Polyester transport carpet and method for manufacturing polyester transport carpet

Abstract

The present invention relates to a flame-retardant carpet suitable for the interiors of vehicles, preferably aircraft, comprising a machine-woven or mechanically woven carpet consisting of warp and weft yarns, a needled felt, and an intermediate layer between the needled felt and the machine-woven or mechanically woven fabric, wherein some of the warp yarns on the back side of the machine-woven or mechanically woven fabric are at least partially fused to each other. The present invention also relates to a method for manufacturing the flame-retardant carpet suitable for the interiors of vehicles, particularly aircraft.

Description

[Technical field]

[0001] FIELD OF THEINVENTION The present invention relates to a flame retardant carpet suitable for use in the interiors of vehicles, preferably aircraft.

[0002] In a second aspect, the present invention also relates to a method for producing a flame retardant carpet suitable for the interior of a vehicle, preferably an aircraft. [Background technology]

[0003] Carpets are part of the normal equipment of the interior of aircraft, but also of any other means of transport, such as trains or ships. In addition to the floors, some of the interior walls of aircraft are often carpeted as well. Very strict requirements are imposed on carpets in aircraft. In particular, they must be flame-retardant and the amount of toxic gases and vapours released in case of fire must not exceed strict requirements. Corresponding standards are generally required by law. In particular for passenger aircraft, carpets may only be used that meet standards such as ABD 0031 for the release of toxic gases and vapours, FAR 25.853 for flammability and ISO 6356 for the static electricity tendency of textile and laminate floor coverings.

[0004] In addition to these strict standards, airlines expect in-flight carpets to be wear- and scratch-resistant. Every day, many passengers walk on the carpets or roll them over with trolleys. That's the kind of strain the carpets have to withstand. For that reason, in-flight mats are replaced regularly.

[0005] Also, to reduce fuel consumption, light weight per unit area is required. An aircraft has many square meters of carpet. Reducing the weight per unit area of ​​carpeting can lead to huge savings for airlines every year.

[0006] Such an invention is known, inter alia, from WO 2007 / 112608, in which a flame-retardant carpet for aircraft interiors is described. The carpet consists of a woven top layer, a needle felt as a bottom layer and an intermediate layer for laminating the two layers together. The carpet is light in weight per unit area and can be quickly installed in the aircraft using Velcro® strips.

[0007] Also known is the invention of WO 2015 / 014335, which relates to a textile floor covering, in particular for use in the interior of aircraft. The carpet consists of a top layer, which may be a pile fabric, a smooth fabric or a tufted carpet, a needle felt as a bottom layer and an intermediate layer for laminating the two layers together. Under the needle felt is applied an acrylic latex. This acrylic latex layer prevents the carpet from slipping and allows it to be installed on the aircraft without the use of Velcro, adhesives or double-sided tape etc.

[0008] JP 2000-308604 A describes a base fabric for dust control carpets.

[0009] Japanese Patent Application Laid-Open No. 2000-282347 describes a pile carpet.

[0010] JP 2005-152159 A describes a woven carpet.

[0011] WO 2005 / 113229 describes a hybrid of vinyl flooring and soft padded carpet.

[0012] EP 3 192 906 describes fray-resistant carpets using soluble yarns.

[0013] WO 2012 / 076348 describes a method for producing a textile product and the resulting textile product.

[0014] EP 3 196 344 describes fray-resistant carpets made with natural yarns.

[0015] WO 2007 / 112608 has the disadvantage that the top layer is a lightweight fabric. As a result, the fabric itself is not sufficiently resistant to the daily passenger and trolley loads and does not have sufficient dimensional stability. The fabric is reinforced by applying a polyacrylate adhesive as an intermediate layer between the fabric and the needle felt. The adhesive not only laminates the fabric and the needle felt, but also keeps the connection of the stretched warp and weft threads together. Therefore, some of the adhesive needs to be mixed with the warp and weft threads. The intermediate layer increases the weight of the carpet. It also makes it difficult to recycle the carpet, since the fabric threads and the needle felt can hardly be separated from the intermediate layer. This is a major drawback in view of the frequent replacement of aircraft carpets. WO 2015 / 014335 has similar drawbacks. When using tufted carpets or pile fabrics, the top layer itself is stronger and more dimensionally stable, but both are heavier than smooth fabrics, which can be a disadvantage. Tufted carpets or pile fabrics also have the drawback of being less suitable for rolling on a trolley and more prone to wear. When using smooth fabrics, it is again necessary to increase the connections of the warp and weft threads together. In WO 2015 / 014335, the top layer and the needle felt are bonded together by fusion lamination, which at the same time keeps the warp and weft threads together. This again leads to an increase in weight, which makes it difficult to recycle the top layer and the needle felt.

[0016] The present invention aims to provide a solution to these drawbacks. Summary of the Invention

[0017] In a first aspect, the invention relates to a solution according to claim 1.

[0018] The advantage of such carpets is that some of the warp threads on the back side of the machine-woven or mechanically woven fabric are at least partially fused together. The fabric itself therefore already has a considerable strength and good dimensional stability. It does not easily break under the load of passengers and trolleys. The warp and weft threads also have a limited freedom of movement relative to each other, which makes them more abrasion-resistant.

