Electrophoretic medium comprising a combination of electrophoretic particles and a charge control agent - Patents.com

Abstract

An electrophoretic medium is disclosed that includes four types of particles. The first type of particles has a first charge polarity. The second and third types of particles have a second charge polarity opposite to the first charge polarity. The electrophoretic medium further includes a first charge control agent and a second charge control agent, the molecular structure of the first charge control agent including a quaternary ammonium group and a non-polar tail, and the molecular structure of the second charge control agent including two or more polar groups and a non-polar tail. In one aspect, the present invention discloses an improved electrophoretic medium for color electrophoretic displays.

Description

[Technical field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to U.S. Provisional Patent Application No. 63 / 296,179, filed January 4, 2022, which is incorporated by reference in its entirety, along with all other patents and patent applications disclosed herein. [Background technology]

[0002] background Electrophoretic displays change color by modifying the position of charged colored particles relative to a light-transmissive viewing surface. Such electrophoretic displays are typically referred to as "electronic paper" or "ePaper" because the resulting display has high contrast similar to ink on paper and is sunlight readable. Electrophoretic displays have been widely adopted in eReaders such as the AMAZON KINDLE® because they provide a book-like reading experience, use little power, and allow users to have a library of hundreds of books on a lightweight, portable device.

[0003] For many years, electrophoretic displays included only two types of charged colored particles: black and white. As used herein, the term "color" includes black and white. The white particles are often light scattering and include, for example, titanium dioxide, while the black particles are light absorbing over the visible range and may include carbon black, or light absorbing metal oxides, for example, copper chromite. In the simplest sense, a black-and-white electrophoretic display requires only a light-transmitting electrode layer at the viewing surface, a second electrode layer (also called the back electrode or bottom electrode), and an electrophoretic medium containing white and black particles with opposite charges. When a voltage of one polarity is applied across the electrophoretic medium, the white particles move to the viewing surface, and when a voltage of the opposite polarity is provided, the black particles move to the viewing surface. If the second electrode layer (back electrode) includes controllable areas (pixels) that are either split electrodes or an active matrix of pixel electrodes controlled by transistors, a pattern can be electronically made to appear on the viewing surface. The pattern may be, for example, a sentence for a book.

[0004] More recently, a variety of color options have become commercially available for electrophoretic displays, including three-color displays (black, white, red, and black, white, yellow) as well as four-color displays (black, white, red, yellow). Similar to the operation of black-and-white electrophoretic displays, electrophoretic displays using three or four reflective particles operate similarly to simple black-and-white displays, as the desired color particles are driven to the viewing surface. Although the driving scheme is much more complicated compared to black-and-white only, ultimately the optical function of the particles is the same.

[0005] Advanced Color Electronic Paper (ACeP™) also contained four particles, but the cyan, yellow, and magenta particles are subtractive rather than reflective, allowing the production of thousands of colors per pixel. The color production process is functionally equivalent to the printing methods used for many years in offset and inkjet printers. A given color is produced by using the appropriate ratios of cyan, yellow, and magenta on a bright white paper background. In the ACeP example, the relative positions of the cyan, yellow, magenta, and white particles with respect to the viewing surface determine the color per pixel. While this type of electrophoretic display allows for thousands of colors per pixel, it is important to carefully control the position of each of the (50-500 nanometer sized) pigments within a working space about 10-20 micrometers thick. Needless to say, variations in particle positioning will result in an inaccurate display of color at a given pixel. Thus, such systems require sophisticated voltage control. Further details of this system are available in the following U.S. patents, all of which are incorporated by reference in their entireties: U.S. Patent No. 9,361,836, U.S. Patent No. 9,921,451, U.S. Patent No. 10,276,109, U.S. Patent No. 10,353,266, U.S. Patent No. 10,467,984, and U.S. Patent No. 10,593,272.

[0006] The term gray state is used herein in its conventional sense in the imaging arts to refer to an intermediate state between two extreme optical states of a pixel, and does not necessarily imply a black-white transition between these two extreme states. For example, some of the E Ink patents and published applications referenced below describe electrophoretic displays whose extreme states are white and deep blue, and thus the intermediate gray state is actually a light blue color. Indeed, as already mentioned, a change in optical state may not be a color change at all. Hereinafter, the terms black and white may be used to refer to the two extreme optical states of a display, and should generally be understood to include extreme optical states that are not strictly black and white, such as the white and dark blue states mentioned above.

[0007] The terms "bistable" and "bistable" are used herein in their conventional sense in the art to refer to displays comprising display elements having first and second display states that differ in at least one optical characteristic, such that any given element exhibits either its first or second display state after being driven with an address pulse of finite duration. After the address pulse is stopped, that state persists for at least several times, e.g., at least four times, the minimum duration of the address pulse required to change the state of the display element. In U.S. Pat. No. 7,170,670, it is shown that some particle-based electrophoretic displays capable of gray scale are stable not only in their extreme black and white states, but also in intermediate gray states, as are several other types of electro-optic displays. This type of display is properly called multistable rather than bistable, but for convenience the term bistable may be used herein to cover both bistable and multistable displays.

[0008] The term impulse, when used herein to refer to driving an electrophoretic display, refers to the integral of the applied voltage with respect to time during which the display is driven.

[0009] Particles that absorb, scatter or reflect light, either broadly or at selected wavelengths, are referred to herein as colored or pigment particles. A variety of materials other than pigments (in the strict sense of the term meaning an insoluble colored material), such as dyes or photonic crystals, that absorb or reflect light may also be used in the electrophoretic media and displays of the present invention.

[0010] Particle-based electrophoretic displays have been the subject of intensive research and development for many years. In such displays, a plurality of charged particles, sometimes called pigment particles, move through a fluid under the influence of an electric field. Electrophoretic displays may have attributes of good brightness and contrast, wide viewing angles, state bistability, and low power consumption compared to liquid crystal displays. Nevertheless, problems with the long-term image quality of these displays have prevented their widespread use. For example, the particles that make up electrophoretic displays tend to settle, and thus the useful life of these displays is insufficient.

[0011] As mentioned above, electrophoretic media require the presence of a fluid. In most of the prior art electrophoretic media, this fluid is a liquid, but electrophoretic media may also be produced using gaseous fluids, see, for example, Kitamura, T., et al., Electrical toner movement for electronic paper-like display, IDW Japan, 2001, Paper HCS1-1, and Yamaguchi, Y., et al., Toner display using insulative particles charged triboelectrically, IDW Japan, 2001, Paper AMD4-4). See also U.S. Pat. Nos. 7,321,459 and 7,236,291. Such gas-based electrophoretic media appear to be susceptible to the same types of problems as liquid-based electrophoretic media due to particle settling, when used in signs where the media is oriented to permit such settling, e.g., where the media is positioned in a vertical plane. Indeed, particle settling appears to be a more severe problem in gas-based electrophoretic media than in liquid-based electrophoretic media, since the lower viscosity of the gaseous suspending fluid compared to the liquid suspending fluid may cause the electrophoretic particles to settle more rapidly.

[0012] Numerous patents and patent applications assigned to or in the name of Massachusetts Institute of Technology (MIT) and E Ink Corporation describe various techniques used in encapsulating electrophoretic and other electro-optic media. Such encapsulated media include numerous microcapsules, each of which itself comprises an internal phase containing electrophoretically mobile particles in a fluid, and a capsule wall surrounding the internal phase. Typically, the capsules themselves are held in a polymeric binder to form a coherent layer positioned between two electrode layers. Techniques described in these patents and patent applications include the following: (a) electrophoretic particles, fluids and fluid additives, see, e.g., U.S. Pat. No. 7,002,728, U.S. Pat. No. 7,679,814, U.S. Pat. No. 10,214,647, and U.S. Pat. No. 11,098,206, and U.S. Patent Application Publication No. 2020 / 0355978; (b) capsules, binders and encapsulation processes, see, e.g., U.S. Pat. No. 6,922,276 and U.S. Pat. No. 7,411,719; (c) microcell structures, wall materials, and methods of forming the microcells, see, e.g., U.S. Pat. No. 7,072,095 and U.S. Pat. No. 9,279,906; (d) methods for filling and sealing microcells, see, e.g., U.S. Pat. Nos. 7,144,942 and 7,715,088; (e) films and subassemblies containing electro-optical materials, see, e.g., U.S. Pat. Nos. 6,982,178 and 7,839,564; (f) backplanes, adhesive layers and other auxiliary layers and methods used in displays, see, e.g., U.S. Pat. Nos. 7,116,318 and 7,535,624; (g) Color Formation Color Control, e.g., U.S. Pat. No. 6,017,584, U.S. Pat. No. 6,545,797, U.S. Pat. No. 6,664,944, U.S. Pat. No. 6,788,452, U.S. Pat. No. 6,864,875, U.S. Pat. No. 6,914,714, U.S. Pat. No. 6,972,893, U.S. Pat. No. 7,038,656, U.S. Pat. No. 7,038,670, U.S. Pat. No. 7,046,228, U.S. Pat. No. 7,052,571, U.S. Pat. No. 7,075,502 *** No. 7,167,155, U.S. Patent No. 7,385,751, U.S. Patent No. 7,492,505, U.S. Patent No. 7,667,684, U.S. Patent No. 7,684,108, U.S. Patent No. 7,791,789, U.S. Patent No. 7,800,813, U.S. Patent No. 7,821,702, U.S. Patent No. 7,839,564 ***No. 7,910,175, U.S. Patent No. 7,952,790, U.S. Patent No. 7,956,841, U.S. Patent No. 7,982,941, U.S. Patent No. 8,040,594, U.S. Patent No. 8,054,526, U.S. Patent No. 8,098,418, U.S. Patent No. 8,159,636, U.S. Patent No. 8,213,076, U.S. Patent No. 8,363,299, U.S. Patent No. 8,422,116, U.S. Patent No. 8,441,714, U.S. Patent No. Patent No. 8,441,716, U.S. Patent No. 8,466,852, U.S. Patent No. 8,503,063, U.S. Patent No. 8,576,470, U.S. Patent No. 8,576,475, U.S. Patent No. 8,593,721, U.S. Patent No. 8,605,354, U.S. Patent No. 8,649,084, U.S. Patent No. 8,670,174, U.S. Patent No. 8,704,756, U.S. Patent No. 8,717,664, U.S. Patent No. 8,786,935, U.S. Patent No. 8 ,797,634, U.S. Patent No. 8,810,899, U.S. Patent No. 8,830,559, U.S. Patent No. 8,873,129, U.S. Patent No. 8,902,153, U.S. Patent No. 8,902,491, U.S. Patent No. 8,917,439, U.S. Patent No. 8,964,282, U.S. Patent No. 9,013,783, U.S. Patent No. 9,116,412, U.S. Patent No. 9,146,439, U.S. Patent No. 9,164,207, U.S. Patent No. 9,170 ,467, U.S. Patent No. 9,170,468, U.S. Patent No. 9,182,646, U.S. Patent No. 9,195,111, U.S. Patent No. 9,199,441, U.S. Patent No. 9,268,191, U.S. Patent No. 9,285,649, U.S. Patent No. 9,293,511, U.S. Patent No. 9,341,916, U.S. Patent No. 9,360,733, U.S. Patent No. 9,361,836, U.S. Patent No. 9,383,623, and U.S. Patent No. 9,423,666, as well as U.S. Patent Application Publication Nos. 2008 / 0043318, 2008 / 0048970, 2009 / 0225398, 2010 / 0156780, 2011 / 0043543, 2012 / 0326957, and U.S. Patent Application Publication Nos. 2013 / 0156780, 2014 / 0156780, 2015 / 0156780, 2016 / 0156780, 2017 / 0156780, 2018 / 0156780, 2019 / 016780, 2020 / 016780, 2021 / 016780, 2022 / 016780, 2023 / 016780, 2024 / 016780, 2025 / 016780, 2026 / 016780, 2027 / 016780, 2028 / 016780, 2029 / 016780, 2030 ...40 / 016780, 2040 / 016780, 2040 / 016780, 2050 / 016780, 2050 / 016780, 2050 / 016780, 2060 / 016780, 2060 / 016780, 2 US Patent Application Publication No. 2013 / 0242378, US Patent Application Publication No. 2013 / 0278995, US Patent Application Publication No. 2014 / 0055840, US Patent Application Publication No. 2014 / 0078576, US Patent Application Publication No. 2014 / 0340430, US Patent Application Publication No. 2014 / 0340736, US Patent Application Publication No. 2014 / 036221 No. 3, U.S. Patent Application Publication No. 2015 / 0103394, U.S. Patent Application Publication No. 2015 / 0118390, U.S. Patent Application Publication No. 2015 / 0124345, U.S. Patent Application Publication No. 2015 / 0198858, U.S. Patent Application Publication No. 2015 / 0234250, U.S. Patent Application Publication No. 2015 / 0268531, U.S. Patent Application Publication No. 201 No. 5 / 0301246, U.S. Patent Application Publication No. 2016 / 0011484, U.S. Patent Application Publication No. 2016 / 0026062, U.S. Patent Application Publication No. 2016 / 0048054, U.S. Patent Application Publication No. 2016 / 0116816, U.S. Patent Application Publication No. 2016 / 0116818, and U.S. Patent Application Publication No. 2016 / 0140909;, (h) Methods for driving displays, e.g., U.S. Pat. No. 5,930,026, U.S. Pat. No. 6,445,489, U.S. Pat. No. 6,504,524, U.S. Pat. No. 6,512,354, U.S. Pat. No. 6,531,997, U.S. Pat. No. 6,753,999, U.S. Pat. No. 6,825,970, U.S. Pat. No. 6,900,851, U.S. Pat. No. 6,995,550, U.S. Pat. No. 7,012,600, U.S. Pat. No. 7,023,420, U.S. Pat. No. 7,034,783, U.S. Pat. No. 7,061,166, U.S. Pat. No. 7,061,662, U.S. Pat. Patent No. 7,116,466, U.S. Patent No. 7,119,772, U.S. Patent No. 7,177,066, U.S. Patent No. 7,193,625, U.S. Patent No. 7,202,847, U.S. Patent No. 7,242,514, U.S. Patent No. 7,259,744, U.S. Patent No. 7,304,787, U.S. Patent No. 7,312,794, U.S. Patent No. 7,327,511, U.S. Patent No. 7,408,699, U.S. Patent No. 7,453,445, U.S. Patent No. 7,492,339, U.S. Patent No. 7,528,822, U.S. Patent No. 7,545,358, U.S. Patent No. 7,583,2 51, U.S. Patent No. 7,602,374, U.S. Patent No. 7,612,760, U.S. Patent No. 7,679,599, U.S. Patent No. 7,679,813, U.S. Patent No. 7,683,606, U.S. Patent No. 7,688,297, U.S. Patent No. 7,729,039, U.S. Patent No. 7,733,311, U.S. Patent No. 7,733,335, U.S. Patent No. 7,787,169, U.S. Patent No. 7,859,742, U.S. Patent No. 7,952,557, U.S. Patent No. 7,956,841, U.S. Patent No. 7,982,479, U.S. Patent No. 7,999,787, U.S. Patent No. 8 ,077,141, U.S. Patent No. 8,125,501, U.S. Patent No. 8,139,050, U.S. Patent No. 8,174,490, U.S. Patent No. 8,243,013, U.S. Patent No. 8,274,472, U.S. Patent No. 8,289,250, U.S. Patent No. 8,300,006, U.S. Patent No. 8,305,341, U.S. Patent No. 8,314,784, U.S. Patent No. 8,373,649, U.S. Patent No. 8,384,658, U.S. Patent No. 8,456,414, U.S. Patent No. 8,462,102, U.S. Patent No. 8,514,168, U.S. Patent No. 8,537,105,U.S. Patent No. 8,558,783, U.S. Patent No. 8,558,785, U.S. Patent No. 8,558,786, U.S. Patent No. 8,558,855, U.S. Patent No. 8,576,164, U.S. Patent No. 8,576,259, U.S. Patent No. 8,593,396, U.S. Patent No. 8,605,032, U.S. Patent No. 8,643,595, U.S. Patent No. 8,665,206, U.S. Patent No. 8,681,191, U.S. Patent No. 8,730,153, U.S. Patent No. 8,810,525, U.S. Patent No. 8,928,562, U.S. Patent No. 8,928,641, U.S. Patent No. Nos. 8,976,444, 9,013,394, 9,019,197, 9,019,198, 9,019,318, 9,082,352, 9,171,508, 9,218,773, 9,224,338, 9,224,342, 9,224,344, 9,230,492, 9,251,736, 9,262,973, 9,269,311, 9,299 No. 9,373,289, U.S. Pat. No. 9,390,066, U.S. Pat. No. 9,390,661, and U.S. Pat. No. 9,412,314, as well as U.S. Patent Application Publication No. 2003 / 0102858, U.S. Patent Application Publication No. 2004 / 0246562, U.S. Patent Application Publication No. 2005 / 0253777, U.S. Patent Application Publication No. 2007 / 0091418, U.S. Patent Application Publication No. 2007 / 0103427, U.S. Patent Application Publication No. 2007 / 0176912, U.S. Patent Application Publication No. 2008 / 0024429, U.S. Patent Application Publication No. US Patent Application Publication No. 2008 / 0024482, US Patent Application Publication No. 2008 / 0136774, US Patent Application Publication No. 2008 / 0291129, US Patent Application Publication No. 2008 / 0303780, US Patent Application Publication No. 2009 / 0174651, US Patent Application Publication No. 2009 / 0195568, US Patent Application Publication No. 2009 / 0322721, US Patent Application Publication No. 2010 / 0194733, US Patent Application Publication No. 2010 / 0194789, US Patent Application Publication No. 2010 / 0220121, US Patent Application Publication No. 2010 / 0265561,U.S. Patent Application Publication No. 2010 / 0283804, U.S. Patent Application Publication No. 2011 / 0063314, U.S. Patent Application Publication No. 2011 / 0175875, U.S. Patent Application Publication No. 2011 / 0193840, U.S. Patent Application Publication No. 2011 / 0193841, U.S. Patent Application Publication No. 2011 / 0199671, U.S. Patent Application Publication No. 2011 / 0221740, U.S. Patent Application Publication No. 2012 / 0001957, U.S. Patent Application Publication No. 2012 / 0098740, U.S. Patent Application Publication No. 2013 / 00633 33, U.S. Patent Application Publication No. 2013 / 0194250, U.S. Patent Application Publication No. 2013 / 0249782, U.S. Patent Application Publication No. 2013 / 0321278, U.S. Patent Application Publication No. 2014 / 0009817, U.S. Patent Application Publication No. 2014 / 0085355, U.S. Patent Application Publication No. 2014 / 0204012, U.S. Patent Application Publication No. 2014 / 0218277, U.S. Patent Application Publication No. 2014 / 0240210, U.S. Patent Application Publication No. 2014 / 0240373, U.S. Patent Application Publication No. 2014 / 02 No. 53425, U.S. Patent Application Publication No. 2014 / 0292830, U.S. Patent Application Publication No. 2014 / 0293398, U.S. Patent Application Publication No. 2014 / 0333685, U.S. Patent Application Publication No. 2014 / 0340734, U.S. Patent Application Publication No. 2015 / 0070744, U.S. Patent Application Publication No. 2015 / 0097877, U.S. Patent Application Publication No. 2015 / 0109283, U.S. Patent Application Publication No. 2015 / 0213749, U.S. Patent Application Publication No. 2015 / 0213765, U.S. Patent Application Publication No. 201 No. 5 / 0221257, U.S. Patent Application Publication No. 2015 / 0262255, U.S. Patent Application Publication No. 2015 / 0262551, U.S. Patent Application Publication No. 2016 / 0071465, U.S. Patent Application Publication No. 2016 / 0078820, U.S. Patent Application Publication No. 2016 / 0093253, U.S. Patent Application Publication No. 2016 / 0140910, and U.S. Patent Application Publication No. 2016 / 0180777 (these patents and patent applications may hereinafter be referred to as the MEDEOD (MEthods for Driving Electro-optic Displays) applications); (i) display applications, see, e.g., U.S. Pat. Nos. 7,312,784 and 8,009,348; and (j) Non-electrophoretic displays, such as those described in U.S. Pat. No. 6,241,921, and U.S. Patent Application Publication Nos. 2015 / 0277160 and 2015 / 0005720 and 2016 / 0012710.

