Cartridge

Abstract

To provide a servo writer that reduces the number of cartridges to be discarded.SOLUTION: A servo writer 210 for a cartridge 10 includes: a traveling portion that feeds out a tape-shaped magnetic recording medium (magnetic tape MT) from the cartridge and winds the feed magnetic recording medium to make the magnetic recording medium travel; a demagnetizing magnet 214 that erases a first servo pattern formed on the traveling magnetic recording medium; a servo signal writing head 215 that writes a servo signal onto the traveling magnetic recording medium after the first servo pattern is erased and forms a second servo pattern; and a control device that controls the head to write the servo signal during at least one of acceleration and deceleration traveling periods of the magnetic recording medium and forms the second servo pattern that does not satisfy the standard on the magnetic recording medium.SELECTED DRAWING: Figure 8

Description

[Technical field]

[0001] The present disclosure relates to a servo writer and a cartridge. [Background technology]

[0002] In recent years, in order to improve the data recording density of tape-type magnetic recording media used as computer data storage, the width of the data tracks and the distance between adjacent data tracks have been narrowed. When the width of the data tracks and the distance between adjacent data tracks are narrowed in this manner, it becomes difficult for the recording / reproducing element of the magnetic head to trace the data tracks.

[0003] For this reason, a technology has been proposed in which a servo signal is written in advance on a magnetic recording medium, and then this servo signal is read by a magnetic head, thereby servo-controlling the position of the recording / reproducing element of the magnetic head in the width direction of the magnetic recording medium (see, for example, Patent Document 1). [Prior art documents] [Patent documents]

[0004] [Patent Document 1] JP 2006-127730 A Summary of the Invention [Problem to be solved by the invention]

[0005] The magnetic recording medium on which the servo signal is written is housed in a cartridge case, and after the quality of the magnetic recording medium is inspected, it is shipped as a product. Conventionally, if the quality of the servo signal is found to be poor at the above-mentioned quality inspection stage, the cartridge has been discarded. Therefore, if a large number of cartridges are discarded, there is a risk that the productivity of the cartridge will decrease.

[0006] An object of the present disclosure is to provide a servo writer that can reduce the number of cartridges that are discarded, and a cartridge on which a servo signal is recorded using the servo writer. [Means for solving the problem]

[0007] In order to solve the above problems, the first disclosure is: a running unit that runs the magnetic recording medium by feeding the tape-like magnetic recording medium from the cartridge and taking up the magnetic recording medium that has been fed out; an erasing unit that erases a first servo pattern formed on the traveling magnetic recording medium; a head for writing a servo signal onto the traveling magnetic recording medium from which the first servo pattern has been erased, to form a second servo pattern; a control unit that controls the head to write a servo signal during at least one of an accelerating running period and a decelerating running period of the magnetic recording medium, and forms a second servo pattern that does not satisfy the standard on the magnetic recording medium; The servo writer includes:

[0008] The second disclosure is: a running unit that runs the magnetic recording medium by feeding the tape-like magnetic recording medium from the cartridge and taking up the magnetic recording medium that has been fed out; an erasing unit that erases a first servo pattern formed on the traveling magnetic recording medium; a head for writing a servo signal onto the traveling magnetic recording medium from which the first servo pattern has been erased, to form a second servo pattern; a control unit that controls the head so as not to write a servo signal during at least one of an accelerating period and a decelerating period of the magnetic recording medium; The servo writer includes:

[0009] The third disclosure is: a wound tape-like magnetic recording medium; A case for accommodating a magnetic recording medium; Equipped with The magnetic recording medium has an unused area, The unused area is a cartridge in which a servo pattern that does not meet the standard is formed, or in which no servo pattern is formed. [Brief description of the drawings]

[0010] [Figure 1] FIG. 1 is an exploded perspective view showing an example of the configuration of a cartridge. [Diagram 2] FIG. 2 is a cross-sectional view showing an example of the configuration of a magnetic tape. [Diagram 3] FIG. 3 is a schematic diagram showing an example of a layout of a data band and a servo band. [Figure 4] FIG. 4 is an enlarged view showing an example of the configuration of a data band. [Diagram 5] FIG. 5 is an enlarged view showing an example of the configuration of a servo band. [Figure 6] FIG. 6 is a schematic diagram showing an example of a format of a magnetic tape. [Figure 7] Fig. 7A is a schematic diagram showing a first example of a servo pattern that does not meet the standard, Fig. 7B is a schematic diagram showing a second example of a servo pattern that does not meet the standard, and Fig. 7C is a schematic diagram showing an example of a servo pattern that meets the standard. [Figure 8] FIG. 8 is a schematic diagram showing an example of the configuration of a servo writer for a cartridge. [Figure 9] FIG. 9 is a schematic diagram showing an example of the configuration of a servo signal recording system. [Figure 10] FIG. 10 is a schematic diagram showing an example of the configuration of a servo writer for pancake recording. [Figure 11] FIG. 11 is a schematic diagram showing an example of the configuration of a winder. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present disclosure will be described in the following order with reference to the drawings. In all the drawings of the following embodiments, the same or corresponding parts are denoted by the same reference numerals. 1 Cartridge Configuration 2. Magnetic Tape Configuration 3 Magnetic Tape Format 4. Configuring a Servo Writer for Cartridges 5. Operation of the servo writer for cartridges 6. Configuration of servo signal recording system 7 Operation of servo signal recording system 8. Effects 9. Variations

[0012] [1 cartridge configuration] FIG. 1 is an exploded perspective view showing an example of the configuration of a cartridge 10. The cartridge 10 is a magnetic tape cartridge conforming to the LTO (Linear Tape-Open) standard, and includes a reel 13 around which a magnetic tape (a tape-like magnetic recording medium) MT is wound, a reel lock 14 and a reel spring 15 for locking the rotation of the reel 13, a spider 16 for unlocking the locked state of the reel 13, a slide door 17 for opening and closing a tape outlet 12C provided in the cartridge case 12 across the lower shell 12A and the upper shell 12B, a door spring 18 for biasing the slide door 17 to a closed position of the tape outlet 12C, a write protector 19 for preventing erroneous erasure, and a cartridge memory 11. The reel 13 is substantially disk-shaped with an opening in the center, and is composed of a reel hub 13A and a flange 13B made of a hard material such as plastic. A leader pin 20 is provided at one end of the magnetic tape MT.

[0013] The cartridge memory 11 is provided near one corner of the cartridge 10. When the cartridge 10 is loaded into the recording and playback device, the cartridge memory 11 faces a reader / writer of the recording and playback device. The cartridge memory 11 communicates with the recording and playback device, specifically, with the reader / writer of the recording and playback device, using a wireless communication standard that complies with the LTO standard.

[0014] [2. Magnetic Tape Structure] 2 is a cross-sectional view showing an example of the configuration of the magnetic tape MT. The magnetic tape MT is a tape-shaped magnetic recording medium, and includes a long substrate 41, an underlayer 42 provided on one main surface (first main surface) of the substrate 41, a magnetic layer 43 provided on the underlayer 42, and a back layer 44 provided on the other main surface (second main surface) of the substrate 41. The underlayer 42 and the back layer 44 are provided as necessary, and may be omitted. The magnetic tape MT may be a perpendicular recording type magnetic recording medium or a longitudinal recording type magnetic recording medium.

[0015] The magnetic tape MT is preferably used in a recording / reproducing device having a ring-type head as a recording head. The magnetic tape MT is preferably configured so that the width of the magnetic tape MT can be kept constant or nearly constant by adjusting the tension in the longitudinal direction of the magnetic tape MT during running using the recording / reproducing device.

[0016] (Base) The substrate 41 is a non-magnetic support that supports the underlayer 42 and the magnetic layer 43. The substrate 41 has a long film shape. The upper limit of the average thickness of the substrate 41 is preferably 4.2 μm or less, more preferably 3.8 μm or less, and even more preferably 3.4 μm or less. When the upper limit of the average thickness of the substrate 41 is 4.2 μm or less, the recording capacity that can be recorded in one data cartridge can be made higher than that of a general magnetic tape. The lower limit of the average thickness of the substrate 41 is preferably 3 μm or more, and more preferably 3.2 μm or more. When the lower limit of the average thickness of the substrate 41 is 3 μm or more, a decrease in the strength of the substrate 41 can be suppressed.

[0017] The average thickness of the substrate 41 is obtained as follows. First, a 1 / 2 inch wide magnetic tape MT is prepared and cut into a length of 250 mm to prepare a sample. Next, layers other than the substrate 41 of the sample (i.e., the underlayer 42, the magnetic layer 43, and the back layer 44) are removed with a solvent such as MEK (methyl ethyl ketone) or dilute hydrochloric acid. Next, the thickness of the sample (substrate 41) is measured at five or more positions using a Mitutoyo Laser Hologram (LGH-110C) as a measuring device, and the measured values ​​are simply averaged (arithmetic average) to calculate the average thickness of the substrate 41. Note that the measurement positions are selected randomly from the sample.

[0018] The substrate 41 preferably contains polyester. By containing polyester, the Young's modulus in the longitudinal direction of the substrate 41 can be reduced. Therefore, by adjusting the tension in the longitudinal direction of the magnetic tape MT during running by a recording / reproducing device (drive), the width of the magnetic tape MT can be kept constant or approximately constant.

[0019] The polyester includes, for example, at least one of polyethylene terephthalate (PET), polyethylene naphthalate (PEN), polybutylene terephthalate (PBT), polybutylene naphthalate (PBN), polycyclohexylene dimethylene terephthalate (PCT), polyethylene-p-oxybenzoate (PEB), and polyethylene bisphenoxycarboxylate. When the base 41 includes two or more types of polyester, the two or more types of polyester may be mixed, copolymerized, or laminated. At least one of the terminals and side chains of the polyester may be modified.

[0020] The inclusion of polyester in the base 41 can be confirmed, for example, as follows. First, in the same manner as in the measurement of the average thickness of the base 41, layers of the sample other than the base 41 are removed. Next, an IR spectrum of the sample (base 41) is obtained by infrared absorption spectrometry (IR). Based on this IR spectrum, it can be confirmed that the base 41 contains polyester.

[0021] The base 41 may further contain, in addition to polyester, for example, at least one of polyamide, polyimide, and polyamideimide, or at least one of polyamide, polyimide, polyamideimide, polyolefins, cellulose derivatives, vinyl resins, and other polymer resins. The polyamide may be an aromatic polyamide (aramid). The polyimide may be an aromatic polyimide. The polyamideimide may be an aromatic polyamideimide.

[0022] When the base 41 contains a polymer resin other than polyester, it is preferable that the base 41 contains polyester as a main component. Here, the main component means the component with the largest content (mass ratio) among the polymer resins contained in the base 41. When the base 41 contains a polymer resin other than polyester, the polyester and the polymer resin other than polyester may be mixed or copolymerized.

[0023] The substrate 41 may be biaxially stretched in the longitudinal direction and the width direction. The polymer resin contained in the substrate 41 is preferably oriented in a direction oblique to the width direction of the substrate 41.

[0024] (magnetic layer) The magnetic layer 43 is a recording layer for recording signals by magnetization patterns. The magnetic layer 43 may be a perpendicular recording type recording layer or a longitudinal recording type recording layer. The magnetic layer 43 includes, for example, a magnetic powder and a binder. The magnetic layer 43 may further include at least one additive selected from the group consisting of a lubricant, an antistatic agent, an abrasive, a hardener, an anticorrosive agent, and nonmagnetic reinforcing particles, as necessary.

[0025] The average thickness t of the magnetic layer 43 m The upper limit of the average thickness t of the magnetic layer 43 is 80 nm or less, preferably 70 nm or less, and more preferably 50 nm or less. m If the upper limit value is 80 nm or less, when a ring-type head is used as the recording head, the influence of the demagnetizing field can be reduced, and therefore further excellent electromagnetic conversion characteristics can be obtained.

[0026] The average thickness t of the magnetic layer 43 m The lower limit of the average thickness t of the magnetic layer 43 is preferably 35 nm or more. m If the lower limit is 35 nm or more, output can be ensured when a magnetoresistive (MR) head, a giant magnetoresistive (GMR) head, or a tunneling magnetoresistive (TMR) head is used as the reproducing head, thereby obtaining even better electromagnetic conversion characteristics.

[0027] The average thickness t of the magnetic layer 43 m is obtained as follows. First, the magnetic tape MT to be measured is processed and sliced ​​by FIB or the like. When the FIB method is used, a carbon layer and a tungsten layer are formed as protective films as a pretreatment for observing a TEM image of the cross section described later. The carbon layer is formed on the surface of the magnetic tape MT on the magnetic layer 43 side and the surface on the back layer 44 side by a vapor deposition method, and the tungsten layer is further formed on the surface on the magnetic layer 43 side by a vapor deposition method or a sputtering method. The slice is performed along the length direction (longitudinal direction) of the magnetic tape MT. That is, the slice forms a cross section parallel to both the longitudinal direction and the thickness direction of the magnetic tape MT.

[0028] The cross section of the obtained sliced ​​sample is observed under the following conditions with a transmission electron microscope (TEM) to obtain a TEM image. Note that the magnification and acceleration voltage may be appropriately adjusted depending on the type of device. Equipment: TEM (Hitachi H9000NAR) Acceleration voltage: 300 kV Magnification: 100,000x

[0029] Next, the thickness of the magnetic layer 43 is measured at at least 10 points in the longitudinal direction of the magnetic tape MT using the obtained TEM image. The measured values ​​are simply averaged (arithmetic average) to obtain an average thickness t m The positions at which the above measurements are performed are to be selected randomly from the test piece.

[0030] (magnetic powder) The magnetic powder includes a plurality of magnetic particles. The magnetic particles are, for example, particles containing hexagonal ferrite (hereinafter referred to as "hexagonal ferrite particles"), particles containing epsilon iron oxide (ε iron oxide) (hereinafter referred to as "ε iron oxide particles"), or particles containing Co-containing spinel ferrite (hereinafter referred to as "cobalt ferrite particles"). It is preferable that the magnetic powder has a crystal orientation preferentially in the thickness direction (perpendicular direction) of the magnetic tape MT.

[0031] (Hexagonal ferrite particles) The hexagonal ferrite particles have a plate shape, such as a hexagonal plate shape. In this specification, the hexagonal slope shape includes an almost hexagonal slope shape. The hexagonal ferrite preferably contains at least one of Ba, Sr, Pb and Ca, more preferably at least one of Ba and Sr. The hexagonal ferrite may be, specifically, for example, barium ferrite or strontium ferrite. The barium ferrite may further contain at least one of Sr, Pb and Ca in addition to Ba. The strontium ferrite may further contain at least one of Ba, Pb and Ca in addition to Sr.

[0032] More specifically, hexagonal ferrite has the general formula MFe 12 O 19 The average composition is represented by the formula: where M is, for example, at least one metal selected from Ba, Sr, Pb, and Ca, and preferably at least one metal selected from Ba and Sr. M may be a combination of Ba and at least one metal selected from the group consisting of Sr, Pb, and Ca. M may also be a combination of Sr and at least one metal selected from the group consisting of Ba, Pb, and Ca. In the above general formula, a part of Fe may be substituted with another metal element.

[0033] (ε iron oxide particles) The ε-iron oxide particles are hard magnetic particles that can obtain high coercivity even in the case of fine particles. The ε-iron oxide particles are spherical or cubic. In this specification, the term "spherical" includes "approximately spherical." Furthermore, the term "cubic" includes "approximately cubic." Since the ε-iron oxide particles have the above-mentioned shape, when the ε-iron oxide particles are used as the magnetic particles, the contact area between the particles in the thickness direction of the magnetic tape MT can be reduced and the aggregation between the particles can be suppressed compared to when hexagonal plate-shaped barium ferrite particles are used as the magnetic particles. Therefore, the dispersibility of the magnetic powder can be improved, and further excellent electromagnetic conversion characteristics (e.g., SNR) can be obtained.

[0034] The ε-iron oxide particles have a core-shell structure. Specifically, the ε-iron oxide particles have a core and a two-layered shell portion provided around the core. The two-layered shell portion has a first shell portion provided on the core and a second shell portion provided on the first shell portion.

[0035] The core portion contains ε-iron oxide. The ε-iron oxide contained in the core portion preferably has ε-Fe2O3 crystals as a main phase, and more preferably is made of single-phase ε-Fe2O3.

[0036] The first shell portion covers at least a part of the periphery of the core portion. Specifically, the first shell portion may cover a part of the periphery of the core portion, or may cover the entire periphery of the core portion. From the viewpoint of ensuring sufficient exchange coupling between the core portion and the first shell portion and improving magnetic properties, it is preferable that the first shell portion covers the entire surface of the core portion.

[0037] The first shell portion is a so-called soft magnetic layer, and contains a soft magnetic material such as α-Fe, a Ni-Fe alloy, an Fe-Si-Al alloy, etc. The α-Fe may be obtained by reducing ε-iron oxide contained in the core portion.

[0038] The second shell portion is an oxide coating serving as an anti-oxidation layer. The second shell portion includes α-iron oxide, aluminum oxide, or silicon oxide. The α-iron oxide includes at least one type of iron oxide, for example, Fe3O4, Fe2O3, and FeO. When the first shell portion includes α-Fe (soft magnetic material), the α-iron oxide may be obtained by oxidizing the α-Fe included in the first shell portion.

[0039] By having the first shell portion as described above, the coercivity Hc of the ε-iron oxide particles as a whole (core-shell particles) can be adjusted to a coercivity Hc suitable for recording while maintaining a high coercivity Hc of the core portion alone to ensure thermal stability. Furthermore, by having the second shell portion as described above, it is possible to prevent the ε-iron oxide particles from being exposed to air during and before the manufacturing process of the magnetic tape MT, which would cause rust or the like to form on the particle surface, thereby preventing the properties of the ε-iron oxide particles from deteriorating. This makes it possible to prevent the properties of the magnetic tape MT from deteriorating.

[0040] The ε-iron oxide particles may have a shell part with a single layer structure. In this case, the shell part has the same structure as the first shell part. However, from the viewpoint of suppressing deterioration of the properties of the ε-iron oxide particles, it is preferable that the ε-iron oxide particles have a shell part with a two-layer structure, as described above.

[0041] The ε iron oxide particles may contain an additive instead of the core-shell structure, or may have a core-shell structure and contain an additive. In this case, part of the Fe in the ε iron oxide particles is replaced with the additive. By containing an additive in the ε iron oxide particles, the coercive force Hc of the ε iron oxide particles as a whole can be adjusted to a coercive force Hc suitable for recording, thereby improving ease of recording. The additive is a metal element other than iron, preferably a trivalent metal element, more preferably at least one of Al, Ga and In, and even more preferably at least one of Al and Ga.

[0042] Specifically, ε-iron oxide containing additives is ε-Fe 2-x M x O3 crystal (wherein M is a metal element other than iron, preferably a trivalent metal element, more preferably at least one of Al, Ga and In, and even more preferably at least one of Al and Ga. x is, for example, 0 <x<1である。)である。

[0043] (Cobalt ferrite particles) The cobalt ferrite particles preferably have uniaxial crystal anisotropy. The cobalt ferrite particles have uniaxial crystal anisotropy, so that the magnetic powder can be preferentially crystal oriented in the thickness direction (vertical direction) of the magnetic tape MT. The cobalt ferrite particles have, for example, a cubic shape. In this specification, the cubic shape includes an almost cubic shape. The Co-containing spinel ferrite may further contain at least one of Ni, Mn, Al, Cu and Zn in addition to Co.

[0044] The Co-containing spinel ferrite has, for example, an average composition represented by the following formula. Co x M y FeO Z (In the formula, M is at least one metal selected from the group consisting of Ni, Mn, Al, Cu, and Zn. x is a value within the range of 0.4≦x≦1.0. y is a value within the range of 0≦y≦0.3. However, x and y satisfy the relationship of (x+y)≦1.0. z is a value within the range of 3≦z≦4. A part of Fe may be substituted with another metal element.)

[0045] (Binding agent) Examples of the binder include thermoplastic resins, thermosetting resins, and reactive resins. Examples of the thermoplastic resins include vinyl chloride, vinyl acetate, vinyl chloride-vinyl acetate copolymers, vinyl chloride-vinylidene chloride copolymers, vinyl chloride-acrylonitrile copolymers, acrylic acid ester-acrylonitrile copolymers, acrylic acid ester-vinyl chloride-vinylidene chloride copolymers, acrylic acid ester-acrylonitrile copolymers, acrylic acid ester-vinylidene chloride copolymers, methacrylic acid ester-vinylidene chloride copolymers, methacrylic acid ester-vinyl chloride copolymers, methacrylic acid ester-ethylene copolymers, polyvinyl fluoride, vinylidene chloride-acrylonitrile copolymers, acrylonitrile-butadiene copolymers, polyamide resins, polyvinyl butyral, cellulose derivatives (cellulose acetate butyrate, cellulose diacetate, cellulose triacetate, cellulose propionate, nitrocellulose), styrene-butadiene copolymers, polyurethane resins, polyester resins, amino resins, and synthetic rubbers.

[0046] Examples of the thermosetting resin include phenol resin, epoxy resin, polyurethane curing resin, urea resin, melamine resin, alkyd resin, silicone resin, polyamine resin, and urea formaldehyde resin.

[0047] All of the above binders contain -SO3M, -OSO3M, -COOM, P=O(OM)2 (where M represents a hydrogen atom or an alkali metal such as lithium, potassium, or sodium), -NR1R2, -NR1R2R3, etc., in order to improve the dispersibility of the magnetic powder. + X -Side chain amines with terminal groups represented by >NR1R2 + X - (wherein R1, R2, and R3 each represent a hydrogen atom or a hydrocarbon group; X - represents a halogen element ion such as fluorine, chlorine, bromine, or iodine, an inorganic ion, or an organic ion.) Polar functional groups such as -OH, -SH, -CN, and an epoxy group may be introduced. The amount of these polar functional groups introduced into the binder is 10 -1 ~10 -8 mol / g, preferably 10 -2 ~10 -6 More preferably, it is expressed in moles / g.

[0048] (Lubricant) The lubricant contains at least one selected from, for example, a fatty acid and a fatty acid ester, and preferably both a fatty acid and a fatty acid ester. The inclusion of a lubricant in magnetic layer 43, and in particular the inclusion of both a fatty acid and a fatty acid ester in magnetic layer 43, contributes to improving the running stability of magnetic tape MT.

[0049] The fatty acid may preferably be a compound represented by the following general formula (1) or (2). For example, the fatty acid may contain either a compound represented by the following general formula (1) or a compound represented by the following general formula (2), or may contain both.

[0050] The fatty acid ester may preferably be a compound represented by the following general formula (3) or (4). For example, the fatty acid ester may contain either a compound represented by the following general formula (3) or a compound represented by the following general formula (4), or may contain both.

[0051] By the lubricant containing either or both of a compound represented by general formula (1) and a compound represented by general formula (2), and either or both of a compound represented by general formula (3) and a compound represented by general formula (4), it is possible to suppress an increase in the dynamic friction coefficient of the magnetic tape MT due to repeated recording or playback.

