tire

Abstract

Provided is a tire having a tread, wherein: the tread includes at least a first layer constituting a tread surface, a second layer adjacent to the inner side of the first layer in the radial direction, and a third layer present on the inner side of the second layer in the radial direction; the first layer, the second layer, and the third layer are each composed of a rubber composition containing a rubber component; the rubber composition constituting the first layer and the second layer contains silica and a mercapto-based silane coupling agent; the content of the silica with respect to 100 parts by mass of the rubber component is greater than the content of carbon black; the tread has land parts partitioned by a plurality of circumferential grooves; the deepest part of the groove bottom of each of the circumferential grooves is formed so as to be positioned closer to the inner side of the tire in the radial direction than the outer surface of the second layer; and when the distance between the extension line of each of the land parts and the extension line of the deepest part of the groove bottom of each of the circumferential grooves is denoted as H1, and the distance between the extension line of the outer surface of the second layer and the extension line of the deepest part of the groove bottom of each of the circumferential grooves is denoted as H2, H2 / H1 is at least 0.20.

Description

[Technical field]

[0001] The present invention relates to a tire. [Background technology]

[0002] Important performances required for tires include wet grip performance and wear resistance. In recent years, from the viewpoint of resource conservation, there has been a demand for improved fuel economy performance by improving the rolling resistance of tires. To improve fuel economy performance, low hysteresis loss is required, and to improve wet grip performance, high wet skid resistance is required. However, low hysteresis loss and high wet skid resistance are contradictory, and it is difficult to improve fuel economy performance and wet grip performance in a well-balanced manner. Reducing the amount of fillers such as silica and carbon black reduces rolling resistance, but reinforcement, wear resistance, and wet grip performance tend to decrease.

[0003] Patent Document 1 discloses a rubber composition for tires that has improved fuel economy, wet grip performance, and abrasion resistance by blending a specific liquid resin and silica. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] JP 2013-53296 A Summary of the Invention [Problem to be solved by the invention]

[0005] In order to improve the balance of fuel economy, wet grip, and wear resistance, a tire has been proposed in which the tread rubber has three layers, a surface layer, an intermediate layer, and a base layer, and the circumferential groove is formed to a position deeper than the outer surface of the intermediate layer. However, in such a tire, since the surface layer and the intermediate layer are composed of different rubber layers, strain tends to concentrate near the interface, resulting in a decrease in adhesion at the interface. In addition, if the groove depth in the intermediate layer relative to the depth of the circumferential groove increases beyond a certain ratio, durability may decrease synergistically.

[0006] An object of the present invention is to provide a tire having improved overall performance including fuel economy, wet grip performance, wear resistance, and durability. [Means for solving the problem]

[0007] As a result of extensive research, the inventors have found that the above-mentioned problems can be solved by providing three or more specified rubber layers in the tread portion, having the rubber layers have a specific composition, and having a groove depth in the intermediate layer relative to the depth of the circumferential grooves at a specified ratio, thereby completing the present invention.

[0008] That is, the present invention provides [1] A tire having a tread, the tread comprising at least a first layer constituting a tread surface, a second layer adjacent to the radially inner side of the first layer, and a third layer present radially inner side of the second layer, the first layer, the second layer and the third layer being constituted by a rubber composition containing a rubber component, the rubber composition constituting the first layer and the second layer containing silica and a mercapto-based silane coupling agent, and a content of silica per 100 parts by mass of the rubber component being greater than a content of carbon black, the tread having a land portion partitioned by a plurality of circumferential grooves, the deepest part of the groove bottom of the circumferential groove being formed to be located radially inward of the tire than an outer surface of the second layer, and the distance between an extension line of the land portion and an extension line of the deepest part of the groove bottom of the circumferential groove being H1, and the distance between an extension line of the outer surface of the second layer and an extension line of the deepest part of the groove bottom of the circumferential groove being H2, H2 / H1 being 0.20 or more; [2] The tire according to the above [1], wherein the difference between the content of the softener per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and the content of the softener per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is 50 parts by mass or less. [3] The tire according to the above [1] or [2], wherein the difference between the sulfur content per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and the sulfur content per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is 1.0 part by mass or less. [4] The tire according to any one of the above [1] to [3], wherein the difference between the content of the vulcanization accelerator per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and the content of the vulcanization accelerator per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is 3.5 parts by mass or less. [5] The tire according to any one of the above [1] to [4], wherein the H2 / H1 is 0.30 or more. [6] The tire according to any one of the above [1] to [5], wherein at least one of the rubber compositions constituting the first layer and the second layer contains 100 parts by mass or more of silica per 100 parts by mass of the rubber component. [7] The tire according to any one of the above [1] to [6], wherein the rubber composition constituting the first layer and the second layer contains 50 to 130 parts by mass of silica per 100 parts by mass of the rubber component, and the ratio of silica to the total content of silica and carbon black is 60% by mass or more. [8] The tire according to any one of the above [1] to [7], wherein the rubber composition constituting the first layer and the second layer contains 10 parts by mass or more of a softener per 100 parts by mass of the rubber component. [9] The tire according to any one of the above [1] to [8], wherein the rubber components constituting the first layer and the second layer contain 40% by mass or more of styrene-butadiene rubber.

[10] The tire according to any one of the above [1] to [9], wherein the content of the diene rubber modified with a functional group having affinity for silica in 100% by mass of the rubber components constituting the first layer and the second layer is 40% by mass or more.

[11] The tire according to any one of the above [1] to

[10] , wherein the rubber composition constituting the first layer contains 1.0 part by mass or more of aluminum hydroxide per 100 parts by mass of the rubber component.

[12] The tire according to any one of the above [1] to

[11] , wherein the first layer, the second layer, and the third layer each have a thickness of 1.0 mm or more.

[13] The tire according to any one of the above [1] to

[12] , wherein the ratio (t2 / t1) of the thickness t2 of the second layer to the thickness t1 of the first layer is 0.4 to 5.0.

[14] The tire according to any one of the above [1] to

[13] , wherein a ratio (t3 / t2) of a thickness t3 of the third layer to a thickness t2 of the second layer is 0.2 to 3.0.

[15] The tire according to any one of the above [1] to

[14] , further comprising at least one selected from the group consisting of a sealant, a sound-damping body, and an electronic component for tire monitoring in the tire cavity.

[16] The tire according to any one of the above [1] to

[15] , which is a passenger car tire. Effect of the Invention

[0009] According to the present invention, a tire is provided in which three or more predetermined rubber layers are provided in the tread portion, the rubber layers have a specific compounding, and the groove depth in the intermediate layer relative to the circumferential groove depth is a predetermined ratio, thereby providing a tire with improved overall performance in terms of fuel economy, wet grip performance, wear resistance, and durability. [Brief description of the drawings]

[0010] [Figure 1] 1 is an enlarged cross-sectional view of a portion of a tread of a tire according to an embodiment of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] A tire according to one embodiment of the present disclosure is a tire having a tread, the tread including at least a first layer constituting a tread surface, a second layer adjacent to the radially inner side of the first layer, and a third layer present radially inner side of the second layer, the first layer, the second layer, and the third layer being constituted by a rubber composition containing a rubber component, the rubber composition constituting the first layer and the second layer containing silica and a mercapto-based silane coupling agent, and a content of silica per 100 parts by mass of the rubber component is greater than a content of carbon black, the tread has land portions partitioned by a plurality of circumferential grooves, the deepest part of the groove bottom of the circumferential groove is formed to be located radially inward of the tire than an outer surface of the second layer, and when the distance between an extension line of the land portion and an extension line of the deepest part of the groove bottom of the circumferential groove is H1, and the distance between an extension line of the outer surface of the second layer and an extension line of the deepest part of the groove bottom of the circumferential groove is H2, H2 / H1 is 0.20 or more (preferably 0.30 or more).

[0012] Without intending to be bound by theory, the mechanism by which tire durability is improved in the present disclosure is believed to be as follows. That is, by blending a highly active coupling agent such as a mercapto-based silane coupling agent, the polymer in the first layer and the silica in the second layer, or the silica in the first layer and the polymer in the second layer, can be more firmly bonded, thereby strengthening the adhesion at the interface of the rubber layers. It is believed that this can improve durability even when the ratio of the groove depth in the second layer to the depth of the circumferential groove is increased.

[0013] The difference between the content of the softener per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and the content of the softener per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is preferably 50 parts by mass or less, more preferably 40 parts by mass or less, even more preferably 30 parts by mass or less, and particularly preferably 20 parts by mass or less. By setting the difference in the content of the softener between the first layer and the second layer within the above range, the difference in hardness between the first layer and the second layer becomes large, and the deterioration of durability due to the concentration of strain near the interface can be suppressed. Note that, as long as the difference is within the above range, the content of the softener in the first layer may be greater or less than the content of the softener in the second layer, but from the viewpoint of suppressing the deterioration of wet grip performance after the first layer is worn, the content of the softener in the first layer is preferably greater than the content of the softener in the second layer.

