Styrene-butadiene aqueous dispersion for highly water-resistant, flexible cementitious coating

Abstract

The present invention is directed to an aqueous dispersion, a copolymer, a redispersible polymer powder produced from the aqueous dispersion, a method for preparing waterproofing material, use of the aqueous dispersion or the redispersible polymer powder in waterproofing material, a waterproofing material comprising the aqueous dispersion or the redispersible polymer powder.

Description

Styrene-butadiene aqueous dispersion for highly water-resistant, flexible cementitious coatingTechnical Field

[0001] The present invention is directed to an aqueous dispersion, a copolymer, a redispersible poly-mer powder produced from the aqueous dispersion, a method for preparing waterproofing mate-rial, use of the aqueous dispersion or the redispersible polymer powder in waterproofing materi-al, a waterproofing material comprising the aqueous dispersion or the redispersible polymer powder.Background

[0002] Typically, polymer dispersion modified cementitious material is widely used in the construction or building industry for sealing and protection of the surfaces of any kind of artificial or construc-tion structures. It can provide flexible watertight membrane with a suitable polymer dispersion together with cement, sand and other inorganic fillers. The resulting membrane protects the underlying structures and prevents the penetration of water and other aqueous solutions, other non-aqueous liquids and / or gases such as carbon dioxide or sulfur dioxide. The polymer disper-sion may be, for example, acrylic dispersion, ethylene-vinyl acetate dispersion, chloroprene dis-persion, styrene-butadiene dispersion, acrylonitrile-butadiene dispersion, natural rubber disper-sion or the like. Among them, styrene-acrylate dispersion is mostly used in this area. However, the adhesion strength is usually not high enough when the polymer membrane is designed with high flexibility.

[0003] CN 111269348 describes compositions for preparing carboxyl styrene-butadiene latex which comprise a combination of styrene, butadiene, butyl acrylate and octyl acrylate. High amounts of acrylates are used in the composition which makes the latex suitable for use to prepare con-crete. The use of the latex for preparing waterproofing coating material for cement matrix is not described or suggested.

[0004] CN 101139413 describes compositions for preparing waterproofing coating material which comprise a combination of styrene, butadiene or isoprene, and butyl acrylate.

[0005] However, current commercial product of cementitious waterproofing product in the market could not achieve high water-resistant performance.

[0006] There is a great demand to provide a polymer dispersion for cementitious waterproofing coating application to provide high water-resistant performance based on requirement of GB50108.

[0007] Summary description

[0008] The object of the present invention is to provide an aqueous dispersion which results in a ce-mentitious waterproofing material with good mechanical properties and high water-resistant per-formance, especially meeting the requirement of GB50108.

[0009] It has been surprisingly found that the object is achieved by an aqueous dispersion, a copoly-mer, a redispersible polymer powder produced from the aqueous dispersion, a method for pre-paring waterproofing material, use of the aqueous dispersion or the redispersible polymer pow-der in waterproofing material, a waterproofing material comprising the aqueous dispersion or the redispersible polymer powder.

[0010] In one aspect, the present invention is directed to an aqueous dispersion, comprising

[0011] i) a copolymer prepared by polymerization of ethylenically unsaturated monomers comprising styrene,

[0012] a conjugated diene,

[0013] at least one ethylenically unsaturated functional monomer (F) ,

[0014] an alkoxysilyl functional ethylenically unsaturated monomer (S) , wherein the monomer (S) is present in an amount of 0.01 to 2.5%by weight, based on the total weight of the monomers; and

[0015] an ethylenically unsaturated monomer (K) having 1, 3-diketo group, wherein the monomer (K) is present in an amount of 0.01 to 3.8 %by weight, based on the total weight of the monomers, wherein the functional monomer (F) is selected from the group consisting of an ethylenically unsaturated monomer having an acid group and / or the corresponding anion thereof, an eth-ylenically unsaturated monomer having an amino, amido, ureido, keto, hydroxyl, polyether chain, or N-heterocyclic group and / or protonated on the nitrogen, or alkylated ammonium derivatives thereof;

[0016] wherein the functional monomer (F) , monomer (S) and monomer (K) are different from each other; and

[0017] ii) an emulsifier system, wherein the emulsifier system comprises at least one of nonionic emul-sifier, anionic emulsifier, and cationic emulsifier.

[0018] In another aspect, the present invention is directed to the copolymer as defined in this disclo-sure.

[0019] In another aspect, the present invention is directed to a redispersible polymer powder produced from the aqueous dispersion.

[0020] In another aspect, the present invention is directed to a method for preparing waterproofing ma-terial, comprising at least one step of mixing the aqueous dispersion of the present invention or the redispersible polymer powder of the present invention with at least one hydraulic binder and / or a filler.

[0021] In another aspect, the present invention is directed to use of the aqueous dispersion of the pre-sent invention or the redispersible polymer powder of the present invention in waterproofing material.

[0022] In another aspect, the present invention is directed to a waterproofing material comprising the aqueous dispersion of the present invention, or the redispersible polymer powder of the present invention, and at least one hydraulic binder and / or a filler.

[0023] In another aspect, the present invention is directed to a waterproofing material (1K) or a water-proofing material (2K) .Detailed description

[0024] The present invention would be illustrated in a detailed way hereinafter.

[0025] In one aspect, the present invention is directed to an aqueous dispersion, comprising

[0026] i) a copolymer prepared by polymerization of ethylenically unsaturated monomers comprising styrene,

[0027] a conjugated diene,

[0028] at least one ethylenically unsaturated functional monomer (F) ,

[0029] an alkoxysilyl functional ethylenically unsaturated monomer (S) , wherein the monomer (S) is present in an amount of 0.01 to 2.5%by weight, based on the total weight of the monomers; and

[0030] an ethylenically unsaturated monomer (K) having 1, 3-diketo group, wherein the monomer (K) is present in an amount of 0.01 to 3.8 %by weight, based on the total weight of the monomers, wherein the functional monomer (F) is selected from the group consisting of an ethylenically unsaturated monomer having an acid group and / or the corresponding anion thereof, an eth-ylenically unsaturated monomer having an amino, amido, ureido, keto, hydroxyl, polyether chain, or N-heterocyclic group and / or protonated on the nitrogen, or alkylated ammonium derivatives thereof;

[0031] wherein the functional monomer (F) , monomer (S) and monomer (K) are different from each other; and

[0032] ii) an emulsifier system, wherein the emulsifier system comprises at least one of nonionic emul-sifier, anionic emulsifier, and cationic emulsifier.

[0033] Styrene can be present in an amount of 25 to 90 %by weight (for example 30%, 40%, 50%, 60%, 70%, or 80%by weight) , preferably 35 to 75%by weight, more preferably 40 to 70%by weight, based on the total weight of the monomers.

[0034] The conjugated diene refers to a di-olefin having a pair of conjugated double bonds. Examples of the conjugated diene include 1, 3-butadiene, 2-methyl-1, 3-butadiene (isoprene) , 2, 3-dimethyl-1, 3-butadiene, 1, 3-pentadiene, 2-methyl-1, 3-pentadiene, 2, 4-hexadiene, 1, 3-hexadiene, 1, 3-heptadiene, 2, 4-heptadiene, 1, 3-octadiene, 2, 4-octadiene, 3, 5-octadiene, 1, 3-nonadiene, 2, 4-nonadiene, 3, 5-nonadiene, 1, 3-decadiene, 2, 4-decadiene, 3, 5-decadiene, and / or 1, 3-cyclo-hexadiene. Such dienes may be used singly or in combination of two or more. In a preferred embodiment, the conjugated diene comprises 1, 3-butadiene.

[0035] The conjugated diene can be present in an amount of 10 to 75 %by weight (for example 20%, 40%or 60%) , preferably 25 to 65%by weight, more preferably 30 to 60%by weight, based on the total weight of the monomers.

[0036] Functional monomer (F)

[0037] According to the present invention, the functional monomer (F) is selected from the group con-sisting of an ethylenically unsaturated monomer having an acid group and / or the corresponding anion thereof, an ethylenically unsaturated monomer having an amino, amido, ureido, keto, hy-droxyl, polyether chain, or N-heterocyclic group and / or protonated on the nitrogen, or alkylated ammonium derivatives thereof;

[0038] wherein the functional monomer (F) is different from monomer (S) and monomer (K) .

[0039] Examples of ethylenically unsaturated monomer having an amino are N, N-dimethylaminoethyl acrylate; N, N-diethylaminoethyl acrylate; N, N-dimethylaminopropyl acrylate; N, N-diethylaminopropyl acrylate; N, N-dimethylaminoethyl methacrylate; N, N-diethylaminoethyl methacrylate; N, N-dimethylaminopropyl methacrylate; and N, N-diethylaminopropyl methacrylate.

[0040] Examples of ethylenically unsaturated monomer having an amido group are monoethylenically unsaturated amides, such as (meth) acrylamide, N-methylol (meth) acrylamide, N, N-dimethylacrylamide (DMA) , 2-hydroxyethyl (meth) acrylamide, dimethylaminoethylmethacryla-mide.

[0041] The acid group in ethylenically unsaturated monomer having an acid group can be selected from carboxyl, sulfonic acid group, phosphonic acid or phosphoric acid group.

