cartridge equipped with developing means that accommodates the electrostatic image developer according to the present embodiment is preferably used.

[0113] An example of an image forming apparatus according to the present embodiment will be described below, but the present invention is not limited to this. Note that only the main parts shown in the drawings will be described, and descriptions of other parts will be omitted.

[0114] FIG. 1 is a schematic diagram showing the configuration of an image forming apparatus according to this embodiment. The image forming apparatus shown in Figure 1 includes first through fourth electrophotographic image forming units 10Y, 10M, 10C, and 10K (image forming means) that output images in the colors yellow (Y), magenta (M), cyan (C), and black (K) based on color-separated image data. These image forming units (hereinafter sometimes simply referred to as "units") 10Y, 10M, 10C, and 10K are arranged side by side horizontally spaced a predetermined distance apart from one another. Note that these units 10Y, 10M, 10C, and 10K may also be process cartridges that are detachable from the image forming apparatus.

[0115] Above each of the units 10Y, 10M, 10C, and 10K in the drawing, an intermediate transfer belt 20 serving as an intermediate transfer body extends through each unit. The intermediate transfer belt 20 is wound around a drive roll 22 and a support roll 24 that are spaced apart from each other and arranged from left to right in the drawing, and is configured to run in a direction from the first unit 10Y to the fourth unit 10K. A force is applied to the support roll 24 in a direction away from the drive roll 22 by a spring or the like (not shown), thereby applying tension to the intermediate transfer belt 20 wound around them. In addition, an intermediate transfer body cleaning device 30 is provided on the image carrier side of the intermediate transfer belt 20, facing the drive roll 22. In addition, the developing devices (developing means) 4Y, 4M, 4C, and 4K of the units 10Y, 10M, 10C, and 10K are supplied with toner including four colors of toner, yellow, magenta, cyan, and black, contained in toner cartridges 8Y, 8M, 8C, and 8K, respectively.

[0116] Since the first to fourth units 10Y, 10M, 10C, and 10K have the same configuration, the first unit 10Y, which forms a yellow image and is disposed upstream in the direction of travel of the intermediate transfer belt, will be described here as a representative. Note that parts equivalent to those of the first unit 10Y are given reference numerals with magenta (M), cyan (C), and black (K) instead of yellow (Y), and descriptions of the second to fourth units 10M, 10C, and 10K will be omitted.

[0117] The first unit 10Y has a photoreceptor 1Y that acts as an image carrier. Around the photoreceptor 1Y, there are arranged in this order: a charging roll (an example of a charging means) 2Y that charges the surface of the photoreceptor 1Y to a predetermined potential; an exposure device (an example of an electrostatic image forming means) 3 that exposes the charged surface to a laser beam 3Y based on a color-separated image signal to form an electrostatic image; a developing device (an example of a developing means) 4Y that supplies charged toner to the electrostatic image to develop it; a primary transfer roll 5Y (an example of a primary transfer means) that transfers the developed toner image onto an intermediate transfer belt 20; and a photoreceptor cleaning device (an example of a cleaning means) 6Y that removes toner remaining on the surface of the photoreceptor 1Y after the primary transfer. The primary transfer roll 5Y is disposed inside the intermediate transfer belt 20 and is positioned opposite the photoreceptor 1Y. Furthermore, a bias power supply (not shown) that applies a primary transfer bias is connected to each of the primary transfer rolls 5Y, 5M, 5C, and 5K. Each bias power supply varies the transfer bias applied to each primary transfer roll under the control of a control unit (not shown).

[0118] The operation of forming a yellow image in first unit 10Y will be described below. First, prior to operation, the surface of the photosensitive member 1Y is charged to a potential of −600V to −800V by the charging roll 2Y. The photoconductor 1Y has conductivity (for example, volume resistivity at 20°C: 1×10 -6 The photosensitive layer is formed by laminating a photosensitive layer on a substrate with a resistivity of Ωcm or less. This photosensitive layer normally has a high resistance (the resistance of ordinary resins), but when irradiated with a laser beam 3Y, the resistivity of the irradiated portion changes. Therefore, a laser beam 3Y is output to the charged surface of the photosensitive element 1Y via an exposure device 3 in accordance with image data for yellow sent from a control unit (not shown). The laser beam 3Y is irradiated onto the photosensitive layer on the surface of the photosensitive element 1Y, thereby forming an electrostatic charge image of a yellow image pattern on the surface of the photosensitive element 1Y.

[0119] An electrostatic image is an image formed on the surface of the photosensitive element 1Y by charging it; the laser beam 3Y reduces the resistivity of the irradiated portion of the photosensitive layer, causing the charged charges on the surface of the photosensitive element 1Y to flow, while the charges remain in the portions not irradiated by the laser beam 3Y, forming a so-called negative latent image. The electrostatic image formed on the photoreceptor 1Y is rotated to a predetermined development position as the photoreceptor 1Y travels. At this development position, the electrostatic image on the photoreceptor 1Y is made visible as a toner image (developed image) by the developing device 4Y.

[0120] The developing device 4Y contains an electrostatic image developer containing, for example, at least yellow toner and a carrier. The yellow toner is frictionally charged by being stirred inside the developing device 4Y, and is held on a developer roll (an example of a developer holder) with a charge of the same polarity (negative polarity) as the charge on the photoreceptor 1Y. As the surface of the photoreceptor 1Y passes through the developing device 4Y, the yellow toner electrostatically adheres to the discharged latent image portion on the surface of the photoreceptor 1Y, and the latent image is developed with the yellow toner. The photoreceptor 1Y on which the yellow toner image has been formed continues to travel at a predetermined speed, and the toner image developed on the photoreceptor 1Y is transported to a predetermined primary transfer position.

[0121] When the yellow toner image on the photoreceptor 1Y is transported to the primary transfer, a primary transfer bias is applied to the primary transfer roll 5Y, and an electrostatic force from the photoreceptor 1Y to the primary transfer roll 5Y acts on the toner image, causing the toner image on the photoreceptor 1Y to be transferred onto the intermediate transfer belt 20. The transfer bias applied at this time has a (+) polarity opposite to the (-) polarity of the toner, and in the first unit 10Y, for example, it is controlled to +10 μA by a control unit (not shown). On the other hand, the toner remaining on the photoreceptor 1Y is removed and collected by the photoreceptor cleaning device 6Y.

[0122] Furthermore, the primary transfer bias applied to the primary transfer rolls 5M, 5C, and 5K of the second unit 10M and subsequent units is also controlled in accordance with the first unit. In this way, the intermediate transfer belt 20 onto which the yellow toner image has been transferred by the first unit 10Y is conveyed sequentially through the second to fourth units 10M, 10C, and 10K, and the toner images of each color are transferred onto the intermediate transfer belt 20 in a superimposed manner.

[0123] The intermediate transfer belt 20, onto which the four-color toner images have been multiplex-transferred through the first to fourth units, reaches a secondary transfer section composed of the intermediate transfer belt 20, a support roll 24 in contact with the inner surface of the intermediate transfer belt, and a secondary transfer roll (an example of a secondary transfer means) 26 arranged on the image bearing surface side of the intermediate transfer belt 20. Meanwhile, recording paper (an example of a recording medium) P is fed via a supply mechanism into the gap between the secondary transfer roll 26 and the intermediate transfer belt 20 at a predetermined timing, and a secondary transfer bias is applied to the support roll 24. The transfer bias applied at this time has a negative polarity, the same as the negative polarity of the toner. Electrostatic force from the intermediate transfer belt 20 toward the recording paper P acts on the toner image, transferring the toner image on the intermediate transfer belt 20 onto the recording paper P. The secondary transfer bias at this time is determined according to resistance detected by resistance detection means (not shown) that detects resistance in the secondary transfer section, and is voltage-controlled.

[0124] Thereafter, the recording paper P is sent to the pressure contact portion (nip portion) of a pair of fixing rolls in a fixing device (an example of fixing means) 28, where the toner image is fixed onto the recording paper P, forming a fixed image.

[0125] Examples of the recording paper P onto which the toner image is transferred include plain paper used in electrophotographic copying machines, printers, etc. In addition to the recording paper P, examples of the recording medium include overhead projector sheets and the like. To further improve the smoothness of the image surface after fixing, it is preferable that the surface of the recording paper P is also smooth. For example, coated paper in which the surface of plain paper is coated with resin or the like, or art paper for printing, etc., is preferably used.

[0126] The recording paper P on which the color image has been fixed is conveyed toward the discharge section, and the series of color image forming operations is completed.

[0127] <Process cartridges / toner cartridges> The process cartridge according to this embodiment will be described. The process cartridge according to this embodiment is a process cartridge that is detachably attached to an image forming apparatus and that contains the electrostatic image developer according to this embodiment and is equipped with a developing means that develops an electrostatic image formed on the surface of an image carrier using the electrostatic image developer into a toner image.

[0128] The process cartridge according to this embodiment is not limited to the above configuration, but may also be configured to include a developing device and, if necessary, at least one other means selected from an image carrier, a charging means, an electrostatic image forming means, and a transfer means.

[0129] An example of a process cartridge according to the present embodiment will be described below, but the present invention is not limited to this. Note that only the main parts shown in the drawings will be described, and descriptions of other parts will be omitted.

[0130] FIG. 2 is a schematic diagram showing the configuration of the process cartridge according to the present embodiment. The process cartridge 200 shown in FIG. 2 is configured to integrally combine and hold a photosensitive member 107 (an example of an image carrier), a charging roll 108 (an example of a charging means) provided around the photosensitive member 107, a developing device 111 (an example of a developing means), and a photosensitive member cleaning device 113 (an example of a cleaning means), which are held by a housing 117 provided with, for example, mounting rails 116 and an opening 118 for exposure, and is made into a cartridge. In FIG. 2, 109 denotes an exposure device (an example of an electrostatic image forming means), 112 denotes a transfer device (an example of a transfer means), 115 denotes a fixing device (an example of a fixing means), and 300 denotes recording paper (an example of a recording medium).

[0131] Next, the toner cartridge according to this embodiment will be described. The toner cartridge according to the present embodiment is a toner cartridge that contains the toner according to the present embodiment and is detachably attached to an image forming apparatus. The toner cartridge contains replenishment toner to be supplied to a developing unit provided in the image forming apparatus.

[0132] 1 is an image forming apparatus having a configuration in which toner cartridges 8Y, 8M, 8C, and 8K can be attached and detached, and developing devices 4Y, 4M, 4C, and 4K are connected to the toner cartridges corresponding to each developing device (color) by toner supply pipes (not shown). When the toner stored in a toner cartridge runs low, the toner cartridge is replaced. [Example]

[0133] Hereinafter, the present embodiment will be described in more detail with reference to examples and comparative examples, but the present embodiment is not limited to these examples. Note that "parts" and "%" indicating amounts are based on mass unless otherwise specified.

[0134] <Preparation of particle dispersions, etc.> [Preparation of Black Particle Dispersion (1)] Carbon black (Cabot, Regal 1330): 50 parts Ionic surfactant Neogen RK (manufactured by Daiichi Kogyo Seiyaku Co., Ltd.): 10 parts Ion-exchanged water: 192.9 parts The above components were mixed and treated for 10 minutes at 240 MPa using an Ultimizer (manufactured by Sugino Machine Co., Ltd.) to prepare a black colored particle dispersion (solid content concentration: 20% by mass).

[0135] [Preparation of amorphous polyester resin dispersion (1)] Terephthalic acid: 70 parts Fumaric acid: 30 parts Ethylene glycol: 44 parts 1,5-pentanediol: 47 parts The above materials were placed in a flask equipped with a stirrer, nitrogen inlet tube, temperature sensor, and distillation column. The temperature was raised to 220°C over 1 hour under a nitrogen gas stream, and 1 part of dibutyltin oxide was added for every 100 parts of the above materials. The temperature was raised to 240°C over 0.5 hours while distilling off the resulting water. The dehydration condensation reaction was continued at this temperature for 1 hour, and then the reaction mixture was cooled. In this way, a polyester resin with a weight-average molecular weight of 95,000 and a glass transition temperature of 62°C was synthesized. 40 parts of ethyl acetate and 25 parts of 2-butanol were added to a vessel equipped with a temperature control device and nitrogen substitution device to prepare a mixed solvent. 100 parts of polyester resin were then gradually added and dissolved. A 10% by mass aqueous ammonia solution (equivalent to three times the molar amount of the acid value of the resin) was then added and stirred for 30 minutes. Next, the atmosphere inside the container was replaced with dry nitrogen, the temperature was maintained at 40°C, and 400 parts of ion-exchanged water was added dropwise at a rate of 2 parts / min while stirring the mixture, thereby emulsifying it. After the addition was completed, the emulsion was returned to 25°C, and a resin particle dispersion in which resin particles having a volume average particle size of 200 nm were dispersed was obtained. Ion-exchanged water was added to the resin particle dispersion to adjust the solid content to 20 mass% to obtain amorphous polyester resin dispersion (A1).