[0052] CH3(CH2) k COOH (1) (However, in general formula (1), k is an integer selected from the range of 14 or more and 22 or less, more preferably from the range of 14 or more and 18 or less.)

[0053] CH3(CH2) n CH=CH(CH2) m COOH (2) (However, in general formula (2), the sum of n and m is an integer selected from the range of 12 to 20, more preferably from the range of 14 to 18.)

[0054] CH3(CH2) p COO(CH2) q CH3···(3) (However, in general formula (3), p is an integer selected from the range of 14 or more and 22 or less, more preferably 14 or more and 18 or less, and q is an integer selected from the range of 2 or more and 5 or less, more preferably 2 or more and 4 or less.)

[0055] CH3(CH2) r COO-(CH2) s CH(CH3)2 ···(4) (In the general formula (4), r is an integer selected from the range of 14 to 22, and s is an integer selected from the range of 1 to 3.)

[0056] (Antistatic agent) Examples of the antistatic agent include carbon black, natural surfactants, nonionic surfactants, and cationic surfactants.

[0057] (Abrasive) Examples of abrasives include acicular α-iron oxide obtained by dehydrating and annealing raw materials such as α-alumina with an α-conversion rate of 90% or more, β-alumina, γ-alumina, silicon carbide, chromium oxide, cerium oxide, α-iron oxide, corundum, silicon nitride, titanium carbide, titanium oxide, silicon dioxide, tin oxide, magnesium oxide, tungsten oxide, zirconium oxide, boron nitride, zinc oxide, calcium carbonate, calcium sulfate, barium sulfate, molybdenum disulfide, and magnetic iron oxide, and these may be surface-treated with aluminum and / or silica as necessary.

[0058] (hardening agent) Examples of the curing agent include polyisocyanates. Examples of the polyisocyanates include aromatic polyisocyanates such as an adduct of tolylene diisocyanate (TDI) and an active hydrogen compound, and aliphatic polyisocyanates such as an adduct of hexamethylene diisocyanate (HMDI) and an active hydrogen compound. The weight average molecular weight of these polyisocyanates is preferably in the range of 100 to 3000.

[0059] (rust inhibitor) Examples of the rust inhibitor include phenols, naphthols, quinones, heterocyclic compounds containing a nitrogen atom, heterocyclic compounds containing an oxygen atom, and heterocyclic compounds containing a sulfur atom.

[0060] (Non-magnetic reinforcing particles) Examples of non-magnetic reinforcing particles include aluminum oxide (α, β or γ alumina), chromium oxide, silicon oxide, diamond, garnet, emery, boron nitride, titanium carbide, silicon carbide, titanium carbide, titanium oxide (rutile or anatase type titanium oxide), and the like.

[0061] (base layer) The underlayer 42 serves to reduce the unevenness of the surface of the substrate 41 and adjust the unevenness of the surface of the magnetic layer 43. The underlayer 42 is a non-magnetic layer containing non-magnetic powder, a binder, and a lubricant. The underlayer 42 supplies the lubricant to the surface of the magnetic layer 43. The underlayer 42 may further contain at least one additive selected from the group consisting of an antistatic agent, a hardener, and an anti-rust agent, as necessary.

[0062] The average thickness of the underlayer 42 is preferably 0.3 μm or more and 2.0 μm or less, and more preferably 0.5 μm or more and 1.4 μm or less. m The magnification of the TEM image is adjusted appropriately according to the thickness of the underlayer 42. When the average thickness of the underlayer 42 is 2.0 μm or less, the elasticity of the magnetic tape MT due to an external force is further increased, so that the width of the magnetic tape MT can be further easily adjusted by adjusting the tension.

[0063] (Non-magnetic powder) The non-magnetic powder includes at least one of inorganic particle powder and organic particle powder. The non-magnetic powder may also include carbon powder such as carbon black. One type of non-magnetic powder may be used alone, or two or more types of non-magnetic powder may be used in combination. The inorganic particles include, for example, metals, metal oxides, metal carbonates, metal sulfates, metal nitrides, metal carbides, or metal sulfides. The shape of the non-magnetic powder may be, for example, various shapes such as needle-like, spherical, cubic, and plate-like, but is not limited to these shapes.

[0064] (Binding agent, lubricant) The binder and lubricant are the same as those in the magnetic layer 43 described above.

[0065] (Additives) The antistatic agent, hardening agent and anticorrosive agent are the same as those in the magnetic layer 43 described above.

[0066] (Back layer) The back layer 44 includes a binder and a non-magnetic powder. The back layer 44 may further include at least one additive selected from the group consisting of a lubricant, a hardener, and an antistatic agent, as necessary. The binder and the non-magnetic powder are the same as those of the underlayer 42 described above.

[0067] The upper limit of the average thickness of the back layer 44 is preferably 0.6 μm or less. If the upper limit of the average thickness of the back layer 44 is 0.6 μm or less, the thickness of the underlayer 42 and the base 41 can be kept thick even when the average thickness of the magnetic tape MT is 5.6 μm or less, so that the running stability of the magnetic tape MT in a recording and reproducing device can be maintained. The lower limit of the average thickness of the back layer 44 is not particularly limited, but is, for example, 0.2 μm or more.

[0068] The average thickness t of the back layer 44 b can be calculated as follows: First, the average thickness t of the magnetic tape MT T Measure the average thickness t T The method for measuring the thickness is as described in the "Average Thickness of Magnetic Tape" below. Next, the back layer 44 of the sample is removed with a solvent such as MEK (methyl ethyl ketone) or dilute hydrochloric acid. Next, the thickness of the sample is measured at five or more points using a Mitutoyo Laser Hologram (LGH-110C), and the measured values ​​are simply averaged (arithmetic average) to obtain the average thickness t B Then, the average thickness t of the back layer 44 is calculated using the following formula: b The measurement points are selected randomly from the sample. t b [μm]=t T [μm]-t B [μm]

[0069] (average thickness of magnetic tape) Average thickness of magnetic tape MT (average total thickness) t T The upper limit of the average thickness t of the magnetic tape MT is 5.6 μm or less, preferably 5.0 μm or less, more preferably 4.6 μm or less, and even more preferably 4.4 μm or less. TIf the average thickness t of the magnetic tape MT is 5.6 μm or less, the recording capacity that can be recorded in one data cartridge can be increased compared to that of a general magnetic tape. T The lower limit is not particularly limited, but is, for example, 3.5 μm or more.

[0070] Average thickness t of magnetic tape MT T can be calculated as follows. First, a 1 / 2 inch wide magnetic tape MT is prepared and cut into a length of 250 mm to prepare a sample. Next, the thickness of the sample is measured at five or more points using a Mitutoyo Laser Hologram (LGH-110C) as a measuring device, and the measured values ​​are simply averaged (arithmetic mean) to obtain the average thickness t T The measurement points are selected randomly from the sample.

[0071] (Coercive force) The upper limit of the coercive force Hc2 of the magnetic layer 43 in the longitudinal direction of the magnetic tape MT is preferably 2000 Oe or less, more preferably 1900 Oe or less, and even more preferably 1800 Oe or less. If the coercive force Hc2 of the magnetic layer 43 in the longitudinal direction is 2000 Oe or less, sufficient electromagnetic conversion characteristics can be obtained even at high recording density.

[0072] The lower limit of the coercive force Hc2 of the magnetic layer 43 measured in the longitudinal direction of the magnetic tape MT is preferably 1000 Oe or more. When the coercive force Hc2 of the magnetic layer 43 measured in the longitudinal direction is 1000 Oe or more, demagnetization due to leakage flux from the recording head can be suppressed.

[0073] The coercive force Hc2 is obtained as follows. First, three magnetic tapes MT are stacked with double-sided tape, and then punched out with a φ6.39 mm punch to prepare a measurement sample. At this time, marking is performed with any non-magnetic ink so that the longitudinal direction (running direction) of the magnetic tape MT can be recognized. Then, the MH loop of the measurement sample (whole magnetic tape MT) corresponding to the longitudinal direction (running direction) of the magnetic tape MT is measured using a vibrating sample magnetometer (VSM). Next, the coating film (underlayer 42, magnetic layer 43, back layer 44, etc.) is wiped off using acetone or ethanol, etc., and only the substrate 41 remains. Then, three obtained substrates 41 are stacked with double-sided tape, and then punched out with a φ6.39 mm punch to prepare a sample for background correction (hereinafter simply referred to as "correction sample"). Thereafter, the MH loop of the correction sample (substrate 41) corresponding to the perpendicular direction of the substrate 41 (perpendicular direction of the magnetic tape MT) is measured using the VSM.

[0074] The MH loop of the measurement sample (entire magnetic tape MT) and the MH loop of the correction sample (substrate 41) are measured using a high-sensitivity vibration sample magnetometer "VSM-P7-15 type" manufactured by Toei Industry Co., Ltd. The measurement conditions are as follows: measurement mode: full loop, maximum magnetic field: 15 kOe, magnetic field step: 40 bits, time constant of locking amp: 0.3 sec, waiting time: 1 sec, number of MH averages: 20.

[0075] After the MH loop of the measurement sample (whole magnetic tape MT) and the MH loop of the correction sample (substrate 41) are obtained, background correction is performed by subtracting the MH loop of the correction sample (substrate 41) from the MH loop of the measurement sample (whole magnetic tape MT), and the MH loop after background correction is obtained. The measurement and analysis program attached to the "VSM-P7-15" is used for this background correction calculation. The coercive force Hc2 is obtained from the obtained MH loop after background correction. The measurement and analysis program attached to the "VSM-P7-15" is used for this calculation. All of the above MH loop measurements are performed at 25°C. In addition, no "demagnetization field correction" is performed when measuring the MH loop in the longitudinal direction of the magnetic tape MT.

[0076] (Square ratio) The squareness ratio S1 of the magnetic layer 43 in the perpendicular direction (thickness direction) of the magnetic tape MT is preferably 65% ​​or more, more preferably 70% or more, even more preferably 75% or more, particularly preferably 80% or more, and most preferably 85% or more. When the squareness ratio S1 is 65% or more, the perpendicular orientation of the magnetic powder is sufficiently high, and therefore, even more excellent electromagnetic conversion characteristics can be obtained.

[0077] The squareness ratio S1 in the vertical direction is obtained as follows. First, three magnetic tapes MT are stacked with double-sided tape, and then punched with a φ6.39 mm punch to prepare a measurement sample. At this time, marking is performed with any non-magnetic ink so that the longitudinal direction (running direction) of the magnetic tape MT can be recognized. Then, the MH loop of the measurement sample (whole magnetic tape MT) corresponding to the vertical direction (thickness direction) of the magnetic tape MT is measured using a VSM. Next, the coating film (underlayer 42, magnetic layer 43, back layer 44, etc.) is wiped off using acetone or ethanol, etc., and only the substrate 41 remains. Then, three obtained substrates 41 are stacked with double-sided tape, and then punched with a φ6.39 mm punch to prepare a sample for background correction (hereinafter simply referred to as a "correction sample"). Then, the MH loop of the correction sample (substrate 41) corresponding to the vertical direction of the substrate 41 (vertical direction of the magnetic tape MT) is measured using a VSM.

[0078] The MH loop of the measurement sample (entire magnetic tape MT) and the MH loop of the correction sample (substrate 41) are measured using a high-sensitivity vibration sample magnetometer "VSM-P7-15 type" manufactured by Toei Industry Co., Ltd. The measurement conditions are as follows: measurement mode: full loop, maximum magnetic field: 15 kOe, magnetic field step: 40 bits, time constant of locking amp: 0.3 sec, waiting time: 1 sec, number of MH averages: 20.

