Atmospheric corrosion-resistant steel molten steel and chromium-vanadium-nitrogen-containing atmospheric corrosion-resistant steel and production method thereof

A technology of atmospheric corrosion resistance and section steel, which is applied in the field of atmospheric corrosion resistance section steel, can solve the problems such as the lack of strength index of section steel, achieve the effect of improving quality, improving center quality and avoiding center cracks

CN106676411BActive Publication Date: 2019-02-15PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
4 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
Publication Date
2019-02-15

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention relates to the field of steelmaking, and particularly provides atmosphere corrosion resistant section steel molten steel. Taking the total weight of the molten steel as a standard, the molten steel comprises 0.01%-0.09% of C, 0.15%-0.35% of Si, 0.30%-0.60% of Mn, 0.30%-0.40% of Cu, 0.20%-0.30% of Ni, 3. 5%-5.0% of Cr, 0.16%-0.20% of V, 0.004%-0.008% of N, not larger than 0.030% of P and not larger than 0.020% of S. The invention provides atmosphere corrosion resistant section steel and a production method of the atmosphere corrosion resistant section steel. Through continuous casting of the molten steel in the invention, the center quality of a casting blank can be improved, center cracks and center line shrinkage can be avoided, and therefore the quality of the high-intensity high-atmosphere-corrosion-resistant section steel casting blank can be improved, and the yield of the casting blank can be greatly improved; and in addition, the finally-obtained atmosphere corrosion resistant section steel is good atmosphere corrosion resistance and has the high intensity performance.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to an atmospheric corrosion-resistant steel molten steel, an atmospheric corrosion-resistant steel obtained by continuous casting and rolling using the molten steel of the invention, a production method of the atmospheric corrosion-resistant steel and the atmospheric corrosion-resistant steel obtained by the method. Background technique

[0002] Atmospheric corrosion-resistant steel is a very important class of steel. Its atmospheric corrosion resistance is 2-8 times that of ordinary steel, and its paintability is improved by 1.5-10 times. Due to the effectiveness of atmospheric corrosion resistance steel compared with ordinary steel, and its good economic efficiency compared with stainless steel, it has been developed rapidly in various countries in the world. Various steel structures used in the open air, railway vehicles and bridges are is the scope of its application.

[0003] The early atmospheric corrosion-resistant steel v...

Examples

Embodiment Construction

[0025] Specific embodiments of the present invention will be described in detail below. It should be understood that the specific embodiments described here are only used to illustrate and explain the present invention, and are not intended to limit the present invention.

[0026] As mentioned above, the present invention provides a kind of atmospheric corrosion-resistant molten steel, based on the total weight of molten steel, molten steel contains: 0.01%-0.09% of C, 0.15%-0.35% of Si, 0.30%-0.60% of Mn, 0.30%-0.40% Cu, 0.20%-0.30% Ni, 3.5%-5.0% Cr, 0.16%-0.20% V, 0.004%-0.008% N, no more than 0.030% P and no Greater than 0.020% S. The central quality of the slab (also called continuous casting slab) obtained by continuous casting of molten steel with the aforementioned composition is improved, and the center of the cross section of the continuous casting slab (after acid etching) basically has no central cracks and holes.

[0027] According to the present invention, prefer...