Electromagnetic wave shielding film

Abstract

Provided is an electromagnetic wave shielding film that can easily exhibit exceptional electrical conductivity between a ground member and a shielding layer when the ground member is positioned on the electromagnetic wave shielding film.　An electromagnetic wave shielding film 1 has an electrically conductive adhesive layer 11, a shielding layer 12, and an insulating layer 13 laminated in the stated order. The ratio [electrically conductive adhesive layer / insulating layer] of the Martens hardness based on ISO 14577-1 of the electrically conductive adhesive layer 11 to the Martens hardness based on ISO 14577-1 of the insulating layer 13 is 0.3 or greater.

Description

[Technical field]

[0001] The present invention relates to an electromagnetic wave shielding film, and more particularly to an electromagnetic wave shielding film used for a printed wiring board. [Background technology]

[0002] Printed wiring boards are widely used in electronic devices such as mobile phones, video cameras, and laptops to incorporate circuits into their mechanisms. They are also used to connect moving parts such as printer heads to control units. Electromagnetic shielding is essential for these electronic devices, and shielded printed wiring boards with electromagnetic shielding are used for the printed wiring boards used within the devices.

[0003] A typical shielded printed wiring board is usually composed of a base film having a printed circuit and an insulating film sequentially provided on a base film, an adhesive layer, a shielding layer laminated on the adhesive layer, and an electromagnetic wave shielding film (hereinafter sometimes simply referred to as a "shielding film") which consists of an adhesive layer, a shielding layer laminated on the adhesive layer, and an insulating layer laminated on the adhesive layer, the adhesive layer being in contact with the base film.

[0004] The printed circuit includes a ground circuit, which is electrically connected to the housing of the electronic device to provide earthing. In order to electrically connect the ground circuit to the housing of the electronic device, it was necessary to pre-drill holes in parts of the insulating film and shielding film. This was a factor that restricted the degree of freedom in designing the printed circuit.

[0005] Patent Document 1 discloses a shielding film formed by coating one side of a separate film with an insulating layer (cover film), providing a shielding layer composed of a metal thin film layer and an adhesive layer on the surface of the insulating layer, and having a protrusion or conductive filler (connecting portion) on one end that is pressed against the insulating layer, penetrates the insulating layer and connects to the shielding layer, and has a ground member on the other end that is exposed and formed so as to be connectable to a ground portion nearby.

[0006] When producing the shielding film described in Patent Document 1, the ground member is pressed against the insulating layer so that the protrusions and conductive filler of the ground member penetrate the insulating layer. This electrically connects the ground member and the shielding layer, so that the ground member can be disposed at any position on the shielding film. When a shielded printed wiring board is produced using such a ground member, the ground circuit and the housing of the electronic device can be electrically connected at any position. [Prior art documents] [Patent documents]

[0007] [Patent Document 1] JP 2004-95566 A Summary of the Invention [Problem to be solved by the invention]

[0008] However, there were cases where the protrusions of the grounding member did not penetrate the insulating layer sufficiently and did not make sufficient contact with the shielding layer of the shielding film. Even when the protrusions of the grounding member and the conductive filler (hereinafter simply referred to as "protrusions") sufficiently penetrated the insulating layer, the protrusions of the grounding member, together with the shielding layer, pushed into and deformed the conductive adhesive layer located on the back side of the shielding layer, and the conductive filler in the conductive adhesive layer was pushed aside by the protrusions, causing the conductive filler to move and separate from the circuit. In these cases, the electrical resistance value increased, causing a problem of impaired connection between the grounding member, the shielding film, and the circuit of the printed wiring board.

[0009] The present invention has been made in consideration of the above, and an object of the present invention is to provide an electromagnetic wave shielding film that can easily achieve excellent conductivity between a grounding member and a shielding layer when the grounding member is placed on top of the electromagnetic wave shielding film. [Means for solving the problem]

[0010] As a result of intensive research to achieve the above object, the inventors have found that by specifying the relationship between the Martens hardness, which is an index showing the hardness of a microscopic region, of the insulating layer and the conductive adhesive layer in the shielding film, it is possible to easily achieve excellent conductivity between the grounding member and the shielding layer when the grounding member is disposed on the electromagnetic wave shielding film. The present invention was completed based on these findings.

[0011] That is, the present invention provides an electromagnetic wave shielding film in which a conductive adhesive layer, a shielding layer, and an insulating layer are laminated in this order, and the ratio of the Martens hardness based on ISO 14577-1 of the conductive adhesive layer to the Martens hardness based on ISO 14577-1 of the insulating layer [conductive adhesive layer / insulating layer] is 0.3 or more.

[0012] In the electromagnetic shielding film, the Martens hardness ratio of 0.3 or more indicates that the Martens hardness of the conductive adhesive layer is relatively large relative to the insulating layer. When the protrusion of the ground member is pressed to penetrate the insulating layer, the protrusion applies pressure locally to the laminated insulating layer, shield layer, and conductive adhesive layer. At this time, since the Martens hardness of the insulating layer is relatively low, the pressure is applied locally to the insulating layer, and the protrusion of the ground member can easily penetrate the insulating layer. When the protrusion of the ground member penetrates the insulating layer and contacts the shield layer, the Martens hardness of the conductive adhesive layer located on the back side of the shield layer is relatively high, so that the conductive adhesive layer is not easily deformed even by the pressure applied locally through the shield layer, and the contact between the conductive particles in the conductive adhesive layer and the shield layer, or between the conductive particles and the printed wiring board is not easily damaged. Therefore, in the electromagnetic shielding film having the above structure, the protrusion of the ground member that penetrates the insulating layer can stably contact the shield layer, and when the ground member is placed on the electromagnetic shielding film, excellent conductivity can be easily exhibited between the ground member and the shield layer.

[0013] The Martens hardness of the insulating layer based on ISO14577-1 is 3 to 150N / mm 2 In an electromagnetic wave shielding film having such a configuration, the local hardness of the insulating layer is appropriate, so that the projections of the grounding member can easily penetrate the insulating layer.

[0014] The Martens hardness of the conductive adhesive layer based on ISO14577-1 is 20 to 200 N / mm 2 In an electromagnetic wave shielding film having such a configuration, the local hardness of the conductive adhesive layer becomes appropriate, so that when the projection of the grounding member presses into the shielding layer, the conductive adhesive layer is unlikely to deform, or even if it does deform, it is likely to return to its original shape, and contact between the conductive particles in the conductive adhesive layer and the shielding layer, or between the conductive particles and the printed wiring board, is unlikely to be impaired. Effect of the Invention

[0015] The electromagnetic wave shielding film of the present invention can easily exhibit excellent electrical conductivity between the grounding member and the shielding layer when the grounding member is disposed on the electromagnetic wave shielding film. [Brief description of the drawings]

[0016] [Figure 1] 1 is a cross-sectional view illustrating an embodiment of an electromagnetic wave shielding film of the present invention. [Diagram 2] 1 is a schematic cross-sectional view showing one embodiment of a shielded printed wiring board using an electromagnetic wave shielding film of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0017] [Electromagnetic wave shielding film] The electromagnetic wave shielding film of the present invention comprises a conductive adhesive layer, a shielding layer which is a layer for blocking electromagnetic waves, and an insulating layer.

[0018] An embodiment of the electromagnetic wave shielding film of the present invention will be described below. Fig. 1 is a cross-sectional view showing an embodiment of the electromagnetic wave shielding film of the present invention.

[0019] The shielding film 1 shown in Fig. 1 has a conductive adhesive layer 11, a shielding layer 12 formed on the surface of the conductive adhesive layer 11, and an insulating layer 13 formed on the surface of the shielding layer 12. That is, in the shielding film 1, the conductive adhesive layer 11, the shielding layer 12, and the insulating layer 13 are laminated in this order. Note that the conductive adhesive layer 11 and the shielding layer 12, and the shielding layer 12 and the insulating layer 13 do not have to be laminated so as to be in contact with each other. That is, at least one arbitrary layer may be provided between the conductive adhesive layer and the shielding layer, or between the shielding layer and the insulating layer.

[0020] The ratio of the Martens hardness of the conductive adhesive layer to the Martens hardness of the insulating layer [conductive adhesive layer / insulating layer] is 0.3 or more, preferably 0.5 or more, more preferably 0.6 or more, and even more preferably 1.0 or more. The Martens hardness is a value measured based on ISO14577-1.

[0021] In the electromagnetic shielding film of the present invention, the Martens hardness ratio of 0.3 or more indicates that the Martens hardness of the conductive adhesive layer is relatively large relative to the insulating layer. When the protrusion of the ground member is pressed to penetrate the insulating layer, the protrusion applies pressure locally to the laminated insulating layer, shield layer, and conductive adhesive layer. At this time, since the Martens hardness of the insulating layer is relatively low, the pressure is applied locally to the insulating layer, and the protrusion of the ground member can easily penetrate the insulating layer. Then, when the protrusion of the ground member penetrates the insulating layer and contacts the shield layer, since the Martens hardness of the conductive adhesive layer located on the back side of the shield layer is relatively high, the conductive adhesive layer is not easily deformed even by the pressure applied locally through the shield layer, and the contact between the conductive particles in the conductive adhesive layer and the shield layer, or between the conductive particles and the printed wiring board is not easily damaged. Therefore, in the electromagnetic shielding film having the above structure, the protrusion of the ground member that penetrates the insulating layer can stably contact the shield layer, and when the ground member is placed on the electromagnetic shielding film, excellent conductivity can be easily exhibited between the ground member and the shield layer.

[0022] The Martens hardness ratio [conductive adhesive layer / insulating layer] is, for example, 50.0 or less, preferably 10.0 or less, more preferably 5.0 or less, even more preferably 3.0 or less, and particularly preferably 2.0 or less.

[0023] (Conductive adhesive layer) The conductive adhesive layer 11 has adhesiveness and conductivity for adhering the electromagnetic shielding film of the present invention to a printed wiring board, for example. The conductive adhesive layer is preferably formed adjacent to the electromagnetic shielding layer. The conductive adhesive layer may be either a single layer or multiple layers.

[0024] The conductive adhesive layer preferably contains a binder component and conductive particles.

[0025] The binder component includes a thermoplastic resin, a thermosetting resin, an active energy ray curable compound, etc. The binder component may be used alone or in combination of two or more.

[0026] Examples of the thermoplastic resin include polystyrene resins, vinyl acetate resins, polyester resins, polyolefin resins (e.g., polyethylene resins, polypropylene resin compositions, etc.), polyimide resins, acrylic resins, etc. Only one type of the thermoplastic resins may be used, or two or more types may be used.

[0027] The thermosetting resin includes both a resin having thermosetting properties (thermosetting resin) and a resin obtained by curing the thermosetting resin. The thermosetting resin includes, for example, a phenolic resin, an epoxy resin, a urethane resin, a melamine resin, an alkyd resin, etc. The thermosetting resin may be used alone or in combination of two or more kinds.

[0028] Examples of the epoxy resin include bisphenol type epoxy resins, spiro ring type epoxy resins, naphthalene type epoxy resins, biphenyl type epoxy resins, terpene type epoxy resins, glycidyl ether type epoxy resins, glycidyl amine type epoxy resins, and novolac type epoxy resins.

[0029] Examples of the bisphenol type epoxy resin include bisphenol A type epoxy resin, bisphenol F type epoxy resin, bisphenol S type epoxy resin, and tetrabromobisphenol A type epoxy resin. Examples of the glycidyl ether type epoxy resin include tris(glycidyloxyphenyl)methane and tetrakis(glycidyloxyphenyl)ethane. Examples of the glycidylamine type epoxy resin include tetraglycidyldiaminodiphenylmethane. Examples of the novolac type epoxy resin include cresol novolac type epoxy resin, phenol novolac type epoxy resin, α-naphthol novolac type epoxy resin, and brominated phenol novolac type epoxy resin.

[0030] The epoxy resin may be an epoxy resin (modified epoxy resin) containing a modified portion having self-reactivity in addition to the epoxy group, such as an epoxy resin having a (meth)acryloyl group (acrylic modified epoxy resin). When such a modified epoxy resin is used, it is easy to make the Martens hardness of the conductive adhesive layer within an appropriate range by utilizing crosslinking.

[0031] The active energy ray curable compound includes both a compound that can be cured by irradiation with active energy rays (active energy ray curable compound) and a compound obtained by curing the active energy ray curable compound. The active energy ray curable compound is not particularly limited, but includes, for example, a polymerizable compound having one or more (preferably two or more) radical reactive groups (e.g., (meth)acryloyl group) in the molecule. The active energy ray curable compound may be used alone or in combination of two or more.

[0032] Among them, the binder component is preferably a thermosetting resin. In this case, after the electromagnetic wave shielding film of the present invention is placed on a printed wiring board in order to adhere to the printed wiring board, the binder component can be cured by applying pressure and heat, resulting in good adhesion to the printed wiring board.

[0033] When the binder component contains a thermosetting resin, the binder component may contain a curing agent for accelerating the thermosetting reaction. The curing agent may be appropriately selected depending on the type of the thermosetting resin. The curing agent may be used alone or in combination of two or more.

[0034] The content of the binder component in the conductive adhesive layer is not particularly limited, but is preferably 5 to 60% by mass, more preferably 10 to 50% by mass, and even more preferably 20 to 45% by mass, relative to 100% by mass of the total amount of the conductive adhesive layer. If the content is 5% by mass or more, the adhesion to the printed wiring board is more excellent. If the content is 60% by mass or less, the conductive particles can be sufficiently contained.

[0035] Examples of the conductive particles include metal particles, metal-coated resin particles, metal fibers, carbon fillers, carbon nanotubes, etc. The conductive particles may be used alone or in combination of two or more kinds.

[0036] Examples of the metal constituting the metal particles and the coating portion of the metal-coated resin particles include gold, silver, copper, nickel, zinc, etc. Only one type of the metal may be used, or two or more types may be used.

[0037] Specific examples of the metal particles include copper particles, silver particles, nickel particles, silver-coated copper particles, gold-coated copper particles, silver-coated nickel particles, gold-coated nickel particles, and silver-coated alloy particles. Examples of the silver-coated alloy particles include silver-coated copper alloy particles in which alloy particles containing copper (e.g., copper alloy particles made of an alloy of copper, nickel, and zinc) are coated with silver. The metal particles can be produced by electrolysis, atomization, reduction, or the like.

[0038] As the metal particles, silver particles, silver-coated copper particles, and silver-coated copper alloy particles are preferred. From the viewpoints of excellent electrical conductivity, suppression of oxidation and aggregation of metal particles, and reduction of the cost of metal particles, silver-coated copper particles and silver-coated copper alloy particles are particularly preferred.

[0039] The conductive particles may have a spherical, flake (scale-like), dendritic, fibrous, amorphous (polyhedral) or other shape.

[0040] The conductive particles preferably have a median diameter (D50) of 1 to 50 μm, more preferably 3 to 40 μm. When the median diameter is 1 μm or more, the conductive particles have good dispersibility, can suppress aggregation, and are less likely to be oxidized. When the average particle diameter is 50 μm or less, the conductive particles have good conductivity. The median diameter can be measured from a volumetric particle size distribution.

[0041] The conductive adhesive layer may be a layer having isotropic conductivity or anisotropic conductivity as required. In particular, the conductive adhesive layer preferably has anisotropic conductivity from the viewpoint of improving the transmission characteristics of high-frequency signals transmitted through the signal circuit of the printed wiring board.

[0042] The content of the conductive particles in the conductive adhesive layer is not particularly limited, but is preferably 2 to 80 mass%, more preferably 5 to 60 mass%, and even more preferably 10 to 40 mass%, relative to 100 mass% of the total amount of the conductive adhesive layer. When the content is 2 mass% or more, the conductivity is better. When the content is 80 mass% or less, the binder component can be sufficiently contained, and the adhesion to the printed wiring board is better.

[0043] The conductive adhesive layer preferably contains a filler other than the conductive particles. By blending the filler, the Martens hardness of the conductive adhesive layer can be adjusted. The above fillers may be used alone or in combination of two or more.

[0044] As the filler, an inorganic filler or an organic filler can be used. From the viewpoint of increasing the Martens hardness of the conductive adhesive layer, an inorganic filler, an organic filler made of crosslinkable resin particles, and an organic phosphorus-based compound are preferable. Examples of the inorganic filler include metal oxides such as silica, boron oxide, alumina, titania, and zirconia; phosphorus compounds such as red phosphorus; metal carbides such as silicon carbide, boron carbide, and titanium carbide; metal nitrides such as aluminum nitride, boron nitride, and titanium nitride; metal hydroxides such as magnesium hydroxide and aluminum hydroxide; and carbonates such as calcium carbonate and magnesium carbonate. Examples of the crosslinkable resin particles include polyolefins such as polyethylene, polypropylene, polystyrene, polyvinyl chloride, polyvinylidene chloride, polytetrafluoroethylene, polyisobutylene, and polybutadiene; acrylic resins such as polymethyl methacrylate and polymethyl acrylate; copolymer resins of acrylate and divinylbenzene, polyalkylene terephthalate, polysulfone, polycarbonate, polyamide, phenol formaldehyde resin, melamine formaldehyde resin, benzoguanamine formaldehyde resin, and urea formaldehyde resin. Examples of the organic phosphorus-based compounds include phosphorus-based compounds such as phosphoric acid esters and metal phosphinates. When the organic filler is a phosphorus-based compound such as phosphoric acid esters and metal phosphinates, it also functions as a flame retardant, so that it is possible to control the Martens hardness and simultaneously impart flame retardancy.

[0045] The median diameter (D50) of the filler is preferably 0.01 to 100 μm, more preferably 1 to 20 μm, from the viewpoint of facilitating control of the Martens hardness of the conductive adhesive layer. The median diameter can be measured from the volume-based particle size distribution.

[0046] The content of the filler in the conductive adhesive layer is not particularly limited, but is preferably 1 to 70 mass%, more preferably 10 to 60 mass%, and even more preferably 35 to 50 mass%, relative to 100 mass% of the total amount of the conductive adhesive layer. When the content is within the above range, the Martens hardness can be easily adjusted within an appropriate range while maintaining the conductivity and adhesion to the printed wiring board.

[0047] The conductive adhesive layer may contain other components in addition to the above-mentioned components within a range that does not impair the effects of the present invention. Examples of the other components include components contained in publicly known or commonly used adhesive layers. Examples of the other components include flame retardants, flame retardant assistants, defoamers, viscosity modifiers, antioxidants, diluents, antisettling agents, colorants, leveling agents, coupling agents, ultraviolet absorbers, tackifier resins, etc. that do not fall under the above-mentioned fillers. Only one type of the other components may be used, or two or more types may be used.

[0048] The Martens hardness of the conductive adhesive layer is 20 to 200 N / mm 2 is preferable, and more preferably 30 to 180 N / mm 2 , and more preferably 50 to 170 N / mm 2 When the Martens hardness is within the above range, the local hardness of the conductive adhesive layer becomes appropriate, so that when the projection of the grounding member presses into the shielding layer, the conductive adhesive layer is unlikely to deform, or even if it does deform, it is likely to return to its original shape, and the contact between the conductive adhesive layer and the shielding layer, or between the conductive particles and the printed wiring board is unlikely to be impaired. 2 When the hardness is not more than 100%, the adhesion to the printed wiring board is good. The Martens hardness of the conductive adhesive layer is a value measured in accordance with ISO14577-1, and is measured on the surface on the shield layer side.

[0049] The conductive adhesive layer has a thickness of preferably 3 to 20 μm, more preferably 5 to 15 μm. When the thickness is 3 μm or more, the film can exhibit sufficient shielding performance as a shielding film that blocks electromagnetic waves in a high frequency band generated inside. When the thickness is 20 μm or less, the film has excellent flexibility.

[0050] (Shield layer) The shield layer 12 is formed on the surface of the conductive adhesive layer 11. As the shield layer, a known or commonly used shield layer having electromagnetic wave shielding properties can be used. Among them, the shield layer preferably includes a metal layer. The shield layer may be either a single layer or a multi-layer.

[0051] Examples of the metal constituting the metal layer include gold, silver, copper, aluminum, nickel, tin, palladium, chromium, titanium, zinc, and alloys thereof. The metal layer is preferably a metal plate or metal foil. That is, the metal layer is preferably a copper plate (copper foil) or a silver plate (silver foil).

[0052] The thickness of the shielding layer is preferably 0.01 to 10 μm. If the thickness is 0.01 μm or more, more sufficient shielding performance can be obtained. If the thickness is 10 μm or less, the bending property is better.

[0053] (insulating layer) The insulating layer 13 is formed on the surface of the shielding layer 12. The insulating layer 13 has insulating properties and functions to protect the conductive adhesive layer 11 and the shielding layer 12 in the electromagnetic wave shielding film 1 of the present invention. The insulating layer may be either a single layer or multiple layers.

[0054] The insulating layer preferably contains a binder component. Examples of the binder component include a thermoplastic resin, a thermosetting resin, and an active energy ray curable compound. Examples of the thermoplastic resin, the thermosetting resin, and the active energy ray curable compound include those exemplified as the binder components that may be contained in the conductive adhesive layer. The binder component may be used in a single type or in combination of two or more types. The binder component preferably contains a thermosetting resin and an active energy ray curable compound.

[0055] The insulating layer may contain other components other than the binder component within a range that does not impair the effects of the present invention. Examples of the other components include flame retardants, flame retardant assistants, defoamers, viscosity modifiers, antioxidants, diluents, antisettling agents, fillers, colorants, leveling agents, coupling agents, ultraviolet absorbers, tackifier resins, etc. Only one type of the other components may be used, or two or more types may be used.

[0056] The Martens hardness of the insulating layer is 3 to 200 N / mm 2 and more preferably 30 to 150 N / mm 2 , and more preferably 50 to 140 N / mm 2 , particularly preferably 70 to 130 N / mm 2 When the Martens hardness is within the above range, the local hardness of the insulating layer becomes appropriate, so that the projection of the grounding member can easily penetrate the insulating layer. 2 If the Martens hardness is 200 N / mm or more, the surface of the insulating layer is appropriately hard, so that the projection of the grounding member can easily pierce the protective layer. 2If the hardness is less than 100%, the surface of the insulating layer is appropriately soft, so that the projection of the grounding member can easily penetrate the insulating layer. The Martens hardness of the insulating layer can be adjusted by, for example, designing the degree of hardening of the thermosetting component constituting the insulating layer, the type of hardener, or the type of binder component. The Martens hardness of the insulating layer is a value measured based on ISO14577-1, and is measured on the surface of the insulating layer opposite to the shield layer side.

[0057] The thickness of the insulating layer is preferably 1 to 15 μm, and more preferably 3 to 10 μm. If the thickness is 1 μm or more, the shield layer and the conductive adhesive layer can be protected more sufficiently. If the thickness is 15 μm or less, the flexibility is excellent and it is also economically advantageous.

[0058] The electromagnetic wave shielding film of the present invention may have other layers in addition to the above layers. For example, the other layers may include an anchor coat layer provided between the insulating layer and the shielding layer. When the anchor coat layer is present, the adhesion between the insulating layer and the shielding layer is improved.

[0059] Materials for forming the anchor coat layer include urethane resins, acrylic resins, core-shell composite resins with urethane resin as the shell and acrylic resin as the core, epoxy resins, polyimide resins, polyamide resins, melamine resins, phenolic resins, urea-formaldehyde resins, blocked isocyanates obtained by reacting polyisocyanates with blocking agents such as phenol, polyvinyl alcohol, polyvinylpyrrolidone, etc. Only one of the above materials may be used, or two or more of them may be used.

[0060] The electromagnetic wave shielding film of the present invention may have a separator (release film) on the insulating layer side and / or the conductive adhesive layer side. The separator is laminated so as to be peelable from the electromagnetic wave shielding film of the present invention. The separator is an element for covering and protecting the insulating layer and the conductive adhesive layer, and is peeled off when the electromagnetic wave shielding film of the present invention is used.

[0061] Examples of the separator include polyethylene terephthalate (PET) film, polyethylene film, polypropylene film, plastic films and papers whose surfaces are coated with a release agent such as a fluorine-based release agent or a long-chain alkyl acrylate-based release agent.

[0062] The thickness of the separator is preferably 10 to 200 μm, and more preferably 15 to 150 μm. If the thickness is 10 μm or more, the protective performance is more excellent. If the thickness is 200 μm or less, the separator is easily peeled off during use.

[0063] The electromagnetic wave shielding film of the present invention is preferably used for a printed wiring board, particularly preferably for a flexible printed wiring board (FPC). The electromagnetic wave shielding film of the present invention can be preferably used as an electromagnetic wave shielding film for a flexible printed wiring board.

[0064] [Shielded printed wiring board] Fig. 2 shows one embodiment of a shielding film printed wiring board including a shielding film 1 which is an electromagnetic wave shielding film of the present invention. The shielding printed wiring board X shown in Fig. 2 includes a printed wiring board 2, a shielding film 1, and a ground member 3. An electronic component 4 is connected to a mounting portion provided on the lower surface of the printed wiring board 2. The shielding film 1 is provided on the printed wiring board 2, and is arranged up to an area facing the mounting portion to which the electronic component 4 is connected. In this way, the shielding film 1 is used to shield the mounting portion of the electronic component 4 from noise such as external electromagnetic waves.

[0065] The ground member 3 is provided on the shielding film 1 and is disposed opposite to a mounting portion to which an electronic component 4 is connected. In FIG. 2, the ground member 3 is composed of a conductive base material 31 and a conductive adhesive 32, and is attached to the insulating layer 13 of the shielding film 1 by the adhesive 3a of the conductive adhesive 32. The conductive particles 3b contained in the conductive adhesive 32 protrude from the adhesive 3a contained in the conductive adhesive 32. The conductive base material 31 bonded via the conductive adhesive 32 is in contact with the conductive particles 3b. Meanwhile, the conductive particles 3b protruding from the lower surface of the conductive adhesive 32 break through the insulating layer 13 of the shielding film 1 as a protrusion provided on the ground member 3, and are in contact with the shielding layer 12 thereunder. As a result, the conductive base material 31 and the shielding layer 12 of the shielding film 1 are in a conductive state via the conductive particles 3b of the conductive adhesive 32, and the conductive ground member 3 and the shielding layer 12 can be at the same potential. Therefore, the conductive ground member 3 can be provided with a shielding effect. Furthermore, by bringing the ground member 3 into contact with the shielding layer 12, the ground member 3 is able to have at least the dual functions of reinforcing the mounting location of the electronic component 4 and blocking noise, such as external electromagnetic waves, from the mounting location of the electronic component 4.

[0066] The state in which the protrusions of the ground member 3 penetrate the insulating layer 13 of the shielding film 1 and contact the shielding layer 12 is not limited to the embodiment in which the conductive particles 3b of the conductive adhesive 32 act as protrusions as shown in FIG. 2. For example, the ground member is formed by folding a conductive base material 31 such as a metal foil, and is laminated on the insulating layer 13 without the conductive adhesive 32, and the mountain fold of the conductive base material 31 acts as a protrusion of the ground part and penetrates the insulating layer 13 to contact the shielding layer 12. Another embodiment is a mode in which the ground member is formed from a conductive layer such as a metal foil, and a conductive protrusion of metal or the like is provided integrally or non-integrally on one side of the conductive layer, and is laminated on the insulating layer 13 without the conductive adhesive 32, and the conductive protrusion acts as a protrusion of the ground part and penetrates the insulating layer 13 to contact the shielding layer 12. The shape of the conductive protrusions can be a columnar shape such as a cylinder or a rectangular column, or a pyramid shape such as a cone or a pyramid.

[0067] The printed wiring board 2 has a base member 21, a circuit pattern 23 partially provided on the surface of the base member 21, an insulating protection layer (coverlay) 24 that covers and insulates the circuit pattern 23, and an adhesive layer 22 that covers the circuit pattern 23 and bonds the circuit pattern 23 and the base member 21 to the insulating protection layer 24. The circuit pattern 23 includes a plurality of signal circuits 23a and a ground circuit 23b. In the adhesive layer 22 and the insulating protection layer 24 on the ground circuit 23b, a through hole 25 is formed for the purpose of ensuring conduction with the conductive adhesive layer 11 of the shielding film 1.

[0068] The shielded printed wiring board X shown in Fig. 2 can be produced by placing a ground member 3 on a shielding film 1 and then hot pressing. The hot pressing is generally carried out under conditions of a temperature of about 150 to 190°C, a pressure of about 1 to 3 MPa, and a time of about 1 to 60 minutes. In order to promote curing, a post cure may be carried out at 150 to 190°C for 30 to 90 minutes after the hot pressing. EXAMPLES

[0069] The present invention will be described in more detail below based on examples, but the present invention is not limited to these examples. The amounts listed in the tables are the relative amounts of each component, and are expressed in "parts by mass" unless otherwise specified.

[0070] Example 1 (1) Formation of insulating layer A resin composition consisting of an acrylic-modified epoxy resin and an acrylic resin was prepared in the ratio shown in Table 1 on the release-treated surface of the base material, a separate film. The resin composition was applied so that the thickness of the insulating layer formed was 3 μm, and the insulating layer was formed by heat treatment at 100° C. for 120 seconds.

[0071] (2) Formation of a shield layer On the insulating layer obtained above, a silver layer having a thickness of 0.1 μm was formed by vapor deposition.

[0072] (3) Formation of a conductive adhesive layer and an electromagnetic wave shielding film Silver-coated copper powder was added to a composition containing a phosphorus-based flame retardant and an acrylic-modified epoxy resin so that the content ratio in the conductive adhesive layer was 20 mass %, to prepare an adhesive composition. The adhesive composition was then coated on the shield layer obtained above so as to have a thickness of 15 μm, to form a coating film. The coating method used was a lip coat method. The coating film was then heated at 100° C. for 30 seconds to volatilize the solvent component of the coating film, to form a conductive adhesive layer. In this manner, an electromagnetic wave shielding film having a structure of conductive adhesive layer / shielding layer / insulating layer was produced.

[0073] Examples 2 to 7 and Comparative Example 1 An electromagnetic wave shielding film was produced in the same manner as in Example 1, except that the components constituting the insulating layer and the conductive adhesive layer were changed as shown in Table 1.

[0074] (evaluation) The electromagnetic wave shielding films obtained in the Examples and Comparative Examples were evaluated as follows. The evaluation results are shown in Table 1.

[0075] (1) Martens hardness of the insulating layer For each of the electromagnetic wave shielding films obtained in the Examples and Comparative Examples, a test sample of 1 mm square was cut out, the separator on the insulating layer was peeled off, and the Martens hardness of the insulating layer surface was measured using a dynamic microhardness tester (product name "DUH-211", manufactured by Shimadzu Corporation) under the following conditions. Indenter shape: triangular pyramid (115°) Measurement method: Single indentation measurement Measurement temperature: 23℃ Load: 0.10mN Load speed: 0.0060mN / s Load holding time: 2s Unloading holding time: 0s

[0076] (2) Martens hardness of the conductive adhesive layer For each of the conductive adhesive layers produced in the examples and comparative examples, the Martens hardness was measured in the same manner as for the insulating layer.

[0077] (3) Connection resistance i) Preparation of ground member Silver-coated nickel powder (average particle size 28 μm) was added to the epoxy resin composition so that the content in the conductive adhesive layer was 35 mass % to prepare an adhesive composition. The adhesive composition was then coated onto a 0.2 mm thick SUS sheet so that the thickness of the conductive adhesive layer formed was 30 μm. The sheet was then heated at 100° C. for 30 seconds to volatilize the solvent components of the coating film and form a conductive adhesive layer. In this manner, a ground member consisting of a SUS sheet / conductive adhesive layer was produced. ii) Connection resistance measurement The ground members obtained above were cut into test samples of 10 mm square, and placed at 10 mm intervals on the surface of the insulating layer of each of the electromagnetic shielding films obtained in the examples and comparative examples, and bonded by hot pressing to prepare measurement samples. The hot pressing was performed under conditions of a temperature of 170°C, a pressure of 3 MPa, and a time of 30 minutes, and then post cured at 150°C for 30 minutes. The connection resistance between adjacent ground members was then measured via the shielding layer of the electromagnetic shielding film.

[0078] [Table 1]

[0079] It was determined that the electromagnetic wave shielding film (Examples) of the present invention had a low connection resistance between adjacent ground members and exhibited excellent conductivity between the ground members and the shielding layer. On the other hand, when the ratio of the Martens hardness of the conductive adhesive layer to the Martens hardness of the insulating layer was less than 0.3 (Comparative Example 1), the connection resistance between adjacent ground members exceeded the measurement limit. [Explanation of symbols]

[0080] 1. Electromagnetic wave shielding film 11 Conductive adhesive layer 12 Shielding Layer 13 Insulating layer X-shielded printed wiring board 2. Printed Wiring Board 21 Base material 22 Adhesive layer 23 Circuit Pattern 23a signal circuit 23b Ground Circuit 24 Insulating protective layer (coverlay) 25 through hole 3 Grounding material 31 Conductive substrate 32 Conductive adhesive 3a Adhesive 3b Conductive particles 4. Electronic Components

Claims

1. A conductive adhesive layer, a shield layer, and an insulating layer are laminated in this order, a ratio of the Martens hardness based on ISO 14577-1 of the conductive adhesive layer to the Martens hardness based on ISO 14577-1 of the insulating layer [conductive adhesive layer / insulating layer] is 0.5 or more; The electromagnetic wave shielding film is used by placing a ground member on the electromagnetic wave shielding film and pressing the projections of the ground member so as to penetrate the insulating layer.

2. The insulating layer has a Martens hardness of 3 to 150 N / mm based on ISO 14577-1. 2 The electromagnetic wave shielding film according to claim 1 ,

3. The conductive adhesive layer has a Martens hardness of 20 to 200 N / mm based on ISO 14577-1. 2 The electromagnetic wave shielding film according to claim 1 or 2,