Heatable composite panes for projection assemblies

Abstract

The present invention relates to a composite pane (1), in particular for a projection assembly (100), comprising at least: - an outer pane (2), an inner pane (3) and a thermoplastic intermediate layer (4) arranged between said outer pane and said inner pane (2, 3), wherein said outer pane and said inner pane (2, 3) respectively have outer surfaces (I, III) and inner surfaces (II, IV), said inner surface (II) of said outer pane (2) and said outer surface (III) of said inner pane (3) facing each other; a first masking strip (5) arranged regionally on one of the outer faces (I, III) or the inner faces (II, IV) of the inner or outer pane (2, 3); - a conductive coating (10), as well as - a reflective layer (9) suitable for reflecting light (12), Here, the reflective layer (9) is spatially positioned in front of the first masking strip (5) when viewed from the inner pane (3) towards the outer pane (2), and wherein the first masking strip (5) overlaps with the reflective layer (9) in at least one area.

Description

[Technical field]

[0001] The present invention relates to a heatable composite pane for a projection assembly, to a method for its manufacture, to its use, and to a projection assembly. [Background technology]

[0002] Head-up displays are now frequently used in vehicles and aircraft. Their operation proceeds through the use of an imaging unit, which uses an optical module and a projection surface to project an image that the driver perceives as a virtual image. When this image is reflected, for example, through the vehicle's windshield as a projection surface, it can display important data to the user, which significantly improves road safety.

[0003] Typically, a vehicle windshield consists of two glass panes that are laminated together via at least one thermoplastic film. In a typically used head-up display, a problem occurs in that the projector image is reflected on both surfaces of the windshield. Thus, the driver does not only perceive the desired primary image, which is caused by a reflection on the inner surface of the windshield (primary reflection). The driver also perceives a slightly offset secondary image, which is usually weaker in intensity and is caused by a reflection on the outer surface of the windshield (secondary reflection). This problem is generally solved by placing the reflective surfaces at a deliberately selected angle relative to each other, so that the primary and secondary images coincide, and thus the secondary image is no longer noticeable.

[0004] Head-up display projector radiation is typically substantially s-polarized because of the superior reflective properties of the windshield compared to p-polarized light. However, if a driver wears polarization-selective sunglasses that transmit only p-polarized light, they will perceive little or no HUD image at all. As a result, there is a need for a HUD projection assembly that is compatible with polarization-selective sunglasses. Thus, a solution to this associated problem is to use a projection assembly that uses p-polarized light.

[0005] A further issue is the recognizability of the information conveyed via the reflected image, regardless of weather and lighting conditions. Critical and safety-relevant information must be sufficiently recognizable by the driver at any time of day or night, and in strong sunlight or rain. As a result, when designing a display based on head-up display technology, care must be taken to ensure that the projector has a correspondingly high output, so that the projected image has sufficient brightness, especially when sunlight is incident, to be easily recognized by the observer. This requires a projector of a certain size, which entails a corresponding power consumption.

[0006] DE 102014220189 A1 discloses a head-up display projection assembly that works with p-polarized radiation to generate a head-up display image. The windshield has a reflective structure that can reflect p-polarized light in the direction of the driver, since the angle of incidence is typically close to the Brewster angle (polarization angle) and therefore p-polarized light is only slightly reflected by the glass surface. A single metal layer (e.g. made of silver or aluminum) with a thickness of 5 nm to 9 nm is proposed as the reflective structure, applied on the outer surface of the inner pane, facing away from the interior of the passenger vehicle.

[0007] US 2004 / 0135742 similarly discloses a head-up display projection assembly that operates with p-polarized radiation to generate a head-up display image and has a reflective structure capable of reflecting the p-polarized radiation in the direction of the driver. A multi-layer polymer layer, as disclosed in the WO 96 / 19347 search report, is proposed as the reflective structure.

[0008] When designing a display based on head-up display technology, more care must be taken to ensure that the projector has a reasonably high power output so that the projected image has sufficient brightness, especially when sunlight is incident, so that it can be easily recognized by the observer, which requires a certain size of projector, with the attendant corresponding power consumption and heat dissipation.

[0009] DE 102009020824 A1 discloses a virtual image system having a reflective Mylar application applied onto a composite pane overlapping a black material. This composite pane may be installed, for example, as a windshield in a vehicle, where the Mylar application is illuminated with a virtual image from an image display device, which is reflected into the vehicle interior for an observer. The image display device is preferably positioned with an air vent, such as one used to heat the composite pane, so that it is not visible to the driver.

[0010] Another major challenge during driving is the heating of the windshield to prevent icing or fogging of the pane, which would impair visibility. Furthermore, the projected image must be easily legible under all weather and temperature conditions, which can be impaired by the formation of condensation on the pane. The pane is usually heated by heated air that is blown onto the pane through an inlet. This type of heating is grouped under the heating, ventilation and air conditioning (HVAC) method. In addition to the huge energy consumption, the inlet, through which the hot air is conveyed and blown onto the pane, requires a large space. Furthermore, the air vents must usually be installed in the form of outlet nozzles in a specific geometric relationship to the pane, which in turn greatly limits the design freedom. These air vents or outlet nozzles make it difficult to accommodate the projector or image display device in the dashboard. They are typically located in the area of ​​the dashboard vents, which makes the heating of the pane weak or completely impossible.

[0011] Alternatively, the pane itself may have an electrical heating function. From DE 103 52 464 A1, for example, a composite glass pane is known, in which an electrically heatable wire is arranged between two glass panes. The specific heating output can be adjusted via the ohmic resistance of the wire. For design and safety reasons, both the number of wires and the wire diameter must remain as small as possible. The wire must be invisible or barely perceptible under headlight illumination during the day and at night.

[0012] Transparent conductive coatings are also known, in particular based on silver. Such conductive coatings may be used as coatings with reflective properties in the infrared range or as heatable coatings. WO 03 / 024155, for example, discloses a conductive coating with two silver layers. Such coatings usually have a sheet resistance in the range of 3 Ω / sq.

[0013] One problem with conductive coatings is that their sheet resistance is often high, which, at least when the dimensions of the pane to be heated are large or the current path is long, requires high operating voltages, which are in any case higher than the normal on-board voltage of the vehicle. WO 2013 / 104439 and EP 2803246 disclose conductive coatings for heating panes that consist of different layers. At least one of these layers contains a high-refractive index material with a refractive index of 2.1 or more. In this way, the sheet resistance of the conductive coating is significantly reduced, so that it is preferably less than 1 Ω / sq. Summary of the Invention [Problem to be solved by the invention]

[0014] SUMMARY OF THE PRESENT EMBODIMENTS Accordingly, it is an object of the present invention to provide an improved composite pane for a projection assembly based on HUD technology. [Means for solving the problem]

[0015] According to the invention, the object is achieved by a composite pane as claimed in claim 1. Preferred embodiments are evident from the dependent claims. [Brief description of the drawings]

[0016] [Figure 1A] FIG. 1A is a plan view of one embodiment of a composite pane according to the present invention. [Figure 1B] FIG. 1B is a cross-sectional view of a projection assembly according to the present invention having the composite pane of FIG. [Diagram 2] FIG. 2 is another cross-sectional view of a projection assembly according to the present invention having a composite pane. [Diagram 3] FIG. 3 is a plan view of a further embodiment of a composite pane according to the present invention. [Figure 4] FIG. 4 is a plan view of a further embodiment of a composite pane according to the present invention. [Diagram 5]FIG. 5 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. [Figure 6] FIG. 6 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. [Figure 7] FIG. 7 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. [Figure 8] FIG. 8 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. [Figure 9] FIG. 9 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. [Figure 10] FIG. 10 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0017] According to the invention, a composite pane, particularly intended for a projection assembly, is described, which comprises at least: an outer pane, an inner pane, and a thermoplastic intermediate layer disposed between the outer pane and the inner pane; - conductive coating, - the first masking strip, - as well as a reflective layer.

[0018] The outer pane and the inner pane each have an outer surface and an inner surface, the inner surface of the outer pane and the outer surface of the inner pane facing each other.

[0019] The first masking strip is regionally disposed on one of the outer or inner surfaces of the inner or outer pane. The reflective layer is adapted to reflect light.

[0020] When viewed from the inner pane towards the outer pane, the reflective layer is spatially disposed in front of the first masking strip, and the first masking strip overlaps the reflective layer in at least one area.

[0021] The reflective layer and the first masking strip may be disposed on different outer or inner surfaces of the inner or outer pane. Alternatively, the reflective layer and the first masking strip may be disposed on the same outer or inner surface of the inner pane, or on the inner surface of the outer pane. The reflective layer may have a portion that does not overlap with the first masking strip, i.e., the reflective layer includes at least one region in which the reflective layer is located in front of the first masking strip when viewed from the inner pane toward the outer pane.

[0022] The conductive coating may be disposed locally or completely on the inner or outer surface of the outer pane, on the inner or outer surface of the inner pane, in a thermoplastic interlayer, or on a masking strip. Preferably, the conductive coating is disposed between the outer and inner panes.

[0023] In the context of the present invention, "between the outer and inner panes" means that the conductive coating may be disposed in the thermoplastic interlayer, on the inner surface of the outer pane, or on the outer surface of the inner pane. If a first masking strip is also disposed between the outer and inner panes, the conductive coating may be disposed on the masking strip, or the first masking strip may be disposed on the conductive coating.

[0024] In the context of the present invention, for example, a statement that an element A completely overlaps with an element B means that an orthogonal projection of element A onto a surface plane of element B is completely located within element B. It goes without saying that "overlap within a certain area" means that an orthogonal projection of element A onto a surface plane of element B is located within element B only regionally.

