Anti-sticking agent

Abstract

The invention discloses an anti-sticking agent, which is prepared by the following materials in mass by weight: 8-12kg of polyvinyl alcohol, 5-8kg of methanol, 0.1-0.8kg of polyethylene glycol octylphenol ether, 3-4kg of n-butyl alcohol and 75-82kg of water. The anti-sticking agent disclosed by the invention has the advantages that the cement paste adhered on the outer wall of a concrete mixer can be effectively removed; and the anti-sticking agent has the curing action on the concrete mixer and is beneficial to the city appearance.

Description

technical field

[0001] The invention relates to a building material, in particular to a cement anti-sticking agent. Background technique

[0002] With the development of the national economy and the improvement of people's living standards, the rapid development of the construction industry has been promoted. In order to speed up building construction, concrete mixer trucks are usually used at present. In the raw material storage place far away from the construction site, the concrete ingredients are loaded into the concrete mixer truck according to the set ratio, and they are mixed while walking. They can be used when they arrive at the construction site, which can improve Increase production efficiency and save manpower. However, during the transportation of concrete, the cement slurry will inevitably splash on the concrete mixer truck and bond into many cement slurry blocks. If it is not cleaned in time, it will stick to the vehicle, which will not only affect the city a...

Examples

Embodiment 1

[0012] An anti-adhesive agent is characterized in that it is prepared from 11kg of polyvinyl alcohol, 5.8kg of methanol, 3.6kg of n-butanol, 0.6kg of polyethylene glycol octylphenyl ether and 80kg of water.

Embodiment 2

[0014] An anti-sticking agent is characterized in that it is prepared from 8kg of polyvinyl alcohol, 5kg of methanol, 3kg of n-butanol, 0.1kg of polyethylene glycol octylphenyl ether and 75kg of water.

Embodiment 3

[0016] An anti-adhesive agent is characterized in that it is prepared from 12kg of polyvinyl alcohol, 8kg of methanol, 4kg of n-butanol, 0.8kg of polyethylene glycol octylphenyl ether and 82kg of water.

technical field

[0001] The invention relates to a building material, in particular to a cement anti-sticking agent. Background technique

[0002] With the development of the national economy and the improvement of people's living standards, the rapid development of the construction industry has been promoted. In order to speed up building construction, concrete mixer trucks are usually used at present. In the raw material storage place far away from the construction site, the concrete ingredients are loaded into the concrete mixer truck according to the set ratio, and they are mixed while walking. They can be used when they arrive at the construction site, which can improve Increase production efficiency and save manpower. However, during the transportation of concrete, the cement slurry will inevitably splash on the concrete mixer truck and bond into many cement slurry blocks. If it is not cleaned in time, it will stick to the vehicle, which will not only affect the city a...

Examples

Embodiment 1

[0012] An anti-adhesive agent is characterized in that it is prepared from 11kg of polyvinyl alcohol, 5.8kg of methanol, 3.6kg of n-butanol, 0.6kg of polyethylene glycol octylphenyl ether and 80kg of water.

Embodiment 2

[0014] An anti-sticking agent is characterized in that it is prepared from 8kg of polyvinyl alcohol, 5kg of methanol, 3kg of n-butanol, 0.1kg of polyethylene glycol octylphenyl ether and 75kg of water.

Embodiment 3

[0016] An anti-adhesive agent is characterized in that it is prepared from 12kg of polyvinyl alcohol, 8kg of methanol, 4kg of n-butanol, 0.8kg of polyethylene glycol octylphenyl ether and 82kg of water.