Absorbent articles that conform to the body

Abstract

The absorbent article has an absorbent structure including a liquid-permeable topsheet, a liquid-impermeable backsheet, and an open-cell absorbent foam material disposed between the topsheet and the backsheet. The absorbent article is incrementally stretched along at least first and second stretch directions so that the topsheet and the backsheet each include plastically stretched zones disposed substantially along a first plurality of deformation lines substantially perpendicular to the first stretch direction and a second plurality of deformation lines substantially perpendicular to the second stretch direction. The absorbent foam material is fractured into a plurality of individual foam segments separated from adjacent segments by gaps substantially along the first and second plurality of deformation lines. An adhesive is disposed between the topsheet and the individual foam segments, bonding the individual foam segments to the topsheet.

Description

[Technical Field]

[0001] FIELD OF THE DISCLOSURE The present disclosure relates to body-conforming absorbent articles and methods of making such absorbent articles. [Background technology]

[0002] Women have long used absorbent articles, such as feminine hygiene pads, also known as sanitary napkins, during menstruation to intercept, contain, absorb, and retain menstrual fluid and prevent it from soiling underwear, outerwear, bedding, etc.

[0003] Ideally, feminine hygiene pads should, to adequately perform their intended functions, be: - Fits snugly to the wearer's body, blocking discharged fluids that move along the skin surface and prevent leakage from the pad; Easily accepts and draws in expelled fluids, · Absorbs fluids easily, - have sufficient absorption capacity for the duration of wear and discharge rate for reasonable convenience to the wearer / user; Prevents absorbed fluids from wicking up from the absorbent material to the surface facing the wearer (which can result in an undesirable wet feel on the wearer's skin); - prevent absorbed fluid from being squeezed out of the pad when pressure is applied to the pad, for example by moving or sitting; and While worn, it stays securely in place inside the wearer's underwear and moves with the wearer's body, allowing the underwear fabric to stretch and move.

[0004] Additionally, many users prefer that the pad be relatively small and / or thin (having a relatively small surface area and / or low bulk or thickness) in some circumstances so as to be unnoticeable when worn under tight-fitting outer and / or revealing clothing. Users also typically prefer that the pad be comfortable to wear, i.e., soft-feeling, flexible, and / or "breathable," i.e., vapor-permeable (to allow water vapor to escape, so that the pad does not feel uncomfortably warm and / or to prevent overhydration of the wearer's skin area beneath the pad during wear).

[0005] Because these objectives are somewhat conflicting, it will be appreciated that it is difficult to design a feminine hygiene pad having a combination of component materials and construction that perfectly meets all of these objectives. For example, achieving sufficient absorbent capacity generally requires a minimum volume and / or amount of absorbent material, which may result in small size, low bulk / thickness, and sacrifice flexibility or conformability. As another example, absorbent materials currently used in many feminine hygiene pads, including combinations that include cellulose fibers, are effective for the purposes of fluid wicking and absorbency, but do not contribute to (and often hinder) the construction of a pad that is particularly flexible, conformable, or body-compatible. Summary of the Invention [Problem to be solved by the invention]

[0006] Thus, there remains room for improvement in the combination of component materials and construction of feminine hygiene pads that more effectively meet more of the above-identified objectives. [Means for solving the problem]

[0007] Described herein is an absorbent article comprising: a liquid-permeable topsheet having longitudinal and lateral axes, a garment-facing surface, and an opposite wearer-facing surface; a liquid-impermeable backsheet having a garment-facing surface and an opposite wearer-facing surface; and an absorbent structure comprising an open-cell absorbent foam material disposed between the topsheet and the backsheet. The absorbent article is incrementally stretched along at least a first stretch direction and a second stretch direction different from the first stretch direction, the topsheet and the backsheet each comprising plastically stretched zones disposed substantially along a first plurality of deformation lines substantially perpendicular to the first stretch direction and a second plurality of deformation lines substantially perpendicular to the second stretch direction. The absorbent foam material is fractured into a plurality of individual foam fragments substantially along the first and second plurality of deformation lines, the individual foam fragments being separated from adjacent fragments by gaps. An adhesive of about 15 gsm to about 35 gsm is disposed between the garment-facing surface of the topsheet and the wearer-facing surface of the individual foam pieces to bond the individual foam pieces to the topsheet.

[0008] Also described herein is an absorbent article comprising: a liquid-permeable topsheet having longitudinal and lateral axes, a garment-facing surface, and an opposite wearer-facing surface; a liquid-impermeable backsheet having a garment-facing surface and an opposite wearer-facing surface; and an absorbent structure comprising an open-cell absorbent foam material disposed between the topsheet and the backsheet. The topsheet and the backsheet each comprise plastically stretched zones disposed substantially along a first plurality of deformation lines extending in a first direction and a second plurality of deformation lines extending in a second direction. The first plurality of deformation lines form an angle α with the longitudinal axis, and the second plurality of deformation lines form an angle β with the longitudinal axis, with angles α and β each being between about 5 and 85 degrees. The absorbent structure comprises a plurality of individual foam segments disposed along the deformation lines, the individual foam segments being separated from adjacent segments by gaps of between 0.3 and 1.2 mm.

[0009] Also described herein is an absorbent article comprising a liquid-permeable topsheet having longitudinal and lateral axes, a liquid-impermeable backsheet having a basis weight of about 20 gsm to about 28 gsm, and an absorbent structure comprising a high internal phase emulsion foam disposed between the topsheet and the backsheet. The topsheet and the backsheet each comprise plastically stretched zones, with a portion of the plastically stretched zones extending continuously from a first side of the topsheet to a second side of the topsheet. The absorbent structure comprises a plurality of individual foam segments arranged in a pattern extending throughout the absorbent structure, the individual foam segments being separated from adjacent segments by gaps greater than 0.1 mm. [Brief explanation of the drawings]

[0010] [Figure 1] FIG. 1 is a plan view of an example absorbent article in the form of a feminine hygiene pad, with the wearer-facing surface facing the reader, illustrating an example pattern of bidirectional deformation. [Figure 2] FIG. 1 is a plan view of an example of an absorbent article in the form of a feminine hygiene pad showing various other features, with the wearer-facing surface facing the reader. [Figure 3A] 1A-1C are schematic plan views of some possible non-limiting examples of patterns of placement of bond regions between the topsheet and underlying components of an absorbent article. [Figure 3B] 1A-1C are schematic plan views of some possible non-limiting examples of patterns of placement of bond regions between the topsheet and underlying components of an absorbent article. [Figure 3C] 1A-1C are schematic plan views of some possible non-limiting examples of patterns of placement of bond regions between the topsheet and underlying components of an absorbent article. [Figure 3D] FIG. 10 is a schematic plan view of another possible example of a pattern of adhesive deposits for forming bond areas between the topsheet and underlying components of the absorbent structure. [Figure 4A] 4A is a schematic transverse cross-sectional view of the article shown in FIG. 1 taken along line 4A-4A of FIG. 1. [Figure 4B]4B is an enlarged view of the portion of FIG. 4A shown within circle 4B in one possible example. [Figure 4C] 4B is an enlarged view of the portion of FIG. 4A shown within circle 4B in FIG. 4A, in another possible example. [Figure 4D] 4B is an enlarged view of the portion of FIG. 4A shown within circle 4B in FIG. 4A, in another possible example. [Figure 5] FIG. 10 is a plan view of another example absorbent article in the form of a feminine hygiene pad showing an example pattern of bidirectional deformation, with the wearer-facing surface facing the reader. [Figure 6] FIG. 1 is an enlarged view of the arrows showing the direction of the stretch and deformation lines along the xy plane relative to the longitudinal and transverse axes of the absorbent structure. [Figure 7] FIG. 1 is a plan view of another example of an absorbent article in the form of a feminine hygiene pad showing certain features, with the wearer-facing surface facing the reader. [Figure 8] FIG. 1 is a simplified schematic side view of components arranged for a process for deforming a composite web. [Figure 9] FIG. 10 is a perspective view of an example of a pair of deforming rollers. [Figure 10] FIG. 10 is a diagram of an engagement feature of a pair of deforming rollers. [Figure 11] FIG. 11 is a detailed view of the feature shown in FIG. 10 shown acting on a web. [Figure 12] FIG. 2 is a schematic cross-sectional view (along the z-direction plane) of an example of a deformed web. [Figure 13] FIG. 10 is a view along the machine direction of another example pair of deforming rollers. [Figure 14] FIG. 10 is a view along the machine direction of another example pair of deforming rollers. [Figure 15A] FIG. 10 is a view along the machine direction of another example pair of deforming rollers. [Figure 15B] FIG. 10 is a view along the machine direction of another example pair of deforming rollers. [Figure 16A] FIG. 10 is a view along the machine direction of another example pair of deforming rollers. [Figure 16B]FIG. 10 is a view along the machine direction of another example pair of deforming rollers. [Figure 17] FIG. 1 is a schematic diagram of an apparatus used in the fit force measurement method described herein. [Figure 18] FIG. 1 is a schematic diagram of the apparatus used in the capillary working potential via pore volume distribution method described herein. [Figure 19] 1 is a photographic reproduction of an absorbent article in the form of a feminine hygiene pad with an example of a bidirectional deformation pattern, with the side facing the wearer facing the reader. [Figure 20] 20 is a reproduction of a portion of a photograph of a transverse cross-sectional cut of the absorbent article shown in FIG. 19, shown adjacent to a ruler with centimeter / millimeter divisions. [Figure 21A] 1 is an enlarged schematic cross-sectional view along a plane along the z-direction of a portion of an absorbent article including two adjacent pieces of absorbent structure shown in a flat configuration. [Figure 21B] 1 is an enlarged schematic cross-sectional view along a plane along the z-direction of a portion of an absorbent article including two adjacent pieces of absorbent structure shown in a bent configuration. [Figure 22A] 1 is an enlarged schematic cross-sectional view along a plane along the z-direction of a portion of an absorbent article including two adjacent pieces of absorbent structure shown in a flat configuration. [Figure 22B] 1 is an enlarged schematic cross-sectional view along a plane along the z-direction of a portion of an absorbent article including two adjacent pieces of absorbent structure shown in a bent configuration. [Figure 23] FIG. 1 is a cross-sectional view of a line contact grip used in the high speed tensile testing herein. [Figure 24] FIG. 1 is a perspective view of a pair of opposing line contact grips for use in the high speed tensile testing herein. [Figure 25] FIG. 1 is a graphical representation of a preferred deformation regime for high speed tensile testing herein. DETAILED DESCRIPTION OF THE INVENTION

[0011] definition For purposes herein, the following terms have the following meanings:

[0012] "Absorbent article" means a layered product that includes an absorbent structure and is configured to be worn about the lower torso and / or externally in the crotch region of a human being and is configured to contain and / or absorb bodily exudates, which may include urine, menstrual fluids, or feces. Examples of absorbent articles include feminine hygiene pads (also known as menstrual pads or sanitary napkins), panty liners, menstrual undergarments, incontinence pads, absorbent undergarments (e.g., configured to manage incontinence), diapers, and training pants.

[0013] "Bidirectional" refers to the orientation of two axes in the xy plane that intersect at the smaller angle in the range of 20 degrees to 90 degrees, with respect to a layered composite web structure or any layer component thereof.

[0014] A web, sheet, or film material, or laminate or composite thereof, is considered to be "extensible" for purposes herein if, when a tensile force of 50 gf / mm (gf per mm of sample width, the width being measured perpendicular to the stretch direction) or less is applied to the material along the stretch direction, the material can be stretched along that direction to an elongated dimension of at least 110% of its original relaxed dimension (i.e., can be stretched to at least 10% of its original relaxed dimension) without substantial fracture or breakage that would substantially damage the web, sheet, or film material, or laminate or composite thereof. For purposes herein, plastic deformation is not considered substantial damage.

[0015] For purposes of this specification, a web, sheet or film material, or laminate or composite thereof, is "elastic" or "elastically extensible" for purposes of this specification if, when a tensile force of 50 gf / mm (gf per mm of sample width, the width being measured perpendicular to the stretch direction) or less is applied to the subject material along the stretch direction, the material can be stretched along the direction to an elongated dimension of at least 110% of its original relaxed dimension (i.e., can be stretched to at least 10% of its original relaxed dimension) without breakage or rupture that would substantially damage the subject web, sheet or film material, or laminate or composite thereof, and when the force is removed from the subject material, the material retracts along the stretch direction to recover at least 40% of such elongation. For example, a piece of fabric having an original relaxed length of 100 mm and a width of 40 mm is "elastic" as defined herein if it can be stretched without substantial damage along its length by a tensile force of 2000 gf (50 gf / mm) to a length of 110 mm, and upon removal of the force, retracts to a length of 106 mm or less (110 mm - 106 mm = 4 mm = 40% of 10 mm). As used herein, "extension" quantifies and describes the amount of strain imparted to an elastic material in the direction of stretch, and means [(strand stretched length - strand length before stretching) / (strand length before stretching)] x 100%.

[0016] "Joined" encompasses both an arrangement in which an element is directly secured to another element by directly attaching the element to the other element, and an arrangement in which an element is indirectly secured to another element by attaching the element to an intermediate member(s) and then attaching the intermediate members to the other element.

[0017] "Lateral direction," with respect to an absorbent article or a component thereof, refers to a direction parallel to a horizontal line tangent to the front of the upper parts of the wearer's legs adjacent the torso when the article is normally worn and the wearer is standing evenly, upright, and in a normal standing position. The "width" dimension of any component or feature of the absorbent article is measured along the lateral direction. When the absorbent article or a component thereof is placed flat on a horizontal surface, the "lateral" direction corresponds to the lateral direction for the structure when it is worn, as defined above. With respect to an absorbent article placed open and flat on a horizontal plane, "lateral direction" refers to a direction perpendicular to the longitudinal direction and parallel to the horizontal plane.

[0018] The "lateral axis" of an absorbent article or component thereof is the horizontal line that lies in the xy plane and divides the length of the article or component when the article or component is laid open and flat on a horizontal surface. The lateral axis is perpendicular to the longitudinal axis.

[0019] "Longitudinal" refers to the direction perpendicular to the lateral direction with respect to an absorbent article or component thereof. The "length" dimension of any component or feature of a layered absorbent structure is measured along the longitudinal direction from its front extent to its rear extent. When an absorbent article or component thereof is placed flat on a horizontal surface, the "longitudinal" direction, as defined above, is perpendicular to the lateral direction for the structure when it is worn.

[0020] The "longitudinal axis" of an absorbent article or component thereof is the longitudinal line that lies in the xy plane and divides the width of the article when the article is laid open and flat on a horizontal surface. The longitudinal axis is perpendicular to the lateral axis.

[0021] "Liquid impermeable" refers to one or more properties or characteristics of a film, web material, or laminate thereof that cause it to resist the passage of aqueous liquids (from one major surface to the other opposing major surface) under normal conditions of use in an absorbent article. A film, web material, or laminate thereof may be liquid impermeable, but may also be vapor permeable ("breathable").

[0022] "Machine direction," with respect to a process for manufacturing a web material or a laminate or layered arrangement of web materials, refers to the primary direction of material transport along the production line as viewed from above the production line. It will be understood that the machine direction may vary in absolute directional orientation in space at particular locations along the line, if the production line is so configured. With respect to the nip between an individual roller or pair of rollers along which a web material or combination of web materials is transported, laminated, or deformed on the production line, the "machine direction" is typically perpendicular to the axis of the roller, and the "cross direction" is typically parallel to the axis of the roller.

[0023] "Permanently mechanically deformed" means being plastically deformed, crushed, or broken, or having individual fiber components plastically deformed, crushed, broken, and / or directionally realigned or reoriented, by the application of a mechanical force.

[0024] With respect to an absorbent article or component thereof, "xy plane" means the horizontal surface of the article or component or any horizontal plane occupied by any layer thereof when laid flat on a horizontal surface.

[0025] With respect to an absorbent article or component thereof, the "z-direction" is the direction perpendicular to the xy-plane when the article is laid flat on a horizontal surface. When the article is being worn by a user (and thus biased into a curved configuration), the "z-direction" at any particular point on the pad refers to the direction perpendicular to the wearer-facing surface of the pad at the particular point.

[0026] With respect to an absorbent article or components thereof, the terms "front", "rear", "fore" and "rear" and similar relative positional terms refer to the position normally worn by a user and to the features or areas of the pad that correspond to the front (anterior) and rear (posterior) sides of the wearer / user's body when standing upright.

[0027] With respect to absorbent articles, "wearer-facing" is a relative positional term that refers to a component or structural feature of the article that, during use, is closer to the wearer than another feature of the component or structure that is located along the same z-direction. For example, a topsheet has a wearer-facing surface that is located closer to the wearer than the opposite, outward-facing surface of the topsheet.

[0028] With respect to absorbent articles, "outward-facing" (also referred to herein as "garment-facing") is a relative positional term that refers to a component or structural feature of the article that, during use, is farther from the wearer than another feature of the component or structure that is located along the same z-direction. For example, a topsheet has an outward-facing surface that is located farther from the wearer than an opposite wearer-facing surface of the topsheet.

[0029] The terms "top," "bottom," "upper," "lower," "above," "below," "lower," "adjacent above," "adjacent below," and similar terms relating to vertical position, when used herein to refer to a layer, component, or other feature of a wearable absorbent article, should be interpreted relative to the article as it appears when laid open and flat on a horizontal surface, with the surface facing the wearer oriented upward and the surface facing outward oriented downward.