[0042] Examples of ethylenically unsaturated monomer having an acid group and / or the corresponding anion thereof are monoethylenically unsaturated carboxylic acids, such as (meth) acrylic acid, β-carboxyethyl acrylate, itaconic acid, fumaric acid, citraconic acid, sorbic acid, cinnamic acid, glutaconic acid and maleic acid and the salts thereof, in particular the alkali metal salts thereof; monoethylenically unsaturated sulfonic acids, such as vinyl sulfonic acid, styrene sulfonic acid, acryloxyethansulfonic acid and acrylamido-2-methylpropane sulfonic acid and the salts thereof, in particular the alkali metal salts thereof; monoethylenically unsaturated phosphonic acids such as vinylphosphonic acid, allylphosphonic acid, styrenephosphonic acid and 2-acrylamido-2-methylpropane phosphonic acid and the salts thereof, in particular the alkali metal salts thereof; and also monoethylenically unsaturated phosphoric acids and the salts thereof, in particular the alkali metal salts thereof.

[0043] Examples of ethylenically unsaturated monomer having a ureido are monomers containing urea groups (e.g., ureidoethyl (meth) acrylate) .

[0044] Examples of ethylenically unsaturated monomer having a hydroxyl are hydroxyalkyl (for exam-ple C2 to C6 alkyl) esters of monoethylenically unsaturated carboxylic acids (for example (meth) acrylic acid) , such as hydroxyethyl (meth) acrylate and hydroxypropyl (meth) acrylate, and glycerol (meth) acrylate.

[0045] Examples of ethylenically unsaturated monomer having a polyether chain are monomers con-taining polyalkylene oxide chain, preferably alkylene oxide having 2 to 6, more preferably 2 to 4, or 2 or 3, most preferably 2 carbon atoms, for example the alkylene oxide can be ethylene oxide, propylene oxide or mixture thereof. The molecular weight of the polyether chain can be in the range from 132 to 3000, or from 250 to 2000, or from 300 to 1500, or from 300 to 1000. In an embodiment, the ethylenically unsaturated monomer having a polyether chain carries one (meth) acrylate (ester) group.

[0046] The N-heterocycle mentioned for monomer (F) can have 1 to 3 nitrogen atoms. In addition to the nitrogen atoms there may also, optionally, be further 1 to 2 heteroatoms (for example N, O or S) present in the ring. The N-heterocycle can have 5 or 6 ring members. Examples of eth-ylenically unsaturated monomer having a N-heterocyclic group are 2-vinylpyridine, 4-vinylpyridine, 1-vinylimidazole, 4-vinylimidazole, 1-vinylpyrazole or 1-vinyl-1, 2, 4-triazole.

[0047] In a preferred embodiment, the functional monomer (F) comprises an ethylenically unsaturated monomer having an acid group and / or the corresponding anion thereof, preferably an ethyleni-cally unsaturated monomer having a carboxyl and / or the corresponding anion thereof.

[0048] In an embodiment, the ethylenically unsaturated functional monomer (F) comprises at least two (for example 2, 3 or 4) monomers. In a preferred embodiment, the functional monomer (F) com-prises an ethylenically unsaturated monomer having an acid group and / or the corresponding anion thereof and a further monomer selected from an ethylenically unsaturated monomer hav-ing an amino, amido, ureido, keto, hydroxyl, polyether chain, or N-heterocyclic group and / or protonated on the nitrogen, or alkylated ammonium derivatives thereof. In a preferred embodi-ment, the functional monomer (F) comprises an ethylenically unsaturated monomer having car-boxyl and / or the corresponding anion thereof and a further monomer selected from an ethyleni-cally unsaturated monomer having an amino, amido, ureido, keto, hydroxyl, polyether chain, sulfonic acid group, or N-heterocyclic group and / or protonated on the nitrogen, or alkylated ammonium derivatives thereof. In a preferred embodiment, the functional monomer (F) com-prises an ethylenically unsaturated monomer having carboxyl and / or the corresponding anion thereof and a further monomer selected from an ethylenically unsaturated monomer having an amido, hydroxyl or sulfonic acid group.

[0049] According to the present invention, the functional monomer (F) is different from monomer (S) and monomer (K) .

[0050] In a preferred embodiment, the functional monomer (F) comprises at least two (for example 2, 3 or 4) monomers.

[0051] In a preferred embodiment, the functional monomer (F) is selected from at least one, preferably at least two (for example 2, 3 or 4) of acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, acrylamide, methacrylamide, and their derivatives, vinylsulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, styrenesulfonic acid, their water soluble salts, hy-droxyethyl methacrylate, and hydroxyethyl acrylate.

[0052] In this disclosure, the ethylenically unsaturated functional monomer (F) is present in an amount of 0.01%to 10%by weight (for example 0.05%, 0.1%, 0.5%, 1%, 2%, 5%, 6%or 8%by weight) , preferable 0.05%to 8%by weight, 0.1 to 8%by weight, or 0.1%to 3.5%by weight, based on the total weight of the monomers.

[0053] Alkoxysilyl functional ethylenically unsaturated monomer (S)

[0054] In an embodiment, the alkoxysilyl functional ethylenically unsaturated monomer (S) has at least one di-C1-C4-alkoxysilane group or tri-C1-C4-alkoxysilane group. Of course, the alkoxysilyl func-tional ethylenically unsaturated monomer (S) has an ethylenically unsaturated group.

[0055] Examples of alkoxysilyl functional ethylenically unsaturated monomer (S) include vinyltri-methoxysilane, vinyltriethoxysilane, methacryloxyethyl trimethoxysilane, methacryloxyethyl tri-ethoxysilane, vinyl tris- (2-methoxyethoxy silane) , vinyl triisopropoxysilane, (3-methacryloxypropyl) -trimethoxysilane, (3-methacryloxypropyl) -triethoxysilane, (3-methacryloxypropyl) -triisopropoxysilane, 2-methyl-2-propenoic acid 3- [tris- (1-methylethoxy) -silyl] -propyl ester, (3-methacryloxypropyl) -methyldiethoxysilane or combinations thereof.

[0056] According to the present invention, the monomer (S) is present in an amount of 0.01 to 2.5%by weight (for example 0.05%, 0.1%, 0.5%, 0.15%, 0.18%, 0.2%, 0.22%, 0.24%, 0.25%, 0.3%, 0.4%, 0.5%, 0.8%, 1%, 1.5%, or 2.2%by weight) , preferably 0.1 to 2.2%by weight, more pref-erably 0.15 to 2.1%by weight, or from 0.22 to 2.1%by weight, based on the total weight of the monomers.

[0057] Ethylenically unsaturated monomer (K) having 1, 3-diketo group

[0058] Monomer (K) can include acetoacetoxyethyl acrylate, 2-acetoacetoxyethyl methacrylate (AAE-MA) , acetoacetoxypropyl acrylate, acetoacetoxypropyl methacrylate, acetoacetoxybutyl acrylate, acetoacetoxybutyl methacrylate, diacetoneacrylamide (DAAM) and diacetonemethacrylamide, preferably 2-acetoacetoxyethyl methacrylate (AAEMA) .

[0059] According to the present invention, the monomer (K) is present in an amount of 0.01 to 3.8 %by weight (for example 0.05%, 0.1%, 0.5%, 1%, 1.5%, 2%, 2.5, 3%or 3.5%by weight) , preferably 0.1 to 3%by weight, more preferably 0.2 to 2.5%by weight, based on the total weight of the monomers.

[0060] According to the present invention, monomer (K) , monomer (S) and monomer (F) are monoeth-ylenically unsaturated monomer.

[0061] Other monomers

[0062] If desired, the ethylenically unsaturated monomers for preparing the copolymer (i) can further comprise itaconic and / or (meth) acrylic acid ester.

[0063] If present, itaconic and / or (meth) acrylic acid ester is present in an amount of about 0.1 to 50%, preferably about 0.1 to 40%by weight, based on the total weight of the monomers.

[0064] In an embodiment, the total amount of itaconic and (meth) acrylic acid ester is no more than 10%by weight, or no more than 5%by weight, or no more than 2%by weight, or no more than 1%by weight, or no more than 0.5%by weight, or no more than 0.1%by weight, based on the total weight of the monomers.

[0065] The itaconic and / or (meth) acrylic acid esters may be C1 to C18, preferably C1 to C10, more pref-erably C1 to C8 alkyl ester of itaconic and / or (meth) acrylic acid, such as methyl ester, ethyl ester, n-propyl ester, iso-propyl ester, n-butyl ester, sec-butyl ester, iso-butyl ester, n-amyl ester, iso-amyl ester, n-hexyl ester, iso-hexyl ester, heptyl ester, octyl ester, 2-ethylhexyl ester, nonyl es-ter, decyl ester, undecyl ester, dodecyl ester, tridecyl ester, tetradecyl ester, pentadecyl ester, hexadecyl ester, heptadecyl ester, octadecyl ester; or C5 to C18, preferably C5 to C10, more pref-erably C5 to C8 cycloalkyl ester of itaconic and / or (meth) acrylic acid, such as cyclopentyl ester, cyclohexyl ester, cycloheptyl ester, or cyclooctyl ester; preferably methyl ester, ethyl ester, n-propyl ester, iso-propyl ester, n-butyl ester, sec-butyl ester, iso-butyl ester, n-amyl ester, iso-amyl ester, n-hexyl ester, iso-hexyl ester, heptyl ester, octyl ester, or 2-ethylhexyl ester; more preferably methyl ester, ethyl ester, n-propyl ester, iso-propyl ester, n-butyl ester, sec-butyl ester, iso-butyl ester, or 2-ethylhexyl ester.

