A method for extracting metal from saprolitic laterite nickel ore

Abstract

The invention discloses a method for extracting metal from saprolitic laterite nickel ore, comprising: performing ore dressing and grinding on saprolitic laterite nickel ore to obtain laterite nickel ore powder; mixing laterite nickel ore powder, water, acid and reducing agent for normal pressure acid leaching to obtain leaching residue and leachate; adding soluble fluoride salt and sodium salt to the leachate to obtain silicon aluminum slag and silicon aluminum removal liquid; adding phosphorus source to the aluminum silicon removal liquid, solid-liquid separation to obtain iron phosphate and iron precipitation liquid; performing one-step cyclone electrolysis on the iron precipitation liquid to obtain zinc chromium alloy and one-step cyclone electrolysis liquid; performing two-step cyclone electrolysis on the one-step cyclone electrolysis liquid to obtain nickel-cobalt alloy, manganese oxide and two-step cyclone electrolysis liquid; adding sodium carbonate to the two-step cyclone electrolysis liquid for precipitation reaction to obtain magnesium carbonate and magnesium precipitation liquid. The invention realizes the short-process separation and extraction of different valuable metal elements such as zinc, chromium, nickel, cobalt and manganese in saprolitic laterite nickel ore, and is an economical, efficient and green extraction process.

Description

Technical Field

[0001] The invention belongs to the technical field of laterite nickel ore hydrometallurgy, and in particular relates to a method for extracting metal from saprolite-type laterite nickel ore. Background Art

[0002] With the rapid development of new energy, ternary lithium battery is an important part of the future new energy field, and nickel is one of the important components of ternary lithium battery. The efficient extraction technology of nickel resources has become the key to the entire new energy industry. Laterite nickel ore is one of the main forms of nickel in nature, with huge reserves.

[0003] The current laterite nickel ore processing technology includes pyrometallurgy and hydrometallurgy. The basic processing flow of laterite nickel ore with a nickel grade below 1.3% is based on hydrometallurgy, including mineral pretreatment, high-pressure leaching, neutralization and impurity removal, nickel cobalt hydroxide precipitation (MHP), acid reverse dissolution, extraction and crystallization to finally obtain various nickel-cobalt products. Low-grade saprolitic laterite nickel ore contains a large amount of iron, magnesium and other elements. In the above process, iron is directly discarded as slag, and magnesium is directly discharged as an entrained element in wastewater, resulting in a great waste of resources.

[0004] At present, the process research for low-grade laterite nickel ore is based on the use of nickel and cobalt in the mineral as the basic starting point, but other valuable metals therein are not reasonably utilized. It is also reported that the iron concentrate is recovered by reduction roasting-magnetic separation of laterite nickel ore smelting slag, but due to the low added value of iron, it is often not economically beneficial. For example, patent No. CN103526046 A discloses an additive for the reduction of humus-type laterite nickel ore and its application, which is obtained by adding an additive to the humus-type laterite nickel ore, crushing and grinding to obtain powder after reduction, and then obtaining nickel-iron alloy by magnetic separation. Therefore, it is necessary to develop a method for extracting multiple valuable metals from saprolite-type laterite nickel ore. Summary of the invention

[0005] In view of the shortcomings of the prior art, the purpose of the present invention is to provide a method for extracting metals from saprolitic laterite nickel ore. The present invention combines wet processing and electrochemical metallurgy to achieve extraction and recovery of elements such as iron and magnesium during the laterite nickel ore processing stage, achieves short-process deep separation of different metal elements, and improves the utilization rate of valuable metals in laterite nickel ore.

