Crushing and classification device and method for crushing and classifying electrode materials

Abstract

To improve a recovery property of an active material included in an electrode material of a secondary battery.SOLUTION: A crushing and classifying device 10 in the present disclosure includes a crushing chamber 14 to which an electrode material is input, a rotation shaft 24, an impact body 30, and a screen 20. The rotation axis 24 is disposed in the crushing chamber 14 and rotates under driving power. The impact body 30 has a stick or chain shape, has one end rotatably connected to the rotation shaft 24, and rotates in the crushing chamber 14 under centrifugal force from the rotation of the rotation shaft 24. The screen 20 is provided on a wall surface of the crushing chamber 14 and classifies the crushed electrode material. The impact body 30 includes an edge part rounded to have a radius of curvature of 1 mm or more and 9 mm or less at least on a tip end. The screen 20 has an opening 21 with a size of 5 mm or less.SELECTED DRAWING: Figure 2

Description

[Technical field]

[0001] The present disclosure relates to a technique for crushing and classifying electrode materials for secondary batteries. [Background technology]

[0002] When recycling electrode materials for secondary batteries such as nickel-metal hydride batteries and lithium-ion batteries, it is necessary to separate and recover the active material that is applied as a paste to the electrode material from the current collector. The cheapest process involves crushing the electrode material and sieving the powder containing the active material to recover it, but in order to fully separate the active material, it is necessary to grind it finely over a long period of time.

[0003] Patent Document 1 discloses a method for separating and recovering a current collector and a positive electrode active material from a positive electrode material for a lithium ion battery. In this method, the positive electrode material is first cut. Next, the cut positive electrode material is sieved with a sieve having an opening of 100 to 200 mm, and the positive electrode material is recovered on the underside of the sieve. Then, the recovered positive electrode material is subjected to an impact force to peel off the positive electrode active material from the current collector. Furthermore, the positive electrode material is sieved with a sieve having an opening of 0.1 to 1.0 mm, and the current collector is recovered on the overside of the sieve, and the positive electrode active material is recovered on the underside of the sieve.

[0004] However, in the method disclosed in Patent Document 1, although the positive electrode material can be finely crushed, there is a risk that the recovered powder containing the active material may be contaminated, or that the powder containing the active material may be re-pressed to the non-recovered material, resulting in a decrease in yield. Furthermore, there is a risk that the separation of the non-recovered materials may be deteriorated.

[0005] In addition to Patent Document 1, Patent Document 2 can also be mentioned as an example of a document showing the state of the art in the technical field related to the present disclosure. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] JP 2013-139592 A [Patent Document 2] JP 2013-211234 A Summary of the Invention [Problem to be solved by the invention]

[0007] The present disclosure has been made in view of the above problems. One object of the present disclosure is to improve the recoverability of an active material contained in an electrode material for a secondary battery. [Means for solving the problem]

[0008] The present disclosure provides a crushing and classifying device for achieving the above object. The crushing and classifying device of the present disclosure includes a crushing chamber into which electrode material for secondary batteries is introduced, a rotating shaft disposed within the crushing chamber and rotated by receiving a driving force, a rod-shaped or chain-shaped impacting body rotatably connected at one end to the rotating shaft and rotating within the crushing chamber by receiving a centrifugal force accompanying the rotation of the rotating shaft, and a screen disposed on the wall surface of the crushing chamber for classifying the crushed electrode material. The impacting body has an edge at least at its tip that is rounded with a radius of curvature of 1 mm or more and 9 mm or less. The screen has openings of 5 mm or less.

[0009] The present disclosure provides a method for crushing and classifying electrode materials to achieve the above object. The method for crushing and classifying electrode materials disclosed herein is a method for crushing and classifying electrode materials for secondary batteries using the above crushing and classifying device. The method for crushing and classifying electrode materials disclosed herein includes the steps of feeding the electrode material into a crushing chamber, crushing the electrode material by rotating an impacting body for a predetermined time, sieving the crushed electrode material with a screen, and separately recovering the sieved powder from the crushed electrode material and the residue in the crushing chamber. Effect of the Invention

[0010] According to the technology of the present disclosure, the electrode material is crushed appropriately so as not to be excessively pulverized, so that the contamination of the powder containing the active material peeled off from the electrode material with the non-recovered material is suppressed. In addition, the powder containing the active material is not re-pressed to the non-recovered material, which reduces the yield. This improves the recoverability of the active material from the electrode material. [Brief description of the drawings]