[0066] In an embodiment, the itaconic and / or (meth) acrylic acid esters are selected from the group of n-butyl acrylate, methyl acrylate and methyl methacrylate (MMA) .

[0067] The itaconic and / or (meth) acrylic acid esters are typically produced by esterification of itaconic and / or (meth) acrylic acid with alkanol, or by transesterification of itaconic and / or (meth) acrylic acid with alkanol.

[0068] Alkanols can be produced on large scale by fermentation from a variety of renewable feed-stocks, including corn, wheat, sorghum, barley, and sugar cane, in particular from cellulose con-taining raw material and thus from biological sources or renewable raw materials, respectively. Therefore, including itaconic and / or (meth) acrylic acid esters into the aqueous dispersion signif-icantly increases the amount of bio-carbon in the aqueous dispersion and thereby reduces the demand of fossil carbon and, hence, the CO2 demand of the production of the aqueous disper-sion. In particular, the amount of carbon of biological origin of at least 10 mol-%, in particular at least 15 mol-%or at least 20 mol-%or higher, e.g., 30 mol-%or 40 mol-%or higher can be achieved.

[0069] It is also possible that at least part of the educts used to synthesize bio-based itaconic and / or (meth) acrylic acid esters from renewable raw materials according to the mass balance ap-proach. Accordingly, in addition to fossil feeds, also renewable feeds such as bio-naphtha (as  e.g., described in EP 2 290 045 A1 or EP 2 290 034 A1) enter the chemical production system, such as a steam cracker. The renewable feeds are converted into products along the chemical value chain, The content of renewable material of these products is defined by the mass bal-ance approach and can be allocated to these products.

[0070] The term “bio-carbon” indicates that the carbon is of biological origin and comes from a bio-material / renewable resource. The content in bio-carbon and the content in biomaterial are ex-pressions that indicate the same value. A material of renewable origin or biomaterial is an or-ganic material wherein the carbon comes from the CO2 fixed recently by photosynthesis from the atmosphere. A biomaterial (Carbon of 100%natural origin) has an isotopic ratio 14C / 12C greater than 10-12, typically about 1.2×10-12, while a fossil material has a zero ratio. Indeed, the isotopic 14C is formed in the atmosphere and is then integrated via photosynthesis, according to a time scale of a few tens of years at most. The half-life of the 14C is 5, 730 years. Thus, the ma-terials coming from photosynthesis, namely plants in general, necessarily have a maximum con-tent in isotope 14C. The determination of the content of biomaterial or of bio-carbon can be car-ried out in accordance with the standards ASTM D 6866-12, the method B (ASTM D 6866-06) and ASTM D 7026 (ASTM D 7026-04) .

[0071] In a preferred embodiment, the copolymer (i) is prepared by polymerization of ethylenically un-saturated monomers comprising

[0072] a) 25 to 90 %by weight, preferably 35 to 75%by weight, more preferably 40 to 70%by weight styrene,

[0073] b) 10 to 75 %by weight, preferably 25 to 65%by weight, more preferably 30 to 60%by weight conjugated diene,

[0074] c) 0.01 to 2.5%by weight, preferably 0.1 to 2.2%by weight, more preferably 0.15 to 2.1%by weight ethylenically unsaturated monomer (S) ,

[0075] d) 0.01%to 10%by weight, preferable 0.05%to 8%by weight, or 0.1%to 3.5%by weight ethylenically unsaturated functional monomer (F) , and

[0076] e) 0.01 to 3.8 %by weight, preferably 0.1 to 3%by weight, more preferably 0.2 to 2.5%by weight monomer (K) ,

[0077] in each case based on the total weight of the monomers.

[0078] The preparation of the copolymer is in principle familiar to the person skilled in the art and can be carried out, for example, by free-radical polymerization, bulk polymerization, emulsion polymerization, solution polymerization, precipitation polymerization or suspension polymeriza-tion of the monomers, although aqueous emulsion polymerization is particularly preferred. It is therefore advantageous according to the invention for the copolymer to be dispersed in an aqueous medium, i.e. to be used in the form of an aqueous emulsion.

[0079] The preparation of copolymer in aqueous media has been described in large numbers of refer-ences. The aqueous emulsion polymerization of the monomers is therefore well known to the person skilled in the art [see, for example, Emulsion polymerization in Encyclopedia of Polymer Science and engineering, Vol. 8, p. 659 ff. (1987) ] .

[0080] The aqueous emulsion polymerization is usually carried out by dispersing the monomers in an aqueous medium, usually with the use of dispersing assistants, such as surfactants and / or pro-tective colloids, and with the use of at least one water-soluble free-radical polymerization initia-tor.

[0081] The aqueous emulsion polymerization may be carried out by first adding the total weight of monomers and the initiator before initiating the polymerization. However, it is also possible, op-tionally, to initially charge only a portion of the monomers in the aqueous reaction medium be-fore initiating the polymerization and then, after initiating the polymerization, to charge the entire or remaining amount under the polymerization conditions during the free-radical emulsion polymerization, continuously at a constant or varying flow rate, or discontinuously. The mono-mers can be metered in as individual streams, as a homogeneous or heterogeneous (partial) mixture, or as a monomer emulsion. Advantageously, the monomers are metered in as a mix-ture.

[0082] The copolymer used in the invention is obtained in the form of its aqueous emulsion by the sim-ultaneous use of a dispersing assistant which maintains the monomer droplets and the pro-duced polymer particles in a dispersed state in the aqueous medium and ensures the stability of the produced aqueous emulsion. As dispersing assistants, protective colloids and / or emulsifiers are considered which are customarily used for carrying out free-radical aqueous emulsion polymerization.

[0083] Suitable protective colloids are, for example, polyvinyl alcohols, polyalkylene glycols, alkali met-al salts of polyacrylic acids and polymethacrylic acids; gelatin derivatives; or acrylic acid-, meth-acrylic acid-or maleic anhydride-containing homopolymers and copolymers, copolymers con-taining 2-acrylamido-2-methyl-1-propanesulfonic acid and / or 4-styrenesulfonic acid and alkali metal salts thereof, and also N-vinylpyrrolidone, N-vinylcaprolactam, N-vinylcarbazole, 1-vinylimidazole, 2-vinylpyridine, 4-vinylpyridine, acrylamide, meth acrylamide, amino-containing acrylates, methacrylates, acrylamide and / or meth acrylamide homopolymers and copolymers. Further suitable protective colloids are described for example in Houben-Weyl, Methoden der organischen Chemie, volume XIV / 1, Makromolekulare Stoffe, Georg-Thieme-Verlag, Stuttgart, 1961, pages 411 to 420. The protective colloids preferably used as dispersing assis-tants are advantageously used in a total weight of 0.005 to 10%by weight, preferably 0.01 to  5%by weight and more particularly 0.1 to 4%by weight, based on the total weight of the mon-omers.

[0084] The polymerization is carried out in the presence of initiator which form radicals under the reaction conditions. The initiator may be peroxides or else azo compounds. Redox initiator systems are also contemplated, of course.

[0085] Peroxides used may in principle be inorganic peroxides and / or organic peroxides. Examples of suitable inorganic peroxides include hydrogen peroxide and also persulfates, such as the mono-or di-alkali metal or -ammonium salts of persulfuric acid, examples being its mono-and di-sodium, -potassium or -ammonium salts, such as sodium persulfate, potassium persulfate and ammonium persulfate. Examples of suitable organic peroxides are alkyl hydroperoxides such as tert-butyl hydroperoxide, aryl hydroperoxides such as p-menthyl hydroperoxide or cumene hydroperoxide, dialkyl or diaryl peroxides, such as di- (tert-butyl) peroxide, and benzoyl peroxide or di-cumene peroxide, and peroxy esters.

[0086] Azo compounds used are essentially 2, 2′-azobis (isobutyronitrile) , 2, 2′-azobis (2-methylbutyronitrile) , 2, 2′-azobis (2, 4-dimethylvaleronitrile) , 2, 2′-azobis (N, N′-dimethyleneisobutyroamidine) dihydrochloride and 2, 2′-azobis (amidinopropyl) dihydrochloride.

[0087] Redox initiator systems are combined systems composed of at least one organic or inorganic reducing agent and at least one oxidizing agent. Oxidizing agents contemplated for redox initiator systems are essentially the peroxides stated above. As corresponding reducing agents it is possible to use compounds of sulfur in a low oxidation state, such as alkali metal sulfites, as for example potassium and / or sodium sulfite, alkali metal hydrogensulfites, as for example potassium and / or sodium hydrogensulfite, alkali metal metabisulfites, as for example potassium and / or sodium metabisulfite, acetone bisulfite, formaldehyde-sulfoxylates, as for example potassium and / or sodium formaldehyde-sulfoxylate, alkali metal salts, especially potassium and / or sodium salts, of aliphatic sulfinic acids, and alkali metal hydrogensulfides, such as potassium and / or sodium hydrogensulfide, for example, salts of polyvalent metals, such as iron (II) sulfate, iron (II) ammonium sulfate, iron (II) phosphate, enediols, such as dihydroxymaleic acid, benzoin and / or ascorbic acid, and also reducing saccharides, such as sorbose, glucose, fructose and / or dihydroxyacetone.

[0088] Preferred initiators are peroxy type initiators such as hydrogen peroxide, tert-butyl hydroperoxide, di- (tert-butyl) peroxide, benzoyl peroxide, peroxy esters; and persulfates such as sodium persulfate, potassium persulfate and ammonium persulfate; and azo type initiators.

[0089] The polymerization takes place in general by using 0.1 to 5%by weight of the radical initiator, preferably 0.5 to 4%by weight of the radical initiator, based on the total weight of the monomers.

[0090] Initiation of the polymerization reaction refers to the start of the polymerization reaction of the monomers present in the polymerization vessel through decomposition of the radical initiator. The polymerization starts, for example, when the polymerization mixture contains monomers and inorganic peroxide and reaches a temperature in the range from 60℃ to 125℃, preferably from 70℃ to 100℃, more preferably from 80℃ to 95℃.

[0091] In addition to the above components, a molecular weight regulator may optionally be used dur-ing the emulsion polymerization to reduce / correct the molecular weight of the copolymer obtain-able by the polymerization. It is possible to use predominantly aliphatic and / or aromatic halogen compounds, for example halogenated hydrocarbons, such as n-butyl chloride, n-butyl bromide, n-butyl iodide, methylene chloride, ethylene chloride, chloroform, bromoform, bromotrichloro-methane, dibromomethylene chloride, carbon tetrachloride, carbon tetrabromide, benzyl chlo-ride, benzyl bromide, organosulfur compounds, such as aliphatic primary, secondary or tertiary mercaptans, for example ethylmercaptan, n-propylmercaptan, 2-propylmercaptan, n-butylmercaptan, 2-methyl-2-propylmercaptan, n-pentylmercaptan, 2-pentylmercaptan, 3-pentylmercaptan, 2-methyl-2-butylmercaptan, 3-methyl-2-butylmercaptan, n-hexylmercaptan, 2-hexylmercaptan, 3-hexylmercaptan, 2-methyl-2-pentylmercaptan, 3-methyl-2-pentylmercaptan, 4-methyl-2-pentylmercaptan, 2-methyl-3-pentylmercaptan, 3-methyl-3-pentylmercaptan, 2-ethylbutylmercaptan, 2-ethyl-2-butylmercaptan, n-heptylmercaptan and its isomer compounds, n-octylmercaptan and its isomer compounds, n-nonylmercaptan and its isomer compounds, n-decylmercaptan and its isomer compounds, n-undecylmercaptan and its isomer compounds, n-dodecylmercaptan and its isomer compounds, n-tridecylmercaptan and its isomer compounds, substituted mercaptans, e.g. 2-hydroxyethylmercaptan, tertiary dodecyl mercaptan, aromatic mercaptans such as benzenethiol, o-benzenethiol, m-or p-methylbenzenethiol, and all others described in Polymerhandbook, 3rd edition, 1989, J. Brandrup and E. H. Immergut, John Wiley & Sons, section II, sulfur compounds from pages 133 to 141, as well as aliphatic and / or aro-matic aldehydes such as acetaldehyde, propionaldehyde and / or benzaldehyde, unsaturated fatty acids such as oleic acid, dienes with nonconjugated double bonds such as divinylmethane or vinylcyclohexane or terpinolene, olefns such as cyclohexene, alpha-methyl styrene and its dimer, or hydrocarbons with readily removable hydrogen atoms such as toluene.

[0092] The total weight of molecular weight regulator used during the emulsion polymerization is gen-erally 5%by weight or less, often 3%by weight or less and often 1%by weight or less, based on the total weight of the monomers. In an embodiment, the total weight of molecular weight  regulator used during the emulsion polymerization is in the range from 0.1%to 5%by weight, or 0.2 to 3%by weight, based on the total weight of the monomers.

[0093] In another embodiment, the aqueous dispersion further comprises a crosslinker. Examples of crosslinker are compounds having at least two functional groups selected from oxazoline, amino, aldehyde, aminoxy, carbodiimide, aziridinyl, epoxy and hydrazide groups, derivatives or com-pounds bearing acetoacetyl groups.

[0094] In an embodiment, the amount of crosslinker used during the emulsion polymerization is in the range from 0%to 10%by weight, or 0 to 7%by weight, based on the total weight of the monomers.

[0095] When it is desired to set the particle size of the polymer particles obtainable by the aqueous emulsion polymerization to a specific value, polymer seeds are used in particular (see, for ex-ample, US 2520959A and US 3397165A) . The seed may be used in an amount of from about 0.01 to about 5%by weight, usually from about 0.05 to about 3%by weight and frequently from about 0.1 to about 2.5%by weight of polymer seeds, based on the total weight of the monomers.

[0096] One type of polymer seed used is in particular polymer seed particles which have a particle size of 60nm or less, usually from 5nm to 50nm and usually from 15nm to 35nm, determined by light scattering.

[0097] When polymer seeds are used, it is advantageous to use exogenous polymer seeds. Unlike in-situ polymer seeds, which are prepared in the reaction vessel before the actual emulsion polymerization reaction begins and which have the same monomer composition as the polymer prepared by the subsequent free-radically initiated aqueous emulsion polymerization reaction, exogenous polymer seeds are polymer seeds which are prepared in a separate reaction step and whose monomer composition differs from the polymer prepared by the aqueous emulsion polymerization reaction, although this means only different monomers, or monomer composi-tions having different compositions, for preparing exogenous polymer seeds and for preparing the copolymer. The preparation of exogenous polymer seeds is well known to those skilled in the art and is generally accomplished by introducing as an initial charge into a reaction vessel having a relatively small amount of monomer and a relatively large amount of surfactant, and by addition of a sufficient amount of polymerization initiator at the reaction temperature.

[0098] According to the invention, it is preferred to use exogenous polymer seeds having a glass tran-sition temperature of more than 50 ℃, usually from 60 to 100℃ and often from 70℃ to 100 ℃. Particularly preferred are polystyrene or polymethylmethacrylate polymer seeds.

[0099] The entire amount of exogenous polymer seeds may be charged first to the polymerization re-action vessel. It is also possible to include only a portion of the exogenous polymer seeds in the initial charge being added to the polymerization vessel and to add monomers along with the remainder during the polymerization. However, if desired, the entire amount of polymer seed may also be added during the polymerization. Preferably, the entire amount of exogenous pol-ymer seeds is first charged to the polymerization vessel prior to initiating the polymerization re-action.

[0100] The polymerization reaction may be carried out at a temperature of 60℃ to 125℃, preferably from 70℃ to 100℃, more preferably from 80℃ to 95℃ for a period of 1 to 10 hours, preferably 2 to 8 hours, more preferably 4 to 6 hours.

[0101] The glass transition temperature Tg of the copolymer obtainable by emulsion polymerization can in principle be in the range from -30 to 5 ℃, preferably -20 to 0℃. The glass transition tem-perature Tg is understood here to mean the actual glass transition temperature which is the midpoint temperature determined by means of Differential Scanning Calorimetry (DSC) accord-ing to ASTM D3418-82 [see also Ullmann's Encyclopedia of Industrial Chemistry, p. 169, Verlag Chemistry, Weinheim, 1992] .

[0102] A theoretical glass transition temperature can be calculated from the monomers used in the emulsion polymerization. The theoretical glass transition temperatures are usually calculated from the monomers by the Fox equation: 1 / Tgt = xa / Tga + xb / Tgb + .... xn / Tgn,

[0103] In this equation xa, xb, .... xn are the mass fractions of the monomers a, b, .... n and Tga, Tgb, .... Tgn are the actual glass transition temperatures in Kelvin of the homopolymers synthesized from only one of the monomers a, b, .... n at a time. The Fox equation is described by T. G. Fox in Bull. Am. Phys. Soc. 1956, 1, page 123 and as well as in Ullmann's  der tech-nischen Chemie [Ullmann's Encyclopedia of Industrial Chemistry] , vol. 19, p. 18, 4th ed., Verlag Chemie, Weinheim, 1980. The actual Tg values for the homopolymers of most monomers are known and listed, for example, in Ullmann’s  der technischen Chemie [Ullmann's Encyclopedia of Industrial Chemistry] , 5th ed., vol. A21, p. 169, Verlag Chemie, Weinheim, 1992. Further sources of glass transition temperatures of homopolymers are, for example, J. Brandrup, E. H. Immergut, Polymer Handbook, 1st Ed., J. Wiley, New York 1966, 2nd Ed. J. Wiley, New York 1975, 3rd Ed. J. Wiley, New York 1989 and 4th Ed. J. Wiley, New York 2004.  Usually, the theoretical glass temperature Tgt calculated according to Fox as described herein and the experimentally determined glass transition temperature as described herein are similar or even same and do not deviate from each other by more than 5 K, in particular they deviate not more than 2 K. Accordingly, both the actual and the theoretical glass transition temperatures of the copolymer can be adjusted by choosing proper monomers a, b …n and their mass frac-tions xa, xb, .... xn in the monomers so to arrive at the desired glass transition temperature. It is common knowledge for a skilled person to choose the proper amounts of monomers a, b …n for obtaining a copolymer and / or copolymer phase with the desired glass transition temperature.

