Steel plate and its manufacturing method

Abstract

Provided is a high-strength steel plate which has excellent ammonia SCC resistance and low-temperature toughness, and is used for storage tanks for storing liquefied gas in energy transport ships. The steel plate: has a predetermined composition; has hardness properties in which the average hardness is 230 HV0.1 or less and the hardness variation is 30 HV0.1 or less at a depth of 0.5 mm from the surface of the steel plate, the maximum hardness in the plate thickness direction is at a position of 1.0 mm or more and 1 / 4 or less of the plate thickness from the surface of the steel plate, and the hardness variation in the plate thickness direction is 70 HV1 or less; and has a metal structure in which the volume fraction of a bainite structure at a depth of 0.5 mm from the surface of the steel plate is 90% or more.

Description

[Technical field]

[0001] The present invention relates to a high-strength steel plate excellent in toughness and corrosion resistance, in particular to a high-strength steel plate for low temperature use excellent in low-temperature toughness and resistance to liquid ammonia stress corrosion cracking, which is suitable for structural members such as tanks used at low temperatures in a liquid ammonia environment, and to a method for producing the same. [Background technology]

[0002] In recent years, the demand for energy has increased, and the transportation of liquefied gas by energy carriers has become more common. In order to operate energy carriers efficiently, the tanks of some carriers may carry not only LPG but also liquid ammonia. Recently, the use of hydrogen carriers for liquid ammonia and liquid ammonia fuel has been promoted, and therefore attempts are being made to increase the size of tanks for transporting and storing liquefied ammonia.

[0003] It is known that liquid ammonia can cause stress corrosion cracking (hereinafter referred to as ammonia SCC) in carbon steel piping, storage tanks, tank cars, line pipes, and other materials that handle liquefied ammonia. For this reason, steel materials with low ammonia SCC susceptibility have been used for steel materials used in liquid ammonia environments, and engineering measures have been taken to suppress ammonia SCC.

[0004] For example, it is known that the occurrence of ammonia SCC is correlated with the strength of the material, and when using carbon steel, it is necessary to control the yield strength (YS) to 440 MPa or less. At the same time, there is an increasing demand for higher strength steel plates in order to prevent stress corrosion cracking caused by ammonia.

[0005] Furthermore, since liquefied gases such as LPG and liquid ammonia are transported and stored at low temperatures, the steel plates used in storage tanks for these liquefied gases are required to have excellent low-temperature toughness.

[0006] The techniques for satisfying the low-temperature toughness and the specified strength range required for liquefied gas storage tanks as described above are disclosed in Patent Documents 1 and 2. In the techniques described in these documents, high low-temperature toughness and the specified strength properties are realized by a method in which a thick steel plate that has been cooled after hot rolling is heat-treated several times, or a thick steel plate that has been water-cooled after hot rolling is heat-treated several times. [Prior art documents] [Patent documents]

[0007] [Patent Document 1] Japanese Patent Application Publication No. 10-140235 [Patent Document 2] Japanese Patent Application Publication No. 10-168516 Summary of the Invention [Problem to be solved by the invention]

[0008] However, the methods described in Patent Documents 1 and 2 above require multiple heat treatments, which poses an economic problem in that the costs for equipment and energy required for the treatment are high.

[0009] The present invention aims to solve the above problems and to provide a high-strength steel plate excellent in ammonia SCC resistance and low-temperature toughness for use in storage tanks, etc. used to store liquefied gas on energy transport ships, and a manufacturing method thereof. [Means for solving the problem]

[0010] In order to achieve the above object, the present inventors have conducted extensive research into various factors affecting the low-temperature toughness and strength properties of steel plates using a TMCP process and an online induction heating device. As a result, the inventors have found that SCC resistance in a liquid ammonia environment can be effectively obtained and costly multiple heat treatments can be omitted by adding predetermined amounts of elements such as C, Si, Mn, and Al to a steel plate, controlling the metal structure so that the volume fraction of the bainite structure at a position 0.5 mm from the surface of the steel plate is 90% or more, making the average hardness at a position 0.5 mm deep from the surface of the steel plate 230 HV0.1 or less and the hardness variation at a position 0.5 mm deep from the surface of the steel plate 30 HV0.1 or less, and further making the maximum hardness value in the plate thickness direction exist at a position 1.0 mm or more from the surface of the steel plate and 1 / 4 or less of the plate thickness, and making the hardness variation in the plate thickness direction 70 HV1 or less.

[0011] That is, the present invention has been made based on the above findings, and the gist of the present invention is as follows. 1. In mass percent, C: 0.010~0.200%, Si: 0.01 to 0.50%, Mn: 0.50-2.50%, Al: 0.010-0.060%, N: 0.0010% or more and 0.0100% or less, P: 0.020% or less, S: 0.0100% or less and O: 0.0100% or less and the balance being Fe and unavoidable impurities, At a depth of 0.5 mm from the surface of the steel plate, the average hardness is 230 HV0.1 or less, the hardness variation is 30 HV0.1 or less, and the maximum hardness value in the plate thickness direction is located at a position 1.0 mm or more and 1 / 4 of the plate thickness or less from the surface of the steel plate, and the hardness variation in the plate thickness direction is 70 HV1 or less; and A steel plate having a metal structure in which the volume fraction of bainite structure at a position 0.5 mm deep from the surface of the steel plate is 90% or more.

