Non-aqueous secondary battery

Abstract

To provide a nonaqueous secondary battery in which the defect of a collection foil occurring when a positive electrode side current collection part is formed can be suppressed.SOLUTION: An electrode body 20 in which a positive electrode plate 21 and a negative electrode plate 25 are stacked in a stacking direction D3 through a separator 28 is provided. The positive electrode plate 21 includes a positive electrode base material 22, a positive electrode mixture layer 23, and insulating layers. The positive electrode base material 22 includes a positive electrode side non-coated part 22A where neither the positive electrode mixture layer 23 nor the insulating layer is provided. The electrode body 20 includes a positive electrode side current collection part 20A where the positive electrode side non-coated part 22A is stacked in the stacking direction D3. The insulating layer exists at a border between the positive electrode mixture layer 23 and the positive electrode side non-coated part 22A. The insulating layer that exists on a central side of the positive electrode current collection part 20A in the stacking direction D3 relative to the positive electrode base material 22 is a first insulating layer 24A. The insulating layer that exists on the side opposite to the first insulating layer 24A relative to the positive electrode base material 22 is a second insulating layer 24B. The thickness of the first insulating layer 24A is larger than that of the second insulating layer 24B.SELECTED DRAWING: Figure 5

Description

[Technical field]

[0001] The present invention relates to a non-aqueous secondary battery. [Background technology]

[0002] Electric vehicles and hybrid vehicles are equipped with non-aqueous secondary batteries as their power sources. A lithium ion secondary battery, which is an example of a non-aqueous secondary battery, is equipped with an electrode body in which a positive electrode plate and a negative electrode plate are stacked with a separator interposed therebetween and wound. The positive electrode plate includes a foil-shaped positive electrode substrate, and a positive electrode mixture layer and an insulating layer provided on the positive electrode substrate (for example, Patent Document 1). The positive electrode substrate includes a positive electrode side uncoated portion in which the positive electrode substrate is exposed without being coated with the positive electrode mixture layer and the insulating layer. The positive electrode side uncoated portion is used as a positive electrode side current collector that is responsible for connection to an external terminal by pressing a plurality of layers together in a stacked state. The insulating layer is located at the boundary between the positive electrode mixture layer and the positive electrode side uncoated portion. The insulating layer is responsible for preventing a short circuit between the positive electrode side uncoated portion and the negative electrode plate. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Patent Publication No. 2021-089857 Summary of the Invention [Problem to be solved by the invention]

[0004] From the viewpoint of suppressing the deterioration of the battery performance, it is preferable that the insulating layer is arranged so as not to narrow the width of the positive electrode mixture layer as much as possible. Moreover, from the viewpoint of suppressing the increase in size of the battery, the insulating layer is arranged so as to narrow the width of the positive electrode side uncoated part so as not to increase the width of the entire positive electrode plate. Then, when the positive electrode side uncoated parts are stacked and pressed together, the width of the positive electrode side uncoated part may be insufficient. As a result, there is a risk of a foil collection failure, such as a part of the positive electrode substrate being torn or the layers of the positive electrode side uncoated part not being properly joined to each other. [Means for solving the problem]

[0005] a positive electrode mixture layer and an insulating layer provided on each of two surfaces of the positive electrode substrate that face in opposite directions, the positive electrode substrate having a positive electrode-side uncoated portion where neither the positive electrode mixture layer nor the insulating layer is provided, the electrode substrate having a positive electrode-side current collecting portion on which the positive electrode-side uncoated portion is laminated in the stacking direction, the insulating layer being located at the boundary between the positive electrode mixture layer and the positive electrode-side uncoated portion, the insulating layer provided on a first surface of the positive electrode substrate that faces a center of the positive electrode-side current collecting portion in the stacking direction is a first insulating layer, the insulating layer provided on a second surface of the positive electrode substrate that is opposite to the first surface is a second insulating layer, and the thickness of the first insulating layer is greater than the thickness of the second insulating layer.

[0006] The insulating layer is formed by applying the insulating layer in a paste state to the positive electrode substrate and then drying the paste. When the insulating layer dries from the paste state, the volume of the insulating layer decreases, causing a contraction stress to act on the positive electrode substrate. By making the thickness of the first insulating layer larger than the thickness of the second insulating layer, the contraction stress applied to the positive electrode substrate by the first insulating layer becomes larger than the contraction stress applied to the positive electrode substrate by the second insulating layer. Due to the contraction stress difference between the first insulating layer and the second insulating layer, the positive electrode substrate is subjected to a resultant force that bends the substrate toward the center of the positive electrode side current collector in the stacking direction. Therefore, the foil collection property is improved when forming the positive electrode side current collector. As a result, foil collection failure can be suppressed.

[0007] In the nonaqueous secondary battery, the thickness of the first insulating layer is preferably 1.2 to 1.7 times the thickness of the second insulating layer. If the thickness of the first insulating layer is 1.2 times or more the thickness of the second insulating layer, the difference in shrinkage stress between the first insulating layer and the second insulating layer can be suitably applied to the positive electrode substrate. If the thickness of the first insulating layer is 1.7 times or less the thickness of the second insulating layer, it is possible to prevent the second insulating layer from becoming too thin and thereby preventing a lack of mechanical strength.