[0104] After the polymerization, the residue content of the monomers is generally removed in order to deodorize, such as by chemical and / or physical processes. The typical chemical and / or physical deodorization processes are known to the person skilled in the art [see, for example, EP-A771328, DE-A19624299, DE-A19621027, DE-A19741184, DE-A19741187, DE-A19805122, DE-A19828183, DE-A19839199, DE-A19840586 and 19847115] . The chemical deodorization process may be carried out by adding a further radical initiator from the group of the abovemen-tioned initiators to the reaction mixture, or to prolong the addition thereof, and carrying out what is called an “Post-polymerization” , in other words a polymerization for achieving a conversion of 95 to 99%. It is sufficient in the majority of cases for the reaction mixture to be stirred for 0.1 to 3 hours, preferably 0.5 to 2 hours, more preferably 0.5 to 1 hour, at the polymerization tempera-ture, after the end of the addition of monomer. The physical deodorization process may be car-ried out by stripping with steam or inert gas, in order to reduce the content of the monomers.

[0105] The solid content is adjusted to the desired value by dilution or concentration, or the resulted aqueous emulsion is mixed with further conventional additives, for example bactericides, foam-modifying additives or viscosity-modifying additives.

[0106] The solid content was determined by drying a defined amount of the aqueous dispersion (about 2 g) to constant weight in an aluminum crucible having an internal diameter of about 5 cm at 130℃ in a drying cabinet (2 hours) . Two separate measurements were conducted. The value reported in the example is the mean of the two measurements.

[0107] The aqueous dispersion (for example obtainable by the emulsion polymerization) generally have a solid content of 10 to 70%by weight, usually 20 to 65%by weight and frequently 25 to 60%by weight, based on the total weight of the aqueous dispersion.

[0108] The particle size of the aqueous dispersion, determined by dynamic light scattering (DLS) using a Malvern HPPS, is generally in the range of 80 to 300nm (for example 100nm, 120 nm, 150nm, 170nm, 180nm, 200nm or 220nm) , frequently in the range of 100 to 250nm.

[0109] The polymerization may be carried out by firstly adding the total weight of monomers and the initiator before initiating the polymerization. However, it is also possible to charge the monomers and the initiator into the aqueous reaction medium continuously at a constant or varying flow rate. The monomers can be metered in as individual streams, as a homogeneous or heteroge-neous (partial) mixture. Advantageously, the monomers are metered in as individual streams.

[0110] The process for producing the aqueous dispersion of the present disclosure may be a single stage polymerization or a multistage emulsion polymerization. In a single stage polymerization, the overall composition of the monomers, which are fed to the polymerization reaction under polymerization conditions, remains the same or almost the same, while in a multistage emulsion polymerization the overall composition of the monomers, which are fed to the polymerization reaction under polymerization conditions, is altered at least once, in particular such that the the-oretical glass transition temperature of the resulting polymer formed in one stage differs from the theoretical glass transition temperature of the resulting polymer formed in another stage by at least 10℃, in particular by at least 20℃ or at least 40℃.

[0111] In a particular group of embodiments, the process of the invention is performed as a 2-stage emulsion polymerization, i.e. the composition of the monomers, which are fed to the polymeriza-tion reaction under polymerization conditions, is altered once, or as a 3-or 4-stage emulsion polymerization, i.e. the composition of the monomers, which are fed to the polymerization reac-tion under polymerization conditions, is altered twice or trice.

[0112] The emulsifier system comprises at least one of nonionic emulsifier, anionic emulsifier, and cat-ionic emulsifier and combination thereof, for example a combination of at least one nonionic emulsifier and at least one anionic emulsifier.

[0113] The nonionic emulsifier in the emulsifier system is selected from the group consisting of ethox-ylated mono-, di-, and tri-alkylphenols and ethoxylated fatty alcohols or alkylphenol / fatty alcohol with polymerizable moiety. Examples thereof are those available from BASF SE Trademark  A (C12C14 fatty alcohol ethoxylate, EO degree: 3 to 8) , Trademark AO (C13C15 oxo-alcohol ethoxylate, EO degree: 3 to 30) , Trademark AT (C16C18 fatty al-cohol ethoxylate, EO degree: 11 to 80) , Trademark ON (C10 oxo-alcohol, EO degree: 3 to 11) , Trademark TO (C13 oxo-alcohol, EO degree: 3 to 20) .

[0114] The anionic emulsifier in the emulsifier system is selected from the group consisting of alkali metal salts and ammonium salts of alkyl sulfates, of sulfuric monoesters with ethoxylated alka- nols and with ethoxylated alkylphenols, of alkylsulfonic acids, of alkoxylated alkanols sulphate, and of alkylarylsulfonic acids, or alkylphenol / fatty alcohol sulphate with polymerizable moiety and a combination thereof. Examples thereof are those available from BASF SE Trademark  LDBS (sodium salts of linear C10C13-alkyl benzene sulfonate) and Trademark Dis- FES (sodium salts of fatty alcohol ethersulfate) .

[0115] Suitable anionic emulsifiers also include compounds of the general formula (I) ,

[0116] wherein R 1 and R2 is H atom or C1 to C24 alkyl radical, with the proviso that R 1 and R2 are not H at the same time, and M1 and M2 may be an alkali metal ion and / or an ammonium ion. In the general formula (I) , R1 and R2 preferably have 6 to 18 carbon atoms, more particularly 6 carbon atoms. M1 and M2 preferably is sodium, potassium or ammonium, sodium. Of particular ad-vantage M1 and M2 are all sodium, R1 is a branched alkyl group of 12 carbon atoms and R2 is H atom or R1.

[0117] And the cationic emulsifier in the emulsifier system is selected from the group consisting of posi-tively charged amines and quaternary ammonium compounds with polymerizable moiety. The polymerizable moiety may be any moiety that could be polymerized by free radical polymeriza-tion, for example, allyl group, (meth) acrylamide group, styryl group, (meth) acrylate group or ma-leate group. The emulsifier with polymerizable moiety and its preparation is known from the pri-or art and commercially available. Suitable emulsifiers with polymerizable moiety may be, sodi-um 2-acrylamido-2-methyl-propyl sulfonate, sodium allyloxy hydroxylpropyl sulfonate, and am-monium allyloxy alkyl phenol polyethylene oxide sulfate. Numerous other examples are found in H. Stache, Tensid-Taschenbuch, Carl-Hanser-Verlag, Munich, Vienna, 1981 and McCutcheon's , Emulsifiers & Detergens, MC Publishing Company, Glen Rock, 1989.

[0118] The emulsifier system is advantageously used in a total weight of 0.005 to 10%by weight (0.01%, 0.05%, 0.1%, 0.5%, 1%, 2%, 5%, 6%or 8%by weight) , preferably 0.01 to 5%by weight and more particularly 0.1 to 4%by weight, based on the total weight of the aqueous dis-persion.

[0119] On aspect of this disclosure is direct to copolymer (i) of the present invention.

[0120] On aspect of this disclosure is direct to a redispersible polymer powder produced from the aqueous dispersion.

[0121] The obtained dispersion could be dried to obtain a redispersible polymer powder. Drying can be carried out in a conventional manner, for example by spray drying, fluidized bed drying, drum drying, flash drying, freeze drying or drying under ambient conditions.

[0122] “Redispersible” as used herein means that the particle size, as determined by dynamic light scattering, of the polymer particles after drying and redispersing in an artificial solution (alkaline aqueous solution containing: Ca2+10 mmol / L, Na+ 98.5 mmol / L, K+ 181.6 mmol / L, SO42-86.2 mmol / L, pH=13.1) is ≤ 1000nm, preferably ≤ 600nm and in particular ≤ 400nm.

[0123] One aspect of the present invention is directed to a waterproofing material comprising the aqueous dispersion of the present invention, or the redispersible polymer powder of the present invention, and at least one hydraulic binder and / or a filler.

[0124] The aqueous dispersion or the redispersible polymer powder could be used in waterproofing material in the building sector by mixing with at least one hydraulic binder and / or a filler. There-fore, in one embodiment, the present invention is directed to a method for preparing waterproof-ing material, comprising at least one step of mixing the aqueous dispersion or the redispersible polymer powder with at least one hydraulic binder and / or a filler.

[0125] The hydraulic binder maybe calcium silicate cement such as ordinary portland cement, calcium aluminate cement, calcium sulfate source, calcium sulfoaluminate cement or latent hydraulic materials such as metakaolin, calcium metasilicate, volcanic slag, volcanic tuff, trass, fly ash, blast furnace slag which are often labeled as supplementary cementitious materials (SCM) etc.

[0126] The content of the hydraulic binder may be from about 1 to 70 %by weight (for example 5%, 10%, 15%, 20%, 30%, 40%, 50%or 60%by weight) , preferably from about 1 to 60%by weight, more preferably from about 1 to 50%by weight, or from 5 to 50%by weight, or from about 10 to 50%by weight or from 20 to 50%by weight, based on the total weight of the waterproofing ma-terial.

[0127] The waterproofing material may further comprise fillers, additives, fibers and / or pigments.

[0128] In an embodiment, fillers comprise inorganic filler and / or organic filler. Inorganic fillers are pre-ferred, such as gypsum, including chalk, talcum, sand, lime, silica, or CaCO3. Organic filler such as ground rubber can also be used in the waterproofing material.

[0129] In a particular embodiment, inorganic pigments are preferred, such as white pigments like tita-nium dioxide (C. I. Pigment White 6) , CaCO3, but also color pigments.

[0130] Examples of additives are flame-proofing materials; antioxidants; fungicides; accelerators such as alkali metal carbonates; retardants such as tartaric acid or citric acid; thickener; foam inhibi-tors; preservatives; wetting agents; rheology modifying agents; vulcanizing agents; adhesion aids, etc. The thickener may be associative thickeners. Associative thickeners are generally hydrophobically modified polymer thickeners having hydrophilic and hydrophobic structural units side by side. Important typical members of this class of thickeners are the polyurethane thick-eners (=hydrophobically modified, ethoxylated urethanes HEUR or PU thickeners) and the HASE thickeners (=hydrophobically modified alkali-swellable emulsions) .

[0131] In one embodiment, the waterproofing material may comprise 10 to 40 %by weight, preferably 15 to 30 %by weight, most preferred 18 to 20 %by weight of the redispersable polymer powder of the present invention, based on the weight of the waterproofing material.

[0132] In another embodiment, the waterproofing material may comprise 10 to 80%by weight, prefera-bly 20 to 70%by weight, or 30 to 60%by weight of the aqueous dispersion of the present inven-tion, based on the weight of the waterproofing material.

[0133] In one embodiment, the waterproofing material (1K) comprises

[0134] 1 to 50 %by weight hydraulic binder,

[0135] 40 to 77 %by weight filler,

[0136] 10 to 40 %by weight, preferably 15 to 30 %by weight, most preferred 18 to 20 %by weight of the redispersable polymer powder of the present invention, and

[0137] 0 to 5 %by weight one or more additives,

[0138] in each case based on the weight of the waterproofing material (1K) .

[0139] In another embodiment, the waterproofing material (2K) comprises

[0140] (a) a dry component comprising

[0141] 20 to 80 %by weight hydraulic binder,

[0142] 20 to 80 %by weight filler, and

[0143] 0 to 5 %by weight one or more additives,

[0144] in each case based on the weight of the total dry component, and

[0145] (b) a wet component comprising

[0146] 80 to 100%by weight of an aqueous dispersion of the present invention, and optionally one or more additives,

[0147] in each case based on the weight of the total wet component,

[0148] and wherein the ratio of dry component (a) to wet component (b) is in the range of 4: 1 to 1: 2.

[0149] The ratio of dry component (a) to wet component (b) can be 3: 1, 2: 1, 1: 1, or 2: 3.

[0150] Typically, the waterproofing material is used in the construction or building industry for sealing and protection of the surfaces of any kind of artificial or construction structures by coating such structures with the waterproofing material that after hydration and hardening form membranes. The resulting membranes protect the underlying structures and prevent the penetration of water and other aqueous solutions, other non-aqueous liquids and / or gases such as carbon dioxide or sulfur dioxide. Furthermore, the waterproofing membranes are also used beneath tiles and slabs of stone or other materials for example on balconies or terraces. In such cases the water-proofing membranes functions not only as a waterproofing membrane, but also as an adhesive and is applied directly to the concrete, masonry or other substrate surface. Further coverings of tiles and slabs are then laid thereon.

[0151] The waterproofing material is applied in one or more layers. In many cases two layers, between 0.5 and 10 mm are applied. The final waterproofing membranes have a thickness of more than 0.5 mm, particularly more than 1 mm. The waterproofing material is usually applied with brushes, swabs, trowels or sprayed.

[0152] The waterproofing material may also be utilized for producing or manufacturing stable and high-ly flexible waterproofing membranes. Such waterproofing membranes may optionally contain a base fabric or matrix which is coated on one or both sides with the inventive composition as a coating to form a non-permeable barrier. Such waterproofing membranes may be composed of one or more layers of each waterproofing material and / or base fabric or matrix and constitute a single or multiple ply membrane. Alternatively, the flexible waterproofing membranes may be prepared by immersing a base fabric or matrix into a bed of waterproofing material, the slurry evenly spread out whereby the slurry and base fabric or matrix combine and form a single foil or wallpaper-like element. These waterproofing membranes can be used in various construction and architectural applications. These types of membranes are generally designed for direct in-stallation, with or without combination with any other layers or materials to provide a waterproof-ing barrier. The base fabric or matrix may be selected from woven, knitted or non-woven natural or polymeric fibers, glass fibers, a polymeric adhesive coating, and optionally a polymeric coat-ing on one or both sides of the base fabric. The resulting flexible waterproofing membranes can  be manufactured or prefabricated in the form of a foil or wallpaper of controlled quality and stored for further use. Such a prefabricated foil can be utilized as a wallpaper providing for ex-ample an immediate to use underground for further tiling without the need of waiting several hours of drying before tile adhesive can be applied as required for standard waterproofing slur-ries.

[0153] The waterproofing material of the present invention shows low Tg, high adhesion strength to the concrete substrate, good tensile strength and elongation at break, and high water-resistant per-formance, for example, the waterproofing membranes formed from the waterproofing material still show high adhesion strength to the concrete substrate, good tensile strength and elongation at break after soaking in water.

[0154] The invention also further relates to the use of the aqueous dispersion or the redispersible pol-ymer powder of the invention in a waterproofing material. It is particularly advantageous that the waterproofing material can be used in the form of dry mixes because the redispersible polymer powder of the invention has particularly good redispersibility.

[0155] More particularly, the use of the redispersible polymer powder of the invention is advantageous for the following waterproofing material, or preference is given to the following waterproofing material of the inventions: tile adhesives and watertight sealing compounds (membranes) .

[0156] The present invention is further illustrated by the following embodiments and combinations of embodiments as indicated by the respective dependencies and back-references. In particular, it is noted that in each instance where a range of embodiments is mentioned, for example in the context of a term such as "The process of any of embodiments 1 to 4" , every embodiment in this range is meant to be explicitly disclosed for the skilled person, i.e. the wording of this term is to be understood by the skilled person as being synonymous to "The process of any of embodi-ments 1, 2, 3, and 4" .

[0157] 1. An aqueous dispersion, comprising

[0158] i) a copolymer prepared by polymerization of ethylenically unsaturated monomers comprising styrene,

[0159] a conjugated diene,

[0160] at least one ethylenically unsaturated functional monomer (F) ,

[0161] an alkoxysilyl functional ethylenically unsaturated monomer (S) , wherein the monomer (S) is present in an amount of 0.01 to 2.5%by weight, based on the total weight of the monomers; and

[0162] an ethylenically unsaturated monomer (K) having 1, 3-diketo group, wherein the monomer (K) is present in an amount of 0.01 to 3.8 %by weight, based on the total weight of the monomers, wherein the functional monomer (F) is selected from the group consisting of an ethylenically unsaturated monomer having an acid group and / or the corresponding anion thereof, an eth-ylenically unsaturated monomer having an amino, amido, ureido, keto, hydroxyl, polyether chain, or N-heterocyclic group and / or protonated on the nitrogen, or alkylated ammonium derivatives thereof;

[0163] wherein the functional monomer (F) , monomer (S) and monomer (K) are different from each other; and

[0164] ii) an emulsifier system, wherein the emulsifier system comprises at least one of nonionic emul-sifier, anionic emulsifier, and cationic emulsifier.

[0165] 2. The aqueous dispersion as defined according to embodiment 1, wherein the ethylenically unsaturated functional monomer (F) is selected from the group consisting of acrylic acid, meth-acrylic acid, maleic acid, fumaric acid, itaconic acid, acrylamide, methacrylamide, and their de-rivatives, vinylsulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, styrenesulfonic acid, their water soluble salts, hydroxyethyl methacrylate, hydroxyethyl acrylate and combinations thereof.

[0166] 3. The aqueous dispersion as defined according to embodiment 1 or 2, wherein the ethylenically unsaturated functional monomer (F) comprises at least two monomers.

[0167] 4. The aqueous dispersion as defined according to any of embodiments 1 to 3, wherein the monomer (S) has at least one di-C1-C4-alkoxysilane group or tri-C1-C4-alkoxysilane group.

[0168] 5. The aqueous dispersion as defined according to any of embodiments 1 to 4, wherein the monomer (S) is selected from vinyltrimethoxysilane, vinyltriethoxysilane, methacryloxyethyl tri-methoxysilane, methacryloxyethyl triethoxysilane, vinyl tris- (2-methoxyethoxy silane) , vinyl triisopropoxysilane, (3-methacryloxypropyl) -trimethoxysilane, (3-methacryloxypropyl) -triethoxysilane, (3-methacryloxypropyl) -triisopropoxysilane, 2-methyl-2-propenoic acid 3- [tris- (1-methylethoxy) -silyl] -propyl ester, (3-methacryloxypropyl) -methyldiethoxysilane or combinations thereof.

