Flame retardant fibers made from long staple and filament yarns

Abstract

DETAILED DESCRIPTION OF THE INVENTION Embodiments of the present invention relate to flame resistant fabrics formed from a combination of filaments and long staple yarns that are relatively lightweight and exhibit excellent physical and thermal properties.

Description

[Technical field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims the benefit of U.S. Provisional Application No. 62 / 943,968, filed December 5, 2019, which is incorporated by reference herein in its entirety.

[0002] Technical Field SUMMARY OF THE DISCLOSURE An embodiment of the present invention relates to a flame resistant fabric formed at least in part from long staple yarns and filament yarns. [Background technology]

[0003] Protective garments are designed to protect the wearer from hazardous environmental conditions that the wearer may encounter. Such garments include those designed to be worn by firefighters and other rescue personnel, industrial and electrical workers, and military personnel.

[0004] To ensure that garments adequately protect the wearer in hazardous situations, standards are published which govern the performance of such garments (or component layers or portions of such garments). For example, the National Fire Protection Association (NFPA) 1971-Standard on Protective Ensembles for Structural Fire Fighting and Proximity Fire Fighting (2018 Edition, incorporated herein by reference) provides a standard for the performance required for firefighter garments. NFPA 2112-Standard on Flame-Resistant Clothing for Protection of Industrial Personnel Against Short-Duration Thermal Exposures from Fire (2012 Edition, incorporated herein by reference) provides a standard for the performance required for garments for industrial workers that provide protection against flash fires. Both of these standards require that the garments and / or individual layers or portions thereof have a char length of 4 inches (or less) when measured according to the test method set forth in ASTM D6413-Standard Test Method for Flame Resistance of Textiles (Vertical Test) (2015 Edition, incorporated herein by reference in its entirety). The EPA requires that LEDs pass a number of different performance tests, including complying with thermal protection requirements of having a 2 second (or less) afterflame length and a 2 second (or less) afterflame.

[0005] To test the char length and afterflame time, a fabric specimen is hung vertically over a flame for 12 seconds. The fabric must self-extinguish within 2 seconds (i.e., it must have an afterflame time of 2 seconds or less). After the fabric self-extinguishes, a weight of a predetermined amount is attached to the fabric, and the fabric is lifted so that the weight is suspended from the fabric. The fabric will typically tear along the charred portion of the fabric. The tear length (i.e., char length) should be 4 inches or less when testing is performed in both the machine / warp and cross-machine / weft directions of the fabric. Typically, a fabric sample is tested for compatibility both before it is washed (so the fabric still contains residual - and often flammable - chemicals from the finishing process) and after a specified number of washes (100 washes for NFPA 2112, 5 washes for NFPA 1971).

[0006] Structured firefighter clothing, such as firefighter turnout gear, usually consists of a matching coat and pants and is primarily designed to protect the wearer from receiving severe burns. An NFPA-compliant turnout suit or garment usually consists of three layers: an outer shell, a middle moisture barrier, and a thermal barrier lining. The outer shell is usually a woven fabric made from flame resistant fibers and is considered the first line of protection for the firefighter. Not only should it withstand flames, but it also needs to be strong and durable so that it will not tear, fray, or get snagged during normal firefighting activities.

[0007] The moisture barrier, which is also fire retardant, is present to keep water and harmful chemicals from soaking into and filling the suit. Excess moisture entering the suit from the outside would add extra weight to the firefighter and increase his or her load.

[0008] The thermal barrier is flame retardant and provides the majority of the thermal protection provided by the ensemble. The traditional thermal barrier is a batting made of a flame retardant fibrous nonwoven quilted to a lightweight woven facecloth also made of flame retardant fibers. The batting can be either a single layer of needle punched nonwoven or a multi-layer spunlace nonwoven. The facecloth is quilted to the batting, usually in a crisscross or chicken wire pattern. The quilted thermal barrier is the innermost layer of a firefighter's garment, and the facecloth usually faces the wearer.

[0009] The thermal protection that a garment fabric provides to the wearer is measured by determining the Thermal Protective Performance (TPP) of the fabric in accordance with ISO 17492: Clothing for protection against heat and flame - Determination of heat transmission on exposure to both flame and radiant heat, as amended by NFPA 1971 (2003 edition, incorporated herein by reference). The TPP test predicts the rate at which radiant and convective heat will be transferred through three layers of a garment fabric (outer shell, moisture barrier, and thermal liner) to a level that will cause a second degree burn to human skin. More specifically, the test measures the amount of time it takes for sufficient heat at a given energy level to pass through the composite to cause a second degree burn. The minimum TPP rating for jackets and pants conforming to NFPA 1971 is 35 calories / cm. 2 (which corresponds to approximately 17.5 seconds of protection before second degree burns occur). The higher this number, the more protective the clothing system is considered to be. The TPP test method is fully described in Chapter 8.10 of NFPA 1971.

