Surfactant composition, emulsion polymerization composition, method for producing polymer emulsion, and polymer emulsion

Abstract

To provide a surfactant composition from which a polymer emulsion excellent in adhesive characteristics, mechanical stability, and water resistance can be obtained.SOLUTION: The present invention provides the surfactant composition containing 95.5-99.2 mass% of an anionic surfactant represented by the following general formula (1) and 0.8-4.5 mass% of a nonionic surfactant represented by the following general formula (2). (In formula (1), R1 represents a C8-15 linear or branched alkyl group; m represents a number of 5-50; and M represents a hydrogen atom, an alkali metal atom or an ammonium group.) (In formula (2), R2 represents a C8-15 linear or branched alkyl group; and n represents a number of 5-50.)SELECTED DRAWING: None

Description

[Technical Field]

[0001] The present invention relates to a surfactant composition that can produce polymer emulsions with excellent adhesive properties, mechanical stability, and water resistance. [Background technology]

[0002] Acrylic resins, styrene resins, and other resin emulsions are used in paints, adhesives, sealants, coatings, inks, cements, mortars, car waxes, and the like. To improve the various properties of these resin emulsions, a method of using reactive emulsifiers when producing resin emulsions by emulsion polymerization of raw material monomers is known, and various reactive emulsifiers have been proposed to date.

[0003] Examples of reactive emulsifiers include various reactive emulsifiers having a (meth)allyl ether group as a reactive group (Patent Documents 1 and 2), and various reactive emulsifiers having a (meth)acrylic acid ester group as a reactive group (Patent Documents 3 and 4). [Prior art documents] [Patent Documents]

[0004] [Patent Document 1] Japanese Patent Application Publication No. 63-054927 [Patent Document 2] Japanese Patent Application Publication No. 63-319035 [Patent Document 3] Japanese Patent Publication No. 63-077530 [Patent Document 4] Japanese Patent Application Publication No. 63-185436 [Disclosure of the Invention] [Problems that the invention aims to solve]

[0005] However, for the reactive emulsifiers described in Patent Documents 1 to 4, the adhesive properties, mechanical stability, and water resistance of the resulting polymer emulsion are not sufficient, and there has still been a demand in the market for a surfactant composition having excellent properties.

[0006] Therefore, an object of the present invention is to provide a surfactant composition capable of obtaining a polymer emulsion excellent in adhesive properties, mechanical stability, and water resistance.

Means for Solving the Problems

[0007] As a result of intensive studies to solve the above problems, the present inventors have found that a surfactant composition containing a specific anionic surfactant and a specific nonionic surfactant in specific amounts can obtain a polymer emulsion excellent in adhesive properties, mechanical stability, and water resistance, and have arrived at the present invention. That is, the present invention is a surfactant composition containing 95.5% to 99.2% by mass of an anionic surfactant represented by the following general formula (1) and 0.8% to 4.5% by mass of a nonionic surfactant represented by the following general formula (2).

[0008]

Chemical formula

[0009] (In the formula, R 1 represents an alkyl group having 8 to 15 carbon atoms, m represents a number from 5 to 50, and M represents a hydrogen atom, an alkali metal atom, or an ammonium group.)

[0010]

Chemical formula

[0011] (In the formula, R 2 represents an alkyl group having 8 to 15 carbon atoms, and n represents a number from 5 to 50.)

Effects of the Invention

[0012] By using the surfactant composition according to the present invention, polymer emulsions with excellent adhesive properties, mechanical stability, and water resistance can be prepared. [Modes for carrying out the invention]

[0013] A. Anionic surfactants The anionic surfactant used in the present invention is an anionic surfactant represented by the following general formula (1).

[0014] [ka]

[0015] R in general formula (1) 1 R represents an alkyl group having 8 to 15 carbon atoms. Examples of such groups include linear or branched alkyl groups such as octyl group, branched octyl group, nonyl group, branched nonyl group, decyl group, branched decyl group, undecyl group, branched undecyl group, dodecyl group, branched dodecyl group, tridecyl group, branched tridecyl group, tetradecyl group, branched tetradecyl group, pentadecyl group, and branched pentadecyl group. Among these, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, R in general formula (1) is considered important. 1 R is preferably a linear or branched alkyl group having 10 to 15 carbon atoms, and more preferably a linear or branched alkyl group having 11 to 13 carbon atoms. Furthermore, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, R in general formula (1) is preferred. 1 R is preferably a branched alkyl group, and more preferably an isoalkyl group which is a branched alkyl group having three or more terminal methyl groups. In the present invention, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with particularly excellent adhesive properties, mechanical stability, and water resistance, R in general formula (1) is preferred. 1It is preferably an isoalkyl group having 10 to 15 carbon atoms, more preferably an isoalkyl group having 11 to 13 carbon atoms, and particularly preferably an isoundecyl group.

[0016] In general formula (1), m represents a number between 5 and 50. Among these, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, m in general formula (1) is preferably between 10 and 40, and more preferably between 10 and 30. Furthermore, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, the average value of m is preferably 7 to 45, more preferably 8 to 40, and even more preferably 10 to 30.

[0017] In general formula (1), M represents a hydrogen atom, an alkali metal atom, or an ammonium group. Examples of alkali metal atoms include lithium atoms, sodium atoms, and potassium atoms. Among these, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, M in general formula (1) is preferably a hydrogen atom, a sodium atom, a potassium atom, or an ammonium group, and more preferably an ammonium group.

[0018] The method for producing an anionic surfactant represented by general formula (1) is not particularly limited and can be produced by known methods, but for example, it can be produced by the method described in Japanese Patent Application Publication No. 2006-075808.

[0019] B. Nonionic surfactants The nonionic surfactant used in the present invention is represented by the following general formula (2). Nonion It is a surfactant.

