Photonic crystal fiber, method of producing the same, and supercontinuum light source

Abstract

To provide a Photonic Crystal Fiber, a method of producing it, and a supercontinuum light source.SOLUTION: A Photonic Crystal Fiber, a method of producing it, and a supercontinuum light source comprising the Photonic Crystal Fiber are provided. The Photonic Crystal Fiber has a longitudinal axis and includes a core extending along the length and a cladding region surrounding the core. At least the cladding region includes a plurality of microstructures in the form of inclusions extending along the longitudinal axis in a microstructured length section. In a degradation resistant length section of the microstructured length section, the Photonic Crystal Fiber includes at least one of hydrogen and deuterium. In the degradation resistant length section, the Photonic Crystal Fiber further includes a main coating surrounding the cladding region, the main coating is hermetic for at least one of the hydrogen and deuterium at a temperature below Th, and the Th is preferably 50°C<Th<250°C.SELECTED DRAWING: Figure 4b

Description

[Technical field]

[0001] The present invention relates to photonic crystal fibers (PCFs), methods for making photonic crystal fibers, and to supercontinuum light sources consisting of such photonic crystal fibers, microstructured optical fibers, and supercontinuum light emitting sources. [Background technology]

[0002] A photonic crystal fiber is a fiber with a core surrounded by a cladding region that has a number of inclusions (sometimes called cladding features or microstructures) typically arranged in a regular array in a background material. Hereinafter, photonic crystal fibers are referred to as photonic crystal fibers or microstructured optical fibers. The inclusions can be gas, liquid or solid inclusions. In principle, the inclusions could be voids, but in practice, the voids usually contain some gas molecules.

[0003] Fibers of this type are well known in the art and are described, for example, in US Pat. Nos. 5,399,413, 5,493,421, 5,596,633, and 5,641,663. Microstructured fibers can be made, for example, from fused silica to which other materials can be added to modify its refractive index or to provide effects such as light amplification, sensitivity, etc.

[0004] The center-to-center spacing between the cladding inclusions is defined as the pitch (Λ). Photonic crystal fibers are typically characterized, at least in part, by the size of their core and the ratio of the size of the inclusions to the spacing or pitch (Λ) of the inclusions. By adjusting the size and pitch of the cladding inclusions, the zero dispersion wavelength (ZDW) of the fiber can be adjusted.

[0005] Photonic crystal fibers are generally suitable for use with high power light sources. Guiding relatively large powers in optical fibers can be important for several commercial applications, such as surgical and / or therapeutic light guiding, optical sensing, and material processing. Some of these applications include the transport of optical energy in the fiber and the exploitation of nonlinear effects, which are generally more pronounced when the optical power in the fiber is greater. The optical power can be continuous wave (CW), pulsed, or a mixture of both. The increased optical power in the fiber can be particularly pronounced for pulsed light, which can achieve large peak powers while having relatively modest average powers.

[0006] One limitation of the average power / spectral density carried by an optical fiber is the damage threshold of the fiber. In particular, when photonic crystal fibers are applied for supercontinuum generation and high power light is launched into the photonic crystal fiber through the input end (sometimes called the input end) of the photonic crystal fiber, it has been found that the photonic crystal fiber degrades over time depending on the peak power of the light launched. Furthermore, it has been found that the fiber section adjacent or close to the input end is more exposed to degradation the longer the distance from the input end.

[0007] US Patent No. 5,399,663 describes a method for mitigating the degradation caused by high power light delivered to a photonic crystal fiber by adding hydrogen and / or deuterium to the core material and optionally the cladding material. This addition was found to result in a measurable increase in the fiber's lifetime. In US Patent No. 5,399,663, this method was further improved by subjecting the photonic crystal fiber to annealing and / or high power radiation after the addition of hydrogen and / or deuterium. [Prior art documents] [Patent documents]

[0008] [Patent Document 1] US Patent Publication No. 2012195554 [Patent Document 2] U.S. Patent No. 8,406,594 [Patent Document 3] US Patent Publication No. 2011116283 [Patent Document 4] U.S. Patent No. 8,145,023 Summary of the Invention [Problem to be solved by the invention]

[0009] An object of the present invention is to provide a photonic crystal fiber suitable for generating a supercontinuum having extremely high decomposition resistance. In one embodiment, an objective is to provide a photonic crystal fiber suitable for supercontinuum generation that has a long lifetime even when used for supercontinuum generation.

[0010] A further object is to provide a supercontinuum light source made of a photonic crystal fiber having high degradation resistance, as well as suitable applications of such a supercontinuum light source. [Means for solving the problem]

[0011] These and other objects are achieved by the present invention or embodiments thereof described hereinafter in the present specification as defined in the claims. It has been found that the present invention, or embodiments thereof, have a number of additional advantages which will become apparent to those skilled in the art from the following description.

[0012] The photonic crystal fiber (PCF) of the present invention has a longitudinal axis and consists of a core extending along the length of the longitudinal axis and a cladding region surrounding the core. At least the cladding region includes a plurality of microstructures in the form of inclusions extending along the longitudinal axis of the photonic crystal fiber within at least a microstructured length section. The photonic crystal fiber has a length section resistant to decomposition, which can be the entire length of the photonic crystal fiber or simply that length section.

[0013] The term "length section resistant to decomposition" is used to indicate that this fiber length section has very high resistance to decomposition over time compared to other prior art fiber length sections.

[0014] The photonic crystal fiber contains hydrogen and / or deuterium within at least the length section resistant to decomposition within at least the microstructured length section, and the photonic crystal fiber further includes a main coating surrounding the cladding region within at least the length section resistant to decomposition, and this main coating is h airtight with respect to the hydrogen and / or deuterium at a temperature below T, where T h is at least about 50°C. Advantageously, T h is around at least the maximum predicted temperature of the photonic crystal fiber during use. Thereby, the hydrogen and / or deuterium diffusing from the fiber over time and / or during use is minimized. Preferably, T h is such that 50°C < Th < 250°C. In one embodiment, T h is at most about 150°C.

[0015] The term "hermetic" is used herein to mean that any diffusion of hydrogen and / or deuterium atoms through the coating is less than about 1% per day, as measured using Raman spectroscopy, for example at atmospheric conditions (i.e., the fiber is placed in air at 1 bar) at the relevant temperature, or by infrared spectroscopy, by measuring the absorption lines of H2 (or D2) at about 1240 nm or about 1870 nm for H2 or about 1715 nm for D2. Preferably, the hermetic coating allows diffusion to be less than 0.5% per day, less than about 0.1%, less than about 0.01% per day, etc.

[0016] The term "inclusions" refers to inclusions in a background material, which have a refractive index different from that of the background material surrounding the inclusions. The inclusions can be, for example, gas inclusions such as air, nitrogen, or any other gas, solid inclusions such as glass-type inclusions different from the background material and / or doped materials (materials that change the refractive index such as F, Ge, P, B), vacuum inclusions, or any combination thereof. Advantageously, at least some of the inclusions are gas or vacuum inclusions. It has been found that gas inclusions can act as reservoirs for hydrogen and / or deuterium, and these inclusions are closed on both sides of the decomposition-resistant length.

[0017] The phrase "radial distance" means the distance measured radially from the longitudinal axis. The term "substantially" as used herein should be construed to mean including normal product variances and tolerances.

