Integrated method and tool for high quality selective silicon nitride deposition

Abstract

To provide processing method and tool for forming a logic and memory device.SOLUTION: A processing method performed in a processing tool without breaking vacuum includes pre-cleaning a top surface of a film stack, the film stack including alternating layers of a first material layer and a second material layer and having one or more of memory holes and slit pattern openings extending through the film stack. The method also includes exposing the top surface of the film stack to a growth inhibitor, selectively depositing a silicon-containing dielectric layer in regions of the film stack, and densifying the silicon-containing dielectric layer.SELECTED DRAWING: Figure 5

Description

[Technical Field]

[0001] FIELD OF THE DISCLOSURE Embodiments of the present disclosure relate to the field of electronic devices and methods and apparatus for manufacturing electronic devices. More particularly, embodiments of the present disclosure provide methods for forming 3D-NAND devices with high-quality silicon-containing dielectric layers. [Background technology]

[0002] Semiconductor technology is advancing rapidly, with device dimensions shrinking as technology advances to provide faster processing and storage per unit space. In NAND devices, the string current must be high enough to provide enough current to distinguish between on and off cells. The string current depends on carrier mobility, which is improved by increasing the grain size of the silicon channel.

[0003] Current processes employed in 3D-NAND manufacturing use high-temperature atomic layer deposition (ALD) or chemical vapor deposition (CVD) silicon nitride (SiN) with a subsequent additional patterning step. Selective deposition of SiN can eliminate the patterning step. Selective deposition, however, requires a relatively low deposition temperature, which results in poor film quality.

[0004] Therefore, there is a need in the art for 3D-NAND devices with high quality SiN films. Additionally, there is a need in the art for methods and apparatus for forming 3D-NAND devices. Summary of the Invention

[0005] One or more embodiments of the present disclosure are directed to a processing method for forming a logic or memory device. In one or more embodiments, the processing method for forming a logic or memory device includes pre-cleaning a top surface of a film stack, the film stack including alternating layers of a first material and a second material and having one or more of a memory hole and a slit pattern opening extending through the film stack, exposing the top surface of the film stack to a growth inhibitor, selectively depositing a silicon-containing dielectric layer in regions of the film stack, and densifying the silicon-containing dielectric layer, wherein the processing method is performed in a processing tool without breaking vacuum.

[0006] A further embodiment of the present disclosure is directed to a processing tool. In one embodiment, the processing tool includes a central transfer station including a robot configured to move wafers, a plurality of process stations, each process station connected to the central transfer station and providing a processing area separated from processing areas of adjacent process stations, the plurality of process stations including one or more of a pre-clean chamber, an inhibitor soak chamber, a selective deposition chamber, and a densification chamber, and a controller connected to the central transfer station and the plurality of process stations, the controller configured to operate the robot to move wafers between the process stations and to control a process performed at each of the process stations.

[0007] So that the above-recited features of the present disclosure may be understood in detail, a more particular description of the present disclosure, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the accompanying drawings. It should be noted, however, that the accompanying drawings illustrate only typical embodiments of the present disclosure and therefore should not be considered as limiting the scope of the present disclosure, as the present disclosure may admit of other equally effective embodiments. The embodiments described herein are illustrated by way of example, and not by way of limitation, in the figures of the accompanying drawings in which like reference numerals indicate similar elements. [Brief explanation of the drawings]

[0008] [Figure 1] FIG. 1 shows a process flow diagram of one embodiment of a method according to embodiments described herein. [Figure 2A] FIG. 1 illustrates a cross-sectional view of a device according to one or more embodiments. [Figure 2B] FIG. 2B illustrates an enlarged cross-sectional view of region 103 of the device of FIG. 2A according to one or more embodiments. [Figure 3A] FIG. 1 illustrates a cross-sectional view of a device according to one or more embodiments. [Figure 3B] FIG. 3B illustrates an enlarged cross-sectional view of region 103 of the device of FIG. 3A according to one or more embodiments. [Figure 3C] FIG. 3B illustrates an enlarged cross-sectional view of region 103 of the device of FIG. 3A according to one or more embodiments. [Figure 4A] FIG. 3B illustrates an enlarged cross-sectional view of region 103 of the device of FIG. 3A according to one or more embodiments. [Figure 4B] FIG. 1 illustrates a cross-sectional view of a device according to one or more embodiments. [Figure 5] FIG. 1 illustrates a cross-sectional view of a device according to one or more embodiments. [Figure 6] 1A-1C illustrate cross-sectional views of devices according to one or more alternative embodiments. [Figure 7]1A-1C illustrate cross-sectional views of devices according to one or more alternative embodiments. [Figure 8] FIG. 1 illustrates a cluster tool according to one or more embodiments. DETAILED DESCRIPTION OF THE INVENTION

[0009] Before describing several example embodiments of the present disclosure, it is to be understood that the present disclosure is not limited to the details of construction or process steps set forth in the following description. The present disclosure is capable of other embodiments and of being practiced or carried out in various ways.

[0010] One or more embodiments provide a processing method in an integrated processing tool to enable selective deposition of a silicon-containing dielectric film, e.g., silicon nitride, on polysilicon sidewalls or tunnel oxide sidewalls through high aspect ratio memory holes or through slit pattern openings in a 3D NAND cell film stack.

[0011] Selective deposition of silicon-containing dielectric films, such as silicon nitride, is a low-temperature process that results in low-quality films. Without intending to be bound by theory, it is believed that selectively deposited silicon-containing films, particularly silicon nitride, cannot be used to form 3D NAND cell structures if the low-quality selectively deposited silicon-containing dielectric films cannot be converted to high-quality silicon-containing films.

[0012] One or more embodiments of the present disclosure are described with reference to the figures. The method of one or more embodiments fabricates a logic device or a memory device. In certain embodiments, a 3D NAND cell structure is fabricated. In some embodiments, the method includes pre-cleaning a top surface of a film stack, the film stack including alternating layers of a first material and a second material and having one or more of a memory hole and a slit pattern opening extending through the film stack; exposing the top surface of the film stack to a growth inhibitor; selectively depositing a silicon-containing dielectric layer in regions of the film stack; and densifying the silicon-containing dielectric layer. In some embodiments, the processing method is performed in a processing tool without breaking vacuum.

