Method for Producing Fluting and / or Liners for Corrugated Board

Abstract

1. A method for producing fluting and / or liners for corrugated board, comprising the steps of: a) using broke obtained from the production of liners in pulp used for the production of fluting, wherein at least 50% of the broke is unrelated to the production of liners; and / or b) using broke obtained from the production of fluting in pulp used for the production of liners, wherein at least 50% of the broke is unrelated to the production of fluting.

Description

[Technical field]

[0001] The present invention relates to a method for making fluting and / or liners for corrugated board. [Background technology]

[0002] Corrugated cardboard (sometimes called corrugated cardboard or corrugated fiberboard) is a packaging material that can be converted into various types of packaging solutions. Corrugated cardboard is a fibrous substrate made from cellulose fibers. The fibers can be virgin or recycled, such as fibers derived from post-consumer cardboard or other materials.

[0003] Corrugated board comprises at least one medium (fluting) and at least one flat base paper (liner or linerboard) bonded to the surface of the medium. For example, corrugated board may consist of a layer of fluting bonded between two layers of liner to form a sandwich structure. The sandwich structure can be formed in various formats such as single, double, and triple wall, as described for example in Kirwan M., J., Paper and Paperboard. Packaging Technology, Blackwell Publishing 2005.

[0004] One challenge when producing corrugated board is the adhesion between the liner and the fluting. Too little adhesion can cause delamination, and adding too much adhesive to ensure adequate adhesion can cause washboarding and curling of the board. It is important that the glue added is optimally absorbed into the liner and / or corrugating medium. If the adhesive does not adhere to the fluting / liner, delamination will occur, and if too much is absorbed into the fluting / liner, the same can happen.

[0005] There are various types of corrugated board qualities, which may contain different types of liner and medium. Container board (also known as CCM or corrugated case stock) is a type of paperboard manufactured specifically for the production of corrugated board and contains both linerboard and medium (or fluting), the two types of paper that make up corrugated board. Container board is generally brown in color because it is made primarily from natural unbleached wood fibers, although its color can vary depending on the wood species, pulping process, recycling rate, and impurity content.

[0006] Examples of different types of liners are kraftliners and testliners. Kraftliners are typically produced from kraft pulp, which can be bleached or unbleached, and may contain one or more layers / plies, where the top layer / ply is often optimized to provide a good print surface and good moisture resistance. Testliners are primarily produced from recycled corrugated cardboard and are usually manufactured with two layers / plies. Due to the presence of recycled fibers, testliners may typically have lower mechanical strength than kraftliners, especially lower burst strength. Kraftliners are often used for packaging boxes with higher demands on strength properties.

[0007] Fluting is formed from paper or paperboard that has been corrugated using a corrugator with the application of heat, moisture and pressure.

[0008] Fluting is often prepared from Neutral Sulfite Semi-Chemical (NSSC) pulp. NSSC pulp, usually made from hardwood species, is noted for its exceptional stiffness and high stiffness, making it suitable for use in fluting. Neutral Sulfite Semi-Chemical (NSSC) pulping is an old process well known in the field of paper pulping. One of the reasons for using NSSC pulping is the high yield, usually above 60%. In NSSC pulping, the cooking liquor is Na 2 SO 3 or (NH 4 ) 2 SO3 Sulfites such as NaOH or Na 2 CO 3 By "neutral" it is meant that the pH of the NSSC cooking liquor is generally between 6 and 10. The pulp can be cooked in a batch or continuous cooker. Cooking times are usually between 5 minutes and 3 hours, and cooking temperatures are between 160 and 200 °C. NSSC pulp contains a relatively high amount of residual lignin, such as 15-20%, which makes it hard. The Kappa number of NSSC pulp is typically greater than 70. NSSC pulping is "semi-chemical" in the sense that it also includes mechanical refining of the pulp. Refining can be done, for example, using a disc refiner at digester pressure or atmospheric pressure.