[0013] Many of the above mentioned patents and patent applications recognize that the walls surrounding the individual microcapsules in an encapsulated electrophoretic medium may be replaced by a continuous phase, thus producing so-called polymer-dispersed electrophoretic displays, where the electrophoretic medium comprises a plurality of individual droplets of fluid and a continuous phase of polymeric material, and the individual droplets of electrophoretic medium in such polymer-dispersed electrophoretic displays may be considered as capsules or microcapsules, even though a separate capsule membrane is not associated with each individual droplet. See, for example, U.S. Patent No. 6,866,760. Thus, for purposes of this application, such polymer-dispersed electrophoretic media are considered a subspecies of encapsulated electrophoretic media.

[0014] A related type of electrophoretic display is the so-called microcell electrophoretic display, in which the charged particles and fluid are not encapsulated in microcapsules, but instead are held within a plurality of voids formed in a carrier medium, typically a polymer film. See, for example, U.S. Pat. Nos. 6,672,921 and 6,788,449.

[0015] Although electrophoretic media are often opaque (e.g., because in many electrophoretic media the particles substantially block the transmission of visible light through the display) and operate in a reflective mode, many electrophoretic displays can be made to operate in a so-called shutter mode, in which one display state is substantially opaque and one is light transmissive. See, for example, U.S. Pat. Nos. 5,872,552, 6,130,774, 6,144,361, 6,172,798, 6,271,823, 6,225,971, and 6,184,856. Dielectrophoretic displays, which are similar to electrophoretic displays but rely on variations in electric field strength, can operate in a similar mode. See U.S. Pat. No. 4,418,346. Other types of electro-optic displays can also be operable in a shutter mode. Electro-optic media operating in shutter mode may be used in multi-layer structures for full-color displays, in which at least one layer adjacent to the viewing surface of the display operates in shutter mode to expose or conceal a second layer further away from the viewing surface.

[0016] Encapsulated electrophoretic displays typically do not suffer from the clustering and settling failure modes of conventional electrophoretic devices, and offer additional advantages such as the ability to print or coat displays on a wide variety of flexible and rigid substrates. The use of the term "printing" is intended to include all forms of printing and coating, including, but not limited to, pre-metered coating, such as patch die coating, slot or extrusion coating, slide or cascade coating, curtain coating, roll coating, such as knife-over-roll coating, forward and reverse roll coating, gravure coating, dip coating, spray coating, meniscus coating, spin coating, brushing, air knife coating, silk screen printing processes, electrostatic printing processes, thermal printing processes, inkjet printing processes, electrophoretic deposition (see U.S. Pat. No. 7,339,715), and other similar techniques. Thus, the resulting display can be flexible. Furthermore, because the display medium can be printed (using a variety of methods), the display itself can be manufactured inexpensively.

[0017] As mentioned above, most of the simple prior art electrophoretic media essentially display only two colors. Such electrophoretic media either use a single type of electrophoretic particles having a first color in a colored fluid having a second, different color, or use first and second types of electrophoretic particles having different first and second colors in a non-colored fluid. In the first case, the first color is displayed when the particles are adjacent to the viewing surface of the display, and the second color is displayed when the particles are spaced from the viewing surface. In the second case, the first color is displayed when the first type of particles are adjacent to the viewing surface of the display, and the second color is displayed when the second type of particles are adjacent to the viewing surface. Typically, the two colors are black and white. If a full color display is desired, a color filter array may be placed over the viewing surface of a monochrome (black and white) display. Displays with color filter arrays rely on area sharing and color blending to create color stimuli. The available display area is shared between three or four primary colors, e.g., red / green / blue (RGB) or red / green / blue / white (RGBW), and the filters can be arranged in a one-dimensional (striped) or two-dimensional (2×2) repeating pattern. Other primary color choices, or more than three, are also known in the art. The three partial pixels in the case of an RGB display, or four partial pixels in the case of an RGBW display, are chosen small enough that at the intended viewing distance they visually blend into one another ("color blending") into a single pixel with a uniform color stimulus. An inherent disadvantage of area sharing is that colorants are always present, and the color can only be adjusted by switching the corresponding pixels of the monochrome display below to white or black, and switching the corresponding primary colors on or off. For example, in an ideal RGBW display, each of the primary colors red, green, blue, and white would occupy a quarter of the display area (one of four partial pixels), with the white partial pixel having a brightness similar to the white of the monochrome display below it, and each of the colored partial pixels being one-third less bright than the white of the monochrome display.The luminance of white shown by the display as a whole cannot be higher than half the luminance of the white partial pixel (the white area of ​​the display is generated by displaying one white partial pixel out of every four partial pixels, and since each colored partial pixel in its colored form is equal to one-third of a white partial pixel, the three colored partial pixels combined only contribute one white partial pixel). The luminance and saturation of the color are reduced by area sharing with color pixels switched to black. Area sharing is particularly problematic when mixing yellow, since yellow is brighter than any other color of equal luminance, and saturated yellow has nearly the same luminance as white. Switching the blue pixel (one-quarter of the display area) to black makes the yellow too dark.

[0018] US Patent Nos. 8,576,476 and 8,797,634 describe multicolor electrophoretic displays having a single backplane with independently addressable pixel electrodes and a common light-transmitting first electrode layer (also called the front electrode or top electrode). A plurality of electrophoretic layers are disposed between the backplane and the first light-transmitting electrode layer. The displays described in these applications are capable of rendering any of the primary colors (red, green, blue, cyan, magenta, yellow, white and black) at any pixel location. However, the use of multiple electrophoretic layers positioned between a single set of address electrodes has drawbacks. The electric field experienced by particles in a particular layer is lower than that experienced by a single electrophoretic layer addressed with the same voltage. Furthermore, optical losses (caused, for example, by light scattering or unwanted light absorption) in the electrophoretic layer closest to the viewing surface can affect the appearance of the image formed in the electrophoretic layer below.

[0019] Another type of electrophoretic display system provides a single electrophoretic medium capable of rendering color at any pixel location. Specifically, U.S. Patent No. 9,697,778 describes a display in which a dyed solvent is combined with white (light scattering) particles that move in a first direction when addressed with a low applied voltage and in the opposite direction when addressed with a higher voltage. If the white particles and dyed solvent are combined with two additional particles of opposite charge to the white particles, it is possible to render a full color display. However, the color state of the '778 patent is not acceptable for applications such as text readers. In particular, there is always some of the dyed fluid that separates the white scattering particles from the viewing surface, which results in a tint in the white state of the display.

[0020] US Patent No. 10,475,399 describes an electrophoretic medium capable of rendering a variety of colors at any pixel location. In this case, the electrophoretic medium includes white pigment particles having a first charge polarity, two types of colored pigment particles having a second charge polarity opposite the first charge polarity, and dyes that are soluble in the fluid and provide the color to the electrophoretic medium.

[0021] Yet another form of electrophoretic media capable of rendering any color at any pixel location is described in U.S. Patent No. 9,921,451 and U.S. Patent No. 10,678,111. The electrophoretic media disclosed in these patents, which can be conveniently referred to as "Type I" electrophoretic media, contain four types of particles, namely white, cyan, magenta and yellow, with two of the particle types having a positive charge and two having a negative charge. However, the corresponding displays suffer from color mixing with the white state. Since one type of particle has the same charge as the white particles, a certain amount of the same-charge particles will move toward the viewing surface along with the white particles when the white state is desired. That is, it is difficult to separate the white pigment from the one type of colored pigment particles that has the same charge polarity as the white pigment particles. While it is possible to overcome this undesirable tinting with complex waveforms, such waveforms significantly increase the update time of the display and, in some instances, result in unacceptable "blinking" between images. For example, switching between white and black optical states can be slow with Type I electrophoretic media. On the other hand, it has been observed that the color gamut achievable with Type I electrophoretic media is wide. Another form of electrophoretic medium capable of rendering any color at any pixel location is described in U.S. Patent Application Publication No. 2022 / 0082896 (Serial No. 17 / 474,582). The electrophoretic medium in this form of electrophoretic medium, which can be conveniently referred to as a "Type II" electrophoretic medium, includes four types of particles: white, cyan, magenta, and yellow. The white particles have a negative charge, and the cyan, magenta, and yellow particles have a positive charge. Equivalently, the white particles can have a positive charge, and the cyan, magenta, and yellow particles can have a negative charge. Having three colored pigments with opposite polarity to the white pigment in the Type II medium allows for an uncontaminated white state. Furthermore, it has been observed that electrophoretic displays with Type II electrophoretic media solve the problem of slow switching between different optical states, for example, between a white optical state and a black optical state. Meanwhile, the inventors of the present invention have found it difficult to separate three types of colored particles of the same charge polarity into the combinations required to render various colors. Thus, it has been observed that the color gamut achieved by Type II electrophoretic media is narrower than that of Type I electrophoretic media. The above shows that it is necessary to develop an electrophoretic medium that can achieve good color gamut and rapid switching between different optical states of the corresponding electrophoretic display. Surprisingly, the inventors of the present invention have found that an electrophoretic medium that includes four types of particles (type I or type II) and further includes a combination of a first charge control agent and a second charge control agent allows the construction of a corresponding display that has both a wide color gamut and rapid switching. The molecular structure of the first charge control agent includes a quaternary ammonium group and a non-polar tail. The molecular structure of the second charge control agent includes two or more polar groups and a non-polar tail. [Prior art documents] [Patent documents]

[0022] [Patent Document 1] U.S. Pat. No. 9,361,836 [Patent Document 2] U.S. Pat. No. 9,921,451 [Patent Document 3] U.S. Pat. No. 10,276,109 [Patent Document 4] U.S. Pat. No. 10,353,266 [Patent Document 5] U.S. Pat. No. 10,467,984 [Patent Document 6] U.S. Pat. No. 10,593,272 [Patent Document 7] U.S. Patent No. 7,170,670 [Patent Document 8] U.S. Patent No. 7,321,459 [Patent Document 9] U.S. Patent No. 7,236,291 [Non-patent literature]

[0023] [Non-Patent Document 1] Kitamura, T., et al., Electrical toner movement for electronic paper-like display, IDW Japan, 2001, Paper HCS1-1 [Non-Patent Document 2] Yamaguchi, Y., et al., Toner display using insulative particles charged triboelectrically, IDW Japan, 2001, Paper AMD4-4 Summary of the Invention [Means for solving the problem]

[0024] overview In one aspect, the present invention discloses an improved electrophoretic medium for color electrophoretic displays. The electrophoretic medium includes a non-polar fluid, four types of particles, a first type of particles, a second type of particles, a third type of particles, and a fourth type of particles, a first charge control agent, and a second type of charge control agent. The first type of particles includes a first type of pigment, the first type of pigment being inorganic and having a first color, the first type of particles having a first charge polarity. The second type of particles includes a second type of pigment, the second type of pigment having a second color, the second color being different from the first and second colors, the second type of particles having a second charge polarity, and the second charge polarity being opposite to the first charge polarity. The third type of particles includes a third type of pigment having a third color, the third color being different from the first and second colors, and the third type of particles having a second charge polarity. The fourth type of particles includes a fourth type of pigment having a fourth color, the fourth color being different from the first, second and third colors, and the fourth type of particles having a first charge polarity or a second charge polarity. The second, third and fourth types of pigments may be light absorbing organic pigments. The fourth type of particles may include pigment particles and a polymer, the polymer having a content of less than 35 weight percent of the weight of the particles. The first color may be white, the second color may be cyan, the third color may be magenta, and the fourth color may be yellow. The yellow, magenta and cyan pigments may exhibit diffuse reflection at 650, 550 and 450 nm, respectively, when each particle is approximately isotropically distributed at 15 volume % (particle volume relative to volume of fluid) in a non-polar fluid having a refractive index less than 1.55.

[0025] The electrophoretic medium of the present invention can be used in a color electrophoretic display. The color electrophoretic display may comprise a first light-transmitting electrode layer at a viewing surface, a second electrode layer, and an electro-optical material layer. The second electrode layer comprises an array of thin film transistors coupled to pixel electrodes. The electro-optical material layer comprising the electrophoretic medium of the present invention is disposed between the first light-transmitting electrode layer and the second electrode layer.

[0026] The first charge control agent has a molecular structure. The molecular structure of the first charge control agent includes at least one quaternary ammonium group and a non-polar tail. The second charge control agent has a molecular structure. The molecular structure of the second charge control agent includes two or more polar groups and a non-polar tail. The two or more polar groups are selected from the group consisting of amino groups, sulfonate groups, sulfate groups, sulfinate groups, carboxylic acid groups, phosphonic acid groups, phosphinate groups, phosphate groups, hydroxyl groups, thiol groups, alpha diketone groups, beta diketone groups, ethylene oxide groups, and propylene oxide groups. The polar group of the second charge control agent may be a primary or secondary amino group. The polar group may also be a tertiary amino group, but is not a quaternary ammonium. The nitrogen of the amino group may be part of a heterocycle that is aromatic or non-aromatic. The molecular structure of the first charge control agent (and the second charge control agent) may include at least one amide group. The amide group may be part of a non-polar tail.

[0027] The non-polar tail comprises a polymeric group formed by monomers that include an alkyl or alkenyl group having at least 10 carbon atoms.

[0028] The molecular structure of the monomer used to form the polymeric group of the non-polar tail of the second charge control agent (as well as the non-polar tail of the first charge control agent) may include a carboxylic acid, a carboxylic acid anhydride, or a carboxylic acid halide. The carboxylic acid and the carboxylic acid halide may include 10 to 22 carbon atoms. The carboxylic acid anhydride may include 20 to 44 carbon atoms. The molecular structure of the monomer forming the polymeric tail of the second charge control agent may further include a hydroxyl group or an amine group. The monomer used to form the polymeric tail of the second charge control agent (as well as the first charge control agent) may be selected from the group consisting of ricinoleic acid, linoleic acid, oleic acid, linoleic acid, acid halides of ricinoleic acid, acid halides of linoleic acid, acid halides of linolenic acid, ricinoleic anhydride, linoleic anhydride, oleic anhydride, and linolenic anhydride.

[0029] The molecular structure of the second charge control agent may include a comb polymer having alkyl or alkenyl branches and two terminal polar functional groups.

[0030] The molecular structure of the second charge control agent may include two or more polar functional groups, none of which are quaternary ammonium groups. That is, the molecular structure of the second charge control agent may include one or more quaternary ammonium functional groups. Alternatively, the molecular structure of the second charge control agent may include two or more polar groups, one or more of which may be quaternary ammonium functional groups.