[0019] Since the fabric is already reinforced by fusion bonding, there is no need to use a heavy intermediate layer to reinforce the fabric and laminate the fabric to the needle felt. A lighter intermediate layer can be used to laminate only the fabric and the needle felt. This reduces the weight per unit area of ​​the carpet. Since the adhesive does not need to be partially mixed with the warp and weft yarns, it becomes easier to separate the fabric and the needle felt for recycling.

[0020] In addition, the present invention uses 100% thermoplastic flame-retardant polyester (PES) for both the fabric and needle felt. As a result, the carpet meets the requirements of ABD 0031 for toxic gas and vapor emissions and FAR 25.853 for flammability. Another advantage is that the fabric and needle felt can be recycled at the same time because only flame-retardant polyester (PES) is used.

[0021] Preferred embodiments of the solution are set out in claims 2 to 9.

[0022] In a specific embodiment, the present invention relates to a solution according to claim 7. In the intermediate layer, PES is also used as an adhesive for laminating the fabric and the needle felt. This further improves recycling. Now it is not even necessary to separate the fabric and the needle felt. The intermediate layer can even be processed and recycled together with the fabric and the needle felt.

[0023] In a second aspect, the invention relates to a method according to claim 10. The method has the advantage in particular that a sufficiently strong and dimensionally stable fabric can be obtained, since before laminating the fabric and the needle felt, the fabric is guided along a heated surface and some of the warp threads on the back side of the interlocking machine-woven or mechanically woven fabric are at least partially melted. The fabric can be laminated to the needle felt with a light intermediate layer, and the fabric and the needle felt can be easily separated for subsequent recycling.

[0024] Preferred embodiments of the solution are set out in the dependent claims 11 to 13.

[0025] In a third aspect, the present invention relates to a method for producing a carpet according to the first aspect using a method according to the second aspect. [Brief description of the drawings]

[0026] [Figure 1] FIG. 1 is a cross-sectional view of one embodiment of the present invention. [Diagram 2] FIG. 2 is a schematic diagram illustrating a molecular model of the bond between a fabric and a needle felt according to one embodiment of the present invention. [Diagram 3] FIG. 3 shows an apparatus suitable for at least partially fusing some of the warp threads together according to one embodiment of the method of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0027] Unless otherwise specified, all terms used in the description of the present invention, including technical and scientific terms, are used in the sense commonly understood by those skilled in the art of the present invention. To facilitate better understanding of the description of the present invention, the following terms are explicitly explained.

[0028] "A," "one," and "the" refer to both the singular and the plural, unless the context clearly indicates otherwise. "A segment," for example, means one or more segments.

[0029] When "about" or "approximately" is used herein, a measurable quantity, parameter, time or moment, etc., means a variation of the cited value of ±20% or less, preferably ±10% or less, more preferably ±5% or less, even more preferably ±1% or less, and even more preferably ±0.1% or less, insofar as such variation applies to the above-mentioned invention, provided that the value of the quantity for which the term "about" or "approximately" is used must itself be specifically expressed.

[0030] The terms "comprise," "contain," "include," "composed of," "provided for," "comprising," "containing," and "including" are synonymous and are inclusive or open-ended terms indicating the presence of the preceding language and do not exclude or preclude other components, features, elements, materials, or phases known or described in the prior art.

[0031] Citations of numerical intervals by endpoints include all integer, fractional and / or real numbers between those endpoints, inclusive.

[0032] The term "thermoplastic" refers to a polymeric material that can be bent, kneaded, or liquefied above a certain temperature and that substantially hardens after cooling. Examples of thermoplastic polymers include, but are not limited to, vinyl-containing thermoplastics such as polyvinyl chloride, polyvinyl acetate, polyvinyl alcohol, other vinyl and vinylidene resins, and copolymers thereof; polyethylene compounds such as low density polyethylene, high density polyethylene, and copolymers thereof; styrenic compounds such as ABS, SAN, polystyrene, and copolymers thereof, polypropylene, and copolymers thereof; saturated and unsaturated polyesters; acrylics; polyamides; engineering plastics such as acetyls, polycarbonates, polyimides, polysulfones, polyphenylene oxides, sulfurized resins, and other resins.

[0033] The term "float" refers to the portion of the yarn that appears on the surface of the fabric. Floats may be top floats and / or bottom floats. The term "top float" refers to the portion of the yarn that appears on the top of the fabric. Top floats are formed in a warp:weft bond pattern with a bond density of 2:1, 3:1, 4:1, 5:1, 6:1, 7:1, 8:1, 9:1, 10:1 or more. This means that each weft yarn floats above at least two warp yarns, above at least three warp yarns, etc. Alternatively, each warp yarn floats above at least two weft yarns, above at least three weft yarns, etc. The term "bottom float" refers to the portion of the yarn that appears on the bottom of the fabric. Bottom floats are formed in a warp:weft bond pattern with a bond density of 1:2, 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9, 1:10 or less. This means that each weft yarn floats below at least two warp yarns, below at least three warp yarns, etc. Alternatively, each warp thread floats under at least two weft threads, under at least three weft threads, etc. The term "bonding" is used to refer to the weaving of weft threads with warp threads to form a fabric.

[0034] The term "weft float" refers to a float formed by the weft yarns. The term "warp float" refers to a float formed by the warp yarns.

