Resin container manufacturing method, manufacturing device, and mold unit

Abstract

This manufacturing method for a resin container comprises: a first injection molding step in which a first layer of a bottomed tubular preform is injection-molded using a first resin material; a second injection molding step in which a second resin material having a color different from the first resin material is injected, and a second layer is laminated on the outer peripheral side or inner peripheral side of the first layer; and a blow molding step in which a multi-layered preform obtained in the second injection molding step is blow-molded while retention heat during injection molding is held, and a resin container having a color pattern according to the thickness distribution of the first layer and the second layer is produced.

Description

[Technical field]

[0001] The present invention relates to a method, an apparatus, and a mold unit for manufacturing a resin container. [Background technology]

[0002] Containers for cosmetics, lotions, etc., are required to have an aesthetically pleasing appearance in order to increase consumer purchasing power. Glass bottles, which have a heavy and luxurious feel and can maintain their beauty even after repeated use, are preferred for containers for storing cosmetics of this kind. In addition, in order to improve the aesthetic appearance of the container, there is a demand for containers for storing cosmetics, etc., to have a gradation pattern with varying shades of color.

[0003] However, glass bottles are heavy and easily broken, and the costs of transportation and manufacturing are high. For this reason, the replacement of glass bottles with plastic containers for storing cosmetics and the like has been considered.

[0004] As one of the methods for manufacturing resin containers, the hot parison type blow molding method has been conventionally known. In the hot parison type blow molding method, the resin container is blow molded by utilizing the heat retained during the injection molding of the preform. Therefore, compared with the cold parison type, the hot parison type blow molding method has the advantage that it can manufacture a variety of resin containers with excellent aesthetic appearance.

[0005] Furthermore, the following methods have been proposed for forming a gradation pattern on a resin container: For example, Patent Document 1 discloses a technique in which colored and transparent outer shell pieces with different thickness distributions are fitted to inner shell pieces to form a multi-layer preform, and a gradation pattern is formed on the blow-molded container according to the thickness distribution of the outer shell pieces.

[0006] For example, Patent Document 2 discloses a technique for forming a multi-layer preform by simultaneously injection molding multiple types of resin materials by co-extrusion, and forming a gradation pattern on the container after blow molding. In the technique of Patent Document 2, the amount of resin material extruded during injection molding is controlled to produce the thickness changes of each layer required for the gradation pattern. [Prior art documents] [Patent documents]

[0007] [Patent Document 1] Special Publication No. 61-59984 [Patent Document 2] International Publication No. 2004 / 022307 Summary of the Invention [Problem to be solved by the invention]

[0008] In the technology of Patent Document 1, the two pieces cannot be fitted together to form a preform unless each piece is sufficiently cooled and has a certain degree of hardness. In other words, the technology of Patent Document 1 cannot be applied to hot parison blow molding methods, and it is not possible to complete the process from injection molding of the preform to blow molding of the container in a short period of time.

[0009] In addition, in the technology of Patent Document 2, it is actually very difficult to precisely control the thickness change in each layer of the preform by co-extrusion. Also, some types of patterns cannot be reproduced by co-extrusion. Therefore, in the technology of Patent Document 2, it is still difficult to stably form a desired color pattern on a container after blow molding.

[0010] The present invention has been made in consideration of these problems, and aims to provide a manufacturing method that can perform the processes from injection molding of a preform to blow molding of a container in a short cycle, and can stably form a desired color pattern by internal coloring of the blow-molded container. [Means for solving the problem]

[0011] A method for producing a resin container which is one embodiment of the present invention includes a first injection molding step of injection molding a first layer of a bottomed cylindrical preform into a first mold using a first resin material; a second injection molding step of housing the first layer in a second mold different from the first mold and injecting a second resin material having a color different from the first resin material into the second mold to laminate the second layer on the outer or inner side of the first layer to form a multi-layered preform having a thickness distribution in which the bottom is thicker than the body; and a blow molding step of blow molding the multi-layered preform obtained in the second injection molding step while retaining heat from the injection molding, to produce a resin container having a color pattern according to the thickness distribution of the first and second layers and having a thickness distribution in which the bottom is thicker than the body. The second mold includes a core mold that retains the shape of the first layer and a cavity mold facing the outer periphery of the first layer, and in the second injection molding process, the core mold is inserted into the inner periphery of the first layer and a second resin material is injected between the cavity mold and the first layer. Another embodiment of the present invention relates to a method for producing a resin container, the method comprising: a first injection molding step of injection molding a first layer of a bottomed cylindrical preform into a first mold using a first resin material; a second injection molding step of housing the first layer in a second mold different from the first mold and injecting a second resin material having a color different from the first resin material into the second mold to laminate the second layer on the outer or inner side of the first layer to form a multi-layered preform having a thickness distribution in which the bottom is thicker than the body; and a blow molding step of blow molding the multi-layered preform obtained in the second injection molding step while retaining heat from the injection molding, to produce a resin container having a color pattern according to the thickness distribution of the first and second layers and having a thickness distribution in which the bottom is thicker than the body. The second mold includes a core mold facing the inner periphery of the first layer and a cavity mold that maintains the shape of the first layer, and in the second injection molding process, the cavity mold is positioned on the outer periphery of the first layer and a second resin material is injected between the core mold and the first layer. Effect of the Invention

[0012] According to one aspect of the present invention, the process from injection molding of a preform to blow molding of a container can be carried out in a short cycle, and a desired color pattern can be stably formed by interior coloring of the blow-molded container. [Brief description of the drawings]