[0136] [Preparation of Crystalline Polyester Resin Dispersion (D1)] Dimethyl sebacate: 97 parts Sodium dimethyl isophthalate-5-sulfonate: 3 parts Ethylene glycol: 100 parts Dibutyltin oxide (catalyst): 0.3 parts by mass The above components were placed in a heated and dried three-neck flask, and the air inside the vessel was evacuated to an inert atmosphere with nitrogen gas. The mixture was then mechanically stirred and refluxed at 180°C for 5 hours. The temperature was then gradually increased to 230°C under reduced pressure and stirred for 2 hours. When the mixture reached a viscous state, it was air-cooled to terminate the reaction, yielding crystalline polyester resin B1. Molecular weight measurement (polystyrene equivalent) revealed that the weight-average molecular weight (Mw) of the resulting crystalline polyester resin B1 was 9,700 and the melting temperature was 84°C. 90 parts by mass of the resulting crystalline polyester resin B1, 1.8 parts by mass of the ionic surfactant NEOGEN RK (manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd.), and 210 parts by mass of ion-exchanged water were heated to 100°C and dispersed using an Ultra-Turrax T50 (manufactured by IKA). The mixture was then dispersed for 1 hour using a pressure-discharge Gaulin homogenizer to obtain crystalline polyester resin dispersion (D1) with a volume average particle size of 200 nm and a solids content of 20 parts by mass.

[0137] [Preparation of crystalline polyester resin dispersion (D2)] 1,10-decanedicarboxylic acid: 260 parts 1,6-Hexanediol: 167 parts Dibutyltin oxide (catalyst): 0.3 parts The above materials were placed in a heated and dried three-neck flask. The air in the flask was replaced with nitrogen gas to create an inert atmosphere, and the mixture was stirred and refluxed at 180°C for 5 hours using mechanical stirring. The temperature was then gradually increased to 230°C under reduced pressure and stirred for 2 hours. When the mixture reached a viscous state, it was air-cooled to terminate the reaction. This resulted in a crystalline polyester resin with a weight-average molecular weight of 12,600 and a melting temperature of 73°C. 90 parts of the crystalline polyester resin, 1.8 parts of anionic surfactant (TaycaPower, manufactured by Tayca Corporation), and 210 parts of ion-exchanged water were mixed, heated to 120°C, and dispersed using a homogenizer (IKA Ultra-Turrax T50). This was followed by a dispersion treatment using a pressure-discharge Gaulin homogenizer for 1 hour, resulting in a resin particle dispersion containing resin particles with a volume average particle size of 160 nm. Ion-exchanged water was added to this resin particle dispersion to adjust the solids content to 20%, yielding crystalline polyester resin particle dispersion (D2).

[0138] [Preparation of Release Agent Particle Dispersion (W1)] Paraffin wax (Nippon Seiro Co., Ltd., HNP-9): 100 parts Anionic surfactant (Dai-ichi Kogyo Seiyaku Co., Ltd., Neogen RK): 1 part Ion-exchanged water: 350 parts The above materials were mixed and heated to 100°C, dispersed using a homogenizer (Ultra Turrax T50 manufactured by IKA), and then dispersed using a Manton-Gaulin high-pressure homogenizer (manufactured by Gaulin). This gave a release agent particle dispersion (W1) (solid content 20% by mass) in which release agent particles with a volume average particle size of 200 nm were dispersed.

[0139] [Preparation of Release Agent Particle Dispersion (W2)] Paraffin wax (Nippon Seiro Co., Ltd., FNP92, melting point 92°C): 100 parts Anionic surfactant (Tayca Power, manufactured by Tayca Corporation): 1 part Ion-exchanged water: 350 parts The above materials were mixed and heated to 100°C, dispersed using a homogenizer (Ultra Turrax T50 manufactured by IKA), and then dispersed using a Manton-Gaulin high-pressure homogenizer (manufactured by Gaulin). This gave a release agent particle dispersion (W2) (solid content 20% by mass) in which release agent particles with a volume average particle size of 220 nm were dispersed.

[0140] [Preparation of Carrier] 500 parts of spherical magnetite powder particles (volume average particle diameter: 0.55 μm) were thoroughly stirred in a Henschel mixer, and then 5.0 parts of a titanate-based coupling agent were added. The mixture was heated to 100°C and mixed and stirred for 30 minutes to obtain spherical magnetite particles coated with a titanate-based coupling agent. Next, 6.25 parts of phenol, 9.25 parts of 35% by weight formalin, 500 parts of the titanate-based coupling agent-coated spherical magnetite particles, 6.25 parts of 25% by weight ammonia water, and 425 parts of water were added to a four-neck flask and mixed and stirred. The mixture was then reacted at 85°C for 120 minutes with stirring, cooled to 25°C, 500 parts of water was added, the supernatant liquid was removed, and the precipitate was washed with water. This was then dried under reduced pressure at 150°C to 180°C to obtain a carrier with a volume average particle size of 35 μm.

[0141] Example 1 [Preparation of Toner and Developer] Ion-exchanged water: 200 parts Amorphous polyester resin dispersion (A1): 150 parts Crystalline polyester resin dispersion (B1): 10 parts Black colored particle dispersion: 15 parts Release agent particle dispersion: 10 parts Anionic surfactant (Tayca Power, manufactured by Tayca Corporation): 2.8 parts The above materials were placed in a round stainless steel flask, and 0.1 N (0.1 mol / L) nitric acid was added to adjust the pH to 3.5. An aluminum sulfate (Al2(SO4)3) aqueous solution prepared by dissolving 2.0 parts of aluminum sulfate in 30 parts of ion-exchanged water was then added. The mixture was dispersed at 30°C using a homogenizer (Ultra-Turrax T50, manufactured by IKA Corporation), then heated to 45°C in a heating oil bath and maintained at that temperature until the volume average particle size reached 4.8 μm. Subsequently, 60 parts of amorphous polyester resin particle dispersion (A1) were added and maintained for 30 minutes. When the volume average particle size reached 5.2 μm, another 60 parts of amorphous polyester resin particle dispersion (A1) were added and maintained for 30 minutes. Subsequently, 20 parts of a 10% by weight NTA (nitrilotriacetic acid) metal salt aqueous solution (Chilest 70, manufactured by Chelest Corporation) was added, and the pH was adjusted to 9.0 using 1 N (1 mol / L) sodium hydroxide aqueous solution. Next, 1.0 parts of anionic surfactant (TaycaPower) was added, and the mixture was heated to 85°C while continuing to stir, and maintained at that temperature for 5 hours. It was then cooled to 20°C at a rate of 20°C / min. Within 60 minutes after cooling, the pH was adjusted to 9.5 using a 1N aqueous sodium hydroxide solution. After adjusting the pH, the mixture was filtered, thoroughly washed with ion-exchanged water, and dried to obtain toner particles (1) with a volume average particle size of 5.9 μm and an average circularity of 0.97.

[0142] 100 parts of the toner particles (1) and 1.5 parts of hydrophobic silica (RY50, manufactured by Nippon Aerosil Co., Ltd.) were mixed and mixed using a sample mill at a rotation speed of 10,000 rpm for 30 seconds. The mixture was sieved using a vibrating sieve with 45 μm openings to obtain a toner.

[0143] Examples 2 and 3 Toners and developers of each example were prepared in the same manner as in Example 1, except that the step of adding the 1N aqueous sodium hydroxide solution was changed as shown in Table 1.

[0144] Example 4 A toner and a developer were prepared in the same manner as in Example 1, except that the volume average particle diameter after drying was changed from 5.9 μm to 4.8 μm.

[0145] Example 5 A toner and a developer were prepared in the same manner as in Example 1, except that the 10% by mass NTA (nitrilotriacetic acid) metal salt aqueous solution (Chilest 70, manufactured by Chelest Co., Ltd.) was replaced with a chelating agent (3-hydroxy-2,2'-iminodisuccinic acid tetrasodium salt (HIDS), manufactured by Nippon Shokubai Co., Ltd.).

[0146] Example 6 A toner and a developer were prepared in the same manner as in Example 1, except that aluminum sulfate was replaced with polyaluminum chloride.

[0147] Example 7 A toner and a developer were prepared in the same manner as in Example 1, except that the crystalline polyester resin dispersion (D1) was changed to the crystalline polyester resin dispersion (D2).

[0148] Example 8 A toner and a developer were prepared in the same manner as in Example 1, except that the release agent particle dispersion liquid (W1) was changed to the release agent particle dispersion liquid (W2).

[0149] (Comparative Examples 1 and 2) Toners and developers of each example were prepared in the same manner as in Example 1, except that the step of adding the 1N aqueous sodium hydroxide solution was changed as shown in Table 1.

[0150] <Toner performance evaluation> [Evaluation of color spot suppression] Each example developer was placed in the developing device of a modified image forming apparatus, "Apeos PortIVC5575 (manufactured by Fuji Xerox Co., Ltd.)." Using this modified image forming apparatus, after leaving it in a high-temperature, high-humidity environment (28°C, 85% RH) for one day, images with an image density of 1%, were printed continuously on 1,000 sheets of A4 paper. The occurrence of color dots was visually observed for 100 sheets between 900 and 1,000 sheets, and evaluated according to the following criteria. Grades up to G2 were considered acceptable. -Evaluation criteria- G1: No color dots G2: The number of images with one or more color dots is between 1 and 5 G3: The number of images with one or more color dots is more than 5

[0151] [Evaluation of fogging suppression] The prepared developer was applied to a DocuCentre 400 manufactured by Fuji Xerox Co., Ltd., and image formation was carried out in a high temperature and high humidity environment (30°C, 88% RH environment) so as to form solid areas. 100 consecutive images were then formed, and the image quality of the solid areas of the first image and the 100th image was visually evaluated according to the following criteria. -Evaluation criteria- A: No overlap on both the 1st and 100th images B: Fog occurs on the 100th image C: Fog occurs from the first image

[0152] The evaluation results are summarized in Table 1.

[0153] [Table 1]

[0154] In Table 1, PAC stands for polyaluminum chloride. From the above results, it is apparent that the present invention provides a toner for developing electrostatic images that is superior in suppressing the occurrence of color spots and fogging in the resulting images compared to the comparative examples. [Explanation of symbols]

[0155] 1Y, 1M, 1C, 1K Photoconductor (an example of an image carrier) 2Y, 2M, 2C, 2K Charging roll (an example of charging means) 3. Exposure device (an example of an electrostatic image forming means) 3Y, 3M, 3C, 3K laser beam 4Y, 4M, 4C, 4K developing device (an example of developing means) 5Y, 5M, 5C, 5K Primary transfer roll (an example of a primary transfer means) 6Y, 6M, 6C, 6K: Photoconductor cleaning device (an example of a cleaning means) 8Y, 8M, 8C, 8K toner cartridges 10Y, 10M, 10C, 10K image forming units 20 Intermediate transfer belt (an example of an intermediate transfer body) 22 Drive Roll 24 Support Roll 26 Secondary transfer roll (an example of a secondary transfer means) 30 Intermediate transfer body cleaning device 107 Photoconductor (an example of an image carrier) 108 Charging roll (an example of charging means) 109 Exposure device (an example of electrostatic image forming means) 111 Developing device (an example of developing means) 112 Transfer device (an example of transfer means) 113 Photosensitive drum cleaning device (an example of cleaning means) 115 Fixing device (an example of fixing means) 116 Mounting Rail 118 Exposure opening 117 Cabinet 200 Process Cartridge 300 Recording paper (an example of a recording medium) P Recording paper (an example of a recording medium)

Claims

1. an aggregating step of aggregating at least resin particles contained in the dispersion using an aluminum-based aggregating agent to form aggregated particles; a fusing step of heating and fusing the aggregated particles to form fused particles; a cooling step of cooling the dispersion containing the fused particles to obtain a toner particle dispersion; a pH adjustment step of adjusting the pH of the toner particle dispersion to 8.0 or more and 11.0 or less, In the cooling step, the dispersion liquid containing the fused particles is cooled to a temperature of 10° C. or more and 30° C. or less, The cooling rate of the dispersion containing the fused particles in the cooling step is 10°C / min or more and 100°C / min or less. A method for producing a toner for developing electrostatic images.

2. 2. The method for producing a toner for developing electrostatic images according to claim 1, wherein the pH of the toner particle dispersion is adjusted to 8.5 or more and 11.0 or less in the pH adjusting step.

3. 3. The method for producing a toner for developing an electrostatic image according to claim 2, wherein the pH of the toner particle dispersion is adjusted to 9.0 or more and 10.0 or less in the pH adjusting step.

4. 4. The method for producing a toner for developing an electrostatic image according to claim 1, wherein at least the resin particles and the release agent particles are aggregated in the aggregation step.

5. 5. The method for producing a toner for developing electrostatic images according to claim 1, wherein the pH is adjusted with an alkali metal hydroxide in the pH adjusting step.