[0031] The electrophoretic medium may further comprise a water-soluble ether. The water-soluble ether has a molecular weight of 75 to 5,000 daltons. The water-soluble ether may be represented by Formula I, Formula II or Formula III, where n is 1 to 145; R1 is hydrogen, a methyl or ethyl group; R2, R3, R4, R5, R6 and R7 are independently selected from the group consisting of hydrogen, a linear or branched alkyl group containing 1 carbon atom to 6 carbon atoms, phenyl, and a benzyl group. Each of Formula I, II and III includes at least one ether functional group. For Formula I, n may also be 1 to 10. [ka] [ka]

[0032] The first, second, third and fourth type of particles may have a layer of a polymer. The polymer may be complexed, adsorbed or covalently bonded to the first, second, third and fourth type of pigment. The first type of particles may be light scattering particles. The first type of particles may include inorganic pigment particles, such as titanium dioxide, treated with a silane and a monomer or combination of monomers. The monomer may be an alkyl methyl methacrylate, such as lauryl methacrylate, or an alkyl acrylate, such as lauryl acrylate. The combination of monomers may include 2,2,2-trifluoroethyl methacrylate. The first type of particles may include inorganic pigment particles, such as titanium dioxide, treated with a monomer, such as alkyl methyl methacrylate and 2,2,2-trifluoroethyl methacrylate. The second type of particles may include a second type of pigment particles, such as Phthalocyanine Blue (Pigment Blue 15:3), and a polymer formed with a monomer including methyl methacrylate and dimethylsiloxane, such as monomethyl methacrylate poly(dimethylsiloxane). The third type of particles may include a third type of pigment particles, and a polymer formed with a monomer including methyl methacrylate and dimethylsiloxane, such as monomethyl methacrylate poly(dimethylsiloxane). The fourth type of particles may include a fourth type of pigment particles, and a polymer formed with a monomer including methyl methacrylate and dimethylsiloxane, such as monomethyl methacrylate poly(dimethylsiloxane). The third type of particles may include a third type of pigment particles, such as Pigment Red 122, treated with a monomer such as vinylbenzyl chloride and methyl methacrylate. A fourth type of particle may include a fourth type of particle, such as Pigment Yellow 155, that is treated with a monomer that includes methyl methacrylate and dimethyl siloxane, for example, monomethyl methacrylate poly(dimethyl siloxane).

[0033] The polarity of the second and third types of particles may have a second polarity, such as positive, and the first and fourth types of particles may have a first polarity, such as negative. The second, third and fourth types of particles may all have a second polarity that is opposite to the first polarity. That is, the first type of particles may have a positive polarity, and the second, third and fourth types of particles may have a negative polarity.

[0034] Alternatively, the first type of particles may have a negative polarity and the second, third and fourth types of particles may have a positive polarity. The second type of particles has a second zeta potential, the third type of particles has a third zeta potential and the fourth type of particles has a fourth zeta potential. The second, third and fourth zeta potentials may all be positive. The second zeta potential may be greater than the third and fourth zeta potentials and the fourth zeta potential may be less than the third zeta potential.

[0035] In another aspect, the present invention provides a color electrophoretic display comprising: (a) a first light-transmissive electrode layer; (b) a microcell layer comprising a plurality of microcells; (c) a sealing layer; and (d) a second electrode layer. Each microcell of the plurality of microcells has an opening. The sealing layer spans the opening of each microcell of the plurality of microcells. Each microcell of the plurality of microcells comprises an electrophoretic medium. The electrophoretic medium comprises a non-polar fluid, four types of particles: a first type of particles, a second type of particles, a third type of particles, and a fourth type of particles, and a first type of charge control agent. The first type of particles comprises a first type of pigment, the first type of pigment being inorganic and having a first color, and the first type of particles having a first charge polarity. The second type of particles includes a second type of pigment, the second type of pigment having a second color, the second color being different from the first and second colors, the second type of particles having a second charge polarity, the second charge polarity being opposite to the first charge polarity. The third type of particles includes a third type of pigment having a third color, the third color being different from the first and second colors, the third type of particles having a second charge polarity. The fourth type of particles includes a fourth type of pigment having a fourth color, the fourth color being different from the first, second and third colors, the fourth type of particles having the first charge polarity or the second charge polarity. The fourth type of particles may include pigment particles and a polymer. The polymer may have a content of less than 35 weight percent of the weight of the particles. The first color may be white, the second color may be cyan, the third color may be magenta, and the fourth color may be yellow.

[0036] The first charge control agent has a molecular structure, and the molecular structure of the first charge control agent includes a quaternary ammonium group and a non-polar tail.

[0037] The color electrophoretic display also includes a water-soluble ether. The water-soluble ether has a molecular weight of 75 to 5,000 Daltons. The water-soluble ether is present in the sealing layer or in the electrophoretic layer of the color electrophoretic display. The water-soluble ether may be present in the sealing layer and the electrophoretic layer of the color electrophoretic display. The water-soluble ether may be represented by Formula I, Formula II, or Formula III, where n is 1 to 145; R1 is hydrogen, a methyl or ethyl group; R2, R3, R4, R5, R6, and R7 are independently selected from the group consisting of hydrogen, a linear or branched alkyl group containing 1 carbon atom to 6 carbon atoms, a phenyl, and a benzyl group. Each of Formula I, II, and III includes at least one ether functional group. For Formula I, n may also be 1 to 10. Water-soluble ethers include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol mono-n-propyl ether, ethylene glycol monoisopropyl ether, ethylene glycol n-monobutyl ether, ethylene glycol monoisobutyl ether, ethylene glycol mono-t-butyl ether, ethylene glycol monobenzyl ether, ethylene glycol monophenyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, ethylene glycol di-n-propyl ether, ethylene glycol diisopropyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol mono-n-propyl ether, diethylene glycol monoisopropyl ether, diethylene glycol n-monobutyl ether, diethylene glycol monoisobutyl ether, diethylene glycol mono-t-butyl ether, diethylene glycol monobenzyl ether, diethylene glycol monophenyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol ethyl methyl ether, diethylene glycol di-n-propyl ether, diethylene glycol disopropyl ether, diethylene glycol di-n-butyl ether, triethylene glycol monomethyl ether, triethylene glycol monoethyl ether,triethylene glycol mono-n-propyl ether, triethylene glycol monoisopropyl ether, triethylene glycol n-monobutyl ether, triethylene glycol monoisobutyl ether, triethylene glycol mono-t-butyl ether, triethylene glycol monobenzyl ether, triethylene glycol monophenyl ether, triethylene glycol dimethyl ether, triethylene glycol diethyl ether, triethylene glycol di-n-propyl ether, triethylene glycol diisopropyl ether, tetraethylene glycol monomethyl ether, tetraethylene glycol monoethyl ether, triethylene glycol monophenyl ether, tetraethylene glycol dimethyl ether, polyethylene glycol monomethyl ether, polyethylene glycol monoethyl ether, polyethylene glycol monophenyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol mono-n-propyl ether, propylene glycol monoisopropyl ether, The propylene glycol mono-n-butyl ether, propylene glycol monoisobutyl ether, propylene glycol monophenyl ether, propylene glycol dimethyl ether, propylene glycol diethyl ether, dipropylene glycol monomethyl ether, dipropylene glycol monoethyl ether, dipropylene glycol mono-n-propyl ether, dipropylene glycol monoisopropyl ether, dipropylene glycol mono-n-butyl ether, dipropylene glycol monoisobutyl ether, dipropylene glycol dimethyl ether, dipropylene glycol diethyl ether, dipropylene glycol di-n-propyl ether, dipropylene glycol diisopropyl ether, tripropylene glycol monomethyl ether, tripropylene glycol monoethyl ether, tripropylene glycol mono-n-propyl ether, tripropylene glycol monoisopropyl ether, tripropylene glycol mono-n-butyl ether, and tripropylene glycol monoisobutyl ether.

[0038] The electrophoretic medium may further include a second charge control agent having a molecular structure. The molecular structure of the second charge control agent may include two or more polar groups and a non-polar tail. The two or more polar groups may be selected from the group consisting of amino groups, sulfonate groups, sulfate groups, sulfinate groups, carboxylic acid groups, phosphonic acid groups, phosphinate groups, phosphate groups, hydroxyl groups, thiol groups, alpha diketone groups, beta diketone groups, ethylene oxide groups, and propylene oxide groups. The non-polar tail includes a polymeric group. The polymeric group may be formed by a monomer including an alkyl or alkenyl group having at least 10 carbon atoms. The molecular structure of the monomer used to form the polymeric group of the non-polar tail of the second charge control agent may include a carboxylic acid, a carboxylic acid anhydride, or a carboxylic acid halide. The carboxylic acid and the carboxylic acid halide may include 10 to 22 carbon atoms. The carboxylic acid anhydride may include 20 to 44 carbon atoms. The molecular structure of the monomer forming the polymer tail of the second charge control agent may further include a hydroxyl group or an amine group. The monomer used to form the polymer tail of the second charge control agent may be selected from the group consisting of ricinoleic acid, linoleic acid, oleic acid, linoleic acid, acid halides of ricinoleic acid, acid halides of linoleic acid, acid halides of linolenic acid, ricinoleic anhydride, linoleic anhydride, oleic anhydride, and linolenic anhydride. The molecular structure of the second charge control agent may include a comb polymer having alkyl or alkenyl branches and two terminal polar functional groups.

[0039] The molecular structure of the second charge control agent may include two or more polar functional groups, none of which are quaternary ammonium groups. That is, the molecular structure of the second charge control agent may include one or more quaternary ammonium functional groups. Alternatively, the molecular structure of the second charge control agent may include two or more polar groups, one or more of which may be quaternary ammonium functional groups. [Brief description of the drawings]

[0040] [Figure 1] FIG. 1 is a schematic cross-sectional view showing the positions of various types of particles in an electrophoretic medium of the present invention when displaying black, white, three subtractive primary colors, and three additive primary colors.

[0041] [Diagram 2] FIG. 2 is a schematic illustration of an electrophoretic display having a Type I electrophoretic medium having four types of particles in a non-polar fluid.

[0042] [Figure 3A] FIG. 3A is a schematic illustration of an electrophoretic display having a Type II electrophoretic medium having four types of particles in a non-polar fluid.

[0043] [Figure 3B] FIG. 3B shows a transition between a first optical state in which all particles of a first charge polarity are present at the observation surface, and a second optical state in which particles having a second (opposite) polarity are present at the observation surface.

[0044] [Figure 3C] FIG. 3C shows a transition between a first optical state, in which all of the particles of a first charge polarity are at the observation surface, and a third optical state, in which intermediate charged particles of the first polarity are located at the observation surface followed by particles having a second (opposite) polarity.

[0045] [Figure 3D] FIG. 3D shows a transition between a first optical state, in which all of the particles of a first charge polarity are at the observation surface, and a fourth optical state, in which the observation surface has particles with a second (opposite) polarity behind the less charged particles of the first polarity.

[0046] [Figure 3E]FIG. 3E shows a transition between a first optical state in which all of the particles of a first charge polarity are at the observation surface, and a fifth optical state having particles with a second (opposite) polarity behind a combination of low and medium charged particles of the first polarity located at the observation surface.

[0047] [Figure 4] FIG. 4 shows an exemplary push-pull drive scheme for addressing an electrophoretic medium containing three subtractive particles and a scattering (white) particle.

[0048] [Diagram 5] FIG. 5 shows an exemplary equivalent circuit of a single pixel of an electrophoretic display.

[0049] [Figure 6] FIG. 6 shows the layers of an exemplary microcell electrophoretic color display.

[0050] [Figure 7] FIG. 7 shows a graph of zeta potential versus weight percentage of charge control agent in an electrophoretic medium containing a white pigment having a polymeric surface treatment.

[0051] [Figure 8] FIG. 8 shows a graph of color versus applied voltage for the white optical state of an electrophoretic display comprising an electrophoretic medium having white, yellow, cyan, and magenta particles and three different ratios of two charge control agents.

[0052] [Figure 9] FIG. 9 shows a graph for determining the time required to switch from a black state to a white state in three electrophoretic compositions having different ratios of two charge control agents.

[0053] [Figure 10] FIG. 10 shows the test waveforms used to determine the color gamut of the inventive and control electro-optical devices.

[0054] [Figure 11] FIG. 11 shows a graph for determining the color gamut of an electrophoretic display comprising an electrophoretic medium having white, yellow, cyan, and magenta particles and three different ratios of two charge control agents. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0055] Detailed Description The term "polyamine" as used herein is an organic compound having a molecular structure that includes two or more amino groups. The amino groups may be primary, secondary or tertiary amino groups.

[0056] The term "carboxylic acid derivative" refers to a compound having a molecular structure that includes a carboxylic acid halide or a carboxylic acid anhydride.

[0057] The term "condensation polymerization" is a form of polymerization in which monomers and / or oligomers react with each other to form larger structures while releasing smaller molecules as by-products, such as water, hydrochloric acid, methanol, etc.

[0058] As used herein, "molecular weight" refers to weight average molecular weight, unless otherwise specified. Molecular weight is measured using industry standard size exclusion column chromatography.

[0059] The terms "amine," "amino group," and "amino functional group" include primary, secondary, and tertiary amines, and primary, secondary, and tertiary amine functional groups. The terms do not include "quaternary amines" and "quaternary amine functional groups."

[0060] The term "quaternary amine" or "quaternary ammonium" or "quaternary ammonium salt" or "quaternary amine functional group" includes functional groups in which the nitrogen atom has four substituents, none of which is hydrogen. That is, the nitrogen atom of a quaternary amine has no hydrogen atoms directly attached to it. The term "cationic charge control agent" means that the charge control agent comprises a "quaternary amine."

[0061] The terms "pigment" and "pigment particles" are synonymous in this application.

[0062] The present invention includes an improved four-particle electrophoretic medium comprising four types of particles in a non-polar fluid: a first type, a second type, a third type, and a fourth type of particles. The first type of particles comprises a first type of pigment having a first color, the first type of pigment being inorganic. The first type of particles has a first charge polarity. The second type of particles comprises a second type of pigment having a second color different from the first color. The second type of particles has a second charge polarity, the second charge polarity being opposite to the first charge polarity. The third type of particles comprises a third type of pigment having a third color different from the first and second colors. The third type of particles has a second charge polarity. The fourth type of particles comprises a fourth type of pigment having a fourth color different from the first, second, and third colors. The fourth type of particles has either the first or second charge polarity.

[0063] Charge Control Agent

[0064] Charge control agents (CCAs) are used in the electrophoretic medium of electrophoretic displays to control the charge of the electrophoretic particles. Typically, CCAs are surfactant-like molecules with an ionic or other polar group, hereafter referred to as the head group, and a non-polar chain (typically a hydrocarbon chain), hereafter referred to as the tail. CCAs may be complexed with the charged particles or absorbed into the particles. That is, the electrophoretic particles and CCA may exist as a charge complex or may be loosely associated by van der Waals forces. It is believed that CCAs form reverse micelles in the electrophoretic medium, and that it is a small population of charged reverse micelles that provide electrical conduction in the medium. Reverse micelles comprise a polar core, which may have a variety of sizes, from 1 nm to tens of nanometers, and may have a spherical, cylindrical or other geometric structure, surrounded by the non-polar tail groups of CCA molecules. In an electrophoretic medium, typically three phases can be distinguished: solid particles with a surface, a highly polar phase distributed in the form of very small droplets (reverse micelles), and a continuous phase containing a non-polar fluid. Both the electrophoretic particles and the charged reverse micelles can move through the fluid upon application of an electric field, and thus there are two parallel paths for electrical conduction through the fluid (which itself typically has negligible electrical conductivity).

[0065] The polar core of the reverse micelles is believed to affect the charge on the surface by adsorption to the surface. In electrophoretic displays, such adsorption can occur on the surface of electrophoretic particles or on the inner walls of microcapsules (or other solid phases, e.g., the walls of microcells) to form structures similar to reverse micelles; these structures are hereafter referred to as semi-micelles. If an ion of one ion pair is more strongly bound to the surface than the other ion, ion exchange between the semi-micelle and the unbound reverse micelle can result in charge separation, with the more strongly bound ion remaining associated with the particle and the more weakly bound ion being incorporated within the core of the free reverse micelle.

[0066] It is also possible that the ionic substance of the head group of CCA induces ion pairing on the particle (or other) surface. Thus, CCA can perform two basic functions: charge generation on the surface and charge separation from the surface. Charge generation can be the result of acid-base or ion exchange reaction between some moieties present in the CCA molecule (or otherwise incorporated in the reverse micelle core or fluid) and the particle surface. Thus, useful CCA substances are those that can participate in such interactions, or any other charge interactions known in the art.

[0067] The mechanism of particle control in electrophoretic media is not fully understood. Uncontrolled processes may result in undesirably high conductivity of the electrophoretic media. Furthermore, if the charge control agent is only physisorbed on the particles, a change in conditions may cause partial or complete desorption of the charge control agent from the particles, resulting in undesirable changes in the electrophoretic properties of the particles. The desorbed charge control agent may re-adsorb on other surfaces in the electrophoretic medium, and such re-adsorption has the potential to cause additional problems. The effect of the charge control agent is particularly difficult to predict in electrophoretic media containing multiple types of electrophoretic particles, and the charge control agent may adsorb on the surfaces of different types of particles. In the case of encapsulated electrophoretic media, it is also possible that the charge control agent may adsorb on the capsule walls.

[0068] The charge control agent may have an average molecular weight of greater than 500 grams / mole, or greater than 1,000 grams / mole, or greater than 1,500 grams / mole, or greater than 3,000, or greater than 5,000, or greater than 10,000. For example, the average molecular weight of the charge control agent may be 500 grams / mole to 12,000 grams / mole, 1,000 to 10,000, 2,000 to 8,000 grams / mole, 600 grams / mole to 2,000 grams / mole, or 2,000 to 11,000 grams / mole.

[0069] The electrophoretic medium of the present invention comprises a combination of first and second charge control agents, the first and second charge control agents being soluble in the non-polar fluid of the electrophoretic medium.

[0070] The molecular structure of the first charge control agent includes a quaternary ammonium group and a non-polar tail.

[0071] The non-polar tail of the first charge control agent may comprise a polymeric group formed by a monomer comprising at least 10 carbon atoms. The non-polar tail of the first charge control agent may comprise a polymeric group formed by a monomer, the molecular structure of which comprises at least 10 carbon atoms.

[0072] The molecular structure of the monomer used to form the non-polar tail of the first charge control agent may include a carboxylic acid, a carboxylic acid anhydride, or a carboxylic acid halide, where the carboxylic acid and the carboxylic acid halides contain 10 to 22 carbon atoms and the carboxylic acid anhydrides contain 20 to 44 carbon atoms.

[0073] The molecular structure of the monomer forming the non-polar tail of the first charge control agent may include at least one carbon-carbon double bond. The molecular structure of the monomer used to form the polymeric tail of the first charge control agent may further include a hydroxyl group. The monomer used to form the polymeric tail of the first charge control agent may be selected from the group consisting of 8-hydroxystearic acid, ricinoleic acid, linoleic acid, oleic acid, linoleic acid, acid halides of 8-hydroxystearic acid, acid halides of ricinoleic acid, acid halides of linoleic acid, acid halides of linolenic acid, 8-hydroxystearic acid anhydride, ricinoleic acid anhydride, linoleic acid anhydride, oleic acid anhydride, and linolenic acid anhydride.

[0074] The molecular structure of the first charge control agent may include one or more quaternary ammonium groups. The molecular structure of the first charge control agent may include 1 to 12 quaternary ammonium groups. The quaternary ammonium group has the structure [NR1R2R3R4] +and examples of R1, R2, R3 and R4 may include alkyl and aryl groups. The molecular structure of the first charge control agent includes a non-polar tail and at least one quaternary ammonium group. A useful reagent for preparing the first charge control agent is a class of fatty acid quaternary ammonium compounds provided by Akzo Nobel under the trade name ARQUAD™.

[0075] Non-limiting examples of charge control agents that meet the structural criteria of the first charge control agent include commercially available polymeric materials such as Solsperse™ 17000, Solsperse™ 16000 and Solsperse™ 19000 supplied by Lubrizol Corporation. Solsperse™ 17000 is a reaction product of 12-hydroxy-octadecanoic acid homopolymer with N,N-dimethyl-1,3-propanediamine and methyl bisulfate. Solsperse™ 16000 and Solsperse™ 19000 have carbon-carbon bonds in their non-polar tails. When unsaturated quaternary ammonium charge control agents are included in the electrophoretic medium, it has been observed that the medium has improved switching speeds at low temperatures. The non-polar tail of the quaternary ammonium charge control agent can be formed from a polymeric or oligomeric compound, such as a polyester. In some examples, the polyester can be formed by the condensation reaction of a carboxylic acid, such as a fatty acid, with a secondary amine. In such instances, the condensation reaction results in repeat units having at least one carbon-carbon double bond (i.e., unsaturated) with a repeating pendant carbon chain that may be saturated or unsaturated. The overall length of the monomer from which the tail is formed is at least 10 carbon atoms in length, such as 14 carbon atoms in length, for example 18 carbon atoms in length.

[0076] Other compounds that meet the structural criteria of the first charge control agent are disclosed in U.S. Patent Application Publication No. 2020 / 0355978, the entirety of which is incorporated herein by reference. Non-limiting examples of the first charge control agent are provided in the structures of Formulae IV-X below, where R1 is polyricinoleic acid and R2 is polyisobutylene. These compounds can be prepared by reacting a molecule containing a primary amino group (or hydroxyl group) and a tertiary amine with a monomer (e.g., ricinoleic acid or isobutylene), followed by reacting the formed polymer with dimethyl sulfate to quaternize the tertiary amine. The amine reagent can be selected from, for example, 3-(dimethylamino)-1-propylamine, 3-dimethylamino-1-propanol, 1,4-bis(3-aminopropyl)piperazine, and tris(3-aminopropyl)amine. [ka] [ka] [ka]

[0077] The first charge control agent may be added to the electrophoretic medium at a concentration of greater than 0.2 g charge control agent per 100 g electrophoretic particles, or greater than 0.5 g charge control agent per 100 g electrophoretic particles, or greater than 1.0 g charge control agent per 100 g electrophoretic particles. The first charge control agent may be added to the electrophoretic medium at a concentration of greater than 1 g charge control agent per 100 g electrophoretic particles. For example, the ratio of the first charge control agent to electrophoretic particles may be 1:30 (wt / wt), such as 1:25 (wt / wt), such as 1:20 (wt / wt).

[0078] The molecular structure of the second charge control agent includes two or more polar groups and a non-polar tail. The polar groups are selected from the group consisting of amino groups, carboxylic acid groups, phosphonic acid groups, hydroxyl groups, thiol groups, alpha diketone groups, beta diketone groups, ethylene oxide groups, and propylene oxide groups. The amino groups may be primary, secondary, or tertiary. The nitrogen atom of the amino group may be part of a heterocycle that is aromatic or non-aromatic. Non-limiting examples of such heterocycles are acridine, benzimidazole, pyrazole, imidazole, piperazine, pyrazine, pyrimidine, pyrrole, quinazoline, triazine, azaindole, pyridine, bipyridine, indole, piperidine, pyridazine, pyrrolidine, quinoxaline, triazole, azetidine, carbazole, imidazole, imidazoline, indoline, isoindoline, piperidone, pyrazoline, pyrazolidine, aziridine, isoquinoline, purine, pyrazolo[1,5,α]pyrimidine, quinazoline, and derivatives thereof. The alpha diketone group may be part of a ring such as squaric acid and derivatives, or croconic acid and derivatives.

[0079] The non-polar tail of the second charge control agent may include a polymeric group having one or more saturated alkyl functional groups. The non-polar tail of the second charge control agent may include a polymeric group having at least one carbon-carbon double bond. The polymeric group may be formed by a monomer containing at least 10 carbon atoms. The molecular structure of the monomer may include a carboxylic acid, a carboxylic acid anhydride, or a carboxylic acid halide, where the carboxylic acid and the carboxylic acid halide contain 10 to 22 carbon atoms and a carbon-carbon double bond, and the carboxylic acid anhydride contains 20 to 44 carbon atoms and two carbon-carbon double bonds. The molecular structure of the monomer may also include a hydroxyl group. Non-limiting examples of monomers used to form the polymeric tail of the second charge control agent may be selected from the group consisting of ricinoleic acid, linoleic acid, oleic acid, linoleic acid, acid halides of ricinoleic acid, acid halides of linoleic acid, acid halides of linolenic acid, ricinoleic acid anhydride, linoleic acid anhydride, oleic acid anhydride, and linolenic acid anhydride. The second charge control agent may be a brush-like polymer with a long non-polar (hydrophobic) chain attached to two or more polar groups (head groups) via a linking group. The head groups of the second charge control agent may independently interact with and adsorb to the surface of the electrophoretic particle. The presence of multiple head groups may introduce strong adsorption of the second charge control agent onto certain electrophoretic particles. As a result, a first charge control agent with affinity for the particle surface containing the second charge control agent may strongly adsorb onto the particle to modify the zeta potential of the particle. Surface modification of particles (pigments and other particles) is common in many industries. In many cases, this is achieved by modifying the synthesis route of the particle to form a customized particle. This method may be costly and the synthesized product may only be used for a specific system. On the other hand, the method of adjusting the zeta potential of the particle using a combination of two charge control agents can be carried out directly on the composition of the present application itself. Specifically, one or more charge control agents may be added directly before or during the milling of the particle dispersion used to prepare the electrophoretic medium. In other words, commercially available pigment products can be used without the need to pre-synthesize customized pigments.Furthermore, the zeta potential of the particles can be adjusted to the desired level by adjusting the nature and weight ratio of the corresponding charge control agent. Thus, the same pigment can be used for various electrophoretic media, and the particles will have different zeta potentials in each of the media. It should be noted here that when the term adsorption of a polymer (or other material) onto a particle in a liquid carrier is used for a polymer that is soluble in the carrier, it is recognized that there is a dynamic equilibrium of the polymer between the particle surface and the soluble polymer in the carrier. A stronger adsorption of the polymer onto the particle means that the amount of polymer on the particle increases relative to the total amount of polymer present.

[0080] A non-limiting example of a commercially available polymeric material that can be used as the second charge control agent is Solsperse™ 8000 supplied by Lubrizol Corporation.

[0081] The second charge control agent may be formed by a condensation reaction of a hydroxycarboxylic acid (or a hydroxycarboxylic acid derivative) in the presence of a polyamine. The polymerization reaction is a polycondensation between the reagents. The condensation reaction forms (a) an ester bond between a hydroxyl group of the hydroxycarboxylic acid (or a hydroxycarboxylic acid derivative) and a carboxyl group (or a carboxylic acid halide or a carboxylic acid anhydride) of another molecule of the hydroxycarboxylic acid (or a hydroxycarboxylic acid derivative), and (b) an amide bond between an amine group of the polyamine and a carboxyl group (or a carboxylic acid halide or a carboxylic acid anhydride) of the hydroxycarboxylic acid (or a hydroxycarboxylic acid derivative).

[0082] The second charge control agent may be added to the electrophoretic medium at a concentration of greater than 0.2 g charge control agent per 100 g electrophoretic particles, or greater than 0.5 g charge control agent per 100 g electrophoretic particles, or greater than 1.0 g charge control agent per 100 g electrophoretic particles. For example, the ratio of the first charge control agent to electrophoretic particles may be 1:30 (wt / wt), such as 1:25 (wt / wt), such as 1:20 (wt / wt).

[0083] The weight ratio of the second charge control agent to the first charge control agent may be about 1:10 to about 10:1, or about 1:9 to about 10:9, or about 1:8 to about 8:1, or about 1:6 to about 6:1, or about 1:5 to about 5:1, or about 1:3 to about 3:1, or about 1:2 to about 2:1, or about 1:1:5 to 1.5:1.

[0084] Electrophoretic Particles

[0085] In one embodiment, the electrophoretic medium of the present invention comprises four types of particles, a first, a second, a third and a fourth type of particles, the first and fourth types of particles having a first charge polarity, the second and third types of particles having a second polarity, the second polarity being opposite to the first polarity. This represents a type I electrophoretic medium. Typically, such a system comprises negatively charged white type particles, negatively charged yellow type particles, positively charged cyan type particles, and positively charged magenta type particles. Yellow, cyan and magenta represent subtractive primary colors.

[0086] In another embodiment, the electrophoretic medium of the present invention comprises four types of particles, a first, a second, a third and a fourth type of particles, the first type of particles having a first charge polarity and the second, third and fourth type of particles having a second polarity, the second polarity being opposite to the first polarity. This represents a type II electrophoretic medium. Typically, such a system comprises negative white type particles and positively charged type particles having subtractive primary colors yellow, magenta and cyan.

[0087] Furthermore, one or more types of particles (in both Type I and Type II electrophoretic media) may be designed such that their electrophoretic mobility is nonlinear with the strength of the applied electric field. Thus, application of a high electric field (e.g., 20V or higher) of the correct polarity will cause one or more types of particles to have reduced electrophoretic mobility. The various optical states of such a four-particle system (Type I and Type II) are shown diagrammatically in Figure 1. A corresponding display can provide white, yellow, red, magenta, blue, cyan, green, and black color states at each pixel.

[0088] As shown in FIG. 1, each of the eight primary colors (red, green, blue, cyan, magenta, yellow, black, and white) corresponds to a different arrangement of four types of particles such that the viewer sees only the colored particles on the viewing side of the white type particles (i.e., the only type of particle that scatters light). To achieve a wide range of colors, additional voltage levels must be used for finer control of particle types. In the described formulation, the first type of particle is reflective (typically white), and the other three types of particles include three substantially non-light scattering ("SNLS"). As discussed above, the use of SNLS particles allows for color mixing, providing more color results than can be achieved with the same number of scattering type particles. These thresholds must be sufficiently separated to avoid crosstalk, which requires the use of high address voltages for some colors. The disclosed four-particle electrophoretic media can also be updated quickly, requiring transitions that are "less likely to blink," and can produce a spectrum of colors that are pleasing to the viewer (and therefore commercially valuable). Additionally, the disclosed combinations provide rapid (e.g., less than 500 ms, e.g., less than 300 ms, e.g., less than 200 ms, e.g., less than 100 ms) updates between black and white pixels, thereby enabling rapid page turns in black against white text.

[0089] In FIG. 1, the viewing surface of the display is at the top (as shown), i.e., the user views the display from this direction and the light is assumed to be incident from this direction. As mentioned above, in a preferred embodiment, only one of the four types of particles used in the electrophoretic medium of the present invention substantially scatters light, and in FIG. 1, this type of particle is assumed to be a white pigment. This light-scattering white-type particle forms a white reflector against which any particles above the white-type particles are viewed (as shown in FIG. 1). Light entering the viewing surface of the display passes through these types of particles, reflects off the white-type particles, and passes through these types of particles again to exit the display. Thus, the particles above the white-type particles may absorb various colors, and the color seen by the user is the color resulting from the combination of the particles above the white-type particles. Any particles placed below (behind the user's viewpoint) the white-type particles are masked by the white-type particles and do not affect the displayed color. Because the second, third and fourth types of particles are substantially non-light scattering, their order or arrangement relative to each other is not important, but for reasons previously discussed, their order or arrangement relative to the white (light scattering) particles is very important.

[0090] More specifically, when the cyan, magenta and yellow type particles are below the white type particles (situation [A] in FIG. 1), there are no particles above the white type particles and the pixel simply displays white. When a single type of particle is above the white type particles, the color of that single type of particle is displayed, which are yellow, magenta and cyan in situations [B], [D] and [F] in FIG. 1, respectively. When two types of particles are above the white type particles, the color displayed is a combination of the colors of these two types of particles, which are red in situation [C] in FIG. 1, red in situation [E] ...

[0091] A subtractive primary color can be rendered by a type of light scattering particles, such that the display contains two types of light scattering particles, one of which is white and the other is colored. However, in this case, the location of the light scattering colored particles relative to the other colored particles that cover the white particles is important. For example, when rendering black (when all three colored particles are on top of the white particles), the scattering colored particles cannot be on top of the non-scattering colored particles (otherwise they will be partially or completely hidden behind the scattering particles and the color rendered will be the color of the scattering colored particles rather than black).

[0092] FIG. 1 shows the ideal situation where there is no color contamination (i.e., the light scattering white type particles completely mask any type of particle behind the white type particles). In reality, masking by the white type particles may be incomplete, and thus some slight light absorption may occur by particle types that would ideally be completely masked. Such contamination typically reduces both the lightness and saturation of the color being rendered. In the electrophoretic media of the present invention, such color contamination should be minimized to the point where the colors produced meet industry standards for color rendering. A particularly preferred standard is SNAP (Standard for Newspaper Advertising Production), which provides L * , a * and b * In what follows, "primary colors" is used to refer to the eight colors shown in Figure 1: black, white, the three subtractive primaries, and the three additive primaries.

[0093] FIG. 2 shows schematic cross-sectional views of four types of particles of a Type I electrophoretic medium used in the present invention.

[0094] A display layer utilizing the improved electrophoretic medium includes a first (viewing) surface 23 on the viewing side, and a second surface 24 opposite the first surface 23. The electrophoretic medium is disposed between the two surfaces. Each space between two vertical dotted lines represents a pixel. Within each pixel, the electrophoretic medium can be addressed and each pixel's viewing surface 23 can achieve the color states shown in FIG. 1 without the need for additional layers and without a color filter array.

[0095] As is standard for electrophoretic displays, the first surface 23 includes a first light-transmitting electrode layer 21 constructed from a sheet of PET with indium tin oxide (ITO) disposed thereon. On the second surface (24) is a second electrode layer 22 including a plurality of pixel electrodes 25. Such pixel electrodes are described in U.S. Pat. No. 7,046,228, the contents of which are incorporated herein by reference in their entirety. It is noted that although the active matrix driven by a thin film transistor (TFT) backplane is mentioned with respect to a layer of pixel electrodes, the scope of the invention encompasses other types of electrode addresses as long as the electrodes perform the desired function. For example, the first and second electrode layers (or top and bottom electrodes) may be continuous. Additionally, pixel electrode backplanes different from those described in the '228 patent are also suitable and may include active matrix backplanes that can provide higher drive voltages than those typically found with amorphous silicon thin film transistor backplanes.

[0096] Newly developed active matrix backplanes may include thin film transistors incorporating metal oxide materials, such as tungsten oxide, tin oxide, indium oxide, zinc oxide, or more complex metal oxides, such as indium gallium zirconium oxide. In these applications, such metal oxide materials are used to form channel-forming regions for each transistor, allowing for faster switching of higher voltages. Such metal oxide transistors also allow for lower leakage in the "off" state of the thin film transistor (TFT) than can be achieved, for example, with amorphous silicon TFTs. In a typical scanning TFT backplane containing n lines, the transistors are in the "off" state for a period of approximately (n-1) / n fraction of the time required to refresh every line of the display. Any leakage of charge from the storage capacitor associated with each pixel results in degradation of the electro-optical performance of the display. TFTs typically include a gate electrode, a gate insulator (typically SiO2), a metal source electrode, a metal drain electrode, and a metal oxide semiconductor film on the gate insulator that at least partially covers the gate electrode, the source electrode, and the drain electrode. Such backplanes are available from manufacturers such as Sharp / Foxconn, LG, and BOE. Such backplanes may provide drive voltages of ±30V (or greater). In some embodiments, mid-voltage drivers are included so that the resulting drive waveform may include five levels, or seven levels, or nine levels, or more levels.

