Glass Ceramic Products

Abstract

The present invention relates to an article, in particular a cooktop or furniture element, comprising at least one substrate, such as a plate, made of glass ceramic, which substrate is coated in at least one area with a paint comprising at least: (1) a silicone resin containing a methyl group and a phenyl group; (2) a silicone resin containing a methyl group; (3) one or more lamellar inorganic fillers having a thickness of less than 2 μm and having lateral dimensions of less than 10 μm for at least 80% by weight, comprising talc and / or one or more carbonates; (4) One or more black pigments. The invention also relates to a method for obtaining this article.

Description

[Technical field]

[0001] The present invention relates to the field of glass ceramics. More specifically, the present invention relates to glass ceramic articles (or products) intended in particular to cover or receive a heating element (e.g. cooktop, oven door, fireplace insert, fire guard, etc.) and / or to act as a surface for a piece of furniture (if appropriate, in combination with a heating element, for example in the case of a central island for a kitchen or dining room). The term "glass ceramic article" is understood to mean an article based on a substrate made of a glass ceramic material (such as a glass ceramic plate), which substrate can be provided, if appropriate, with additional accessories or elements (decorative or functional) required for its final use, and which article refers only to the substrate and can be provided with additional accessories (e.g. cooktop provided with its control panel, its heating element, etc.). [Background technology]

[0002] There are several commonly used glass-ceramic products, particularly glass-ceramic cooktops, that have enjoyed great success among appliance vendors, appliance manufacturers, and users, which is explained, among other things, by the attractive appearance of these tops and their ease of cleaning.

[0003] Glass-ceramics start out as glasses, called precursor glasses (or parent or green glasses), whose specific chemical composition allows for controlled crystallization by a suitable heat treatment, called ceramization. This specific partially crystalline structure confers unique properties on glass-ceramics.

[0004] Currently, there are various types of glass-ceramic plates. Given that it is very difficult to modify these plates and / or their manufacturing methods without the risk of having unfavorable effects on the desired properties, each variant is the result of major research and the result of numerous tests. In particular, to be able to be used as a cooktop, glass-ceramic plates must generally have a transmittance in the visible light range that is low enough to hide at least part of the underlying heating element when it is switched off, and, depending on the situation (radiative heating, inductive heating, etc.), exhibit a transmittance in the visible range of wavelengths that is high enough so that the user, for safety purposes, visually detects the heating element in the operating state. Glass-ceramic plates should also exhibit a high transmittance in the infrared range of wavelengths, especially in the case of plates with radiative heating elements. Glass-ceramic plates must also exhibit sufficient mechanical strength required in their field of use. In particular, to be used as a cooktop in the household appliances field or as a surface for pieces of furniture, glass-ceramic plates must exhibit good resistance (for example defined in accordance with standard EN 60335-2-6) to pressure, impacts (supports and drops of furniture, etc.).

[0005] The most widespread current cooktops are dark in colour, in particular black, but there are also plates with a lighter appearance (in particular white, exhibiting a haze of at least 50%, as described, for example, in patent FR 2 766 816) and, in fact, even transparent plates provided with an opacifying coating.

[0006] Known (functional and / or decorative) coatings for glass-ceramic plates traditionally include enamels based on glass frits and pigments, as well as certain paints resistant to high temperatures, such as those based on silicone resins (mainly silicone alkyd type). Enamels in particular present the advantage that they can be deposited on the precursor glass (or on the parent glass or on the green glass) before ceramming and can also be fired during ceramming, and that they can withstand high temperatures (allowing the use of different heating means for the plate). However, they can locally reduce the mechanical strength of the glass-ceramic plate and can spall, especially for very thick deposits or deposits produced in several passes. Furthermore, certain strong colors are difficult to obtain (especially in a single pass) and the firing of the enamels often leads to the appearance of undesirable hues (e.g. brown or grey for black enamels). In particular, by using conventional enamels, it is difficult to obtain strong black or white decorations on the surface of the glass-ceramic without interference hues.

[0007] The paint can be applied in several layers, if necessary for the part, and can present various colors. However, the paint must be applied after ceramization, therefore requiring additional firing, and generally remains limited in the case of cooktops to plates for induction burners (which operate at lower temperatures). Also, for enamels, it is difficult to obtain strong black or white decorations. In particular, "deep black" colors are very difficult to achieve. In existing formulations based on silicone resins, the black pigment is not thermally stable, which can lead to color changes, making it necessary to provide a particularly high proportion of pigment, and moreover the silicone binder is absorbed to an even greater extent by the pigment, thus producing, at the end, a mechanically brittle coating, which in some cases can split or peel off under the effect of thermomechanical stress. Thus, existing black paints that are resistant to high temperatures are generally not black enough and / or do not adhere well to glass-ceramic substrates and / or are not resistant enough to the specific thermomechanical stresses desired in the applications aimed at in the present invention. To minimize these drawbacks or to obtain a more intense color, it is necessary, in particular, to cover the existing paint with a covering layer of paint (especially transparent) and / or an organometallic paste (especially black) or a layer of resin, but these solutions are relatively expensive and in some cases do not prevent the formation of cracks.