[0006] To achieve the above object, the present invention is implemented through the following technical solutions:

[0007] A method for extracting metal from saprolitic laterite nickel ore comprises the following steps:

[0008] (1) beneficiating and grinding the saprolite-type laterite-nickel ore to obtain laterite-nickel ore powder;

[0009] (2) mixing laterite nickel ore powder, water, acid and a reducing agent to prepare a slurry, and then performing acid leaching at normal pressure to obtain leached residue and leaching solution;

[0010] (3) adding a soluble fluoride salt and a soluble sodium salt to the leaching solution to obtain a silicoaluminate slag and a silicoaluminate-free solution; the silicoaluminate slag contains sodium fluoroaluminate and sodium fluorosilicate;

[0011] (4) adding a phosphorus source to the liquid after silicon and aluminum are removed, and performing solid-liquid separation to obtain iron phosphate and iron precipitation liquid;

[0012] (5) performing one-step cyclone electrolysis on the iron precipitation liquid to obtain a zinc-chromium alloy and a one-step cyclone electrolysis liquid;

[0013] (6) performing a second-step cyclone electrolysis on the first-step cyclone electrolysis solution to obtain a nickel-cobalt alloy, manganese oxide, and a second-step cyclone electrolysis solution;

[0014] (7) adding sodium carbonate to the liquid after the second-step cyclonic electrolysis to carry out a precipitation reaction to obtain magnesium carbonate and a magnesium precipitation liquid.

[0015] Preferably, the acid in step (2) is an organic acid or an inorganic acid, and the reducing agent is one or more of sodium sulfite, sodium bisulfite, sodium pyrosulfite, iron powder, and ferrous sulfate.

[0016] Preferably, in step (2), the concentration of the acid is 1-3 mol / L, the amount of the reducing agent is 5-20 g / L, and the solid-liquid ratio of the slurry is 50-300 g / L.

[0017] Preferably, the leaching temperature of the normal pressure acid leaching in step (2) is 50-90° C., and the leaching time is 1-5 h.

[0018] Preferably, in step (3), the soluble fluoride salt is at least one of sodium fluoride, potassium fluoride and ammonium fluoride; and the soluble sodium salt is at least one of sodium fluoride, sodium chloride and sodium sulfate.

[0019] Preferably, in step (3), the amount of soluble fluoride salt used is 3-20 g / L, and the amount of soluble sodium salt used is 5-20 g / L; and the pH of the leaching solution is controlled to 1-3 using a dilute alkali solution, and the reaction is carried out at room temperature for 0.5-3 hours.

[0020] Preferably, the phosphorus source in step (4) is one or more of phosphoric acid, sodium phosphate, diammonium phosphate, monoammonium phosphate, and ammonium phosphate; and the molar ratio of the phosphorus source to the iron element in the leaching solution is (1-1.1):1.

[0021] Preferably, in the one-step cyclone electrolysis in step (5), the acidity of the solution after iron precipitation is 0.1-0.3 mol / L, the temperature is 30-40°C, and the current density is 400-600 A / m 2, the electrolysis time is 5-10h.

[0022] Preferably, in step (6) of the two-step cyclone electrolysis: the pH of the solution after the first-step cyclone electrolysis is controlled to be 2-4, the temperature to be 40-50°C, and the current density to be 100-200A / m 2 , the electrolysis time is 5-10h.

[0023] Preferably, the method further comprises evaporating and concentrating the solution after magnesium precipitation to obtain sodium sulfate, and recycling the sodium sulfate as sodium salt for silicon and aluminum removal in step (3).

[0024] The beneficial effects of the present invention are:

[0025] In view of the current situation of low resource recovery rate in saprolitic laterite nickel ore, the present invention proposes a method for extracting metals from saprolitic laterite nickel ore. The method realizes short-process deep separation and extraction of different valuable metal elements such as zinc, chromium, nickel, cobalt and manganese in saprolitic laterite nickel ore through the steps of normal pressure acid leaching-silicon and aluminum removal-ferric phosphate precipitation-one-step cyclone electrolysis-two-step cyclone electrolysis-magnesium carbonate precipitation, and is an economical, efficient, green and environmentally friendly extraction process.