[0030] explanation The present disclosure relates to absorbent articles, and more particularly, to absorbent articles with improved flexibility and conformability. In some configurations, the absorbent article may include a liquid-permeable topsheet, a liquid-impermeable backsheet, and an absorbent structure disposed between the topsheet and the backsheet. The absorbent structure may be incrementally stretched along with one or both of the topsheet and the backsheet, causing permanent deformation of the topsheet and / or the backsheet and fracture of the absorbent structure into individual pieces. Surprisingly, it has been discovered that absorbent articles with non-orthogonal bidirectional deformation move more easily and adapt to the wearer's body movements (e.g., walking) when adhered to the inside of a wearer's undergarments. The absorbent articles described herein can bend, flex, and stretch along with the wearer's undergarments, allowing the article to remain in intimate contact with the body as the wearer moves, creating a more comfortable experience for the wearer while still maintaining the individual pieces of the absorbent structure in place.

[0031] 1 and 4A, an absorbent article 10 (referred to herein as a feminine hygiene pad) can include a liquid-permeable topsheet 20, a liquid-impermeable backsheet 30, and an absorbent structure 40 disposed between the topsheet and backsheet. The absorbent structure has a perimeter 40a. In the area outside the perimeter 40a, the topsheet and backsheet can be bonded together in a laminated configuration by any suitable mechanism, including, but not limited to, adhesive bonding, thermal bonding, pressure bonding, etc., to maintain and retain the absorbent structure 40 in the enclosed space between the topsheet 20 and backsheet 30. The article 10 can also include opposed wing portions 15 extending laterally outside the perimeter 40a with width dimensions that are relatively greater than the frontmost and rearmost portions of the pad. The outer surface of the backsheet, which forms the underside of the main and wing portions 15, can have a deposit of adhesive 35 thereon. Adhesive deposit 35 is provided to enable a user to adhere the pad to the inside of their undergarment in the crotch region and wrap wing portions 15 through and around the inside edges of the leg openings of the undergarment, adhering them to the outside / underside of the undergarment in the crotch region, and can provide additional support and help protect the inside leg edges of the undergarment from soiling. Once article 10 is packaged, adhesive deposit 35 may be covered by one or more sheets (not shown) of release film or paper, which covers / shields adhesive deposit 35 from contact with other surfaces until the user removes the release film or paper and places the pad within the undergarment for donning / use.

[0032] Top sheet The topsheet 20 may be formed from any suitable nonwoven web material having plastic / inelastic extensibility suitable for the purposes described herein. Referring again to the Figures, the topsheet 20 is positioned adjacent to the wearer-facing surface of the absorbent structure 40 and may be joined thereto and to the backsheet 30 by any suitable attachment or bonding method. The topsheet 20 and backsheet 30 may be joined directly to each other in a peripheral region outside the periphery 40a of the absorbent structure 40, or may be joined indirectly by being directly bonded to the wearer-facing and outward-facing surfaces of the absorbent structure, respectively.

[0033] The article 10 can have any known or otherwise effective topsheet 20, such as one that is conformable, soft-feeling, and non-irritating against the wearer's skin. Suitable topsheet materials include liquid-permeable materials that are comfortable in contact with the wearer's skin and allow discharged menstrual fluid to rapidly permeate therethrough. Suitable topsheets can be made from any of a variety of materials, such as woven or knitted materials, nonwoven web materials, or apertured films.

[0034] Non-limiting examples of nonwoven web materials that may be suitable for use in forming the topsheet 20 include fibrous materials made from natural fibers, modified natural fibers, synthetic fibers, or combinations thereof. Some suitable examples are described in U.S. Patent Nos. 4,950,264, 4,988,344, 4,988,345, 3,978,185, 7,785,690, 7,838,099, 5,792,404, and 5,665,452. Particularly suitable topsheet materials may include spunbond nonwoven materials comprising polyethylene (PE) / polypropylene (PP) bicomponent fibers (PE sheath and PP core).

[0035] In some configurations, the topsheet may be a highly extensible nonwoven web comprising staple or continuous multicomponent fibers, such as those described in U.S. Patent Application Publication No. 2020 / 0337910(A1). Highly extensible nonwoven webs may be beneficial for reducing fiber breakage during mechanical processing, which can cause the nonwoven web to experience high strain forces, for example, during incremental stretching processes. In the context of absorbent articles, this may have the desirable effect of reducing the amount of broken fibers that adhere to the wearer's skin. In some configurations, the topsheet may comprise a first polymer component having a first melting temperature and a second polymer component having a second melting temperature. The first polymer component may have a low crystallinity of, for example, about 10% to about 41%, about 15% to about 38%, about 20% to about 35%, about 25% to about 33%, or about 28% to about 30%, including all 0.1% increments within the specified ranges and all ranges formed therein or therefrom. Crystallinity may be measured in fibers or nonwoven webs comprising the fibers according to the Crystallinity Test disclosed herein. The first polymer component may have a melting temperature of, for example, about 130°C to about 161°C, about 130°C to about 155°C, or about 135°C to about 155°C, including all 0.1°C increments within the specified ranges and all ranges formed therein or therefrom. Without wishing to be bound by theory, it is believed that polymers with low crystallinity may increase fiber extensibility by increasing the ultimate tensile strength of the fiber. In one example, the first polymer of the multicomponent fibrous nonwoven web may be polypropylene having a crystallinity of about 20% to about 41%. In another example, the first polymer of the multicomponent fibrous nonwoven web may be polyethylene terephthalate having a crystallinity of about 20% to about 41%. The second polymer component may have a high crystallinity of, for example, about 40% to about 80%, about 45% to about 75%, about 50% to about 70%, or about 55% to about 65%, including all 0.1% increments within the specified ranges and all ranges formed therein or thereby.Without being bound by theory, it is believed that polymers with high crystallinity can increase the tensile strength of fibers and nonwoven webs containing such fibers. The second polymer component may optionally have a melting temperature that is the same as or lower than the melting temperature of the first polymer component. In one example, polyethylene may be the second polymer component of a multicomponent continuous fiber.

[0036] In the context of nonwoven webs comprising continuous bicomponent fibers, the first polymer component may be or may include polypropylene having a crystallinity of about 20% to about 41%. The polypropylene may have a melting temperature of about 130°C to about 161°C. The second polymer component may be or may include polyethylene having a crystallinity of about 45% to about 75%. The polyethylene may have a crystallization rate of about 1300 ms to about 1360 ms. The polyethylene may have a melting temperature of about 100°C to about 140°C. The bicomponent fibers may have a core / sheath configuration, with the polypropylene forming the core of the fiber and the polyethylene forming the sheath of the fiber, partially or completely surrounding the polypropylene core. Without being bound by theory, it is believed that the use of low crystallinity polypropylene fiber cores can produce nonwoven webs with improved tensile properties, including increased extensibility. Additionally, it is believed that a sheath material with high crystallinity and fast crystallization time that partially or completely surrounds the core material during fiber spinning can protect the core material and achieve a more amorphous structure in the finished fiber.

[0037] In another example, the first polymer component of the bicomponent continuous fiber can be polyethylene terephthalate (PET) having a crystallinity of about 20% to about 41%. The second polymer component can be polyethylene. The continuous fiber can include a core / sheath structure in which the PET can form the core of the fiber and the polyethylene can partially or completely surround the PET and form the sheath of the fiber.

[0038] In some configurations, the topsheet may comprise a highly extensible nonwoven web having an extensibility of about 300% to about 500%, about 305% to about 450%, about 310% to about 425%, about 315% to about 400%, or about 320% to about 375% according to a high-speed tensile test, including all 1% increments within the specified ranges and all ranges therein or formed thereby. Highly extensible nonwoven webs having extensibility within the above ranges can be beneficial in reducing fiber breakage during mechanical processing, which can cause the nonwoven web to be subjected to high strain forces. Reduced fiber breakage can result in a stronger nonwoven web with reduced lint.

[0039] In some configurations, the topsheet 20 may include multiple apertures. In some configurations, it may be preferable to have a topsheet that does not include apertures to help prevent foam pieces from leaking out of the article during use.

[0040] In some configurations, the topsheet 20 has a tensile strength of about 10 gsm (as used herein, "gsm" stands for "grams per square meter"). 2 ") to about 50 gsm, about 22 gsm to about 45 gsm, or about 25 gsm to about 30 gsm, specifically including all values ​​within these ranges or any ranges generated thereby.

[0041] In some configurations, the topsheet 20 can include a tufted structure as described in U.S. Patent Nos. 8,728,049, 7,553,532, 7,172,801, 8,440,286, 7,648,752, and 7,410,683. The topsheet 20 may have a pattern of individual hair-like fibrils as described in U.S. Patent Nos. 7,655,176 or 7,402,723. Additional examples of suitable topsheet materials include those described in U.S. Patent Nos. 8,614,365, 8,704,036, 6,025,535, and U.S. Patent Application Publication No. 2015 / 041640. Another suitable topsheet may be formed from a three-dimensional substrate as detailed in U.S. Patent Application Publication No. 2017 / 0258647. The topsheet may have one or more layers, as described in U.S. Patent Application Publication Nos. 2016 / 0167334, 2016 / 0166443, and 2017 / 0258651.

[0042] As contemplated herein, the component nonwoven web material from which the topsheet 20 may be cut may be a nonwoven web material that includes, consists primarily (by weight), or consists entirely of cellulosic plant fibers, such as cotton, flax, hemp, jute, or mixtures thereof, that are either naturally hydrophilic or have been suitably processed to be hydrophilic (or have increased hydrophilicity) and have been treated to have a suitably soft feel against the skin. In some configurations, plant fibers may be preferred to appeal to consumer preferences for natural products. In other examples, semi-synthetic fibers derived from cellulosic materials such as rayon (for purposes of this specification, "rayon" includes viscose, lyocell, MODAL (a product of Lenzing AG, Lenzing, Austria), and cuprammonium rayon) may be included as a component of the nonwoven.

[0043] The nonwoven web may be formed via any suitable process in which finite length fibers (e.g., staple fibers) can be distributed and deposited in a controlled manner on a forming belt to form a batt having a desired fiber distribution and a desired basis weight. Suitable processes may include carding, air laying, and wet lamination. The batt may be treated to consolidate the fibers and entangle them in the z-direction by processes that may include calendering, needle punching, and hydroentangling.

[0044] In some examples, topsheets cut from nonwovens comprising, consisting primarily (by weight) of, or consisting entirely of vegetable fibers such as cotton fibers may be preferred. In some examples, the nonwoven web material may be formed by a carding process. In other examples, the nonwoven web material may be formed by an air-laying or wet-laminating process. In some examples, the nonwoven web material may be a spunbond web comprising monocomponent continuous fibers spun from a polymer resin, or alternatively, bicomponent or multicomponent fibers, or a blend of monocomponent fibers spun from different polymer resins, or any combination thereof. In some examples, the web may be formed by a co-forming process, in which finite length vegetable fibers are physically blended or mixed with a stream of long but indefinite length spun fibers spun from a polymer resin and placed on a forming belt to form a web. Co-forming processes are described, for example, in U.S. Pat. No. 8,017,534, U.S. Pat. No. 4,100,324, U.S. Patent Application Publication No. 2003 / 0200991, U.S. Pat. No. 5,508,102, U.S. Patent Application Publication No. 2003 / 0211802, European Patent No. 0333228, International Publication No. WO 2009 / 10938, U.S. Patent Application Publication Nos. 2017 / 0000695, 2017 / 0002486, U.S. Pat. No. 9,944,047, U.S. Patent Application Publication Nos. 2017 / 0022643 and 2018 / 0002848.

[0045] To ensure that fluid contacting the top (wearer-facing) surface of the hydrophilic topsheet can be suitably rapidly wicked in the z-direction to the bottom (outward-facing) surface of the topsheet, where it can be drawn into the absorbent structure, it can be important to ensure that the nonwoven web material forming the topsheet has an appropriate weight / volume density, thereby providing suitable gap channels within and between the constituent fibers through which fluid can migrate within the nonwoven material. Nonwovens with fibers that are too tightly consolidated may have an insufficient number and / or volume of gap channels, and the nonwoven may hinder rather than promote rapid fluid movement in the z-direction. In contrast, nonwovens with fibers that are not sufficiently consolidated to provide sufficient fiber-to-fiber contact and / or sufficiently small gap channels may provide insufficient potential for wicking in the z-direction by capillary action. In those instances where the nonwoven web material comprises, or consists primarily or entirely of, cotton fibers, it may be desirable for the web to have a basis weight of from about 20 gsm to about 50 gsm, more preferably from about 25 gsm to about 45 gsm, and even more preferably from about 30 gsm to about 40 gsm, in order to balance the priorities of absorbed fluid barrier and mechanical strength properties (required for processing) and limiting the amount of topsheet material through which liquid must travel in the z-direction to reach the underlying absorbent structure. In combination, the web may have a basis weight of from about 74 kg / m 3 ~Approx. 110kg / m 3 , more preferably about 83 kg / m 3 ~Approx. 101kg / m 3It may be desirable to have a density of about 0.20 mm to about 0.60 mm, where density is calculated as basis weight divided by caliper (thickness in the z-direction measured using the caliper measurement method described below). Alternatively, or in combination with controlling the above values, the caliper of a topsheet material may be controlled to balance the conflicting needs of opacity and loft (requiring a higher caliper) and limiting the z-direction distance that exuded fluid must travel through the topsheet from the wearer-facing surface to the outward-facing surface to reach the underlying absorbent structure. Thus, it may be desirable to control the production of topsheet materials to produce topsheet materials with a caliper of about 0.20 mm to about 0.60 mm, more preferably about 0.25 mm to about 0.55 mm, and even more preferably about 0.30 mm to about 0.45 mm. For purposes of this specification, caliper is measured using the caliper measurement method described below.

[0046] Immediately after separation from the pod, cotton fibers are naturally hydrophobic due to the presence of natural waxes and oily compounds on the surface of the fibers. After ginning to separate the cotton fibers from the seeds, the raw cotton fiber mass (stored and transported as bales) typically contains a significant amount of impurities (particles, plant debris, etc.) trapped within the fiber matrix and / or attached to the waxes and oils, which discolor the cotton fibers and make them unsuitable for many applications. To make raw cotton fibers commercially acceptable for most applications, the fibers must first be processed in several steps to remove impurities. Typical processes also remove natural waxes and oils and make the cotton fibers hydrophilic. While hydrophobic agents such as oils, waxes, or silicones can be reintroduced to make cotton fibers and cotton-based fibrous structures hydrophobic and non-absorbent, for the purposes of this specification, nonporous hydrophobic cotton-based topsheets are inappropriate because they cannot adequately accept and wick away fluid discharge.

[0047] Following treatment to remove impurities, the cotton fiber mass is further mechanically treated to convert it to its intended end-use conditions and structure. Because the fibers are hydrophilic, any mass of treated cotton fibers (whether appearing as a textile / fabric component, paper product, nonwoven web product, or absorbent product) will absorb aqueous fluids to some extent and exhibit capillary wicking properties.

[0048] Rayon fibers are made from regenerated cellulose. At the molecular level, they are chemically similar to cotton fibers. At the fiber level, rayon fibers can be imparted with complex surface topography and substantial curl or crimp, and are naturally hydrophilic. A mass of rayon fibers typically has absorbency properties that exceed those of a comparable mass of cotton fibers.

[0049] Absorbency and wicking performance may vary depending on and be manipulated by how the fibers are further processed. Factors such as the level of compaction (i.e., densification) of the fiber mass in the end structure and the orientation of the individual fibers within the end structure can affect absorbency and wicking performance.

[0050] Thus, for the purposes contemplated herein, in combination with imparting a suitable basis weight, density, and / or caliper as discussed above, it may be desirable for the cotton and / or rayon-based nonwoven web material used to make the topsheet 20 to be formed via a nonwoven web manufacturing process in which the fibers are not primarily forced to orient along the machine direction or xy plane of the web structure's formation, but rather a significant number of fibers are imparted with a directional orientation, including some z-direction orientation. Any suitable process (e.g., spunlaying, airlaying, wet-laid, carding, etc.) in which fibers are distributed and laid in a batt on a horizontal forming belt can be followed by additional process steps that force some or a portion of the fibers to reorient in the z-direction. Suitable process steps may include needlepunching and hydroentangling. Hydroentanglement, in which an array of fine, high-velocity water jets is directed at the batt as it is conveyed past the array of water jets on a perforated belt or drum, may be desirable due to its effectiveness in reorienting the fibers with less fiber breakage and less formation of fiber strings and surface fuzz (free fiber ends extending from the main structure of the web). Vacuum water removal systems (air is drawn through the web in the z-direction and through a pattern of orifices or pores on the drum or belt conveying the batt, pulling the water-jetted water) may be desirable because they tend to create, add, open, and / or pass small z-direction passages, approximately the pattern of orifices or pores, within the fiber matrix of the web. Without intending to be bound by theory, it is believed that increasing the number of fibers (or portions thereof) oriented in the z-direction and the number of z-direction passages increases the web's ability and tendency to wick aqueous fluids in the z-direction. In a topsheet, this would mean that the material may more easily wick aqueous fluids from the wearer-facing surface of the topsheet to the outward-facing surface of the topsheet, i.e., directly downward to the absorbent structure underneath, thereby reducing fluid wicking along the xy-plane direction (which would cause the expelled fluid to spread laterally and / or longitudinally, resulting in staining).