[0011] [Figure 1] 1A to 1C are diagrams illustrating a process for dismantling a secondary battery according to an embodiment of the present disclosure. [Diagram 2] FIG. 1 is a diagram showing a configuration of a hammer crusher according to an embodiment of the present disclosure. [Diagram 3] FIG. 1 is a diagram showing a configuration of a chain crusher according to an embodiment of the present disclosure. [Figure 4] FIG. 13 is a diagram showing the results of confirming the relationship between the hammer corner R and the peeling rate of the active material. [Diagram 5] FIG. 13 is a diagram showing the results of confirming the relationship between the rotation speed of the hammer and the peeling rate of the active material. [Figure 6] FIG. 13 shows the results of a peeling test using a hammer crusher according to an embodiment of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0012] 1. Secondary battery dismantling process Dismantling of secondary batteries is carried out for the purpose of extracting recyclable materials from the various materials that compose the secondary batteries and safely recovering harmful materials. The materials to be recycled are the active materials used in the electrodes, particularly the expensive positive electrode active materials, which are recovered in the form of black mass. Iron, copper, and aluminum are also recovered for recycling. The electrolyte is recovered as a harmful material.

[0013] 1 shows the dismantling process of the secondary battery according to the present embodiment. The dismantling process of the secondary battery according to the present embodiment includes a discharging process S10, a primary crushing process S20, a drying process S30, a secondary crushing process S40, a sieving process S50, and a mechanical sorting process S60. The dismantling process of the secondary battery according to the present embodiment will be described below.

[0014] In the discharging step S10, the secondary battery is discharged. The reason for discharging the secondary battery is to prevent the separator from melting due to heat generated by a short circuit when the secondary battery is crushed in a later step. The adhesion of the melted separator to the electrode material deteriorates recyclability.

[0015] In the primary crushing step S20, the case of the secondary battery is crushed to expose the electrode material inside. By exposing the electrode material, it is possible to evaporate the electrolyte adhering to the electrode material and dry the electrode material. As a method for crushing the secondary battery, for example, a method of cutting the case of the secondary battery with a shredder is used.

[0016] In the drying step S30, the exposed electrode material is dried, and the electrolyte is collected during the drying process.

[0017] In the secondary crushing step S40, the dried electrode material is crushed to peel off the active material from the current collector. In the secondary crushing step S40, crushing may be performed while heating the electrode body. A crushing and classifying device such as a hammer crusher or a chain crusher, which will be described later, is used to crush the dried electrode material. The crushing and classifying device is operated for a certain period of time necessary and sufficient for the active material to peel off from the current collector, thereby crushing the electrode material.

[0018] The sieving process S50 is a process for sorting the objects crushed in the secondary crushing process S40. In the sieving process S50, powder is sorted from the crushed objects. The powder is black mass, which is mainly composed of active materials. A crushing and classifying device such as a hammer crusher or chain crusher, which will be described later, is used to sort the powder. Residues remaining in the crushing and classifying device, such as iron, aluminum, copper, and resin, are mechanically sorted by material in the mechanical sorting process S60.

[0019] 2. Crushing and classification equipment 2-1.Hammer Crusher 2A is a diagram showing the configuration of a hammer crusher according to this embodiment as a crushing and classifying device. The hammer crusher 10 has a crushing chamber 14 inside a main body 12. The crushing chamber 14 is provided with an input lid 16. The secondary batteries to be crushed are input into the crushing chamber 14 by opening the input lid 16.

[0020] A rotating shaft 24 that rotates by receiving a driving force from a motor (not shown) is disposed in the crushing chamber 14. A rotor 26 is attached to the rotating shaft 24. A plurality of hammers 30 are rotatably connected to the periphery of the rotor 26 via a shaft 28. A plurality of rotors 26 are attached in the axial direction of the rotating shaft 24, and a hammer 30 is attached to each rotor 26. The hammer 30 is an impacting body that rotates in the crushing chamber 14 by receiving a centrifugal force accompanying the rotation of the rotating shaft 24 when the rotating shaft 24 rotates. In addition, a fixed blade 32 that shears the object to be crushed between the hammer 30 and the rotor 26 is provided inside the crushing chamber 14.

[0021] 2B and 2C, the edge of the hammer 30 is provided with a radius R (referred to as a "corner R"). The radius of curvature of the corner R is preferably 1 mm or more and 9 mm or less, more preferably 4 mm or more and 8 mm or less. The corner R is provided at least on the tip of the hammer 30, and preferably on the entire portion that may come into contact with the object to be crushed when the hammer 30 rotates.

[0022] A screen 20 for classifying the crushed objects is provided at the bottom of the crushing chamber 14. The screen 20 constitutes a part of the wall of the crushing chamber 14. The screen 20 may be a mesh or a punched metal. However, the opening size of the screen 20 is set to 5 mm or less. A more preferable opening size is 1 mm or less. When the screen 20 is a mesh as shown in FIG. 2D, the opening size is defined as the minimum width of the opening, and when the screen 20 is a punched metal having a circular opening, the opening size is defined as the diameter of the opening. The screen 20 also serves as the bottom cover of the crushing chamber 14. By opening the screen 20, the residue in the crushing chamber 14 can be taken out.

[0023] 2A is a vertical rotation type that rotates the hammers 30 in a vertical plane, but the crushing and classifying device of the present disclosure is also applicable to a horizontal rotation type hammer crusher that rotates the hammers in a horizontal plane. There is no limitation on the number of hammers, and there is no limitation on the shape of the hammers except for the R.

[0024] 2-2.Chain Crusher 3A is a diagram showing the configuration of a chain crusher according to this embodiment as a crushing and classifying device. The chain crusher 40 has a crushing chamber 44 inside a main body 42. The crushing chamber 44 is provided with an input lid 46. The secondary batteries to be crushed are input into the crushing chamber 44 by opening the input lid 46.

[0025] A rotating shaft 54 ​​that receives a driving force from a motor 56 and rotates is disposed within the crushing chamber 44. A plurality of chains 60 are attached to the rotating shaft 54. The chains 60 are attached in a plurality of rows in the axial direction of the rotating shaft 54. The chains 60 are impact bodies that rotate within the crushing chamber 44 by receiving centrifugal force accompanying the rotation of the rotating shaft 54 ​​when the rotating shaft 54 ​​rotates.

[0026] 3B, a corner R is provided on the edge of the chain 60. The radius of curvature of the corner R is preferably 1 mm or more and 9 mm or less, more preferably 4 mm or more and 8 mm or less. The corner R is provided at least on the tip of the chain 60, and preferably on the entire portion that may come into contact with the object to be crushed when the chain 60 rotates.

[0027] A screen 50 for classifying the crushed objects is provided at the bottom of the crushing chamber 44. The screen 50 constitutes a part of the wall of the crushing chamber 44. The screen 50 may be a mesh or a punched metal. However, the opening size of the screen 50 is set to 5 mm or less. More preferably, the opening size is 1 mm or less. When the screen 50 is a mesh as shown in FIG. 3C, the opening size is defined as the minimum width of the opening, and when the screen 50 is a punched metal having a circular opening, the opening size is defined as the diameter of the opening. The screen 50 also serves as the bottom cover of the crushing chamber 44. By opening the screen 50, the residue in the crushing chamber 44 can be taken out.

[0028] 3A is a horizontal rotation type that rotates the chain 60 in a horizontal plane, but the crushing and classifying device of the present disclosure is also applicable to a vertical rotation type chain crusher that rotates the chain in a vertical plane. There is no limit to the number of chains, and there is no limit to the number of metal rings that make up the chain.

[0029] 3. Test Results 3-1. Test to determine the optimum range of hammer corner R 4 is a diagram showing the results of confirming the relationship between the corner R of the hammer 30 of the hammer crusher 10 and the peeling rate of the active material. In the test, a screen 20 with an opening of 5 mm was used, and the rotation speed of the hammer 30 was set to 1100 rpm. A high-power lithium-ion battery (Li2.1) was used as the test specimen.

[0030] The test was performed twice when the corner R of the hammer 30 was 1 mm, three times when it was 6 mm, two times when it was 9 mm, and once when it was 12 mm. As a result of the test, it was confirmed that if the corner R of the hammer 30 was 1 mm, a peeling rate of about 62% or more could be obtained. It was also confirmed that if the corner R of the hammer 30 was 6 mm, a peeling rate of about 87% or more could be obtained. It was also confirmed that if the corner R of the hammer 30 was 9 mm, a peeling rate of about 72% or more could be obtained. On the other hand, it was confirmed that if the corner R of the hammer 30 was 12 mm, the peeling rate decreased to about 42%. What was directly confirmed from the test results was that if the corner R of the hammer 30 was in the range of 1 mm or more and 9 mm or less, a peeling rate of 60% or more could be obtained. In addition, the band shown in FIG. 4 is a prediction band showing the relationship between the corner R of the hammer 30 and the peeling rate predicted from the test results. As shown by this prediction band, it is predicted from the test results that if the corner R of the hammer 30 was in the range of 4 mm or more and 8 mm or less, a peeling rate of 80% or more could be obtained.

[0031] From the above confirmation results, it can be concluded that if a preferable peeling rate is 60% or more, then a preferable corner R of the hammer 30 is in the range of 1 mm or more and 9 mm or less. Also, if a preferable peeling rate is 80% or more, then a preferable corner R of the hammer 30 is in the range of 4 mm or more and 8 mm or less.

[0032] 3-2. Test to investigate the relationship between hammer rotation speed and peeling rate FIG. 5 is a diagram showing the results of confirming the relationship between the rotation speed of the hammer 30 of the hammer crusher 10 and the peeling rate of the active material. In the test, the corner R of the hammer 30 was set to 6 mm. As a result of testing a number of rotation speeds, the peeling rate increased as the rotation speed increased, and the highest peeling rate was obtained at a rotation speed of 1100 rpm. However, this does not mean that the rotation speed at which the peeling rate reaches its peak is 1100 rpm. It means that there is no significant change in the peeling rate at rotation speeds of 1100 rpm or more, so it is not necessary to increase the rotation speed beyond 1100 rpm. In other words, the higher the rotation speed of the hammer 30 of the hammer crusher 10, the more preferable it is, but above a certain rotation speed, the greater the disadvantage of increased power consumption becomes than the advantage of improved peeling rate.

[0033] 3-3. Test to confirm the peeling rate of active material 6 is a diagram showing the results of a peeling test using the hammer crusher 10. In the test, the hammer 30 used had a corner R of 6 mm, the screen 20 had an opening of 5 mm, and the rotation speed of the hammer 30 was set to 1100 rpm. A lithium ion battery and a nickel metal hydride battery were used as test specimens.

[0034] In the peeling test, the electrode material was crushed by the hammer crusher 10 to peel the active material from the current collector, and the peeling rate was investigated. The test pieces used in the peeling test were a high-power lithium-ion battery (Li2.1), a medium-capacity lithium-ion battery (Li3.A), a high-capacity lithium-ion battery (Li6.A), and a nickel-metal hydride battery (Ni-MH). The horizontal axis of the graph of the test results is the particle size of the crushed electrode material. The test results show that a peeling rate exceeding the target value of 80% was obtained in all samples. In other words, the test results confirmed that the hammer crusher 10 can recover active materials at a high recovery rate.

[0035] It is to be noted that the above test results for the hammer crusher 10 can also be considered to apply to the chain crusher 40. [Explanation of symbols]

[0036] 10 Hammer Crusher, 20 Screen, 21 Opening, 30 Hammer, 40 Chain Crusher, 50 Screen, 51 Opening, 60 Chain

Claims

1. a crushing chamber into which electrode materials for secondary batteries are introduced; A rotating shaft that is disposed in the crushing chamber and rotates by receiving a driving force; a rod-shaped or chain-shaped impacting body that is rotatably connected at one end to the rotating shaft and rotates in the crushing chamber by receiving a centrifugal force caused by the rotation of the rotating shaft; A screen is provided on a wall surface of the crushing chamber and classifies the crushed electrode material, The impacting body has at least a tip end having a rounded edge with a radius of curvature of 1 mm or more and 9 mm or less, The screen has openings of 5 mm or less. A crushing and classification device characterized by the above.

2. The crushing and classifying apparatus according to claim 1, The impacting body has an edge that is rounded with a radius of curvature of 1 mm to 9 mm over the entire area that may come into contact with the electrode material during rotation. A crushing and classification device characterized by the above.

3. The crushing and classifying apparatus according to claim 1 or 2, The edge is rounded to a radius of curvature of 4 mm or more and 8 mm or less. A crushing and classification device characterized by the above.

4. a crushing chamber into which the material to be treated is fed; A rotating shaft that is disposed in the crushing chamber and rotates by receiving a driving force; a rod-shaped or chain-shaped impacting body that is rotatably connected at one end to the rotating shaft and rotates in the crushing chamber by receiving a centrifugal force caused by the rotation of the rotating shaft; A method for crushing and classifying an electrode material of a secondary battery using a crushing and classifying device including a screen provided on a wall surface of the crushing chamber and classifying the crushed material to be treated, comprising: The impacting body has at least a tip end having a rounded edge with a radius of curvature of 1 mm or more and 9 mm or less, The screen has openings of 5 mm or less, The method comprises: charging the electrode material into the crushing chamber; rotating the impactor for a predetermined time to crush the electrode material; sieving the crushed electrode material through the screen; and separately recovering the powder sieved from the crushed electrode material and the residue in the crushing chamber. A method for crushing and classifying electrode materials, comprising the steps of: