Polyethersulfone web

Abstract

Polyethersulfone webs are described. There is provided a fibrous web comprising polyethersulfone fibers having an average diameter of less than or equal to 250 nm wherein the relative surface area of the fibrous web is greater than or equal to 80%. There is provided a fibrous web comprising polyethersulfone fibers having an average diameter of less than or equal to 250 nm, where the relative surface area of the fibrous web is greater than or equal to 75%, and where the measured surface area of the fibrous web is greater than or equal to 25 m2 / g. The invention further provides a filter medium which comprises the fiber web.

Description

[0001] This application is a divisional application of the Chinese patent application entitled "Polyethersulfone Fiber Mesh" and application number 201880030741.0. Patent application 201880030741.0 is a national application entering the Chinese national phase based on the international application (PCT / US2018 / 027032) filed on April 11, 2018 under the Patent Cooperation Treaty. The priority date of the application is April 11, 2017. Technical Field

[0002] The present invention relates generally to fiber webs and, more particularly, to fiber webs comprising polyethersulfone fibers. Background Art

[0003] Filter media can be used in a variety of applications to remove contaminants. Depending on the application, the filter media can be designed to have different performance characteristics.

[0004] Typically, the filter medium can be formed by a fiber mesh. For example, the mesh can include components such as polyethersulfone fibers. The fiber mesh provides a porous structure that allows fluid to flow through the filter medium. Contaminant particles contained in the fluid can be captured on the fiber mesh. Filter media features (such as fiber diameter and basis weight) affect filter performance including filter efficiency, dust holding capacity, and resistance to fluid flow through the filter.

[0005] Webs formed from polyethersulfone fibers typically contain fibers having a large average diameter, fibers having a broad distribution of diameters, and / or contain defects that reduce the surface area of ​​the web. Summary of the invention

[0006] Fibrous webs comprising polyethersulfone fibers and related components and methods associated therewith are provided.

[0007] In one set of embodiments, a fiber web is provided. In one embodiment, the fiber web comprises polyethersulfone fibers having an average diameter less than or equal to 250 nm, and the relative surface area of ​​the fiber web is greater than or equal to 80%.

[0008] In some embodiments, the fiber web comprises polyethersulfone fibers having an average diameter of less than or equal to 250 nm, having a surface area greater than or equal to 75%, and having a surface area greater than or equal to 25 nm. 2 / g of measured surface area.

[0009] When considered in conjunction with the accompanying drawings, other advantages and new features of the present invention will become apparent from the following detailed description of multiple non-limiting embodiments of the present invention. In the case where this specification and the documents incorporated by reference contain conflicting and / or inconsistent disclosures, this specification should be used as the standard. If two or more documents incorporated by reference contain conflicting and / or inconsistent disclosures relative to each other, the documents with a later effective date should be used as the standard. BRIEF DESCRIPTION OF THE DRAWINGS

[0010] Non-limiting embodiments of the present invention will be described by way of example with reference to the accompanying drawings. In the drawings:

[0011] Figure 1 Shown is a graph showing the relationship between filtration efficiency and relative surface area for 0.2 micron diameter polystyrene spheres according to some embodiments. DETAILED DESCRIPTION

[0012] Fiber webs and related concepts and methods are described herein. Typically, the fiber web comprises polyethersulfone (PES) fibers. PES fibers can have a low average diameter and a small amount of defects. As further described below, in some embodiments, the fiber web can have a high relative surface area and / or a high measured surface area. The above features can enhance the filtration performance of the fiber web by, for example, improving filtration efficiency. In certain embodiments, the fiber web can be a filter medium or a layer within a filter medium. The filter medium can be suitable for filtering fluids, such as air, water and / or oil.

[0013] In some embodiments, the fiber web can be formed by an electrospinning process, as described in more detail below. Also as described further below, it should be understood that, optionally, the fiber web can be a layer (e.g., a first layer) in a filter medium that also includes additional layers, such as a second layer and / or a third layer, etc.

[0014] In some embodiments, a fiber web (e.g., a fiber web within a filter medium) may contain PES in relatively high amounts (e.g., at least about 75% by weight of the fiber web may be PES, at least about 90% by weight of the fiber web may be PES, at least about 95% by weight of the fiber web may be PES, at least about 99% by weight of the fiber web may be PES, or at least about 99.9% by weight of the fiber web may be PES). In some embodiments, a fiber web may contain PES fibers (i.e., fibers containing PES) in relatively high amounts (e.g., PES fibers may account for at least about 75% by weight of the fibers in the fiber web, at least about 90% by weight of the fibers in the fiber web, at least about 95% by weight of the fibers in the fiber web, at least about 99% by weight of the fibers in the fiber web, at least about 99.9% by weight of the fibers in the fiber web, or 100% by weight of the fibers in the fiber web). It should be understood that, as used herein, the terms "PES fibers" and "polyethersulfone fibers" refer to fibers containing at least 50% by weight of PES. In some cases, the PES fibers may comprise at least about 75% by weight PES, at least about 90% by weight PES, at least about 95% by weight PES, or at least about 99% by weight PES. In some cases, the PES fibers are formed entirely of PES. It should be understood that other types of fibers may also be present in the PES web, such as fibers that do not comprise PES and / or fibers that comprise less than 50% by weight PES.

[0015] In some embodiments, the PES fibers in the web can have a low average diameter. In some embodiments, the average diameter of the PES fibers in the web can be less than or equal to about 250 nanometers, less than or equal to about 225 nanometers, less than or equal to about 200 nanometers, less than or equal to about 175 nanometers, less than or equal to about 150 nanometers, less than or equal to about 130 nanometers, less than or equal to about 100 nanometers, less than or equal to about 90 nanometers, or less than or equal to about 50 nanometers. In some embodiments, the average diameter of the PES fibers in the web can be greater than or equal to about 20 nanometers, greater than or equal to about 50 nanometers, greater than or equal to about 90 nanometers, greater than or equal to about 100 nanometers, greater than or equal to about 130 nanometers, greater than or equal to about 150 nanometers, greater than or equal to about 175 nanometers, greater than or equal to about 200 nanometers, or greater than or equal to about 225 nanometers. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to about 20 nanometers and less than or equal to about 250 nanometers, greater than or equal to about 50 nanometers and less than or equal to about 250 nanometers, greater than or equal to about 90 nanometers and less than or equal to about 130 nanometers). Other ranges are also possible. Generally, individual fiber diameters can be measured by a microscope, such as a scanning electron microscope (SEM), and statistics about fiber diameters, such as the average fiber diameter and the fiber diameter standard deviation, can be determined by subjecting the measured fiber diameters to appropriate statistical techniques.

[0016] In some embodiments, the PES fiber in the net can have a relatively tight fiber diameter distribution. In some embodiments, the standard deviation of the PES fiber diameter is less than or equal to about 75 nanometers, less than or equal to about 60 nanometers, less than or equal to about 50 nanometers, less than or equal to about 40 nanometers, less than or equal to about 30 nanometers, less than or equal to about 25 nanometers, or less than or equal to about 10 nanometers. In some embodiments, the standard deviation of the PES fiber diameter is greater than or equal to about 10 nanometers, greater than or equal to about 20 nanometers, greater than or equal to about 25 nanometers, greater than or equal to about 30 nanometers, greater than or equal to about 40 nanometers, greater than or equal to about 50 nanometers, greater than or equal to about 60 nanometers, or greater than or equal to about 70 nanometers. The combination of the above-mentioned scope is also possible (for example, greater than or equal to about 20 nanometers and less than or equal to about 75 nanometers or greater than or equal to about 25 nanometers and less than or equal to about 50 nanometers). Other scopes are also possible.

[0017] Typically, the PES in the fiber can have any suitable weight average molecular weight. For example, the weight average molecular weight of PES can be greater than or equal to about 25kg / mol, greater than or equal to about 45kg / mol, greater than or equal to about 60kg / mol, greater than or equal to about 80kg / mol, greater than or equal to about 100kg / mol, or greater than or equal to about 125kg / mol. The weight average molecular weight of PES can be less than or equal to about 150kg / mol, less than or equal to about 125kg / mol, less than or equal to about 100kg / mol, less than or equal to about 80kg / mol, less than or equal to about 60kg / mol, or less than or equal to about 45kg / mol. The combination of the above range is also possible (for example, greater than or equal to about 25kg / mol and less than or equal to about 150kg / mol, or greater than or equal to about 45kg / mol and less than or equal to about 80kg / mol). Other ranges are also possible. The weight average molecular weight of PES can be measured by conventional gel permeation chromatography technology.

[0018] In some embodiments, the PES fiber webs as described herein can have one or more advantageous properties (e.g., high measured surface area, high relative surface area, high filtration efficiency). It should be understood that any property of the fiber web described herein can refer to the properties of the fiber web without any surface treatment after manufacture, or can refer to the properties of the fiber web that has undergone one or more surface treatments (as described in further detail below).

[0019] In some embodiments, the PES fiber web may preferably have a relatively high measured surface area. For example, the measured surface area of ​​the fiber web may be greater than or equal to about 19 m 2 / g, greater than or equal to about 22m2 / g, greater than or equal to about 25m 2 / g, greater than or equal to about 35m 2 / g, greater than or equal to about 40m 2 / g, greater than or equal to about 55m 2 / g, greater than or equal to about 75m 2 / g, greater than or equal to about 95m 2 / g, greater than or equal to about 115m 2 / g, greater than or equal to about 135m 2 / g, or greater than or equal to about 155m 2 In some embodiments, the measured surface area of ​​the fiber web may be less than or equal to about 200 m 2 / g, less than or equal to about 155m 2 / g, less than or equal to about 135m 2 / g, less than or equal to about 115m 2 / g, less than or equal to about 95m 2 / g, less than or equal to about 75m 2 / g, less than or equal to about 55m 2 / g, less than or equal to about 40m 2 / g, less than or equal to about 35m 2 / g, less than or equal to about 25m 2 / g, or less than or equal to about 22m 2 Combinations of the above ranges are also possible (e.g., greater than or equal to about 19 m 2 / g and less than or equal to about 200m 2 / g, greater than or equal to about 55m 2 / g and less than or equal to about 200m 2 / g, greater than or equal to about 95m 2 / g and less than or equal to about 200m 2 / g, greater than or equal to about 155m 2 / g and less than or equal to about 200m 2 / g, greater than or equal to about 19m 2 / g and less than or equal to about 40m 2 / g, or greater than or equal to about 22m 2 / g and less than or equal to about 35m 2 / g). Other ranges are also possible.