[0051] For purposes of this specification, depending on the degree of xy-planar deformation imparted as described herein, in some circumstances a nonwoven web precursor to the topsheet formed partially, primarily, or even entirely from continuous fibers (also known as "filaments") spun from polymer resins and / or regenerated cellulose (rayon) may be preferred. (As used herein, "continuous" fibers are understood to be fibers that are not cut to staple length, but rather are continuously spun and accumulated without cutting or chopping to form a batt on a moving forming belt in a continuous process. The batt is then consolidated and bonded (e.g., via calendaring and heat compression spot bonding) to form a coherent web. It will be understood that the fibers are not of infinite length, but generally have a variety of indefinite lengths that are substantially longer than the length of staple fibers. Processes for forming such webs are sometimes known as "spunbond" processes and are described in the art.) Without being bound by theory, it is believed that spunbond webs, or topsheets formed therefrom, may be more suitable for the deformation processes described herein because they may allow deformation / plastic extension along the x-y plane while better retaining cohesion and structural integrity than webs formed primarily from staple fibers and / or short length natural plant fibers such as cotton.

[0052] Absorbent structure The absorbent structure 40 of the present disclosure may be provided with any suitable shape, including, but not limited to, an oval, a discorectangle, a rectangle, an asymmetrical shape, and an hourglass shape. For example, in some configurations, the absorbent structure 40 may have a contoured shape, e.g., a shape in which the mid-region is narrower than the end regions. In yet another example, the absorbent structure may include a tapered shape, having a wider portion at one end region of the pad and tapering to a narrower end region at the other end region of the pad. If the article is an absorbent pad intended for use by women, it may be desirable for the rear end region to be wider and the front end region to be narrower. If the article is an absorbent pad intended for use by men, it may be desirable for the rear end region to be narrower and the front end region to be wider. The absorbent structure 40 may have varying stiffness in the longitudinal and lateral directions.

[0053] The configuration and construction of the absorbent structure 40 can vary (e.g., the absorbent structure 40 can have varying caliper zones, hydrophilic gradients, superabsorbency gradients, or acquisition zones of lower average density and lower average basis weight). Additionally, the dimensions and absorbent capacity of the absorbent structure 40 can also be modified to accommodate different wearers. However, the total absorbent capacity of the absorbent structure 40 must be consistent with the design load and intended use of the absorbent article.

[0054] In some configurations, the absorbent structure 40 may include multiple multi-functional layers. For example, the absorbent structure 40 may include a core wrap (not shown) useful for enclosing the other layers. The core wrap may be formed from one or two portions of a nonwoven material, substrate, laminate, film, or other material. In some examples, the core wrap may be formed from a single material or laminate at least partially wrapped around itself.

[0055] The absorbent structure 40 may include one or more adhesives to help secure, for example, absorbent gelling materials / superabsorbent polymers (SAPs) or other absorbent materials contained within the absorbent structure.

[0056] Absorbent structures containing relatively large amounts of SAP with various absorbent structure / core designs are disclosed in U.S. Patent No. 5,599,335, European Patent No. 1,447,066, International Publication No. WO 95 / 11652, U.S. Patent Application Publication No. 2008 / 0312622 A1 to Hundorf et al., and International Publication No. WO 2012 / 052172 and may be used to construct superabsorbent layers.

[0057] Additions to the absorbent structure of the present disclosure are envisioned. In particular, potential additions to current multilayer absorbent structures are described in U.S. Patent Nos. 4,610,678, 4,673,402, 4,888,231, and 4,834,735. The absorbent structure may further include additional layers that mimic a dual-core system, including a chemically stiffened fiber acquisition / distribution structure disposed over the absorbent structure, as detailed in U.S. Patent Nos. 5,234,423 and 5,147,345. These are useful to the extent that they do not negate or compete with the effects of the laminates described below of the absorbent structure of the present invention.

[0058] Further examples of suitable absorbent structures 40 that can be used in the absorbent articles of the present disclosure are described in U.S. Patent Application Publication Nos. 2018 / 0098893 and 2018 / 0098891. Examples of possible suitable configurations are further described and shown in U.S. Patent Application Publication No. 16 / 831,851.

[0059] In some configurations, the absorbent structure 40 may be formed from or include layers of absorbent open-cell foam material. In some examples, the foam material may include at least first and second sub-layers (e.g., 40t, 40b; see FIG. 4D) of absorbent open-cell foam material, the sub-layers being in direct face-to-face contact with one another. In such examples, the wearer-facing sub-layer may be a relatively larger foam material and the outward-facing sub-layer may be a relatively smaller cell foam material, for purposes described in more detail below.

[0060] The open-cell foam material may be a foam material produced by polymerization of the continuous oil monomer phase of a water-in-oil high internal phase emulsion ("HIPE"). For purposes herein, a HIPE is a two-phase water-in-oil emulsion having a water-to-oil ratio greater than about 2.85:1, i.e., about 74 percent water / dispersed phase (by volume). Due to this relatively high ratio of water to oil phase, upon sufficient emulsification to produce foams of the type contemplated herein (i.e., average cell size of 1 to 300 micrometers), the dispersed aqueous phase has the form of polyhedral droplets as a result of compaction, separated by thin film walls formed from the oil / continuous phase. An example of such an open-cell HIPE foam material is found in the absorbent structure of ALWAYS INFINITY brand feminine hygiene pads currently manufactured and sold by The Procter & Gamble Company (Cincinnati, Ohio). The open-cell foam materials described herein may be preferred for the purposes herein because they can be made to be relatively brittle under tension so that they can be cleanly fractured along regular lines to form pieces of approximately or substantially uniform size and shape in the deformation processes described herein.

[0061] The oil phase of the HIPE is continuous and contains the monomer to be polymerized and an emulsifier that aids in the formation and stabilization of the HIPE. The oil phase may also contain one or more photoinitiators. The monomer component may be present in an amount of about 80% to about 99% by weight of the oil phase, and in certain examples, about 85% to about 95% by weight. The emulsifier component, which is soluble in the oil phase and suitable for forming a stable water-in-oil emulsion, may be present in the oil phase in an amount of about 1% to about 20% by weight of the oil phase. The emulsion may be formed at an emulsification temperature of about 20°C to about 130°C, and in certain examples, about 50°C to about 100°C.

[0062] Typically, the monomer may be present in an amount of about 20% to about 97% by weight of the oil phase and may include at least one substantially water-insoluble monofunctional alkyl acrylate or alkyl methacrylate. For example, this type of monomer may include C4 to C18 alkyl acrylates and C2 to C18 methacrylates, such as ethylhexyl acrylate, butyl acrylate, hexyl acrylate, octyl acrylate, nonyl acrylate, decyl acrylate, isodecyl acrylate, tetradecyl acrylate, benzyl acrylate, nonylphenyl acrylate, hexyl methacrylate, 2-ethylhexyl methacrylate, octyl methacrylate, nonyl methacrylate, decyl methacrylate, isodecyl methacrylate, dodecyl methacrylate, tetradecyl methacrylate, and octadecyl methacrylate.

[0063] The oil phase may also contain from about 2% to about 40% by weight of the oil phase, and in one specific example, from about 10% to about 30% by weight of a substantially water-insoluble multifunctional crosslinked alkyl acrylate or methacrylate. This crosslinking comonomer or crosslinking agent is added to impart strength and resilience to the resulting HIPE foam. Examples of this type of crosslinking monomer include monomers containing two or more activated acrylate or methacrylate groups, or combinations thereof. Non-limiting examples of this group include 1,6-hexanediol diacrylate, 1,4-butanediol dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, 1,12-dodecyl dimethacrylate, 1,14-tetradecanediol dimethacrylate, ethylene glycol dimethacrylate, neopentyl glycol diacrylate (2,2-dimethylpropanediol diacrylate), hexanediol acrylate methacrylate, glucose pentaacrylate, sorbitan pentaacrylate, and the like. Other examples of crosslinkers contain mixtures of acrylate and methacrylate moieties, such as ethylene glycol acrylate-methacrylate and neopentyl glycol acrylate-methacrylate. The ratio of methacrylate to acrylate groups in the mixed crosslinker can vary from 50:50 to any other ratio as desired.

[0064] An optional third substantially water-insoluble comonomer can be added to the oil phase in a weight percentage of about 0% to about 15% by weight of the oil phase, and in certain instances, about 2% to about 8% by weight, to modify the properties of the HIPE foam. In certain cases, a "toughening" monomer may be desired, imparting toughness to the resulting HIPE foam. These include monomers such as styrene, vinyl chloride, vinylidene chloride, isoprene, and chloroprene. Without being bound by theory, it is believed that such monomers help stabilize the HIPE during polymerization (also known as "curing"), resulting in a more homogeneous and better-formed HIPE foam with improved toughness, tensile strength, abrasion resistance, and the like. Monomers can also be added to impart flame retardancy, as disclosed, for example, in U.S. Pat. No. 6,160,028. Monomers can be added to impart color (e.g., vinylferrocene), fluorescent properties, radiation resistance, radiation opacity (e.g., lead tetraacrylate), charge dispersion, reflect incident infrared light, absorb radio waves, wet the surface of the HIPE foam struts or cell walls, or any other desired property in the HIPE foam. In some cases, these additional monomers may slow the overall conversion process of the HIPE to a HIPE foam, but this tradeoff is necessary if the desired properties are to be imparted. Therefore, such monomers can also be used to slow down the polymerization rate of the HIPE. Examples of such monomers include styrene and vinyl chloride.

[0065] The oil phase may further contain an emulsifier to promote emulsification and stabilize the HIPE. Examples of emulsifiers used in HIPEs include: (a) sorbitan monoesters of branched C16 to C24 fatty acids; straight-chain unsaturated C16 to C22 fatty acids; and straight-chain saturated C12 to C14 fatty acids, such as sorbitan monooleate, sorbitan monomyristate, and sorbitan monoesters, sorbitan monolaurate, diglycerol monooleate (DGMO), polyglycerol monoisostearate (PGMIS), and polyglycerol monomyristate (PGMIS). monomyristate (PGMM); (b) polyglycerol monoesters of branched C16-C24 fatty acids, linear unsaturated C16-C22 fatty acids, or linear saturated C12-C14 fatty acids, such as diglycerol monooleate (e.g., diglycerol monoester of C18:1 fatty acid), diglycerol monomyristate, diglycerol monoisostearate, and diglycerol monoester; (c) diglycerol monoaliphatic ethers of branched C16-C24 alcohols, linear unsaturated C16-C22 alcohols, and linear saturated C12-C14 alcohols, as well as mixtures of these emulsifiers. See U.S. Patent Nos. 5,287,207 and 5,500,451. Another emulsifier that can be used is polyglycerol succinate (PGS), which is formed from alkyl succinate, glycerol, and triglycerol.

[0066] Such emulsifiers, and combinations thereof, may be added to the oil phase such that they comprise from about 1% to about 20%, in certain instances from about 2% to about 15%, and in certain other instances from about 3% to about 12% by weight of the oil phase. In certain examples, co-emulsifiers may also be used to provide further control of bubble size, bubble size distribution, and emulsion stability, especially at higher temperatures, e.g., above about 65° C. Examples of the co-emulsifier include phosphatidylcholine and phosphatidylcholine-containing compositions, aliphatic betaine, long-chain C12 to C22 divalent aliphatic quaternary ammonium salts, short-chain C1 to C4 divalent aliphatic quaternary ammonium salts, long-chain C12 to C22 dialkoyl(alkenoyl)-2-hydroxyethyl, short-chain C1 to C4 divalent aliphatic quaternary ammonium salts, long-chain C12 to C22 divalent aliphatic imidazolinium quaternary ammonium salts, short-chain C1 to C4 divalent aliphatic imidazolinium quaternary ammonium salts, long-chain C12 to C22 monovalent aliphatic benzyl quaternary ammonium salts, long-chain C12 to C22 dialkoyl(alkenoyl)-2-aminoethyl, short-chain C1 to C4 monovalent aliphatic benzyl quaternary ammonium salts, and short-chain C1 to C4 monohydroxy aliphatic quaternary ammonium salts. In a particular example, ditallow dimethyl ammonium methyl sulfate (DTDMAMS) may be used as a co-emulsifier.

[0067] The optional photoinitiator may comprise from about 0.05% to about 10% by weight of the oil phase, and in some examples, from about 0.2% to about 10% by weight. Small amounts of photoinitiator can allow better light penetration into the HIPE foam, thereby resulting in polymerization deeper within the HIPE foam. However, if polymerization is carried out in an oxygen-containing environment, it may be desirable to have sufficient photoinitiator present to initiate polymerization and overcome oxygen inhibition. Photoinitiators can respond rapidly and efficiently to a light source with the generation of radicals, cations, and other species capable of initiating a polymerization reaction. Photoinitiators selected for use in forming foams within the contemplated scope of the present disclosure can absorb ultraviolet radiation at wavelengths from about 200 nanometers (nm) to about 800 nm, and in certain examples, from about 250 nm to about 450 nm. When a photoinitiator is present in the oil phase, suitable types of oil-soluble photoinitiators include benzil ketals, α-hydroxyalkylphenones, α-aminoalkylphenones, and acylphosphine oxides.Examples of photoinitiators include 2,4,6-[trimethylbenzoyldiphosphine]oxide in combination with 2-hydroxy-2-methyl-1-phenylpropan-1-one (a 50:50 blend of the two is sold as DAROCUR® 4265 by Ciba Specialty Chemicals, Ludwigshafen, Germany); benzil dimethyl ketal (sold as IRGACURE 651 by Ciba Geigy); α-,α-dimethoxy-α-hydroxyacetophenone (sold as DAROCUR® 1173 by Ciba Specialty Chemicals); 2-methyl-1-[4-(methylthio)phenyl]-2-morpholino-propan-1-one (sold as IRGACURE® 907 by Ciba Specialty Chemicals); 1-hydroxycyclohexyl-phenyl ketone (sold as IRGACURE® 907 by Ciba Specialty Chemicals); bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide (sold as IRGACURE 819 by Ciba Specialty Chemicals); diethoxyacetophenone, and 4-(2-hydroxyethoxy)phenyl-(2-hydroxy-2-methylpropyl)ketone (sold as IRGACURE 2959 by Ciba Specialty Chemicals); and oligo[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone] (sold as ESACURE KIP EM by Lamberti spa, Gallarate, Italy).

[0068] The dispersed aqueous phase of the HIPE comprises primarily water and may also comprise one or more components, such as an initiator, a photoinitiator, or an electrolyte, which in certain instances are at least partially water-soluble.

[0069] One component contained in the aqueous phase may be a water-soluble electrolyte. The aqueous phase may contain from about 0.2% to about 40% by weight of the water-soluble electrolyte, and in certain examples, from about 2% to about 20% by weight of the water-soluble electrolyte. The electrolyte minimizes the tendency of primarily oil-soluble monomers, comonomers, and crosslinkers to dissolve in the aqueous phase. Examples of electrolytes include chlorides or sulfides of alkaline earth metals such as calcium or magnesium, and chlorides or sulfides of alkaline earth metals such as sodium. Such electrolytes may include buffers for controlling pH during polymerization, including inorganic counterions such as phosphate, borate, and carbonate, and mixtures thereof. Water-soluble monomers may also be used in the aqueous phase, examples of which include acrylic acid and vinyl acetate.

[0070] Another component that can be included in the aqueous phase is a water-soluble free radical initiator. The initiator can be present in an amount of up to about 20 mole percent based on the total moles of polymerizable monomer present in the oil phase. In certain examples, the initiator can be included in the oil phase in an amount of about 0.001 to about 10 mole percent based on the total moles of polymerizable monomer. Suitable initiators include ammonium persulfate, sodium persulfate, potassium persulfate, 2,2'-azobis(N,N'-dimethyleneisobutylamidine) dihydrochloride, azo initiators, redox couples such as persulfate-bisulfate, persulfate-ascorbic acid, and other suitable redox initiators. In certain examples, the addition of the initiator to the monomer phase can be performed near the end of the emulsification process or immediately after emulsification to reduce the possibility of premature polymerization, which could interfere with the emulsion system.

[0071] The photoinitiator, when present in the aqueous phase, may be at least partially water-soluble and may comprise from about 0.05% to about 10% by weight of the oil phase, and in certain embodiments, from about 0.2% to about 10% by weight. Small amounts of photoinitiator can allow better light penetration into the HIPE foam, thereby resulting in polymerization deeper into the HIPE foam. However, if polymerization is carried out in an oxygen-containing environment, sufficient photoinitiator should be present to initiate polymerization and overcome oxygen inhibition. Photoinitiators can respond rapidly and efficiently to a light source with the generation of radicals, cations, and other species capable of initiating a polymerization reaction. Photoinitiators for use in foam formation within the contemplated scope of the present disclosure can absorb ultraviolet radiation at wavelengths from about 200 nanometers (nm) to about 800 nm, in certain embodiments, from about 200 nm to about 350 nm, and in certain embodiments, from about 350 nm to about 450 nm. When the photoinitiator is contained in the aqueous phase, suitable types of water-soluble photoinitiators can include benzophenones, benzils, and thioxanthones. Examples of photoinitiators include 2,2'-azobis[2-(2-imidazolin-2-yl)propane]dihydrochloride; 2,2'-azobis[2-(2-imidazolin-2-yl)propane]disulfate dehydrate; 2,2'-azobis(1-imino-1-pyrrolidino-2-ethylpropane)dihydrochloride; 2,2'-azobis[2-methyl-N-(2-hydroxyethyl)propionamide]; 2,2'-azobis(2-methylpropionamidine)dihydrochloride; 2,2'-dicarboxymethoxydibenzalacetone, 4,4'-dicarboxymethoxydibenzalacetone, 4,4'-dicarboxymethoxydibenzalcyclohexanone, 4-dimethylamino-4'-carboxymethoxydibenzalacetone; and 4,4'-disulfoxymethoxydibenzalacetone. Other suitable photoinitiators that can be used are described in US Pat. No. 4,824,765.

[0072] In addition to the above-mentioned components, other components may be included in either the water phase or the oil phase of the HIPE. Examples include antioxidants such as hindered phenols and hindered amine light stabilizers; plasticizers such as dioctyl phthalate and dinonyl sebacate; flame retardants such as halogenated hydrocarbons, phosphates, borates, inorganic salts such as antimony trioxide, ammonium phosphate, or magnesium hydroxide; dyes and pigments; fluorescent agents; filler particles such as starch, titanium dioxide, carbon black, or calcium carbonate; fibers; chain transfer agents; odor absorbers such as activated carbon particulates; dissolved polymers; dissolved oligomers; and the like.

[0073] HIPE foams are produced from the polymerization of monomers that comprise the continuous oil phase of the HIPE. In certain examples, a HIPE foam layer may have one or more sublayers (e.g., 40t, 40b, see FIG. 4D) and may be either a homogeneous or heterogeneous open-cell polymeric foam. Homogeneity and heterogeneity refer to different layers within the same HIPE foam, which are similar in the case of homogeneous HIPE foams and different in the case of heterogeneous HIPE foams. Heterogeneous HIPE foams may contain at least two different sublayers that differ in chemical composition, physical properties, or both. For example, these sublayers may differ in one or more of foam density, polymer composition, specific surface area, or pore size (also called cell size). For example, in HIPE foams that differ in pore size, the average pore size of each sublayer may differ by at least about 20%, in certain examples by at least about 35%, and in still other examples by at least about 50%. In another example, where the difference in sublayers of a HIPE foam layer is with respect to density, the densities of the layers may differ by at least about 20%, in certain instances by at least about 35%, and in still other instances by at least about 50%. For example, if one layer of HIPE foam has a density of 0.020 g / cm 3 If the layer has a density of at least 0.024 g / cm 3 or approximately 0.016 g / cm 3 less than about 0.027 g / cm 3 or approximately 0.013 g / cm3 and in still other embodiments, at least about 0.030 g / cm 3 or approximately 0.010 g / cm 3 The HIPE or HIPE foam may have a density of less than 100 . When the difference between the layers relates to the chemical composition of the HIPE or HIPE foam, the difference may reflect a difference in the relative amount of at least one monomer component, e.g., by at least about 20%, and in certain instances, by at least about 35%, and in further instances, by at least about 50%. For example, if one sublayer of the HIPE or HIPE foam is comprised of about 10% styrene in its formulation, another sublayer of the HIPE or HIPE foam may be comprised of at least about 12%, and in certain instances, by at least about 15%.

[0074] A HIPE foam layer structured with distinct sublayers formed from different HIPEs can provide a HIPE foam layer with a range of desirable performance characteristics. For example, a HIPE foam layer comprising first and second foam sublayers, where the first foam sublayer has a relatively larger pore or cell size than the second foam sublayer, can absorb incoming fluids more quickly than the second sublayer when used in an absorbent article. For example, when a HIPE foam layer is used to form the absorbent structure of a feminine hygiene pad, the first foam sublayer can be layered on a second foam sublayer having a relatively smaller pore size than the first foam sublayer. The smaller pore size exerts greater capillary pressure, drawing acquired fluids from the first foam sublayer and restoring the first foam sublayer's ability to acquire more fluid from above. The pore size of the HIPE foam can range from about 1 to about 200 μm, and in certain instances, can be less than about 100 μm. A HIPE foam layer of the present disclosure having two major parallel surfaces may be about 0.5 to about 10 mm thick, and in certain instances, about 2 to about 10 mm thick. The desired thickness of the HIPE foam layer will depend on the material used to form the HIPE foam layer, the rate at which the HIPE is deposited onto the belt, and the intended use of the resulting HIPE foam layer. An example of an open-cell HIPE foam layer having two sublayers is found in the absorbent structure of ALWAYS INFINITY brand feminine hygiene pads currently manufactured and sold by The Procter & Gamble Company (Cincinnati, Ohio).

[0075] The HIPE foam layers of the present disclosure are relatively open-celled. This refers to the individual cells or pores of the HIPE foam layer that are in substantially unobstructed fluid communication with adjacent cells. The cells of such substantially open-celled HIPE foam structures have intracellular openings or windows large enough to allow rapid fluid transfer from one cell to another within the HIPE foam structure. For purposes of this disclosure, a HIPE foam is considered "open-celled" if at least about 80% of the cells in the HIPE foam that are at least 1 μm in size are in fluid communication with at least one adjacent cell.

[0076] In addition to being open-celled, in certain instances, the HIPE foam is adapted to be sufficiently hydrophilic to allow the HIPE foam to absorb aqueous fluids. In some instances, the interior surface of the HIPE foam may be rendered hydrophilic by residual hydrophilizing surfactants or salts remaining in the HIPE foam after polymerization, or by selected post-polymerization HIPE foam treatment procedures, such as those described in the references cited herein.

[0077] In some configurations, for example, when used to form absorbent structures in feminine hygiene pads, the HIPE foam layer can be flexible and exhibit an appropriate glass transition temperature (Tg). Tg represents the midpoint of the transition between the glassy and rubbery states of a polymer. Generally, HIPE foams with a Tg higher than the use temperature may be strong, but also relatively stiff and potentially prone to fracture (brittle). In certain instances, regions of the HIPE foam of the present disclosure that exhibit either a relatively high Tg or excessive brittleness will be discontinuous. These discontinuous regions also generally exhibit high strength and can be prepared at low densities without compromising the overall strength of the HIPE foam.

[0078] HIPE foams intended for applications requiring flexibility should include at least one continuous region having the lowest possible Tg, so long as the HIPE foam as a whole has acceptable strength at the temperatures in use. In certain instances, the Tg of this region will be less than about 40°C for foams used at about ambient temperature conditions, and in other instances, the Tg will be less than about 30°C. For HIPE foams used in applications where the use temperature is higher or lower than ambient temperatures, the Tg of the continuous region may be up to 10°C higher than the use temperature, in certain instances, the same as the use temperature, and in further instances, about 10°C lower than the use temperature if flexibility is desired. Thus, monomers are selected to provide the corresponding polymer with the lowest possible Tg.

[0079] HIPE foams useful for forming absorbent structures and / or sublayers within the contemplated scope of the present disclosure, as well as materials and methods for their manufacture, include those disclosed in U.S. Pat. Nos. 10,045,890, 9,056,412, 8,629,192, 8,257,787, 7,393,878, 6,551,295, 6,525,106, 6,550,960, 6,406,648, 6,406,648, 6,551,295, 6,525,106, 6,550,960 ...51,295, 6,525,106, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,960, 6,550,9 U.S. Patent No. 6376565, U.S. Patent No. 6372953, U.S. Patent No. 6369121, U.S. Patent No. 6365642, U.S. Patent No. 6207724, U.S. Patent No. 6204298, U.S. Patent No. 6158144, U.S. Patent No. 6107538, U.S. Patent No. 6107356, U.S. Patent No. 6083211, U.S. Patent No. 6013589, U.S. Patent No. 5899893, U.S. Patent No. 5873869, U.S. Patent No. 5863958, U.S. Patent No. 5849805, U.S. Patent No. 5827909, U.S. Patent Nos. 5827253, 5817704, 5817081, 5795921, 5741581, 5652194, 5650222, 5632737, 5563179, 5550167, 5500451, 5387207, 5352711, 5397316, 5331015, 52927 ... Also included are, but are not necessarily limited to, the foams and methods described in U.S. Patent No. 5,268,224, U.S. Patent No. 5,260,345, U.S. Patent No. 5,250,576, U.S. Patent No. 5,149,720, U.S. Patent No. 5,147,345, and U.S. Patent Application Publication Nos. 2005 / 0197414, 2005 / 0197415, 2011 / 0160326, 2011 / 0159135, 2011 / 0159206, 2011 / 0160321, and 2011 / 0160689.

[0080] As reflected in FIG. 2 , the absorbent structure 40 formed from HIPE foam can include one or more patterns of openings 43, including at least a first pattern located within an expected discharge location overlying the intersection of the pad's longitudinal axis 100 and lateral axis 200. The openings 43 can be punched, cut, or otherwise formed through the entire z-depth of the HIPE foam absorbent structure, or through only the wearer-facing layer or partially through its wearer-facing portion. As described herein, when the HIPE foam absorbent structure is placed in direct contact with a topsheet without an intervening acquisition layer formed of another material, the openings 43 can function as a group of reservoirs to receive, temporarily hold, and aid in the distribution of relatively small amounts of rapid menstrual discharge until the HIPE foam has had sufficient time to distribute and absorb the fluid by capillary action. Additionally, such openings can help reduce the bending stiffness of the absorbent structure, which can help improve the pad's comfort to the wearer. For example, within the area occupied by bond region 25, a pattern of openings having an average radius or other maximum dimension of 1.0 mm to 4.0 mm, more preferably 1.5 mm to 3.5 mm, may be included. 2 3.0 to 9.0 openings per cm, preferably 1 cm 2 The apertures may be included at a numerical density of 4.0 to 8.0 apertures per opening. In selecting the appropriate average size, numerical density, and surface area occupied by the aperture pattern, manufacturers may wish to balance the desired "reservoir" volume required to keep absorbent material in close proximity to and near the anticipated discharge location. Further details regarding such aperture configurations, along with examples of suitable absorbent structures, can be found in U.S. Patent No. 8,211,078.

[0081] The absorbent structure 40 formed from the HIPE foam should be endowed with sufficient capillary work potential in absorption mode (CWPA) (described below) so that it has the ability to effectively draw exuded fluid from the topsheet over the period of normal and expected menstrual pad use / wear, e.g., 4-8 hours. As described below, a material's CWPA is affected in part by its volume. Thus, it may be desirable for the absorbent structure 40 formed from the HIPE foam to have a caliper (before wetting) that provides a satisfactory volume for a standard-sized pad. Naturally, relatively thick pads can be manufactured, but given the desire for flexibility / softness and thinness for comfort and inconspicuousness under clothing, these may be deemed undesirable for daytime use. Manufacturing must balance these competing objectives. Thus, in feminine hygiene pads having a HIPE foam absorbent structure as contemplated herein, it may be desirable for the layer to have a caliper (before wetting) of about 1 mm to about 5 mm, or more preferably about 1.5 mm to about 3.5 mm, or even more preferably about 2.0 mm to about 3.0 mm over the majority of its wearer-facing surface area (the caliper of the HIPE foam layer can be measured visually, using magnification / microscopy and / or photography, or other facilitating techniques and equipment, to the extent deemed useful). When the absorbent structure 40 includes two sublayers as described herein, the upper sublayer 40t may desirably have a caliper (before wetting) of about 0.64 mm to about 3.2 mm, or preferably about 0.96 mm to about 2.24 mm, or even more preferably about 1.28 mm to about 1.92 mm, and the lower sublayer 40b may desirably have a caliper (before wetting) of about 0.16 mm to about 0.80 mm, or more preferably about 0.24 mm to about 0.56 mm, or even more preferably about 0.32 mm to about 0.48 mm.

[0082] In some configurations, the absorbent structure 40 may consist of or include a heterogeneous layer of absorbent foam material (such as the HIPE foam material described above) that has been polymerized to thereby form structures around, between, and / or within the matrix of fibers of the nonwoven web material. Examples of such heterogeneous layers are shown and described in U.S. Patent Application Publication Nos. 2017 / 0119587, 2017 / 0119596, 2017 / 0119597, 2017 / 0119588, 2017 / 0119593, 2017 / 0119594, 2017 / 0119595, and 2017 / 0199598.

[0083] Absorbency characteristics and the interface between the topsheet and the absorbent structure The affinity and absorbency of an absorbent / hydrophilic structure for aqueous fluids can be characterized, in part, by its capillary absorption pressure. Capillary absorption pressure (CAP) can be measured according to the steps in the capillary working potential measurement method described below. This is a value that reflects the magnitude of the structure's tendency to draw in aqueous fluids. It will be seen that a plot of CAP for an absorbent structure versus saturation level has an initial maximum (at the beginning of fluid absorption) and decreases as the structure draws in fluid and approaches its full absorption capacity, i.e., full saturation.

[0084] The resistance of an absorbent / hydrophilic structure to desorption, or its tendency to retain absorbed fluid, can be characterized, in part, by its capillary desorption pressure (CDP). CDP, which may also be measured according to the steps in the Capillary Working Potential Measurement Method described below, is a value that reflects the amount of pressure (or pressure differential) required to expel (or draw) aqueous fluid absorbed and retained in the structure. It will be appreciated that a plot of CDP of a structure versus saturation level will have an initial minimum (before any fluid exits the structure) and increase as fluid leaves the structure.

[0085] The CAP and CDP of a given structure are a function of the degree of hydrophilicity of the solid surfaces within the structure, the average size of the interstitial spaces or voids, cells or pores within the structure in / between the solid surfaces, and the number of interstitial spaces, cells or pores within the structure per unit volume of the structure.

[0086] In addition to other conditions described herein, the CAP of the absorbent structure must be greater than the CDP of the topsheet at a selected, preferably relatively low, level of absorbed fluid content of the topsheet so that the laminated topsheet / absorbent structure combination can effectively transfer exuded fluid from the upper surface of the topsheet in the z-direction away from the wearer. For the laminated topsheet / absorbent structure combination to be able to transfer exuded fluid in the z-direction away from the wearer at an acceptable rate, i.e., so that the topsheet does not have time to excessively wick exuded fluid and thereby distribute (i.e., spread) it along the xy-plane (forming undesirably large stains on the topsheet), and so that the wearer does not feel overly wet immediately after fluid is exuded onto the topsheet, the capillary absorption pressure of the absorbent structure at, for example, 20 percent saturation must be greater than the capillary desorption pressure of the topsheet at the same saturation. In this case, percent saturation is the percent of the total pore volume of the material that is occupied by fluid, and the test fluid is saline as specified in the Capillary Work Potential measurement method described below.

[0087] The total absorbency of a given material structure can be further characterized by its capillary work potential in the absorption mode (CWPA) and in the drainage or desorption mode (CWPD), as measured using the capillary work potential measurement method described below. CWPA is a measure of the work an absorbent material does to draw in a quantity of aqueous fluid under the conditions of the described method. CWPD is a measure of the work required to drain or draw away the aqueous fluid absorbed and retained by the structure under the conditions of the described method. For a given structure that is hydrophilic and absorbs aqueous fluids, the CWPD will be greater than the CWPA because the absorbent structure's properties (hydrophilicity; cell / pore size and volume) tend to cause the absorbent structure to retain fluid. The CWPA and CWPD of a given structure are affected by the characteristics and properties that affect the CAP and CDP, and are also affected by the total volume of interstitial spaces or voids, cells, or pores in the structure. It will therefore be appreciated that the CWPA and CWPD of a structure are affected in part by the overall volume (ie, dimensions) of the structure.

[0088] To ensure that the absorbent structure 40 wicks the topsheet 20 of fluid absorbed into the topsheet, providing a fully satisfactory pad for the two (absorbent structure and topsheet), the absorbent structure 40 should have a CWPA greater than the CWPD of the topsheet. If this condition is not met, the absorbent structure will not wick fluid sufficiently away from the topsheet to ensure both: (1) that the topsheet does not retain an unacceptable wetness after wicking, and (2) that the topsheet remains drained and capable of accepting continuous wicking of fluid over a reasonable period of use of the article 10.

[0089] It has been found that absorbent structures formed from HIPE foams as described herein can be manufactured to have capillary absorption pressures that are great enough to draw fluid from absorbent cotton topsheets at an acceptably fast rate over repeated drainages, i.e., over a reasonable period of use of the pad.

[0090] In examples where the topsheet is formed in part or entirely of a web material containing hydrophilic fibers, the topsheet material may tend to retain fluid on its wearer-facing and outward-facing surfaces and in the interstitial spaces between and along the fibers of the web material, unless the underlying material has an absorption capacity and absorption pressure higher than the topsheet's desorption pressure, as described above, and sufficient direct contact is maintained between the topsheet and the underlying absorbent structure to allow fluid to migrate directly from the fiber surfaces in the topsheet structure to the material surfaces in the underlying absorbent structure, so that the underlying absorbent structure can draw fluid from the topsheet. Before the absorbent material is fully saturated, the absorbent material will not release the absorbed fluid unless an adjacent material with a greater affinity for the fluid is in sufficient direct contact. Therefore, it is important to provide sufficient structure to maintain sufficient contact without impeding fluid movement. No intervening layer or structure of material, or at least an intervening layer or structure of material less absorbent than the topsheet or more absorbent than the absorbent structure, should be interposed between the material of the topsheet 20 and the material of the absorbent structure 40, at least in the bond region 25, and more preferably over a majority of the wearer-facing surface area of ​​the absorbent structure 40, and even more preferably over the entire wearer-facing surface area of ​​the absorbent structure 40. This differs from the systems provided in many current feminine hygiene pads, which include a separate layer of fluid acquisition / distribution material between the topsheet and the absorbent material of the absorbent structure.

