Flexible, explosion-resistant, multi-layered material for an electric battery

Abstract

The invention relates to a multilayer material comprising n basic units with n a non-zero natural number, a basic unit consisting of a laminate comprising in the following order: - a layer (7) of crosslinked silicone resin comprising graphite particles expandable from a temperature above a crosslinking temperature of said resin, - a layer (5) of impregnated silica or alumina fabric or knit, the fabric or knit being provided with interstices all impregnated with a crosslinked silicone resin comprising graphite particles expandable from a temperature above a crosslinking temperature of said resin, in which: - the number n of basic units is between 1 and 5 inclusive, - the nth basic unit being covered with another layer (7') of crosslinked silicone resin also comprising graphite particles expandable from a temperature above a crosslinking temperature of said resin,so as to form a laminate consisting of alternating layers of resin and fabric or knit material. Figure 1,

Description

Title of the invention: Flexible multi-layer material resistant to the explosion of an electric battery Technical field

[0001] The invention relates to the field of electric batteries.

[0002] The invention relates more specifically to a multilayer material capable of serving as a mechanical and thermal shield for application to electric batteries. Previous Art

[0003] Many areas require the use of mechanical and thermal protection.

[0004] In particular, the protection of batteries, especially lithium-ion batteries, is currently a major issue for the safety and reliability of electric or hybrid transport vehicles, whatever the sector concerned (automobile, in particular light vehicles, heavy goods vehicles, buses or coaches, aeronautics, railways, naval, etc.).

[0005] Indeed, electric vehicle batteries can, under certain conditions, undergo an uncontrollable thermal runaway phenomenon leading to the explosion of the battery in a few seconds.

[0006] This explosion, in addition to a blast effect, is accompanied by a projection of particles having a temperature likely to exceed 1500°C. This is referred to as a "blast" phenomenon in Anglo-Saxon terminology.

[0007] This is why mechanical and thermal shields are placed on and / or around the assembly constituting the battery, in order to confine the blast of the explosion and the projection of hot particles.

[0008] Most of the shields currently in existence are based on mica plates.

[0009] These mica plates effectively guarantee the mechanical and thermal integrity of the shield and consequently protect everything around it.

[0010] However, mica plates are mechanically rigid.

[0011] Thus, particularly when the battery has a complex shape or has many curves or angular areas, the shield is formed by cutting the mica plates into pieces of suitable dimensions which are then assembled on the various hollows and reliefs of the battery and joined together.

[0012] Besides the fact that this process of adapting the shield made of cut mica plates to the shape of the battery is time-consuming, there may be areas of weakness in terms of mechanical and thermal protection at the junctions between each mica plate.

[0013] In order to avoid the presence of weak zones, it has already been proposed to manufacture a mold in the shape of the battery which is then used to form a shield of a composite material comprising mica plates embedded in a resin. The hardening of the resin makes it possible to form the rigid mica buckle.

[0014] However, the manufacture of the shield remains time-consuming and, above all, a dedicated mold must be manufactured for each battery shape.

[0015] Furthermore, multi-layer materials are also known for thermal protection. These multi-layer materials have the advantage of being flexible and therefore adaptable to all shapes, whether for objects or people.

[0016] A multilayer material typically used for this purpose is formed from a silica fabric coated on at least one of its faces with a crosslinked silicone resin.

[0017] For example, reference may be made to document KR102349628B1 which describes a fire shield comprising a multi-layer material comprising a silica fabric coated with a layer of silicone resin with, optionally, flame retardants, such as particles of alumina hydroxide, magnesium hydroxide, silica, phosphorus-based, ceramic or mixtures thereof.

[0018] However, this multi-layer material does not withstand the very restrictive mechanical and thermal conditions of an electric battery “blast” phenomenon.

[0019] One objective of the invention is to resolve at least one of the aforementioned drawbacks.