[0014] The difference between the sulfur content per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and the sulfur content per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is preferably 1.0 parts by mass or less, more preferably 0.8 parts by mass or less, even more preferably 0.6 parts by mass or less, even more preferably 0.4 parts by mass or less, and particularly preferably 0.3 parts by mass or less. By setting the difference in sulfur content between the first layer and the second layer within the above range, it is possible to suppress the deterioration of durability performance due to the transition from a rubber layer with a high content of sulfur to a rubber layer with a low content of sulfur during vulcanization, resulting in a weakening of the strength near the interface. Note that, as long as the difference is within the above range, the sulfur content of the first layer may be greater or less than the sulfur content of the second layer, but from the viewpoint of low fuel consumption performance, it is preferable that the sulfur content of the first layer is less than the sulfur content of the second layer.

[0015] The difference between the content of the vulcanization accelerator per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and the content of the vulcanization accelerator per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is preferably 3.5 parts by mass or less, more preferably 3.0 parts by mass or less, even more preferably 2.5 parts by mass or less, and particularly preferably 2.0 parts by mass or less. By setting the difference in the content of the vulcanization accelerator between the first layer and the second layer within the above range, the vulcanization accelerator moves from the rubber layer with a large amount of vulcanization accelerator to the rubber layer with a small amount of vulcanization accelerator during vulcanization, and the strength near the interface is weakened, thereby suppressing the deterioration of durability performance. Note that, as long as the difference is within the above range, the content of the vulcanization accelerator in the first layer may be greater or less than the content of the vulcanization accelerator in the second layer, but it is preferable that the content of the vulcanization accelerator in the first layer is greater than the content of the vulcanization accelerator in the second layer. As described above, when the content of the softener in the first layer is greater than the content of the softener in the second layer, the vulcanization speed of the rubber composition constituting the first layer tends to be slow. In addition, when the content of silica in the rubber composition constituting the first layer is increased in order to improve wet grip performance, the vulcanization speed of the rubber composition constituting the first layer also tends to slow down. For these reasons, it is preferable to make the content of the vulcanization accelerator in the first layer greater than the content of the vulcanization accelerator in the second layer to ensure the vulcanization speed of the rubber composition constituting the first layer.

[0016] At least one of the rubber compositions constituting the first layer and the second layer preferably contains 100 parts by mass or more of silica per 100 parts by mass of the rubber component.

[0017] The rubber composition constituting the first layer and the second layer preferably contains 50 to 130 parts by mass of silica per 100 parts by mass of the rubber component, and the proportion of silica to the total content of silica and carbon black is preferably 60% by mass or more.

[0018] The rubber composition constituting the first layer and the second layer preferably contains 10 parts by mass or more of a softener per 100 parts by mass of the rubber component.

[0019] The rubber components constituting the first and second layers preferably contain 40% by mass or more of styrene-butadiene rubber.

[0020] The rubber composition constituting the first layer and the second layer preferably contains, as a rubber component, a diene rubber modified with a functional group having affinity for silica, the content of which is preferably 40% by mass or more, more preferably 50% by mass or more, further preferably 60% by mass or more, and particularly preferably 70% by mass or more.

[0021] The rubber composition constituting the first layer preferably contains aluminum hydroxide in an amount of preferably 1.0 part by mass or more, more preferably 3.0 parts by mass or more, and even more preferably 5.0 parts by mass or more, per 100 parts by mass of the rubber component.

[0022] It is preferable that the first layer, the second layer, and the third layer each have a thickness of 1.0 mm or more.

[0023] The ratio (t2 / t1) of the thickness t2 of the second layer to the thickness t1 of the first layer is preferably 0.4 to 5.0.

[0024] The ratio (t3 / t2) of the thickness t3 of the third layer to the thickness t2 of the second layer is preferably 0.2 to 3.0.

[0025] The tire of the present disclosure preferably includes, in the tire cavity, at least one selected from the group consisting of a sealant, a sound damper, and an electronic component for tire monitoring.

[0026] The tire of the present disclosure is suitably used as a passenger vehicle tire.

[0027] A procedure for producing a tire according to an embodiment of the present disclosure will be described in detail below. However, the following description is merely an example for explaining the present invention, and is not intended to limit the technical scope of the present invention to the described range. In this specification, when a numerical range is indicated using "to" it is intended to include both ends of the numerical range.

[0028] Fig. 1 is an enlarged cross-sectional view showing a portion of a tread of a tire according to the present disclosure, in which the up-down direction is the radial direction of the tire, the left-right direction is the axial direction of the tire, and the direction perpendicular to the paper surface is the circumferential direction of the tire.

[0029] As shown in the figure, the tread portion of the tire of the present disclosure comprises a first layer 6, a second layer 7 and a third layer 8, with the outer surface of the first layer 6 constituting the tread surface 3, the second layer 7 adjacent to the radially inner side of the first layer 6, and the third layer 8 being present radially inner side of the second layer 7. It is preferable that the third layer 8 is adjacent to the radially inner side of the second layer 7. Furthermore, as long as the object of the present invention is achieved, one or more rubber layers may be further provided between the second layer 7 and the third layer 8 and / or between the third layer 8 and the belt layer.

[0030] In Fig. 1, double arrow t1 indicates the thickness of the first layer 6, double arrow t2 indicates the thickness of the second layer 7, and double arrow t3 indicates the thickness of the third layer 8. In Fig. 1, an arbitrary point on the tread surface where no grooves are formed is indicated by the symbol P. The straight line indicated by the symbol N is a straight line (normal line) that passes through point P and is perpendicular to the tangent plane at point P. In this specification, thicknesses t1, t2, and t3 are measured along the normal line N drawn from point P on the tread surface at a position where no grooves exist in the cross section of Fig. 1.

[0031] In the present disclosure, the thickness t1 of the first layer 6 is not particularly limited, but from the viewpoint of wet grip performance, it is preferably 1.0 mm or more, more preferably 1.5 mm or more, and even more preferably 2.0 mm or more. On the other hand, from the viewpoint of heat generation, the thickness t1 of the first layer 6 is preferably 10.0 mm or less, more preferably 9.0 mm or less, and even more preferably 8.0 mm or less.

[0032] In the present disclosure, the thickness t2 of the second layer 7 is not particularly limited, but is preferably 1.5 mm or more, more preferably 2.0 mm or more, and even more preferably 2.5 mm or more. The thickness t2 of the second layer 7 is preferably 10.0 mm or less, more preferably 9.0 mm or less, and even more preferably 8.0 mm or less.

[0033] In the present disclosure, the thickness t3 of the third layer 8 is not particularly limited, but is preferably 1.0 mm or more, more preferably 1.5 mm or more. Also, the thickness t3 of the third layer 8 is preferably 10.0 mm or less, more preferably 9.0 mm or less, and even more preferably 8.0 mm or less.

[0034] The ratio (t2 / t1) of the thickness t2 of the second layer 7 to the thickness t1 of the first layer 6 is preferably 0.4 or more, more preferably 0.5 or more, even more preferably 0.7 or more, and particularly preferably 0.9 or more, from the viewpoint of fuel economy performance, while it is preferably 5.0 or less, more preferably 4.5 or less, even more preferably 4.0 or less, and particularly preferably 3.5 or less, from the viewpoint of wet grip performance.

[0035] From the viewpoint of better exerting the effects of the present disclosure, the ratio (t3 / t2) of the thickness t3 of the third layer 8 to the thickness t2 of the second layer 7 is preferably 0.2 or more, more preferably 0.3 or more, and even more preferably 0.4 or more. On the other hand, from the viewpoint of better exerting the effects of the present disclosure, the ratio (t3 / t2) of the thickness t3 of the third layer 8 to the thickness t2 of the second layer 7 is preferably 3.0 or less, more preferably 2.0 or less, even more preferably 1.5 or less, and particularly preferably 0.9 or less.

[0036] The thickness t2 of the second layer 7 relative to the thickness of the entire tread portion is preferably 20 to 90%, more preferably 25 to 80%, and even more preferably 30 to 75%. Note that the thickness of the entire tread portion in the present disclosure means the total thickness of the rubber layers constituting the tread portion, and is calculated as the shortest distance from the tread surface 3 to the belt layer.

[0037] The tread of the present disclosure has a plurality of circumferential grooves 1 that extend continuously in the circumferential direction of the tire. The circumferential grooves 1 may extend linearly along the circumferential direction, or may extend in a zigzag pattern along the circumferential direction.