[0079] After obtaining the MH loop of the measurement sample (whole magnetic tape MT) and the MH loop of the correction sample (substrate 41), background correction is performed by subtracting the MH loop of the correction sample (substrate 41) from the MH loop of the measurement sample (whole magnetic tape MT), and the MH loop after background correction is obtained. The measurement and analysis program attached to the "VSM-P7-15" is used for the calculation of this background correction.

[0080] The saturation magnetization Ms (emu) and residual magnetization Mr (emu) of the MH loop after background correction are substituted into the following formula to calculate the squareness ratio S1 (%). Note that all of the above MH loop measurements are performed at 25°C. Also, no "demagnetizing field correction" is performed when measuring the MH loop in the perpendicular direction to the magnetic tape MT. Note that the measurement and analysis program included with the "VSM-P7-15" is used for this calculation. Squareness ratio S1(%)=(Mr / Ms)×100

[0081] The squareness ratio S2 of the magnetic layer 43 in the longitudinal direction (running direction) of the magnetic tape MT is preferably 35% or less, more preferably 30% or less, even more preferably 25% or less, particularly preferably 20% or less, and most preferably 15% or less. When the squareness ratio S2 is 35% or less, the magnetic powder has a sufficiently high vertical orientation, so that even more excellent electromagnetic conversion characteristics can be obtained.

[0082] The squareness ratio S2 in the longitudinal direction is determined in the same manner as the squareness ratio S1, except that the MH loop is measured in the longitudinal direction (running direction) of the magnetic tape MT and the substrate 41.

[0083] (Coercive force ratio) The ratio Hc2 / Hc1 of the coercive force Hc1 of the magnetic layer 43 in the perpendicular direction to the coercive force Hc2 of the magnetic layer 43 in the longitudinal direction satisfies the relationship Hc2 / Hc1≦0.8, preferably Hc2 / Hc1≦0.75, more preferably Hc2 / Hc1≦0.7, even more preferably Hc2 / Hc1≦0.65, and particularly preferably Hc2 / Hc1≦0.6. When the coercive forces Hc1 and Hc2 satisfy the relationship Hc2 / Hc1≦0.8, the degree of perpendicular orientation of the magnetic powder can be increased. Therefore, the magnetization transition width can be reduced and a high output signal can be obtained during signal reproduction, so that even better electromagnetic conversion characteristics can be obtained. As mentioned above, when Hc2 is small, the magnetization reacts sensitively to the magnetic field in the perpendicular direction from the recording head, so that a good recording pattern can be formed.

[0084] When the ratio Hc2 / Hc1 is Hc2 / Hc1≦0.8, the average thickness t m It is particularly effective that the average thickness t of the magnetic layer 43 is 90 nm or less. m If the thickness exceeds 90 nm, when a ring-type head is used as a recording head, the lower region of the magnetic layer 43 (the region on the underlayer 42 side) may be magnetized in the longitudinal direction, and the magnetic layer 43 may not be uniformly magnetized in the thickness direction. Therefore, even if the ratio Hc2 / Hc1 is Hc2 / Hc1≦0.8 (i.e., even if the degree of perpendicular orientation of the magnetic powder is increased), there is a risk that further excellent electromagnetic conversion characteristics may not be obtained.

[0085] The lower limit of Hc2 / Hc1 is not particularly limited, but is, for example, 0.5≦Hc2 / Hc1. Note that Hc2 / Hc1 represents the degree of vertical orientation of the magnetic powder, and the smaller Hc2 / Hc1 is, the higher the degree of vertical orientation of the magnetic powder is.

[0086] The method for calculating the coercive force Hc2 of the magnetic layer 43 in the longitudinal direction is as described above. The coercive force Hc1 of the magnetic layer 43 in the perpendicular direction is determined in the same manner as the coercive force Hc2 of the magnetic layer 43 in the longitudinal direction, except that the MH loop is measured in the perpendicular direction (thickness direction) of the magnetic tape MT and the substrate 41.

[0087] (Young's modulus in the longitudinal direction of magnetic tape) The Young's modulus in the longitudinal direction of the magnetic tape MT is preferably 8.0 GPa or less, more preferably 7.9 GPa or less, even more preferably 7.5 GPa or less, and particularly preferably 7.1 GPa or less. When the Young's modulus in the longitudinal direction of the magnetic tape MT is 8.0 GPa or less, the magnetic tape MT becomes more elastic due to external forces, so that the width of the magnetic tape MT can be more easily adjusted by adjusting the tension. Therefore, off-track can be more appropriately suppressed, and data recorded on the magnetic tape MT can be more accurately reproduced.

[0088] The Young's modulus in the longitudinal direction of the magnetic tape MT is a value that indicates the difficulty of the magnetic tape MT to expand and contract in the longitudinal direction due to external forces; the larger this value, the more difficult it is for the magnetic tape MT to expand and contract in the longitudinal direction due to external forces, and the smaller this value, the more easily the magnetic tape MT can expand and contract in the longitudinal direction due to external forces.

[0089] The Young's modulus in the longitudinal direction of the magnetic tape MT is a value related to the longitudinal direction of the magnetic tape MT, but it also correlates with the difficulty of the magnetic tape MT expanding and contracting in the width direction. In other words, the larger this value, the more difficult it is for the magnetic tape MT to expand and contract in the width direction due to an external force, and the smaller this value, the more easily the magnetic tape MT expands and contracts in the width direction due to an external force. Therefore, from the viewpoint of tension adjustment, it is advantageous for the magnetic tape MT to have a smaller Young's modulus in the longitudinal direction.

[0090] A tensile tester (AG-100D, manufactured by Shimadzu Corporation) is used to measure Young's modulus. If you wish to measure Young's modulus in the longitudinal direction of the tape, cut the tape to a length of 180 mm to prepare a measurement sample. Attach a jig capable of fixing the width of the tape (1 / 2 inch) to the tensile tester, and fix the top and bottom of the tape width. The distance (length of tape between chucks) is set to 100 mm. After chucking the tape sample, gradually apply stress in the direction in which the sample is pulled. The pulling speed is 0.1 mm / min. From the change in stress and the amount of elongation at this time, Young's modulus is calculated using the following formula. E(N / m 2 )=((ΔN / S) / (Δx / L))×10 6 ΔN: Change in stress (N) S: Cross-sectional area of ​​the test piece (mm 2 ) Δx: Elongation (mm) L: Distance between gripping jigs (mm) The stress range is set to 0.5N to 1.0N, and the change in stress (ΔN) and the amount of elongation (Δx) at this point are used in the calculation.

[0091] (Young's modulus in the longitudinal direction of the substrate) The Young's modulus in the longitudinal direction of the substrate 41 is preferably 7.5 GPa or less, more preferably 7.4 GPa or less, even more preferably 7.0 GPa or less, and particularly preferably 6.6 GPa or less. When the Young's modulus in the longitudinal direction of the substrate 41 is 7.5 GPa or less, the elasticity of the magnetic tape MT due to an external force is further increased, so that the width of the magnetic tape MT can be further easily adjusted by adjusting the tension. Therefore, off-track can be further appropriately suppressed, and data recorded on the magnetic tape MT can be reproduced more accurately.

[0092] The Young's modulus in the longitudinal direction of the substrate 41 is obtained as follows. First, the underlayer 42, the magnetic layer 43, and the back layer 44 are removed from the magnetic tape MT to obtain the substrate 41. Using this substrate 41, the Young's modulus in the longitudinal direction of the substrate 41 is obtained in the same manner as in the Young's modulus in the longitudinal direction of the magnetic tape MT.

[0093] The thickness of the substrate 41 accounts for more than half of the total thickness of the magnetic tape MT. Therefore, the Young's modulus in the longitudinal direction of the substrate 41 correlates with the difficulty of the magnetic tape MT to expand and contract due to an external force, and the larger this value is, the less likely the magnetic tape MT is to expand and contract in the width direction due to an external force, and the smaller this value is, the more likely the magnetic tape MT is to expand and contract in the width direction due to an external force.

[0094] The Young's modulus in the longitudinal direction of the substrate 41 is a value related to the longitudinal direction of the magnetic tape MT, but it also correlates with the difficulty of the magnetic tape MT to expand and contract in the width direction. In other words, the larger this value is, the more difficult it is for the magnetic tape MT to expand and contract in the width direction due to an external force, and the smaller this value is, the more easily the magnetic tape MT expands and contracts in the width direction due to an external force. Therefore, from the viewpoint of tension adjustment, it is advantageous for the substrate 41 to have a smaller Young's modulus in the longitudinal direction.

[0095] [3 Magnetic tape format] 3 is a schematic diagram showing an example of the layout of data bands and servo bands. The magnetic tape MT (specifically, the magnetic layer 43) has a plurality of servo bands SB and a plurality of data bands DB in advance. The plurality of servo bands SB are provided at equal intervals in the width direction of the magnetic tape MT. A data band DB is provided between adjacent servo bands SB. The servo band SB is for guiding a magnetic head 51 (specifically, servo read heads 51A, 51B) of a recording and reproducing device (drive) when recording or reproducing data. A servo pattern (servo signal) for tracking control of the magnetic head 51 is written in advance in the servo band SB. User data is recorded in the data band DB.

[0096] The total area S of the servo bands SB relative to the surface area S of the magnetic layer 43 SB The ratio of R S (=(S SB From the viewpoint of ensuring a high recording capacity, the upper limit of the ratio of the total area S of the plurality of servo bands SB to the area S of the surface of the magnetic layer 43 is preferably 4.0% or less, more preferably 3.0% or less, and even more preferably 2.0% or less. SB The ratio of R S The lower limit is preferably 0.8% or more from the viewpoint of ensuring 5 or more servo bands SB.

[0097] The total area S of the servo bands SB relative to the total surface area S of the magnetic layer 43 SB The ratio RS of the servo band width W is calculated as follows: The magnetic tape MT is developed using a ferricolloid developer (Sigma Marker Q, manufactured by Sigma High Chemical Co., Ltd.), and the developed magnetic tape MT is then observed under an optical microscope. SB and the number of servo bands SB. Next, calculate the ratio R from the following formula: S Request. Ratio R S [%]=(((Servo bandwidth W SB ) x (number of servo bands SB)) / (width of magnetic tape MT)) x 100

[0098] The number of servo bands SB is preferably 5 or more, more preferably 5+4n (where n is a positive integer) or more. If the number of servo bands SB is 5 or more, the effect of dimensional changes in the width direction of the magnetic tape MT on the servo signal can be suppressed, and stable recording and reproducing characteristics with less off-track can be ensured. The upper limit of the number of servo bands SB is not particularly limited, but is, for example, 33 or less.

[0099] The number of servo bands SB is calculated in the same manner as the ratio RS described above.

[0100] Servo Bandwidth W SB From the viewpoint of ensuring a high recording capacity, the upper limit of the servo band width W is preferably 99 μm or less, more preferably 60 μm or less, and even more preferably 30 μm or less. SB The lower limit is preferably 10 μm or more.

[0101] Servo Bandwidth W SB The width is calculated in the same manner as the ratio RS described above.

[0102] 4 is an enlarged view showing an example of the configuration of a data band. The magnetic layer 43 is configured so that a plurality of data tracks Tk can be formed on the data band DB. From the viewpoint of improving the track recording density and ensuring a high recording capacity, the upper limit of the data track width W is preferably 2000 nm or less, more preferably 1500 nm or less, and even more preferably 1000 nm. Taking into account the magnetic particle size, the lower limit of the data track width W is preferably 20 nm or more.