[0008] There are also coatings based on reflective layers which, by juxtaposition with an enamel or paint layer, make it possible to obtain effects particularly desired for aesthetic and / or functional reasons. However, these coatings are generally relatively expensive since they require specific installation and their manufacture, which is carried out offline after ceramization, is more complex or problematic, and are restricted, as in the case of paints, to plates for induction burners (in the case of cooktops). Summary of the Invention [Problem to be solved by the invention]

[0009] The object of the present invention was to provide a novel glass-ceramic plate based on a substrate made of glass ceramic, in particular a transparent glass ceramic, in particular intended to cover or receive a heating element, such as a cooktop, and / or to act as a surface of a piece of furniture, optionally combined with a heating element, where this glass ceramic exhibits, in at least one region, an intensely dark coating, where appropriate, whose color persists despite thermomechanical stresses imposed on the coated substrate, which coating exhibits good mechanical strength, heat and wear resistance, and good durability, while minimizing weakening of the glass ceramic, and is economical and simple to obtain and can adhere well to the glass ceramic. [Means for solving the problem]

[0010] This object is obtained by an article (or product) according to the invention, which is in particular a cooktop or furniture element (piece of furniture or part of a piece of furniture), which comprises at least one substrate, such as a plate made of glass ceramic, which article and / or this substrate is in particular intended to be used together with (in particular for covering or receiving) at least one light source and / or at least one heating element and / or to act as a surface of a piece of furniture (if appropriate in combination with one or more heating elements and / or one or more light sources), which substrate is coated in at least one region with a paint comprising (or formed from) at least (1) Silicone resin containing methyl and phenyl groups 、 ( 2 ) having a thickness of less than 2 μm and at least 80% by weight (or D80) of less than 10 μm ~65μm (inclusive) and having a lateral dimension of At least (2a) mica, and (2b) one or more lamellar inorganic (or mineral) fillers (or fillers) comprising talc and / or one or more carbonates, ( 3) one or more black pigments. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] The article according to the invention comprises or is formed from at least one glass-ceramic substrate. Preferably, this substrate (or the article itself, if formed only from a substrate) is in particular a plate intended to cover or receive at least one light source and / or one heating element. This substrate (or respectively this plate) is generally of geometric shape, in particular rectangular, indeed square, indeed circular or elliptical, etc., and generally presents an "upper" or "external" face in the position of use (the face that is visible or facing the user), and another "lower" or "internal" face in the position of use (the face that is generally hidden, for example in the framework or casing of a piece of furniture), and an edge face (or edge or thickness). The upper face is generally flat and smooth, but can also present at least one protruding area and / or at least one recessed area and / or at least one opening, etc. The lower face is according to the invention preferentially flat and smooth, but can also present, if appropriate, a structure.

[0012] The thickness of the glass-ceramic substrate is in particular at least 2 mm, in particular at least 2.5 mm, advantageously less than 15 mm, in particular in the order of 3 to 15 mm, in particular in the order of 3 to 6 mm. The substrate is preferably a flat or virtually flat plate (in particular having a deflection of less than 0.1% from the diagonal of the plate, preferably of the order of zero).

[0013] The substrate can be based on any glass ceramic, which has a zero or substantially zero CTE, in particular a CTE of 30×10 (in absolute value) between 20 and 300° C. -7 K -1 Less than 15×10 -7 K -1 Less than 5×10 -7 K -1 The compound advantageously exhibits a CTE of less than 1.0.

[0014] Preferably, a transparent or translucent substrate is used, in particular a transparent or translucent substrate based on any glass ceramic that essentially has a light transmittance TL (integrated in the visible wavelength range) of more than 50%, in particular 50% to 90%. The term "essentially" is understood to mean that the plate has such a transmittance by itself, without the presence of a coating. The light transmittance TL is measured according to standard NF EN 410 using a D65 light source and is the total transmittance (integrated in the visible range of wavelengths between 0.38 μm and 0.78 μm), taking into account both direct transmission and possible diffuse transmission, the measurement being carried out, for example, using a spectrophotometer with an integrating sphere, and the measurement at a given thickness is then converted, if appropriate, to a reference thickness of 4 mm according to standard NF EN 410.

[0015] In particular, it generally contains crystals of β-quartz structure in the residual glass phase, advantageously with an absolute value of 15×10 -7 / ℃ or less, in reality 5×10 -7 A transparent glass-ceramic substrate exhibiting an expansion coefficient of 1000 nm / °C is used. This glass-ceramic is, for example, a plate sold under the name KeraLite by the company Eurokera. This glass-ceramic can have, in particular, the composition described in the patent applications published under the following numbers: WO2013 / 171288, US2010-167903, WO2008 / 065166, EP2,086,895, JP2010-510951, EP2,086,896, WO2008 / 065167, US2010-099546, JP2010-510952 and EP0,437,228. This glass-ceramic is, in particular, a lithium aluminosilicate glass-ceramic. If necessary, this substrate / glass-ceramic can be body-colored and / or translucent.

[0016] According to the invention, the substrate has (is provided with or is coated with) a coating (or a coating formed of a coating or one or more layers of a coating) as defined in the invention on or in one or more areas of at least one surface of the substrate (in particular one of the main surfaces (upper or lower)), generally on its lower or inner surface, in particular on a major part (at least 50%, preferably at least 75%, in practice at least 90%) of this surface (the coating being defined by its initial composition when applied to the substrate, before drying or baking, if appropriate), with the exception, if appropriate, of the display device or display area (for which a coating that is not relatively less opaque than any coating or base coating (or main coating) of said surface is preferred in order to hide the electronics of the display when the display is switched off and to let the light of the display through when the display is switched on). If appropriate, the paint according to the invention can be applied locally, thereby in particular forming decorative and / or functional patterns (e.g. for delimiting heating areas); and, if appropriate, a second coating (formed for example from a paint according to the invention of a different hue or opacity, or optionally formed from another paint or layer of different nature) can be used to cover other parts of the substrate and / or to form contrasts.

[0017] The coating composition comprises, in particular as binder, one or more silicone (or polysiloxane) resins selected from resins containing methyl and phenyl groups (in particular the so-called "silicone resins of the methyl / phenyl type"). ) is used. These resins have methyl and phenyl groups (or functional groups or radicals) as organic groups or substituents (or are functionalized with them or mixtures thereof, or have been added or introduced with them, or are substituted or modified with them or mixtures thereof). Books The methyl / phenyl type silicone resin used in accordance with the invention FatIn particular, the type of dendrimer in which the organic substituents consist essentially or exclusively of methyl and phenyl groups (or functional groups) With fat In contrast, other types of silicone resins , for example "methyl-type" silicone resins (i.e., the organic substituents consist (only) of methyl groups (and therefore no phenyl groups)) or silicone resins modified with organic resins, e.g. For example, alkyd, epoxy or polyester. Ru Tree There are silicone resins modified by silicones, which are designated in particular by "(modified) epoxy type resins" (hybridized / modified / substituted by epoxy groups) or "(modified) alkyd type resins" (hybridized / modified / substituted by alkyd groups) or "(modified) polyester type resins" (hybridized / modified / substituted by polyester groups). These selected resins according to the invention are in particular free of (or not functionalized by) one or more of the following groups or functional groups: halogen, epoxy, polyester, alkenyl, vinyl, allyl, alkynyl, mercapto or thiol, or acrylic. Preferably, the coating material according to the invention contains, as silicone resin, at least 75% by weight (relative to the total weight of silicone resins present) of silicone resins of the methyl / phenyl type. Fat, In particular, at least 80% by weight, preferably 100% by weight, of silicone resins of the methyl / phenyl type. Fat In particular, the coating material according to the invention is of the (modified) alkyd type and / or of the (modified) epoxy type and / or of the (modified) polyester type. Silicone resin of the polyamide and / or methyl type Does not include.

[0018] In particular, the silicone resins used can be provided in the form of (co)polymers and / or oligomers, in particular in the form of (co)polymers and / or oligomers which are crosslinkable or, if appropriate, already crosslinked. These resins are advantageously colourless and have a decomposition temperature of more than 350° C., in particular between 350° C. and 700° C., and an average molecular weight (Mw) in particular between 2000 and 300,000 g / mol (or Daltons). The silicone resins preferentially used in the coating composition according to the invention are in particular , PoOne or more resins selected from polyphenylmethylsiloxane (or phenylmethylsiloxane polymer) and / or polydiphenyldimethylsiloxane (or diphenyldimethylsiloxane polymer), etc. do.

[0019] Preferably , S Ricon resin (preferably In the coating material according to the present invention, The content of the resin (consisting essentially or exclusively of the resin selected) is between 20% and 50% by weight, in particular between 28% and 40% by weight, of the paint (these contents being given with respect to the total composition including the solvent as deposited on the substrate and, where appropriate, removed by subsequent drying and / or baking), or between 30% and 80% by weight of the solids content of the paint.

[0020] As defined according to the invention, the paint also contains one or more inorganic (or mineral) fillers. These fillers do not melt, in particular during firing, and are insoluble. They have a particular reinforcing role, and also participate in the cohesion and heat resistance of the combined product (but compared to pigments, they only contribute a low opacity and have little effect on the hue). These fillers are of specific shape (lamellae) and dimensions (thickness less than 2 μm and less than 10 μm) selected according to the invention. Between 65μm and 65μm Horizontal dimension) , at least one or more mica particles, and The composition preferably comprises at least one or more particles of talc and / or carbonate (eg, selected from calcium carbonate and / or barium carbonate). The mica particles contribute relatively more to mechanical reinforcement and have less effect on the colorimetric system compared to the talc and / or carbonate particles in the paint according to the invention, the presence of both of which is advantageous according to the invention. Preferably, the coating composition according to the invention contains, as filler, at least 90% by weight (based on the total weight of fillers present) of fillers of the shape and size selected according to the invention. , mica particles, and granules of ruthenium and / or carbonate Child mixture and advantageously 100% by weight This mixture (In other words, the filler present is , from this mixture or consisting solely of this mixture )。

[0021] These fillers as selected according to the invention are fillers of lamellar shape, i.e. in the form of platelets that are thin compared to their "transverse" dimensions (dimensions in the respective planes of the platelets). The thickness (or smallest dimension) of these platelets is, according to the invention, less than 2 μm (in particular for all particles). Their "transverse" dimension is, according to the invention, less than 2 μm for at least 80% by weight of the particles (D80). , between 10 μm and 65 μm (in particular, the relatively small dimensions do not prevent the appearance of cracks in the coating composition selected according to the invention), in particular between 10 μm and 60 μm (both end values ​​included). If so, the platelets may be locally aggregated by forming aggregates or clumps. "Horizontal" dimension is understood to mean for each platelet the dimensions in the plane of the platelet (in particular the length (maximum dimension) and the width (maximum dimension perpendicular to the length direction), where the width is generally less than the length (giving a more or less elongated or rectangular platelet shape), but may optionally be close to the length (giving an irregular platelet shape in the more or less circular range). For the evaluation of these transverse dimensions, the dimensional parameter D80 corresponding to the dimension of at least 80% by weight of the particles is taken into account here. This parameter is evaluated in particular by particle size measurement according to the standard ISO 13320:2009 or by particle size analysis by laser diffraction. The shape of the fillers can be observed in particular by optical microscopy before incorporation into the paint or by scanning electron microscopy (SEM) after incorporation into the paint. These fillers are obtained in particular by grinding until the selected dimensions are obtained.

[0022] The content of fillers selected in the coating material according to the invention is determined, with respect to the coating material (total composition including the solvent as deposited on the substrate and, if appropriate, subsequently removed by drying and / or baking), by: In particular, it is between 5% and 20% by weight, preferentially between 8% and 20% by weight or between 1% and 10% by volume (in particular between 2% and 10% by volume). Preferably, the talc / carbonate content is between 5% and 15% by weight and the mica content is between 3% and 12% by weight. be.

[0023] As indicated above, the paint used according to the present invention is also formed from a black pigment, the pigment (preferably consisting of a black pigment) content being between 10% and 30% by weight (both inclusive) of the paint, preferably between 15% or 20% and 30% by weight of the paint.

[0024] The pigments used to prepare the paint are preferably (only) inorganic pigments, preferably only black pigments. They are preferentially selected from black pigments based on metal oxides, in particular black pigments based on chromium oxide, black pigments based on copper oxide, black pigments based on iron oxide and / or black pigments based on manganese oxide. Examples of said pigments are, for example, in particular, sold by Kremer as PBk 26.77494, or sold by Tomatec as 42-303B, or sold by Asahi Sangyo as 3250LM, or sold by Shepherd as Black 430.

[0025] The pigment is in particular dispersed in the abovementioned silicone resin(s) (acting as a binder, the term "silicone binder" may also be used to denote the silicone resin) and / or in the medium to which it is added (as specified below). The pigment is generally provided in powder form before being suspended or dispersed in the binder or medium. The pigment is, in the present invention, at least 50% (by number), preferably at least 75%, in practice of the particles of the pigment, dispersed in water. At least 80% Whatever the shape of these particles, they are preferentially selected to exhibit dimensions less than 1 μm.

[0026] The term "particle size" refers to its equivalent diameter, i.e. the diameter of a sphere that behaves identically during a particle size analysis of the particles forming the pigment under consideration (or of the powder formed from said particles), the particle size distribution (combined particle size) being measured in particular by laser particle size measurement.

[0027] The silicone resins mentioned above coat in particular the pigment powders in the paint and allow bulk aggregation of the particles after drying in order to form a solid paint layer. If appropriate, the paint, in particular in a form ready for deposition, also contains, besides the silicone resin that binds the pigment, at least one (other) medium or solvent that forms part of the silicone resin when added to the paint composition (or is added together with the silicone resin) and / or forms part of the paint (or is added to the paint). This solvent allows the achievement of the viscosity desired for application to the substrate and allows the pre-bonding of the paint to the substrate. As solvents, for example, white spirit (or heavy naphtha), toluene, solvents of aromatic hydrocarbon type (for example the solvent sold under the brand name Solvesso 100 by Exxon) can be used. The content of solvent in the paint during deposition is generally about 25% to 45% by weight of the paint, which is subsequently removed (this removal is carried out in particular during drying and / or baking) to obtain the final layer. Preferably, the paint used according to the invention does not contain water or aqueous solvents, in particular for better use.

[0028] The coating material may optionally contain other types of ingredients, for example one or more additives selected from dispersants (e.g. those sold by Byk or Evonik as Disperbyk-102 or Tego Dispers 689), air release additives (e.g. those sold by Byk or Evonik as Byk A506 or Byk A530), wetting agents, stabilizers, surfactants, pH or viscosity modifiers, biocides, antifoams, antioxidants, drying agents, with the total additive content not exceeding 10% by weight, in particular in an amount between 1% and 10% by weight (in addition to the silicone binder, pigments, fillers and solvents mentioned above).

[0029] Unlike enamel compositions, the coating composition according to the invention does not contain glass frits or components capable of forming a glassy matrix together. The coating composition according to the invention is provided for deposition in the form of a dispersion and advantageously does not contain silica gel or colloidal silica for better use of the composition (unlike hydrolysates or sol-gels, which are in particular simpler to form and use).

[0030] In a preferred embodiment according to the invention, the coating composition according to the invention exhibits the following composition (or comprises the following components within the boundaries defined below, inclusive), the proportions being expressed as percentages by weight (relative to the total weight of the coating composition ready for deposition): - Methyl / phenyl type silicone resins: 20~50% , preferably 28~40%、 - Black pigment: 10-30%, preferably 18-25%, - mica-based lamellar fillers, and Lamellar fillers based on talc and / or carbonates: 5-20%, preferably 10-20%, in practice 15-20%, - dispersants and defoamers: 1-10%, preferably 2-5%, - Solvent: 25-45%, preferably 28-45%.

[0031] The paint coating after curing is mainly formed from the silicone resin, fillers and pigments mentioned above. The paint before deposition is generally provided in the form of a stable liquid / solid mixture of a paste-like consistency. The viscosity of the paint as deposited is preferentially between 1000 and 3000 mPa·s, in particular between 1300 and 1800 mPa·s.

[0032] The paint can be formed directly by mixing the components in the required proportions, with the viscosity being adjusted, if necessary, by the addition of solvent.

[0033] The thickness of the final paint coating (after drying) is preferentially 20-40 μm, in particular 25-35 μm.

[0034] The solution according to the invention makes it possible to obtain the product desired according to the invention in a simple and economical manner, without complex operations (the paint layer is advantageously and simply deposited in particular by screen printing), in a sustainable manner and with great flexibility. The coating obtained (after drying / baking) is particularly deep black and is characterized by an unusually low lightness L* of less than 5 (the lightness of existing paints for the intended application is generally at least 12). The lightness L* is a defined component in the CIE colorimetric system and is evaluated in a known manner, in particular using a Byk-Gardner Color Guide 45 / 0 colorimeter (colorimetry in reflection), with a D65 light source, with respect to the upper surface of the substrate (the substrate used for the measurement of the lightness of the paint is a transparent glass-ceramic substrate with a thickness of 4 mm and an inherent light transmission TL (integrated in the visible wavelength range) of 85-90%, arranged on an opaque white background) (the sample is irradiated under a right angle of 45° and observed at an angle of 0°). Furthermore, the coating exhibits good resistance to typical thermomechanical stresses of glass ceramics, and no discoloration or peeling is observed, especially in the case of temperature fluctuations up to 500° C. The coating composition can be used in any area of ​​the glass ceramic substrate, even if these areas are exposed to high temperatures and / or strong lighting. Good adhesion of the coating to the substrate is also observed, and the coating further exhibits good scratch resistance, especially resistance to a 2B pencil according to standard ISO 15184, and at least 1N according to standard ISO 1518-1.

[0035] If appropriate, the substrate may comprise one or more additional coatings, in particular topical coatings (e.g. enamel on the top surface to form a logo or a simple pattern). Advantageously, the paint selected coats the substrate according to the invention without the need for an upper or lower layer.

[0036] The article according to the invention may comprise at least one or more light sources and / or one or more heating elements (such as one or more induction heating means) arranged on the underside of the substrate. The light sources may be integrated / coupled to one or more structures of the display type (for example "7-segment" light-emitting diodes), touch-sensitive digital display electronic control panels, LCD screens, etc. The light sources are advantageously formed by more or less spaced light-emitting diodes.

[0037] An article according to the invention may, if appropriate, comprise other elements; for example, in the case of a cooking section or cooktop, the article may comprise (or be combined with) additional functional or decorative elements (frames, connectors, cables, control elements), etc.

[0038] The invention also relates to a method for the manufacture of an article according to the invention, in which a glass-ceramic substrate is coated in at least one area with a coating material as selected above.

[0039] For the record, the manufacture of glass-ceramic plates is generally carried out as follows: a glass of the composition selected to form the glass ceramic is melted in a melting furnace, then the molten glass is rolled to give a standard ribbon or sheet by passing it between rolling rolls, and the glass ribbon is cut to the desired dimensions. The plates thus cut are then cerammed in a manner known per se. Ceramming consists of firing the plates according to a thermal profile selected to convert the glass into a polycrystalline material known as a "glass-ceramic", where the coefficient of expansion is zero or practically zero and which withstands thermal shocks that may range up to 700°C. Ceramming generally includes the steps of gradually increasing the temperature to a nucleation range, generally in the vicinity of the transformation range of the glass, passing through the nucleation interval in a few minutes, gradually increasing the temperature further to the temperature of the ceramming stationary phase, maintaining the temperature of the ceramming stationary phase for several minutes, and then quenching to ambient temperature.

[0040] The coating material selected according to the invention is applied (in one or more layers, preferably in one layer) quickly and simply by screen printing (in the form of solid tones, if appropriate with transparent intervals in the display area) to the glass-ceramic substrate (this deposition being carried out after any ceramization of the substrate), advantageously to the underside of the glass-ceramic substrate, preferentially in suitable areas (e.g. for the emitting areas).

[0041] Preferably, the screen printing screen used, consisting for example of a woven polyester or polyamide thread, is chosen to exhibit a number of threads per cm between 32 and 43 threads per cm, thereby making it possible to obtain a particularly suitable thickness and definition of the paint coating.

[0042] Once deposited, the coating is dried (e.g., at 160 °C for a few minutes) on the ceramified substrate and then heated at temperatures between 350 and 480 °C. about The final paint coating, which is baked (off-line) for 40-60 minutes, forms a polymer-based layer.

[0043] Where appropriate, the method includes a cutting operation (generally before ceramming), for example using a water jet, mechanical marking using a cutting wheel, etc., followed by a shaping operation (grinding, chamfering, etc.).

[0044] A better understanding of the invention and its advantages can be obtained by reading the following comparative examples, which are given by way of illustration only and are not limiting, the glass-ceramic substrates used being transparent substrates as defined in EP 0 437 228 A1. EXAMPLES

[0045] Example 1 according to the invention: The coating material used is prepared by mixing: - 30% by weight of a methyl / phenyl type silicone resin sold by Dow Corning as RSN-0249 、 - 20% by weight of a black pigment based on oxides of iron and manganese with a size distribution of less than 0.5 μm, sold by Kremer under the name PBk 26.77494, - 10% by weight of a filler (in particles) in the form of lamellar mica sold by Merck under the name Ronaflair Mica M, with a thickness of less than 2 μm and a D80 of 15 μm; - 18% by weight of Imerys-sold, lamellar, less than 2 μm thick, D80 30 μm, talc (form of filler), 1% by weight of a dispersant sold by Byk as Disperbyk 103, 1% by weight of a defoamer, sold by Byk as Byketol OK, - 30% by weight of a naphtha-type solvent sold by Exxon as Solvesso 100.

[0046] The paint is then applied to the substrate by screen printing with a mesh of standard 32 (32 threads per cm) and then dried for 4 minutes at 160°C, followed by baking using a heat treatment at 350°C to 450°C for 45 minutes.

[0047] Example 2 according to the invention: The coating material used is prepared by mixing: - 30 % by weight KR-282 as Shinetsu Methyl / phenyl type silicone resin sold by 、 20% by weight of Oxides of copper, chromium and manganese, with a size distribution of 0.6 μm, sold by Tomatec as 42-303B A black pigment based on - 10% by weight of a filler in the form of particles of lamellar mica sold by Merck under the name Iriodin 600, having a thickness of less than 2 μm and a D80 of 60 μm, - 8 % by weight of Imerys, thin plate, less than 2 μm thick, D80 30 μm, talc (form of filler), 1% by weight of a dispersant sold by Byk as Disperbyk 103, 1% by weight of a defoamer, sold by Byk as Byketol OK, - 30% by weight of a naphtha-type solvent sold by Exxon as Solvesso 100.

[0048] The paint is then applied to the substrate by screen printing with a mesh of standard 32, then dried at 160°C for 4 minutes, followed by baking using a heat treatment at 350°C to 450°C for 45 minutes.

[0049] Reference Example 1 not according to the present invention: The coating material used is prepared by mixing: 35% by weight of a silicone resin of the methyl / phenyl type sold by Dow Corning under the name RSN-0249; - 25% by weight of a black pigment based on oxides of copper, chromium and manganese, with a size distribution of 0.6 μm, sold by Tomatec as 42-303B, - 8% by weight of (filler in the form of) talc, sold by Imerys, lamellar, having a thickness of less than 2 μm and a D80 of 8 μm; 1% by weight of a dispersant sold by Byk as Disperbyk 103, 1% by weight of a defoamer, sold by Byk as Byketol OK, - 30% by weight of a naphtha-type solvent sold by Exxon as Solvesso 100.

[0050] The paint is then applied to the substrate by screen printing with a mesh of standard 32, then dried at 160°C for 4 minutes, followed by baking using a heat treatment at 350°C to 450°C for 45 minutes.

[0051] Reference Example 2 not according to the present invention: The coating material used is prepared by mixing: 35% by weight of a methyl-type silicone resin sold by Shin-Etsu as KR-220L, - 20% by weight of a black pigment based on oxides of iron and manganese with a size distribution of less than 0.5 μm, sold by Kremer under the name PBk 26.77494, - 13% by weight of (filler in the form of) talc, sold by Imerys, lamellar, with a thickness of less than 2 μm and a D80 of 8 μm; 1% by weight of a dispersant sold by Byk as Disperbyk 103, 1% by weight of a defoamer, sold by Byk as Byketol OK, - 30% by weight of a naphtha-type solvent sold by Exxon as Solvesso 100.

[0052] The paint is then applied to the substrate by screen printing with a mesh of standard 32, then dried at 160°C for 4 minutes, followed by baking using a heat treatment at 350°C to 450°C for 45 minutes.

[0053] A sample of each glass ceramic provided with each coating is then placed on a heating element. The temperature measured on the coating is 260° C. (corresponding to the temperature it undergoes during cooking of sausage-type foods). It is then subjected to several heating cycles at 260° C. for 15 minutes, followed by cooling to ambient temperature (total duration of each cycle is 20 minutes).

[0054] The coatings in the examples according to the invention withstand at least 1500 heating cycles without showing separation or cracking or peeling, whereas in the reference comparative example the coating shows separation / cracks and peeling after 100 cycles. Furthermore, the coatings of the examples according to the invention are particularly black in colour (having L*<5), adhere well to glass-ceramic substrates and the scratch tests according to standards ISO 15184 and ISO 1518-1 give resistance to a 2B pencil and a force of at least 1 N, respectively.

[0055] The articles according to the invention, in particular the plates, can in particular be advantageously used to manufacture a new range of cooktops for kitchen ranges or cooking surfaces, or a new range of worktops, consoles, central islands and the like. The embodiments of the present invention are as follows. <Aspect 1> An article, in particular a cooktop or furniture element, comprising at least one substrate made of glass ceramic, said substrate being coated in at least one region with a paint comprising at least (1) a silicone resin containing a methyl group and a phenyl group; (2) one or more lamellar inorganic fillers having a thickness of less than 2 μm and having a lateral dimension of 10 μm to 65 μm for at least 80% by weight, comprising at least: (2a) mica; and (2b) talc and / or one or more carbonates; (3) One or more black pigments. <Aspect 2> 2. The glass-ceramic article of claim 1, wherein the silicone resin of the coating is free of one or more of the following functional groups: halogen, epoxy, polyester, alkenyl, vinyl, allyl, alkynyl, mercapto or thiol, or acrylic; in particular one or more polyphenylmethylsiloxane resins, and / or one or more polydiphenyldimethylsiloxane resins. <Aspect 3> the coating composition contains, as silicone resin, at least 75% by weight of a silicone resin of the methyl / phenyl type, in particular at least 80% by weight, advantageously 100% by weight, based on the total weight of the silicone resins present; and The coating composition does not contain alkyd type and / or epoxy type and / or polyester type and / or methyl type silicone resins; 3. The glass-ceramic article of any of claims 1 and 2, characterized in that: <Aspect 4> 4. The glass-ceramic article according to any one of aspects 1 to 3, wherein the content of the silicone resin in the coating is 20% to 50% by weight. <Aspect 5> 5. A glass-ceramic article according to any one of the preceding aspects, characterized in that the content of the lamellar filler is between 5% and 20% by weight, preferentially between 8% and 20% by weight, or between 1% and 10% by volume, relative to the paint, the content of the talc / carbonate is preferentially between 5% and 15% by weight, relative to the paint, and the content of the mica is preferentially between 3% and 12% by weight, relative to the paint. Aspect 6 6. The glass-ceramic article according to any one of the preceding claims, characterized in that the pigment content is between 10% and 30% by weight of the paint and that at least 50% by weight, preferably at least 75% by weight, indeed at least 80% by weight of the particles of the pigment exhibit a size of less than 1 μm. Aspect 7 7. The glass-ceramic article according to any one of the preceding claims, wherein the paint coating has a thickness of 20-40 μm. <Aspect 8> 8. The glass-ceramic article of any one of the preceding claims, wherein the paint coating exhibits a lightness L* of less than 5. <Aspect 9> A method for making the glass-ceramic article of any one of the preceding claims, comprising coating, in at least one region, the glass-ceramic substrate with a coating comprising at least: (1) a silicone resin containing a methyl group and a phenyl group; (2) one or more lamellar inorganic fillers having a thickness of less than 2 μm and having a lateral dimension of 10 μm to 65 μm for at least 80% by weight, comprising at least: (2a) mica; and (2b) talc and / or one or more carbonates; (3) One or more black pigments. Aspect 10 10. A method for producing a glass-ceramic article according to claim 9, characterized in that the coating is applied to the glass-ceramic substrate by screen printing, the screen printing screen used being preferentially chosen to exhibit a thread count between 32 threads / cm and 43 threads / cm, and the coating is fired at a temperature between 350 and 480° C. for a period of 40 to 60 minutes.

Claims

1. An article comprising at least one substrate made of a glass ceramic, The substrate is coated in at least one region with a paint comprising at least: (1) a silicone resin containing a methyl group and a phenyl group; (2) a lamellar inorganic filler having a thickness of less than 2 μm and a D80 of 10 μm to 65 μm, comprising at least (2a) lamellar mica, and (2b) lamellar talc and / or one or more lamellar carbonates; (3) one or more black pigments; based on the weight of the coating as deposited on the substrate, The (1) is 20% by weight to 50% by weight, The content of (2) is 5% by weight to 20% by weight, The (3) is 10% by weight to 30% by weight; and The content of the lamellar talc and / or the lamellar carbonate is 5% by weight to 15% by weight of the paint, and the content of the lamellar mica is 3% by weight to 12% by weight of the paint. Goods.

2. The glass-ceramic article of claim 1, characterized in that the silicone resin of the coating does not have one or more of the following functional groups: halogen, epoxy, polyester, alkenyl, vinyl, allyl, alkynyl, mercapto or thiol, or acrylic.

3. the coating contains, as silicone resin, at least 75% by weight of a methyl / phenyl type silicone resin, relative to the total weight of the silicone resins present; and The coating composition does not contain alkyd type and / or epoxy type and / or polyester type and / or methyl type silicone resins; 3. The article according to claim 1 or 2, characterized in that

4. The article according to any one of claims 1 to 3, characterized in that the content of the silicone resin in the paint is 28% by weight to 40% by weight.

5. The article according to any one of claims 1 to 4, wherein the content of the lamellar filler is 8% by weight to 20% by weight, or 1% by volume to 10% by volume, relative to the paint.

6. An article according to claim 1, wherein at least 50% by weight of the particles of the pigment exhibit dimensions less than 1 μm.

7. An article according to any one of claims 1 to 6, characterized in that the paint coating has a thickness of 20 to 40 μm.

8. The article according to any one of claims 1 to 7, characterized in that the paint coating exhibits a lightness L* of less than 5.

9. A method for producing an article according to any one of claims 1 to 8, comprising the steps of: In at least one region, the glass-ceramic substrate is coated with a coating comprising at least: (1) a silicone resin containing a methyl group and a phenyl group; (2) one or more lamellar inorganic fillers having a thickness of less than 2 μm and a D80 of 10 μm to 65 μm, comprising at least (2a) lamellar mica, and (2b) lamellar talc and / or one or more lamellar carbonates; (3) one or more black pigments; based on the weight of the coating as deposited on the substrate, The (1) is 20% by weight to 50% by weight, The content of (2) is 5% by weight to 20% by weight, The (3) is 10% by weight to 30% by weight; and The content of the lamellar talc and / or the lamellar carbonate is 5% by weight to 15% by weight, and the content of the lamellar mica is 3% by weight to 12% by weight. Manufacturing method.

10. The method of claim 9, characterized in that the coating is applied to the glass-ceramic substrate by screen printing and the coating is baked at a temperature of 350-480° C. for 40-60 minutes.