[0091] In some examples, sufficient direct contact between the topsheet 20 and the absorbent structure 40 may be provided by deposits of adhesive between the topsheet 20 and the absorbent structure 40 that adhesively bond the topsheet 20 and absorbent structure 40 in close proximity in the z-direction. The adhesive may be applied in a pattern or arrangement of adhesive deposits interspersed with areas where there is no adhesive (unbonded areas), such that the adhesive holds the two layers in close proximity in the z-direction while maintaining areas where there is no adhesive to impede z-direction fluid movement between the layers.

[0092] 2, to ensure that the topsheet 20 and absorbent structure 40 are held in sufficient proximity in the z-direction, at least in the area of ​​the topsheet 20 expected to receive fluid discharge, it may be desirable to dispose a bonded area 25 on the pad at a location that includes the intersection of the longitudinal axis 100 and the transverse axis 200. The bonded area 25 should be of sufficient size to ensure that it is under the expected discharge location when the pad is in use, but with reasonable variability in placement within the undergarment by the wearer. Thus, the bonded area should be at least about 15 cm 2 , more preferably at least about 30 cm 2 Even more preferably, it may be desirable for the bonded region 25 to have an area that is at least half of the total wearer-facing surface area (within its periphery 40a) of the absorbent structure 40. (Note: Figure 2 is not presented herein as a representation of actual size or scale.)

[0093] 2-3C, to ensure that the topsheet 20 and absorbent structure 40 remain sufficiently close together in the z-direction during use, it may be desirable for any distinct first bond point location 27 within a bond region 25 where the topsheet is bonded to the absorbent structure to have a second distinct point location where the topsheet is bonded to the absorbent structure, the second distinct point location being within a radius r of about 10 mm, more preferably within a radius r of about 6 mm, about a radius r of about 5 mm, about a radius r of about 4 mm, and even more preferably within a radius r of about 3 mm of the first point location. Referring to FIGS. 3A-3C, which show three non-limiting examples, it can be seen that various patterns or arrangements of bonds (via adhesive deposits 26 or other bonding mechanisms) may be employed to impart this feature. Within the radius r of each distinct bond point location 27, there are numerous additional point locations where bonds exist between the topsheet and the absorbent structure in the examples shown.

[0094] A continuous film or coating deposit of adhesive can be applied to bond the topsheet and absorbent structure throughout the bonded region 25, although it will be appreciated that such a continuous adhesive deposit may form a barrier to fluid migration from the topsheet to the absorbent structure. Thus, in instances where the bonding mechanism is an adhesive deposit, the deposit is preferably arranged in a discontinuous or intermittent pattern or arrangement to form bonded regions interspersed with unbonded regions between the topsheet and the absorbent structure, as suggested in Figures 3A-3C.

[0095] 3D , a dense arrangement of relatively small point bond locations may be produced by spraying a suitable adhesive onto one or both of the outward-facing surface of the topsheet 20 and the wearer-facing surface of the absorbent structure in contact with the outward-facing surface of the topsheet. If the adhesive is properly matched (e.g., its viscosity), the spray nozzle is properly configured, and the spray rate (liquid volume or weight of sprayed adhesive / time / surface area of ​​spray coverage) is properly adjusted, the sprayed adhesive can produce a dense random pattern 27p of discrete point bond locations included in the description of the above paragraph, such that discrete spray droplets impinge on and adhere to the surface at discrete locations to an extent that is appropriately limited to prevent the formation of a continuous deposit or continuous film, but does not result in a continuous film of deposited adhesive that blocks pores in the underlying absorbent structure or prevents fluid transfer from the topsheet to the underlying absorbent structure.

[0096] Additionally, when the absorbent structure is formed of an open-cell foam (such as the HIPE foams contemplated herein), it may be desirable for the selected adhesive not to bond to the absorbent structure via chemical, dispersion, or diffusion bonding with the foam layer at the adhesive deposition location, but rather to mechanically bond to the foam layer by confiningly flowing into the cells, at least partially assuming their shape, and solidifying at such location to form a mechanical interlock with the cell structure, thereby allowing the adhesive to hold the topsheet and / or backsheet to the absorbent structure. Such adhesives may be preferred because they do not alter the molecular structure or composition of the foam material, potentially adversely affecting its fluid absorption properties or mechanical strength. In some configurations, a portion of the adhesive may penetrate the wearer-facing surface of the foam material and the garment-facing surface of the topsheet, and / or a portion of the adhesive may penetrate the garment-facing surface of the foam material and the wearer-facing surface of the backsheet to bond the foam material to the topsheet and / or backsheet. One suitable example may be an adhesive designated H2031-C5X, a product of Bostik, a division or subsidiary of Arkema Group (Colombes, France).

[0097] back seat The backsheet 30 can be positioned below or below and adjacent to the outward-facing surface of the absorbent structure 40 and can be joined to that surface by any suitable attachment method. For example, the backsheet 30 can be secured to the absorbent structure 40 by a uniform continuous layer of adhesive, a patterned layer of adhesive, or an array of separate lines, spirals, or dots of adhesive. Alternatively, attachment methods may include thermal bonding, pressure bonding, ultrasonic bonding, dynamic mechanical bonding, or any other suitable attachment mechanism, or combinations thereof. It is contemplated that in some configurations, the absorbent structure 40 will not be directly joined to the backsheet 30.

[0098] The backsheet 30 may be impermeable or substantially impermeable to aqueous liquids (e.g., urine, menstrual fluid) and may be fabricated from a thin plastic film, although other flexible, liquid-impermeable materials can also be used. As used herein, the term "flexible" refers to a material that is conformable and easily conforms to the overall shape and contours of the human body. The backsheet 30 can prevent, or at least substantially prevent, fluids absorbed and contained within the absorbent structure 40 from leaking out and reaching articles of the wearer's clothing that may come into contact with the pad 10, such as undergarments and garments. However, while in some instances the backsheet 30 is fabricated and / or adapted to allow vapors to escape from the absorbent structure 40 (i.e., the backsheet is fabricated so as to be breathable), in other instances the backsheet 30 may be fabricated so as not to allow vapors to escape (i.e., it is fabricated so as to be non-breathable). Thus, the backsheet 30 may comprise a polymeric film, such as a thermoplastic film of polyethylene or polypropylene. A suitable material for the backsheet 30 is a thermoplastic film having a thickness of, for example, about 0.012 mm (0.5 mil) to about 0.051 mm (2.0 mil). Any suitable backsheet known in the art may be utilized with the present invention.

[0099] Some suitable examples of materials suitable for forming the backsheet are described in U.S. Patent Nos. 5,885,265, 4,342,314, and 4,463,045. Suitable single-layer breathable backsheets for use herein include those described in, for example, British Patent Nos. A2184389, A2184390, A2184391, U.S. Patent Nos. 4,591,523, 3,989,867, 3,156,242, WO 97 / 24097, U.S. Patent Nos. 6,623,464, 6,664,439, and 6,436,508.

[0100] The backsheet 30 may have two layers, a first layer comprising a vapor-permeable apertured formed film layer and a second layer comprising a breathable microporous film layer, as described in U.S. Patent No. 6,462,251. Other suitable examples of dual or multi-layer breathable backsheets for use herein include those described in U.S. Patent Nos. 3,881,489, 4,341,216, 4,713,068, 4,818,600, EP 203821, EP 710471, EP 710472, and EP 0793952.

[0101] For the purposes described herein, it may be preferred that the film from which the backsheet is formed be formed from a construction material (e.g., a polymer resin) that results in a film that exhibits suitable plastic deformability / extensibility such that it can be locally plastically stretched (to a limited extent) along the xy-plane direction along discrete locations by passing it through a deformation roller as described herein without breaking or tearing. The thermoplastic resins identified explicitly or by reference above are considered to be potentially non-limiting examples suitable for such purposes.

[0102] Suitable backsheet materials may have a basis weight of from about 20 gsm to about 28 gsm, or from about 22 gsm to about 25 gsm. Surprisingly, it has been found that absorbent articles described herein having a backsheet with a basis weight of less than 20 gsm may be too thin in the plastically stretched zones, resulting in a backsheet with a thin appearance that may be undesirable to some consumers.

[0103] Mechanical Treatment It has been found that mechanically treating at least the absorbent structure 40, or the absorbent structure together with one or both of the topsheet 20 and backsheet 30, in the manner described herein can provide many unexpected advantages.

[0104] A process known as "incremental stretching" involves passing a web through a nip between a pair of rollers having mating features that stretch discrete, incremental sections of the web across lines coincident with the roller features. Non-limiting examples of incremental stretching processes and apparatus are disclosed in U.S. Patent No. 6,383,431. It has been found that this process can be applied to beneficial effects not only to single web layers, but also to multi-layer composite webs containing components of an absorbent structure. With reference to FIGS. 8-13, for example, mating rollers 302a, 302b can include respective circumferential ridges 302d separated by circumferential grooves 302e. The rollers may be configured so that the ridges of one roller engage with the grooves of the other to a desired engagement depth ED (FIG. 10). As a layered composite web 400 being transported along the machine direction MD passes through the nip 302c between the mated rollers, it is forced to bend over the respective ridges 302d of each roller, thereby being stretched along the cross direction CD. If the depth of engagement ED is properly adjusted, one or more layer components of composite web 400 can be stretched beyond their yield point along the machine direction and plastically deformed or fractured as web 400 passes through the nip, resulting in a deformed composite web 401. (The roller configurations reflected in FIGS. 9-11 and 13 are sometimes known as "ring rolling" configurations, or "ring rollers.") The resulting less deformed or undeformed zones 420 and more deformed zones 410 of this potential CD deformation or fracture in the layer components of web 401 are shown schematically in FIGS. 11 and 12. In the configurations shown in FIGS. 10 and 11, the direction of stretching deformation DD is aligned or substantially parallel to the cross direction CD.

[0105] 14, in another configuration, the deforming rollers 306a, 306b may be configured with mating / engaging ridges 306d and grooves 306e around their circumferential surfaces that are parallel to their axes of rotation. In this configuration, the rollers resemble a pair of mating elongated spur gears with their axes oriented in the cross direction CD. A web passing through the nip between these rollers is stretched over each "gear tooth," i.e., ridges 306d, substantially along the machine direction, rather than along the cross direction as described above and shown in FIGS. 11 and 12.

[0106] 8, it has been found that a composite web 400 including an absorbent structure may be sequentially passed through the nip between two successive pairs of deformation rollers 302 and 306, incrementally stretching and / or disrupting the web along two different directions (in this particular, non-limiting example, the machine direction and the cross direction) as described above. Following such deformation, it has been found that, compared to a similar structure that has not been so deformed, the absorbent structure (1) is dramatically faster at acquiring and distributing fluid along and through it, (2) exhibits a relatively greater absorption capacity per unit weight of absorbent material included over the same period of time, and (3) is dramatically more flexible and pliable, thereby making it better able to bend around and conform to non-ruled surfaces (i.e., body contours) and move with the movements of the wearer's body (i.e., move and move with the undergarment fabric as the wearer's body moves). Without being bound by theory, it is believed that absorbent articles having one or more layer components so engineered are dramatically more comfortable for the wearer / user of the product and more effective at blocking the excretion of bodily fluids as a result of better conformance to the characteristics of the body and more rapid acceptance, distribution, and absorption of fluids within their structure.

[0107] During the deformation process, the overall xy-plane surface area of ​​the absorbent structure can be increased by up to about 35 percent or more. At the same time, the increased fluid acquisition and distribution rate capabilities and absorbent capacity imparted to the article can allow manufacturers to reduce or omit the inclusion of certain amounts of material and / or layers of material (e.g., separate acquisition / distribution layers, etc.), thereby enabling material cost savings and allowing manufacturers to provide thinner, more comfortable, and more discrete absorbent articles (e.g., feminine hygiene pads) that perform comparably to thicker competing / equivalent products while being thinner, more discrete, and more comfortable to the user. Because the pad is stretched and permanently deformed longitudinally and laterally (along the xy-plane), manufacturers can reduce the overall xy-plane size of the absorbent structure and the entire pad prior to deformation, allowing the reduced-size pad structure to assume the expanded, final desired pad product size through the deformation process. The enhanced fluid acquisition rate and absorption capacity made possible through the transformation process allows for more efficient use of absorbent material, resulting in relatively less absorbent material being required per pad to provide the desired fluid acquisition and absorption performance. Additionally, the transformation process described herein can eliminate the need to include openings 43 (e.g., as shown in FIG. 2) through the absorbent structure, as discussed above, simplifying the manufacturing process.

[0108] In some configurations, the basis weight of the absorbent structure 40 may be from about 130 gsm to about 200 gsm.

[0109] The enhanced liquid acquisition / distribution and absorption capacity is believed to result from the creation of additional and / or larger internal voids (due to material fracture) within the absorbent structure along the deformation lines. Furthermore, when the composite web 400 passing between the deformation rollers includes not only the absorbent structure but also one or both of the topsheet and backsheet components of the absorbent article, all layers may be deformed to various degrees depending on their deformability or plastic extensibility, thereby imparting all layers as a composite with expanded size in the x and y directions, increased bidirectional extensibility, flexibility, and softness.

[0110] This deformation along two directions is referred to herein as "bidirectional" deformation. Importantly, a bidirectionally deformed composite web has an enhanced ability to bend and conform more closely around non-woven, curved, contoured surfaces, such as the surfaces of features of the human body. This degree of conformability is reflected in measurements that may be made using the Fit Force Measurement Method described below. In some configurations, the absorbent articles described herein may exhibit a fit force of from about 140 N / m to about 1500 N / m, or from about 150 N / m to about 1000 N / m, or from about 225 N / m to about 800 N / m. In contrast, current feminine hygiene pads exhibit a fit force of greater than 1600 N / m, and some even exceed 5100 N / m. Without being bound by theory, it is believed that products exhibiting a fit force of from about 140 N / m to about 1500 N / m are highly flexible and can move with the panty during wear, thereby providing a more comfortable and / or closer fit to the body.

[0111] 1, 4A-4C, 5, 11, and 12, the materials of the respective topsheet 20 and backsheet 30 may be selected and / or manufactured and / or formulated to have properties, and the engagement features and engagement depth of the deformation rollers may be configured and adjusted, for example, to only stretch elastically but not plastically, or to stretch plastically but not crush / break / fracture, in the deformation zone 410 as the topsheet and / or backsheet pass through the respective nips between the deformation rollers. In combination, the material(s) / layer(s) of the absorbent structure 40 may be selected and / or manufactured and / or formulated to have properties such that they are plastically stretched or broken / fractured in an orderly manner and pattern in the regions 410, mirroring the pattern of ridges and grooves on the deformation rollers. Preferably, the topsheet and backsheet are selected and / or manufactured and / or formulated to be plastically (or permanently) stretched / deformed in zones 20s, 30s that substantially correspond to the deformation lines 50, but not fracture during the deformation process, and the absorbent structure material 40 is similarly stretched to fracture to form gaps 40s that substantially correspond to the deformation lines 50. In such a configuration, the combination of materials for forming the absorbent article as a composite can be imparted with bidirectional extensibility, as well as substantially enhanced softness and body conformability.

[0112] When the topsheet and backsheet are plastically stretched only in the larger x and y dimensions and not fractured, and one or more of the absorbent structure components / layers are stretched and fractured to form separate fractured fragments 40p thereof, the gaps 40s between the fractured edges of the fragments substantially along the deformation lines 50 open, thereby providing and opening fluid pathways through the absorbent structure and providing additional surface area for the absorbent material, allowing fluid to contact the absorbent material for more rapid absorption compared to absorbent layer components that have not been so fractured. A non-limiting example of an absorbent article in the form of a feminine hygiene pad that has undergone such bidirectional deformation along the CD and MD is shown schematically in FIG. 1. The longitudinal / y and transverse / x directions of the pad correspond to the CD and MD directions of deformation along the deformation lines 50 and are disposed at or approximately 90 degrees to each other. Another non-limiting example of an absorbent article in the form of a feminine hygiene pad that has undergone such bidirectional deformation along an oblique angle to the CD and MD is shown schematically in FIG. 5.

[0113] 1 and 5, the absorbent article 10 includes sides 11, e.g., a first side, a second side, a third side, and a fourth side. The absorbent article 10 may include a first longitudinal side 12a extending in a direction substantially parallel to a longitudinal axis 100 and a second longitudinal side 12b opposite the first longitudinal side 12a. The absorbent article 10 may also include a first lateral side 14a extending in a direction substantially parallel to a lateral axis 200 and a second lateral side 14b opposite the first lateral side 14a. As shown in FIG. 5 , in some configurations, the absorbent article may include a first plurality of deformation lines 55 extending in a first direction substantially perpendicular to the first stretch direction 51 a and a second plurality of deformation lines 56 extending in a second direction substantially perpendicular to the second stretch direction 51 b. In some configurations, at least some of the first plurality of deformation lines 55 extend from a first side of the absorbent article 10 to a second side of the absorbent article 10. In some configurations, some of the first plurality of deformation lines 55 may extend from the first longitudinal side 12 a to at least one of the second lateral side 14 b and the second longitudinal side 12 b. In some configurations, some of the second plurality of deformation lines 56 may extend from the first longitudinal side 12 a to at least one of the first lateral side 14 a and the second longitudinal side 12 b.

[0114] 1, 4B-4D, and 5, the topsheet 20 and the backsheet 30 may each have sides 21, 31. For example, the topsheet 20 may include a first side, a second side, a third side, and a fourth side, and the backsheet 30 may include a first side, a second side, a third side, and a fourth side. The topsheet 20 may have a first longitudinal side 22a extending in a direction substantially parallel to the longitudinal axis 100 and a second longitudinal side 22b opposite the first longitudinal side 22a. The topsheet 20 may also have a first lateral side 24a extending in a direction substantially parallel to the lateral axis 200 and a second lateral side 24b opposite the first lateral side 24a. The backsheet 30 may include a first longitudinal side 32a extending in a direction substantially parallel to the longitudinal axis 100 and a second longitudinal side 32b opposite the first longitudinal side 32a. The backsheet 30 may also include a first lateral side 34a extending in a direction substantially parallel to the lateral axis 200 and a second lateral side 34b opposite the first lateral side 34a. In some configurations, the topsheet 20 and the backsheet 30 may include plastically stretched zones 20s, 30s, respectively, arranged substantially along a first plurality of deformation lines 55 and a second plurality of deformation lines 56. In some configurations, the topsheet 20 may include a plurality of plastically stretched zones 20s extending continuously throughout the topsheet 20. In some configurations, a portion of the plastically stretched zone 20s of the topsheet 20 may extend continuously from a first side of the topsheet 20 to a second side of the topsheet 20. For example, a portion of the plastically stretched zone 20s of the topsheet 20 may extend continuously from the first longitudinal side 22a to the second longitudinal side 22b. In some configurations, a portion of the plastically stretched zone 20s of the topsheet 20 may extend continuously from the first lateral side 24a to the second lateral side 24b. In some configurations, the backsheet 30 may comprise multiple plastically stretched zones 30s that extend continuously throughout the backsheet 30.In some configurations, a portion of the plastically stretched zone 30s of the backsheet 30 may extend continuously from a first side of the backsheet 30 to a second side of the backsheet 30. For example, a portion of the plastically stretched zone 30s of the backsheet 30 may extend continuously from the first longitudinal side 32a to the second longitudinal side 32b. In some configurations, a portion of the plastically stretched zone 30s of the backsheet 30 may extend continuously from the first lateral side 34a to the second lateral side 34b.

[0115] In feminine hygiene pads having an absorbent foam layer (e.g., a HIPE foam layer as described above) forming part or substantially all of the absorbent structure 40, it may be desirable to configure and dimension the deformation roller to impart plastic deformation to the topsheet and backsheet, as well as fracture the absorbent foam layer, so that the pieces 40p have an average xy planar size of 15 mm or less, more preferably 10 mm or less, even more preferably 7 mm or less, and even more preferably 5 mm or less throughout the absorbent structure, to provide the desired overall pad flexibility and effective fluid passageway. (For purposes herein, the "xy planar size" of a piece 40p is its maximum xy planar dimension.) In some configurations, the average xy planar size of the foam pieces 40p may be from about 1.5 mm to about 15 mm, or from about 2 mm to about 5 mm. In some configurations, the foam pieces 40p may have a diamond-shaped xy planar shape. To achieve the improved fluid acquisition and absorption performance and pad flexibility / softness contemplated herein, it may be desirable for the deformation roller to be configured and dimensioned to impart plastic deformation to the topsheet and backsheet, along with fracture of the absorbent foam layer, so that the gaps 40s have an average xy-plane gap size throughout the absorbent structure of greater than 0.1 mm, more preferably 0.3 mm, even more preferably 0.6 mm, and even more preferably 1 mm, or from 0.3 mm to about 1.2 mm, or any subrange therein. (For purposes herein, the "xy-plane gap size" of the gaps 40s is the xy-plane dimension of the space between adjacent pieces measured along a direction perpendicular to the corresponding deformation line 50.) Alternatively, for the same purpose, it may be desirable for the average xy-plane gap size to be proportional to the average caliper ("C") of the absorbent structure 40. Therefore, it may be desirable for the gaps 40s to have an average xy plane gap size throughout the absorbent structure of at least (0.04 x C), more preferably (0.12 x C), even more preferably (0.24 x C), and even more preferably (0.4 x C), or from (0.04 x C) to (0.48 x C), or any subrange therebetween.

[0116] 4A-4D schematically illustrate non-limiting examples of potential effects resulting from incremental stretching of a composite web comprising a topsheet material, a backsheet material, and an absorbent structure material along the transverse direction of the pad shown in FIG. 1. The topsheet 20 may be imparted with plastically stretched zones 20s, and the backsheet 30 may be imparted with plastically stretched zones 30s, where plastic deformation of the topsheet and / or backsheet material occurs in a relatively regular configuration along deformation lines 50 (FIG. 1) between roller teeth or ridges in the nip between deformation rollers. The topsheet 20 and backsheet 30 may each include zones 20u, 30u of reduced or substantially no deformation disposed intermediate the plastically stretched zones. The absorbent structure 40 may be imparted with relatively regular lines of plastic strain deformation or, preferably, fracture to form gaps 40s. As shown in FIG. 4C, in an alternative composite configuration, the absorbent structure 40 may include additional acquisition and / or distribution layers 41, 42 imparted with relatively regular lines of strain deformation or even fracture to form strain regions or even gaps 41s, 42s. In some examples, the additional layers 41, 42 may comprise a nonwoven web material having portions of absorbent foam precursors integrated into its fibrous matrix and subsequently cured or polymerized into a foam structure, as suggested, for example, in U.S. Patent Application Publication Nos. 2017 / 0119587, 2017 / 0119596, 2017 / 0119597, 2017 / 0119588, 2017 / 0119593, 2017 / 0119594, 2017 / 0119595, and 2017 / 0199598.

[0117] The size of the gaps 40s between the foam segments 40p in an article in which the absorbent foam described herein is formed or which is a component of the absorbent structure 40 can be adjusted by the configuration of the deformation roller. One aspect of such a configuration that is particularly effective is the engagement depth ED of the respective cooperating / interlocking deformation ridges 302d and grooves 302e (see FIG. 10 ). A larger engagement depth ED causes greater deformation of the topsheet and backsheet, thereby resulting in relatively larger gaps 40s, while a smaller engagement depth ED causes less deformation of the topsheet and backsheet, thereby resulting in relatively smaller gaps 40s. In general, articles with gaps 40s large enough to minimize interference between the segments 40p and allow bending across them will be relatively more flexible and conforming to the body, while articles with smaller gaps 40s that are not sufficient to allow bending across them without interference between the segments 40p will be relatively less flexible and conforming to the body. This effect of gap size GS is shown schematically in Figures 21A, 21B, 22A, and 22B. Figure 21A schematically illustrates the effect of deformation at a relatively small deformation roller engagement depth—an example in which deformation of the topsheet 20 and backsheet 30 is relatively small, and the size GS of the gaps 40s between the segments 40p is relatively small. As a result, when bending the article in the z-direction, if one of the topsheet 20 and backsheet 30 is pulled taut, adjacent segments 40p will begin to interfere at interference locations 40i. The cumulative effect of such interference between the many segments 40p in the many gaps 40s within the article impairs bending along the deformation line 50, thereby reducing the article's overall flexibility and body fit. Conversely, Figure 22A illustrates the effect of deformation at a relatively large deformation roller engagement depth—an example in which deformation of the topsheet 20 and backsheet 30 is relatively large, and the size GS of the gaps 40s between the segments 40p is relatively large. As a result, when the article is bent in the z-direction, the segments 40p are less likely to interfere with each other during bending. The cumulative effect of such reduced interference between the many segments 40p within the article is to facilitate bending along deformation lines 50, thereby increasing the flexibility and body conformability of the article.However, the deformation roller engagement depth must be limited so that the topsheet 20 and backsheet 30 are not stretched to the point of failure along the deformation line 50 and / or so as to avoid potentially creating a negative consumer perception of the quality of the article (e.g., the article being too thin or brittle or damaged).

[0118] Referring now to FIG. 5, in some examples, an absorbent article may be imparted with deformation lines 50 that are oblique to the transverse axis 200 and the longitudinal axis 100. To achieve this result, in some examples, the combined web or assembled article may be passed between machine direction ring rollers 302a, 302b, such as those shown in FIGS. 9-11 and 13, and fed through the rollers in two successive steps along two different oblique orientations relative to the machine direction. In other examples (not shown), the combined web or assembled article traveling along the machine direction may be immobilized and compressed or stamped continuously and intermittently along the z-direction between pairs of flat deformation plates having ridges and grooves suitably configured to incrementally stretch the web or article along the oblique directions. However, for the purpose of incrementally stretching a combined web along two different directions oblique to the machine direction of continuous production, such methods may be found to be cumbersome and inefficient compared to using a spiral deformation roller as described herein.

[0119] Alternatively, the deformation rollers used may be provided with a configuration similar to that of intermeshing pairs of helical, spiral, or worm gears (collectively, herein, deformation rollers have a "helical" configuration of alternating grooves and ridges), as suggested in Figures 15A, 15B, 16A, and 16B. As reflected in Figures 15A, 15B, 16A, and 16B (and see also Figures 5 and 6), a first pair of such helical deformation rollers 307a, 307b may be configured to intermesh and have a selected helix angle γ1 to impart a deformation line 50 in the article 10 that is substantially parallel to one of the deformation line directions 50a, 50b by gradually straining the article along one of the strain directions 51a, 51b as the article (or precursor combined web) passes through the nip between them. After passing through the nip between rollers 307a, 307b, the article (or precursor combined web) may pass through a second nip between a second pair of deformation rollers 308a, 308b (Figures 15B, 16B), which may be helically configured, adapted to intermesh, and configured to have a selected helix angle γ2 so as to impart a deformation line 50 to the article 10 that is substantially parallel to the other of the deformation line directions 50a, 50b by gradually straining the article along the other of the strain directions 51a, 51b as the article (or precursor combined web) passes through the nip between them.

[0120] In such a configuration, deformation of the web resulting from passage through the nip occurs along deformation lines 50 that are oblique to the MD and CD of the web, along deformation angles imparted relative to the machine and cross directions as a result of the helical angles of the helical ridges 307d, 308d and interlocking helical grooves 307e, 308e along the outer periphery or outer radial edge of the rollers. Two successive pairs of such helical deformation rollers with different or oppositely oriented helical angles may be arranged along a processing line to successively strain and deform the composite web along two different directions, thus imparting bidirectional deformation to the article or its precursor web, as suggested, for example, in FIG. 5. The helical angles of successive pairs of helical deformation rollers are preferably selected so that the angles α and β formed at the intersection of the longitudinal axis of the article with the resulting deformation lines 50 are substantially equal for the purpose of imparting stretch / extensibility / conformability properties to the article, and the features are substantially symmetrical and / or aligned with the longitudinal axis.

[0121] 5 and 6, the spiral deformation roller may be configured to impart bidirectional strain and deformation along strain directions 51 a, 51 b that are oblique to the longitudinal / x and lateral / y directions of an absorbent article 10, such as a feminine hygiene pad. For feminine hygiene pads, bidirectionally deforming pads in which the deformation line 50 is parallel to the line of deformation directions 50 a, 50 b, and the deformation directions 50 a, 50 b are substantially perpendicular to the strain directions 51 a, 51 b, and the strain directions are oriented at angles α and β, respectively, relative to the lateral direction, have been found to move more easily and better accommodate the wearer's body movements (e.g., walking) when adhered to the inner crotch region of a wearer's undergarments when the angles α and β are each between about 5 degrees and about 85 degrees, more preferably between about 15 degrees and about 70 degrees, and even more preferably between about 30 degrees and about 60 degrees. Correspondingly, it is preferred that the lines of deformation directions 50a, 50b each be at an angle of from about 5 degrees to about 85 degrees, more preferably from about 15 degrees to about 70 degrees, and even more preferably from about 30 degrees to about 60 degrees relative to the longitudinal axis of the article, and all subranges within these ranges are contemplated herein.

[0122] When adhered to the inside surface of the wearer's underwear, the pad is able to move and move better with the fabric of the underwear as the wearer moves about, resulting in a dramatic improvement in comfort for the wearer.

[0123] It has also been found that such strain directions oblique to the machine direction of the web's movement through the nip are less likely to fracture the nonwoven web material than strains along a direction parallel or perpendicular to the machine direction (such as those imparted by rollers as shown in Figures 9-14). This is believed to be a previously unrecognized synergistic effect resulting from the typical machine direction bias of fibers in nonwoven web materials, particularly spunbond nonwoven web materials. Spunbond nonwoven web materials typically have a machine direction bias as a result of the way they are made, i.e., by depositing spun fibers on a forming belt that moves along the machine direction. ("Machine direction bias," with respect to the fibers forming the nonwoven web, means that the majority of the fibers, in the web and unstretched, have a length with a machine direction vector component equal to or greater than their transverse vector component.) As a result of the way article 10 and its component web materials are typically manufactured, nonwoven web components typically have a machine direction bias that is aligned with the longitudinal direction (y) of the article. When the deformation direction 51a, 51b is oblique to the machine / longitudinal direction as suggested in Figures 5 and 6, the fibers are less likely to be pulled directly along their length in the machine direction or to separate in the cross direction, and as a result are less likely to be stretched along their length beyond their limits and break, and are less likely to suffer separation along the cross direction which could result in undesirable changes or damage to the structural integrity and quality of the web material.

[0124] It is contemplated that a pair of deformation rollers may be configured to impart bidirectional deformation to the composite web in a single pass through the nip, i.e., the roller features are configured to simultaneously incrementally stretch the composite web in two different directions, including directions parallel and perpendicular to the machine direction, or oblique to the machine direction, as described above. However, it may be preferable to impart stretching sequentially along two different directions via two successive pairs of deformation rollers. This may allow for better control over the stretching process along each direction and reduce the possibility of undesired lines or paths of fracture in the absorbent structure or damage to components of the web.

[0125] It is also contemplated that one or more pairs of deformation rollers may be configured to deform only discrete regions or zones of the composite web while leaving adjacent regions or zones undeformed. As a non-limiting example shown in FIG. 7 , an article in the form of a feminine hygiene pad 10 may be bidirectionally deformed only in a defined zone or region (in the non-limiting example shown in FIG. 7 , the central region indicated by diagonal deformation line 50), while the remaining regions remain undeformed. Bidirectional deformation may be imparted along directions 50a, 50b and 51a, 51b, angles α and β, as described above. In the example shown in FIG. 7 , the central region is deformed, while the side regions, including wing portions 15, remain undeformed. The regions of deformation and the regions left undeformed may be configured for various effects.

[0126] However, it may be preferable to bidirectionally deform the entire xy region of the layered material forming article 10 (as suggested by FIGS. 1 and 5), with one or more portions remaining undeformed, without any breaks or discontinuities in the bidirectional deformation pattern, such as that shown in FIG. 7. This is because discontinuities or interruptions in the bidirectional deformation pattern could result in discontinuities in the softness and flexibility imparted by the deformation, which could impair the ability of article 10 to closely conform to the features of the wearer's body and move with the movements of the wearer's undergarment fabric and / or the wearer's body.

[0127] 1, 4A-4D, 19, and 20, as described above, the bidirectional deformation process may be configured to fracture the material of the absorbent structure 40 into a plurality of individual pieces 40p in an orderly manner along the deformation lines 50. For example, if the material of the structure 40 includes a layer of material that is relatively inelastic or brittle under tension (such as an absorbent foam of appropriate composition as described herein), a properly configured process will fracture the structure 40 in an orderly manner to produce individual pieces 40p of approximately uniform size separated along the deformation lines 50 and separated by gaps 40s. Photographs of an actual prototype example of an absorbent article 10 showing such deformation lines 50, pieces 40p, and gaps 40s are reproduced in FIGS. 19 and 20.

[0128] To prevent the individual pieces 40p from shifting and becoming displaced within the structure after fracture (i.e., to hold them in place substantially in their relative pre-fracture positions), it may be desirable to include a structure that holds them in place within the enclosed space between the topsheet and backsheet. To this end, a deposit 45 of suitable adhesive / glue material may be placed between one or both of the wearer-facing and outward-facing interfaces between the absorbent structure 40 and the topsheet and backsheet, or between the absorbent structure and other interlayer components, such as a distribution layer. In particular, with respect to adhesives that may be placed between the wearer-facing surface of the absorbent structure 40 and the topsheet 20, the deposit 45 may be applied via a controlled spray in the manner described above so as not to create an occlusive film of adhesive but to bond the respective materials together at discrete locations corresponding to the deposited glue droplets, while avoiding the creation of a fluid barrier and leaving the absorbent structure 40 effectively unoccluded on its wearer-facing surface. However, in some configurations, it may be considered suitable or even preferable for the adhesive application disposed between the outward-facing surface of the absorbent structure 40 and the backsheet to be more extensive, continuous, or even substantially film-like, as blockage at or on the outward-facing surface of the absorbent structure (e.g., a layer of absorbent foam) may be less of an issue and such a more extensive or continuous application may better serve to hold broken pieces 40p of the absorbent structure 40 in place following deformation as described herein. Thus, adhesive deposits may be disposed on both the top and bottom surfaces of the absorbent structure 40 or its layer components to provide a more cohesive overall pad structure and minimize the likelihood of the pieces 40p moving and becoming displaced within the structure.

[0129] Preferably, the adhesive deposit is applied across a majority of the xy-planar surface area of ​​one or both of the wearer-facing and garment-facing surfaces of the absorbent structure 40. To reduce the potential stiffening effect caused by applying adhesive / glue between adjacent layers below / above each other in the pad, it may be desirable for the adhesive / glue material selected to be a resilient and / or elastic formulation. In some configurations, the adhesive may be a pressure-sensitive adhesive with a relatively long open time. A suitable adhesive may have a relatively high modulus of elasticity (G') to withstand forces applied during machining as the material is stretched. Adhesives utilizing styrene / isoprene / styrene (SIS) building blocks may be preferred. One suitable example may be an adhesive designated H2031-C5X, a product of Bostik, a division or subsidiary of the Arkema Group (Colombes, France).

[0130] In some configurations, the adhesive may be disposed between the wearer-facing surface of the absorbent structure 40 and the topsheet, as shown and described in Figures 3A-3D. In some configurations, the adhesive may be disposed between the wearer-facing surface of the absorbent structure 40 and the topsheet at a basis weight of about 15 gsm to about 35 gsm, or about 18 gsm to about 32 gsm, or about 20 gsm to about 30 gsm, including all values ​​within these ranges and any ranges formed therewith. In some configurations, the adhesive may be disposed between the outward-facing surface of the absorbent structure 40 and the backsheet at a basis weight of about 15 gsm to about 35 gsm, or about 18 gsm to about 32 gsm, or about 20 gsm to about 30 gsm, including all values ​​within these ranges and any ranges formed therewith. Consumer testing surprisingly revealed that when the basis weight of the adhesive between the topsheet and the absorbent structure and / or between the backsheet and the absorbent structure is less than 15 gsm, respectively, foam fragments can move and shift within the absorbent article during wear, creating an uneven distribution of absorbent material that can adversely affect comfort and / or fluid handling performance.

[0131] It will be appreciated that the absorbent structures described above may be adapted not only for use as feminine hygiene pads, but also as incontinence pads or absorbent inserts for use within undergarments, or even as structural subcomponents of disposable menstrual or adult incontinence undergarments adapted for use / wear by men or women.

[0132] In some configurations, the absorbent article structure manufactured as described herein may have a porous / liquid-permeable nonwoven web material (such as a spunbond web material) substituted for either or both of the topsheet 20 and backsheet 30 materials described above, similarly arranged and positioned to allow fluid to freely enter and exit the structure on both its upper and lower surfaces. The structure may also be mechanically treated as described above for similar effects and benefits. Such absorbent article structures may then be incorporated as layer components, for example, of an absorbent core structure, within absorbent articles such as, for example, disposable baby / toddler diapers, disposable children's training pants, disposable feminine hygiene pads, disposable incontinence pads, disposable menstrual undergarments, or disposable incontinence undergarments.

[0133] Test / Measurement Method Capillary working potential via pore volume distribution. Pore ​​volume distribution determines the estimated effective porosity within a porous sample by measuring fluid movement into and out of the sample when controlled differential pressure steps are applied to the sample within the sample chamber. The incremental and cumulative amounts of fluid absorbed / exhausted by the porous sample at each pressure are then determined. The work done by the porous sample, normalized by the area of ​​the sample, is then calculated as the capillary work potential.

[0134] Principle of the method For a uniform cylindrical pore, the radius of the pore is related to the pressure differential required to fill or empty the pore by the following equation: Differential pressure = [2γcosΘ)] / r where γ=liquid surface tension, Θ=contact angle, and r=pore radius.

[0135] The pores contained in natural and manufactured porous materials are often thought of in terms such as voids, holes, or conduits, and these pores are generally not perfectly cylindrical or uniform. Nevertheless, the above equation can be used to relate differential pressure to effective pore radius, and by monitoring liquid movement into and out of the material as a function of differential pressure, the effective pore radius distribution in the porous material can be characterized. (Because non-uniform pores are approximated as uniform by the use of effective pore radius, this general methodology may not produce results that precisely match pore size measurements obtained by other methods, such as microscopy.)

[0136] The pore volume distribution method employs the above principles and is implemented using the apparatus and techniques described in "Liquid Porosimetry: New Methodologies and Applications" by B. Miller and I. Tyomkin, published in The Journal of Colloid and Interface Science (1994), volume 162, pages 163-170, which is incorporated herein by reference. This method relies on measuring the incremental liquid volume entering or leaving a porous sample as the air pressure differential between ambient ("lab") air pressure and a slightly elevated air pressure (positive differential pressure) surrounding the sample in a sample test chamber is changed. The sample is introduced into a dry sample chamber, which is controlled at a positive differential pressure (relative to the lab) sufficient to prevent fluid uptake into the sample after the fluid bridge is opened. After opening the fluid bridge, the air pressure differential is gradually reduced to zero, and in the process, a subpopulation of pores within the sample capture liquid according to their effective pore radius. After reaching the minimum differential pressure where the mass of fluid in the sample is greatest, the differential pressure is again increased in steps toward the starting pressure, and liquid is drained from the sample. The absorption portion of the stepped sequence begins at the maximum differential pressure (smallest corresponding effective pore radius) and ends at the minimum differential pressure (largest corresponding effective pore radius). The drain portion of the sequence begins at the minimum pressure differential and ends at the maximum pressure differential. After correcting for any fluid movement for each particular pressure step, the fluid uptake by the sample (mg) at each differential pressure, as well as the cumulative volume (mm), measured on the chamber while draining the entire absorption / drain sequence, are 3 / mg) is determined.

[0137] Sample conditioning and sample preparation The pore volume distribution method is performed on samples conditioned for at least two hours in a room maintained at a temperature of 23°C ± 2.0°C and a relative humidity of 50% ± 2%, and all tests are performed under the same environmental conditions and in such a conditioned room. Damaged products or samples with defects such as wrinkles, tears, or holes are not tested. Samples conditioned as described herein are considered dry for the purposes of this invention. Determine which side of the sample is intended to face the wearer during use, and then cut it to a length of 55 mm by a width of 55 mm. Measure the mass of the sample and record it to the nearest 0.1 mg. Three samples are measured for any given material to be tested, and the results of these three replicate tests are averaged to obtain the final reported value.

[0138] Device A suitable apparatus for this method is described in "Liquid Porosimetry: New Methodology and Applications" by B. Miller and I. Tyomkin, published in The Journal of Colloid and Interface Science (1994), volume 162, pages 163-170. Furthermore, any pressure control scheme capable of controlling a sample chamber pressure differential between 0 mmH20 and 1098 mmH20 may be used in place of the pressure control subsystem described in this reference. One example of a suitable overall instrument and software is the TRI / Autoporosimeter (Textile Research Institute (TRI) / Princeton Inc. of Princeton, NJ, USA). The TRI / Autoporosimeter is an automated, computer-controlled instrument for measuring the pore volume distribution (e.g., the volume of pores of different sizes within the effective pore radius range of 5 μm to 1200 μm) of porous materials. Computer programs such as Automated Instrument Software Releases 2000.1 or 2003.1 / 2005.1 or 2006.2, or Data Treatment Software Release 2000.1 (available from TRI Princeton Inc.), and spreadsheet programs can be used to collect and analyze the measured data.

[0139] A schematic diagram of a suitable instrument is shown in Figure 18. The instrument consists of a balance 800 with a fluid reservoir 802 in direct fluid communication with a sample 805 present in a sealed, air-pressurized sample chamber 810. Fluid communication between the reservoir 802 and the sample chamber 810 is controlled by a valve 815. A weight 803 placed on top of a Plexiglas plate 804 (55 mm long x 55 mm wide) is used to apply a confining pressure of 0.25 psi on the test sample to ensure good contact between the sample and a fluid-saturated membrane 806 throughout the test. The membrane 806 (90 mm diameter, 150 um thick, 1.2 μm pore size, mixed cellulose ester filter RAWP09024, available from Millipore Corporation of Bedford, MA) is attached to a macroporous frit 807 (90 mm diameter, 60 mm thick Monel plate, available from Mott Corporation, Farmington, CT, or equivalent) as follows: Krylon® spray paint (gloss white spray paint #1501, available from FilmTools, or equivalent) is used as an adhesive to adhere membrane 806 to frit 807. The prepared membrane / frit assembly is allowed to dry before use.

[0140] To prepare the device for testing, fill the inner base 812 of the sample chamber 810 with the test fluid. The test fluid is 9.0 g of reagent-grade NaCl (liquid density 1.01 g / cm) per liter of deionized water. 3The membrane / frit assembly is placed membrane 806 side up onto the inner base 812 of the sample chamber 810, and secured in place with a locking collar 809. The reservoir 802 and connecting tubing 816 are filled with the test fluid. Valve 815 is opened to ensure that no air bubbles are trapped in the connecting tubing or in the pores in the membrane / frit assembly. Using the feet 811 of the sample chamber 810, the sample chamber is leveled, if necessary, to adjust its height (and / or the amount of fluid in the reservoir 802) so that the top of the membrane 806 is in the same horizontal plane as the top of the fluid in the reservoir 802.

[0141] Program the system to progress through a sequence of stepwise differential pressures (in mmH20) as follows: 1098, 549, 366, 275, 220, 183, 137, 110, 92, 78, 69, 61, 55, 50, 46, 42, 39, 37, 34, 32, 31, 29, 27, 24, 22, 20, 18, 14, 9.2, 6.9, 5.5, 4.6, 5.5, 6.9, 9.2, 14, 18, 20, 22, 24, 27, 29, 31, 32, 34, 37, 39, 42, 46, 50, 55, 61, 69, 78, 92, 110, 137, 183, 220, 275, 366, 549, 1098. These pressures correlate to effective pore radii of 5 μm (1098 mmH20) to 1200 μm (4.6 mmH20). The criterion for moving from one pressure step to the next is that the fluid uptake / exhaust from the sample, as measured by balance 800, is less than 10 mg / min for 15 seconds.

[0142] Method Steps The system can be checked for leaks and ensured to reach the maximum test pressure as follows: Open the liquid valve 815, place the top 808 of the sample chamber 810 in place, and seal the chamber. Apply sufficient air pressure to the chamber 810 (via connection 814) to achieve a differential pressure of 1098 mmH2O (effective pore radius of 5 μm). After closing the liquid valve 815, open the sample chamber. Place the sample 805 (wearer side facing down) directly on the membrane 806, then center the cover plate 804 and restraining weight 803 over the sample. Replace the top 808 and reseal the sample chamber 810. Open the liquid valve 815 to allow fluid transfer between the liquid reservoir 802 and the sample, and proceed through the test through a pre-specified sequence of differential pressures. The amount of fluid absorbed (or expelled) by the sample at each pressure step throughout the sequence is recorded as uptake to the nearest 0.1 mg.

[0143] A separate "blank" measurement is performed following this same method procedure (same stepwise sequence of differential pressure) on an empty sample chamber with no sample 805, cover plate 804, or restraining weight 803 present on the membrane / frit assembly. Any observed fluid movement is recorded (in mg) at each pressure step. The sample fluid uptake data is corrected for any fluid movement associated with the empty sample chamber by subtracting the fluid uptake value of this "blank" measurement from the corresponding value in the sample measurement, and is recorded to the nearest 0.1 mg as the blank-corrected sample uptake.

[0144] Determination of capillary pressure, cumulative volume and capillary working potential The percent saturation of the sample at each pressure step in both the absorption and drainage portions of the test sequence can be calculated by dividing the maximum blank-corrected sample uptake (mg) by the blank-corrected sample uptake (mg) and then multiplying by 100. From the data collected throughout the sequence, one skilled in the art can then determine the percent saturation at any given capillary absorption pressure (CAP) or capillary desorption (drainage) pressure (CDP). CAP and CDP are reported to the nearest 0.1 mmH2O for any specified percent saturation.

[0145] The cumulative volume is calculated from each of the pressure steps using the following equation: Cumulative volume (mm 3 / mg) = blank-corrected sample uptake (mg) / fluid density (g / cm 3 ) / sample mass (mg) The capillary work potential (CWP) is the work done by the sample normalized by the area of ​​the sample. The trapezoidal rule is used to integrate the ith pressure as a function of cumulative volume over n data points for the absorption and drainage portions of the cycle.

[0146]

number

[0147] Caliper Measurement The caliper, or thickness, of a test sample of a nonwoven web, laminate, foam layer material, or combination thereof is measured as the distance between a reference platform on which the sample rests and a foot presser that applies a specific amount of pressure on the sample for a specific period of time. All measurements are performed in a laboratory maintained at 23°C ± 2°C and 50% ± 2% relative humidity, and the test sample is conditioned in this environment for at least two hours before testing.

[0148] Caliper is measured with a manual micrometer equipped with a footplate capable of applying a steady pressure of 2.0 kPa ± 0.01 kPa to the test sample. The manual micrometer is a dead-weight instrument with a reading accurate to 0.001 mm. A suitable instrument is the Mitutoyo Series 543 ID-C Digimatic, available from VWR International, or equivalent. The footplate is a flat, grounded, circular, movable surface with a diameter smaller than the test sample and capable of applying the required pressure. A suitable footplate has a diameter of 25.4 mm, although smaller or larger footplates can be used depending on the size of the sample being measured. The test sample is supported by a horizontal, flat reference platform larger than and parallel to the surface of the footplate. The system is calibrated and operated according to the manufacturer's instructions.

[0149] If necessary, obtain the test sample by removing it from the absorbent article. When cutting the test sample from the absorbent article, care is taken not to contaminate or dimensionally deform the test sample. The test sample should be obtained from an area that does not contain folds or wrinkles and should be larger than the presser foot.

[0150] To measure thickness, first zero the micrometer against a horizontal, flat reference platform. Place the test specimen on the platform with the test location centered under the pressure foot. Gently lower the pressure foot at a rate of 3.0 mm ± 1.0 mm / sec until full pressure is applied to the test specimen. After waiting 5 seconds, record the caliper of the test specimen to the nearest 0.01 mm. Repeat for a total of five replicate test specimens. Calculate the arithmetic mean of all caliper measurements and report the caliper to the nearest 0.01 mm.

[0151] Compatibility measurement method Measurements made using this compliance measurement method reflect the degree to which a composite web material (i.e., a combination, assembly, or laminate of web materials) resists bending and stretching around a non-ruled surface. A bidirectionally extensible composite web material will bend and stretch more easily around a non-ruled surface than a comparable composite that is not bidirectionally extensible. In this method, the non-ruled surface is a spherical ball with a diameter of 25.4 mm.

[0152] The compliance force measurement method is performed on a constant rate of extension tensile tester (a suitable instrument is an MTS Insight tensile tester, MTS Systems Corp, Eden Prairie, MN, operating under TestSuite software, or equivalent) using a custom-made fixture and appropriate capacitance load cell. All testing is performed in a laboratory controlled at 23°C ± 2°C and 50% ± 2% relative humidity.

[0153] Referring to FIG. 17, the bottom fixture 1100 is a pneumatic clamping system used to hold the test specimen 1117 horizontally for testing. The fixture consists of a 6.4 mm Plexiglas box 1103, with the top 1101 and bottom 1102 both made from 9.5 mm thick aluminum plates. The bottom plate 1102 is attached to the bottom mount of the tensile tester via an adapter 1104 and locking collar 1105, which are used to secure the fixture perpendicular to the tensile tester's mount. Inside the box, a 9.5 mm thick aluminum movable plate 1106 is attached to two pneumatic cylinders 1107 and 1108, which are used to raise and lower the test specimen 1117. A rubber gasket 1113 is secured to the bottom side of the top plate 1101, and a matching rubber gasket 1114 is secured to the top of the movable plate 1106. A circular, 50.1 mm diameter, vertically oriented orifice 1115 penetrates the longitudinal and lateral centers of top plate 1101 and gasket 1113. A corresponding circular, 50.1 mm diameter orifice 1116, perpendicularly aligned with orifice 1115, penetrates movable plate 1106 and gasket 1114. Pressurized air 1110 is supplied to switch 1109, which is fluidly connected to cylinders 1107 and 1108 via tubes 1111 and 1112, and is used to raise and lower movable plate 1106. The air pressure is sufficient to hold the sample securely without slippage for testing.

[0154] The top fixture includes a cylindrical plunger 1003 terminating in a 25.4 mm diameter ball 1004. The plunger has an adapter 1001 that fits into a mount on a load cell that can secure the plunger orthogonally to the top plate 1101 of the bottom fixture. When the fixture is assembled with the testing machine, the ball 1004 is centered vertically over the orifices 1115 and 1116, with the center of the ball traveling along a vertical path coincident with the vertical axes of the orifices. The gauge length is set at 10 mm between the bottom surface of the ball 1004 and the bottom surface of the gasket 1113.

[0155] The instrument is programmed into compression mode. The crosshead is lowered at a rate of 500 mm / min for the specified engagement distance, and the crosshead is returned to its original position. Data from the force and distance channels are recorded at a rate of 100 Hz during the downward stroke. Measurement cycles are run for each sample for three specific crosshead distances: 15 mm (i.e., 5 mm engagement), 20 mm (i.e., 10 mm engagement), and 25 mm (i.e., 15 mm engagement).

[0156] Test samples are conditioned in a laboratory controlled at 23°C ± 2°C and 50% ± 2% relative humidity. Place the sample on a flat bench with the top sheet facing up. Identify the sample's longitudinal axis. Measure 45 mm down from the top edge of the absorbent structure along the longitudinal axis and mark with a dot. This is the center of the measurement site. Remove the release paper (or adhesive cover sheet, if present) from the sample. Center the marked dot in the opening of the lower plate. Before clamping the sample between the gaskets 1113 and 1114, the sample should be gently pulled taut with approximately equal tension applied along two perpendicular directions, only enough to eliminate slack above the opening 1116. After the sample is pulled taut, activate switch 1109 to admit air into cylinders 1107 and 1108, thereby raising the movable plate 1106 and clamping the sample between the gaskets 1113 and 1114. Zero the force and crosshead channel and start the program. After the test, lower the moving plate and remove the sample before analyzing the next sample. Tests are run on seven replicate samples at each of the three crosshead distances.

[0157] A graph of force (N) versus displacement (mm) is prepared for each test run. The peak force (N) is read from the graph and recorded to the nearest 0.01 N. The compliance force is calculated as the maximum slope of the curve using a line segment that is at least 20% of the maximum force and recorded to the nearest 0.1 N / m. When the specimen is displaced 5 mm from its starting position (i.e., when the ball has moved down a maximum of 5 mm after first contacting the specimen), the compliance force is reported to the nearest 1 N / m as the average obtained from seven replicate specimens.

[0158] High-Speed ​​Tensile Testing High-speed tensile testing is used to measure the tensile strength of material samples at relatively high strain rates. This method uses a suitable tensile testing machine equipped with a servo-hydraulic actuator, such as an MTS810, available from MTS Systems Corp. (Eden Prairie, Minnesota), or equivalent, capable of speeds of greater than 1 m / s after a 5 mm crosshead displacement and at least about 1.5 m / s after a 10 mm crosshead displacement. The tensile testing machine is fitted with a 50-pound force transducer (part 9712 B50, available from Kistler North America (Amherst, New York), or equivalent) and a signal conditioner with a dual-mode amplifier (part 5010, available from Kistler North America, or equivalent).

[0159] FIG. 23 shows a cross-sectional view of a single line contact grip 2700 used in this test. The line grip 2700 is selected to provide a well-defined gauge and avoid excessive slippage of the specimen. The specimen is positioned with minimal slack. The top 2707 of the grip 2700 is grounded to provide good gauge definition while avoiding specimen breakage or shear. Portions of the grip 2700 may be configured to include a material 2705 that reduces the tendency of the specimen to slip. FIG. 24 shows a pair of opposing line contact grips 2700 suitable for use in this test. Pairs of grips of various specific designs may alternatively be used, while having equivalent functionality to those described above (i.e., capable of facilitating a well-defined 3 mm gauge length, without excessive slippage, and at least as wide as the specimen being analyzed).

[0160] For each nonwoven fabric sample of interest, five similar specimens are cut, each measuring 50.8 mm wide by 15 mm long. The shorter dimension of each specimen is parallel to the machine direction of the nonwoven fabric. When the specimens are removed from the finished absorbent article(s), the shorter dimension of the specimen is oriented parallel to the longitudinal axis of the absorbent article. The line contact grips are moved to a grip spacing (i.e., the distance between the lines of contact between the specimen and the grip surface) of 3.0 millimeters. The specimen is attached to the line contact grips, and a thin piece of tape is attached to help hold the specimen straight and flat while attached to the grips. (If used, the tape must stay behind the gripping line so as not to interfere with the specimen gauge during testing. The line contact grips are moved closer together to place as much slack as possible into the film specimen without the line contact grips interfering with each other. The actuator movement is selected so that the specimen experiences a relative grip velocity of approximately 1 m / s at an engineering strain of 1 and 1.5 m / s at an engineering strain of 4. Typically, one of the line contact grips remains stationary during testing while the opposing line contact grip is moved, although configurations in which both line contact grips move are also contemplated herein.)

[0161] The force and actuator displacement data generated during the test were recorded using a Nicolet Integra Model 10, 4-channel 1 Ms / s, 12-bit digitizer oscilloscope, with the data acquisition frequency set at 50 kHz. The data obtained are expressed as force (measured in Newtons) versus engineering strain. Engineering strain (ε) is dimensionless and is defined as:

[0162]

number

[0163] FIG. 25 shows a suitable exemplary graph 2900 with two curves 2910 and 2920. The first curve 2910 shows a plot of actuator velocity (i.e., the relative speed at which one grip moves away from the other) versus engineering strain. Arrow 2911 points to the right vertical axis used for plot 2910. The second curve 2920 shows a plot of force versus engineering strain, using the left vertical axis, as indicated by arrow 2921. The point of maximum force on the force versus engineering strain plot is identified. Moving toward higher engineering strain, the first point at which the force drops below 90% of the maximum force value is then identified, and the engineering strain at that point is defined as the specimen's compliance parameter and recorded to the nearest 0.01. (The region in which this point is found is indicated by arrow 2930.) The arithmetic mean of the five compliance parameter values ​​determined for each of the five similar specimens is reported to the nearest 0.01 as the compliance parameter of the material sample.

[0164] Melting Enthalpy and Crystallinity Test The enthalpy of fusion and crystallinity test is used to determine the enthalpy of fusion and percent crystallinity parameters. The enthalpy of fusion and crystallinity test involves implementing ASTM E793-06 with the following additional guidance: Specimens from nonwoven webs are die-cut from the sample nonwoven web. The specimen mass is 3 ± 2 mg, and the specimen mass is recorded to the nearest 0.01 mg. (If multiple layers are required to achieve the required sample mass, the sample nonwoven web is folded so that multiple layers of the same nonwoven web are simultaneously perforated to create the specimen.) The differential scanning calorimeter (DSC) uses dry nitrogen as the purge gas. The test temperature range is -90°C to 200°C. The heating rate in the DSC is 20°C / min, and the cooling rate is 20°C / min. The peak melting temperature is determined as described in §11 of ASTM E793-06. Mass-normalized enthalpy of fusion was calculated as specified in §11 of ASTM E793-06 and is the enthalpy of fusion parameter (ΔH) in units of joules per gram (J / g) to the nearest 0.01 J / g. m )

[0165] From the enthalpy of fusion parameter, the percent crystallinity is determined using the following formula:

[0166]

number

[0167]

number

[0168] In view of the foregoing, the following non-limiting examples are contemplated herein. A1. An absorbent article (10) comprising a liquid permeable topsheet (20), a liquid impermeable backsheet (30), and an absorbent structure (40) disposed between the topsheet and the backsheet, the absorbent article having a longitudinal axis (100) and a lateral axis (200); The absorbent article is incrementally stretched along at least a first stretch direction (51a) and a second stretch direction (51b) different from the first stretch direction, the topsheet and the backsheet each have permanent or plastically stretched deformation zones (20s, 30s) arranged substantially along two respective groups of deformation lines (50), a first group of deformation lines (50) being substantially perpendicular to a first direction of stretch (51a) and a second group of deformation lines (50) being substantially perpendicular to a second direction of stretch (51b); and An absorbent article wherein the topsheet and backsheet each have zones (20u, 30u) between the deformation lines (50) that are relatively less deformed or substantially undeformed.

[0169] A2. The article of embodiment A1, wherein the two groups of deformation lines (50) form respective angles (α) and (β) with respect to the longitudinal axis (100) of between 5 degrees and 85 degrees, more preferably between 15 degrees and 70 degrees, even more preferably between 30 degrees and 60 degrees, and any subrange therein.

[0170] A3. An article described in embodiment A1 or A2, wherein the absorbent structure comprises a layer of absorbent foam material, preferably HIPE foam material, and the layer of absorbent foam material is fractured into a plurality of individual pieces (40p) substantially along the deformation lines (50), and all or some of the individual pieces (40p) are separated from adjacent pieces by gaps (40s).

[0171] A4. An article as described in example A3, wherein the individual pieces (40p) have an average xy planar size throughout the absorbent structure of 15 mm or less, more preferably 10 mm or less, even more preferably 7 mm or less, and even more preferably 5 mm or less.

[0172] A5. An article described in any one of Examples A1 to A4, wherein the absorbent structure has an average caliper (C) and the gaps (40s) have an average xy plane gap size (GS) throughout the absorbent structure of at least (0.04 x C), more preferably (0.12 x C), even more preferably (0.24 x C), even more preferably (0.4 x C), or from (0.04 x C) to (0.48 x C), or any subrange therebetween.

[0173] A6. The article of any one of Examples A1-A5, wherein the backsheet (30) comprises a polymer film.

[0174] A7. The article of any one of Examples A1-A6, wherein the topsheet (20) comprises a nonwoven web material.

[0175] A8. The article of example A7, wherein the nonwoven web material is a spunbond nonwoven web material.

[0176] A9. The article of any one of Examples A1-A8, wherein the adhesive deposit (45) is disposed between the absorbent structure (40) and the topsheet (20).

[0177] A10. The article of any one of Examples A1-A9, wherein the adhesive deposit (45) is disposed between the absorbent structure (40) and the backsheet (30).

[0178] A11. The article of either example A9 or A10, wherein the adhesive deposit between the absorbent structure and the topsheet is in the form of atomized discrete droplets.

[0179] A12. The article of any one of Examples A9-A11, wherein the adhesive deposit between the absorbent structure and the backsheet is in the form of a continuous film of adhesive.

[0180] A13. The article of any one of Examples A9-A12, wherein the adhesive functions to hold the individual pieces (40s) in position relative to each other in the xy plane occupied by the absorbent structure.

[0181] A14. The article of any one of Examples A1-A13, wherein substantially all or the entire article is incrementally stretched along a first stretch direction (51a) and a second stretch direction (51b) in a pattern of stretch and non-stretch zones substantially lacking discontinuous regions.

[0182] A15. The article of any one of Examples A1-A14 configured as or incorporated into a feminine hygiene article.

[0183] A16. The article of any one of embodiments A1-A14 configured as or incorporated into a wearable incontinence article.

[0184] A17. The article of any one of Examples A1-A14 incorporated into an adult panty garment.

[0185] A18. The article of any one of embodiments A1-A14 incorporated into a diaper or infant training pants.

[0186] A19. A method for manufacturing an absorbent article (10), providing a topsheet material comprising an extensible nonwoven web material; providing a backsheet material comprising a compliant film; Providing an absorbent structure material; combining a topsheet material, a backsheet material, and an absorbent structure material to form a composite web (400), wherein the absorbent structure material is disposed between the topsheet material and the backsheet material to form the absorbent structure (40); conveying the composite web (400) through a first nip between a first pair of deformation rollers (302, 306, 307, 308) configured with respective interlocking / engaging ridges (302d, 306d, 307d, 308d) and grooves (302e, 306e, 307e, 308e), thereby incrementally stretching the composite web along a first deformation direction (51a, 51b), whereby the topsheet material and the backsheet material are each permanently / plastically deformed along parallel first deformation lines (50) oriented substantially perpendicular to the first deformation direction; a second pair of deformation rollers configured with respective interlocking / engaging ridges (302d, 306d, 307d, 308d) and grooves (302e, 306e, 307e, 308e), thereby incrementally stretching the composite web along a second deformation direction (51a, 51b) different from the first deformation direction, whereby the topsheet material and the backsheet material are each permanently / plastically deformed along parallel second deformation lines (50) oriented substantially perpendicular to the second deformation direction.

[0187] A20. The method described in example A19, wherein the absorbent structure material is fractured as it passes through the first nip and the second nip, thereby forming a plurality of individual pieces (40p) of fractured absorbent structure material between the topsheet material and the backsheet material.

[0188] A21. The method of either embodiment A19 or A20, further comprising disposing an adhesive at a first location between the wearer-facing surface of the absorbent structure material and the topsheet material.

[0189] A22. The method of any one of Examples A19-A21, further comprising disposing an adhesive at a second location between the outwardly facing surface of the absorbent structure material and the backsheet material.

[0190] A23. The method of either embodiment A21 or A22, wherein the adhesive is disposed in the form of discrete droplets.

[0191] A24. The method of example A22, wherein the adhesive is disposed in the form of a continuous film.

[0192] A25. The method of any one of Examples A19-A24, wherein the absorbent structure material is an absorbent foam material.

[0193] A26. The method of example A25, wherein the absorbent foam material is a HIPE foam material.

[0194] A27. The method of any one of embodiments A19-A25, wherein at least one, preferably both, of the first and second pairs of deforming rollers comprises an interlocking helical configuration of ridges (307d, 308d) and grooves (308d, 308e).

[0195] A28. The method of embodiment A27, wherein at least one, and preferably both, of the first and second pairs of deformation rollers are configured with helix angles (γ1, γ2) selected to impart strain to the composite web along a strain direction (51a, 51b) that forms an angle (α, β) of 5 degrees to 85 degrees, more preferably 15 degrees to 70 degrees, and even more preferably 30 degrees to 60 degrees with the transverse axis of the article, and / or to impart a deformation line (50) along the article that forms an angle (α, β) of 5 degrees to 85 degrees, more preferably 15 degrees to 70 degrees, and even more preferably 30 degrees to 60 degrees with the longitudinal axis of the article.

[0196] A29. The method of embodiment A20 or any embodiment dependent thereon, wherein the deformation roller is configured to break the absorbent structure material into pieces (40p) having an average xy planar size of 15 mm or less, more preferably 10 mm or less, even more preferably 7 mm or less, and even more preferably 5 mm or less throughout the absorbent structure of the article.

[0197] A30. The method of embodiment A20 or any embodiment dependent thereon, wherein the deformation roller is configured to break the absorbent material into pieces (40p) having gaps (40s) therebetween having an average xy plane gap size of at least (0.04 x C), more preferably (0.16 x C), even more preferably (0.28 x C), even more preferably (0.4 x C), or between (0.04 x C) and (0.48 x C), or any subrange therein, throughout the absorbent structure of the article, where "C" is the average caliper of the absorbent structure (40).

[0198] The dimensions and values ​​disclosed herein should not be understood as being strictly limited to the exact numerical values ​​recited. Instead, unless otherwise indicated, each such dimension is intended to mean both the recited value and a functionally equivalent range surrounding that value. For example, a dimension disclosed as "40 mm" is intended to mean "approximately 40 mm."

[0199] When a range of measured quantities or property values ​​is described and / or listed as characterizing the subject matter contemplated herein, such range is deemed to include and contemplate any and all subranges within that range.

[0200] All documents cited herein, including any cross-references or related patents or applications, are incorporated herein by reference in their entirety unless expressly excluded or otherwise limited. The citation of any document shall not be deemed to be prior art to any invention disclosed or claimed herein, or to teach, suggest, or disclose any such invention, either alone or in combination with any other reference or references. Furthermore, if any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in this document shall control.

[0201] While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this invention.

Claims

1. An absorbent article comprising: a longitudinal axis and a lateral axis; a liquid pervious topsheet having a garment-facing surface and an opposite wearer-facing surface; a liquid-impermeable backsheet having a garment-facing surface and an opposite wearer-facing surface; an absorbent structure comprising an open-cell absorbent foam material disposed between the topsheet and the backsheet, The absorbent article is incrementally stretched along at least a first stretch direction and a second stretch direction different from the first stretch direction, the topsheet and the backsheet each include plastically stretched zones disposed substantially along a first plurality of deformation lines that are substantially perpendicular to the first direction of stretch and a second plurality of deformation lines that are substantially perpendicular to the second direction of stretch; the absorbent foam material is fractured into a plurality of individual foam segments substantially along the first plurality of deformation lines and the second plurality of deformation lines, the individual foam segments being separated from adjacent segments by gaps; an adhesive of 15 gsm to 35 gsm, preferably 18 gsm to 32 gsm, more preferably 20 gsm to 30 gsm, disposed between the garment-facing surface of the topsheet and the wearer-facing surfaces of the individual foam pieces, bonding the individual foam pieces to the topsheet.

2. 10. The absorbent article of claim 1, further comprising an adhesive of 15 gsm to 35 gsm, preferably 18 gsm to 32 gsm, more preferably 20 gsm to 30 gsm, disposed between the wearer-facing surface of the backsheet and the garment-facing surface of the individual foam pieces, said adhesive bonding the individual foam pieces to the backsheet.

3. 3. The absorbent article of claim 1 or 2, wherein the adhesive is in the form of atomized discrete droplets.

4. The absorbent article of claim 2 , wherein the adhesive is in the form of a continuous film of adhesive.

5. 5. The absorbent article of any one of claims 1 to 4, wherein the individual foam pieces are arranged in a continuous pattern across the absorbent structure, and wherein the individual foam pieces have an average xy planar size of from 2 mm to 15 mm.

6. 6. The absorbent article of any one of claims 1 to 5, wherein the absorbent structure has an average caliper (C), and the gaps between the individual foam pieces have an average xy plane gap size of from 0.04 x C to 0.48 x C.

7. The absorbent article of any one of claims 1 to 5, wherein the individual foam pieces are separated from adjacent pieces by gaps of between 0.3mm and 1.2mm.

8. The absorbent article of any one of claims 1 to 7, wherein the backsheet comprises a polymeric film having a basis weight of from 20 gsm to 28 gsm.

9. The absorbent article of any one of claims 1 to 8, wherein the topsheet is a spunbond nonwoven material.

10. 10. The absorbent article of any one of claims 1 to 9, wherein the first plurality of deformation lines form an angle α with the longitudinal axis and the second plurality of deformation lines form an angle β with the longitudinal axis, the angle α and the angle β each being between about 5 degrees and 45 degrees, preferably between 15 degrees and 40 degrees, more preferably between 20 degrees and 38 degrees.

11. The absorbent article of any one of claims 1 to 10, wherein the open-cell foam material is a high internal phase emulsion foam.

12. The absorbent article of any one of claims 1 to 11, wherein a portion of the adhesive penetrates the garment-facing surface of the topsheet and the wearer-facing surfaces of the individual foam pieces.

13. The absorbent article of any preceding claim, wherein the plurality of individual foam segments are arranged in a continuous pattern extending throughout the absorbent structure.

14. The absorbent article of any one of claims 1 to 13, wherein a portion of the plastically stretched zone of the topsheet extends continuously from a first side of the topsheet to a second side of the topsheet.

15. 15. The absorbent article of claim 14, wherein the first side of the topsheet is a first longitudinal side edge that extends in a direction substantially parallel to the longitudinal axis, and the second side of the topsheet is a second longitudinal side edge that extends in a direction substantially parallel to the longitudinal axis.