[0025] Various preferred layer arrangements of the composite pane according to the present invention are described below:

[0026] (1) When the first masking strip is disposed on the outer surface of the outer pane and the conductive coating is disposed on the inner surface of the outer pane, the reflective layer may be disposed on the inner or outer surface of the inner pane, or within the thermoplastic interlayer. Alternatively, the reflective layer may be disposed on the inner surface of the outer pane and on the conductive coating. In another alternative, the reflective layer may be disposed only on the inner surface of the outer pane or on the conductive coating.

[0027] (2) If the first masking strip is disposed on the inner surface of the outer pane and the conductive coating is also disposed on the inner surface of the outer pane or on the first masking strip, or on the first masking strip and on the inner surface of the outer pane, the reflective layer may be disposed on the inner or outer surface of the inner pane, or in the thermoplastic interlayer. Alternatively, the reflective layer may also be disposed on the inner surface of the outer pane, on the conductive coating and on the first masking strip. In another alternative, the reflective layer may be disposed on the first masking strip and on the inner surface of the outer pane. In another alternative, the reflective layer may be disposed on the first masking strip and on the conductive coating. Additionally, the reflective layer may be disposed only on the masking strip.

[0028] (3) When a first masking strip is disposed on the outer surface of the inner pane and a conductive coating is disposed on the outer surface of the inner pane or on the first masking strip, or on the first masking strip and on the outer surface of the inner pane, a reflective layer may be disposed on the inner surface of the inner pane.

[0029] (4) When a first masking strip is disposed on the inner surface of the inner pane and a conductive coating is disposed on the inner surface of the outer pane or on the outer surface of the inner pane, a reflective layer may be disposed on the first masking strip and on the inner surface of the inner pane, or further, the reflective layer may be disposed only on the masking strip.

[0030] (5) When the first masking strip is disposed on the outer surface of the outer pane and the conductive coating is disposed on the outer surface of the inner pane, the reflective layer may be disposed on the inner surface of the outer pane, on the inner surface of the inner pane, or within the thermoplastic interlayer. Alternatively, the reflective layer may be disposed on the outer surface of the inner pane or on the conductive coating. In another alternative, the reflective layer may be disposed on the outer surface of the inner pane and on the conductive coating.

[0031] (6) When the first masking strip is disposed on the inner surface of the outer pane and the conductive coating is disposed on the outer surface of the inner pane, the reflective layer may be disposed on the inner surface of the inner pane or in the thermoplastic interlayer. Alternatively, the reflective layer may be disposed on the outer surface of the inner pane or on the conductive coating. Also, the reflective layer may be disposed on the outer surface of the inner pane and on the conductive coating. As another alternative, the reflective layer may be disposed on the inner surface of the outer pane and on the first masking strip, or only on the first masking strip.

[0032] (7) When the first masking strip is disposed on the outer surface of the inner pane and the conductive coating is disposed on the inner surface of the outer pane, a reflective layer may be disposed on the inner surface of the inner pane.

[0033] The conductive coating may overlap the first masking strip and / or the reflective layer. It may be disposed regionally or completely over the first masking strip.

[0034] The composite pane is intended to separate the interior from the external environment. The inner surface of the inner pane faces the interior, and the outer surface of the outer pane faces the external environment. In the context of the present invention, the expression "when viewed from the inner pane towards the outer pane, the reflective layer is spatially arranged in front of the first masking strip" means that the reflective layer is spatially closer to the interior than the first masking strip. That is, when viewed from the interior towards the outside through the composite pane, the reflective layer is spatially arranged in front of the first masking strip. The outer pane and the inner pane preferably have two opposing lateral edges, an upper edge and a lower edge. In the installed state, the upper edge is intended to be arranged in the upper region, and the opposite, lower edge is intended to be arranged in the lower region in the installed state.

[0035] The conductive coating is preferably transparent. The first masking strip is opaque. The reflective layer may be opaque or transparent. Preferably, the reflective layer is transparent.

[0036] In the context of the present invention, "transparent" means that the total transmittance of the composite pane complies with the legal requirements for windscreens (e.g. European Union Directive ECE-R43), preferably having a transmittance for visible light of more than 50%, in particular more than 60%, for example more than 70% (ISO 9050:2003). "Opaque" therefore means a light transmittance of less than 10%, preferably less than 5%, in particular 0%.

[0037] The present invention is based on the realization that the reflective layer, which at least in areas overlaps the first masking strip, allows a good image display with high contrast to the opaque first masking strip, which makes the image display appear bright and thus also allows for good recognition. Advantageously, this allows the power of the image display device to be reduced, thus reducing energy consumption and heat generation. The conductive coating allows the use of outlet nozzles for heating the composite pane to be largely omitted, thus saving space in the vehicle for the image display device. This is a major advantage of the present invention.

[0038] In certain embodiments of the invention, the reflective layer is disposed on the outer surface of the inner pane, or on one of the inner or outer panes, in the thermoplastic interlayer, or on the first masking strip, where the first masking strip has a larger surface area than the reflective layer and completely overlaps the reflective layer. In this embodiment, the reflected image is particularly high in contrast; because the reflective layer is disposed completely in front of the first masking strip.

[0039] The first masking strip is preferably arranged in a circumferential frame-like manner in the edge region of the inner or outer side of the outer pane, and in particular has a greater width in one part overlapping the reflective layer than in another part. The first masking strip is particularly preferably arranged on the inner or outer side of the outer pane along the lateral edges and the upper and lower edges. In the context of the present invention, "having a greater width" means that the masking strip has a greater width in this part perpendicular to its extension direction than in the other parts. In this way, the masking strip can be appropriately adapted to the dimensions of the reflective layer.

[0040] The first masking strip is preferably a coating having one or more layers. Alternatively, however, it may be an opaque element, such as a film, inserted into the composite pane.

[0041] According to a preferred embodiment of the composite pane, the first masking strip consists of a single layer, which has the advantage that the production of the composite pane is particularly simple and economical, since only a single layer has to be formed for the masking strip.

[0042] In addition to the modes of action described in the context of the present invention, it may also serve to mask other structures that are discernible through the pane in the installed state. In particular, in the case of a windscreen, the first masking strip serves to mask the adhesive bead for gluing the windscreen into the vehicle body. This means that the adhesive bead, which is usually applied irregularly, is prevented from being visible from the outside, thereby creating a harmonious impression of the entire windscreen. On the other hand, the masking strip also serves as a UV protection for the adhesive used. Continued exposure to UV light would damage the adhesive and over time would loosen the adhesion of the pane to the vehicle body. In the case of a pane with an electrically controllable functional layer, the first masking strip may also serve to hide, for example, busbars and / or connection elements.

[0043] The first masking strip is preferably printed on the outer pane, in particular by screen printing. The printing ink is pressed onto the glass pane through a finely woven fabric. The printing ink is pressed through the fabric, for example, with a rubber squeegee. The fabric has areas that are permeable to the printing ink and areas that are not permeable to the ink, which define the geometry of the print. In this way, the fabric acts as a stencil for the printing. The printing ink contains at least one pigment and a glass frit suspended in a liquid phase (solvent), for example water or an organic solvent (such as alcohol). The pigment is typically a black pigment, for example carbon black, aniline black, bone black, iron oxide black, spinel black, and / or graphite.

[0044] After the ink has been printed, the glass pane is subjected to a temperature treatment in which the liquid phase is expelled by evaporation and the glass frit melts and becomes permanently bonded to the glass surface. The temperature treatment is typically carried out at a temperature in the range of 450°C to 700°C. The pigment remains as a masking strip in the glass matrix formed by the molten glass frit.

[0045] Alternatively, the first masking strip is an opaque, i.e. colored or pigmented, preferably black-pigmented, thermoplastic composite film, preferably based on polyvinyl butyral (PVB), ethyl vinyl acetate (EVA) or polyethylene terephthalate (PET), preferably PVB. The coloring or pigmentation of the composite film may be freely selected, but is preferably black. The colored or pigmented composite film is preferably arranged between the outer and inner panes, particularly preferably on the inner face of the outer pane. The colored or pigmented thermoplastic composite film preferably has a thickness of 0.25 mm to 1 mm.

[0046] When something is "based on" a material, it consists largely of that material, and particularly consists essentially of that material in addition to impurities or dopants.

[0047] According to another preferred embodiment of the composite pane according to the invention, in addition to the first masking strip on the inner side of the outer pane, at least one additional masking strip is arranged on the outer side of the inner pane and / or on the inner side of the inner pane. The additional masking strip serves to improve the adhesion between the outer pane and the inner pane and is preferably mixed with ceramic particles, which give the masking strip a rough and adhesive surface. This supports, for example, on the inner side of the inner pane, the joining of the composite pane in the vehicle body. On the outer side of the inner pane, it supports the lamination of the two individual panes of the composite pane. An additional masking strip applied on the inner side of the inner pane may also be provided for aesthetic reasons, for example to hide the edges of the reflective layer or to form the edges of the transition to the transparent area. The first and additional masking strips preferably have a thickness of 5 μm to 50 μm, particularly preferably 8 μm to 25 μm.

[0048] The light reflected by the reflective layer is preferably visible light, i.e. light in the wavelength range of about 380 nm to 780 nm. Thus, the reflective layer is suitable for reflecting visible light in the wavelength range of about 380 nm to 780 nm. The reflective layer preferably has a high and uniform reflectance (at various angles of incidence) for p-polarized and / or s-polarized radiation, thereby ensuring a bright, color-neutral image display.

[0049] The reflective layer is preferably partially transparent to light, which in the context of the present invention means that the reflective layer has an average transmittance (according to ISO 9050:2003) in the visible spectrum of preferably at least 60%, particularly preferably at least 70%, in particular less than 85%, and thus does not substantially restrict the view through the pane. The reflective layer preferably reflects at least 15%, particularly preferably at least 20%, most particularly preferably at least 30% of the light incident on the reflective layer. The reflective layer preferably reflects only p-polarized or s-polarized light. The reflective layer is intended to reflect light from an image display device.