[0035] Yarn count is the thickness of the yarn. It is measured as a ratio between the weight and length of a single yarn. Weight measurements give the weight of a certain length of yarn. Length measurements give the length of a certain weight of yarn. An example of a weight measurement is tex, where tex is the weight in grams of 1000m of yarn. Dtx is more frequently used, which is the weight in grams of 10,000m of yarn. Another example of a weight measurement is denier, which is written as den, which is the weight in grams of 9000m of yarn. For yarns made of filaments, the weight measurement denier is also used for the filaments. Last per filament or DPF means the weight number of one filament in the yarn.

[0036] In a first aspect, the present invention relates to a flame retardant carpet suitable for use inside vehicles, particularly aircraft.

[0037] According to one embodiment, the solution has a front side and a back side as the use surface, and essentially comprises 100% thermoplastic flame retardant polyester (PES) warp and weft yarns, and has a maximum weight of 650 g / m 2 and consisting essentially of 100% thermoplastic flame-retardant polyester (PES) up to 220 g / m 2 between needle felt and machine-woven or mechanically woven fabrics of a weight of up to 180 g / m 2 and an intermediate layer of about 100% by weight, wherein some of the warp yarns on the back side of the machine woven or mechanically woven fabric are at least partially fused together.

[0038] The fabric is made up of a top side and a bottom side: the top side is the surface on which passengers walk and roll their trolleys and luggage, and which becomes the visible portion of the carpet once installed.

[0039] Fabrics have the advantage over tufted carpets in that they do not require a base, such as a fabric or needle felt, through which the pile yarns can be threaded. Because there is no base, fabrics can be lighter than tufted carpets. Tufted mats also tend to have long pile, which makes them difficult to roll on dollies and suitcases. Furthermore, such long pile mats wear out more quickly.

[0040] The fabric should preferably be smooth. Pile fabrics have the same disadvantages as long pile tufted carpets when used in dollies and suitcases. They wear out faster. A second disadvantage of pile fabrics is that in addition to the pile yarns used to form the pile, additional yarns are also included in the warp to bind the pile. As a result, the fabric is heavier compared to smooth fabrics.

[0041] The fabric preferably has a smooth bond. In a smooth bond, each weft thread runs alternately over and under the warp thread, and each warp thread runs alternately over and under the weft thread. This is the simplest and strongest bond possible. Heavy daily loads from passengers and trolleys can pull the warp and weft threads apart, reducing dimensional stability. To counter this, a strong bond is advantageous. A strong bond also means that the warp and weft threads are less likely to move relative to each other under the loads of passengers and trolleys, resulting in less friction between the threads and less wear. This does not affect wear on the wires due to friction with, for example, passenger shoes and trolley wheels.

[0042] In another embodiment, the bond in the fabric is the weft. Each weft runs alternately over and under two juxtaposed warp threads, and each warp runs alternately over and under the weft. This creates a different visual effect than a smooth bond. This is still a strong bond, since the weft only runs over or under two juxtaposed warp threads in the weft loop.

[0043] The fabric preferably has a limited number of floats, both top and bottom. The floats can be used in combination with different colored threads to weave patterns, emblems, or indicia into the fabric. The drawback of using floats is that they introduce deviations from smooth bonding, which weakens the bonds of the fabric locally. The floats preferably have a bond density of 7:1 or less and 1:7 or more, more preferably 5:1 or less and 1:5 or more, and even more preferably 2:1 or less and 1:2 or more.

[0044] In one embodiment, the fabric is a jacquard weave. A jacquard weave consists of intricate patterns and / or emblems that cannot be woven using a frame on a loom. A framed weave means that all the warp threads threaded through a frame are either all to one side or all to the opposite side of the weft threads in the fabric. A jacquard weave is woven using a jacquard loom. In a jacquard, each individual warp thread can be on one side or the opposite side of the weft thread, independent of the position of the other warp threads.

[0045] The fabric is made of warp and weft yarns of virtually 100% thermoplastic flame retardant polyester (PES). PES is very strong, stiff, dimensionally stable and has low creep, making it suitable for use under heavy loads. The yarn is not attacked by mould and bacteria, which is an advantage as liquids and food can be spilled on aircraft, which can lead to the growth of mould and bacteria. PES does not absorb liquids very well. It resists acids, oxidising agents and dilute alkaline detergents well. It can also be sterilised by steam. These properties make the fabric suitable for efficient and rapid cleaning, which is also an advantage for carpets on aircraft.

[0046] Flame retardant PES has excellent heat resistance. Flame retardant PES is less likely to burn and can extinguish flames, so it produces less smoke. These properties allow it to comply with ABD 0031 for the production of toxic gases and vapors and FAR 25.853 for flammability.

[0047] The carpet also includes a needle felt of substantially 100% thermoplastic flame retardant polyester (PES). The needle felt therefore meets the ABD 0031 standard for toxic gas and vapor emissions and the FAR 25.853 standard for flammability. The needle felt is a type of nonwoven fabric. The needle felt has a thickness of 0.5 mm to 4 mm, preferably 0.5 mm to 3 mm, more preferably 0.5 mm to 2 mm, and even more preferably 0.5 mm to 1 mm.

[0048] The needle felt is attached to the back side of the fabric with the help of an intermediate layer. The needle felt is suitable for mechanically reinforcing the fabric. It is suitable for providing stiffness to the sharp corners of the carpet, giving the carpet high dimensional stability, increasing the walking comfort on the carpet, improving sound insulation and thus improving the acoustics inside the aircraft.

