Resin film for current collection sheet, current collection sheet, solar cell element with current collection sheet, and solar cell

Abstract

To provide a resin film for current collection sheet having good UV transmittance and resistance.SOLUTION: A resin film for current collection sheet of solar cells includes a heat-resistant layer and a sealing layer that is arranged on one surface side of the heat-resistant layer. The heat-resistant layer contains a polypropylene resin and the sealing layer contains a thermoplastic resin and a silane modified polyethylene resin.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present disclosure relates to a film for a current collector sheet, a current collector sheet, a solar cell element with a current collector sheet, and a solar cell. [Background technology]

[0002] In recent years, global warming, which is believed to be caused by carbon dioxide, has become a worldwide problem. In response to this problem, solar cells that utilize solar energy have attracted attention as an environmentally friendly, clean energy source, and active research and development into them is being carried out.

[0003] Solar cells are used, for example, in the form of a module in which a plurality of solar cell elements are connected. As a method for connecting solar cell elements to each other, for example, a method of connecting solar cell elements to each other using a strip-shaped conductor wire with a width of about 2 mm to 5 mm, called a bus bar, has been used conventionally. The connection method using a bus bar has a problem that the amount of sunlight incident on the solar cell electronic element is reduced because sunlight is physically blocked in the area where the bus bar is arranged in the solar cell module.

[0004] In response to this, in recent years, a method called multi-wire connection has begun to be adopted in which solar cell elements are connected to each other using wires (thin conductive wires) with a diameter of, for example, about 150 μm to 300 μm. In multi-wire connection, a method for fixing wires to solar cell elements includes, for example, a method in which wires are embedded in a resin film having thermal adhesion properties to form a current collecting sheet, and the current collecting sheet is then thermocompressed to the solar cell elements to fix them (Patent Documents 1 and 2). [Prior art documents] [Patent documents]

[0005] [Patent Document 1] International Publication No. 2004 / 021455 [Patent Document 2] International Publication No. 2017 / 076735 Summary of the Invention [Problem to be solved by the invention]

[0006] In recent years, solar cells have been required to have improved power generation efficiency and longer life spans, and therefore the resin film of the current collector sheet used in multi-wire connections is required to have good UV transmittance and UV resistance.

[0007] The present disclosure is an invention made in consideration of the above-mentioned circumstances, and has as its main object to provide a resin film for a current collector sheet having good UV transmittance and UV resistance, a current collector sheet using the same, a solar cell element with a current collector sheet, and a solar cell with high light utilization efficiency. [Means for solving the problem]

[0008] The present disclosure provides a resin film for a current collector sheet used in a current collector sheet of a solar cell, the resin film comprising a heat-resistant layer and a sealing layer disposed on one side of the heat-resistant layer, the heat-resistant layer containing a polypropylene resin.

[0009] The present disclosure also provides a current collecting sheet for use in a solar cell, comprising the above-mentioned resin film for the current collecting sheet and a wire arranged on a surface of the resin film for the current collecting sheet facing the sealing layer.

[0010] The present disclosure also provides a solar cell element with a current collecting sheet, comprising: the current collecting sheet described above; and a solar cell element disposed on the surface of the current collecting sheet facing the sealing layer and electrically connected to the wire.

[0011] The present disclosure further provides a solar cell comprising a transparent substrate, a first encapsulant, the solar cell element with the current collecting sheet described above, a second encapsulant, and a counter substrate arranged in this order. Effect of the Invention

[0012] The resin film for current collecting sheets according to the present disclosure has the advantage of being excellent in UV transmittance and UV resistance, and the solar cell according to the present disclosure has the advantage of being highly efficient in light utilization. [Brief description of the drawings]

[0013] [Figure 1] FIG. 1 is a schematic cross-sectional view illustrating a resin film for a current collector sheet according to the present disclosure. [Diagram 2] FIG. 1 is a schematic cross-sectional view illustrating a resin film for a current collector sheet according to the present disclosure. [Diagram 3] 1A and 1B are a schematic plan view and a schematic cross-sectional view illustrating a current collecting sheet according to the present disclosure. [Figure 4] 1 is a schematic cross-sectional view illustrating a current collecting sheet according to the present disclosure. [Diagram 5] 1 is a schematic plan view illustrating a current collecting sheet according to the present disclosure. [Figure 6] 1A and 1B are a schematic perspective view and a schematic cross-sectional view illustrating a solar cell element with a current collecting sheet according to the present disclosure. [Figure 7] 1 is a schematic plan view illustrating a solar cell of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] The following describes the embodiments of the present disclosure with reference to the drawings. However, the present disclosure can be implemented in many different forms, and should not be interpreted as being limited to the description of the embodiments exemplified below. In addition, the drawings may be schematic in terms of the width, thickness, shape, etc. of each part compared to the actual form in order to make the explanation clearer, but these are merely examples and do not limit the interpretation of the present disclosure. In this specification and each figure, elements similar to those described above with respect to the previous figures may be given the same reference numerals, and detailed explanations may be omitted as appropriate.

[0015] When written as "above" or "below", unless otherwise specified, it includes both cases where another member is placed directly above or below a certain member so as to be in contact with the member, and cases where another member is placed above or below a certain member via another member. Similarly, in this specification, when written as "on the surface side of a certain member", it includes both cases where another member is placed directly so as to be in contact with the surface of a certain member, and cases where another member is placed on the surface of a certain member via another member, unless otherwise specified.

[0016] Furthermore, in this specification, terms such as "film," "sheet," and "substrate" are not distinguished from one another based on differences in name.

[0017] As described above, when a plurality of solar cell elements are connected by multi-wire connection in a solar cell module, a method of fixing the wires to the solar cell elements can be, for example, a method of fixing the wires to the solar cell elements by thermocompression bonding a current collecting sheet having a resin film and wires to the solar cell elements. The resin film used in the current collecting sheet is also called a connecting film. For example, a resin film having a heat-resistant layer containing polyethylene terephthalate resin (PET resin) and a sealing layer containing polyolefin resin is widely used as the resin film used in the current collecting sheet.

[0018] PET resin has a melting point of about 260°C and is highly heat resistant. In addition, PET resin has good rigidity when molded into a film. Therefore, a current collector sheet containing PET resin can press the wire against the solar cell element with the resin film during thermocompression bonding, and can secure the wire to the solar cell element well. On the other hand, PET resin has poor UV transmittance and is prone to yellowing due to absorption of UV rays. In addition, PET resin is prone to cracks and breakage due to damage from UV rays. Therefore, when a current collector sheet containing PET resin is incorporated into a solar cell, it is necessary to add an UV absorber to the encapsulant that is placed on the outer side of the current collector sheet.

[0019] However, solar cell elements that have a structure capable of generating electricity even with ultraviolet light in the ultraviolet region of sunlight are widely used. Therefore, from the viewpoint of increasing the light utilization efficiency, it is required that the resin film of the current collector sheet used together with the solar cell element has high ultraviolet transmittance and good ultraviolet resistance. Therefore, as an improvement method for imparting ultraviolet resistance to a resin film containing a PET resin, for example, an improvement method such as adding an additive has been considered, but the reality is that it is difficult to obtain a resin film with the desired ultraviolet transmittance and ultraviolet resistance.

[0020] In view of the above circumstances, the inventors of the present disclosure have conducted extensive research and discovered that by using polypropylene resin (PP resin) instead of PET resin as the resin for the heat-resistant layer, a resin film having sufficient rigidity for use as a current collector sheet and having good UV transmittance and UV resistance can be obtained, leading to the completion of the present invention. The resin film of the present disclosure, and the current collector sheet, solar cell element with current collector sheet, and solar cell using the same are described in detail below.

[0021] In this specification, "ultraviolet rays" refers to light rays with a wavelength of 400 nm or less. In this specification, "ultraviolet rays" refers to light rays with a wavelength of 300 nm to 400 nm that is ultraviolet light in the solar spectrum at air mass 1.5.

[0022] A. Resin film for current collecting sheets The resin film for current collector sheets of the present disclosure is a resin film for current collector sheets used in current collector sheets of solar cells, and comprises a heat-resistant layer and a sealing layer disposed on one side of the heat-resistant layer, wherein the heat-resistant layer contains a polypropylene resin.

[0023] The resin film for current collector sheets of the present disclosure will be described with reference to the drawings. FIG. 1 is a schematic cross-sectional view illustrating a resin film for current collector sheets of the present disclosure. The resin film for current collector sheets 10 shown in FIG. 1 has a heat-resistant layer 1 and a sealing layer 2 arranged on one surface side of the heat-resistant layer 1, and the heat-resistant layer 1 contains a polypropylene resin. As will be described later in FIGS. 3(a) to (b), the resin film 10 constitutes a current collector sheet 20 together with a wire 11. In addition, as will be described later in FIGS. 6(a) to (c), the resin film 10 is used to fix the wire 11 electrically connected to a solar cell element 31.

[0024] According to the present disclosure, since the heat-resistant layer contains a polypropylene resin, the resin film has good ultraviolet transmittance and ultraviolet resistance, and has rigidity that can be used for a current collector sheet. Furthermore, since the resin film for current collector sheet has rigidity, it is possible to suppress thermal shrinkage and curl deformation of the resin film for current collector sheet in a heating process such as fixing wires to solar cell elements using the resin film for current collector sheet.

[0025] I. Composition of resin film for current collector sheet The resin film for a current collector sheet used in the present disclosure has at least a heat-resistant layer and a sealing layer.