[0020] The surface area is measured by using a standard BET surface area measurement technique. The BET surface area is measured according to the Battery Council International Standard BCIS-03A (2009) "Recommended Battery Materials Specifications Valve Regulated Recombinant Batteries" Section 10 "Standard Test Method for Surface Area of ​​Recombinant Battery Separator Mat". According to this technique, the BET surface area is measured via adsorption analysis with nitrogen using a BET surface analyzer (e.g., Micromeritics Gemini III 2375 surface area analyzer); the sample amount is 0.5 to 0.6 grams in, for example, a 3 / 4" tube; and the sample is degassed at 75°C for at least 3 hours.

[0021] PES fiber web can also be characterized by theoretical surface area. As used herein, theoretical surface area is defined by the following equation:

[0022]

[0023] Among them, SA 理论 is the theoretical surface area, and p is the density of the polymer forming the fiber (e.g., for PES fibers, it is the density of PES (for PES fibers that are 100 wt. % PES, it is 1.37 g / cm 3 )), and average (1 / D) refers to the reciprocal of the harmonic mean of the diameters of the fibers forming the web. In some embodiments, the theoretical surface area of ​​the PES fiber web is greater than or equal to about 19 m 2 / g, greater than or equal to about 22m 2 / g, greater than or equal to about 25m 2 / g, greater than or equal to about 35m 2 / g, greater than or equal to about 40m 2 / g, greater than or equal to about 55m 2 / g, greater than or equal to about 75m 2 / g, greater than or equal to about 95m 2 / g, greater than or equal to about 115m 2 / g, greater than or equal to about 135m 2 / g, greater than or equal to about 155m 2 / g, greater than or equal to about 175m 2 / g, greater than or equal to about 200m 2 / g, greater than or equal to about 225m 2 / g, greater than or equal to about 250m 2 / g, or greater than or equal to about 275m 2 / g. The theoretical surface area of ​​the fiber web may be less than or equal to about 300 m 2 / g, less than or equal to about 275m 2 / g, less than or equal to about 250m 2 / g, less than or equal to about 225m 2 / g, less than or equal to about 200m 2 / g, less than or equal to about 155m 2 / g, less than or equal to about 135m 2 / g, less than or equal to about 115m 2 / g, less than or equal to about 95m 2 / g, less than or equal to about 75m 2 / g, less than or equal to about 55m 2 / g, less than or equal to about 40m 2 / g, less than or equal to about 35m 2 / g, less than or equal to about 25m 2 / g, or less than or equal to about 22m 2 Combinations of the above ranges are also possible (e.g., greater than or equal to about 19 m 2 / g and less than or equal to about 200m 2 / g, greater than or equal to about 55m 2 / g and less than or equal to about 200m 2 / g, greater than or equal to about 95m 2 / g and less than or equal to about 200m 2 / g, greater than or equal to about 155m 2 / g and less than or equal to about 200m 2 / g, greater than or equal to about 19m 2 / g and less than or equal to about 40m 2 / g, or greater than or equal to about 22m 2 / g and less than or equal to about 35m 2 / g). Other ranges are also possible.

[0024] In some embodiments, the PES fiber web can have a high relative surface area. As used herein, the relative surface area of ​​a fiber web refers to 100% times the ratio of the measured surface area of ​​a fiber web (having fibers with density and average diameter) as described above to the theoretical surface area of ​​a fiber web containing fibers of the same density and average diameter. In some embodiments, the relative surface area of ​​the fiber web can be greater than or equal to about 65%, greater than or equal to about 70%, greater than or equal to about 75%, greater than or equal to about 80%, greater than or equal to about 85%, greater than or equal to about 90%, or greater than or equal to about 95%. In some embodiments, the relative surface area of ​​the fiber web can be less than or equal to about 100%, less than or equal to about 95%, less than or equal to about 90%, less than or equal to about 85%, less than or equal to about 80%, less than or equal to about 75%, or less than or equal to about 70%. Combinations of the above-referenced ranges are also possible (eg, greater than or equal to about 65% and less than or equal to about 100%, or greater than or equal to about 80% and less than or equal to about 100%). Other ranges are also possible.

[0025] Without wishing to be bound by theory, it is believed that a fiber web having a high relative surface area (e.g., approaching about 100%) contains few defects such as beads. As used herein, beads are portions of a fiber web having a width greater than 10 times the average fiber diameter of the fibers within the fiber web and an aspect ratio less than 50. In some embodiments, it can be advantageous for a fiber web to have a relatively small amount of beads. A fiber web having a relatively small amount of beads can have improved filtration efficiency compared to an otherwise equivalent fiber web containing a higher amount of beads. In some cases, the relative surface area of ​​the fibers can be within or outside the above ranges and can have a low concentration of beads. For example, a fiber web can have less than 40,000 beads / mm 2 Less than 10,000 beads / mm 2 Less than 5000 beads / mm 2 , or less than 300 beads / mm 2 . per mm 2 The number of beads can be determined microscopically.

[0026] The PES fiber web may have any suitable basis weight. In some embodiments, the basis weight of the fiber web may be greater than or equal to about 0.05 g / m 2 , greater than or equal to about 0.1 g / m 2 , greater than or equal to about 0.2g / m 2 , greater than or equal to about 0.5 g / m 2 , greater than or equal to about 1g / m 2 , or greater than or equal to about 2 g / m 2 , greater than or equal to about 3g / m2 , greater than or equal to about 5g / m 2 , greater than or equal to about 10g / m 2 , or greater than or equal to about 15 g / m 2 In some embodiments, the basis weight of the fiber web may be less than or equal to about 30 g / m 2 , less than or equal to about 25g / m 2 , less than or equal to about 15g / m 2 , less than or equal to about 10g / m 2 , less than or equal to about 5g / m 2 , less than or equal to about 3g / m 2 , less than or equal to about 2g / m 2 , less than or equal to about 1g / m 2 , less than or equal to about 0.5g / m 2 , less than or equal to about 0.2g / m 2 , or less than or equal to about 0.1 g / m 2 Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to about 0.5 g / m 2 and less than or equal to about 30g / m 2 , greater than or equal to about 2g / m 2 and less than or equal to about 25g / m 2 , greater than or equal to about 3g / m 2 and less than or equal to about 15g / m 2 , greater than or equal to about 0.05 g / m 2 and less than or equal to about 1g / m 2 , greater than or equal to about 0.1 g / m 2 and less than or equal to about 0.5 g / m 2 , greater than or equal to about 0.05 g / m 2 and less than or equal to about 5g / m 2 , or greater than or equal to about 0.5 g / m 2 and less than or equal to about 2g / m 2 ). Other ranges are also possible. The basis weight of the fiber web can be determined according to standard ISO 536:2012. In embodiments where the fiber web is supported on a substrate or is a layer within a fiber web, the basis weight of the fiber web can be measured by determining the basis weight of the substrate or the filter medium without the fiber web, determining the basis weight of the substrate and the fiber web, or the filter medium including the fiber web, and taking the difference between these two values.

[0027] The PES web can have any suitable thickness. In some embodiments, the PES web has a thickness of about 20 nanometers or more, about 50 nanometers or more, about 90 nanometers or more, about 100 nanometers or more, about 130 nanometers or more, about 150 nanometers or more, about 175 nanometers or more, about 200 nanometers or more, about 225 nanometers or more, about 500 nanometers or more, about 1 micrometer or more, about 2.5 micrometers or more, about 5 micrometers or more, about 7.5 micrometers or more, about 10 micrometers or more, about 12.5 micrometers or more, about 15 micrometers or more, or about 17.5 micrometers or more. In some embodiments, the thickness of the PES fiber web is less than or equal to about 20 microns, less than or equal to about 17.5 microns, less than or equal to about 15 microns, less than or equal to about 12.5 microns, less than or equal to about 10 microns, less than or equal to about 7.5 microns, less than or equal to about 5 microns, less than or equal to about 2.5 microns, less than or equal to about 1 micron, less than or equal to about 500 nanometers, less than or equal to about 225 nanometers, less than or equal to about 200 nanometers, less than or equal to about 175 nanometers, less than or equal to about 150 nanometers, less than or equal to about 130 nanometers, less than or equal to about 100 nanometers, less than or equal to about 90 nanometers, or less than or equal to about 50 nanometers. Combinations of the above ranges are also possible (e.g., greater than or equal to about 20 nanometers and less than or equal to about 20 microns, or greater than or equal to about 5 microns and less than or equal to about 20 microns). Other ranges are also possible. The thickness of the layer can be determined by using cross-sectional SEM imaging.

