Multicolor jade quality glaze with mutton fat jade effect, glazed tile and preparation method thereof

Abstract

The invention discloses a multi-color jade quality glaze with sheep fat jade effect, glazed tiles and a preparation method thereof, and belongs to the technical field of ceramic production processes. The multi-color jade quality glaze with sheep fat jade effect comprises a multi-color jade quality base glaze, a jade quality transparent glaze and a jade quality dry particle glaze. The multi-color jade quality base glaze comprises a multi-color jade quality base glaze and a multi-color jade quality colored base glaze. The jade quality dry particle glaze comprises a jade quality dry particle, a multi-color dry particle and an ice crystal dry particle. The invention adjusts and optimizes the formula of the multi-color jade quality glaze, adopts the multi-color jade quality base glaze in combination with the jade quality transparent glaze, optimizes the jade quality dry particle glaze (including the jade quality dry particle, the multi-color dry particle and the ice crystal dry particle), and obtains the ceramic tile product with soft texture, distinct levels and strong jade quality, i.e. the multi-color jade quality glazed tile with sheep fat jade effect.

Description

TECHNICAL FIELD

[0001] The application belongs to the technical field of ceramic production process, and particularly relates to a multi-color jade quality glaze with sheep fat jade effect, glazed brick and a preparation method thereof. BACKGROUND

[0002] With the continuous development of the building and decoration industry, ceramic tiles as important decorative materials have increasingly diversified market demand. Among them, imitation jade ceramic tiles are favored by consumers due to their unique texture and beautiful appearance. However, the existing imitation jade ceramic tiles on the market generally have some problems, such as unrealistic glaze texture, not soft enough texture, unclear level, and not strong three-dimensional effect. At the same time, the design pattern is usually presented in the form of 2D plane, combined with the common ink dot defects of inkjet printing technology, which makes it difficult for these products to well represent the three-dimensional texture of stone, especially in jade or marble designs with strong level. These problems not only affect the aesthetic degree and texture of the product, but also limit the application of imitation jade ceramic tiles in high-end decoration field. SUMMARY

[0003] In view of the problems in the prior art, the application provides a multi-color jade quality glaze with sheep fat jade effect, glazed brick and a preparation method thereof. The application adjusts and optimizes the multi-color jade quality glaze formula, uses multi-color jade quality base glaze in combination with jade quality transparent glaze, optimizes jade quality dry particle glaze (including jade quality dry particle, multi-color dry particle and ice crystal dry particle), improves the gluing glaze application process, and combines with inkjet technology to obtain a digital glaze ceramic tile product with soft texture, clear level and strong jade three-dimensional effect: multi-color jade quality glazed brick with sheep fat jade effect.

[0004] To solve the above problems, the application is realized by the following technical scheme:

[0005] The first application purpose of the application is:

[0006] A multi-color jade quality glaze with sheep fat jade effect is provided, which comprises: multi-color jade quality base glaze, jade quality transparent glaze and jade quality dry particle glaze.

[0007] The multi-color jade quality base glaze comprises multi-color jade quality colorless base glaze and multi-color jade quality colored base glaze.

[0008] The multi-color jade quality colorless base glaze is mainly white.

[0009] The multi-color jade quality colored base glaze comprises one or more mixed colors of yellow, blue, green, red and black, and the base glaze ratio can be adjusted to obtain the required jade quality feeling such as white jade quality feeling, yellow jade quality feeling, blue jade quality feeling, green jade quality feeling, red jade quality feeling and black jade quality feeling.

[0010] The multi-color jade quality base glaze ratio is determined as follows:

[0011] The base glaze and the colored base glaze are reasonably and flexibly selected according to the layout requirements, and part of the matching effect is shown in Tables 1-3.

[0012] Table 1 Analysis and research on matching of base glaze and colored base glaze in multi-color jade base glaze (mass percentage)

[0013]

[0014] Table 2 Analysis and research on matching of multi-color jade base glaze and jade transparent glaze (mass percentage)

[0015]

[0016] Table 3 Analysis and research on matching of multi-color jade base glaze, jade transparent glaze and jade dry particle glaze (mass percentage)

[0017]

[0018] The multi-color jade base glaze comprises the following mass percentage components:

[0019] The multi-color jade base glaze comprises the following mass percentage components:

[0020] The multi-color jade base glaze comprises the following mass percentage components:

[0021] The jade transparent glaze comprises the following mass percentage components:

[0022] The jade transparent glaze comprises the following mass percentage components:

[0023] The jade transparent glaze comprises the following mass percentage components:

[0024] The jade transparent glaze comprises the following mass percentage components:

[0025] 8# stone powder 30~35%, 9# stone powder 17~22%, ball clay 5~8%, white sand 15~19%, talc 3~6%, white clay 11~15%, wollastonite 3~5%, bentonite 2~4%, calcined kaolin 3~5%, the sum of all components is 100%; additional water glass 0.6%, sodium tripolyphosphate 0.1%, and appropriate amount of water;

[0026] The multi-color dry particles include: jade dry particle glaze slurry prepared from the jade dry particle and glaze color slurry, and the jade dry particle glaze slurry and the glaze color slurry are appropriately matched according to color requirements.

[0027] The preferred mass ratio (uniform mixing) of the jade dry particle glaze slurry and various glaze color slurries is:

[0028] Jade dry particle glaze slurry: zirconium silicate slurry = 100:3~5;

[0029] Jade dry particle glaze slurry: zirconium silicate slurry = 100:6~13;

[0030] Jade dry particle glaze slurry: vanadium zirconium blue + praseodymium yellow color slurry = 100:1~3;

[0031] Jade dry particle glaze slurry: praseodymium yellow color slurry = 100:1~3;

[0032] Jade dry particle glaze slurry: zirconium iron red color slurry = 100:1~3;

[0033] Jade dry particle glaze slurry: cobalt black color slurry = 100:1~3;

[0034] According to the requirements of the layout, one or more, light or dark, and other ways of multi-color dry particles can be configured, so that multi-color, multi-level flexible and flexible color effects are obtained.

[0035] The fineness of the multi-color dry particles is 20~60 mesh;

[0036] The ice crystal dry particles are zirconite fine particles, and the fineness is 60~200 mesh.

[0037] The further optimization of the multi-color jade glaze with mutton fat jade effect of the application is:

[0038] The glaze color slurry in the multi-color jade colored base glaze is prepared by mixing one or more of the following color materials: praseodymium yellow, vanadium zirconium blue, fruit green, zirconium iron red, and cobalt black;

[0039] The glaze color slurry in the multi-color dry particles is prepared by mixing one or more of the following color materials: zirconium silicate, vanadium zirconium blue, praseodymium yellow, zirconium iron red, and cobalt black.

[0040] The second invention purpose of the application is:

[0041] Provided is a preparation method of the multicolor jade glaze with mutton fat jade effect, wherein the multicolor jade base glaze comprises the following preparation method:

[0042] The multicolor jade base glaze is prepared by mixing the multicolor jade base glaze and the multicolor jade colored base glaze according to requirements, and is ready for use.

[0043] The multicolor jade base glaze comprises the following preparation method:

[0044] The corresponding raw material components are weighed according to the multicolor jade base glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the multicolor jade base glaze, which is ready for use.

[0045] The multicolor jade colored base glaze comprises the following preparation method:

[0046] The multicolor jade base glaze and the glaze colorant paste are mixed according to the proportion, to prepare the multicolor jade colored base glaze, which is ready for use.

[0047] The jade light-transmitting glaze comprises the following preparation method:

[0048] The corresponding raw material components are weighed according to the jade light-transmitting glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the jade light-transmitting glaze, which is ready for use.

[0049] The jade dry particle glaze comprises the following preparation method:

[0050] The jade dry particle, the multicolor dry particle, and the ice crystal dry particle are combined according to the proportion, to prepare the jade dry particle glaze, which is ready for use.

[0051] The preparation method of the multicolor jade glaze with mutton fat jade effect is further optimized as follows:

[0052] The jade dry particle comprises the following preparation method:

[0053] The corresponding raw material components are weighed according to the jade dry particle formula, ball milling, slurry, and 250 mesh screen, to prepare the jade dry particle slurry, which is ready for use.

[0054] The prepared jade dry particle slurry is mixed uniformly, and is placed in a high-temperature smelting furnace at 1250°C for melting, and is kept for 3-5 hours, and then is slowly cooled to room temperature at a cooling rate of 6-20°C / hour, so that crystals are precipitated, and are broken and screened to 20-120 mesh dry particles, to prepare the jade dry particle.

[0055] The multicolor dry particle comprises the following preparation method:

[0056] The jade dry particle glaze prepared from the jade dry particle and the glaze colorant slurry are weighed according to the multi-color dry particle formula, and are mixed uniformly according to the color requirement to prepare the mixed slurry of the multi-color dry particle, which is ready for use.

[0057] The mixed slurry of the multi-color dry particle prepared above is placed in a high-temperature melting furnace and is melted at 1255 DEG C for 3-5 hours, and then is slowly cooled to room temperature at a cooling rate of 6-20 DEG C / hour, so that crystals are precipitated, the dry particles of 20-60 mesh are broken and sieved, and the multi-color dry particle is prepared.

[0058] The preparation method of the multi-color jade glaze with mutton fat jade effect of the present application is further optimized as follows:

[0059] The glaze slurry of the multi-color jade base glaze has a ball-milling fineness of 325 mesh and a water content of 28-30%.

[0060] The glaze colorant slurry of the multi-color jade base glaze has a ball-milling fineness of 325 mesh and a water content of 20-30%.

[0061] The glaze slurry of the jade transparent glaze has a ball-milling fineness of 325 mesh and a water content of 28-30%.

[0062] The glaze slurry of the jade dry particle has a ball-milling fineness of 250 mesh and a water content of 30-34%.

[0063] The glaze colorant slurry of the multi-color dry particle has a ball-milling fineness of 250 mesh and a water content of 30-34%.

[0064] The third object of the present application is to provide a preparation method of multi-color jade glazed tile with mutton fat jade effect.

[0065] The preparation method of the multi-color jade glazed tile with mutton fat jade effect of the present application adopts the multi-color jade glaze with mutton fat jade effect described above, and comprises the following preparation steps:

[0066] S1. A body is prepared, and the multi-color jade base glaze described above is applied to the body to obtain a tile body A.

[0067] S2. The jade transparent glaze described above is applied to the tile body A to obtain a tile body B.

[0068] S3. A design inkjet pattern is printed on the tile body B to obtain a tile body C.

[0069] S4. The brick body C is applied with gluey glaze by using a spraying machine to obtain a brick body D;

[0070] S5. The brick body D is applied with the jade dry granular glaze mentioned above by using a material distributing machine to obtain a brick body E;

[0071] S6. The brick body E is applied with gluey glaze by using a spraying machine to obtain a brick body F;

[0072] S7. The brick body F is dried to obtain a brick body G;

[0073] S8. The brick body G is fired at high temperature to obtain a brick body H;

[0074] S9. The brick body H is polished, edge-ground, sorted, packed and warehoused to obtain the multi-color jade glaze face brick with sheep fat jade effect;

[0075] The gluey glaze comprises glue and jade dry granular glaze slurry, and the mass ratio of the glue and the jade dry granular glaze slurry is 100:50;

[0076] The glue and the jade dry granular glaze slurry are uniformly mixed to obtain the gluey glaze.

[0077] The preparation method of the multi-color jade glaze face brick with sheep fat jade effect further optimizes as follows:

[0078] It comprises one or several combinations of the following features:

[0079] The specific gravity of the slurry of the multi-color jade base glaze is 1.90 g / ml, the flow rate is 38-48 seconds, and the glazing amount is 500 g / m 2 ;

[0080] The specific gravity of the slurry of the jade light-transmitting glaze is 1.90 g / ml, the flow rate is 38-48 seconds, and the glazing amount is 416 g / m 2 ;

[0081] The glazing amount of the jade dry granular glaze is 611 g / m 2 ;

[0082] The specific gravity of the gluey glaze is 1.15 g / ml, and the glazing amount is 194 g / m 2 .

[0083] The preparation method of the multi-color jade glaze face brick with sheep fat jade effect further optimizes as follows:

[0084] The glue comprises the following components by mass:

[0085] Water 100 parts, CMC 4 parts, ethylene glycol 12 parts, sodium tripolyphosphate 0.12 parts, preservative 0.12 parts.

[0086] The fourth inventive object of the present application is:

[0087] The multicolor jade glazed tile with sheep fat jade effect is prepared by the preparation method of the multicolor jade glazed tile with sheep fat jade effect.

[0088] The main core innovation points of the present application include the following aspects:

[0089] (1) A multicolor jade base glaze is developed, and the semi-transparency of the base glaze is used to match the softness of the single color or multi-color to improve the jade quality.

[0090] (2) A jade light-transmitting glaze is applied before inkjet printing, which can greatly reduce the ink dot defects through the fusion with ceramic ink, so that the design pattern is more soft and natural, and the level of feeling is improved.

[0091] (3) A variety of new dry particles are used to increase the three-dimensional effect, and the jade dry particles with opalescent effect are added to the multicolor dry particles with flocculent effect and ice crystal dry particles, and the fusion effect of the jade light-transmitting glaze with ceramic ink makes the tile surface have rich details and three-dimensional effect.

[0092] (4) The developed jade dry particles with micro-opalescent effect are closer to the jade quality than the common single high-transparency dry particles.

[0093] The preparation process of the multicolor jade glazed tile with sheep fat jade effect has the following characteristics:

[0094] (1) Potassium feldspar and sodium feldspar are introduced into the jade light-transmitting glaze formula

[0095] Potassium feldspar and sodium feldspar are strong flux raw materials, which can reduce the firing temperature of the glaze, and the sodium feldspar in the form of hexagonal flake can improve the refraction effect and greatly improve the jade quality.

[0096] (2) Appropriate amount of quartz is introduced into the multicolor jade single-color base glaze, and appropriate amount of calcite is introduced into the jade light-transmitting glaze

[0097] The scattering of bubbles produced by quartz particles and calcium feldspar crystals in calcite at high temperature can significantly improve the jade quality. In addition, calcium oxide can improve the chemical stability of the glaze and increase the suspension of the glaze paste.

[0098] (3) Appropriate amount of zinc oxide is introduced into the jade light-transmitting glaze

[0099] Zinc oxide makes the glaze easy to melt, reduces the firing temperature, and has good effects on the mechanical strength, elasticity, melting performance and fire resistance of the glaze, increases the firing range of the glaze material, and improves the color development ability.

[0100] (4) Introducing appropriate amount of calcined alumina into the colorful jade color base glaze

[0101] The calcined alumina can make the glaze surface more delicate, uniform, and the glaze surface more smooth and delicate, and stable and appropriate gloss.

[0102] (5) Introducing appropriate amount of strontium carbonate into the jade light-transmitting glaze

[0103] The strontium carbonate can effectively improve the gloss of the glaze surface, make the glaze surface more smooth and bright, and also make the glaze surface present elegant light color and become more soft, and increase the jade quality of the glaze surface. BRIEF DESCRIPTION OF DRAWINGS

[0104] Figure 1 It is a comparison diagram of ink dots on the colorful jade glaze brick (right) with the sheep fat jade effect of the application and the conventional full polishing glaze brick (left).

[0105] Figure 2 It is a physical diagram of the colorful jade glaze brick with the sheep fat jade effect of the application. DETAILED DESCRIPTION

[0106] In order to make the application, technical scheme and advantages of the application more clear and explicit, the application content is described in detail in combination with specific examples. It should be understood that the examples are only used to illustrate the application, and not to limit the protection scope of the application, and any simple improvement of the preparation method of the application within the concept of the application is within the protection scope of the application.

[0107] Example 1

[0108] A preparation method of a colorful jade glaze brick with a sheep fat jade effect, which adopts the aforementioned colorful jade glaze with a sheep fat jade effect, comprises the following preparation steps:

[0109] S1. Preparing a body, and applying a colorful jade base glaze to the body to obtain a brick body A;

[0110] S2. Applying a jade light-transmitting glaze to the brick body A to obtain a brick body B;

[0111] S3. Printing a design inkjet pattern on the brick body B to obtain a brick body C;

[0112] S4. Applying a glue glaze to the brick body C using a jet printer to obtain a brick body D;

[0113] S5. Applying a jade dry granular glaze to the brick body D using a distributing machine to obtain a brick body E;

[0114] S6. Applying a glue glaze to the brick body E using a jet printer to obtain a brick body F;

[0115] S7. Drying the brick body F to obtain a brick body G;

[0116] S8. High-temperature firing the brick body G to obtain a brick body H;

[0117] S9. Polishing, edge grinding, sorting, packing and warehousing the brick body H to obtain the multi-color jade quality glazed tile with mutton fat jade effect;

[0118] The gluey glaze comprises: glue and jade quality dry granular glaze slurry, and the mass ratio of the glue and the jade quality dry granular glaze slurry is 100:50.

[0119] The gluey glaze is prepared by uniformly mixing the glue and the jade quality dry granular glaze slurry.

[0120] The specific gravity of the glaze slurry of the multi-color jade quality base glaze is 1.90 g / ml, the flow rate is 38-48 seconds, and the glaze application amount is 500 g / m 2 ;

[0121] The specific gravity of the glaze slurry of the jade quality light-transmitting glaze is 1.90 g / ml, the flow rate is 38-48 seconds, and the glaze application amount is 416 g / m 2 ;

[0122] The glaze application amount of the jade quality dry granular glaze is 611 g / m 2 ;

[0123] The specific gravity of the gluey glaze is 1.15 g / ml, and the glaze application amount is 194 g / m 2 .

[0124] The glue comprises the following components by mass fraction:

[0125] 100 parts of water, 4 parts of CMC, 12 parts of ethylene glycol, 0.12 parts of sodium tripolyphosphate, and 0.12 parts of preservative.

[0126] The multi-color jade quality base glaze comprises the following components by mass fraction:

[0127] 19% of calcined alumina, 23% of quartz powder, 25% of potassium feldspar, 9% of nepheline powder, 14% of kaolin, 2% of dolomite, 8% of zirconium silicate, 0.13% of sodium carboxymethyl cellulose, 0.25% of sodium tripolyphosphate, and an appropriate amount of water.

[0128] The multi-color jade quality colored base glaze comprises: base glaze slurry prepared from the multi-color jade quality base glaze and glaze colorant slurry, and the mass ratio of the base glaze slurry and the glaze colorant slurry is 100:2. Figure 2 The base glaze slurry and the glaze colorant slurry are used.

[0129] The jade translucent glaze comprises the following mass percentage components:

[0130] Potassium feldspar 45%, sodium feldspar 17%, kaolin 14%, calcined zinc oxide 4%, calcite 14%, strontium carbonate 3%, glass powder 3%; additionally, sodium carboxymethyl cellulose 0.12%, sodium tripolyphosphate 0.21%, and appropriate amount of water;

[0131] The jade dry granular glaze comprises jade dry granules, multicolor dry granules and ice crystal dry granules, and the mass ratio of the jade dry granules, the multicolor dry granules and the ice crystal dry granules is 100:3:1.5;

[0132] The jade dry granules comprise the following mass percentage raw material components:

[0133] 8# stone powder 32%, 9# stone powder 19%, ball clay 6%, white sand 16%, talc mud 4%, white clay 12%, wollastonite 4%, bentonite 3%, calcined kaolin 4%; additionally, water glass 0.6%, sodium tripolyphosphate 0.1%, and appropriate amount of water;

[0134] The multicolor dry granules comprise jade dry granule slurry prepared from the jade dry granules and glaze color slurry, and the jade dry granule slurry and the glaze color slurry are properly matched according to color requirements;

[0135] The fineness of the multicolor dry granules is 20-60 mesh;

[0136] The ice crystal dry granules are zirconium silicate fine particles, and the fineness is 60-200 mesh.

[0137] The preparation of various specific raw materials involved in this embodiment 1 is described in detail in the specification part.

[0138] The detection product indexes are as shown in Table 4.

[0139] Table 4 Product quality test results (rule 600x900x9.8mm)

[0140]

[0141] Table 5 Special test results of mutton fat jade effect

[0142]

[0143] The multicolor jade glaze with mutton fat jade effect, the glazed tile and the preparation method thereof have the characteristics of strong technical adaptability and strong practicability. The method is easy to popularize and apply, will promote the innovation and development of jade effect products in the tile industry, and promote the application of the products in the high-end decoration field.

[0144] In summary, only the preferred examples of the present application are described above, and the present application is not limited to any form; for those skilled in the art, some changes, modifications and equivalent variations of the disclosed technical contents within the scope of the technical solutions of the present application are equivalent examples of the present application; at the same time, any equivalent changes, modifications and evolution of the above embodiments according to the essential technology of the present application are still within the protection scope of the technical solutions of the present application.

[0145] The technical features of the above-described embodiments can be combined arbitrarily. In order to make the description concise, all possible combinations of the technical features in the above-described embodiments are not described, however, as long as the combinations of the technical features do not exist in contradiction, they should be considered as the scope of the present disclosure.

