Improved polymer composition

Abstract

The present invention provides polymeric compositions that are flame retardant and produce less smoke when exposed to heat or flame.

Description

[Technical field]

[0001] The present invention relates to the field of polymer blends, in particular flame retardant polyesters, in particular copolyesters (e.g. copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrenic elastomers, thermoplastic polyurethanes and thermoplastic vulcanizates. [Background technology]

[0002] Copolyetheresters are a family of elastomeric polyesters with hard segments containing polyester blocks and soft segments containing long chain polyether diols. They are widely used in applications requiring elasticity and stretchability.

[0003] Typical copolyetheresters are prepared by reacting one or more diacid moieties with a short chain diol and a long chain polyether diol. The copolyetheresters exhibit excellent elasticity, retention of mechanical properties at low temperatures and good fatigue performance.

[0004] There is a continuing need for halogen-free fire-resistant ("NHFR") copolyetheresters. Dialkylphosphinate salts are well-known non-halogenated flame-retardant molecules. U.S. Patent No. 7,420,007 [Clariant Produkte (Deutsch) GmbH] describes the following formula (I):

[0005] [ka]

[0006] (In the formula, R 1 , R 2 are the same or different and are linear or branched C1-C6 alkyl; M is Mg, Ca, Al, Sb, Sn, Ge, Ti, Fe, Zr, Zn, Ce, Bi, Sr, Mn, Li, Na, K, and / or a protonated nitrogen base; m is 1 to 4. Dialkylphosphinate salts of the formula have been described for use as flame retardants in many different polymers, such as polyetheresters.

[0007] US2013 / 0190432 describes the use of aluminum diethylphosphinate together with an aluminum salt of phosphorous acid as a flame retardant combination in nylon-6,6, nylon-6T / 6,6, nylon-4,6, copolyetheresters and PBT.

[0008] U.S. Patent No. 7,439,288 describes titanium diethylphosphinate which is said to be useful as a flame retardant in blends or polyblends of the type typified by high impact polystyrene, polyphenylene ether, polyamide, polyester, polycarbonate, or ABS (acrylonitrile-butadiene-styrene), or PC / ABS (polycarbonate / acrylonitrile-butadiene styrene), or PPE / HIPS (polyphenylene ether / HI polystyrene).

[0009] Unfortunately, while the use of flame retardants in polymer resins can significantly reduce flammability, they can also produce more smoke when exposed to heat or flame, which is a concern because smoke can significantly affect fire damage and mortality.

[0010] There is a need for a combination of resins and flame retardants that not only reduces flammability but also reduces smoke generation upon exposure to heat and / or flame. Summary of the Invention

[0011] In a first aspect, the present invention provides a method for producing a composition comprising the steps of: (1) at least one polymer selected from polyesters (e.g., copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrene-based elastomers, thermoplastic polyurethanes, and thermoplastic vulcanizates; (2) aluminum diethylphosphinate, (3) titanium diethylphosphinate salt; and The present invention provides a flame retardant polymer composition comprising:

[0012] In a second aspect, the present invention provides a method for producing a pharmaceutical composition comprising the steps of: (1) at least one polymer selected from polyesters (e.g., copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrene-based elastomers, thermoplastic polyurethanes, and thermoplastic vulcanizates; (2) aluminum diethylphosphinate, (3) titanium diethylphosphinate salt; and Titanium diethylphosphinate d 50 (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer instrument) greater than 35 microns, the concentration of aluminum diethylphosphinate is 15 wt% or less, based on the total weight of the composition.

[0013] In a third aspect, the present invention provides a method for producing a pharmaceutical composition comprising the steps of: (1) at least one copolyetherester; (2) aluminum diethylphosphinate, (3) titanium diethylphosphinate salt; and Titanium diethylphosphinate salt d 50(volume %, in acetone, as measured using a laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer) greater than 35 microns, the concentration of aluminum diethylphosphinate is 15 wt% or less, based on the total weight of the composition.

[0014] In a fourth aspect, the present invention provides a method for producing a pharmaceutical composition comprising the steps of: (1) at least one polymer selected from polyesters (e.g., copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrene-based elastomers, thermoplastic polyurethanes, and thermoplastic vulcanizates; (2) aluminum diethylphosphinate, (3) titanium diethylphosphinate salt; and Titanium diethylphosphinate salt d 50 (volume %, in acetone, as measured using a laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer) greater than 35 microns, the concentration of aluminum diethylphosphinate is 15 wt% or less, based on the total weight of the composition.

[0015] In a fifth aspect, the present invention provides a polymerizable composition comprising an optically or electrically conductive core and (1) at least one polymer selected from polyesters (e.g., copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrene-based elastomers, thermoplastic polyurethanes, thermoplastic vulcanizates, and mixtures thereof; (2) aluminum diethylphosphinate, (3) titanium diethylphosphinate salt; and Titanium diethylphosphinate salt d 50(volume %, in acetone, as measured using a laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer) greater than 35 microns, the concentration of aluminum diethylphosphinate is 15 wt% or less, based on the total weight of the composition.

[0016] In a sixth aspect, the present invention provides a method of making a composition of the present invention comprising melt mixing the recited ingredients in an extruder. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0017] Definitions and Abbreviations PBT: Poly(butylene terephthalate) PTMEG: Polytetramethylene ether glycol Copolyetherester or TPC: A thermoplastic elastomer obtained from the reaction of at least one diol, at least one diacid, and at least one poly(alkylene oxide) diol. DEPAl: Aluminum diethylphosphinate DEPTi: Titanium salts of diethylphosphinate, including species represented by the formula:

[0018] [ka]

[0019] (In the formula, x is 0 to 1.9.) DEPZn: Zinc diethylphosphinate Phosphite: as used herein is synonymous with "salts of phosphorous acid" or "salts of phosphonic acid" of aluminum and / or zinc.

[0020] The inventors have surprisingly found that blending polymers selected from polyesters, (e.g. copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrenic elastomers, thermoplastic polyurethanes and thermoplastic vulcanizates, in particular copolyetheresters, with DEPAl and DEPTi results in compositions that have good flame retardant properties and reduced smoke generation when exposed to heat and / or flame.

[0021] DEPAl and DEPTi are known to impart flame retardancy to polymer formulations. A well-recognized problem with adding flame retardants to polymer resins is that while they improve the flame retardancy of the polymer resin, they generally increase smoke generation. The inventors have found that by using a mixture of DEPAl and DEPTi, good flame retardancy can be achieved while maintaining an acceptable level of smoke generation. Polymer Resin The formulations of the present invention comprise at least one polymer selected from polyesters, (e.g., copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrenic elastomers, thermoplastic polyurethanes, and thermoplastic vulcanizates.

[0022] Preferred polymers are polyesters, especially copolyetheresters, and polyamides, with copolyetheresters being especially preferred. Suitable polyesters may include those selected from PET, PBT, copolyetheresters, and mixtures thereof.

[0023] Suitable polyamides include those selected from PA6, PA66, PA610, PA66 / 610, PA11, PA12, PA612, PA46, PA6T66, PA6 / 66, PA6 / 69, PA1010, PA1012 and mixtures thereof. Particularly preferred are PA66 and PA6T66.

[0024] Copolyetheresters suitable for the compositions of the present invention are polymers made by reacting a C2-C6 diol with an aromatic diacid moiety and a poly(alkylene oxide) diol.

[0025] The poly(alkylene oxide) diol is preferably selected from poly(ethylene oxide) diol, poly(propylene oxide) diol, poly(tetramethylene oxide) diol ("PTMEG"), and mixtures thereof. The poly(propylene oxide) diol, poly(tetramethylene oxide) diol may be linear or branched. If branched at the carbon containing the terminal hydroxyl, they are preferably end-capped with ethylene glycol or poly(ethylene oxide) diol. Particularly preferred are poly(propylene oxide) diol and poly(tetramethylene oxide) diol ("PTMEG"), and mixtures thereof, with PTMEG being more particularly preferred.

[0026] The C2-C6 diol is preferably selected from ethylene glycol, propylene glycol, butylene glycol, and mixtures thereof, with butylene glycol being more particularly preferred.

[0027] Preferably, the aromatic diacid is selected from terephthalate, isoterephthalate, and mixtures thereof, including the free acid, salts, and esters, with terephthalate being especially preferred.

[0028] Particularly preferred copolyetheresters are: 1. A copolyetherester made from butylene diol, terephthalate and PTMEG; 2. A copolyetherester made from butylene diol, terephthalate and poly(propylene oxide) diol; 3. A copolyetherester made from propylene diol, terephthalate and PTMEG; 4. Copolyetheresters made from propylene diol, terephthalate and poly(propylene oxide) diol; is selected from.

[0029] Particularly preferred are copolyetheresters made from butylene diol, terephthalate and PTMEG. The softness of the copolyetheresters is influenced by the chain length (ie, molecular weight) of the poly(alkylene oxide) diol and the relative amount of poly(alkylene oxide) diol used to make the polymer.

[0030] In a preferred embodiment, the poly(alkylene oxide) diol has a molecular weight of about 2000 g / mol. In another preferred embodiment, the poly(alkylene oxide) diol constitutes 40 wt % to 80 wt % of the copolyetherester, more preferably 50 to 75 wt %, and especially preferably 72.5 wt %, based on the total weight of the copolyetherester.

[0031] In a particularly preferred embodiment, the copolyetherester comprises 40 wt. % to 80 wt. %, more preferably 50 to 75 wt. %, and especially preferably 72.5 wt. %, of a poly(alkylene oxide) diol having a molecular weight of about 2000 g / mol, based on the total weight of the copolyetherester.

[0032] A particularly preferred copolyetherester comprises about 72.5 weight percent of polytetramethylene oxide, preferably having an average molecular weight of about 2000 g / mol, as the polyether block segment, the weight percent being based on the total weight of the copolyetherester elastomer, and the short chain ester units of the copolyetherester being polybutylene terephthalate segments. Phosphinate In addition to at least one polyester (e.g., copolyetherester, copolyesterester), polyamide, polyamide elastomer, thermoplastic polyolefin-based elastomer, styrenic elastomer, thermoplastic polyurethane, and thermoplastic vulcanizate, the compositions of the present invention include aluminum diethylphosphinate ("DEPAl") and titanium diethylphosphinate ("DEPTi").

[0033] The total concentration of the phosphinate in the composition is preferably 5 to 50 wt %, more preferably 10 to 40 wt %, and particularly preferably 10 to 25 wt %, based on the total weight of the copolyetherester composition.

[0034] If the total phosphinate loading exceeds 40 wt%, the mechanical properties may be poor. In some applications, sufficient mechanical properties may be obtained even at such high loadings, but it is generally preferred that the total phosphinate concentration does not exceed 40 wt%.

[0035] In a preferred embodiment, the DEPAl has a D of 10 microns or less, more preferably 8 microns or less. 95 (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer2000 particle size analyzer).

[0036] DEPTi includes the titanium salt of diethylphosphinate of the formula:

[0037] [ka]

[0038] (In the formula, x is a number from 0 to 1.9.) In a preferred embodiment, x is 1-1.05, which means that the ratio of Ti to diethylphosphinate is 1.9-2.

[0039] Furthermore, in a preferred embodiment, DEPTi has a D of 35 microns or less, more preferably 25 microns or less. 50 (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer2000 particle size analyzer).

[0040] In another preferred embodiment, the DEPAl has a D 95 (volume %, in acetone, measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer) and DEPTi has a D of 35 microns or less. 50 (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer2000 particle size analyzer).

[0041] Titanium diethylphosphinate salt D 50 (volume %, in acetone, as measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer) greater than 35 microns, the concentration of aluminum diethylphosphinate is less than or equal to 15 wt%, based on the total weight of the composition.

[0042] The concentration of DEPAl in the composition is preferably 5 to 25 wt %, more preferably 5 to 15 wt %, based on the total weight of the composition. The concentration of DEPTi in the composition is preferably 1 to 15 wt %, more preferably 5 to 12 wt %, based on the total weight of the composition. Phosphite The compositions of the present invention may further comprise an aluminum salt of phosphorous acid, a zinc salt of phosphorous acid, or both.

[0043] Phosphorous acid has the following tautomers:

[0044] [ka]

[0045] Aluminum salts of phosphorous acid are also called aluminum phosphites. Preferred aluminum phosphites are those having CAS numbers [15099-32-8], [119103-85-4], [220689-59-8], [CAS56287-23-1], [156024-71-4], [71449-76-8] and [15099-32-8]. Particularly preferred are aluminum phosphites of the type Al2(HPO3)3*0.1-30Al2O3*0-50H2O, more preferably of the type Al2(HPO3)3*0.2-20Al2O3*0-50H2O, and most preferably of the type Al2(HPO3)3*1-3Al2O3*0-50H2O.

[0046] Particularly preferred is a mixture of aluminum phosphite and aluminum hydroxide having a composition of 5-95% by weight Al2(HPO3)3*nH2O and 95-5% by weight Al(OH)3, more preferably 10-90% by weight Al2(HPO3)3*nH2O and 90-10% by weight Al(OH)3, and most preferably 35-65% by weight Al2(HPO3)3*nH2O and 65-35% by weight Al(OH)3, where n=0-4 in each case.

[0047] Preferred are aluminum phosphites having CAS numbers [15099-32-8], [119103-85-4], [220689-59-8], [56287-23-1], [156024-71-4], [71449-76-8] and [15099-32-8]. Particularly preferred is aluminum phosphite having CAS number [CAS56287-23-1].

[0048] Particularly preferred are aluminum phosphites of the formula: [HP(=O)O2] 2- 3Al 3+ 2 Also, aluminum phosphite [Al(H2PO3)3], secondary aluminum phosphite [Al2(HPO3)3], basic aluminum phosphite [Al(OH)(H2PO3)2·2H2O], aluminum phosphite tetrahydrate [Al2(HPO3)3·4H2O], aluminum phosphonate, Al7(HPO3)9(OH)6(1,6-hexanediamine) 1.5 ·12H2O, Al2(HPO3)3·xAl2O3·nH2O (x=2.27~1) and / or Al4H6P 16 O 18 and aluminum phosphites of formula (IV), (V) and / or (VI): Al2(HPO3)3x(H2O) q (IV) (wherein q is 0 to 4); Al 2.00 M z (HPO3) y (OH) v x(H2O) w (V) (wherein M is an alkali metal cation, z is 0.01 to 1.5, y is 2.63 to 3.5, v is 0 to 2, and w is 0 to 4); Al 2.00 (HPO3) u (H2PO3) t ×(H2O) s (VI) (wherein u is 2 to 2.99, t is 2 to 0.01, and s is 0 to 4) is also preferred.

[0049] Furthermore, mixtures of the aluminum phosphite of formula (IV) with sparingly soluble aluminum salts having nitrogen-free counterions, mixtures of the aluminum phosphite of formula (VI) with aluminum salts, mixtures of aluminum phosphite [Al(H2PO3)3] with secondary aluminum phosphite [Al2(HPO3)3], basic aluminum phosphite [Al(OH)(H2PO3)2·2H2O], aluminum phosphite tetrahydrate [Al2(HPO3)3·4H2O], aluminum phosphonate, Al7(HPO3)9(OH)6(1,6-hexadiamine)1.5 ·12H2O, Al2(HPO3)3·xAl2O3·nH2O (x=2.27~1) and / or Al4H6P 16 O 18 is also preferred.

[0050] In a preferred embodiment, the phosphite has a D of 10 microns or less. 95 (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer2000 particle size analyzer).

[0051] In a preferred embodiment, the aluminum phosphite has a D of 10 microns or less. 95 (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer2000 particle size analyzer).

[0052] Particularly preferred is a D of 10 microns or less. 95 (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer) aluminum phosphite [56287-23-1].

[0053] The zinc salt of phosphorous acid is referred to as zinc phosphite in this specification.Preferred are zinc phosphites having CAS numbers [14332-59-3], [114332-59-3], [1431544-62-5], [14902-88-6], [52385-12-3] and [51728-08-6].Particularly preferred is zinc phosphite having CAS number [CAS14332-59-3] as shown below.

[0054] [ka]

[0055] In a preferred embodiment, the zinc phosphite has a D of 10 microns or less. 95(% by volume, in acetone, measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer). Alternatively, the zinc phosphite preferably has a particle size of 0.1 to 100 microns, particularly preferably 0.1 to 30 microns.

[0056] Preferred zinc phosphites include (ZnHPO), Zn(HPO), Zn / 3HPO, zinc phosphite hydrate, zinc pyrophosphite (ZnHPO), Zinc 1+x HPO3(OH) 2x Zinc 1-x Na 2x HPO4 (wherein x=0 to 0.25) can be mentioned.

[0057] Particularly preferred is a D of 10 microns or less. 95 (volume %, in acetone, measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer) zinc phosphite [14332-59-3].

[0058] Particularly preferred is a zinc phosphite represented by the formula: [HP(=O)O2] 2- Zinc 2+ In the preferred compositions of the present invention, aluminum phosphite [CAS 56287-23-1] and zinc phosphite [CAS 14332-59-3] are used.

[0059] In a preferred composition of the invention, a mixture of aluminum phosphite and zinc phosphite having the formula: [HP(=O)O2] 2- Zinc 2+ [HP(=O)O2] 2- 3Al 3+ 2 The total phosphite concentration is 0.1-20 wt%, more preferably 2-20 wt%, and more particularly preferably 2.5-10 wt% or less, based on the total weight of the copolyetherester composition. If the total weight of the phosphites exceeds 10 wt%, a good smoke reduction effect is obtained, but the flame retardant properties of the composition are impaired, which may make it unsuitable for certain applications. In a preferred embodiment, the total phosphite concentration is 2.5-10 wt%, based on the total weight of the composition.

[0060] In a preferred embodiment, the composition comprises 2.5 to 10 wt % of aluminum phosphite, in particular aluminum phosphite [CAS56287-23-1]. In another preferred embodiment, the composition comprises 2.5 to 10 wt. % zinc phosphite, in particular zinc phosphite [CAS14332-59-3]. Synergists containing nitrogen and / or phosphorus The composition of the present invention may further comprise at least one nitrogen-containing synergist and / or phosphorus-containing flame retardant and / or nitrogen-containing flame retardant. More preferably, the composition further comprises at least one melamine derivative selected from melamine salts with organic or inorganic acids and mixtures thereof. More particularly preferably, the composition of the present invention further comprises at least one component selected from salts of melamine with boric acid, cyanuric acid, phosphoric acid and / or pyrophosphoric acid / polyphosphoric acid and mixtures thereof. Particularly preferred is melamine pyrophosphate.

[0061] Also preferred are melem, melam, melon, dimelamine pyrophosphate, melamine polyphosphate, melem polyphosphate, melam polyphosphate, melon polyphosphate, and mixtures and salts thereof.

[0062] The nitrogen or phosphorus containing synergists preferably have a D of less than 20 microns, more preferably less than 18 microns. 50 has. Particularly preferred are Ds of less than 20 microns, more preferably less than 18 microns. 50It is a melamine pyrophosphate having the formula:

[0063] When present, the nitrogen and / or phosphorus containing synergists are preferably present at 2 to 10 wt%, more preferably 3 to 8 wt%, based on the total weight of the composition. In a preferred embodiment, melamine pyrophosphate is used. In a more preferred embodiment, the melamine pyrophosphate is used in an amount of 2 to 10 wt%, more preferably 3 to 8 wt%, based on the total weight of the composition. Other Ingredients Some particularly preferred compositions contain other optional additives such as antioxidants, heat stabilizers, UV stabilizers, mineral fillers, glass fibers, colorants, lubricants, plasticizers, impact modifiers, and the like.

[0064] In particular, the compositions of the present invention may include fillers and / or reinforcing agents such as calcium carbonate, silica, glass fibers, wollastonite, talc, kaolin, mica, barium sulfate, metal oxides and / or hydroxides, carbon black, zeolites and graphite.

[0065] The compositions of the present invention may further comprise an antioxidant, such as a phosphite and / or a phenolic antioxidant. Examples of antioxidants include alkylated monophenols, such as 2,6-di-tert-butyl-4-methylphenol; 1,2-alkylthiomethylphenols, such as 2,4-di-octylthiomethyl-6-tert-butylphenol; hydroquinone and alkylated hydroquinones, such as 2,6-di-tert-butyl-4-methoxyphenol; tocopherols, such as α-β-γ- and δ-tocopherol, and mixtures thereof (vitamin E); hydroxylated thiodiphenyl ethers, such as 2,2′-thio-bis-(6-tert-butyl-4-methylphenol), 2,2′-thio-bis-(4-octylphenol), 4,4′-thio-bis-(6-tert-butyl-3-methylphenol), 4,4′-thio-bis(6-tert-butyl-2-methylphenol), 4,4′-thio- Bis(3,6-di-sec-amylphenol), 4,4'-bis(2,6-dimethyl-4-hydroxyphenyl) disulfide; alkylidene bisphenols such as 2,2'-methylenebis(6-tert-butyl-4-methylphenol; O-, N- and S-benzyl compounds such as 3,5,3',5'-tetra-tert-butyl-4,4'-dihydroxydi-benzyl ether; hydroxybenzylated malonates such as dioctadecyl-2,2-bis-(3,5-di-tert-butyl-2-hydroxybenzyl)malonate; hydroxybenzyl aromatic compounds such as 1,3,5-tris-(3,5-di-tert-butyl)-4-hydroxybenzyl)-2,4,6-trimethylbenzene, 1,4-bis(3,5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetramethylbenzene 2,4,6-tris-(3,5-di-tert-butyl-4-hydroxybenzyl)-phenol; triazine compounds such as 2,4-bis-octylmercapto-6(3,5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine; benzyl phosphonates such as dimethyl 2,5-di-tert-butyl-4-hydroxybenzylphosphonate;Acylaminophenols, 4-hydroxylauric acid amide, 4-hydroxystearic acid anilide, N-(3,5-di-tert-butyl-4-hydroxyphenyl)-carbamic acid octyl ester;β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with monohydric or polyhydric alcohols;β-(5-tert-butyl-4-hydroxy-3-methylphenyl)propionic acid with monohydric or polyhydric alcohols;β-(3,5-dicyclohexyl-4-hydroxyphenyl)propionic acid with monohydric or polyhydric alcohols Esters; esters of 3,5-di-tert-butyl-4-hydroxyphenylacetic acid with monohydric or polyhydric alcohols; amides of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid, such as N,N'-bis-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hexamethylenediamine, N,N'-bis-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-trimethylenediamine, and N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazine;

[0066] Some specific examples of antioxidants include tris(2,4-di-tert-butylphenyl)phosphite (Irgafos® 168), N,N'-1,6-hexanediylbis[3,5-bis(1,1-dimethylethyl)-4-hydroxyphenylpropanamide] (Irganox® 1098), mixtures of Irgafos® 168 and Irganox® 1098 (such mixtures are particularly suitable for polyamides such as PA66), N,N' -1,6-hexanediylbis[3,5-bis(1,1-dimethylethyl)-4-hydroxyphenylpropanamide] (Ultranox® 626), octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate (Irganox® 1076), and mixtures of Ultranox® 626 and Irganox® 1076 (such mixtures are particularly suitable for polyesters such as PBT).

[0067] The compositions of the present invention may contain UV absorbers and light stabilizers, such as 2-(2'-hydroxy-5'-methylphenyl)benzotriazole; 2-hydroxybenzophenones, such as 4-hydroxy, 4-methoxy, 4-octoxy, 4-decyloxy-, 4-dodecyloxy-, 4-benzyloxy-, 4,2',4'-trihydroxy-, 2'hydroxy-4,4'-dimethoxy-derivatives; optionally substituted esters of benzoic acid, such as 4-tert-butyl-phenylsalicylate, phenylsalicylate, octylphenylsalicylate, dibenzoylresorcinol, bis(4-tert-butylbenzoyl)resorcinol, benzoylresorcinol, 3,5-di-tert-butyl-4-hydroxybenzoic acid-2,4-diphenylsalicylate, benzoylresorcinol ... ,4-di-tert-butylphenyl ester, 3,5-di-tert-butyl-4-hydroxybenzoic acid hexadecyl ester, 3,5-di-tert-butyl-4-hydroxybenzoic acid octadecyl ester, 3,5-di-tert-butyl-4-hydroxybenzoic acid-2-methyl-4,6-di-tert-butylphenyl ester; acrylates such as α-cyano-β,β-diphenylacrylic acid ethyl ester or -isooctyl ester, α-carbomethoxycinnamate, α-cyano-β-methyl-p-methoxycinnamate or butyl ester, α-carbomethoxy-p-methoxycinnamic acid methyl ester, N-(β-carbomethoxy-β-cyanovinyl)-2-methyl-indoline.

[0068] Suitable polyamide stabilizers are, for example, copper salts in combination with iodides and / or phosphorus compounds, and salts of divalent manganese. Suitable basic costabilizers are melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali and alkaline earth salts of higher fatty acids, such as Ca stearate, Zn stearate, Mg behenate, Mg stearate, Na ricinoleate, K palmitate, antimony catecholate or tin catecholate.

[0069] Suitable nucleating agents are, for example, 4-tert-butylbenzoic acid, adipic acid, diphenylacetic acid and the like. As further flame retardants, the composition may contain aryl phosphates, organic phosphonates, salts of hypophosphorous acid and red phosphorus.

[0070] Examples of other additives include plasticizers, expandable graphite, emulsifiers, pigments, fluorescent whitening agents, flame retardants, antistatic agents, and propellants. Examples of the Preferred Embodiments Some preferred compositions of the present invention are given below, where wt% is based on the total weight of the composition. 1. A preferred composition of the present invention comprises (1) at least one polyester (e.g., copolyetherester, copolyesterester), polyamide, polyamide elastomer, thermoplastic polyolefin-based elastomer, styrenic elastomer, thermoplastic polyurethane, and thermoplastic vulcanizate; (2) DEPAl and (3) DEPTi and and the concentration of DEPAl(2)+DEPTi(3) is 8-30 wt %, based on the total weight of the composition. 2. (1) at least one copolyetherester; (2) DEPAl and (3) DEPTi and (4) an aluminum salt of phosphorous acid, a zinc salt of phosphorous acid, or both; (5) a nitrogen-containing synergist; and 2. The composition of embodiment 1, comprising: 3. (1) at least one copolyetherester; (2) DEPAl and (3) DEPTi and (4) a zinc salt of phosphorous acid; (5) a nitrogen-containing synergist; and 3. The composition of embodiment 1 or 2, comprising: 4. (1) at least one copolyetherester; (2) DEPAl and (3) DEPTi and (4) an aluminum salt of phosphorous acid, a zinc salt of phosphorous acid, or both; (5) a nitrogen-containing synergist which is melamine pyrophosphate; and 4. The composition of any one of embodiments 1 to 3, comprising: 5. (1) at least one copolyetherester; (2) DEPAl and (3) DEPTi and (4) a zinc salt of phosphorous acid; (5) a nitrogen-containing synergist which is melamine pyrophosphate; and 5. The composition of any one of embodiments 1 to 4, comprising: 6. (1) at least one copolyetherester; (2) DEPAl and (3) DEPTi and (4) an aluminum salt of phosphorous acid, a zinc salt of phosphorous acid, or both; 6. The composition of any one of embodiments 1 to 5, comprising: 7. 7. The composition of any one of the preceding embodiments, wherein DEPAl is present at 5-50 wt.%, based on the total weight of the composition. 8. 8. The composition of any one of the preceding embodiments, wherein DEPTi is present in an amount of 5-50 wt%, based on the total weight of the composition. 9. 9. The composition of any one of the preceding embodiments, wherein DEPAl is present at 5-50 wt.% and DEPTi is present at 5-50 wt.%, based on the total weight of the composition. 10. 10. The composition of any one of the preceding embodiments, wherein the concentration of DEPAl is 5-25 wt.%, based on the total weight of the composition. 11. 11. The composition of any one of the preceding embodiments, wherein the concentration of DEPTi is 1-15 wt%, based on the total weight of the composition. 12. DEPAl is 10 microns or less D 95 12. The composition of any one of the preceding claims, having a particle size distribution of 0.1 to 0.5% by volume in acetone, as measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer. 13. DEPTi is 35 microns or less D 50 13. The composition of any one of the preceding claims, having a particle size distribution of 0.1 to 0.5% by volume in acetone as measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer. 14. 14. The composition of any one of the preceding claims, wherein the at least one copolyetherester is selected from a polymer made by reacting a C2-C6 diol with an aromatic diacid moiety and a poly(alkylene oxide) diol. 15. 15. The composition of any one of the preceding embodiments, further comprising an aluminum salt of phosphorous acid, a zinc salt of phosphorous acid, or both. 16. 16. The composition of any one of the preceding claims, further comprising an aluminum phosphite having a CAS number [CAS56287-23-1], a zinc phosphite having a CAS number [CAS14332-59-3], or a mixture thereof. 17. Aluminum phosphite is D below 10 microns 95 17. The composition of any one of the preceding claims, having a particle size distribution of 0.1 to 0.2 mm / s (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer). 18. Zinc phosphite is D below 10 microns 9518. The composition of any one of the preceding claims, having a particle size distribution of 0.1 to 0.2 mm / s (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer). 19. 19. The composition of any one of the preceding embodiments, wherein the total phosphite concentration is 0.1 to 20 wt%, based on the total weight of the composition. 20. 20. The composition of any one of the preceding embodiments, wherein the ratio of DEPAl / DEPTi is 1 or less. twenty one. 21. The composition according to any one of the preceding embodiments, wherein the ratio of DEPAl / DEPTi is from 0.5 to 1. twenty two. 22. The composition of any one of the preceding embodiments, further comprising a nitrogen-containing synergist and / or a phosphorus-containing synergist. twenty three. 23. The composition of any one of the preceding embodiments, further comprising the nitrogen-containing synergist melamine pyrophosphate. twenty four. 24. The composition of any one of the preceding embodiments, wherein the nitrogen-containing synergist is present in an amount of 2 to 10 wt%, based on the total weight of the composition. twenty five. 25. The composition of any one of the preceding embodiments, wherein the nitrogen-containing synergist is present in an amount of 3-8 wt%, based on the total weight of the composition. 26. (1) at least one copolyetherester; (2) DEPAl and (3) DEPTi and (4) an aluminum salt of phosphorous acid, a zinc salt of phosphorous acid, or both; (5) a nitrogen-containing synergist; and 26. The composition of any one of the preceding embodiments, comprising: 27. (1) at least one copolyetherester; (2) DEPAl and (3) DEPTi and (4) a zinc salt of phosphorous acid; (5) a nitrogen-containing synergist; and 27. The composition of embodiment 26, comprising: 28. 28. The composition of embodiment 26 or 27, wherein the nitrogen-containing synergist is melamine pyrophosphate. 29. 29. The composition of embodiment 26, 27 or 28, wherein DEPAl is present in 5 to 15 wt%, based on the total weight of the composition. 30. 30. The composition of any one of embodiments 26 to 29, wherein DEPTi is present in an amount of 5 to 15 wt%, based on the total weight of the composition. 31. The composition of any one of embodiments 26 to 30, wherein the zinc salt of phosphorous acid is zinc phosphite having the CAS number [CAS14332-59-3]. 32. 32. The composition of any one of embodiments 26 to 31, wherein the nitrogen-containing synergist is present in an amount of 2 to 10 wt%, based on the total weight of the composition. 33. DEPAl is 10 microns or less D 95 The composition of any one of embodiments 26 to 32, having a particle size distribution of 0.01 to 0.1% by volume in acetone, as measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer. 34. DEPTi is 35 microns or less D 50 The composition of any one of embodiments 26 to 33, having a particle size distribution of 0.01 to 0.1% by volume in acetone, as measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer. 35. D, zinc salt of phosphorous acid less than 10 microns 95 The composition of any one of embodiments 26 to 34, having a particle size distribution of 0.01 to 0.1% by volume in acetone as measured using laser diffraction techniques with a Malvern Mastersizer 2000 particle size analyzer. 36. 36. The composition of any one of embodiments 26 to 35, wherein the copolyetherester is a polymer made by reacting a C2-C6 diol with an aromatic diacid moiety and a poly(alkylene oxide) diol. 37. 37. The composition of any one of the preceding embodiments, having an LOI of 30 or greater, more preferably 31 or greater, and more particularly preferably 33 or greater, as measured according to test method ISO 4589-1 / -2. 38. D of 60 or less, more preferably 46 or less, more particularly 40 or less, measured using a plaque having an area of ​​75 mm x 75 mm and a thickness of 2 mm according to the ISO 5659 test standard. s,max The composition of any one of the preceding embodiments, having a retention mass (g). 39. an LOI of 30 or more, more preferably 31 or more, and more particularly preferably 33 or more, as measured according to test method ISO 4589-1 / -2; and A D of 60 or less, more preferably 46 or less, more particularly 40 or less, measured according to the ISO 5659 test standard using a plaque having an area of ​​75 mm x 75 mm and a thickness of 2 mm. s,max The composition of any one of the preceding embodiments, having a retention mass (g). 40. The composition of any one of the preceding embodiments, wherein DEPTi comprises a titanium salt of diethylphosphinate of the formula:

[0071] [ka]

[0072] (In the formula, x is a number from 0 to 1.9.) 41. The composition of embodiment 40, wherein x is from 1 to 1.05, meaning that the ratio of Ti to diethylphosphinate is from 1.9 to 2. 42. 42. The composition of any one of the preceding embodiments, wherein the composition is in the form of a pellet. 43. 43. A wire or cable comprising an optically or electrically conductive core surrounded by at least one sheath made from the composition of any one of embodiments 1 to 42. 44. (1) at least one polymer selected from copolyesters (e.g., copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrene-based elastomers, thermoplastic polyurethanes, and thermoplastic vulcanizates; (2) a flame retardant mixture comprising 5 to 50 wt. % of aluminum diethylphosphinate and / or zinc diethylphosphinate and 5 to 50 wt. % of titanium diethylphosphinate salt, based on the total weight of the flame retardant mixture; 1. A flame retardant polymer composition comprising: 45. The composition of embodiment 44, wherein the titanium diethylphosphinate salt has the formula:

[0073] [ka]

[0074] (In the formula, x is 0 to 1.9.) 46. 46. ​​The composition of embodiment 44 or 45, wherein the polymer is selected from polyesters, copolyetheresters, polyamides, and mixtures thereof. 47. (1) at least one polymer selected from polyesters; (2) aluminum diethylphosphinate, (3) titanium diethylphosphinate salt; and 1. A flame retardant polymer composition comprising: 48. The composition of embodiment 47, wherein the polyester is selected from PET, PBT, and mixtures thereof. 49. (1) at least one polymer selected from polyamides; (2) aluminum diethylphosphinate, (3) titanium diethylphosphinate salt; and 1. A flame retardant polymer composition comprising: 50. 50. The composition of embodiment 49, wherein the polyamide is selected from PA66, PA6T66, and mixtures thereof. 51. 51. The composition of any one of embodiments 47 to 50, further comprising an aluminum phosphite and / or a zinc phosphite of the formula: [HP(=O)O2] 2- Zinc 2+ (II) [HP(=O)O2] 2- 3Al 3+ 2(III) 52. The composition of any one of embodiments 47 to 51, further comprising at least one nitrogen-containing synergist and / or phosphorus-containing flame retardant and / or nitrogen-containing flame retardant. 53. The composition of embodiment 52, wherein the nitrogen-containing synergist / flame retardant is selected from melamine cyanurate, melamine pyrophosphate, melamine polyphosphate, melem, and mixtures thereof. manufacturing The compositions of the present invention can be made by incorporating the ingredients into the polymer in various steps: for example, the ingredients can be added at the beginning or end of the polycondensation reaction to build up the polymer, or the ingredients can be melt mixed with the polymer, for example by melting the polymer in a twin screw extruder and mixing the other ingredients.

[0075] If desired, the non-polymeric components may be formulated as a mixture prior to incorporation into the polymer, or alternatively, the non-polymeric components may be added separately to the polymer. The non-polymeric components may be blended in concentrated form into the polymer by melt mixing. Such concentrated blends are called "masterbatches." The invention extends to such masterbatches in which the non-polymeric components are dispersed in a polymer matrix at concentrations 2-6 times higher than the desired final concentration in the polymer used to make the molded article (e.g., wire or cable sheath). performance The composition of the present invention exhibits good flammability. Flammability can be evaluated by methods known to those skilled in the art. One method is the limiting oxygen index ("LOI") according to test method ISO4589-1 / -2. Preferably, the composition of the present invention exhibits an LOI of 30 or more, more preferably 31 or more, and more particularly preferably 33 or more, when measured according to test method ISO4589-1 / -2.

[0076] The compositions of the present invention achieve a good combination of good combustion performance and reduced smoke production. Smoke density tests can be performed in an NBS smoke chamber according to the ISO 5659 test standard. Test specimens are prepared as plaques with an area of ​​75mmx75mm and a thickness of 2mm. The specimens are mounted horizontally in the chamber and subjected to a 25kW / m2 smoke at the top surface through a radiator cone and heat flux meter in the presence of a pilot flame for approximately 40 minutes. 2 The smoke generated over time is collected in a chamber and the attenuation of light passing through the smoke is measured with a photometric system equipped with a 6.5 V incandescent lamp, a photomultiplier tube and a high-precision photodetector. The results are measured in terms of light transmittance over time and the specific optical density D s D s is inversely proportional to the optical transmittance and is given for a specific optical path length equal to the thickness of the molded specimen. Smoke generation is determined by the maximum specific optical density D s,max Any dripping from the plaque specimen that occurs during the test is recorded. Normalized D to the mass retained during the experimental time s.max We can calculate D s,max Reported as g / mass retained.

[0077] D s,max A low value for / mass retention (g) is desirable and is an indication of a material that does not impede visibility in the event of a fire, thereby allowing people to escape from enclosed spaces more quickly. When there is no smoke, the light transmittance is 100%, and D s is 0.

[0078] The composition of the present invention has a D of 60 or less, more preferably 46 or less, more particularly 40 or less, measured according to the ISO 5659 test standard using a plaque having an area of ​​75 mm x 75 mm and a thickness of 2 mm. s,max It is preferable to indicate the weight per unit area / retention mass (g).

[0079] In a more particularly preferred embodiment, the composition of the invention has an LOI of 30 or more, more preferably 31 or more, more particularly preferably 33 or more, when measured according to the test method ISO 4589-1 / -2, and a D of 60 or less, more preferably 46 or less, more particularly 40 or less, measured according to the ISO 5659 test standard using a plaque having an area of ​​75 mm x 75 mm and a thickness of 2 mm. s,max / retention mass (g). Purpose The compositions of the present invention are suitable for any application where flame retardant and low smoke performance is required.They can be provided to consumers, for example, in the form of pellets.The pellets can be melted and used, for example, in an extruder, and then molded, for example, using injection molding, blow molding, extrusion molding.

[0080] A particularly suitable application for the composition is as a jacket or sheath for an electrical or optical cable. The cable comprises an electrically or optically conductive core surrounded by a sheath made from the composition of the present invention. The cable may further comprise other layers, such as a reinforcing layer or an insulating layer.

[0081] Such cables can be made, for example, by extruding a sheath made from the composition of the present invention around a conductive core and / or around additional layers of the cable. In a particularly preferred embodiment, the cable is a USB cable. EXAMPLES

[0082] The present invention is further illustrated by specific embodiments in the following examples, which provide more detailed descriptions of the compositions, uses and processes described herein. material The following materials were used to prepare the flame retardant polymer compositions described herein, as well as comparative compositions.

[0083] Copolyetherester (TPC1 and TPC2): A copolyetherester elastomer containing about 72.5 weight percent polytetramethylene oxide as polyether block segments having an average molecular weight of about 2000 g / mol, the weight percent being based on the total weight of the copolyetherester elastomer, and the short chain ester units of the copolyetherester being polybutylene terephthalate segments. The copolyetherester elastomer contained up to 6 weight percent of a heat stabilizer, antioxidant, and metal deactivator. TPC1 had a melt mass flow rate of 11 g / 10 min measured at 190° C. and 2.16 kg. TPC2 had a melt mass flow rate of 5 g / 10 min measured at 190° C. and 2.16 kg. PBT: Poly(butylene terephthalate) PA66: Polyamide 6,6 Polyamide 6T / 66: A polyamide made from the comonomers hexamethylenediamine, adipic acid and terephthalic acid DEPAl: Aluminum diethylphosphinate having a D90max of 7.506 microns (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer). DEPTi: Titanium diethylphosphinate. Particle size d 50Three lots were evaluated with particle sizes of 20 μm, 31 μm, and 41 μm (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer2000 particle size analyzer). DEPZn: zinc diethylphosphinate. Aluminum phosphite: Aluminum salt of phosphorous acid [CAS56287-23-1] Melamine pyrophosphate (MDP): D measured in acetone using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer 50 Melamine pyrophosphate at 15 microns. Melamine Cyanurate Melamine polyphosphate (MPP) Melem: 2,5,8-triaminoheptazine Irganox® 1010: (Pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate), a sterically hindered phenolic antioxidant Irganox® 1330: (3,3',3',5,5',5'-hexa-tert-butyl-a,a',a'-(mesitylene-2,4,6-triyl)tri-p-cresol), a sterically hindered phenolic antioxidant Irganox® 245: Ethylene bis(oxyethylene) bis-(3-(5-tert-butyl-4-hydroxy-m-tolyl)-propionate), a sterically hindered phenolic antioxidant LICOWAX® E: Ester of montanic acid and polyfunctional alcohol, a lubricating wax compound The additive components shown in Tables 1-6 were mixed with polymer pellets / granules in a twin screw extruder at a temperature approximately 10-20°C above the melt temperature of the polymer. The homogenized resin blend was extruded, cooled and chopped into pellets. The pellets were remelted as necessary and molded into test specimens as described in the test methods. Test Method Flame retardant-LOI Test specimens based on TPC1 thermoplastic elastomer were prepared from the compositions in the table by melt extruding narrow flat strips in a standard extruder with barrel temperatures set at about 170°C to about 190°C and cutting the test specimens from the flat strips thus obtained in the shape of rectangular bars with dimensions of 125 mm in length, 13 mm in width and an average thickness of about 1.7±0.1 mm. Test specimens based on TPC2 thermoplastic elastomer were prepared from the compositions in the table by melt extruding pellets in a standard extruder with barrel temperatures set at about 200°C and injection molding test specimens in the shape of ISO 178 flex bars with dimensions of 80 mm in length, 10 mm in width and 4 mm in thickness. The test specimens were conditioned at room temperature and at 50% relative humidity for at least 72 hours before testing. According to this test, the test specimens are fixed vertically in the center of a glass chimney at room temperature in an atmosphere of a mixture of oxygen and nitrogen that is slowly fed upwards into the glass column, allowing the relative concentrations of oxygen and nitrogen to be varied. A pilot flame is ignited at the top of the test specimen and allowed to burn downwards. The burning behavior of the specimens is observed and the time that burning continues is compared. The LOI is the minimum concentration of oxygen, expressed as a volume percent, required to sustain burning of the specimen as indicated by a target burn time after ignition of less than 180 seconds. A high LOI is desirable and is an indication of a material that is difficult to ignite and difficult to catch fire. Flame Retardant-UL94 Flame testing was also performed according to the UL94 vertical test. UL94 defines the following categories: V-0: Burning duration is 10 seconds or less. The total burning duration during 10 flame contacts is 50 seconds or less. There are no burning droplets. The sample is not completely burned. There are no embers on the sample for more than 30 seconds after the end of flame contact. V-1: The duration of combustion after the flame is removed does not exceed 30 seconds. The total duration of combustion after 10 flame applications is 250 seconds or less. There is no residual glow on the sample for more than 60 seconds after the flame is removed. Other criteria are the same as V-0. V-2: Absorbent cotton ignites due to burning dripping. Other standards are the same as V-1. Not classifiable (nk): Does not meet fire class V-2. In the examples, the combustion duration is shown when five test pieces are exposed to flame ten times. smoke density Smoke density testing was performed according to ISO 5659 test standard in an NBS smoke chamber supplied by Fire Testing Technologies. Test specimens based on TPC1 thermoplastic elastomer were made from the compositions listed in the table by melt extruding narrow flat strips in a standard extruder with barrel temperatures set at about 170°C to about 190°C and compression molding the strips to form plaques with an area of ​​75 mm x 75 mm and a thickness of 2 mm. Test specimens based on TPC2 thermoplastic elastomer were prepared from the compositions listed in the table by melt extruding pellets in a standard extruder with barrel temperatures set at about 200°C and injection molding test specimens in the shape of plaques with an area of ​​80 mm x 80 mm and a thickness of 2 mm. The test specimens were mounted horizontally in the chamber and exposed to a radiator cone and heat flux meter at 25 kW / m at the top surface for about 40 minutes in the presence of a pilot flame. 2 The smoke was exposed to a constant thermal radiation of 1000 Hz. The smoke evolved over time was collected in a chamber and the attenuation of light passing through the smoke was measured with a photometric system equipped with a 6.5 V incandescent lamp, a photomultiplier tube and a high-precision photodetector. The results were measured in terms of light transmittance over time and the specific optical density D s D s is inversely proportional to the optical transmittance and is given for a specific optical path length equal to the thickness of the molded specimen. Comparisons between material compositions can be made by the maximum specific optical density D s,max Any dripping from the plaque specimen that occurred during the test was recorded. Normalized D to the mass retained during the experimental time s.max Calculate D s,max,ret reported as.

[0084] D s,max The value of was calculated automatically by the NBS smoke chamber software. s,max,retA low value of D is desirable and is an indication of a material that is less likely to adversely affect visibility in the event of a fire, thereby allowing people to escape from enclosed spaces more quickly. When there is no smoke, the light transmittance is 100%, and D s is 0. Experimental Data Compositions designated "CE" are comparative, compositions designated "E" are the invention. Table 1 Table 1 shows compositions of the present invention based on a combination of DEPAl and DEPTi, with optional ingredients of metal phosphite salt and / or melamine pyrophosphate.

[0085] All of the inventive compositions exhibit very good flame retardant performance (LOI ≥ 30) and good smoke performance (D s,max,ret <60). In some cases, such as E4 and E7, the smoke performance is poorer (i.e., D s,max,ret The higher values ​​of LOI are compensated for by better flammability performance (i.e., higher LOI). Table 2 Table 2 shows the composition, flammability and smoke performance of polyester (PBT) formulations according to the invention (containing DEPAl and DEPTi) compared to compositions containing only DEPAl, only DEPZn, and only DEPTi. Table 3 Table 3 shows the composition, flammability and smoke performance of polyamide (PA66) formulations according to the invention (containing DEPAl and DEPTi) compared to compositions containing only DEPAl, only DEPZn and only DEPTi. Table 4 Table 4 shows the composition, flammability and smoke performance of PA6T / 66 formulations according to the invention (containing DEPAl and DEPTi) compared to compositions containing only DEPAl, only DEPZn, and only DEPTi. Table 5 Table 5 shows the composition, flammability and smoke performance of polyamide (PA66) formulations according to the invention (containing DEPAl and DEPTi) compared to compositions containing only DEPAl, only DEPZn and only DEPTi. Table 6 Table 6 shows the composition, flammability and smoke performance of polyamide (PA66) formulations according to the invention (containing DEPAl and DEPTi) compared to compositions containing only DEPAl, only DEPZn and only DEPTi.

[0086] [Table 1]

[0087] [Table 2]

[0088] [Table 3]

[0089] [Table 4]

[0090] [Table 5]

[0091] [Table 6]

Claims

1. 1. A flame retardant polymer composition comprising: (1) at least one polymer selected from polyesters (e.g., copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrene-based elastomers, thermoplastic polyurethanes, and thermoplastic vulcanizates; (2) aluminum diethylphosphinate; and (3) titanium diethylphosphinate salt; and 1. A flame retardant polymer composition comprising:

2. 2. The flame retardant polymer composition of claim 1, (1) at least one polymer selected from polyesters (e.g., copolyetheresters, copolyesteresters), polyamides, polyamide elastomers, thermoplastic polyolefin-based elastomers, styrene-based elastomers, thermoplastic polyurethanes, and thermoplastic vulcanizates; (2) aluminum diethylphosphinate; and (3) titanium diethylphosphinate salt; and The titanium diethylphosphinate salt comprises ５０ % by volume, in acetone, measured using a laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer, greater than 35 microns, the concentration of said aluminum diethylphosphinate is 15 wt % or less, based on the total weight of said composition; A flame retardant polymer composition.

3. 3. The flame retardant polymer composition according to claim 1 or 2, (1) at least one copolyetherester; (2) aluminum diethylphosphinate; and (3) titanium diethylphosphinate salt; and The titanium diethylphosphinate salt comprises ５０ % by volume, in acetone, measured using a laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer, greater than 35 microns, the concentration of said aluminum diethylphosphinate is 15 wt % or less, based on the total weight of said composition; A flame retardant polymer composition.

4. 3. The composition according to claim 1 or 2, wherein the copolyetherester is ２ ~C ６ A composition made by reacting a diol with an aromatic diacid moiety and a poly(alkylene oxide) diol.

5. 10. The composition of claim 1, wherein the copolyetherester is made with a poly(alkylene oxide) diol selected from poly(ethylene oxide) diol, poly(propylene oxide) diol, poly(tetramethylene oxide) diol ("PTMEG"), and mixtures thereof.

6. 10. The composition of claim 1, wherein the copolyetherester is selected from ethylene glycol, propylene glycol, butylene glycol, and mixtures thereof. ２ ~C ６ The composition is made using a diol.

7. 10. The composition of claim 1, wherein the copolyetherester is made with an aromatic diacid selected from terephthalate, isoterephthalate, and mixtures thereof, with terephthalate being particularly preferred.

8. 10. The composition of claim 1, wherein the copolyetherester is made from butylene diol, terephthalate and PTMEG.

9. 2. The composition of claim 1, wherein the concentration of DEPAl(2)+DEPTi(3) is 8-30 wt %, based on the total weight of the composition.

10. 10. The composition of claim 1, wherein the concentration of DEPA1 is from 5 to 25 wt %, based on the total weight of the composition.

11. 2. The composition of claim 1, wherein the concentration of DEPTi is 1 to 15 wt %, based on the total weight of the composition.

12. 2. The composition of claim 1, wherein the DEPA1 has a D ９５ (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer).

13. 2. The composition of claim 1, wherein the DEPTi is less than or equal to 35 microns. ５０ (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer).

14. 2. The composition of claim 1, wherein the at least one copolyetherester is selected from the group consisting of C ２ ~C ６ The composition is selected from a polymer made by reacting a diol with an aromatic diacid moiety and a poly(alkylene oxide) diol.

15. 10. The composition of claim 1, further comprising an aluminum salt of phosphorous acid, a zinc salt of phosphorous acid, or both.

16. 10. The composition of claim 1, further comprising an aluminum phosphite having a CAS number [CAS56287-23-1], a zinc phosphite having a CAS number [CAS14332-59-3], or a mixture thereof.

17. 17. The composition of claim 16, wherein the aluminum phosphite has a D ９５ (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer).

18. 17. The composition of claim 16, wherein the zinc phosphite has a D ９５ (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer).

19. 17. The composition of claim 16, wherein the total phosphite concentration is from 0.1 to 20 wt %, based on the total weight of the composition.

20. 2. The composition of claim 1, wherein the ratio of DEPA1 / DEPTi is 1 or less.

21. 2. The composition of claim 1, wherein the ratio of DEPA1 / DEPTi is from 0.5 to 1.

22. 10. The composition of claim 1, further comprising a nitrogen-containing synergist and / or a phosphorus-containing synergist.

23. 23. The composition of claim 22, further comprising the nitrogen-containing synergist melamine pyrophosphate.

24. 23. The composition of claim 22, wherein the nitrogen-containing synergist is present at 2 to 10 wt %, based on the total weight of the composition.

25. 23. The composition of claim 22, wherein the nitrogen-containing synergist is present at 3 to 8 wt %, based on the total weight of the composition.

26. 2. The composition of claim 1 , (1) at least one copolyetherester; (2) DEPA1, (3) DEPTi, and (4) an aluminum salt of phosphorous acid, a zinc salt of phosphorous acid, or both; (5) a nitrogen-containing synergist; and A composition comprising:

27. 27. The composition of claim 26, (1) at least one copolyetherester; (2) DEPA1, (3) DEPTi, and (4) a zinc salt of phosphorous acid; and (5) a nitrogen-containing synergist; and A composition comprising:

28. 28. The composition of claim 26 or 27, wherein the nitrogen-containing synergist is melamine pyrophosphate.

29. 28. The composition of claim 26 or 27, wherein the DEPA1 is present at 5 to 15 wt%, based on the total weight of the composition.

30. 28. The composition of claim 26 or 27, wherein the DEPTi is present at 5 to 15 wt %, based on the total weight of the composition.

31. 28. The composition according to claim 26 or 27, wherein the zinc salt of phosphorous acid is zinc phosphite having CAS number [CAS14332-59-3].

32. 28. The composition of claim 26 or 27, wherein the nitrogen-containing synergist is present at 2 to 10 wt %, based on the total weight of the composition.

33. 28. The composition of claim 26 or 27, wherein the DEPA1 has a D of 10 microns or less. ９５ (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer).

34. 28. The composition according to claim 26 or 27, wherein the DEPTi is 35 microns or less. ５０ (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer).

35. 28. The composition of claim 26 or 27, wherein the zinc salt of phosphorous acid has a D of 10 microns or less. ９５ (volume %, in acetone, measured using laser diffraction technique with a Malvern Mastersizer 2000 particle size analyzer).

36. 28. The composition of claim 26 or 27, wherein the copolyetherester is ２ ~C ６ A composition which is a polymer made by reacting a diol with an aromatic diacid moiety and a poly(alkylene oxide) diol.

37. 10. The composition of claim 1, having an LOI of 30 or greater, as measured according to test method ISO 4589-1 / -2.

38. 10. The composition of claim 1, having a D of 46 or less, measured according to the ISO 5659 test standard using a plaque having an area of ​​75 mm x 75 mm and a thickness of 2 mm. ｓ，ｍａｘ / retention mass (g).

39. 13. A wire or cable comprising an optically or electrically conductive core surrounded by a sheath made from the composition of claim 1.

40. A molded article made from the composition of claim 1.

41. A method of making the composition of claim 1 comprising the step of melt mixing the components.