[0009] The fluting and liner are attached to one another by placing an adhesive between the core and the liner. The liner is attached to at least one surface of the core by the adhesive. The adhesive is preferably applied to at least one surface of the fluted core, and then the liner is attached to said surface. Any adhesive conventional in the art can be used. The adhesive can be, for example, a starch-based glue that can be extracted from a wide variety of plants. Some of the most common plants are corn, wheat, barley, rice, potato, tapioca, and pea. The starch is preferably natural, i.e., the starch is not modified. The adhesive can also include water, sodium hydroxide, and boric acid. Other additives may be added, such as additives that improve wet strength or adhesive bond strength. Also, other functional chemicals, such as borax, glyoxal, or mixtures thereof, can be added, for example to improve moisture resistance or gelling behavior.

[0010] One significant challenge when making corrugated board and medium is resistance to moisture. When corrugated board is exposed to moisture, water and water vapor can diffuse through the liner and soften the medium. Common solutions to this problem are fluting and / or increasing the basis weight of the liner, but this conflicts with environmental imperatives that call for lower basis weight materials that consume less raw materials.

[0011] Another solution is to provide a barrier layer in the liner to reduce water and water vapor transmission. However, this is only an incomplete solution, since moisture diffusion can still occur on the other side or through the edges, thus affecting the mechanical stability of the board. Barrier layers also increase costs and usually reduce the recyclability of the material.

[0012] The flutings or medium may also be treated or coated with hydrophobizing chemicals, but this generally increases cost and may also have a negative effect on the mechanical properties of the fluting. High levels of hydrophobizing chemicals may also impair the adhesion of the fluting to the liner. In particular, NSSC pulp requires high levels of hydrophobizing chemicals to obtain the required level of water resistance in the finished fluting.

[0013] Broken means partially or completely manufactured paper or board that is discarded from the paper or board making, converting, and finishing processes. During the manufacture of liners, fluting, and corrugated board, significant amounts of broken are generated. Since broken can amount to well over 5% of the total machine output, it is a significant source of fiber and broken disposal is an essential part of the paper making process from both a financial and operational standpoint.

[0014] Broken paper is produced continuously, and a "broken paper handling system" is typically implemented to collect, process, and make this resource available for reuse. Broken paper can be wet or dry, depending on what point in the process it is obtained. The wet or dry broken paper is then broken down and possibly diluted into a slurry or put into broken stock for reuse. Broken paper handling systems typically include a broken paper pulper, which is used to break down the broken paper into broken stock that can be pumped, processed, and then mixed with new stock. The term broken paper pulper can include a wide range of machines and can refer to both stand-alone broken paper pulpers and below-the-machine (or UTM) pulpers that receive paper directly from the machine, including any trim. Stand-alone broken paper pulpers are typically used to process rejected finished reels, or for broken paper that has been baled or collected for any reason. For efficient broke handling and management, it is important to monitor and control the broken paper chemistry.

[0015] New machine concepts and increased machine speeds coupled with an increased desire to conserve resources have further increased the need for pulps with improved properties.

[0016] There remains a need for new and improved fluting and liner materials and methods that combine strength, low basis weight, water / moisture resistance, low chemical consumption, low cost, and / or high recyclability. Summary of the Invention

[0017] It is an object of the present disclosure to provide an improved method for producing corrugated board consisting of liners and fluting that overcomes or ameliorates at least some of the problems discussed above.

[0018] It is a further object of the present disclosure to provide an improved method for recycling materials in producing corrugated board consisting of liners and fluting.

[0019] It is still a further object of the present disclosure to provide an improved method of producing corrugated board which increases recycled paper and maintains the quality and characteristics of the board produced.

[0020] The above objectives, as well as other objectives that will be appreciated by those skilled in the art in light of this disclosure, are accomplished by various aspects of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0021] Broken paper means partially or completely manufactured paper or board that is discarded from the paper or board making, converting, and finishing processes. Broken paper can be broken down, diluted into a slurry, or put into broke stock for reuse. Broken paper is most commonly reused in the same or same type of process from which it was obtained.