[0038] The tread of the present disclosure has land portions 2 partitioned by circumferential grooves 1 in the tire width direction.

[0039] The groove depth H1 of the circumferential groove 1 is determined by the distance between the extension line 4 of the land portion 2 and the extension line 5 of the deepest part of the groove bottom of the circumferential groove 1. Note that, for example, when there are multiple circumferential grooves 1, the groove depth H1 can be the distance between the extension line 4 of the land portion 2 and the extension line 5 of the deepest part of the groove bottom of the circumferential groove 1 having the deepest groove depth among the multiple circumferential grooves 1 (the circumferential groove 1 on the left side in FIG. 1 ).

[0040] The tire of the present disclosure is formed so that the deepest part of the groove bottom of the circumferential groove 1 is located radially inward of the outer surface of the second layer 7. When the distance between the extension line 4 of the land portion 2 and the extension line 5 of the deepest part of the groove bottom of the circumferential groove 1 is H1, and the distance between the extension line 9 of the outer surface of the second layer 7 and the extension line 5 of the deepest part of the groove bottom of the circumferential groove 1 is H2, H2 / H1 is 0.20 or more, preferably 0.25 or more, more preferably 0.30 or more, even more preferably 0.35 or more, and particularly preferably 0.40 or more. By setting H2 / H1 in the above range, it is possible to improve fuel efficiency performance and wet grip performance in a well-balanced manner. In addition, by separating the deepest part of the groove bottom from the outer surface of the second layer 7, it is possible to ensure the durability of the groove bottom.

[0041] The tire of the present disclosure may be provided with a sealant, a sound damper, electronic components for tire monitoring, and the like in the tire cavity.

[0042] As the sealant, a sealant generally used on the inner peripheral surface of the tire tread portion for puncture prevention can be suitably used. Specific examples of such a sealant layer include those described in JP 2020-23152 A. The thickness of the sealant is usually preferably 1 to 10 mm. The width of the sealant is usually preferably 85 to 115% of the maximum width of the belt layer, and preferably 95 to 105%.

[0043] Any sound-damping body can be suitably used as long as it can exert a sound-damping effect in the tire cavity. Specific examples of such sound-damping bodies include those described in JP 2019-142503 A. The sound-damping body is, for example, made of a porous sponge material. The sponge material is a spongy porous structure, and includes, for example, a so-called sponge having continuous bubbles formed by foaming rubber or synthetic resin, as well as a web-like structure in which animal fibers, plant fibers, synthetic fibers, etc. are intertwined and connected together. In addition, the "porous structure" includes those having not only continuous bubbles but also closed bubbles. An example of the sound-damping body is a sponge material having continuous bubbles made of polyurethane. Suitable sponge materials include synthetic resin sponges such as ether-based polyurethane sponge, ester-based polyurethane sponge and polyethylene sponge, and rubber sponges such as chloroprene rubber sponge (CR sponge), ethylene propylene rubber sponge (EDPM sponge) and nitrile rubber sponge (NBR sponge). In particular, polyurethane-based or polyethylene-based sponges including ether-based polyurethane sponge are preferred from the standpoints of sound-damping properties, light weight, foaming adjustability, durability, and the like.

[0044] The sound-damping body is in the form of a long strip having a bottom surface fixed to the inner surface of the tread portion and extends in the circumferential direction of the tire. In this case, the outer ends in the circumferential direction may be butted against each other to form a substantially annular shape, or the outer ends may be spaced apart from each other in the circumferential direction.

[0045] In this disclosure, unless otherwise specified, the dimensions and angles of each component of the tire are measured when the tire is mounted on a standard rim and inflated to a standard internal pressure. No load is applied to the tire during measurement. In this specification, the term "standard rim" refers to a rim that is determined for each tire by a standard system that includes the standard on which the tire is based, such as a standard rim for JATMA, a "Design Rim" for TRA, and a "Measuring Rim" for ETRTO. In this specification, the term "standard internal pressure" refers to the air pressure determined for each tire by the standard, such as the maximum air pressure for JATMA, the maximum value listed in the table "TIRE LOAD LIMITS AT VARIOUS COLD INFLATION PRESSURES" for TRA, and "INFLATION PRESSURE" for ETRTO.

[0046] [Rubber composition for tread] As described above, the rubber composition constituting each rubber layer of the tread (rubber composition for tread) contains a rubber component and a plasticizer.

[0047] <Rubber component> The rubber composition constituting each rubber layer of the tread according to the present disclosure (rubber composition for tread) preferably contains at least one rubber component selected from the group consisting of isoprene-based rubber, styrene butadiene rubber (SBR) and butadiene rubber (BR). The rubber components constituting the first layer 6 and the second layer 7 preferably contain SBR, more preferably contain SBR and BR, or may be rubber components consisting of only SBR and BR. The rubber component constituting the third layer 8 preferably contains isoprene-based rubber, more preferably contains isoprene-based rubber and BR, or may be rubber components consisting of only isoprene-based rubber and BR.

[0048] (Isoprene rubber) As the isoprene-based rubber, for example, isoprene rubber (IR) and natural rubber, which are common in the tire industry, can be used. In addition to unmodified natural rubber (NR), natural rubber also includes modified natural rubber such as epoxidized natural rubber (ENR), hydrogenated natural rubber (HNR), deproteinized natural rubber (DPNR), high-purity natural rubber, and grafted natural rubber. These isoprene-based rubbers may be used alone or in combination of two or more.

[0049] The NR is not particularly limited, and any NR commonly used in the tire industry can be used, such as SIR20, RSS#3, and TSR20.

[0050] When the rubber composition constituting the first layer 6 and the second layer 7 contains an isoprene-based rubber (preferably natural rubber, more preferably unmodified natural rubber (NR)), the content in 100% by mass of the rubber component is preferably 50% by mass or less, more preferably 40% by mass or less, even more preferably 30% by mass or less, and particularly preferably 20% by mass or less, from the viewpoint of wet grip performance. In addition, the lower limit of the content when the isoprene-based rubber is contained is not particularly limited, but can be, for example, 1% by mass or more, 3% by mass or more, 5% by mass or more, 10% by mass or more, or 15% by mass or more. When the rubber composition constituting the third layer 8 contains an isoprene-based rubber, the content in 100% by mass of the rubber component is not particularly limited, but can be, for example, 10% by mass or more, 30% by mass or more, 40% by mass or more, 50% by mass or more, or 60% by mass or more.

[0051] (SBR) There are no particular limitations on the SBR, and examples thereof include solution-polymerized SBR (S-SBR), emulsion-polymerized SBR (E-SBR), and modified SBRs thereof (modified S-SBR, modified E-SBR). Modified SBRs include SBRs whose ends and / or main chains are modified, and modified SBRs (condensates, those having a branched structure, etc.) coupled with tin or silicon compounds. Of these, S-SBR and modified SBR are preferred. Furthermore, hydrogenated products of these SBRs (hydrogenated SBR), etc. can also be used. These SBRs may be used alone or in combination of two or more.

[0052] As the SBR, oil-extended SBR or non-oil-extended SBR can be used. When oil-extended SBR is used, the amount of oil extension of SBR, i.e., the content of oil extension oil contained in SBR, is preferably 10 to 50 parts by mass per 100 parts by mass of rubber solid content of SBR.

[0053] As the S-SBR that can be used in the present disclosure, commercially available products from JSR Corporation, Sumitomo Chemical Co., Ltd., Ube Industries, Ltd., Asahi Kasei Corporation, ZS Elastomers Co., Ltd., and the like can be used.

[0054] From the viewpoints of wet grip performance and abrasion resistance, the styrene content of SBR is preferably 10% by mass or more, more preferably 15% by mass or more, and even more preferably 20% by mass or more. From the viewpoints of temperature dependency of grip performance and blow resistance, the styrene content is preferably 60% by mass or less, more preferably 55% by mass or less, and even more preferably 50% by mass or less. In this specification, the styrene content of SBR is 1 It is calculated by H-NMR measurement.

[0055] The vinyl content of SBR is preferably 10 mol% or more, more preferably 15 mol% or more, and even more preferably 20 mol% or more, from the viewpoints of ensuring reactivity with silica, wet grip performance, rubber strength, and abrasion resistance. Also, the vinyl content of SBR is preferably 70 mol% or less, more preferably 65 mol% or less, and even more preferably 60 mol% or less, from the viewpoints of preventing an increase in temperature dependency, breaking elongation, and abrasion resistance. In this specification, the vinyl content of SBR (amount of 1,2-bonded butadiene units) is measured by infrared absorption spectroscopy.

[0056] From the viewpoint of wet grip performance, the weight average molecular weight (Mw) of SBR is preferably 200,000 or more, more preferably 250,000 or more, and even more preferably 300,000 or more. From the viewpoint of crosslinking uniformity, the weight average molecular weight is preferably 2,000,000 or less, more preferably 1,800,000 or less, and even more preferably 1,500,000 or less. In this specification, the weight average molecular weight of SBR can be calculated in terms of standard polystyrene based on the measured value by gel permeation chromatography (GPC) (for example, GPC-8000 series manufactured by Tosoh Corporation, detector: differential refractometer, column: TSKGEL SUPERMALTIPORE HZ-M manufactured by Tosoh Corporation).

[0057] When the rubber composition constituting the first layer 6 and the second layer 7 contains SBR, the content of SBR in 100% by mass of the rubber component is preferably 40% by mass or more, more preferably 50% by mass or more, even more preferably 60% by mass or more, and particularly preferably 70% by mass or more, from the viewpoint of wet grip performance. The upper limit of the content of SBR in the rubber component is not particularly limited, and may be 100% by mass. When the rubber composition constituting the third layer 8 contains SBR, the content of SBR in 100% by mass of the rubber component is not particularly limited.

[0058] (BR) The BR is not particularly limited, and can be one that is commonly used in the tire industry, such as BR with a cis content of less than 50% (low cis BR), BR with a cis content of 90% or more (high cis BR), rare earth butadiene rubber (rare earth BR) synthesized using a rare earth catalyst, BR containing syndiotactic polybutadiene crystals (SPB-containing BR), and modified BR (high cis modified BR, low cis modified BR). Modified BR can be BR modified with the same functional groups as those described above for SBR. These BRs can be used alone or in combination of two or more.

[0059] As the high cis BR, for example, those commercially available from Zeon Corporation, Ube Industries, Ltd., JSR Corporation, etc. can be used. By containing high cis BR, low temperature properties and wear resistance can be improved. The cis content is preferably 95% or more, more preferably 96% or more, further preferably 97% or more, and particularly preferably 98% or more. In this specification, the cis content (amount of cis-1,4-bonded butadiene units) is a value calculated by infrared absorption spectrum analysis.

[0060] The rare earth BR is synthesized using a rare earth catalyst, and has a vinyl content of preferably 1.8 mol% or less, more preferably 1.0 mol% or less, and even more preferably 0.8 mol% or less, and a cis content of preferably 95% or more, more preferably 96% or more, even more preferably 97% or more, and particularly preferably 98% or more. As the rare earth BR, for example, commercially available products from LANXESS Co., Ltd. can be used.

[0061] The SPB-containing BR is not one in which 1,2-syndiotactic polybutadiene crystals are simply dispersed in the BR, but one in which the 1,2-syndiotactic polybutadiene crystals are dispersed after being chemically bonded to the BR. As such an SPB-containing BR, commercially available products from Ube Industries, Ltd. can be used.

[0062] As the modified BR, a modified butadiene rubber (modified BR) in which the terminals and / or the main chain are modified with a functional group containing at least one element selected from the group consisting of silicon, nitrogen and oxygen is preferably used.

[0063] Other modified BRs include those obtained by polymerizing 1,3-butadiene with a lithium initiator and then adding a tin compound, and further having the terminals of the modified BR molecule bonded with tin-carbon bonds (tin-modified BR), etc. The modified BR may be either non-hydrogenated or hydrogenated.

[0064] The BRs listed above may be used alone or in combination of two or more.

[0065] From the viewpoint of wear resistance, the weight average molecular weight (Mw) of BR is preferably 300,000 or more, more preferably 350,000 or more, and even more preferably 400,000 or more. From the viewpoint of crosslinking uniformity, it is preferably 2,000,000 or less, and more preferably 1,000,000 or less. The weight average molecular weight of BR can be determined by standard polystyrene conversion based on the measured value obtained by gel permeation chromatography (GPC) (for example, GPC-8000 series manufactured by Tosoh Corporation, detector: differential refractometer, column: TSKGEL SUPERMALTIPORE HZ-M manufactured by Tosoh Corporation).

[0066] When the rubber compositions constituting the first layer 6, the second layer 7 and the third layer 8 contain BR, the content thereof in 100 mass% of the rubber component is preferably 50 mass% or less, more preferably 40 mass% or less, even more preferably 30 mass% or less, and particularly preferably 20 mass% or less, from the viewpoint of wet grip performance. Furthermore, when BR is contained, the lower limit of the content is not particularly limited, and can be, for example, 1 mass% or more, 3 mass% or more, 5 mass% or more, 10 mass% or more, or 15 mass% or more.

[0067] As the rubber component according to the present disclosure, a diene rubber modified by a functional group having affinity with silica is preferably used. Specifically, diene rubber whose terminal and / or main chain are modified by a functional group having affinity with silica can be mentioned. When such modified diene rubber is compounded, the interaction between the polymer and silica is enhanced, and the reinforcement property is improved, thereby improving the abrasion resistance. In addition, the interaction with silica makes it difficult for the silica and the polymer to move, reducing internal friction, thereby improving fuel efficiency. In particular, when the terminal has a functional group having affinity with silica, the movement of the terminal, which is likely to cause internal friction, is restricted, so that the internal friction between the polymers is more effectively reduced.

[0068] Examples of functional groups having affinity with silica include, but are not limited to, epoxy groups, silyl groups, amino groups, hydroxyl groups, carboxyl groups, amide groups, mercapto groups, etc. Specific examples of silyl groups include alkoxysilyl groups such as trimethoxysilyl, triethoxysilyl, triisopropoxysilyl, dimethoxymethylsilyl, diethoxymethylsilyl, dimethylmethoxysilyl, and dimethylethoxysilyl; acetoxysilyl groups such as triacetoxysilyl, diacetoxymethylsilyl, and acetoxydimethylsilyl; and chlorosilyl groups such as chlorodimethylsilyl, dichloromethylsilyl, and trichlorosilyl.

[0069] Specific examples of diene rubbers modified with a functional group having affinity for silica include SBR or BR modified with an alkoxysilyl group, with SBR modified with an alkoxysilyl group being preferred.

[0070] In the case where a diene rubber modified with a functional group having affinity for silica is contained, the content in 100% by mass of the rubber component is preferably 40% by mass or more, more preferably 50% by mass or more, even more preferably 60% by mass or more, and particularly preferably 70% by mass or more. The upper limit of the content of the diene rubber in the rubber component is not particularly limited and may be 100% by mass.

[0071] (Other rubber components) The rubber component according to the present disclosure may contain rubber components other than the isoprene-based rubber, SBR, and BR. As the other rubber components, crosslinkable rubber components generally used in the tire industry can be used, such as styrene-isoprene-butadiene copolymer rubber (SIBR), styrene-isobutylene-styrene block copolymer (SIBS), chloroprene rubber (CR), acrylonitrile-butadiene rubber (NBR), hydrogenated nitrile rubber (HNBR), butyl rubber (IIR), ethylene propylene rubber, polynorbornene rubber, silicone rubber, chlorinated polyethylene rubber, fluororubber (FKM), acrylic rubber (ACM), hydrin rubber, etc. These other rubber components may be used alone or in combination of two or more.

[0072] <Filler> The rubber composition for treads according to the present disclosure preferably uses a filler containing carbon black and / or silica. The rubber composition constituting the first layer 6 and the second layer 7 preferably contains silica as a filler, more preferably carbon black and silica. The rubber composition constituting the third layer 8 preferably contains carbon black as a filler.

[0073] (Carbon Black) As the carbon black, any carbon black commonly used in the tire industry can be appropriately used, such as GPF, FEF, HAF, ISAF, SAF, etc. These carbon blacks may be used alone or in combination of two or more kinds.

[0074] From the perspective of reinforcement, the nitrogen adsorption specific surface area (N2SA) of carbon black is 10m 2 / g or more is preferable, and 20m 2 From the viewpoints of fuel economy and processability, it is more preferable that the tensile strength is 200 m 2 / g or less is preferable, and 150m 2 / g or less is more preferable, and 100m 2 / g or less is more preferable, and 80m 2 / g or less is more preferable, and 50m 2 The N2SA of carbon black is a value measured in accordance with JIS K 6217-2 "Basic properties of carbon black for rubber - Part 2: Determination of specific surface area - Nitrogen adsorption method - Single point method".

[0075] When carbon black is contained, the content per 100 parts by mass of the rubber component is preferably 1 part by mass or more, more preferably 3 parts by mass or more, and even more preferably 5 parts by mass or more from the viewpoint of abrasion resistance and wet grip performance, and is preferably 50 parts by mass or less, more preferably 40 parts by mass or less, even more preferably 20 parts by mass or less, still more preferably 10 parts by mass or less, and particularly preferably 8 parts by mass or less from the viewpoint of fuel economy.

[0076] (silica) The silica is not particularly limited, and can be, for example, silica prepared by a dry method (anhydrous silica), silica prepared by a wet method (hydrated silica), or other silica commonly used in the tire industry. Among them, hydrated silica prepared by a wet method is preferred because it contains a large number of silanol groups. These silicas can be used alone or in combination of two or more.

[0077] The nitrogen adsorption specific surface area (N2SA) of silica is set at 140m from the viewpoints of fuel efficiency and wear resistance. 2 / g or more is preferable, and 170m 2 / g or more is more preferable, and 200m 2 From the viewpoints of fuel efficiency and processability, it is more preferable that the tensile strength is 350 m 2 / g or less is preferable, and 300m 2 / g or less is more preferable, and 250m 2 / g or less is more preferable. In this specification, the N2SA of silica is a value measured by the BET method in accordance with ASTM D3037-93.

[0078] When silica is contained, the content per 100 parts by mass of the rubber component is preferably 50 parts by mass or more, more preferably 60 parts by mass or more, even more preferably 70 parts by mass or more, still more preferably 80 parts by mass or more, still more preferably 90 parts by mass or more, and particularly preferably 100 parts by mass or more, from the viewpoint of wet grip performance. Also, from the viewpoint of abrasion resistance, the content is preferably 140 parts by mass or less, more preferably 130 parts by mass or less, even more preferably 120 parts by mass or less, and particularly preferably 110 parts by mass or less.

[0079] At least one of the rubber compositions constituting the first layer 6 and the second layer 7 preferably contains 70 parts by mass or more of silica per 100 parts by mass of the rubber component, more preferably 80 parts by mass or more, even more preferably 90 parts by mass or more, and particularly preferably 100 parts by mass or more.

[0080] The total content of silica and carbon black per 100 parts by mass of the rubber component is preferably 40 parts by mass or more, more preferably 50 parts by mass or more, and even more preferably 60 parts by mass or more from the viewpoint of abrasion resistance, and is preferably 160 parts by mass or less, more preferably 140 parts by mass or less, and even more preferably 120 parts by mass or less from the viewpoint of fuel economy and elongation at break.

[0081] From the viewpoint of a balance between fuel economy performance, wet grip performance, and abrasion resistance, the rubber composition constituting the first layer 6 and the second layer 7 preferably has a silica content greater than the carbon black content per 100 parts by mass of the rubber component. The ratio of silica to the total content of silica and carbon black in the first layer 6 and the second layer 7 is preferably 60% by mass or more, more preferably 70% by mass or more, even more preferably 80% by mass or more, even more preferably 85% by mass or more, and particularly preferably 90% by mass or more. The ratio of silica and carbon black to the total content of silica and carbon black in the third layer 8 is not particularly limited, but the ratio of carbon black to the total content of silica and carbon black can be, for example, 50% by mass or more, 70% by mass or more, 90% by mass or more, or 100% by mass.

[0082] (Silane coupling agent) Silica is preferably used in combination with a silane coupling agent. The rubber composition constituting the first layer 6 and the second layer 7 contains a mercapto-based silane coupling agent as a silane coupling agent, and may be used in combination with other silane coupling agents. By blending a mercapto-based silane coupling agent, the reactivity of silica with the polymer can be further improved.

[0083] The mercapto-based silane coupling agent is preferably a compound represented by the following formula (1) and / or a compound containing a bonding unit A represented by the following formula (2) and a bonding unit B represented by the following formula (3). [ka] (In the formula, R 101 , R 102 , and R 103 are each independently an alkyl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, or -O-(R 111 -O) z -R 112 (z R 111 each independently represents a divalent hydrocarbon group having 1 to 30 carbon atoms; R 112 represents an alkyl group having 1 to 30 carbon atoms, an alkenyl group having 2 to 30 carbon atoms, an aryl group having 6 to 30 carbon atoms, or an aralkyl group having 7 to 30 carbon atoms; z represents an integer of 1 to 30; 104 represents an alkylene having 1 to 6 carbon atoms. [ka] [ka] (wherein x represents an integer of 0 or more; y represents an integer of 1 or more; R 201 represents a hydrogen atom, a halogen atom, an alkyl group having 1 to 30 carbon atoms, an alkenyl group having 2 to 30 carbon atoms, or an alkynyl group having 2 to 30 carbon atoms, which may be substituted by a hydroxyl or carboxyl group; R 202represents an alkylene having 1 to 30 carbon atoms, an alkenylene having 2 to 30 carbon atoms, or an alkynylene having 2 to 30 carbon atoms; 201 and R 202 may form a ring structure.)

[0084] Examples of the compound represented by formula (1) include 3-mercaptopropyltrimethoxysilane, 3-mercaptopropyltriethoxysilane, 2-mercaptoethyltrimethoxysilane, 2-mercaptoethyltriethoxysilane, and the compound represented by the following formula (4) (Si363 manufactured by Evonik Degussa), and the compound represented by the following formula (4) can be preferably used. These may be used alone or in combination of two or more. [ka]

[0085] Examples of compounds containing a bond unit A represented by formula (2) and a bond unit B represented by formula (3) include those manufactured and sold by Momentive, Inc. These may be used alone or in combination of two or more.

[0086] The content of mercapto-based silane coupling agent with respect to 100 parts by mass of silica is preferably 0.5 parts by mass or more, more preferably 1.5 parts by mass or more, and even more preferably 2.5 parts by mass or more, from the viewpoint of increasing the dispersibility of silica.Furthermore, from the viewpoint of cost and processability, it is preferably 20 parts by mass or less, more preferably 15 parts by mass or less, and even more preferably 10 parts by mass or less.

[0087] In addition to the mercapto-based silane coupling agent, any silane coupling agent that has been used together with silica in the past can also be used together, for example, sulfide-based silane coupling agents such as bis(3-triethoxysilylpropyl) disulfide and bis(3-triethoxysilylpropyl) tetrasulfide; vinyl-based silane coupling agents such as vinyl triethoxysilane and vinyl trimethoxysilane; amino-based silane coupling agents such as 3-aminopropyl triethoxysilane, 3-aminopropyl trimethoxysilane, and 3-(2-aminoethyl) aminopropyl triethoxysilane; glycidoxy-based silane coupling agents such as γ-glycidoxypropyl triethoxysilane and γ-glycidoxypropyl trimethoxysilane; nitro-based silane coupling agents such as 3-nitropropyl trimethoxysilane and 3-nitropropyl triethoxysilane; chloro-based silane coupling agents such as 3-chloropropyl trimethoxysilane and 3-chloropropyl triethoxysilane. Among them, sulfide-based silane coupling agents are preferred. These silane coupling agents may be used alone or in combination of two or more.

[0088] The content of silane coupling agent with respect to 100 parts by mass of silica (when multiple silane coupling agents are used, the total amount of all of them) is preferably 1.0 parts by mass or more, more preferably 2.0 parts by mass or more, and even more preferably 2.5 parts by mass or more, from the viewpoint of increasing the dispersibility of silica.Furthermore, from the viewpoint of cost and processability, it is preferably 20 parts by mass or less, more preferably 15 parts by mass or less, and even more preferably 10 parts by mass or less.

[0089] As the filler, other fillers may be used in addition to carbon black and silica. Such fillers are not particularly limited, and any fillers generally used in this field, such as aluminum hydroxide, alumina (aluminum oxide), calcium carbonate, magnesium sulfate, talc, clay, etc., may be used. Among them, aluminum hydroxide is preferably used because it has excellent abrasion resistance, durability, wet grip performance, and fuel efficiency. These other fillers may be used alone or in combination of two or more.

[0090] From the perspective of wet grip performance, the nitrogen adsorption specific surface area (N2SA) of aluminum hydroxide is 5m 2 / g or more is preferable, and 10m 2 From the viewpoints of dispersibility of aluminum hydroxide, prevention of re-aggregation, and wear resistance, it is more preferable that the surface area is 50 m 2 / g or less is preferable, and 40m 2 / g or less is more preferable, and 30m 2 / g or less is more preferable. The BET specific surface area of ​​aluminum hydroxide in this specification is a value measured by the BET method in accordance with ASTM D3037-81.

[0091] The average particle size (D50) of aluminum hydroxide is preferably 0.1 μm or more, more preferably 0.2 μm or more, and even more preferably 0.3 μm or more, from the viewpoint of dispersibility of aluminum hydroxide, prevention of re-aggregation, and wear resistance. From the viewpoint of wear resistance, it is preferably 3.0 μm or less, and more preferably 2.0 μm. In this specification, the average particle size (D50) is the particle size at 50% of the cumulative mass value of the particle size distribution curve obtained by a particle size distribution measuring device.