[0010] TPP is a measure of a garment fabric's ability to protect the wearer from heat and flame, but this must be balanced with the fabric's total heat loss (THL), which measures the garment fabric's ability to allow heat and water vapor to escape from the wearer through the fabric, thereby avoiding heat stress to the wearer.

[0011] The test method used to measure THL is specified in ASTM F1868-14: Standard Test Method for Thermal and Evaporative Resistance of Clothing Materials Using a Sweating Hot Plate, as amended by NFPA 1971 (2002, incorporated herein by reference). Generally, however, the garment fabric (consisting of the outer shell, moisture barrier, and thermal liner) is placed on a 35°C (+ / -0.5°C) hot plate in an environment with an air temperature of 25°C (+ / -0.5°C). Testing is performed using both wet and dry hot plates. The amount of energy (in watts / m2) required to maintain the hot plate at 98.6°F is measured. 2 The THL is measured in watts per square meter (W / m). Because fabrics allow heat to escape through the fabric of a garment, a higher THL value means that more energy must be supplied to the plate to maintain temperature. Thus, the higher the THL value, the less insulative the fabric is, but the lower the risk that the fabric will contribute to heat stress in the wearer. To comply with NFPA 1971, a minimum of 205 watts per square meter is required. 2 A THL value of at least 100% is required.

[0012] Fabrics used in these environments also need to be strong. The strength of such fabrics, such as the outer shell of a firefighter's gear, can be measured by assessing the fabric's tear strength and tensile strength.

[0013] Tear strength is the force required to initiate or continue or propagate a tear in a fabric. ASTM 5587-05: Standard Test Method for Tearing Strength of Fabrics by Trapezoid Procedure (2015 Edition, incorporated herein by reference) measures tear strength. According to this method, the outline of an isosceles trapezoid is marked on a rectangular specimen cut to determine tear strength. The specimen is slit at the smallest base of the trapezoid to initiate the tear. The non-parallel sides of the trapezoid marked on the specimen are clamped into the parallel jaws of a tensile tester. The jaw separation is successively increased to apply a force that propagates the tear across the specimen. Simultaneously, the force generated is recorded. The maximum force to sustain the tear is calculated from an autographic chart recorder or a microprocessor data collection system.

[0014] Tensile strength is the force required to break a fabric when a load is applied, and is measured according to ASTM D5034-09:Standard Test Method for Breaking Strength and Elongation of Textile Fabrics (Grab Test), 2013 edition, incorporated herein by reference. According to this method, a test specimen is attached to the center of the clamp of a tensile machine and a force is applied until the specimen breaks. The breaking force and elongation values ​​of the test specimen are obtained from a machine scale, dial, self-recording chart, or a computer interfaced to the test machine.

[0015] NFPA 1971 also includes requirements regarding the degree to which fabrics will shrink when subjected to heat in tests in accordance with ASTM F2894-19:Standard Test Method for Evaluation of Materials, Protective Clothing, and Equipment for Heat Resistance Using a Hot Air Circulating Oven (2014 Edition, incorporated herein by reference). To conduct thermal shrinkage testing of outer shell fabrics, marks are made on the fabric in both the machine / warp and machine width / weft directions, spaced apart from one another. The distance between sets of marks is recorded. The fabric is then hung in a 500° F. oven for 5 minutes. The distance between sets of marks is then remeasured. The thermal shrinkage of the fabric is then calculated as the percentage by which the fabric shrinks in both the machine / warp and machine width / weft directions, and must be less than the percentage stated in the applicable standard. For example, NFPA 1971 requires that outer shell fabrics exhibit heat shrinkage of 10% or less in both the machine / warp and cross machine / weft directions.

[0016] NFPA 1971 also includes requirements regarding the degree to which conforming fabrics may shrink when laundered in accordance with AATCC 135, 1, V, Ai-Dimensional Changes of Fabrics after Home Laundering (2004 Edition, incorporated herein by reference). This property is called dimensional stability or laundry shrinkage. NFPA 1971 conforming fabrics are required to shrink less than 5% in both the warp and weft directions.