[0020] In particular, an objective of the invention is to propose a solution capable of form a mechanical and thermal shield capable of resisting the “blast” phenomenon of an electric battery, capable of adapting to any battery geometry without further difficulty Summary of the invention

[0021] To achieve at least one of these objectives, the invention proposes a multilayer material comprising n basic units with n a non-zero natural integer, a basic unit consisting of a laminate comprising in order: - a crosslinked silicone resin layer comprising expandable graphite particles with a temperature higher than a crosslinking temperature of said resin; - a layer of silica or alumina fabric or knit, the fabric or knit being provided with interstices all impregnated with a crosslinked silicone resin comprising graphite particles expandable from a temperature higher than a crosslinking temperature of said resin, in which: - the number n of basic units is between 1 and 5 inclusive, - the nth base unit being coated with another layer of crosslinked silicone resin comprising particles of graphite expandable from a temperature higher than a crosslinking temperature of said resin, so as to form a laminate formed by an alternation of a layer of resin and a layer of fabric or knit.

[0022] The invention may comprise at least one of the following characteristics, taken alone or in combination: - the thickness of the basic unit is between 900 and 1150 pm; - the number n of base units is between 1 and 3 inclusive, and is worth preference 2 or 3; - the multi-layer material has a total thickness between 1100 and 5950 pm; - the multilayer material comprises a number n = 2 of basic units, for a total thickness between 2000 and 2500 pm; - the multilayer material comprises a number n= 3 of basic units, for a total thickness of 2900 and 3650 pm; - the silicone resin comprises an additional filler selected from the group consisting of short silica or alumina fibers, fumed silica particles, magnesium hydroxide particles, vermiculite, clay particles, titanium oxide particles, silicon carbide particles or mixtures of two or more thereof; - the silicone resin, crosslinked or not, comprises from 5 to 15% by mass, relative to the total mass of the resin, of expandable graphite particles and comprises from 4 to 7% by mass, relative to the total mass of the resin, of fumed silica; - the expandable graphite particles have their largest dimension between 80 and 110 pm, preferably a largest dimension of 90 pm; Brief description of the figures

[0023] [Fig.l] represents a multilayer material in accordance with the invention, according to an exemplary embodiment;

[0024] [Fig.2] represents a multilayer material in accordance with the invention, according to another exemplary embodiment;

[0025] [Fig.3] represents the different stages of a possible manufacturing process for obtaining the multilayer material of [Fig.l];

[0026] [Fig.4] represents the different stages of a possible manufacturing process for obtaining the multilayer material of [Fig.2];

[0027] [Fig.5] is a diagram of an experimental installation suitable for testing the behavior of the multilayer material of the invention in a “blast” test of an electric battery. Detailed description

[0028] The invention provides a multilayer material comprising n basic units with n a non-zero natural integer, a basic unit consisting of a laminate comprising in order: - a crosslinked silicone resin layer comprising graphite particles expandable from a temperature above a crosslinking temperature of said resin; - a layer of silica or alumina fabric or knit, the fabric or knit being provided with interstices all impregnated with a crosslinked silicone resin comprising graphite particles expandable from a temperature higher than a crosslinking temperature of said resin, in which: - the number n of basic units is between 1 and 5 inclusive, - the nth base unit being coated with another layer of crosslinked silicone resin comprising particles of graphite expandable from a temperature higher than a crosslinking temperature of said resin, so as to form a laminate formed by an alternation of a layer of resin and a layer of fabric or knit.

[0029] [Fig. 1] shows an example of a multilayer material Mi according to the invention, providing a basic unit (n=1). Similarly, [Fig. 2] shows an example of a multilayer material M2 according to the invention, providing two basic units (n=2).

[0030] A layer 5, 5' of silica or alumina fabric typically has a thickness of between 420 and 460 μm. The fabric is formed from silica or alumina fibers formed into woven threads, for example with a plain weave.