[0026] The present invention evaporates and concentrates the filtrate after magnesium extraction, crystallizes sodium sulfate, and reuses the sodium sulfate in the silicon and aluminum removal step, thereby greatly reducing production costs and achieving a high degree of resource utilization. BRIEF DESCRIPTION OF THE DRAWINGS

[0027] In order to more clearly illustrate the technical solution of the embodiment of the present invention, the drawings of the embodiment are briefly introduced below.

[0028] Figure 1 The present invention is a flow chart of a method for extracting metal from saprolitic laterite nickel ore;

[0029] Figure 2 It is a SEM picture of the iron phosphate prepared in Example 1 of the present invention. DETAILED DESCRIPTION

[0030] The following will be combined with the embodiments of the present invention to clearly and completely describe the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only part of the embodiments of the present invention, not all of the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by ordinary technicians in this field without creative work are within the scope of protection of the present invention.

[0031] See also Figure 1 The method for extracting metal from saprolite-type laterite nickel ore provided by the present invention comprises the following steps:

[0032] (1) beneficiating and grinding the saprolite-type laterite-nickel ore to obtain laterite-nickel ore powder;

[0033] (2) mixing laterite nickel ore powder, water, acid and a reducing agent to prepare a slurry, and then acid leaching at a temperature of 50-90° C. for 1-5 hours at normal pressure to obtain leaching residue and leaching liquid; wherein the acid concentration is 1-3 mol / L, the amount of the reducing agent is 5-20 g / L, and the solid-liquid ratio of the slurry is 50-300 g / L.

[0034] The acid used in the atmospheric pressure acid leaching of the present invention is an organic acid or an inorganic acid commonly used in the art, such as the inorganic acid can be one or more of sulfuric acid, phosphoric acid, nitric acid, and hydrochloric acid, and the organic acid can be one or more of formic acid, oxalic acid, citric acid, acetic acid, and ascorbic acid; the reducing agent can be a reducing agent commonly used in the art, such as one or more of sodium sulfite, sodium bisulfite, sodium pyrosulfite, iron powder, and ferrous sulfate.

[0035] (3) adding any one or more soluble fluoride salts such as sodium fluoride, potassium fluoride, ammonium fluoride and the like and soluble sodium salts such as sodium chloride, sodium fluoride and sodium sulfate to the leachate, wherein the amount of the soluble fluoride salt is 3-20 g / L and the amount of the soluble sodium salt is 5-20 g / L; and controlling the pH of the leachate to 1-3 with a dilute alkali solution, reacting at room temperature for 0.5-3 h, so that aluminum is precipitated in the form of cryolite and silicon is precipitated in the form of sodium fluorosilicate, and obtaining silicon-aluminum slag and liquid after silicon-aluminum removal after solid-liquid separation;

[0036] (4) adding a phosphorus source to the liquid after silicon and aluminum removal to carry out precipitation reaction, wherein the phosphorus source can be one or more of phosphoric acid, sodium phosphate, ammonium dihydrogen phosphate, ammonium monohydrogen phosphate, and ammonium phosphate, preferably sodium phosphate, and the molar ratio of the phosphorus source to the iron element in the leaching solution is (1-1.1):1, and after solid-liquid separation, iron phosphate and iron precipitation liquid are obtained;

[0037] The precipitation method for preparing iron phosphate of the present invention preferably adopts a "two-step method", that is, first precipitating to prepare crude iron phosphate and then transforming and aging to prepare battery-grade iron phosphate. The whole process parameters are controlled as follows: first, dilute sulfuric acid or dilute alkali solution is used to control the pH of the liquid after silicon and aluminum removal to 1.8-2.0, and the phosphorus source and the iron in the solution are reacted for 2 hours at a temperature of 55-60°C, and then the phosphorus source is added to the solution in an amount of 0.1 mol / L, the temperature is controlled at 85-90°C, the reaction is continued for 2 hours, and the battery-grade iron phosphate is obtained by filtering and washing.