[0097] One preferred metal oxide for such applications is indium gallium zinc oxide (IGZO). IGZO-TFTs have an electron mobility 20-50 times that of amorphous silicon. By using IGZO TFTs in an active matrix backplane, it is possible to provide voltages in excess of 30V via a suitable display driver. Furthermore, a source driver capable of providing at least five, and preferably seven, levels provides different driving paradigms for a four-particle electrophoretic display system. In one embodiment, there are two positive voltages, two negative voltages, and zero volts. In another embodiment, there are three positive voltages, three negative voltages, and zero volts. In one embodiment, there are four positive voltages, four negative voltages, and zero volts. These levels may be selected within the range of approximately -27V to +27V, without the limitations imposed by the top plane switching discussed above.

[0098] The electrophoretic display of Figure 2 comprises a Type I electrophoretic medium of the present invention. It contains four types of electrophoretic particles in a non-polar fluid 27. The first type of particles (W- * ; open circles) have a negative charge and may be surface treated such that the electrophoretic mobility of the first type of particle depends on the strength of the driving electric field (discussed in detail below). In such an example, the electrophoretic mobility of this type of particle actually decreases in the presence of a stronger electric field, which is somewhat counterintuitive.

[0099] The second type of particles (C++; grey circles) may have a higher positive charge than the third type of particles. It may have a surface treatment. As shown in FIG. 2, the colors of this type of particles are nominally white, magenta, yellow, and cyan, producing the colors shown in FIG. 1. However, the invention is not limited to this particular set of colors, nor is it limited to one reflective particle and three absorbing particles. For example, the system may include one black absorbing particle and three reflective particles of red, yellow, and blue with appropriately matched reflectance spectra, producing a process white state when all three reflective particles are mixed and observable on the surface.

[0100] The third type of particle (M+ * ; dark circles) have a positive charge and may be surface treated (or may be intentionally untreated) such that the electrophoretic mobility of the third type of particle depends on the strength of the driving electric field, or the release rate of the population of second and third types of particles after being driven to one side of the void containing that type of particle upon reversal of the electric field direction is slower than the release rate of the population of second type of particles.

[0101] The fourth type of particles (Y-; checkered circles) have a negative charge. It may have a higher or lower charge magnitude than the first type of particles. Furthermore, the fourth type of particles may be surface treated. The electrophoretic mobility of the fourth type of particles may or may not depend on the strength of the driving electric field. That is, the fourth type of particles may have a surface treatment, but such a surface treatment may not result in the above-mentioned reduction in electrophoretic mobility with increasing electric field.

[0102] Figure 3A shows a schematic cross-sectional view of four types of particles of type II electrophoretic medium used in the present invention. The display shown in Figure 3A is similar to the display shown in Figure 2, but has a different electrophoretic medium (type II in Figure 3A versus type I in Figure 2).

[0103] The type II electrophoretic medium of the present invention contains four types of electrophoretic particles in a non-polar fluid 27, as shown in Figures 3A to 3E. * ; open circles) have a negative charge and may be surface treated such that the electrophoretic mobility of the first type of particle depends on the strength of the driving electric field (discussed in detail below). In such an example, the electrophoretic mobility of this type of particle actually decreases in the presence of a stronger electric field, which is somewhat counterintuitive.

[0104] The second type of particles (C+++; grey circles) have the highest magnitude of positive charge and have the same type of surface treatment as the third and fourth types of particles. As shown in FIG. 3A, the colors of this type of particles are nominally white, magenta, yellow, and cyan, producing the colors shown in FIG. 1. However, the invention is not limited to this particular set of colors, nor is it limited to one reflective particle and three absorbing particles. For example, the system may include one black absorbing particle and three reflective particles of red, yellow, and blue with appropriately matched reflectance spectra, producing a process white state when all three reflective particles are mixed and observable on the surface.

[0105] The third type of particle (M++ * ; dark circles) have a positive charge and may be surface treated (or may be intentionally untreated) such that the electrophoretic mobility of the third type of particle depends on the strength of the driving electric field, or the release rate of the third population of particles after being driven to one side of the void containing that type of particle upon reversal of the electric field direction is slower than the release rates of the second and fourth populations of particles.

[0106] The fourth type of particles (Y+; checkered circles) are positive, but have a smaller charge magnitude than the third type of particles. Additionally, the fourth type of particles may be surface treated, but not in such a manner that the electrophoretic mobility of the fourth type of particles is dependent on the strength of the driving electric field. That is, the fourth type of particles may have a surface treatment, but such surface treatment does not result in the aforementioned decrease in electrophoretic mobility with increasing electric field.

[0107] 3B-3E show schematic cross-sectional views of different optical states of a display pixel having four types of particles (type II) used in the present invention.

[0108] In one embodiment, the first type of particles (negative) are white and scattering. The second type of particles (positive, high charge magnitude) are cyan and absorbing. The third type of particles (positive, medium charge magnitude) are magenta and absorbing. The fourth type of particles (positive, low charge magnitude) are yellow and absorbing. In another embodiment, the first type of particles (negative) are white and scattering. The second type of particles (positive, high charge magnitude) are cyan and absorbing. The third type of particles (positive, medium charge magnitude) are magenta and absorbing. The fourth type of particles (negative) are yellow and absorbing. Table 1 below shows the diffuse reflectance according to Kubelka-Munk analysis of exemplary yellow, magenta, cyan and white particles useful in the electrophoretic media of the present invention when dispersed in a poly(isobutylene) matrix for these materials, along with the ratio of their extinction and scattering coefficients.

[0109] [Table 1]

[0110] The electrophoretic medium of the present invention may be in any of the forms discussed above. Thus, the electrophoretic medium may be unencapsulated, encapsulated in individual capsules surrounded by capsule walls, encapsulated in sealed microcells, or in the form of a polymer dispersion medium. Pigments are described in detail elsewhere, for example in U.S. Pat. Nos. 9,697,778 and 9,921,451. Briefly, white-type particles W1 are silanol-functionalized light-scattering pigments (titanium dioxide) to which is attached a polymeric material comprising lauryl methacrylate (LMA) monomer as described in U.S. Pat. No. 7,002,728. White-type particles W2 are polymer-coated titania produced substantially as described in Example 1 of U.S. Pat. No. 5,852,196, the polymeric coating comprising lauryl methacrylate and 2,2,2-trifluoroethyl methacrylate in a ratio of about 99:1. Yellow type particles Y1 are CI Pigment Yellow 180, used without coating and dispersed by milling in the presence of Solsperse ™ 19000, as outlined in US Patent No. 9,697,778. Yellow type particles Y2 are CI Pigment Yellow 155, used without coating and dispersed by milling in the presence of Solsperse ™ 19000, as outlined in US Patent No. 9,697,778. Yellow type particles Y3 are CI Pigment Yellow 139, used without coating and dispersed by milling in the presence of Solsperse ™ 19000, as outlined in US Patent No. 9,697,778. Yellow type particles Y4 are CI Pigment Yellow 139 coated by dispersion polymerization and incorporating trifluoroethyl methacrylate, methyl methacrylate and dimethylsiloxane containing monomers as described in Example 4 of US Pat. No. 9,921,451.Magenta type particles M1 are positively charged magenta material (dimethylquinacridone, CI Pigment Red 122) coated using vinylbenzyl chloride and LMA as described in Example 5 of U.S. Pat. Nos. 9,697,778 and 9,921,451.

[0111] Magenta type particles M2 are CI Pigment Red 122 coated with dispersion polymerization, methyl methacrylate and dimethylsiloxane containing monomers as described in Example 6 of US Pat. No. 9,921,451. Cyan type particles C1 are copper phthalocyanine material (CI Pigment Blue 15:3) coated with dispersion polymerization and incorporating methyl methacrylate and dimethylsiloxane containing monomers as described in Example 7 of US Pat. No. 9,921,451. In some embodiments, it has been found that the color gamut is improved by using Inkjet Yellow 4GC (Clariant) as the core yellow pigment and incorporating a methyl methacrylate surface polymer. The zeta potential of this yellow pigment can be adjusted by adding 2,2,2-trifluoroethyl methacrylate (TFEM) monomer and monomethacrylate terminated poly(dimethylsiloxane).

[0112] Electrophoretic media additives and surface treatments to promote electrophoretic mobility differences, as well as proposed mechanisms of interaction between the surface treatment and surrounding charge control agents and / or free polymers, are discussed in detail in U.S. Patent No. 9,697,778, which is incorporated by reference in its entirety. In such electrophoretic media, one approach to control interactions between various types of particles is by controlling the type, amount and thickness of polymer coatings on the particles. For example, to control particle properties such that particle-particle interactions are smaller between the second type of particles and the third and fourth types of particles than between the third type of particles of the third species and the fourth type of particles, for example, the second type of particles may have a polymer surface treatment, while the third and fourth types of particles may have no polymer surface treatment or a polymer surface treatment with a lower mass coverage per unit area of ​​particle surface than the second type of particles. More generally, the Hammerker constant (a measure of the strength of the van der Waals interactions between two particles; the pair potential is proportional to the Hammerker constant and inversely proportional to the sixth power of the distance between the two particles) and / or the interparticle spacing needs to be adjusted by judicious selection of the polymer coating(s) on the three particles.

[0113] As discussed in US Pat. No. 9,921,451, different types of polymers may include different types of polymer surface treatments. For example, Coulombic interactions may be weak when the closest distance of particles with opposite charges is maximized by steric hindrance (typically polymers grafted or adsorbed to the surface of one or both particles). The polymer shell may be a covalently bonded polymer made by grafting processes or chemisorption as known in the art, or may be physically adsorbed onto the particle surface. For example, the polymer may be a block copolymer containing insoluble and soluble segments. Alternatively, the polymer shell may be dynamic in that it is a loose network of free polymer from the electrophoretic medium complexed with the pigment particle in the presence of an electric field and a sufficient amount and type of charge control agent (CCA - discussed below). Thus, depending on the strength and polarity of the electric field, the particle may have more associated polymer, which causes the particle to interact differentially with the container (e.g., microcapsule or microcell) and other particles. The extent of the polymer shell is conveniently assessed by thermogravimetric analysis (TGA), a technique in which the temperature of a dried sample of the particle is increased and the mass loss due to thermal decomposition is measured as a function of temperature. Using TGA, the percentage of the mass of the particle that is polymer can be measured, which can be converted to a volume fraction using the known densities of the core pigment and the polymer attached to it. Conditions can be found under which the polymer coating is lost but the core pigment remains (these conditions depend on the exact core pigment particle used). Various combinations of polymers can be made to act as described below with respect to Figures 3B-3E. For example, in some embodiments, the particles (typically the first and / or second particles) may have a covalently attached polymer shell that interacts strongly with the container (e.g., microcell or microcapsule), while other particles of the same charge either do not have a polymer coating or are complexed with free polymer in the solution, and therefore those particles have little interaction with the container.In other embodiments, the particles (typically the first and / or second particles) do not have a surface coating, and therefore the particles more readily form a charge double layer and have reduced electrophoretic mobility in the presence of strong fields.

[0114] The fluid 27 in which the four types of particles are dispersed is clear and colorless. The fluid contains charged electrophoretic particles that move through the fluid under the influence of an electric field. A preferred suspending fluid has a low dielectric constant (about 2), a high volume resistivity (about 10 15 They have a low viscosity (<5 mPas), low toxicity and environmental impact, low water solubility (<10 parts per million (ppm) if traditional aqueous encapsulation methods are used; note however that this requirement may be relaxed for non-encapsulated or certain microcell displays), a high boiling point (above about 90° C.), and a low refractive index (<1.5). The last requirement is due to the use of high refractive index scattering (typically white) pigments, whose scattering efficiency depends on the refractive index mismatch between the particle and the fluid.

[0115] Organic solvents such as saturated linear or branched hydrocarbons, silicone oils, halogenated organic solvents, and low molecular weight halogen-containing polymers are some useful fluids. The fluid may contain a single component or may be a blend of more than one component to tailor its chemical and physical properties. Reactants for the microencapsulation process, such as oil-soluble monomers or solvents (if used), may also be contained in the fluid.

[0116] The fluid preferably has a low viscosity and a dielectric constant in the range of about 2 to about 30, preferably about 2 to about 15, for high particle mobility. Examples of suitable dielectric fluids are hydrocarbons such as Isopar®, decahydronaphthalene (DECALIN), 5-ethylidene-2-norbornene, fatty oils, paraffin oils, silicone fluids, aromatic hydrocarbons such as toluene, xylene, phenylxylylethane, dodecylbenzene or alkylnaphthalenes, halogenated solvents such as perfluorodecalin, perfluorotoluene, perfluoroxylene, dichlorobenzotrifluoride, 3,4,5-trichlorobenzotrifluoride, chloropentafluoro-benzene, dichlorononane or pentachlorobenzene, and perfluorinated solvents such as FC-43, FC-70 or FC-5060 from 3M Company, St. Paul, Minn., low molecular weight halogen-containing polymers such as poly(perfluoropropylene oxide) from TCI America, Portland, Oregon, poly(chlorotrifluoro-ethylene) such as Halocarbon Product Corp., River Halocarbon oils from Edge, NJ; perfluoropolyalkyl ethers such as Galden from Ausimont or the Krytox oils and greases K-Fluid series from DuPont, Delaware; polydimethylsiloxane-based silicone oil (DC-200) from Dow-corning.

[0117] As described in US Patent No. 7,170,670, the bistability of the electrophoretic medium can be improved by including in the fluid a polymer with a number average molecular weight of more than about 20,000, which is essentially non-absorbing on the electrophoretic particles; poly(isobutylene) or polydimethylsiloxane can be used for this purpose. Furthermore, as described, for example, in US Patent No. 6,693,620, a particle with a fixed charge on its surface builds up an electric double layer of opposite charge in the surrounding fluid. The ionic head groups of the CCA can ion-pair with the charged groups on the electrophoretic particle surface, forming a layer of fixed or partially fixed charged species. Outside of this layer, there is a diffusion layer that contains charged (reverse) micelles containing CCA molecules in the medium. In conventional DC electrophoresis, the applied electric field exerts a force on the fixed surface charge and an opposing force on the mobile counter charge, resulting in slippage within the diffusion layer and the particle moving relative to the fluid. The electric potential at the slip surface is known as the zeta potential.

[0118] As a result, some of the particle types in the electrophoretic medium have different electrophoretic mobilities depending on the strength of the electric field across the electrophoretic medium. For example, when a first (low strength, i.e., about ±10V or less) electric field is applied to the electrophoretic medium, the first type of particle moves in a first direction relative to the electric field, but when a second (high strength, i.e., about ±20V or more) electric field is applied, the first type of particle begins to move in the opposite direction relative to the electric field, even though it has the same polarity as the first electric field. This behavior is theorized to result from conduction in highly non-polar fluids being mediated by charged inverse micelles or electrophoretic particles with opposite charges. Thus, any electrochemically generated protons (or other ions) are transported through the non-polar fluid, presumably within the micelle core, or adsorbed onto the electrophoretic particles. For example, as shown in FIG. 5B of US Pat. No. 9,697,778, a positively charged reverse micelle can approach a negative electrophoretic particle moving in the opposite direction, and the reverse micelle can be incorporated into an electric double layer around the negatively charged particle. The electric double layer includes both a diffuse layer of charge with increased counterion concentration, and a semimicellar surface adsorbed coating on the particle, in the latter case the reverse micelle charge associates with the particle in a slip envelope that defines the zeta potential of the particle as described above. Through this mechanism, an electrochemical flow of positively charged ions flows through the electrophoretic fluid, and the negatively charged particle can be biased toward a more positive charge. As a result, the electrophoretic mobility of, for example, a first negatively charged particle is a function of the magnitude of the electrochemical flow and the residence time of the positive charge close to the particle surface, which residence time is a function of the strength of the electric field.

[0119] Additionally, positively charged particles can be prepared that may also exhibit different electrophoretic mobilities depending on the applied electric field, as also described in U.S. Patent No. 9,697,778. In the present invention, a combination of charge control agents can be used in the electrophoretic medium to adjust the zeta potential of various particles.

[0120] In some embodiments, a portion of the charge control agent intended for the final formulation is added during synthesis of the electrophoretic particles to engineer the desired zeta potential and affect the reduction in electrophoretic mobility due to strong electric fields. For example, it has been observed that adding a charge control agent during polymer grafting causes a certain amount of CCA to complex to the particles. This can be confirmed by removing the particles from the electrophoretic medium and then stripping the surface species from the pigment with THF to remove all adsorbed species. When the THF extract is evaluated by 1H NMR, it is clear that a significant amount of CCA has adsorbed to the pigment particles or complexed with the surface polymer. Experiments suggest that high CCA loading in the surface polymer of the particles promotes the formation of a charge double layer around the particles in the presence of a strong electric field. For example, magenta particles with more than 200 mg of charge control agent (CCA) per gram of final magenta particles have excellent retention properties in the presence of a high positive electric field. (See, for example, FIG. 3C and the discussion above.)

[0121] Table 2 shows exemplary relative zeta potentials for three types of colored particles and a single white particle in a preferred embodiment.

[0122] [Table 2]

[0123] In one embodiment, the negative (white) particles have a zeta potential of -30mV, and the remaining three particles are all positive relative to the white particles. Thus, a display containing positive cyan, magenta, and yellow particles can switch between a black state (all colored particles are in front of the white particles relative to the viewing surface) and a white state in which the white particles are closest to the observer and block the observer from perceiving the remaining three particles. In contrast, if the white particles have a zeta potential of 0V, the negatively charged yellow particles are the most negative of all the particles, and thus a display containing this particle will switch between a yellow and a blue state. This would also occur if the white particles had a positive charge. However, the positively charged yellow particles will be more positive than the white particles unless their zeta potential exceeds +20mV.

[0124] The behavior of the electrophoretic medium of the present invention is consistent with the mobility of the white particles depending on the applied electric field (represented as zeta potential in Table 2). Thus, in the example shown in Table 2, when addressed at a low voltage, the white particles may behave as if their zeta potential were -30 mV, but when addressed at a higher voltage, they may behave as if their zeta potential were more positive, possibly as high as +20 mV (matching the zeta potential of the yellow particles). Thus, when addressed at a low voltage, the display switches between black and white states, but when addressed at a higher voltage, it switches between blue and yellow states.

[0125] The motion of various particles in the presence of high (e.g. "±H", e.g. ±20V, e.g. ±25V) and low (e.g. "±L", e.g. ±5V, e.g. ±10V) electric fields is shown in Figures 3B-3E. For illustrative purposes, each box defined by dashed lines represents a pixel defined by a first light-transmissive electrode layer 21 (front electrode) and a second electrode layer 22 (back electrode), which may comprise a pixel electrode of the active matrix, but which may also be a light-transmissive electrode, or a split electrode, etc. Starting from a first state (nominally black) in which all of the positive particles are present at the viewing surface, the electrophoretic medium can be driven into four different optical states as shown in Figures 3B-3E. In a preferred embodiment, this results in a white optical state (Figure 3B), a magenta optical state (Figure 3C), a yellow optical state (Figure 3D), and a red optical state (Figure 3E). It will be apparent that the remaining four optical states of FIG. 1 can be achieved by reversing the sequence of the initial states and the driving electric fields, as shown diagrammatically in FIG.

[0126] When addressed with a low voltage, as in FIG. 3B, the particles behave according to their relative zeta potentials with relative velocities indicated by the arrows when a negative voltage is applied to the backplane. Thus, in this example, the cyan particles move faster than the magenta particles, which move faster than the yellow particles. The first (positive) pulse does not change the particle position because the particles are already constrained by the enclosure walls. The second (negative) pulse swaps the positions of the colored and white particles, so that the display switches between black and white states, but with a transitional color reflecting the relative mobility of the colored particles. Reversing the starting position and polarity of the pulse allows a white to black transition. Thus, this embodiment provides a black-white update that requires lower voltages (and consumes less power) compared to other black-white combinations achieved with multiple colors by process black or process white.

[0127] In FIG. 3C, the first (positive) pulse is of sufficiently high positive voltage to reduce the mobility of the magenta particles (i.e., intermediate mobility particles among the three positively charged colored particles). Due to their reduced mobility, the magenta particles are essentially fixed in place, and a subsequent lower voltage, opposite direction pulse moves the cyan, white and yellow particles further than the magenta particles, thereby producing a magenta color at the viewing surface, with the negative white particles behind the magenta particles. Importantly, if the starting position and polarity of the pulses are reversed (equivalent to viewing the display from the opposite side of the viewing surface, i.e., through the second electrode layer 22), this pulse sequence produces a green color (i.e., a mix of yellow and cyan particles).

[0128] In FIG. 3D, the first pulse is a low voltage pulse that does not significantly reduce the mobility of the magenta or white particles. However, the second pulse is a high negative voltage pulse that reduces the mobility of the white particles. This allows a more effective competition between the three positive particles, so that the slowest type of particle (yellow in this example) remains visible before the white particles whose mobility has been reduced by the previous negative pulse. In particular, the yellow particles do not reach the upper surface of the particle-containing cavity. Importantly, if the starting position and polarity of the pulses are reversed (equivalent to viewing the display from the opposite side of the viewing surface, i.e. through the second electrode layer 22), this pulse sequence produces a blue color (i.e. a mix of magenta and cyan particles).

[0129] Finally, Figure 3E shows that when both pulses are high voltage pulses, the mobility of the magenta particles is reduced by the first highly positive pulse, and the reduction in white mobility caused by the second highly negative pulse enhances the competition between cyan and yellow, thereby producing the color red. Importantly, if the starting position and polarity of the pulses are reversed (equivalent to viewing the display from the opposite side of the viewing surface, i.e. through the second electrode layer 22), this pulse sequence produces the color cyan.

[0130] To obtain a high resolution display, each pixel of the display must be addressable without interference from adjacent pixels. One approach to achieving this objective is to provide an array of nonlinear elements, such as transistors or diodes, with at least one nonlinear element associated with each pixel, producing an "active matrix" display. An address electrode or pixel electrode, which addresses a pixel, is connected to an appropriate voltage source through the associated nonlinear element. Typically, where the nonlinear element is a transistor, the pixel electrode is connected to the drain of the transistor, and this arrangement will be assumed in the following description, but this is essentially arbitrary and the pixel electrode may be connected to the source of the transistor. Conventionally, in high resolution arrays, the pixels are arranged as a two-dimensional array of rows and columns, such that any particular pixel is uniquely defined at the intersection of one designated row and one designated column. The sources of all the transistors in each column are connected to a single column electrode, while the gates of all the transistors in each row are connected to a single row electrode. Again, the source-to-row and gate-to-column designations are conventional but essentially arbitrary, and may be reversed if desired. The row electrodes are connected to row drivers, which essentially ensure that at a given moment only one row is selected, i.e. a selected voltage is applied to the selected row electrode, e.g. to ensure that all transistors in the selected row are conductive, while a non-select voltage is applied to all other rows, e.g. to ensure that all transistors in the unselected rows remain non-conductive. The column electrodes are connected to column drivers, which apply voltages to the various column electrodes selected to drive the pixels in the selected row to the desired optical state. The voltages mentioned above are relative to a common front electrode (first light-transmissive electrode layer), which is conventionally provided on the opposite side of the electro-optic medium from the non-linear array and extends across the display. After a preselected interval, known as the "line address time", the selected row is deselected, the next row is selected, and the voltages to the column drivers are changed so that the next line of the display is written.This process is repeated until the entire display is written row by row.

[0131] Conventionally, each pixel electrode is associated with a capacitor electrode, such that the pixel electrode and the capacitor electrode form a capacitor. For example, see International Patent Application WO01 / 07961. In some embodiments, an N-type semiconductor (e.g., amorphous silicon) may be used to form a transistor, and the "select" and "unselect" voltages applied to the gate electrode may be positive and negative, respectively.

[0132] FIG. 5 of the accompanying drawings shows an exemplary equivalent circuit of a single pixel of an electrophoretic display. As shown, the circuit includes a capacitor 10 formed between a pixel electrode and a capacitor electrode. An electrophoretic medium 20 is represented as a parallel capacitor and resistor. In some examples, a direct or indirect coupling capacitance 30 (usually referred to as "parasitic capacitance") between the gate electrode of a transistor associated with a pixel and the pixel electrode may create undesirable noise in the display. Typically, the parasitic capacitance 30 is much smaller than the capacitance of the storage capacitor 10, and when a pixel row of the display is selected or deselected, the parasitic capacitance 30 may result in a slight negative offset voltage, also known as a "kickback voltage", on the pixel electrode, which is typically less than 2 volts. In some embodiments, to compensate for the undesirable "kickback voltage", a common potential V com may be provided, so that V com is the kickback voltage (V KB ), any voltage supplied to the display can be offset by the same amount and no net DC imbalance is experienced.

[0133] However, V comProblems can arise if V is set to a voltage that is not compensated for kickback voltage. This can occur when it is desired to apply a higher voltage to the display than is available from the backplane alone. In the art, it is often said that the maximum voltage applied to a display is, for example, V com It is well known that this can be doubled if the top plane is supplied with -V while the backplane is selectively supplied with, for example, nominally +V, 0, or -V. In this case the maximum voltage experienced is +2V (i.e. at the backplane relative to the top plane), while the minimum is zero. If a negative voltage is required, V com The potential must be raised to at least zero. Thus, the waveforms used to address displays with positive and negative voltages using top-plane switching must have more than one V com Each voltage setting must have a specific frame assigned to it.

[0134] A set of waveforms for driving a color electrophoretic display having four particles is described in U.S. Pat. No. 9,921,451, which is incorporated herein by reference. In U.S. Pat. No. 9,921,451, seven different voltages are applied to the pixel electrodes: three positive voltages, three negative voltages, and zero. However, in some embodiments, the maximum voltages used in these waveforms are higher than can be accommodated by amorphous silicon thin film transistors. In such instances, suitable high voltages can be obtained by the use of top-plane switching. (As discussed above) V com Intentionally V KB If the V com Using as many separate power supplies as there are setups is costly and inconvenient, and topplane switching is known to increase kickback, thereby reducing color state stability.

[0135] Display devices can be constructed using the electrophoretic medium of the present invention in several ways known in the art. The electrophoretic medium may be encapsulated in microcapsules or incorporated into a microcell structure that is then sealed with a polymer layer. The microcapsule or microcell layer can be coated or embossed onto a plastic substrate or film with a transparent coating of an electrically conductive material. This assembly can be laminated to a backplane with pixel electrodes using an electrically conductive adhesive. Alternatively, the electrophoretic medium can be dispensed directly onto a thin open cell grid placed on a backplane containing the active matrix of pixel electrodes. The filled grid can then be top sealed with an integrated protective sheet / light-transparent electrode.

[0136] FIG. 6 shows a schematic cross-sectional view (not to scale) of a display structure 600 suitable for use according to the invention. In display 600, the electrophoretic medium is shown confined in microcells, although equivalent structures incorporating microcapsules may also be used. Substrate 602, which may be glass or plastic, has a second electrode layer with pixel electrodes 604 that are individually addressed segments or associated with thin film transistors in an active matrix arrangement. The combination of substrate 602 and second electrode layer with pixel electrodes 604 is conventionally referred to as the backplane of the display. Layer 606 is an optional dielectric layer according to the invention that is applied to the backplane. Methods for depositing suitable dielectric layers are described in U.S. Patent Application Serial No. 16 / 862,750, which is incorporated by reference. The front surface of the display comprises a transparent substrate 622 having a first light-transmitting electrode layer 620, which may be formed by an electrically conductive coating. Overlying the first light-transmitting layer 620 is an optional dielectric layer 618. Layer(s) 616 is a polymer layer that may include a primer layer for adhesion of the microcell to the first light-transmitting electrode layer 620, and some residual polymer including the bottom of the microcell. The walls of the microcell 612 are used to contain the electrophoretic medium 614. The microcell is sealed with a sealing layer 610, and the entire front structure may be attached to a backplane using an electrically conductive adhesive layer 608. Processes for forming microcells are described in the prior art, for example in U.S. Pat. No. 6,930,818. In some examples, the microcell is less than 20 μm deep, for example less than 15 μm deep, for example less than 12 μm deep, for example about 10 μm deep, for example about 8 μm deep.

[0137] Most commercial electrophoretic displays use amorphous silicon-based thin film transistors (TFTs) in the construction of the active matrix backplane due to the wider availability of manufacturing facilities and the cost of various starting materials. Unfortunately, amorphous silicon thin film transistors are unstable when supplied with gate voltages that allow switching voltages higher than about + / -15V. Nevertheless, as described below, the performance of ACeP is improved when the magnitude of high positive and negative voltages is allowed to exceed + / -15V. Thus, as explained in the previous disclosure, improved performance is achieved by further varying the bias of the first light-transmitting electrode relative to the bias on the backplane pixel electrodes (also known as top-plane switching). Thus, if a voltage of +30V (relative to the backplane) is required, the appropriate backplane pixels can be switched to +15V while the top plane can be switched to -15V. Methods for driving four-particle electrophoretic systems by top-plane switching are described in more detail, for example, in U.S. Pat. No. 9,921,451.

[0138] These waveforms are illustrated with each pixel of the display as 30V, 15V, 0, -15V and -30V. 高 , +V 低 , 0, -V 低 and -V 高 It is necessary that the pixel can be driven with five different address voltages, specified by +V 高 , 0 and -V 高 ) is available, the voltage V 高 By addressing the pulse with 1 / n duty cycle, a lower voltage (e.g. V 高 / n, where n is a positive integer greater than 1), the same results may be achievable.

[0139] FIG. 4 shows typical waveforms (in simplified form) used to drive the four-particle color electrophoretic display system described above. Such waveforms have a "push-pull" structure, i.e., they consist of a dipole containing two pulses of opposite polarity. The magnitude and length of these pulses dictate the resulting color. At a minimum, there should be five such voltage levels. FIG. 4 shows high and low positive and negative voltages, as well as zero volts. Typically, "low" (L) refers to a range of about 5-15V, while "high" (H) refers to a range of about 15-30V. In general, the higher the magnitude of the "high" voltage, the better the color gamut achieved by the display. In some embodiments, a "medium" (M) level is also used, which is typically about 15V, although the value of M depends somewhat on the composition of the particles, and the environment of the electrophoretic medium.

[0140] Figure 4 shows the simplest dipoles needed to form colors, but the actual waveform may be multiple repetitions of these patterns, or other patterns that are aperiodic and use more than five voltage levels.

[0141] Of course, achieving a desired color with the drive pulses of FIG. 4 depends on the particles starting the process from a known state, which is unlikely to be the final color displayed on the pixel. Thus, a series of reset pulses precede the drive pulse, which increases the amount of time required to update the pixel from a first color to a second color. Reset pulses are described in detail in U.S. Pat. No. 10,593,272, which is incorporated by reference. The lengths of these pulses (refresh and address), as well as the lengths of any pauses (i.e., periods of zero voltage between them), may be selected such that the entire waveform (i.e., the integral of voltage with respect to time over the entire waveform) is DC balanced (i.e., the integral of voltage over time is substantially zero). DC balance may be achieved by adjusting the length of the pulses and pauses in the reset phase such that the net impulse delivered in the reset phase relative to the net impulse delivered in the address phase is equal in magnitude and opposite in sign (during the address phase, the display is switched to a particular desired color). However, as shown in FIGS. 3B-3E, the starting states of the eight primary colors are black or white states, which may be achieved by sustained low voltage drive pulses. The simplicity of achieving this starting state further reduces the update time between states, which is more comfortable for the user, and also reduces power consumption (thus increasing battery life).

[0142] Furthermore, the above waveform discussion, and especially the DC balance discussion, ignores the issue of kickback voltage. In reality, as mentioned above, any backplane voltage will vary from the voltage provided by the power supply by a kickback voltage V KB Therefore, if the power supply used provides three voltages, +V, 0, and -V, the backplane will actually see a voltage of V+V KB , V KB and -V+V KB (V for amorphous silicon TFTs) KB(Note that V is typically a negative number.) However, the same power supply will provide +V, 0 and -V to the first electrode (front electrode) without any kickback voltage cancellation. So, for example, if the first electrode (front electrode) is provided with -V, the display will provide 2V +V KB Maximum voltage and V KB The first electrode (front electrode) receives a minimum voltage of V KB Instead of using a separate power supply to supply V (which can be expensive and inconvenient), the waveform is split into sections and supplies a positive voltage, a negative voltage and V to the first electrode (front electrode). KB may be provided.

[0143] Microcell electrophoretic display

[0144] As shown in FIG. 6, a typical microcell electrophoretic display includes a first light-transmissive electrode layer, a microcell layer including a plurality of microcells, and a second electrode layer including a pixel electrode. Each of the plurality of microcells has an opening. The plurality of microcells includes an electrophoretic medium. The sealing layer spans the openings of the plurality of microcells. The sealing layer may be formed by an aqueous sealing composition. As described in U.S. Patent Application Serial No. 18 / 055,072, filed on November 14, 2022, the aqueous sealing composition affects the volume resistivity of the sealing layer. This reference is incorporated herein by reference in its entirety. Specifically, it has been found that an aqueous sealing composition including a water-soluble ether reduces the volume resistivity of the sealing layer and affects display performance. The water-soluble ether may have a weight average molecular weight of 75 to 5,000 Daltons. The water-soluble ether may be represented by Formula I, Formula II, or Formula III shown above. Water-soluble ethers include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol mono-n-propyl ether, ethylene glycol monoisopropyl ether, ethylene glycol n-monobutyl ether, ethylene glycol monoisobutyl ether, ethylene glycol mono-t-butyl ether, ethylene glycol monobenzyl ether, ethylene glycol monophenyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, ethylene glycol di-n-propyl ether, ethylene glycol diisopropyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol mono-n-propyl ether, diethylene glycol monoisopropyl ether, diethylene glycol n-monobutyl ether, diethylene glycol monoisobutyl ether, diethylene glycol mono-t-butyl ether, diethylene glycol monobenzyl ether, diethylene glycol monophenyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol ethyl methyl ether, diethylene glycol di-n-propyl ether, diethylene glycol diisopropyl ether,Diethylene glycol di-n-butyl, triethylene glycol monomethyl ether, triethylene glycol monoethyl ether, triethylene glycol mono-n-propyl ether, triethylene glycol monoisopropyl ether, triethylene glycol n-monobutyl ether, triethylene glycol monoisobutyl ether, triethylene glycol mono-t-butyl ether, triethylene glycol monobenzyl ether, triethylene glycol monophenyl ether, triethylene glycol dimethyl ether, triethylene glycol diethyl ether, triethylene glycol di-n-propyl ether, triethylene glycol diisopropyl ether, tetraethylene glycol monomethyl ether, tetraethylene glycol monoethyl ether, triethylene glycol monophenyl ether, tetraethylene glycol dimethyl ether, polyethylene glycol monomethyl ether, polyethylene glycol monoethyl ether, polyethylene glycol monophenyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether ter, propylene glycol mono-n-propyl ether, propylene glycol monoisopropyl ether, propylene glycol mono-n-butyl ether, propylene glycol monoisobutyl ether, propylene glycol monophenyl ether, propylene glycol dimethyl ether, propylene glycol diethyl ether, dipropylene glycol monomethyl ether, dipropylene glycol monoethyl ether, dipropylene glycol mono-n-propyl ether, dipropylene glycol monoisopropyl ether, dipropylene glycol mono-n-butyl ether, dipropylene glycol monoisobutyl ether, dipropylene glycol dimethyl ether, dipropylene glycol diethyl ether, dipropylene glycol di-n-propyl ether, dipropylene glycol diisopropyl ether, tripropylene glycol monomethyl ether, tripropylene glycol monoethyl ether, tripropylene glycol mono-n-propyl ether, tripropylene glycol monoisopropyl ether, tripropylene glycol mono-n-butyl ether,The water-soluble ether may be selected from the group consisting of tripropylene glycol monoisobutyl ether, tripropylene glycol monoisobutyl ether, and mixtures thereof. The aqueous sealing composition may contain the water-soluble ether in an amount of 1.0% by weight to 40% by weight of the aqueous sealing composition excluding water. The sealing layer may contain the water-soluble ether in an amount of 0.5% by weight to 25% by weight of the sealing film. The water-soluble ether may contain a hydroxyl group as required.