[0031] An example of silica fabric used to form the multilayer material of the invention is a silica fabric marketed under the reference Valmiera® Glass, KA-300. Reference may be made to the technical data sheet for this product to know all the characteristics of this fabric. However, this silica fabric has the following main characteristics: fabric made of 34x6 (warp / weft) or 68x3 (warp / weft) yarns with filaments of 6 μm in diameter, canvas-type weave with a full feather length of 5 to 8 mm, heat-treated with an aminosilane finish, tensile strength in the warp direction: greater than or equal to

[0032]

[0033]

[0034]

[0035]

[0036]

[0037]

[0038]

[0039]

[0040]

[0041] 700N / 25mm and in the weft direction: greater than or equal to 600N / 25mm, basic weight of 300g / m2, thickness of around 440 pm. An example of an alumina fabric that can be used to form the multilayer material of the invention is an alumina fabric marketed by the company 3M, under the reference Nextel® 440. The use of silica or alumina fabric provides great flexibility, while contributing to the mechanical and thermal resistance requirements of an electric battery blast test. The interstices of this fabric are all impregnated with crosslinked silicone resin. As a result, expandable graphite particles are present in all interstices of the silica or alumina fabric, not just in a portion of these interstices. To obtain impregnation of the silica or alumina fabric in all its interstices, a liquid non-crosslinked silicone resin is therefore used during manufacturing. By "liquid resin" is meant a resin having an apparent viscosity of between 20 and 35 Pa.s. This viscosity can be measured using the Brookfield method (NF EN ISO 2555 - Plastics - Resins in liquid state or in emulsions or dispersions - Determination of apparent viscosity using the single-cylinder rotary viscometer method) with the following operating conditions: [Tables 1] Mobile reference S06 Cylinder rotation speed (rpm) 20 Sample temperature (°C) 24.7 Sample volume (mL) 400 Generally speaking, to make the non-crosslinked, liquid silicone resin, the following composition can be used: - dimethylsiloxane: 65 to 75 parts by mass, - Vinyl siloxane: 0 to 7 parts by mass (optional) - Methyl hydrogensiloxane: 15 to 25 parts by mass - Additional charge: 0 to 10 parts by mass (optional) - Platinum Catalyst: 0.3 to 1 part by mass - Expandable graphite: 4 to 14 parts by mass Optionally, the silicone resin may therefore contain one or more additional fillers chosen from the group consisting of short fibers (i.e. fibers having a length less than or equal to 6 mm) of silica or alumina, particles fumed silica, magnesium hydroxide particles, vermiculite, clay particles such as montmorillonite, titanium oxide particles, silicon carbide (SiC) particles and mixtures of two or more of these.

[0042] Thus and for example, the silicone resin, crosslinked or not, may in particular comprise: - from 5 to 15% and in particular between 5% and 10% by mass, relative to the total mass of the resin, of expanded graphite particles, and - 4% and 7% by mass, relative to the total mass of the resin, of fumed silica.

[0043] During manufacture, the monomers of dimethylsiloxane, methylhydrogensiloxane and, where provided, vinylsiloxane, crosslink.

[0044] The expandable graphite particles have the property of resisting temperatures well above 1500°C, in the absence of oxygen, which is the case when they are embedded in the crosslinked silicone resin.

[0045] As they are integrated into the silicone resin, which impregnates the silica fabric at its core, they will, during their expansion, mix intimately with the silica fibers and form, with these silica fibers, a real integral barrier of a material resistant to at least 1500°C while also reinforcing the mechanical resistance of the silica fabric.

[0046] For this, it is of course necessary that the graphite particles are in an unexpanded state in the crosslinked silicone; in other words, that the crosslinking temperature of the silicone resin is lower than the temperature at which the graphite particles begin to expand. A slight expansion can be tolerated, so that this temperature at which the graphite particles begin to expand must be understood as a temperature from which a strong and rapid expansion of the graphite particles is observed.

[0047] Typically, expandable graphite particles have the property of beginning to expand (increase in volume) strongly and rapidly from a temperature which can be between 160°C and 220°C, sometimes beyond. It is therefore advisable to choose a silicone resin whose crosslinking temperature is suitable.

[0048] Preferably, the expandable graphite particles are particles having their largest dimension between 80 and 110 μm because this allows a more homogeneous distribution of the particles in the silicone resin. An example of expandable graphite particles that can be used in the invention are the graphite particles marketed by the company NEOGRAF® Solutions under the brand name GrafGuard®, grade 210-200N (the first number, namely 210, designates the critical temperature from which the graphite begins to expand, i.e. 210°C and the second number, namely 200, is a reference, designating particles qualified as small sizes, i.e. in the range from 80 to 110 μm).