[0049] Because the needlefelt is a non-woven fabric, the carpet is suitable for rapid installation and replacement within the aircraft. The carpet is secured to the aircraft floor with Velcro strips. The Velcro strips are glued to the aircraft floor. The carpet is secured by hooking the hooks of the Velcro strips onto the threads of the needlefelt. The carpet can be easily removed by peeling it off the Velcro strips. The Velcro strips are reusable and remain attached to the aircraft floor. The new carpet according to the invention can be easily installed by attaching the new carpet to the existing Velcro strips so that the new carpet is secured in place.

[0050] The Velcro tape is made of flame retardant material and meets the FAR 25.853 (a)(1)(ii) standard for flammability. A non-limiting example of a suitable material is polyamide PA6. The weight is preferably 0.60 kg / m 2 less than 0.55 kg / m 2 less than 0.45 kg / m 2The Velcro strip includes a hook on one side of the strip, configured to hook a thread, and an adhesive on the opposite side. The adhesive has an adhesive strength of at least 10.0 N / cm to aluminum, preferably at least 12.0 N / cm to aluminum, and more preferably at least 13.0 N / cm to aluminum. The force required to peel the carpet from the hook of the Velcro tape is at least 0.60 N / cm, preferably at least 0.70 N / cm, and more preferably at least 0.80 N / cm. The shear strength of the Velcro tape is at least 20 N / cm. 2 , preferably at least 25N / cm 2 , more preferably at least 29 N / cm 2 The loop tension is at least 5N / cm 2 , preferably at least 7N / cm 2 , more preferably at least 8 N / cm 2 A non-limiting example of a suitable Velcro tape is HTH 577 from Velcro Corporation.

[0051] Fabrics up to 650 g / m 2 Needle felt has a weight of up to 220 g / m 2 The weight of the intermediate layer is up to 180 g / m 2 Therefore, the total weight of the carpet is up to 1050 g / m 2 A standard carpet has a weight of 2000g / m 2 , and even 3000g / m 2 For this reason, the carpet according to the invention is particularly suitable for aircraft applications where reduced weight translates into reduced fuel consumption.

[0052] Some of the warp threads of a machine-woven or mechanically woven fabric are at least partially fused together on the back side. It is desirable that the warp threads are fused over at least 10% of the length of the juxtaposed warp threads, more preferably at least 20% of their length, even more preferably at least 30% of their length, and even more preferably at least 50% of their length. Because some of the warp threads are fused together, they can move relative to each other to a limited extent. This increases dimensional stability, reduces friction between the threads, and reduces wear. This strengthens the fabric and the carpet. In the case of carpets according to the current state of the art, the fabric is reinforced by using a layer of adhesive or fusion coating that adheres to the knots of the fabric. Since the adhesive or fusion coating must then penetrate between the threads of the fabric, more adhesive or fusion coating is required than simply attaching the fabric to the needle felt. Therefore, in the case of the carpet according to the invention, there is a further weight reduction compared to the state of the art. An additional advantage is that it is easier to recycle the yarns and needle felt of the fabric, since no adhesive or fusion coating needs to penetrate between the yarns.

[0053] According to one embodiment, the yarn count of the warp and weft threads is between 1100 dtex and 4400 dtex.

[0054] A higher thread count means a heavier and thicker thread. A higher thread count indicates a heavy and durable fabric with good dimensional stability. A lower thread count indicates a light and soft fabric. A transportation carpet is desired to be light and durable in shape to withstand the daily loads of passengers and trolleys. A thread count of 1100 dtex to 4400 dtex, preferably 1500 dtex to 3700 dtex, more preferably 1800 dtex to 3100 dtex is suitable for transportation carpet. The belt then has sufficient lightness and strength.

[0055] The weft and warp yarns are made of filaments. To obtain a lightweight fabric, lightweight filaments are required. The filaments have a weight number of 2 DPF to 20 DPF, preferably 2 DPF to 15 DPF, more preferably 2 DPF to 10 DPF, and even more preferably 2 DPF to 5 DPF.

[0056] In another embodiment, a stronger fabric is required to obtain sufficient dimensional stability. In this case, slightly stronger filaments are required. The filaments have a weight number of 2 DPF to 20 DPF, preferably 5 DPF to 20 DPF, more preferably 8 DPF to 20 DPF, and even more preferably 10 DPF to 20 DPF.

[0057] According to one embodiment, the weft and warp threads are so-called continuous filament threads, the threads being made of continuous filaments.

[0058] According to one embodiment, the weft and warp yarns are so-called continuous filament yarns, the yarns being made of continuous filaments, the texture of the yarns being modified by air injection to form small loops in them, which provides additional insulation and strength.

[0059] In one embodiment, the number of warp threads per cm of fabric is between 8 and 30.

[0060] The number of warp threads per cm of fabric also determines the density of the fabric. A denser fabric is stronger and more dimensionally stable, but heavier. Fewer warp threads per cm of fabric results in a lighter and softer fabric, but weaker and less dimensionally stable. The number of warp threads per cm of fabric is between 8 and 30, preferably between 13 and 25, and more preferably between 15 and 20. This ensures that the carpet is sufficiently light and strong.

[0061] In one embodiment, the number of weft threads per cm of fabric is between 3 and 10.

[0062] The number of weft threads per cm of fabric also determines the density of the fabric. A denser fabric is stronger and more dimensionally stable, but heavier. Fewer weft threads per cm of fabric makes the fabric lighter and softer, but weaker and less dimensionally stable. The number of weft threads per cm of fabric is 3 to 10, preferably 3 to 8, more preferably 3 to 7. The carpet is then sufficiently light and strong.