[0017] The water resistance of the fabric is also important. Fabrics that absorb water become heavier and cause more strain on the wearer. Therefore, it is desirable for fabrics, such as those used for outer shells, to be water resistant so that they do not absorb water. The water repellency of fabrics can be tested according to AATCC 42-Water Resistance: Impact Penetration Test (2013 edition, incorporated herein by reference). In AATCC 42, the fabric is immersed in water and the weight of the wet fabric is measured. The fabric is allowed to dry for 24 hours and then its weight is measured again. The percentage change in weight between the wet and dry fabric is calculated. The lower the percentage, the less water the fabric absorbs during immersion. Summary of the Invention

[0018] The terms "invention," "the invention," "this invention," and "the present invention" as used in this patent are intended to broadly refer to all of the subject matter of this patent and the claims that follow. Statements containing these terms should not be understood as limiting the subject matter described herein or as limiting the meaning or scope of the claims that follow. The embodiments of the invention covered by this patent are defined by the claims that follow, and not by this Summary. This Summary is a high-level overview of various aspects of the invention and introduces certain concepts that are further described in the Detailed Description section below. This Summary is not intended to identify key or primary features of the claimed subject matter, nor is it intended to be used solely to determine the scope of the claimed subject matter. The subject matter should be understood with reference to the entire specification of this patent, all figures, and each claim.

[0019] DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention relates to flame resistant fabrics formed from a combination of filaments and long staple yarns that are relatively lightweight and exhibit excellent physical and thermal properties.

[0020] In some embodiments, the flame resistant fabric comprises a plurality of long staple yarns formed of a plurality of long staple fibers of a flame resistant material. The fabric also comprises a plurality of filament yarns comprising the flame resistant material. In some embodiments, the flame resistant fabric is devoid of short staple yarns.

[0021] In some embodiments, the flame resistant fabric is a woven fabric having a warp direction and a weft direction. The flame resistant woven fabric comprises a plurality of flame resistant long staple yarns extending in both the warp direction and the weft direction, at least a portion of the plurality of long staple yarns having a fiber blend comprising a plurality of first long staple fibers of a first type of material and a plurality of second long staple fibers of a second type of material different from the first type of material. The fabric also comprises a plurality of flame resistant filament yarns interwoven with the plurality of long staple yarns in both the warp direction and the weft direction.

[0022] In some embodiments, the flame resistant fabric is a woven fabric having a warp direction and a weft direction. The flame resistant woven fabric includes flame resistant first long staple yarns extending in both the warp direction and the weft direction, each first long staple yarn having a fiber blend formed of a plurality of first long staple fibers of a first type of material and a plurality of second long staple fibers of a second type of material different from the first type of material. The fabric also includes flame resistant second long staple yarns extending in both the warp direction and the weft direction, each second long staple yarn being formed of a single type of material. The fabric also includes a flame retardant filament yarn interwoven with first and second long staple yarns in both the warp and weft directions, each end of the first long staple yarn including at least two first long staple yarns plied together and each end of the second long staple yarn including at least two second long staple yarns plied together, with more than three and less than eight first long staple yarn ends and second long staple yarn ends collectively between adjacent filament yarn ends in at least one of the warp or weft directions. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0023] Although the subject matter of the embodiments of the present invention has been specifically described to meet statutory requirements, this description is not necessarily intended to limit the scope of the claims. The claimed subject matter may be embodied in other ways, may include other elements or steps, and may be used in conjunction with other existing or future technologies. This description should not be construed to imply any particular order or arrangement of or among the various steps or elements, unless the order of individual steps or arrangement of elements is explicitly recited.

[0024] As used herein, "filament yarn" or "continuous filament yarn" refers to a yarn composed of one or more fibers or "filaments" of indefinite or extreme length, such as those found naturally in silk. Filament yarns are measured in denier. Filament yarns may be composed of a single filament, which is called a monofilament. Fishing line is an example of a monofilament yarn. In contrast, some filament yarns are composed of multiple filaments that are twisted together to form a filament yarn (called a multifilament yarn). Both monofilament and multifilament yarns are considered filament yarns.

[0025] As used herein, a "short staple yarn" is a yarn formed of short staple fibers, such as fibers having a length of 2 inches or less. Short staple yarn differs from filament yarn in that it is measured in yarn count (e.g., metric count).