[0049] It is understood that the more the number n of basic units of the multilayer material increases, the more the resistance to the “blast” phenomenon of an electric battery increases.

[0050] However, the more the number n of basic units of the multilayer material increases, the more flexibility is also lost. Indeed, although the fabric provides great flexibility, the total thickness and therefore the quantity of crosslinked resin used have an impact on this flexibility.

[0051] For this reason, it is preferable that the number n of basic units is not greater than 5.

[0052] When a very intimate wrapping of the battery is sought, it is preferable that the number of basic units n is between 1 and 3. And when, in addition, resistance to the "blast" phenomenon of an electric battery is also desired, it is then preferable to choose n = 2 or 3 basic units.

[0053] All the comments made previously on the silicone resin concern not only the resin impregnated in the silica fabric, but also the resin which may be used to form the other layers.

[0054] It is also advantageous if the silicone resin used is the same for the entire manufacture of the multilayer material. This facilitates manufacturing. However, it is entirely possible to have different compositions provided, of course, that in the non-crosslinked state, these resins are liquid to impregnate all the interstices of the silica or alumina fabric.

[0055] Depending on the number of basic units, between 1 and 5, and the choices made for each layer (thickness of the fabric, quantity of resin deposited) of layers of the multilayer material, the latter will have a total thickness typically between 1100 and 5950 μm.

[0056] Finally, it should be noted that the fabric can be replaced by a knit, i.e. using a silica or alumina knit. Example No. 1 of embodiment of the invention

[0057] We will now describe, with the support of [Fig.3], a method of manufacturing a multilayer material according to the invention, and more precisely the multilayer material represented in [Fig.1] (n = 1 basic unit).

[0058] The fabric used is a silica fabric marketed under the reference Valmiera® Glass KA-300, the main properties of which have been provided previously. Fabric 1 is visible in [Fig.2], step a).

[0059] This fabric is then impregnated by coating with 350 g / m2 of the non-crosslinked silicone resin on the face 3, exposed to the coating roller 2, of the fabric 1 (the face 4 of the fabric 1 is not exposed to the coating roller 2). The positioning of the coating roller before the actual coating is shown in [Fig.2], step a).

[0060] To produce the liquid, non-crosslinked silicone resin, the following composition is provided: - dimethylsiloxane: 69 parts by mass, - Vinyl siloxane: 6 parts by mass, - Methyl hydrogensiloxane: 20 parts by mass, - Pyrogenic silica: 4.5 parts by mass, - Platinum Catalyst: 0.5 parts by mass, - Expandable graphite: 7 parts by mass.

[0061] No solvent or diluent is used.

[0062] The viscosity was measured by the Brookfield method under the conditions specified previously, but recalled below:

[0063] [Tables2] Mobile reference S06 Cylinder rotation speed (rpm) 20 Sample temperature (°C) 24.7 Sample volume (mL) 400

[0064] The quantity of silicone resin deposited makes it possible to impregnate the fabric 5, in all its interstices, and also to form at the same time, a layer 7 of silicone resin protruding from the fabric.

[0065] The assembly thus obtained is passed through an oven at 200°C, to crosslink the resin. The resin does not shrink during its crosslinking. [Fig.2], step b) represents the fabric 5 impregnated with the crosslinked silicone resin, with the layer 7 of silicone resin above.

[0066] [Fig.2], step b) therefore represents a basic unit of the multilayer material.

[0067] This base unit is then returned ready to be coated. This is what is shown in [Fig.2], step c).

[0068] A coating of the same non-crosslinked silicone resin is then carried out on the opposite face 4 of the layer 5 of fabric of the basic unit, at a rate of 700g / m2. At this stage, an assembly with layers 7, 5 and 7 is obtained.

[0069] The assembly thus obtained is again passed through the oven at 200°C to crosslink all the non-crosslinked silicone resin. This results in the desired multi-layer Mi material, as shown in [Fig.2], step d). The multi-layer Mi material is in the form of a laminate formed by alternating a layer of resin and a layer of fabric.

[0070] The multi-layer Mi material finally obtained (n=1 basic unit) has a total thickness of between 1100 and 1350 pm. Example No. 2 of embodiment of the invention

[0071] Here, steps a), b) and c) of [Fig.4] (n=2 basic units) repeat steps a), b) and c) of [Fig.3] (n=1 basic unit).

[0072] Then, additional steps are planned.

[0073] Thus, a coating of the same non-crosslinked silicone resin is carried out on the opposite face 4 of the fabric 5, at a rate of 700g / m2. However, no crosslinking is carried out. We then end up with the assembly shown in [Fig.4], step d').

[0074] We then recover a part of the set obtained in step b).

[0075] The latter is then affixed to layer 7' of the assembly obtained in step b).

[0076] The assembly thus obtained is again passed through the oven at 200°C to crosslink all the non-crosslinked silicone resin.

[0077] We then obtain the multilayer material M2 represented in [Fig.4], step e') consisting, from the bottom up: - a first base unit formed from a layer 7 of crosslinked resin coated with a silica fabric 5 impregnated with crosslinked silicone resin; - a second base unit formed from a 7' layer of crosslinked resin coated with a 5' silica fabric impregnated with crosslinked silicone resin; and - another 7” layer of crosslinked resin.

[0078] The multi-layer M2 material is in the form of a laminate formed by alternating a layer of resin and a layer of fabric.

[0079] This multilayer material (n = 2 basic units) has a total thickness of between 2000 and 2500 pm. Other examples of embodiments of the invention

[0080] It should be noted that to manufacture a multilayer material comprising n = 3, 4 or even 5 basic units, it is then necessary to repeat as many times as necessary, namely 1, 2 or 3 times in a row, the additional steps described in support of example No. 2 of the invention.

[0081] Typically, a multilayer material according to the invention with n = 3 basic units will have a total thickness of between 2900 and 3650 pm.

[0082] Typically, a multilayer material according to the invention with n = 4 basic units will have a total thickness of between 3800 and 4800 μm.

[0083] Typically, a multilayer material according to the invention with n = 5 basic units will have a total thickness of between 4700 and 5950 μm. Blast test

[0084] A “blast test” is, in this text, a test conducted under extreme conditions which reproduce the worst conditions which could occur during the explosion of a Li-ion battery, i.e. a projection of molten particles at a temperature of 1500°C.

[0085] A simplified diagram of the experimental setup used to carry out the “blast test” is shown in [Fig.5].

[0086] As seen in [Fig.3], a sample 20 of 250 mm x 250 mm of the material to be tested is placed in a frame 10 made of EN AW-5182 aluminum. A particle projection system 30 is placed at a distance of 30 mm (impact distance) and centered on the desired impact zone 40 to reproduce the "blast" phenomenon. The particle projection system 30 is a pyrotechnic rocket whose characteristics are as follows: effect distance between 4 and 5 m, lateral range between 1.5 and 2.5 m, sound pressure level of 94 dB (Almax) at 3 m, and comprising particles capable of forming incandescent particles at 1500 ° C. The sound pressure level makes it possible to account for the speed of the particles at 3 m, and therefore indirectly for this speed at the impact distance (30 mm).

[0087] The particle projection system 1 is started. The duration of the projection of the incandescent particles is limited to 20 seconds, after which the system stops automatically if the sample is not perforated beforehand.

[0088] If the sample is punctured before the 20-second blast time, the time at which the puncture occurs is noted. In this case, the sample is considered not to have achieved the desired blast resistance.

[0089] If after 20 seconds the sample is not perforated, the sample is considered to have reached the desired blast resistance. Blast test results

[0090] The multi-layer material shown in [Fig.l] (n= 1 basic unit) has been subjected to a “blast test”, which was passed successfully. In addition, it proves to be sufficiently flexible to conform to even complex or curved shapes of the electric battery.

[0091] The multi-layer material shown in [Fig.2] (n= 2 basic units) has also been subjected to a "blast test", which was passed successfully. In addition, it proves to be sufficiently flexible to conform to even complex or curved shapes of the electric battery.

[0092] Other materials were tested, as comparative examples (comparative examples 1 to 5). Comparative example 1

[0093] A multi-layer material was manufactured by proceeding as in “exemplary embodiment No. 1 of the invention” (a single basic unit), but using a silicone resin which does not contain expandable graphite particles.