[0012] 2. The composition further comprises, in mass%, Cu: 0.01 to 0.50%, Ni: 0.01 to 2.00%, Cr: 0.01 to 1.00%, Sn: 0.01 to 0.50%, Sb: 0.01 to 0.50%, Mo: 0.01 to 0.50% and W: 0.01 to 1.00% The steel plate according to 1 above, containing one or more selected from the following:

[0013] 3. The composition further comprises, in mass%, V: 0.01 to 1.00%, Ti: 0.005 to 0.100%, Co: 0.01 to 1.00%, Nb: 0.005 to 0.100%, B: 0.0001~0.0100%, Ca: 0.0005~0.0200%, Mg: 0.0005 to 0.0200% and REM: 0.0005~0.0200% 3. The steel sheet according to claim 1 or 2, comprising one or more selected from the following:

[0014] 4. In mass percent, C: 0.010~0.200%, Si: 0.01 to 0.50%, Mn: 0.50-2.50%, Al: 0.010-0.060%, N: 0.0010% or more and 0.0100% or less, P: 0.020% or less, S: 0.0100% or less and O: 0.0100% or less A method for producing a steel sheet, comprising the steps of: hot rolling a steel material having a composition containing, with the balance being Fe and unavoidable impurities, with a rolling end temperature being equal to or higher than the Ar3 transformation point; subsequently performing accelerated cooling from a cooling start temperature equal to or higher than the Ar3 transformation point; and subsequently performing reheating, In the accelerated cooling, the cooling stop temperature is in the range of 200 to 600 ° C., and the cooling rate at the 1 / 4 position of the plate thickness of the steel plate is in the range of 20 to 120 ° C. / s, The reheating is performed with the ultimate temperature at a position 1 / 4 of the plate thickness of the steel plate set to 500°C or less, until the ultimate temperature at a position 0.5 mm deep from the surface of the steel plate reaches a range of 400 to 680°C.

[0015] 5. The composition of the steel material is further, in mass%, Cu: 0.01 to 0.50%, Ni: 0.01 to 2.00%, Cr: 0.01 to 1.00%, Sn: 0.01 to 0.50%, Sb: 0.01 to 0.50%, Mo: 0.01 to 0.50% and W: 0.01 to 1.00% 5. The method for producing a steel sheet according to 4 above, comprising one or more selected from the following:

[0016] 6. The composition of the steel material is further, in mass%, V: 0.01 to 1.00%, Ti: 0.005 to 0.100%, Co: 0.01 to 1.00%, Nb: 0.005 to 0.100%, B: 0.0001~0.0100%, Ca: 0.0005~0.0200%, Mg: 0.0005 to 0.0200% and 6. The method for producing a steel sheet according to 4 or 5 above, containing one or more selected from the group consisting of REM: 0.0005 to 0.0200%. Effect of the Invention

[0017] According to the present invention, it is possible to provide, by an inexpensive process, a steel plate having excellent toughness at low temperatures, i.e., excellent impact resistance and ammonia SCC resistance at low temperatures, and high strength suitable for structural members such as tanks used at low temperatures and in a liquid ammonia environment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0018] Hereinafter, an embodiment of the present invention will be described. Note that "%" representing the content of the following components (elements) means "% by mass" unless otherwise specified.

[0019] (1) Composition The composition (chemical composition) of the steel sheet will be described below.

[0020] C: 0.010~0.200% C is the most effective element for increasing the strength of the steel plate produced by the cooling according to the present invention. To obtain this effect, the C content is specified to be 0.010% or more. Furthermore, from the viewpoint of reducing the content of other alloy elements and producing at a lower cost, the C content is preferably 0.013% or more. On the other hand, if the C content exceeds 0.200%, the toughness and weldability of the steel plate are deteriorated. Therefore, the C content is specified to be 0.200% or less. Furthermore, from the viewpoint of toughness and weldability, the C content is preferably 0.170% or less.

[0021] Silicon: 0.01 to 0.50% Si is added for deoxidation. To obtain this effect, the Si content is set to 0.01% or more. It is preferably set to 0.03% or more. On the other hand, if the Si content exceeds 0.50%, it leads to deterioration of the toughness and weldability of the steel plate. Therefore, the Si content is set to 0.50% or less. From the viewpoint of toughness and weldability, it is preferably set to 0.40% or less.

[0022] Mn: 0.50-2.50% Mn is an element that has the effect of increasing the hardenability of steel, and is one of the important elements that must be added to achieve high strength as in the present invention. In order to obtain this effect, the Mn content is specified to be 0.50% or more. Furthermore, from the viewpoint of reducing the content of other alloy elements and manufacturing at a lower cost, the Mn content is preferably 0.70% or more. On the other hand, if the Mn content exceeds 2.50%, the toughness and weldability of the steel plate are reduced, and the alloy cost becomes excessively high. Therefore, the Mn content is specified to be 2.50% or less. Furthermore, from the viewpoint of suppressing the deterioration of toughness and weldability, the Mn content is preferably 2.30% or less.