[0146] Unless otherwise specified, the experimental methods in the present application are generally carried out under conventional conditions or according to the conditions recommended by the manufacturers.

[0147] Unless otherwise specified, the various optimized technical solutions in the present application can be combined with each other.

[0148] Unless otherwise specified, the percentages and parts are mass percentages and mass parts.

[0149] Unless otherwise specified, the experimental methods in the present application are generally carried out under conventional conditions or according to the conditions recommended by the manufacturers.

[0150] Unless otherwise defined, all professional and scientific terms used herein have the same meaning as familiar to those skilled in the art. In addition, any method and material similar or equivalent to those described can be applied in the present application.

Claims

1. A multicolor jade glaze with sheep fat jade effect, characterized in that: it comprises a multicolor jade base glaze, a jade transparent glaze and a jade dry grain glaze; the multicolor jade base glaze comprises a multicolor jade base glaze and a multicolor jade colored base glaze; the multicolor jade base glaze comprises the following components by mass percentage: calcined alumina 16-22%, quartz powder 22-26%, potassium feldspar 23-30%, nepheline powder 8-14%, kaolin 14-18%, dolomite 2-5%, zirconium silicate 7-13%, and the sum of all components is 100%; additionally, sodium carboxymethyl cellulose 0.13%, sodium tripolyphosphate 0.25%, and an appropriate amount of water; the multicolor jade colored base glaze comprises a base glaze slurry prepared from the multicolor jade base glaze and a glaze colorant slurry, and the mass ratio of the base glaze slurry and the glaze colorant slurry is 100:1-3; the jade transparent glaze comprises the following components by mass percentage: potassium feldspar 40-48%, sodium feldspar 15-20%, kaolin 13-16%, calcined zinc oxide 3-5%, calcite 12-18%, strontium carbonate 2-6%, glass powder 2-5%, and the sum of all components is 100%; additionally, sodium carboxymethyl cellulose 0.12%, sodium tripolyphosphate 0.21%, and an appropriate amount of water; the jade dry grain glaze comprises jade dry grain, multicolor dry grain and ice crystal dry grain, and the mass ratio of the jade dry grain, the multicolor dry grain and the ice crystal dry grain is 100:2-5:1-4; the jade dry grain comprises the following raw material components by mass percentage: 8# stone powder 30-35%, 9# stone powder 17-22%, ball clay 5-8%, white sand 15-19%, talc clay 3-6%, white clay 11-15%, wollastonite 3-5%, bentonite 2-4%, calcined kaolin 3-5%, and the sum of all components is 100%; additionally, water glass 0.6%, sodium tripolyphosphate 0.1%, and an appropriate amount of water; the multicolor dry grain comprises a jade dry grain glaze slurry prepared from the jade dry grain and a glaze colorant slurry, and the jade dry grain glaze slurry and the glaze colorant slurry are appropriately matched according to color requirements; the multicolor dry grain has a fineness of 20-60 mesh; and the ice crystal dry grain is zirconite fine particles with a fineness of 60-200 mesh. 2.The multicolor jade glaze with sheep fat jade effect according to claim 1, characterized in that: it comprises one or a combination of the following features: the glaze colorant slurry in the multicolor jade colored base glaze is prepared by mixing one or more of praseodymium yellow, vanadium zirconium blue, fruit green, zirconium iron red and cobalt black; and the glaze colorant slurry in the multicolor dry grain is prepared by mixing one or more of zirconium silicate, vanadium zirconium blue, praseodymium yellow, zirconium iron red and cobalt black. 3.A preparation method of the multicolor jade glaze with sheep fat jade effect according to claim 1, characterized in that: the multicolor jade base glaze comprises the following preparation method: ​ ​ ​ ​ ​ ​ ​ ​ ​ ​ ​ ​ ​ ​ ​ ​ ​ The multicolor jade quality base glaze is prepared by mixing the multicolor jade quality base glaze and the multicolor jade quality colored base glaze according to needs, and is ready for use. The multicolor jade quality base glaze is prepared by the following method: The corresponding raw material components are weighed according to the multicolor jade quality base glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the multicolor jade quality base glaze, ready for use. The multicolor jade quality base glaze is prepared by the following method: The multicolor jade quality base glaze is prepared by the following method: The corresponding raw material components are weighed according to the multicolor jade quality base glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the multicolor jade quality base glaze, ready for use. The multicolor jade quality base glaze is prepared by the following method: The corresponding raw material components are weighed according to the multicolor jade quality base glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the multicolor jade quality base glaze, ready for use. The multicolor jade quality base glaze is prepared by the following method: The corresponding raw material components are weighed according to the multicolor jade quality base glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the multicolor jade quality base glaze, ready for use.