[0022] The use of NSSC pulp for the manufacture of liners is problematic due to the presence of particles and shives that negatively affect the appearance and optical properties of the liner. The present invention is based on the inventive recognition that broke, i.e. recycled material, obtained from the manufacture of fluting can be conveniently reused in the pulp used for the manufacture of liners. The inventors have also found that broke obtained from the manufacture of liners can be conveniently reused in the pulp used for the manufacture of fluting for corrugated board.

[0023] Broken paper obtained from the manufacture of fluting typically contains a higher amount of NSSC pulp than broken paper from liners. Using NSSC pulp in liners is desirable as it can provide advantages in terms of improved strength and reduced cost. However, using NSSC pulp in the manufacture of liners is typically problematic due to the presence of particles and shives that negatively affect the appearance and optical properties of the liner. The advantage of using NSSC pulp from broken paper compared to using virgin NSSC pulp is that the NSSC pulp from broken paper has been subjected to additional mechanical and / or chemical treatments that reduce the presence of particles and shives that negatively affect the appearance and optical properties of the liner. This means that it may be possible to use a higher amount of NSSC pulp from broken paper in liners than virgin NSSC pulp.

[0024] Broken paper from liner manufacture typically contains a higher amount of kraft pulp than broken paper from fluting, which can improve the mechanical strength of the flutes. Since the broken paper has already been refined to an appropriate level, it can help reduce the tendency for cracking in the flutes. Broken paper from liner manufacture also typically contains a higher amount of internally sized (hydrophobized) kraft pulp than broken paper from fluting, which can improve the flutes' resistance to water and moisture.

[0025] Typically the liners and fluting are made on different equipment, although it is also common for the liners and fluting to be made on different machines in the same facility.

[0026] According to a first aspect presented herein, 1. A method for producing fluting and / or liners for corrugated board, comprising the steps of: a) using broke resulting from the manufacture of liners in pulp used for the manufacture of fluting, wherein at least 50% of the broke is unrelated to the manufacture of liners; and / or b) using broke resulting from the manufacture of fluting in the pulp used to manufacture liners, wherein at least 50% of the broke is unrelated to the manufacture of fluting. A method is provided, comprising:

[0027] By irrelevant broke is meant broke originating from another production line, i.e. from production in another paper or board machine. As a result, the irrelevant broke is produced in another place or in another production line. By internal broke is meant broken produced in the same production line, i.e. on the same paper or board machine. It has been found to be beneficial to use broke from the production of liners for the production of flutings and vice versa. For the production of flutings, it would be preferred that at least 60%, preferably at least 70%, even more preferably at least 80%, even more preferably at least 90% of the broke is broke irrelevant to the production of liners. For the production of liners, it would be preferred that at least 60%, preferably at least 70%, even more preferably at least 80%, even more preferably at least 90% of the broke is broke irrelevant to the production of flutings. From a sustainability and economic point of view, it is still possible to use some amount of internal broke for the production of flutings or liners according to the invention.

[0028] The extraneous broke used is obtained from the manufacture of either the liner or the fluting, i.e. not broke from pre-made corrugated board which contains both liner and fluting.

[0029] The fluting or liner can be manufactured on a paper or board machine adapted for making fluting or liners. Paper or board machines for making fluting and liners are well known in the art. Typically, the machine layout includes a stock processing section, a wet end section, a press section, a drying section, and a calender and / or coating section. In the wet end section, the fluting or liner web is formed by distributing and partially dewatering the pulp suspension, or stock, on one or more wires using one or more headboxes. The formed fluting or liner web can be single ply or multi-ply.

[0030] The formed web is typically subjected to further dewatering, which may for example include passing the web through a press section of a paper machine, where the web passes between large rolls under high pressure to squeeze out as much water as possible. The press section may consist of traditional nip press units and press woven felts, and / or one or several shoe presses or extended dewatering nips. These may operate at various nip or press loads, various positions, temperatures and delay times. The press section may comprise one or more shoe presses to maximize production. If one or several shoe presses are used, these may operate at press levels of more than 800 kN / m, such as more than 1000 kN / m, such as more than 1200 kN / m, or such as more than 1450 kN / m. The removed water is typically received by a fabric or felt.