[0092] When aluminum hydroxide is contained, the content per 100 parts by mass of the rubber component is preferably 1.0 part by mass or more, more preferably 3.0 parts by mass or more, and even more preferably 5.0 parts by mass or more from the viewpoint of wet grip performance, and the content of aluminum hydroxide is preferably 50 parts by mass or less, more preferably 40 parts by mass or less, and even more preferably 30 parts by mass or less from the viewpoint of abrasion resistance.

[0093] <Softener> The rubber composition for a tread according to the present disclosure preferably contains a softener. Examples of the softener include a resin component, oil, liquid rubber, and an ester-based plasticizer.

[0094] The resin component is not particularly limited, but examples thereof include petroleum resins, terpene resins, rosin resins, phenol resins, etc. These resin components may be used alone or in combination of two or more.

[0095] In this specification, the term "C5 petroleum resin" refers to a resin obtained by polymerizing a C5 fraction. Examples of C5 fractions include petroleum fractions having 4 to 5 carbon atoms, such as cyclopentadiene, pentene, pentadiene, and isoprene. As the C5 petroleum resin, dicyclopentadiene resin (DCPD resin) is preferably used.

[0096] In this specification, the term "aromatic petroleum resin" refers to a resin obtained by polymerizing a C9 fraction, and may be a hydrogenated or modified resin. Examples of C9 fractions include petroleum fractions having 8 to 10 carbon atoms, such as vinyl toluene, alkyl styrene, indene, and methyl indene. Specific examples of aromatic petroleum resins include, for example, Coumarone-indene resin, coumaron resin, indene resin, and aromatic vinyl resin are preferably used. As the aromatic vinyl resin, a homopolymer of α-methylstyrene or styrene, or a copolymer of α-methylstyrene and styrene is preferred, and a copolymer of α-methylstyrene and styrene is more preferred, because they are economical, easy to process, and have excellent heat generation properties. As the aromatic vinyl resin, for example, commercially available products from Kraton, Eastman Chemical, etc. can be used.

[0097] In this specification, the term "C5C9 petroleum resin" refers to a resin obtained by copolymerizing the C5 fraction and the C9 fraction, and may be a hydrogenated or modified resin. Examples of the C5 fraction and the C9 fraction include the petroleum fractions described above. As the C5C9 petroleum resin, for example, those commercially available from Tosoh Corporation, LUHUA, etc. can be used.

[0098] Examples of the terpene resin include polyterpene resins consisting of at least one selected from terpene compounds such as α-pinene, β-pinene, limonene, and dipentene; aromatic modified terpene resins made from the terpene compounds and aromatic compounds; terpene phenolic resins made from terpene compounds and phenolic compounds; and terpene resins obtained by subjecting these terpene resins to hydrogenation treatment (hydrogenated terpene resins). Examples of aromatic compounds that are raw materials for aromatic modified terpene resins include styrene, α-methylstyrene, vinyltoluene, and divinyltoluene. Examples of phenolic compounds that are raw materials for terpene phenolic resins include phenol, bisphenol A, cresol, and xylenol.

[0099] The rosin-based resin is not particularly limited, but examples thereof include natural rosin resin and rosin-modified resins obtained by modifying rosin by hydrogenation, disproportionation, dimerization, esterification, or the like.

[0100] The phenol-based resin is not particularly limited, but examples thereof include phenol formaldehyde resin, alkylphenol formaldehyde resin, alkylphenol acetylene resin, and oil-modified phenol formaldehyde resin.

[0101] From the viewpoint of wet grip performance, the softening point of the resin component is preferably 60° C. or higher, and more preferably 65° C. or higher. From the viewpoint of processability and improving the dispersibility of the rubber component and the filler, the softening point is preferably 150° C. or lower, more preferably 140° C. or lower, and even more preferably 130° C. or lower. In this specification, the softening point may be defined as the temperature at which the ball drops when the softening point specified in JIS K 6220-1:2001 is measured using a ring and ball softening point tester.

[0102] When a resin component is contained, the content per 100 parts by mass of the rubber component is preferably 1 part by mass or more, more preferably 3 parts by mass or more, and even more preferably 5 parts by mass or more from the viewpoint of wet grip performance, and is preferably 60 parts by mass or less, more preferably 50 parts by mass or less, even more preferably 40 parts by mass or less, and particularly preferably 30 parts by mass or less from the viewpoint of suppressing heat buildup.

[0103] Examples of the oil include process oil, vegetable oil, and animal oil. Examples of the process oil include paraffin-based process oil, naphthenic process oil, and aromatic process oil. In addition, as an environmental measure, process oil with a low content of polycyclic aromatic compound (PCA) compounds can be used. Examples of the low PCA content process oil include light extract solvate (MES), treated distillate aromatic extract (TDAE), and heavy naphthenic oil.

[0104] When oil is contained, the content per 100 parts by mass of the rubber component is preferably 5 parts by mass or more, more preferably 10 parts by mass or more, and even more preferably 15 parts by mass or more from the viewpoint of processability. Also, from the viewpoint of abrasion resistance, the content is preferably 120 parts by mass or less, more preferably 100 parts by mass or less, and even more preferably 90 parts by mass or less. In this specification, the content of oil includes the amount of oil contained in the oil-extended rubber.

[0105] The liquid rubber is not particularly limited as long as it is a polymer that is in a liquid state at room temperature (25° C.), and examples thereof include liquid butadiene rubber (liquid BR), liquid styrene butadiene rubber (liquid SBR), liquid isoprene rubber (liquid IR), liquid styrene isoprene rubber (liquid SIR), liquid farnesene rubber, etc. These liquid rubbers may be used alone or in combination of two or more kinds.

[0106] When the liquid rubber is contained, the content per 100 parts by mass of the rubber component is preferably 1 part by mass or more, more preferably 2 parts by mass or more, even more preferably 3 parts by mass or more, and particularly preferably 5 parts by mass or more. The content of the liquid rubber is preferably 50 parts by mass or less, more preferably 40 parts by mass or less, and even more preferably 20 parts by mass or less.

[0107] Examples of ester-based plasticizers include dibutyl adipate (DBA), diisobutyl adipate (DIBA), dioctyl adipate (DOA), di-2-ethylhexyl azelate (DOZ), dibutyl sebacate (DBS), diisononyl adipate (DINA), diethyl phthalate (DEP), dioctyl phthalate (DOP), diundecyl phthalate (DUP), dibutyl phthalate (DBP), dioctyl sebacate (DOS), tributyl phosphate (TBP), trioctyl phosphate (TOP), triethyl phosphate (TEP), trimethyl phosphate (TMP), thymidine triphosphate (TTP), tricresyl phosphate (TCP), trixylenyl phosphate (TXP), etc. These ester-based plasticizers may be used alone or in combination of two or more.

[0108] The content of the softener per 100 parts by mass of the rubber component (the total amount when multiple softeners are used in combination) is preferably 5 parts by mass or more, more preferably 10 parts by mass or more, and even more preferably 15 parts by mass or more from the viewpoint of wet grip performance, and is preferably 120 parts by mass or less, more preferably 100 parts by mass or less, even more preferably 90 parts by mass or less, and particularly preferably 80 parts by mass or less from the viewpoint of processability.

[0109] <Other compounding agents> In addition to the above-mentioned components, the rubber composition according to the present disclosure may appropriately contain compounding agents commonly used in the tire industry, such as wax, processing aids, stearic acid, zinc oxide, antioxidants, vulcanizing agents, and vulcanization accelerators.

[0110] When the wax is contained, the content thereof per 100 parts by mass of the rubber component is preferably 0.5 parts by mass or more, and more preferably 1 part by mass or more, from the viewpoint of weather resistance of the rubber, and is preferably 10 parts by mass or less, and more preferably 5 parts by mass or less, from the viewpoint of preventing whitening of the tire due to bloom.

[0111] Examples of the processing aid include fatty acid metal salts, fatty acid amides, amide esters, silica surfactants, fatty acid esters, mixtures of fatty acid metal salts and amide esters, mixtures of fatty acid metal salts and fatty acid amides, etc. These processing aids may be used alone or in combination of two or more. Examples of the processing aids that can be used include those commercially available from Schill+Seilacher, Performance Additives, etc.

[0112] When a processing aid is contained, the content thereof per 100 parts by mass of the rubber component is preferably 0.5 parts by mass or more, more preferably 1 part by mass or more, from the viewpoint of improving processability, and is preferably 10 parts by mass or less, more preferably 8 parts by mass or less, from the viewpoints of abrasion resistance and breaking strength.

[0113] The antiaging agent is not particularly limited, but examples thereof include amine-based, quinoline-based, quinone-based, phenol-based, and imidazole-based compounds, and carbamic acid metal salts, and the like. Phenylenediamine-based antiaging agents such as N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine, N-isopropyl-N'-phenyl-p-phenylenediamine, N,N'-diphenyl-p-phenylenediamine, N,N'-di-2-naphthyl-p-phenylenediamine, and N-cyclohexyl-N'-phenyl-p-phenylenediamine, and quinoline-based antiaging agents such as 2,2,4-trimethyl-1,2-dihydroquinoline polymer and 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline are preferred. These antiaging agents may be used alone or in combination of two or more.

[0114] When an antioxidant is contained, the content per 100 parts by mass of the rubber component is preferably 0.5 parts by mass or more, more preferably 1 part by mass or more, from the viewpoint of ozone crack resistance of the rubber, and is preferably 10 parts by mass or less, more preferably 5 parts by mass or less, from the viewpoint of abrasion resistance and wet grip performance.

[0115] When stearic acid is contained, the content thereof per 100 parts by mass of the rubber component is preferably 0.5 parts by mass or more, more preferably 1 part by mass or more, from the viewpoint of processability, and is preferably 10 parts by mass or less, more preferably 5 parts by mass or less, from the viewpoint of vulcanization speed.

[0116] When zinc oxide is contained, the content per 100 parts by mass of the rubber component is preferably 0.5 parts by mass or more, more preferably 1 part by mass or more, from the viewpoint of processability, and is preferably 10 parts by mass or less, more preferably 5 parts by mass or less, from the viewpoint of abrasion resistance.

[0117] As the vulcanizing agent, sulfur is preferably used, and examples of the sulfur that can be used include powdered sulfur, oil-treated sulfur, precipitated sulfur, colloidal sulfur, insoluble sulfur, and highly dispersible sulfur.

[0118] When sulfur is contained as a vulcanizing agent, the content per 100 parts by mass of the rubber component is preferably 0.1 parts by mass or more, more preferably 0.3 parts by mass or more, and even more preferably 0.5 parts by mass or more, from the viewpoint of ensuring sufficient vulcanization reaction. Also, from the viewpoint of preventing deterioration, the content is preferably 5.0 parts by mass or less, more preferably 4.0 parts by mass or less, and even more preferably 3.0 parts by mass or less. Note that, when oil-containing sulfur is used as a vulcanizing agent, the content of the vulcanizing agent is the total content of the pure sulfur contained in the oil-containing sulfur.

[0119] Examples of vulcanizing agents other than sulfur include alkylphenol-sulfur chloride condensates, sodium 1,6-hexamethylene-dithiosulfate dihydrate, 1,6-bis(N,N'-dibenzylthiocarbamoyldithio)hexane, etc. As these vulcanizing agents other than sulfur, commercially available products from Taoka Chemical Co., Ltd., Lanxess Co., Ltd., Flexis, etc. can be used.

[0120] Examples of the vulcanization accelerator include sulfenamide-based, thiazole-based, thiuram-based, thiourea-based, guanidine-based, dithiocarbamic acid-based, aldehyde-amine-based or aldehyde-ammonia-based, imidazoline-based, and xanthate-based vulcanization accelerators. These vulcanization accelerators may be used alone or in combination of two or more. Among them, one or more vulcanization accelerators selected from the group consisting of sulfenamide-based, guanidine-based, and thiazole-based vulcanization accelerators are preferred, and it is more preferred to use a sulfenamide-based vulcanization accelerator and a guanidine-based vulcanization accelerator in combination.

[0121] Examples of sulfenamide vulcanization accelerators include N-tert-butyl-2-benzothiazolylsulfenamide (TBBS), N-cyclohexyl-2-benzothiazolylsulfenamide (CBS), N,N-dicyclohexyl-2-benzothiazolylsulfenamide (DCBS), etc. Among them, N-cyclohexyl-2-benzothiazolylsulfenamide (CBS) is preferred.

[0122] Examples of the guanidine vulcanization accelerator include 1,3-diphenylguanidine (DPG), 1,3-di-o-tolylguanidine, 1-o-tolylbiguanide, di-o-tolylguanidine salt of dicatechol borate, 1,3-di-o-cumenylguanidine, 1,3-di-o-biphenylguanidine, 1,3-di-o-cumenyl-2-propionylguanidine, etc. Among them, 1,3-diphenylguanidine (DPG) is preferable.

[0123] Examples of the thiazole-based vulcanization accelerator include 2-mercaptobenzothiazole, cyclohexylamine salt of 2-mercaptobenzothiazole, di-2-benzothiazolyl disulfide, etc. Among these, 2-mercaptobenzothiazole is preferred.

[0124] When a vulcanization accelerator is contained, the content per 100 parts by mass of the rubber component is preferably 1 part by mass or more, more preferably 2 parts by mass or more. The content per 100 parts by mass of the rubber component is preferably 8 parts by mass or less, more preferably 7 parts by mass or less, and even more preferably 6 parts by mass or less. By setting the content of the vulcanization accelerator within the above range, breaking strength and elongation tend to be secured.

[0125] The rubber composition according to the present disclosure can be produced by a known method, for example, by kneading the above-mentioned components using a rubber kneading device such as an open roll or an internal kneader (such as a Banbury mixer or kneader).

[0126] The kneading step includes, for example, a base kneading step in which compounding ingredients and additives other than the vulcanizing agent and the vulcanization accelerator are kneaded, and a final kneading (F kneading) step in which the vulcanizing agent and the vulcanization accelerator are added to the kneaded product obtained in the base kneading step and kneaded. Furthermore, the base kneading step can be divided into a plurality of steps as desired.

[0127] The kneading conditions are not particularly limited, but examples thereof include a method in which in the base kneading step, kneading is performed for 3 to 10 minutes at a discharge temperature of 150 to 170° C., and in the final kneading step, kneading is performed for 1 to 5 minutes at 70 to 110° C. The vulcanization conditions are not particularly limited, but examples thereof include a method in which vulcanization is performed for 10 to 30 minutes at 150 to 200° C.

[0128] [tire] The tire according to the present disclosure has a tread including a first layer 6, a second layer 7, and a third layer 8, and may be a pneumatic tire or a non-pneumatic tire. Examples of pneumatic tires include passenger car tires, truck and bus tires, motorcycle tires, and high performance tires, and are particularly suitable for use as passenger car tires. In this specification, the high performance tire is a tire that is particularly excellent in grip performance, and is a concept that also includes racing tires used on racing vehicles.

[0129] A tire having a tread including the first layer 6, the second layer 7, and the third layer 8 can be manufactured by a normal method using the above rubber composition. That is, an unvulcanized rubber composition in which the above components are blended with the rubber component as necessary is extruded into the shapes of the first layer 6, the second layer 7, and the third layer 8 using an extruder equipped with a die of a predetermined shape, and then laminated together with other tire components on a tire building machine and molded by a normal method to form an unvulcanized tire, and the unvulcanized tire is heated and pressurized in a vulcanizer to manufacture a tire. EXAMPLES

[0130] The present disclosure will be described based on examples, but the present disclosure is not limited to only the examples.

[0131] The various chemicals used in the examples and comparative examples are listed below. NR:TSR20 SBR: modified solution-polymerized SBR produced in Production Example 1 described below (styrene content: 30 mass%, vinyl content: 52 mol%, Mw: 250,000, non-oil extended product) BR: UBEPOL BR (registered trademark) 150B manufactured by Ube Industries, Ltd. (vinyl content: 1.5 mol%, cis content: 97%, Mw: 440,000) Carbon black: Diablack N220 (N2SA: 115m) manufactured by Mitsubishi Chemical Corporation 2 / g) Silica: ULTRASIL (registered trademark) 9100GR (N2SA: 230 m) manufactured by Evonik Degussa 2 / g, average primary particle diameter: 15nm) Aluminum hydroxide: Navaltec's Apilar 120E (average particle size: 0.9 μm, N2SA: 11 μm) 2 / g) Silane coupling agent 1: NXT-Z45 (mercapto-based silane coupling agent) manufactured by Momentive Silane coupling agent 2: Si266 (bis(3-triethoxysilylpropyl) disulfide) manufactured by Evonik Degussa Oil: Process oil X-140 manufactured by JXTG Energy Corporation Resin component: Kraton SYLVARES SA85 (copolymer of α-methylstyrene and styrene, softening point: 85°C) Liquid rubber: Cray Valley Ricon 100 (liquid SBR) Wax: Sannock N manufactured by Ouchi Shinko Chemical Industry Co., Ltd. Antioxidant 1: Nocrac 6C (N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine) manufactured by Ouchi Shinko Chemical Industry Co., Ltd. Antioxidant 2: Nocrac 224 (2,2,4-trimethyl-1,2-dihydroquinoline polymer) manufactured by Ouchi Shinko Chemical Industry Co., Ltd. Stearic acid: Beads of stearic acid camellia manufactured by NOF Corporation Zinc oxide: Two types of zinc oxide manufactured by Mitsui Mining & Smelting Co., Ltd. Sulfur: Powdered sulfur manufactured by Tsurumi Chemical Industry Co., Ltd. (Powdered sulfur containing 5% oil) Vulcanization accelerator 1: Noccela CZ (N-cyclohexyl-2-benzothiazolyl sulfenamide) manufactured by Ouchi Shinko Chemical Industry Co., Ltd. Vulcanization accelerator 2: Soxinol DG (N,N'-diphenylguanidine) manufactured by Sumitomo Chemical Co., Ltd.

[0132] Preparation Example 1: Synthesis of SBR1 Cyclohexane, tetrahydrofuran, styrene, and 1,3-butadiene were charged into a nitrogen-substituted autoclave reactor. After adjusting the temperature of the reactor contents to 20°C, n-butyllithium was added to initiate polymerization. Polymerization was performed under adiabatic conditions, with the maximum temperature reaching 85°C. When the polymerization conversion reached 99%, 1,3-butadiene was added, and polymerization was continued for another 5 minutes, after which N,N-bis(trimethylsilyl)-3-aminopropyltrimethoxysilane was added as a modifier to carry out the reaction. After the polymerization reaction was completed, 2,6-di-tert-butyl-p-cresol was added. Next, the solvent was removed by steam stripping, and the mixture was dried with a heated roll adjusted to 110°C to obtain SBR1.

[0133] Examples and Comparative Examples According to the compounding recipe shown in Table 1, chemicals other than sulfur and vulcanization accelerator were kneaded for 1 to 10 minutes using a 1.7L closed type Banbury mixer until the discharge temperature reached 150 to 160 ° C., and a kneaded product was obtained. Next, sulfur and vulcanization accelerator were added to the kneaded product obtained using a two-axis open roll, and the mixture was kneaded for 4 minutes until the temperature reached 105 ° C., and an unvulcanized rubber composition was obtained. The unvulcanized rubber composition obtained was molded according to the shape of the first layer, second layer, and third layer of the tread, and laminated together with other tire components to prepare an unvulcanized tire, which was vulcanized at 150 ° C. for 30 minutes to obtain each test tire (size: 205 / 55R15, rim: 15 × 6.0J, internal pressure: 230kPa) shown in Table 2.

[0134] <Low fuel consumption performance> Using a rolling resistance tester, the rolling resistance of each test tire was measured when it was run on a rim of 15×6JJ, with an internal pressure of 230 kPa, a load of 3.43 kN, and at a speed of 80 km / h. The rolling resistance of the test tire of Comparative Example 8 was set at 100, and the results were expressed as an index using the following calculation formula. The larger the value, the better the fuel economy performance. (Fuel economy performance index)=(Rolling resistance of the tire of Comparative Example 8) / (Rolling resistance of each test tire)×100

[0135] <Wet grip performance> Each test tire was attached to all wheels of a vehicle (domestic FF 2000cc), and the braking distance from the point where the brakes were applied at a speed of 100 km / h on a wet asphalt road surface was measured. The braking distance of the test tire of Comparative Example 8 was set to 100, and the wet grip performance was expressed as an index according to the following calculation formula. The larger the value, the better the wet grip performance. (Wet grip performance index)=(braking distance of tire of Comparative Example 8) / (braking distance of each test tire)×100

[0136] <Wear resistance> Each test tire was mounted on all wheels of a vehicle (domestic FF 2000cc) and run, and the change in pattern groove depth after 50,000 km of running was measured. The reciprocal value of the amount of change was expressed as an index, with Comparative Example 8 being set at 100. The larger the value, the better the wear resistance performance.

[0137] <Durability> The test tires were fitted to all wheels of a vehicle (domestic FF 2000cc) and driven on a test course, and the vehicle was driven in a zigzag manner at the limit of grip to check for the occurrence of cracks near the interface between the first and second layers of the tread. The durability index was calculated using the following formula. The higher the value, the better the durability. (Durability performance index)=(Number of cracks generated in the tire of Comparative Example 8)−(Number of cracks generated in each test tire)+100

[0138] The target performance value for the overall performance of fuel economy, wet grip performance, abrasion resistance, and durability (the sum of the fuel economy performance index, wet grip performance index, abrasion resistance performance index, and durability performance index) is more than 400.

[0139] [Table 1]

[0140] [Table 2]

[0141] The results in Tables 1 and 2 show that the tire of the present disclosure, which has three or more specified rubber layers in the tread portion, which have a specific compounding, and which has a specified ratio of the groove depth in the second layer to the circumferential groove depth, has improved overall performance in terms of fuel economy, wet grip performance, wear resistance, and durability. [Explanation of symbols]

[0142] 1...Circumferential groove 2... land department 3. Tread surface 4. Land extension 5. Extension line of the deepest part of the bottom of the circumferential groove 6...First layer 7...Second layer 8...Third layer 9. Extension of the outer surface of the second layer

Claims

1. A tire having a tread, The tread includes at least a first layer constituting a tread surface, a second layer adjacent to the radially inner side of the first layer, and a third layer located radially inner side of the second layer, the first layer, the second layer and the third layer are made of a rubber composition containing a rubber component, the rubber composition constituting the first layer and the second layer contains silica and a mercapto-based silane coupling agent, and a content of silica per 100 parts by mass of the rubber component is greater than a content of carbon black, The tread has land portions partitioned by a plurality of circumferential grooves, The deepest portion of the groove bottom of the circumferential groove is formed to be located radially inward of the outer surface of the second layer, a distance between an extension line of the land portion and an extension line of the deepest part of the groove bottom of the circumferential groove is H1, and a distance between an extension line of an outer surface of the second layer and an extension line of the deepest part of the groove bottom of the circumferential groove is H2, wherein H2 / H1 is 0.20 or more.

2. 2. The tire according to claim 1, wherein a difference between a content of the softener per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and a content of the softener per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is 50 parts by mass or less.

3. 3. The tire according to claim 1, wherein a difference between a sulfur content per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and a sulfur content per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is 1.0 part by mass or less.

4. The tire according to any one of claims 1 to 3, wherein a difference between a content of a vulcanization accelerator per 100 parts by mass of the rubber component of the rubber composition constituting the first layer and a content of a vulcanization accelerator per 100 parts by mass of the rubber component of the rubber composition constituting the second layer is 3.5 parts by mass or less.

5. The tire according to any one of claims 1 to 4, wherein the H2 / H1 is 0.30 or more.

6. The tire according to any one of claims 1 to 5, wherein at least one of the rubber compositions constituting the first layer and the second layer contains 100 parts by mass or more of silica per 100 parts by mass of the rubber component.

7. The tire according to any one of claims 1 to 6, wherein a rubber composition constituting the first layer and the second layer contains 50 to 130 parts by mass of silica per 100 parts by mass of the rubber component, and a ratio of silica to a total content of silica and carbon black is 60% by mass or more.

8. The tire according to any one of claims 1 to 7, wherein the rubber composition constituting the first layer and the second layer contains 10 parts by mass or more of a softener per 100 parts by mass of the rubber component.

9. The tire according to any one of claims 1 to 8, wherein the rubber components constituting the first layer and the second layer contain 40 mass % or more of styrene-butadiene rubber.

10. The tire according to any one of claims 1 to 9, wherein a content of a diene rubber modified with a functional group having affinity for silica in 100% by mass of the rubber component constituting the first layer and the second layer is 40% by mass or more.

11. The tire according to any one of claims 1 to 10, wherein the rubber composition constituting the first layer contains 1.0 part by mass or more of aluminum hydroxide per 100 parts by mass of the rubber component.

12. The tire according to any one of claims 1 to 11, wherein the first layer, the second layer, and the third layer each have a thickness of 1.0 mm or more.

13. The tire according to any one of claims 1 to 12, wherein a ratio (t2 / t1) of a thickness t2 of the second layer to a thickness t1 of the first layer is 0.4 to 5.

0.

14. The tire according to any one of claims 1 to 13, wherein a ratio (t3 / t2) of a thickness t3 of the third layer to a thickness t2 of the second layer is 0.2 to 3.

0.

15. The tire according to any one of claims 1 to 14, further comprising at least one selected from the group consisting of a sealant, a sound-damping material, and an electronic component for tire monitoring, in a tire cavity.

16. The tire according to any one of claims 1 to 15, wherein the tire is a passenger tire.