[0103] From the viewpoint of ensuring a high recording capacity, the magnetic layer 43 is configured to be able to record data such that the minimum distance L between magnetization reversals is preferably 48 nm or less, more preferably 44 nm or less, and even more preferably 40 nm or less. Taking into consideration the magnetic grain size, the lower limit of the minimum distance L between magnetization reversals is preferably 20 nm or more.

[0104] The magnetic layer 43 is configured to be capable of recording data such that the minimum value L of the magnetic reversal distance and the data track width W are preferably W / L≦35, more preferably W / L≦30, and even more preferably W / L≦25. If the minimum value L of the magnetic reversal distance is a constant value and the minimum value L of the magnetic reversal distance and the track width W are W / L>35 (i.e., if the track width W is large), the track recording density does not increase, and there is a risk that the recording capacity cannot be sufficiently secured. Also, if the track width W is a constant value and the minimum value L of the magnetic reversal distance and the track width W are W / L>35 (i.e., if the minimum value L of the magnetic reversal distance is small), the bit length becomes small and the linear recording density increases, but there is a risk that the electromagnetic conversion characteristics may be significantly deteriorated due to the influence of spacing loss. Therefore, in order to suppress the deterioration of the electromagnetic conversion characteristics while securing the recording capacity, it is preferable that W / L is in the range of W / L≦35 as described above. The lower limit of W / L is not particularly limited, but is, for example, 1≦W / L.

[0105] The data track width W is obtained as follows. A magnetic tape MT on which data is recorded over the entire surface is prepared, and the data recording pattern in the data band DB portion of the magnetic layer 43 is observed using a magnetic force microscope (MFM) to obtain an MFM image. The Dimension3100 manufactured by Digital Instruments and its analysis software are used as the MFM. The measurement area of ​​the MFM image is 10 μm×10 μm, and the 10 μm×10 μm measurement area is divided into 512×512 (=262,144) measurement points. Measurements are performed by the MFM on three 10 μm×10 μm measurement areas at different locations, that is, three MFM images are obtained. From the three obtained MFM images, the track width is measured at 10 points using the analysis software attached to the Dimension3100, and the average value (simple average) is calculated. The average value is the data track width W. The measurement conditions for the above MFM were: sweep speed: 1 Hz, tip used: MFMR-20, lift height: 20 nm, and correction: flatten order 3.

[0106] The minimum value L of the distance between magnetization reversals is obtained as follows. A magnetic tape MT on which data is recorded over the entire surface is prepared, and the data recording pattern in the data band DB portion of the magnetic layer 43 is observed using a magnetic force microscope (MFM) to obtain an MFM image. The Dimension3100 manufactured by Digital Instruments and its analysis software are used as the MFM. The measurement area of ​​the MFM image is 2 μm×2 μm, and the 2 μm×2 μm measurement area is divided into 512×512 (=262,144) measurement points. Measurements are performed by the MFM on three 2 μm×2 μm measurement areas in different locations, that is, three MFM images are obtained. Fifty bit distances are measured from a two-dimensional concave-convex chart of the recording pattern of the obtained MFM image. The bit distances are measured using analysis software attached to the Dimension3100. The value that is approximately the greatest common divisor of the 50 measured bit distances is set as the minimum value L of the distance between magnetization reversals. The measurement conditions were: sweep speed: 1 Hz, tip used: MFMR-20, lift height: 20 nm, and correction: Flatten order 3.

[0107] The servo pattern is a magnetized area, and is formed by magnetizing a specific area of ​​the magnetic layer 43 in a specific direction by a servo writer during the manufacturing of the magnetic tape. The area of ​​the servo band SB where the servo pattern is not formed (hereinafter referred to as the "non-pattern area") may be a magnetized area where the magnetic layer 43 is magnetized, or may be a non-magnetized area where the magnetic layer 43 is not magnetized. When the non-pattern area is a magnetized area, the servo pattern forming area and the non-pattern area may be magnetized in different directions (for example, opposite directions). The servo pattern (servo signal) has LPOS (Longitudinal Position Of Signal) information embedded therein. The LPOS information indicates the position in the longitudinal direction of the magnetic tape MT, and is longitudinal position information for uniquely identifying each servo band SB.

[0108] 5 is an enlarged view showing an example of the configuration of the servo band SB. In the LTO standard, a servo pattern consisting of a plurality of servo stripes (linear magnetized regions) 113 inclined with respect to the width direction of the magnetic tape MT is formed on the servo band SB.

[0109] The servo band SB includes a plurality of servo frames 110. Each servo frame 110 is made up of 18 servo stripes 113. More specifically, each servo frame 110 is made up of a servo subframe 1 (111) and a servo subframe 2 (112).

[0110] The servo subframe 1 (111) is composed of an A burst 111A and a B burst 111B. The B burst 111B is disposed adjacent to the A burst 111A. The A burst 111A has five servo stripes 113 formed at regular intervals and inclined at a predetermined angle φ with respect to the width direction of the magnetic tape MT. In FIG. 5, these five servo stripes 113 are indicated by symbols A1, A2, A3, A4, and A5 from the EOT (End Of Tape) to the BOT (Beginning Of Tape) of the magnetic tape MT. The B burst 111B, like the A burst 111A, has five servo stripes 113 formed at regular intervals and inclined at a predetermined angle φ with respect to the width direction of the magnetic tape MT. In FIG. 5, these five servo stripes 113 are indicated by symbols B1, B2, B3, B4, and B5 from the EOT to the BOT of the magnetic tape MT. The servo stripes 113 of the B burst 111B are inclined in the opposite direction to the servo stripes 113 of the A burst 111A. That is, the servo stripes 113 of the A burst 111A and the servo stripes 113 of the B burst 111B are arranged in a V-shape.

[0111] Servo subframe 2 (112) is composed of C burst 112C and D burst 112D. D burst 112D is disposed adjacent to C burst 112C. C burst 112C has four servo stripes 113 formed at a specified interval and inclined at a specified angle φ with respect to the tape width direction. In FIG. 5, these four servo stripes 113 are indicated by symbols C1, C2, C3, and C4 from the EOT to the BOT of the magnetic tape MT. D burst 112D, like C burst 112C, has four servo stripes 113 formed at a specified interval and inclined at a specified angle φ with respect to the tape width direction. In FIG. 5, these four servo stripes 113 are indicated by symbols D1, D2, D3, and D4 from the EOT to the BOT of the magnetic tape MT. The servo stripes 113 of the D burst 112D are inclined in the opposite direction to the servo stripes 113 of the C burst 112C. That is, the servo stripes 113 of the C burst 112C and the servo stripes 113 of the D burst 112D are arranged in a V-shape.

[0112] The predetermined angle φ of the servo stripes 113 in the A burst 111A, the B burst 111B, the C burst 112C, and the D burst 112D may be, for example, 5° to 25°, and in particular 11° to 25°.

[0113] Reading the servo band SB with the magnetic head 51 provides information to obtain the tape speed and the longitudinal position of the magnetic head. The tape speed is calculated from the times between four timing signals (A1-C1, A2-C2, A3-C3, A4-C4). The head position is calculated from the times between the aforementioned four timing signals and another four timing signals (A1-B1, A2-B2, A3-B3, A4-B4).

[0114] 5, the servo patterns (i.e., the plurality of servo stripes 113) are preferably arranged linearly in the longitudinal direction of the magnetic tape MT. That is, the servo bands SB preferably have a linear shape in the longitudinal direction.

[0115] Fig. 6 is a schematic diagram showing an example of the format of a magnetic tape MT. The magnetic tape MT is divided into seven regions in the longitudinal direction by eight logical points LP0 to LP7. LP0 to LP7 are set in this order from one end of the magnetic tape MT at the end of the winding to the other end at the beginning of the winding. The magnetic tape MT is also divided into five or more servo bands and four or more data bands in the width direction. Note that Fig. 6 shows an example in which the magnetic tape MT is divided into five servo bands and four data bands in the width direction.

[0116] The seven areas are comprised of an unused area R1 (area between LP0 and LP1), a forward servo recognition area (area between LP1 and LP2) R2, a calibration area (area between LP2 and LP3) R3, a user data area (area between LP3 and LP4) R4, an unused data area (area between LP4 and LP5) R5, a reverse servo recognition area (area between LP5 and LP6) R6, and an unused area (area between LP6 and LP7) R7. In the following description, the servo recognition area R2, the calibration area R3, the user data area R4, the unused data area R5, and the reverse servo recognition area R6 may be collectively referred to as the used areas.

[0117] In this specification, the "forward direction" refers to the running direction of the magnetic tape MT when it is fed out of the cartridge 10 and wound up by a reel of a servo writer or the like. The "reverse direction" refers to the running direction of the magnetic tape MT when it is fed out of a reel of a servo writer or the like and wound up by the cartridge 10.

[0118] In the used area, a servo pattern that satisfies the standard is formed. The servo pattern that satisfies the standard is a servo pattern that is formed by dividing an A burst 111A and a C burst 112C by a distance D. AC and the distance D between C burst 112C and A burst 111A CAmeets the standard. In this case, as shown in Fig. 7A, the leading ends of B burst 111B and C burst 112C are separated from each other, and the leading ends of D burst 112D and A burst 111A are separated from each other. This forms a V-shaped servo pattern. The servo pattern shown in Fig. 5 is an example of a servo pattern formed in a used area that meets the standard.

[0119] In both unused area R1 and unused area R7, servo patterns that do not meet the standards are formed. The servo patterns that do not meet the standards may be formed in a part of unused area R1 or in the entirety of unused area R1. Similarly, the servo patterns that do not meet the standards may be formed in a part of unused area R7 or in the entirety of unused area R7. As described above, unused area R1 is provided at the end of magnetic tape MT on the winding end side, and unused area R7 is provided at the end of magnetic tape MT on the winding start side.

[0120] A servo pattern that does not meet the standard is, for example, A burst 111A and C burst 112C at a distance D. AC and the distance D between C burst 112C and A burst 111A CA is narrower than the standard or wider than the standard.

[0121] When the magnetic tape MT runs in the forward direction, the unused area R1 is an area where the magnetic tape MT runs at an accelerated speed. Therefore, when servo signals are written by the same control as in the used area, the distance D between the A burst 111A and the C burst 112C becomes AC and the distance D between C burst 112C and A burst 111A CA is narrower than the standard.

[0122] When the magnetic tape MT runs in the forward direction, the unused area R7 is an area where the magnetic tape MT runs at a reduced speed. Therefore, when servo signals are written by the same control as in the used area, the distance D between the A burst 111A and the C burst 112C becomes AC and the distance D between C burst 112C and A burst 111A CAis narrower than the standard.

[0123] Distance D AC and distance D CA 7B, for example, the ends of B burst 111B and C burst 112C overlap, forming a V-shaped servo pattern with B burst 111B and C burst 112C. Also, the ends of D burst 112D and A burst 111A overlap, forming a V-shaped servo pattern with D burst 112D and A burst 111A.

[0124] Distance D AC and distance D CA 7C, for example, when B burst 111B and C burst 112C cross each other, they form an X-shaped servo pattern. Also, when D burst 112D and A burst 111A cross each other, they form an X-shaped servo pattern.

[0125] It is possible to check whether or not servo patterns that do not meet the standards are formed in the unused areas R1 and R7 as follows. First, the cartridge 10 is disassembled, and the magnetic tape MT is taken out. Next, the servo patterns (i.e., servo bands SB) formed in the magnetic layer 43 of the unused areas R1 and R7 of the taken-out magnetic tape MT are observed using a magnetic force microscope (MFM) to obtain an MFM image. As the MFM, Dimension3100 manufactured by Digital Instruments and its analysis software are used. Next, it is checked whether or not the servo patterns in the obtained MFM image meet the standards. In addition, after applying a ferricolloid developer (Sigma Marker Q manufactured by Sigma High Chemical Co., Ltd.), it is also possible to check with a microscope at about 100 to 1000 times magnification.

[0126] In conventional cartridges, servo signals that meet the standards are written in the unused areas at the beginning and end of the cartridge. This is because, in the manufacturing process of conventional cartridges, a magnetic tape on which a servo pattern that meets the standards is written from one end to the other in the longitudinal direction is assembled into the cartridge, and no processing is performed to rewrite the servo signals after assembly.

[0127] [4. Configuration of servo writer for cartridges] 8 is a schematic diagram showing an example of the configuration of a cartridge servo writer 210. The servo writer 210 erases the servo signal written in the above-mentioned cartridge 10 and rewrites the servo signal. By rewriting the servo signal, a servo pattern (second servo pattern) that does not meet the standard is formed in the above-mentioned unused area R1 and unused area R7.

[0128] The servo writer 210 includes a cartridge storage section 211, a reel 212, guide rollers 213A, 213B, 213C, 213D, a degaussing magnet 214, a servo signal writing head 215, a verify head 216, a control device 217, a pulse generating circuit 218, a spindle driving circuit 219A, a reel driving circuit 219B, and an operation section (not shown).

[0129] A running section is constituted by the cartridge housing section 211, the reel 212, and the guide rollers 213A, 213B, 213C, and 213D. When writing a servo signal, this running section feeds out the tape-like magnetic tape MT from the cartridge 10 and winds up the fed magnetic tape MT by the reel 212, thereby running the magnetic tape MT in the forward direction. After writing the servo signal, this running section feeds out the tape-like magnetic tape MT from the reel 212 and winds up the fed magnetic tape MT by the cartridge 10, thereby running the magnetic tape MT in the reverse direction. In the following description, the term "running path" refers to the path along which the magnetic tape MT runs in the servo writer 210. Additionally, the terms "upstream side" and "downstream side" refer to the upstream side and downstream side of the running path when the magnetic tape MT runs in the forward direction.

[0130] (Cartridge storage section) The cartridge accommodating section 211 is configured to be able to accommodate the cartridge 10. The cartridge accommodating section 211 includes a loading mechanism (not shown) and is configured to be able to load the cartridge 10. The cartridge accommodating section 211 feeds out the magnetic tape MT on which the servo signal is to be rewritten. The cartridge accommodating section 211 includes a spindle 241A. The spindle 241A is configured to be able to mount the cartridge 10. The magnetic tape MT is fed out by the rotation of the spindle 241A.

[0131] (reel) The reel 212 winds up the magnetic tape MT on which the servo signals have been rewritten. The reel 212 is configured so as to be able to fix the leading end (leader pin 20) of the magnetic tape MT pulled out from the cartridge 10.

[0132] (Guide roller) The guide rollers 213A and 213B are provided on a running path between the cartridge accommodating portion 211 and the servo signal write head 215. The guide rollers 243A and 243B guide the magnetic tape MT running from the cartridge accommodating portion 211 toward the servo signal write head 215. The guide rollers 243C and 243D are provided on a running path between the servo signal write head 215 and the reel 212. The guide rollers 243C and 243D guide the magnetic tape MT running from the servo signal write head 215 toward the reel 212.

[0133] (Degaussing magnet) The degaussing magnet 214 is provided upstream of the travel path from the servo signal write head 215. The degaussing magnet 214 erases a servo pattern (first servo pattern) formed on the magnetic tape MT traveling in the forward direction. The degaussing magnet 214 is rotatable as shown in JP2018-005970A, and may be a magnet that can change the magnetic field applied to the magnetic layer 43 in response to the rotation.

[0134] (Servo signal writing head) The servo signal write head 215 is a magnetic head for rewriting a servo signal on the magnetic tape running in the forward direction from which the servo pattern has been erased, to form a servo pattern (second servo pattern). As the servo signal write head 215, for example, the one described in Patent Document 1 can be used.

[0135] The servo signal write head 215 has a sliding surface that slides against the magnetic tape MT. The servo signal write head 215 has five or more recording elements and at least one bottomed cavity (recess) on the sliding surface. The recording elements have magnetic gaps. The magnetic gaps are arranged in a row on the sliding surface at a predetermined interval so as to correspond to the positions of each servo band in the width direction of the magnetic tape MT. The five or more recording elements each write a servo signal on the magnetic tape MT to form five or more servo bands SB.

[0136] The bottomed cavity is closed and is formed only within the width of the running area of ​​the magnetic tape MT. By providing a bottomed cavity having such a configuration on the sliding surface, the expansion of the air between the sliding surface and the magnetic tape MT is promoted when the magnetic tape MT runs, and the air pressure is reduced, i.e., negative pressure is generated, thereby reducing spacing and improving the running stability of the magnetic tape MT.

[0137] (Verify Head) The verify head 216 is provided downstream of the travel path from the servo signal write head 215. The verify head 216 is a magnetic head that comes into sliding contact with the magnetic tape MT, on which servo signals are written, traveling in the forward direction, and reads the servo signals written on the servo bands SB. The verify head 216 may have a configuration similar to that of the servo signal write head 215, except that it includes a plurality of reproducing elements instead of a plurality of recording elements.

[0138] (Control device) The control device 217 is a device that controls the operation of each part of the servo writer 210, and includes a CPU (Central Processing Unit) and various storage devices. The control device 217 controls the servo signal write head 215 to write servo signals during the accelerating and decelerating running periods of the magnetic tape MT, and forms a servo pattern on the magnetic tape MT that does not satisfy the standard. The control device 217 controls the servo signal write head 215 to write servo signals during the constant speed running period of the magnetic tape MT, and forms a servo pattern on the magnetic tape MT that satisfies the standard.

[0139] The control device 217 generates a pulse control signal for controlling the current value, pulse width and generation timing of the recording pulse current so that the servo signal written onto the magnetic tape MT by the servo signal write head 215 becomes a specified servo pattern, and supplies the signal to a pulse generating circuit 218.

[0140] The control device 217 checks whether the servo signal is properly recorded on the magnetic tape MT based on the servo signal supplied from the verify head 216. Specifically, the control device 217 stores information on the servo signal that satisfies the standard (hereinafter referred to as "standard information") in a storage device, compares this standard information with the servo signal supplied from the verify head 216, and checks whether the servo signal is properly recorded on the magnetic tape MT.

[0141] The control device 217 erases the servo signals written on the magnetic tape MT by moving the degaussing magnet 214 and bringing it into contact with the magnetic tape MT.

[0142] The control device 217 controls the spindle drive circuit 219A to rotate the spindle 211A. The control device 217 controls the reel drive circuit 219B to rotate the reel 212. Specifically, the control device 217 generates motor current signals for controlling the motor currents of the spindle drive circuit 219A and the reel drive circuit 219B to control the running speed of the magnetic tape MT when writing servo signals, and supplies the signals to the spindle drive circuit 219A and the reel drive circuit 219B.

[0143] (Operation unit) The operation unit is for operating the servo writer 210 and executing servo writing operations, etc. The operation unit is connected to the control device 217.

[0144] (Pulse generation circuit) The pulse generating circuit 218 generates a recording pulse current based on a pulse control signal supplied from the control device 217 , and supplies it to the servo signal write head 215 .

[0145] (Spindle drive circuit) The spindle drive circuit 219A rotates the spindle 211A based on the control of the control device 217. The spindle drive circuit 219A is a device for driving the rotation of the spindle 211A, and includes a motor integrated with the spindle 211A, a motor drive circuit for supplying a current to the motor, etc. In the spindle drive circuit 219A, a motor current is generated by the motor drive circuit based on a motor current signal supplied from the control device 217, and the motor current is supplied to the motor to drive the rotation of the spindle 211A.

[0146] (Reel drive circuit) The reel drive circuit 219B rotates the reel 212 under the control of the control device 217. The reel drive circuit 219B is a device for driving the reel 212 to rotate, and includes a motor, a motor drive circuit for supplying current to the motor, and gears for connecting the motor shaft to the reel 212. In the reel drive circuit 219B, a motor current is generated by the motor drive circuit based on a motor current signal supplied from the control device 217, and the motor current is supplied to the motor, thereby transmitting the rotational drive force of the motor to the reel 212 via the gears, thereby driving the reel 212 to rotate.

[0147] [5. Operation of the cartridge servo writer] An example of the operation of the servo writer 210 having the above configuration will now be described.

[0148] First, an operator loads the cartridge 10 into the cartridge storage section 211. After loading, the operator pulls out the magnetic tape MT from the cartridge 10 and fixes its tip (leader pin 20) to the reel 212. Note that the cartridge 10 stored in the cartridge storage section 211 may be one in which the magnetic tape MT has been confirmed to be defective in quality.

[0149] Next, when the operator operates an operation unit (not shown), the control device 217 brings the degaussing magnet 214 into contact with the magnetic tape MT. The control device 217 controls the rotation of the spindle 211A and the reel 212 via the spindle drive circuit 219A and the reel drive circuit 219B, feeds out the magnetic tape from the cartridge 10, and winds up the fed magnetic tape MT by the reel 212. This causes the magnetic tape MT to accelerate and run in the forward direction. The degaussing magnet 214 erases the servo pattern (i.e., the servo signal written on the magnetic tape MT) formed on the magnetic tape MT running in the forward direction.

[0150] Next, during the accelerating running period of the magnetic tape MT, the control device 217 erases the servo patterns (i.e., the servo signals written on the magnetic tape MT) formed in the unused area R1 of the magnetic tape MT running in the forward direction by the degaussing magnet 214. Next, during the accelerating running period of the magnetic tape MT, the control device 217 controls the servo signal write head 215 to write servo signals, and forms servo patterns that do not meet the standard in the unused area R1 of the magnetic tape running in the forward direction.

[0151] Next, when the running speed of the magnetic tape MT reaches a specified running speed, the control device 217 controls the rotation of the spindle 211A and the reel 212 via the spindle drive circuit 219A and the reel drive circuit 219B, causing the magnetic tape MT to run in the forward direction at a specified constant speed.

[0152] Next, during the constant speed running period of the magnetic tape MT, the control device 217 erases the servo pattern (i.e., the servo signal written on the magnetic tape MT) formed in the used area of ​​the magnetic tape MT running in the forward direction by the degaussing magnet 214. Next, during the constant speed running period of the magnetic tape MT, the control device 217 rewrites the servo signal in the used area of ​​the magnetic tape MT running in the forward direction by the servo signal write head 215 to form a servo pattern that satisfies the standard. The servo signal includes LPOS information, and when the servo signal is rewritten, the LPOS information is also written in the servo band SB.

[0153] Next, during a period in which the magnetic tape MT is traveling at a constant speed, the control device 217 uses the verify head 216 to read servo signals from the magnetic tape MT traveling in the forward direction, and based on the read servo signals, verifies whether the servo signals have been written properly.

[0154] Next, when a specified length of magnetic tape MT has been wound onto cartridge 10, control device 217 controls the rotation of spindle 211A and reel 212 via spindle drive circuit 219A and reel drive circuit 219B to decelerate the magnetic tape MT in the forward direction.

[0155] Next, during the deceleration period of the magnetic tape MT, the control device 217 erases the servo patterns (i.e., the servo signals written on the magnetic tape MT) formed in the unused area R7 of the magnetic tape MT running in the forward direction by the degaussing magnet 214. Next, during the deceleration period of the magnetic tape MT, the control device 217 controls the servo signal write head 215 to write servo signals, and forms servo patterns that do not meet the standards in the unused area R7 of the magnetic tape running in the forward direction.

[0156] Next, when the magnetic tape MT stored in the cartridge 10 has been entirely fed out, the control device 217 stops the rotational driving of the spindle 211A and the reel 212 via the spindle drive circuit 219A and the reel drive circuit 219B. This stops the running of the magnetic tape MT. Next, the control device 217 stops the degaussing function by moving the degaussing magnet 214 away from the magnetic tape MT. Next, the control device 217 controls the rotation of the spindle 211A and the reel 212 via the spindle drive circuit 219A and the reel drive circuit 219B, feeds out the magnetic tape MT from the reel 212, and takes up the fed magnetic tape MT by the cartridge 10.

[0157] Next, when the magnetic tape MT that had been wound around the reel 212 has been entirely unwound and wound around the cartridge 10, the control device 217 stops the rotational driving of the spindle 211A and the reel 212 via the spindle drive circuit 219A and the reel drive circuit 219B. Thereafter, the control device 217 unloads the cartridge 10 from the cartridge storage section 211 in response to the operation of the operation section.

[0158] [6 Configuration of servo signal recording system] 9 is a schematic diagram showing an example of the configuration of a servo signal recording system. The servo signal recording system includes a pancake servo writer 220, a winder 230, a quality inspection device 240, and a cartridge servo writer 210. Here, "pancake" refers to magnetic tape MT wound in a roll (a wound body of magnetic tape MT) before being cut to a specified length.

[0159] The servo writer 210 for cartridges has been described above, so the servo writer 210 for pancakes, the winder 230, and the quality inspection device 240 will be described below.

[0160] (Servo writer for pancakes) 10 is a schematic diagram showing an example of the configuration of a pancake servo writer 220. The servo writer 220 is configured to be able to write servo signals onto a magnetic tape MT serving as a pancake.

[0161] The servo writer 220 includes reels 221 and 212, guide rollers 213A, 213B, 213C, and 213D, a degaussing magnet 214, a servo signal write head 215, a verify head 216, a control device 222, a pulse generating circuit 218, reel driving circuits 219C and 219B, and an operation unit (not shown). Note that the same reference numerals are used to designate the same parts of the servo writer 220 as those of the servo writer 210, and descriptions thereof will be omitted.

[0162] A pancake magnetic tape MT can be attached to the reel 221. The reel 221 delivers the magnetic tape MT onto which servo signals are written.

[0163] The control device 222 controls the rotation of the reels 212 via the reel drive circuit 219C and the reel drive circuit 219B, and runs the magnetic tape MT in the forward direction at a prescribed constant speed. The control device 222 may control the servo signal write head 215 not to write a servo signal during the accelerating and decelerating running periods of the magnetic tape MT, or may control the servo signal write head 215 to write a servo signal. However, unlike the control device 217, the control device 222 does not have a function of running the magnetic tape MT in the reverse direction.

[0164] The operation unit is for operating the servo writer 220 and executing servo writing operations, etc. The operation unit is connected to the control device 222.

[0165] (winder) 11 is a schematic diagram showing an example of the configuration of the winder 230. The winder 230 incorporates the magnetic tape MT, on which servo signals are written, into the cartridge case 12. The winder 230 includes a reel 231, a guide roller 232, a cartridge storage section 211, a control device 233, a spindle drive circuit 219A, and an operation section (not shown). Note that the same parts of the winder 230 as those of the servo writer 210 are denoted by the same reference numerals and will not be described.

[0166] The reel 231 is configured so that a pancake magnetic tape MT on which a servo signal is written can be attached. The reel 231 feeds out the magnetic tape MT on which the servo signal is written. The guide roller 232 is provided on a running path between the reel 231 and the cartridge storage section 211. The guide roller 232 guides the magnetic tape MT running from the reel 231 toward the cartridge storage section 211. The control device 233 controls the spindle drive circuit 219A to rotate the spindle 211A. As a result, the magnetic tape MT is fed out from the reel 231, and the fed magnetic tape MT is taken up by the cartridge 10.

[0167] The operation unit is for operating the winder 230 and executing operations such as winding up the magnetic tape MT. The operation unit is connected to the control device 233.

[0168] (Quality Inspection Equipment) The quality inspection device 240 inspects the quality of the servo signal of the magnetic tape MT incorporated in the cartridge case 12. Poor quality of the servo signal includes, for example, a missing servo signal, poor servo tracking characteristics, and the like.

[0169] [7 Operation of servo signal recording system] An example of the operation of the servo signal recording system having the above configuration will now be described.

[0170] (Servo signal writing process) As described below, a servo signal is written on the magnetic tape MT cut to a specified width by using the servo writer 220. First, an operator loads the magnetic tape MT as a pancake onto the reel 221, and pulls out the outer circumferential end of the magnetic tape MT and fixes it to the reel 212. Next, when the operator operates an operation unit (not shown), the control device 222 controls the rotation of the reel 212 via the reel drive circuit 219B, feeds out the magnetic tape MT from the cartridge 10, and takes up the fed magnetic tape MT by the reel 212. This causes the magnetic tape MT to run in the forward direction.

[0171] Next, the control device 222 erases the magnetic tape MT running in the forward direction by the degaussing magnet 214, and then writes a servo signal on the magnetic tape MT running in the forward direction by the servo signal write head 215 to form a servo pattern. Next, the control device 222 reads the written servo signal from the magnetic tape MT running in the forward direction by the verify head 216, and checks whether the servo signal has been written properly based on the read servo signal.

[0172] Next, when the entire pancake magnetic tape MT has been fed out, the control device 222 stops the rotation of the reel 212 via the reel drive circuit 219B. This stops the transport of the magnetic tape MT. After that, the operator removes the pancake magnetic tape MT with the servo signals written thereon from the reel 212 and transports it to the winder 230.

[0173] (Installation process) The magnetic tape MT on which the servo signals are written is assembled into the cartridge 10 using the winder 230 as follows. First, an operator mounts the magnetic tape MT as a pancake on the reel 231, and loads the cartridge 10 into the cartridge housing section 211. Next, the leading end of the magnetic tape MT on the outer periphery mounted on the reel 231 is pulled out and fixed to the reel 13 (see FIG. 1) of the cartridge 10.

[0174] Next, when the operator operates an operating unit (not shown), the control device 233 controls the rotational drive of the spindle 211A via the spindle drive circuit 219A, unwinds the magnetic tape MT from the reel 231, and winds up the unwound magnetic tape MT by the cartridge 10.

[0175] Next, when a specified length of magnetic tape has been wound around the cartridge 10, the control device 233 stops the rotation of the spindle 211A via the spindle drive circuit 219A. This stops the transport of the magnetic tape MT. Thereafter, the control device 233 unloads the cartridge 10 from the cartridge storage unit 211 in response to the operation of the operation unit. The unloaded cartridge 10 is transported to the quality inspection device 240 by an operator.

[0176] If servo patterns that do not meet the standards are formed in portions within a predetermined range from both ends of the pancake magnetic tape MT in the longitudinal direction, these portions may be cut and removed from the magnetic tape MT in this assembly process. Alternatively, if servo patterns are not formed in portions within a predetermined range from both ends of the pancake magnetic tape MT in the longitudinal direction, these portions may be cut and removed from the magnetic tape MT in this assembly process.

[0177] (Quality inspection process) The quality of the servo signal of the magnetic tape MT incorporated in the cartridge 10 is inspected using the quality inspection device 240. If the inspection reveals no quality defects in the magnetic tape MT, the cartridge 10 is shipped. On the other hand, if the inspection reveals a quality defect in the magnetic tape MT, the cartridge 10 is transported to the servo writer 210. Then, the servo signal is rewritten on the magnetic tape MT in a "servo signal rewriting process" described below, and a servo pattern (i.e., servo band SB) is formed. After the servo signal has been rewritten, the quality of the servo signal of the magnetic tape MT incorporated in the cartridge 10 is inspected again using the quality inspection device 240.

[0178] If the quality inspection device 240 confirms that the quality of the servo signal is poor even after the "servo signal rewriting process" has been repeated a specified number of times (eg, three times), the cartridge 10 is discarded by an operator.

[0179] (Servo signal rewriting process) Using the servo writer 210, the servo signals are re-written onto the magnetic tape MT of the cartridge 10. Details of this process are as explained above in [5 Operation of the Servo Writer for Cartridge].

[0180] It is preferable that the quality inspection process is performed after a specified time has elapsed since the magnetic tape MT is incorporated into the cartridge 10. That is, it is preferable that the servo signal is rewritten after a specified time has elapsed since the magnetic tape MT is incorporated into the cartridge 10. As described above, the quality inspection, i.e., the servo signal is rewritten after the specified time has elapsed, so that the width dimension of the magnetic tape MT is stabilized and then the servo signal can be recorded on the magnetic tape MT. Therefore, the dimensional change of the interval between the servo bands SB is reduced. The lower limit of the specified time is preferably one day or more, more preferably three days or more, and even more preferably seven days or more. When the lower limit of the specified time is one day or more, the width dimension of the magnetic tape MT can be effectively stabilized. The upper limit of the specified time is, for example, 30 days or less or 15 days or less, preferably 7 days or less. When the upper limit of the specified time is 7 days or less, a decrease in productivity can be suppressed.

[0181] After the assembly process and before the quality inspection process, the cartridge 10 may be annealed. By performing the annealing process in this manner, the width dimension of the magnetic tape MT is stabilized, and then servo signals can be recorded on the magnetic tape MT. From the viewpoint of stabilizing the width dimension of the magnetic tape MT, it is preferable to perform the annealing process for the above-mentioned specified time. The temperature for the annealing process is preferably 23° C. or higher and 70° C. or lower.

[0182] [8 Effects] As described above, the servo writer 210 according to an embodiment of the present disclosure includes a running section that runs the magnetic tape MT by feeding the magnetic tape MT from the cartridge 10 and winding up the fed magnetic tape MT, a degaussing magnet 214 that erases the first servo pattern formed on the running magnetic tape MT, a servo signal writing head 215 that writes a servo signal on the running magnetic tape MT from which the first servo pattern has been erased, and forms a second servo pattern, and a control device 217 that controls the servo signal writing head 215 to write a servo signal during both the accelerating and decelerating running periods of the magnetic tape MT, and forms a second servo pattern that does not meet the standard on the magnetic tape MT. This makes it possible to rewrite the servo signal of the cartridge 10 whose servo signal has been confirmed to have a quality defect. Therefore, the number of cartridges 10 to be discarded can be reduced. Therefore, the productivity of the cartridges 10 can be improved.

[0183] In terms of servo signal performance, when the drive reads the servo signal, two servo signal reading elements (sensors) indicated by 51A and 51B (see FIG. 3) are used, but the tape width dimension, in other words the interval between the servo bands SB (servo band pitch), usually changes in the wider direction due to the effects of temperature, humidity, and winding pressure inside the cartridge 10. As a result, the position of the recording / reproducing elements may shift, making it difficult to read the data track Tk.

[0184] In contrast, as in the above-described embodiment, if the servo signals are recorded after the width dimension of the magnetic tape MT has stabilized after storage for a specified time (e.g., several days) after winding the cartridge 10, the dimensional change in the interval between the servo bands SB is reduced. Therefore, the positional deviation of the recording / reproducing element is reduced, the read accuracy of the data track Tk is improved, and a high track density can be achieved.