[0026] 1.Heat-resistant layer The heat-resistant layer is a layer that imparts heat resistance to the resin film for current collector sheets. Here, "heat resistance" refers to durability against heat applied in the manufacturing process of solar cells, such as fixing wires to solar cell elements using the resin film for current collector sheets, and against heat in the environment in which the solar cells are used.

[0027] (1) Characteristics of the heat-resistant layer The heat-resistant layer used in the present disclosure preferably has the following properties:

[0028] (a) Melting point The melting point of the resin constituting the heat-resistant layer is not particularly limited as long as it can exhibit the desired heat resistance, but is, for example, 80° C. or higher, preferably 120° C. or higher, and more preferably 150° C. or higher. The upper limit of the melting point of the resin constituting the heat-resistant layer is usually 200° C. or lower. If the melting point of the resin constituting the heat-resistant layer is too low, the resin film for the current collector sheet may be significantly deteriorated during the manufacturing process of the solar cell or during use of the solar cell. If the melting point of the resin is too high, it may be difficult to form it into a film, or the manufacturing cost may increase because it is necessary to increase the temperature for melting the resin during the manufacturing of the resin film for the current collector sheet.

[0029] In the present disclosure, the melting point of the resin can be measured by differential scanning calorimetry (DSC) in accordance with the method for measuring transition temperature of plastics (JIS K7121). In this case, if there are two or more melting point peaks, the higher temperature can be used as the melting point.

[0030] (b) Storage modulus In addition, when the resin film for current collecting sheets of the present disclosure is used in a solar cell, it is placed in close contact with a solar cell element as a current collecting sheet. In this case, it is preferable that the resin film for current collecting sheets has a rigidity sufficient to press a wire against the solar cell element to electrically connect it. Since such rigidity is imparted by the heat-resistant layer, it is preferable that the heat-resistant layer has a predetermined rigidity.

[0031] Such rigidity can be evaluated, for example, by the storage modulus. The storage modulus of the heat-resistant layer at 150°C is, for example, 0.1 MPa or more and 1.0 GPa or less, and preferably 1.0 MPa or more and 100 MPa or less. If the storage modulus is smaller than the above range, the rigidity of the heat-resistant layer is insufficient, and therefore the rigidity as a resin film for a current collector sheet is also insufficient, and when the current collector sheet is placed on the solar cell element, there is a possibility that a defect such as insufficient contact between the wire and the solar cell element occurs. On the other hand, if the storage modulus is larger than the above range, it is necessary to apply a large pressure when placing the current collector sheet on the solar cell element, and there is a possibility that a defect such as unnecessary costs such as an increase in the size of the manufacturing equipment occurs.

[0032] Here, the storage modulus can be measured by dynamic viscoelasticity measurement (DMA) according to a method conforming to JIS K7244 4:1999. Specifically, first, the resin film for the current collector sheet is cut to a desired size, and the sealing layer is peeled off from the resin film for the current collector sheet or scraped off from the resin film for the current collector sheet to prepare a sample of the heat-resistant layer. Next, both ends of the sample are attached to the chucks of a dynamic viscoelasticity measuring device so that the tensile direction is the longitudinal direction of the sample, and a tensile load is applied to perform measurement by the tensile method. As the dynamic viscoelasticity measuring device, for example, Rheogel-E4000 manufactured by UBM Co., Ltd. can be used. Specific measurement conditions are shown below.

[0033] (Storage modulus measurement conditions) Measurement sample: 5mm x 20mm rectangle Measurement mode: Tensile method (sine wave strain, tension mode, strain amount: automatic strain) Heating rate: 3℃ / min ·Temperature: -60℃ or higher and 150℃ or lower Frequency: 10Hz Tensile load (static load): 100g

[0034] In preparing a sample of the heat-resistant layer, the sealing layer may be peeled off from the resin film for current collector sheet using, for example, a peel tester. Specifically, a resin film for current collector sheet having a predetermined size is fixed to the peel tester after providing a peel trigger at the interface between the heat-resistant layer and the sealing layer, and the sealing layer is pulled, whereby the sealing layer can be peeled off from the resin film for current collector sheet.

[0035] The storage modulus of the heat-resistant layer at 150° C. can be adjusted, for example, by the type of polypropylene resin contained in the heat-resistant layer, the addition of materials other than polypropylene resin, the material composition, etc. For example, the storage modulus can be increased by adding a filler.

[0036] (c) Ultraviolet transmittance The heat-resistant layer in the present disclosure contains a polypropylene resin as described above, and has better ultraviolet transmittance than those using conventional PET resins.

[0037] The ultraviolet transmittance of the heat-resistant layer can be evaluated, for example, by the transmittance of light having a wavelength of 350 nm. The transmittance of the heat-resistant layer at a wavelength of 350 nm is, for example, preferably 75% or more, more preferably 80% or more, and even more preferably 85% or more. Since the heat-resistant layer used in the present disclosure has a high transmittance of light having a wavelength of 350 nm, when the resin film for current collecting sheets of the present disclosure is used in a solar cell element, the ultraviolet region can be contributed to the power generation of the solar cell element.

[0038] Here, the transmittance of light having a wavelength of 350 nm can be measured, for example, using a spectrophotometer. When measuring the transmittance of light having a wavelength of 350 nm through the heat-resistant layer, a measurement sample is prepared and used for the measurement. The measurement sample is prepared by laminating an olefin resin-containing sealing material sheet ("CVF2SS" manufactured by Dai Nippon Printing Co., Ltd.) having a thickness of 450 μm on one side of the heat-resistant layer, and performing vacuum lamination under the conditions of a set temperature of 150° C., evacuation for 5 minutes, atmospheric pressure pressurization for 9 minutes, and a pressure of 100 kPa.

[0039] (2) Composition of heat-resistant layer The composition of the heat-resistant layer used in the present disclosure contains a polypropylene resin, and may contain, as necessary, a light stabilizer, an adhesion improver for improving adhesion to the sealing layer, and the like.

[0040] (a) Polypropylene resin The heat-resistant layer contains at least a polypropylene resin.

[0041] Such polypropylene resin may be, for example, a homopolypropylene resin (homo PP) which is a propylene homopolymer, a random polypropylene resin (random PP) which is a random copolymer of propylene and an α-olefin, or a block polypropylene resin (block PP) which is a block copolymer. The heat-resistant layer may contain one or more of the above-mentioned various polypropylene resins. In the present disclosure, the polypropylene resin is preferably a homopolypropylene resin, because the homopolypropylene resin has high rigidity and therefore can easily fix wires to solar cell elements using the resin film for current collector sheets.

[0042] The heat-resistant layer in the present disclosure may contain only polypropylene resin as a resin, or may contain other resins so as to have polypropylene resin as the main component. Here, having polypropylene resin as the main component means that the proportion of polypropylene resin is the highest among all resin components.

[0043] The proportion of the polypropylene resin in the total resin components of the heat-resistant layer is, for example, 50% by mass or more, 60% by mass or more, 65% by mass or more, or 70% by mass or more, and the proportion of the polypropylene resin is 100% by mass or less, 90% by mass or less, 80% by mass or less, or 75% by mass or less.

[0044] When the polypropylene resin is a homopolypropylene resin, the ratio of the homopolypropylene resin to the total resin components of the heat-resistant layer is preferably, for example, 50% by mass or more and 90% by mass or less. If the ratio of the homopolypropylene resin is too small, it is difficult to impart the desired heat resistance to the resin film for current collector sheets. On the other hand, since the homopolypropylene resin is inferior in transparency to, for example, random polypropylene resin, if the ratio of the homopolypropylene resin is too high, the transparency of the resin film for current collector sheets may decrease.

[0045] The ratio of each resin component contained in each layer of the resin film for the current collector sheet can be analyzed, for example, from peak ratios detected by differential scanning calorimetry (DSC), infrared spectroscopy (IR), or nuclear magnetic resonance (NMR).

[0046] (b) Light stabilizers The heat-resistant layer in the present disclosure may contain a light stabilizer. When the heat-resistant layer contains a light stabilizer, the heat-resistant layer can be further prevented from being deteriorated by ultraviolet rays. As the light stabilizer, for example, a hindered amine light stabilizer (HALS) is preferably used.

[0047] The hindered amine light stabilizer is not particularly limited as long as it can exert a light stabilizing effect. For example, a high molecular weight light stabilizer which is a copolymer of ethylene and a cyclic aminovinyl compound (hindered amine acrylate) and has a molecular structure with a molecular weight of 30,000 or more can be suitably used.

[0048] A specific example of a high molecular weight type light stabilizer is a copolymer of ethylene and a cyclic aminovinyl compound (hindered amine acrylate) represented by the following chemical formula (1).

[0049] [ka]

[0050] A specific example of a high molecular weight type hindered amine light stabilizer is "XJ-100H (product name)" (molecular weight: 35,000) manufactured by Japan Polyethylene Corporation.

[0051] Another example of the hindered amine-based light stabilizer is a NOR-type hindered amine-based light stabilizer. An example of the NOR-type hindered amine-based light stabilizer is a compound containing a group represented by general formula (1).

[0052] [ka]

[0053] In general formula (1), R is a substituted or unsubstituted hydrocarbon group or acyl group. Examples of R include alkyl groups, alkenyl groups, alkylene groups, cycloalkyl groups, bicycloalkyl groups, phenyl groups, naphthyl groups, phenylalkyl groups, alkyl-substituted phenyl groups, hydroxyl-substituted alkyl groups, acyl groups, alkoxy-substituted alkyl groups, and thioalkoxy-substituted alkyl groups. In general formula (1), * and ** indicate a state in which they can bond with other elements.