[0031] After the press section, the web may be subjected to drying in a drying section. Drying may include, for example, drying the web by passing the web around a series of heated drying cylinders. Drying may remove the water content, typically to a level of about 1-15 wt%, preferably about 2-10 wt%.

[0032] Broken paper is formed in all sections of the paper or board machine and may contain wet or dry material depending on which section it is obtained from.

[0033] The method of the present disclosure comprises: a) using broke resulting from the manufacture of liners in the pulp used for the manufacture of fluting, wherein at least 50% of the broke is unrelated to the manufacture of liners; or b) using broke resulting from the manufacture of fluting in the pulp used to manufacture liners, wherein at least 50% of the broke is unrelated to the manufacture of fluting; or Combination of steps a) and b) Includes.

[0034] Typically, the liners and fluting are made on different equipment; however, it is also common for the liners and fluting to be made on different machines in the same facility.

[0035] The method of the present invention is preferably carried out in a plant where both the liners and the fluting are produced.

[0036] In plants where both liners and flutings are produced, the broke from each process can be conveniently used in the other process, i.e., the broke from the manufacture of liners can be recycled into the pulp used to manufacture flutings and the broke from the manufacture of flutings can be recycled into the pulp used to manufacture liners. In this way, the benefits of both process steps can be combined and waste can be minimized.

[0037] The use of broke in steps a) and b) typically involves breaking down the broke using a broke pulper and optionally diluting the broke into a broken stock which can be pumped, treated and then mixed with fresh pulp.

[0038] The broke resulting from the manufacture of liners is preferably broken down using a broke pulper and optionally diluted into broken stock which can be pumped, treated and then mixed with the pulp used for the manufacture of fluting.

[0039] The broke resulting from the production of fluting is preferably broken down using a broke pulper and optionally diluted into broken stock which can be pumped, treated and then mixed with the pulp used to produce the liners.

[0040] Thus, in some embodiments, the broke used in steps a) and / or b) is broke stock.

[0041] The broke may be broken down, for example, in a vertical or horizontal pulper. The consistency may be, for example, in the range of 2-20 wt%, more preferably in the range of 4-10 wt%. The broken down pulp is optionally further diluted.

[0042] The pH of the broke during disintegration and optional dilution is preferably in the range of 5 to 11, more preferably in the range of 6 to 10. The temperature of the broke during disintegration and optional dilution is preferably in the range of 20 to 80°C, more preferably in the range of 30 to 50°C. Before recycling, the broke may be deflaked or defiberized or fibrillated to ensure that no residual flakes or fiber agglomerates or clumps remain. The Schopper Riegler (SR) number of the resulting broke stock is preferably in the range of 18 to 50, more preferably in the range of 20 to 45, determined according to ISO 5267-1.

[0043] The advantage of using pulp from broke compared to virgin pulp is that pulp from broke has already been dewatered once, so that the presence of colloidal matter and impurities, including electrolytes, in the liquid phase is reduced. This reduction can be measured by measuring the conductivity of the broke or broken stock. In some embodiments, the conductivity of the broke is less than 1200, less than 1000, less than 800, or less than 600 when dissolved at 3.5 wt % in distilled water, more preferably less than 500, less than 450, less than 400, less than 350, or less than 300 mS / m.

[0044] The conductivity of the resulting broke stock is preferably less than 1200, less than 1000, less than 800, or less than 600, and more preferably less than 500, less than 450, less than 400, less than 350, or less than 300 mS / m.

[0045] In some embodiments, the broke from the manufacture of liners and fluting is split and optionally diluted in a separate broke pulper, resulting in pure liner broke and pure fluting broke, respectively. In some embodiments, the internal and unrelated broke from the manufacture of liners and fluting is split and optionally diluted in a common pulp broker, resulting in a mixture of liner broke and fluting broke.

[0046] Broken paper resulting from liner manufacture typically contains a higher amount of kraft pulp than broken paper from fluting, hi some embodiments, broken paper resulting from liner manufacture contains at least 60 wt.%, preferably at least 70 wt.%, more preferably at least 80 wt.% kraft pulp based on the dry weight of the broken paper.

