Anti-wear systems for improved copper corrosion

Abstract

The present invention discloses an organometallic phosphorus antiwear additive having improved copper corrosion performance and a lubricating composition comprising the organometallic phosphorus antiwear additive. The organometallic phosphorus antiwear additive is obtained by reacting an organic hydroxy compound with phosphorus pentasulfide to form a reaction product, distilling the reaction product and recovering a condensate, and neutralizing the condensate with a basic or neutral metal compound including one or more of a metal oxide, a metal hydroxide or a metal carbonate to form the organometallic phosphorus antiwear additive or a salt thereof.

Description

Technical Field

[0001] The present disclosure relates to an organometallic phosphorus-providing antiwear additive having improved copper corrosion and a lubricating composition containing the organometallic phosphorus-providing antiwear additive. Background Art

[0002] Lubricating compositions are designed to achieve a balance between low wear and low friction while minimizing other performance disadvantages. For example, zinc dialkyl dithiophosphates, commonly referred to as ZDDP, are widely used anti-wear additives in lubricants such as engine oils, transmission fluids, and / or hydraulic oils. However, while zinc dialkyl dithiophosphates have good anti-wear and extreme pressure properties, in some cases, these additives may have a tendency to corrode metals, particularly copper and bronze metals. Summary of the invention

[0003] In one method or embodiment, a lubricating composition is described herein that includes: a major portion of one or more base oils of lubricating viscosity; an organometallic phosphorus antiwear additive or a salt thereof, the organometallic phosphorus antiwear additive or a salt thereof being prepared by a process comprising the steps of: (a) reacting an organic hydroxy compound with phosphorus pentasulfide to form a reaction product; (b) distilling the reaction product and recovering a condensate; and (c) neutralizing the condensate with a basic or neutral metal compound comprising one or more of a metal oxide, a metal hydroxide, or a metal carbonate to form the organometallic phosphorus antiwear additive or a salt thereof.

[0004] In another method or embodiment, the lubricating composition of the previous paragraph may include optional features or embodiments in any combination. These optional features or embodiments may include one or more of the following: wherein the distillation is carried out at a temperature of at least about 50°C, a pressure of at least about 0.1 Torr, or a combination thereof; and / or wherein the condensate is recovered at a temperature of about 10°C or less; and / or wherein the distillation is carried out in a falling film evaporator, a wiped film evaporator, a thin film evaporator, a short path evaporator, or a combination thereof; and / or wherein the condensate comprises a dialkyl dithiophosphoric acid; and / or wherein the dialkyl dithiophosphoric acid is dipropyl dithiophosphoric acid, diisopropyl dithiophosphoric acid, dibutyl dithiophosphoric acid, diisobutyl dithiophosphoric acid or a combination thereof; and / or wherein the basic or neutral metal compound is a metal oxide, metal hydroxide or metal carbonate of aluminum, lead, tin, molybdenum, manganese, nickel, copper, titanium, zirconium, zinc or a combination thereof; and / or wherein the basic or neutral metal compound is a molar excess of zinc oxide; and / or wherein the organic hydroxy compound is a C1 to C6 straight or branched alcohol, a hydroxyaryl compound or a mixture thereof; and / or wherein there is The organic hydroxy compound is methanol, ethanol, propanol, isopropanol, butanol, isobutanol, tert-butanol, sec-butanol, phenol, naphthol, pentanol, hexanol, isohexanol, octanol, decanol, dodecanol, octadecanol, 2-ethylhexanol, 4-methyl-2-pentanol, phenyl alcohol, butylphenyl alcohol, cyclohexanol, methylcyclopentanol, propenyl alcohol, butenyl alcohol or a combination thereof; and / or wherein the organic hydroxy compound is ethylhexanol, the reaction product comprises diethylhexyl dithiophosphoric acid and one or more phosphorus polysulfides, and the condensate comprises diethylhexyl dithiophosphoric acid. acid and is substantially free of the one or more phosphorus polysulfides, and the condensate is further reacted with zinc oxide to form an organometallic phosphorus providing antiwear additive; and / or wherein the lubricating composition comprises from about 0.1 wt. % to about 5 wt. % of the organometallic phosphorus providing antiwear additive; and / or wherein the organic hydroxy compound is provided in a molar ratio of from about 4:1 to about 10:1 relative to phosphorus pentasulfide; and / or wherein the basic or neutral metal compound is provided in a molar ratio of from about 0.01:1 to about 0.5:1 relative to the organic hydroxy compound.

[0005] In another method or embodiment, described herein is a method of preparing an organometallic phosphorus providing antiwear additive, wherein the method comprises reacting an organic hydroxy compound with phosphorus pentasulfide to form a reaction product; distilling the reaction product and recovering a condensate therefrom; and neutralizing the condensate with an alkaline or neutral metal compound comprising one or more of a metal oxide, a metal hydroxide, or a metal carbonate to form the organometallic phosphorus providing antiwear additive or a salt thereof.

[0006] In other methods or embodiments, the method of the preceding paragraph may include optional features, steps or embodiments in any combination. These optional features or embodiments may include one or more of the following: wherein the distillation is conducted at a temperature of at least about 80°C and a pressure of at least about 0.4 Torr; and / or wherein the condensate is recovered at a temperature of about 10°C or less; and / or wherein the distillation is conducted in a falling film evaporator, a wiped film evaporator, a thin film evaporator, a short path evaporator, or a combination thereof; and / or wherein the condensate comprises a dialkyl dithiophosphoric acid; and / or wherein the dialkyl dithiophosphoric acid is dipropyl dithiophosphoric acid, diisopropyl dithiophosphoric acid, dibutyl dithiophosphoric acid, diisobutyl dithiophosphoric acid, or a combination thereof; and / or wherein the basic or neutral metal compound is a metal oxide, metal hydroxide, or metal carbonate of aluminum, lead, tin, molybdenum, manganese, nickel, copper, titanium, zirconium, zinc, or a combination thereof; and / or wherein the basic or neutral metal compound is a molar excess of zinc oxide; and / or wherein the organic hydroxy compound is a C1 to C6 straight or branched chain alcohol, a hydroxyarylated and / or wherein the organic hydroxy compound is methanol, ethanol, propanol, isopropanol, butanol, isobutanol, tert-butanol, sec-butanol, phenol, naphthol, pentanol, hexanol, isohexanol, octanol, decanol, dodecanol, octadecanol, 2-ethylhexanol, 4-methyl-2-pentanol, phenyl alcohol, butylphenyl alcohol, cyclohexanol, methylcyclopentanol, propenyl alcohol, butenyl alcohol, or a combination thereof; and / or wherein the organic hydroxy compound is isopropanol, the reaction product comprises diisopropyl dithiophosphoric acid and one or more phosphorus polysulfides, the condensate comprises diisopropyl dithiophosphoric acid and is substantially free of one or more phosphorus polysulfides, and the condensate is further reacted with ethyl acrylate to form an oil-soluble phosphorus antiwear additive; and / or wherein the organic hydroxy compound is provided in a molar ratio of about 4:1 to about 10:1 relative to phosphorus pentasulfide; and / or wherein the unsaturated ester of the carboxylic acid is provided in a molar ratio of about 0.01:1 to about 0.5:1 relative to the organic hydroxy compound.

[0007] In yet another embodiment or method, an organometallic phosphorus providing antiwear additive or a salt thereof is described herein, wherein the additive is prepared by a process comprising the steps of: (a) reacting an organic hydroxy compound with phosphorus pentasulfide to form a reaction product; (b) distilling the reaction product and recovering a condensate; and (c) neutralizing the condensate with a basic or neutral metal compound comprising one or more of a metal oxide, a metal hydroxide, or a metal carbonate to form an organometallic phosphorus providing antiwear additive or a salt thereof. In other methods or embodiments, the additive may include any optional features or embodiments as further described in the lubricant or method of the present disclosure.

[0008] In yet other methods or embodiments, described herein is the use of evaporation or distillation to recover a condensate from the reaction product of an organic hydroxy compound and phosphorus pentasulfide, and wherein the condensate is neutralized with a basic or neutral metal compound comprising one or more of a metal oxide, a metal hydroxide, or a metal carbonate to form an organometallic phosphorus anti-wear additive or salt thereof. The use herein may include any additional embodiment as described in the present disclosure.

[0009] Other embodiments of the disclosure will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein.The following term definitions are provided to clarify the meaning of certain terms as used herein.

[0010] The terms "gear oil," "gear fluid," "gear lubricant," "base gear lubricant," "lubricating oil," "lubricant composition," "lubricating composition," "lubricant," and "lubricating fluid" refer to a finished lubricating product comprising a major amount of a base oil as discussed herein and a minor amount of an additive composition as discussed herein. In one approach, such fluids are used in extreme pressure situations, such as for transmissions and gear drive components having metal-to-metal contact situations, for example, in transmissions and / or limited slip differentials. In another approach, such fluids are used to lubricate an engine.