[0008] In the nonaqueous secondary battery, it is preferable that the first insulating layer has a thickness of 5.0 μm or more and 20.0 μm or less, and the second insulating layer has a thickness of 3.0 μm or more and 16.0 μm or less. This configuration ensures the mechanical strength of the first insulating layer and the second insulating layer, suppresses a decrease in foil collecting ability due to an increase in the thickness of the first insulating layer, and achieves an effect of improving foil collecting ability due to a difference in contraction stress between the first insulating layer and the second insulating layer with respect to the positive electrode substrate.

[0009] In the nonaqueous secondary battery, the mass ratio of the binder is preferably 10% by mass or more and 30% by mass or less with respect to the mass of the insulating layer. By making the binder content of the insulating layer 30% by mass or less, it is possible to prevent the mechanical strength of the insulating layer from being excessively reduced. By making the binder content of the insulating layer 10% by mass or more, it is possible to ensure the peel strength between the insulating layer and the positive electrode substrate, and to favorably express the shrinkage stress difference between the first insulating layer and the second insulating layer.

[0010] In the nonaqueous secondary battery, the width of the first insulating layer and the second insulating layer is preferably 2.5 mm or more and 4.5 mm or less. By making the width of the first insulating layer and the second insulating layer 2.5 mm or more, it is possible to preferably prevent a short circuit between the positive electrode side uncoated portion and the negative electrode plate while preferably realizing a shrinkage stress difference between the first insulating layer and the second insulating layer. By making the width of the first insulating layer and the second insulating layer 4.5 mm or less, it is possible to prevent the width of the positive electrode side uncoated portion from becoming excessively small. Effect of the Invention

[0011] According to the present invention, it is possible to suppress foil collection defects when forming a positive electrode side current collecting portion. [Brief description of the drawings]

[0012] [Figure 1] FIG. 1 is a perspective view of a lithium ion secondary battery. [Diagram 2] FIG. 2 is a perspective view showing the electrode body in an expanded state. [Diagram 3] FIG. 3 is a cross-sectional view taken along line III-III in FIG. [Figure 4] FIG. 4 is an enlarged cross-sectional view of a main portion showing an uncoated portion on the positive electrode side before the positive electrode current collecting portion is formed. [Diagram 5] FIG. 5 is an enlarged cross-sectional view of a main part of the positive electrode side current collecting portion. [Figure 6] FIG. 6 is an enlarged cross-sectional view of a main portion of a positive electrode-side uncoated portion after the positive electrode-side current collecting portion has been constructed. [Figure 7] FIG. 7 is a flowchart showing the manufacturing process of a lithium ion secondary battery. [Figure 8] FIG. 8 is a table showing the parameters of the examples and comparative examples. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0013] [Lithium-ion secondary battery] As shown in FIG. 1, a lithium ion secondary battery 10, which is an example of a non-aqueous secondary battery, includes a case 11 and an electrode assembly 20. The case 11 includes a storage section 11A and a lid 12. The storage section 11A has a flat, bottomed, rectangular outer shape with an opening on the upper side. The storage section 11A stores the electrode assembly 20 and a non-aqueous electrolyte. The lid 12 closes the opening of the storage section 11A. The case 11 forms a sealed rectangular parallelepiped battery container by attaching the lid 12 to the storage section 11A. The case 11 is made of a metal such as aluminum or an aluminum alloy.

[0014] The lid 12 is provided with a positive external terminal 13A and a negative external terminal 13B. The positive electrode side current collector 20A, which is the end of the electrode body 20 on the positive electrode side, is electrically connected to the positive electrode external terminal 13A via a positive electrode side current collector 14A. The negative electrode side current collector 20B, which is the end of the electrode body 20 on the negative electrode side, is electrically connected to the negative electrode external terminal 13B via a negative electrode side current collector 14B. The lid 12 also includes an injection port 15 for injecting a nonaqueous electrolyte. The shapes of the external terminals 13A and 13B are not limited to those shown in FIG. 1 and may be any shape.

[0015] [Electrode body] As shown in FIG. 2, the electrode body 20 is a flat wound body formed by winding a laminate in which a long positive electrode plate 21 and a negative electrode plate 25 are stacked with a separator 28 interposed therebetween. The positive electrode plate 21, the negative electrode plate 25, and the separator 28 are stacked so that their respective longitudinal directions coincide with the longitudinal direction D1. In the laminate before winding, the positive electrode plate 21, the separator 28, the negative electrode plate 25, and the separator 28 are stacked in this order in the stacking direction D3 (see FIG. 3). The electrode body 20 has a structure in which the positive electrode plate 21 and the negative electrode plate 25 stacked with the separator 28 sandwiched therebetween are wound around a winding axis L1 extending in the width direction D2 of the band shape.

[0016] [Positive plate] As shown in FIG. 3, the positive electrode plate 21 includes a positive electrode substrate 22, a positive electrode mixture layer 23, and an insulating layer 24. The positive electrode substrate 22 is a foil-like member formed in an elongated shape. The positive electrode mixture layer 23 and the insulating layer 24 are provided on two surfaces of the positive electrode substrate 22 that face in opposite directions. The positive electrode substrate 22 includes a positive electrode-side uncoated portion 22A at one end in the width direction D2 where neither the positive electrode mixture layer 23 nor the insulating layer 24 is formed and the positive electrode substrate 22 is exposed. The insulating layer 24 is located at the boundary between the positive electrode-side uncoated portion 22A and the positive electrode mixture layer 23. The insulating layer 24 prevents the positive electrode-side uncoated portion 22A and the negative electrode plate 25 from being short-circuited via foreign matter or the like.