[0028] The PES fiber web can have any suitable mean flow pore size. In some embodiments, the mean flow pore size of the fiber web is greater than or equal to about 0.05 microns, greater than or equal to about 0.1 microns, greater than or equal to about 0.2 microns, greater than or equal to about 0.5 microns, greater than or equal to about 1 micron, greater than or equal to about 2 microns, greater than or equal to about 4 microns, greater than or equal to about 5 microns, greater than or equal to about 8 microns, or greater than or equal to about 10 microns. In some embodiments, the mean flow pore size of the fiber web is less than or equal to about 20 microns, less than or equal to about 10 microns, less than or equal to about 8 microns, less than or equal to about 5 microns, less than or equal to about 4 microns, less than or equal to about 2 microns, less than or equal to about 1 micron, less than or equal to about 0.5 microns, or less than or equal to about 0.2 microns. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to about 0.05 microns and less than or equal to about 4 microns, greater than or equal to about 0.1 microns and less than or equal to about 4 microns, greater than or equal to about 0.1 microns and less than or equal to about 2 microns, greater than or equal to about 0.2 microns and less than or equal to about 2 microns, greater than or equal to about 2 microns and less than or equal to about 20 microns, greater than or equal to about 8 microns and less than or equal to about 10 microns, greater than or equal to about 1 micron and less than or equal to about 10 microns, or greater than or equal to about 2 microns and less than or equal to about 5 microns). Other ranges are also possible. The mean flow pore size can be determined according to ASTM F316 (2003).

[0029] In certain embodiments, the PES fiber web can have a relatively low maximum pore size. In some embodiments, the maximum pore size of the fiber web can be less than or equal to about 80 microns, less than or equal to about 70 microns, less than or equal to about 60 microns, less than or equal to about 50 microns, less than or equal to about 40 microns, less than or equal to about 30 microns, less than or equal to about 20 microns, less than or equal to about 10 microns, less than or equal to about 5 microns, less than or equal to about 2 microns, less than or equal to about 1 micron, less than or equal to about 0.5 microns, less than or equal to about 0.2 microns, less than or equal to about 0.1 microns, or less than or equal to about 0.8 microns. In some embodiments, the maximum pore size of the fiber mesh can be greater than or equal to about 0.06 microns, greater than or equal to about 0.08 microns, greater than or equal to about 0.1 microns, greater than or equal to about 0.2 microns, greater than or equal to about 0.5 microns, greater than or equal to about 1 micron, greater than or equal to about 2 microns, greater than or equal to about 5 microns, greater than or equal to about 10 microns, greater than or equal to about 20 microns, greater than or equal to about 30 microns, greater than or equal to about 40 microns, greater than or equal to about 50 microns, greater than or equal to about 60 microns, or greater than or equal to about 70 microns. Combinations of the above ranges are also possible (e.g., greater than or equal to about 0.06 microns and less than or equal to about 80 microns, greater than or equal to about 0.08 microns and less than or equal to about 50 microns). Other ranges are also possible. The maximum pore size can be determined according to ASTM F316 (2003).

[0030] In some embodiments, the PES fiber web can have a relatively low maximum pore size to mean flow pore size ratio. The maximum pore size to mean flow pore size ratio can be less than or equal to about 4.0, less than or equal to about 3.8, less than or equal to about 3.6, less than or equal to about 3.4, less than or equal to about 3.2, less than or equal to about 3.0, less than or equal to about 2.8, less than or equal to about 2.6, less than or equal to about 2.4, less than or equal to about 2.2, less than or equal to about 2.0, less than or equal to about 1.8, less than or equal to about 1.6, or less than or equal to about 1.4. In some embodiments, the ratio of the maximum pore size to the mean flow pore size can be greater than or equal to about 1.2, greater than or equal to about 1.4, greater than or equal to about 1.6, greater than or equal to about 1.8, greater than or equal to about 2.0, greater than or equal to about 2.2, greater than or equal to about 2.4, greater than or equal to about 2.8, greater than or equal to about 3.0, greater than or equal to about 3.2, greater than or equal to about 3.4, greater than or equal to about 3.6, or greater than or equal to about 3.8. Combinations of the above-referenced ranges are also possible (e.g., less than or equal to about 4.0 and greater than or equal to about 1.2, less than or equal to about 2.6 and greater than or equal to about 1.6). Other ranges are also possible.

[0031] The PES fiber web can have any suitable air permeability. In some embodiments, the fiber web has an air permeability of greater than or equal to about 0.2 CFM, greater than or equal to about 0.3 CFM, greater than or equal to about 0.5 CFM, greater than or equal to about 1 CFM, greater than or equal to about 1.7 CFM, greater than or equal to about 5 CFM, greater than or equal to about 10 CFM, greater than or equal to about 20 CFM, or greater than or equal to about 30 CFM at a pressure of 0.5 inches of water. In some embodiments, the fiber web has an air permeability of less than or equal to about 40 CFM, less than or equal to about 30 CFM, less than or equal to about 20 CFM, less than or equal to about 10 CFM, less than or equal to about 5 CFM, less than or equal to about 1.7 CFM, less than or equal to about 1 CFM, less than or equal to about 0.5 CFM, or less than or equal to about 0.3 CFM at a pressure of 0.5 inches of water. Combinations of the above ranges are also possible (e.g., greater than or equal to about 0.2 CFM and less than or equal to about 5 CFM, greater than or equal to about 0.3 CFM and less than or equal to about 1.7 CFM, greater than or equal to about 5 CFM and less than or equal to about 40 CFM, or greater than or equal to about 10 CFM and less than or equal to about 30 CFM). Other ranges are also possible. Air permeability can be measured by ASTM D737-04 (2016) at a pressure of 0.5 inches of water.

[0032] In some embodiments, the air permeability of the PES fiber mesh under the pressure of 10 inches of water is greater than or equal to about 0.5 CFM, greater than or equal to about 1 CFM, greater than or equal to about 2 CFM, greater than or equal to about 5 CFM, greater than or equal to about 10 CFM, or greater than or equal to about 20 CFM. In some embodiments, the air permeability of the fiber mesh under the pressure of 10 inches of water is less than or equal to about 50 CFM, less than or equal to about 20 CFM, less than or equal to about 10 CFM, less than or equal to about 5 CFM, less than or equal to about 2 CFM, or less than or equal to about 1 CFM. Combinations of the above ranges are also possible (e.g., greater than or equal to about 0.5 CFM and less than or equal to about 50 CFM, or greater than or equal to about 1 CFM and less than or equal to about 20 CFM). Other ranges are also possible. Air permeability can be measured by ASTM D737-04 (2016) under the pressure of 10 inches of water.

[0033] The PES fiber web may have any suitable water permeability. In some embodiments, the water permeability of the fiber web is greater than or equal to about 0.1 mL / (min*cm 2 *psi), greater than or equal to about 0.2 mL / (minute*cm 2 *psi), greater than or equal to about 0.5 mL / (minute*cm 2 *psi), greater than or equal to about 1 mL / (minute*cm 2*psi), greater than or equal to about 1.5 mL / (minute*cm 2 *psi), greater than or equal to about 2 mL / (minute*cm 2 *psi), greater than or equal to about 5 mL / (minute*cm 2 *psi), or greater than or equal to about 8 mL / (minute*cm 2 *psi). In some embodiments, the water permeability of the fiber web is less than or equal to about 10 mL / (minute*cm 2 *psi), less than or equal to about 8mL / (minute*cm 2 *psi), less than or equal to about 5mL / (minute*cm 2 *psi), less than or equal to about 2mL / (minute*cm 2 *psi), less than or equal to about 1.5 mL / (minute*cm 2 *psi), less than or equal to about 1 mL / (minute*cm 2 *psi), less than or equal to about 0.5 mL / (minute*cm 2 *psi), or less than or equal to about 0.2 mL / (minute*cm 2 *psi). Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to about 0.1 mL / (min*cm 2 *psi) and less than or equal to about 10 mL / (minute*cm 2 *psi), greater than or equal to about 0.5 mL / (minute*cm 2 *psi) and less than or equal to about 10 mL / (minute*cm 2 *psi), greater than or equal to about 1 mL / (minute*cm 2 *psi) and less than or equal to about 8 mL / (minute*cm 2 *psi), or greater than or equal to about 1.5 mL / (minute*cm 2 *psi) and less than or equal to about 5 mL / (minute*cm 2 *psi)). Other ranges are possible. The water permeability can be determined by placing a 4.8 cm2 thick 2 The fiber web is exposed to deionized water and the water flowing through the fiber web is collected to measure. The time required for 1000 mL of water to flow through the fiber web is determined, and then the water permeability is determined using the following formula:

[0034]

[0035] Prior to exposing the fiber web to deionized water, the fiber web was first immersed in isopropyl alcohol and then immersed in deionized water.

[0036] In some embodiments, the PES fiber web can have a relatively high filtration efficiency for various substances. In some embodiments, the initial filtration efficiency of the fiber web for 4 micron diameter particles can be greater than or equal to about 80%, greater than or equal to about 85%, greater than or equal to about 90%, greater than or equal to about 95%, greater than or equal to about 97%, or greater than or equal to about 99%. In some embodiments, the initial filtration efficiency of the fiber web for 4 micron diameter particles can be less than or equal to about 100%, less than or equal to about 99%, less than or equal to about 97%, less than or equal to about 95%, less than or equal to about 90%, or less than or equal to about 85%. Combinations of the above ranges are also possible (e.g., greater than or equal to about 80% and less than or equal to about 100%, or greater than or equal to about 95% and less than or equal to about 100%). Other ranges are also possible. The initial filtration efficiency for 4 micron diameter particles can be determined according to the ISO 19438:2003(E) fuel test standard, wherein ISO Medium Test Dust (ISO 12103-A3) is used as the test material.