[0169] 6. The aqueous dispersion as defined according to any of embodiments 1 to 5, wherein the monomer (K) is selected from acetoacetoxyethyl acrylate, 2-acetoacetoxyethyl methacrylate (AAEMA) , acetoacetoxypropyl acrylate, acetoacetoxypropyl methacrylate, acetoacetoxybutyl acrylate, acetoacetoxybutyl methacrylate, diacetoneacrylamide (DAAM) and diacetonemethac-rylamide, preferably 2-acetoacetoxyethyl methacrylate (AAEMA) .

[0170] 7. The aqueous dispersion as defined according to any of embodiments 1 to 6, wherein the sty-rene is present in an amount of 25 to 90 %by weight, preferably 35 to 75%by weight, more preferably 40 to 70%by weight, based on the total weight of the monomers.

[0171] 8. The aqueous dispersion as defined according to any of embodiments 1 to 7, wherein the con-jugated diene is present in an amount of 10 to 75 %by weight, preferably 25 to 65%by weight, more preferably 30 to 60%by weight, based on the total weight of the monomers.

[0172] 9. The aqueous dispersion as defined according to any of embodiments 1 to 8, wherein the eth-ylenically unsaturated functional monomer (F) is present in an amount of 0.01%to 10%, prefer-able 0.05%to 8%, or 0.1%to 3.5%by weight, based on the total weight of the monomers.

[0173] 10. The aqueous dispersion as defined according to any of embodiments 1 to 9, wherein the ethylenically unsaturated monomer (S) is present in an amount of 0.1 to 2.2%by weight, prefer-ably 0.15 to 2.1%by weight, based on the total weight of the monomers.

[0174] 11. The aqueous dispersion as defined according to any of embodiments 1 to 10, wherein the monomer (K) is present in an amount of 0.1 to 3%by weight, preferably 0.2 to 2.5%by weight, based on the total weight of the monomers.

[0175] 12. The aqueous dispersion as defined according to any of embodiments 1 to 11, wherein the copolymer (i) is prepared by polymerization of ethylenically unsaturated monomers comprising

[0176] a) 25 to 90 %by weight, preferably 35 to 75%by weight, more preferably 40 to 70%by weight styrene,

[0177] b) 10 to 75 %by weight, preferably 25 to 65%by weight, more preferably 30 to 60%by weight conjugated diene,

[0178] c) 0.01 to 2.5%by weight, preferably 0.1 to 2.2%by weight, more preferably 0.15 to 2.1%by weight ethylenically unsaturated monomer (S) , and

[0179] d) 0.01%to 10%by weight, preferable 0.05%to 8%by weight, or 0.1%to 3.5%by weight ethylenically unsaturated functional monomer (F) ,

[0180] e) 0.01 to 3.8 %by weight, preferably 0.1 to 3%by weight, more preferably 0.2 to 2.5%by weight monomer (K) ,

[0181] in each case based on the total weight of the monomers.

[0182] 13. The aqueous dispersion as defined according to any one of embodiments 1 to 12, wherein the copolymer (i) is obtained by free radical polymerization in the presence a molecular weight regulator.

[0183] 14. The aqueous dispersion as defined according to embodiment 13, wherein the molecular weight regulator is selected from the group consisting of mercaptans such as n-dodecylmercaptan, tertiary dodecyl mercaptan; cyclohexene; halogenated hydrocarbons such as chloroform, bromoform, carbon tetrachloride; alpha-methyl styrene and its dimer, and ter-pinolene.

[0184] 15. The aqueous dispersion as defined according to any of embodiments 1 to 14, further com-prising a crosslinker.

[0185] 16. The copolymer (i) as defined in any of embodiments 1 to 1 to 15.

[0186] 17. A redispersible polymer powder produced from the aqueous dispersion as defined accord-ing to any one of embodiments 1 to 15.

[0187] 18. A method for preparing waterproofing material, comprising at least one step of mixing the aqueous dispersion as defined in any one of embodiments 1 to 15 or the redispersible polymer powder of embodiment 17 with at least one hydraulic binder and / or a filler.

[0188] 19. Use of the aqueous dispersion as defined in any one of embodiments 1 to 15 or the redis-persible polymer powder of embodiment 17 in waterproofing material.

[0189] 20. A waterproofing material comprising the aqueous dispersion as defined according to em-bodiments 1 to 15, or the redispersible polymer powder as defined according to embodiment 17, and at least one hydraulic binder and / or a filler.

[0190] 21. The waterproofing material according to embodiment 19, wherein the content of the hydrau-lic binder may be from about 1 to 70 %by weight, preferably from about 1 to about 60%by weight, more preferably from about 5 to 50%by weight, based on the total weight of the water-proofing material.

[0191] 22. A waterproofing material (1K) comprising

[0192] 1 to 50 %by weight hydraulic binder,

[0193] 40 to 77 %by weight filler,

[0194] 10 to 40 %by weight, preferably 15 to 30 %by weight, most preferred 18 to 20 %by weight of the redispersable polymer powder according to embodiment 17, and

[0195] 0 to 5 %by weight one or more additives,

[0196] in each case based on the weight of the waterproofing material (1K) .

[0197] 23. A waterproofing material (2K) comprising

[0198] (a) a dry component comprising

[0199] 20 to 80 %by weight hydraulic binder,

[0200] 20 to 80 %by weight filler, and

[0201] 0 to 5 %by weight one or more additives,

[0202] in each case based on the weight of the total dry component, and

[0203] (b) a wet component comprising

[0204] 80 to 100%by weight of an aqueous dispersion as defined according to embodiments 1 to 15, and

[0205] optionally one or more additives,

[0206] in each case based on the weight of the total wet component,

[0207] and wherein the ratio of dry component (a) to wet component (b) is in the range of 4: 1 to 1: 2.

[0208] 24. The waterproofing material according to any one of embodiments 19 to 22, wherein the hy-draulic binder is selected from a calcium silicate cement such as ordinary portland cement, cal-cium aluminate cement, calcium sulfate source, calcium sulfoaluminate cement, and further latent hydraulic materials and combinations thereof.

[0209] The present invention would be further explained by the following examples. These, however, would not be construed to further limit the scopes set forth in the following claims.

[0210] Examples

[0211] The materials used in the examples are present below. St:             Styrene, Bd:             Butadiene (1, 3-butadiene) , VTEO:           Vinyltriethoxysilane (monomer S) , VTMO:           Vinyltrimethoxysilane (monomer S) , AAEMA:          2-acetoacetoxyethyl methacrylate (monomer K) , AMPS:           2-Acrylamido-2-methyl-1-propanesulfonic acid (monomer F) , HEMA:           hydroxyethyl methacrylate (monomer F) , HEA:            Hydroxyethyl acrylate (monomer F) , MAM:            Meth acrylamide, aqueous solution, 30wt. % (monomer F) , AM:             Acrylamide, aqueous solution, 50wt. % (monomer F) , MAA:            Methacrylic acid (monomer F) , AA:             Acrylic acid (monomer F) , TSPP:           Tetrasodium pyrophosphate, PH buffer TDMC:           tert-dodecylmercaptan,

[0212] Terpinolene FES 27:         Disponil FES 27 from BASF (Emulsifier) , FES 77:         Disponil FES 77 from BASF (Emulsifier) , DS-4:           Rhodacal DS-4, Dodecyl (branched) sodium benzene sulfonate surfactant from  Solvay (Emulsifier) , FES 993:        Disponil FES 993 from BASF (Emulsifier) , AT18:           Lutensol AT 18 from BASF (Emulsifier) , TO4070:         Emulan TO 4070 from BASF (Emulsifier) , SD6772:         Vorproduct SD 6772, an aqueous polystyrene seed dispersion, solid content of 33  wt %, from BASF Advanced Chemicals Co. Ltd., NAPS:          (sodium persulfate) aqueous solution, 7wt. %, from ABC UNITED-INITIATORS  HEFEI LIMITED COMPANY.

[0213] Examples 1-12:

[0214] The components for Example 1 through 12 were shown in Table 1. All values listed in Table 1 refer to grams.

[0215] Table 1 *comparative examples

[0216] Procedure

[0217] For examples 1-12, 700g water and seed Vorproduct SD 6772 were charged into a reactor.

[0218] The temperature was raised to 85℃, then an aqueous stream was started to feed which was composed of remaining water (the amount of free water as shown in table above -700g -60g) , emulsifier, monomers, chain transfer agents (TDMC and terpinolene) , TSPP and 7%sodium persulphate.

[0219] The reactor content was allowed to polymerize for 5 hours. Then the reaction mixture was cooled down to 60℃.

[0220] 60g water was dosed over 15 minutes with a constant dosing rate. The reaction mixture was stirred for another 30 mins at 60℃ before cooling down to room temperature to obtain the aqueous dispersion.

[0221] 97.71g aqueous dispersion of each example, 0.26g 10%thickener Rheovis AS 1125, 1g defoamer Foamstar PB2706 from BASF and 1.03g water were mixed with 50g cement PO42.5, 50g CaCO3 to make a homogeneous slurry with good flowability.

[0222] Performance

[0223] Table 2 *comparative examples

[0224] TS: Tensile strength

[0225] Elongation: Elongation at break

[0226] TSw: Tensile strength after water treatment

[0227] Elongationw: Elongation at break after water treatment

[0228] Adhesionw: Adhesion after water treatment

[0229] The glass transition temperature Tg is the actual glass transition temperature which is the mid-point temperature determined by means of Differential Scanning Calorimetry (DSC) according to ASTM D3418-82.