[0023] Al: 0.010~0.060% Al acts as a deoxidizer. To obtain this effect, the Al content is set to 0.010% or more. On the other hand, if the Al content exceeds 0.060%, oxide-based inclusions increase, and the cleanliness and toughness decrease. Therefore, the Al content is set to 0.060% or less. Furthermore, from the viewpoint of further preventing deterioration of toughness, the Al content is preferably set to 0.050% or less.

[0024] N: 0.0010~0.0100% N contributes to refining the structure and improves the toughness of the steel plate. In order to obtain this effect, the N content is set to 0.0010% or more, and preferably 0.0020% or more. On the other hand, if the N content exceeds 0.0100%, it leads to a decrease in toughness. Therefore, the N content is set to 0.0100% or less. Furthermore, from the viewpoint of further suppressing the decrease in toughness and weldability, the N content is preferably set to 0.0080% or less. Note that, when Ti is present, N can combine with the Ti and precipitate as TiN.

[0025] P:0.020% or less P has adverse effects such as reducing toughness and weldability by segregating at grain boundaries. Therefore, it is desirable to make the P content as low as possible, but it is acceptable if it is 0.020% or less. The lower limit of the P content is not particularly limited and may be 0%, but since P is usually an element that may remain in steel industrially, it may be more than 0%. In addition, excessive reduction leads to an increase in refining costs, so from the viewpoint of cost, it is preferable to make the P content 0.0005% or more.

[0026] S: 0.0100% or less S is an element that exists in steel as sulfide-based inclusions such as MnS, and has adverse effects such as becoming the starting point of fracture and reducing the toughness of the steel plate. Therefore, it is desirable to make the S content as low as possible, but it is acceptable if it is 0.0100% or less. The lower limit of the S content is not particularly limited and may be 0%, but since S is usually an element that may remain in steel industrially, it may be more than 0%. In addition, since excessive reduction leads to an increase in refining costs, it is preferable to make the S content 0.0005% or more from the viewpoint of cost.

[0027] O: 0.0100% or less O is an element that forms oxides, becomes the starting point of fracture, and has adverse effects such as reducing the toughness of the steel plate, so it is limited to 0.0100% or less. The O content is preferably 0.0050% or less, and more preferably 0.0030% or less. On the other hand, the lower limit of the O content is not particularly limited and may be 0%, but since O is usually an element that may remain in steel industrially, it may be more than 0%. In addition, excessive reduction leads to an increase in refining costs, so from the viewpoint of cost, it is preferable that the O content is 0.0010% or more.

[0028] In the composition of the steel sheet of the present invention, the balance other than the above-mentioned components is Fe and unavoidable impurities, however, the above-mentioned composition may contain the elements described below as necessary.

[0029] One or more selected from Cu: 0.01-0.50%, Ni: 0.01-2.00%, Cr: 0.01-1.00%, Sn: 0.01-0.50%, Sb: 0.01-0.50%, Mo: 0.01-0.50%, and W: 0.01-1.00% Cu, Ni, Cr, Sn, Sb, Mo and W are elements that improve strength and ammonia SCC resistance, and one or more of these can be contained. In order to obtain such effects, it is preferable to adjust the Cu content to 0.01% or more when Cu is contained, the Ni content to 0.01% or more when Ni is contained, the Cr content to 0.01% or more when Cr is contained, the Sn content to 0.01% or more when Sn is contained, the Sb content to 0.01% or more when Sb is contained, the Mo content to 0.01% or more when Mo is contained, and the W content to 0.01% or more when W is contained. On the other hand, excessive Ni content leads to deterioration of weldability and increase in alloy cost. In addition, excessive Cu, Cr, Sn, Sb, Mo and W content deteriorate weldability and toughness, which is also disadvantageous from the viewpoint of alloy cost. Therefore, it is preferable to adjust the Cu content to 0.50% or less, the Ni content to 2.00% or less, the Cr content to 1.00% or less, the Sn content to 0.50% or less, the Sb content to 0.50% or less, the Mo content to 0.50% or less, and the W content to 1.00% or less. More preferably, the Cu content is adjusted to 0.40% or less, the Ni content is adjusted to 1.50% or less, the Cr content is adjusted to 0.80% or less, the Sn content is adjusted to 0.40% or less, the Sb content is adjusted to 0.40% or less, the Mo content is adjusted to 0.40% or less, and the W content is adjusted to 0.80% or less.

[0030] V: 0.01 to 1.00% V is an element that has the effect of improving the strength of a steel sheet, and can be added as desired. In order to obtain such an effect, when V is added, the V content is preferably 0.01% or more. On the other hand, if the V content exceeds 1.00%, it leads to deterioration of weldability and an increase in alloy costs. Therefore, when V is added, the V content is preferably 1.00% or less. More preferably, the lower limit of the V content is 0.05% and the upper limit is 0.50%.

[0031] Ti: 0.005 to 0.100% Ti is an element that has a strong tendency to form nitrides and has the effect of fixing N and reducing the amount of solute N, and can be added as desired. Ti can also improve the toughness of the base material and welded parts. In order to obtain such an effect, when Ti is added, the Ti content is preferably 0.005% or more. Furthermore, it is more preferable to make it 0.007% or more. On the other hand, when the Ti content exceeds 0.100%, the toughness is rather reduced. Therefore, when Ti is added, the Ti content is preferably 0.100% or less. Furthermore, it is more preferable to make the Ti content 0.090% or less.