[0145] The present inventors have observed that the inclusion of a water-soluble ether in the electrophoretic medium improves the color gamut achievable by the electro-optical performance of a display, as demonstrated in the Examples section below. EXAMPLES

[0146] Example 1 Preparation of white particle dispersion.

[0147] Dispersions of titanium dioxide pigment were prepared as described in U.S. Patent No. 7,002,728, which involves silanization of titanium dioxide particles followed by covalent attachment of poly(lauryl methacrylate) to the silanized pigment.

[0148] Example 2 Zeta potential determination of white particles in various electrophoretic media.

[0149] Mixtures of this dispersion from Example 1 with various combinations of charge control agents (Solsperse™ 19000 and Solsperse™ 8000) were prepared. The zeta potential of the white particles of each mixture was determined using a Colloidal Dynamics AcoustoSizer II and ZetaProbe on samples dispersed in Isopar G. A graph of the zeta potential of the particles versus the weight fraction of Solsperse™ 8000 in the total weight of charge control agents (Solsperse™ 8000 + Solsperse™ 19000) is shown in FIG. 7. FIG. 7 shows that the zeta potential of the white particles in an electrophoretic medium containing only Solsperse™ 19000 (no Solsperse™ 8000) is negative. With the addition of Solsperse™ 8000, the zeta potential becomes less negative and at a weight fraction of Solsperse™ 8000 of about 0.4, the zeta potential of the white particles becomes positive. Presumably, when a sufficient amount of Solsperse™ 8000 is adsorbed onto the particles, the amount of Solsperse™ 19000, which has a positive charge, is increased and modifies the charge on the particle surface. The data in FIG. 7 demonstrate that the surface charge of electrophoretic particles can be controlled by varying the nature and amount of charge control agent used.

[0150] Example 3 Preparation of Type I electrophoresis medium.

[0151] Three different electrophoretic media A, B, C were prepared according to Example 11 of US Pat. No. 10,678,111, except that the charge control agent was a compound of formula IV (R1 is polyricinoleic acid; MW 9,000) instead of Solsperse™ 19000 used in US Pat. No. 10,678,111. The electrophoretic media comprised white particles (W1), cyan particles (C1) and magenta particles (M1) according to US Pat. No. 10,678,111. The electrophoretic media further comprised a yellow pigment (Pigment Yellow 155; Inkjet Yellow 4GC supplied by Clariant, Basel, Switzerland) dispersed as described in Example 11 of US Pat. No. 10,678,111. All three electrophoretic media A, B and C also contained polydimethylsiloxane (PDMS DMS-T72 having a molecular weight of about 700,000, available from Gelest Corporation) at a concentration of 0.9 weight percent of the weight of the electrophoretic medium composition. The polydimethylsiloxane was added to act as an image stabilizer. Electrophoretic medium A does not contain Solsperse™ 8000. Electrophoretic medium B contains Solsperse™ 8000 at a concentration of 140 mg of charge control agent per gram of yellow pigment. Electrophoretic medium C contains Solsperse™ 8000 at a concentration of 280 mg of charge control agent per gram of yellow pigment. Table 3 provides the concentration of particles in the electrophoretic media as the weight percent of each type of particle by weight of the electrophoretic medium composition.

[0152] [Table 3]

[0153] Example 4 Preparation of electrophoretic displays A, B, and C.

[0154] Electrophoretic media A, B and C from Example 3 were used to prepare electrophoretic displays A, B and C, respectively.

[0155] Electrophoretic displays A, B and C from Example 4 (prepared from electrophoretic media A, B and C, respectively) were addressed with a square wave pulse of 500 ms duration with a voltage varying between +24V and -24V in 1 volt intervals at 25°C. The rate of change of density was evaluated using an electro-optical measurement bench including a spectrophotometer. See D. Hertel, "Optical measurement standards for reflective e-paper to predict colors displayed in ambient illumination environments," Color Research & Application, 43, 6, (907-921), (2018).

[0156] The rate of change was higher in electrophoretic displays B and C compared to electrophoretic display A, as shown in Figures 8A-8C. Figures 8A, 8B, and 8C show the optical appearance of displays containing electrophoretic media A, B, and C, respectively, with voltage on the x-axis and time on the y-axis.

[0157] The color of the white state of each of electrophoretic displays A, B and C was determined at the end of 500 ms of driving at various negative voltages. This investigation demonstrated that the separation of the white and yellow particles was more complete in displays B and C than in display A (display A did not have Solsperse™ 8000). The voltage window available to make the transition between the white and black states is preferably as wide as possible with a simple voltage pulse. Investigations showed that in display A with electrophoretic medium A without Solsperse™ 8000, the white state was contaminated by yellow at voltages more negative than about -8V. In the case of display B with electrophoretic medium B containing 140 mg of Solsperse™ 8000 per gram of yellow pigment, the white state was contaminated at voltages more negative than about -10V, while in the case of electrophoretic medium C, there was almost no yellow contamination even when addressed at -13V. Also, the white / yellow boundary point was found to be sharper in displays B and C with electrophoretic media B and C containing Solsperse™ 8000 compared to display A, which has an electrophoretic medium without additive.

[0158] The ability to use more negative voltages to achieve the white state results in faster switching from black to white. Figure 9 shows traces of black to white switching for three electrophoretic media A, B and C at -8V, -10V and -13V, respectively. These are the most negative voltages possible without producing excessive white state contamination by the yellow pigment.

[0159] The color gamuts of electrophoretic displays A, B and C at 25° C. were determined using the color gamut measurement method set forth below. The results are summarized in FIG.

[0160] [Table 4]

[0161] The data in Table 4 show that displays using electrophoretic media B and C, which contain Solsperse™ 8000 and a first charge control agent, have a higher color gamut than the display using electrophoretic medium A, which does not contain Solsperse™ 8000.

[0162] Color Gamut Measurement Method.

[0163] Electrophoretic displays A, B and C from Example 4 were electrically driven to produce eight optical states (white, yellow, red, magenta, blue, cyan, green and black). * , a * and b *Measurements were made using a color computer at 1000 Hz. A sequence of electrical pulses was used to address the electrophoretic device (such a sequence is called a "waveform"). In the following description, it is assumed that the voltages used in the waveforms are supplied to the second electrode layer (back electrode) of the display, and that the first light-transmissive electrode on the front (viewing) surface of the display is the common electrode for all pixels and is connected to earth. The test waveforms contain a sequence of "dipoles" as shown in Figure 10. Each dipole is composed of two monopoles, each a pulse of length t and magnitude V. The two monopoles in each dipole have opposite polarities. The voltages used at the test wavelengths were + / -24V, + / -18V, + / -15V and + / -10V. Time was discretized into units of 11.74 ms, called "frames". Each frame corresponds to one scan of a thin film transistor array backplane refreshed at a frequency of 85Hz, although in the described tests the backplane was segmented and directly driven. Two test waveforms were used to evaluate the electro-optical performance of the device. The waveform used in the first test had a length of 18 frames, while the waveform used in the second test had a length of 42 frames. In each case, the waveform had as many identical dipoles placed as would fit within the allowed number of frames. The color gamut of the display was measured by calculating the volume of a convex hull that contained each colored state produced by the set of test waveforms. The color gamut was determined by the DE 3 A wider color gamut, i.e., a larger space, means better electro-optical performance of the electrophoretic display.

[0164] Example 5 Preparation of Type II electrophoretic media and corresponding electrophoretic displays.

[0165] A type II electrophoretic medium was prepared similar to that prepared in Example 1, but using different yellow particles. The yellow particles and their preparation are described in Example 6 below. Using the yellow particles from Example 6 and the control yellow particles from Example 7, various electrophoretic media were prepared (both inventive and control) with various contents of the second charge control agent (e.g., Solsperse™ 8000) and the first charge control agent (Formula IV).

[0166] Example 6 Preparation of yellow pigment for type II electrophoretic medium of Example 5.

[0167] To a 1 liter plastic bottle was added 72.0 g of Pigment Yellow 155 (Inkjet Yellow 4GC, supplied by Clariant Corporation), 28.8 g of an Isopar E solution of a charge control agent represented by formula IV (containing 21.6 g of charge control agent and 7.2 g of Isopar E), and 349.2 g of Isopar E. The dispersion was roll milled for 16 hours using Zirconox beads (1.7-2.4 mm). A quantity of 450 g of the resulting dispersion was mixed in a reactor with 1.94 g of 2,2,2-trifluoroethyl methacrylate, 27.68 g of methyl methacrylate, 52.36 g of monomethacrylate terminated poly(dimethylsiloxane) (Gelest MCR-M22), and 65.38 g of Isopar E. The reactor was equipped with a nitrogen impregnated tube, an overhead stirring impeller, and an air condenser. Set the overhead stirring to 250 rpm and purge the reaction mixture with nitrogen for 65-70 seconds. oC for 60 minutes, after which the impregnation tube was removed and a rotameter nitrogen level was set. In a small vial, 0.187 g of 2,2'-azobis(2-methylpropionitrile) (AIBN) was dissolved in 2.24 g of ethyl acetate and added to the syringe. The resulting AIBN solution was pumped into the reactor over 5-10 minutes, and the reaction mixture was heated at 65°C for 16 hours. The reaction mixture was dispensed into two 1-liter centrifuge bottles and centrifuged. The supernatant was decanted, and the remaining pigment was washed with Isopar E and centrifuged. The washing process was repeated two more times. The remaining pigment was dried in a vacuum oven at 40°C. The dried pigment was dispersed in Isopar E to 25 weight percent using sonication. The resulting dispersion was filtered through a 200 μm mesh and used to prepare the electrophoretic medium. The yellow particles contain 31 weight percent polymer of the weight of the particles. The zeta potential of the yellow particles in the final dispersion was determined using a Colloidal Dynamics AcoustoSizer II and ZetaProbe on the sample and found to be +6 mV, i.e. the yellow particles have a slightly positive surface.

[0168] Example 7 The process of Example 6 was repeated, but without the charge control agent. This is the control yellow particles for Type II media.

[0169] Using the color gamut measurement method described above, the color gamuts of various inventive electrophoretic displays from Example 5 and the control display were determined. The results of this evaluation are summarized in Table 5. For each display, the upper number in the corresponding cell corresponds to the color gamut measurement using a waveform 18 frames long. The lower number in the corresponding cell corresponds to the color gamut measurement using a waveform 42 frames long. The color gamut volume of Type II electrophoretic media is somewhat smaller than that achieved by Type I media.

[0170] [Table 5]

[0171] The same display with a Type II electrophoretic medium was evaluated for the time required to switch from a white to a black state. The determination was made by applying a +16V pulse and a delta L of 30 between the initial and final states. * This was done by measuring the time required to reach 0.05° C. The times were measured and are reported in milliseconds in Table 6.

[0172] [Table 6]

[0173] The data show that Type II electrophoretic media switches much more rapidly than Type I media.

[0174] The data presented above demonstrates that electrophoretic medium compositions of the present invention containing a combination of first and second charge control agents perform better in terms of color gamut and switching speed than media not according to the present invention, for both Type I and Type II electrophoretic media.

[0175] Example 8 Preparation of charge control agent A (hydrogenated polyfarnesene with two terminal sulfate functional groups and H+ as the counter ion).

[0176] A quantity of 9.8 g of hydrogenated hydroxyl-terminated polyfarnesene (Krasol F3100, with a number average molecular weight of 3100 g / mol; supplied by Cray Valley) was dissolved in 65 mL of ethyl ether. A quantity of 0.66 mL of 6 mL of chlorosulfonic acid was slowly added to the solution under constant stirring at 0 °C under nitrogen gas. The reaction was allowed to warm to room temperature under constant stirring for 18 h. The ethyl ether layer was washed once with an equal volume of water and then dried over sodium sulfate. The solvent was removed under reduced pressure and the material was purified by column chromatography (0-10% methanol / dichloromethane). This afforded the desired product in 76% yield.

[0177] Example 9 Preparation of charge control agent B (hydrogenated polyfarnesene with two terminal sulfate functional groups and Na+ as the counter ion).

[0178] A quantity of hydrogenated hydroxyl-terminated polyfarnesene (Krasol F3100, having a number average molecular weight of 3100 g / mol; supplied by Cray Valley) was dissolved in 62 mL of ethyl ether. A quantity of 0.4 mL of 6 mL of chlorosulfonic acid was slowly added to the solution under nitrogen gas and constant stirring. The reaction was stirred at room temperature for 48 hours. Then, 0.75 g of NaOH dissolved in 50 mL of water was added to the reaction and stirred for an additional hour. The organic layer was then separated from the aqueous layer and dried over sodium sulfate. The solvent was removed under reduced pressure to give the desired product in 91% yield.

[0179] Example 10 Preparation of various electrophoretic displays using charge control agent A and charge control agent B.

[0180] The charge control agent of Examples 8 and 9 is a comb polymer with hydrogenated farnesyl groups and two terminal sulfate groups. Various electrophoretic displays with the above-mentioned type II electrophoretic medium. Pigments of the electrophoretic medium (white, cyan, magenta and yellow particles). The white particles have a negative charge, and the cyan, magenta and yellow particles have a positive charge. The weight ratio of the particles is 72:9:11:9 white:cyan:magenta:yellow. The total charge control agent content is 42 mg of charge control agent per gram of pigment. When two charge control agents are present, the weight ratio of the cationic Solsperse™ 8000 charge control agent to the non-cationic Solsperse™ 8000 charge control agent is 1:8. The composition of the electrophoretic medium also includes a charge control agent or a combination of two charge control agents as shown in Table 7, a hydrocarbon solvent, and a polydimethylsiloxane fluid. The displays were exposed to a drive voltage sweep of -11 V to -16 V for 500 ms at 25°C, which provided a change in the color state of the display. At 0 s and approximately every 80 ms during the voltage sweep, the color (L * , a *, and b * ) was measured by a color computer. Examples 10B, 10C and 10D of the present invention showed significantly faster color switching than Comparative Example 10A. The fastest switching was observed for the display of Example 10C, followed by the display of Example 10D, followed by the display of Example 10B. The display of Comparative Example 10A did not provide a stable color (steady state) within the 500 millisecond test interval. Evaluation of the displays of the four examples was repeated for a voltage sweep of -18V to -22V over 500 milliseconds at 0°C. Results were similar to those observed for the evaluation at 25°C.

[0181] [Table 7-1]

[0182] Example 11 An aqueous sealing composition for forming a sealing layer.

[0183] Evaluation of the sealing layer of the microcell electrophoretic display. A variety of microcell electrophoretic displays were prepared using a type II electrophoretic medium. The microcell electrophoretic display included a first light-transmitting electrode layer, a microcell layer, and a second electrode layer. The microcell layer included a plurality of microcells, each of which had an opening, and a sealing layer spanning the openings of the microcells. The sealing layer was formed by coating an aqueous composition as described in U.S. Patent Application Publication No. 2022 / 0251364A1 (Application Serial No. 17 / 590,705), U.S. Patent Application Publication No. 2022 / 0244612A1 (Application Serial No. 17 / 590,835), and U.S. Patent Application Serial No. 18 / 055,072. To evaluate the effect of the sealing layer, two different aqueous sealing compositions were prepared and used to form the corresponding sealing layers (Examples 11A and 11B in Table 7). Example 1 contains a water-soluble ether, while Example 12 does not contain a water-soluble ether.

[0184] [Table 7-2]

[0185] [1] Poly(vinyl alcohol-co-ethylene) copolymer; Exceval™ RS-1717, supplied by Kuraray; [2] Polyurethane aqueous dispersion; L3838 aqueous dispersion, supplied by Hauthaway as a 35% dispersion in water; [3] Carbon black; Nerox® 3500, supplied by Orion Engineered Carbon; [4] Polycarbodiimide (polyfunctional polycarbodiimide-aqueous solution); CARBODILITE® V-02-L2, supplied by Nisshinbo Chemical Inc. as a 40% aqueous solution; [5] Hydrophobically modified alkali swellable acrylic emulsion; Solthix™ A-100, supplied by Lubrizol; [6] Siloxane polyalkylene oxide copolymer; Silwet® L-7607 copolymer, supplied by Momentive.

[0186] Example 12 Preparation and evaluation of electrophoretic displays having an electrophoretic medium containing a charge control agent or combination of charge control agents.

[0187] A series of microcell electrophoretic displays with different type II electrophoretic media were prepared and evaluated. The microcell electrophoretic displays included a first light-transmitting electrode layer, a microcell layer, and a second electrode layer. The microcell layer included a plurality of microcells, each microcell having an opening, and a sealing layer over the openings of the microcells. The sealing layer was formed by coating with the aqueous composition of Example 11B, which did not include the water-soluble ether dipropylene glycol dimethyl ether. The electrophoretic media included negatively charged white particles, and positively charged cyan, magenta, and yellow particles. The white particles were based on titanium dioxide pigment surface-treated with a polymer formed by copolymerization of methyl methacrylate monomer and 2,2,2-trifluoroethyl methacrylate. The cyan particles were based on copper phthalocyanine pigment (PB15:3) surface-treated with a polymer formed by methyl methacrylate and dimethylsiloxane monomer as described in Example 7 of U.S. Pat. No. 9,921,451. The magenta particles were based on dimethylquinacridone (PR122) surface-treated with a polymer formed by vinylbenzyl chloride and laurylmethylacrylate as described in Example 5 of US Pat. Nos. 9,697,778 and 9,921,451. The yellow particles were based on Pigment Yellow 155 surface-treated with a polymer formed by methylmethacrylate and dimethylsiloxane. All electrophoretic media also contained a cationic charge control agent from Example 1 of CCA111 of US2020 / 0355978. Two of the electrophoretic media-containing examples of the present invention (12B and 12E) also contained another charge control agent (Solsperse™ 8000). The molecular structure of the second charge control agent includes two or more polar groups (amino groups) and a non-polar tail. All compositions and evaluation data are described in Table 8, Examples 12A-12E. The symbol X in the table means the presence of the corresponding component in the composition. The color gamut of the electrophoretic display was measured by the color gamut measurement method described above. C of each color state in the table *The (chroma) measurements were performed using a color computer. The zeta potential was measured using the method disclosed in Example 6.

[0188] [Table 8-1] [Table 8-2]

[0189] The data in Table 8 demonstrate that electrophoretic displays using electrophoretic media containing a combination of charge control agents (charge control agent from Example 1 CCA111 of US2020 / 0355978 and Solsperse™ 8000) exhibited improved electro-optical performance. Specifically, the color gamut of an electrophoretic display electrophoretic medium containing Solsperse™ 8000 in combination with a cationic charge control agent (and yellow particles having a zeta potential of 7) is wider than an electrophoretic display having an electrophoretic medium containing the same yellow particles but without Solsperse™ 8000 (Example 12B vs. Comparative Example 12A). Similarly, the color gamut of the display of Example 12E is wider than the color gamut of Example 12D.

[0190] (Example 13) Compositions and evaluation data for electrophoretic displays having (a) an electrophoretic medium comprising a charge control agent or combination of charge control agents, and (b) a sealing layer comprising a water-soluble ether.

[0191] Another series of microcell electrophoretic displays with different type II electrophoretic media were prepared and evaluated. The structure of the displays is described in Example 12 above. The properties of the electrophoretic particles are also described in Example 12. The aqueous sealing compositions of Example 13 (from Example 11A) forming the sealing layers of the electrophoretic displays of Example 12 all contained a water-soluble ether. All of the electrophoretic media also contained a cationic charge control agent from Example 1 of CCA111 of US2020 / 0355978. Different yellow particles with various polymer contents and zeta potentials were prepared, as shown in Table 9. The symbol X in the table means the presence of the corresponding component in the composition. The color gamut of the electrophoretic displays was measured by the color gamut measurement method described above. The C of each color state in the table * The (chroma) measurements were performed using a color computer. The zeta potential was measured using the method disclosed in Example 6.

[0192] [Table 9-1] [Table 9-2]

[0193] The data in Table 9 demonstrate that the inclusion of a water-soluble ether in the sealing composition forming the sealing layer significantly improves the electro-optical performance of the corresponding electrophoretic display (color gamut of Example 13A vs. Comparative Example 12A, Example 13B vs. Example 12B, Example 13C vs. Comparative Example 12C, Example 13E vs. Comparative Example 12D, Example 13F vs. Example 12E). Furthermore, the data in Table 9 demonstrate that improved electro-optical performance is observed in displays in which a combination of charge control agents is present in an electrophoretic medium having similar yellow particles (color gamut of Example 13B vs. Example 13A, Example 13D vs. Example 13C, Example 13F vs. Example 13D, etc.). Finally, the data in Table 9 demonstrate that an electrophoretic medium having yellow particles with a lower zeta potential exhibits better performance (color gamut of Example 13H vs. Example 13G). The improved color performance is due to increased C in the yellow and green states. *This may be due to the better of these two states, as shown by the lower dark state C of Comparative Example 13B compared to Comparative Example 13A. * As shown by (and from the series of examples in Table 8), a more achromatic dark state (black) can also be obtained. Thus, both (a) the combination of charge control agents (cationic charge control agent from Example 1 CCA111 of US2020 / 0355978 and Solsperse™ 8000) and (b) the use of water-soluble ethers in the aqueous sealing composition of the electrophoretic display improve the yellow, green and dark states, as well as the overall color gamut of the corresponding electrophoretic display. This improvement is observed in all cases, regardless of the yellow particles used (see Example 13D vs. Example 13C, Example 12E vs. Comparative Example 12D, and Example 13F vs. Example 13E). However, the data in Table 1 show that the highest color gamut is achieved in examples where the zeta potential of the yellow particles is in the range of 6 to 11 and the polymer content of the yellow particles is relatively low, such as in the case of Examples 13F and 13H.

[0194] Thus, in general, electrophoretic displays having an electrophoretic medium (Example 13G and Example 13H) that includes (a) an electrophoretic medium that includes a combination of charge control agents, (b) a water-soluble ether in the aqueous sealing composition that forms the sealing layer, and (c) yellow particles that have a relatively low polymer content while maintaining a low zeta potential, exhibit a higher chroma (C * ), higher saturation in the green state (C * ), and a lower C in the dark state. * The present inventors have also observed that displays having the provided features (a), (b) and (c) exhibit significantly faster switching speeds from a dark state to a white state (when driven with a voltage sweep from +24V to -24V) than displays not having these features. The most significant switching speed improvement was observed in displays having electrophoretic media including yellow particles with a relatively low polymer content, e.g., Example 13F, in which the polymer content is 32.7% by weight of the yellow particles.

[0195] Example 14 Compositions and evaluation data for electrophoretic displays comprising (a) an electrophoretic medium containing a charge control agent or combination of charge control agents, and (b) a water-soluble ether.

[0196] Another series of microcell electrophoretic displays having different Type II electrophoretic media were prepared and evaluated. The display construction is described above in Example 12. The properties of the electrophoretic particles are also described in Example 12.

[0197] Two of the aqueous sealing compositions of Example 14 (from Example 11A) that formed the sealing layer of the electrophoretic display of Example 14 contained a water-soluble ether (Example 14D and Example 14E). The remainder of the aqueous sealing compositions of Example 14 (from Example 11B) that formed the sealing layer of the electrophoretic display of Example 14 did not contain a water-soluble ether (Comparative Example 14A, Example 14B, Example 14C and Example 14F). All of the electrophoretic media contained the cationic charge control agent from Example 1 of CCA111 of US2020 / 0355978. Three of the electrophoretic medium compositions of Example 14 (Example 14B, Example 14E and Example 14F) also contained a second charge control agent (Solsperse™ 8000). The molecular structure of the second charge control agent contains two or more polar groups (amino groups) and a non-polar tail. All the yellow particles in the examples contain the same polymer content of 33.3 weight percent of the weight of the particle. The symbol X in the table means the presence of the corresponding component in the composition. The color gamut of the electrophoretic display was measured by the color gamut measurement method described above. The C of each color state in the table * (Chroma) measurements were taken using a color computer. The compositions and evaluation data are listed in Table 10.

[0198] The combined data in Tables 8 and 9, as can be concluded by comparing Example 12A, Example 12B, Example 13A and Example 13B, showed that there was a synergistic effect on the elements of (a) Solsperse™ 8000 in the electrophoretic medium and (b) the presence of a water-soluble ether in the sealing layer, i.e., the effect of expanding the color gamut by the inclusion of (a) Solsperse™ 8000 in the electrophoretic medium and (b) a water-soluble ether in the sealing layer was greater than the additive effect of each of the independent elements (a) and (b).

[0199] The combined data in Tables 8 and 9 also showed that there was a synergistic effect of the elements (b) the presence of the water-soluble ether in the sealing layer, (c) the lower polymer content on the yellow particles, as can be concluded by comparing Example 12A, Example 12C, Example 13A and Example 13C, i.e., the effect of expanding the color gamut by the inclusion of (c) the yellow particles having a lower polymer content in the electrophoretic medium, and (b) the water-soluble ether in the sealing layer is greater than the additive effect of each of the independent elements (c) and (b).

[0200] [Table 10-1] [Table 10-2]

[0201] The inventors of the present invention have surprisingly found that the effect of having a water-soluble ether in the aqueous sealing composition forming the sealing layer of a microcell electrophoretic display on the color performance of the display can be partially achieved by incorporating a water-soluble ether in the electrophoretic medium. This is shown in the data in Table 10. The data in Example 14C showed that the presence of the charge control agent from Example 1 of CCA111 of US2020 / 0355978 in conjunction with dipropylene glycol dimethyl ether in the electrophoretic medium improves the electro-optical performance of the corresponding display compared to the control Comparative Example 14A. The further addition of a second charge control agent (Solsperse™ 8000) in the electrophoretic medium of Comparative Example 14C resulted in further improvement as shown in Example 14F, but the effect was not as pronounced as with the water-soluble ether in the aqueous sealing composition forming the sealing layer (Example 14E).

[0202] Microcell electrophoretic displays were constructed using various electrophoretic media (Type II). The displays included a first light-transmissive electrode layer, a microcell layer comprising a plurality of microcells, each microcell of the plurality of microcells having an opening, a sealing layer spanning the openings of the plurality of microcells, and a second electrode layer (bottom electrode).

[0203] Thus, although several aspects and embodiments of the technology of the present application have been described, it should be understood that those skilled in the art may easily conceive of various alterations, modifications and improvements. Such alterations, modifications and improvements are intended to be within the spirit and scope of the technology described in the present application. For example, those skilled in the art may easily envision various other means and / or structures for performing the functions and / or obtaining one or more of the results and / or advantages described herein, and each such variation and / or modification is considered to be within the scope of the embodiments described herein.

Claims

1. A non-polar fluid; a first type of particles including a first type of pigment, the first type of pigment being inorganic and having a first color, the first type of particles having a first charge polarity; a second type of particles comprising a second type of pigment, the second type of pigment having a second color, the second color being different from the first color, the second type of particles having a second charge polarity, the second charge polarity being opposite to the first charge polarity; a third type of particles including a third type of pigment having a third color, the third color being different from the first and second colors, the third type of particles having the second charge polarity; and a fourth type of particles including a fourth type of pigment having a fourth color, the fourth color being different from the first, second and third colors, the fourth type of particles having the first charge polarity or the second charge polarity; a first charge control agent having a molecular structure, the molecular structure of the first charge control agent including at least one quaternary ammonium group and a non-polar tail; a second charge control agent having a molecular structure comprising two or more polar groups and a non-polar tail, the two or more polar groups being selected from the group consisting of amino groups, sulfonate groups, sulfate groups, sulfinate groups, carboxylic acid groups, phosphonic acid groups, phosphinate groups, phosphate groups, hydroxyl groups, thiol groups, alpha diketone groups, beta diketone groups, ethylene oxide groups, and propylene oxide groups, the non-polar tail comprising a polymeric group formed by a monomer comprising an alkyl or alkenyl group having at least 10 carbon atoms; 13. An electrophoretic medium comprising:

2. 2. The electrophoretic medium of claim 1, wherein the molecular structure of the monomer used to form the polymeric group of the non-polar tail of the second charge control agent comprises a carboxylic acid, a carboxylic acid anhydride, or a carboxylic acid halide, the carboxylic acid and the carboxylic acid halide comprising from 10 to 22 carbon atoms and the carboxylic acid anhydride comprising from 20 to 44 carbon atoms.

3. 3. An electrophoretic medium according to claim 2, wherein the molecular structure of the monomer forming the polymer tail of the second charge control agent further comprises a hydroxyl group or an amine group.

4. 2. The electrophoretic medium of claim 1, wherein the monomers used to form the polymer tail of the second charge control agent are selected from the group consisting of ricinoleic acid, linoleic acid, oleic acid, linoleic acid, acid halides of ricinoleic acid, acid halides of linoleic acid, acid halides of linolenic acid, ricinoleic anhydride, linoleic anhydride, oleic anhydride, and linolenic anhydride.

5. 2. An electrophoretic medium as defined in claim 1, wherein the molecular structure of the second charge control agent comprises a comb polymer having alkyl or alkenyl branches and two terminal polar functional groups.

6. 2. The electrophoretic medium of claim 1 further comprising a water-soluble ether, said water-soluble ether having a molecular weight of 75 to 5,000 Daltons.

7. 2. An electrophoretic medium as claimed in claim 1, wherein the first, second, third and fourth types of particles have a layer of a polymer, the polymer being complexed, adsorbed or covalently bonded to the first, second, third and fourth types of pigments.

8. 8. An electrophoretic medium as defined in claim 7, wherein the second and fourth types of particles comprise a polymer formed from a monomer comprising methyl methacrylate and dimethyl siloxane.

9. 8. An electrophoretic medium as claimed in claim 7, wherein the third type of particles is formed by treatment of pigment particles with (a) methyl methacrylate and a monomer comprising dimethyl siloxane, or (b) vinyl benzyl chloride and an acrylate or methacrylate monomer.

10. 2. The electrophoretic medium of claim 1 further comprising a water-soluble ether, said water-soluble ether having a molecular weight of 75 to 5,000 Daltons.

11. 2. An electrophoretic medium as claimed in claim 1, wherein the polarities of the second, third and fourth types of particles are all positive, the second type of particles having a second zeta potential, the third type of particles having a third zeta potential, and the fourth type of particles having a fourth zeta potential, the first zeta potential being greater than the second and third zeta potentials and the fourth zeta potential being less than the third zeta potential.

12. 2. The electrophoretic display of claim 1, wherein the first color is white, the second color is cyan, the third color is magenta, and the fourth color is yellow.

13. a first light transmissive first electrode layer at the viewing surface; a second electrode layer including an array of thin film transistors coupled to the pixel electrodes; 2. An electro-optical material layer comprising the electrophoretic medium of claim 1, the electro-optical material layer being disposed between the first light-transmitting electrode layer and the second electrode layer; A color electrophoretic display comprising:

14. a first light transmissive electrode layer; a microcell layer comprising a plurality of microcells, each microcell of the plurality of microcells having an opening, each microcell of the plurality of microcells containing an electrophoretic medium; a sealing layer with a sealing membrane spanning the opening of each microcell; A second electrode layer; A color electrophoretic display comprising: The electrophoretic medium is A non-polar fluid; a first type of particles including a first type of pigment, the first type of pigment being inorganic and having a first color, the first type of particles having a first charge polarity; a second type of particles comprising a second type of pigment, the second type of pigment having a second color, the second color being different from the first color, the second type of particles having a second charge polarity, the second charge polarity being opposite to the first charge polarity; a third type of particles including a third type of pigment having a third color, the third color being different from the first and second colors, the third type of particles having the second charge polarity; and a fourth type of particles including a fourth type of pigment having a fourth color, the fourth color being different from the first, second and third colors, the fourth type of particles having the first charge polarity or the second charge polarity; a first charge control agent having a molecular structure, the molecular structure of the first charge control agent including a quaternary ammonium group and a non-polar tail; Including, A color electrophoretic display comprising a water soluble ether, said water soluble ether having a molecular weight of 75 to 5,000 Daltons, said water soluble ether being present in said sealing layer or in said electrophoretic layer of said color electrophoretic display.

15. 15. The color electrophoretic display of claim 14, wherein the electrophoretic medium further comprises a second charge control agent having a molecular structure comprising two or more polar groups and a non-polar tail, the two or more polar groups being selected from the group consisting of amino groups, sulfonate groups, sulfate groups, sulfinate groups, carboxylic acid groups, phosphonic acid groups, phosphinate groups, phosphate groups, hydroxyl groups, thiol groups, alpha diketone groups, beta diketone groups, ethylene oxide groups, and propylene oxide groups, the non-polar tail comprising a polymeric group formed by a monomer comprising an alkyl or alkenyl group having at least 10 carbon atoms.

16. 15. The color electrophoretic display of claim 14, wherein the second type of particles has a second zeta potential, the third type of particles has a third zeta potential, and the fourth type of particles has a fourth zeta potential, the second, third and fourth zeta potentials are positive, the second zeta potential being greater than the third and fourth zeta potentials, and the fourth zeta potential being less than the third zeta potential.

17. 15. The color electrophoretic display of claim 14, wherein the fourth type of particles comprises pigment particles and a polymer, the polymer having a content of less than 35 weight percent of the weight of the particles.

18. 15. The color electrophoretic display of claim 14, wherein the first color is white, the second color is cyan, the third color is magenta, and the fourth color is yellow.

19. 15. The color electrophoretic display of claim 14 wherein the second and fourth types of particles comprise a polymer formed from a monomer comprising methyl methacrylate and dimethyl siloxane.

20. 15. The color electrophoretic display of claim 14 wherein the third type of particles is formed by treatment of pigment particles with (a) methyl methacrylate and a monomer comprising dimethyl siloxane, or (b) vinyl benzyl chloride and an acrylate or methacrylate monomer.