[0054] Other examples of the NOR type hindered amine light stabilizer include compounds represented by general formula (2) or general formula (3).

[0055] [ka]

[0056] In the general formula (2), R1 and R2 are each independently a substituted or unsubstituted hydrocarbon group or acyl group, similar to R in the above-mentioned general formula (1). Among them, it is preferable that R1 and R2 are each independently an alkyl group having 4 to 20 carbon atoms.

[0057] In general formula (3), R3 and R4 are each independently a substituted or unsubstituted hydrocarbon group or acyl group, similar to R in general formula (1) described above. Of these, R3 and R4 are each preferably independently an alkyl group having 4 to 20 carbon atoms. R5 is an alkylene group having 1 to 8 carbon atoms.

[0058] Specific examples of NOR-type hindered amine light stabilizers include "ADEKA STAB LA-81 (trade name)" manufactured by Adeka Corporation, "TINUVIN 123 (trade name)" manufactured by BASF (decanedioic acid bis(2,2,6,6-tetramethyl-1-(octyloxy)-4-piperidinyl) ester), and "TINUVIN XT850FF (trade name)" manufactured by BASF.

[0059] The ratio of the light stabilizer to the total solid content of the heat-resistant layer is, for example, 3% by mass or more and 10% by mass or less, and preferably 3.5% by mass or more and 4.5% by mass or less. By setting the ratio of the light stabilizer within the above range, the ultraviolet resistance of the resin film for current collector sheet can be improved. On the other hand, if the ratio of the light stabilizer is too high, the transparency of the heat-resistant layer may decrease due to bleeding out of the light stabilizer, and the adhesion between the heat-resistant layer and the sealing layer may decrease.

[0060] (c) Adhesion improver The heat-resistant layer in the present disclosure may contain an adhesion improver in order to improve adhesion to the sealing layer, particularly when the sealing layer contains a polyethylene resin.

[0061] Examples of such adhesion improvers include polyethylene-based elastomers, polyethylene-based plastomers, etc. In the present disclosure, by including a polyethylene-based elastomer or a polyethylene-based plastomer in the heat-resistant layer, not only can the adhesion to the sealing layer be improved, but also the durability of the resin film for current collecting sheets can be improved.

[0062] Examples of the polyethylene elastomer and the polyethylene plastomer include copolymers of ethylene and an α-olefin other than ethylene (hereinafter sometimes referred to as ethylene-α-olefin copolymer).

[0063] The polyethylene constituting the ethylene-α-olefin copolymer is not particularly limited, but is preferably a low-density polyethylene. In addition, the low-density polyethylene may be, for example, a polyethylene having a density of 0.870 g / cm. 3 More than 0.910g / cm 3 The following low-density polyethylene is preferred: The density of the polyethylene can be measured, for example, by a method in accordance with JIS 6922-2:2010.

[0064] Examples of the α-olefin constituting the ethylene-α-olefin copolymer include α-olefins having 3 to 20 carbon atoms. Specific examples include propylene, 1-butene, 4-methyl-1-pentene, 3-methyl-1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 1-decene, 1-undecene, and 1-dodecene. These may be used alone or in combination.

[0065] The ethylene-α-olefin copolymer may be, for example, a commercially available product. Examples of commercially available products include "TAFMER DF-710 (trade name)", "TAFMER DF-119 (trade name)", "TAFMER DF-110 (trade name)", "TAFMER A-1085S (trade name)", "TAFMER A-4070S (trade name)", "TAFMER A-4085S (trade name)", and "TAFMER A-4090S (trade name)" manufactured by Mitsui Chemicals. In addition, examples of commercially available products include "Kernel KF260T (trade name)", "Kernel KF270 (trade name)", "Kernel KF370 (trade name)", "Kernel KF360T (trade name)", "Kernel KS240T (trade name)", "Kernel KS340T (trade name)", and "Kernel KS260 (trade name)" manufactured by Japan Polyethylene Corporation. Further examples include "Excellen VL100 (product name)", "Excellen VL102 (product name)", "Excellen VL200 (product name)", "Excellen FX201 (product name)", "Excellen FX301 (product name)", "Excellen FX307 (product name)", "Excellen FX351 (product name)", "Excellen FX352 (product name)" and "Excellen FX357 (product name)" manufactured by Sumitomo Chemical Co., Ltd.

[0066] The ratio of the adhesion improver to the total resin components of the heat-resistant layer is, for example, 5% by mass or more, may be 10% by mass or more, or may be 15% by mass or more. The ratio of the adhesion improver is, for example, less than 50% by mass, may be 40% by mass or less, may be 30% by mass or less, or may be 20% by mass or less. If the ratio of the adhesion improver is too high, the transparency of the resin film for current collector sheets may decrease. Also, the resin film for current collector sheets may not have the desired heat resistance.

[0067] (d) Other The heat-resistant layer in the present disclosure may contain a polypropylene-based elastomer (PP-based elastomer). By containing the polypropylene-based elastomer, the transparency of the heat-resistant layer can be increased.

[0068] An example of the polypropylene-based elastomer is a copolymer of propylene and an α-olefin other than propylene (hereinafter, sometimes referred to as a propylene-α-olefin copolymer).

[0069] Examples of the α-olefin constituting the propylene-α-olefin copolymer include α-olefins having 2 or 4 to 20 carbon atoms. Specific examples include ethylene, 1-butene, 4-methyl-1-pentene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, and 1-eicosene. These may be used alone or in combination.

[0070] Among them, the propylene-α-olefin copolymer is preferably a copolymer of propylene, ethylene, and an α-olefin other than propylene and ethylene.

[0071] The propylene-α-olefin copolymer may be, for example, a commercially available product, such as Tafmer PN-3560 (trade name) or Tafmer PN-0040 (trade name) manufactured by Mitsui Chemicals, Inc.

[0072] The proportion of the polypropylene-based elastomer relative to the total resin components of the heat-resistant layer is, for example, 5% by mass or more, may be 10% by mass or more, or may be 15% by mass or more. The proportion of the polypropylene-based elastomer is, for example, less than 50% by mass, may be 40% by mass or less, may be 30% by mass or less, or may be 20% by mass or less. If the proportion of the polypropylene-based elastomer is less than the above range, the effect of improving the transparency of the resin film for current collector sheets may not be obtained. If the proportion of the polypropylene-based elastomer exceeds the above range, the resin film for current collector sheets may not have the desired heat resistance.

[0073] (3)Other The thickness of the heat-resistant layer can be appropriately selected depending on the size and use of the solar cell in which the resin film for current collector sheet is used, and is not particularly limited, but is, for example, 10 μm or more, may be 15 μm or more, or may be 20 μm or more. The thickness of the heat-resistant layer is, for example, 50 μm or less, may be 45 μm or less, or may be 40 μm or less.

[0074] 2. Sealing layer The sealing layer in the present disclosure is a layer that has thermal adhesion properties and supports the wires when used in a current collecting sheet.

[0075] The resin used in the sealing layer is usually a resin having thermal adhesion. In addition, the resin used in the sealing layer preferably has a property of wrapping around the wire when the current collecting sheet is thermocompression bonded to the solar cell element. Hereinafter, the above-mentioned property may be referred to as molding property.

[0076] The sealing layer needs to have adhesion to the heat-resistant layer and to the wire, which is a metal material. Such a sealing layer may be composed of a single layer or multiple layers. Hereinafter, the sealing layer will be described separately for the case where the sealing layer is a single layer and the case where the sealing layer is a multiple layer.

[0077] (1) When the sealing layer is a single layer When the sealing layer is a single layer, the sealing layer usually contains a resin having heat-welding properties and molding properties. Examples of such resins include thermoplastic resins. Considering ultraviolet light transmittance and visible light transmittance, it is preferable to use polyolefin resins and ionomer resins as the thermoplastic resins. In the present disclosure, polyolefin resins are particularly preferable. The details of polyolefin resins are described below.

[0078] (a) Polyolefin resin The melting point of the polyolefin resin used in the sealing layer is not particularly limited as long as it can exhibit the desired heat welding property and molding property. The melting point of the polyolefin resin is, for example, 125°C or less, may be 120°C or less, or may be 110°C or less. The melting point of the polyolefin resin is, for example, 80°C or more. If the melting point of the polyolefin resin is too high, it is necessary to increase the temperature when thermocompression bonding the current collecting sheet to the solar cell element, which may increase the manufacturing cost or deteriorate the solar cell element. On the other hand, if the melting point of the polyolefin resin is too low, the sealing layer may melt in the environment in which the solar cell is used, making it difficult to fix the wire.

[0079] In the present disclosure, among the above polyolefin resins, polyethylene resin and polypropylene resin are preferred, and polyethylene resin is particularly preferred, because it has excellent molding properties.

[0080] Examples of polyethylene resins include high density polyethylene (HDPE), linear low density polyethylene (LLDPE), low density polyethylene (LDPE), and very low density polyethylene (VLDPE). These may be used alone or in combination of two or more. In the present disclosure, linear low density polyethylene (LLDPE) is preferred among them. This is because it can improve the adhesion between the heat-resistant layer and the sealing layer.

[0081] The density of the polyethylene resin is not particularly limited, but is, for example, 0.890 g / cm 3 More than 0.930g / cm 3 It is preferable that the density is 0.900 g / cm or less. 3 More than 0.925g / cm 3 It is more preferable that the density of the polyethylene resin is not more than 100%.

[0082] The sealing layer preferably contains the above-mentioned polyethylene elastomer or polyethylene plastomer as the polyolefin resin.