[0032] Co: 0.01 to 1.00% Co is an element that has the effect of improving the strength of the steel sheet, and can be added as desired. In order to obtain such an effect, when Co is added, the Co content is preferably 0.01% or more. On the other hand, if the Co content exceeds 1.00%, it leads to deterioration of weldability and an increase in alloy costs. Therefore, when Co is added, the Co content is preferably 1.00% or less. More preferably, the lower limit of the Co content is 0.05% and the upper limit is 0.50%.

[0033] Nb: 0.005 to 0.100% Nb is an element that has the effect of reducing the prior austenite grain size and improving toughness by precipitating as carbonitride. In order to obtain such an effect, when Nb is added, the Nb content is preferably 0.005% or more. More preferably, it is 0.007% or more. On the other hand, when the Nb content exceeds 0.100%, a large amount of NbC precipitates, and the toughness decreases. Therefore, when Nb is added, the Nb content is preferably 0.100% or less. More preferably, it is 0.060% or less.

[0034] B: 0.0001 to 0.0100% B is an element that has the effect of significantly improving hardenability even when added in a small amount. In other words, it can improve the strength of the steel sheet. In order to obtain this effect, when B is added, the B content is preferably 0.0001% or more. On the other hand, when the B content exceeds 0.0100%, the weldability decreases. Therefore, when B is added, the B content is preferably 0.0100% or less. More preferably, the lower limit of the B content is 0.0010% and the upper limit is 0.0030%.

[0035] Ca: 0.0005~0.0200% Ca is an element that combines with S and has the effect of suppressing the formation of MnS and the like that elongates in the rolling direction. That is, by adding Ca, the morphology of sulfide-based inclusions can be controlled to be spherical, and the toughness of welds and the like can be improved. In order to obtain such an effect, when Ca is added, the Ca content is preferably 0.0005% or more. On the other hand, if the Ca content exceeds 0.0200%, the cleanliness of the steel decreases. The decrease in cleanliness leads to a decrease in toughness. Therefore, when Ca is added, the Ca content is preferably 0.0200% or less. More preferably, the lower limit of the Ca content is 0.0020% and the upper limit is 0.0100%.

[0036] Mg: 0.0005~0.0200% Like Ca, Mg is an element that combines with S and has the effect of suppressing the formation of MnS and the like that elongates in the rolling direction. That is, by adding Mg, the morphology of sulfide-based inclusions can be controlled to be spherical, and the toughness of welds and the like can be improved. In order to obtain such an effect, when Mg is added, the Mg content is preferably 0.0005% or more. On the other hand, when the Mg content exceeds 0.0200%, the cleanliness of the steel decreases. The decrease in cleanliness leads to a decrease in toughness. Therefore, when Mg is added, the Mg content is preferably 0.0200% or less. More preferably, the lower limit of the Mg content is 0.0020% and the upper limit is 0.0100%.

[0037] REM: 0.0005~0.0200% Like Ca and Mg, REM (rare earth metal) is an element that combines with S and inhibits the formation of MnS, etc., which elongates in the rolling direction. That is, by adding REM, the shape of sulfide-based inclusions can be controlled to be spherical, and the toughness of welds, etc. can be improved. When REM is added to obtain such an effect, the REM content is preferably 0.0005% or more. On the other hand, if the REM content exceeds 0.0200%, the cleanliness of the steel decreases. The decrease in cleanliness leads to a decrease in toughness. Therefore, when REM is added, the REM content is preferably 0.0200% or less. More preferably, the lower limit of the REM content is 0.0020% and the upper limit is 0.0100%.

[0038] (2) Hardness characteristics and metal structure In addition to having the above-mentioned chemical composition, the steel plate of the present invention has hardness characteristics in which the average hardness at a position 0.5 mm deep from the surface of the steel plate (also referred to as the 0.5 mm position in the present invention) is 230 HV0.1 or less, the hardness variation at the 0.5 mm position is 30 HV0.1 or less, and the maximum hardness value in the plate thickness direction is located at a position 1.0 mm or more and 1 / 4 of the plate thickness from the surface of the steel plate, and the hardness variation in the plate thickness direction is 70 HV1 or less. Furthermore, the steel sheet of the present invention has a metal structure in which the volume fraction of bainite structure (hereinafter also simply referred to as bainite) at the 0.5 mm position is 90% or more. The reasons for limiting the hardness characteristics and metal structure of the steel sheet as described above will be explained below.