[0037] In some embodiments, the PES fiber web can have a filtration efficiency of greater than or equal to about 75%, greater than or equal to about 80%, greater than or equal to about 85%, greater than or equal to about 90%, greater than or equal to about 95%, greater than or equal to about 97%, or greater than or equal to about 99% for 0.2 micron diameter polystyrene spheres. In some embodiments, the fiber web can have a filtration efficiency of less than or equal to about 100%, less than or equal to about 99%, less than or equal to about 97%, less than or equal to about 95%, less than or equal to about 90%, less than or equal to about 85%, or less than or equal to about 80% for 0.2 micron diameter polystyrene spheres. Combinations of the above ranges are also possible (e.g., greater than or equal to about 75% and less than or equal to about 100%, or greater than or equal to about 90% and less than or equal to about 100%). Other ranges are also possible. The filtration efficiency of the filter medium for 0.2 micron diameter polystyrene spheres can be determined by placing a 43 mm diameter fiber mesh disk in a stirring unit (e.g., Model UHP 4370ML, Sterlitech) and exposing it to a 5 ppm suspension in water of polystyrene spheres having an average diameter of 0.2 microns, a diameter range of 0.02 microns to 20 microns, and a coefficient of variation of 5% to 10%. The suspension is stirred so that a vortex of about 25% of the total solution height is formed and passed through the fiber mesh under the influence of gravity until 50 mL of solution crosses the fiber mesh. The ratio of the turbidity of the suspension after passing through the fiber mesh to the turbidity of the suspension before passing through the fiber mesh can be determined and multiplied by 100% to derive the filtration efficiency. Turbidity can be measured with a nephelometer or turbidimeter, which detects the amount of light scattered by small particles when small particles are exposed to a light beam. An example of a turbidimeter that can be used to measure turbidity is the model Micro TPI / TPW manufactured by HF Scientific, Inc. The meter is configured to meet the design criteria set forth in EN-ISO 7027:1999 (Section 6.2.4) and ASTM D1889:1994 for turbidity measurements and to meet the criteria set forth in Standard US EPA 180.1.

[0038] In some embodiments, the initial permeability of the PES fiber web to 0.3 micron diameter dioctyl phthalate (DOP) particles can be less than or equal to about 40%, less than or equal to about 30%, less than or equal to about 20%, less than or equal to about 10%, less than or equal to about 5%, or less than or equal to about 2%. In some embodiments, the initial permeability of the fiber web to 0.3 micron diameter DOP particles can be greater than or equal to about 1%, greater than or equal to about 2%, greater than or equal to about 5%, greater than or equal to about 10%, greater than or equal to about 20%, or greater than or equal to about 30%. Combinations of the above ranges are also possible (e.g., greater than or equal to about 1% and less than or equal to about 40%, or greater than or equal to about 10% and less than or equal to about 20%). Other ranges are also possible. The initial permeability to 0.3 micron DOP particles can be measured by blowing 0.3 micron diameter DOP particles through the fiber web at a face velocity of 5.33 cm / sec and measuring the percentage of particles that penetrate through the fiber web. The penetration rate of 0.3 micron diameter DOP particles can be measured by an ATI Model 100P Aerosol Tester in accordance with MIL-STD-282 (1956).

[0039] In some embodiments, the fiber web can be designed for sterile filtration. In some such embodiments, the microparticle efficiency for microorganisms can be very high (e.g., greater than or equal to about 99.999%). In some embodiments, the microparticle efficiency of the filter media for microorganisms can be expressed as a logarithmic reduction value (i.e., LRV, Log Reduction Value), which is a quantitative measure of the microbial retention of the fiber web. LRV is the permeability- 1 The logarithm of and is expressed as follows:

[0040] LRV = Log{[CFU]Challenge / [CFU]Effluent]}

[0041] where [CFU]Challenge is the number of bacteria in colony forming units in the fluid before passing through the fiber web, and [CFU]Effluent is the total number of bacteria in colony forming units in the fluid after passing through the fiber web.

[0042] LRV can be determined using ASTM F838-05 (2015). If the [CFU] effluent is zero, then use 1 in the above equation to calculate the LRV. Briefly, the LRV for 76 cm 2 The sample area concentration is 10 7 CFU / 1cm 2 Brevundimonas diminuta was used as the challenge. Therefore, the [CFU] challenge was 7.6×10 8. An LRV greater than 8.88 is considered sterile. In some embodiments, the LRV of the filter medium can be greater than or equal to about 3, greater than or equal to about 4, greater than or equal to about 5, greater than or equal to about 6, greater than or equal to about 7, greater than or equal to about 8, or greater than or equal to about 8.88. In some embodiments, the LRV of the filter medium can be less than or equal to about 8.881, less than or equal to about 8.88, less than or equal to about 8, less than or equal to about 7, less than or equal to about 6, less than or equal to about 5, or less than or equal to about 4. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to about 3 and less than or equal to about 8.881). Other ranges are also possible.

[0043] In some embodiments, the PES fiber web can have a relatively high BSA throughput. The BSA throughput can be greater than or equal to 1000 L / m 2 , greater than or equal to 1500L / m 2 , greater than or equal to 2000L / m 2 , or greater than or equal to 2500L / m 2 . BSA throughput can be less than or equal to 3000L / m 2 , less than or equal to 2500L / m 2 , less than or equal to 2000L / m 2 , or less than or equal to 1500L / m 2 Combinations of the above ranges are also possible (e.g., greater than or equal to 1000 L / m 2 And less than or equal to 3000L / m 2 Other ranges are possible. BSA throughput can be obtained by passing a freshly prepared solution of 10 mg to 50 mg BSA dissolved in 1 L of phosphate buffered saline through an effective area of ​​4.8 cm at a pressure of 3 psi to 30 psi. 2 The fiber mesh is measured by collecting the filtrate. The measurement ends when the filtrate stops collecting. The following equation can then be evaluated:

[0044]

[0045] In some embodiments, the PES fiber web can be relatively resistant to wear and tear. For example, conventional handling of the fiber web, conventional winding and unwinding of the fiber web, exposure to liquid testing environments, and / or exposure to pressure do not result in observable wear and tear of the fiber web.

[0046] As described above, in certain embodiments, the PES fiber web can be a layer of a filter medium that also includes one or more additional layers (e.g., a second layer, a third layer, a fourth layer, a fifth layer, etc.). In some embodiments, the filter medium can include at least two layers that are PES fiber webs. For example, the filter medium can include a second PES fiber web having an average fiber diameter similar to that of the first PES fiber web, or can include a second PES fiber web that includes fibers that are thicker than the fibers in the first PES fiber web.

[0047] In some embodiments, the PES web can be a layer of a filter medium comprising one or more support layers. One or more support layers can be used to support the PES web. For example, the support layer can be a substrate on which the PES web is supported. In some cases, one or more support layers can be used to protect and / or cover the PES web, shape the PES web, improve the filtration efficiency of the filter medium, and / or increase the amount of pollutants that the filter medium can adsorb. The characteristics of the support layer will be described in further detail below.

[0048] References herein to one or more support layers should be understood to refer independently to each support layer in the filter medium (if any support layer is present at all). That is, each support layer present may independently have any or none of the properties described below. In some embodiments, two or more support layers in the filter medium may have similar compositions and / or properties. In other embodiments, each support layer in the filter medium may have different compositions and / or properties.

[0049] In some embodiments including at least one support layer, one or more support layers can be wet-laid layers. That is, in some embodiments, one or more support layers can be formed by a wet-laid process. In other embodiments, one or more support layers can be non-wet-laid layers. That is, in some embodiments, one or more support layers can be formed by a non-wet-laid process (e.g., air-laid process, carding process, melt-blown process, spinning process (e.g., spunbond process)). In some embodiments, one or more support layers can be melt-blown layers, or layers formed by melt-blown processes. In some such embodiments, the filter medium can include a PES web positioned between two support layers that are melt-blown layers.

[0050] In some embodiments of the filter medium including at least one support layer, one or more support layers can include fiber types such as synthetic fibers, glass fibers, and / or cellulose fibers. For example, one or more support layers can include synthetic fibers formed by meltblowing, melt spinning, centrifugal spinning, electrostatic spinning, wet-laid, dry-laid, or air-laid processes. In some cases, the synthetic fibers can be continuous. In some embodiments, the filter medium can include at least one support layer comprising glass fibers (e.g., microglass fibers, chopped glass fibers, or a combination thereof).

[0051] In some embodiments, the filter medium may include one or more supporting layers and one or more supporting layers may include synthetic fibers. Synthetic fibers may include any suitable type of synthetic polymer. Examples of suitable synthetic fibers include polyesters (e.g., polyethylene terephthalate, polybutylene terephthalate), polycarbonates, polyamides (e.g., various nylon polymers), polyaramids, polyimides, polyethylene, polypropylene, polyetheretherketone, polyolefins, acrylics, polyvinyl alcohol, regenerated cellulose (e.g., synthetic cellulose, such as lyocell, rayon), polyacrylonitrile, polyvinylidene fluoride (PVDF), copolymers of polyethylene and PVDF, polyethersulfone, and combinations thereof. In some embodiments, synthetic fibers are organic polymer fibers. Synthetic fibers may also include multicomponent fibers (i.e., fibers with multiple components, such as bicomponent fibers). In some embodiments, synthetic fibers may be staple fibers (e.g., wet-laid staple fibers, air-laid staple fibers). The various layers in the filter medium and the filter medium may also include a combination of more than one type of synthetic fibers. It should be understood that other types of synthetic fibers may also be used.

[0052] In some embodiments, it may be preferred that one or more support layers are capable of being bonded to the PES fiber web by one or more of compression, chemical adhesion, solvent-induced partial fiber dissolution and / or softening. For example, a support layer comprising one or more polyester fibers may be suitable for this purpose.

[0053] In some embodiments, the filter media may include at least one support layer, and one or more support layers may include fibers. In some embodiments, one or more support layers may include fibers having an average diameter of about 0.1 microns or more, about 0.2 microns or more, about 0.5 microns or more, about 1 microns or more, about 1.5 microns or more, about 2.5 microns or more, about 4 microns or more, about 7 microns or more, about 10 microns or more, about 15 microns or more, about 17 microns or more, about 20 microns or more, about 25 microns or more, about 30 microns or more, about 35 microns or more, about 40 microns or more, about 45 microns or more, about 50 microns or more, or about 55 microns or more. In some embodiments, one or more support layers may include fibers having an average diameter of less than or equal to about 60 microns, less than or equal to about 55 microns, less than or equal to about 50 microns, less than or equal to about 45 microns, less than or equal to about 40 microns, less than or equal to about 35 microns, less than or equal to about 30 microns, less than or equal to about 25 microns, less than or equal to about 20 microns, less than or equal to about 17 microns, less than or equal to about 15 microns, less than or equal to about 10 microns, less than or equal to about 7 microns, less than or equal to about 4 microns, less than or equal to about 2.5 microns, less than or equal to about 1.5 microns, less than or equal to about 1 micron, less than or equal to about 0.5 microns, or less than or equal to about 0.2 microns. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to about 0.1 microns and less than or equal to about 60 microns, greater than or equal to about 1 micron and less than or equal to about 20 microns, greater than or equal to about 1.5 microns and less than or equal to about 10 microns, greater than or equal to 4 microns and less than or equal to 60 microns, greater than or equal to 7 microns and less than or equal to 40 microns, greater than or equal to 10 microns and less than or equal to 60 microns, or greater than or equal to 17 microns and less than or equal to 35 microns). Other ranges are also possible.

[0054] In embodiments where the filter media includes at least one support layer and one or more support layers contain fibers, the average length of the fibers in the one or more support layers can be any suitable value. In some embodiments, the average length of the fibers in the one or more support layers is greater than or equal to 3 mm, greater than or equal to 6 mm, greater than or equal to 10 mm, greater than or equal to 20 mm, greater than or equal to 50 mm, greater than or equal to 100 mm, greater than or equal to 200 mm, greater than or equal to 500 mm, greater than or equal to 1000 mm, greater than or equal to 2000 mm, greater than or equal to 5000 mm, greater than or equal to 10000 mm, greater than or equal to 25400 mm, greater than or equal to 50000 mm, or greater than or equal to 100000 mm. In some embodiments, the average length of the fibers in one or more supporting layers is less than or equal to 200000mm, less than or equal to 100000mm, less than or equal to 50000mm, less than or equal to 25400mm, less than or equal to 20000mm, less than or equal to 10000mm, less than or equal to 5000mm, less than or equal to 2000mm, less than or equal to 1000mm, less than or equal to 500mm, less than or equal to 200mm, less than or equal to 100mm, less than or equal to 50mm, less than or equal to 20mm, or less than or equal to 10mm, less than or equal to 6mm. Combinations of the above ranges are also possible (e.g., greater than or equal to 3mm and less than or equal to 200000mm, greater than or equal to 3mm and less than or equal to 25400mm, or greater than or equal to 6mm and less than or equal to 25400mm). Other ranges are also possible. In some embodiments, the fibers are continuous fibers. In other embodiments, the fibers are discontinuous fibers (e.g., staple fibers).

[0055] In some embodiments where the filter media includes at least one support layer, the thickness of the one or more support layers may be greater than or equal to 0.02 mm, greater than or equal to 0.05 mm, greater than or equal to 0.1 mm, greater than or equal to 0.25 mm, greater than or equal to 0.38 mm, greater than or equal to 0.5 mm, greater than or equal to 1 mm, greater than or equal to 2 mm, or greater than or equal to 3 mm. In some embodiments, the thickness of the one or more support layers (e.g., the first layer, the third layer, the fifth layer) may be less than or equal to 5 mm, less than or equal to 3 mm, less than or equal to 2 mm, less than or equal to 1 mm, less than or equal to 0.5 mm, less than or equal to 0.38 mm, less than or equal to 0.25 mm, less than or equal to 0.1 mm, or less than or equal to 0.05 mm. Combinations of the above ranges are also possible (e.g., greater than or equal to 0.02 mm and less than or equal to 5 mm, greater than or equal to 0.25 mm and less than or equal to 2 mm, greater than or equal to 0.38 mm and less than or equal to 1 mm, greater than or equal to 0.05 mm and less than or equal to 5 mm, or greater than or equal to 0.1 mm and less than or equal to 3 mm). Other ranges are also possible. The thickness of the one or more supporting layers can be determined according to standard ISO 534:2011 at 50 kPa.

[0056] In embodiments where the filter media includes at least one support layer, the one or more support layers may have any suitable basis weight. In some embodiments, the basis weight of the one or more support layers may be greater than or equal to 10 g / m 2 , greater than or equal to 20g / m 2 , greater than or equal to 35g / m 2 , greater than or equal to 40g / m 2 , greater than or equal to 80g / m 2 , greater than or equal to 120g / m 2 , greater than or equal to 150g / m 2 , greater than or equal to 200g / m 2 , or greater than or equal to 250g / m 2 In some embodiments, the basis weight of one or more support layers may be less than or equal to 300 g / m 2 , less than or equal to 250g / m 2 , less than or equal to 200g / m 2 , less than or equal to 150g / m 2 , less than or equal to 120g / m 2 , less than or equal to 80g / m 2 , less than or equal to 40g / m 2 , less than or equal to 35g / m 2 , or less than or equal to 20g / m 2Combinations of the above ranges are also possible (e.g., greater than or equal to 10 g / m 2 And less than or equal to 300g / m 2 , greater than or equal to 10g / m 2 And less than or equal to 150g / m 2 , greater than or equal to 20g / m 2 And less than or equal to 200g / m 2 , greater than or equal to 40g / m 2 And less than or equal to 120g / m 2 , or greater than or equal to 35g / m 2 And less than or equal to 80g / m 2 ). Other ranges are also possible. The quantitative determination can be made according to standard ISO 536:2012.

[0057] As mentioned above, in some embodiments, the filter medium may include a support layer that is a meltblown layer. In some such embodiments, the filter medium may include two support layers that are meltblown layers. For example, a PES fiber web may be positioned between two meltblown layers. Suitable meltblown layers and processes are described in U.S. Publication No. 2009 / 0120048, entitled "Meltblown Filter Medium," filed on November 7, 2008, and U.S. Publication No. 2012-0152824, entitled "Fine Fiber Filter Media and Processes," filed on December 17, 2010, each of which is incorporated herein by reference as a whole for all purposes.

[0058] In some embodiments, the average diameter of the meltblown fibers in one or more meltblown layers is greater than or equal to about 0.1 microns, greater than or equal to about 0.2 microns, greater than or equal to about 0.5 microns, greater than or equal to about 1 micron, greater than or equal to about 2 microns, greater than or equal to about 5 microns, greater than or equal to about 10 microns, greater than or equal to about 20 microns, greater than or equal to about 22 microns, greater than or equal to about 24 microns, greater than or equal to about 26 microns, or greater than or equal to about 28 microns. In some cases, the average diameter of the meltblown fibers can be less than or equal to about 30 microns, less than or equal to about 28 microns, less than or equal to about 26 microns, less than or equal to about 24 microns, less than or equal to about 22 microns, less than or equal to about 20 microns, less than or equal to about 18 microns, less than or equal to about 16 microns, less than or equal to about 15 microns, less than or equal to about 14 microns, less than or equal to about 12 microns, less than or equal to about 10 microns, less than or equal to about 8 microns, less than or equal to about 6 microns, less than or equal to about 5 microns, less than or equal to about 2 microns, or less than or equal to about 1 micron. Combinations of the above ranges are also possible (e.g., greater than or equal to about 0.1 micron and less than or equal to about 30 microns, greater than or equal to about 0.2 microns and less than or equal to about 15 microns).

[0059] In some embodiments, the meltblown fibers can be continuous. For example, the average length of the meltblown fibers can be at least about 5 cm, at least about 10 cm, at least about 15 cm, at least about 20 cm, at least about 50 cm, at least about 100 cm, at least about 200 cm, at least about 500 cm, at least about 700 cm, at least about 1000 cm, at least about 1500 cm, at least about 2000 cm, at least about 2500 cm, at least about 5000 cm, at least about 10000 cm; and / or less than or equal to about 10000 cm, less than or equal to about 5000 cm, less than or equal to about 2500 cm, less than or equal to about 2000 cm, less than or equal to about 1000 cm, less than or equal to about 500 cm, or less than or equal to about 200 cm. Combinations of the above ranges are also possible (e.g., greater than or equal to about 100 cm and less than or equal to about 2500 cm). Other values ​​of average fiber length are also possible.

[0060] Meltblown fibers can be formed by any suitable type of synthetic polymer. Examples of suitable synthetic fibers include polyester (e.g., polybutylene terephthalate), polycarbonate, polyamide (e.g., various nylon polymers), polypropylene, polyolefin, polyvinylidene fluoride (PVDF), and combinations thereof. In some embodiments, synthetic fibers are organic polymer fibers. Synthetic fibers can also include multicomponent fibers (i.e., fibers with multiple components, such as bicomponent fibers). It should be understood that other types of synthetic fiber types can also be used. The meltblown layer can have any suitable thickness. For example, the thickness of the meltblown layer can be greater than or equal to 0.02mm, greater than or equal to 0.05mm, greater than or equal to 0.1mm, greater than or equal to 0.2mm, greater than or equal to 0.5mm, greater than or equal to 1mm, or greater than or equal to 2mm. In some embodiments, the thickness of the meltblown layer can be less than or equal to 5mm, less than or equal to 2mm, less than or equal to 1mm, less than or equal to 0.5mm, less than or equal to 0.2mm, less than or equal to 0.1mm, or less than or equal to 0.05mm. Combinations of the above ranges are also possible (e.g., greater than or equal to 0.02 mm and less than or equal to 5 mm, or greater than or equal to 0.1 mm and less than or equal to 1 mm). Other ranges are also possible. The thickness of the one or more supporting layers can be determined according to standard ISO 534:2011 at 50 kPa.

[0061] In certain embodiments, the PES fiber webs described herein can be in a wavy configuration. For example, the PES fiber web can be a filter layer, for example, maintained in a wavy configuration by one or more support layers to maintain the separation of the peaks and valleys of adjacent waves of the filter layer (or all). When only one coarse support layer is provided, the support layer can be arranged above (e.g., upstream) or below (e.g., downstream) the PES fiber web. Suitable coarse support layers and wavy configurations have been described, for example, in co-owned U.S. Patent No. 7,883,562 and co-owned U.S. Patent Application No. 15 / 466,809 (filed on March 22, 2017), each of which is incorporated herein by reference in its entirety.