[0083] The sealing layer may contain only the above-mentioned polyolefin resin, or may contain a resin other than the polyolefin resin in addition to the polyolefin resin. In the latter case, the sealing layer preferably contains the polyolefin resin as the main component. The term "containing the polyolefin resin as the main component" means that the proportion of the polypropylene resin is the highest among all the resin components.

[0084] The proportion of the polyolefin resin to the total resin components in the sealing layer is, for example, 50% by mass or more, 60% by mass or more, or 70% by mass or more. The proportion of the polyolefin resin is, for example, 99% by mass or less, 95% by mass or less, or 90% by mass or less. The proportion of the polyolefin resin may be 100% by mass.

[0085] In addition, when the polyolefin resin contains the above-mentioned polyethylene-based elastomer or polyethylene-based plastomer, the ratio of the polyolefin resin to the total resin components in the sealing layer is preferably, for example, 90% by mass or more and 100% by mass or less. This is because the adhesion between the heat-resistant layer and the sealing layer can be particularly good, and the resin film for current collector sheets can be excellent in durability. In addition, in a heating step in which wires are fixed to solar cell elements using the resin film for current collector sheets, the resin film for current collector sheets can be suppressed from thermally shrinking and curling deformation.

[0086] (b) Light stabilizers The sealing layer in the present disclosure is not particularly limited as long as it contains a thermoplastic resin, and other components can be appropriately selected and added as necessary. For example, such components can include a light stabilizer. The light stabilizer is the same as that described in the above section "1. Heat-resistant layer (2) Composition of heat-resistant layer (b) Light stabilizer", so the description here is omitted.

[0087] The proportion of the light stabilizer relative to the total solid content of the sealing layer is, for example, from 0.2% by mass to 5% by mass, and preferably from 0.5% by mass to 3% by mass.

[0088] (c) Adhesion improver The sealing layer in the present disclosure may also contain a component that improves adhesion to wires and solar cell elements.

[0089] An example of such a component is a silane-modified polyethylene resin. The silane-modified polyethylene resin is a silane copolymer in which an α-olefin and an ethylenically unsaturated silane compound are copolymerized as comonomers. In the present disclosure, the silane-modified polyethylene resin is preferably a resin in which an ethylenically unsaturated silane compound is graft-polymerized as a side chain to a linear low-density polyethylene (LLDPE) main chain.

[0090] Examples of ethylenically unsaturated silane compounds include vinyltrimethoxysilane, vinyltriethoxysilane, vinyltripoxysilane, vinyltriisopropoxysilane, vinyltributoxysilane, vinyltripentyloxysilane, vinyltriphenoxysilane, vinyltribenzyloxysilane, vinyltrimethylenedioxysilane, vinyltriethylenedioxysilane, vinylpropionyloxysilane, vinyltriacetoxysilane, and vinyltricarboxysilane.

[0091] The silane-modified polyethylene resin can be obtained, for example, by the production method described in JP-A-2003-46105.

[0092] The ratio of the silane-modified polyethylene resin to the total resin components of the sealing layer is not particularly limited, but is preferably, for example, 5% by mass or more and 25% by mass or less. Also, the graft amount, which is the content of the ethylenically unsaturated silane compound, is preferably, for example, 0.001 parts by weight or more and 15 parts by weight or less, based on 100 parts by weight of the total resin components of the sealing layer.

[0093] (2) When the sealing layer is multi-layered The sealing layer may be a multi-layer structure in which a plurality of resin layers are laminated. When the sealing layer is a multi-layer structure, for example, as shown in FIG. 2, the sealing layer 2 preferably has a base layer 2a disposed on the surface of the heat-resistant layer 1 and an adhesive layer 2b disposed on the surface of the base layer 2a opposite to the heat-resistant layer 1.

[0094] In the present disclosure, it is preferable to add the above-mentioned adhesion improver to the above-mentioned adhesive layer. By adding the above-mentioned adhesion improver to the adhesive layer, the amount of the adhesion improver used can be reduced, and therefore the manufacturing cost of the resin film for current collector sheet can be reduced.

[0095] The resins and optional components used in the base layer and adhesive layer can be the same as those described in the above section “(1) When the sealing layer is a single layer,” and therefore will not be described here.

[0096] (3)Other The thickness of the sealing layer in the present disclosure is not particularly limited as long as it can support the wire when made into a current collecting sheet, and can be appropriately selected according to the thickness of the wire. The thickness of the sealing layer is, for example, 10 μm or more, may be 20 μm or more, may be 50 μm or more, or may be 65 μm or more. The thickness of the heat-resistant layer is, for example, 170 μm or less, may be 100 μm or less, may be 45 μm or less, or may be 40 μm or less.

[0097] 3. Middle tier The resin film for current collecting sheet of the present disclosure may have an intermediate layer disposed between the heat-resistant layer and the sealing layer. The intermediate layer may be, for example, an adhesive layer containing an adhesive for bonding the heat-resistant layer and the sealing layer. The adhesive may be an adhesive used for bonding general films. The thickness of the intermediate layer is not particularly limited as long as it does not excessively impede the transparency of the resin film for current collecting sheet.

[0098] When the heat-resistant layer contains a polypropylene resin and the sealing layer contains a polyethylene resin, an intermediate layer may be provided which is made of a mixture of a polypropylene resin and a polyethylene resin.

[0099] 4.Other The interlayer adhesion strength between the heat-resistant layer and the sealing layer is, for example, preferably 1.0 N / 15 mm or more, more preferably 2.0 N / 15 mm or more, and even more preferably 5.0 N / 15 mm or more. By having the interlayer adhesion degree at least the above value, the adhesion between the heat-resistant layer and the sealing layer can be improved, and peeling between them can be effectively suppressed.

[0100] The interlayer adhesion strength can be measured, for example, by the following measurement method. A sample is prepared by cutting the resin film for the current collector sheet to a width of 15 mm and a length of 100 mm. A peel trigger is provided between the heat-resistant layer and the sealing layer of the obtained sample. Next, a peel test is performed by holding the top and bottom 10 mm of a peel tester (Tensilon universal testing machine RTF-1150-H manufactured by A&D Co., Ltd.) with a jig, with a chuck distance of 30 mm and a pulling speed of 50 mm / min, and the force required for peeling between the layers is measured as the adhesion strength.

[0101] In addition, the total thickness of the resin film for current collector sheets in the present disclosure can be appropriately selected depending on the thickness of the wires used in the current collector sheet, and is not particularly limited, and may be, for example, 50 μm or more and 200 μm or less. If the resin film for current collector sheets is too thin, it may be difficult to sufficiently fix the wires to the solar cell elements. On the other hand, if the resin film for current collector sheets is too thick, transparency may decrease.

[0102] In the resin film for current collecting sheets, the thicknesses of the heat-resistant layer and the sealing layer can be appropriately selected according to, for example, the thickness and arrangement of the wire used when the current collecting sheet is formed, and the form of the solar cell element on which the current collecting sheet is formed, and are not particularly limited. The ratio of the thickness of the sealing layer to the thickness of the heat-resistant layer (thickness of the sealing layer / thickness of the heat-resistant layer) is, for example, 0.1 to 2.4, preferably 0.2 to 2.0, and more preferably 0.4 to 1.8. By setting the ratio of the thickness of the sealing layer to the thickness of the heat-resistant layer within the above-mentioned range, when the current collecting sheet is formed on the solar cell element, the wire can be well fixed to the solar cell element.

[0103] II. Physical properties of resin films for current collector sheets 1.UV transmittance The ultraviolet transmittance of the resin film for current collecting sheets of the present disclosure is not particularly limited as long as it can transmit the ultraviolet region to an extent that the solar cell element can generate electricity. The ultraviolet transmittance of the resin film for current collecting sheets can be evaluated, for example, by the transmittance of light with a wavelength of 350 nm. The transmittance of the resin film for current collecting sheets of the present disclosure for light with a wavelength of 350 nm is, for example, preferably 76% or more, more preferably 80% or more, and even more preferably 85% or more. Since the resin film for current collecting sheets of the present disclosure has a high transmittance of light with a wavelength of 350 nm, the ultraviolet region of sunlight can contribute to the power generation of the solar cell element.

[0104] Here, the transmittance of light having a wavelength of 350 nm can be measured, for example, using a spectrophotometer. When measuring the transmittance of light having a wavelength of 350 nm of the resin film for current collector sheet, a measurement sample is prepared and used for the measurement. The measurement sample is prepared by laminating a sealant sheet ("CVF2SS" manufactured by Dai Nippon Printing Co., Ltd.) containing an olefin resin having a thickness of 450 μm on the heat-resistant layer side of the resin film for current collector sheet, and performing vacuum lamination under the conditions of a set temperature of 150° C., 5 minutes of vacuum drawing, 9 minutes of atmospheric pressure pressure, and a pressure of 100 kPa. Since the resin film for current collector sheet in the present disclosure has good ultraviolet resistance, a UV-through type sealant ("CVF2SS" manufactured by Dai Nippon Printing Co., Ltd.) is used as the sealant sheet. However, when the resin film for current collector sheet has poor ultraviolet resistance, a UV-cut type sealant, for example, "CVF" manufactured by Dai Nippon Printing Co., Ltd. is used as the sealant sheet. As the spectrophotometer, for example, a UV-Visible-Near-Infrared Spectrophotometer V-670 manufactured by JASCO Corporation can be used.

[0105] 2.Total light transmittance The total light transmittance of the resin film for current collecting sheet is not particularly limited as long as it can transmit sunlight to an extent that the solar cell element can generate electricity. The total light transmittance of the resin film for current collecting sheet is, for example, 75% or more, preferably 80% or more, and more preferably 85% or more. When the total light transmittance is within the above range, the light utilization efficiency of the solar cell element can be increased. The total light transmittance is measured in accordance with JIS K7361-1. The total light transmittance can be measured, for example, by a haze meter HM150 manufactured by Murakami Color Research Laboratory Co., Ltd.

[0106] 3.Transparency The transparency of the resin film for current collecting sheets of the present disclosure is not particularly limited as long as it can transmit sunlight to an extent that the solar cell element can generate electricity. The transparency of the resin film for current collecting sheets can be evaluated, for example, by haze. The haze of the resin film for current collecting sheets is, for example, 1% or more and 20% or less, or may be 2% or more and 15% or less, or may be 3% or more and 8% or less. The haze is measured in accordance with JIS K7136.

[0107] Here, the haze can be measured, for example, by a haze meter HM150 manufactured by Murakami Color Research Institute Co., Ltd. When measuring the haze of the resin film for current collector sheet, a measurement sample is prepared and used for the measurement. The measurement sample is prepared by the following method. First, the resin film for current collector sheet is cut to 50 mm x 50 mm to prepare a test piece. Next, an ETFE (tetrafluoroethylene-ethylene copolymer) film, a test piece, and an ETFE film are laminated in this order, and vacuum lamination is performed under the conditions of a set temperature of 165°C, vacuuming for 2 minutes, pressing for 2.5 minutes, and a pressure of 100 kPa. This is to eliminate fine irregularities on the surface of the resin film for current collector sheet at the film formation stage. Next, the ETFE film is removed from both sides of the test piece to prepare a measurement sample.

[0108] 4. Slope of the TMA curve In the resin film for current collecting sheets of the present disclosure, the slope of the TMA curve defined below between temperatures of 90° C. and 100° C. is preferably −3.0 or more and −1.3 or less. In this case, the behavior of the material resin during the thermal lamination process for integration into a solar cell module is optimized, and the compatibility of heat resistance and molding properties can be more stably achieved in a typical solar cell module manufacturing process.

[0109] In this specification, the "slope of the TMA curve" is defined as follows. "The slope of the TMA curve" In the "TMA curve" obtained by the "Thermo-mechanical analysis (TMA) test" described below, when the indentation depth is Y1 (μm) at temperature X1 (℃) and the indentation depth is Y2 (μm) at temperature X2 (℃) (>X1 (℃)), the "slope (a) of the TMA curve" between X1 and X2 refers to the value of (a) expressed as (a) = (Y2-Y1) / (X2-X1). However, if the indentation depth reaches -150μm (if the needle penetrates the film being measured) before the temperature reaches X2, the temperature X2 is replaced with the temperature at which the indentation depth reaches -150μm.

[0110] In addition, the above-mentioned "thermo-mechanical analysis (TMA) test" refers to a test performed under the following conditions. "Thermo-mechanical analysis (TMA) test" A 150μm thick resin film for current collector sheets is placed in a thermomechanical analysis (TMA) test device, and a φ1mm needle is pressed into it at a constant pressure of 100kPa. The temperature is raised from room temperature to 150°C at a rate of 5°C / min, and the needle penetration depth is measured. At this time, the needle is pressed into the surface of the sealing layer side of the resin film for current collector sheets.

[0111] The "TMA curve" that can be obtained by the above-mentioned thermomechanical analysis (TMA) test refers to a curve that shows the correlation between temperature and needle penetration depth in the XY coordinate system, where X is the temperature and Y is the needle penetration depth at that temperature, in the above-mentioned thermomechanical analysis (TMA) test.

[0112] As a thermomechanical analysis (TMA) device, for example, TMA / SS7100 manufactured by SII Nano Technology can be used.

[0113] By making the slope of the TMA curve as defined above -3.0 or more, sufficient molding properties are exhibited during the thermal lamination process for integration into a solar cell module, in which the resin film for the current collector sheet on the sealing layer side of the resin film for the current collector sheet conforms to the outer peripheral shape of the wire on the same side and adheres closely to the solar cell element.

[0114] On the other hand, by making the slope of this TMA curve -1.3 or less, excessive flow of the resin in the resin film for the current collector sheet as a whole is suppressed during the above-mentioned thermal lamination processing, thereby making it possible to prevent the wire from penetrating through the resin film for the current collector sheet and becoming exposed from the surface on the heat-resistant layer side.

[0115] III. Manufacturing method The manufacturing method of the resin film for current collector sheets of the present disclosure is not particularly limited as long as it can obtain a resin film for current collector sheets in which each of the above-mentioned layers is laminated, and for example, a method of preparing a resin composition for forming each of the above-mentioned layers and melt molding the resin composition can be mentioned. As the melt molding method, a known molding method can be used, and for example, injection molding, extrusion molding, blow molding, compression molding, rotational molding, etc. can be mentioned. The temperature condition during molding is, for example, equal to or higher than the melting point of the resin composition, and the upper limit is appropriately adjusted depending on the type of resin composition.

[0116] In the method for producing the resin film for current collector sheets, for example, the heat-resistant layer and the sealing layer may be formed as separate films and then bonded together with an adhesive or the like, or a laminate film in which the heat-resistant layer and the sealing layer are laminated may be formed by co-extrusion, but the latter is more preferred because it can improve the interlayer adhesion between the heat-resistant layer and the sealing layer and also allows the resin film for current collector sheets to be produced with high production efficiency.

[0117] B. Current collecting sheet The current collecting sheet of the present disclosure is a current collecting sheet for use in solar cells, and comprises the resin film for current collecting sheet described above in "A. Resin film for current collecting sheet" and a wire arranged on the surface of the resin film for current collecting sheet facing the sealing layer.

[0118] The current collecting sheet of the present disclosure will be described with reference to the drawings. Fig. 3(a) is a schematic plan view illustrating the current collecting sheet of the present disclosure, and Fig. 3(b) is a cross-sectional view taken along line AA in Fig. 3(a). The current collecting sheet shown in Figs. 3(a) and (b) has a resin film 10 for current collecting sheet, and a wire 11 arranged on the surface of the resin film 10 for current collecting sheet facing the sealing layer 2. Fig. 3(a) shows a schematic plan view of the current collecting sheet viewed from the sealing layer side of the resin film for current collecting sheet.

[0119] According to the present disclosure, by having the resin film for current collector sheet of the present disclosure described above in "A. Resin film for current collector sheet", it is possible to contact the wire with the solar cell element with sufficient stress, and to obtain a current collector sheet with good UV transmittance and UV resistance.

[0120] I. Configuration of current collector sheet The current collector sheet includes a resin film for a current collector sheet and a wire.

[0121] 1. Resin film for current collecting sheets The resin film for current collector sheet is a member that supports the wires. The resin film for current collector sheet is also a member that exhibits thermal adhesion to the solar cell element and fixes the wires to the solar cell element. The resin film for current collector sheet can be the same as that described above in "A. Resin film for current collector sheet", so a description thereof will be omitted here.

[0122] As described below in "II. Structure of the current collector sheet", when the current collector sheet has multiple resin films for the current collector sheet, it is sufficient that at least one of the resin films for the current collector sheet is the resin film for the current collector sheet of the present disclosure, and other resin films for the current collector sheet may be included, but it is preferable that all of the multiple resin films for the current collector sheet that the current collector sheet has are the resin films for the current collector sheet of the present disclosure.

[0123] 2. Wire The wire is disposed on the sealing layer side of the resin film for current collector sheet. The wire is used, for example, to connect solar cell elements to each other in a solar cell module. The wire is also used, for example, to collect electricity generated in a solar cell element in a single-cell solar cell. The wire is usually disposed so as to connect to an electrode of the solar cell element.

[0124] The cross-sectional shape of the wire is typically a circular shape such as a perfect circle or an ellipse, but is not limited to this.

[0125] The wire thickness, i.e., the size of the wire cross section, is not particularly limited as long as it does not prevent the incidence of sunlight into the solar cell element, but is, for example, 100 μm to 200 μm. The size of the wire cross section refers to, for example, the diameter when the cross section is circular, the major axis when the cross section is elliptical, and the distance when the maximum diagonal is drawn when the cross section is polygonal.

[0126] The wire material is not particularly limited as long as it has the desired electrical conductivity, and may be the same as the wire material used in the current collector sheets of general solar cell elements. Examples of the wire material include metal materials such as copper (Cu) and silver (Ag). The wire may have, for example, a core portion and a skin portion disposed on the outer side of the core portion. In this case, for example, the above-mentioned metal material may be used as the material of the core portion, and solder may be used as the material of the skin portion.

[0127] In the present disclosure, the melting point of the solder is, for example, preferably 70° C. or more and 140° C. or less, and more preferably 80° C. or more and 135° C. or less. If the melting point of the solder is higher than the above range, there is a risk that the heat-resistant layer using the polyethylene resin described above will be deteriorated when connecting the wire to the solar cell element.

[0128] In order to achieve such a melting point range, for example, a compound made of Sn, In, Ag, and Bi can be used as the solder.

[0129] II. Structure of the current collector sheet In the current collecting sheet of the present disclosure, at least one wire may be disposed on one resin film for a current collecting sheet, but from the viewpoint of increasing the conductivity of the current collecting sheet, it is preferable that a plurality of wires are disposed on one resin film for a current collecting sheet.

[0130] When the current collecting sheet has a plurality of wires, the arrangement of the wires in a plan view can be the same as the arrangement of wires in a known current collecting sheet, and is not particularly limited. The arrangement of the wires may be, for example, a line arrangement as shown in Fig. 3(a) or a lattice arrangement (not shown).

[0131] In addition, in the current collecting sheet, the wire is disposed on the sealing layer side of the resin film for current collecting sheet. In the present disclosure, for example, as shown in FIG. 3(b), it is preferable that a part of the wire 11 is embedded in the sealing layer 2 of the resin film for current collecting sheet 10 and a part of the wire is exposed. This is because the wire 11 can be fixed well. Also, for example, as shown in FIG. 3(b), the wire 11 may be embedded in the sealing layer 2 so as not to contact the heat-resistant layer 1, or as shown in FIG. 4, the wire 11 may be embedded in the sealing layer 2 so as to contact the heat-resistant layer 1. When the wire is embedded in the sealing layer so as to contact the heat-resistant layer, the thickness of the current collecting sheet can be made thinner, so that the solar cell described later can be made thinner. The degree of embedding of the wire (degree of exposure of the wire) is not particularly limited, and can be appropriately selected according to the material and thickness of the sealing layer, the thickness of the wire, and the form of the solar cell element on which the current collecting sheet is disposed.

[0132] In the present disclosure, for example, the same wire may be arranged for a plurality of resin films for current collector sheets. For example, in the example shown in FIG. 5, the same wire 11 is arranged for two resin films for current collector sheets 10A and 10B. In addition, as shown in FIG. 5, adjacent resin films for current collector sheets may be arranged such that the surfaces on the sealing layer side are in the opposite surface direction. That is, the surface on the sealing layer 2 side of one resin film for current collector sheet 10A and the surface on the heat-resistant layer 1 side of the other resin film for current collector sheet 10B may be arranged in the same surface direction. By having the above-mentioned structure of the current collector sheet, for example, as shown in FIG. 6(a), the current collector sheet 10 can be formed so that two solar cell elements 31 can be arranged in series. Although not shown, the surfaces on the sealing layer side may be arranged in the same surface direction.

[0133] III. Manufacturing method The method for producing the current collector sheet is not particularly limited as long as the wire can be embedded in the sealing layer side of the resin film for current collector sheet to an extent that the wire can be fixed, and any known method can be used. One example is a method in which a wire is placed on the sealing layer side of the resin film for current collector sheet and heated to melt a part of the resin component in the sealing layer and embed the wire.

[0134] C. Solar cell element with current collector sheet The solar cell element with a current collecting sheet of the present disclosure is characterized in that it comprises the current collecting sheet described above in "B. Current collecting sheet" and a solar cell element arranged on the sealing layer side of the current collecting sheet and electrically connected to the wire.

[0135] The solar cell element with a current collecting sheet of the present disclosure will be described with reference to the drawings. Fig. 6(a) is a schematic perspective view illustrating a solar cell element with a current collecting sheet of the present disclosure, Fig. 6(b) is a cross-sectional view taken along line AA in Fig. 6(a), and Fig. 6(c) is a cross-sectional view taken along line BB in Fig. 6(a). A solar cell element 30 with a current collecting sheet shown in Figs. 6(a) to (c) includes a current collecting sheet 10 and a solar cell element 31 disposed on the surface of the current collecting sheet 10 facing the sealing layer 2 and electrically connected to a wire 11. Figs. 6(a) to (c) show an example in which the current collecting sheet 20 has two resin films 10 for current collecting sheets, and a solar cell element 31 is disposed on each of the resin films 10 for current collecting sheets.

[0136] According to the present disclosure, by using the current collecting sheet of the present disclosure described above in "B. Current collecting sheet", it is possible to increase the light utilization efficiency of the solar cell element.

[0137] I. Structure of solar cell element with current collector sheet The solar cell element with a current collecting sheet has a current collecting sheet and a solar cell element.

[0138] 1. Current collecting sheet The current collecting sheet can be the same as that described in "B. Current collecting sheet" above, and therefore description here is omitted. In the present disclosure, when a solar cell element with a current collecting sheet has multiple current collecting sheets, at least one of the current collecting sheets needs to be the current collecting sheet of the present disclosure, and other current collecting sheets may be included. In the present disclosure, it is preferable that all of the current collecting sheets are the current collecting sheets of the present disclosure. In addition, it is preferable that the current collecting sheet of the present disclosure is arranged so as to be located on the light receiving surface side when the solar cell is formed.

[0139] 2. Solar cell element The solar cell element may be the same as an element used in a general solar cell. Examples of the solar cell element include a single crystal silicon type solar cell element, a polycrystalline silicon type solar cell element, an amorphous silicon type solar cell element, a compound semiconductor type solar cell element, a dye-sensitized type solar cell element, a quantum dot type solar cell element, and an organic thin film type solar cell element. The size, shape, and the like of the solar cell element may be appropriately selected depending on the application of the solar cell.

[0140] II. Structure of solar cell element with current collecting sheet A solar cell element with a current collecting sheet usually has a laminated structure in which a current collecting sheet and a solar cell element are laminated.

[0141] When the solar cell element with the current collector sheet is viewed based on the arrangement surface of the current collector sheet of the solar cell element, for example, as shown in FIG. 6(c), L It is preferable that the thickness of the resin film 10 for current collector sheet in the solar cell element 31, i.e., the distance from the surface of the solar cell element 31 on which the current collector sheet 20 is arranged to the surface of the heat-resistant layer 1 opposite the solar cell element 31, is thicker (the distance is larger) in the region where the wire 11 is arranged than in other regions. This is because such a laminated structure allows the heat-resistant layer 1 to effectively press the wire 11 toward the solar cell element 31, preventing problems such as poor contact of the wire 11 with the solar cell element 31.

[0142] In this case, the vertical direction D L The maximum distance y of the wire 11 is, that is, the maximum distance y of the wire 11 from the surface on which the current collector sheet 20 of the solar cell element 31 is arranged, and the vertical direction D L The ratio x / y of the minimum distance x of the sealing layer 2, i.e., the minimum distance x of the distance from the surface of the solar cell element 31 on which the current collecting sheet 20 is arranged to the surface of the heat-resistant layer 1 opposite the solar cell element 31, is preferably 2 / 3 or less, and more preferably 1 / 2 or less.

[0143] The lower limit of the ratio x / y is a value that is appropriately adjusted depending on the thickness of the sealing layer in the current collecting sheet and the thickness of the wire, but is, for example, 1 / 20 or more. When the ratio x / y is within the above range, the wire can be satisfactorily fixed to the solar cell element using the resin film for current collecting sheets of the current collecting sheet.

[0144] Such a ratio x / y can be obtained by adjusting the thickness (diameter, etc.) of the wire and the thickness of the sealing layer, or by adjusting the pressure when the current collector sheet is thermocompression bonded to the solar cell element in the manufacturing method of the solar cell element with the current collector sheet described later.

[0145] Furthermore, as shown in Figure 6(c), for example, in a cross-sectional view of the solar cell element 30 with the collector sheet, it is preferable that the distance from the surface of the solar cell element 31 facing the collector sheet 20 to the surface of the heat-resistant layer 1 opposite the solar cell element 31 gradually decreases from the position of the maximum distance y toward the position of the minimum distance x.

[0146] In addition, when a plurality of wires are arranged, it is preferable that, in a cross-sectional view of the solar cell element 30 with the current collecting sheet, a portion that is the shortest distance from the surface of the solar cell element 31 on which the current collecting sheet 20 is arranged to the surface of the heat-resistant layer 1 opposite the solar cell element 31 is arranged between adjacent wires, as shown in FIG. 6(c). Since depressions are formed between the wires and the current collecting sheet has an uneven structure, the surface area of ​​the heat-resistant layer opposite the solar cell element becomes large. Therefore, the contact area between the heat-resistant layer and the sealing material described later becomes large, and the adhesion to the sealing material can be improved.

[0147] Furthermore, in the solar cell element with the current collecting sheet, as described above in the section "B. Current collecting sheet", for example as shown in Fig. 6(c), the wire 11 may be embedded in the sealing layer 2 so as to be in contact with the heat-resistant layer 1. This allows the thickness of the solar cell element with the current collecting sheet to be made thinner, thereby making it possible to reduce the thickness of the solar cell.

[0148] The solar cell element with a current collector sheet is not particularly limited as long as it has at least one solar cell element and a current collector sheet connected to at least one of the positive and negative electrodes of the solar cell element. For example, it may be a solar cell element with a current collector sheet constituting a single-cell type solar cell in which a current collector sheet is disposed on each of the positive and negative electrodes of one solar cell element. In addition, it may be a solar cell element with a current collector sheet constituting a solar cell module type solar cell (solar cell module) in which a plurality of solar cell elements are connected in parallel or in series using a current collector sheet.

[0149] III.Other The manufacturing method of the solar cell element with the current collecting sheet of the present disclosure is not particularly limited as long as it can obtain a structure in which the wires of the current collecting sheet are electrically connected and fixed to the solar cell element. For example, a manufacturing method having a temporary adhesion step of temporarily adhering the current collecting sheet to the solar cell element and a fixing step of electrically connecting and fixing the wires of the current collecting sheet to the solar cell element by thermocompression bonding the temporarily adhered current collecting sheet to the solar cell element can be mentioned. As the temporary adhesion method and the thermocompression bonding method, a known method can be used, for example, a vacuum thermal lamination method can be mentioned. In addition, the fixing step may be performed simultaneously with an integration step in which each component of the solar cell is laminated and integrated, for example, as described in the section "D. Solar Cell" described later.

[0150] The solar cell element with the current collector sheet is usually used as a member constituting a solar cell. When the solar cell element with the current collector sheet has, for example, one solar cell element and a current collector sheet connected to only one of the positive and negative electrodes of the solar cell element, the solar cell element with the current collector sheet can be used as a part of the solar cell element with the current collector sheet constituting the single cell type solar cell or solar cell module described above.

[0151] D. Solar cells The solar cell of the present disclosure comprises a transparent substrate, a first sealing material, a solar cell element with a current collecting sheet, a second sealing material, and a counter substrate, and is characterized in that the solar cell element with the current collecting sheet is the solar cell element with the current collecting sheet described above.

[0152] The solar cell of the present disclosure will be described with reference to the drawings. Fig. 7 is a schematic cross-sectional view illustrating a solar cell of the present disclosure. A solar cell 40 shown in Fig. 7 includes a transparent substrate 41, a first sealing material 42, a solar cell element 30 with a current collecting sheet, a second sealing material 43, and a counter substrate 44. The solar cell element 30 with a current collecting sheet includes the current collecting sheet described above in "C. Solar cell element with current collecting sheet". The solar cell of the present disclosure may be used as a solar cell module including a plurality of the solar cell elements with the current collecting sheet.

[0153] According to the present disclosure, a current collecting sheet with good ultraviolet transmittance and ultraviolet resistance is disposed, thereby making it possible to obtain a solar cell with high light utilization efficiency.

[0154] I. Solar Cell Structure The solar cell of the present disclosure includes a transparent substrate, a first encapsulant, a solar cell element with a current collecting sheet, a second encapsulant, and an opposing substrate.

[0155] 1. Solar cell element with current collecting sheet The solar cell element with the current collecting sheet can be similar to the contents explained in the above section "C. Solar cell element with current collecting sheet", and therefore the explanation here is omitted.

[0156] 2. Transparent substrate and opposing substrate The transparent substrate is a member that protects the solar cell element together with the opposing substrate. The transparent substrate is usually disposed on the light-receiving surface side of the solar cell and functions as a front protective plate on the light-receiving surface side. The transparency of the transparent substrate is not particularly limited as long as it does not inhibit the power generation of the solar cell element. The transparent substrate can be the same as a transparent substrate used in a general solar cell, and therefore a description thereof will be omitted here.

[0157] The counter substrate is a member that protects the solar cell element together with the transparent substrate described above. The counter substrate may or may not be transparent. When the counter substrate is transparent, both sides of the solar cell can be used as light receiving surfaces for sunlight. The counter substrate can be the transparent substrate described above. Also, the counter substrate can be a back surface protective sheet for solar cells.

[0158] 3. First and second sealing materials The first encapsulant is a member that encapsulates the solar cell element together with the second encapsulant. The first encapsulant is usually disposed on the light-receiving surface side of the solar cell.

[0159] The first sealing material contains a thermoplastic resin. The thermoplastic resin used in the first sealing material can be the same as the thermoplastic resin used in general solar cell sealing materials, and for example, a sealing material mainly composed of various olefin resins such as polyethylene resin and ethylene-vinyl acetate copolymer (EVA) can be used. "Mainly composed of these resins" means that the proportion of these resins is the highest among all resin components.

[0160] In the present disclosure, it is preferable that the first sealing material does not substantially contain an ultraviolet absorbing agent.

[0161] In conventional solar cells, polyethylene terephthalate (PET) is used for the heat-resistant layer, and an ultraviolet absorber is contained in the first encapsulant to prevent deterioration of PET due to ultraviolet rays. Therefore, such solar cells have low power generation efficiency in the ultraviolet light region.

[0162] On the other hand, the solar cell of the present disclosure uses the current collecting sheet described in the section "C. Solar cell element with current collecting sheet" as described above, and therefore deterioration of the heat-resistant layer due to ultraviolet rays can be suppressed. Therefore, there is no need to include an ultraviolet absorbing agent in the first sealing material, and by using a first sealing material that is substantially free of an ultraviolet absorbing agent, the solar cell of the present disclosure can improve the power generation efficiency in the ultraviolet region, and therefore the overall power generation efficiency can also be improved.

[0163] As described above, the first sealing material in the present disclosure does not substantially contain an ultraviolet absorbing agent. Specifically, the content of the ultraviolet absorbing agent in the first sealing material is preferably 3.0% by mass or less, more preferably 1.0% by mass or less, and further preferably 0.5% by mass or less.

[0164] The content of the ultraviolet absorber is measured, for example, by infrared spectroscopy (FTIR).

[0165] The ultraviolet absorber may be the same as the ultraviolet absorbers used in general solar cell encapsulants, specifically benzotriazole-based, triazine-based, and benzophenone-based ones. The first encapsulant being substantially free of ultraviolet absorbers means that the first encapsulant is substantially free of the ultraviolet absorbers.

[0166] The second encapsulant in the present disclosure is a member that encapsulates the solar cell element together with the first encapsulant. When the opposing substrate described above has transparency, it is preferable that the second encapsulant does not contain an ultraviolet absorbing agent, similar to the first encapsulant.

[0167] The thicknesses of the first and second encapsulating materials are appropriately selected depending on the type and size of the solar cell.

[0168] II. Physical properties of solar cells The solar cell of the present disclosure has a current collecting sheet with good ultraviolet transmittance and ultraviolet resistance, and therefore can actively utilize ultraviolet rays. The solar cell of the present disclosure preferably has an absorption sensitivity in the ultraviolet region, specifically, preferably has an absorption sensitivity in the range of 100 nm to 400 nm.

[0169] III. Manufacturing method The method for manufacturing the solar cell of the present disclosure can be the same as the method for manufacturing a general solar cell. One example is a manufacturing method having a laminate formation step of forming a laminate by laminating a transparent substrate, a first sealing material, a solar cell element with a current collecting sheet, a second sealing material, and an opposing substrate in this order, and an integration step of integrating the laminate by heating and pressurizing the laminate to form a solar cell.

[0170] The heating and pressurizing treatment can be the same as that performed during the manufacture of a general solar cell, and is not particularly limited, but is preferably, for example, a vacuum heat lamination method. The conditions of the vacuum heat lamination method can be appropriately selected according to the size of the solar cell, the type of each member, etc., and are not particularly limited, but for example, the lamination temperature is preferably 130°C or more and 170°C or less, and the lamination time is preferably 5 minutes or more and 30 minutes or less, and more preferably 8 minutes or more and 15 minutes or less.

[0171] IV.Applications The solar cell of the present disclosure can be used in a variety of applications, such as a solar cell for electronic devices and a large solar cell for outdoor installation.

[0172] The present disclosure is not limited to the above-described embodiments. The above-described embodiments are merely examples, and anything that has substantially the same configuration as the technical idea described in the claims of the present disclosure and exhibits similar effects is included in the technical scope of the present disclosure. EXAMPLES

[0173] [Examples 1 to 10] Resin compositions for forming the heat-resistant layer and the substrate layer and adhesive layer constituting the sealing layer were prepared using the resin components and additives shown in Table 1 below. The above-mentioned resin compositions were melted at 190°C using an extruder equipped with a T-die and co-extruded to obtain a resin film for a current collector sheet in which a heat-resistant layer, a substrate layer, and an adhesive layer were laminated in this order. The resin film for the current collector sheet had a total thickness of 100 μm, a heat-resistant layer thickness of 40 μm, a substrate layer thickness of 30 μm, and an adhesive layer thickness of 30 μm.

[0174] [Examples 11 to 20] Resin compositions for forming the heat-resistant layer and the sealing layer were prepared using the resin components and additives shown in Table 1 below. The above-mentioned resin compositions were melted at 190°C using an extruder equipped with a T-die and co-extruded to obtain a resin film for a current collector sheet in which a heat-resistant layer and a sealing layer were laminated. The resin film for the current collector sheet had a total thickness of 100 μm, a thickness of the heat-resistant layer of 40 μm, and a thickness of the sealing layer of 60 μm.

[0175] [Comparative Example 1] A resin film for a current collecting sheet was obtained in the same manner as in Example 1, except that resin compositions for forming each of the substrate layer and adhesive layer constituting the heat-resistant layer and the sealing layer were prepared using the resin components and additives shown in Table 1 below.

[0176] [Comparative Example 2] A PET film was prepared as the film constituting the heat-resistant layer, and an LDPE film was prepared as the film constituting the sealing layer. The PET film and the LDPE film were bonded together by dry lamination using an acrylic adhesive to obtain a resin film for a current collecting sheet.

[0177] [evaluation] (UV transmittance) First, for Examples 1 to 20 and Comparative Example 1, a sealant sheet ("CVF2SS" manufactured by Dai Nippon Printing Co., Ltd.) containing an olefin resin having a thickness of 450 μm was laminated on the heat-resistant layer side of the resin film for current collector sheet, and vacuum lamination was performed under the conditions of a set temperature of 150° C., vacuuming for 5 minutes, atmospheric pressure pressurization for 9 minutes, and pressure of 100 kPa to prepare a measurement sample. For Comparative Example 2, a sealant sheet ("CVF" manufactured by Dai Nippon Printing Co., Ltd.) containing an olefin resin having a thickness of 450 μm was laminated on the heat-resistant layer side of the resin film for current collector sheet, and vacuum lamination was performed under the conditions of a set temperature of 150° C., vacuuming for 5 minutes, atmospheric pressure pressurization for 9 minutes, and pressure of 100 kPa to prepare a measurement sample. Next, the transmittance of light at a wavelength of 350 nm of the measurement sample was measured using a spectrophotometer ("V-650" manufactured by JASCO Corporation).

[0178] (Total light transmittance) The total light transmittance of the obtained resin film for a current collecting sheet was measured in accordance with JIS K7361-1 using a haze meter HM150 manufactured by Murakami Color Research Laboratory Co., Ltd.

[0179] (Hayes) The obtained resin film for current collector sheet was cut to 50 mm x 50 mm to prepare a test piece. Next, an ETFE (tetrafluoroethylene-ethylene copolymer) film, a test piece, and an ETFE film were laminated in this order, and vacuum lamination was performed under the conditions of a set temperature of 165°C, vacuuming for 2 minutes, pressing for 2.5 minutes, and a pressure of 100 kPa. Next, the ETFE film was removed from both sides of the test piece to obtain a measurement sample. The haze of the measurement sample was measured using a haze meter HM150 manufactured by Murakami Color Research Laboratory Co., Ltd. in accordance with JIS K7136.

[0180] (Interlayer adhesion strength between heat-resistant layer and sealing layer (suitability for co-extrusion film formation)) The obtained resin film for current collector sheet was cut to a width of 15 mm and a length of 100 mm to prepare a sample. After providing an opportunity for peeling at the interface between the heat-resistant layer and the sealing layer of the obtained sample, a peel test was performed by holding the sample 10 mm above and below with a jig (Tensilon universal testing machine RTF-1150-H manufactured by A&D Corporation) with a chuck distance of 30 mm and a tensile strength of 50 mm / min, to measure the interlayer adhesion strength between the heat-resistant layer and the sealing layer.

[0181] (Storage modulus of heat-resistant layer) First, the resin film for the current collector sheet was cut into a size of 5 mm x 20 mm, and the sealing layer was scraped off from the resin film for the current collector sheet to prepare a sample of the heat-resistant layer. Next, the storage modulus of the heat-resistant layer was measured by dynamic viscoelasticity measurement (DMA) according to a method conforming to JIS K7244-4:1999. Specifically, both ends of the sample were attached to the chucks of a dynamic viscoelasticity measuring device (Rheogel-E4000 manufactured by UBM) so that the tensile direction was the longitudinal direction of the sample, and a tensile load was applied under the following measurement conditions to perform the measurement by the tensile method.

[0182] <Storage modulus measurement conditions> Measurement sample: 5mm x 20mm rectangle Measurement mode: Tensile method (sine wave strain, tension mode, strain amount: automatic strain) Heating rate: 3℃ / min ·Temperature: -60℃ or higher and 150℃ or lower Frequency: 10Hz Tensile load (static load): 100g

[0183] (Lightfastness test) A test piece of the resin film for the current collector sheet cut to 50 mm x 50 mm was placed in a Super UV tester (Iwasaki Electric Co., Ltd.'s "Eye Super UV Tester") and rated at 100 mW / cm 2 After 168 hours had passed, the appearance of the test piece was visually observed to evaluate the light resistance. A: No particular change in appearance B: Fine cracks have occurred C: Completely cracked in appearance

[0184] (Heat shrinkage rate) A test piece of the resin film for current collector sheet cut to 150 mm x 150 mm was drawn with a lattice pattern with a length of 100 mm, and then heated on talc in an oven set to 150°C for 10 minutes. The distance inside the lattice pattern was measured with a glass scale before and after heating to determine the thermal shrinkage rate. Note that in Comparative Examples 1 and 2, the resin film for current collector sheet melted when heated, making it impossible to measure.

[0185] (Curl test) The obtained resin film for current collecting sheet was cut into a size of 150 mm x 150 mm to prepare a sample. The above sample was placed on a horizontal surface with the surface of the heat-resistant layer facing downward, and the average deviation distance of each side of the test piece from the horizontal surface was measured. A deviation distance of less than 10 mm was rated as "A," and a deviation distance of more than 40 mm was rated as "B."

[0186] [Table 1]

[0187] [Table 2]

[0188] In Tables 1 and 2, "S135" refers to S135 (product name) manufactured by Prime Polymer Co., Ltd. (density 0.9 g / cm 3 , melting point 165°C, MFR (190°C) 4.0g / 10min), "S235" is S235 (product name) manufactured by Prime Polymer Co., Ltd. (density 0.900g / cm 3 , melting point 135°C, MFR (230°C) 10g / 10min), "PN3560" is Toughmer PN3560 (product name) manufactured by Mitsui Chemicals Inc. (density 0.866g / cm 3, melting point 160°C, MFR (190°C) 2.8g / 10min), "PN0040" is Toughmer PN0040 (product name) manufactured by Mitsui Chemicals Inc. (density 0.868g / cm 3 , melting point 160°C, MFR (190°C) 2.0g / 10min), "DF110" is Toughmer DF110 (product name) manufactured by Mitsui Chemicals Inc. (density 0.905g / cm 3 , melting point 94℃, MFR(190℃) 1.2g / 10min), "A4090S" is Toughmer A4090S (product name) manufactured by Mitsui Chemicals Inc. (density 0.893g / cm 3 , melting point 77℃, MFR(190℃) 3.6g / 10min), "XJ100H" is XJ-100X (product name) manufactured by Japan Polyethylene Co., Ltd. (density 0.93g / cm 3 , melting point 115°C, MFR (190°C) 3.0g / 10min), "KF260T" is Kernel KF260T (product name) manufactured by Japan Polyethylene Co., Ltd. (density 0.9g / cm 3 , melting point 93℃, MFR(190℃) 2.0g / 10min), "MF900N" is Mitsubishi Chemical's Linklon MF900N (product name) (density 0.9g / cm 3 , melting point 83°C, MFR (190°C) 1.0g / 10min).

[0189] From the results of Examples 1 to 20, it was confirmed that by incorporating polypropylene resin into the heat-resistant layer of the resin film for current collector sheet, it is possible to obtain a resin film for current collector sheet that has good ultraviolet transmittance and exhibits little deterioration in appearance even after light resistance testing.

[0190] That is, the present disclosure provides the following inventions. [1] A resin film for use in a current collector sheet of a solar cell, comprising a heat-resistant layer and a sealing layer disposed on one side of the heat-resistant layer, the heat-resistant layer containing a polypropylene resin. [2] The resin film for a current collecting sheet according to [1], wherein the heat-resistant layer contains a light stabilizer. [3] The resin film for a current collecting sheet according to [1] or [2], wherein the melting point of the resin used in the heat-resistant layer is 80°C or higher and 200°C or lower. [4] The resin film for current collecting sheets according to any one of [1] to [3], wherein the heat-resistant layer has a storage modulus at 150°C of 0.1 MPa or more and 1.0 GPa or less. [5] The resin film for current collecting sheets according to any one of [1] to [4], wherein the polypropylene resin is a homopolypropylene resin. [6] The resin film for a current collecting sheet according to any one of [1] to [5], wherein the heat-resistant layer contains at least one of a polyethylene-based elastomer and a polyethylene-based plastomer. [7] The resin film for a current collecting sheet according to any one of [1] to [6], wherein the sealing layer contains a polyolefin resin having a melting point of 80°C or higher and 125°C or lower. [8] The resin film for current collecting sheets according to [7], wherein the polyolefin resin is a polyethylene resin. [9] The resin film for a current collecting sheet according to [8], wherein the sealing layer contains a silane-modified polyethylene resin.

[10] A current collecting sheet for use in a solar cell, comprising: a resin film for current collecting sheets according to any one of [1] to [9]; and a wire arranged on the sealing layer side of the resin film for current collecting sheets.

[11]

[10] A solar cell element with a current collecting sheet, comprising: the current collecting sheet according to

[11] ; and a solar cell element arranged on the sealing layer side of the current collecting sheet and electrically connected to the wire.

[12] The solar cell element with a current collecting sheet according to

[11] , wherein the minimum distance from the surface of the solar cell element on which the current collecting sheet is arranged to the surface of the heat-resistant layer opposite the solar cell element is 2 / 3 or less of the maximum distance of the wire from the surface of the solar cell element on which the current collecting sheet is arranged.

[13] A solar cell element with a current collecting sheet as described in

[12] , comprising a plurality of the wires, and in a cross-sectional view of the solar cell element with the current collecting sheet, the shortest distance from the surface of the solar cell element on which the current collecting sheet is arranged to the surface of the heat-resistant layer opposite the solar cell element is located between adjacent wires.

[14] The solar cell element with a current collecting sheet according to any one of

[11] to

[13] , wherein the wire is in contact with the heat-resistant layer.

[15] A solar cell comprising a transparent substrate, a first encapsulant, a solar cell element with a current collecting sheet according to any one of

[11] to

[14] , a second encapsulant, and an opposing substrate, arranged in this order.

[16] The solar cell according to

[15] , wherein the first encapsulant has an ultraviolet absorbing agent content of 3.0 mass % or less.

[17] The solar cell according to

[15] or

[16] , wherein the solar cell is a solar cell module including a plurality of solar cell elements with the current collecting sheet. [Explanation of symbols]

[0191] 1 … Heat-resistant layer 2 … Sealing layer 2a...Base material layer 2b…adhesive layer 10, 10A, 10B ... Resin film for current collector sheet 11 ... Wire 20... Current collector sheet 30...Solar cell element with current collector sheet 31 ... Solar cell element 40... Solar cell 41 ... Transparent substrate 42 … First sealing material 43 ... Second sealing material 44 ... Opposing substrate

Claims

[Claim 1] A resin film for a current collector sheet used in a current collector sheet of a solar cell, comprising: A heat-resistant layer and a sealing layer disposed on one surface side of the heat-resistant layer, The heat-resistant layer contains a polypropylene resin, The sealing layer comprises a thermoplastic resin and a silane-modified polyethylene resin.