[0011] As used herein, the term "hydrocarbyl substituent" or "hydrocarbyl group" is used in its ordinary sense, which is well known to those skilled in the art. Specifically, it refers to a group having a carbon atom directly attached to the remainder of the molecule and having predominantly hydrocarbon character. Each hydrocarbyl group is independently selected from a hydrocarbon substituent and a hydrocarbon substituent containing one or more halogen groups, hydroxyl groups, alkoxy groups, mercapto groups, nitro groups, nitroso groups, amino groups, pyridyl groups, furanyl groups, imidazolyl groups, oxygen and nitrogen substitutions, and wherein there are no more than two non-hydrocarbon substituents for every ten carbon atoms in the hydrocarbyl group.

[0012] As used herein, unless otherwise expressly stated, the term "weight percent" or "weight %" means the percentage of the component by weight of the entire composition. Unless otherwise stated, all percentages herein are weight percentages.

[0013] The terms "soluble", "oil-soluble" or "dispersible" as used herein may, but do not necessarily, mean that the compound or additive is soluble, dissolvable, miscible or capable of being suspended in oil in all proportions. However, the aforementioned terms do mean that they are, for example, soluble, suspendable, dissolvable or stably dispersible in oil to a sufficient extent to exert their intended effect in the environment in which the oil is employed. In addition, the additional incorporation of other additives may also allow for the incorporation of higher levels of a particular additive, if desired.

[0014] As used herein, the term "alkyl" refers to a straight chain, branched, cyclic and / or substituted saturated chain portion of about 1 to about 200 carbon atoms. As used herein, the term "alkenyl" refers to a straight chain, branched, cyclic and / or substituted unsaturated chain portion of about 3 to about 30 carbon atoms. As used herein, the term "aryl" refers to monocyclic and polycyclic aromatic compounds, which may include alkyl, alkenyl, alkylaryl, amino, hydroxyl, alkoxy, halogen substituents and / or heteroatoms including, but not limited to, nitrogen and oxygen.

[0015] As used herein, molecular weight is determined by gel permeation chromatography (GPC) using commercially available polystyrene standards (having an Mn of about 180 to about 18,000 as a calibration reference). The molecular weight (Mn) of any embodiment herein can be measured using an instrument such as a gel permeation chromatography (GPC) instrument obtained from Waters, and the data processed using software such as Waters Empower software. The GPC instrument can be equipped with a Waters separation module and a Waters refractive index detector (or similar optional equipment). GPC operating conditions can include a guard column, 4 Agilent PLgel columns (length 300×7.5 mm; particle size 5μ, and pore size range ), the column temperature is about 40 ° C. Unstabilized HPLC grade tetrahydrofuran (THF) can be used as a solvent with a flow rate of 1.0 mL / min. The GPC instrument can be calibrated with commercially available polystyrene (PS) standards with a narrow molecular weight distribution ranging from 500 g / mol to 380,000 g / mol. For samples with a mass of less than 500 g / mol, the calibration curve can be extrapolated. Samples and PS standards can be dissolved in THF and prepared at a concentration of 0.1 wt % to 0.5 wt % and can be used without filtration. GPC measurements are also described in US 5,266,223, which is incorporated herein by reference. The GPC method also provides molecular weight distribution information; see, for example, WW Yau, JJ Kirkland and DD Bly, "Modern Size Exclusion Liquid Chromatography", John Wiley and Sons, New York, 1979, which is also incorporated herein by reference.

[0016] It should be understood that throughout this disclosure, the terms "comprising," "including," "containing," and the like are considered open ended and include any elements, steps, or ingredients not expressly listed. The phrase "consisting essentially of" is meant to include any expressly listed elements, steps, or ingredients as well as any additional elements, steps, or ingredients that do not materially affect the basic and novel aspects of the invention. The present disclosure also contemplates that any composition described using the terms "comprising," "including," "containing" is also to be interpreted as including disclosure of the same composition "consisting essentially of" or "consisting of" its specifically listed components. BRIEF DESCRIPTION OF THE DRAWINGS

[0017] Figure 1 The comparison of the zinc dialkyl dithiophosphate reaction product disclosed herein and the zinc dialkyl dithiophosphate reaction product of the present invention are 31 P NMR spectrum;

[0018] Figure 2 and Figure 3 is a graph comparing copper corrosion of a zinc dialkyl dithiophosphate antiwear additive and a zinc dialkyl dithiophosphate antiwear additive of the present invention;

[0019] Figure 4 is an image representing comparative reaction products between an organic hydroxy compound and phosphorus pentasulfide; and

[0020] Figure 5 is an image representing a condensate obtained from the distillation of a reaction product between an organic hydroxy compound and phosphorus pentasulfide. DETAILED DESCRIPTION

[0021] Disclosed herein are improved organometallic phosphorus providing antiwear additives and lubricating compositions containing such improved antiwear additives, which provide good antiwear performance while having improved copper corrosion. In one embodiment, the organometallic phosphorus providing antiwear additive is a metal dialkyl dithiophosphate, such as zinc dialkyl dithiophosphate. In one method, the lubricating composition of the present invention comprises at least one or more base oils of lubricating viscosity and a novel organometallic phosphorus providing antiwear additive. In one aspect, the organometallic phosphorus providing antiwear additive of the present invention is prepared by: (a) reacting an organic hydroxy compound with phosphorus pentasulfide to form a reaction product; (b) evaporating and / or distilling the reaction product and recovering a condensate therefrom to provide a distilled reaction product comprising a dithiophosphate diester; and (c) neutralizing the condensate with an alkaline or neutral metal compound including one or more of a metal oxide, a metal hydroxide or a metal carbonate to form an organometallic phosphorus providing antiwear additive or a salt thereof. The improved organometallic phosphorus providing antiwear additives of the present disclosure exhibit good antiwear performance (as measured by 4-ball test at 1200 rpm, 40 kg, 75° C., 1 hour according to ASTM D4172) and simultaneously also exhibit good copper corrosion performance (measured according to ASTM D4951).

[0022] As described in more detail below, in some embodiments, the improved performance of the organometallic phosphorus antiwear additives and lubricating compositions containing such antiwear additives is the result of evaporating and / or distilling the reaction product of the organic hydroxy compound and phosphorus pentasulfide and recovering the condensate from the distillation. In some methods or embodiments, the condensate from the evaporation and / or distillation contains a separated and / or improved dithiophosphoric acid intermediate (i.e., a distilled dithiophosphoric acid diester) that is used to react with a variety of organic compounds and / or metal compounds (such as basic or neutral metal compounds discussed in more detail below) to form the improved organometallic phosphorus antiwear additives of the present disclosure.

[0023] The organometallic phosphorus anti-wear additives provided herein can be prepared in a variety of ways, but preferably, by first reacting an organic hydroxy compound such as an alcohol or phenol with phosphorus pentasulfide (optionally in the presence of caprolactam). In some methods, phosphorus pentasulfide can be a monomer or dimer thereof. Suitable organic hydroxy compounds can include normal straight-chain alcohols, branched alcohols, hydroxyaryl compounds (such as phenol and naphthol), substituted aryl hydroxy compounds (such as diamylphenol), or any other hydroxy organic material in which the hydroxyl group will react with phosphorus pentasulfide. In one method, the starting alcohol is a saturated alcohol or a substituted aryl hydroxy compound, such as an aryl hydroxy compound substituted with a saturated alkyl radical. In some methods, the organic hydroxy compound can be one or more of C1 to C10 (in other methods, C4 to C10) straight or branched alcohols, hydroxyaryl compounds or mixtures thereof, such as methanol, ethanol, propanol, isopropanol, butanol, isobutanol, tert-butyl alcohol, sec-butyl alcohol, phenol, naphthol, amyl alcohol, hexanol, isohexanol, octanol, decanol, dodecanol, octadecyl alcohol, 2-ethylhexanol, 4-methyl-2-pentanol, phenyl alcohol, butylphenyl alcohol, cyclohexanol, methylcyclopentanol, propenyl alcohol, butenyl alcohol or combinations thereof. Preferred organic hydroxy compounds herein include C6 to C10 alcohols, such as hexanol, isohexanol, octanol, decanol, dodecanol, octadecyl alcohol, 2-ethylhexanol, 4-methyl-2-pentanol, and the most preferred organic hydroxy compound is 2-ethylhexanol.

[0024] The resulting reaction product of the organic hydroxy compound and phosphorus pentasulfide may contain various residual side reactants, including polysulfides, such as polysulfides of dithiophosphoric acid diesters. An exemplary reaction scheme for the first reaction step is shown in the following Scheme 1 (wherein R1 is a C1 to C10 straight or branched alcohol, a hydroxyaryl compound, or other alcohols as defined above, and preferably 2-ethylhexanol or a 2-ethylhexyl group) to form a reaction product comprising one or more dithiophosphoric acid diesters and various polysulfide phosphorus side reactants, which include at least the exemplary diethylhexyl dithiophosphoric acid polysulfide species shown below, wherein x is an integer from 1 to 6 (in some methods, 1 to 3, or 1 to 5, or 2 to 5, or 3 to 5, or 4 to 5):

[0025]

[0026] Before further reaction, use evaporation or distillation technology to further process the above-mentioned reaction product that comprises dithiophosphoric acid diester and various residual polysulfide phosphorus at least, to separate the dithiophosphoric acid diester of expectation from the polysulfide phosphorus of expectation in the reaction product.Can use many evaporation and / or distillation technology to realize this separation and segregation of the dithiophosphoric acid diester of expectation.For example, according to the needs of specific application, suitable evaporation and / or distillation can use falling film evaporator, scraped film evaporator, thin film evaporator, short-range evaporation / distillation, rotary cone evaporator, evaporation scraped surface heat exchanger, rising film evaporator, centrifugal distillation etc. or their combination to carry out.One or more operations in each unit operation can be used in parallel or in series according to the needs of specific application.

[0027] In one method, a suitable evaporator generally includes a cylindrical heated body and a rotor. Generally, the above-mentioned intermediate reaction mixture enters the heated body at the top and is evenly distributed on the heated inner surface by the rotor. The volatile components (in this case, the desired dithiophosphate diester of distillation) are evaporated quickly, while the non-volatile components (in this case, the undesirable polysulfide residual product) are discharged at the bottom outlet. More specifically, a suitable evaporator may include an upright cylindrical container having a vertical rotor shaft extending concentrically in the container. The inlet supplies the material to be evaporated to a distributor mechanism, which distributes the material in a thin film form around the inner wall of the container and may include one or more arc brush assemblies connected to the rotor shaft below the distributor, which are used to form a thin liquid film on the inner wall. The inner wall is heated and the liquid film is then evaporated. An internal condenser, which is generally located in the center of the cylinder, is used to condense the distillate phase, which can be collected in a suitable tank. The non-volatile bottoms having the undesirable polysulfide components are collected in a separate tank and separated therefrom from the upper volatiles having the desired phosphorodithioate diesters which are condensed into a distillate.

[0028] Separation techniques include a combination of selected pressures and temperatures of an evaporator or distillation to separate and isolate the desired product. In a method or embodiment, the distillation of the reaction product comprising a mixture of the above-mentioned dithiophosphoric acid diester and phosphorus polysulfide may preferably be carried out in a wiped film evaporator or a short path evaporator. Suitable distillation conditions may include a temperature of at least about 50°C, at least about 80°C (and preferably about 90°C to about 120°C, and more preferably about 90°C to about 110°C) and a combination of a suitable pressure of at least about 0.1 Torr, or about 0.3 Torr to about 1.0 Torr, or about 0.4 Torr to about 1 Torr (preferably about 0.4 Torr to about 0.6 Torr, and more preferably about 0.45 Torr to about 0.55 Torr). Condensate may be recovered from the distillation at a temperature of about 10°C or less (and preferably about 2°C to about 8°C, and more preferably about 4°C to about 6°C). In the process, the distillation may include a split ratio of distillate (recovered as condensate) to bottoms or residue, i.e., about 90% to 98% distillate to about 2% to about 10% residue or bottoms. In one process using a wiped-surface or thin-film evaporator, the residence time of the components of the composition in the heating device is short because the thin film allows for relatively rapid distillation and / or evaporation.

[0029] The condensate from the distillation contains the desired dithiophosphate diester (e.g., dialkyl dithiophosphoric acids) and is substantially free of phosphorus polysulfide from the reaction products. In one approach, the dialkyl dithiophosphoric acids in the condensate may include one or more of dipropyl dithiophosphoric acid, diisopropyl dithiophosphoric acid, dibutyl dithiophosphoric acid, diisobutyl dithiophosphoric acid, diethylhexyl dithiophosphoric acid, or a combination thereof, and preferably includes diethylhexyl dithiophosphoric acid. Without wishing to be bound by theory, it is believed that the condensate is substantially free of phosphorus polysulfide from the above reaction products, and at such levels may contain less than about 1 wt%, less than about 0.5 wt%, or less than about 0.25 wt% of any phosphorus polysulfide, such as phosphorus polysulfide of the dithiophosphate diester.

[0030] Then in a second step, the condensate from the evaporation or distillation (which contains the distilled phosphorodithioate diester) is further reacted or neutralized with an alkaline or neutral metal compound (which includes one or more of a metal oxide, a metal hydroxide or a metal carbonate) to form the resulting organometallic phosphorodithioate anti-wear reaction product of the present disclosure. A variety of alkaline or neutral metal compounds can be used for this further reaction or neutralization step, including those having other functional groups in addition to the multiple bonds. Preferred alkaline or neutral metal compounds can include metal oxides, metal hydroxides or metal carbonates of aluminum, lead, tin, molybdenum, manganese, nickel, copper, titanium, zirconium, zinc or a combination thereof. Preferably, the alkaline or neutral metal compound is zinc oxide, and more preferably, a molar excess of zinc oxide. The reaction or neutralization can be carried out at about 60° C. to about 100° C. for about 2 hours to about 5 hours or as needed to obtain the desired final product.

[0031] The resulting organometallic dithiophosphate antiwear additive or salt thereof may comprise a variety of organometallic alkylated dithiophosphates, such as, but not limited to, O,O-di(C 1-14 -alkyl) dithiophosphate zinc; (mixed O,O-bis(sec-butyl and isooctyl)) dithiophosphate zinc; O,O-bis(branched and straight chain C 3-8 -alkyl) zinc dithiophosphate; O,O-bis(2-ethylhexyl) zinc dithiophosphate; O,O-bis(mixed isobutyl and amyl) zinc dithiophosphate; mixed O,O-bis(1,3-dimethylbutyl and isopropyl) zinc dithiophosphate; O,O-diisooctyl zinc dithiophosphate; O,O-dibutyl zinc dithiophosphate; mixed O,O-bis(2-ethylhexyl and isobutyl and isopropyl) dithiophosphate; O,O-bis(dodecylphenyl) zinc dithiophosphate; O,O-diisodecyl zinc dithiophosphate; O-(6-methylheptyl)-O-( Zinc O-(1-methylpropyl) dithiophosphate; zinc O-(2-ethylhexyl)-O-(isobutyl) dithiophosphate; zinc O,O-diisopropyl dithiophosphate; zinc (mixed hexyl and isopropyl) dithiophosphate; zinc (mixed O-(2-ethylhexyl) and O-isopropyl) dithiophosphate; zinc O,O-dioctyl dithiophosphate; zinc O,O-diamyl dithiophosphate; zinc O-(2-methylbutyl)-O-(2-methylpropyl) dithiophosphate; and zinc O-(3-methylbutyl)-O-(2-methylpropyl) dithiophosphate.

[0032] An exemplary reaction scheme II of the second step herein is shown below, wherein R1 is as defined above (preferably a 2-ethylhexyl or 4-methyl-2-pentyl group), and wherein each R1 in the final product may be the same or different depending on the starting organic hydroxy compound mixture:

[0033]

[0034] In one method or embodiment, the organometallic phosphorus-providing antiwear additive herein can be prepared by reacting the above-mentioned organic hydroxyl compound (preferably 2-ethylhexanol) with phosphorus pentasulfide in a molar ratio of about 4:1 to about 10:1 in a first reaction step to form a reaction product. The reaction product is then distilled and a condensate is recovered from the distillate, the condensate comprising dialkyl dithiophosphoric acid and preferably substantially free of polysulfide phosphorus products. The condensate is then further reacted or neutralized with the above-mentioned basic or neutral metal compound (preferably a molar excess of zinc oxide) in a second reaction step, and wherein the molar ratio of the basic or neutral metal compound to the organic hydroxyl compound is about 0.01:1 to about 0.5:1. The resulting organometallic phosphorus-providing antiwear additive can be preferably used in a lubricating composition in an amount of about 0.1 wt % to about 5 wt %, about 0.1 wt % to about 2.0 wt % in other methods, and about 0.2 wt % to about 0.5 wt % in another method.

[0035] Base oil

[0036] In one approach, suitable base oils for use in the lubricating compositions of the present invention with novel organometallic antiwear additives include mineral oils, synthetic oils, and include all common lubricating base stocks. The mineral oil may be a naphthenic oil or a paraffinic oil. The mineral oil may be refined by conventional methods using acids, alkalis and clay or other reagents such as aluminum chloride, or may be an extracted oil, produced, for example, by solvent extraction with solvents such as phenol, sulfur dioxide, furfural or dichlorodiethyl ether. The mineral oil may be hydrotreated or hydrofined, dewaxed by cooling or catalytic dewaxing processes, or hydrocracking, such as from SK Innovation Co., Ltd. (Seoul, Korea). A series of hydrocracked base oils. Mineral oils may be produced from natural crude oil sources or consist of isomerized wax materials or residues of other refining processes.

[0037] The base oil or base oil of lubricating viscosity used in the composition herein can be selected from the base oils in Group IV as specified in the American Petroleum Institute (API) Base Oil Interchangeability Guidelines. The three groups of base oils are as follows:

[0038] Table 1: Base oil types

[0039]

[0040] Class I, Class II and Class III are mineral oil processing raw materials, and can be preferably used for the fluid of the present application.It should be noted that although Class III base oil is derived from mineral oil, the strict processing of these fluid experiences causes their physical properties to be very similar to some real synthetic oils, such as PAO.Therefore, the oil derived from Class III base oil can be called synthetic fluid in industry.Suitable oil can be derived from hydrocracking, hydrogenation, hydrofining, unrefined, refined and re-refined oil and its mixture.In some methods, base oil can be the blend of Class I oil, Class II oil and / or Class III oil, and this blend can be approximately 0% to approximately 100% Class I oil, approximately 0% to approximately 100% Class II oil, approximately 0% to approximately 100% Class III oil, or various blends of Class I and Class II, Class I and Class III, or Class II and Class III oil blends.

[0041] Unrefined oils are those derived from natural, mineral or synthetic sources with little or no further purification. Refined oils are similar to unrefined oils, except that they have been subjected to one or more purification steps, which may result in improvements in one or more properties. Examples of suitable purification techniques are solvent extraction, secondary distillation, acid or base extraction, filtration, percolation, etc. Oils refined to edible quality may or may not be useful. Edible oils may also be referred to as white oils. In some embodiments, the lubricating oil composition does not contain edible oils or white oils.

[0042] Re-refined oils are also called reclaimed oils or reprocessed oils. Similar to refined oils, these oils are obtained using the same or similar processes. Typically these oils are further processed by techniques directed to the removal of spent additives and oil breakdown products.

[0043] Mineral oil can include oil obtained by drilling or oil from plants and animals or any mixture thereof. For example, such oil can include but is not limited to: castor oil, lard, olive oil, peanut oil, corn oil, soybean oil and linseed oil, and mineral lubricating oil, such as liquid petroleum and paraffins, cycloparaffins or mixed paraffin-cycloparaffins through solvent treatment or acid-treated mineral lubricating oil. If desired, such oil can be partially or completely hydrogenated. The oil derived from coal or shale can also be applicable.

[0044] The major amount of base oil included in the fluids herein may be selected from the group consisting of Group I, Group II, Group III, and a combination of two or more of the foregoing, and wherein the major amount of base oil is not a base oil resulting from providing an additive component or a viscosity index improver in the composition. In another embodiment, the major amount of base oil included in the lubricating composition may be selected from the group consisting of Group I, Group II, and a combination of two or more of the foregoing, and wherein the major amount of base oil is not a base oil resulting from providing an additive component or a viscosity index improver in the composition.

[0045] The base oil may also be any of the synthetic base oils from API Group IV or Group V and / or a combination of synthetic base oils and mineral base oils. Useful synthetic lubricating oils may include hydrocarbon oils such as polymerized, oligomeric or copolymerized olefins (e.g., polybutene, polypropylene, propylene isobutylene copolymers); poly(1-hexene), poly(1-octene), trimers or oligomers of 1-decene, such as poly(1-decene), such materials are generally referred to as alpha-olefins, and mixtures thereof; alkyl-benzenes (e.g., dodecylbenzene, tetradecylbenzene, dinonylbenzene, di-(2-ethylhexyl)-benzene); polyphenyls (e.g., biphenyl, terphenyl, alkylated polyphenyls); diphenylalkanes, alkylated diphenylalkanes, alkylated diphenyl ethers, and alkylated diphenyl sulfides and derivatives, analogs, and homologs thereof, or mixtures thereof. Polyalphaolefins are typically hydrogenated materials.

[0046] Other synthetic lubricating oils include polyol esters, diesters, liquid esters (e.g., diethyl esters of toluene phosphate, trioctyl phosphate and decanephosphonic acid) or polytetrahydrofurans containing phosphoric acid. Synthetic oils can be produced by Fischer-Tropsch reaction and can generally be Fischer-Tropsch hydrocarbons or waxes of hydroisomerization. In one embodiment, oil can be prepared by Fischer-Tropsch gas-liquid synthesis procedures and other gas-liquid oils.

[0047] In the compositions herein, the amount of base oil of lubricating viscosity can be the balance remaining after subtracting the sum of the amounts of performance additives from 100 wt%. For example, the oil of lubricating viscosity that can be present in the finished fluid can be a "major amount", such as greater than about 50 wt%, greater than about 60 wt%, greater than about 70 wt%, greater than about 80 wt%, greater than about 85 wt%, greater than about 90 wt%, or greater than about 95 wt%.

[0048] In some methods, the preferred base oil or base oil of lubricating viscosity has less than about 25 ppm sulfur, a viscosity index greater than about 120, and a kinematic viscosity of about 2 cSt to about 8 cSt at about 100°C. In other methods, the base oil of lubricating viscosity has less than about 25 ppm sulfur, a viscosity index greater than 120, and a kinematic viscosity of about 4 cSt at 100°C. The base oil may have a CP (paraffinic carbon content) greater than 40%, greater than 45%, greater than 50%, greater than 55%, or greater than 90%. The base oil may have a CA (aromatic carbon content) less than 5%, less than 3%, or less than 1%. The base oil may have a CN (naphthenic carbon content) less than 60%, less than 55%, less than 50%, or less than 50% and greater than 30%. The base oil may have a ratio of 1-ring naphthalene to 2-6-ring naphthalene less than 2 or less than 1.5 or less than 1.

[0049] Suitable lubricant compositions herein may include additive components within the ranges listed in Table 2 below.

[0050] Table 2: Suitable and preferred transmission or gear fluid compositions

[0051] Components Weight % (suitable embodiment) Weight % (preferred embodiment) Organometallic dithiophosphate antiwear reaction products 0.1 to 5.0 0.15 to 0.5 Antioxidants 0.1-5.0 0.01-4.0 Detergent 0.0-15.0 1.0-8.0 Ashless TBN Accelerator 0.0-1.0 0.01-0.5 Corrosion Inhibitors 0.0-5.0 0.1-3.0 Metal dihydrocarbyl dithiophosphates 0.0-15.0 0.1-5.0 Other phosphorus compounds without ash 0.0-15.0 0.1-5.0 Defoaming agent 0.0-1.0 0.001-0.5 Antiwear Agents 0.0-1.0 0.0-0.8 Pour Point Depressant 0.0-1.0 0.01-0.5 Viscosity Index Improver 0.0-20.0 0.1-10.0 Dispersants 0.0-10.0 1.0-6.0 Dispersant Viscosity Index Improver 0.0-10.0 0.0-5.0 Friction modifiers 0.0-10.0 0.01-4.0 Extreme Pressure Agents 0.0-1.05 .035-.35 Base oil margin margin total 100 100

[0052] The percentages of each component above represent the weight percentage of each component based on the weight of the total final additive or lubricating oil composition. The remainder of the lubricating oil composition consists of one or more base oils or solvents. The additives used to formulate the compositions described herein can be blended into the base oil or solvent individually or in various sub-combinations. However, it may be appropriate to use an additive concentrate (i.e., additives plus diluents, such as hydrocarbon solvents) to blend all components simultaneously.

[0053] When included in a lubricant, the organometallic dithiophosphate antiwear reaction product of the present disclosure exhibits good antiwear performance (measured by a 4-ball test at 1200 rpm, 40 kg, 75° C., 1 hour according to ASTM D4172), and the additive reaction product also exhibits good copper corrosion performance (measured as a neat additive according to ASTM D130 and D4951). For example, a lubricating composition having the additive reaction product herein may exhibit a wear scar of about 0.350 mm to about 0.500 mm (preferably about 0.350 mm to about 0.480 mm, or more preferably about 0.350 mm to about 0.470 mm). At the same time, the additive reaction product as a neat additive may exhibit copper corrosion of about 150 ppm or less copper, more preferably about 80 ppm or less copper, about 50 ppm or less copper, about 20 ppm or less copper, and even more preferably 15 ppm or less copper, as measured by ASTM D130 and D4951 according to the Examples.

[0054] In one approach, the lubricating compositions herein are suitable for use in hydraulic fluids or transmission lubricating compositions and can be used to lubricate mechanical parts, such as gears, transmissions, or gearbox components. Lubricating fluids according to the present disclosure can be used in gear applications, such as industrial gear applications, automotive gear applications, axles, and fixed gearboxes. Gear types can include, but are not limited to, spur gears, helical gears, worm gears, rack gears, involute gears, bevel gears, helical gears, planetary gears, and hypoid gears, as well as limited slip applications and differentials. The transmission lubricating compositions disclosed herein are also suitable for use in automatic or manual transmissions, including stepped automatic transmissions, continuously variable transmissions, semi-automatic transmissions, automated manual transmissions, toroidal transmissions, and dual clutch transmissions.

[0055] Optional additives

[0056] In other methods, the lubricating composition herein containing such additives as described above may also contain one or more optional components, as long as such components and their amounts do not affect the performance characteristics as described in the above paragraphs. These optional components are described in the following paragraphs.

[0057] Other phosphorus compounds

[0058] The lubricant composition of this invention may include one or more phosphorus-containing compounds that can impart anti-wear benefits to the fluid. The one or more phosphorus-containing compounds are present in an amount of about 0% to about 15% by weight of the lubricant composition, or about 0.01% to about 10% by weight, or about 0.05% to about 5% by weight, or about 0.1% to about 3% by weight of the lubricant composition. The phosphorus-containing compound can provide up to 5000ppm of phosphorus, or about 50 to about 5000ppm of phosphorus, or about 300 to about 1500ppm of phosphorus, or up to 600ppm of phosphorus, or up to 900ppm of phosphorus to the lubricant composition.

[0059] The one or more phosphorus-containing compounds may include ashless phosphorus-containing compounds. Examples of suitable phosphorus-containing compounds include, but are not limited to, thiophosphates, dithiophosphates, phosphates, phosphate esters, phosphate esters, phosphites, phosphonates, phosphorus-containing carboxylates, ethers or amides thereof and mixtures thereof. Phosphorus-containing antiwear agents are more fully described in European Patent 0612839.

[0060] It should be noted that the terms phosphonate and phosphite are often used interchangeably in the lubricant industry. For example, dibutyl hydrogen phosphonate is often referred to as dibutyl hydrogen phosphite. It is within the scope of the present invention that the lubricant composition of the present invention includes a phosphorus-containing compound that may be referred to as a phosphite or a phosphonate.

[0061] In any of the above phosphorus-containing compounds, the compound can have from about 5 wt % to about 20 wt % phosphorus, or from about 5 wt % to about 15 wt % phosphorus, or from about 8 wt % to about 16 wt % phosphorus, or from about 6 wt % to about 9 wt % phosphorus.

[0062] In some embodiments, the ash-free phosphorus-containing compound may be dialkyl dithiophosphate, amyl phosphate, diamyl phosphate, dibutyl hydrogen phosphonate, dimethyl octadecylphosphonate, salts thereof, and mixtures thereof.

[0063] The ash-free phosphorus-containing compound may have the formula:

[0064]

[0065] wherein R1 is S or O; R2 is -OR", -OH or -R"; R3 is -OR", -OH or SR"'C(O)OH; R4 is -OR"; R"' is a C1 to C3 branched or straight alkyl chain; and R" is a C1 to C18 hydrocarbon chain. When the phosphorus-containing compound has the structure shown in Formula XIV, the compound can have from about 8 to about 16 weight percent phosphorus.

[0066] In some embodiments, the lubricant composition comprises a phosphorus-containing compound of Formula XIV, wherein R1 is S; R2 is -OR", R3 is SR"'COOH; R4 is -OR", R"' is a C3 branched alkyl chain; R" is C4; and wherein the phosphorus-containing compound is present in an amount to deliver 80 ppm to 900 ppm of phosphorus to the lubricant composition.

[0067] In another embodiment, the lubricant composition comprises a phosphorus-containing compound of Formula XIV, wherein R1 is O; R2 is -OH; R3 is -OR" or -OH; R4 is -OR"; R" is C5; and wherein the phosphorus-containing compound is present in an amount to deliver 80 ppm to 1500 ppm of phosphorus to the lubricant composition.

[0068] In another embodiment, the lubricant composition comprises a phosphorus-containing compound of Formula XIV, wherein R1 is O; R2 is OR", R3 is H; R4 is -OR", R" is C4; and wherein the one or more phosphorus-containing compounds are present in an amount to deliver 80 ppm to 1550 ppm of phosphorus to the lubricant composition.

[0069] In other embodiments, the lubricant composition comprises a phosphorus-containing compound of Formula XIV, wherein R1 is O; R2 is -R"; R3 is -OCH3 or -OH; R4 is -OCH3; R" is C18; and wherein the one or more phosphorus-containing compounds are present in an amount to deliver 80 ppm to 850 ppm of phosphorus to the lubricant composition.

[0070] In some embodiments, the phosphorus-containing compound has a structure as shown in Formula XIV and delivers from about 80 ppm to about 4500 ppm of phosphorus to the lubricant composition. In other embodiments, the phosphorus-containing compound is present in an amount that delivers from about 150 ppm to about 1500 ppm of phosphorus, or from about 300 ppm to about 900 ppm of phosphorus, or from about 800 ppm to 1600 ppm of phosphorus, or from about 900 ppm to about 1800 ppm of phosphorus to the lubricant composition.

[0071] Other anti-wear agents

[0072] The lubricant composition may also include an antiwear agent that is a phosphorus-free compound. Examples of such antiwear agents include boric acid esters, boric acid ester epoxides, thiocarbamate compounds (including thiocarbamates, alkylene-coupled thiocarbamates and bis (S-alkyl dithiocarbamoyl) disulfides, thiocarbamate amides, thiocarbamate ethers, alkylene-coupled thiocarbamates and bis (S-alkyl dithiocarbamoyl) disulfides and mixtures thereof), sulfided olefins, tridecyl adipates, titanium compounds and long-chain derivatives of hydroxycarboxylic acids, such as tartrate derivatives, tartrate amides, tartrimides, citrates and mixtures thereof. Suitable thiocarbamate compounds are dithiocarbamate platinum. Suitable tartrate derivatives or tartrimides may contain alkyl ester groups, wherein the total number of carbon atoms on the alkyl group may be at least 8. Tartrate derivatives or tartrimides may contain alkyl ester groups, wherein the total number of carbon atoms on the alkyl group may be at least 8. In one embodiment, the antiwear agent may include citric acid esters. Additional antiwear agents may be present in a range comprising about 0 wt % to about 15 wt %, or about 0.01 wt % to about 10 wt %, or about 0.05 wt % to about 5 wt %, or about 0.1 wt % to about 3 wt % of the lubricating oil composition.

[0073] Other extreme pressure agents

[0074] The lubricant composition of the present disclosure may also include other extreme pressure agents. The extreme pressure agent may include sulfur, and may include at least 12% by weight of sulfur. In some embodiments, the extreme pressure agent added to the lubricating oil is sufficient to provide at least 350 ppm of sulfur, 500 ppm of sulfur, 760 ppm of sulfur, about 350 ppm to about 2,000 ppm of sulfur, about 2,000 ppm to about 30,000 ppm of sulfur, or about 2,000 ppm to about 4,800 ppm of sulfur, or about 4,000 ppm to about 25,000 ppm of sulfur to the lubricant composition.

[0075] A variety of sulfur-containing extreme pressure agents are suitable and include sulfurized animal or vegetable fats or oils, sulfurized animal or vegetable fatty acid esters, fully or partially esterified esters of trivalent or pentavalent acids of phosphorus, sulfurized olefins (see, e.g., U.S. Pat. Nos. 2,995,569; 3,673,090; 3,703,504; 3,703,505; 3,796,661; 3,873,454; 4,119,549; 4,119,550; 4,147,640; 4,191,659; 4,240,958; 4,344,854; 4,472,306; and 4,711,736), dihydrocarbyl polysulfides (see, e.g., U.S. Pat. Nos. 2,237,625; 2,237,627; 2,527,948; 2,695,316; 3,022,351; 3,308,166; 3,392,201; 4,564,709; and British 1,162,334), functionally substituted dihydrocarbyl polysulfides (see, e.g., U.S. Pat. No. 4,218,332), and polysulfide olefin products (see, e.g., U.S. Pat. No. 4,795,576). Other suitable examples include organic sulfur compounds selected from sulfurized olefins, sulfur-containing amino heterocyclic compounds, 5-dimercapto-1,3,4-thiadiazole, polysulfides having a majority of S3 and S4 sulfides, sulfurized fatty acids, sulfurized branched olefins, organic polysulfides, and mixtures thereof.

[0076] In some embodiments, the extreme pressure agent is present in the lubricating composition in an amount of up to about 3.0 wt % or up to about 5.0 wt %. In other embodiments, the extreme pressure agent is present in an amount of about 0.05 wt % to about 0.5 wt % based on the total lubricant composition. In other embodiments, the extreme pressure agent is present in an amount of about 0.1 wt % to about 3.0 wt % based on the total lubricant composition. In other embodiments, the extreme pressure agent is present in an amount between about 0.6 wt % and about 1 wt % based on the total lubricant composition. In other embodiments, the detergent is present in an amount of about 1.0 wt % based on the total lubricant composition.

[0077] One class of suitable extreme pressure agents is a polysulfide composed of one or more compounds represented by the formula: Ra—Sx—Rb, wherein Ra and Rb are hydrocarbyl groups, each of which may contain 1 to 18 and in other methods 3 to 18 carbon atoms, and x may be in the range of 2 to 8, typically in the range of 2 to 5, especially 3. In certain methods, x is an integer from 3 to 5, wherein about 30% to about 60% of x is an integer of 3 or 4. The hydrocarbyl group may be of widely different types, such as alkyl, cycloalkyl, alkenyl, aryl or aralkyl. Tertiary alkyl polysulfides such as di-tert-butyl trisulfide, and mixtures containing di-tert-butyl trisulfide (e.g., mixtures consisting mainly or entirely of tris, tetras and pentasulfides) may be used. Examples of other useful dihydrocarbyl polysulfides include diamyl polysulfide, dinonyl polysulfide, dodecyl polysulfide and dibenzyl polysulfide.

[0078] Another suitable extreme pressure agent is a sulfurized isobutylene prepared by reacting an olefin such as isobutylene with sulfur. Sulfurized isobutylene (SIB), particularly sulfurized polyisobutylene, typically has a sulfur content of about 10% to about 55%, desirably about 30% to about 50%, by weight. A variety of other olefins or unsaturated hydrocarbons, such as isobutylene dimers or trimers, can be used to form sulfurized olefin extreme pressure agents. Various methods for preparing sulfurized olefins have been disclosed in the prior art. See, for example, U.S. Pat. No. 3,471,404 to Myers; U.S. Pat. No. 4,204,969 to Papay et al.; U.S. Pat. No. 4,954,274 to Zaweski et al.; U.S. Pat. No. 4,966,720 to DeGonia et al.; and U.S. Pat. No. 3,703,504 to Horodysky et al., each of which is incorporated herein by reference.

[0079] Methods for preparing sulfurized olefins, including methods disclosed in the above-mentioned patents, generally include forming a material commonly referred to as an "adduct", wherein an olefin is reacted with a sulfur halide such as sulfur monochloride. The adduct is then reacted with a sulfur source to provide a sulfurized olefin. The quality of the sulfurized olefin is generally measured by various physical properties, including, for example, viscosity, sulfur content, halogen content, and copper corrosion test weight loss. U.S. Patent No. 4,966,720 relates to sulfurized olefins used as extreme pressure additives in lubricating oils, and to a two-step reaction for their preparation.

[0080] Antioxidants

[0081] The lubricating oil composition herein may also optionally contain one or more antioxidants. Antioxidant compounds are known and include, for example, phenates, phenate sulfides, sulfided olefins, phosphorus sulfided terpenes, sulfided esters, aromatic amines, alkylated diphenylamines (e.g., nonyl diphenylamine, dinonyl diphenylamine, octyl diphenylamine, dioctyl diphenylamine), phenyl-α-naphthylamine, alkylated phenyl-α-naphthylamine, hindered non-aromatic amines, phenols, hindered phenols, oil-soluble molybdenum compounds, macromolecular antioxidants, or mixtures thereof. The antioxidant compounds may be used alone or in combination.

[0082] The hindered phenol antioxidant may contain a sec-butyl and / or tert-butyl group as a sterically hindered group. The phenol group may be further substituted with a hydrocarbyl group and / or a bridging group connected to a second aromatic group. Examples of suitable hindered phenol antioxidants include 2,6-di-tert-butylphenol, 4-methyl-2,6-di-tert-butylphenol, 4-ethyl-2,6-di-tert-butylphenol, 4-propyl-2,6-di-tert-butylphenol or 4-butyl-2,6-di-tert-butylphenol, or 4-dodecyl-2,6-di-tert-butylphenol. In one embodiment, the hindered phenol antioxidant may be an ester and may include, for example, BASF commercially available L-135 or the addition product derived from 2,6-di-tert-butylphenol and an alkyl acrylate, wherein the alkyl group may contain from about 1 to about 18, or from about 2 to about 12, or from about 2 to about 8, or from about 2 to about 6, or about 4 carbon atoms. Another commercially available hindered phenol antioxidant may be an ester and may include the esters available from Albemarle Corporation. 4716.

[0083] Useful antioxidants may include diarylamines and phenols. In one embodiment, the lubricating oil composition may contain a mixture of diarylamines and phenols such that each antioxidant may be present in an amount sufficient to provide up to about 5 weight percent based on the weight of the lubricant composition. In one embodiment, the antioxidant may be a mixture of about 0.3 weight percent to about 1.5 weight percent diarylamine and about 0.4 weight percent to about 2.5 weight percent phenol based on the lubricant composition.

[0084] Examples of suitable olefins that can be sulfurized to form sulfurized olefins include propylene, butylene, isobutylene, polyisobutylene, pentene, hexene, heptene, octene, nonene, decene, undecene, dodecene, tridecene, tetradecene, pentadecene, hexadecene, heptadecene, octadecene, nonadecaene, or mixtures thereof. In one embodiment, hexadecene, heptadecene, octadecene, nonadecaene, or mixtures thereof, and dimers, trimers, and tetramers thereof are particularly suitable olefins. Alternatively, the olefin can be a Diels-Alder adduct of a diene (such as 1,3-butadiene) and an unsaturated ester (such as butyl acrylate).

[0085] Another class of sulphurized olefins includes sulphurized fatty acids and esters thereof. Fatty acids are usually obtained from vegetable oils or animal oils and usually contain about 4 to about 22 carbon atoms. Examples of suitable fatty acids and esters thereof include triglycerides, oleic acid, linoleic acid, palmitoleic acid or mixtures thereof. Usually, fatty acids are obtained from lard, pine oil, peanut oil, soybean oil, cottonseed oil, sunflower oil or mixtures thereof. Fatty acids and / or esters can be mixed with olefins such as alpha-olefins.

[0086] The one or more antioxidants may be present in a range from about 0 wt % to about 20 wt %, or from about 0.1 wt % to about 10 wt %, or from about 1 wt % to about 5 wt % of the lubricating oil composition.

[0087] Dispersants

[0088] Dispersants contained in the lubricant composition may include, but are not limited to, oil-soluble polymeric hydrocarbon backbones having functional groups capable of associating with particles to be dispersed. Typically, dispersants contain amine, alcohol, amide or ester polar moieties attached to the polymer backbone, typically via a bridging group. The dispersant may be selected from Mannich dispersants as described in U.S. Pat. Nos. 3,634,515, 3,697,574, and 3,736,357; ashless succinimide dispersants as described in U.S. Pat. Nos. 4,234,435 and 4,636,322; amine dispersants as described in U.S. Pat. Nos. 3,219,666, 3,565,804, and 5,633,326; Koch dispersants as described in U.S. Pat. Nos. 5,936,041, 5,643,859, and 5,627,259; and U.S. Pat. Nos. 5,851,965; 5,853,434; and 5,792,729.

[0089] In some embodiments, the additional dispersant may be derived from polyalphaolefin (PAO) succinic anhydride, olefin maleic anhydride copolymer. As an example, the additional dispersant may be described as poly-PIBSA. In another embodiment, the additional dispersant may be derived from an anhydride grafted with ethylene-propylene copolymer. Another additional dispersant may be a high molecular weight ester or half ester amide.

[0090] If present, additional dispersants may be used in an amount sufficient to provide up to about 10 wt % based on the final weight of the lubricating oil composition. Another amount of dispersant that may be used may be from about 0.1 wt % to about 10 wt %, or from about 0.1 wt % to about 10 wt %, or from about 3 wt % to about 8 wt %, or from about 1 wt % to about 6 wt %, based on the final weight of the lubricating oil composition.

[0091] Viscosity Index Improver

[0092] The lubricant composition herein may also optionally contain one or more viscosity index improvers. Suitable viscosity index improvers may include polyolefins, olefin copolymers, ethylene / propylene copolymers, polyisobutylene, hydrogenated styrene-isoprene polymers, styrene / maleic acid ester copolymers, hydrogenated styrene / butadiene copolymers, hydrogenated isoprene polymers, alpha-olefin maleic anhydride copolymers, polymethacrylates, polyacrylates, polyalkylstyrenes, hydrogenated alkenyl aryl conjugated diene copolymers, or mixtures thereof. Other viscosity index improvers may include star polymers, and suitable examples are described in U.S. Publication No. 20120101017A1, which is incorporated herein by reference.

[0093] The lubricating oil compositions herein may optionally contain one or more dispersant viscosity index improvers in addition to or in place of the viscosity index improvers. Suitable viscosity index improvers may include functionalized polyolefins, for example, ethylene-propylene copolymers that have been functionalized with the reaction product of an acylating agent (such as maleic anhydride) and an amine; polymethacrylates functionalized with amines, or esterified maleic anhydride-styrene copolymers reacted with amines.

[0094] The total amount of viscosity index improver and / or dispersant viscosity index improver can be from about 0 wt % to about 20 wt %, from about 0.1 wt % to about 15 wt %, from about 0.1 wt % to about 12 wt %, or from about 0.5 wt % to about 10 wt %, from about 3 wt % to about 20 wt %, from about 3 wt % to about 15 wt %, from about 5 wt % to about 15 wt %, or from about 5 wt % to about 10 wt % of the lubricating oil composition.

[0095] In some embodiments, the viscosity index improver is a polyolefin or olefin copolymer having a number average molecular weight of about 10,000 to about 500,000, about 50,000 to about 200,000, or about 50,000 to about 150,000. In some embodiments, the viscosity index improver is a hydrogenated styrene / butadiene copolymer having a number average molecular weight of about 40,000 to about 500,000, about 50,000 to about 200,000, or about 50,000 to about 150,000. In some embodiments, the viscosity index improver is a polymethacrylate having a number average molecular weight of about 10,000 to about 500,000, about 50,000 to about 200,000, or about 50,000 to about 150,000.

[0096] Other optional additives

[0097] Other additives can be selected to perform one or more functions required by the lubricant composition. In addition, one or more of the additives mentioned can be multifunctional and provide functions other than those specified herein or different from those specified herein. These other additives can be additives other than the specified additives of the present disclosure and / or can include one or more of the following: metal deactivators, viscosity index improvers, ashless TBN promoters, antiwear agents, corrosion inhibitors, rust inhibitors, dispersants, dispersant viscosity index improvers, extreme pressure agents, antioxidants, foam inhibitors, demulsifiers, emulsifiers, pour point depressants, seal swelling agents and mixtures thereof. Typically, a fully formulated lubricating oil will contain one or more of these additives.

[0098] Suitable metal deactivators may include derivatives of benzotriazole (typically tolyltriazole), dithiothiadiazole derivatives, 1,2,4-triazole, benzimidazole, 2-alkyldithiobenzimidazole or 2-alkyldithiobenzothiazole; foam inhibitors including copolymers of ethyl acrylate and 2-ethylhexyl acrylate and optionally vinyl acetate; demulsifiers including trialkyl phosphates, polyethylene glycol, polyethylene oxide, polypropylene oxide and (ethylene oxide-propylene oxide) polymers; pour point depressants including esters of maleic anhydride-styrene, polymethacrylates, polyacrylates or polyacrylamides.

[0099] Suitable foam suppressors include silicon-based compounds such as siloxanes.

[0100] Suitable pour point depressants may include polymethyl methacrylate or mixtures thereof. The pour point depressant may be present in an amount sufficient to provide about 0 wt % to about 1 wt %, about 0.01 wt % to about 0.5 wt %, or about 0.02 wt % to about 0.04 wt % based on the final weight of the lubricating oil composition.

[0101] Suitable rust inhibitors can be single compounds or compound mixtures having the property of inhibiting corrosion of ferrous metal surfaces. Non-limiting examples of useful rust inhibitors herein include: oil-soluble high molecular weight organic acids, such as 2-ethylhexanoic acid, lauric acid, myristic acid, palmitic acid, oleic acid, linoleic acid, linolenic acid, behenic acid, and cerotic acid; and oil-soluble polycarboxylic acids including dimer acids and trimer acids, such as those produced by pine oil fatty acids, oleic acid, and linoleic acid. Other suitable corrosion inhibitors include long-chain α, ω-dicarboxylic acids with a molecular weight ranging from about 600 to about 3000, and alkenyl succinic acids in which the alkenyl group contains about 10 or more carbon atoms, such as tetrapropylene succinic acid, tetradecene succinic acid, and hexadecene succinic acid. Another type of acidic corrosion inhibitor available is a half ester of alkenyl succinic acid and an alcohol (such as polyethylene glycol) having about 8 to about 24 carbon atoms in the alkenyl group. The corresponding half amides of such alkenyl succinic acids are also useful. Useful rust inhibitors are high molecular weight organic acids.In some embodiments, the engine oil contains no rust inhibitors.

[0102] Rust inhibitors, if present, may be used in optional amounts sufficient to provide from about 0 wt % to about 5 wt %, from about 0.01 wt % to about 3 wt %, from about 0.1 wt % to about 2 wt % based on the final weight of the lubricating oil composition.

[0103] The lubricant composition may also include a corrosion inhibitor (it should be noted that some of the other mentioned components may also have copper corrosion inhibiting properties). Suitable copper corrosion inhibitors include etheramines, polyethoxylated compounds such as ethoxylated amines and ethoxylated alcohols, imidazolines, mono- and di-alkylthiadiazoles, and the like.

[0104] Thiazoles, triazoles, and thiadiazoles may also be used in lubricants. Examples include benzotriazole, tolyltriazole, octyltriazole, decyltriazole; dodecyltriazole, 2-mercaptobenzotriazole, 2,5-dimercapto-1,3,4-thiadiazole, 2-mercapto-5-alkylthio-1,3,4-thiadiazole, and 2-mercapto-5-alkyldithio-1,3,4-thiadiazole. In one embodiment, the lubricant composition includes a 1,3,4-thiadiazole, such as 2-alkyldithio-5-mercapto-1,3,4-dithiadiazole.

[0105] Defoamers / surfactants may also be included in the fluids according to the present invention. Various agents are known for such purposes. Copolymers of ethyl acrylate and hexyl acrylate may be used, such as PC-1244 available from Solutia. In other embodiments, silicone fluids may be included, such as 4% DCF. A mixture of defoamers may also be present in the lubricant composition.

[0106] Example

[0107] The following examples are illustrations of exemplary embodiments of the present disclosure. In these examples, and elsewhere in this application, unless otherwise stated, all ratios, parts and percentages are by weight. It is intended to present these examples only for illustrative purposes, and is not intended to limit the scope of the invention disclosed herein.

[0108] Comparative Example 1

[0109] A comparative zinc dialkyl dithiophosphate was prepared as follows: About 32.6 pounds of 2-ethylhexanol was charged to a stainless steel reactor, followed by the slow addition of about 13.8 pounds of phosphorus pentasulfide (containing about 27.7% phosphorus as P2S5) to maintain the temperature in the range of about 55° C. to about 77° C. with vigorous stirring. Next, about 41.2 pounds of additional phosphorus pentasulfide was charged to the reactor, followed by the slow addition of about 97.8 pounds of additional 2-ethylhexanol, maintaining the temperature between about 92° C. and about 97° C. After the second charge of 2-ethylhexanol was completed, the reactor was maintained at about 92° C. to about 97° C. for about 45 minutes to form reaction product A. Reaction product A consists of Figure 4 The image representation is considered to contain at least the following structure of 2-ethylhexyl dithiophosphoric acid and at least one 2-ethylhexyl dithiophosphoric acid polysulfide phosphorus species:

[0110]

[0111] Next, the zinc dialkyl dithiophosphate additive was prepared directly from the above reaction product A of 2-ethylhexyl dithiophosphoric acid as follows: about 6.3 pounds of base oil was charged into a stainless steel reactor, and then about 5.3 pounds of ZnO was charged into the reactor at about 60° C. and under vigorous stirring. Next, about 32.6 pounds of the above reaction product A containing 2-ethylhexyl dithiophosphoric acid and polysulfide species was slowly charged at about 85° C. over about 1.5 hours. After the reaction, a vacuum (about 28 inches of mercury) was applied for about 1 hour. After vacuum stripping, about 5.6 pounds of base oil was charged into the reactor.

[0112] Example 1

[0113] The reaction product A from Comparative Example 1 comprising 2-ethylhexyl dithiophosphoric acid and residual phosphorus polysulfide was further processed in a wiped film evaporator (ICL-04 short path distillation system, GIG Karasek, Austria). The wiped film evaporator was operated at a jacket temperature of about 108° C. and a pressure of about 0.5 Torr. The condenser was cooled to about 5° C. The evaporator had a split ratio of about 94% distillate to about 6% bottoms or residue. The condensate was collected as distilled 2-ethylhexyl dithiophosphoric acid.

[0114] Next, the zinc dialkyl dithiophosphate reaction product of the present invention is prepared from the condensate or distilled 2-ethylhexyl dithiophosphoric acid obtained from the wiped film evaporator as follows: about 6.3 pounds of base oil are charged to a stainless steel reactor, and then about 5.3 pounds of ZnO are charged to the reactor at 60° C. and under vigorous stirring. Next, about 32.6 pounds of condensate or distilled 2-ethylhexyl dithiophosphoric acid is slowly charged over about 1.5 hours at about 85° C. After the reaction, a vacuum (about 28 inches of mercury) is applied for about 1 hour. After vacuum stripping, about 5.6 pounds of base oil are charged to the reactor to produce the zinc dialkyl dithiophosphate reaction product of the present invention, which is believed to be substantially free of any phosphorus polysulfide.

[0115] Example 2

[0116] Hydraulic lubricating compositions containing the zinc dialkyl dithiophosphate additives of Comparative Example 1 and Inventive Example 1 were prepared as shown in Table 3 below.

[0117] Table 3: Comparative hydraulic fluids and hydraulic fluids of the present invention

[0118] Comparison of hydraulic fluids, % Hydraulic fluid of the present invention, % Comparative Example 1 0.5 - Example 1 - 0.5 Hydraulic Additive Package* 1.6 1.6 Group I base oil 93.4 95.9

[0119] *Hydraulic additive package includes base oil, demulsifier, friction modifier, viscosity modifier, anti-wear agent, detergent, anti-corrosion agent and antioxidant

[0120] Figure 1 The phosphorus NMR spectra of the comparative hydraulic fluid and the inventive hydraulic fluid from Table 3 are shown and demonstrate that the comparative hydraulic fluid has additional peaks identified in the figure which are believed to be the presence of various phosphorus polysulfide compositions not found in the inventive hydraulic fluid.

[0121] Copper corrosion was also evaluated at 121°C for an extended period of two days according to the method of ASTM D130. For this test, three sample containers were prepared for each finished fluid (each container held approximately 45 grams of finished fluid and copper strip). The containers were removed and the solutions were collected at each time point in Table 4. Two grams of each solution were then used for copper corrosion according to ASTM D4951, and the results are shown in Table 4 below.

[0122] Table 4: Copper corrosion

[0123] Comparative Hydraulic Fluids (ppm of Copper) Hydraulic fluid of the present invention (ppm of copper) 0 0 0 3 hours 285 11 24 hours 627 12 48 hours 641 13

[0124] The reaction products of the present invention exhibit from about 90% to about 98% improvement in copper corrosion. Figure 2 (showing both comparative and inventive additives) and Figure 3 The graph of (Inventive Additive Only) also shows the significant improvement in copper corrosion between the comparative additive and the inventive additive.

[0125] The anti-wear performance of the comparative reaction product and the inventive reaction product was also evaluated according to ASTM D4172 (4 balls) at 1200 rpm, 40 KG weight, 75°C, 1 hour. Each fluid contained the same additive package and base oil composition, the only difference being 0.5 wt% of the comparative additive or the inventive additive. The results of the wear scar testing are provided in Table 5 below.

[0126] Table 5: Wear scars

[0127] Comparison of hydraulic fluids, mm Hydraulic fluid of the present invention, mm Test 1 0.492 0.462 Test 2 0.479 0.440

[0128] As shown in Table 5 above, the hydraulic fluids of the present invention exhibit wear scarring that is equal to or even slightly better than the comparative hydraulic fluids, and as shown in Table 4 above, significantly improve copper corrosion.

[0129] It should be noted that, as used in this specification and the appended claims, the singular forms "a," "an," and "the" include plural referents unless expressly and affirmatively limited to one referent. Thus, for example, reference to "an antioxidant" includes two or more different antioxidants. As used herein, the term "comprising" and its grammatical variations are intended to be non-limiting, such that recitation of items in a list does not exclude other like items that can be substituted or added to the listed items.

[0130] For purposes of this specification and the appended claims, unless otherwise indicated, all numbers and other numerical values ​​used in the specification and claims indicating quantities, percentages or ratios should be understood to be modified in all cases by the term "about". Therefore, unless otherwise indicated, the numerical parameters set forth in the following specification and the appended claims are approximate values ​​that may vary depending on the desired properties sought to be obtained by the present disclosure. At a minimum, and without attempting to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be interpreted in light of the number of reported significant figures and by applying ordinary rounding techniques.

[0131] It should be understood that each component, compound, substituent or parameter disclosed herein should be interpreted as disclosed for use alone or in combination with one or more of each of the other components, compounds, substituents or parameters disclosed herein.

[0132] It should be further understood that each range disclosed herein should be interpreted as a disclosure of each specific value within the disclosed range with the same number of significant figures. Thus, for example, a range of 1 to 4 should be interpreted as an explicit disclosure of the values ​​1, 2, 3, and 4, as well as any range of such values.

[0133] It should be further understood that each lower limit of each scope disclosed herein should be interpreted as being disclosed in combination with each upper limit of each scope disclosed herein for the same component, compound, substituent or parameter and each specific value in each scope. Therefore, the disclosure should be interpreted as being disclosed by combining each lower limit of each scope with each upper limit of each scope or with each specific value in each scope, or by combining each upper limit of each scope with each specific value in each scope. That is, it should also be further understood that any scope between the endpoint values ​​in a wide range is also discussed herein. Therefore, the scope of 1 to 4 also means the scope of 1 to 3, 1 to 2, 2 to 4, 2 to 3, etc.

[0134] In addition, a specific amount / value of a component, compound, substituent or parameter disclosed in this specification or the examples should be interpreted as a disclosure of a lower or upper limit of a range, and therefore can be combined with any other lower or upper limit or specific amount / value of a range for the same component, compound, substituent or parameter disclosed elsewhere in this disclosure to form a range for that component, compound, substituent or parameter.

[0135] Although specific embodiments have been described, alternatives, modifications, variations, improvements, and substantial equivalents that are not currently foreseen or may not currently be foreseen may occur to applicants or other persons skilled in the art. Therefore, the appended claims as filed and as they may be amended are intended to cover all such alternatives, modifications, variations, improvements, and substantial equivalents.

Claims

1. A lubricating composition, comprising: Most base oils of one or more lubricating viscosities; An organometallic phosphorus antiwear additive or a salt thereof is provided, wherein the organometallic phosphorus antiwear additive or a salt thereof is prepared by a method comprising the following steps: (a) reacting an organic hydroxy compound with phosphorus pentasulfide to form a reaction product; (b) distilling the reaction product and recovering a condensate; and (c) neutralizing the condensate with an alkaline or neutral metal compound comprising one or more of a metal oxide, a metal hydroxide or a metal carbonate to form the organometallic phosphorus antiwear additive or a salt thereof.

2. The lubricating composition of claim 1, wherein the distillation is carried out at one or more of a temperature of at least 50°C, a pressure of at least 0.1 Torr, or a combination thereof; and / or wherein the condensate is recovered at a temperature of 10°C or less; and / or wherein the distillation is carried out in a thin film evaporator, a short path evaporator, or a combination thereof.

3. The lubricating composition of claim 1, wherein the distillation is performed in a falling film evaporator, a wiped film evaporator, or a combination thereof.

4. The lubricating composition of claim 1, wherein the condensate comprises dialkyl dithiophosphoric acid; wherein the dialkyl dithiophosphoric acid is dipropyl dithiophosphoric acid, diisopropyl dithiophosphoric acid, dibutyl dithiophosphoric acid, diisobutyl dithiophosphoric acid, or a combination thereof.

5. The lubricating composition of claim 1, wherein the basic or neutral metal compound is a metal oxide, metal hydroxide or metal carbonate of aluminum, lead, tin, molybdenum, manganese, nickel, copper, titanium, zirconium, zinc or a combination thereof.

6. The lubricating composition of claim 1 wherein the basic or neutral metal compound is a molar excess of zinc oxide.

7. The lubricating composition according to claim 1, wherein the organic hydroxy compound is a C1 to C6 straight or branched chain alcohol, a hydroxy aromatic compound, or a mixture thereof.

8. The lubricating composition of claim 1, wherein the organic hydroxy compound is methanol, ethanol, propanol, isopropanol, butanol, isobutanol, tert-butanol, sec-butanol, phenol, naphthol, pentanol, hexanol, isohexanol, octanol, decanol, dodecanol, octadecanol, 2-ethylhexanol, 4-methyl-2-pentanol, phenyl alcohol, butylphenyl alcohol, cyclohexanol, methylcyclopentanol, propenyl alcohol, butenyl alcohol, or a combination thereof.

9. The lubricating composition of claim 1, wherein the organic hydroxy compound is ethylhexanol, the reaction product comprises diethylhexyl dithiophosphoric acid and one or more phosphorus polysulfides, the condensate comprises diethylhexyl dithiophosphoric acid and is substantially free of the one or more phosphorus polysulfides, and the condensate is further reacted with zinc oxide to form the organometallic phosphorus providing antiwear additive.

10. The lubricating composition of claim 1, wherein the lubricating composition comprises 0.1 wt % to 5 wt % of the organometallic phosphorus providing antiwear additive; and / or wherein the organic hydroxy compound is provided in a molar ratio of 4:1 to 10:1 relative to the phosphorus pentasulfide; and / or wherein the basic or neutral metal compound is provided in a molar ratio of 0.01:1 to 0.5:1 relative to the organic hydroxy compound.

11. A method for preparing an organometallic phosphorus antiwear additive, the method comprising: reacting an organic hydroxy compound with phosphorus pentasulfide to form a reaction product; distilling the reaction product and recovering a condensate therefrom; as well as The condensate is neutralized with a basic or neutral metal compound including one or more of a metal oxide, a metal hydroxide or a metal carbonate to form the organometallic phosphorus providing antiwear additive or a salt thereof.

12. The process of claim 11, wherein the distillation is carried out at a temperature of at least 80°C and a pressure of at least 0.4 Torr; and / or wherein the condensate is recovered at a temperature of 10°C or less; and / or wherein the distillation is carried out in a thin film evaporator, a short path evaporator, or a combination thereof.

13. The process of claim 11, wherein the distillation is carried out in a falling film evaporator, a wiped film evaporator, or a combination thereof.

14. The method of claim 11, wherein the condensate comprises dialkyl dithiophosphoric acid; wherein the dialkyl dithiophosphoric acid is dipropyl dithiophosphoric acid, diisopropyl dithiophosphoric acid, dibutyl dithiophosphoric acid, diisobutyl dithiophosphoric acid, or a combination thereof.

15. The method of claim 11, wherein the basic or neutral metal compound is a metal oxide, metal hydroxide or metal carbonate of aluminum, lead, tin, molybdenum, manganese, nickel, copper, titanium, zirconium, zinc or a combination thereof.

16. The method of claim 11, wherein the basic or neutral metal compound is a molar excess of zinc oxide.

17. The method according to claim 11, wherein the organic hydroxy compound is a C1 to C6 straight or branched alcohol, a hydroxyaryl compound, or a mixture thereof.

18. The method of claim 11, wherein the organic hydroxy compound is methanol, ethanol, propanol, isopropanol, butanol, isobutanol, tert-butanol, sec-butanol, phenol, naphthol, pentanol, hexanol, isohexanol, octanol, decanol, dodecanol, octadecanol, 2-ethylhexanol, 4-methyl-2-pentanol, phenyl alcohol, butylphenyl alcohol, cyclohexanol, methylcyclopentanol, propenyl alcohol, butenyl alcohol, or a combination thereof.

19. The method of claim 11 wherein the organic hydroxy compound is isopropyl alcohol, the reaction product comprises diisopropyl dithiophosphoric acid and one or more phosphorus polysulfides, the condensate comprises the diisopropyl dithiophosphoric acid and is substantially free of the one or more phosphorus polysulfides, and the condensate is neutralized with a molar excess of zinc oxide.

20. The method of claim 11, wherein the organic hydroxy compound is provided in a molar ratio of 4:1 to 10:1 relative to the phosphorus pentasulfide; and / or wherein the basic or neutral metal compound is provided in a molar ratio of 0.01:1 to 0.5:1 relative to the organic hydroxy compound.

21. An organometallic phosphorus antiwear additive or a salt thereof, wherein the organometallic phosphorus antiwear additive or a salt thereof is prepared by a process comprising the following steps: (a) reacting an organic hydroxy compound with phosphorus pentasulfide to form a reaction product; (b) distilling the reaction product and recovering a condensate; and (c) neutralizing the condensate with an alkaline or neutral metal compound comprising one or more of a metal oxide, a metal hydroxide or a metal carbonate to form the organometallic phosphorus antiwear additive or a salt thereof.

Images