[0050] The reflective layer may be opaque. The reflective layer is preferably opaque when it is positioned in line with the opaque areas of the masking layer or when the reflective layer completely overlaps the opaque areas of the masking layer. An opaque reflective layer preferably reflects at least 60%, particularly preferably at least 70%, and most particularly preferably at least 80% of the light incident on the reflective layer.

[0051] The reflective layer is suitably implemented to reflect light from the image display device, and preferably reflects at least 30%, preferably at least 50%, most particularly preferably at least 70%, especially at least 90% of the light from the image display device that is incident on the reflective layer.

[0052] In preferred embodiments of the invention, the reflective layer preferably reflects at least 10%, more preferably at least 50%, most particularly at least 70%, especially 90% of p-polarized light.

[0053] The indication of polarization direction refers to the plane of incidence of the radiation on the composite pane. The expression "p-polarized radiation" refers to radiation whose electric field oscillates in the plane of incidence. The expression "s-polarized radiation" refers to radiation whose electric field oscillates perpendicular to the plane of incidence. The plane of incidence is generated by the incidence vector and the surface normal of the composite pane at the geometric center of the illuminated area.

[0054] In other words, the polarization, i.e. in particular the proportion of p-polarized and s-polarized radiation, is determined at one point of the area illuminated by the image display device, preferably at the geometric center of the illuminated area. Since the composite panes may be curved (for example when they are windshields) and thus affect the incidence surface of the radiation of the image display device, slightly deviated polarization proportions may occur in the remaining areas, which is unavoidable for physical reasons.

[0055] The reflective layer preferably comprises at least one metal selected from the group consisting of aluminum, tin, titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, manganese, iron, cobalt, rhodium, iridium, nickel, palladium, platinum, copper, silver, gold, or mixed alloys thereof. The reflective layer particularly preferably contains aluminum or a nickel-chromium alloy. In particular, the reflective layer consists of aluminum or a nickel-chromium alloy. Aluminum and nickel-chromium alloys have a particularly high reflectivity for visible light.

[0056] In one particular embodiment of the invention, the reflective layer is a coating containing a thin film stack, i.e. a layer sequence of thin individual layers. This thin film stack contains one or more conductive layers based on silver. The conductive layers based on silver provide the reflective coating with the basic reflective properties as well as the IR reflective effect and also electrical conductivity. The conductive layers are based on silver. This conductive layer preferably contains at least 90% by weight of silver, particularly preferably at least 99% by weight of silver, most particularly preferably at least 99.9% by weight of silver. The silver layer may have dopants, such as palladium, gold, copper or aluminum. Silver-based materials are particularly suitable for reflecting light, particularly preferably p-polarized light. The use of silver in the reflective layer has proven to be particularly advantageous in reflecting light. The coating has a thickness of 5 μm to 50 μm, preferably 8 μm to 25 μm.

[0057] The reflective layer may be implemented as a reflective coated or uncoated film that reflects light, preferably p-polarized light. The reflective layer may be a carrier film with a reflective coating or a reflective polymer film. The reflective coating preferably comprises at least one layer based on a metal and / or dielectric layer sequence with alternating refractive index. The metal-based layer preferably contains or is made of silver and / or aluminum. The dielectric layer may be based, for example, on silicon nitride, zinc oxide, zinc tin oxide, mixed silicon-metal nitrides (such as silicon-zirconium nitride), zirconium oxide, niobium oxide, hafnium oxide, tantalum oxide, tungsten oxide or silicon carbide. The above oxides and nitrides may be deposited stoichiometrically, substoichiometrically or superstoichiometrically. They may have dopants, such as aluminum, zirconium, titanium, boron, etc. The reflective uncoated polymer film preferably comprises or is made of a dielectric polymer layer. The dielectric polymer layer preferably contains PET.If the reflective layer is implemented as a reflective film, its thickness is preferably 30 μm to 300 μm, particularly preferably 50 μm to 200 μm, in particular 100 μm to 150 μm.

[0058] If the reflective layer is implemented as a coating, it is preferably applied on the inner or outer pane by physical vapor deposition (PVD), particularly preferably by cathodic sputtering ("sputtering"), most particularly preferably by magnetron enhanced cathodic sputtering ("magnetron sputtering"). In principle, however, the coating may also be applied, for example, by chemical vapor deposition (CVD), plasma enhanced chemical vapor deposition (PECVD), by evaporation or by atomic layer deposition (ALD). The coating is preferably applied to the pane before lamination.

[0059] When the reflective layer is coated on the reflective film, CVD or PVD coating methods may be used for manufacturing.

[0060] According to another preferred embodiment of the composite pane according to the invention, the reflective layer is implemented as a reflective coated carrier film or a reflective uncoated polymer film and is arranged in the thermoplastic interlayer. The advantage of this arrangement is that the reflective layer does not have to be applied to the outer or inner pane using thin film techniques (such as CVD or PVD). This leads to the use of a reflective layer with further advantageous functions, such as a more uniform reflection of light on the reflective layer. Furthermore, the manufacture of the composite pane can be simplified; since the reflective layer does not have to be arranged on the outer or inner pane via an additional process before lamination.

[0061] In a particularly preferred embodiment of the present invention, the reflective layer is a reflective film that does not contain metal and preferably reflects visible light with p-polarization. The reflective layer is a film that functions based on a prism and a reflective polarizer that act synergistically with each other. Such films for use as reflective layers are commercially available, for example from 3M.

[0062] In another preferred embodiment of the invention, the reflective layer is a holographic optical element (HOE). The term "HOE" refers to an element based on the working principle of holography. HOEs modify the light in a line (beam) path using information stored in a hologram, usually as a change in the refractive index. Their function is based on the superposition of plane or spherical light waves whose interference pattern produces the desired optical effect. HOEs are already used in the transportation field (e.g. head-up displays, etc.). The advantage of using HOEs compared to simple reflective layers is due to the relatively large degree of freedom in the geometric design, with regard to the arrangement of the eye and projector positions, as well as the respective inclination angles of the projector, the reflective layer, etc. Furthermore, with this variant, double images are particularly significantly reduced or even prevented. HOEs are suitable for displaying real or even virtual images at different image widths. Furthermore, since the geometric reflection angle can be adjusted with the HOE, for example in the case of applications in vehicles, the information transmitted to the driver can be displayed very well from the desired viewing angle.

[0063] Advantageously, the reflective layer may improve the properties of the reflected light compared to simple reflection of the light at the pane: the proportion of p-polarized light reflected is preferably high, for example the reflectance of the light is about 90%.

[0064] In one particular embodiment of the invention, the high refractive index coating is applied to the entire inner surface of the inner pane or to a region thereof. The high refractive index coating is preferably in direct spatial contact with the inner surface of the inner pane. The high refractive index coating is located at least in a region on the inner surface of the inner pane that completely overlaps the reflective layer when viewed through the composite pane. In this way, the reflective layer is located spatially closer to the outer surface of the outer pane than the high refractive index coating, but spatially farther from the inner surface of the inner pane. This means that light projected by the image display device onto the reflective layer, preferably with a majority of p-polarized light, passes through the high refractive index coating before hitting the reflective layer.

[0065] The high refractive index coating has a refractive index of at least 1.7, particularly preferably at least 1.9, and most particularly preferably at least 2.0. The increased refractive index results in a high refractive effect. The high refractive index coating reduces the reflection of light, particularly p-polarized light, at the inner surface of the inner pane, so that the desired reflection of the reflective coating appears with greater contrast.

[0066] According to the inventors' explanation, this effect is due to the increase in the refractive index of the inner surface due to the high refractive index coating. This reduces the Brewster angle α Brewster increases since it is known to be determined as: where n1 is the refractive index of air and n2 is the refractive index of the material on which the radiation impinges.

[0067]

number

[0068] A high refractive index coating with a high refractive index results in an increase in the effective refractive index of the glass surface, thus resulting in a shift in the Brewster angle to a larger value compared to an uncoated glass surface. As a result, due to the general geometric relationship of the projection assembly based on HUD technology, the difference between the incidence angle and the Brewster angle is reduced, suppressing the reflection of p-polarized light on the inner surface of the inner pane, thereby weakening the ghost image that occurs.

[0069] The high refractive index coating is preferably formed from a single layer, without any further layers above or below it. A single layer is sufficient to achieve a good effect and is technically simpler than applying layers one on top of the other. In principle, however, the high refractive index coating may have several individual layers, which may be desirable in order to optimize certain parameters in individual cases.

[0070] Suitable materials for the high refractive index coating are silicon nitride (Si3N4), mixed silicon-metal nitrides (such as silicon-zirconium nitride (SiZrN), mixed silicon-aluminum nitride, mixed silicon-hafnium nitride, or mixed silicon-titanium nitride), aluminum nitride, tin oxide, manganese oxide, tungsten oxide, niobium oxide, bismuth oxide, titanium oxide, mixed tin-zinc oxide, and zirconium oxide. Transition metal oxides (such as scandium oxide, yttrium oxide, tantalum oxide, etc.) or lanthanide oxides (such as lanthanum oxide or cerium oxide) may also be used. The high refractive index coating preferably contains or is based on one or more of these materials.

[0071] The high refractive index coating may be applied by physical or chemical vapor deposition, i.e. it may be a PVD or CVD coating (PVD: physical vapor deposition, CVD: chemical vapor deposition). Suitable materials on which the coating is preferably based are as follows; in particular silicon nitride, mixed silicon-metal nitrides (for example silicon-zirconium nitride, mixed silicon-aluminum nitride, mixed silicon-hafnium nitride or mixed silicon-titanium nitride), aluminum nitride, tin oxide, manganese oxide, tungsten oxide, niobium oxide, bismuth oxide, titanium oxide, zirconium oxide, zirconium nitride or mixed tin-zinc oxide. Preferably, the high refractive index coating is a coating applied by cathodic sputtering ("sputtering"), in particular a coating applied by magnetron-enhanced cathodic sputtering ("magnetron sputtering").

[0072] Alternatively, the high refractive index coating is a sol-gel coating. In the sol-gel method, first a sol containing the precursors of the coating is provided and aged. The aging may involve hydrolysis of the precursors and / or (partial) reaction between the precursors. The precursors are usually present in a solvent, preferably water, alcohol (especially ethanol) or a mixture of water and alcohol. In this case, the sol preferably contains a silicon oxide precursor in a solvent. The precursor is preferably a silane, in particular tetraethoxysilane or methyltriethoxysilane (MTEOS). However, alternatively, the following may be used as precursors; silicates, in particular sodium silicate, lithium silicate or potassium silicate, for example tetramethyl orthosilicate, tetraethyl orthosilicate (TEOS), tetraisopropyl orthosilicate or organosilanes of the general form R2nSi(OR1)4-n. where R1 is preferably an alkyl group; R2 is an alkyl, epoxy, acrylate, methacrylate, amine, phenyl or vinyl group; n is an integer from 0 to 2. Silicon halides or alkoxides may also be used. A silicon oxide precursor forms a sol-gel coating of silicon oxide. To increase the refractive index of the coating to the value according to the invention, a refractive index increasing additive, preferably titanium oxide and / or zirconium oxide or their precursors, is added to the sol. In the finished coating, the refractive index increasing additive is present in the silicon oxide matrix. The molar ratio of silicon oxide to the refractive index increasing additive may be freely selected depending on the desired refractive index, for example about 1:1.

[0073] In another particular embodiment of the invention, the high refractive index coating is applied regionally onto an additional masking strip, which is applied to the inner surface of the inner pane. In this context, the word "regionally" means that the high refractive index coating is partially or completely located on the additional masking strip, but may also be applied onto the inner surface of the inner pane. This has the advantage that the high refractive index layer can be applied to the entire inner pane, regardless of whether a masking strip has been previously applied to the inner pane or not.

[0074] Preferably, a further conductive coating is applied at least regionally on the outer surface of the inner pane or on the inner surface of the outer pane.

[0075] The conductive coating may extend over the entire outer surface of the inner pane or the entire inner surface of the outer pane. The conductive coating preferably extends over at least 50%, particularly preferably at least 70%, and most particularly preferably at least 90% of the outer surface of the inner pane or the inner surface of the outer pane.

[0076] The conductive coating may be applied directly onto the inner or outer pane, the reflective layer, or the masking strip, or alternatively, the conductive coating may be applied to a carrier film bonded to the outer or inner pane.

[0077] The conductive coating typically contains one or more, for example two, three or four, conductive functional layers. The functional layers preferably contain at least one metal, for example silver, gold, copper, nickel and / or chromium, or a metal alloy. The functional layers particularly preferably contain at least 90% by weight of the metal, in particular at least 99.9% by weight of the metal. The functional layers may consist of the metal or its metal alloy. The functional layers particularly preferably contain silver or a silver-containing alloy. Such functional layers have a particularly advantageous electrical conductivity and at the same time a high transmittance in the visible spectral range. The thickness of the functional layers is preferably 5 nm to 50 nm, particularly preferably 8 nm to 25 nm. With a thickness of the functional layers in this range, an advantageously high transmittance in the visible spectral range and a particularly advantageous electrical conductivity are achieved.

[0078] Preferably, at least one dielectric layer is arranged between each of two adjacent functional layers of the coating. Preferably, a further dielectric layer is arranged below the first functional layer and / or above the last functional layer. The dielectric layer contains at least one monolayer of a dielectric material, for example a dielectric material containing a nitride, such as silicon nitride, or an oxide, such as aluminum oxide. However, the dielectric layer may also comprise several individual layers, for example individual layers of dielectric material, smoothing layers, matching layers, blocking layers, and / or anti-reflection layers. The thickness of the dielectric layer is, for example, between 10 nm and 200 nm.

[0079] This layer structure is generally obtained by a sequence of deposition operations carried out by a vacuum process, such as magnetron enhanced cathode sputtering.

[0080] Other suitable conductive coatings preferably contain indium tin oxide (ITO), fluorine-doped tin oxide (SnO2:F) or aluminum-doped zinc oxide (ZnO:Al). The functional layer preferably has a layer thickness of 8 nm to 25 nm, particularly preferably 13 nm to 19 nm. This is particularly advantageous in terms of transparency, color neutrality and sheet resistance of the conductive coating.

[0081] In an advantageous embodiment, the conductive coating is a layer or a layer structure of several individual layers, the total thickness of which is less than or equal to 2 μm, particularly preferably less than or equal to 1 μm.

[0082] The total layer thickness of all conductive layers is preferably 40 nm to 80 nm, particularly preferably 45 nm to 60 nm. In this range of the total thickness of all conductive layers, a sufficiently high specific heat power P and at the same time a sufficiently high transmittance are advantageously achieved with a typical distance h between two busbars and an operating voltage U in the range of 12 V to 15 V for vehicle panes, in particular for windshields. Furthermore, in this range of the total thickness of all conductive layers, the conductive coating has particularly good reflection properties in the infrared range. If the total layer thickness of all conductive layers is too low, the sheet resistance R square would be too high, and therefore the specific heat power P would be too low, and the reflective properties in the infrared range would be poor. If the total layer thickness of all conductive layers were too large, the transmission through the pane would be too low, and would not meet the transmission requirements for vehicle windows.

[0083] In a preferred embodiment of the invention, the conductive coating is implemented in the form of a thin metal wire, which preferably extends from one edge region of the inner or outer pane to the opposite edge region of the inner or outer pane, respectively. The wires may overlap. The diameter of the metal wire is preferably less than 0.5 mm. The metal wire preferably contains at least one metal, such as silver, gold, copper, nickel and / or chromium, or a metal alloy. The metal wire particularly preferably comprises at least 90% by weight of the metal, in particular at least 99.9% by weight of the metal. The metal wire as an embodiment of the coating is particularly suitable for applications in which the conductive coating is heated via a heating current.

[0084] Regardless of the IR reflection effect of the heating coating, the coating may be used to heat the composite pane. For this purpose, preferably at least two outer busbars provided for connection to a voltage source are connected to the conductive coating, whereby a current path for the heating current is formed between the busbars. As a result of the heating of the composite pane via the conductive coating, various aspects of heating using heating, ventilation and air conditioning (HVAC) methods typically used when the composite pane is installed in a vehicle are not necessary. This allows further space saving in the area of ​​the dashboard. Heating using HVAC requires supply lines that lead the air that is usually heated in the engine compartment to the composite pane. These supply lines are usually installed in the dashboard of the vehicle and require a lot of space. However, electrical heating of the electrical coating is also advantageous for use in electric vehicles. In electric vehicles, heating the windshield via the conductive coating means energy savings compared to electrical heating of the air directed to the composite pane. In addition, there is freedom in design; since the exhaust of the HVAC system must be arranged in a defined geometric arrangement with respect to the glass surface in order to realize the blowing function. The use of conductive coatings eliminates such boundary conditions and allows for greater freedom in placement of the dashboard.

[0085] The conductive coating of the composite pane according to the invention preferably has a sheet resistance of less than or equal to 1 Ω / sq, particularly preferably between 0.4 Ω / sq and 0.9 Ω / sq, most particularly preferably between 0.5 Ω / sq and 0.85 Ω / sq, for example about 0.7 Ω / sq. In this range of sheet resistance, a high specific heat power P is advantageously achieved. Furthermore, in this range of sheet resistance, the conductive coating has particularly good reflection properties in the infrared range.

[0086] In a particular embodiment of the invention, the conductive coating is connected in the edge region of the outer or inner pane to two busbars provided for connection to a voltage source, whereby a current path for the heating current is formed between the busbars. In this context, the conductive coating preferably extends over 90% or more of the outer or inner pane. This arrangement allows efficient heating of a large portion of the composite pane.

[0087] In another particular embodiment of the invention, the conductive coating is arranged to completely overlap the first masking strip and is connected to two busbars provided for connection to a voltage source, whereby a current path for the heating current is formed between the busbars. Preferably, the conductive coating is applied onto the masking strips. In another possibility, the masking strips are applied onto the conductive coating. In this variant, the area coinciding with the first masking strip can be selectively heated.

[0088] The busbar may be implemented as a printed and fired conductive structure. The printed busbar preferably contains at least a metal, a metal alloy, a metal compound and / or carbon, particularly preferably a precious metal, in particular silver. The printing paste preferably contains metallic particles, metal particles and / or carbon, in particular precious metal particles such as silver particles. The electrical conductivity is preferably achieved through conductive particles. The particles may be present in an organic and / or inorganic matrix, for example in a paste or ink, preferably as a printing paste containing glass frit.

[0089] The layer thickness of the printed busbar is preferably 5 μm to 40 μm, particularly preferably 8 μm to 20 μm, most particularly preferably 8 μm to 12 μm. Printed busbars with these thicknesses are technically easy to realize and have an advantageous current-carrying capacity.

[0090] The width of the busbars is preferably between 2 mm and 30 mm, particularly preferably between 4 mm and 20 mm, in particular between 10 mm and 20 mm. Busbars thinner than this would have excessively high electrical resistance, which would result in the busbars heating up excessively during operation. Furthermore, thinner busbars are difficult to manufacture by printing techniques such as screen printing. Thicker busbars would require undesirably high material usage.

[0091] The resistivity ρa of the busbar is preferably 0.8 μΩ·cm to 7.0 μΩ·cm, and particularly preferably 1.0 μΩ·cm to 2.5 μΩ·cm. A busbar having a resistivity within this range is technically easy to realize and has an advantageous current-carrying capacity.

[0092] Alternatively, however, the busbar may be implemented as a strip of conductive foil, which for example contains at least aluminium, copper, tinned copper, gold, silver, zinc, tungsten and / or tin or alloys thereof. The strip preferably has a thickness of 10 μm to 500 μm, particularly preferably 30 μm to 300 μm. Busbars made of conductive foils with these thicknesses are technically easy to realise and have an advantageous current carrying capacity. The strip may be conductively connected to the conductive structure, for example via a solder compound, via a conductive adhesive or by direct placement.

[0093] In another particular embodiment of the invention, the conductive coating is disposed on the entire inner surface of the outer pane or the entire outer surface of the inner pane, excluding the peripheral edge regions of the outer pane or inner pane, preferably with a width of 5 mm to 100 mm, particularly preferably 10 mm to 50 mm. When installed in a vehicle, the non-coated areas thus formed (i.e. the edge regions without the conductive coating) serve as electrical insulation between the conductive coating and the vehicle body.

[0094] The outer and inner panes preferably contain or are made of glass, particularly preferably flat glass, float glass, quartz glass, borosilicate glass, soda-lime glass, aluminosilicate glass, or transparent plastic, preferably rigid transparent plastic, in particular polyethylene, polypropylene, polycarbonate, polymethyl methacrylate, polystyrene, polyamide, polyester, polyvinyl chloride, and / or mixtures thereof.

[0095] The outer and inner panes may further comprise suitable coatings known per se, such as anti-reflective, non-stick, scratch-resistant, photocatalytic or solar-shading or Low-E coatings.

[0096] The thickness of the individual panes (outer and inner panes) may vary and may be adapted to the requirements of each individual case. Preferably, panes having a standard thickness of 0.5 mm to 5 mm, more preferably 1.0 mm to 2.5 mm, are used. The size of the panes may vary and depends on the application.

[0097] The composite pane may have any desired three-dimensional shape. Preferably, the outer and inner panes have no shadow zones, which allows them to be coated, for example, by cathodic sputtering. Preferably, the outer and inner panes are flat or slightly or strongly curved in one or more spatial directions.

[0098] The thermoplastic intermediate layer contains or is made of at least one thermoplastic, preferably polyvinyl butyral (PVB), ethylene vinyl acetate (EVA) and / or polyurethane (PU), or copolymers or derivatives thereof, optionally in combination with polyethylene terephthalate (PET). However, the thermoplastic intermediate layer may also contain, for example, polypropylene (PP), polyacrylate, polyethylene (PE), polycarbonate (PC), polymethyl methacrylate, polyvinyl chloride, polyacetate resin, casting resin, acrylate, fluorinated ethylene propylene, polyvinyl fluoride and / or ethylene tetrafluoroethylene, or copolymers or mixtures thereof.

[0099] The thermoplastic intermediate layer is preferably implemented as at least one thermoplastic composite film and contains or is made of polyvinyl butyral (PVB), particularly preferably polyvinyl butyral (PVB) and additives known to those skilled in the art, such as plasticizers. Preferably, the thermoplastic intermediate layer contains at least one plasticizer.

[0100] A plasticizer is a chemical compound that makes plastics softer, more flexible, smoother and / or more elastic. Plasticizers shift the thermoelastic range of plastics to lower temperatures, thereby making the plastic have greater desirable elastic properties in the temperature range of use. Preferred plasticizers are carboxylic acid esters, especially low volatility carboxylic acid esters, fats and oils, soft resins and camphor. Other plasticizers are preferably aliphatic diesters of tri- or tetraethylene glycol. Particularly preferably used as plasticizers are 3G7, 3G8 or 4G7, where the first digit indicates the number of ethylene glycol units and the last digit indicates the number of carbon atoms in the carboxylic acid part of the compound. Thus, 3G8 represents triethylene glycol-bis-(2-ethylhexanoate), in other words a compound of formula C4H9CH(CH2CH3)CO(OCH2CH2)3O2CCH(CH2CH3)C4H9.

[0101] Preferably, the PVB-based thermoplastic intermediate layer contains at least 3% by weight, preferably at least 5% by weight, particularly preferably at least 20% by weight, even more preferably at least 30% by weight and in particular at least 35% by weight of a plasticizer, which preferably contains or is made of triethylene glycol-bis-(2-ethylhexanoate).

[0102] The thermoplastic intermediate layer may be formed by a single film or by multiple films. The thermoplastic intermediate layer may be formed by one or multiple thermoplastic films arranged above and below each other, and the thickness of the thermoplastic intermediate layer is preferably 0.25 mm to 1 mm, typically 0.38 mm or 0.76 mm.

[0103] The thermoplastic interlayer may be a functional thermoplastic interlayer, in particular an interlayer having acoustic damping properties, an infrared reflective interlayer, an infrared absorbing interlayer, and / or an ultraviolet absorbing interlayer, for example a bandpass filter film that blocks a narrow band of visible light.

[0104] The invention further extends to a projection assembly comprising a composite pane according to the invention and an image display device associated with a reflective layer, the image display having an image display directed towards the reflective layer, the image being reflected by the reflective layer and the image then leaving the composite pane according to the invention, preferably via the inner face of the inner pane, where the area of ​​the reflective layer overlapping at least the first masking strip is illuminated by the image display device. If several reflective layers are arranged offset relative to one another in their extension, a corresponding number of image display devices may be provided.

[0105] In a particular embodiment of the invention, in addition to the area overlapping with the first masking strip, the reflective layer also extends over the area not overlapping with the first masking strip. In this case, the projection assembly includes a further image display device, the image of which is reflected by the reflective layer and then leaves the composite pane according to the invention via the inner surface of the inner pane, where the part of the reflective layer located in the area not overlapping with the first masking strip is illuminated by the further image display device. The advantage of this application is that a high-contrast reflected image can be obtained in the part where the reflective layer overlaps with the first masking strip. The image of the further image display device is preferably reflected in the area seen through the composite pane, thus forming a conventional head-up display image as used in vehicles.

[0106] In the context of the present invention, the expression "area not overlapping with the first masking strip" means that, in a perspective through the composite pane, this area does not overlap with the first masking strip.

[0107] According to a preferred embodiment of the projection assembly according to the invention, the image display, which may also be called a display, may be implemented as: liquid crystal display (LCD), thin film transistor display (TFT), light emitting diode display (LED), organic light emitting diode display (OLED), electroluminescent display (EL), micro LED display, etc., preferably an LCD display. Due to the high reflectivity of p-polarized light, energy-intensive projectors, such as those typically used in head-up display applications, are not necessary. The various aspects of the display described above and other similar energy-saving image display devices are sufficient. As a result, energy consumption and heat dissipation can be reduced.

[0108] In another preferred embodiment of the present invention, the projection assembly includes a field of view camera intended to capture the user's field of view, which interacts with the image display device and the composite pane, thereby allowing the user to visually optimally locate the image reflected through the reflective layer.

[0109] The field of view camera includes at least an eye camera and an infrared light source. The field of view camera operates on the principle of a "remote eye tracker". As a result, when the projection assembly according to the invention is installed in a vehicle, the field of view camera may be mounted in the dashboard area or on the composite pane. The infrared light source emits infrared light, which the eye camera detects via reflection on the user's eyeball, thus allowing the eye position to be tracked. The data thus obtained on the user's eye position may be evaluated and may lead to an adjustment of the orientation of the image display device. A change in the orientation of the image display device is determined by the user's eye position, which results in a change in the angle of reflection of the image on the reflective layer. The reflected image thus hits the user's eye at an improved angle, allowing a better visual perception of the image.

[0110] In another preferred embodiment of the invention, the projection assembly includes a functional element intended to detect the movements of the user's free hand and which interacts with the image display device, thereby making it possible to obtain information therefrom that can be used to control the image display device.

[0111] The functional elements may include one or more optical sensors capable of generating a 3D image of a defined area, from which, for example, movements, gestures or approaches can be detected and used to control and monitor the image display, which is made visually accessible to the user via reflection on a reflective layer. The functional elements are connected to an evaluation unit for detecting movements and / or the presence of human body parts.

[0112] In a particular embodiment of the invention, the optical sensor preferably emits and detects in a frequency range of at least 300 GHz, and particularly preferably in the infrared light frequency range. Infrared light systems for recognizing hand signals or gestures have already been extensively studied and are therefore particularly suitable for commercial use.

[0113] In a further particular embodiment of the invention, the optical sensor emits and detects preferably in a frequency range of at most 300 GHz. Lower frequency beams are particularly suitable for detecting movements and gestures because they are less susceptible to radiation contamination in the form of light rays in the visible or infrared range.

[0114] Alternatively, the functional element may include a number of capacitive sensors. The capacitive sensors form a switching area, which may be formed by a surface electrode or by an arrangement of two coupled electrodes. When an object approaches the capacitive switching area, the capacitance of the surface electrode to ground or the capacitance of the capacitor formed by the two coupled electrodes changes. The change in capacitance is measured by a circuit arrangement or by the sensor electronics, and a switching signal is activated if a threshold value is exceeded. The switching signal activated in this way may be used to operate an image display device electrically connected to the functional element. Movements at close ranges, preferably up to 15 cm, in particular up to 10 cm, can be particularly easily detected. By operating the different switching signals in a specific sequence, the direction of movement can also be detected. In this way, an image display, which is made visually accessible to a user via reflection on a reflective layer, can be controlled and monitored.

[0115] The functional element and / or the field of view camera are preferably mounted on the composite pane according to the invention, but may also be located within the composite pane, i.e. between the outer and inner panes. A location on the inner face of the outer pane and on the outer face of the inner pane is likewise possible. Alternatively, when the projection assembly according to the invention is installed in a vehicle, the functional element and / or the field of view camera are mounted in the dashboard area.

[0116] The present invention further extends to a method for manufacturing a composite pane according to the invention, said method comprising the steps of: (a) In a first step, an outer pane, an inner pane, and a thermoplastic intermediate layer are provided, where the outer pane and the inner pane each have an outer surface and an inner surface. (b) In a second step, a first masking strip is regionally placed on one of the exterior or interior surfaces of the inner or outer pane. (c) In the third step, a conductive coating is applied. (d) In a fourth step, a thermoplastic intermediate layer is disposed between the outer pane and the inner pane, thereby forming a layer stack with the inner surface of the outer pane facing the outer surface of the inner pane. The reflective layer is always spatially disposed in front of the first masking strip when viewed from the inner pane towards the outer pane, and the first masking strip overlaps the reflective layer in at least one area. The reflective layer is suitably designed to reflect light. (e) In the fifth step, the ply stack is laminated to form a composite pane.

[0117] These steps are preferably performed in the order ((a)-(d)) above. However, the second and third steps may be performed in a different order.

[0118] The layer stack is laminated under the action of heat, vacuum and / or pressure, where the individual layers are joined (laminated) to one another by at least one thermoplastic intermediate layer. Methods known per se may be used to manufacture the composite pane. For example, the so-called autoclave process may be carried out at a high pressure of about 10 bar to 15 bar and at a temperature of 130° C. to 145° C. for approximately 2 hours. The vacuum bag or vacuum ring process known per se operates, for example, at approximately 200 mbar and at 130° C. to 145° C. The outer pane, the inner pane and the thermoplastic intermediate layer may be pressed in a calender between at least one pair of rollers to form the composite pane. Installations of this type for manufacturing composite panes are known and usually have at least one heating tunnel upstream from the press. The temperature during the pressing operation is, for example, between 40° C. and 150° C. The combination of calendering and autoclave processes has proven to be particularly useful in practice. Alternatively, a vacuum laminator may be used. These consist of one or more heatable and evacuable chambers in which the outer and inner panes may be laminated, for example, under reduced pressure of 0.01 mbar to 800 mbar, at temperatures of 80° C. to 170° C., for up to about 60 minutes.

[0119] The invention further extends to the use of a composite pane according to the invention in a means of transport for travelling on land, air or water, in particular in a motor vehicle, in which case the composite pane may be used, for example, as a windscreen, rear window, side window and / or glass roof, preferably as a windscreen. Preferably, the composite pane is used as a windscreen for the vehicle.

[0120] The various embodiments of the invention may be implemented individually or in any combination. In particular, the features described above and below may be used not only in the combinations shown, but also in other combinations or alone, without departing from the scope of the invention.

[0121] The invention will now be described in more detail by way of exemplary embodiments with reference to the accompanying drawings, in which: Figure 1 is a simplified representation and is not to scale;

[0122] FIG. 1A is a plan view of one embodiment of a composite pane according to the present invention. FIG. 1B is a cross-sectional view of a projection assembly according to the present invention having the composite pane of FIG. FIG. 2 is another cross-sectional view of a projection assembly according to the present invention having a composite pane. FIG. 3 is a plan view of a further embodiment of a composite pane according to the present invention. FIG. 4 is a plan view of a further embodiment of a composite pane according to the present invention. FIG. 5 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. FIG. 6 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. FIG. 7 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. FIG. 8 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. FIG. 9 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention. FIG. 10 is an enlarged cross-sectional view of various embodiments of a projection assembly according to the present invention.

[0123] Figure 1A shows a plan view, in a highly simplified schematic representation, of an embodiment of a composite pane 1 according to the invention in a vehicle. Figure 1B shows a cross-sectional view of the exemplary embodiment of Figure 1A in a projection assembly 100. The cross-sectional view of Figure 1B corresponds to the section line A-A' of the composite pane 1 as shown in Figure 1A.

[0124] The composite pane 1 is implemented in the form of a composite pane (see Figures 5 to 10) and has an outer pane 2 and an inner pane 3 with a thermoplastic intermediate layer 4 disposed between the outer pane 2 and the inner pane 3. The composite pane 1 is installed, for example, in a vehicle and separates the vehicle interior 14 from the external environment 15. The composite pane 1 is, for example, the windshield of an automobile.

[0125] The outer and inner panes 2, 3 are each made of glass, preferably heat-strengthened soda-lime glass, and are transparent to visible light. The thermoplastic interlayer 4 is made of a thermoplastic, preferably polyvinyl butyral (PVB), ethylene vinyl acetate (EVA), and / or polyethylene terephthalate (PET).

[0126] The outer surface I of the outer pane 2 faces away from the thermoplastic intermediate layer 4 and is also the outer surface of the composite pane 1. The inner surface II of the outer pane 2 and the outer surface III of the inner pane 3 each face the intermediate layer 4. The inner surface IV of the inner pane 3 faces away from the thermoplastic intermediate layer 4 and is also the inner surface of the composite pane 1. It goes without saying that the composite pane 1 may have any suitable geometric shape and / or curvature. As a composite pane 1, it typically has a convex curvature. Also, the composite pane 1 has an upper edge located at the top in the installed state and a lower edge located at the bottom in the installed state, as well as side edges located on the left and right.

[0127] In the end region 13 of the composite pane 1, in the frame-like circumferential direction, a first masking strip 5 is present on the inner face II of the outer pane 2. The first masking strip 5 is opaque and prevents the visibility of structures arranged on the inside of the composite pane 1, for example adhesive beads for gluing the composite pane 1 into the vehicle body. The first masking strip 5 is preferably black in colour. The first masking strip 5 is made of a non-conductive material conventionally used for masking strips, for example a fired black screen printing ink.

[0128] Furthermore, as shown in FIG. 1B, the composite pane 1 has a second masking strip 6 in an edge region 13 on the inner side IV of the inner pane 3. The second masking strip 6 is implemented in a circumferential frame-like manner. Like the first masking strip 5, the second masking strip 6 is made of a non-conductive material conventionally used for masking strips, for example a fired black screen printing ink.

[0129] In the central region of the composite pane 1, a conductive coating 10 is present on the inner surface II of the outer pane 2. In the plan view of the composite pane 1, the conductive coating 10 is located approximately within the circumferential frame formed by the first masking strip 5. However, beyond this, and different from what is shown here, the conductive coating 10 may be applied regionally or completely on the first masking strip 5 or on the inner surface II of the outer pane 2. The conductive coating 10 is transparent and does not impede or only slightly impedes the view through the composite pane 1. The edge regions 13 of the composite pane 1 are not coated with the conductive coating 10, which serves as an electrical insulation between the conductive coating 10 and the vehicle body.

[0130] Alternatively, the conductive coating 10 may be arranged on the outer face III of the inner pane 3, in the central region.

[0131] As shown in Fig. 1A, a first busbar 11 is arranged in the left edge region and another, a second busbar 11' is arranged in the right edge region, respectively, on the conductive coating 10 (not visible in Fig. 1B) for electrical contact of the conductive coating 10. The busbars 11, 11' contain, for example, silver particles and are applied by screen printing and then fired. The length of the busbars 11, 11' corresponds approximately to the extent of the conductive coating 10 along the lateral edges of the composite pane 1.

[0132] When a voltage is applied to the busbars 11, 11', a uniform current flows in the conductive coating 10 between the busbars 11, 11'. On each busbar 11, 11', a connection to a supply line may be located approximately centrally (not shown here). This connection may be electrically connected to the busbars via a contact surface. Via an electrical connection, the busbars 11, 11' are for example connected to a voltage source, which supplies the on-board voltage customary in motor vehicles, preferably 12V to 15V, for example about 14V. Alternatively, the 14V voltage source may have a higher voltage, for example 35V to 45V, in particular 42V. The conductive coating 10 is for example a layer system, which contains for example three conductive silver layers, which are separated from each other by a dielectric layer. When a current flows through the conductive coating 10, it is heated by its electrical resistance and the generation of Joule heat. This heat may be used to protect the composite pane 1 against icing or fogging.

[0133] As an alternative to this embodiment as well as the embodiment in Figures 3 and 4, the conductive coating 10 and, if present, the bus bars 11, 11' may be arranged on the outer surface III of the inner pane 3 in a manner similar to the example depicted here.

[0134] On the first masking strip 5 there is a reflective layer 9 deposited by a PVD method. When viewed through the composite pane 1, the reflective layer 9 does not overlap the second masking strip 6. The reflective layer 9 is for example a metal coating comprising at least one thin layer stack with at least one silver layer and one dielectric layer. Alternatively, the reflective layer 9 may be implemented as a reflective film and may be arranged on the first masking strip 5, for example by means of an adhesive layer. The reflective film may comprise a metal coating, or it may consist of a dielectric polymer layer in a layer sequence. Combinations of these variants are also possible.

[0135] When viewed through the composite pane 1, the reflective layer 9 is arranged overlapping the first masking strip 5, which in turn completely overlaps the reflective layer 9. That is to say, the reflective layer 9 has no portion that does not overlap the first masking strip 5. Here, the reflective layer 9 is arranged, for example, only in the lower (engine side) portion 13' of the edge region 13 of the composite pane 1. However, the reflective layer 9 could also be arranged in the upper (roof side) portion 13'' or in a lateral portion of the edge region 13. Furthermore, multiple reflective layers 9 may be provided, for example arranged in the lower (engine side) portion 13' and in the upper (roof side) portion 13'' of the edge region 13. For example, the reflective layer 9 may be arranged such that a (partial) perimeter image is generated.

[0136] The first masking strip 5 is wider in the lower (engine side) portion 13' of the edge region 13, i.e. the first masking strip 5 has a greater width in the lower (engine side) portion 13' of the edge region 13 than in the upper (roof side) portion 13'' of the edge region 13 of the composite pane 1. By "width" is meant the dimension of the first masking strip 5 perpendicular to its extension. Here, the second masking strip 6 is not arranged wider in the lower (engine side) portion 13' (i.e. it does not overlap the reflective layer 9).

[0137] The projection assembly 100 further comprises an image display device 8 arranged in the dashboard 7 as an image generating device. The image display device 8 is used to generate light 12 (image information), which is directed to the reflective layer 9 and reflected by the reflective layer 9 as reflected light 12' into the vehicle interior 14, which can be seen by an observer, for example the driver. The reflective layer 9 is suitably implemented to reflect the light 12 of the image display device 8, i.e. the image from the image display device 8. The light 12 of the image display device 8 preferably strikes the composite pane 1 at an incidence angle of 50°-80°, in particular 60°-70°, typically about 65°, which remains conventional for HUD projection assemblies. For example, the image display device 8 could also be arranged in the A-pillar or on the roof of a car (in either case inside the vehicle interior), provided that the reflective layer 9 is suitably arranged for this purpose. When multiple reflective layers 9 are provided, a separate image display device 8 may be associated with each reflective layer 9, i.e. multiple image display devices 8 may be arranged. The image display device 8 is, for example, a display such as an LCD display, an OLED display, an EL display, or a μLED display. Also, for example, the composite pane 1 could be a roof panel, a side window, or a rear window of a vehicle.

[0138] Since the variant shown in FIG. 2 essentially corresponds to the variant in FIGS. 1A and 1B, only the differences will be discussed here and otherwise reference is made to the description regarding FIGS. 1A and 1B.

[0139] Unlike what is shown in Figures 1A and 1B, the reflective layer 9 overlaps the entire inner surface II of the outer pane 2 when viewed through the composite pane 1. Thus, when viewed through the composite pane 1, the reflective layer 9 completely overlaps the first masking strip 5 and the conductive coating 10. The reflective layer 9 is deposited on the first masking strip 5 and the conductive coating 10, for example by means of a PVD method. However, it is equally possible (not shown in Figure 2) to apply the reflective layer 9 entirely on the inner surface II, IV of the inner or outer pane 2, 3 or on the outer surface III of the inner pane 3. As a result of the fact that the reflective layer 9 extends over the entire inner surface II of the outer pane 2, not only the area overlapping the first masking strip 5 can be used to reflect an image. Other image display devices may also be used, for example other image display devices that illuminate the areas of the reflective layer 9 that do not overlap the first masking strip 5. In this way, the functionality of a head-up display can be utilized.

[0140] Since the variant depicted in FIGS. 3 and 4 essentially corresponds to the variant in FIGS. 1A and 1B, only the differences will be discussed here and otherwise reference is made to the description regarding FIGS. 1A and 1B.

[0141] 1A, in FIG 3 the busbars 11, 11' in this variant are not disposed along the edge regions of the conductive coating 10 that extend along the lateral edges of the composite pane 1, but instead are disposed in the lower and upper edge regions along the lower and upper edges of the composite pane 1. The length of the busbars 11, 11' corresponds approximately to the extent of the conductive coating 10 along the lower or upper edge of the composite pane 1.

[0142] 4, the conductive coating 10 is not electrically contacted by the busbars 11, 11'. In this exemplary embodiment, the coating 10 is not used to heat the entire composite pane 1, but rather the IR reflective properties of the coating 10 are used, for example, to protect the interior of the vehicle from solar radiation and to keep it cool.

[0143] 5-10, there are shown enlarged cross-sectional views of various embodiments of the composite pane 1. The cross-sectional views of Figures 5-10 correspond to section line A-A' at the lower portion 13' of the edge region 13 of the composite pane 1, as shown in Figure 1B.

[0144] In the variant of the composite pane 1 shown in FIG. 5, a first (opaque) masking strip 5 is located on the inner surface II of the outer pane 2. A reflective layer 9 is applied directly on the first masking strip 5. Light 12 from the image display device 8 is reflected by the reflective layer 9 into the vehicle interior 14 as reflected light 12'. The light 12, 12' may have s-polarization and / or p-polarization. Since the angle of incidence of the light 12 on the composite pane 1 is close to the Brewster angle, the p-polarized portion of the light 12 is hardly hindered in transmission through the inner pane 3. This variant has the advantage that a relatively large proportion of the incident p-polarized light 12 is reflected. And, due to the fact that the angle of incidence is equal to the angle of reflection (indicated by α in FIGS. 5-10), this variant has the advantage that a relatively large proportion of the incident p-polarized light 12 is transmitted almost unhindered through the inner pane 3 into the vehicle interior 14. Moreover, the image is easily recognizable with high contrast against the background of the (opaque) first masking layer 5. The angle of incidence α of the light 12 of the image display device 8 on the inner surface IV of the inner pane 3 is, for example, 68°.

[0145] Since the variants shown in Figures 6 to 10 essentially correspond to the variants in Figures 1A, 1B, and 5, only the differences will be described here, and otherwise reference will be made to the descriptions regarding Figures 1A, 1B, and 5.

[0146] Different from what is shown in figure 5, in figure 6 the reflective layer 9 is not applied on the first masking strip 5 but instead on the inner face IV of the inner pane 3. This variant has the advantage that the incident light 12 is not hindered by transmission through the inner pane 3. Moreover, it is also preferred for light 12 with a high s-polarized component, since there is less double image due to reflection on the inner pane 3.

[0147] Unlike what is shown in figure 5, in figure 7 the reflective layer 9 is not applied onto the first masking strip 5, but instead onto the outer face III of the inner pane 3. This variant is particularly suitable when the first masking strip 5 cannot be coated with the reflective layer 9 or when a two-step application of the first masking strip 5 and the second reflective layer 9 is not suitable.

[0148] The variant of the composite pane 1 shown in Figure 8 differs from that of Figure 5 in that the reflective layer 9 is implemented as a reflective film that reflects light 12 into the vehicle interior 14. This variant represents a viable alternative to the reflective layer 9 shown in Figures 5, 6 and 7, which is deposited on the masking strip 5 using, for example, a PVD method.

[0149] As a further difference with the variant of FIG. 5, the reflective layer 9 in FIG. 8 is laminated between two thermoplastic interlayers 4', 4'' (e.g. PVB film) in the composite pane 1. To compensate for the height difference (thickness jump) caused by the reflective layer 9 with respect to the rest of the composite pane 1, it is advantageous for the thermoplastic interlayer 4, 4' to have a correspondingly smaller thickness than outside its area (where the reflective layer 9 is not provided). In this way, a uniform distance (i.e. a constant total thickness) between the outer pane 2 and the inner pane 3 can be achieved, reliably and safely avoiding any glass breakage during lamination. Also, the first masking strip 5 is not arranged on the inner face II of the outer pane 2, but rather on the outer face I of the outer pane 2. For example, when using a PVB film, the PVB film has a smaller thickness in the area of ​​the reflective layer 9 than in the area where the reflective layer 9 is not provided. Moreover, the image is easily recognizable with a high contrast against the background of the opaque (first) masking layer 5. Inside the composite pane 1, the reflective layer 9 is well protected from external influences.

[0150] The variant of the composite pane 1 shown in Figure 9 differs from the variant of Figure 8 only in that a first (opaque) masking strip 5 is implemented as a thermoplastic interlayer impermeable to light, which is arranged on the inner face II of the outer pane 2. The first masking strip 5 is for example made on the basis of a pigmented PVB, EVA or PET film. In this case, a reflective layer 9 is laminated between the thermoplastic interlayer 4 and the first masking strip 5.

[0151] The variant of the composite pane 1 shown in Figure 10 differs from the variant of Figure 5 only in that a high refractive index coating 14 is arranged on the inner face IV of the inner pane 3. The high refractive index coating 14 is applied, for example, by a sol-gel method and consists of a titanium oxide coating. The high refractive index of the high refractive index coating 14 compared to the inner pane 3 (for example 1.7) makes it possible to modify the Brewster angle, which is usually about 56.5° (for soda-lime glass), thus simplifying the application and reducing the disturbing double image effects due to reflections at the inner face IV of the inner pane 3.

[0152] In all exemplary embodiments, the reflective layer 9 is positioned towards the vehicle interior relative to the first masking strip 5, i.e., when viewed from the inner face of the composite pane 1, the reflective layer 9 is positioned in front of the first masking strip 5.