[0038] (5) performing one-step cyclone electrolysis on the iron precipitation liquid to obtain a zinc-chromium alloy and a one-step cyclone electrolysis liquid; wherein the conditions of the one-step cyclone electrolysis are: solution acidity 0.1-0.3 mol / L, temperature 30-40° C., current density 400-600 A / m 2 The electrolysis time is 5-10h, the cathode is a crude zinc plate, and the anode is a lead-silver alloy plate. During the electrolysis process, zinc-chromium alloy is deposited on the cathode plate, and the cathode plate replacement cycle is 48h.

[0039] After the one-step cyclone electrolysis, the present invention can further electrolytically refine the zinc-chromium alloy deposited on the cathode plate by using current means in the industry to obtain high-purity zinc.

[0040] (6) performing a second-step cyclone electrolysis on the first-step cyclone electrolysis solution to obtain a nickel-cobalt alloy, manganese oxide, and a second-step cyclone electrolysis solution; the conditions for the second-step cyclone electrolysis are: controlling the pH of the first-step cyclone electrolysis solution to be 2-4, the temperature to be 40-50° C., and the current density to be 100-200 A / m 2 The electrolysis time is 5-10h, the cathode is a stainless steel plate, the anode is a lead-silver alloy plate, and a diaphragm bag is placed in it. The stripping cycle of the Ni-Co alloy formed by cathode electrodeposition is 48h to obtain the Ni-Co alloy, and MnO2 is collected in the anode diaphragm bag.

[0041] (7) Sodium carbonate is added to the solution after the second-step cyclone electrolysis to adjust the pH of the solution to 10-12, and a precipitation reaction is carried out at room temperature for 0.5 h. After solid-liquid separation, magnesium carbonate and magnesium precipitation solution are obtained.

[0042] (8) The solution after magnesium precipitation is evaporated and concentrated, and crystallized to obtain sodium sulfate, which is then reused as sodium salt for the silicon and aluminum removal in step (3).

[0043] In order to make the objectives, technical solutions and advantages of the present invention more clear, the embodiments of the present invention will be described in further detail below.

[0044] The composition of the saprolite-type laterite nickel ore used in the following examples is shown in Table 1:

[0045] Table 1 Composition of saprolitic laterite nickel ore

[0046] element Ni Co Mn Fe Al Cr Ca Mg Si content 1.24％ 0.1％ 0.75％ 43.82％ 3.36％ 0.97％ 0.01％ 0.89％ 12-14％

[0047] Example 1

[0048] A method for extracting metal from saprolitic laterite nickel ore comprises the following steps:

[0049] The saprolite laterite nickel ore is subjected to beneficiation and grinding to obtain laterite nickel ore powder; then the laterite nickel ore powder, water, sulfuric acid and sodium pyrosulfite are mixed at a solid-liquid ratio of 200g / L to obtain a slurry, wherein the concentration of sulfuric acid in the slurry is 2mol / L and the concentration of sodium pyrosulfite is 10g / L; the slurry is heated to 80°C and stirred for leaching for 2h, and after the reaction is completed, the leaching residue and the leaching liquid are obtained after filtering. The contents of metals such as Ni, Co, Mn and Fe in the leaching residue are measured to be less than 0.05%, and the residual acid in the leaching liquid is about 0.3mol / L. The leaching residue is used as a brick making material or directly landfilled.

[0050] Add 10g / L NaF and 10g / L Na2SO4 to the leachate, and adjust the pH to 2 with 10% NaOH solution. After reacting for 1h, filter to obtain silicon-aluminum slag and silicon-aluminum-free liquid. The concentrations of residual aluminum and silicon in the silicon-aluminum-free liquid are measured to be below 5ppm. Continue to add sodium phosphate to the silicon-aluminum-free liquid, adjust the molar ratio P / Fe in the solution to 1.05, adopt the "two-step method" process to precipitate iron, filter to obtain iron phosphate and iron-precipitated liquid; the Fe / P molar ratio in iron phosphate is measured to be 0.975, and the content of impurity elements meets the requirements of the battery-grade iron phosphate industry standard (HG / T 4701-2021). The SEM image of iron phosphate is as follows: Figure 2 shown.