[0063] In one embodiment, the weight per unit area of ​​the carpet is up to 950 g / m 2 It is.

[0064] The weight of a carpet is determined by the weight of the fabric, the interlayer and the needle felt. The weight of a carpet can be optimized by a careful selection of the fabric, the interlayer and the needle felt. Heavier fabrics are inherently stronger and require a thinner needle felt to improve dimensional stability. Since some of the warp threads in mechanically woven fabrics are at least partially fused together on the backside, the interlayer is minimal. The interlayer is the interface between the fabric and the needle felt. Lighter fabrics require a slightly thicker needle felt to improve dimensional stability. The interlayer can always be minimal. With a good choice of fabric thickness, determined by the yarn count, the number of warps per cm of fabric and the number of wefts per cm of fabric, and with appropriate needle felt, the carpet weight can be increased up to 950 g / cm. 2 , preferably up to 925g / cm 2 , more preferably up to 900 g / cm 2 , and even more preferably 875 g / cm 2 It is.

[0065] In one embodiment, the machine-woven or mechanically woven fabric and the needle felt are laminated together with the aid of an intermediate layer.

[0066] The machine-woven or mechanically woven fabric and the needle felt are bonded together. The needle felt provides dimensional stability and strengthens the fabric as it adheres to the fabric. The fabric and the needle felt are laminated together with the help of an intermediate layer.

[0067] In one embodiment, the intermediate layer comprises a PES adhesive.

[0068] The use of PES as an adhesive allows transportation carpets to be easily recycled. The fabric, needle felt and interlayer adhesive all contain PES, so the entire carpet can be recycled together. There is no need to separate the fabric and needle felt. The PES adhesive can be, for example, a PES fusing adhesive film, PES fusing powder or other suitable means.

[0069] In one embodiment, the carpet includes reactive molecules for forming thermally reversible covalent interactions between the layers.

[0070] In this way, the covalent interactions can be reversed by heating the carpet, which contributes to easy recycling of the carpet. By reversing the reaction between the reactive molecules, the original bond structure of the interlayer that binds the fabric and the needle felt is broken down into smaller molecules. These small molecules can be removed from the fabric and needle felt more easily than with conventional adhesives or fusion coatings. For example, it is possible to dissolve the remaining small molecules in a weak solvent and recover these molecules from the solvent. Another possibility is to recycle the molecules together with the fabric and / or needle felt, for example by mixing them with the filament yarns of the fabric and / or needle felt.

[0071] Thermoreversible covalent bonding reactions are already known in chemistry, including, but not limited to, the Michael reaction, the nitroso dimerization reaction, the cyclic anhydride reaction leading to ester compounds, the urethane formation reaction, the aliphatic ion formation reaction, and the phenol-azlactone adduct formation reaction.

[0072] According to another embodiment, the reaction is between a first molecule consisting of a conjugated diene group and a second molecule consisting of a dienophile group. Such a reaction between a conjugated diene group and a dienophile group is called the Diels-Alder reaction. The advantage of the Diels-Alder reaction is that it is thermoreversible at a relatively low temperature. This prevents physical and chemical damage to the fabric and needle felt.

[0073] A conjugated diene is an acyclic hydrogen with a molecular structure that contains two hydrogen-hydrogen dimers separated by one single compound. A conjugated diene group may be part of a molecule that consists of atoms other than carbon and hydrogen. A dienophile is an alkene component (a dimer of carbon) from the reaction of an alkene with a diene. A dienophile group may be part of a molecule that contains atoms other than carbon and hydrogen.

[0074] According to another embodiment, the diene group is furan (such as furfuryl), anthracene, thiophene, or pyrrole. The dienophile group is maleimide, fumarate, maleate, or alkylene. These groups are suitable for use in the present invention. Obviously, this embodiment does not exclude the use of other diene groups and / or dienophile groups.

[0075] In one embodiment, some of the weft yarns on the back side of a machine-woven or mechanically woven fabric are at least partially merged with some of the warp yarns.

[0076] Since some of the weft threads are integrated with the warp threads, the weft threads and the warp threads can move relative to each other to a limited extent. Some nodes of the weft threads and the warp threads are therefore fixed. This increases dimensional stability, reduces friction between the threads and reduces wear. This strengthens the fabric and the carpet. In the case of carpets according to the current state of the art, the fabric is reinforced by using a layer of adhesive or fusion coating that adheres to the knots of the fabric. Since the adhesive or fusion coating must then penetrate between the threads of the fabric, more adhesive or fusion coating is required than simply attaching the fabric to the needle felt. In the case of the carpet according to the invention, there is therefore a further weight reduction compared to the current state of the art. A further advantage is that it is easier to recycle the fabric threads and the needle felt, since the adhesive or fusion coating does not have to penetrate between the threads.

[0077] In a second aspect, the present invention relates to a method for producing a flame retardant carpet suitable for the interiors of vehicles, particularly aircraft.

[0078] According to one embodiment, the method comprises the steps of machine weaving a fabric comprising a front side and a back side as the use surface, the front side and back side being made of substantially 100% thermoplastic flame retardant polyester (PES) warp and weft yarns, making a needle felt of substantially 100% thermoplastic flame retardant polyester (PES), and laminating the needle felt to the fabric with the help of an intermediate layer, the method comprising the additional step of leading the back side of the fabric along a heated surface prior to lamination to at least partially melt a portion of the warp yarns of the back side of the machine-woven or mechanically woven fabric.

[0079] The fabric preferably has a maximum weight of 650 g / m 2 The maximum weight of needle felt is 220 g / m 2 The middle layer has a maximum weight of 180 g / m 2 It is.

[0080] Machine weaving or mechanical weaving of textile fabrics using looms is known in the art.

[0081] Forming needle felt from filaments is known in the art. This can be done in two ways: continuous and discontinuous. In the continuous method, the filaments are formed directly in an uninterrupted process by extrusion from the granules to form the needle felt, and the filaments are bonded to the needle felt. In the discontinuous method, the filament yarn is fed from a spool to a needle felting machine, where it is opened and formed into a needle felt of the desired shape, and then tied. Preferably, a mechanical method is used to bond the filaments to the needle felt, for example, by needling the needle felt with a barbed needle. Needling intermixes the filaments, but also leaves many loose filament ends or loops that can get caught by hooks of a Velcro tape when applied to the floor of an aircraft. Chemical reinforcement of needle felt is less preferred as it can affect the recycling of the needle felt. Heat reinforcement of needle felt can reduce the number of loops or loose filament ends that can get caught by hooks of a Velcro tape.

[0082] The needle felt is laminated to the fabric. In the lamination step, the back side of the fabric is guided through a heated surface, which at least partially melts some of the warp threads together. The fabric is guided through a series of support rollers. Between two support rollers there is a heated surface. The heated surface is pressed against the back side of the fabric. The heated surface is preferably adjustable so that it can press more or less against the back side of the fabric. Back side here refers to one side of the fabric, not the position of the heated surface relative to the fabric. The heated surface can be located horizontally or vertically, above, below, left or right, in front of or below the fabric. It will be clear to a person skilled in the art how the arrangement of the support rollers and the orientation of the fabric must be adapted so that the heated surface presses against the back side of the fabric.

[0083] In one embodiment, the heated surface is a hot plate, a hot roller, a tipped metal sheet, another suitable surface, or a combination of the above.

[0084] The fabric is led on its back side through the heated surface so that some of the warp threads at least partially melt together. The degree of melting of the warp threads can be varied by pressing the heated surface more or less against the warp threads. Other influencing parameters are the temperature of the heated surface and the speed at which the fabric is led through the heated body.

[0085] The fabric can be directed through one, two, three, or more heated elements depending on the desired degree to which some of the warp yarns are fused.

[0086] In one embodiment, an additional support roller can be placed on the other side of the fabric, facing the heated element, to support the fabric while the heated element presses against the backside of the fabric. The use of a support roller facing the heated element allows the heated surface to be pressed harder against the fabric without tearing the fabric.

[0087] In one embodiment, the laminate comprises using PES as the adhesive in the interlayer.

[0088] In one embodiment, a PES melt adhesive film is used during lamination. The fabric is unwound from a first roll, the PES fusion self-adhesive film from a second roll, and the needle felt from a third roll. The fabric, the self-adhesive film, and the needle felt are bonded together so that the self-adhesive film is in contact with the backsides of the fabric and the needle felt. The whole is heated to make the PES melt adhesive film sticky and is sandwiched between two rollers. After cooling, the fabric and the needle felt are bonded together with the self-adhesive film. The self-adhesive film forms an intermediate layer.

[0089] In one embodiment, PES molten powder is used during lamination. The fabric is unwound from a first roll and the needle felt from a second roll. The PES molten powder is dispensed by a suitable dispenser either on the back side of the fabric or on one side of the needle felt, or across the back side of the fabric and one side of the needle felt. The fabric and needle felt are joined together so that the back side of the fabric faces the needle felt and the PES molten powder is between the fabric and the needle felt. This is heated to make the PES molten powder sticky and pressed between two rollers. After cooling, the fabric and needle felt are joined together with the PES molten powder. The PES molten powder forms the intermediate layer.

[0090] In one embodiment, lamination comprises using reactive molecules to form thermally reversible covalent interactions in the interlayer.

[0091] According to one embodiment, a composition comprising reactive molecule A is applied to the backside of the fabric. A composition consisting of reactive molecule B is applied to the face of the needled felt. The fabric and needled felt are assembled such that the backside of the fabric and the face of the needled felt having the composition thereon are in contact with each other, and molecules A and B react, resulting in the formation of a thermally reversible covalent interaction. A thin interlayer is formed that connects the fabric and the needled felt.

[0092] According to another embodiment, a composition comprising reactive molecule B is applied to the back side of the fabric. One side of the needle felt is also applied with a composition comprising reactive molecule B. The fabric and needle felt are assembled and the back side of the fabric and the side of the needle felt with the composition thereon are oriented relative to each other. A thin intermediate layer of reactive molecule A is applied between the fabric and the needle felt. The situation is such that molecule A reacts with molecule B, resulting in the formation of a thermo-reversible covalent interaction. The thin intermediate layer connects the fabric and the needle felt.

[0093] In one embodiment, the method includes the further step prior to lamination of directing the backside of the machine-woven or mechanically woven fabric along a heated surface to melt at least part of the weft yarns on the backside of the fabric, or part of the warp yarns.

[0094] By increasing the temperature of at least one heated surface, or as a result of the speed at which the fabric is guided along the heated surface, or as a result of the pressure with which the heated surface is pressed against the backside of the fabric, it is possible to at least partially melt some of the warp threads, as well as at least partially melt some of the weft threads to the warp threads, which makes it less likely that the weft and warp threads will move relative to one another, improving dimensional stability, reducing mutual friction and therefore wear, and providing a stronger fabric.

[0095] In a third aspect, the present invention relates to the manufacture of a carpet according to the first aspect using a method according to the second aspect.

[0096] It will be apparent to those skilled in the art that the carpets of the present invention are suitable not only for use in aircraft, but also for use in other modes of transportation such as trains and ships, where light weight, high wear resistance, and little fire resistance are required.

[0097] The invention will now be explained in more detail with reference to non-limiting examples or figures.

[0098] (Figure description) FIG. 1 shows a cross section of one embodiment of the present invention.

[0099] The polyester transport carpet comprises a needled felt 1 laminated to a smooth fabric 6 by an intermediate layer 2. The intermediate layer 2 is made of a PES adhesive or reactive molecules that form a thermo-reversible covalent interaction. The smooth fabric 6 is composed of a first warp thread group 3 and a second warp thread group 4. The warp threads 3 and 4 are arranged in a juxtaposed fashion in the longitudinal direction of the fabric. The smooth fabric 6 comprises a weft thread 5. The weft thread 5 is transverse to the direction of the warp threads 3 and 4. The first weft thread 5 is below the warp thread 3 and above the warp thread 4. The next weft thread 5 is above the warp thread 3 and below the warp thread 4, thus building up the fabric. The resulting bond is a flat bond. If two warp threads 3 are arranged in a group and two warp threads 4 are arranged in a group alternating with each other in the longitudinal direction of the fabric, a weft repeat is obtained in a similar manner. Parts of the warp yarns 3 and 4 are at least partially fused to each other on the back side of the smooth fabric 6. This is shown in Figure 1. Preferably, parts of the warp yarns 3, 4 are at least partially fused to parts of the weft yarns 5 on the back side of the smooth fabric 6.

[0100] FIG. 2 is a schematic diagram illustrating a molecular model of the bond between a fabric and a needle felt according to one embodiment of the present invention.

[0101] A composition containing reactive molecule B is applied to the back side of fabric 6 and one side of needled felt 1. The back side of fabric 6 and the side of needled felt 1 to which the composition consisting of reactive molecule B has been applied are brought together, and an intermediate layer having reactive molecule A is provided between these surfaces. After the reaction between molecule A and molecule B has occurred, bond 7 is formed between fabric 6 and needled felt 1. This bond 7 utilizes the covalent interaction between molecule A and molecule B.

[0102] FIG. 3 shows an apparatus suitable for at least partially fusing some of the warp threads together according to one embodiment of the method of the present invention.

[0103] The fabric 50' is directed through the support rolls 41 and 42. The direction is from the support roller 41 to the support roller 42. Between the two support rollers 41, 42 is the heated surface 30. The heated surface presses against the back side of the fabric 50' at a point 33. On the back side of the fabric 50', some of the warp threads are at least partially fused together. The fused warp threads are distributed on an essentially flat surface by their movement through the tip 33 of the heated surface 30. They are then cooled, forming the fabric 50, which is stronger, dimensionally more stable and more wear-resistant than the fabric 50'.

[0104] The heated surface 30 can be moved over a distance d, which can be, for example, between 0 mm and 50 mm. By making the distance d greater than 0 mm, the tip 33 of the heated surface 30 is pressed against the back side of the fabric. The required distance d is determined by the desired result of at least partial melting of some of the warp threads, together with the temperature of the heated surface 30 and its tip 33, the speed at which the fabric 50' is led through the tip 33, and the fabric 50' itself. If the fabric 50' cannot tolerate a large distance d, other variations of the parameters speed, distance d, and temperature of the heated surface 30 and its tip 33 are possible in order to obtain the desired result. EXAMPLES

[0105] The present invention will now be described with reference to the following examples, but is not limited thereto.

[0106] This example relates to an embodiment of a polyester transportation carpet according to the present invention, more particularly an aircraft carpet, which comprises a smooth fabric, an intermediate layer, and a needle felt.

[0107] Both the smooth fabric and the needle felt consist of 100% flame retardant PES. The middle layer contains a PES adhesive. Therefore, the aircraft carpet can be 100% recycled in a simple way after it has been replaced with a new aircraft carpet.

[0108] Needle felt is a type of nonwoven fabric. HTH577 type Velcro strips are glued to the aircraft floor. Many loose filament ends or loops in the needle felt catch on the hooks of the Velcro tape. As a result, aircraft carpet can be installed quickly and can also be replaced quickly. The aircraft carpet is simply peeled off the Velcro strip and new aircraft carpet is stuck to the Velcro strip. There is no adhesive residue that needs to be removed from the aircraft floor. Needle felt also leaves no adhesive residue, making it easy to recycle.

[0109] The fabric is made up of warp and weft threads with a yarn count of 2200 dtex. The yarns have an average breaking elongation of 30% and a minimum tensile strength of 3 g / den, tested according to ISO 2062. The average boiling shrinkage of the yarns is 1.5% according to ISO 12590. The warp threads are 17 threads per cm of fabric and the weft threads are 5 threads per cm of fabric. The result is a strong, yet lightweight fabric. The fabric weight is 570 g / m 2 is limited to.

[0110] Some of the warp and weft threads are at least partially fused to each other on the back side of the fabric. This strengthens the fabric and improves its dimensional stability. As the warp and weft threads move less against each other, there is less friction between them, which results in less wear and tear during daily passenger and trolley traffic. As a result of the warp and weft threads being at least partially fused, the fabric is stronger and has greater dimensional stability, so that no adhesive needs to be used to fix the knots between the warp and weft threads. The intermediate layer, consisting of adhesive, is therefore lighter. The weight of the intermediate layer is 130 g / m 2 is limited to.

[0111] Needle felt is suitable for imparting the necessary dimensional stability to aircraft carpets. Needle felt is suitable for improving the walkability of passengers on aircraft carpets and for increasing sound insulation. The fabric already has a certain dimensional stability, since the warp and weft threads are at least partially melted, which increases the strength of the fabric. This allows thinner needle felts to be used for aircraft carpets. Needle felts can be used with a maximum weight of 150 g / m 2 The total weight of the carpet is therefore 850 g / m 2 It becomes.

[0112] Aircraft carpet was tested for flammability in accordance with FAR25.853, specifically FAR25.853(A)-App.f Part I para (a)(1)(ii) Determination of Flammability of Aircraft Materials. Testing was performed in a draft-free cabinet in accordance with Federal Test Method Standard 191, Method 5903.2. Three aircraft carpet samples, 75 mm x 305 mm, were exposed to a Bunsen burner flame at a temperature of at least 843°C for 60 seconds. The samples were suspended vertically along their length and 20 mm above the tip of the Bunsen burner. The height of the Bunsen burner flame was 40 mm measured from the tip of the burner. The aircraft carpet was then burned for a maximum average of 2 seconds over an area less than 80 mm in length and width. No burned portions of the aircraft carpet fell off. This aircraft carpet therefore meets standards which require the carpet to continue to burn for a maximum of 15 seconds after the flame is removed, the carpet to burn for a maximum length of 152 mm, and the burning portion of the carpet to burn for a maximum of 5 seconds.

[0113] The aircraft carpet was subjected to the Betterman and Lisson tests. The Betterman test simulates wear under laboratory conditions. The Lisson test measures the loss of mass and the bond of fibers or yarns after a set number of double passes of an aircraft carpet by a four-wheeled vehicle. In both tests, the aircraft carpet achieved the highest classification of 33, which means the carpet is suitable for heavy loads. This aircraft carpet is suitable for heavy daily loads from passengers and trolleys.

[0114] Aircraft carpets meet the ISO 6356 standard for static electricity tendencies of textile and laminate flooring.

Claims

1. 1. A flame retardant carpet for use inside a vehicle, comprising: - Maximum weight of 650 g / m2 consisting of front and back sides as usable surfaces ２ a mechanically woven fabric of the present invention, the fabric consisting essentially of 100% thermoplastic flame retardant polyester warp and weft yarns; - essentially 100% thermoplastic flame retardant polyester with a maximum weight of 220 g / m ２ Needle felting and - maximum weight between needle felt and mechanically woven fabric of 180 g / m ２ and the middle class. A carpet comprising: A mechanically woven fabric, characterized in that some of the warp yarns on the back side are at least partially fused to each other. carpet.

2. 2. Carpet according to claim 1, characterized in that the yarn count of the warp and weft threads is between 1100 dtex and 4400 dtex.

3. 3. Carpet according to claim 1 or 2, characterized in that the number of warp threads per cm of fabric is between 8 and 30.

4. 4. Carpet according to claim 1, characterized in that the number of weft threads per cm of fabric is between 3 and 10.

5. Carpet weight up to 950 g / m ２ 5. The carpet according to claim 1, wherein the

6. 6. The carpet according to claim 1, characterized in that the mechanically woven fabric and the needle felt are laminated to each other with the aid of an intermediate layer.

7. 7. The carpet of claim 1, wherein the intermediate layer comprises a thermoplastic flame retardant polyester adhesive.

8. 8. A carpet according to any one of claims 1 to 7, characterized in that some of the weft yarns of the mechanically woven fabric are at least partially fused with some of the warp yarns.

9. 1. A method for making a flame retardant carpet for use in a vehicle interior, comprising: - a maximum weight of 650 g / m2, consisting of a front side and a back side as the working surface and consisting essentially of warp and weft threads of 100% thermoplastic flame-retardant polyester ２ Mechanically weaving the fabric; - Maximum weight of 220 g / m2 of essentially 100% thermoplastic flame retardant polyester ２ and producing a needle felt of - Maximum weight 180 g / m2 depending on intermediate layer ２ Laminating the needle felt onto fabric, The method includes: The method further comprises the step of directing the backside of the mechanically woven fabric along a heated surface to at least partially fuse together some of the warp yarns on the backside of the fabric prior to lamination. method.

10. 10. The method of claim 9, wherein the lamination comprises using a thermoplastic flame retardant polyester as an adhesive for the interlayer.

11. 10. The method of claim 9, wherein lamination comprises using reactive molecules to form thermally reversible covalent interactions with the interlayer.

12. 12. The method according to claim 9, 10 or 11, characterized in that it comprises an additional step, prior to lamination, of directing the backside of the mechanically woven fabric along a heated surface in order to at least partially fuse some of the weft yarns of the backside of the fabric with some of the warp yarns.

13. A method for producing a carpet according to any one of claims 1 to 8, using a method according to any one of claims 9 to 12.