[0039] [At the 0.5 mm position, the average hardness is 230HV0.1 or less, and the hardness variation is 30HV0.1 or less] At the 0.5 mm position, the average hardness is 230HV0.1 or less, and the hardness variation is 30HV0.1 or less. If a high hardness region exists at the extreme surface layer of the steel sheet, specifically at a position 0.5 mm from the surface of the steel sheet, stress corrosion cracking in a liquid ammonia environment is promoted. In addition, if a local high hardness region exists, stress concentration occurs when stress is applied to the steel sheet, and stress corrosion cracking is promoted. Therefore, in the steel sheet of the present invention, by adjusting the hardness characteristics by setting the average hardness to 230HV0.1 or less at the 0.5 mm position and setting the hardness variation to 30HV0.1 or less, excellent ammonia SCC resistance can be ensured. The lower limit of the average hardness at the 0.5 mm position is not particularly limited, but is preferably about 130HV0.1. Furthermore, the lower limit of the hardness variation at a 0.5 mm position may be 0HV0.1, but industrially it is about 10HV0.1. Here, the average hardness can be calculated by measuring the Vickers hardness at multiple points (e.g., 100 points) at 0.5 mm positions. The variation in hardness means the standard deviation of the Vickers hardness measured to obtain the average hardness.

[0040] [The maximum hardness in the plate thickness direction is located at a position 1.0 mm or more from the surface of the steel plate and up to 1 / 4 of the plate thickness] If the maximum hardness of the steel plate is present at a position some distance from the surface, the hardness of the surface layer alone can be reduced while maintaining the hardness of most of the steel plate, i.e., the strength of the steel plate can be maintained while ensuring excellent ammonia SCC resistance. Specifically, if the maximum value is located at a position less than 1.0 mm from the surface of the steel plate, the hardness at the position 0.5 mm cannot be sufficiently reduced. On the other hand, if the maximum value is located at a position more than 1 / 4 of the plate thickness from the surface of the steel plate, sufficient strength of the steel plate itself cannot be ensured. Therefore, in the steel plate of the present invention, the maximum value of the hardness in the plate thickness direction (Vickers hardness (HV1)) is specified to be located at a position from 1.0 mm to 1 / 4 of the plate thickness from the surface of the steel plate.

[0041] [Hardness variation through the plate thickness is 70HV1 or less] If the hardness variation in the plate thickness direction is large, not only does the uniform elongation of the steel plate decrease, but the residual stress caused by the internal stress introduced by accelerated cooling increases, which may cause a deterioration in ammonia SCC resistance. Therefore, in the present invention, the hardness variation in the plate thickness direction is specified to be 70HV1 or less. Here, the above-mentioned variation is calculated by measuring the Vickers hardness (HV1) at 0.5 mm pitches in the sheet thickness direction and finding the difference between the maximum and minimum values.

[0042] [Volume fraction of bainite at 0.5 mm position is 90% or more] In order to satisfy the strength characteristics and ammonia SCC resistance, the volume fraction of bainite at the 0.5 mm position must be 90% or more. When hard phases such as martensite and island martensite (MA) structures are formed in the surface layer, the surface hardness increases, the hardness variation within the steel plate increases, and the material uniformity is impaired. In other words, if the volume fraction of bainite is less than 90%, the volume fractions of other structures, i.e., ferrite, island martensite, martensite, pearlite, and austenite, increase, and sufficient strength and / or ammonia SCC resistance cannot be obtained.

[0043] Here, bainite includes a structure called bainitic ferrite or granular ferrite that transforms during or after accelerated cooling, which contributes to transformation strengthening, and also includes structures obtained by tempering these.

[0044] The remaining structure, which accounts for 10% or less by volume, may include a martensite structure in addition to a ferrite, pearlite structure, and austenite structure. The fraction of each structure in the remaining structure does not need to be particularly limited, but it is preferable that the remaining structure is a pearlite structure. The volume fractions of various metal structures can be measured by the methods described in the examples below.

[0045] (3) Manufacturing conditions In the manufacturing method of the present invention, a steel material having the same composition as that described above for the steel plate is heated and hot-rolled, then accelerated cooled, and then reheated. The reasons for limiting the manufacturing conditions for the steel plate are explained below. First, the manufacturing conditions of the steel material do not need to be particularly limited, but it is preferable to melt molten steel having the above-mentioned composition by a known melting method such as a converter, and form the steel material into a slab or the like of a predetermined size by a known casting method such as a continuous casting method. There is no problem in forming the steel material into a slab or the like of a predetermined size by the ingot casting-disassembly rolling method.

[0046] The steel material thus obtained is either directly hot rolled without cooling or reheated and then hot rolled. Hot rolling is performed with the rolling end temperature set to the Ar3 transformation point or higher, followed by accelerated cooling under specified conditions from a cooling start temperature above the Ar3 transformation point, and then reheating under specified conditions.

[0047] The heating temperature of the steel material is not particularly limited, but if the heating temperature is too low, the deformation resistance increases, which increases the load on the hot rolling machine and may make hot rolling difficult. On the other hand, if the heating temperature is higher than 1300°C, oxidation becomes significant, which increases the oxidation loss and increases the risk of a decrease in yield. For these reasons, the heating temperature is preferably 950°C or higher and 1300°C or lower.