[0020] [ka]

[0021] R in general formula (2) 2 represents an alkyl group having 8 to 15 carbon atoms. Examples of such groups include an octyl group, a branched octyl group, a nonyl group, a branched nonyl group, a decyl group, a branched decyl group, an undecyl group, a branched undecyl group, a dodecyl group, a branched dodecyl group, a tridecyl group, a branched tridecyl group, a tetradecyl group, a branched tetradecyl group, a pentadecyl group, a branched pentadecyl Moto etc. linear or branched alkyl group and the like. Among these, from the viewpoint of obtaining a surfactant composition that gives a polymer emulsion having more excellent adhesion properties, mechanical stability, and water resistance, R in general formula (2) 2 is preferably a linear or branched alkyl group having 10 to 15 carbon atoms, and more preferably a linear or branched alkyl group having 11 to 13 carbon atoms. Also, from the viewpoint of obtaining a surfactant composition that gives a polymer emulsion having more excellent adhesion properties, mechanical stability, and water resistance, R in general formula (2) 2 is preferably a branched alkyl group, and more preferably an isoalkyl group which is a branched alkyl group having 3 or more terminal methyl groups. In the present invention, among these, from the viewpoint of obtaining a surfactant composition that gives a polymer emulsion having particularly excellent adhesion properties, mechanical stability, and water resistance, R in general formula (2) 2 is preferably an isoalkyl group having 10 to 15 carbon atoms, more preferably an isoalkyl group having 11 to 13 carbon atoms, and particularly preferably an isoundecyl group.

[0022] n in general formula (2) represents a number from 5 to 50. Among these, from the viewpoint of obtaining a surfactant composition that gives a polymer emulsion having more excellent adhesion properties, mechanical stability, and water resistance, n in general formula ( 2 ) is preferably from 10 to 40, and more preferably from 10 to 30. Also, the average value of n is preferably from 7 to 45, more preferably from 8 to 40, and even more preferably from 10 to 30, from the viewpoint of obtaining a surfactant composition that gives a polymer emulsion having more excellent adhesion properties, mechanical stability, and water resistance.

[0023] The method for producing a nonionic surfactant represented by general formula (2) is not particularly limited and can be produced by known methods, but for example, it can be produced by the method described in Japanese Patent Application Publication No. 2002-301353.

[0024] C. Surfactant composition The surfactant composition of the present invention is a surfactant composition containing an anionic surfactant represented by the above-mentioned general formula (1) in an amount of 95.5% to 99.2% by mass of the total amount of the surfactant composition, and a nonionic surfactant represented by the above-mentioned general formula (2) in an amount of 0.8% to 4.5% by mass of the total amount of the surfactant composition. If the content of the anionic surfactant represented by general formula (1) is less than 95.5% by mass, when used in emulsion polymerization, it may result in a polymer emulsion with poor adhesive properties and water resistance, and if it is more than 99.2% by mass, when used in emulsion polymerization, it may result in a polymer emulsion with poor adhesive properties and mechanical stability. Similarly, if the content of the nonionic surfactant represented by general formula (2) is less than 0.8% by mass, when used in emulsion polymerization, it may result in a polymer emulsion with poor adhesive properties and mechanical stability, and if it is more than 4.5% by mass, it may result in a polymer emulsion with poor adhesive properties and water resistance when used in emulsion polymerization. In the present invention, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, the surfactant composition of the present invention comprises 95.8% to 99.1% by mass of an anionic surfactant represented by general formula (1) and 0.9% by mass of a nonionic surfactant represented by general formula (2). % It is preferable to contain approximately 4.2% by mass of anionic surfactants represented by general formula (1), and more preferably 96.0% to 99.0% by mass of anionic surfactants represented by general formula (1) and 1.0% to 4.0% by mass of nonionic surfactants represented by general formula (2).

[0025] In the surfactant composition of the present invention, other components (for example, various components described later) other than the anionic surfactant represented by general formula (1) and the nonionic surfactant represented by general formula (2) described above may be included, as long as the effects of the present invention are not impaired. However, from the viewpoint of easily obtaining a polymer emulsion with excellent adhesive properties, mechanical stability, and water resistance, the total content of the anionic surfactant represented by general formula (1) and the nonionic surfactant represented by general formula (2) in the surfactant composition is preferably 96.5% by mass or more, more preferably 97.0% by mass or more, and even more preferably 99.0% by mass or more, based on the total amount of the surfactant composition. 0 quality It is particularly preferable that the amount be in percent. In other words, it is particularly preferable that the surfactant composition of the present invention consists of an anionic surfactant represented by the above-mentioned general formula (1) and a nonionic surfactant represented by the above-mentioned general formula (2), excluding unavoidable impurities.

[0026] In the present invention, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, the alkyl group R of the anionic surfactant represented by general formula (1) is used. 1 And the alkyl group R of the nonionic surfactant represented by general formula (2) 2 Preferably, and are the same alkyl group. Specifically, for example, in the surfactant composition of the present invention, R in general formula (1) 1 95.5% to 99.2% by mass of anionic surfactants in which alkyl groups have 8 to 15 carbon atoms, and R in general formula (2) 2 R 1 Preferably contains 0.8% to 4.5% by mass of a nonionic surfactant which is the same alkyl group as and, in general formula (1) R 1 95.5% to 99.2% by mass of an anionic surfactant in which R is a linear or branched alkyl group having 11 to 13 carbon atoms, and R in general formula (2) 2 R 1 It is more preferable to contain 0.8% to 4.5% by mass of a nonionic surfactant which is the same alkyl group as R in general formula (1), and1 95.5% to 99.2% by mass of an anionic surfactant in which is an isoalkyl group having 11 to 13 carbon atoms, and R in general formula (2) 2 R 1 It is even more preferable to include 0.8% to 4.5% by mass of a nonionic surfactant which is the same alkyl group as R in general formula (1), and 1 96.0% to 99.0% by mass of an anionic surfactant in which is an isoalkyl group having 11 to 13 carbon atoms, and R in general formula (2) 2 R 1 It is even more preferable to contain 1.0 to 4.0% by mass of a nonionic surfactant which is the same alkyl group as [the other component].

[0027] In this invention, the alkyl group R of the anionic surfactant represented by general formula (1) 1 And the alkyl group R of the nonionic surfactant represented by general formula (2) 2 The statement that and are the same alkyl group means that the alkyl group R of the anionic surfactant represented by general formula (1) is the same alkyl group, excluding unintended structures derived from trace components in the raw materials used in their respective manufacturing processes. 1 And the alkyl group R of the nonionic surfactant represented by general formula (2) 2 This indicates that the number of carbon atoms and their linear / branched structure are substantially identical. For example, this refers to the alkyl group R of an anionic surfactant represented by general formula (1) in a surfactant composition. 1 If it consists of one type of structure, the alkyl group R of the nonionic surfactant represented by general formula (2) 2 It was shown that they also consist of the same type of structure, and that R is present in the surfactant composition. 1 If it contains two or more different anionic surfactants represented by general formula (1), then even in the case of a nonionic surfactant represented by general formula (2), R 2This indicates that the product contains two or more nonionic surfactants represented by general formula (2) with different alkyl groups, in amounts equivalent to the amount of anionic surfactant represented by general formula (1) whose alkyl group structure corresponds to that of the nonionic surfactant. Here, "equivalent amounts" means that the difference in the content of the two is within 5% by mass, preferably within 3% by mass, and more preferably within 1% by mass.