[0230] The particle size (PS) is determined by dynamic light scattering (DLS) using a Malvern HPPS.

[0231] For normal tensile property and adhesion property, the samples preparation and measurement follow GB / T 23445-2009 standard.

[0232] For retention of tensile property and adhesion property after water treatment, samples are measured after 7days soak in room temperature water followed by 10 minutes patting by a dry cloth to remove water at surface of samples. Measurement method still follow GB / T 23445-2009 standard.

[0233] Retention %= Performance (Normal)  / Performance (after water treatment) .

[0234] All results were shown in Table 2. The waterproofing material of the present invention shows low Tg, high adhesion strength, good tensile strength and elongation at break, and high water-resistant performance, based on requirement of GB50108, for example, high adhesion strength, good tensile strength and elongation at break after soaking in water. Comparative example 9 comprises too much AAEMA, comparative example 10 comprises too much monomer (S) , com-parative example 11 does not comprise AAEMA, comparative example 12 does not comprise monomer (S) , the resulted waterproofing materials show poor water-resistant performance.

[0235] It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope or spirit of the invention. Thus, it is intended that the present invention cover such modifications and variations as come within the scope of the appended claims and their equivalents.

Claims

1.An aqueous dispersion, comprisingi) a copolymer prepared by polymerization of ethylenically unsaturated monomers comprising styrene,a conjugated diene,at least one ethylenically unsaturated functional monomer (F) ,an alkoxysilyl functional ethylenically unsaturated monomer (S) , wherein the monomer (S) is present in an amount of 0.01 to 2.5%by weight, based on the total weight of the monomers; andan ethylenically unsaturated monomer (K) having 1, 3-diketo group, wherein the monomer (K) is present in an amount of 0.01 to 3.8 %by weight, based on the total weight of the monomers, wherein the functional monomer (F) is selected from the group consisting of an ethylenically unsaturated monomer having an acid group and / or the corresponding anion thereof, an eth-ylenically unsaturated monomer having an amino, amido, ureido, keto, hydroxyl, polyether chain, or N-heterocyclic group and / or protonated on the nitrogen, or alkylated ammonium derivatives thereof;wherein the functional monomer (F) , monomer (S) and monomer (K) are different from each other; andii) an emulsifier system, wherein the emulsifier system comprises at least one of nonionic emul-sifier, anionic emulsifier, and cationic emulsifier.2.The aqueous dispersion as defined according to claim 1, wherein the ethylenically unsaturat-ed functional monomer (F) is selected from the group consisting of acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, acrylamide, methacrylamide, and their derivatives, vi-nylsulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, styrenesulfonic acid, their water soluble salts, hydroxyethyl methacrylate, hydroxyethyl acrylate and combinations thereof.3.The aqueous dispersion as defined according to claim 1 or 2, wherein the ethylenically un-saturated functional monomer (F) comprises at least two monomers.4.The aqueous dispersion as defined according to any of claims 1 to 3, wherein the monomer (S) has at least one di-C1-C4-alkoxysilane group or tri-C1-C4-alkoxysilane group.5.The aqueous dispersion as defined according to any of claims 1 to 4, wherein the monomer (S) is selected from vinyltrimethoxysilane, vinyltriethoxysilane, methacryloxyethyl trimethox-ysilane, methacryloxyethyl triethoxysilane, vinyl tris- (2-methoxyethoxy silane) , vinyl triiso-propoxysilane, (3-methacryloxypropyl) -trimethoxysilane, (3-methacryloxypropyl) -triethoxysilane,  (3-methacryloxypropyl) -triisopropoxysilane, 2-methyl-2-propenoic acid 3- [tris- (1-methylethoxy) -silyl] -propyl ester, (3-methacryloxypropyl) -methyldiethoxysilane or combinations thereof.6.The aqueous dispersion as defined according to any of claims 1 to 5, wherein the monomer (K) is selected from acetoacetoxyethyl acrylate, 2-acetoacetoxyethyl methacrylate (AAEMA) , acetoacetoxypropyl acrylate, acetoacetoxypropyl methacrylate, acetoacetoxybutyl acrylate, acetoacetoxybutyl methacrylate, diacetoneacrylamide (DAAM) and diacetonemethacrylamide, preferably 2-acetoacetoxyethyl methacrylate (AAEMA) .7.The aqueous dispersion as defined according to any of claims 1 to 6, wherein the styrene is present in an amount of 25 to 90 %by weight, preferably 35 to 75%by weight, more preferably 40 to 70%by weight, based on the total weight of the monomers.8.The aqueous dispersion as defined according to any of claims 1 to 7, wherein the conjugated diene is present in an amount of 10 to 75 %by weight, preferably 25 to 65%by weight, more preferably 30 to 60%by weight, based on the total weight of the monomers.9.The aqueous dispersion as defined according to any of claims 1 to 8, wherein the ethylenical-ly unsaturated functional monomer (F) is present in an amount of 0.01%to 10%, preferable 0.05%to 8%, or 0.1%to 3.5%by weight, based on the total weight of the monomers.10.The aqueous dispersion as defined according to any of claims 1 to 9, wherein the ethyleni-cally unsaturated monomer (S) is present in an amount of 0.1 to 2.2%by weight, preferably 0.15 to 2.1%by weight, based on the total weight of the monomers.11.The aqueous dispersion as defined according to any of claims 1 to 10, wherein the mono-mer (K) is present in an amount of 0.1 to 3%by weight, preferably 0.2 to 2.5%by weight, based on the total weight of the monomers.12.The aqueous dispersion as defined according to any of claims 1 to 11, wherein the copoly-mer (i) is prepared by polymerization of ethylenically unsaturated monomers comprisinga) 25 to 90 %by weight, preferably 35 to 75%by weight, more preferably 40 to 70%by weight styrene,b) 10 to 75 %by weight, preferably 25 to 65%by weight, more preferably 30 to 60%by weight conjugated diene,c) 0.01 to 2.5%by weight, preferably 0.1 to 2.2%by weight, more preferably 0.15 to 2.1%by weight ethylenically unsaturated monomer (S) , andd) 0.01%to 10%by weight, preferable 0.05%to 8%by weight, or 0.1%to 3.5%by weight ethylenically unsaturated functional monomer (F) ,e) 0.01 to 3.8 %by weight, preferably 0.1 to 3%by weight, more preferably 0.2 to 2.5%by weight monomer (K) ,in each case based on the total weight of the monomers.13.The aqueous dispersion as defined according to any one of claims 1 to 12, wherein the co-polymer (i) is obtained by free radical polymerization in the presence a molecular weight regula-tor.14.The aqueous dispersion as defined according to claim 13, wherein the molecular weight regulator is selected from the group consisting of mercaptans such as n-dodecylmercaptan, tertiary dodecyl mercaptan; cyclohexene; halogenated hydrocarbons such as chloroform, bro-moform, carbon tetrachloride; alpha-methyl styrene and its dimer, and terpinolene.15.The aqueous dispersion as defined according to any of claims 1 to 14, further comprising a crosslinker.16.The copolymer (i) as defined in any of claims 1 to 15.17.A redispersible polymer powder produced from the aqueous dispersion as defined accord-ing to any one of claims 1 to 15.18.A method for preparing waterproofing material, comprising at least one step of mixing the aqueous dispersion as claimed in any one of claims 1 to 15 or the redispersible polymer powder of claim 17 with at least one hydraulic binder and / or a filler.19.Use of the aqueous dispersion as claimed in any one of claims 1 to 15 or the redispersible polymer powder of claim 17 in waterproofing material.20.A waterproofing material comprising the aqueous dispersion as defined according to claims 1 to 15, or the redispersible polymer powder as defined according to claim 17, and at least one hydraulic binder and / or a filler.21.The waterproofing material according to claim 19, wherein the content of the hydraulic bind-er may be from about 1 to 70 %by weight, preferably from about 1 to about 60%by weight, more preferably from about 5 to 50%by weight, based on the total weight of the waterproofing material.22.A waterproofing material (1 K) comprising1 to 50 %by weight hydraulic binder,40 to 77 %by weight filler,10 to 40 %by weight, preferably 15 to 30 %by weight, most preferred 18 to 20 %by weight of the redispersable polymer powder according to claim 17, and0 to 5 %by weight one or more additives,in each case based on the weight of the waterproofing material (1 K) .23.A waterproofing material (2K) comprising(a) a dry component comprising20 to 80 %by weight hydraulic binder,20 to 80 %by weight filler, and0 to 5 %by weight one or more additives,in each case based on the weight of the total dry component, and(b) a wet component comprising80 to 100%by weight of an aqueous dispersion as defined according to claims 1 to 15, andoptionally one or more additives,in each case based on the weight of the total wet component,and wherein the ratio of dry component (a) to wet component (b) is in the range of 4: 1 to 1: 2.24.The waterproofing material according to any one of claims 19 to 23, wherein the hydraulic binder is selected from a calcium silicate cement such as ordinary portland cement, calcium aluminate cement, calcium sulfate source, calcium sulfoaluminate cement, and further latent hydraulic materials and combinations thereof.