[0094] The only difference compared to embodiment No. 1 is therefore the absence of graphite particles.

[0095] The blast test failed. Comparative example 2

[0096] A multi-layer material was manufactured by proceeding as in “exemplary embodiment No. 2 of the invention” (two basic units), but using a silicone resin which does not contain expandable graphite particles.

[0097] The only difference compared to embodiment No. 2 is therefore the absence of graphite particles.

[0098] The blast test failed. Comparative example 3

[0099] A multi-layer material was manufactured by repeating one of the “other embodiments of the invention” (three basic units), using a silicone resin which does not contain expandable graphite particles.

[0100] Here too, the blast test was a failure. Comparative example 4

[0101] A multilayer material of the prior art consisting of a mica plate of the “Mica board Vonroll shield T18®” type marketed by the company VonRoll was considered.

[0102] The blast test failed.

[0103] Furthermore, this plate is too rigid to fit the complex or curved shapes of an electric battery, without making cuts or applying a method involving a mold. Comparative example 5

[0104] We have considered here a multilayer material of the prior art consisting of two mica plates, each of the “Mica board Vonroll shield T18®” type marketed by the company VonRoll.

[0105] The blast test was passed successfully.

[0106] However, this set of two plates is of course too rigid to fit the complex or curved shapes of an electric battery, without making cuts or applying a method involving a mold.

[0107] Comparative examples 1 to 3 clearly show the advantage of the presence of expanded graphite particles in the silicone resin, moreover with a homogeneous presence, in particular throughout the thickness of the silica fabric. Without this, the blast test cannot be successfully passed.

[0108] Furthermore, if the multilayer material according to the invention passes the blast test successfully already with a basic unit and its behavior can only improve with additional base units, we also see that increasing the number of base units in the comparative examples does not allow the blast test to be successfully passed.

[0109] As for the mica plate solution, we see that a minimum thickness remains necessary to pass the blast test successfully.

Claims

Claims

1. Multilayer material comprising n basic units with n a non-zero natural integer, a basic unit B consisting of a laminate comprising in order: - a layer (7) of crosslinked silicone resin comprising particles of graphite expandable from a temperature higher than a crosslinking temperature of said resin, - a layer (5) of impregnated silica or alumina fabric or knit, the fabric or knit being provided with interstices all impregnated with a crosslinked silicone resin comprising particles of graphite expandable from a temperature higher than a crosslinking temperature of said resin, in which: - the number n of basic units is between 1 and 5 inclusive,- the nth basic unit being covered with another layer (7') of crosslinked silicone resin also comprising particles of expandable graphite from a temperature higher than a crosslinking temperature of said resin, so as to form a laminate formed by an alternation of a layer of resin and a layer of fabric or knit.,

2. A multilayer material according to claim 1, wherein the thickness of the base unit is between 900 and 1150 pm.

3. Multilayer material according to any one of the preceding claims in which the number n of basic units is between 1 and 3 inclusive, and is preferably 2 or 3.

4. Multilayer material according to the preceding claim, having a total thickness of between 1100 and 5950 pm.

5. Multilayer material according to any one of the preceding claims, comprising a number n = 2 of basic units for a total thickness of between 2000 and 2500 pm.

6. Multilayer material according to any one of claims 1 to 4, comprising a number n = 3 basic units for a total thickness of 2900 and 3650 pm.

7. A multi-layer material according to any preceding claim, wherein the silicone resin comprises an additional filler selected from the group consisting of short silica or alumina fibers, fumed silica particles, magnesium hydroxide particles, vermiculite, clay particles, titanium oxide particles, silicon carbide (SiC) particles, and mixtures of two or more thereof.

8. Multilayer material according to any one of the preceding claims, in which the silicone resin, crosslinked or not, comprises: - 5 to 15% by mass, relative to the total mass of the resin, of expanded graphite particles, and - 4 to 7% by mass, relative to the total mass of the resin, of pyrogenic silica.

9. A multilayer material according to any preceding claim wherein the expandable graphite particles have their largest dimension between 80 and 110 pm, preferably a largest dimension of 90 pm.