[0048] (Hot Rolling) [Rolling end temperature: Ar3 transformation point or higher] In the present invention, after the steel material is heated to the above temperature, hot rolling is started and the steel material is rolled at or above the Ar3 transformation point. The hot rolling is then terminated. If the rolling end temperature is lower than the Ar3 transformation point, ferrite is generated and the material quality of the steel sheet surface layer deteriorates. The uniformity is hindered and the hardness variation increases, which leads to a deterioration in ammonia SCC resistance. In addition, the formed ferrite is affected by processing, which leads to a deterioration in toughness. Furthermore, the load on the hot rolling mill increases. Therefore, the rolling end temperature in the hot rolling in the present invention is set to be equal to or higher than the Ar3 transformation point. The rolling end temperature is more preferably Ar3 transformation point +10°C or higher. If the rolling end temperature exceeds 950°C, the structure may become coarse and the toughness may deteriorate. Therefore, the rolling end temperature is preferably 950°C or lower. Here, the Ar3 transformation point (°C) can be calculated using the following formula. Ar3(℃)=910-310×C-80×Mn-20×Cu-15×Cr-55×N i-80×Mo Here, each element indicates the content (mass%) of the element in the steel.

[0049] (accelerated cooling) [Cooling start temperature: above Ar3 transformation point] Next, the hot-rolled steel sheet is subjected to accelerated cooling from a cooling start temperature above the Ar3 transformation point. If the cooling start temperature is below the Ar3 transformation point, excessive ferrite will be generated and the cooling rate will be Since the degree of hardness becomes large, it coexists with martensite or bainite, which have large strength differences, resulting in insufficient strength and deterioration of toughness, and further deterioration of ammonia SCC resistance. Therefore, the cooling start temperature is set to the Ar3 transformation point or higher.

[0050] [Cooling rate at 1 / 4 of the plate thickness: 20~120℃ / s] Accelerated cooling, in which the cooling rate at the 1 / 4 position of the steel plate thickness is 20°C / s or more, is an essential process for obtaining a steel plate with high strength and high toughness, and cooling at a high cooling rate can increase the strength by transformation strengthening. Therefore, in order to obtain such an effect, the cooling rate at the 1 / 4 position of the plate thickness during accelerated cooling according to the present invention is specified to be 20°C / s or more. On the other hand, if the cooling rate exceeds 120°C / s, the volume fraction of martensite becomes too high, and the toughness decreases. Therefore, the cooling rate at the 1 / 4 position of the plate thickness of the steel plate is specified to be 120°C / s or less. The cooling rate can be increased by active cooling such as water cooling, and can be controlled by appropriately performing the cooling intermittently (providing a period during which the cooling is stopped). It is physically difficult to directly measure the temperature at the 1 / 4 position in the thickness direction of the steel plate. However, the temperature distribution in the thickness direction, particularly the temperature at the 1 / 4 position in the thickness direction, can be obtained in real time by performing a difference calculation using, for example, a process computer based on the surface temperature at the start of cooling measured by a radiation thermometer and the target surface temperature at the end of cooling.

[0051] [Cooling stop temperature: 200~600℃] In the present invention, after completion of hot rolling, a predetermined accelerated cooling is performed up to a cooling stop temperature set arbitrarily within the range of 200 to 600°C, whereby it is possible to obtain a predetermined volume fraction of ferrite and bainite in the center of the plate thickness, and it is possible to satisfactorily improve the strength and toughness. Here, if the cooling stop temperature is less than 200°C, the volume fraction of the island martensite structure becomes too high, resulting in a decrease in toughness. On the other hand, if the cooling stop temperature exceeds 600°C, ferrite and pearlite structures are excessively generated, resulting in insufficient strength and deterioration of toughness. Therefore, the cooling stop temperature is specified to be in the range of 200 to 600°C. The cooling stop temperature in the present invention is the temperature at the 1 / 4 position of the plate thickness of the steel plate.

[0052] (reheat) [Temperature reached at 0.5 mm from the surface is 400-680℃] In the present invention, it is necessary to reheat the steel plate after the accelerated cooling. When a thick steel plate is accelerated cooled, the cooling rate of the surface layer of the steel plate becomes faster, and the surface layer of the steel plate is cooled to a lower temperature than the inside of the steel plate. Therefore, the surface layer of the steel plate is likely to generate hard structures such as martensite, which may deteriorate the ammonia SCC resistance. Therefore, in the present invention, the surface layer of the steel plate is reheated after the accelerated cooling. This is because it is possible to reduce the hardness of the surface layer. Preferably, reheating is performed immediately after the accelerated cooling. Here, if the reheating temperature at a position 0.5 mm from the surface is less than 400°C, the reduction in hardness is insufficient, whereas if it exceeds 680°C, the strength of the entire steel plate decreases, making it difficult to obtain the specified strength. Therefore, the temperature to be reached at a position 0.5 mm from the surface during reheating after accelerated cooling is specified to be in the range of 400 to 680°C.

[0053] [Temperature reached at 1 / 4 of the steel plate thickness is 500°C or less] If the temperature reached at 1 / 4 of the plate thickness during reheating exceeds 500°C, a decrease in strength and toughness will occur. Therefore, the temperature reached at 1 / 4 of the plate thickness during reheating is specified to be 500°C or less.

[0054] As a means for reheating after accelerated cooling, it is preferable to use induction heating. In particular, it is preferable to use high-frequency induction heating so that heating is concentrated on the surface layer of the steel plate. In addition, after reheating, cooling can be performed appropriately. There are no particular limitations on the cooling after reheating, but in thick steel plates with a plate thickness of more than about 40 mm, the cooling rate becomes slow, and there is a concern that the toughness will deteriorate due to the aggregation and coarsening of carbides. In such cases, cooling with water or mist may be performed after the reheating treatment.

[0055] By manufacturing a steel material having the above-mentioned composition according to the above-mentioned manufacturing conditions, a steel plate having the composition, hardness characteristics, and metal structure according to the present invention can be obtained. The steel plate thus obtained has excellent strength characteristics and toughness, and is a steel plate with excellent ammonia SCC resistance. Here, excellent strength characteristics are: yield strength YS (yield point YP when there is a yield point, 0.2% proof stress σ0.2 when there is no yield point): 450 MPa or more, tensile strength (TS): 57 0MPa or more and uniform elongation (uEl): 10% or more. In addition, excellent toughness means J The vTrs according to IS Z 2241 is −30° C. or less. A steel plate having these properties is the steel plate of the present invention having excellent ammonia SCC resistance.

[0056] In the production method according to the present invention, any item not described in this specification can be carried out in a conventional manner. EXAMPLES

[0057] Steels (steel types A to AI, the remainder being Fe and unavoidable impurities) with the chemical compositions shown in Table 1 were formed into slabs by continuous casting, and hot rolling, accelerated cooling and reheating were successively carried out under the conditions shown in Table 2 to obtain thick steel plates (Nos. 1 to 50) with a plate thickness of 30 mm. For the obtained steel plates, the structure fraction of the metal structure at a position 0.5 mm from the steel plate surface in the plate thickness was measured, and evaluations of hardness characteristics, strength characteristics and toughness, and ammonia SCC resistance were carried out. The test methods are as follows. The results are also shown in Table 2.

[0058] [Metal structure fraction at 0.5 mm from the steel plate surface] A sample was taken from each steel plate so that the observation surface was located at a position 0.5 mm from the sample. The sample was then mirror-polished and further etched with nital, after which an image of a 10 mm x 10 mm area was taken at a magnification of 500 to 3000 times using a scanning electron microscope (SEM). The image was then analyzed using an image analyzer to determine the areal fraction of the microstructure (structural fraction of the metal structure). When the anisotropy of the microstructure is small, the areal fraction corresponds to the volume fraction, and therefore in the present invention, the areal fraction was regarded as the volume fraction.

[0059] In this embodiment, the fraction of the metal structure of the sample was determined as follows. That is, in the images taken as described above, polygonal ferrite was identified as ferrite, and the structure having elongated, lath-like ferrite and containing carbides with a circle equivalent diameter of 0.05 μm or more was identified as bainite (B in Table 2).

[0060] [Hardness characteristics] For the cross section perpendicular to the rolling direction of each steel sheet, the Vickers hardness (HV0.1) was measured at 100 points at 0.5 mm positions in accordance with JIS Z 2244, and the average value was calculated. The standard deviation of the 100 Vickers hardness values ​​was also calculated to represent the variation in hardness at 0.5 mm positions. Here, HV0.1 was used instead of HV10, which is usually used to measure the hardness of steel sheets, because measurement at HV0.1 makes the indentation smaller, making it possible to obtain hardness information at a position closer to the surface and hardness information that is more sensitive to the microstructure. In addition, the Vickers hardness (HV1) was measured in the thickness direction, and the position in the thickness direction (distance from the surface) where the maximum value was found was measured. Furthermore, the difference between the maximum and minimum values ​​of the Vickers hardness (HV1) in this measurement was calculated to represent the hardness variation in the thickness direction.

[0061] [Strength characteristics] A JIS Z 2201 No. 1B test piece was taken from the entire thickness of each steel plate so that the direction perpendicular to the rolling direction was the longitudinal direction of the test piece, and a tensile test was carried out in the manner described in JIS Z 2241. The yield strength YS (yield point YP if there is a yield point, 0.2% proof stress σ0.2 if there is no yield point), Tensile strength (TS) and uniform elongation (uEl) were measured. Those with a yield strength of 450 MPa or more, a tensile strength of 570 MPa or more, and a uniform elongation of 10% or more were deemed to have excellent strength properties. The steel plate was evaluated as having the above properties.

[0062] [Toughness] A V-notch test piece according to JIS Z 2202 was taken from a portion 1 mm removed from the surface side of each steel plate so that the rolling direction was the longitudinal direction of the test piece, and a Charpy impact test was carried out in accordance with JIS Z 2242 to measure vTrs (fracture transition temperature). Steel plates with a vTrs of -30°C or less were evaluated as having excellent toughness.

[0063] [Ammonia SCC resistance] The ammonia SCC resistance was evaluated by an accelerated test in which a four-point bending test was performed in a test solution and constant-potential anodic electrolysis was performed to accelerate corrosion. Specifically, the following steps were taken: Test pieces measuring 5 mm thick x 15 mm x 115 mm were taken from the surface of the steel plates, ultrasonically degreased in acetone for 5 minutes, and then subjected to a four-point bending test with a stress equal to the yield strength of each steel plate. The test cell in which the four-point bending test pieces were placed was filled with a solution of 12.5 g of ammonium carbamate and 1 L of liquid ammonia, and a voltage of +2.0 V vs Pt was applied to the test pieces using a potentiostat, and the pieces were immersed at room temperature (25°C). If no cracks were observed after 168 hours of immersion, the ammonia SCC resistance was judged to be "good", and if cracks were observed, the ammonia SCC resistance was judged to be "poor".