[0013] [Figure 1] FIG. 2 is a longitudinal sectional view of a preform having a multi-layer structure according to the present embodiment. [Diagram 2] 1A and 1B are diagrams showing an example of a resin container according to an embodiment of the present invention. [Diagram 3] 1 is a diagram showing a schematic configuration of a blow molding device according to an embodiment of the present invention; [Figure 4] 1A to 1C are diagrams illustrating a manufacturing process of a preform according to a first example. [Diagram 5] 11A to 11C are diagrams illustrating a manufacturing process of a preform according to a second example. [Figure 6] 4 is a flow chart showing steps of a method for manufacturing a container. [Figure 7] FIG. 4 is an explanatory diagram of a first modified example of the present embodiment. [Figure 8] FIG. 11 is an explanatory diagram of a second modified example of the present embodiment. [Figure 9] FIG. 11 is an explanatory diagram of a third modified example of the present embodiment. [Figure 10] FIG. 11 is a diagram illustrating a schematic configuration of a blow molding device according to another embodiment. [Figure 11] 10 is a flowchart showing steps of a method for manufacturing a container in another embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] Hereinafter, an embodiment of the present invention will be described with reference to the drawings. In the embodiments, in order to make the description easier to understand, structures and elements other than the main parts of the present invention will be described in a simplified or omitted manner. In addition, in the drawings, the same elements are given the same reference numerals. Note that the shapes, dimensions, etc. of each element shown in the drawings are shown only for illustrative purposes, and do not represent the actual shapes, dimensions, etc.

[0015] <Example of preform configuration> First, with reference to FIG. 1, a configuration example of a preform having a multi-layer structure according to this embodiment will be described. FIG. 1(a) is a vertical cross-sectional view of a preform 10 of a first example of this embodiment, and FIG. 1(b) is a vertical cross-sectional view of a preform 10 of a second example of this embodiment.

[0016] The overall shape of the preforms 10 shown in Figures 1(a) and (b) is a bottomed cylindrical shape with one end open and the other end closed. These preforms 10 include a cylindrical body 14, a bottom 15 closing the other end of the body 14, and a neck 13 formed at the opening of one end of the body 14. These preforms also have a multi-layer structure in which a first layer 11 is laminated with a second layer 12. The first layer 11 and the second layer 12 are formed by two-stage injection molding as described below.

[0017] In the first example preform 10 shown in Figure 1 (a), a neck portion 13 is formed in a first layer 11 located on the inner circumference side, and a second layer 12 is laminated on the outer circumference side from a body portion 14 to a bottom portion 15 of this first layer 11.

[0018] 1(b), a neck portion 13 is formed in a first layer 11 located on the outer periphery side, and a second layer 12 is laminated on the inner periphery side from a body portion 14 to a bottom portion 15 of the first layer 11. In the preform 10 of the second example, a hole 16 is formed in the center of the bottom of the first layer 11, and the hole 16 of the first layer 11 is blocked from the inside by the second layer 12.

[0019] As shown in Figs. 1(a) and (b), these preforms 10 have a tapered region 17 in which the thickness of the second layer 12 gradually decreases in the axial direction from the bottom side to the neck side. For example, the tapered region 17 is formed in the upper part of the second layer 12 facing the neck side in the figure. In this tapered region 17, the thickness t2 of the second part of the second layer 12, which is closer to the neck 13 than the first part, is thinner than the thickness t1 of the first part of the second layer 12. The specifications such as the shapes and dimensions of the first layer 11 and the second layer 12 are appropriately adjusted depending on the shape of the container to be manufactured and the color pattern to be formed on the container.

[0020] Hereinafter, the resin material forming the first layer 11 will also be referred to as a first resin material, and the resin material forming the second layer 12 will also be referred to as a second resin material. Both the first resin material and the second resin material are thermoplastic synthetic resins and can be appropriately selected according to the specifications of the container. Specific types of materials include, for example, PET (polyethylene terephthalate), PEN (polyethylene naphthalate), PCTA (polycyclohexane dimethylene terephthalate), Tritan (Tritan (registered trademark): a copolyester manufactured by Eastman Chemical Co.), PP (polypropylene), PE (polyethylene), PC (polycarbonate), PES (polyethersulfone), PPSU (polyphenylsulfone), PS (polystyrene), COP / COC (cyclic olefin polymer), PMMA (polymethyl methacrylate: acrylic), PLA (polylactic acid), nylon, etc. Additives such as colorants can be added as appropriate to these resin materials.

[0021] In each of the preforms 10, resin materials of different colors are used for the first layer 11 and the second layer 12. For example, the first resin material and the second resin material differ in the amount of colorant (shade of color) or the type of colorant (type of color). It is not necessary to add a colorant to one of the first resin material and the second resin material. In addition, both or at least one of the first layer 11 and the second layer 12, for example, a layer having a portion facing the outer periphery, may have a property of transmitting light (translucency). The layer having translucency may be colored. In this embodiment, the first resin material is described as being transparent (having translucency).

[0022] The first and second resin materials can be appropriately combined according to the specifications of the container, but it is preferable to combine materials that are highly adhesive to each other. As an example, the first and second resin materials may be the same type of resin material but have different colorant compositions (e.g., PET).

[0023] <Examples of resin container configurations> Next, with reference to FIG. 2, a configuration example of the resin container (hereinafter also simply referred to as the container) according to this embodiment will be described.

[0024] Fig. 2(a) is a diagram showing an example of a container 20 obtained by blow molding the preform 10 of the first example, and Fig. 2(b) is a diagram showing an example of a container 20 obtained by blow molding the preform 10 of the second example. In each of Figs. 2(a) and (b), the right half of the figure shows the appearance of the container 20, and the left half of the figure shows a vertical cross section of the container 20.

[0025] 2(a) and (b) contains, for example, lotion, milky lotion, etc. Container 20 has a neck 21 with an opening at the top, a cylindrical body 22 continuing from neck 21, and a bottom 23 continuing from body 22.

[0026] In addition, three regions (first region 22a, middle region 22b, and second region 22c) are formed along the axial direction in the body 22 of the container 20, thereby creating a gradation pattern in which the color gradually changes in the axial direction. The decorative pattern improves the aesthetic appearance of the container 20, and can further increase consumer purchasing power when used as a cosmetic container or the like.

[0027] First, the first region 22a including the neck portion 21 and the upper portion of the body portion 22 is formed of the first layer 11. Therefore, the color of the first layer 11 appears in the neck portion 21 and the first region 22a of the body portion 22. On the other hand, the second region 22c including the bottom 23 and the lower part of the body 22 is formed by laminating the first layer 11 and the second layer 12. Therefore, in the second region 22c of the bottom 23 or the body 22, the color of the second layer 12 located on the outer periphery appears in Fig. 2(a), or the color of the second layer 12 on the inner layer side appears through the transparent first layer 11 in Fig. 2(b).

[0028] Between the first region 22a and the second region 22c, an intermediate region 22b is provided, which is formed by stretching the tapered region 17 of the preform 10. In this intermediate region 22b, the thickness of the second layer 12 gradually decreases from the bottom side to the neck side. Therefore, in the intermediate region 22b, the color gradually changes in the axial direction according to the thickness ratio of the first layer 11 and the second layer 12. Specifically, the ratio of the first layer 11 increases toward the neck side, so the intermediate region 22b has a color closer to the first region 22a. On the other hand, the ratio of the second layer 12 increases toward the bottom side, so the intermediate region 22b has a color closer to the second region 22c.

[0029] The thickness of the body 22 of the container 20 may be made considerably thinner than that of the bottom 23, and the body 22 may have a uniform thickness distribution. Giving the container 20 a shape with the above-mentioned thickness distribution emphasizes a sense of luxury and weight, and allows the container 20 to come closer to the image of a cosmetic container that consumers have in mind.

[0030] <Explanation of container manufacturing equipment> 3 is a diagram showing a schematic configuration of a blow molding apparatus according to the present embodiment. The blow molding apparatus 30 according to the present embodiment is an example of a container manufacturing apparatus, and employs a hot parison method (also called a one-stage method) in which the container 20 is blow molded by utilizing the heat (internal heat) retained during injection molding without cooling the preform 10 to room temperature.

[0031] Blow molding apparatus 30 includes first injection molding section 31, second injection molding section 32, temperature adjustment section 33, blow molding section 34, removal section 35, and conveying mechanism 36. First injection molding section 31, second injection molding section 32, temperature adjustment section 33, blow molding section 34, and removal section 35 are disposed at positions rotated a predetermined angle (e.g., 72 degrees) around conveying mechanism 36.

[0032] (Transport mechanism 36) The transport mechanism 36 includes a transfer plate (not shown in FIG. 3) that rotates around an axis perpendicular to the plane of the drawing in FIG. 3. A neck mold 36a (not shown in FIG. 3) that holds the neck 13 of the preform 10 (or the neck 21 of the container 20) is arranged on the transfer plate. When the transfer plate is composed of a single, approximately disk-shaped member, one or more neck molds 36a are arranged at each predetermined angle. When the transfer plate is composed of an approximately fan-shaped member divided into each molding section, one or more neck molds 36a are arranged on each of the divided transfer plates.

[0033] The conveying mechanism 36 rotates the transfer plate to convey the preform 10 (or the container 20) whose neck portion is held by the neck mold 36a to the first injection molding section 31, the second injection molding section 32, the temperature adjustment section 33, the blow molding section 34, and the removal section 35 in that order. Therefore, each of the neck molds 36a is shared by a plurality of molding stations (at least the first injection molding section 31 and the second injection molding section 32). In addition, a tapered section 36a1 is formed on the outer surface (or inner surface) of the neck mold 36a. The tapered section 36a1 comes into contact with or fits into the mold of each molding station, thereby regulating the relative positional relationship between the two during molding. The conveying mechanism 36 can also raise and lower the transfer plate, and also performs operations related to mold closing and mold opening (mold release) in the first injection molding section 31 and the second injection molding section 32.

[0034] (First injection molding section 31) The first injection molding section 31 is equipped with a first injection molding die consisting of a cavity mold 40, a core mold 41, and a hot runner mold 42, and produces the first layer 11 of the preform 10. A first injection device 37 that supplies a first resin material to the hot runner mold 42 is connected to the first injection molding section 31. The cavity mold 40 is equipped with a fitting portion (fitting concave and convex portion, position regulating portion) 40b on the surface opposite to the surface facing the hot runner mold 42 (see Figures 4(a), 5(a), and (b)). The fitting portion 40b has a tapered portion 40b1 that is approximately similar in shape to the tapered portion 36a1 of the neck mold 36a, and the neck mold 36a is equipped with a first injection device 37 that supplies a first resin material to the hot runner mold 42. The cavity mold 40 is equipped with a fitting portion (fitting concave and convex portion, position regulating portion) 40b on the surface opposite to the surface facing the hot runner mold 42 (see Figures 4(a), 5(a), and (b)). 36a The tapered portion 36a1 is received by the tapered portion 40b1.

[0035] Fig. 4(a) shows a first injection molding section 31a which molds the first layer 11 of the preform 10 of the first example (Fig. 1(a)). Figs. 5(a) and (b) show a first injection molding section 31b which molds the first layer 11 of the preform 10 of the second example (Fig. 1(b)). In this specification, when there is no need to distinguish between the first injection molding sections 31a and 31b, they will be collectively referred to as the first injection molding section 31.

[0036] As shown in Figures 4(a) and 5(a), in the first injection molding section 31, the above-mentioned cavity mold 40, core mold 41, and neck mold 36a of the conveying mechanism 36 are closed to form a mold space (molding space) for the first layer 11. A cavity mold 40 shown in Fig. 4(a) defines the outer peripheral shape of the inner layer (first layer 11) of the preform 10. A core mold 41 shown in Fig. 4(a) is inserted into the cavity mold 40 and defines the inner peripheral shape of the inner layer. 5(a) and (b) defines the outer peripheral shape of the outer layer (first layer 11) of the preform 10. A core mold 41 shown in Fig. 5(a) and (b) is inserted into the cavity mold 40 and defines the inner peripheral shape of the outer layer. Then, a first resin material is poured into the above-mentioned mold space from a first injection device 37 via a hot runner mold 42, whereby a first layer 11 of a preform 10 is produced in the first injection molding section 31.

[0037] 4(a), a region 40a that narrows toward the bottom side is formed at the body position of the cavity mold 40 of the first injection molding part 31a. Therefore, a region where the thickness changes in a tapered shape is formed on the outer periphery side of the first layer 11 formed by the first injection molding part 31a.

[0038] 5(b), in first injection molding section 31b, a valve pin 43 that is axially movable to a position adjacent to core mold 41 is provided inside hot runner mold 42. Valve pin 43 is housed inside hot runner mold 42 until the mold space is filled with the first resin material, and protrudes to a position adjacent to core mold 41 after the mold space is filled with the first resin material. By such movement of valve pin 43 during injection molding, a thin film portion 18 in which the resin material is thinner than the peripheral portion can be formed in the center of the bottom of first layer 11.

[0039] Furthermore, even when the first injection molding section 31 is opened, the neck mold 36a of the transport mechanism 36 is not opened, but continues to hold and transport the first layer 11 of the preform 10. The number of preforms 10 simultaneously molded in the first injection molding section 31 (i.e., the number of containers 20 that can be simultaneously molded by the blow molding device 30) can be set appropriately.

[0040] (Second injection molding section 32) The second injection molding section 32 is equipped with a second injection molding die consisting of a cavity mold 50, a core mold 51, and a hot runner mold 52, and injection molds the second layer 12 onto the outer or inner periphery of the first layer 11. A second injection device 38 that supplies a second resin material to the hot runner mold 52 is connected to the second injection molding section 32. The cavity mold 50 is also equipped with a fitting portion (position restriction portion) 50b on the surface opposite to the surface facing the hot runner mold 52 (see Figures 4(b) and 5(c)). The fitting portion 50b has a tapered portion 50b1 that is approximately similar in shape to the tapered portion 36a1 of the neck mold 36a, and the tapered portion 50b1 is formed in a shape similar to the tapered portion 36a1 of the neck mold 36a. 36a The tapered portion 36a1 is received by the tapered portion 50b1.

[0041] Fig. 4(b) shows a second injection molding section 32a which molds the second layer 12 of the preform 10 of the first example (Fig. 1(a)). Fig. 5(c) shows a second injection molding section 32b which molds the second layer 12 of the preform 10 of the second example (Fig. 1(b)). In this specification, when there is no need to distinguish between the second injection molding sections 32a and 32b, they will be collectively referred to as the second injection molding section 32.

[0042] The second injection molding section 32a accommodates the first layer 11 of the preform 10 injection molded in the first injection molding section 31a. As shown in Fig. 4(b), when the second injection molding section 32a is in a closed state, a mold space is formed between the inner surface of the cavity mold 50 and the outer circumferential side of the first layer 11 from the body to the bottom. The core mold 51 shown in Fig. 4(b) is inserted into the inner layer (first layer 11) of the preform 10 and holds the inner layer from the inside. The cavity mold 50 shown in Fig. 4(b) receives the inner layer into which the core mold 51 is inserted, and forms a mold space for the outer layer (second layer 12) between itself and the outer peripheral surface of the inner layer, thereby defining the outer peripheral shape of the outer layer. The second resin material is injected from the second injection device 38 through the hot runner mold 52 into the mold space, thereby forming a second layer 12 on the outer circumferential side of the first layer 11. In the second layer 12, a tapered region 17 is formed, the diameter of which increases toward the bottom side in relation to the thickness of the first layer 11. In this way, the preform 10 of the first example is manufactured.

[0043] The second injection molding section 32b accommodates the first layer 11 of the preform 10 injection molded in the first injection molding section 31b. As shown in Fig. 5(c), when the second injection molding section 32b is in a closed state, a mold space is formed between the inner periphery of the first layer 11 and the surface of the core mold 51 from the body to the bottom. A cavity mold 50 shown in Fig. 5(c) receives the outer layer (first layer 11) of the preform 10 and holds the outer layer from the outside. A core mold 51 shown in Fig. 5(c) is inserted inside the outer layer and forms a mold space for the inner layer (second layer 12) between itself and the inner peripheral surface of the outer layer, thereby defining the inner peripheral shape of the inner layer. The second resin material is injected from the second injection device 38 through the hot runner mold 52 into the above mold space, thereby forming the second layer 12 on the inner peripheral side of the first layer 11. In this way, the preform 10 of the second example is manufactured.

[0044] 5(c), a region 51a that narrows toward the bottom side is formed in the core mold 51 of the second injection molding part 32b. Therefore, a tapered region 17 where the thickness changes can be formed in the second layer 12 formed by the second injection molding part 32b.

[0045] (Temperature adjustment section 33) The temperature adjustment section 33 includes a temperature adjustment mold (temperature adjustment pot and temperature adjustment core) (not shown). The temperature adjustment section 33 accommodates the preform 10 transferred from the second injection molding section 32 in a temperature adjustment mold kept at a predetermined temperature, thereby equalizing the temperature and removing temperature deviation, and adjusts the temperature of the preform 10 to a temperature suitable for the final blow (for example, about 90°C to 105°C). The temperature adjustment section 33 also has a function of cooling the preform 10 in a high temperature state after injection molding. The temperature adjustment pot includes a fitting portion (position restriction portion) that can come into contact with and be fitted to the neck mold 36a, and the fitting portion has a tapered portion having a shape approximately similar to the tapered portion 36a1 of the neck mold 36a.

[0046] (Blow molding section 34) The blow molding section 34 performs blow molding on the preform 10 whose temperature has been adjusted in the temperature adjustment section 33 , to manufacture the container 20 . The blow molding section 34 is equipped with a blow molding die consisting of a blow cavity mold, which is a pair of split molds corresponding to the shape of the container 20, a bottom mold, a stretching rod, and an air introduction member (blow core, neither of which are shown). The blow molding section 34 blow molds the preform 10 while stretching it. As a result, the preform 10 is shaped into the shape of the blow cavity mold, and the container 20 can be manufactured. The pair of blow cavity molds are equipped with fitting portions (position regulating portions) that can come into contact with and fit into the neck mold 36a, and the fitting portions have a tapered portion that is approximately similar in shape to the tapered portion 36a1 of the neck mold 36a.

[0047] (Removal part 35) The removal section 35 is configured to release the neck 21 of the container 20 manufactured in the blow molding section 34 from the neck mold 36a and remove the container 20 to the outside of the blow molding apparatus 30. The removal section 35 includes a removal rod (a metal mold for removal) that is inserted from an opening of the neck mold 36a. The removal rod includes a fitting portion (position restriction portion) that can substantially come into contact with the neck mold 36a.

[0048] <Explanation of container manufacturing method> Next, a method for manufacturing a container using the blow molding apparatus 30 of this embodiment will be described. Fig. 6 is a flow chart showing the steps of the method for manufacturing a container.

[0049] (Step S101: First injection molding process) 4(a) and 5(a), in the first injection molding section 31, a first resin material is injected from a first injection device 37 into a mold space formed by a cavity mold 40, a core mold 41, and a neck mold 36a of a transport mechanism 36, to mold a first layer 11 of a preform 10. When forming the preform 10 of the first example, the first injection molding section 31a is used, and when forming the preform 10 of the second example, the first injection molding section 31b is used.

[0050] 5(b), after the first layer 11 of the preform 10 is molded in the first injection molding section 31b, a step of protruding the valve pin 43 to a position close to the core mold 41 is carried out. As a result, a thin film portion 18 having a thickness thinner than that of the peripheral portion is formed in the center of the bottom of the first layer 11.

[0051] Thereafter, when the first injection molding section 31 is opened, the transfer plate of the conveying mechanism 36 rotates a predetermined angle, and the first layer 11 of the preform 10 held in the neck mold 36a is conveyed to the second injection molding section 32 while retaining the heat retained during injection molding.

[0052] (Step S102: Second injection molding process) Next, the first layer 11 of the preform 10 is accommodated in the second injection molding section 32, and injection molding of the second layer 12 is performed. When forming the preform 10 of the first example, the second injection molding section 32a is used, and when forming the preform 10 of the second example, the second injection molding section 32b is used.

[0053] 4(b), in the second injection molding section 32a, a mold space is formed between the body and bottom of the outer periphery of the first layer 11 and a cavity mold 50 facing the outer periphery of the first layer 11. A second resin material is filled into the mold space from a hot runner mold 52.

[0054] 4(b), a core mold 51 is inserted into the inner periphery side of the first layer 11, and the shape of the first layer 11 is maintained from the inner periphery side by the core mold 51. Therefore, even if the second resin material comes into contact with the first layer 11, thermal deformation of the first layer 11 can be suppressed. When the preform 10 of the first example is molded in the above manner, the second layer 12 can be formed on the outer periphery side of the first layer 11.

[0055] On the other hand, in the second injection molding section 32b, as shown in Fig. 5(c), a mold space is formed between the body part on the inner periphery side of the first layer 11 and the core mold 51 facing the inner periphery of the first layer 11 from the bottom part. The second resin material is filled into the mold space from the hot runner mold 52. Note that a thin film part 18 is formed on the bottom part of the first layer 11, but the thin film part 18 is broken by the injection pressure of the second resin material to form a hole 16 on the bottom part, and the second resin material is guided from the hole 16 to the inner periphery side of the first layer 11.

[0056] 5(c), a cavity mold 50 faces the outer periphery side of the first layer 11, and the shape of the first layer 11 is maintained from the outer periphery side by the cavity mold 50. Therefore, even if the second resin material comes into contact with the first layer 11, thermal deformation of the first layer 11 can be suppressed. When molding the preform 10 of the second example in the above manner, the second layer 12 can be formed on the inner periphery side of the first layer 11.

[0057] In the second injection molding step, the first layer 11 has the heat retained during injection molding and is in a state where it is relatively easy to deform. Therefore, when the second resin material is injected into the mold space, the air present in the mold space is pushed upward and exhausted while slightly elastically deforming the first layer 11. Therefore, air is unlikely to accumulate during molding of the second layer 12, and molding defects of the preform 10 are suppressed.

[0058] As described above, the preform 10 of the first or second example is manufactured by the first injection molding step and the second injection molding step. Thereafter, when the second injection molding section 32 is opened, the transfer plate of the conveying mechanism 36 rotates a predetermined angle, and the preform 10 held in the neck mold 36a is conveyed to the temperature adjustment section 33 while retaining the heat retained during injection molding.

[0059] (Step S103: Temperature adjustment process) Next, in the temperature adjustment section 33, the preform 10 is accommodated in a mold unit for temperature adjustment, and temperature adjustment is performed to bring the temperature of the preform 10 close to a temperature suitable for the final blow. After that, the transfer plate of the conveying mechanism 36 rotates by a predetermined angle, and the temperature-adjusted preform 10 held in the neck mold 36a is conveyed to the blow molding section 34.

[0060] (Step S104: Blow molding process) Next, in the blow molding section 34, the container 20 is blow molded. First, the blow cavity mold is closed to accommodate the preform 10 in the mold space, and the air introduction member (blow core) is lowered to bring the air introduction member into contact with the neck portion 13 of the preform 10. Then, the stretch rod is lowered to hold the bottom portion 15 of the preform 10 from the inside, and while performing vertical axis stretching as necessary, blow air is supplied from the air introduction member to stretch the preform 10 in the horizontal direction. As a result, the preform 10 is shaped by expanding so as to be in close contact with the mold space of the blow cavity mold, and is blow molded into the container 20. Note that if the preform 10 is longer than the container 20, the bottom mold is made to wait at a lower position where it does not come into contact with the bottom portion of the preform 10 before the blow cavity mold is closed, and is quickly raised to the molding position after the mold is closed.

[0061] Moreover, in this embodiment, by blow molding the preform 10 of the first or second example, a container 20 is produced having a gradation pattern in which the color tone gradually changes in the axial direction due to the stretching of the first layer 11 and the second layer 12.

[0062] (Step S105: container removal process) Once the blow molding is complete, the blow cavity mold is opened, allowing the container 20 to be removed from the blow molding section 34. Next, the transfer plate of the transport mechanism 36 rotates a predetermined angle, and the container 20 is transported to the removal section 35. In the removal section 35, the neck portion 21 of the container 20 is released from the neck mold 36a, and the container 20 is removed to the outside of the blow molding apparatus 30.

[0063] This completes one cycle in the method for manufacturing containers. Thereafter, the transfer plate of the conveying mechanism 36 is rotated by a predetermined angle to repeat the above steps S101 to S105. During operation of the blow molding apparatus 30, five sets of containers are manufactured in parallel, with a time difference between each step.

[0064] In addition, due to the structure of the blow molding apparatus 30, the times for the first injection molding process, the second injection molding process, the temperature adjustment process, the blow molding process, and the container removal process are all the same. Similarly, the transport times between each process are also the same.

[0065] As described above, in this embodiment, the first layer 11 of the preform 10 is injection molded in the first injection molding process, and the second layer 12 is injection molded on the inner or outer periphery of the first layer 11 in the second injection molding process to manufacture the multi-layered preform 10. In this embodiment, the first layer 11 and the second layer 12 of the multi-layered preform 10 are molded in two injection molding steps, respectively, so that the shapes and thickness distributions of the first layer 11 and the second layer 12 can be precisely controlled. This allows the container 20 to be stably formed with a desired gradation pattern by coloring the inside.

[0066] In this embodiment, a multi-layered preform 10 is manufactured by two-stage injection molding, and the preform 10 is blow molded while retaining the heat from the injection molding to manufacture a container 20. The second layer of the preform 10 has a tapered region 17 in which the wall thickness gradually decreases in the axial direction from the bottom side to the neck side. Then, by blow molding the preform 10 while retaining the heat from the injection molding, a container 20 is manufactured that has a gradation pattern in which the color shade gradually changes in the axial direction due to the stretching of the first layer 11 and the second layer 12.

[0067] For example, compared to a case where cooled preforms are fitted together to produce a multi-layered preform, and then reheated and blow molded (cold parison method), in this embodiment, the preforms do not need to be cooled to near room temperature, and the steps of assembling and reheating the preforms are also unnecessary. Therefore, according to this embodiment, a series of steps from injection molding of the preforms 10 to blow molding of the container 20 can be completed in a relatively short time, and the container 20 having a gradation pattern can be manufactured in a shorter cycle.

[0068] <Modification> 7 to 9 are diagrams illustrating first to third modified examples of the above embodiment. In each of the following modified examples, a container 20 is manufactured by blow molding an inverted paraboloid of revolution preform. The basic configuration of the blow molding apparatus 30 in the modified examples is the same as that of the above embodiment.

[0069] Fig. 7 is an explanatory diagram of a first modified example for manufacturing a container 20 having a horizontal stripe color pattern 24. Fig. 7(a) is a vertical cross-sectional view of a cavity mold 60 for forming a first layer of a preform, and Fig. 7(b) is a plan view of the cavity mold 60 of Fig. 7(a). Also, Fig. 7(c) is a front view of the container 20 of the first modified example.

[0070] In the first modification, at least two or more annular projections (or step-like projections) 61a, 61b are concentrically formed on the inner surface of the cavity mold 60 that forms the first layer. Note that the projections of the cavity mold 60 in each modification are all formed to have a draft angle. As a result, an annular recess is formed on the outer surface of the first layer of the preform. When a resin material of a different color is injection molded on the outer periphery of this first layer to form a second layer, the second layer fits into the recess of the first layer, and a preform (not shown) having an annular thick portion of the second layer can be manufactured. By blow molding this preform, a container 20 having a horizontal striped color pattern 24 according to the thickness distribution of the first and second layers can be manufactured, as shown in FIG. 7(c).

[0071] Fig. 8 is an explanatory diagram of a second modified example for manufacturing a container 20 having a spiral color pattern 25. Fig. 8(a) is a vertical cross-sectional view of a cavity mold 60 for forming a first layer of a preform, and Fig. 8(b) is a plan view of the cavity mold 60 of Fig. 8(a). Also, Fig. 8(c) is a front view of the container 20 of the second modified example.

[0072] In the second modification, a spiral protrusion 61c is formed on the inner surface of the cavity mold 60 that forms the first layer. This forms a spiral recess on the outer surface of the first layer of the preform. When a resin material of a different color is injection molded on the outer periphery of this first layer to form a second layer, the second layer enters the recess of the first layer, and a preform (not shown) having a spiral thick portion of the second layer can be manufactured. By blow molding this preform, a container 20 having a spiral color pattern 25 according to the thickness distribution of the first and second layers can be manufactured, as shown in FIG. 8(c).

[0073] Fig. 9 is an explanatory diagram of a third modified example for manufacturing a container 20 having a color pattern 26 of an arbitrary pattern such as letters. Fig. 9(a) is a vertical cross-sectional view of a cavity mold 60 for forming a first layer of a preform, and Fig. 9(b) is a plan view of the cavity mold 60 of Fig. 9(a). Fig. 9(c) is a front view of the container 20 of the third modified example.

[0074] In the third modified example, protrusions 61d of an arbitrary pattern (such as the letter "A") are formed on the inner surface of the cavity mold 60 which forms the first layer. As a result, depressions in the shape of the above pattern are formed on the outer surface of the first layer of the preform. When a resin material of a different color is injection molded on the outer periphery of this first layer to form a second layer, the second layer fills the depressions in the first layer, and a preform (not shown) having a thick portion in the shape of the above pattern can be manufactured by the second layer. This preform is then blow molded, as shown in FIG. 9 As shown in (c), a container 20 can be manufactured having a color pattern 26 in the shape of the above pattern according to the distribution of thicknesses of the first and second layers.

[0075] The present invention is not limited to the above-described embodiment, and various improvements and design changes may be made without departing from the spirit of the present invention.

[0076] In the above embodiment, an example has been described in which a two-layer preform 10 is molded by two-stage injection molding, and this preform 10 is blow molded. However, in the blow molding apparatus 30 of the present invention, an injection molding section may be further added, and a preform with an n-layer structure may be molded by n-stage injection molding (where n is an integer of 3 or more). This makes it possible to manufacture containers with more complicated color patterns. When three or more injection molding sections are provided, temperature adjustment sections may be appropriately added between the injection molding sections in order to adjust the retained heat of each layer to a preferred temperature.

[0077] In the above embodiment, a configuration example of the so-called five-station type blow molding apparatus 30 has been described. However, the blow molding apparatus of the present invention may be a six-station type blow molding apparatus having a temperature adjustment unit between the first injection molding section 31 and the second injection molding section 32 that supplementarily heats or cools the first layer 11 of the preform 10.

[0078] Fig. 10 is a schematic diagram showing a configuration example of a six-station blow molding apparatus 30a as another embodiment. Fig. 11 is a flow chart showing steps of a container manufacturing method in another embodiment. In the following description of the other embodiment, repeated description of elements similar to those in the above embodiment will be omitted as appropriate.

[0079] 10 includes a first injection molding section 31, a temperature adjustment section 39 (first temperature adjustment section), a second injection molding section 32, a temperature adjustment section 33 (second temperature adjustment section), a blow molding section 34, a take-out section 35, and a conveying mechanism 36. The first injection molding section 31, the temperature adjustment section 39, the second injection molding section 32, the temperature adjustment section 33, the blow molding section 34, and the take-out section 35 are disposed at positions rotated by a predetermined angle (for example, 60 degrees) around the conveying mechanism 36.

[0080] The transport mechanism 36 of the blow molding apparatus 30a includes a transfer plate 36b that rotates about an axis perpendicular to the plane of the paper in Fig. 10. The transfer plate 36b transports the preform 10 (or the container 20) whose neck portion is held by a neck mold through the first injection molding section 31, the temperature adjustment section 39, the second injection molding section 32, the temperature adjustment section 33, the blow molding section 34, and the removal section 35 in this order.

[0081] The temperature adjustment unit 39 has a configuration similar to that of the temperature adjustment unit 33, and includes a mold for temperature adjustment (a temperature adjustment pot and a temperature adjustment core) (not shown). The temperature adjustment unit 39 is a first injection molding unit. 31 The first layer 11 of the preform 10 conveyed from the mold unit 10 is accommodated in a mold unit maintained at a predetermined temperature, thereby subjecting the first layer 11 to auxiliary heating or cooling.

[0082] As shown in FIG. 11, the manufacturing method of a container using a blow molding apparatus 30a of another embodiment differs from the manufacturing method of the above embodiment shown in FIG. 6 in that a first temperature adjustment process (S101a) is performed between the first injection molding process (S101) and the second injection molding process (S102).

[0083] In the first temperature adjustment step (S101a), the first layer 11 of the preform 10 is accommodated in a mold unit for temperature adjustment in the temperature adjustment section 39, and the first layer 11 is cooled and the temperature distribution is adjusted (temperature uniformization and removal of temperature deviation). At this time, the first layer 11 may be heated in the temperature adjustment section 39 as necessary. Thereafter, the transfer plate 36b of the transfer mechanism 36 rotates by a predetermined angle, and the first layer 11 of the preform 10 held in the neck mold is transferred to the second injection molding section. 32 Other steps in FIG. 11 are the same as those in FIG.

[0084] In addition, the embodiments disclosed herein should be considered to be illustrative and not restrictive in all respects. The scope of the present invention is defined by the claims, not the above description, and is intended to include all modifications within the meaning and scope of the claims. [Explanation of symbols]

[0085] Reference Signs List 10...preform, 11...first layer, 12...second layer, 13...neck portion, 14...body portion, 15...bottom portion, 16...hole, 17...tapered region, 18...thin film portion, 20...container, 22...body portion, 22a...first region, 22b...middle region, 22c...second region, 30...blow molding device, 31...first injection molding section, 32...second injection molding section, 34...blow molding section, 37...first injection device, 38...second injection device, 50...cavity mold, 51...core mold

Claims

1. a first injection molding step of injection molding a first layer of a bottomed cylindrical preform into a first mold using a first resin material; a second injection molding process in which the first layer is accommodated in a second mold different from the first mold, a second resin material having a color different from that of the first resin material is injected into the second mold to laminate a second layer on the outer circumferential side or the inner circumferential side of the first layer, and a multi-layer preform having a wall thickness distribution in which a bottom portion is thicker than a body portion is molded; a blow molding step of blow molding the multi-layer preform obtained in the second injection molding step while the multi-layer preform has the heat retained during injection molding, to produce a resin container having a color pattern according to the thickness distribution of the first layer and the second layer and a thickness distribution in which the bottom portion is thicker than the body portion; having the second mold includes a core mold that holds the shape of the first layer and a cavity mold that faces an outer periphery of the first layer, In the second injection molding step, the core mold is inserted into the inner periphery of the first layer, and the second resin material is injected between the cavity mold and the first layer. A method for manufacturing a resin container.