[0017] A metal foil made of aluminum or an alloy mainly composed of aluminum is used for the positive electrode substrate 22. The positive electrode side uncoated portion 22A of the positive electrode substrate 22 is pressed against the positive electrode substrate 22 so that the opposing portions are stacked in the stacking direction D3 in the wound body state to form the positive electrode side current collecting portion 20A.

[0018] The positive electrode mixture layer 23 is a hardened body of a liquid positive electrode mixture paste. The positive electrode mixture paste includes a positive electrode active material, a positive electrode solvent, a positive electrode conductive agent, and a positive electrode binder. The positive electrode mixture layer 23 is formed by drying the positive electrode mixture paste and evaporating the positive electrode solvent. Therefore, the positive electrode mixture layer 23 includes a positive electrode active material, a positive electrode conductive agent, and a positive electrode binder.

[0019] The positive electrode active material is a lithium-containing composite metal oxide capable of absorbing and releasing lithium ions, which are charge carriers in the lithium-ion secondary battery 10. The lithium-containing composite oxide is an oxide containing lithium and a metal element other than lithium. The metal element other than lithium is at least one selected from the group consisting of nickel, cobalt, manganese, vanadium, magnesium, molybdenum, niobium, titanium, tungsten, aluminum, and iron contained in the lithium-containing composite oxide as iron phosphate.

[0020] For example, the lithium-containing composite oxide is lithium cobalt oxide (LiCoO2), lithium nickel oxide (LiNiO2), or lithium manganese oxide (LiMn2O4). For example, the lithium-containing composite oxide is a ternary lithium-containing composite oxide (NCM) containing nickel, cobalt, and manganese, which is lithium nickel cobalt manganese oxide (LiNiCoMnO2). For example, the lithium-containing composite oxide is lithium iron phosphate (LiFePO4).

[0021] The positive electrode solvent is an NMP (N-methyl-2-pyrrolidone) solution, which is an example of an organic solvent. The positive electrode conductive agent is, for example, carbon black such as acetylene black (AB) or Ketjen black, carbon fiber such as carbon nanotube (CNT) or carbon nanofiber, or graphite. The positive electrode binder is an example of a resin component contained in the positive electrode mixture paste. The positive electrode binder is, for example, polyvinylidene fluoride (PVDF), polyvinyl alcohol (PVA), styrene butadiene rubber (SBR), or the like.

[0022] The insulating layer 24 is a hardened product of the insulating paste in a liquid state. The insulating paste contains an inorganic component for the insulating layer having insulating properties, a binder for the insulating layer, and a solvent for the insulating layer. The insulating layer 24 is formed by drying the insulating paste and evaporating the solvent for the insulating layer. Therefore, the insulating layer 24 contains an inorganic component for the insulating layer and a binder for the insulating layer.

[0023] The inorganic component for the insulating layer is at least one selected from the group consisting of powdered boehmite, titania, and alumina. The binder for the insulating layer is a resin component soluble in the solvent for the insulating layer, and is at least one selected from the group consisting of, for example, PVDF, PVA, SBR, and acrylic. The solvent component is an organic solvent or water. An example of the organic solvent is an NMP solution.

[0024] The mass ratio of the insulating layer binder to the total mass of the insulating layer 24 is, for example, 10 mass% or more and 30 mass% or less. If the mass ratio of the insulating layer binder is 10 mass% or more, it is possible to ensure the peel strength between the insulating layer 24 and the positive electrode substrate 22. If the mass ratio of the insulating layer binder is 30 mass% or less, it is possible to prevent an excessive decrease in the mechanical strength of the insulating layer 24 that accompanies a relative decrease in the mass ratio of the insulating layer inorganic component.

[0025] [Negative plate] The negative electrode plate 25 includes a negative electrode substrate 26 and a negative electrode mixture layer 27. The negative electrode substrate 26 is a foil-like member formed in an elongated shape. The negative electrode mixture layer 27 is provided on each of two surfaces of the negative electrode substrate 26 that face in opposite directions. The negative electrode substrate 26 includes a negative electrode-side uncoated portion 26A at one end in the width direction D2, which is located opposite the positive electrode-side uncoated portion 22A, where the negative electrode mixture layer 27 is not formed and the negative electrode substrate 26 is exposed.

[0026] A metal foil made of copper or an alloy mainly composed of copper is used for the negative electrode substrate 26. In the negative electrode uncoated portion 26A, when wound, opposing surfaces are pressed against each other to form the negative electrode current collecting portion 20B.

[0027] The negative electrode mixture layer 27 is a hardened body of the liquid negative electrode mixture paste. The negative electrode mixture paste contains a negative electrode active material, a negative electrode solvent, a negative electrode thickener, and a negative electrode binder. The negative electrode mixture layer 27 is formed by drying the negative electrode mixture paste and evaporating the negative electrode solvent. Therefore, the negative electrode mixture layer 27 contains a negative electrode active material, a negative electrode thickener, and a negative electrode binder. The negative electrode mixture layer 27 may further contain an additive such as a conductive agent.

[0028] The negative electrode active material is a material capable of absorbing and releasing lithium ions. For example, carbon materials such as graphite, non-graphitizable carbon, graphitizable carbon, and carbon nanotubes are used as the negative electrode active material. The negative electrode active material may be composite particles in which graphite particles are coated with an amorphous carbon layer.

[0029] The negative electrode solvent is, for example, water. The negative electrode dispersant can be, for example, carboxymethyl cellulose (CMC). The negative electrode binder can be the same as the positive electrode binder. The negative electrode binder can be, for example, SBR.

[0030] [Separator] The separator 28 prevents contact between the positive electrode plate 21 and the negative electrode plate 25, and retains a nonaqueous electrolyte between the positive electrode plate 21 and the negative electrode plate 25. When the electrode body 20 is immersed in a nonaqueous electrolyte, the nonaqueous electrolyte permeates the separator 28 from the ends toward the center.

[0031] The separator 28 is a nonwoven fabric made of polypropylene, etc. As the separator 28, for example, a porous polymer membrane such as a porous polyethylene membrane, a porous polyolefin membrane, a porous polyvinyl chloride membrane, an ion-conductive polymer electrolyte membrane, etc. can be used.

[0032] [Nonaqueous electrolyte] The non-aqueous electrolyte is a composition in which a supporting salt is contained in a non-aqueous solvent. The non-aqueous solvent is, for example, one or more materials selected from the group consisting of propylene carbonate, ethylene carbonate, diethyl carbonate, dimethyl carbonate, and ethyl methyl carbonate. The supporting salt is, for example, one or more lithium compounds (lithium salts) selected from LiPF6, LiBF4, LiClO4, LiAsF6, LiCF3SO3, LiC4F9SO3, LiN(CF3SO2)2, LiC(CF3SO2)3, LiI, etc.

[0033] In this embodiment, ethylene carbonate is used as the non-aqueous solvent. Lithium bis(oxalato)borate (LiBOB) is added to the non-aqueous electrolyte as a lithium salt as an additive. For example, LiBOB is added to the non-aqueous electrolyte so that the concentration of LiBOB in the non-aqueous electrolyte is 0.001 to 0.1 [mol / L].

[0034] [Positive electrode end configuration] As shown in FIG. 4, the positive electrode base material 22 has a first surface 22B and a second surface 22C. The first surface 22B and the second surface 22C are two surfaces facing in opposite directions, and are surfaces on which the positive electrode mixture layer 23 and the insulating layer 24 are provided. Of the insulating layers 24 provided on the first surface 22B and the second surface 22C, the insulating layer 24 provided on the first surface 22B is the first insulating layer 24A. And, the insulating layer 24 provided on the second surface 22C opposite to the first surface 22B is the second insulating layer 24B. In the following, when the first insulating layer 24A and the second insulating layer 24B are not distinguished from each other, they are simply referred to as the insulating layer 24.

[0035] The thickness T1 of the first insulating layer 24A is greater than the thickness T2 of the second insulating layer 24B. The thickness T1 of the first insulating layer 24A and the thickness T2 of the second insulating layer 24B are, for example, configured so that the thickness T1 of the first insulating layer 24A is greater than the thickness T2 of the second insulating layer 24B within a range of 3.0 μm or more and 20.0 μm or less.

[0036] By setting the thickness T1 of the first insulating layer 24A and the thickness T2 of the second insulating layer 24B to 3.0 μm or more, the mechanical strength of the first insulating layer 24A and the second insulating layer 24B can be increased. This makes it possible to more reliably prevent a short circuit between the positive electrode side uncoated portion 22A and the negative electrode plate 25 due to the foreign matter penetrating the insulating layer 24 even if the foreign matter is interposed between the insulating layer 24 and the negative electrode plate 25. By setting the thickness T1 of the first insulating layer 24A and the thickness T2 of the second insulating layer 24B to 20.0 μm or less, it is possible to suppress a decrease in the foil collection property that makes it difficult to bend the positive electrode side uncoated portion 22A as the thickness T1 of the first insulating layer 24A and the thickness T2 of the second insulating layer 24B increase.

[0037] Furthermore, the thickness T1 of the first insulating layer 24A and the thickness T2 of the second insulating layer 24B are smaller than the thickness T3 of the positive electrode mixture layer 23. This makes it possible to prevent the first insulating layer 24A and the second insulating layer 24B from contacting the press roll when adjusting the thickness T3 of the positive electrode mixture layer 23 in the manufacturing process. Note that the thickness T3 of the positive electrode mixture layer 23 is, for example, 20.0 μm or more and 25.0 μm or less.

[0038] The first insulating layer 24A and the second insulating layer 24B have the same width W1 in the width direction D2. The width W1 of the insulating layer 24 corresponds to the distance from the boundary between the positive electrode mixture layer 23 and the insulating layer 24 to the tip of the insulating layer 24 when viewed in the direction along the stacking direction D3 from a viewpoint facing the positive electrode mixture layer 23 and the insulating layer 24.

[0039] The width W1 of the insulating layer 24 is, for example, 2.5 mm or more and 4.5 mm or less. By setting the width W1 of the insulating layer 24 within the above range, it is possible to prevent the width W2 of the positive electrode side uncoated portion 22A in the width direction D2 from becoming excessively small while suitably preventing a short circuit between the positive electrode side uncoated portion 22A and the negative electrode plate 25. The width W2 of the positive electrode side uncoated portion 22A is, for example, 7.0 mm or more and 13.0 mm or less.

[0040] At the boundary between the positive electrode mixture layer 23 and the insulating layer 24, an end of the positive electrode mixture layer 23 may be covered by the insulating layer 24, or an end of the insulating layer 24 may be covered by the positive electrode mixture layer 23. In this case, the insulating layer 24 may be configured so that the width W1 of the insulating layer 24 when viewed in the direction along the stacking direction D3 from a viewpoint facing the positive electrode mixture layer 23 and the insulating layer 24 satisfies the above range.

[0041] As shown in Fig. 5, the positive electrode side current collecting part 20A of the electrode body 20 is formed by pressing the positive electrode side uncoated parts 22A in a wound state while stacking them in the stacking direction D3. The positive electrode side uncoated parts 22A are curved toward the center of the positive electrode side current collecting part 20A. In Fig. 5, the center of the positive electrode side current collecting part 20A in the stacking direction D3 is indicated by a center line CL.

[0042] In the state of the electrode body 20, the first surface 22B of the positive electrode substrate 22 faces the center side of the positive electrode side current collector 20A in the stacking direction D3 of the positive electrode substrate 22. The second surface 22C of the positive electrode substrate 22 faces the opposite side of the positive electrode substrate 22 with respect to the center of the positive electrode side current collector 20A in the stacking direction D3 of the positive electrode substrate 22. The first insulating layer 24A is located on the center side (the center line CL side) of the positive electrode side current collector 20A in the stacking direction D3 with respect to the positive electrode substrate 22. The second insulating layer 24B is located opposite the first insulating layer 24A with respect to the positive electrode substrate 22.

[0043] [Operation of the embodiment] 6, the volume of the positive electrode substrate 22 is reduced when the insulating paste is dried to form the insulating layer 24, and thus a contraction stress caused by the insulating layer binder acts on the positive electrode substrate 22. For example, when the first insulating layer 24A is formed, a first contraction stress F1 acts on the first surface 22B of the positive electrode substrate 22 toward the positive electrode mixture layer 23 in the width direction D2. When the second insulating layer 24B is formed, a second contraction stress F2 acts on the second surface 22C of the positive electrode substrate 22 toward the positive electrode mixture layer 23 in the width direction D2.

[0044] The magnitude of the shrinkage stress has a positive correlation with the volume of the insulating layer 24. Therefore, since the thickness T1 of the first insulating layer 24A is greater than the thickness T2 of the second insulating layer 24B, the first shrinkage stress F1 acting on the first surface 22B is greater than the second shrinkage stress F2 acting on the second surface 22C. Therefore, a resultant force F3 acts on the positive electrode substrate 22 to bend it toward the center of the positive electrode side current collecting portion 20A in the stacking direction D3 due to the shrinkage stress difference between the first shrinkage stress F1 and the second shrinkage stress F2. This can improve the foil collecting property of the positive electrode side uncoated portion 22A when forming the positive electrode side current collecting portion 20A.

[0045] For example, if the width W1 of the first insulating layer 24A and the second insulating layer 24B is 2.5 mm or more, the contraction stress difference between the first insulating layer 24A and the second insulating layer 24B can be suitably expressed. In addition, the resultant force F3 may be large enough to easily bend the positive electrode substrate 22 toward the center of the positive electrode side current collecting portion 20A. For example, the resultant force F3 may be large enough to bend the positive electrode substrate 22 against the rigidity of the positive electrode substrate 22, or may be large enough to prevent the positive electrode substrate 22 from being bent due to the rigidity of the positive electrode substrate 22. In other words, the first insulating layer 24A and the second insulating layer 24B, which have different thicknesses, may be in a state in which they have a contraction stress difference that makes it easy to bend the positive electrode substrate 22, or may be in a state in which they have a contraction stress difference that makes it easy to bend the positive electrode substrate 22.

[0046] As an example, the thickness T1 of the first insulating layer 24A is preferably 1.2 times or more and 1.7 times or less than the thickness T2 of the second insulating layer 24B. If the thickness T1 of the first insulating layer 24A is 1.2 times or more than the thickness T2 of the second insulating layer 24B, the contraction stress difference between the first insulating layer 24A and the second insulating layer 24B can be suitably applied to the positive electrode base material 22. If the thickness T1 of the first insulating layer 24A is 1.7 times or less than the thickness T2 of the second insulating layer 24B, it is possible to prevent the second insulating layer 24B from becoming excessively thin and thereby preventing a lack of mechanical strength.

[0047] For example, the thickness T1 of the first insulating layer 24A is preferably 5.0 μm or more and 20.0 μm or less. In this case, the thickness T2 of the second insulating layer 24B is preferably set to satisfy the condition that the thickness T1 is 1.2 times or more and 1.7 times or less than the thickness T2 within the range of 3.0 μm or more and 16.0 μm or less. By setting the thickness T1 and the thickness T2 within the above range, it is possible to ensure the mechanical strength of the second insulating layer 24B, suppress the decrease in the foil collecting property due to the increase in the thickness T1 of the first insulating layer 24A, and achieve the effect of improving the foil collecting property due to the shrinkage stress difference with respect to the positive electrode base material 22.

[0048] The magnitude of the shrinkage stress has a positive correlation with the mass ratio of the binder for the insulating layer to the total mass of the insulating layer 24. Therefore, for example, if the mass ratio of the binder for the insulating layer to the total mass of the insulating layer 24 is 10 mass% or more, the shrinkage stress difference between the first insulating layer 24A and the second insulating layer 24B can be suitably applied to the positive electrode base material 22. The magnitude of the shrinkage stress also depends on the type and molecular weight of the binder for the insulating layer.

[0049] In addition, in the portion of the positive electrode substrate 22 where the insulating layer 24 is provided, the distance of the first surface 22B from the negative electrode plate 25 and the separator 28 is smaller than the distance of the second surface 22C from the negative electrode plate 25 and the separator 28. Therefore, when a foreign object M shown by a two-dot chain line in Fig. 6 enters between the negative electrode plate 25 and the separator 28 and the first insulating layer 24A, the force applied by the foreign object M to the insulating layer 24 is larger than when the foreign object M enters between the negative electrode plate 25 and the separator 28 and the second insulating layer 24B.

[0050] In this regard, by making the thickness T1 of the first insulating layer 24A greater than the thickness T2 of the second insulating layer 24B, the mechanical strength of the first insulating layer 24A can be increased, thereby more reliably suppressing a short circuit between the first surface 22B and the negative electrode plate 25.

[0051] [Method of manufacturing lithium-ion secondary batteries] As shown in FIG. 7, the manufacturing method of the lithium ion secondary battery 10 includes steps S1 to S4. Step S1 is a source process for manufacturing each of the positive electrode plate 21 and the negative electrode plate 25. In the manufacturing process of the positive electrode plate 21, one strip of positive electrode mixture paste and two strips of insulating paste are simultaneously applied to each of the first surface 22B and the second surface 22C so as to form the positive electrode side uncoated portion 22A at both ends in the width direction D2. At this time, the two strips of insulating paste are applied so that one of the two strips of insulating paste contacts one end of the positive electrode mixture paste in the width direction D2 and the other strip of insulating paste contacts the other end of the positive electrode mixture paste. Thereafter, the positive electrode mixture paste and the insulating paste are dried to form the positive electrode mixture layer 23 and the insulating layer 24. Next, the positive electrode mixture layer 23 formed on both sides of the positive electrode substrate 22 is pressed to adjust the thickness of the positive electrode mixture layer 23. Thereafter, the positive electrode substrate 22 is cut at the center in the width direction D2. Through the above steps, two positive electrode plates 21 are produced at once.

[0052] In the manufacturing process of the negative electrode plate 25, a negative electrode mixture paste is applied to two surfaces of the negative electrode substrate 26 facing in opposite directions so as to form negative electrode-side uncoated portions 26A at both ends in the width direction D2. The negative electrode mixture paste is then dried to form a negative electrode mixture layer 27. Next, the negative electrode mixture layer 27 formed on both sides of the negative electrode substrate 26 is pressed to adjust the thickness of the negative electrode mixture layer 27. The negative electrode substrate 26 is then cut at the center in the width direction D2. Through the above steps, two negative electrode plates 25 are manufactured at once.

[0053] In step S2, the positive electrode plate 21 and the negative electrode plate 25 are stacked with the separator 28 interposed therebetween, then wound and pressed flat. Next, in step S3, the wound positive electrode uncoated portion 22A is collected so as to be stacked in the stacking direction D3. In this state, the collected positive electrode uncoated portion 22A is pressed to form the positive electrode current collector 20A. One example of the pressing means is ultrasonic welding. Also, in step S3, the negative electrode uncoated portion 26A is pressed in the same manner as the positive electrode side to form the negative electrode current collector 20B. Through the above procedure, the electrode body 20 is manufactured.

[0054] In step S4, the electrode body 20 is sealed in the case 11. At this time, the positive electrode side current collector 20A is electrically connected to the positive electrode external terminal 13A via the positive electrode side current collector 14A. The negative electrode side current collector 20B is electrically connected to the negative electrode external terminal 13B via the negative electrode side current collector 14B. The top of the housing section 11A is closed by the lid 12. Next, moisture is removed from the electrode body 20 by heating, and then a nonaqueous electrolyte is injected into the case 11. The lithium ion secondary battery 10 is assembled by the above procedure.

[0055] [Effects of the embodiment] According to the above embodiment, the following effects can be obtained. (1) By making the thickness T1 of the first insulating layer 24A larger than the thickness T2 of the second insulating layer 24B, a resultant force F3 acts on the positive substrate 22 to bend it toward the center of the positive current collecting portion 20A in the stacking direction D3. This improves the foil collecting property of the positive current collecting portion 22A when forming the positive current collecting portion 20A. This prevents foil collecting defects such as a part of the positive current collecting portion 22A being torn (foil breakage) when forming the positive current collecting portion 20A, or layers of the positive current collecting portion 22A not being properly joined to each other.

[0056] (2) By making the thickness T1 1.2 to 1.7 times the thickness T2, the resultant force F3, which is the difference in contraction stress between the first insulating layer 24A and the second insulating layer 24B, can be appropriately applied to the positive electrode substrate 22, while preventing the mechanical strength of the second insulating layer 24B from becoming insufficient.

[0057] (3) By setting thickness T1 within the range of 5.0 μm or more and 20.0 μm or less and thickness T2 within the range of 3.0 μm or more and 16.0 μm or less, the mechanical strength of second insulating layer 24B can be ensured while suppressing the decrease in foil collection ability that occurs with an increase in thickness T1 of first insulating layer 24A.

[0058] (4) By setting the mass of the insulating layer binder to 30 mass % or less with respect to the mass of the insulating layer 24, it is possible to prevent an excessive decrease in the mechanical strength of the insulating layer 24. By setting the mass of the insulating layer binder to 10 mass % or more with respect to the mass of the insulating layer 24, it is possible to ensure the peel strength between the insulating layer 24 and the positive electrode substrate 22 and to preferably exhibit the resultant force F3, which is the shrinkage stress difference between the first insulating layer 24A and the second insulating layer 24B.

[0059] (5) By setting the width W1 of the first insulating layer 24A and the second insulating layer 24B to 2.5 mm or more, it is possible to preferably generate the resultant force F3, which is the shrinkage stress difference, while preferably preventing a short circuit between the positive electrode side uncoated portion 22A and the negative electrode plate 25. By setting the width W1 to 4.5 mm or less, it is possible to prevent the width W2 in the width direction D2 of the positive electrode side uncoated portion 22A from becoming excessively small.

[0060] [Example of change] The above embodiment can be modified as follows. The width W1 of the first insulating layer 24A and the second insulating layer 24B may be more than 4.5 mm as long as it does not adversely affect the foil collecting property. Also, the width W1 may be less than 2.5 mm as long as it is possible to secure a shrinkage stress difference for improving the foil collecting property and to prevent a short circuit between the positive electrode side uncoated portion 22A and the negative electrode plate 25.

[0061] The mass of the insulating layer binder may be more than 30 mass % relative to the mass of the insulating layer 24, so long as the mechanical strength of the insulating layer 24 can be sufficiently ensured. In addition, the mass of the insulating layer binder may be less than 10 mass % relative to the mass of the insulating layer 24, so long as a shrinkage stress difference for improving the foil collection property can be ensured and the peel strength between the insulating layer 24 and the positive electrode substrate 22 can be ensured.

[0062] As long as a shrinkage stress difference for improving the foil collecting property can be ensured, the thickness T1 of the first insulating layer 24A may be less than 5.0 μm, and the thickness T2 of the second insulating layer 24B may be more than 16.0 μm. As long as the foil collecting property is not significantly reduced with an increase in the thickness T1 of the first insulating layer 24A, the thickness T1 may be more than 20.0 μm. As long as the mechanical strength of the second insulating layer 24B can be ensured, the thickness T2 of the second insulating layer 24B may be less than 3.0 μm.

[0063] · As long as the resultant force F3 acts favorably on the positive electrode substrate 22, the thickness T1 of the first insulating layer 24A may be less than 1.2 times the thickness T2 of the second insulating layer 24B. Also, for example, in the case where the thickness T1 of the first insulating layer 24A is increased rather than the thickness T2 of the second insulating layer 24B being excessively small, the thickness T1 may be more than 1.7 times the thickness T2. Note that in this case, the thickness T1 may be set to a size that does not cause a decrease in foil collecting property, such as making it difficult to bend the positive electrode side uncoated portion 22A, as the thickness T1 increases.

[0064] The constituent material of the first insulating layer 24A and the constituent material of the second insulating layer 24B may be the same or different. If the constituent material of the first insulating layer 24A and the constituent material of the second insulating layer 24B are different, the constituent materials should be such that the first contraction stress F1 generated in the first insulating layer 24A is larger than the second contraction stress F2 generated in the second insulating layer 24B.

[0065] The electrode assembly 20 may be a laminate, in which a rectangular positive electrode plate 21 and a rectangular negative electrode plate 25 are laminated with a separator 28 interposed therebetween, housed in the case 11, instead of a wound body. The lithium ion secondary battery 10 may be another non-aqueous secondary battery, for example, a nickel-metal hydride battery.

[0066] The lithium ion secondary battery 10 may be mounted on an automatic transport vehicle, a special vehicle for loading and unloading, an electric vehicle, a hybrid vehicle, a computer, or other electronic device, or may be part of other systems. For example, it may be mounted on a moving object such as a ship or an aircraft, or may be a power supply system that supplies power from a power plant via a substation to a building or home in which a secondary battery is installed.

[0067] [Example] Example 1 and Comparative Examples 1 to 4 will be described below. Note that the following examples are merely examples for explaining the effects of the above-described embodiment, and do not limit the present invention. The manufacturing conditions and evaluation results of Example 1 and Comparative Examples 1 to 4 are shown in FIG.

[0068] [Example 1] In Example 1, an electrode body 20 was produced that included a positive electrode plate 21 in which the thickness T1 of the first insulating layer 24A was 13 μm and the thickness T2 of the second insulating layer 24B was 10 μm. In Example 1, the thickness T1 of the first insulating layer 24A was 1.3 times the thickness T2 of the second insulating layer 24B. In Example 1, the same insulating paste was used to form the first insulating layer 24A and the second insulating layer 24B. In Example 1, the mass ratio of the insulating layer binder to the entire first insulating layer 24A was 20%, and the mass ratio of the insulating layer binder to the entire second insulating layer 24B was 20%.

[0069] [Comparative Example 1] In Comparative Example 1, the electrode body 20 was produced in the same manner as in Example 1, except that in the positive electrode plate 21, neither the first insulating layer 24A nor the second insulating layer 24B was formed.

[0070] [Comparative Example 2] In Comparative Example 2, the electrode body 20 was produced in the same manner as in Example 1, except that the thickness T1 of the first insulating layer 24A was set to 2 μm, and the thickness T2 of the second insulating layer 24B was set to 2 μm.

[0071] [Comparative Example 3] In Comparative Example 3, the electrode body 20 was produced in the same manner as in Example 1, except that the thickness T1 of the first insulating layer 24A was set to 10 μm, and the thickness T2 of the second insulating layer 24B was set to 10 μm.

[0072] [Comparative Example 4] In Comparative Example 4, the electrode body 20 was produced in the same manner as in Example 1, except that the thickness T1 of the first insulating layer 24A was set to 20 μm, and the thickness T2 of the second insulating layer 24B was set to 20 μm.

[0073] [Foreign matter resistance evaluation] In each electrode body 20, a foreign object M of a predetermined size was sandwiched between the first insulating layer 24A located on the first surface 22B side and the separator 28, and between the second insulating layer 24B located on the second surface 22C side and the separator 28. In Comparative Example 1, the foreign object M was placed at the same position as the position where the first insulating layer 24A and the second insulating layer 24B were provided in Example 1. Then, it was determined whether the foreign object M penetrated the insulating layer 24 and reached the positive electrode substrate 22 for each of the first surface 22B side and the second surface 22C side. The foreign object M did not penetrate the insulating layer 24 and did not reach the positive electrode substrate 22 was determined as good (◯), and the foreign object M penetrated the insulating layer 24 and contacted the positive electrode substrate 22 was determined as bad (×).

[0074] [Evaluation of Foil Collection] In Example 1 and Comparative Examples 1 to 4, the presence or absence of foil collection defects was confirmed in the positive electrode side current collecting part 20A of each electrode body 20. Note that the electrode body 20 used in the foil collection evaluation was different from the electrode body 20 used in the foreign matter resistance evaluation.

[0075] [Evaluation Results] As shown in FIG. 8, in the foreign object resistance evaluation, in Example 1 and Comparative Examples 3 and 4, the foreign object M did not penetrate either the first insulating layer 24A or the second insulating layer 24B, and did not reach the positive electrode substrate 22. On the other hand, in Comparative Example 1, the electrode body 20 was determined to be defective because it did not have either the first insulating layer 24A or the second insulating layer 24B. In Comparative Example 2, the foreign object M penetrated the first insulating layer 24A and reached the positive electrode substrate 22. Similarly, in Comparative Example 2, the foreign object M penetrated the second insulating layer 24B and reached the positive electrode substrate 22. This is considered to be because, in Comparative Example 2, both the thickness T1 and the thickness T2 were small, and the mechanical strength of the first insulating layer 24A and the second insulating layer 24B was insufficient.

[0076] Regarding the evaluation of the foil collecting property, in Example 1 and Comparative Examples 1 and 2, no foil collecting defects were observed in the positive electrode side current collecting part 20A, and the bonding state was good. In contrast, in Comparative Examples 3 and 4, foil collecting defects such as tearing of the positive electrode side uncoated part 22A were observed. In particular, the incidence of foil collecting defects was higher in Comparative Example 4 than in Comparative Example 3. This is because, as the thickness of the insulating layer 24 increases, the part of the positive electrode substrate 22 where the insulating layer 24 is provided becomes more difficult to bend, and therefore, when the positive electrode side uncoated part 22A is collected, excessive force is applied to the positive electrode side uncoated part 22A.

[0077] From the above, it has been confirmed that even when the thickness of insulating layer 24 is increased to increase the mechanical strength of insulating layer 24, the foil collection ability when forming positive electrode side current collecting portion 20A can be improved by making thickness T1 of first insulating layer 24A greater than thickness T2 of second insulating layer 24B. [Explanation of symbols]

[0078] D2…Width direction D3…Layer direction T1, T2…Thickness 10...Lithium-ion secondary battery 20...Electrode body 20A…Positive electrode current collector 20B: Negative electrode current collector 21…Positive electrode plate 22...Positive electrode substrate 22A: Positive electrode uncoated area 22B…Side 1 22C…Second side 23...Positive electrode mixture layer 24…Insulating layer 24A…First insulating layer 24B: Second insulating layer 25…Negative plate 26...Negative electrode substrate 27...Negative electrode mixture layer 28…Separator

Claims

1. An electrode assembly in which positive and negative electrode plates are stacked in a stacking direction with a separator interposed therebetween, The positive electrode plate includes a foil-shaped positive electrode base material, and a positive electrode mixture layer and an insulating layer provided on each of two surfaces of the positive electrode base material facing in opposite directions, the positive electrode base material includes a positive electrode-side uncoated portion in which neither the positive electrode mixture layer nor the insulating layer is provided, The electrode body includes a positive electrode-side current collecting portion in which the positive electrode-side uncoated portion is laminated in the lamination direction, the insulating layer is located at the boundary between the positive electrode mixture layer and the positive electrode-side uncoated portion, the insulating layer provided on a first surface of the positive electrode base material facing a center side of the positive electrode-side current collecting portion in the stacking direction is a first insulating layer, and the insulating layer provided on a second surface of the positive electrode base material opposite to the first surface is a second insulating layer, The thickness of the first insulating layer is greater than the thickness of the second insulating layer, The thickness of the first insulating layer is 1.2 times or more and 1.7 times or less than the thickness of the second insulating layer, The thickness of the first insulating layer is 5.0 μm or more and 20.0 μm or less, The thickness of the second insulating layer is 3.0 μm or more and 16.0 μm or less. Non-aqueous secondary battery.

2. The insulating layer includes a binder, The mass ratio of the binder is 10% by mass or more and 30% by mass or less with respect to the mass of the insulating layer. The nonaqueous secondary battery according to claim 1 .

3. The width of the first insulating layer and the second insulating layer is 2.5 mm or more and 4.5 mm or less. The nonaqueous secondary battery according to claim 1 or 2.

4. The thickness of the first insulating layer is smaller than the thickness of the positive electrode mixture layer provided on the first surface. The nonaqueous secondary battery according to claim 1 .

5. Each of the first insulating layer and the second insulating layer has a flat shape. The nonaqueous secondary battery according to claim 1 .

Images