[0013] FIG. 1 shows a flowchart for an exemplary method 10 for forming a memory device. Those skilled in the art will recognize that method 10 can include any or all of the illustrated processes. Additionally, the order of the individual processes may vary in some respects. Method 10 can begin with any of the listed processes without departing from this disclosure. Referring to FIG. 1 , in operation 12, a film stack is provided. As used herein, the term "providing" means that a substrate is made available for processing (e.g., placed in a processing chamber). In operation 14, impurities, such as native oxide, are removed from the surface of the film stack. In operation 16, the film stack is exposed to a growth inhibitor. In operation 18, a silicon-containing dielectric layer is selectively deposited in regions of the film stack. In operation 20, the silicon-containing dielectric layer is densified. In operation 22, the silicon-containing dielectric layer may optionally be oxidized.

[0014] 2A-5 illustrate portions of an electronic device 100 following the process flow illustrated for method 10 in FIG. 1. FIG. 2A illustrates electronic device 100 according to one or more embodiments of the present disclosure. In some embodiments, electronic device 100 illustrated in FIG. 2A is formed in layers on a substrate 105, which may be bare, as shown. The electronic device of FIG. 2A is comprised of substrate 105, semiconductor layer 110, optional sacrificial layer 120, stack 130, and optional oxide layer 140.

[0015] The substrate 105 can be any suitable material known to those skilled in the art. As used herein and in the appended claims, the term "substrate" refers to a surface or portion of a surface on which a process operates. It will also be understood by those skilled in the art that, unless the context clearly indicates otherwise, a reference to a substrate can refer to only a portion of a substrate. Furthermore, a reference to depositing on a substrate can refer to both a bare substrate and a substrate having one or more films or features deposited or formed thereon.

[0016] As used herein, "substrate" refers to any substrate or material surface formed on a substrate on which film processing is performed during a fabrication process. For example, substrate surfaces on which processing may be performed include materials such as silicon, silicon oxide, strained silicon, silicon-on-insulator (SOI), carbon-doped silicon oxide, amorphous silicon, doped silicon, germanium, gallium arsenide, glass, sapphire, and any other material, such as metals, metal nitrides, metal alloys, and other conductive materials, depending on the application. Substrates include, but are not limited to, semiconductor wafers. Substrates may be subjected to pretreatment processes to polish, etch, reduce, oxidize, hydroxylate, anneal, and / or bake the substrate surface. In addition to film processing directly on the surface of the substrate itself, the present disclosure also provides that, as disclosed in more detail below, any of the disclosed film processing steps may also be performed on an underlying layer formed on the substrate, and the term "substrate surface" is intended to include such underlying layers as the context indicates. Thus, for example, if a film / layer or partial film / layer is being deposited on a substrate surface, the exposed surface of the newly deposited film / layer becomes the substrate surface.

[0017] In one or more embodiments, the semiconductor layer 110 is on the substrate 105. In some embodiments, the semiconductor layer 110 may also be referred to as a common source line. The semiconductor layer 110 may be formed by any suitable technique known to those skilled in the art and may be fabricated from any suitable material, including, but not limited to, polysilicon (poly-Si). In some embodiments, the semiconductor layer 110 is a common source line fabricated from a conductive or semiconducting material.

[0018] In one or more embodiments, optional sacrificial layer 120 is formed on semiconductor layer 110 and can be made of any suitable material. In some embodiments, optional sacrificial layer 120 is removed and replaced in a later process. In some embodiments, optional sacrificial layer 120 is not removed and remains in electronic device 100. In this case, the term "sacrificial" has an expanded meaning to include permanent layers, which may be referred to as conductive layers. In one or more embodiments, optional sacrificial layer 120 comprises a material that can be selectively removed relative to the adjacent semiconductor layer 110 and second material layer 132.

[0019] In one or more embodiments, a stack 130 is formed on the optional sacrificial layer 120. The stack 130 in the illustrated embodiment includes a plurality of alternating second material layers 132 and first material layers 134. In one or more embodiments, the first material layers 134 include nitride layers, and the second material layers 132 include oxide layers. In some embodiments, the stack 130 includes a non-exchange gate, such as alternating oxide and polysilicon, or oxide and metal, or oxide and sacrificial layers. The first material layers 134 include a material that is etch-selective with respect to the second material layers 132 such that the first material layers 134 can be removed without substantially affecting the second material layers 132. In one or more embodiments, the first material layers 134 include one or more of polysilicon, silicon nitride (SiN), silicon carbide (SiC), silicon oxycarbide (SiOC), germanium (Ge), and titanium nitride (TiN). In one or more embodiments, the first material layer 134 comprises silicon nitride, and in one or more embodiments, the second material layer 132 comprises silicon oxide.

[0020] The individual alternating layers may be formed to any suitable thickness. In some embodiments, the thickness of each second material layer 132 is approximately equal. In one or more embodiments, each second material layer 132 has a second layer thickness. In some embodiments, the thickness of each first material layer 134 is approximately equal. As used in this regard, approximately equal thicknesses are within + / - 5% of each other. In some embodiments, a silicon layer (not shown) is formed between the second material layer 132 and the first material layer 134. The thickness of the silicon layer may be relatively thin compared to the layer thickness of the second material layer 132 or the first material layer 134.

[0021] In one or more embodiments, a memory hole channel 150 is opened through stack 130. In some embodiments, opening memory hole channel 150 includes etching through optional oxide layer 140, stack 130, optional sacrificial layer 120, and into semiconductor layer 110. Referring to FIG. 2B, which is an expanded view of region 103, memory hole channel 150 has sidewalls that extend through stack 130 and expose surface 138 of second material layer 132 and surface 139 of first material layer 134.

[0022] In one or more embodiments, the memory hole channel 150 has a high aspect ratio. As used herein, the term "high aspect ratio" refers to a feature having a height:width ratio greater than or equal to about 10, 20, or 50 or more.

[0023] In one or more embodiments, the optional sacrificial layer 120 has an exposed surface 122 as a sidewall of a memory hole channel 150. The memory hole channel 150 extends a distance into the semiconductor layer 110 such that the sidewall surface 112 and a bottom 114 of the memory hole channel 150 are formed within the semiconductor layer 110. The bottom 114 of the memory hole channel 150 can be formed at any point within the thickness of the semiconductor layer 110. In some embodiments, the memory hole channel 150 extends a thickness into the semiconductor layer 110 within a range of about 10% to about 90%, or within a range of about 20% to about 80%, or within a range of about 30% to about 70%, or within a range of about 40% to about 60% of the thickness of the semiconductor layer 110. In some embodiments, the memory hole channel 150 extends a distance into the semiconductor layer 110 that is greater than or equal to 10%, 20%, 30%, 40%, 50%, 60%, 70%, or 80% of the thickness of the semiconductor layer 110.

[0024] 1 and 2A and 2B, in operation 14, exposed surfaces of the film stack, such as the surface 138 of the second material layer 132, the surface 139 of the first material layer 134, and the bottom 114 of the memory hole channel 150, may be cleaned / pre-cleaned. In some embodiments, the cleaning / pre-cleaning process includes a sublimation etch for native oxide removal. The etch process may be plasma-based or thermal-based. The plasma process may be any suitable plasma (e.g., conductively coupled plasma, inductively coupled plasma, microwave plasma). In one or more embodiments, the cleaning process may include a conventional plasma etch or a remote plasma-assisted dry etch process, such as the SiCoNi™ etch process available from Applied Materials, Inc., Santa Clara, California. In the SiCoNi™ etch process, the device or film stack is exposed to H, NF, and / or NH plasma species, e.g., plasma-excited hydrogen and fluorine species. For example, in some embodiments, the device or film stack may be subjected to simultaneous exposure to H, NF, and NH plasma. The SiCoNi™ etch process can be performed in a SiCoNi™ pre-clean chamber, which can be integrated into one of a variety of multi-processing platforms available from Applied Materials®, including the Centura®, DUAL ACP, Producer® GT, and Endura® platforms. The wet etch process can include a hydrofluoric (HF) acid last process, i.e., a so-called "HF last" process, in which an HF etch of the surface is performed, resulting in hydrogen termination of the surface. Alternatively, any other liquid-based pre-clean process can be employed.

[0025] 1 , in one or more embodiments, in operation 16, electronic device 100 is exposed to a growth inhibitor to prevent deposition. The growth inhibitor may be added onto second material layer 132 to prevent deposition on the second material layer. In operation 18, silicon-containing dielectric layer 152 may be selectively deposited onto first material layer 134 and not (or substantially not) deposited onto second material layer 132. Silicon-containing dielectric layer 152 may be deposited by any suitable means known to those skilled in the art. In one or more embodiments, silicon-containing dielectric layer 152 is deposited at a temperature below 500° C., for example, by atomic layer deposition (ALD) or chemical vapor deposition (CVD).

[0026] Method 10 of one or more embodiments is an integrated method. In one or more embodiments, method 10 can be performed in one or more processing chambers without breaking vacuum during any of operations 12, 14, 16, 18, 20, and 22.

[0027] 3A-5 illustrate one or more embodiments in which a silicon-containing layer is deposited on a recessed region 142 adjacent to the first material layer 134 through the memory hole channel 150. In particular, FIG. 3A illustrates recessing the first material layer 134 relative to the second material layer 132 through the memory hole channel 150. In one or more embodiments, the recessed region 142 is formed. The first material layer 134 may be recessed according to any suitable process known to those skilled in the art. In other embodiments, the memory hole channel 150 may be structurally formed; for example, a polysilicon channel material may be deposited in the memory hole of a SiN / SiO / SiN stack, after which the SiN is removed and the SiO is trimmed, leaving a SiO structure with a recess that opens to the poly-Si channel. In this case, 134 is not only recessed, but is also completely removed, exposing the filled channel material.

[0028] In one or more embodiments, referring to FIG. 1 , in operation 16, a surface treatment, e.g., exposure to a growth inhibitor, is used to ensure that different terminating groups are present on the second material layer 132 so that subsequent ALD film growth can be differentiated based on the various surfaces. For example, to create a bare Si surface terminated with Si-H groups, a dilute HF wet clean or a plasma-based dry clean can be used to remove native oxide on the Si surface and form Si-H bonds. To create a passivated surface that can prevent ALD film growth, a hydrophobic surface monolayer can be formed on the silicon oxide surface. For example, an alkylaminosilane can be adsorbed onto the silicon oxide surface to form alkylsilyl groups on the SiO surface. The ALD film growth chemistry of some embodiments is based on a silicon halide and ammonia reaction that can selectively grow on bare Si surfaces but not on passivated SiO surfaces. The maximum thickness achievable by some embodiments is approximately 100 Å of growth on bare Si, with substantially no film growth on passivated SiO surfaces. Periodic SiO surface regeneration and passivation can be used to grow thicker on bare Si than on SiO.

[0029] 3B-3C show representations of operation 16 according to one or more embodiments of the present disclosure. In one or more embodiments, second material layer 132 may have a hydroxyl-terminated surface, while first material layer 134 may have a hydrogen-terminated surface. In some not-shown embodiments, first material layer 134 may also have some native oxide formed thereon. While the embodiments shown by FIGS. 3B-3C show simple single bonds to the substrate surface, those skilled in the art will understand that this is for illustrative purposes only and will appreciate that surface atomic bonding is not as simple as depicted. For example, an oxide surface may be a bridging oxygen atom bonded to two or more silicon atoms, and the surface stoichiometry and bulk composition are not necessarily one-to-one.

[0030] The first material layer 134 and the second material layer 132 can be any suitable surfaces for selective deposition. In some embodiments, the second material layer 132 comprises a dielectric surface with —OH terminal groups, and the first material layer 134 comprises a silicon surface with Si—H groups, with or without a native oxide. In some embodiments, the second material layer 132 comprises a dielectric surface with —OH terminal groups, and the first material layer 134 comprises a metal surface, with or without a native oxide. In some embodiments, the second material layer 132 comprises a metal oxide surface with —OH terminal groups, and the first material layer 134 comprises a silicon surface with Si—H groups, with or without a native oxide. In some embodiments, the second material layer 132 comprises a metal oxide surface with —OH terminal groups, and the first material layer 134 comprises a clean metal surface, with or without a native oxide.

[0031] If a native oxide is present on the first material layer 134, removal of the native oxide may enable a more effective selective deposition process. The native oxide may be removed from the first material layer 134 by exposing the substrate to an etch process. The etch process may be a wet etch process (e.g., exposure to dilute HF (1%)) or a dry etch process (e.g., exposure to a plasma). In some embodiments, the etch process is a plasma-based process. In some embodiments, the plasma-based etch process includes exposing the substrate to a plasma of ammonia and hydrofluoric acid.

[0032] In some embodiments, removing the native oxide from the first material layer 134 results in a surface with a substantially hydrogen-only termination. As used in this manner, the term "substantially hydrogen-only termination" means that the surface termination is hydrogen over greater than or equal to about 98% of the surface area. In some embodiments, removing the native oxide from the first material layer 134 results in a surface with a substantially oxygen-free termination. As used in this manner, the term "substantially oxygen-free termination" means that less than about 2% of the surface area of the surface termination contains oxygen atoms.

[0033] In one or more embodiments, the process used to remove native oxide from the first material layer 134 also oxidizes the second material layer 132 to provide a surface with a substantially hydrogen-free termination. As used in this manner, the term "substantially hydrogen-free termination" means that the surface termination of the described surface is hydrogen over less than or equal to about 2% of the surface area. In some embodiments, the second material layer 132 includes substantially only hydroxyl terminations. As used in this manner, the term "substantially only hydroxyl terminations" means that the surface termination of the described surface is hydroxyl over more than or equal to about 98% of the surface area.

[0034] To form blocking layer 170, the substrate including first material layer 134 and second material layer 132 can be exposed to a growth inhibitor to react with the hydroxyl-terminated surface. In some embodiments, the growth inhibitor comprises an alkylsilane. In some embodiments, the growth inhibitor has the general formula SiR4, where each R independently is a C1-C6 alkyl, a substituted or unsubstituted amine, or a substituted or unsubstituted cyclic amine.

[0035] In some embodiments, the alkylsilane is substantially free of Si—H bonds. As used in this manner, the term “substantially free of Si—H bonds” means that the growth inhibitor contains less than about 1% Si—H bonds, based on the total number of silicon bonds. The growth inhibitor of some embodiments forms surface-terminated —OSiRx on the second material layer 132, replacing —OH terminations. In some embodiments, the growth inhibitor comprises one or more of 1-(trimethylsilyl)pyrrolidine or bis(dimethylamino)dimethylsilane.

[0036] In some embodiments, the alkylsilane comprises at least one substituted or unsubstituted cyclic amine having a ring with 4 to 10 atoms. In some embodiments, the alkylsilane comprises a cyclic amine having one nitrogen atom. In some embodiments, the cyclic amine has one or more nitrogen atoms, but not two or more nitrogen atoms. In one or more embodiments, the cyclic amine comprises pyrrolidine, where the nitrogen atom of the pyrrolidine is bonded to the silicon atom of the alkylsilane. In some embodiments, the alkylsilane comprises 1-(trimethylsilyl)pyrrolidine. In one or more embodiments, the alkylsilane consists essentially of 1-(trimethylsilyl)pyrrolidine. As used in this manner, the term "consisting essentially of" means that the alkylsilane is greater than or equal to about 98% 1-(trimethylsilyl)pyrrolidine, on a molecular basis.

[0037] The substrate can be exposed to the growth inhibitor at any suitable temperature and pressure. In some embodiments, the substrate is exposed to the growth inhibitor at a temperature in the range of about 50°C to about 500°C, or in the range of about 100°C to about 400°C. In some embodiments, the substrate is exposed to the growth inhibitor at a pressure in the range of about 30 Torr to about 120 Torr, or in the range of about 40 Torr to about 100 Torr, or in the range of about 50 Torr to about 90 Torr. In one or more embodiments, the substrate is exposed to the growth inhibitor during a plasma-free thermal process.

[0038] 4A-4B illustrate operation 14, in which a silicon-containing dielectric layer 152 is selectively deposited in recessed region 142. In one or more embodiments, silicon-containing dielectric layer 152 can be deposited by any suitable means known to those skilled in the art. In one or more embodiments, silicon-containing dielectric layer 152 is deposited at a temperature below 500°C, for example, atomic layer deposition (ALD) or chemical vapor deposition (CVD). In other embodiments, silicon-containing dielectric layer 152 is deposited at a temperature below 500°C, including temperatures below 490°C, below 450°C, below 400°C, below 350°C, and below 300°C.

[0039] The silicon-containing dielectric layer 152 may comprise any suitable dielectric material known to those skilled in the art. As used herein, the term "dielectric material" refers to a layer of material that is an electrical insulator that can be polarized in an electric field. In one or more embodiments, the silicon-containing dielectric layer 152 comprises one or more of silicon nitride (SiN), silicon carbonitride (SiCN), silicon oxynitride (SiON), silicon oxycarbonitride (SiOCN), silicon boride (SiB), and silicon boron nitride (SiBN). In particular embodiments, the silicon-containing dielectric layer 152 comprises silicon nitride (SiN).

[0040] In one or more embodiments, the deposition of the silicon-containing dielectric layer 152 is selective to the first material layer 134 over the second material layer 132 such that the silicon-containing dielectric layer 152 is deposited in the recessed regions 142 adjacent to the first material layer 134. In one or more embodiments, the selectivity is greater than 2:1, greater than 5:1, greater than 10:1, or greater than 100:1.

[0041] In one or more embodiments, the silicon-containing dielectric layer 152 has a thickness in the range of from greater than 0 Å to 25 Å.

[0042] Without intending to be bound by theory, it is believed that a relatively low deposition temperature (i.e., below 490° C.) results in a low quality silicon-containing dielectric layer 152. Accordingly, a low quality silicon-containing dielectric layer 152 has a low wet etch rate (WER) greater than 300 Å.

[0043] 4A and 4B , after forming the blocking layer 170, the substrate is exposed to one or more deposition gases to selectively deposit a silicon-containing dielectric layer 152 on the first material layer 134 over the second material layer 132. As used in this regard, the term “selectively on” means that a film is formed on the first material layer 134 to a greater extent than a film can be formed on the second material layer 132. For example, the silicon-containing dielectric layer 152 can be formed on the first material layer 134 to a thickness that is 20, 30, 40, or 50 times thicker than or equal to 20 times thicker than a film formed on the second material layer 132.

[0044] Formation of the silicon-containing dielectric layer 152 may be performed by any suitable technique, including, but not limited to, atomic layer deposition. In one or more embodiments, the silicon-containing dielectric layer 152 is formed in a single processing chamber. In other embodiments, the silicon-containing dielectric layer 152 is formed in a batch processing chamber similar to that shown in FIG. 8 . For example, the silicon-containing dielectric layer 152 may be formed by sequential exposure to a silicon precursor and a reactant. The silicon-containing dielectric layer 152 of some embodiments comprises one or more of SiN, SiO, SiON, SiC, SiCO, SiCN, or SiCON. In some embodiments, the silicon-containing dielectric layer 152 comprises silicon and one or more of oxygen, carbon, or nitrogen atoms. In some embodiments, the silicon-containing dielectric layer 152 is doped with one or more of boron (B), arsenic (As), or phosphorus (P) in an amount up to about 2 percent on an atomic basis.

[0045] In some embodiments, the silicon precursor includes a silicon halide and the reactant includes ammonia. In some embodiments, the silicon precursor includes an organosilicon compound with or without a halogen atom. In some embodiments, the reactant includes a nitrogen-contributing species, an oxygen-contributing species, and / or a carbon-contributing species. In some embodiments, the silicon precursor contributes one or more of nitrogen, oxygen, or carbon to the silicon-containing dielectric layer 152.

[0046] In a single processing chamber, the substrate may be exposed to the silicon precursor and the reactants in the same process region of the processing chamber. In a batch processing chamber, the substrate may be exposed to the silicon precursor and the reactants in alternating process regions of the processing chamber.

[0047] The substrate can be exposed to the growth inhibitor in any suitable process chamber. In some embodiments, the substrate is exposed to the growth inhibitor in a pre-clean chamber. In some embodiments, the substrate is exposed to the growth inhibitor in a separate inhibitor chamber. In some embodiments, the substrate is exposed to the growth inhibitor in a batch processing chamber. For example, the process region of the batch processing chamber can be modified so that the reactive gas flowing in the process region is replaced with the growth inhibitor. After forming the blocking layer 170, the flow of the growth inhibitor in the process region can be replaced with a silicon precursor and reactants.

[0048] The film thickness can be deposited up to a predetermined amount. After a time, the silicon-containing dielectric layer 152 may begin to deposit on the second material layer 132 despite the presence of the blocking layer 170. While not intending to be bound by a particular theory of operation, it is believed that the blocking layer 170 may be removed by repeated exposure to the deposition reactants. To increase the thickness of the silicon-containing dielectric layer 152 and maintain selectivity, the blocking layer 170 may be periodically replenished. In some embodiments, the substrate is exposed to a growth inhibitor after no more than 20, 30, 40, 50, 60, 70, 80, 90, or 100 atomic layer deposition cycles to deposit the silicon-containing dielectric layer 152. In some embodiments, the substrate is exposed to a growth inhibitor after the formation of the silicon-containing dielectric layer 152 to a thickness in the range of about 30 Å to about 100 Å, or after the formation of the silicon-containing dielectric layer 152 to a thickness of up to about 20 Å, 30 Å, 40 Å, 50 Å, 60 Å, or 70 Å.

[0049] Regeneration of the blocking layer 170 can be accomplished by any suitable process. For example, the surface of the substrate can be purged with an inert gas (e.g., N2 or He) at a pressure in the range of about 1 Torr to about 30 Torr for a time in the range of about 10 minutes to about 60 minutes. After purging the surface, the substrate can be again exposed to a growth inhibitor to regenerate the blocking layer 170. In some embodiments, the surface is purged for a time in the range of about 15 minutes to about 50 minutes, or for a time in the range of about 20 minutes to about 40 minutes. In some embodiments, the surface is purged at a pressure in the range of about 10 Torr to about 25 Torr, or for a time in the range of about 15 Torr to about 20 Torr.

[0050] In some embodiments, blocking layer 170 is regenerated by first etching the entire surface of the substrate and then exposing it to a growth inhibitor. The etching process may be the same process used to pre-clean the surface or may be a different etching process.

[0051] The silicon-containing dielectric layer 152 can be formed at any suitable temperature. In some embodiments, the silicon-containing dielectric layer 152 is formed at a temperature in the range of about 200°C to about 700°C, or in the range of about 300°C to about 500°C, or in the range of about 350°C to about 450°C. In some embodiments, the silicon-containing dielectric layer 152 is formed by a thermal process without plasma exposure. In some embodiments, the silicon-containing dielectric layer 152 is formed by a plasma-enhanced process.

[0052] The deposited silicon-containing dielectric layer 152 may have film properties that can be optimized or improved by post-deposition processing. For example, a deposited silicon nitride film may have a high wet etch rate. Exposing the film to a post-deposition process can be used to improve the wet etch rate of the deposited silicon-containing dielectric layer 152. In some embodiments, the post-deposition process improves film quality. In some embodiments, the improved film quality includes one or more of the wet etch rate, refractive index, density, or hydrogen concentration.

[0053] In some embodiments, the post-deposition process includes exposing the substrate surface to a decoupled plasma. In one or more embodiments, the decoupled plasma includes helium. In some embodiments, the decoupled plasma consists essentially of helium. As used in this context, the term "consisting essentially of helium" means that the plasma contains greater than or equal to about 95 atomic percent helium. In some embodiments, the process pressure is in the range of about 1 mTorr to about 1 Torr. For isotropic processing of high aspect ratio structures, lower pressures may be used. The wafer temperature during processing may range from about room temperature to about 500°C.

[0054] In some embodiments, the processing platform has an environment that does not readily oxidize the cleaned substrate surface. As used in this regard, the term "environment" refers to ambient conditions at least within the central transfer station. In some embodiments, the processing platform environment also includes any processing chambers used in the deposition process. For example, if two processing chambers are used in the process, the "environment" may include the two processing chambers and the central transfer station. In some embodiments, the processing platform environment includes water vapor. The water vapor may or may not be mixed with an inert gas. In some embodiments, the water vapor is present in the inert gas in an amount ranging from about 0.1% to about 90% by weight. In some embodiments, the water vapor is present in an amount ranging from about 1% to about 80%, or from about 2% to about 70%, or from about 3% to about 60%, or from about 4% to about 50%, or from about 5% to about 40%, or from about 10% to about 20% by weight. In some embodiments, the environment comprises one or more of nitrogen, hydrogen, helium, argon, krypton, neon, or xenon, along with water vapor in an amount greater than or equal to about 0.1%, 0.5%, 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 12%, 14%, 16%, 18%, or 20%.

[0055] According to one or more embodiments, the substrate is subjected to processing before and / or after forming a layer. This processing can be performed in the same chamber or in one or more separate processing chambers. In some embodiments, the substrate is moved from the first chamber to a separate second chamber for further processing. The substrate can be moved directly from the first chamber to a separate processing chamber, or the substrate can be moved from the first chamber to one or more transfer chambers and then to a separate processing chamber. Thus, the processing apparatus can include multiple chambers in communication with a transfer station. This type of apparatus is sometimes referred to as a "cluster tool" or a "clustered system," among other terms.

[0056] FIG. 5 illustrates operations 16 and 18 in which the silicon-containing dielectric layer 152 is densified to form a high-quality silicon-containing dielectric film 154. The silicon-containing dielectric layer 152 may be densified by any suitable means known to those skilled in the art. In one or more embodiments, the silicon-containing dielectric layer 152 is densified by one or more thermal or other treatments without adding oxygen to the silicon-containing layer. In one or more embodiments, the silicon-containing dielectric layer 152 is subjected to rapid thermal processing (RTP) to provide the high-quality silicon-containing dielectric film 154. In other embodiments, densifying the silicon-containing dielectric layer includes exposing the silicon-containing dielectric layer 152 to a high-density plasma at a temperature less than or equal to 500° C. and a pressure less than 1 Torr. The high-density plasma may be selected from one or more of helium (He), hydrogen (H), neon (Ne), argon (Ar), krypton (Kr), and xenon (Xe).

[0057] In one or more embodiments, in operation 18, the selectively deposited silicon-containing dielectric layer 152 is densified at a temperature greater than 800° C. to provide the silicon-containing dielectric film 154. In some embodiments, the silicon-containing dielectric layer 152 is treated at a temperature greater than 1000° C. to provide the silicon-containing dielectric film 154. In one or more embodiments, after treatment, the silicon-containing dielectric film 154 is a high quality film and has a wet etch rate less than 4 Å / min, including wet etch rates less than 3 Å / min, less than 2 Å / min, and less than 1 Å / min.

[0058] In one or more embodiments, the silicon-containing dielectric film 154 has a thickness in the range of from greater than 0 Å to 25 Å.

[0059] The method of one or more embodiments is an integrated method: in one or more embodiments, the method can be performed in one or more processing chambers without breaking vacuum.

[0060] Referring to FIG. 1, in operation 22, in one or more embodiments, the surface of the high-quality silicon-containing dielectric film 154 is optionally oxidized.

[0061] In one or more alternative embodiments not shown, a silicon-containing layer may be deposited through the memory holes on the first material layer, and the first material layer is not recessed.

[0062] 6-7, in one or more alternative embodiments, during processing, after the second material layer 132 in the stack 130 is removed to form an opening 200 in the mold and a slit pattern opening 202 is formed, a silicon-containing dielectric layer 152 may be selectively deposited on the non-oxide-containing material through the word line slit pattern opening 202, thus depositing the silicon-containing dielectric layer 152 adjacent to the transistor layer 204 on the word line side of the device.

[0063] FIG. 7 illustrates operations in which the silicon-containing dielectric layer 152 is densified to form a high-quality silicon-containing dielectric film 154. The silicon-containing dielectric layer 152 may be densified by any suitable means known to those skilled in the art. In one or more embodiments, the silicon-containing dielectric layer 152 is densified by one or more thermal or other treatments without adding oxygen to the silicon-containing layer. In one or more embodiments, the silicon-containing dielectric layer 152 is subjected to rapid thermal processing (RTP) to provide the high-quality silicon-containing dielectric film 154. In other embodiments, densifying the silicon-containing dielectric layer includes exposing the silicon-containing dielectric layer 152 to a high-density plasma at a temperature less than or equal to 500° C. and a pressure less than 1 Torr. The high-density plasma may be selected from one or more of helium (He), hydrogen (H), neon (Ne), argon (Ar), krypton (Kr), and xenon (Xe).

[0064] In one or more embodiments, the selectively deposited silicon-containing dielectric layer 152 is densified at a temperature greater than 800° C. to provide the silicon-containing dielectric film 154. In some embodiments, the silicon-containing dielectric layer 152 is treated at a temperature greater than 1000° C. to provide the silicon-containing dielectric film 154. In one or more embodiments, after treatment, the silicon-containing dielectric film 154 is a high quality film and has a wet etch rate less than 4 Å / min, including wet etch rates less than 3 Å / min, less than 2 Å / min, and less than 1 Å / min.

[0065] In one or more embodiments, the silicon-containing dielectric film 154 has a thickness in the range of from greater than 0 Å to 25 Å.

[0066] The method of one or more embodiments is an integrated method: in one or more embodiments, the method can be performed in one or more processing chambers without breaking vacuum.

[0067] An additional embodiment of the present disclosure is directed to a processing tool 900 and described methods for the formation of logic or memory devices, as shown in FIG.

[0068] In one or more embodiments, the processing tool 900 is a cluster tool that includes at least one central transfer station with multiple sides, e.g., a first transfer chamber 921 and a second transfer chamber 931. At least one robot 925, 935 is disposed in the at least one central transfer station, e.g., the first transfer chamber 921 and the second transfer chamber 931, and configured to move a robot blade and wafer to each of the multiple sides.

[0069] In one or more embodiments, the processing tool 900 is a cluster tool including multiple processing chambers 902, 904, 906, 908, 910, 912, 914, 916, and 918, also referred to as process stations, connected to a central transfer station. The various processing chambers provide distinct processing regions isolated from adjacent process stations. The processing chambers may be any suitable chambers, including, but not limited to, pre-clean (SiCoNi™) chambers, inhibitor soak chambers, selective deposition (ALD) chambers, and densification chambers (RTP). The specific configurations and components of the process chambers may vary depending on the cluster tool and should not be taken as limiting the scope of the present disclosure.

[0070] 8, a factory interface 950 is connected to the front of the processing tool 900. The factory interface 950 includes a loading chamber 954 and an unloading chamber 956 in front of the factory interface 950. While the loading chamber 954 is shown on the left and the unloading chamber 956 is shown on the right, one skilled in the art will understand that this represents only one possible configuration.

[0071] The size and shape of the loading chamber 954 and unloading chamber 956 can vary depending on, for example, the substrate being processed in the processing tool 900, e.g., a cluster tool. In the embodiment shown, the loading chamber 954 and unloading chamber 956 are sized to hold a wafer cassette, with multiple wafers arranged in the cassette.

[0072] A robot 952 resides within the factory interface 950 and can move between a loading chamber 954 and an unloading chamber 956. The robot 952 can transfer wafers from a cassette in the loading chamber 954 through the factory interface 950 to a load lock chamber 960. The robot 952 can also transfer wafers from the load lock chamber 962 through the factory interface 950 to a cassette in the unloading chamber 956. As will be appreciated by those skilled in the art, the factory interface 950 can have more than one robot 952. For example, the factory interface 950 can have a first robot that transfers wafers between the loading chamber 954 and the load lock chamber 960 and a second robot that transfers wafers between the load lock chamber 962 and the unloading chamber 956.

[0073] In one or more embodiments, the processing tool 900 is a cluster tool having a first section 920 and a second section 930. The first section 920 is connected to the factory interface 950 through load lock chambers 960, 962. The first section 920 includes a first transfer chamber 921 having at least one robot 925 disposed therein. The at least one robot 925 is also referred to as a robotic wafer transfer mechanism. The first transfer chamber 921 is centrally located relative to the load lock chambers 960, 962, the processing chambers 902, 904, 916, 918, and the buffer chambers 922, 924. In some embodiments, the at least one robot 925 is a multi-arm robot capable of independently moving two or more wafers at a time. In some embodiments, the first transfer chamber 921 includes two or more robotic wafer transfer mechanisms. The at least one robot 925 in the first transfer chamber 921 is configured to move wafers between chambers around the first transfer chamber 921. Individual wafers are transported on a wafer transfer blade located at the distal end of the first robotic mechanism.

[0074] After processing the wafer in the first section 920, the wafer may be passed through a pass-through chamber to the second section 930. For example, the chambers 922, 924 may be one-way or two-way pass-through chambers. The pass-through chambers 922, 924 may be used, for example, to cryogenically cool the wafer before processing in the second section 930 or to allow for cooling or post-processing of the wafer before returning to the first section 920.

[0075] A system controller 990 is in communication with the first robot 925, the second robot 935, the first plurality of processing chambers 902, 904, 916, 918, and the second plurality of processing chambers 906, 908, 910, 912, 914. The system controller 990 may be any suitable component capable of controlling the processing chambers and robots. For example, the system controller 990 may be a computer including a central processing unit, memory, suitable circuitry, and storage.

[0076] The processes may generally be stored in the memory of the system controller 990 as software routines that, when executed by a processor, cause the process chamber to perform the processes of the present disclosure. The software routines may also be stored and / or executed by a second processor (not shown) remote from the hardware being controlled by the processor. Some or all of the methods of the present disclosure may also be performed in hardware. Thus, the processes may be implemented in software and executed using a computer system in hardware, for example, as an application-specific integrated circuit or other type of hardware implementation, or as a combination of software and hardware. The software routines, when executed by a processor, transform a general-purpose computer into a special-purpose computer (controller) that controls chamber operation to perform the processes.

[0077] In some embodiments, the system controller 990 is configured to control a selective deposition chamber to selectively deposit a silicon-containing dielectric layer in a region of the film stack at a temperature below 490° C. In some embodiments, the system controller 990 is configured to operate a plasma processing chamber to expose the silicon-containing dielectric layer to thermally treat the silicon-containing dielectric layer at a temperature above 800° C. to provide a silicon-containing dielectric film having a wet etch rate of less than 4 Å / min.

[0078] In one or more embodiments, the processing tool includes a central transfer station including a robot configured to move wafers, a plurality of process stations, each process station connected to the central transfer station to provide a processing region separated from the processing region of an adjacent process station, the plurality of process stations including one or more of a pre-clean chamber, an inhibitor soak chamber, a selective deposition chamber, and a densification chamber, and a controller connected to the central transfer station and the plurality of process stations, the controller configured to operate the robot to move the wafer between the process stations and to control processes performed at each of the process stations. In one or more embodiments, the controller causes the processing tool to perform the following operations: pre-cleaning a top surface of a film stack, the film stack including alternating layers of a first material and a second material and having one or more of a memory hole and a slit pattern opening extending through the film stack; exposing the top surface of the film stack to a growth inhibitor; selectively depositing a silicon-containing dielectric layer in a region of the film stack; and densifying the silicon-containing dielectric layer. In one or more embodiments, the processing tool is maintained under vacuum during each processing operation.

[0079] In the context of describing the materials and methods described herein (particularly in the context of the claims that follow), the use of the terms "a," "an," and "the" and similar referents should be construed to cover both the singular and the plural, unless otherwise specified herein or clearly contradicted by context. The recitation of ranges of values herein merely serves as a shorthand method of individually referring to each separate value falling within the range, unless otherwise specified herein, and each separate value is incorporated herein as if it were individually recited herein. All methods described herein can be performed in any suitable order, unless otherwise specified herein or clearly contradicted otherwise by context. The use of any and all examples, or exemplary language (e.g., "etc.") provided herein, is intended merely to better clarify the materials and methods and does not impose a limitation on the scope unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the disclosed materials and methods.

[0080] References throughout this specification to "one embodiment," "an embodiment," "one or more embodiments," or "an embodiment" mean that a particular feature, structure, material, or characteristic described with respect to that embodiment is included in at least one embodiment of the present disclosure. Thus, the appearances of phrases such as "in one or more embodiments," "in an embodiment," "in one embodiment," or "in an embodiment" in various places throughout this specification are not necessarily all referring to the same embodiment of the present disclosure. Furthermore, particular features, structures, materials, or characteristics may be combined in any suitable manner in one or more embodiments.

[0081] Although the disclosure herein has been described with reference to particular embodiments, it is to be understood that these embodiments are merely illustrative of the principles and applications of the disclosure. Various modifications and variations to the disclosed method and apparatus will be apparent to those skilled in the art without departing from the spirit and scope of the disclosure. Accordingly, the present disclosure is intended to cover modifications and variations that come within the scope of the appended claims and their equivalents.

Claims

1. 1. A process for forming a logic or memory device, the process comprising: pre-cleaning a top surface of a film stack, the film stack including alternating layers of a first material and a second material and having one or more of a memory hole and a slit pattern opening extending through the film stack; exposing the top surface of the film stack to a growth inhibitor; Selectively depositing a silicon-containing dielectric layer within regions of the film stack; densifying the silicon-containing dielectric layer; Including, A processing method for forming logic or memory devices, wherein the processing method is performed in a processing tool without breaking vacuum.

2. The method of claim 1 , wherein the second material layer comprises an oxide layer.

3. 2. The method of claim 1, wherein said region is a recessed region formed by recessing said first material layer relative to said second material layer through said memory hole.

4. The method of claim 1 , wherein the region is on a wordline side of the film stack.

5. 10. The process of claim 1, wherein the first layer of material comprises one or more of polysilicon, silicon nitride, silicon carbide, silicon carbonitride, germanium, and titanium nitride.

6. 10. The process of claim 1, wherein the silicon-containing dielectric layer comprises one or more of silicon nitride (SiN), silicon carbonitride (SiCN), silicon oxynitride, silicon oxycarbonitride (SiOCN), silicon boride (SiB), and silicon boron nitride (SiBN).

7. The process of claim 6 , wherein the silicon-containing dielectric layer comprises silicon nitride.

8. 10. The method of claim 1, wherein selectively depositing the silicon-containing dielectric layer comprises depositing at a temperature below 500[deg.]C.

9. 10. The process of claim 1, wherein the silicon-containing dielectric layer has a wet etch rate of less than 1 Å / min.

10. 10. The method of claim 1, wherein densifying the silicon-containing dielectric layer comprises exposing the silicon-containing dielectric layer to a rapid thermal processing (RTP) process.

11. Densifying the silicon-containing dielectric layer comprises exposing the silicon-containing dielectric layer to a high-density plasma at a temperature of less than or equal to 500° C. and at a pressure of less than 1 Torr, the high-density plasma comprising a mixture of helium (He) and hydrogen (H ２ 2. The method of claim 1, wherein the gas is selected from one or more of: fluorine (H2O), neon (Ne), argon (Ar), krypton (Kr), and xenon (Xe).

12. 10. The process of claim 1, wherein the silicon-containing dielectric layer has a thickness in the range of greater than 0 to 25 Å.

13. 10. The method of claim 1, further comprising oxidizing the silicon-containing dielectric layer.

14. The processing method of claim 1 , wherein the processing tool is selected from the group consisting of a single processing chamber and a batch processing chamber.

15. 1. A processing tool comprising: a central transfer station including a robot configured to move the wafer; a plurality of process stations, each process station connected to the central transfer station and providing a processing area separated from the processing areas of adjacent process stations, the plurality of process stations including one or more of a pre-clean chamber, an inhibitor soak chamber, a selective deposition chamber, and a densification chamber; a controller connected to the central transfer station and the plurality of process stations, the controller configured to operate the robot to move the wafer between the process stations and to control a process performed at each of the process stations; Processing tools, including:

16. The controller: pre-cleaning a top surface of a film stack, the film stack including alternating layers of a first material and a second material and having one or more of a memory hole and a slit pattern opening extending through the film stack; exposing the top surface of the film stack to a growth inhibitor; selectively depositing a silicon-containing dielectric layer within regions of the film stack; densifying the silicon-containing dielectric layer; causing the processing tool to execute The processing tool of claim 15 , wherein the processing tool is maintained under vacuum.

17. The processing tool of claim 16 , wherein the region is on a wordline side of the film stack.

18. 17. The processing tool of claim 16, wherein the region is a recessed region formed by recessing the second material layer relative to the first material layer through the memory hole.

19. 17. The processing tool of claim 16, wherein the first material layer comprises an oxide layer and the second material layer comprises one or more of polysilicon, silicon nitride, silicon carbide, silicon carbonitride, germanium, and titanium nitride.

20. 17. The processing tool of claim 16, wherein the silicon-containing dielectric layer comprises one or more of silicon nitride (SiN), silicon carbonitride (SiCN), silicon oxynitride, silicon oxycarbonitride (SiOCN), silicon boride (SiB), and silicon boron nitride (SiBN).

21. 17. The processing tool of claim 16, wherein selectively depositing the silicon-containing dielectric layer comprises deposition at a temperature below 500°C.

22. exposing the densified silicon-containing dielectric layer to a growth inhibitor; Selectively depositing a second silicon-containing dielectric layer in regions of the film stack; densifying the second silicon-containing dielectric layer; and The method of claim 1 further comprising:

23. selectively depositing a second silicon-containing dielectric layer within a region of the film stack; densifying the second silicon-containing dielectric layer; and The method of claim 1 further comprising:

24. The method of claim 1 further comprising repeating the method.

25. 1. A process for forming a logic or memory device, the process comprising: pre-cleaning a top surface of a film stack, the film stack including alternating layers of a first material and a second material and having one or more of a memory hole and a slit pattern opening extending through the film stack; Selectively depositing a silicon-containing dielectric layer within regions of the film stack; densifying the silicon-containing dielectric layer; Including, A processing method for forming logic or memory devices, wherein the processing method is performed in a processing tool without breaking vacuum.

26. pre-cleaning a top surface of the densified silicon-containing dielectric layer; Selectively depositing a second silicon-containing dielectric layer in regions of the film stack; densifying the second silicon-containing dielectric layer; and 26. The method of claim 25, further comprising:

27. Selectively depositing a second silicon-containing dielectric layer in regions of the film stack; densifying the second silicon-containing dielectric layer; and 26. The method of claim 25, further comprising:

28. 1. A process for forming a logic or memory device, the process comprising: pre-cleaning a top surface of a film stack, the film stack including alternating layers of a first material and a second material and having one or more of a memory hole and a slit pattern opening extending through the film stack; exposing the top surface of the film stack to a growth inhibitor; Selectively depositing a silicon-containing dielectric layer within regions of the film stack; densifying the silicon-containing dielectric layer; Optionally, repeating one or more of pre-cleaning the top surface of the film stack, exposing the top surface of the film stack to a growth inhibitor, selectively depositing a silicon-containing dielectric layer, and densifying the silicon-containing dielectric layer. Including, A processing method for forming logic or memory devices, wherein the processing method is performed in a processing tool without breaking vacuum.