[0062] As described above, in some embodiments, the PES fiber web can be a filter medium, or can be a layer in a filter medium. Suitable filter media include filter media designed for various applications such as the following: water filtration applications (e.g., applications suitable for filtering water and other aqueous fluids such as wastewater, aqueous fluids used in biopharmaceutical processes, aqueous fluids used in microelectronic processes, inks, foods, beverages, beer, and biological fluids (e.g., plasma and blood)), air filtration applications, oil filtration applications, and / or fuel filtration applications. Although it should be understood that any filter medium or fiber web described herein can have any of the properties described herein, it may be preferred that the filter medium or fiber web has different properties depending on the desired application.

[0063] For example, a PES fiber web used in a filter medium suitable for water filtration applications may have a relatively high basis weight, a relatively low mean flow pore size, and a relatively low air permeability compared to a PES fiber web used in a filter medium suitable for other applications. For example, the basis weight may be greater than or equal to about 0.5 g / m 2 as determined according to standard ISO 536:2012. 2 and less than or equal to about 30g / m 2 , greater than or equal to about 2g / m 2 and less than or equal to about 25g / m 2 , or greater than or equal to about 3 g / m 2 and less than or equal to about 15g / m 2 The mean flow pore size may be greater than or equal to about 0.05 microns and less than or equal to about 4 microns, or greater than or equal to about 0.2 microns and less than or equal to about 2 microns, as measured according to ASTM F316 (2003). The air permeability may be greater than or equal to about 0.2 CFM and less than or equal to about 5 CFM, or greater than or equal to about 0.3 CFM and less than or equal to about 1.7 CFM, as measured at a pressure of 0.5 inches of water according to ASTM D737-04 (2016).

[0064] As another example, a PES web for filter media suitable for air filtration applications can have a relatively low basis weight, a relatively high mean flow pore size, and a relatively high air permeability compared to a PES web for filter media suitable for other applications. The basis weight can be greater than or equal to about 0.05 g / m 2 and less than or equal to about 1g / m 2 , or greater than or equal to about 0.1 g / m 2 and less than or equal to about 0.5 g / m 2The mean flow pore size may be greater than or equal to about 2 microns and less than or equal to about 20 microns, or greater than or equal to about 8 microns and less than or equal to about 10 microns, as measured according to ASTM F316 (2003). The air permeability may be greater than or equal to about 5 CFM and less than or equal to about 40 CFM, or greater than or equal to about 10 CFM and less than or equal to about 30 CFM, as measured at a pressure of 0.5 inches of water according to ASTM D737-04 (2016).

[0065] As a third example, a PES fiber web used in filter media suitable for fuel filtration applications can have a medium basis weight, a medium mean flow pore size, and a relatively high air permeability compared to a PES fiber web used in filter media suitable for other applications. The basis weight can be greater than or equal to about 0.1 g / m 2 and less than or equal to about 3g / m 2 , or greater than or equal to about 0.2 g / m 2 and less than or equal to about 1.5 g / m 2 The mean flow pore size may be greater than or equal to about 1 micron and less than or equal to about 20 microns, or greater than or equal to about 2 microns and less than or equal to about 20 microns, as measured according to ASTM F316 (2003). The air permeability may be greater than or equal to about 5 CFM and less than or equal to about 40 CFM, or greater than or equal to about 10 CFM and less than or equal to about 30 CFM, as measured according to ASTM D737-04 (2016) at a pressure of 0.5 inches of water.

[0066] In embodiments where the PES fiber web can be a component of the filter media, the filter media as a whole (including the fiber web and any other layers present) can have any suitable basis weight. In some embodiments, the basis weight of the filter media as a whole can be greater than or equal to about 15 g / m 2 , greater than or equal to about 25g / m 2 , greater than or equal to about 30g / m 2 , greater than or equal to about 50g / m 2 , greater than or equal to about 75g / m 2 , greater than or equal to about 100g / m 2 , greater than or equal to about 125g / m 2 , greater than or equal to about 130g / m 2 , greater than or equal to about 150g / m 2 , greater than or equal to about 175g / m 2 , greater than or equal to about 200g / m 2 , greater than or equal to about 225g / m 2 , greater than or equal to about 250g / m2 , or greater than or equal to about 300 g / m 2 In some embodiments, the filter media as a whole may have a basis weight of less than or equal to about 300 g / m 2 , less than or equal to about 275 g / m 2 , less than or equal to about 250g / m 2 , less than or equal to about 225 g / m 2 , less than or equal to about 200 g / m 2 , less than or equal to about 175g / m 2 , less than or equal to about 150 g / m 2 , less than or equal to about 130 g / m 2 , less than or equal to about 125g / m 2 , less than or equal to about 100 g / m 2 , less than or equal to about 75 g / m 2 , less than or equal to about 50g / m 2 , less than or equal to about 30g / m 2 , or less than or equal to about 25 g / m 2 Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to about 15 g / m 2 and less than or equal to about 300 g / m 2 , greater than or equal to about 15g / m 2 and less than or equal to about 130 g / m 2 , greater than or equal to about 30g / m 2 and less than or equal to about 125 g / m 2 , greater than or equal to about 25g / m 2 and less than or equal to about 100 g / m 2 , or greater than or equal to about 50 g / m 2 and less than or equal to about 125 g / m 2 ). Other ranges are also possible. The quantitative determination can be made according to standard ISO 536:2012.

[0067] In some embodiments, the PES fiber web is a layer of the following filter medium: the filter medium has an air permeability of greater than or equal to about 0.5 CFM, greater than or equal to about 1 CFM, greater than or equal to about 2 CFM, greater than or equal to about 5 CFM, greater than or equal to about 10 CFM, or greater than or equal to about 20 CFM under a pressure of 10 inches of water. In some embodiments, the filter medium has an air permeability of less than or equal to about 30 CFM, less than or equal to about 20 CFM, less than or equal to about 10 CFM, less than or equal to about 5 CFM, less than or equal to about 2 CFM, or less than or equal to about 1 CFM under a pressure of 10 inches of water. Combinations of the above ranges are also possible (e.g., greater than or equal to about 0.5 CFM and less than or equal to about 30 CFM, or greater than or equal to about 0.5 CFM and less than or equal to about 20 CFM). Other ranges are also possible. Air permeability can be measured by ASTM D737-04 (2016) under a pressure of 10 inches of water.

[0068] In some embodiments, the PES fiber web is a layer of a filter medium having a water permeability greater than or equal to 0.1 mL / (min*cm 2 *psi), greater than or equal to 0.2mL / (minute*cm 2 *psi), greater than or equal to 0.5mL / (minute*cm 2 *psi), greater than or equal to 1mL / (minute*cm 2 *psi), greater than or equal to 2mL / (minute*cm 2 *psi), or greater than or equal to 5mL / (minute*cm 2 *psi). The water permeability of the filter medium can be less than or equal to 10mL / (min*cm 2 *psi), less than or equal to 5mL / (minute*cm 2 *psi), less than or equal to 2mL / (minute*cm 2 *psi), less than or equal to 1mL / (minute*cm 2 *psi), less than or equal to 0.5mL / (minute*cm 2 *psi), or less than or equal to 0.2mL / (minute*cm 2 *psi). Combinations of the above ranges are also possible (e.g., greater than or equal to 0.1 mL / (min*cm 2 *psi) and less than or equal to 10mL / (minute*cm 2 *psi)). Other ranges are possible. The water permeability can be determined by placing a 4.8 cm2 thick 2The filter media web is exposed to deionized water and the water flowing through the filter media is collected for measurement. The time required for 1000 mL of water to flow through the fiber web is determined, and then the water permeability is determined using the following formula:

[0069]

[0070] Prior to exposing the fiber web to deionized water, the fiber web was first immersed in isopropyl alcohol and then in deionized water.

[0071] The fiber web described herein can be manufactured using any suitable technology or combination of technologies. In some embodiments, the PES fiber web can be manufactured by one or more of an electrospinning process, a force spinning process, and an electrostatic blowing (electroblowing) process. In some embodiments, an electrospinning process is used. As an example, the material (e.g., PES) that will form the fiber can be dissolved in a composition comprising at least one or more poor solvents and one or more good solvents, and then electrospun to a suitable carrier. The good solvent can be distinguished from the poor solvent by turbidity titration measurement, which can be done by dissolving the polymer in the target solvent at 10% by weight, and then slowly adding water to the solution in a dropwise manner at 25°C. After adding a certain amount of water, the solution will become turbid or will pass through the turbidity point. If water constitutes less than 7% by weight of the composition at the turbidity point, the solvent is a poor solvent. If water constitutes more than or equal to 7% by weight of the composition at the turbidity point, the solvent is a good solvent. Non-limiting examples of poor solvents for PES include dimethylformamide (DMF) and dimethyl sulfoxide (DMSO). Non-limiting examples of good solvents for PES include dimethylacetamide (DMAc), N-methylpyrrolidone, and tetramethylurea. In some embodiments, the solution may also include other components, such as conductivity enhancers (e.g., organic salts and / or surfactants, such as tetraethylammonium bromide, tetraoctylammonium chloride, etc.). After the electrospinning process, the electrospun fiber web may be optionally separated from the support.

[0072] When the fiber web described herein is manufactured using an electrospinning process as described above, the composition of the solution containing a poor solvent and a good solvent can be selected as desired. In some embodiments, the poor solvent can account for greater than or equal to about 50% by weight of the total solvent present (the total solvent present includes the good solvent and the poor solvent), greater than or equal to about 55% by weight of the total solvent present, greater than or equal to about 60% by weight of the total solvent present, greater than or equal to about 65% by weight of the total solvent present, greater than or equal to about 70% by weight of the total solvent present, or greater than or equal to about 75% by weight of the total solvent present. In some embodiments, the poor solvent can account for less than or equal to about 80% by weight of the total solvent present, less than or equal to about 75% by weight of the total solvent present, less than or equal to about 70% by weight of the total solvent present, less than or equal to about 65% by weight of the total solvent present, less than or equal to about 60% by weight of the total solvent present, or less than or equal to about 55% by weight of the total solvent present. Combinations of the above-referenced ranges are also possible (eg, greater than or equal to about 50 wt % and less than or equal to about 80 wt %, or greater than or equal to about 60 wt % and less than or equal to about 75 wt %). Other ranges are also possible.

[0073] When the fiber web described herein comprises PES and is manufactured using an electrospinning process as described above, the PES can be dissolved in a solvent (e.g., a poor solvent, a good solvent) at any suitable weight %. In some embodiments, the PES can account for, for example, 10% to 40% by weight of the resulting solution, 20% to 40% by weight of the resulting solution, or 30% to 40% by weight of the resulting solution. Other ranges are also possible.

[0074] In some embodiments of the fiber web described herein manufactured using an electrostatic spinning process as described above, the solution for electrostatic spinning may include one or more wetting agents. These wetting agents may exist in any suitable form (e.g., dissolve, suspend, partially dissolve or suspend). The non-limiting examples of suitable wetting agents include poly (ethylene oxide), poly (ethylene oxide) copolymers, poly (vinyl pyrrolidone), poly (vinyl pyrrolidone) copolymers, poly (propylene oxide) and poly (vinyl alcohol). When present, the wetting agent may account for a solution greater than or equal to about 1% by weight, a solution greater than or equal to about 2% by weight, a solution greater than or equal to about 5% by weight, a solution greater than or equal to about 10% by weight, or a solution greater than or equal to about 15% by weight. In some embodiments, the wetting agent accounts for a solution less than or equal to about 20% by weight, a solution less than or equal to about 15% by weight, a solution less than or equal to about 10% by weight, a solution less than or equal to about 5% by weight, or a solution less than or equal to about 2% by weight. Combinations of the above-referenced ranges are also possible (eg, greater than or equal to about 1 wt % of the solution and less than or equal to about 20 wt % of the solution). Other ranges are also possible.

[0075] When the fiber web is manufactured using an electrospinning process as described above, the ambient humidity can be selected as needed. In some embodiments, the ambient humidity is greater than or equal to about 10% RH, greater than or equal to about 15% RH, greater than or equal to about 20% RH, greater than or equal to about 25% RH, greater than or equal to about 30% RH, greater than or equal to about 35% RH, greater than or equal to about 40% RH, or greater than or equal to about 45% RH. In some embodiments, the ambient humidity is less than or equal to about 50% RH, less than or equal to about 45% RH, less than or equal to about 40% RH, less than or equal to about 35% RH, less than or equal to about 30% RH, less than or equal to about 25% RH, less than or equal to about 20% RH, or less than or equal to about 15% RH. Combinations of the above ranges are also possible (e.g., greater than or equal to about 10% RH and less than or equal to about 50% RH, or greater than or equal to about 25% RH and less than or equal to about 35% RH). Other ranges are also possible.

[0076] In some embodiments, the formation of the fiber web (e.g., by an electrospinning process) can be followed by one or more optional surface treatments. For example, chemical vapor deposition (CVD) (e.g., plasma enhanced CVD, audio and / or radio frequency plasma enhanced CVD, microwave discharge CVD, atmospheric plasma discharge CVD, DC plasma discharge CVD) can be used to functionalize the fiber web surface. As an example, the fiber web can be exposed to oxygen plasma. The treatment can cause surface oxidation of the fiber web, can produce functional groups such as alcohols and carboxylic acids on the fiber web surface, and / or can increase the hydrophilicity of the fiber web. As another example, CVD can be used to deposit one or more monomers (e.g., acrylic monomers such as hydroxyethyl methacrylate; fluorinated monomers such as hexafluorobutyric acid, CF4, CHF3, C2F6, C3F8, C4F8, C2F4, C3F6, etc.) onto the fiber web. In some embodiments, the monomer can be deposited in the presence of a carrier gas (e.g., an inert gas such as helium or argon). Depositing these monomers can affect the hydrophobicity of the web surface (e.g., acrylic monomers can make the surface more hydrophilic, fluorinated monomers can make the web surface more hydrophobic). In some embodiments, the CVD treatment can include exposing the web to ammonia, optionally accompanied by one or more inert gases (e.g., helium, argon). Other surface treatments (e.g., other CVD treatments) are also possible.

[0077] In some embodiments, the PES fiber mesh may include a coating suitable for biofiltration applications. In some embodiments, the coated fiber mesh may be suitable for use as an absorbent membrane filter. The coating may be able to interact with one or more proteins or biomolecules and / or may capture one or more proteins or biomolecules. In some embodiments, the coating may conformally coat at least a portion of the fibers in the mesh and / or may not block a significant portion of the holes in the mesh. Non-limiting examples of suitable coatings for biofiltration applications include polymers such as cross-linked poly (ethyleneimine), hydrogels, ligands, positively charged molecules such as positively charged polymers (e.g., polymers comprising one or more quaternized groups (e.g., quaternized dialkylamine groups)) and negatively charged molecules such as negatively charged polymers (e.g., polymers comprising one or more sulfonate groups (e.g., acrylamide sulfonic acid groups), polymers comprising one or more acrylate groups (e.g., hydroxyalkyl acrylate groups), polymers comprising one or more carboxylate groups). The coating may be applied using chemical vapor deposition as described above, or may be applied by applying a solution comprising a coating to the fiber mesh. In some embodiments, a monomer may be applied to the fiber web (eg, by CVD, in solution) that is polymerizable on the surface of at least some of the fibers within the fiber web.

[0078] When present, the coating disposed on the web can have any suitable thickness. The thickness of the coating can be greater than or equal to about 50 nm, greater than or equal to about 100 nm, greater than or equal to about 150 nm, greater than or equal to about 200 nm, greater than or equal to about 250 nm, greater than or equal to about 300 nm, greater than or equal to about 350 nm, or greater than or equal to about 400 nm, greater than or equal to about 450 nm. The thickness of the coating can be less than or equal to about 500 nm, less than or equal to about 450 nm, less than or equal to about 400 nm, less than or equal to about 350 nm, less than or equal to about 300 nm, less than or equal to about 250 nm, less than or equal to about 200 nm, less than or equal to about 150 nm, or less than or equal to about 100 nm. Combinations of the above ranges are also possible (e.g., greater than or equal to about 50 nm and less than or equal to about 500 nm). Other ranges are also possible.

[0079] As described above, in some embodiments, the filter media can include a PES fiber web and can include one or more layers other than the fiber web. In some cases, the filter media can be formed by stacking two or more layers. The stacked layers can optionally be adhered to each other using any suitable method (e.g., lamination and calendaring).

[0080] Lamination can involve, for example, compressing two or more layers together at a specific pressure and temperature using a flat-bed laminator or any other suitable device for a certain dwell time (i.e., the amount of time spent under pressure and heat). For example, the pressure can be about 10 psi to about 150 psi (e.g., about 30 psi to about 90 psi, about 60 psi to about 120 psi, about 30 psi to 60 psi, or about 120 psi to about 90 psi); the temperature can be about 75°F. to about 400°F. (e.g., about 75°F. to about 300°F., about 200°F. to about 350°F., or about 275°F. to about 390°F.); and the dwell time can be about 1 second to about 60 seconds (e.g., about 1 second to about 30 seconds, about 10 seconds to about 25 seconds, or about 20 seconds to about 40 seconds). Other ranges of pressure, temperature, and dwell time are also possible.

[0081] Calendering can involve, for example, using a calendering roller to compress two or more layers together at a specific linear pressure, temperature, and line speed. For example, the linear pressure can be about 50 pounds per inch to about 400 pounds per inch (e.g., about 200 pounds per inch to about 400 pounds per inch, about 50 pounds per inch to about 200 pounds per inch, or about 75 pounds per inch to about 300 pounds per inch); the temperature can be 75°F. to about 400°F. (e.g., about 75°F. to about 300°F., about 200°F. to about 350°F., or about 275°F. to about 390°F.); and the line speed can be about 5 feet per minute to about 100 feet per minute (e.g., about 5 feet per minute to about 80 feet per minute, about 10 feet per minute to about 50 feet per minute, about 15 feet per minute to about 100 feet per minute, or about 20 feet per minute to about 90 feet per minute). Other ranges of linear pressure, temperature, and line speed are also possible.

[0082] Example 1

[0083] This example compares a filter media comprising a PES fiber web to a commercially available filter media comprising a PES membrane (non-fiber based).

[0084] The PES fiber web was manufactured by an electrospinning process. Two samples were formed by laminating a PES fiber web between two meltblown layers.

[0085] Table 1 below shows the measured surface area, filtration efficiency for 0.2 micron diameter polystyrene spheres, water permeability, BSA throughput, log reduction value and quantitation for each of the filter media (Samples 1 and 2) comprising a PES fiber web and three commercially available PES membranes (Commercial Samples 1 to 3). The BSA throughput was measured by dissolving 50 mg of BSA in 1 liter of phosphate buffered saline and then passing the BSA solution through the filter media at a pressure of 6 psi.

[0086] Table 1

[0087]

[0088] The filter media including the PES fiber web had a much higher measured surface area, comparable or better filtration efficiency, and much better water permeability than the commercially available samples. The filter media including the PES fiber web also showed high BSA throughput, indicating no clogging during use. Sample 2 also showed a high log reduction value.

[0089] Example 2

[0090] This example compares PES webs having different relative surface areas.