[0064] [Table 1]

[0065] [Table 2] TIFF0007601218000003.tif223124

[0066] As can be seen from Tables 1 and 2, all of the examples of the invention have a yield strength YS of 450 MPa or more, a tensile strength TS of 570 MPa or more, a uniform elongation uEl of 10% or more, and a vTrs of -30°C or less, and thus provide steel plates with excellent toughness and ammonia SCC resistance at low temperatures.

[0067] On the other hand, although the composition of Nos. 31 to 39 is within the range of the present invention, the manufacturing method is outside the range of the present invention, and therefore the desired metal structure and / or hardness characteristics are not obtained, resulting in inferior yield strength YS, tensile strength TS, low temperature toughness, or ammonia SCC resistance.

[0068] In addition, Nos. 40 to 50 have steel compositions outside the range of the present invention, and therefore are inferior in either yield strength YS, tensile strength TS, low temperature toughness, or ammonia SCC resistance. In the present invention, the steel composition may be considered as the steel plate composition as it is.

Claims

1. In mass percent, C: 0.017-0.162%, Si: 0.01-0.39%, Mn: 0.72 to 2.28%, Al: 0.010-0.048% N: 0.0023% or more and 0.0100% or less, P: 0.020% or less, S: 0.0100% or less; O: 0.0100% or less and the balance being Fe and unavoidable impurities, At a depth of 0.5 mm from the surface of the steel plate, the average hardness is 218 HV0.1 or less, the hardness variation is 24 HV0.1 or less, and the maximum hardness value in the plate thickness direction is at a position 1.0 mm or more and 1 / 4 of the plate thickness or less from the surface of the steel plate, and the hardness variation in the plate thickness direction is 70 HV1 or less; and A metal structure in which the volume fraction of a bainite structure at a position 0.5 mm deep from the surface of the steel plate is 90% or more. A steel plate having a yield strength YS of 450 MPa or more, a tensile strength TS of 570 MPa or more, a uniform elongation uEl of 10% or more, and a vTrs of -30°C or less.

2. The composition further comprises, in mass%, Cu: 0.01 to 0.50%, Ni: 0.01-2.00%, Cr: 0.01-1.00%, Sn: 0.01-0.50%, Sb: 0.01 to 0.50%, Mo: 0.01 to 0.50% and W: 0.01~1.00% The steel sheet according to claim 1, comprising one or more selected from the following:

3. The composition further comprises, in mass%, V: 0.01-1.00%, Co: 0.01 to 1.00%, B: 0.0001 to 0.0100%, Mg: 0.0005 to 0.0200% and REM: 0.0005-0.0200% The steel sheet according to claim 1 or 2, comprising one or more selected from the following:

4. In mass percent, C: 0.017-0.162%, Si: 0.01-0.39%, Mn: 0.72 to 2.28%, Al: 0.010-0.048% N: 0.0023% or more and 0.0100% or less, P: 0.020% or less, S: 0.0100% or less; O: 0.0100% or less The steel material has a composition containing Fe and unavoidable impurities, and the rolling end temperature is Ar ３ The transformation point is reached and the hot rolling is performed. ３ A method for producing a steel sheet, comprising: performing accelerated cooling from a cooling start temperature equal to or higher than a transformation point, and then performing reheating; In the accelerated cooling, the cooling stop temperature is in the range of 200 to 600 ° C., and the cooling rate at the 1 / 4 position of the plate thickness of the steel plate is in the range of 20 to 120 ° C. / s, The reheating is performed with an attained temperature of 500°C or less at a position 1 / 4 of the plate thickness of the steel plate, until the attained temperature at a position 0.5 mm deep from the surface of the steel plate is in the range of 400 to 680°C; the method for producing a steel plate having hardness characteristics in which, at a position 0.5 mm deep from the surface of the steel plate, the average hardness is 218 HV0.1 or less and the hardness variation is 24 HV0.1 or less, and the maximum hardness in the plate thickness direction is at a position 1.0 mm or more and 1 / 4 of the plate thickness from the surface of the steel plate, and the hardness variation in the plate thickness direction is 70 HV1 or less; and the steel plate has a metal structure in which the volume fraction of bainite structure at a position 0.5 mm deep from the surface of the steel plate is 90% or more. The method for producing a steel plate having a yield strength YS of 450 MPa or more, a tensile strength TS of 570 MPa or more, a uniform elongation uEl of 10% or more, and a vTrs of -30°C or less.

5. The composition of the steel material further comprises, in mass%, Cu: 0.01 to 0.50%, Ni: 0.01-2.00%, Cr: 0.01-1.00%, Sn: 0.01-0.50%, Sb: 0.01 to 0.50%, Mo: 0.01 to 0.50% and W: 0.01~1.00% The method for producing a steel sheet according to claim 4, further comprising the step of:

6. The composition of the steel material further comprises, in mass%, V: 0.01-1.00%, Co: 0.01 to 1.00%, B: 0.0001 to 0.0100%, Mg: 0.0005 to 0.0200% and REM: 0.0005-0.0200% The method for producing a steel sheet according to claim 4 or claim 5, further comprising: