Building block and associated manufacturing process

Abstract

The invention relates to a building block (1) comprising at least one core (2) and a casing (3), said at least one core (2) being arranged inside said casing (3). This block is particular in that said at least one core (2) comprises particles (4) of wood and / or plastic and / or plaster and / or glass and / or pebbles and / or brick and / or concrete and / or glass wool and / or rock wool and / or soiled cardboard and / or polystyrene and / or clinker and / or rubber, and in that said casing (3) is made of a concrete comprising at least 90% by weight of mineral matter. The invention also relates to a method for manufacturing a building block (1) according to the invention. Figure for abstract: Fig 1

Description

Title of the invention: Building block and associated manufacturing method Technical field

[0001] The present invention relates to the field of construction. It relates more particularly to a building block and its manufacturing method. The invention makes it possible in particular to recover construction waste and other waste, in particular waste that is difficult to recover using known methods. Prior art

[0002] Building blocks are now commonly made from cement concrete. This concrete contains large amounts of sand and cement, and has a particularly large carbon footprint.

[0003] Several solutions exist today to obtain building blocks with a reduced carbon footprint. It has been proposed to modify the composition of concrete, by replacing at least part of the mineral filler with bio-sourced elements such as wood. This concrete still requires a large quantity of mineral binders, and bio-sourced elements, even to a lesser degree than mineral elements, remain costly resources for the environment. There is therefore still significant interest in developing new construction materials with an even smaller carbon footprint.

[0004] It has been proposed to produce building blocks from materials containing construction waste. These blocks have significant limitations. Indeed, they are usually subject to the following compromise. Either the waste that composes them is carefully sorted and selected to obtain blocks with good mechanical properties, but in this case the cost of the blocks is higher and some waste cannot be used, and is therefore not recovered. Or the waste that composes them is very little sorted, which allows optimal recovery of all the waste, to the detriment of the repeatability of the mechanical properties of the building blocks. We therefore obtain building blocks that either have a limited impact on the environment, or have a guarantee at the level of their mechanical properties that is insufficient for a large number of applications. Statement of the invention

[0005] The present invention aims to overcome these drawbacks by proposing a building block comprising at least one core and one envelope, said at least one core being arranged inside said envelope.

[0006] This building block is particular in that said at least one core comprises particles of wood and / or plastic and / or plaster and / or glass and / or pebbles and / or brick and / or concrete and / or glass wool and / or rock wool and / or soiled cardboard and / or polystyrene and / or clinker and / or rubber, and in that said envelope is made of a concrete comprising at least 90% by weight of mineral matter.

[0007] Thanks to these provisions, it is possible to recover a large proportion of construction waste, or even all construction waste, as well as other types of waste, and to obtain a building block that is mechanically strong enough to be used in numerous applications. The invention therefore makes it possible to obtain building blocks using a reduced quantity of raw material, and making it possible to reduce the waste taken to landfill, buried and / or incinerated.

[0008] The core may comprise a binder, and the volume content of particles in the core may be between 50 and 80%, which makes it possible to give the building block good mechanical properties while recovering a significant quantity of waste.

[0009] The volume content of core particles in the block can be between 40 and 80%, which makes it possible to give the building block good mechanical properties while recovering a significant quantity of waste.

[0010] The core may comprise particles of at least two different elements from wood, plastic, plaster, glass, pebble, brick, concrete, glass wool, rock wool, soiled cardboard, polystyrene, clinker and rubber, which allows the recovery of a large quantity of waste that is difficult to recover.

[0011] The core may comprise particles of at least five different elements from wood, plastic, plaster, glass, pebble, brick, concrete, glass wool, rock wool, soiled cardboard, polystyrene, clinker and rubber, which allows the recovery of an even greater quantity of waste that is difficult to recover and in particular non-recyclable.

[0012] The particle size can be between 0 and 100 mm, which is an effective embodiment of the invention.

[0013] Said building block may comprise a first face comprising at least one lug, and a second face opposite the first face comprising at least one recess configured to receive a lug of another building block, in order to make said building block stackable, which allows the building block to be used in a simple manner.

[0014] The present invention also comprises a method of manufacturing a building block according to the invention, comprising the following steps: - collection of waste consisting at least in part of wood and / or plastic and / or plaster and / or glass and / or pebbles and / or brick and / or concrete and / or wool of glass and / or rock wool and / or soiled cardboard and / or polystyrene and / or clinker and / or rubber on a construction site and / or an incinerator and / or a used tire collection point and / or a sorting center, - crushing waste to obtain said particles.

[0015] Thanks to these provisions, it is possible to recover a large proportion of construction waste, or even all construction waste, as well as other types of waste, and to obtain a building block that is mechanically strong enough to be used in numerous applications. The invention therefore makes it possible to obtain building blocks using a reduced quantity of raw material, and making it possible to reduce the waste taken to landfill, buried or incinerated.

[0016] Said method may further comprise the following steps: - manufacturing a building block according to the invention, the collection of waste taking place at least partially on a construction site, and the manufacturing taking place on said construction site, - use of the building block to build a wall on said construction site.

[0017] This allows very rapid recovery of construction waste, significantly reducing the energy spent on transporting waste and building blocks.

[0018] The collected waste may comprise at least one used building block according to the invention, which makes it possible to successively recycle the same waste, making it possible to avoid burial and / or landfilling and / or incineration of this waste at the end of the life of the building block.

[0019] The present invention also relates to a method of manufacturing a building block according to the invention, comprising the following steps: - pouring the base of the envelope into the bottom of the mold, - placing at least one separator in the mold, the separator comprising lateral elements defining an interior volume corresponding to the volume of the core, the separator being open at its lower and upper ends, the separator comprising a suspension means located above its lateral elements and being suspended in the mold by said suspension means, so that the lower part of its lateral elements is flush with the top of the base of the casing, - before the base of the casing is dry, pouring the core inside the separator, the core being held in place by the base of the casing and the lateral elements of the separator, - before the base of the envelope is dry, pouring the side walls of the envelope around the side elements of the separator, - removal of the separator from the mold, in order to bring the core into contact with the side walls of the envelope.

[0020] The building block according to the invention can then be produced in a simple and efficient manner, and have good mechanical properties thanks to the adhesion of all its parts linked together. Brief description of the drawings

[0021] The present invention and its advantages will appear better in the following description of several embodiments given as non-limiting examples, with reference to the appended drawings, in which:

[0022] [Fig-1] [Fig.l] is a schematic sectional view of a building block according to a preferred embodiment of the invention,

[0023] [Fig.2] [Fig.2] is a perspective view of the first step of a method of manufacturing a building block according to a preferred embodiment of the invention,

[0024] [Fig.3] [Fig.3] is a perspective view of the second step of the method of the [Fig.2],

[0025] [Fig.4] [Fig.4] is a perspective view of the third step of the method of the [Fig.2],

[0026] [Fig.5] [Fig.5] is a perspective view of the fourth step of the method of the [Fig.2],

[0027] [Fig.6] [Fig.6] is a perspective view of the fifth step of the method of the [Fig.2],

[0028] [Fig.7] [Fig.7] is a perspective view of the sixth step of the method of the [Fig.2],

[0029] [Fig.8] [Fig.8] is a perspective view of the seventh step of the method of the [Fig.2],

[0030] [Fig.9] [Fig.9] is a perspective view of several building blocks manufactured according to the process of [Fig.2], stacked. Description of the embodiments

[0031] With reference to the figures, the building block 1 according to the invention comprises at least one core 2, arranged in a shell 3. The building block 1 may comprise a single core 2, surrounded by a shell 3, or a plurality of cores 2, each surrounded by its own shell 3. If the building block 1 comprises a plurality of cores 2, portions of shell 3 may be common to the cores 2 located next to each other.

[0032] The building block 1 preferably has the shape of a rectangular parallelepiped, but it can take other shapes without departing from the scope of the present invention.

[0033] The core 2 also preferably has the shape of a rectangular parallelepiped, but can take other shapes without departing from the scope of the present invention.

[0034] The envelope 3 may completely surround the core 2, or it may leave the core 2 flush with the building block 1 at one of its faces.

[0035] The core 2 comprises particles 4 made of one or more materials included in the following list: wood, plastic, plaster, glass, pebble, brick, concrete, glass wool, rock wool, soiled cardboard, polystyrene, clinker and rubber. By soiled cardboard is meant here a cardboard which is considered non-recyclable due to the presence of products on this cardboard. By rubber is meant in particular particles from tires of cars, trucks, vans, bicycles, etc.

[0036] The particles 4 of the core 2 may be derived from several elements listed above: preferably at least two different elements, but advantageously at least three, four, five, six, seven or eight of these elements. Indeed, the particles 4 are, in a preferred embodiment of the invention, derived from waste from a construction site, in particular for all of the materials cited with the exception of clinker and rubber. Thus, increasing the number of different materials used for the particles 4 makes it possible to recover a greater proportion of the waste from construction sites. This is why in a particular embodiment of the invention, the core 2 comprises particles 4 made up of at least eight, and preferably nine, ten or even all of the materials cited with the exception of clinker and rubber. Indeed, construction waste is usually recovered for some, and stored in landfills for others.The waste usually recovered is for example scrap metal, uncontaminated cardboard, or certain plastics, which are easily recycled. Preferably, all construction waste that is usually stored in landfills can be used to produce the particles 4 of the building block 1. This concerns, for example, waste that is difficult to recover using known techniques, such as windows with PVC frames, or even class C wood.

[0037] The clinker usually comes from an incinerator, and the rubber from a used tire collection point. The use of one, the other, or both of these materials, which are usually not very recoverable, is also particularly relevant in the context of the present invention, and allows a reduction in waste and a reduction in the carbon footprint of the building blocks.

[0038] Waste from sources other than construction sites, incinerators or used tire collection points can be used to produce the particles 4 used in the building blocks 1. Indeed, a wide variety of waste can be used and the waste can come for example from sorting centers, industrial installations, or any other relevant place.

[0039] The core 4 may also comprise other types of waste, for example ferrous and non-ferrous metal residues, ordinary industrial waste, household waste, production waste, sewage sludge, waste sludge, etc. If the core comprises residues comprising organic matter, it is then preferable for it to comprise a binder 5 making these matters inert, for example by the presence of lime.

[0040] When the particles 4 come from a construction site, the manufacture of the building block 1 and its use, for example to erect a wall, can take place on this same construction site.

[0041] The particles 4 of the core 2 have, for example, a particle size of less than 100 mm, preferably less than 80 mm. These dimensions present a good balance between the energy required to grind the materials, and the homogeneity of the core 4. This particle size can be obtained following one or more grinding steps. In a preferred embodiment of the invention, a first grinding is carried out, to obtain a particle size of less than a value between 70 and 90 mm, for example 80 mm, then a second grinding is carried out to obtain a particle size of less than a value between 10 and 30 mm, for example 20 mm. In this example, the particles 4 will therefore have a particle size of less than 20 mm for certain materials such as plaster, but for other materials such as wood, pieces of which a dimension of up to 100 mm may remain.

[0042] In order to obtain a block 1 according to the invention, the particles 4 can therefore be obtained in the following way:

[0043] - collection of waste consisting at least in part of wood and / or plastic and / or plaster and / or glass and / or pebbles and / or brick and / or concrete and / or glass wool and / or rock wool and / or soiled cardboard and / or polystyrene and / or clinker and / or rubber on a construction site and / or an incinerator and / or a used tire collection point and / or a sorting center, - crushing of the waste in order to obtain said particles 4.

[0044] The collected waste may comprise one or more used building blocks 1. Thus, the building blocks 1 may be recycled several times successively, or even infinitely, further increasing their impact in terms of waste reduction and reduction of the carbon footprint of the building blocks. To facilitate this operation, a distinctive sign may be affixed to certain building blocks 1 during their manufacture, for example referring to the fact that these building blocks 1 are designed to be recyclable, and where can used building blocks 1 are transported for use in the manufacture of new building blocks 1.

[0045] The envelope 3 is made of a concrete whose dry matter comprises at least 90%, preferably at least 95%, by weight of mineral matter. For example, this dry matter is a mixture of at least 90%, preferably at least 95%, cement and sand, the sand being for example of grain size less than 16 mm and being either sand from a quarry or recycled sand. It can however be made of any construction material having the mechanical properties required to give the building block, whatever the nature of the particles 4 of the core 2, sufficient mechanical strength for the use which will be made of the building block 1. This criterion can therefore vary according to the use which is made of the building block 1.

[0046] The core 2 also preferably comprises a binder 5. The binder 5 preferably comprises a mineral binder, such as a cement. The binder 5 may also comprise lime, which has the advantage of neutralizing any organic matter present in the particles 4 of the core 2. The binder 5 may be necessary to obtain a building block 1 having the desired mechanical properties. However, in certain cases, the core 2 may be composed solely of particles 4, possibly additives, but without binder 5, which has the advantage of increasing the content of particles 4 in the building block 1.

[0047] The core 2 may also comprise fillers, for example mineral or biosourced, other than the particles 4.

[0048] The envelope 3 may comprise additives in order to give this element certain properties. The envelope 3 may thus comprise a setting accelerator additive, which is particularly useful when the core comprises particles having a certain moisture content, to accelerate the drying of the building blocks 1 during their manufacture. The envelope 3 may also comprise an air-entraining additive, which makes it possible to increase its resistance to freeze / thaw cycles and to bad weather, which is particularly advantageous in the presence of particles originating from a mixture of materials whose exact composition may vary from one building block 1 to another.

[0049] The envelope 3 may also comprise mechanical reinforcing additives, such as structural fibers, for example based on textile materials, or even a metal frame.

[0050] The envelope 3 may also comprise a water-repellent additive, in order to avoid physical or chemical phenomena which may occur during variation in the humidity level of the core 2 and which may affect the mechanical performance of the building block 1.

[0051] The volume content of the particles 4 in the core 2 is preferably greater than 50%, for example between 50 and 80%, or between 60 and 80%. In certain cases, this value may be greater than 80%, or even reach 100%, when the thickness and strength of the envelope make it possible to use a core 2 without binder 5.

[0052] The volume content of particles 4 of the core 2 in the complete block 1, that is to say taking into account the envelope 3, is preferably greater than 20%, for example between 40 and 80%. Indeed, it has been found that such contents, even with particles 4 from unsorted construction waste, made it possible to obtain blocks 1 which can be used for construction.

[0053] The building block 1 may be a stackable block, which makes it possible to build walls without using mortar between the building blocks 1. To do this, the building block 1 may comprise on a first of its faces at least one lug 6, and on a second of its faces opposite the first face at least one recess configured to receive the lug 6 of another building block 1. The lug 6 has for example the shape of a truncated pyramid with a square base. In a preferred embodiment illustrated in [Fig.9], the first face comprises eight lugs 6 arranged in two rows of four.

[0054] The building block 1 can also be used as a building block. Its dimensions, and the thickness as well as the formulation of the envelope 3 will in this case be adapted.

[0055] The building block 1 may comprise at least one lifting anchor, for example of the Arteon type (registered trademark). The means for fixing the lifting anchor is preferably arranged at the level of the casing 3, the mechanical strength of which is greater than that of the core 2. If the building block 1 comprises lugs 6, the lifting anchor is arranged on the same face as the lugs 6.

[0056] The dimensions of the building block 1 depend on the use for which it is designed.

[0057] The building block 1, particularly in the embodiment in which it is stackable, has for example a length of 150 cm, a width of 60 cm and a height of 60 cm. The thickness of the envelope all around the core 2 is then preferably between 4 and 15 cm, for example 5 cm.

[0058] In other embodiments, for example for use as a concrete block, the thickness of the envelope is for example between 10 and 25 mm.

[0059] In all cases, it is sought to use a minimum thickness of envelope 3 in order to have a maximum content of particles 3 in the building block 1, which avoids using materials whose extraction is expensive and costly for the environment, and which reduces the quantities of waste to be incinerated or buried.

[0060] The building block 1 can be manufactured according to a method comprising the following steps, illustrated in Figures 2 to 8:

[0061] - casting of the base 3a of the envelope 3 at the bottom of a mold 7. The state of the process following this step is illustrated in [Fig.2], - placing at least one separator 8 in the mold 7. The separator 8 comprises lateral elements defining an interior volume corresponding to the volume of the core 2. When it is in position in the mold 7, the separator 8 is open at its lower and upper ends. In a preferred embodiment, an example of which is illustrated in Figures 3 to 6, the separator 8 comprises four lateral elements consisting of vertical plates, in order to form a rectangular parallelepiped open on its lower and upper faces. Other shapes than a rectangular parallelepiped can be used. In addition, other configurations are possible, in particular one or more separators 8 can be used to obtain a plurality of cores 2.The separator 8 is suspended in the mold 7 by a suspension means 9 located above its lateral elements, so that the lower part of its lateral elements is flush with the first wall of the casing 3. The suspension means 9 is for example constituted, as illustrated in Figures 3 to 6, by a plurality of loops fixed to the top of the lateral elements of the separator 8. This suspension from above makes it possible in particular to cast the core 2 and the casing 3 with the separator 8 in place in the mold 7, then to remove the separator 8 before drying without modifying the relative positions of the core 2 and the casing 3 in the mold 7. The state of the process following this step is illustrated in [Fig. 3], - casting the lateral walls 3b of the casing 3 around the lateral elements of the separator 8.This step is preferably carried out before the drying of the base 3a of the casing 3, so that the lower part of the side walls 3b of the casing 3 and the upper part of the base 3a of the casing 3 dry against each other, which thus makes it possible to obtain a strong adhesion between these parts, reinforcing the mechanical strength of the block 1. The state of the process following this step is illustrated in [Fig. 4], - casting the core 2 inside the separator 8, the core being held in place by the base 3a of the casing 3 and the side elements of the separator. This step is preferably carried out before the drying of the base 3a of the casing 3, so that the lower part of the core 2 and the upper part of the base 3a of the casing 3 dry against each other, which thus makes it possible to obtain a strong adhesion between these parts, reinforcing the mechanical strength of the block 1.This step can be carried out before or after the step described above of casting the side walls 3b of the casing 3. The state of the process following this step is illustrated in [Fig.5], - removal of the separator 8 from the mold 1, by an upward translational movement, in order to bring the core 2 into contact with the side walls of the casing 3. The means . suspension 9 can then be used as a means of lifting the separator 8. This step is preferably carried out before drying the core 2 and before drying the side walls of the casing 3, so that the inner part of the side walls of the casing 3 and the outer part of the core 2 dry against each other, which thus makes it possible to obtain a strong adhesion between these parts, reinforcing the mechanical resistance of the block 1. The state of the process following this step is illustrated in [Fig.6], - possibly casting the top 3c of the casing 3, in order to cover the core. This step is optional.This step is preferably carried out before drying the core 2 and before drying the side walls of the casing 3, so that the upper part of the side walls of the casing 3 and the upper part of the core 2 dry against each other, which thus makes it possible to obtain a strong adhesion between these parts, reinforcing the mechanical resistance of the block 1. The state of the process following this step is illustrated in [Fig.7].

[0062] It should be noted that the above terms “base”, “side walls” and “top”, relating to the envelope 3, designate parts of the envelope 3 by their position during the manufacturing process. Indeed, the building block 1 can be manufactured on one of its side walls, as illustrated in Figures 2 to 8. In this case, when using the building block 1, the building block 1 is rotated 90° along a horizontal axis relative to its manufacture. Thus the elements which were, during manufacture, the base and the top of the envelope 3 become, when using the building block 1, side walls, and the side walls become for two of them the base and the top of the envelope 3.

[0063] At the end of these steps, and when the core 2 and / or the casing 3 are sufficiently dry, the mold 7 can be removed. The mold 7 can be a single-piece mold, or a mold made of several parts. In the example illustrated in Figures 2 to 8, the mold 7 comprises two parts. This embodiment is the simplest to implement when the building block comprises lugs 6 and corresponding recesses. In fact, it allows the building block to be manufactured on one of its sides, and then the face with the lugs 6 and the face with the recesses to be demolded separately.

[0064] After removal from the mold, the building block undergoes a drying step. This drying can be done in the open air, or by any means known to those skilled in the art. When it is carried out in the open air, the drying time is for example between 3 and 7 days, and in some cases up to 21 days.

[0065] The present invention is of course not limited to the embodiments described but extends to any modification and variant obvious to a person skilled in the art within the limits of the appended claims. In addition, the characteristics techniques of the different embodiments and variants mentioned above can be, in whole or in part, combined with each other.

Claims

Claims

1. Building block (1) comprising at least one core (2) and a casing (3), said at least one core (2) being arranged inside said casing (3), characterized in that said at least one core (2) comprises particles (4) of wood and / or plastic and / or plaster and / or glass and / or pebbles and / or brick and / or concrete and / or glass wool and / or rock wool and / or soiled cardboard and / or polystyrene and / or clinker and / or rubber, and in that said casing (3) is made of a concrete comprising at least 90% by weight of mineral matter.

2. Building block (1) according to claim 1, characterized in that the core (2) comprises a binder (5), and the volume content of particles (4) in the core (2) is between 50 and 80%.

3. Building block according to one of claims 1 to 2, characterized in that the volume content of the particles (4) of the core (2) in the building block (1) is between 40 and 80%.

4. Building block (1) according to one of claims 1 to 3, characterized in that the core (2) comprises particles (4) of at least two different elements among wood, plastic, plaster, glass, pebble, brick, concrete, glass wool, rock wool, soiled cardboard, polystyrene, clinker and rubber.

5. Building block (1) according to one of claims 1 to 4, characterized in that the core (2) comprises particles of at least five different elements from wood, plastic, plaster, glass, pebble, brick, concrete, glass wool, rock wool, soiled cardboard, polystyrene, clinker and rubber.

6. Building block (1) according to one of claims 1 to 5, characterized in that the particle size of the particles (4) is between 0 and 100 mm.

7. Building block (1) according to one of claims 1 to 6, comprising a first face comprising at least one lug (6), and a second face opposite the first face comprising at least one recess configured to receive a lug (6) of another building block, in order to make said building block (1) stackable.

8. A method of manufacturing a building block (1) according to one of claims 1 to 7, comprising the following steps: - collection of waste consisting at least in part of wood and / or plastic and / or plaster and / or glass and / or pebbles and / or brick and / or concrete and / or glass wool and / or rock wool and / or soiled cardboard and / or polystyrene and / or clinker and / or rubber on a construction site and / or an incinerator and / or a used tire collection point and / or a sorting center, - crushing of the waste in order to obtain said particles (4).

9. A method of manufacturing a building block (1) according to claim 8, wherein the collected waste comprises at least one used building block (1) according to one of claims 1 to 7.

10. A method of manufacturing and using a building block (1) according to one of claims 1 to 7, further comprising the following steps: - manufacturing a building block (1) according to one of claims 8 to 9, the collection of waste taking place at least partially on a construction site, and the manufacturing taking place on said construction site, - using the building block (1) to make a wall on said construction site.

11. A method of manufacturing a building block (1) according to one of claims 1 to 7, comprising the following steps: - casting the base (3a) of the casing (3) at the bottom of a mold (7), - placing at least one separator (8) in the mold (7), the separator (8) comprising lateral elements defining an interior volume corresponding to the volume of the core (2), the separator (8) being open at its lower and upper ends, the separator (8) comprising a suspension means (9) located above its lateral elements and being suspended in the mold (7) by said suspension means (9), so that the lower part of its lateral elements is flush with the top of the base (3a) of the casing (3), - before the base (3a) of the casing (3) is dry, casting the side walls of the casing (3) around the lateral elements of the separator (8), - before the base (3a) of the casing (3) is dry,casting the core (2) inside the separator (8), the core (2) being held, 14 in place by the base (3a) of the casing (3) and the side elements of the separator (8), - removal of the separator (8) from the mold (7), in order to bring the core (2) into contact with the side walls of the casing (3).

12. A method of manufacturing a building block according to one of claims 8 to 10 and claim 11.