[0028] In the present invention, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, it is preferable that the number of ethylene oxide groups m in the anionic surfactant represented by general formula (1) and the number of ethylene oxide groups n in the nonionic surfactant represented by general formula (2) are the same. Specifically, for example, the surfactant composition of the present invention preferably contains 95.5% to 99.2% by mass of an anionic surfactant in which m in general formula (1) is a number from 5 to 50, and 0.8% to 4.5% by mass of a nonionic surfactant in which n in general formula (2) is the same number as m, or it may contain 95.5% to 99.2% by mass of an anionic surfactant in which m in general formula (1) is a number from 10 to 30, and 0.8% to 4.5% by mass of a nonionic surfactant in which n in general formula (2) is the same number as m. It is more preferable to contain 95.5% to 99.2% by mass of an anionic surfactant in which m is 10, 20, or 30 in general formula (1) and 0.8% to 4.5% by mass of a nonionic surfactant in which n is the same number as m in general formula (2), and it is even more preferable to contain 96.0% to 99.0% by mass of an anionic surfactant in which m is 10 or 30 in general formula (1) and 1.0% to 4.0% by mass of a nonionic surfactant in which n is the same number as m in general formula (2).

[0029] Furthermore, when we say that the number of ethylene oxide groups m in an anionic surfactant represented by general formula (1) and the number of ethylene oxide groups n in a nonionic surfactant represented by general formula (2) are the same, it means that, excluding unintended structures derived from by-products during their respective manufacturing, the values ​​of the number of ethylene oxide groups m in an anionic surfactant represented by general formula (1) and the number of ethylene oxide groups n in a nonionic surfactant represented by general formula (2) are identical. This indicates, for example, that if the number of ethylene oxide groups m in an anionic surfactant represented by general formula (1) in a surfactant composition is a specific single number, then the number of ethylene oxide groups n in a nonionic surfactant represented by general formula (2) is also the same number. Furthermore, if a surfactant composition contains two or more anionic surfactants represented by general formula (1) with different values ​​of m, then the nonionic surfactants represented by general formula (2) also contain two or more nonionic surfactants represented by general formula (2) with different n values ​​in an amount equivalent to the amount of the corresponding anionic surfactant represented by general formula (1). The definition of "equivalent amount" is the same as above.

[0030] Furthermore, in the surfactant composition of the present invention, when the value of the number of ethylene oxide groups added, m, of the anionic surfactant represented by general formula (1) and the value of the number of ethylene oxide groups added, n, of the nonionic surfactant represented by general formula (2) are expressed by the average value of the number of ethylene oxide groups added to the anionic surfactant represented by general formula (1) and the average value of the number of ethylene oxide groups added to the nonionic surfactant represented by general formula (2) contained in the surfactant composition, respectively, from the viewpoint of obtaining a surfactant composition that yields a polymer emulsion with superior adhesive properties, mechanical stability, and water resistance, it is preferable that the average value of the number of ethylene oxide groups added to the anionic surfactant represented by general formula (1) and the average value of the number of ethylene oxide groups added to the nonionic surfactant represented by general formula (2) contained in the surfactant composition of the present invention are equivalent values. Here, "equivalent average values" means that the difference between the two values ​​is within 20%, preferably within 10%, and more preferably within 5%, based on the average value of the number of ethylene oxide groups added to the anionic surfactant represented by general formula (1).

[0031] The surfactant compositions of the present invention can be used without particular limitations for the normal uses of surfactants. For example, surfactant compositions for emulsion polymerization, surfactant compositions for suspension polymerization, and surfactant compositions for resin modification (improvement of water repellency, adjustment of hydrophilicity, improvement of compatibility, improvement of antistatic properties, improvement of antifogging properties, improvement of water resistance, improvement of adhesion, improvement of dyeability, improvement of film-forming properties, improvement of weather resistance, improvement of blocking properties, etc.). thing, It can be used as a surfactant composition for textile processing, a surfactant composition for antifouling of textiles, and the like. Among these, from the viewpoint of the effects of the present invention, it is preferable to use the surfactant composition of the present invention as a surfactant composition for emulsion polymerization. When the surfactant composition of the present invention is used as a surfactant composition for emulsion polymerization, the specific product field is not limited, and for example, it can be used as a surfactant composition for emulsion polymerization to produce polymer emulsions for use in paints, adhesives, sealants, inks, films, coatings, paper coatings, sizing agents, sealers, etc.

[0032] The polymerizable monomers that can be used when producing polymer emulsions using the surfactant composition of the present invention as an emulsion polymerization surfactant composition are not particularly limited and can be appropriately selected depending on the purpose. For example, one or more selected from the group consisting of acrylate monomers, styrene monomers, vinyl ester monomers, diene monomers, and acrylonitrile monomers can be used.

[0033] Examples of acrylate monomers include methyl acrylate, ethyl acrylate, propyl acrylate, n-butyl acrylate, isobutyl acrylate, t-butyl acrylate, n-hexyl acrylate, 2-ethylhexyl acrylate, n-octyl acrylate, n-nonyl acrylate, n-decyl acrylate, lauryl acrylate, stearyl acrylate, eicosanyl acrylate, behenyl acrylate, cyclohexyl acrylate, benzyl acrylate, tetracosanyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, t- Examples include butyl methacrylate, n-hexyl methacrylate, 2-ethylhexyl methacrylate, n-octyl methacrylate, n-nonyl methacrylate, n-decyl methacrylate, lauryl methacrylate, 2-methoxyethyl acrylate, 2-butoxyethyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, diethylene glycol monoacrylate, polyethylene glycol monoacrylate, methoxytetraethylene glycol acrylate, methoxypolyethylene glycol acrylate, 2-(dimethylamino)ethyl acrylate, acrylic acid, etc., and one or more of these can be used.

[0034] Examples of styrene monomers include styrene, α-methylstyrene, o-methylstyrene, p-methylstyrene, p-tert-butylstyrene, 2,4-dimethylstyrene, 2-methylstyrene, 3-methylstyrene, 4-methylstyrene, 2-ethylstyrene, 3-ethylstyrene, 4-ethylstyrene, 2,4-diisopropylstyrene, 2,4-dimethylstyrene, 4-t-butylstyrene, 5-t-butyl-2-methylstyrene, methoxystyrene, 4-methoxy-3-methylstyrene, dimethoxystyrene, 2-chlorostyrene, 3-chlorostyrene, 4-chlorostyrene, 4-bromostyrene, 2-methyl-4,6-dichlorostyrene, and 2,4-dibromostyrene. One or more of these can be used.

[0035] Examples of vinyl ester monomers include vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl pivalate, vinyl versatate, vinyl caproate, vinyl caprylate, vinyl caprate, vinyl laurate, vinyl myristate, vinyl palmitate, vinyl stearate, vinyl oleate, and vinyl benzoate, and one or more of these can be used.

[0036] Examples of diene monomers include 1,3-butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, 2,3-dimethyl-1,3-butadiene, 2-chloro-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene, 2,4-hexadiene, 1,3-octadiene, 2-methyl-1,3-pentadiene, 2,3-dimethyl-1,3-pentadiene, 3,4-dimethyl-1,3-hexadiene, 2,3-diethyl-1,3-butadiene, 4,5-diethyl-1,3-octadiene, 3-butyl-1,3-octadiene, 3,7-dimethyl-1,3,6-octatriene, and 2-methyl-6-methylene-1,7-octadiene. Examples include 7-methyl-3-methylene-1,6-octadiene, 1,3,7-octatriene, 2-ethyl-1,3-butadiene, 2-amyl-1,3-butadiene, 3,7-dimethyl-1,3,7-octatriene, 3,7-dimethyl-1,3,6-octatriene, 3,7,11-trimethyl-1,3,6,10-dodecatetraene, 7,11-dimethyl-3-methylene-1,6,10-dodecatriene, 2,6-dimethyl-2,4,6-octatriene, 2-phenyl-1,3-butadiene, 2-methyl-3-isopropyl-1,3-butadiene, 1,3-cyclohexadiene, etc., and one or more of these can be used.

[0037] Examples of acrylonitrile monomers include acrylonitrile, methacrylonitrile, α-ethoxyacrylonitrile, and fumaronitrile, and one or more of these can be used.

[0038] When the surfactant composition of the present invention is used as a surfactant composition for emulsion polymerization, from the viewpoint of the effects of the present invention, it is preferable to use it as a surfactant composition for emulsion polymerization to emulsion polymerization one or more selected from the group consisting of acrylate monomers, styrene monomers, vinyl ester monomers, diene monomers, and acrylonitrile monomers; more preferable to use it as a surfactant composition for emulsion polymerization to emulsion polymerization one or more selected from the group consisting of acrylate monomers, styrene monomers, and vinyl ester monomers; and even more preferable to use it as a surfactant composition for emulsion polymerization to emulsion polymerization one or more selected from the group consisting of acrylate monomers and styrene monomers.

[0039] When using the surfactant composition of the present invention as a surfactant composition for emulsion polymerization, the amount of surfactant composition used is not particularly limited and can be adjusted as appropriate depending on the purpose. For example, 0.1 to 20 parts by mass per 100 parts by mass of the total mass of one or more polymerizable monomers selected from the group consisting of acrylate monomers, styrene monomers, vinyl ester monomers, diene monomers, and acrylonitrile monomers. mass Preferably, it is used in amounts of 0.2 to 10 parts by mass. mass It is more preferable to use 0.5 to 8 parts by mass. mass It is even more preferable to use it in parts.

[0040] D. Composition for emulsion polymerization The emulsion polymerization composition of the present invention is an emulsion polymerization composition containing the surfactant composition described above. Depending on the purpose, the emulsion polymerization composition of the present invention may contain water, polymerizable monomers, polymerization initiators, chain transfer agents, pH buffers, anionic surfactants other than the anionic surfactant represented by general formula (1), nonionic surfactants other than the nonionic surfactant represented by general formula (2), amphoteric surfactants, cationic surfactants, organic solvents, plasticizers, preservatives, thickeners, dispersants, etc.

[0041] When the emulsion polymerization composition of the present invention contains a surfactant composition and water, the water content is not particularly limited and can be adjusted according to the purpose. However, from the viewpoint of easily obtaining a polymer emulsion with excellent adhesive properties, mechanical stability, and water resistance, the water content is preferably 1% to 95% by mass, more preferably 2% to 90% by mass, and even more preferably 5% to 80% by mass, based on the total amount of the emulsion polymerization composition.

[0042] As polymerizable monomers that can be contained in the emulsion polymerization composition of the present invention, for example, the acrylate monomers, styrene monomers, vinyl ester monomers, diene monomers, acrylonitrile monomers, etc., mentioned above can be used. When the emulsion polymerization composition of the present invention contains polymerizable monomers, the content of the polymerizable monomers is not particularly limited and can be adjusted according to the purpose, but from the viewpoint of easily obtaining polymer emulsions with excellent adhesive properties, mechanical stability, and water resistance, the content of the polymerizable monomers is preferably 5% to 90% by mass, more preferably 10% to 80% by mass, and even more preferably 20% to 70% by mass, based on the total amount of the emulsion polymerization composition.

[0043] In the emulsion polymerization composition of the present invention, when it contains a surfactant composition and a polymerizable monomer, the ratio of the surfactant composition to the polymerizable monomer is not particularly limited and can be adjusted according to the purpose. However, from the viewpoint of easily obtaining a polymer emulsion with excellent adhesive properties, mechanical stability, and water resistance, the content of the surfactant composition in the emulsion polymerization composition is preferably 0.1 to 20 parts by mass, more preferably 0.2 to 10 parts by mass, and even more preferably 0.5 to 8 parts by mass, per 100 parts by mass of polymerizable monomer.

[0044] When the emulsion polymerization composition of the present invention contains a surfactant composition, water, and a polymerizable monomer, the content of the surfactant composition, water, and polymerizable monomer described above is not particularly limited and can be adjusted according to the purpose. However, from the viewpoint of easily obtaining a polymer emulsion with excellent adhesive properties, mechanical stability, and water resistance, it is preferable that the content of the surfactant composition is 0.1% to 10% by mass, the content of water is 10% to 70% by mass, and the content of polymerizable monomer is 20% to 80% by mass, relative to the total amount of the emulsion polymerization composition; it is more preferable that the content of the surfactant composition is 0.2% to 8% by mass, the content of water is 20% to 65% by mass, and the content of polymerizable monomer is 30% to 75% by mass; and it is even more preferable that the content of the surfactant composition is 0.5% to 5% by mass, the content of water is 25% to 60% by mass, and the content of polymerizable monomer is 35% to 70% by mass.

[0045] Polymerization initiators that can be contained in the emulsion polymerization composition of the present invention include, for example, ammonium persulfate, sodium persulfate, potassium persulfate, ammonium peroxide, potassium peroxide, hydrogen peroxide, acetyl peroxide, lauroyl peroxide, benzoyl peroxide, isopropoxycarbonyl peroxide, tert-butoxycarbonyl peroxide, methyl ethyl ketone peroxide, cyclohexanone peroxide, t-butyl hydroperoxide, cumene hydroperoxide, di-t-butyl peroxide, dicumyl peroxide, t-butyl peroxyacetate, t-butyl peroxide Examples include oxypivalate, 2,2'-azobisisobutyronitrile, 2,2'-azobis(2,4-dimethylvaleronitrile), 2,2'-azobis(2-methylvaleronitrile), 2,2'-azobis(2-cyclopropylpropionitrile), 2,2'-azobisisobutyrate dimethyl, 2,2'-azobis[2-(hydroxymethyl)propionitrile], 2,2'-azobis(2-amidinopropane)dihydrochloride, 2,2'-azobis-2-methylpropionamidine hydrochloride, 2,2'-azobis-2-(2-imidazolin-2-yl)propane hydrochloride, and others, and one or more of these may be included. In addition to polymerization initiators, accelerators such as sodium bisulfite, metadisulfite, sodium hypophosphite, Fe(II) salts such as Mohr's salt, sodium hydroxymethanesulfinate dihydrate, hydroxylamine hydrochloride, thiourea, sodium L-ascorbate, and sodium erythorbate can also be used. For example, a combination of persulfate and sodium bisulfite, peroxide A redox initiator consisting of a combination of sodium ascorbate may also be used.

[0046] When the emulsion polymerization composition of the present invention contains a polymerization initiator, the content of the polymerization initiator is not particularly limited and can be adjusted according to the purpose. However, from the viewpoint of easily obtaining a polymer emulsion with excellent adhesive properties, mechanical stability, and water resistance, it is preferably 0.01% to 5% by mass, more preferably 0.02% to 3% by mass, and even more preferably 0.05% to 2% by mass, based on the total amount of the emulsion polymerization composition.

[0047] Examples of chain transfer agents that can be contained in the emulsion polymerization composition of the present invention include butyl mercaptan, pentyl mercaptan, octyl mercaptan, dodecyl mercaptan, tetradecyl mercaptan, hexadecyl mercaptan, octadecyl mercaptan, glycidyl mercaptan, mercaptoacetic acid, mercaptoethanol, mercaptopropionic acid, 2,3-dimercapto-1-propanol, aminoethanethiol, thioglycolic acid, thiomalic acid, thioglycolic acid, and thioglycolic acid. Ri Ethyl cholate, n-butyl thioglycolate, methoxybutyl thioglycolate, thioglycolate Ri 2-Ethylhexyl Cholate, Hexanedithiol, Decanedithiol, 1,4-Butanediol Bisthiopropionate, 1,4-Butanediol Bisthioglycolate, Ethylene Glycol Bisthioglycolate, Ethylene Glycol Bisthiopropionate, Trimethylolpropane Tristhioglycolate, Trimethylolpropane Tristhiopropionate, Trimethylolpropane Tris(3-Mercaptobutyrate), Pentaerythritol Tetrakisthioglycolate, Pentaerythritol Tetrakisthiopropionate, 2,4,6-Trimercapto-s-Triadin, 2-(N,N-Dibutylamino)-4,6-Dimercapto-s-Triadin, α-Terpinene, γ-Terpinene Pi Examples include methylcellulose, 2,4-diphenyl-4-methyl-1-pentene, and the product may contain one or more of these.

[0048] The pH buffering agent that can be contained in the emulsion polymerization composition of the present invention is not particularly limited as long as it is a compound that has a pH buffering effect, but examples include sodium carbonate, potassium carbonate, ammonium carbonate, sodium bicarbonate, potassium bicarbonate, sodium formate, potassium formate, ammonium formate, sodium acetate, potassium acetate, ammonium acetate, monosodium phosphate, monopotassium phosphate, disodium phosphate, dipotassium phosphate, trisodium phosphate, tripotassium phosphate, acetic acid, phosphoric acid, formic acid, glycine, alanine, valine, leucine, isoleucine, serine, asparagine, glutamine, arginine, lysine, etc., and one or more of these can be contained.

[0049] Other anionic surfactants (excluding anionic surfactants represented by general formula (1)) that can be contained in the emulsion polymerization composition of the present invention include, for example, fatty acid soaps, higher alcohol sulfate salts, sulfurized olefin salts, higher alkyl sulfonates, α-olefin sulfonates, sulfated fatty acid salts, sulfonated fatty acid salts, phosphate ester salts, sulfate salts of fatty acid esters, glyceride sulfate salts, sulfonates of fatty acid esters, α-sulfo fatty acid methyl ester salts, polyoxyalkylene alkyl ether sulfate salts, polyoxyethylene alkylphenyl ether sulfate salts, sulfate salts of alkylene oxide adducts of fatty acid alkanolamides, sulfosuccinate esters, alkylbenzene sulfonates, alkylnaphthalene sulfonates, alkyl benzimidazole sulfonates, salts of N-acyl-N-methyl taurine, acyloxyethane sulfonates, alkoxyethanesulfonic acids, N-acyl-N-carboxyethyl taurine or its salts, alkyl or alkenylaminocarboxymethyl sulfates, and one or more of these can be contained.

[0050] Other nonionic surfactants (excluding nonionic surfactants represented by general formula (2)) that can be contained in the emulsion polymerization composition of the present invention include, for example, polyoxyethylene alkyl ethers, polyoxyethylene alkylphenyl ethers, and Ri Examples include copolymers of two or more alkylene oxides such as serine fatty acid esters, polyglycerin fatty acid esters, sorbitan fatty acid esters, polyoxyethylene fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene alkylamines, polyoxyethylene-polyoxypropylene ethylenediamines, polyoxyethylene alkylamides, polyoxyethylene castor oil, polyoxyethylene hydrogenated castor oil, polyoxyethylene rosin esters, polyoxyethylene lanolin ethers, acetylene glycol ethylene oxide adducts, and ethylene oxide / propylene oxide block copolymers, and one or more of these may be included.

[0051] Examples of amphoteric surfactants that can be contained in the emulsion polymerization composition of the present invention include alkylbetaine-type amphoteric surfactants such as alkyldimethylbetaine and alkyldihydroxyethylbetaine, imidazolium betaine-type amphoteric surfactants such as N-fatty acid acyl-N-carboxymethyl-N-hydroxyethylethylenediamine salt and N-fatty acid acyl-N-carboxyethyl-N-hydroxyethylethylenediamine salt, amidopropylbetaine-type amphoteric surfactants such as fatty acid amidopropylbetaine, and amino acid-type amphoteric surfactants such as alkylaminopropionate and alkylaminodipropionate, and one or more of these can be contained.

[0052] Examples of cationic surfactants that can be contained in the emulsion polymerization composition of the present invention include alkyl(alkenyl)trimethylammonium salts, dialkyl(alkenyl)dimethylammonium salts, alkyl(alkenyl)quaternary ammonium salts, mono or dialkyl(alkenyl)quaternary ammonium salts containing an ether group, an ester group, or an amide group, alkyl(alkenyl)pyridinium salts, alkyl(alkenyl)dimethylbenzylammonium salts, alkyl(alkenyl)isoquinolinium salts, dialkyl(alkenyl)morphonium salts, alkyl(alkenyl)amine salts, benzalkonium chloride, benzethonium chloride, and others, and one or more of these can be contained.

[0053] The emulsion polymerization composition of the present invention may contain, for example, ketones such as methyl ethyl ketone, methyl amyl ketone, diethyl ketone, acetone, methyl isopropyl ketone, methyl isobutyl ketone, cyclohexanone, and 2-heptanone; ether solvents such as ethyl ether, dioxane, tetrahydrofuran, 1,2-dimethoxyethane, 1,2-diethoxyethane, and dipropylene glycol dimethyl ether; ester solvents such as methyl acetate, ethyl acetate, n-propyl acetate, isopropyl acetate, n-butyl acetate, cyclohexyl acetate, ethyl lactate, and dimethyl succinate; and ethylene glycol monomethyl ether. Examples of solvents include cellosolve solvents such as ethylene glycol monoethyl ether, alcohol solvents such as methanol, ethanol, propanol, butanol, and amyl alcohol, ether ester solvents such as ethylene glycol monomethyl acetate, ethylene glycol monoethyl acetate, propylene glycol-1-monomethyl ether, propylene glycol-1-monomethyl ether-2-acetate, dipropylene glycol monomethyl ether acetate, 3-methoxybutyl acetate, and ethoxyethyl propionate, and BTX solvents such as benzene, toluene, and xylene. One or more of these may be included.

[0054] Examples of plasticizers that can be contained in the emulsion polymerization composition of the present invention include adipic acid esters, fumaric acid esters, sebadic acid esters, citrate esters, maleic acid esters, phosphate esters, epoxy fatty acid esters, aliphatic dibasic acid esters, sulfonamides, fatty acid amides, polyesters, chlorinated paraffins, and others, and one or more of these may be contained.

[0055] Examples of preservatives that can be contained in the emulsion polymerization composition of the present invention include parabens, methylparaben, benzoates, benzyl alcohol, isothiazolone, isothiazolinone, phenoxyethanol, phenylethanol, alkanediols, alkylglyceryl ethers, triazine compounds, benzoic acid, benzoates, salicylic acid, salicylates, quaternary ammonium salt compounds, halogenated compounds, cyclic organic nitrogen compounds, sodium bisulfite, sodium bisulfite, sodium thiosulfate, ascorbates, thimerosal, bronopol, thiabendazole, zinc pyrithione, carbendazim, and sodium pyridine oxide thiol salts, and one or more of these can be contained.

[0056] Examples of thickeners that can be contained in the emulsion polymerization composition of the present invention include carrageenan, xanthan gum, guar gum, locust bean gum, gatcha gum, karaya gum, pectin, methylcellulose, ethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose, hydroxyethylmethylcellulose, hydroxypropylmethylcellulose, carboxymethylcellulose, polyacrylic acid, polyacrylic acid-maleic acid copolymer, polyvinyl alcohol, carboxyvinyl polymer, and others, and one or more of these can be contained.

[0057] Examples of dispersants that can be contained in the emulsion polymerization composition of the present invention include polyacrylic acid, polymethacrylic acid, polymaleic acid, polyitaconic acid, acrylic acid-methacrylic acid copolymer, acrylic acid-maleic acid copolymer, olefin-maleic acid copolymer, acrylic acid-sulfonic acid copolymer, maleic anhydride-styrene copolymer, maleic anhydride-ethylene copolymer, maleic anhydride-vinyl acetate copolymer, maleic anhydride-acrylic acid ester copolymer, and salts thereof, and one or more of these may be contained.

[0058] When the emulsion polymerization composition of the present invention contains one or more selected from the group consisting of other anionic surfactants, other nonionic surfactants, amphoteric surfactants, cationic surfactants, organic solvents, plasticizers, preservatives, thickeners, and dispersants, the content of each component is not particularly limited and can be adjusted as appropriate depending on the purpose. For example, each component may be contained in an amount of 0.01 to 10% by mass relative to the total amount of the surfactant composition.

[0059] E. Method for producing polymer emulsions The present invention provides a method for producing a polymer emulsion, comprising polymerizing one or more polymerizable monomers selected from the group consisting of acrylate monomers, styrene monomers, vinyl ester monomers, diene monomers, and acrylonitrile monomers in the presence of the surfactant composition described above. The polymer emulsion of the present invention exhibits excellent tackiness, mechanical stability, and water resistance by polymerizing the polymerizable monomers in the presence of the surfactant composition described above. While there are no particular limitations on the specific method for producing the polymer emulsion of the present invention, from the viewpoint of easily obtaining a polymer emulsion with excellent tackiness, mechanical stability, and water resistance, polymerization by any of the following methods (Method 1) to (Method 3) is preferred.

[0060] (Method 1) Place the monomer mixture in a reaction vessel and raise the temperature to 40°C to 100°C. Add the polymerization initiator dissolved in water or an organic solvent dropwise or in portions over 5 minutes to 4 hours, and polymerize at 40°C to 100°C for 1 to 12 hours. (Method 2) Place 1% to 50% by mass of the monomer mixture to be used into a reaction vessel and raise the temperature to 40°C to 90°C. Then, add the polymerization initiator dissolved in water or an organic solvent dropwise or in portions, and polymerize at 40°C to 90°C for 5 minutes to 4 hours. After that, add the remaining monomer mixture dropwise or in portions over a period of 1 to 6 hours at 40°C to 90°C, and polymerize further at 40°C to 90°C for 10 minutes to 3 hours. (Method 3) A polymerization initiator dissolved in water or an organic solvent is placed in a reaction vessel and heated to 40°C to 90°C. Then, a mixed solution consisting of the monomer mixture and water or an organic solvent is added dropwise or in portions over 2 to 6 hours at 40°C to 90°C, and polymerization is carried out for another 1 to 5 hours at 40°C to 90°C.

[0061] In the method for producing the polymer emulsion of the present invention, the ratio of the amount of polymerizable monomer to the amount of surfactant composition used is not particularly limited and can be adjusted according to the purpose. However, from the viewpoint of easily obtaining a polymer emulsion with excellent adhesive properties, mechanical stability, and water resistance, it is preferable to use 0.1 to 10 parts by mass of surfactant composition per 100 parts by mass of polymerizable monomer, more preferably 0.2 to 6 parts by mass, and even more preferably 0.5 to 4 parts by mass.

[0062] In the method for producing a polymer emulsion of the present invention, when a polymerization initiator is used, the amount of polymerization initiator used is not particularly limited and can be adjusted according to the purpose. However, from the viewpoint of easily obtaining a polymer emulsion with excellent adhesive properties, mechanical stability, and water resistance, it is preferable to use 0.01 to 7 parts by mass of polymerization initiator per 100 parts by mass of polymerizable monomer, more preferably 0.02 to 5 parts by mass, and even more preferably 0.05 to 3 parts by mass.

[0063] In the method for producing a polymer emulsion of the present invention, when polymerizable monomers are polymerized in an aqueous solution in the presence of a surfactant composition, the ratios of the surfactant composition, water, and polymerizable monomers used are not particularly limited and can be adjusted according to the purpose. However, from the viewpoint of obtaining a polymer emulsion with excellent adhesive properties, mechanical stability, and water resistance, the amount of the surfactant composition used is 0.1% to 10% by mass, the amount of water is 10% to 70% by mass, and the amount of polymerizable monomer is 20% to 80% by mass, relative to the total amount of the surfactant composition, water, and polymerizable monomer used. It is preferable that the amount is % by mass, more preferably that the amount of surfactant composition is 0.2% to 8% by mass, the amount of water is 20% to 65% by mass, and the amount of polymerizable monomer is 30% to 75% by mass, even more preferably that the amount of surfactant composition is 0.5% to 6% by mass, the amount of water is 25% to 60% by mass, and the amount of polymerizable monomer is 35% to 70% by mass, and even more preferably that the amount of surfactant composition is 0.5% to 5% by mass, the amount of water is 30% to 55% by mass, and the amount of polymerizable monomer is 40% to 65% by mass.

[0064] In the method for producing polymer emulsions of the present invention, from the viewpoint of obtaining polymer emulsions with excellent adhesive properties, mechanical stability, and water resistance, it is preferable to use emulsion polymerization using water instead of an organic solvent in (Method 1) to (Method 3). Furthermore, among these, from the viewpoint of obtaining polymer emulsions with excellent adhesive properties, mechanical stability, and water resistance, polymerization by (Method 2) or (Method 3) described above is more preferable, and polymerization by (Method 3) is even more preferable.

[0065] F. Polymer Emulsion The polymer emulsion of the present invention is a polymer emulsion obtained by polymerizing one or more polymerizable monomers selected from the group consisting of acrylate monomers, styrene monomers, vinyl ester monomers, diene monomers, and acrylonitrile monomers in the presence of the surfactant composition described above. Specifically, the surfactant composition and polymerizable monomers used when producing the polymer emulsion of the present invention can be those described above. From the viewpoint of excellent adhesive properties, mechanical stability, and water resistance, the polymer emulsion of the present invention is preferably a polymer emulsion obtained by the polymer emulsion production method described above.

[0066] In the polymer emulsion of the present invention, the polymer content is not particularly limited and can be adjusted as appropriate depending on the purpose. However, from the viewpoint of excellent adhesive properties, mechanical stability, and water resistance, the polymer emulsion of the present invention preferably contains a polymer of anionic surfactant represented by general formula (1), nonionic surfactant represented by general formula (2), and polymerizable monomer in an amount of 30% to 90% by mass, more preferably 35% to 80% by mass, even more preferably 40% to 75% by mass, and still more preferably 45% to 70% by mass, based on the total mass of the polymer emulsion.

[0067] Furthermore, the water content in the polymer emulsion of the present invention is not particularly limited and can be adjusted as appropriate depending on the purpose. However, from the viewpoint of excellent adhesive properties, mechanical stability, and water resistance, the water content of the polymer emulsion of the present invention is preferably 10% to 70% by mass, more preferably 20% to 65% by mass, even more preferably 25% to 60% by mass, and still more preferably 30% to 55% by mass.

[0068] The polymer emulsion of the present invention can be used without particular limitations in products in which polymers are commonly used, for example, as a polymer emulsion for use in paints, adhesives, sealants, inks, films, coatings, paper coatings, sizing agents, sealers, etc. Furthermore, depending on the purpose, the polymer emulsion of the present invention may contain, each in an amount of 0.01% to 10% by mass of the total amount of polymer emulsion, other anionic surfactants other than the anionic surfactant represented by general formula (1) described above, other nonionic surfactants other than the nonionic surfactant represented by general formula (2), amphoteric surfactants, cationic surfactants, organic solvents, plasticizers, preservatives, thickeners, dispersants, etc. [Examples]

[0069] The present invention will be further described in detail below with reference to examples. In the following examples, percentages are by mass unless otherwise specified. The components used in the examples and comparative examples are shown below.

[0070] <Anionic surfactants> Anionic surfactant 1: In general formula (1), R 1 An anionic surfactant in which is an isoundecyl group, m is 10 (average value), and M is an ammonium group. Anionic surfactant 2: In general formula (1), R 1 An anionic surfactant in which is an isoundecyl group, m is 30 (average value), and M is an ammonium group.

[0071] <Nonionic surfactant> Nonionic surfactant 1: In general formula (2), R 2 A nonionic surfactant in which the group is an isoundecyl group and n is 10 (average value). Nonionic surfactant 2: In general formula (2), R 2 A nonionic surfactant in which the group is an isoundecyl group and n is 30 (average value).

[0072] <Mixed monomers> Mixed monomer 1: A mixed monomer consisting of 48% by mass of butyl acrylate, 40% by mass of 2-ethylhexyl acrylate, 10% by mass of styrene, and 2% by mass of acrylic acid. Mixed monomer 2: A mixed monomer consisting of 48% by mass of butyl acrylate, 40% by mass of 2-ethylhexyl acrylate, 10% by mass of methyl methacrylate, and 2% by mass of acrylic acid.

[0073] <Polymerization initiator> Polymerization initiator 1: Ammonium persulfate

[0074] [Preparation of surfactant compositions] Surfactant compositions 1 to 8 were prepared by mixing anionic surfactants 1 to 2 and nonionic surfactants 1 to 2 in the mass ratios shown in Tables 1 to 2.

[0075] [Table 1]

[0076] [Table 2]

[0077] [Preparation of polymer emulsions] 103 g of distilled water was charged into a reaction vessel equipped with a reflux condenser, stirrer, dropping funnel, and thermometer. After purging the system with nitrogen gas, the temperature was raised to 80°C. Next, 1.2 g of ammonium persulfate was added to the reaction vessel as a polymerization initiator. Then, 47 g of distilled water and a mixed solution of 5 g of surfactant composition and 200 g of mixed monomer in the combinations shown in Tables 3-4 were added dropwise to the reaction vessel, which was kept at 80°C, over 5 hours to carry out the polymerization reaction. After the dropwise addition was complete, the reaction was continued at 80°C for another 1 hour to obtain the polymer emulsions of Examples 5-12 and Comparative Examples 5-12. The final mixing ratios of each polymer emulsion are shown in Tables 3-4.

[0078] [Evaluation of adhesive properties] For each of the polymer emulsions obtained in Examples 5-12 and Comparative Examples 5-12, the retention time was measured in accordance with the retention strength test of JIS Z 0237 (2009), and the peeling force was measured in accordance with the peel adhesion strength test of JIS Z 0237 (2009). The adhesive properties of each polymer emulsion were then evaluated based on the following criteria for evaluating adhesive properties. For measuring the retention time, first, the polymer emulsions of Examples 5-12 and Comparative Examples 5-12 were coated onto a 38 μm thick PET film, and then dried at 105°C for 3 minutes to create a 20 μm thick coating. Next, a 25 mm x 25 mm test piece was pressed onto a SUS plate with a 2 kg pressure roller so that the coating side was the adhesive surface. After curing for 24 hours, a 1 kg load was suspended, and the time elapsed until the test piece fell in a 40°C environment was measured as the retention time. Furthermore, for measuring the peeling force, polymer emulsions from Examples 5-12 and Comparative Examples 5-12 were first coated onto 38 μm thick PET films, and then dried at 105°C for 3 minutes to create coatings with a thickness of 20 μm. Next, 25 mm x 25 mm test pieces were pressed onto a SUS plate with a 2 kg pressure roller so that the coated side was the adhesive surface, and after curing for 24 hours, the peeling force was measured by pulling the material off at 180° at a speed of 300 mm / min. Then, using the measurement results of the retention time and peeling force of each polymer emulsion, the adhesive properties were evaluated based on the following evaluation criteria for adhesive properties. The evaluation results are shown in Tables 3-4.

[0079] <Evaluation Criteria for Adhesion Properties> ○: Holding time of 6 hours or more and peeling force of 5.0N or more △: Holding time is 6 hours or more and peeling force is less than 5.0 N, or Holding time less than 6 hours and peeling force of 5.0 N or more ×: Holding time less than 6 hours and peeling force less than 5.0N

[0080] [Evaluation of mechanical stability] 50 g of each polymer emulsion from Examples 5-12 and Comparative Examples 5-12 was weighed and subjected to a load of 20 kg at 1000 rpm for 10 minutes using a Marlon stability tester, followed by filtration through an 80-mesh wire mesh. Subsequently, the residue (aggregates) on the wire mesh was washed with water and dried at 105°C for 2 hours, after which its mass was measured. The amount of aggregates relative to the mass of solids in the polymer emulsion (mass %) was calculated, and the mechanical stability was evaluated based on this calculation result and the mechanical stability evaluation criteria described below. The evaluation results are shown in Tables 3-4.

[0081] <Criteria for evaluating mechanical stability> ○: Amount of aggregated material is less than 0.50% by mass. ×: Agglomerated material content is 0.50% by mass or more

[0082] [Evaluation of water resistance] The polymer emulsions obtained in Examples 5-12 and Comparative Examples 5-12 were applied to 2 mm thick glass plates to a thickness of 100 μm, and then dried at 105°C for 3 minutes to prepare coating films. Subsequently, the films were immersed in 25°C water for 6 hours, removed, and the appearance of the coating films was visually observed. The water resistance was evaluated based on the water resistance evaluation criteria described below. The evaluation results are shown in Tables 3-4.

[0083] <Criteria for evaluating water resistance> ○: No whitening was observed. ×: Albinism was observed.

[0084] [Table 3]

[0085] [Table 4]

[0086] From the above results, it can be seen that polymer emulsions with excellent adhesive properties, mechanical stability, and water resistance can be obtained by polymerizing various monomers in the presence of the surfactant composition of the present invention.

Claims

1. A surfactant composition containing 95.5% to 99.2% by mass of an anionic surfactant represented by the following general formula (1) and 0.8% to 4.5% by mass of a nonionic surfactant represented by the following general formula (2). 【Chemistry 1】 (In the formula, R １ (where represents a branched alkyl group with 10 to 15 carbon atoms, m represents a number between 10 and 30, and M represents an ammonium group.) 【Chemistry 2】 (In the formula, R ２ (where n represents a branched alkyl group with 10 to 15 carbon atoms, and n represents a number between 10 and 30.)

2. The surfactant composition according to claim 1, wherein R1 represents a branched alkyl group having 10 to 12 carbon atoms, and R2 represents a branched alkyl group having 10 to 12 carbon atoms.

3. R of an anionic surfactant represented by general formula (1) １ And the R of the nonionic surfactant represented by general formula (2) ２ The surfactant composition according to claim 1 or 2, wherein and are the same alkyl group.

4. The surfactant composition according to claim 1 or 2, which is a surfactant composition for emulsion polymerization.

5. A composition for emulsion polymerization containing the surfactant composition according to claim 1 or 2.

6. A method for producing a polymer emulsion, comprising the step of polymerizing one or more polymerizable monomers selected from the group consisting of acrylate monomers, styrene monomers, and vinyl ester monomers in the presence of the surfactant composition described in claim 1 or 2.

7. A polymer emulsion obtained by polymerizing one or more polymerizable monomers selected from the group consisting of acrylate monomers, styrene monomers, and vinyl ester monomers in the presence of the surfactant composition according to claim 1 or 2.