2. a first injection molding step of injection molding a first layer of a bottomed cylindrical preform into a first mold using a first resin material; a second injection molding process in which the first layer is accommodated in a second mold different from the first mold, a second resin material having a color different from that of the first resin material is injected into the second mold to laminate a second layer on the outer circumferential side or the inner circumferential side of the first layer, and a multi-layer preform having a wall thickness distribution in which a bottom portion is thicker than a body portion is molded; a blow molding step of blow molding the multi-layer preform obtained in the second injection molding step while the multi-layer preform has the heat retained during injection molding, to produce a resin container having a color pattern according to the thickness distribution of the first layer and the second layer and a thickness distribution in which the bottom portion is thicker than the body portion; having the second mold includes a core mold facing an inner periphery side of the first layer and a cavity mold that holds a shape of the first layer, In the second injection molding step, the cavity mold is disposed on the outer periphery side of the first layer, and the second resin material is injected between the core mold and the first layer. A method for manufacturing a resin container.

3. In the first injection molding step, a thin film portion having a small thickness is formed in a part of the first layer, In the second injection molding step, the thin film portion is broken by injecting the second resin material, and the second resin material is introduced to the inner periphery side of the first layer. The method for producing the resin container according to claim 2.

4. The preform produced in the second injection molding step has a region in which a wall thickness ratio between the first layer and the second layer changes in a predetermined direction, The resin container has a gradation pattern formed by stretching the region. A method for producing a resin container according to any one of claims 1 to 3.

5. The first resin material and the second resin material are the same type of resin material but have different colorant compositions. A method for producing a resin container according to any one of claims 1 to 3.

6. a first injection molding section that injection molds a first layer of a bottomed cylindrical preform into a first mold using a first resin material; a second injection molding unit that accommodates the first layer in a second mold different from the first mold, and injects a second resin material having a color different from that of the first resin material into the second mold to laminate a second layer on the outer circumferential side or the inner circumferential side of the first layer, thereby molding a multi-layer preform having a thickness distribution in which a bottom portion is thicker than a body portion; a blow molding section for blow molding the multi-layer preform obtained in the second injection molding section while the multi-layer preform has the retained heat during injection molding, to produce a resin container having a color pattern according to the thickness distribution of the first layer and the second layer and a thickness distribution in which the bottom portion is thicker than the body portion; having the second mold includes a core mold that holds the shape of the first layer and a cavity mold that faces an outer periphery of the first layer, The second injection molding section inserts the core mold into the inner periphery of the first layer and injects the second resin material between the cavity mold and the first layer. Plastic container manufacturing equipment.

7. a first injection molding section that injection molds a first layer of a bottomed cylindrical preform into a first mold using a first resin material; a second injection molding unit that accommodates the first layer in a second mold different from the first mold, and injects a second resin material having a color different from that of the first resin material into the second mold to laminate a second layer on the outer circumferential side or the inner circumferential side of the first layer, thereby molding a multi-layer preform having a thickness distribution in which a bottom portion is thicker than a body portion; a blow molding section for blow molding the multi-layer preform obtained in the second injection molding section while the multi-layer preform has the retained heat during injection molding, to produce a resin container having a color pattern according to the thickness distribution of the first layer and the second layer and a thickness distribution in which the bottom portion is thicker than the body portion; having the second mold includes a core mold facing an inner periphery side of the first layer and a cavity mold that holds a shape of the first layer, The second injection molding section disposes the cavity mold on the outer circumferential side of the first layer, and injects the second resin material between the core mold and the first layer. Plastic container manufacturing equipment.

8. A mold unit for use in a manufacturing apparatus including a first injection molding section and a second injection molding section for molding a multi-layer preform having a thickness distribution in which a bottom portion is thicker than a body portion, and a blow molding section for blow molding the multi-layer preform to manufacture a resin container, A first mold used in the first injection molding section for forming a bottomed cylindrical inner layer of the preform; a second mold used in the second injection molding section for laminating an outer layer of the preform on the outside of the inner layer; The first mold comprises: A first cavity mold that defines an outer circumferential shape of the inner layer; a first core mold inserted into the first cavity mold and defining an inner peripheral shape of the inner layer; The second mold comprises: A second core mold that is inserted into the inner layer and holds the inner layer from the inside; a second cavity mold that receives the inner layer into which the second core mold is inserted and forms a mold space for the outer layer between the second core mold and an outer peripheral surface of the inner layer, thereby defining an outer peripheral shape of the outer layer; The first cavity mold has a shape having a tapered portion in which the outer periphery of the inner layer tapers toward the bottom. Mold unit.

9. A mold unit for use in a manufacturing apparatus including a first injection molding section and a second injection molding section for molding a multi-layer preform having a thickness distribution in which a bottom portion is thicker than a body portion, and a blow molding section for blow molding the multi-layer preform to manufacture a resin container, a first mold used in the first injection molding section to form an outer layer of the preform; A second mold used in the second injection molding section for laminating a bottomed cylindrical inner layer of the preform inside the outer layer, The first mold comprises: a first cavity mold that defines an outer peripheral shape of the outer layer; a first core mold inserted into the first cavity mold and defining an inner circumferential shape of the outer layer; The second mold comprises: a second cavity mold for receiving the outer layer and externally supporting the outer layer; a second core mold that is inserted inside the outer layer and forms a mold space for the inner layer between itself and an inner peripheral surface of the outer layer, and that defines an inner peripheral shape of the inner layer; The second core mold has a shape having a tapered portion in which the outer periphery of the inner layer is tapered toward the bottom. Mold unit.

10. Further, a neck mold is provided which is shared by at least the first injection molding section and the second injection molding section, and which grips the molded product of the first injection molding section and transports it to the second injection molding section; The mold unit according to claim 8 or 9, wherein the first cavity mold and the second cavity mold each have a position restricting portion that restricts the position of the neck mold.

11. The mold unit according to claim 10 , further comprising a third mold that is used in a process of the manufacturing device different from the first injection molding section and the second injection molding section and that is provided with the position regulating section.

12. The mold unit according to claim 11, wherein the third mold is a mold used in any one of a temperature adjustment section that adjusts the temperature of the preform or the molded product of the first injection molding section, the blow molding section, and the removal section for the resin container.