[0051] The liquid after iron precipitation was subjected to two-step cyclone electrolysis to recover valuable metals. The process parameters of the one-step cyclone electrolysis were as follows: the acidity of the liquid after iron precipitation was controlled to be 0.2 mol / L, the solution temperature was 35 °C, and the current density was 500 A / m 2 The electrolysis time is 8h, the cathode is a crude zinc plate, and the anode is a lead-silver alloy plate. During the electrolysis process, zinc-chromium alloy is deposited on the cathode plate. The cathode plate replacement cycle is 48h. After the electrolysis is completed, the Zn content in the solution is measured. 2+ The concentration of Cr 3+ The concentration of Ni 2+ 、Co 2+ , Mn 2+ The loss rate is below 1%. Then, the first-step cyclone electrolysis solution is subjected to a second-step cyclone electrolysis to obtain nickel-cobalt alloy, manganese oxide and the second-step cyclone electrolysis solution; the second-step cyclone electrolysis process parameters are as follows: adjust the solution pH to 3, the solution temperature to 50°C, the current density to 150A / m 2 The electrolysis time is 8h, the cathode is a stainless steel plate, the anode is a lead-silver alloy plate, and a diaphragm bag is used. The stripping cycle of the Ni-Co alloy formed by cathode electrodeposition is 48h to obtain the Ni-Co alloy, and MnO2 is collected in the anode diaphragm bag. After the electrolysis is completed, the Ni in the solution 2+ 、Co 2+ The ion concentration dropped to below 50ppm, Mn 2+ The ion concentration dropped to below 10ppm;

[0052] Saturated sodium carbonate solution was added to the solution after the second-step cyclonic electrolysis to adjust the solution pH to 11. After reacting for 1 hour, MgCO3 was obtained by filtration. 2+ The concentration is reduced to below 20ppm; the existing industry process is used to evaporate and concentrate the liquid after magnesium precipitation to obtain sodium sulfate, and the sodium sulfate is reused in the silicon and aluminum removal section.

[0053] Example 2

[0054] A method for extracting metal from saprolitic laterite nickel ore comprises the following steps:

[0055] The saprolite laterite nickel ore is subjected to beneficiation and grinding to obtain laterite nickel ore powder; then the laterite nickel ore powder, water, sulfuric acid and sodium pyrosulfite are mixed at a solid-liquid ratio of 200g / L to obtain a slurry, wherein the concentration of sulfuric acid in the slurry is 2mol / L and the concentration of sodium pyrosulfite is 10g / L; the slurry is heated to 80°C and stirred for leaching for 2h, and after the reaction is completed, the leaching residue and the leaching liquid are obtained after filtering. The contents of metals such as Ni, Co, Mn and Fe in the leaching residue are measured to be less than 0.05%, and the residual acid in the leaching liquid is about 0.3mol / L. The leaching residue is used as a brick making material or directly landfilled.

[0056] 10 g / L NaF and 10 g / L Na2SO4 were added to the leachate, and the pH was adjusted to 2 with a 10% NaOH solution. After reacting for 1 hour, the solution was filtered to obtain silicon-aluminum slag and silicon-aluminum-free solution. The concentrations of aluminum and silicon remaining in the silicon-aluminum-free solution were measured to be below 5 ppm. Sodium phosphate was continued to be added to the silicon-aluminum-free solution to adjust the molar ratio P / Fe in the solution to 1.05. The "two-step method" process was used to precipitate iron, and iron phosphate and iron-precipitated solution were filtered. The Fe / P molar ratio in the iron phosphate was measured to be 0.975, and the content of impurity elements met the requirements of the battery-grade iron phosphate industry standard (HG / T 4701-2021).

[0057] The two-step cyclone electrolysis was used to recover valuable metals from the iron precipitation solution. The process parameters of the one-step cyclone electrolysis were as follows: the acidity of the iron precipitation solution was controlled to be 0.3 mol / L, the solution temperature was 35 °C, and the current density was 600 A / m 2 The electrolysis time is 5h, the cathode is a crude zinc plate, and the anode is a lead-silver alloy plate. During the electrolysis process, zinc-chromium alloy is deposited on the cathode plate. The cathode plate replacement cycle is 48h. After the electrolysis is completed, the Zn content in the solution is measured. 2+ The concentration of Cr 3+ The concentration of Ni 2+ 、Co 2+ , Mn 2+ The loss rate is below 1%. Then, the first-step cyclone electrolysis solution is subjected to a second-step cyclone electrolysis to obtain nickel-cobalt alloy, manganese oxide and the second-step cyclone electrolysis solution; the process parameters of the second-step cyclone electrolysis are as follows: adjust the solution pH to 2, the solution temperature to 50°C, the current density to 100A / m 2 The electrolysis time is 8h, the cathode is a stainless steel plate, the anode is a lead-silver alloy plate, and a diaphragm bag is used. The stripping cycle of the Ni-Co alloy formed by cathode electrodeposition is 48h to obtain the Ni-Co alloy, and MnO2 is collected in the anode diaphragm bag. After the electrolysis is completed, the Ni in the solution 2+ 、Co 2+ The ion concentration dropped below 50ppm, Mn2+ The ion concentration dropped to below 10ppm;

[0058] Saturated sodium carbonate solution was added to the solution after the second-step cyclonic electrolysis to adjust the solution pH to 11. After reacting for 1 hour, MgCO3 was obtained by filtration. 2+ The concentration is reduced to below 20ppm; the existing process means in the industry are used to evaporate and concentrate the liquid after magnesium precipitation to obtain sodium sulfate, and the sodium sulfate is reused in the aluminum silicon removal section.

[0059] Example 3

[0060] A method for extracting metal from saprolitic laterite nickel ore comprises the following steps:

[0061] The saprolite laterite nickel ore is subjected to beneficiation and grinding to obtain laterite nickel ore powder; then the laterite nickel ore powder, water, sulfuric acid and sodium pyrosulfite are mixed at a solid-liquid ratio of 300g / L to obtain a slurry, wherein the concentration of sulfuric acid in the slurry is 3mol / L and the concentration of sodium pyrosulfite is 5g / L; the slurry is heated to 50°C and stirred for leaching for 5h, and after the reaction is completed, the leaching residue and the leaching liquid are obtained after filtering. The contents of metals such as Ni, Co, Mn and Fe in the leaching residue are measured to be less than 0.05%, and the residual acid in the leaching liquid is about 0.3mol / L. The leaching residue is used as a brick making material or directly landfilled.

[0062] Add 20g / L NaF and 10g / L Na2SO4 to the leachate, adjust the pH to 2 with 10% NaOH solution, react for 1h and filter to obtain silicon-aluminum slag and silicon-aluminum-free liquid. The concentrations of aluminum and silicon remaining in the silicon-aluminum-free liquid are measured to be below 5ppm. Continue to add sodium phosphate to the silicon-aluminum-free liquid, adjust the molar ratio P / Fe in the solution to 1.05, adopt the "two-step method" process to precipitate iron, filter to obtain iron phosphate and iron-precipitated liquid; the Fe / P molar ratio in the iron phosphate is measured to be 0.975, and the content of impurity elements meets the requirements of the battery-grade iron phosphate industry standard (HG / T 4701-2021).

[0063] The two-step cyclone electrolysis was used to recover valuable metals from the iron precipitation solution. The process parameters of the one-step cyclone electrolysis were as follows: the acidity of the iron precipitation solution was controlled to be 0.1 mol / L, the solution temperature was 35 °C, and the current density was 400 A / m 2 The electrolysis time is 10 hours. The cathode is a crude zinc plate and the anode is a lead-silver alloy plate. During the electrolysis process, zinc-chromium alloy is deposited on the cathode plate. The cathode plate replacement cycle is 48 hours. After the electrolysis is completed, the Zn content in the solution is measured. 2+ The concentration of Cr 3+ The concentration of Ni 2+ 、Co 2 + , Mn 2+The loss rate is below 1%. Then the first-step cyclone electrolysis solution is subjected to a second-step cyclone electrolysis to obtain nickel-cobalt alloy, manganese oxide and the second-step cyclone electrolysis solution; the second-step cyclone electrolysis process parameters are as follows: adjust the solution pH to 4, the solution temperature to 50°C, the current density to 200A / m 2 The electrolysis time is 10 hours. The cathode is a stainless steel plate, the anode is a lead-silver alloy plate, and a diaphragm bag is used. The stripping cycle of the Ni-Co alloy formed by cathode electrodeposition is 48 hours to obtain the Ni-Co alloy. MnO2 is collected in the anode diaphragm bag. After the electrolysis is completed, Ni in the solution 2+ 、Co 2+ The ion concentration dropped below 50ppm, Mn 2+ The ion concentration dropped to below 10ppm;

[0064] Saturated sodium carbonate solution was added to the solution after the second-step cyclonic electrolysis to adjust the solution pH to 11. After reacting for 1 hour, MgCO3 was obtained by filtration. 2+ The concentration is reduced to below 20ppm; the existing process means in the industry are used to evaporate and concentrate the liquid after magnesium precipitation to obtain sodium sulfate, and the sodium sulfate is reused in the aluminum silicon removal section.

[0065] The extraction rates of valuable metals from saprolitic laterite nickel ore in Examples 1 to 3 are shown in Table 2 below, where the extraction rates of Zn and Cr are the ratio of the mass of the Zn-Cr alloy stripped from the cathode plate of the first-step cyclone electrolysis to the total amount of Zn and Cr in the laterite nickel ore; the extraction rates of Ni and Co are the ratio of the total mass of the Ni-Co alloy stripped from the cathode plate of the second-step cyclone electrolysis to the total amount of Ni and Co in the laterite nickel ore.

[0066] Table 2 Extraction rate of various valuable metals

[0067]

[0068]

[0069] It can be seen from the above table that through the process steps provided by the present invention, an effective extraction rate of Ni and Co exceeding 95%, an effective extraction rate of Mn exceeding 90%, and an effective extraction rate of Zn and Cr exceeding 98% in the whole process are achieved.

[0070] In summary, the present invention: (1) avoids the large amount of energy consumption caused by high-pressure leaching in the existing process by means of normal pressure leaching, thereby promoting carbon dioxide emission reduction.

[0071] (2) During the processing, the resource utilization of iron is realized simultaneously to prepare battery-grade iron phosphate, and magnesium is prepared into magnesium carbonate. No additional smelting slag recycling process is required, which greatly reduces the complexity of the process flow and has more economic cost advantages.

[0072] (3) The cyclone electrolysis technology was introduced into the field of laterite nickel ore smelting. The two-step cyclone electrolysis solved the problem of separation of zinc chromium and nickel cobalt manganese in the traditional smelting process, and obtained high-purity Zn-Cr alloy and Ni-Co alloy respectively. Manganese was extracted and utilized in the form of MnO2 at the same time.

[0073] It should be noted that the above embodiments all belong to the same inventive concept, and the description of each embodiment has its own focus. For matters that are not described in detail in some embodiments, reference may be made to the description in other embodiments.

[0074] The above-mentioned embodiments only express the implementation methods of the present invention, and the descriptions thereof are relatively specific and detailed, but they cannot be understood as limiting the scope of the invention patent. It should be pointed out that, for ordinary technicians in this field, several variations and improvements can be made without departing from the concept of the present invention, which all belong to the protection scope of the present invention. Therefore, the protection scope of the patent of the present invention shall be subject to the attached claims.

Claims

1. A method for extracting metal from saprolitic laterite nickel ore, characterized in that: The following steps are involved: (1) beneficiating and grinding the saprolite-type laterite-nickel ore to obtain laterite-nickel ore powder; (2) mixing laterite nickel ore powder, water, acid and a reducing agent to prepare a slurry, and then performing acid leaching at normal pressure to obtain leaching residue and leaching liquid; (3) adding a soluble fluoride salt and a soluble sodium salt to the leaching solution, and performing solid-liquid separation to obtain a silicoaluminate slag and a silicoaluminate-free liquid; the silicoaluminate slag contains sodium fluoroaluminate and sodium fluorosilicate; (4) adding a phosphorus source to the liquid after silicon and aluminum removal, and performing solid-liquid separation to obtain iron phosphate and iron precipitation liquid; (5) performing one-step cyclone electrolysis on the iron precipitation liquid to obtain a zinc-chromium alloy and a one-step cyclone electrolysis liquid; in the one-step cyclone electrolysis, the acidity of the iron precipitation liquid is 0.1-0.3 mol / L, the temperature is 30-40° C., and the current density is 400-600 A / m 2 , electrolysis time is 5-10 h; (6) subjecting the first-step cyclone electrolysis solution to a second-step cyclone electrolysis to obtain a nickel-cobalt alloy, manganese oxide, and a second-step cyclone electrolysis solution; in the second-step cyclone electrolysis, controlling the pH of the first-step cyclone electrolysis solution to 2-4, the temperature to 40-50° C., and the current density to 100-200 A / m 2 , electrolysis time is 5-10 h; (7) Adding sodium carbonate to the liquid after the two-step cyclonic electrolysis to carry out a precipitation reaction to obtain magnesium carbonate and a magnesium precipitation liquid.

2. The method for extracting metal from saprolite-type laterite nickel ore according to claim 1, characterized in that: In step (2), the acid is an organic acid or an inorganic acid, and the reducing agent is one or more of sodium sulfite, sodium bisulfite, sodium pyrosulfite, iron powder, and ferrous sulfate.

3. The method for extracting metal from saprolite-type laterite nickel ore according to claim 1, characterized in that: In step (2), the concentration of the acid is 1-3 mol / L, the amount of the reducing agent is 5-20 g / L, and the solid-liquid ratio of the slurry is 50-300 g / L.

4. The method for extracting metal from saprolitic laterite nickel ore according to claim 1, characterized in that: The leaching temperature of the normal pressure acid leaching in step (2) is 50-90°C, and the leaching time is 1-5 h.

5. The method for extracting metal from saprolite-type laterite nickel ore according to claim 1, characterized in that: In step (3), the soluble fluoride salt is at least one of sodium fluoride, potassium fluoride and ammonium fluoride; the soluble sodium salt is at least one of sodium fluoride, sodium chloride and sodium sulfate.

6. The method for extracting metal from saprolitic laterite nickel ore according to claim 1, characterized in that: In step (3), the amount of the soluble fluoride salt is 3-20 g / L, and the amount of the soluble sodium salt is 5-20 g / L; and the pH of the leaching solution is controlled to 1-3 using a dilute alkali solution, and the reaction is carried out at room temperature for 0.5-3 h.

7. The method for extracting metal from saprolite-type laterite nickel ore according to claim 1, characterized in that: The phosphorus source in step (4) is one or more of phosphoric acid, sodium phosphate, diammonium phosphate, monoammonium phosphate, and ammonium phosphate; the molar ratio of the phosphorus source to the iron element in the leaching solution is (1-1.1):

1.

8. The method for extracting metal from saprolite-type laterite nickel ore according to claim 1, characterized in that: The method further comprises evaporating and concentrating the magnesium precipitation liquid to obtain sodium sulfate, and recycling the sodium sulfate as a sodium salt for silicon and aluminum removal in step (3).