[0018] It should be noted that the cladding region can have a homogenous background material or can have several regions, each of which has a different background material from each other. The background material is advantageously silica, optionally doped. In one embodiment, the cladding region consists of an inner cladding region and an outer cladding region surrounding the inner cladding region, the background material of the inner cladding region being different from that of the outer cladding region, as described, for example, in U.S. Pat. No. 8,600,207.

[0019] In one embodiment, the cladding region consists of an inner cladding region and an outer cladding region surrounding the inner cladding region, the background material of the inner cladding region having the same refractive index as the background material of the outer cladding region. In this embodiment, it is advantageous for the inner cladding region and the outer cladding region to have the same background material. The difference between the inner cladding region and the outer cladding region is, for example, a difference in the size, type and / or number of inclusions. The cladding region confines the light to the core, and advantageously the inclusions are arranged to affect the average refractive index to confine the light. This means that the inclusions should be relatively close to the core, preferably the center-to-center distance between at least some of the inclusions and the core is at most about 50 μm, preferably at most about 40 μm, such as at most about 30 μm, such as at most about 15 μm.

[0020] When describing materials for the cladding regions, inclusions, and core, amounts of hydrogen and / or deuterium are not included as part of the material. In one embodiment, the background material and the core material of the cladding region are substantially pure silica.

[0021] In one embodiment, the background material of the cladding region and the core material are fluoride doped silica. It has been found that even greater resistance to light induced degradation can be achieved if the core material is doped with fluoride, at least within the degradation resistant length.

[0022] Advantageously, the content of hydrogen and / or deuterium in the form of H2 or D2 within at least the core of the decomposition resistant length comprises at least about 0.001 ppm, such as at least about 0.01 ppm, such as from about 0.1 to about 10000 ppm. The amount of hydrogen and / or deuterium can be determined, for example, by determining the resulting absorption at the respective hydrogen or deuterium absorption peaks, as explained above.

[0023] The decomposition-resistant length can have any length. Advantageously, the decomposition-resistant length extends from an end of the photonic crystal fiber. In one embodiment, the decomposition-resistant length extends from an input end of the photonic crystal fiber. The input end is an end that is optically coupled or adapted to be coupled to a pump laser that launches light into the photonic crystal fiber. The decomposition-resistant length can thereby be positioned such that high power light is launched into the photonic crystal fiber. It has been observed that the main damage to prior art photonic crystal fibers occurs close to the input end of the photonic crystal fiber. By ensuring sufficient loading of hydrogen and / or deuterium at the input end of the photonic crystal fiber, the photonic crystal fiber becomes increasingly resistant to damage due to applied stresses, further increasing the lifetime of the entire photonic crystal fiber.

[0024] In this application, the phrase "inclusion ring" refers to cladding inclusions that are typically substantially equal distances from the core and aligned in a circular or non-circular ring surrounding the core. Typically, the inclusion ring is not perfectly circular, but has a shape with multiple gentle corners, such as a hexagonal shape. Preferably, all of the inclusions in an inclusion ring are substantially the same size, and preferably are the same material.

[0025] In one embodiment, the multiple inclusions in the cladding region are arranged in a pattern including at least two rings of inclusions surrounding the core. To obtain a photonic crystal fiber that is very good for supercontinuum generation, the center-to-center distance (also called pitch Λ) is advantageously at least about 1 μm, such as from about 1.5 μm to about 5 μm, or more. The inclusion diameter (d) is advantageously at least about 0.5 μm, such as from about 1 μm to about 3 μm. The relative diameter / pitch d / Λ is preferably from about 0.4 to about 0.85.

[0026] The inclusion diameter or diameter of an inclusion is also referred to as the characteristic diameter of an inclusion. The phrase "characteristic diameter" is a measure of the size of an inclusion (also referred to as a cladding feature). If the cladding feature is circular, the characteristic diameter is the diameter of the circle of the cladding feature. If the cladding feature is non-circular, the characteristic diameter is determined in one embodiment as the average of the maximum and minimum lengths of the cladding feature, and in another embodiment, the characteristic diameter is the diameter of a circle having an area corresponding to the calculated or measured area of ​​the cladding feature.

[0027] The inclusions may have equal or different diameters, and the inclusion diameter of each inclusion may be equal or different along the length of the fiber, as described above. Various preferred combinations of inclusions and their diameters are disclosed in co-pending application DKPA201470146, which is incorporated herein by reference, relating to the structure of the core, cladding region, and inclusions, and which discloses preferred embodiments of the photonic crystal fiber of the present invention, with the difference being that at least the lengths of photonic crystal fiber disclosed in PA201470146 have been modified to be or include decomposition-resistant lengths that include hydrogen and / or deuterium and hermetic coatings as described herein.

[0028] In one embodiment, the inclusion diameter (d) of each inclusion is equal along the length of the fiber, hi one embodiment, the inclusion diameter (d) of each inclusion varies along at least a section of the length of the fiber, such as along a tapered section.

[0029] The inclusions can in principle include or consist of any type of material, as described above, and the inclusions typically include a material that has a different refractive index than the background material that each inclusion is embedded or contained in. Examples of suitable inclusion materials are disclosed above.

[0030] In one embodiment, the inclusions include gas inclusions, such as air vents, e.g., air vents having air at low or ambient pressure (atmospheric pressure). Suitably, the gas inclusions are closed on both sides of the degradation-resistant length.

[0031] In one embodiment, the degradation-resistant length section is the entire length of the photonic crystal fiber, optionally excluding the closed end of the photonic crystal fiber. It has been found that closing the ends of the photonic crystal fiber further reduces the diffusion of hydrogen and / or deuterium out of the photonic crystal fiber, thereby increasing the decomposition resistance and thereby the lifetime of the entire photonic crystal fiber.

[0032] The ends of the photonic crystal fiber can be closed, for example, by crushing the photonic crystal fiber within a short end section, or by fusing short lengths of solid silica to each end.

[0033] Advantageously, the length of each closed end is relatively short along the length of the photonic crystal fiber to reduce the risk of losing light. Advantageously, the length of each closed end of the photonic crystal fiber is at most about 3 mm, such as at most about 2 mm, such as at most about 1 mm, such as at most about 0.5 mm, such as at most about 0.3 mm, such as at most about 0.2 mm.

[0034] In one embodiment, the plurality of inclusions in at least the decomposition-resistant length of the cladding region comprises an inner cladding region including an inner inclusion and an outer cladding region including an outer inclusion. This embodiment has been found to provide a very good photonic crystal fiber for supercontinuum generation. Advantageously, the inner inclusion is larger than the outer inclusion. Preferably, the inner inclusion includes at least one inclusion ring and the outer inclusion includes at least one outer inclusion ring. More preferably, in one embodiment, the diameter d of the inner inclusion is greater than d. inner is the diameter of the outer inclusion d outer The optical fiber may be at least about 15%, such as at least about 20%, such as at least about 25%, such as at least about 30% greater than the optical fiber of the present invention. This provides a photonic crystal fiber for supercontinuum generation with high stability even in the blue light range. Furthermore, the degradation-resistant length of the photonic crystal fiber provides a long lifetime even when operated at very high powers.

[0035] In one embodiment, d inner is preferably at least about 1.5 μm, such as from about 1.8 to about 4 μm, such as from about 2 to about 2.5 μm. In one embodiment, d outer is preferably less than about 2.5 μm, such as about 0.8 to about 2 μm, such as about 1 to about 1.8 μm.

[0036] Advantageously, the background material of the inner cladding region and the background material of the outer cladding region are identical, and optionally also identical to the core material. Advantageously, the background material of the inner cladding region and the background material of the outer cladding region, and optionally the core material, are substantially pure silica, or optionally fluorine-doped silica.

[0037] Advantageously, the outer cladding region includes at least three outer inclusion rings. The structure and arrangement of the inclusions, in one embodiment, are as described in co-pending application DKPA201470146, e.g., as described and illustrated in Figures 2a and 3a of DKPA201470146, except that the photonic crystal fiber is modified to be or to include decomposition-resistant lengths that include hydrogen and / or deuterium and hermetic coatings as described herein.

[0038] In one embodiment, the cladding region within at least the degradation-resistant length comprises an inner cladding region including inclusions and an outer cladding region surrounding the inner cladding region, the radial distance between an outermost inclusion of the inner cladding region and the primary coating being at least about 10 μm. Optionally, material between the inner cladding region and the primary coating forms a reservoir for hydrogen and / or deuterium.

[0039] By having a relatively large radial distance between the outermost inclusions of the inner cladding region and the primary coating, a large area reservoir for hydrogen and / or deuterium can be formed which can gradually diffuse into the core as hydrogen and / or deuterium is consumed within the core, thereby maintaining a relatively stable and sufficient hydrogen and / or deuterium concentration within the core.

[0040] In one embodiment, the material between the inner cladding region and the primary coating forms a reservoir for hydrogen and / or deuterium, for example the reservoir for hydrogen is porous silica.

[0041] In one embodiment, the reservoir for hydrogen between the inner cladding region and the primary coating comprises glass or plastic that has a higher adsorption capacity for hydrogen and / or deuterium than the background material of the inner cladding region.

[0042] Those skilled in the art can find suitable materials by several hydrogen and / or deuterium loading tests. The core can have any size in principle. The larger the core, the more power can be delivered to the photonic crystal fiber, but if the core becomes too large, it may be difficult to extend the bandwidth to the desired range. To provide a wide and stable supercontinuum light, it is advantageous for the core diameter to be at least about 1 μm, preferably at least about 2 μm. This ensures that the optical fiber can withstand the power required for supercontinuum generation and / or large powers in general.

[0043] In one embodiment, the core diameter of the core, at least within the degradation-resistant length, is about 10 μm or less, such as about 8 μm or less, such as about 6 μm or less. In one embodiment, the core diameter is in the range from about 3 μm, such as about 3 μm to about 7 μm.

[0044] In one embodiment, the core is defined by inclusions, ie, the inclusions surrounding the core have different refractive indices, thereby forming the core. Advantageously, the photonic crystal fibre is made from silica, and is optionally doped, as described above.

[0045] In one embodiment, the material of the core and / or cladding regions is doped. In one embodiment, the center-to-center distance between the innermost inclusion and the core, at least within the degradation-resistant length, is less than about 50 μm, preferably less than about 40 μm, such as less than about 30 μm, such as less than about 10 μm.

[0046] The core is a solid core. The term "solid core" means that the core is made of a solid material and is substantially free of gas voids. In one embodiment, the core is a microstructured core.

[0047] Advantageously, the core is a solid core, optionally comprising a solid microstructure. The core, in one embodiment, is substantially pure silica. As mentioned above, a very beneficial property of photonic crystal fiber is the ability to tune the zero dispersion wavelength (ZDW) of the fiber by adjusting the size and pitch of the cladding inclusions.

[0048] In one embodiment, the anomalous dispersion of the photonic crystal fiber for at least one wavelength is between 1000 nm and 1100 nm. Preferably, the anomalous dispersion of the photonic crystal fiber is about 1030 nm or 1064 nm.

[0049] In one embodiment, the core of the photonic crystal fiber is single mode at the pump wavelength. Advantageously, the core of the photonic crystal fiber is spatially single mode at 1064 nm.

[0050] Spatially single mode means that for a 2m length of fiber, the loss of higher order modes is at least 19.3dB higher than the fundamental mode. This can be measured, for example, using the S^2 method. See "Spatially and spectrally resolved imaging of modal content in large mode-area fibers," JWNicholson et al, Optics Express, vol.16, Issue 10, p.7233, 2008.

[0051] In one embodiment, the photonic crystal fiber core is single mode at 1030 nm. In one embodiment, the core of the photonic crystal fiber is multimode at pump wavelengths such as 1064 nm or 1030 nm.

[0052] Advantageously, at least the core of the photonic crystal fiber is essentially free of germanium. It has been found that the inclusion of germanium can result in certain structural defects in the silica, and therefore it is desirable for the germanium content to be as low as possible. Hydrogen and / or deuterium have also been found to increase the resistance to structural defects induced by germanium, and therefore, if the photonic crystal fiber contains germanium, the addition of hydrogen and / or deuterium can be increased.

[0053] In one embodiment, the entire photonic crystal fiber is essentially germanium free. In one embodiment, the entire photonic crystal fiber is essentially undoped silica. In one embodiment, at least a portion of the photonic crystal fiber is doped with fluorine, for example at a level greater than 1000 ppm.

[0054] For purposes of the present invention, the phrase "essentially germanium-free" means that the concentration of germanium is less than about 10 ppm, including zero. In the present invention, the phrase "essentially undoped" refers to a concentration of refractive index modifying dopants, such as active materials such as Ge, B, F, P, Al, and / or the rare earth elements Er or Yb, at levels below 1000 ppm. In one embodiment, the dopant levels are even lower, such as about 1 ppm or less.

[0055] In one embodiment, at least the core of the photonic crystal fiber is essentially free of active materials such as rare earth ions. In one embodiment, the entire photonic crystal fiber is free of active ions.

[0056] In the present invention, the phrase "essentially free of active materials" means that the concentration of active materials, such as the rare earth elements Er or Yb, is at a level below 1000 ppm. Preferably, the level of active materials is even lower, such as about 1 ppm or less.

[0057] The primary coating may be made from any material that provides a hermetic coating as defined above. Examples of materials suitable for the primary coating include materials comprising nitrides (such as carbon nitride, silicon nitride, boron nitride, silicon nitride, and / or silicon oxynitride), carbon, aluminum, metallic glasses, or combinations comprising one or more of the above.

[0058] A particularly suitable material for the main coating is carbon. The thickness of the primary coating depends on the type of material. In general, it is desirable to select a material for the primary coating that is hermetic at a relatively small thickness, thereby ensuring high flexibility and bendability of the photonic crystal fiber without substantial risk of crack formation.

[0059] In one embodiment, the thickness of the primary coating is from about 5 nm to about 10 μm, such as from 10 nm to about 5 μm, such as from about 20 nm to about 1 μm. In one embodiment, the thickness of the primary coating is about 30 nm.

[0060] In the case of a metallic main coating, the thickness is advantageously between 15 μm and 60 μm. In one embodiment, the primary coating is o’ Diffusion open to hydrogen and / or deuterium at temperatures above T o is T hIt is larger, thereby allowing hydrogen and / or deuterium to be loaded into the photonic crystal fiber after the coating has been applied. This provides a preferred embodiment for producing photonic crystal fibers, since the primary coating protects the fiber during mechanical and dust-free handling. Furthermore, a more homogeneous and precise content of hydrogen and / or deuterium can be loaded. It has been found that without the primary coating, the photonic crystal fiber starts to lose the loaded hydrogen and / or deuterium immediately after loading, and in fact an undesirably large amount of hydrogen and / or deuterium can be lost before the primary coating is applied. It is therefore desirable to initially load the photonic crystal fiber with a larger amount of hydrogen and / or deuterium, if the primary coating is applied after loading.

[0061] Preferably, T o is at least about 25° C., and preferably T o is in the interval of about 50° C. to about 300° C., such as at least about 70° C., such as at least about 100° C. In one embodiment, T o is determined at 1 bar. In one embodiment, T o is calculated at 100 bar.

[0062] In general, T o It is desirable for T to be greater than the temperature (or expected temperature) of the photonic crystal fiber during use. o Advantageously, the softening temperature of the material should not be increased at the risk of deforming the material.

[0063] A photonic crystal fiber may advantageously include one or more additional coatings above or below the primary coating. Such additional coatings may have the purpose of providing additional mechanical protection, reducing the risk of cracking in the main coating, and / or providing an outermost appearance and / or feel.

[0064] The additional coating is preferably a polymeric coating, and advantageously comprises an acrylate, a polyimide, a polyurethane, a silicone, or any combination thereof. In one embodiment, when the primary coating is carbon, the additional coating is a metal such as aluminum, gold, copper, nickel, a metallic glass, or a combination, or an alloy containing at least one of the above metals.

[0065] In one embodiment, the photonic crystal fiber includes at least one tapered length, where the core in a first end of the tapered length has a core diameter D1 and the core in a second end of the tapered length has a core diameter D2, where D1 is greater than D2, preferably D2 is up to about 0.95 times D1, such as about 0.1 to about 0.9 times D1. Advantageously, the first end is an input end.

[0066] It has been found that the supercontinuum generation properties of photonic crystal fibers can be increased by tapering the photonic crystal fiber, for example as described in PCT / DK2014 / 050205. In one embodiment, the photonic crystal fiber is as described in PCT / DK2014 / 050205, with the difference that the photonic crystal fiber has been modified to be or include a decomposition-resistant length that includes hydrogen and / or deuterium and a hermetic coating as described herein.

[0067] Preferably, the first end of the tapered length is at the input end of the fiber or up to 5 cm along the length from the input end of the fiber, and preferably the first end of the tapered length is adjacent to or contained within the degradation-resistant length.

[0068] Thereby, the photonic crystal fiber is particularly protected from degradation when the peak powers are very large. In one embodiment, the photonic crystal fiber does not contain any seams.

[0069] In one embodiment, the photonic crystal fiber comprises two or more spliced ​​fiber lengths, and at least one of the spliced ​​fiber lengths is or comprises a decomposition-resistant length.

[0070] It has been found that in order to provide an optimal supercontinuum, a fiber comprising fiber length sections with different properties can be advantageous, for example as described in PCT / DK2014 / 050206.

[0071] In one embodiment, the photonic crystal fiber comprises a first length comprising or consisting of a decomposition-resistant length and a second length spliced ​​to the first length, the second length having a lower hydrogen and / or deuterium content than the decomposition-resistant length.

[0072] In one embodiment, the photonic crystal fiber comprises: a first length section having a first length L1, in which inclusions of the optical fiber have a first pitch Λ1, a first inclusion diameter d1, and a first inclusion relative size d1 / Λ1, at least in a first cross-section of the first length section perpendicular to the longitudinal axis; a second length section having a second length L2, wherein the microstructural elements of the optical fiber have, at least in a second cross-section of the second length section perpendicular to the longitudinal axis, a second pitch Λ2, a second inclusion diameter d2, and a second inclusion relative size d2 / Λ2; At least one of the first length L1 and the second length L2 comprises or consists of a degradation-resistant length section.

[0073] One or more of the lengths of fiber may be tapered. In one embodiment, the photonic crystal fiber of the present invention is as described in PCT / DK2014 / 050206, with the difference that at least the lengths of photonic crystal fiber disclosed in PCT / DK2014 / 050206 have been modified to be decomposition-resistant lengths comprising hydrogen and / or deuterium and a hermetic coating as described herein.

[0074] In one embodiment, the photonic crystal fiber comprises a mode adapter extending along the length of the photonic crystal fiber within a mode field adapted length section that extends at least from the input end of the photonic crystal fiber or extends up to about 5 cm from the input end of the photonic crystal fiber. Preferably, the mode field adapted length section has a length of at least about 5 cm, such as at least about 10 cm, such as at least about 20 cm. Advantageously, the mode field adapted length section is partially or completely contained within the degradation resistant length section.

[0075] The present invention also includes a method of making a photonic crystal fiber, the method comprising: - preparing a preform including a preform structure for a core and cladding region of a photonic crystal fiber; - drawing the preform to obtain the core and cladding regions of the photonic crystal fiber; subjecting at least the degradation-resistant length of the photonic crystal fiber to loading with hydrogen and / or deuterium; applying a primary coating to at least a degradation-resistant length of the photonic crystal fiber.

[0076] Preferably, the degradation-resistant length is the entire length of the photonic crystal fiber, optionally excluding the closed end of the photonic crystal fiber. Advantageously, the closed end is as described above.

[0077] In one embodiment, the method includes subjecting the photonic crystal fiber to loading with hydrogen and / or deuterium prior to applying the primary coating. If the loading of hydrogen and / or deuterium is performed prior to applying the main coating, the loading of hydrogen and / or deuterium includes placing the photonic crystal fiber in a chamber containing hydrogen and / or deuterium at a pressure of at least about P1 and a temperature of at least about T1 for a duration of at least t1.

[0078] To provide for relatively fast addition of hydrogen and / or deuterium, the temperature and optionally the pressure are advantageously increased. In one embodiment, T1 is preferably at least 40° C., such as from about 50° C. to about 250° C., such as from about 100° C. to about 800° C., such as up to about 500° C., such as up to about 200° C. In practice, the photonic crystal fiber material sets an upper limit for the temperature T1.

[0079] The addition time t1 is preferably at least about 1 hour, such as from about 2 hours to about 200 hours, such as from about 24 hours to about 96 hours. The addition pressure P1 is preferably from about 1 bar, such as from more than 1 bar to about 250 bar, such as from about 50 bar to about 200 bar, such as from about 100 bar to about 200 bar.

[0080] In this embodiment, it is desirable to apply the primary coating within a few hours of dosing, since otherwise much of the doped hydrogen and / or deuterium may diffuse out of the fiber. Preferably, the primary coating is applied to the photonic crystal fiber within about 5 hours, such as within about 2 hours, of the end of dosing.

[0081] In a preferred embodiment, the method includes the step of subjecting the photonic crystal fiber to loading with hydrogen and / or deuterium after applying the primary coating. Thereby, little of the loaded hydrogen and / or deuterium diffuses out of the photonic crystal fiber after loading, which can increase the quality of the photonic crystal fiber as described above. Furthermore, the amount of loaded hydrogen and / or deuterium can be smaller, and as a result, the loading time can be shorter.

[0082] Preferably, the method comprises the steps of: - preparing a preform including a preform structure for a core and cladding region of a photonic crystal fiber; - drawing the preform to obtain the core and cladding regions of the photonic crystal fiber; applying a primary coating to the photonic crystal fiber; At least about T o exposing the photonic crystal fiber to hydrogen and / or deuterium at a temperature of Photonic crystal fiber h followed by a cooling step.

[0083] Cooling can be achieved by passive cooling (simply letting the photonic crystal fiber cool, for example at room temperature) or by active cooling, for example by blowing cool air over the photonic crystal fiber.

[0084] In one embodiment, if the primary coating is applied prior to the addition of hydrogen and / or deuterium, the addition is preferably performed at a pressure of at least about P2 and at least about T2>T o The method includes placing the photonic crystal fiber in a chamber containing hydrogen and / or deuterium at a temperature of t for a duration of at least t2.

[0085] In one embodiment, T2 is suitably at least 50° C., such as from about 75° C. to about 250° C., such as from about 100° C. to about 200° C., or more. In practice, the material of the main coating or any additional coatings applied sets an upper limit for the temperature T2, which means that for some types of main coatings, the temperature T2 can be up to about 500° C. or even up to about 800° C.

[0086] The addition time T2 is suitably at least about 1 hour, such as from about 2 hours to about 200 hours, such as from about 24 hours to about 96 hours. The addition pressure P2 is preferably from about 1 bar, such as from more than 1 bar to about 250 bar, such as from about 50 bar to about 200 bar, such as from about 100 bar to about 200 bar.

[0087] If the photonic crystal fiber contains gas inclusions, the method of making the photonic crystal fiber preferably includes closing the gas inclusions on either side of the degradation-resistant length. The method preferably includes closing the gas inclusions on both ends of the photonic crystal fiber.

[0088] In one embodiment, the method includes closing the gas inclusion before subjecting the photonic crystal fiber to loading with hydrogen and / or deuterium, thereby reducing the risk of hydrogen and / or deuterium diffusing through the inclusion.

[0089] In one embodiment, the method includes subjecting the photonic crystal fiber to loading with hydrogen and / or deuterium prior to closing the gas inclusion at the end of the fiber. In one embodiment, loading can include loading via an unclosed gas inclusion, followed by closing the gas inclusion at the end of the fiber. In this embodiment, a primary coating can be applied prior to loading.

[0090] The material of the primary coating as well as its thickness may be as described above. In one embodiment, the primary coating is applied to the photonic crystal fiber by chemical vapor deposition (CVD) or similar or modified deposition methods.

[0091] In one embodiment, the primary coating is a carbon coating and the method includes applying the primary carbon coating by a chemical vapor deposition process. Advantageously, the CVD process includes passing the fiber through a reactor chamber of a reactor and subjecting the fiber in the reactor chamber to a reactor gas at a temperature of at least about 700° C. Suitably, the temperature is in the interval between about 700° C. and about 1100° C., such as between about 700° C. and about 900° C. Temperatures above 900° C. may result in the formation of a carbon coating having a diamond-like structure.

[0092] The method of carbon coating the fiber can be, for example, as described in US Pat. No. 5,000,541. The reactor gas may advantageously contain carbonaceous compositions, preferably alkynes (C), such as acetylene (C2H2). n H 2n-2 ), and / or alkenes (C n H 2n+2 ) where n is 2 to 10, 2 to 4, etc. Suitably, the reactor gas is substantially free of oxygen.

[0093] It has been found to be very effective to apply the primary carbon coating immediately after drawing the fiber in the drawing tower. This ensures that the surface of the fiber is not contaminated before the application of the primary coating, and it has further been found that by applying the primary carbon coating immediately after drawing the fiber, without allowing the fiber to cool below the reaction temperature for the reactor gases before applying the carbon coating, it is not necessary to reheat the fiber before carbon coating. In an alternative embodiment, the fiber is reheated to the reaction temperature. The reaction temperature in the reaction chamber is advantageously at least about 700° C., such as from about 800° C. to about 1100° C.

[0094] Advantageously, the reactor is an integral part of the drawing tower, whereby the fiber is suitably passed through the reactor chamber, carbon coated and then wound, ie, subjected to an in-line process.

[0095] In one embodiment, the method includes applying an additional coating onto the carbon coating, preferably a polymeric or metallic coating as described above, preferably applied onto the carbon coating in a draw tower prior to winding the fiber.

[0096] In one embodiment, the primary coating is a metal coating and the method includes applying the primary metal coating by passing the fiber through a liquid metal melt, wherein the temperature of the fiber as it enters the melt is lower than the temperature of the metal melt.

[0097] The temperature of the metal melt depends on the type of metal, In one embodiment, the metal coating is applied to the fiber in a drawing tower after immersing the fiber in water and allowing it to at least partially cool, preferably prior to winding the fiber in an in-line process.

[0098] In one embodiment, the method includes the step of applying at least one additional coating, for example, outside the primary coating. The present invention also includes a supercontinuum source comprising a photonic crystal fiber as described above and a pump source arranged to deliver pump pulses to an input end of the photonic crystal fiber.

[0099] In one embodiment, a photonic crystal fiber is configured to generate supercontinuum light having a bandwidth broadened relative to the bandwidth of the pump pulse. Advantageously, the photonic crystal fiber is arranged to generate supercontinuum light having a bandwidth that is at least about 100% broadened relative to the bandwidth of the pump pulses, such as at least about 200% broadened.

[0100] In one embodiment, the supercontinuum generated has a bandwidth that spans at least an octave. The pump source can be any kind of pump source capable of providing pump pulses of sufficiently high energy, for example a mode-locked pump source such as a MOPA, with or without a pulse picker (gating means).

[0101] The pump pulses preferably have a relatively high peak power, hi one embodiment, the pump pulses generated by the pulse source are high peak power pulses having a peak power at the input end of the photonic crystal fiber of at least about 5 kW, such as at least about 10 kW, such as at least about 15 kW, such as at least about 20 kW.

[0102] In one embodiment, the pulse width of the pump pulses generated by the pulse source is at most about 200 ps, ​​such as at most about 100 ps, ​​such as at most about 50 ps, ​​such as at most about 30 ps, ​​such as at most about 10 ps, ​​such as at most about 8 ps, such as at most about 5 ps, such as at most about 3 ps, or such as at most about 1 ps.

[0103] Advantageously, the pulse width of the pump pulses generated by the pulsed source is at least about 200 fs, such as at least about 1 ps, such as at least about 5 ps. Preferably, the repetition rate of the pump pulses generated by the pulse source is at least about 100 kHz, at least about 10 kHz, at least about 1 MHz, etc., and the repetition rate is preferably tunable using, for example, an electro-optic modulator (EOM), an acousto-optic modulator (AOM), or an acousto-optic tunable filter (AOTF), which simultaneously acts as a wavelength filter.

[0104] In one embodiment, the wavelength of the pump pulses generated by the pulse source is from about 900 nm to about 1100 nm, such as about 1030 or about 1064 nm. In one embodiment, the average output power of the supercontinuum light source is at least about 1 W, such as at least about 5 W, such as at least about 10 W, such as at least about 20 W, such as at least about 50 W, such as at least about 100 W, or even at least about 500 W. Generally, it has been found that the degradation-resistant lengths of the photonic crystal fiber of the present invention make it possible to provide high power supercontinuum light sources having a desired high output power while at the same time having a surprisingly long lifetime.

[0105] In one embodiment, the output of the supercontinuum light source comprises wavelengths less than about 600 nm, such as less than about 550 nm, such as less than about 450 nm, such as less than about 420 nm, such as less than about 410 nm, such as less than about 400 nm, such as less than about 380 nm, such as less than about 360 nm.

[0106] In one embodiment, the output of the supercontinuum light source comprises wavelengths greater than about 1800 nm, such as greater than about 2000 nm, such as greater than about 2200 nm. In one embodiment, the supercontinuum source further comprises a spectral filtering unit arranged to filter the output of the supercontinuum source into a filtered SC output having a central wavelength λ1 and an output bandwidth BW1, at least one of which is tunable. The output bandwidth BW1 is advantageously less than about 5 nm (at least in one tuning). The spectral filtering unit may, for example, comprise an AOTF.

[0107] The invention also provides an illumination source comprising a supercontinuum light source as described above. Preferably, the illumination source is suitable for stimulated emission suppression. In one embodiment, the illumination source is adapted for fluorescence imaging, Fluorescence Lifetime Imaging (FLIM), Total Internal Reflection Fluorescence (TIRF) microscopy, fluorescence resonance energy transfer (FRET), broadband spectroscopy, nanophotonics, flow cytometry, industrial testing such as metrology, ring-down spectroscopy such as gas sensing, hyperspectral spectroscopy, crop analysis, e.g., of fruits, and analytical spectroscopy such as time of flight spectroscopy (TCSPC), single molecule imaging, and / or combinations thereof.

[0108] In one embodiment, the microscope is preferably an optical fluorescence microscope, such as an optical fluorescence microscope based on Fluorescence Lifetime Imaging (FLIM), Total Internal Reflection Fluorescence (TIRF) microscopy. In one embodiment, the spectrometer is preferably a broadband spectrometer.

[0109] The invention also comprises an optical coherence tomograph for optical coherence tomography (OCT), the tomograph comprising an illumination source as described above.

[0110] The present invention also includes an industrial inspection comprising the above-described illumination source. All of the above-mentioned features of the invention and embodiments of the invention, including ranges and preferred ranges, can be combined in various ways within the scope of the invention, unless there is a specific reason not to combine such features.

[0111] The above and / or additional objects, features, and advantages of the present invention will be further elucidated by the following illustrative and non-limiting description of embodiments of the present invention, with reference to the accompanying drawings. [Brief description of the drawings]

[0112] [Figure 1]1 is a cross-sectional view of a photonic crystal fiber according to one embodiment of the present invention. [Diagram 2] FIG. 2 is a cross-sectional view of a photonic crystal fiber according to another embodiment of the present invention. [Diagram 3] FIG. 4 is a cross-sectional view of a photonic crystal fiber according to yet another embodiment of the present invention. [Figure 4a] 1 is a side view of a photonic crystal fiber according to one embodiment of the present invention. [Figure 4b] 1 is a cross-sectional view of a first length of photonic crystal fiber according to one embodiment of the present invention. [Figure 4c] 3A is a cross-sectional view of a second length of photonic crystal fiber according to an embodiment of the present invention. [Diagram 5] 1 is a schematic diagram of one embodiment of a supercontinuum radiation source according to the present invention. [Figure 6] Schematic of a drawing tower with a coating station including a reactor for applying a carbon coating, where the main coating and additional coatings are applied in an in-line process. [Figure 7] Schematic of a drawing tower with a coating station for applying metallic coatings, where the main coating and additional coatings are applied in an in-line process. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0113] The figures are schematic and may be simplified for clarity, and the same reference numbers are used throughout for identical or corresponding parts. Further scope of applicability of the present invention will become apparent from the following description. It should be understood, however, that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.

[0114] The photonic crystal fiber shown in FIG. 1 has a core 1 and cladding regions 2, 3 surrounding the core 1. The photonic crystal fiber has a length and a longitudinal axis, not shown, which in the embodiment shown coincides with the central axis of the core. The cladding regions consist of an inner cladding region 2 and an outer cladding region 3. The inner cladding region includes a plurality of microstructures in the form of inclusions, which extend along the longitudinal axis of the photonic crystal fiber. As mentioned above, the inclusions can include any material, but are advantageously gaseous inclusions, such as air inclusions. Advantageously, the inclusions are crushed at one or more locations along the length of the fiber, such as at each end of the degradation-resistant length, which in one embodiment is substantially the entire length of the photonic crystal fiber, as mentioned above.

[0115] As will be appreciated, the cross-section of the photonic crystal fiber is a cross-section within a degradation-resistant length of the photonic crystal fiber, which may consist of the entire length of the photonic crystal fiber or only a portion of the length of the photonic crystal fiber, as discussed above.

[0116] The photonic crystal fiber is loaded with hydrogen and / or deuterium (not shown), preferably in the form of molecular hydrogen and / or molecular deuterium (H2 / D2). Hydrogen and / or deuterium are typically present in both the core 1 and the cladding regions 2, 3. The photonic crystal fiber is h The primary coating 4 is hermetic to hydrogen and / or deuterium at temperatures below 0.5° C. Various types of suitable primary coatings have been described above.

[0117] The photonic crystal fiber includes an additional coating 5 for mechanical protection and optionally for providing a desired appearance and / or texture to the photonic crystal fiber. In use, as mentioned above, when photonic crystal fibers are subjected to high peak power light, this light can induce defects in the core material. This effect is believed to be caused by a variety of chemical reactions and is sometimes referred to as light-induced decomposition or photodarkening. Hydrogen and / or deuterium have been found to mitigate decomposition by combining with the material, for example by quenching free radicals.

[0118] As the hydrogen and / or deuterium in the core 1 is consumed, fresh hydrogen and / or deuterium migrate from the cladding regions 2, 3 to the core 1. Due to the primary coating 4 being gas-tight against hydrogen and / or deuterium, the amount of hydrogen and / or deuterium required can be relatively low when the photonic crystal fiber is in use or stored prior to use, and / or the photonic crystal fiber is protected from excessive decomposition for long periods of time, such as up to several years, e.g., 3, 4, or even 5 years or more.

[0119] The photonic crystal fibre is preferably made from silica as described above and is, for example, doped. The photonic crystal fiber shown in FIG. 2 has a core 11 and a cladding region 12 surrounding the core 11. The photonic crystal fiber has a length and a longitudinal axis, not shown, which in the illustrated embodiment coincides with the central axis of the core 11. The cladding region 12 includes a plurality of microstructures 12a in the form of inclusions in a cladding background material 12b. The inclusions 12a extend along the longitudinal axis of the photonic crystal fiber. As mentioned above, the inclusions can include any material, but are advantageously gaseous inclusions, such as air inclusions. Advantageously, the inclusions are crushed at one or more locations along the length of the fiber, such as at each end of a degradation-resistant length, which in one embodiment is substantially the entire length of the photonic crystal fiber, as mentioned above.

[0120] A plurality of inclusions 12a are arranged within the cladding region in a pattern including several inclusion rings surrounding the core, the innermost inclusion ring surrounding the core being indicated by dashed ring 12c.

[0121] As will be appreciated, the cross-section of the photonic crystal fiber is a cross-section within a degradation-resistant length of the photonic crystal fiber, which may consist of the entire length of the photonic crystal fiber or only a portion of the length of the photonic crystal fiber, as discussed above.

[0122] Photonic crystal fibers are h The primary coating 14 includes a primary coating 14 that is hermetic to hydrogen and / or deuterium at temperatures below 0.5° C. Various types of suitable primary coatings have been described above. The photonic crystal fiber includes an additional layer of material 16 that is sufficiently remote from the core 11 to have any effect as a cladding (ie, the refractive index of the material of layer 16 does not affect the light guiding in the core).

[0123] The radial distance 17 between the outermost of the inclusions 12a in the cladding region and the primary coating 14 is at least about 10 μm. The additional material layer 16 may be the same or a different material as the cladding background material 12b. The additional material layer 16 is advantageously selected to have a high capacity for hydrogen and / or deuterium, thereby acting as a reservoir for hydrogen and / or deuterium.

[0124] As mentioned above, the photonic crystal fiber is loaded with hydrogen and / or deuterium (not shown), which is typically present in both the core 11 and the cladding region 12, as well as in the additional layer of material 16.

[0125] In use, as described above, when the photonic crystal fiber is subjected to high peak powers of light, as the hydrogen and / or deuterium in the core 11 is consumed, fresh hydrogen and / or deuterium migrates from the cladding region 12 and material layer 16 to the core 11. Due to the primary coating 14 being gas-tight to hydrogen and / or deuterium, the amount of hydrogen and / or deuterium required when the photonic crystal fiber is in use or stored prior to use can be relatively low and / or the photonic crystal fiber is protected from excessive decomposition for extended periods of time, such as up to several years, e.g., 3, 4, or even 5 years or more.

[0126] The photonic crystal fibre is preferably made from silica as described above and is, for example, doped. The photonic crystal fiber shown in Figure 3 has a core 21 and cladding regions 22, 23 surrounding the core 21. The photonic crystal fiber has a length and a longitudinal axis (not shown), which in the embodiment shown coincides with the central axis of the core 21.

[0127] The cladding regions consist of an inner cladding region 22 and an outer cladding region 23. The inner cladding region 22 includes an inner inclusion 22a within an inner cladding background material 22b. The outer cladding region 23 includes an outer inclusion 23a within an outer cladding background material 22b.

[0128] Inner inclusion 22a includes two inner inclusion rings and outer inclusion 23a includes five outer inclusion rings. The inclusions 22a, 23a extend along the longitudinal axis of the photonic crystal fiber. As noted above, the inclusions may comprise any material, but are advantageously gaseous inclusions, such as air inclusions. Advantageously, the inclusions are crushed at one or more locations along the length of the fiber, such as at each end of the degradation-resistant length, which in one embodiment is substantially the entire length of the photonic crystal fiber, as noted above.

[0129] The background material 22b of the inner cladding region 22 and the background material 23b of the outer cladding region 23, and optionally the core material, are advantageously the same material, such as silica, optionally doped with fluorine.

[0130] As will be appreciated, the cross-section of the photonic crystal fiber is a cross-section within a degradation-resistant length of the photonic crystal fiber, which may consist of the entire length of the photonic crystal fiber or only a portion of the length of the photonic crystal fiber, as discussed above.

[0131] Photonic crystal fibers are h The primary coating 24 includes a primary coating 24 that is hermetic to hydrogen and / or deuterium at temperatures below 0.5° C. Various types of suitable primary coatings have been described above. The photonic crystal fiber includes an additional layer of material 26 that is far enough from the core 21 that it has any effect as a cladding.

[0132] The additional layer of material 26 is, in this embodiment, the same as the cladding background material 23b. The radial distance 27 between the outermost of the inner inclusions 22a of the inner cladding region and the primary coating 24 is at least about 10 μm.

[0133] The photonic crystal fiber is loaded with hydrogen and / or deuterium (not shown), as mentioned above, which is typically present in both the core 21 and the cladding regions 22, 23, as well as in the additional layer of material 26.

[0134] In use, as described above, when the photonic crystal fiber is subjected to high peak powers of light, as the hydrogen and / or deuterium in the core 21 is consumed, fresh hydrogen and / or deuterium migrates from the cladding regions 22, 23 and material layer 26 into the core 21.

[0135] Figures 4a, 4b and 4c show an embodiment of a photonic crystal fiber 30 comprising two spliced ​​fiber lengths, at least one of which is or comprises a decomposition-resistant length as described above. This type of fiber is also called a spliced ​​cascaded optical fiber. Figure 4b shows a cross-sectional view of a first length 31 and Figure 4c shows a cross-sectional view of a second length 32 spliced ​​to the first length. Preferably, at least the first length 31 of photonic crystal fiber is a decomposition-resistant length as described above.

[0136] The photonic crystal fiber 30 is arranged to generate supercontinuum light when light having a first wavelength λ1, for example, about 900 nm to about 1100 nm, is transmitted into an input end 34 of the photonic crystal fiber 30.

[0137] The optical fiber 30 comprises along its length a first length 31, a second length 32, and a joint 33 between the first length 32 and the second length 33. The optical fiber 30 may optionally include end caps, not shown, to close the containment.

[0138] The first length section 31 has a core 41a with a first core diameter W1 and a cladding region 42a with a first pitch Λ1, a first inclusion diameter d1, and a first inclusion relative size Λ1 / d1. h The primary coating 44a is hermetic to hydrogen and / or deuterium at temperatures below 100° C. Various types of suitable primary coatings are described above. At least the first length is loaded with hydrogen and / or deuterium.

[0139] The second length section 32 has a core 41b having a second core diameter W2 and a cladding region 42b having a second pitch Λ2, a second inclusion diameter d2, and a second inclusion relative size Λ2 / d2.

[0140] Advantageously, at least one of the dimensions of the first core diameter W1, the first pitch Λ1, the first inclusion diameter d1, and the first inclusion relative size Λ1 / d1 is different from the corresponding dimensions of the second core diameter W2, the second pitch Λ2, the second inclusion diameter d2, and the second inclusion relative size Λ2 / d2 of the second length section 32.

[0141] Over the entire first length 31 the fiber dimensions are substantially constant, and over the entire second length 32 the fiber dimensions are substantially constant. The respective lengths of the first length section 31 and the second length section 32 are in this embodiment 1-10 m and 10 m, respectively, but it should be understood that these lengths are given merely as examples and that the fibre length sections can in principle have any other length.

[0142] FIG. 5 is a schematic diagram of a supercontinuum source. The supercontinuum source 50 consists of a photonic crystal fiber 54 having a length of degradation resistant section as described above, and a pump source 52. The photonic crystal fiber has two ends, an input end 55 and an output end 56. In FIG. 5, the input end 55 of the photonic crystal fiber 54 has or is optically connected to a mode adapter 58 that matches the mode of the pump pulses from the pump source 52. In FIG. 5, the mode adapter 58 is shown as being larger than the optical fiber 54, but this is for illustrative purposes only, and in practice the mode adapter can have any suitable outer dimensions, for example, outer dimensions similar to those of the optical fiber 54. The output end 56 of the optical fiber 54 is shown as being a free end, but the output end may have an end cap or may be spliced ​​to further equipment.

[0143] The pump light source 52 has an output 53 arranged to deliver light into the photonic crystal fiber 54 via a delivery fiber 57 and a mode adapter 58, in which a supercontinuum spectrum is generated and output at an output end 56 of the photonic crystal fiber. The delivery fiber 57 may, for example, be omitted or replaced by an optical element, such as, for example, a lens.

[0144] The drawing tower shown in FIG. 6 is in the process of drawing a photonic crystal fiber 63 from a preform 63a. The preform is sealed in a pressure controlled chamber 61, which consists of one or more pressure chambers that control the pressure of the gas contents in the photonic crystal fiber. The bottom extends into a furnace 62, where the bottom of the preform is heated to allow drawing of the photonic crystal fiber 63. The speed of the photonic crystal fiber, and therefore the photonic crystal fiber diameter, is controlled by a drawing wheel 69 that passes the photonic crystal fiber through various stations of the drawing tower. The speed of the photonic crystal fiber 63 is adjustable, and by adjusting the temperature of the furnace 62 and the speed of the photonic crystal fiber 63, the diameter of the fiber can be adjusted. The photonic crystal fiber passes through a monitoring station 67a, where the diameter of the photonic crystal fiber from the furnace 62 is monitored in-line.

[0145] The photonic crystal fiber 63 exits the monitoring station 67a and proceeds to a coating station for application of a primary carbon coating. The photonic crystal fiber 63 passes through a reactor chamber of a reactor 64, where reactant gases are introduced and exhausted in a continuous flow, as indicated by the arrows, to maintain a substantially constant amount of fresh gas within the reactor.

[0146] To ensure that the photonic crystal fiber 63 has a sufficiently high temperature when it enters the reactor 64, it is desirable for the reactor to be positioned relatively close to where the photonic crystal fiber 63 leaves the furnace 62. Alternatively, an oven can be positioned before the reactor to preheat the photonic crystal fiber 63, although this latter alternative is not preferred due to the additional cost of the oven.

[0147] The thickness of the carbon layer can be adjusted, for example, by adjusting the concentration of reactive carbonaceous gas in the reaction gas or by varying the photonic crystal fiber velocity.

[0148] The carbon coated photonic crystal fiber exits the reactor and proceeds to an additional coating station for application of an additional coating, which in the illustrated embodiment is a polymer coating station 65. The coated photonic crystal fiber exits the coating station and proceeds to a concentricity monitor 67b and then to a curing station 66 where the polymer coating is cured by light.

[0149] The coated photonic crystal fiber exits curing station 66 and proceeds further to an additional monitor 67c which monitors the fiber diameter. The coated photonic crystal fiber 63 exits draw wheel 69 and is wound onto a spool 68.

[0150] The coated photonic crystal fiber 63 can be advantageously loaded with hydrogen or deuterium on the spool by subjecting the coated photonic crystal fiber on the spool 68 to hydrogen and / or deuterium in a loading chamber.

[0151] The drawing tower shown in Figure 7 is in the process of drawing a photonic crystal fiber 73 from a preform 73a. The preform is sealed in a pressure controlled chamber 71, which consists of one or more pressure chambers that control the pressure of the gas inclusions in the photonic crystal fiber. The bottom extends into a furnace 72, where the bottom of the preform is heated and the fiber 73 is drawn to the desired thickness. The speed of the fiber is controlled by a drawing wheel 79 that passes the photonic crystal fiber 73 through the various stations of the drawing tower. The fiber exits the furnace 72 and passes through a monitoring station 77a, where the diameter of the fiber is monitored in-line.

[0152] The photonic crystal fiber 73 exits the monitoring station 77a and proceeds to a coating station 74 for application of a primary metal coating. The coating station 74 contains a relatively high temperature liquid metal melt, but to ensure a uniform coating layer, the fiber should have a temperature below that of the melt. A blower or similar cooling means can be applied before the coating station 74 to blow cold air 70 to cool the photonic crystal fiber 73.

[0153] Suitable melt temperatures are shown in Table 1.

[0154] [Table 1] The photonic crystal fiber 73 passes through the metal melt at a desired speed equal to the fiber draw speed. The thickness of the metal coating can be adjusted, for example, by adjusting the amount of melt in the melt chamber of the coating station 74 or the fiber speed.

[0155] The metal coated photonic crystal fiber exits coating station 74 and proceeds further to additional coating station 75 for application of an additional coating, which in the illustrated embodiment is a polymer coating station 75. The coated photonic crystal fiber exits coating station 75 and proceeds to a concentricity monitor 77b and then to curing station 76 where the polymer coating is cured by light.

[0156] The coated photonic crystal fiber exits curing station 76 and proceeds further to an additional monitor 77c which monitors the fiber diameter. The coated photonic crystal fiber exits draw wheel 79 and is wound onto spool 78.

Claims

1. 1. A method of making a microstructured optical fiber doped with at least one of hydrogen and deuterium, comprising the steps of: preparing a preform including a preform structure for a core and cladding region of the microstructured optical fiber; drawing the preform to obtain the microstructured optical fiber having the core and the cladding region, at least the cladding region comprising a plurality of inclusions extending along a longitudinal axis of the microstructured optical fiber; providing a coating about the cladding region, the coating being heated to a temperature T ｈ It is airtight at the following temperature: T ｈ is at least about 50° C., and at least one of the hydrogen and deuterium is T ０ The coating can be penetrated at temperatures above T ０ But, T ｈ providing a coating around the larger cladding region; and causing the microstructured optical fiber to be doped with at least one of hydrogen and deuterium, the doping comprising exposing the microstructured optical fiber to at least one of hydrogen and deuterium after applying the coating.

2. 2. The method of claim 1, wherein causing the loading of the microstructured optical fiber with at least one of hydrogen and deuterium comprises placing the microstructured optical fiber in a chamber containing hydrogen and / or deuterium.

3. The method of claim 1 , comprising closing inclusions on either side of a selected length of the microstructured optical fiber.

4. The method of claim 3 , wherein the closed inclusion is closed prior to exposing the microstructured optical fiber to at least one of hydrogen and deuterium.

5. The method of claim 1 further comprising the step of applying at least one additional coating over the coating.

6. The method of claim 1 , wherein the coating comprises a carbon coating.

7. 7. The method of claim 6, wherein the step of applying the carbon coating is by chemical vapor deposition and comprises drawing the fiber through a reactor chamber of a reactor.

8. 8. The method of claim 7, comprising subjecting the fiber in the reactor chamber to a reactor gas at a temperature of at least about 700°C, the reactor gas comprising a carbonaceous composition.

9. 8. The method of claim 7, wherein the reactor is an integral part of a stretching tower.

10. The method of claim 1 , wherein the coating comprises a metallic coating.

11. 11. The method of claim 10, comprising applying the coating by passing the fiber through a liquid metal melt, wherein the temperature of the fiber as it enters the melt is less than the temperature of the metal melt.

12. 2. The method of claim 1 , wherein the cladding region comprises an inner cladding region and an outer cladding region, the inner cladding region comprising the inclusions, and a radial distance between an outermost inclusion of the inner cladding region and the coating is at least 10 μm.

13. The method of claim 1 , wherein material between the inner cladding region and the coating of the microstructured optical fiber forms a reservoir of at least one of hydrogen and deuterium.

14. The method of claim 1 , wherein the core region of the microstructured optical fiber has a diameter of about 10 μm or less.

15. 2. The method of claim 1 , wherein an outer cladding region of the microstructured optical fiber comprises inclusions extending along a longitudinal axis of the microstructured optical fiber, the inclusions comprised in the inner cladding region having a larger diameter than the inclusions comprised in the outer cladding region.

16. The method of claim 1 , wherein the plurality of inclusions are arranged in a pattern of at least two rings.

17. 10. The method of claim 1, wherein the diffusion of at least one of hydrogen and deuterium through the hermetic coating of the microstructured optical fiber is less than 1% per day.

18. 1. A method for generating a supercontinuum light source, comprising: Providing a microstructured optical fiber according to the method of claim 1; and optically coupling an input end of the microstructured optical fiber to a pump laser to provide light to the microstructured optical fiber.