[0153] From the above, it follows that the present invention makes available an improved composite pane for projection assemblies, which allows good image display with high contrast. Undesirable secondary images are avoided. By using a conductive coating together with the composite pane, the space in the dashboard area can be significantly reduced when installed in the vehicle, allowing for a slim design of the interior of the vehicle. By displaying the image through a reflective layer in front of a masking strip, the displays that are usually mounted in the dashboard with the speedometer, tachometer, warning indicators and fuel gauge can be replaced. The heating of the composite pane by the conductive layer replaces the supply lines that normally direct the air heated by the engine heat to the windshield. Furthermore, an additional degree of geometric freedom is provided in the design of the interior of the vehicle, when the exhaust nozzle, which is usually mounted in a specific geometric relationship to the glazing, is omitted. The composite pane according to the present invention can be manufactured simply and economically using known manufacturing methods. The present disclosure includes the following aspects. <Aspect 1> A composite pane (1), in particular for a projection assembly (100), comprising at least: - an outer pane (2), an inner pane (3) and a thermoplastic intermediate layer (4) arranged between said outer pane and said inner pane (2, 3), wherein said outer pane and said inner pane (2, 3) respectively have outer surfaces (I, III) and inner surfaces (II, IV), said inner surface (II) of said outer pane (2) and said outer surface (III) of said inner pane (3) facing each other; a first masking strip (5) arranged regionally on one of the outer faces (I, III) or the inner faces (II, IV) of the inner or outer pane (2, 3); - a conductive coating (10), as well as - a reflective layer (9) suitable for reflecting light (12), Here, the reflective layer (9) is spatially positioned in front of the first masking strip (5) when viewed from the inner pane (3) towards the outer pane (2), and wherein the first masking strip (5) overlaps with the reflective layer (9) in at least one area. <Aspect 2> 2. The composite pane (1) of claim 1, wherein the reflective layer (9) is disposed on the outer surface (III) of the inner pane (3) or on one of the inner surfaces (II, IV) of the inner pane or the outer pane (2, 3), within the thermoplastic intermediate layer (4), or on the first masking strip (5), the first masking strip (5) having a larger surface area than the reflective layer (9) and completely overlapping the reflective layer (9). <Aspect 3> A composite pane (1) according to aspect 1 or 2, wherein the first masking strip (5) is arranged in a circumferential frame-like manner in the edge region of the outer pane (2), in particular having a width in a portion (13') overlapping the reflective layer (9) that is greater than its width in a portion (13'') other than the portion. <Aspect 4> A composite pane (1) according to any of aspects 1 to 3, wherein the first masking strip (5) is implemented as an opaque thermoplastic composite film and is arranged on the inner surface (II) of the outer pane (2). <Aspect 5> 5. A composite pane (1) according to any of the preceding claims, wherein the reflective layer (9) is implemented as a coated carrier film or an uncoated polymer film and is disposed within the thermoplastic intermediate layer (4). <Aspect 6> 6. The composite pane (1) of any of aspects 1-5, wherein a high refractive index coating (16) having a refractive index of at least 1.7 is disposed on at least the inner surface (IV) of the inner pane (3) in the area overlapping with the reflective layer (9), and the reflective layer (9) is disposed spatially closer to the outer surface (I) of the outer pane (2) and spatially farther from the inner surface (IV) of the inner pane (3) than the high refractive index coating (16). <Aspect 7> 7. The composite pane (1) according to embodiment 6, wherein the high refractive index coating (16) has a refractive index of at least 1.9, preferably at least 2.0. <Aspect 8> The conductive coating (10) may be made of silver (Ag), indium tin oxide (ITO), fluorine doped tin oxide (SnO 2 8. The composite pane (1) according to any one of the preceding aspects, comprising: <Aspect 9> A composite pane (1) according to any of the preceding aspects, wherein the conductive coating (10) is connected in an edge region of the outer or inner pane to two busbars (11, 11') provided for connection to a voltage source, whereby a current path for the heating current is formed between the busbars (11, 11'). <Aspect 10> 10. A composite pane (1) according to any of the preceding aspects 1 to 9, wherein the conductive coating (10) is arranged on the entire inner surface (II) of the outer pane (2) or the entire outer surface (III) of the inner pane (3), excluding the peripheral regions of the outer pane or the inner pane (2, 3), preferably with a width of 5 mm to 100 mm, particularly preferably 10 mm to 50 mm. <Aspect 11> A projection assembly (100) including: - a composite pane (1) according to any one of aspects 1 to 10; - an image display device (8) having an image display associated with and directed towards said reflective layer (9), the image being reflected by said reflective layer (9), wherein at least the area of ​​said reflective layer (9) overlapping with said first masking strip (5) is illuminated by said image display device (8). <Aspect 12> A projection assembly (100) as described in embodiment 11, further comprising a field of view camera, which is intended to capture a user's field of view and interacts with the image display device (8) and the composite pane (1), thereby enabling the user to optimally visually capture the image reflected through the reflective layer (9). <Aspect 13> A projection assembly (100) as described in aspect 11 or 12, further comprising a functional element intended to recognize the user's free hand movements and interacting with the image display device (8), thereby obtaining information from the user's free hand movements that can be used to control the image display device (8). <Aspect 14> A method for producing a composite pane (1) according to any one of aspects 1 to 10, comprising the steps of: (a) providing said outer pane (2), said inner pane (3) and said thermoplastic intermediate layer (4); (b) disposing the first masking strip (5) regionally on one of the outer faces (I, III) or the inner faces (II, IV) of the inner pane (3) or the outer pane (2); (c) introducing said conductive coating (10); (d) disposing said thermoplastic intermediate layer (4) between said outer pane (2) and said inner pane (3), thereby forming a layer stack; (e) laminating the ply stack to form a composite pane (1); A method comprising: <Aspect 15> Use of the composite pane (1) according to any of the aspects 1 to 10 in a vehicle for travelling on land, air or water, in particular as a windscreen for the vehicle. [Explanation of symbols]

[0154] 1. Composite pane 2 Outer Pane 3 Inner Pane 4, 4', 4'' Thermoplastic Interlayer 5 First Masking Strip 6 Second Masking Strip 7. Dashboard 8 Image display devices 9 Reflective layer 10 Conductive Coating 11, 11' busbar 12, 12' light 13, 13', 13'' edge area 14 Inside the vehicle 15 External environment 16 High refractive index coating 100 Projection Assembly

[0155] I Outer surface of outer pane 2 II. Inner surface of outer pane 2 III. Outer surface of inner pane 3 IV Inner surface of inner pane 3 A-A' section line

Claims

1. A composite pane (1), in particular for a projection assembly (100), comprising at least: an outer pane (2), an inner pane (3) and a thermoplastic intermediate layer (4) arranged between said outer pane and said inner pane (2, 3), wherein said outer pane and said inner pane (2, 3) respectively have an outer surface (I, III) and an inner surface (II, IV), said inner surface (II) of said outer pane (2) and said outer surface (III) of said inner pane (3) facing each other; a first masking strip (5) arranged regionally on one of the outer faces (I, III) or the inner faces (II, IV) of the inner or outer pane (2, 3); - a conductive coating (10), as well as a reflective layer (9) suitable for reflecting light (12), wherein the reflective layer (9) is spatially arranged in front of the first masking strip (5) when viewed from the inner pane (3) towards the outer pane (2), and wherein the first masking strip (5) overlaps the reflective layer (9) in at least one area; Here, at least a portion of the reflective layer (9) is disposed directly on the conductive coating (10).

2. 2. A composite pane (1) according to claim 1, wherein the reflective layer (9) is arranged on the outer surface (III) of the inner pane (3) or on one of the inner or outer panes (2, 3) on the inner surface (II, IV), in the thermoplastic intermediate layer (4) or on the first masking strip (5), the first masking strip (5) having a larger surface area than the reflective layer (9) and completely overlapping the reflective layer (9).

3. 3. A composite pane (1) according to claim 1 or 2, wherein the first masking strip (5) is arranged in a circumferential frame-like manner in the edge region of the outer pane (2), in particular having a width in the portion (13') overlapping the reflective layer (9) that is greater than its width in the other portion (13'').

4. A composite pane (1) according to any one of claims 1 to 3, wherein the first masking strip (5) is implemented as an opaque thermoplastic composite film and is arranged on the inner face (II) of the outer pane (2).

5. 5. A composite pane (1) according to any one of claims 1 to 4, wherein the reflective layer (9) is implemented as a coated carrier film or an uncoated polymer film and is arranged within the thermoplastic intermediate layer (4).

6. 6. A composite pane (1) according to any one of claims 1 to 5, wherein a high refractive index coating (16) having a refractive index of at least 1.7 is disposed on at least the inner surface (IV) of the inner pane (3) in the area overlapping with the reflective layer (9), the reflective layer (9) being disposed spatially closer to the outer surface (I) of the outer pane (2) and spatially further from the inner surface (IV) of the inner pane (3) than the high refractive index coating (16).

7. 7. Composite pane (1) according to claim 6, wherein said high refractive index coating (16) has a refractive index of at least 1.9, preferably at least 2.

0.

8. 8. A composite pane (1) according to any one of the preceding claims, wherein the conductive coating (10) comprises silver (Ag), indium tin oxide (ITO), fluorine doped tin oxide (SnO2:F), or aluminium doped zinc oxide (ZnO:Al).

9. A composite pane (1) according to any one of the preceding claims, wherein the electrically conductive coating (10) is connected in an edge region of the outer or inner pane to two busbars (11, 11') provided for connection to a voltage source, whereby a current path for the heating current is formed between the busbars (11, 11').

10. 10. A composite pane (1) according to any one of the preceding claims, wherein the conductive coating (10) is arranged on the entire inner side (II) of the outer pane (2) or the entire outer side (III) of the inner pane (3), except for the peripheral areas of the outer or inner panes (2, 3), preferably with a width of 5 mm to 100 mm, particularly preferably 10 mm to 50 mm.

11. A projection assembly (100) comprising: - a composite pane (1) according to any one of claims 1 to 10, an image display device (8) having an image display associated with and directed towards said reflective layer (9), the image being reflected by said reflective layer (9), wherein at least the area of ​​said reflective layer (9) overlapping with said first masking strip (5) is illuminated by said image display device (8).

12. 12. The projection assembly (100) of claim 11, further comprising a field of view camera, intended to capture a user's field of view and interacting with the image display device (8) and the composite pane (1), thereby allowing the user to optimally visually capture an image reflected through the reflective layer (9).

13. A projection assembly (100) as described in claim 11 or 12, further comprising a functional element intended to recognize the movements of a user's free hand and interacting with the image display device (8), thereby making it possible to obtain information from the movements of the user's free hand that can be used to control the image display device (8).

14. A method for manufacturing a composite pane (1) according to any one of claims 1 to 10, comprising the steps of: (a) providing said outer pane (2), said inner pane (3) and said thermoplastic intermediate layer (4); (b) disposing said first masking strip (5) regionally on one of said outer faces (I, III) or said inner faces (II, IV) of said inner pane (3) or said outer pane (2); (c) introducing said conductive coating (10); (d) disposing said thermoplastic intermediate layer (4) between said outer pane (2) and said inner pane (3), thereby forming a layer stack; (e) laminating the layer stack to form a composite pane (1); A method comprising:

15. Use of a composite pane (1) according to any one of claims 1 to 10 in a vehicle moving on land, in the air or on water, in particular as a windscreen for the vehicle.