Tire cavity resonance sound absorber

Abstract

1. A tire comprising a tread portion, a bead portion, and a sidewall portion extending between the bead portion and the tread portion, the tread portion, the bead portion, and the sidewall portion defining an internal cavity of the tire, the tire further comprising a sealant layer disposed on the tread portion of the tire in the internal cavity of the tire, and a silicone foam noise reduction layer disposed on the sealant layer in the internal cavity of the tire.

Description

[Technical field]

[0001] The present disclosure relates to improved noise reduction and self-sealing in tires. [Background technology]

[0002] Tires are used in various vehicles under various conditions. Under some operating conditions, tires may generate undesirable levels of noise, which may have adverse effects on drivers or passengers. In order to reduce tire noise, a noise absorbing or noise reducing layer may be provided inside the tire.

[0003] Some tires are equipped with a sealant layer designed to automatically seal a punctured hole in the tire. Such tires are sometimes referred to as "self-sealing" tires. The sealant layer may be a viscous coating on the inside of the tire. The purpose of the sealant layer is to maintain the integrity of the tire in the event of a puncture, even if the puncturing object becomes dislodged from the tire.

[0004] It has not been possible to provide a self-sealing tire with good noise absorption without compromising the sealing performance. The use of a noise-reducing layer together with a sealant layer brings about a number of challenges. The noise-reducing layer can stick to the sealant layer, causing the noise-reducing layer to deform and reducing its performance. This can occur, for example, when the tire is impacted and forced to deform, forcing the noise-reducing layer into the sealant layer.

[0005] Similarly, the noise reduction layer may stick to the sealant layer and prevent the sealant layer from flowing to seal the puncture. This can occur if a portion of the noise reduction layer blocks the sealant layer from flowing to the puncture. A small portion of the noise reduction layer may break off from the rest of the noise reduction layer and be sucked into the puncture, preventing the sealant layer from sealing the puncture. Summary of the Invention

[0006] It has been found that a tire according to the present disclosure overcomes the disadvantages associated with the prior art. A tire according to the present disclosure provides improved noise reduction without compromising self-sealing performance. A tire as described herein provides improved noise reduction and sealing performance without increasing the complexity of the internal design of the tire cavity.

[0007] According to the present disclosure is a tire. The tire may include a tread portion, a bead portion, and a sidewall portion. The sidewall portion may extend between the bead portion and the tread portion. The tread portion, the bead portion, and the sidewall portion may define an internal cavity of the tire. The tire may further include a sealant layer disposed on the tread portion of the tire in the internal cavity of the tire. The tire may further include a silicone foam noise reduction layer disposed on the sealant layer in the internal cavity of the tire.

[0008] The tire may be a pneumatic tire, such as those used on vehicles including passenger cars, light goods vehicles, and heavy goods vehicles. The tire may be mounted on a hub and filled with compressed air. The bead portion may be the radially innermost portion of the tire. The bead portion may be configured to provide stiffness to the tire and allow mounting of the tire on a wheel hub. The tread portion may include a tread on its outer surface for contacting the road surface and providing grip. The sidewall portion may include two sidewall portions on either side of the tread, extending between the tread portion and the bead portion.

[0009] The tire may be a self-sealing tire. The tire may be configured to automatically seal a puncture. The sealant layer may be configured to provide this self-sealing capability. The sealant layer may be configured to automatically seal a puncture through the tread, for example a puncture in the range of 0-5 mm in diameter.

[0010] The sealant layer may include or consist of a viscous fluid configured to flow into a puncture or hole in the tread and act to seal the puncture or hole and prevent air loss through the puncture or hole.

[0011] The sealant layer may be a homogenous layer. The sealant layer may be formed from a single homogenous composition. The sealant layer may be configured to adhere (e.g., directly) to the tread and the noise-reducing layer.

[0012] The sealant layer may be in direct contact with the tire tread and the silicone foam noise reduction layer.

[0013] The sealant layer may be sandwiched between the tread and the silicone foam noise reduction layer without an intermediary layer.

[0014] The tire may not include a separate adhesive layer in addition to, for example, a sealant layer and a silicone foam noise reduction layer.

[0015] The tire may only include a sealant layer and a silicone foam noise reduction layer in the interior cavity of the tire.

[0016] This arrangement of sealant and noise reducing layers eliminates the need for a separate adhesive or support layer, greatly simplifying tire construction.

[0017] The sealant layer has a thermal conductivity of 50 to 1000 Pa·s (Pascal seconds (Nsm)) at 100°C. -2 The sealant layer may have a viscosity of greater than 50, 100, 200, 400, 600, or 800 Pa·s and / or the sealant layer may have a viscosity of less than 1000, 800, 600, 400, 200, or 100 Pa·s at 100° C.

[0018] Viscosity is measured according to ASTM D5099.

[0019] The sealant layer may have a layer thickness of 1 to 6 mm. The sealant layer may have a thickness of more than 1 mm, 2 mm, 3 mm, 4 mm, or 5 mm, and / or the sealant layer may have a thickness of less than 6 mm, 5 mm, 4 mm, 3 mm, or 2 mm.

[0020] The sealant layer may have a tack of 0.1 to 25 N. The sealant layer may have a tack of greater than 0.1, 2, 5, 10, 15, or 20 N, and / or the sealant layer may have a tack of less than 25, 20, 15, 10, 5, 2, or 0.1 N.

[0021] Tack has been measured by Probe Tack Test with a 25-30 mm diameter plunger and a 30 mm diameter probe, a preload of 0.5 N, a dwell time of 30 seconds, and a release speed of 2000 mm / min.

[0022] The sealant layer may include or consist of a rubber-based material. The sealant layer may be a composite sealant layer.

[0023] The sealant layer may include or consist of butyl rubber (i.e., any butylic rubber), a plasticizer, and a tackifier resin. The butyl rubber may be a halobutyl rubber.

[0024] The sealant layer may include butyl rubber. The sealant layer may include 100-400 PHR of plasticizer (PHR means parts per hundred parts of rubber). The sealant layer may include 10-80 PHR of tackifier resin.

[0025] The sealant layer may comprise or consist of butyl rubber, 100-400 PHR of a plasticizer, and 10-80 PHR of a tackifier resin.

[0026] The term PHR refers to the ratio of a component to 100 parts of rubber. For example, a 50 PHR component means that for every 100 parts of rubber, 50 parts of that component are required. PHR may be based on weight or volume.

[0027] During use, as the road surface impacts the tire tread, the air within the cavity and / or the tire itself may vibrate. In tires without a noise-reducing layer, this vibration may be transmitted to the interior of the vehicle as noise. This noise may typically be in the frequency range of 200-250 Hz. For tires with rim diameters larger than 19 inches, the frequency range may shift to frequencies below 200 Hz, such as 170-220 Hz or 160-210 Hz.

[0028] The tire has a noise reduction layer, which is a silicone foam noise reduction layer.

[0029] Surprisingly, it was found that the use of silicone foam in the noise reduction layer overcomes the disadvantages associated with existing constructions that use polyurethane (PU) or ethylene propylene diene monomer (EPDM) foam: the silicone foam noise reduction layer provides good noise absorption while its low tack allows the sealant to function properly.

[0030] The silicone foam noise reduction layer is a cellular silicone foam having an open cell structure. The use of an open cell structure improves adhesion of the noise reduction layer to the sealant layer.

[0031] The use of an open cell structure allows for mechanical adhesion; that is, the sealant can penetrate the open cell structure of the silicone foam while still holding the silicone foam in place within the tire. This is accomplished without significant adhesion of the sealant to the surface of the silicone foam itself; that is, the silicone foam does not impede the sealant's flow, and thus the sealant can freely flow into the puncture and perform its sealing function.

[0032] The silicone foam noise reduction layer may have an operating temperature ranging from -40°C to over 150°C, as measured according to the ASTM D 1056 standard.

[0033] Silicone foam noise reduction layer: 105kg / m 3 The silicone foam noise reduction layer may have a density of less than 60 kg / m 3 It may have a density of less than 1000 nm, which may be measured according to the ASTM D 1056 standard.

[0034] The silicone foam noise reduction layer may have a tensile strength of greater than 70 kPa, which may be measured according to the ASTM D 412 standard.

[0035] The silicone foam noise reduction layer may have an ultimate elongation of greater than 40%, which may be measured according to the ASTM D 412 standard.

[0036] The silicone foam noise reduction layer may have a compression set of less than 5%. The silicone foam noise reduction layer may have a compression set of less than 2%, which may be measured according to the ASTM D 1056 standard.

[0037] The silicone foam noise reduction layer may have a temperature resistance of -40 to +150° C. The silicone foam noise reduction layer may have a temperature resistance of -40 to +100° C. This may be measured according to the ASTM D 1056 standard.

[0038] The silicone foam noise reduction layer may have a width of 50 to 150 mm. The width may be measured in a direction parallel to the axis of rotation of the tire.

[0039] The silicone foam noise reduction layer may have a thickness of 15-40 mm, 15-30 mm, 20-35 mm, or 25-30 mm. The thickness may extend in a radial direction of the tire.

[0040] The silicone foam noise reduction layer may extend over 80-100% or 90-100% of the inner circumference of the tire.

[0041] The silicone foam noise reduction layer may be cubic. The silicone foam noise reduction layer may have a triangular or trapezoidal cross section. The silicone foam noise reduction layer may be tapered. The silicone foam noise reduction layer may have a varying width or thickness around the circumference of the tire. The silicone foam noise reduction layer may have an undulating thickness or width around the circumference of the tire.

[0042] The silicone foam noise reduction layer may be centrally located on the sealant layer. The silicone foam noise reduction layer may be centrally and symmetrically located with respect to the center plane of the tire. This may improve tire balance.

[0043] Also in accordance with the present disclosure is a vehicle including a tire as described herein. [Brief description of the drawings]

[0044] [Figure 1] FIG. 2 is a partial cross-sectional view of a tire having a sealant layer and a silicone foam noise reduction layer. [Diagram 2] 1 is a graph illustrating the noise absorption performance of a tire over a range of frequencies. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0045] Turning now to Figure 1, there is shown a cross-section of a tire 10. Tire 10 is a pneumatic tire of the type used on passenger cars and other vehicles. Figure 1 is a partial cross-sectional view of one side of tire 10.

[0046] The tire 10 includes a tread portion 12 that is disposed in contact with the road surface. The tread portion 12 is disposed radially outward of the tire 10. The tire 10 also includes bead portions 14 that are disposed radially inward of the tire 10. The bead portions 14 are disposed to connect the tire to a hub or wheel (not shown). The tire 10 also includes sidewall portions 16 that extend between and connect the tread portion 12 and the bead portions 14. The tread portion 12, the bead portions 14, and the sidewall portions 16 collectively define an interior cavity of the tire 10. The tire cavity is pressurized during use.

[0047] The tread portion 12 comprises a tread designed to engage and grip the road surface during use. A sealant layer 18 is disposed on an inner surface of the tread portion 12. The sealant layer 18 is disposed to cover at least a portion, or in some cases, substantially the entire inner surface of the tread 12. The sealant layer 18 is configured to repair damage caused to the tread 12 during use, for example, due to a puncture.

[0048] The sealant layer 18 accomplishes this due to the layer's viscous and adhesive properties that enable it to flow into the puncture or hole in the tread 12, seal the puncture and prevent pressure loss in the tire 10. The sealant layer 18 can act to seal punctures up to 5 mm in size, even if the object that punctured the tire is removed.

[0049] The sealant used to form the sealant layer 18 has a tack that ensures adhesion to both the interior of the tread 12 of the tire 10 and to the noise reduction layer 20 without the need for an additional adhesive layer. This means that there are only two layers within the tire tread 12 instead of three.

[0050] Exemplary properties of sealant materials suitable for use as a sealant layer that provide adequate sealing performance are shown in Table 1 below. [Table 1]

[0051] In some examples, the adhesion may be from 5 to 20N.

[0052] The bead portions 14 include reinforcing members 22 located inside cavities formed within the bead portions 14 and which provide, for example, strength and stiffness to the tire 10 .

[0053] The sidewall portion 16 includes sidewalls on both sides of the tire 10 .

[0054] The tire 10 further includes a noise reduction layer 20. The noise reduction layer 20 is located on the sealant layer 18 such that the sealant layer 18 is sandwiched between the tread portion 12 and the noise reduction layer 20. In this example, the noise reduction layer 20 is centrally located with respect to the center plane of the tire 10. This is seen to improve the balance and rolling stability of the tire 10. In the example of FIG. 1, the noise reduction layer 20 extends over a majority of the sealant layer 18 (e.g., in a direction parallel to the tire's rotational axis and / or in a circumferential direction). In other examples, the noise reduction layer 20 may extend over the entire sealant layer 18 or over only a small portion of the sealant layer 18.

[0055] In this example, a substantially cubic shaped noise reduction layer 20 is used. Such a configuration is convenient to allow the noise reduction layer 20 to be made and transported in rolls. However, in other examples, alternative shapes of noise reduction layer may be employed. For example, the noise reduction layer may have a triangular or trapezoidal cross section, or may have surface undulations or surface variations in thickness parallel to the radius of the tire.

[0056] The noise reduction layer 20 is configured to absorb vibrations of the tire 10 during use, thereby dampening vibration noise of the tire 10. This noise is generated by the air within the tire 10 being vibrated by external inputs such as contact with the road surface and deformation of the tire tread portion 12. The majority of this excitation and noise, typically referred to as tire cavity noise, is in the frequency band between 200 Hz and 250 Hz.

[0057] In this example, the noise reduction layer 20 is made from silicone foam, which has low adhesion while also having good noise reduction properties. This means that the silicone foam provides good noise absorption and, critically, does not interfere with the sealing of the sealant layer. Thus, the use of silicone foam provides the tire 10 with both good self-sealing and noise reduction properties.

[0058] In the example of FIG. 1, an open-cell silicone foam is used as the noise reduction layer 20. The use of the open-cell silicone foam allows the sealant material to penetrate inside the open-cell structure of the silicone foam, thus achieving a "mechanical bond". Here, the silicone foam is bonded to the sealant by the penetration of the sealant into the foam structure. This allows the sealant to improve the overall adhesion in both the lateral and radial directions without adhering to the surface of the foam itself. This minimizes foam movement even during large deformations of the tire 10. However, the sealant still flows freely against the silicone foam, so the sealing properties are largely unaffected.

[0059] A lower density silicone foam is used, which reduces the overall weight of the tire.

[0060] Sealing tests were carried out on tires with only sealant, tires with sealant and a PU foam noise reducing layer, and tires with sealant and a silicone foam noise reducing layer, and the results are shown in Table 2 below.

[0061] The test conditions for indoor testing were as follows: Tire size: 215 / 65 R17; Inflation pressure: 2.5 bar; Test speed: 100 km / h; Tire load: 500 kg; Test drum diameter: 2 m; Test room temperature: 38 °C.

[0062] The test conditions for outdoor testing were as follows: Tyre sizes: a.) 215 / 65 R17 and b.) 235 / 55 R19; Inflation pressure: 2.5 bar; Test speed: 100 km / h; Tyre load: 500 kg; Test vehicle: VW Tiguan, or equivalent in the same compact SUV segment; Ambient temperature range 1: -25°C to -5°C (tested in tyre size a.)) and ambient temperature range 2: 20°C to 40°C (tested in tyre size b.)).

[0063] The passing criterion was a minimum residual inflation pressure of 1.8 bar for a tire that had been driven 1000 km with a nail in the tread, then the nail was removed, driven an additional 400 km, and stored for 14 days. As shown in the table, the use of the silicone foam noise reduction layer resulted in good sealing performance. On the other hand, the use of the PU foam noise reduction layer did not result in good sealing performance. This is because the PU foam noise reduction layer was adversely affected by the disadvantages described herein. That is, the PU foam noise reduction layer may have prevented the sealant layer from functioning, thereby suppressing proper sealing. The silicone foam noise reduction layer, however, does not interfere with the performance of the sealant layer. [Table 2]

[0064] Turning now to Figure 2 and Table 3 below, the absorption (i.e., absorption coefficient or rate) from the use of a 25mm thick silicone foam noise reduction layer is compared to similar 25mm and 30mm PU foam noise reduction layers of the same diameter. Figure 2 plots the noise absorption rate over the frequency range of 100-350Hz for the three noise reduction layers. Table 3 below shows representative values ​​for noise reduction over the range of 200-250Hz, which is the predominant frequency range for noise caused by tire cavity vibrations. It can be seen that the silicone foam noise reduction layer outperforms not only the PU noise reduction layer of corresponding dimensions, but also the larger PU noise reduction layer.

[0065] Absorption is measured according to ISO 10534-2. [Table 3]

[0066] Table 4 presents the noise level difference in decibels during an outdoor road test, the so-called interior noise test, performed by driving a vehicle of the compact SUV segment on a rough road at a constant speed. The indicated value in dB(A) is the arithmetic average of the measurements of microphones positioned at the driver's left ear and at the front passenger's right ear. The test tire size was 235 / 55 R19.

[0067] The results for a silicone foam noise reducing layer having a thickness of 25mm are compared to the results of a corresponding tire having a 30mm PU foam noise reducing layer. The results are shown as a reduction in decibel levels relative to an identical tire without the foam noise reducing layer. As shown in the table, the silicone foam noise absorbing layer is significantly more effective than the PU foam noise absorbing layer. [Table 4]

[0068] The improved performance of the silicone foam noise reduction layer allows for a reduction in the thickness of the noise reduction layer in the tire.

[0069] Silicone foams suitable for use as noise reduction layers may have a wide range of operating temperatures, for example, from −40 to +100° C. or +150° C. The silicone foams may also have low compression set values, for example, less than 5%, or more preferably less than 2%.

[0070] An example of a silicone foam suitable for use in the silicone foam noise reduction layer is Rogers® MF1-35®.

[0071] Suitable properties of silicone foam for use as the silicone foam noise reduction layer are given in Table 5. [Table 5]

[0072] The compression set reading indicates the material's ability to return to its original shape after being compressed under a load, which is preferred as it allows the silicone foam to return to approximately its original thickness and shape after deformation.

[0073] The present invention has been described above purely by way of example. Detailed modifications may be made to the invention within the scope of the claims attached hereto. Moreover, it will be understood that the invention is in no way limited to the combination of features shown in the examples described herein. Features disclosed with respect to one example can be combined with features disclosed with respect to a further example.

Claims

1. A tire, A tread portion; A bead portion, a sidewall portion extending between the bead portion and the tread portion; Equipped with the tread, bead, and sidewall portions define an internal cavity of the tire; The tire is a sealant layer disposed on the tread portion of the tire in the internal cavity of the tire; a silicone foam noise reduction layer disposed on the sealant layer in the interior cavity of the tire; and The tire further comprises:

2. 10. The tire of claim 1, wherein the silicone foam noise reduction layer is a cellular silicone foam having an open cell structure.

3. The tire of claim 1 or claim 2, wherein the silicone foam noise reduction layer has an operating temperature range of -40°C to greater than 150°C.

4. The silicone foam noise reduction layer is 105kg / m ３ Density less than Tensile strength greater than 70 kPa; Ultimate elongation greater than 40%; A compression set of less than 5%; and / or Temperature resistance: -40 to +200°C The tire according to any one of claims 1 to 3, having

5. The silicone foam noise reduction layer has a resistance of 60 kg / m ３ A tire according to any one of claims 1 to 4, having a density of less than 0.05%.

6. The tire of any one of claims 1 to 5, wherein the silicone foam noise reduction layer has a compression set of less than 2%.

7. 7. A tire according to claim 1, wherein the silicone foam noise reduction layer has a width of 50-150 mm, a thickness of 15-30 mm and / or extends over 90-100% of the inner circumference of the tire.

8. The tire according to any one of claims 1 to 7, wherein the silicone foam noise reduction layer is centrally located in the sealant layer.

9. The tire of any one of claims 1 to 8, wherein the sealant layer is formed from a single homogenous composition and is configured to adhere to the tread and to the noise reducing layer.

10. The tire according to any one of claims 1 to 9, wherein the sealant layer is sandwiched between the tread portion and the silicone foam noise reduction layer without an intermediary.

11. A tire according to any one of claims 1 to 10, comprising only the sealant layer and a silicone foam noise reduction layer in the internal cavity of the tire.

12. A tire according to any one of the preceding claims, wherein the tire does not comprise a separate adhesive layer, for example in addition to the sealant layer and the silicone foam noise reduction layer.

13. 13. Tire according to any one of the preceding claims, wherein the sealant layer has a viscosity of 50 to 1000 Pa·s at 100°C, a layer thickness of 1 to 6 mm and / or a tack of 0.1 to 25 N.

14. The tire according to any one of claims 1 to 13, wherein the sealant layer comprises butyl rubber, a plasticizer, and a tackifier resin.

15. A vehicle comprising a tire according to any one of claims 1 to 14.