[0185] When the magnetic tape MT is run, an acceleration region is required at the end where the tape is wound, and a deceleration region is required at the end where the tape is wound. If a recording current pattern with a fixed interval is applied to the acceleration and deceleration regions, a servo pattern that does not meet the standards will be created. On the other hand, in order to form a servo pattern that meets the standards, it is necessary to vary the time interval of the recording pattern by synchronizing the feed position of the magnetic tape MT with the recording current pattern, which is technically very difficult. In the servo writer 210 according to the embodiment described above, the servo patterns that do not meet the standard are recorded in the unused area R1 and the unused area R7, so that the above-mentioned difficulties can be avoided. Also, a pulse generating circuit that has been conventionally used in a pancake servo writer or the like can be used as the pulse generating circuit 218.

[0186] [9 Variations] (Variation 1) In the above embodiment, a case has been described in which servo signals that do not meet the standard are written in the unused area R1 and the unused area R7, but the servo patterns may not be formed in the unused area R1 and the unused area R7. In this case, the servo patterns may not be formed in a part of the unused area R1, or may not be formed in the entirety of the unused area R1. Similarly, the servo patterns may not be formed in a part of the unused area R7, or may not be formed in the entirety of the unused area R7.

[0187] The unused areas R1 and R7 described above are formed as follows when the servo writer 210 rewrites the servo signals. The control device 217 controls the servo signal write head 215 so as not to write servo signals during the accelerating and decelerating periods when the magnetic tape MT is run in the forward direction.

[0188] As described above, by not forming servo patterns in unused areas R1 and R7, it is no longer necessary to fabricate a pulse generating circuit capable of varying the recording pulse time in synchronization with the tape feed position, which would be technically impossible, and it is possible to use the pulse generating circuit that has been conventionally used as pulse generating circuit 218.

[0189] (Variation 2) It is also possible that a servo signal that does not meet the standard is written in one of unused area R1 and unused area R7, whereas no servo signal is written in the other area.

[0190] The unused areas R1 and R7 described above are formed when the servo writer rewrites the servo signals as follows: The control device 217 controls the servo signal write head 215 to write servo signals during one of the acceleration and deceleration periods when the magnetic tape MT is run in the forward direction, thereby forming a servo pattern that does not satisfy the standard on the magnetic tape MT, while controlling the servo signal write head 215 not to write servo signals during the other period, thereby not forming a servo pattern on the magnetic tape MT.

[0191] (Variation 3) In the above embodiment, the case where the cartridge servo writer 210 is used to rewrite the servo signal has been described, but the cartridge servo writer 210 may also be used to write the initial servo signal. In this case, it is preferable that the initial writing of the servo signal is performed after a specified time has elapsed since the magnetic tape MT is incorporated into the cartridge 10. After the incorporation process and before the quality inspection process, it is preferable to perform an annealing process on the cartridge 10. From the viewpoint of stabilizing the width dimension of the magnetic tape MT, it is preferable to perform the annealing process for the specified time.

[0192] Although the embodiments and modifications of the present disclosure have been specifically described above, the present disclosure is not limited to the above-mentioned embodiments and modifications, and various modifications based on the technical ideas of the present disclosure are possible. For example, the configurations, methods, steps, shapes, materials, and numerical values, etc., given in the above-mentioned embodiments and modifications are merely examples, and configurations, methods, steps, shapes, materials, and numerical values, etc., different from these may be used as necessary. The configurations, methods, steps, shapes, materials, and numerical values, etc., of the above-mentioned embodiments and modifications can be combined with each other as long as they do not deviate from the gist of the present disclosure.

[0193] The chemical formulas of the compounds and the like exemplified in the above-mentioned embodiments and modifications are representative, and are not limited to the valences and the like described as long as they are the general names of the same compounds. In the numerical ranges described in stages in the above-mentioned embodiments and modifications, the upper limit or lower limit of a numerical range in a certain stage may be replaced with the upper limit or lower limit of a numerical range in another stage. The materials exemplified in the above-mentioned embodiments and modifications may be used alone or in combination of two or more types, unless otherwise specified.

[0194] The present disclosure may also employ the following configuration. (1) a running unit that runs the magnetic recording medium by feeding out the tape-like magnetic recording medium from the cartridge and winding up the magnetic recording medium that has been fed out; an erasing unit that erases a first servo pattern formed on the traveling magnetic recording medium; a head that writes a servo signal onto the traveling magnetic recording medium from which the first servo pattern has been erased, to form a second servo pattern; a control unit that controls the head to write the servo signal during at least one of an accelerating running period and a decelerating running period of the magnetic recording medium, and forms the second servo pattern that does not satisfy the standard on the magnetic recording medium; A servo writer comprising: (2) a running unit that runs the magnetic recording medium by feeding out the tape-like magnetic recording medium from the cartridge and winding up the magnetic recording medium that has been fed out; an erasing unit that erases a first servo pattern formed on the traveling magnetic recording medium; a head that writes a servo signal onto the traveling magnetic recording medium from which the first servo pattern has been erased, to form a second servo pattern; a control unit that controls the head so as not to write the servo signal during at least one of an accelerating period and a decelerating period of the magnetic recording medium; A servo writer comprising: (3) The servo writer according to (1) or (2), wherein the head has five or more recording elements. (4) five or more of the recording elements write the servo signals to the magnetic recording medium, thereby forming five or more servo bands; 4. The servo writer according to claim 3, wherein the servo signal includes information for uniquely identifying each of the servo bands. (5) a wound tape-like magnetic recording medium; a case for accommodating the magnetic recording medium; Equipped with the magnetic recording medium has an unused area; A cartridge in which a servo pattern that does not meet standards or no servo pattern is formed in the unused area. (6) The unused area is a first unused area provided at the end of the magnetic recording medium; a second unused area provided at the beginning of the winding of the magnetic recording medium; The cartridge according to (5) above, further comprising: (7) The cartridge according to (5) or (6), wherein the magnetic recording medium has five or more servo bands. (8) The cartridge described in (7) wherein the five or more servo bands include information for uniquely identifying each of the servo bands. (9) The magnetic recording medium includes a magnetic layer, The cartridge according to any one of (5) to (8), wherein the squareness ratio of the magnetic layer in the perpendicular direction is 65% or more. (10) The magnetic layer includes a magnetic powder. The cartridge according to (9), wherein the magnetic powder contains hexagonal ferrite, ε iron oxide, or Co-containing spinel ferrite. (11) incorporating a tape-like magnetic recording medium into a cartridge; forming a servo pattern on the magnetic recording medium after a specified time has elapsed since the magnetic recording medium was incorporated into the cartridge; A method for writing a servo pattern comprising: (12) forming the servo pattern on the magnetic recording medium, The method for writing a servo pattern according to (11) includes controlling a head to write a servo signal during at least one of an accelerating period and a decelerating period of the magnetic recording medium, and forming a servo pattern that does not meet the standard on the magnetic recording medium. (13) forming the servo pattern on the magnetic recording medium, feeding the magnetic recording medium from a cartridge and winding up the fed magnetic recording medium, thereby running the magnetic recording medium; erasing a first servo pattern formed on the traveling magnetic recording medium; writing a servo signal by a head onto the traveling magnetic recording medium from which the first servo pattern has been erased, thereby forming a second servo pattern; Including, Forming the second servo pattern includes: The method for writing a servo pattern described in (11) includes controlling the head to write the servo signal during at least one of an acceleration period and a deceleration period of the magnetic recording medium, and forming the second servo pattern that does not meet the standard on the magnetic recording medium. (14) incorporating a tape-like magnetic recording medium into a cartridge; forming a servo pattern on the magnetic recording medium after a specified time has elapsed since the magnetic recording medium was incorporated into the cartridge; A method for manufacturing a cartridge comprising: (15) forming the servo pattern on the magnetic recording medium, A method for manufacturing a cartridge as described in (14), comprising controlling a head to write a servo signal during at least one of an accelerating period and a decelerating period of the magnetic recording medium, and forming a servo pattern that does not meet the standard on the magnetic recording medium. (16) forming the servo pattern on the magnetic recording medium, feeding the magnetic recording medium from a cartridge and winding up the fed magnetic recording medium, thereby running the magnetic recording medium; erasing a first servo pattern formed on the traveling magnetic recording medium; writing a servo signal by a head onto the traveling magnetic recording medium from which the first servo pattern has been erased, thereby forming a second servo pattern; Including, Forming the second servo pattern includes: A method for manufacturing a cartridge as described in (14), which includes controlling the head to write the servo signal during at least one of an accelerating running period and a decelerating running period of the magnetic recording medium, and forming the second servo pattern that does not meet the standard on the magnetic recording medium. [Explanation of symbols]

[0195] 10 Cartridge 11 Cartridge Memory 12 Cartridge case 41 Base 42 Base layer 43 Magnetic layer 44 Back layer 110 servo frame 111 Servo subframe 1 111A A Burst 111B B Burst 112 Servo subframe 2 112C C-Burst 112D D-Burst 113 Servo Stripe 210, 220 Servo writer 211 Cartridge storage section 211A Spindle 212 Reel 213A, 213B, 213C, 213D Guide rollers 214 Degaussing Magnet 215 Servo signal writing head 216 Verify Head 217 Control Device 218 Pulse Generator Circuit 219A Spindle Drive Circuit 219B, 219C Reel drive circuit 230 Winder 240 Quality Inspection Equipment MT magnetic tape SB servo band DB Data Binding

Claims

1. a running unit that runs the magnetic recording medium by feeding out the tape-like magnetic recording medium from the cartridge and winding up the magnetic recording medium that has been fed out; an erasing unit that erases a first servo pattern formed on the traveling magnetic recording medium; a head for writing a servo signal onto the traveling magnetic recording medium from which the first servo pattern has been erased, to form a second servo pattern; a control unit that controls the head to write the servo signal during at least one of an accelerating running period and a decelerating running period of the magnetic recording medium, and forms the second servo pattern that does not satisfy the standard on the magnetic recording medium; A servo writer comprising:

2. a running unit that runs the magnetic recording medium by feeding out the tape-like magnetic recording medium from the cartridge and winding up the magnetic recording medium that has been fed out; an erasing unit that erases a first servo pattern formed on the traveling magnetic recording medium; a head for writing a servo signal onto the traveling magnetic recording medium from which the first servo pattern has been erased, to form a second servo pattern; a control unit that controls the head so as not to write the servo signal during at least one of an accelerating period and a decelerating period of the magnetic recording medium; A servo writer comprising:

3. 2. The servo writer of claim 1, wherein the head has five or more recording elements.

4. five or more of the recording elements write the servo signals onto the magnetic recording medium, thereby forming five or more servo bands; 4. The servo writer of claim 3, wherein the servo signal includes information for uniquely identifying each of the servo bands.

5. a wound tape-like magnetic recording medium; a case for accommodating the magnetic recording medium; Equipped with the magnetic recording medium has an unused area; A cartridge in which a servo pattern that does not meet standards or no servo pattern is formed in the unused area.

6. The unused area is a first unused area provided at the end of the magnetic recording medium; a second unused area provided at the beginning of the winding of the magnetic recording medium; The cartridge of claim 5 comprising:

7. 6. A cartridge according to claim 5, wherein said magnetic recording medium has five or more servo bands.

8. 8. The cartridge of claim 7, wherein five or more of said servo bands include information to uniquely identify each of said servo bands.

9. The magnetic recording medium includes a magnetic layer, 6. A cartridge according to claim 5, wherein the squareness of said magnetic layer in the perpendicular direction is 65% or more.

10. The magnetic layer includes a magnetic powder, 10. The cartridge of claim 9, wherein the magnetic powder comprises hexagonal ferrite, ε iron oxide, or Co-containing spinel ferrite.