4. The preparation method of the multicolor jade quality glaze with sheep fat jade effect according to claim 3, characterized in that: It includes one or more combinations of the following characteristics: The multicolor jade quality base glaze is prepared by the following method: The corresponding raw material components are weighed according to the multicolor jade quality base glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the multicolor jade quality base glaze, ready for use. The multicolor jade quality base glaze is prepared by the following method: The corresponding raw material components are weighed according to the multicolor jade quality base glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the multicolor jade quality base glaze, ready for use. The multicolor jade quality base glaze is prepared by the following method: The corresponding raw material components are weighed according to the multicolor jade quality base glaze formula, ball milling, slurry, and 325 mesh screen, to prepare the multicolor jade quality base glaze, ready for use.

5. The preparation method of the multicolor jade quality glaze with sheep fat jade effect according to claim 3, characterized in that: It includes one or more combinations of the following characteristics: The glaze slurry of the multicolor jade quality base glaze is finely ground to 325 mesh screen with a residual fineness of 0.1-0.3%, and the water content is 28-30% by mass percentage; The glaze slurry of the multicolor jade quality base glaze is finely ground to 325 mesh screen with a residual fineness of 0.1-0.3%, and the water content is 28-30% by mass percentage; The glaze slurry of the multicolor jade quality base glaze is finely ground to 325 mesh screen with a residual fineness of 0.1-0.3%, and the water content is 28-30% by mass percentage, The dry granular jade glaze has a 250-mesh residue of 0.6-0.8% and a water content of 30-34%. The dry granular jade glaze has a 250-mesh residue of 0.6-0.8% and a water content of 30-34%.

6. A method for preparing a multi-color jade glazed tile with a jade effect, using the multi-color jade glaze with a jade effect according to claim 1, characterized in that: It comprises the following preparation steps: S1. Preparing a body and applying the multi-color jade base glaze to the body to obtain a tile body A; S2. Applying the jade transparent glaze to the tile body A to obtain a tile body B; S3. Printing a design inkjet pattern on the tile body B to obtain a tile body C; S4. Applying a glue glaze to the tile body C using a jet printer to obtain a tile body D; S5. Applying the dry granular jade glaze to the tile body D using a distributor to obtain a tile body E; S6. Applying a glue glaze to the tile body E using a jet printer to obtain a tile body F; S7. Drying the tile body F to obtain a tile body G; S8. High-temperature firing the tile body G to obtain a tile body H; S9. Polishing, edging, sorting, packaging, and warehousing the tile body H to obtain the multi-color jade glazed tile with a jade effect; The glue glaze comprises a glue and a dry granular jade glaze, and the mass ratio of the glue and the dry granular jade glaze is 100:

50. The glue and the dry granular jade glaze are mixed uniformly to obtain the glue glaze.

7. The method for preparing a multi-color jade glazed tile with a jade effect according to claim 6, characterized in that: It comprises one or a combination of the following characteristics: The specific gravity of the glaze slurry of the multicolor jade quality base glaze is 1.90 g / ml, the flow rate is 38-48 seconds, and the glaze application amount is 500 g / m 2 ; The specific gravity of the glaze slurry of the jade quality transparent glaze is 1.90 g / ml, the flow rate is 38-48 seconds, and the glaze application amount is 416 g / m 2 ; The application amount of the said jade dry granular glaze is 611g / m 2 ; The specific gravity of the glue enamel is 1.15 g / ml, and the enamel application amount is 194 g / m 2 .

8. The method for preparing a multi-color jade glazed tile with a jade effect according to claim 6, characterized in that: The glue comprises the following components by mass: Water 100 parts, CMC 4 parts, ethylene glycol 12 parts, sodium tripolyphosphate 0.12 parts, and preservative 0.12 parts.

9. A multi-color jade glazed tile with a jade effect, characterized in that: It is prepared by the method for preparing a multi-color jade glazed tile with a jade effect according to claim 6.