[0047] The broke obtained from the manufacture of fluting typically contains a higher amount of NSSC pulp than the broke from the liner.

[0048] "NSSC pulp" is obtained by "NSSC pulping", as such is defined in the Background section. NSSC pulp can be hardwood or softwood pulp, or a mixture thereof. NSSC pulp is preferably hardwood pulp or a hardwood / softwood pulp mixture containing less than 15 wt% softwood, preferably less than 10 wt% softwood, more preferably less than 5 wt% softwood. Hardwood may be, for example, aspen, alder, poplar, eucalyptus, birch, acacia, or beech. NSSC pulp is preferably free of sulfite, preferably Na 2 SO 3 or (NH 4 ) 2 SO 3 and a base, preferably NaOH or Na 2 CO 3 In some embodiments, the yield from NSSC pulping is greater than 60%, preferably greater than 65%, preferably greater than 70%, more preferably greater than 75%. The term "neutral" means that the pH of the NSSC cooking liquor is in the range of 6-10. The cooking time is preferably in the range of 5 minutes to 3 hours. The cooking temperature is preferably in the range of 160-200°C. The NSSC pulp may contain a relatively high amount of residual lignin, such as 15-20%. The Kappa number of the NSSC pulp is typically greater than 70 according to ISO 3260, preferably greater than 80, preferably greater than 95, more preferably greater than 100. NSSC pulping is "semi-chemical" in the sense that it also includes mechanical refining of the pulp. Refining may be performed, for example, using a disc refiner at digester pressure or at atmospheric pressure. Refining may be performed in one or more steps with the same or different pulp consistencies. The first refining step may preferably be performed at a higher consistency such as 5-35% and the second refining step may preferably be performed at a lower consistency <5%.

[0049] In some embodiments, the broke resulting from the production of fluting contains less than 2%, preferably less than 1.8%, and more preferably less than 1.6% Pulmac shives (slot size 0.1 mm).

[0050] In some embodiments, the broke obtained from the manufacture of fluting contains at least 30 wt%, preferably at least 40 wt%, more preferably at least 50 wt% NSSC pulp based on the dry weight of the broke. In some embodiments, the broke obtained from the manufacture of fluting contains at least 60 wt%, preferably at least 70 wt%, more preferably at least 80 wt% NSSC pulp based on the dry weight of the broke. This means that the addition of the broke obtained from the manufacture of liners containing at least 60 wt% kraft pulp increases the overall kraft pulp content of the fluting.

[0051] In some embodiments, the pulp used for the manufacture of the liner comprises at least 60 wt.%, preferably at least 70 wt.%, more preferably at least 80 wt.% kraft pulp based on the dry weight of the pulp, meaning that the overall NSSC pulp content of the liner is increased by adding broke obtained from the manufacture of e.g. fluting, which comprises at least 60 wt.% NSSC pulp.

[0052] Various amounts of broke can be used depending on the composition, quality and availability of the broke. In some embodiments, the amount of broke obtained from the manufacture of liners used in the pulp for the manufacture of fluting is in the range of 1-30 wt% based on the dry weight of the pulp, preferably in the range of 5-30 wt%, more preferably in the range of 1-20 wt%, even more preferably in the range of 5-20 wt%, and even more preferably in the range of 10-20 wt%.

[0053] In some embodiments, the amount of broke obtained from the production of fluting used in the pulp for the production of liners is in the range of 1-30 wt.%, preferably in the range of 5-30 wt.%, more preferably in the range of 1-20 wt.%, even more preferably in the range of 5-20 wt.%, and even more preferably in the range of 10-20 wt.%, based on the dry weight of the pulp.

[0054] Monitoring and controlling the broke chemistry is important for efficient broke handling and management. Long delays such as resting can increase microbial activity within the broke. Microbial activity can cause changes in the broke chemistry, which can affect quality and viability when making fluting or liners.

[0055] Broken paper as used in this disclosure is preferably fresh broken paper, which refers to broken paper from fluting or liners that has been disintegrated and optionally diluted less than 20 days ago, more preferably less than 15 days ago, more preferably less than 5 days ago, more preferably less than 3 days ago, and most preferably less than 1 day ago.

[0056] Broken paper as used in this disclosure is preferably mill broke, i.e. waste paper and trim obtained from mill production. Mill broke can be obtained from various sections of the production process.

[0057] In some embodiments, broke from the manufacture of liners is obtained from the forming section, press section and / or dryer section.

[0058] In some embodiments, broke from the manufacture of fluting is obtained from the forming section, the press section, the dryer section, and / or the corrugator.

[0059] In some embodiments, the fluting or liner is a multi-layer fluting or multi-layer liner that includes two outer plies and at least one intermediate ply sandwiched between the outer plies, where the broke is added to the pulp that is used to prepare the intermediate ply. Placing the broke in the intermediate ply can, for example, reduce the effect of the broke on the appearance of the fluting or liner in which it is used.

[0060] In some embodiments, the broke from the manufacture of liners in step a) improves the hydrophobicity of the manufactured flutes. The broke from the manufacture of liners typically contains a higher amount of internally sized (hydrophobized) kraft pulp than the broke from fluting, which can improve the resistance of the flutes to water and moisture.

[0061] In some embodiments, the broke of step b) obtained from the production of fluting contains less impurities and shives compared to virgin NSSC. The use of NSSC pulp in the production of liners is usually problematic due to the presence of particles and shives that have a negative effect on the appearance and optical properties of the liner. The advantage of using NSSC pulp from broke compared to virgin NSSC pulp is that NSSC pulp from broke has been subjected to additional mechanical and / or chemical treatments that reduce the presence of particles and shives that have a negative effect on the appearance and optical properties of the liner. This means that it may be possible to use a higher amount of NSSC pulp from broke than virgin NSSC pulp.

[0062] According to a second aspect presented herein, there is provided a fluting or liner for corrugated board obtainable by a method according to any one of the preceding claims.

[0063] The resulting fluting and liner are intended for use in corrugated board, which includes at least one layer of uncorrugated liner adhered to at least one layer of fluting. For example, a corrugated board may consist of a layer of fluting sandwiched between two layers of liner.

[0064] According to a third aspect presented herein, there is provided a corrugated board comprising fluting and a liner, the corrugated board comprising: i) Fluting containing broke resulting from the manufacture of liners, where at least 50% of the broke is unrelated to the manufacture of liners; and / or ii) A liner containing broke resulting from the manufacture of fluting, where at least 50% of the broke is unrelated to the manufacture of fluting. A cardboard is provided, comprising:

[0065] While the invention has been described with reference to various exemplary embodiments, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is not intended that the invention be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but the invention is intended to include all embodiments falling within the scope of the appended claims. EXAMPLES

[0066] Example 1 (Comparison) NSSC beechwood pulp was obtained in dry form and then decomposed into furnish and compressed at 150 g / m on a pilot paper machine of the Fourdrinier type. 2 The production speed was 45 m / min and the furnish temperature was 45°C.

[0067] Example 2 (Comparison) The NSSC beechwood pulp used in Example 1 was refined to higher SR values ​​and webs were prepared as in Example 1. The increased SR due to refining notably increased the tensile index (Geom).

[0068] Example 3 NSSC beechwood pulp, as used in Example 1, was washed with water (40 m per tonne of pulp) using an Eimco belt washing unit. 3The pulp was washed with 100 ml of fresh water (100 ml of water per minute). 2.7% of the fines were removed along with colloidal matter and impurities, including electrolytes, in the liquid phase. The pH of the pulp suspension increased as a result of the washing, confirming the removal of electrolytes and the reduction in ash. Webs were prepared as in Example 1. Small improvements were observed in both tensile strength and elongation.

[0069] Example 4 NSSC beechwood pulp as used in Example 1 was mixed with washed NSSC birch broke pulp (washed as described in Example 3). The pulps were mixed in a 50-50 ratio. Webs were prepared as in Example 1. Significant improvements in both tensile strength and elongation were observed.

[0070] Example 5 In this example, washed NSSC birch broke pulp as used in Example 4 was used without any other fibers. Webs were prepared similar to Example 1. Tensile strength properties and elongation were further improved. TIFF2024519011000001.tif76170TIFF2024519011000002.tif93170

[0071] Unless otherwise specified, the physical properties discussed in this disclosure are determined according to the following standards: Whiteness C / 2°+UV ISO 2470-1 L* C / 2°+UV ISO 5631-1 a* C / 2°+UV ISO 5631-1 b* C / 2°+UV ISO 5631-1 Basis weight ISO 536 Thickness, single sheet ISO 534 Umbrella, single sheet ISO 534 Air permeability GH ISO 5636-5 Cobb 30s ISO 535 Moisture content 50%rh ISO 287 Scott-Bond TAPPI T569 Tensile strength ISO 1924-3 Tensile Index ISO 1924-3 Tensile strength md / cd ISO 1924-3 Elongation ISO 1924-3 Tensile stiffness ISO 1924-3 Tensile stiffness index ISO 1924-3 E-Module ISO 1924-3 TEA ISO 1924-3 TEA index ISO 1924-3 TEA index ISO 1924-3 Fracture toughness ISO / TS 17958 Fracture toughness index ISO / TS 17958 Tear resistance ISO 1974 Tear index ISO 1974 SCT ISO 9895 SCT index ISO 9895 RCT ISO 12192 RCT index ISO 12192 Rupture Index ISO 2759 Bursting strength ISO 2759

[0072] Unless otherwise specified, standard methods may be applied to determine the physical and mechanical properties in both the cross direction (cd) and machine direction (md).

Claims

1. 1. A method for producing fluting and / or liners for corrugated board, comprising the steps of: a) using broke obtained from the manufacture of liners in the pulp used for the manufacture of fluting, wherein at least 50% of the broke is unrelated to the manufacture of liners. and / or b) using broke resulting from the manufacture of fluting in the pulp used to manufacture liners, wherein at least 50% of the broke is unrelated to the manufacture of fluting. A method comprising:

2. The method of claim 1 comprising step a).

3. The method of claim 1 , further comprising step b).

4. The method of claim 1 comprising steps a) and b).

5. 5. The method according to any one of claims 1 to 4, wherein the amount of broke obtained from the production of liners, which is used in the pulp for the production of flutings, is in the range of 1 to 30 wt. %, preferably in the range of 5 to 20 wt. %, based on the dry weight of the pulp.

6. 5. The method according to any one of claims 1 to 4, wherein the amount of broke obtained from the production of fluting, which is used in the pulp for the production of the liner, is in the range of 1 to 30 wt. %, preferably in the range of 5 to 20 wt. %, based on the dry weight of the pulp.

7. 5. The method of claim 1, wherein the broke is mill broke.

8. 5. The method of any one of claims 1 to 4, wherein the broke from the production of fluting is obtained from the forming section, the press section, the dryer section, and / or the corrugator.

9. 5. The method according to any one of claims 1 to 4, wherein broke from the manufacture of the liner is obtained from the forming section, the press section and / or the dryer section.

10. 5. The method according to any one of claims 1 to 4, wherein the fluting or liner is a multi-layer fluting or multi-layer liner comprising two outer plies and at least one intermediate ply sandwiched between the outer plies, and broke is applied to the pulp used to prepare the intermediate ply.

11. 5. The method according to any one of claims 1 to 4, wherein the broke in step a) obtained from the production of the liner improves the hydrophobicity of the produced fluting.

12. 5. The method according to any one of claims 1 to 4, wherein the broke in step b) obtained from the production of fluting contains less impurities and shives compared to virgin NSSC.

13. 1. A corrugated board comprising fluting and a liner, the corrugated board comprising: i) Fluting containing broke resulting from the manufacture of liners, wherein at least 50% of the broke is unrelated to the manufacture of liners. and / or ii) A liner containing broke resulting from the manufacture of fluting, wherein at least 50% of the broke is unrelated to the manufacture of fluting. Including cardboard.