[0091] PES fiber webs with different levels of relative surface area were made by an electrospinning process and their filtration efficiency for 0.2 micron diameter polystyrene spheres was measured. Table 2 shows the fiber diameter, quantitative, maximum pore size to mean flow pore size ratio, water permeability, bead density, relative surface area, and filtration efficiency for 0.2 micron diameter spheres for five of these samples. The quantitative, water permeability, bead density, and filtration efficiency for 0.2 micron diameter polystyrene spheres were measured as described above. The relative surface area was determined by utilizing the linear correlation of the measured relative area to the bead area measured using SEM. As shown in Table 2, the low per mm 2 The number of beads and a low maximum pore size to mean flow pore size ratio are also related to filtration efficiency.

[0092] Table 2

[0093]

[0094] like Figure 1 As shown in Table 2, fiber webs having higher levels of relative surface area have higher filtration efficiencies for 0.2 micron diameter polystyrene spheres.

[0095] Example 3

[0096] This example shows the effect of oxygen plasma treatment on the water permeability of a PES fiber web.

[0097] Two PES webs (Samples 3 and 4) produced by the electrospinning process were further treated with oxygen plasma using a CVD process. The water permeability of the PES webs was measured before and after the process and is shown in Table 3 below.

[0098] Table 3

[0099]

[0100] For both PES webs, oxygen plasma treatment increased the water permeability by at least 50%.

[0101] Although multiple embodiments of the present invention have been described and illustrated herein, a person of ordinary skill in the art will readily recognize a variety of other means and / or structures for performing the functions described herein and / or obtaining the results and / or one or more advantages described herein, and each such variation and / or modification is considered to be within the scope of the present invention. More generally, it will be readily appreciated by those skilled in the art that all parameters, dimensions, materials, and configurations described herein are intended to be exemplary, and that the actual parameters, dimensions, materials, and / or configurations will depend on one or more specific applications to which the teachings of the present invention are applied. Those skilled in the art will recognize or be able to determine many equivalents of the specific embodiments of the invention described herein using only routine experiments. Therefore, it should be understood that the foregoing embodiments are shown only as examples, and within the scope of the appended claims and their equivalents, the present invention may be practiced in other ways than those specifically described and claimed. The present invention relates to each individual feature, system, article, material, kit, and / or method described herein. In addition, if two or more such features, systems, articles, materials, kits, and / or methods are not mutually inconsistent, any combination of such features, systems, articles, materials, kits, and / or methods is included within the scope of the present invention.

[0102] All definitions, as defined and used herein, should be understood to control over dictionary definitions, definitions in documents incorporated by reference, and / or ordinary meanings of the defined terms.

[0103] Unless explicitly indicated to the contrary, as used herein in the specification and claims, the term "at least one" should be understood to mean "at least one".

[0104] As used herein in the specification and claims, the phrase "and / or" should be understood to mean "either or both" of the elements so united, i.e., elements that exist together in some cases and separately in other cases. Multiple elements listed with "and / or" should be understood in the same way, i.e., "one or more" of the elements so united. In addition to the elements specifically indicated by the "and / or" clause, other elements may optionally be present, whether related or unrelated to those specifically indicated. Thus, as a non-limiting example, when used in conjunction with an open language such as "comprising", a reference to "A and / or B" may refer to only A (optionally including elements other than B) in one embodiment; to only B (optionally including elements other than A) in another embodiment; to both A and B (optionally including other elements) in yet another embodiment; and so on.

[0105] As used herein in the specification and claims, "or" shall be understood to have the same meaning as "and / or" as defined above. For example, when separating items in a list, "or" or "and / or" shall be understood to include, i.e., include at least one of a plurality of elements or a list of elements, but also include more than one of them, and optionally include additional unlisted items. Only explicitly indicating the opposite term, such as "only one" or "exactly one", or when used in a claim, "consisting of..." means including exactly one element of a plurality of elements or a list of elements. Generally, when preceded by an exclusive term (e.g., "either", "one", "only one" or "exactly one"), the term "or" as used herein shall only be understood to represent an exclusive alternative (i.e., "one or the other, but not both"). "Substantially consisting of..." when used in a claim shall have its ordinary meaning used in the field of patent law.

[0106] As used herein in the specification and claims, the phrase "at least one" when referring to a list of one or more elements should be understood to mean at least one element selected from any one or more elements in the list of elements, but does not necessarily include at least one of each element specifically listed in the list of elements, nor does it exclude any combination of elements in the list of elements. This definition also allows that elements other than the elements specifically indicated in the list of elements referred to by the phrase "at least one" may optionally be present, whether related or unrelated to those elements specifically indicated. Thus, as a non-limiting example, "at least one of A and B" (or equivalently, "at least one of A or B", or equivalently, "at least one of A and / or B") may refer to at least one A, optionally including more than one A, but no B (and optionally including elements other than B) in one embodiment; may refer to at least one B, optionally including more than one B, but no A (and optionally including elements other than A) in another embodiment; may refer to at least one A, optionally including more than one A, and at least one B, optionally including more than one B (and optionally including other elements) in yet another embodiment; and so on.

[0107] It should also be understood that in any method claimed herein that includes more than one step or action, the order of the method steps or actions is not necessarily limited to the order of the method steps or actions listed unless explicitly indicated to the contrary.

[0108] In the claims and the foregoing specification, all transitional phrases such as "comprising," "including," "carrying," "having," "containing," "involving," "having," "comprising," etc. shall be understood as open-ended, i.e., meaning including but not limited to. Only the transitional phrases "consisting of" and "consisting essentially of" shall be closed or semi-closed transitional phrases, respectively, as set forth in Section 2111.03 of the U.S. Patent Office Manual of Patent Examining Procedures.

[0109] The present invention also provides the following technical solutions:

[0110] Note 1. A fiber web comprising:

[0111] Polyethersulfone fibers having an average diameter less than or equal to 250 nm,

[0112] The relative surface area of ​​the fiber web is greater than or equal to 80%.

[0113] Note 2. A fiber web comprising:

[0114] Polyethersulfone fibers having an average diameter less than or equal to 250 nm,

[0115] wherein the relative surface area of ​​the fiber web is greater than or equal to 75%, and wherein the measured surface area of ​​the fiber web is greater than or equal to 25 m 2 / g.

[0116] Note 3. The fiber web according to any of the preceding notes, wherein the fiber web is an electrospun fiber web.

[0117] Note 4. The fiber web according to any of the preceding notes, wherein the fiber web has a relative surface area greater than or equal to about 90%.

[0118] Note 5. The fiber web according to any of the preceding notes, wherein the fiber web has a relative surface area greater than or equal to about 95%.

[0119] Note 6. The fiber web according to any of the preceding notes, wherein the fiber web has a measured surface area greater than or equal to about 55 m 2 / g.

[0120] Note 7. The fiber web according to any of the preceding notes, wherein the fiber web has a measured surface area greater than or equal to about 95 m 2 / g.

[0121] Note 8. The fiber web of any preceding note, wherein the polyethersulfone fibers have an average diameter greater than or equal to about 20 nanometers.

[0122] Note 9. The fiber web of any preceding note, wherein the fiber web has a relative surface area of ​​less than or equal to about 100%.

[0123] Note 10. The fiber web according to any of the preceding notes, wherein the fiber web has a measured surface area of ​​less than or equal to about 200 m 2 / g.

[0124] Note 11. The fiber web according to any of the preceding notes, wherein at least 75% by weight of the fiber web is polyethersulfone.

[0125] Note 12. The fiber web of any preceding note, wherein the fiber web has a filtration efficiency for 4 micron diameter particles greater than or equal to about 80% and less than or equal to about 100%.

[0126] Note 13. The fiber web of any preceding note, wherein the fiber web has a filtration efficiency for 0.2 micron diameter polystyrene spheres greater than or equal to about 75% and less than or equal to about 100%.

[0127] Note 14. The fiber web of any preceding note, wherein the fiber web has a filtration efficiency for 0.3 micron diameter DOP particles greater than or equal to 1% and less than or equal to about 40%.

[0128] Note 15. The filter media of any preceding note, wherein the filter media has a Log Reduction value greater than or equal to about 3 and less than or equal to about 8.81.

[0129] Note 16. The fiber web of any preceding note, wherein the polyethersulfone fibers of the fiber web have a modified surface.

[0130] Note 17. The fiber web of Note 14, wherein the surface is modified by chemical vapor deposition.

[0131] Note 18. A filter medium comprising a fiber web according to any of the preceding notes.

[0132] Note 19. The filter medium of note 18, further comprising one or more layers.

[0133] Note 20. The filter medium of any of Notes 18 to 19 further comprising a support layer.

[0134] Note 21. The filter medium of any of Notes 18 to 20, further comprising a meltblown layer.

[0135] Note 22. The filter medium of any of Notes 18 to 22, wherein the PES fiber web is between two meltblown layers.

[0136] Note 23. The filter medium of any preceding note, wherein the PES fiber web is in a corrugated configuration.

Claims

1. A fiber web comprising: Polyethersulfone fibers having an average diameter less than or equal to 250 nm, The relative surface area of ​​the fiber web is greater than or equal to 80%.

2. A fiber web comprising: Polyethersulfone fibers having an average diameter less than or equal to 250 nm, wherein the relative surface area of ​​the fiber web is greater than or equal to 75%, and wherein the measured surface area of ​​the fiber web is greater than or equal to 25 m 2 / g.

3. The fiber web according to any preceding claim, wherein the fiber web is an electrospun fiber web.

4. The fiber web of any preceding claim, wherein the fiber web has a relative surface area greater than or equal to about 90%.

5. The fiber web of any preceding claim, wherein the fiber web has a measured surface area greater than or equal to about 55 m 2 / g.

6. The fiber web of any preceding claim, wherein the polyethersulfone fibers have an average diameter greater than or equal to about 20 nanometers.

7. The fiber web of any preceding claim, wherein the fiber web has a relative surface area of ​​less than or equal to about 100%.

8. The fiber web of any preceding claim, wherein at least 75% by weight of the fiber web is polyethersulfone.

9. A filter medium comprising a fibre web according to any preceding claim.

10. The filter media of claim 9, further comprising one or more layers.