[0026] As used herein, "long staple yarn" refers to yarn formed from long staple fibers. Long staple fibers are defined as fibers having a length greater than 2 inches up to about 40 inches. Long staple yarns are formed from long staple fibers using systems and methods specifically designed for use with long staple fibers. Those skilled in the art will recognize that systems and methods for forming long staple yarns are distinguishable from systems and methods for forming short staple yarns using short fibers (e.g., short staple fibers). Long staple yarns, like short staple yarns, are measured in count.

[0027] Long staple fibers useful in the present invention can be formed by a variety of processes known to those skilled in the art, including, but not limited to, the stretch-break process (see Continuous Filament to Staple Length Conversion document, a copy of which is attached hereto), cutting continuous fibers to long staple lengths, or harvesting long staple fibers by shearing from an animal (e.g., to obtain long staple wool fibers). As an example, during the stretch-break process, long staple fibers are formed by cutting filaments to form non-continuous long staple fibers having lengths of greater than 2 inches and up to about 40 inches. These and other processes for forming long staple fibers may provide long staple fibers of uniform or non-uniform length. Similarly, the long staple fibers in long staple yarns suitable for use in embodiments of the present invention may be of the same or different lengths.

[0028] Long staple yarns may be formed from long staple fibers using systems and processes specifically designed for use with long staple fibers, including, but not limited to, woolen and worsted systems and processes.

[0029] An embodiment of the present invention includes a flame resistant fabric comprising a combination of yarns, at least some of which are long staple yarns and at least some of which are filament yarns. In some embodiments, the fabric does not include short staple yarns. However, in other embodiments, short staple yarns may be included.

[0030] In some examples of the present invention, the long staple yarn comprises flame-retardant ("FR") long staple fibers, such as essentially FR long staple fibers or long staple fibers that have been treated to be flame-retardant. In some embodiments, the long staple yarn may comprise at least some non-FR long staple fibers. Exemplary FR and non-FR materials useful in forming the long staple fibers and yarns of the present invention include aramids (including para-aramids and meta-aramids); polybenzimidazoles ("PBI"); polybenzoxazoles ("PBO"); modacrylics; poly{2,6-diimidazo[4,5-b:40;50-e]-pyridinylene-1,4(2,5-dihydroxy)phenylene} ("PIPD"); ultra-high molecular weight ("UHMW") polyethylene; UHMW polypropylene; polyvinyl alcohol; polyacrylonitrile; liquid crystal polymers; glass; nylon; carbon; silk; polyamides; polyesters; and natural and synthetic celluloses (e.g., cotton, rayon, acetate, triacetate, and lyocell fibers, as well as their flame retardant counterparts FR cotton, FR rayon, FR acetate, FR triacetate, and FR lyocell), TANLON™ fibers (Shanghai Tanlon Fibers). Available from Basofil Fibers), wool, melamine (such as BASOFIL™ available from Basofil Fibers), polyetherimide, polyethersulfone, pre-oxidized acrylic, polyamide-imide fibers such as KERMEL™, polytetrafluoroethylene, polyvinyl chloride, polyetheretherketone, polyetherimide fibers, polyclar, polyimide, polyimideamide, polyolefin, polyacrylate, and any combination or blend thereof.

[0031] Examples of para-aramid materials include KEVLAR™ (available from DuPont), TECHNORA™ (available from Teijin Twaron BV, Arnheim, Netherlands), and TWARON (available from Teijin Twaron BV). Examples of meta-aramid materials include NOMEX™ (available from DuPont), CONEX™ (available from Teijin), and Kermel (available from Kermel). An example of a suitable modacrylic material is PROTEX™ available from Kaneka Corporation, Osaka, Japan. An example of a PIPD material is M5 (DuPont). An example of a UHMW polyethylene material is the polymeric material VECTRAWM (available from Kuraray). Examples of suitable rayon materials are Viscose™ and Modal™ by Lenzing available from Lenzing Fibers Corporation. An example of a FR rayon material is Lenzing FR™, also available from Lenzing Fibers Corporation. Examples of lyocell materials include TENCEL G100™ and TENCEL A100™, both available from Lenzing Fibers Corporation.

[0032] In some embodiments, all long staple yarns in a fabric may be formed of 100% of a single type of fiber material, such that all long staple yarns in a fabric contain the same fiber material. Alternatively, two or more different types of fiber materials may be used in the long staple yarns, where each long staple yarn contains 100% of a single type of fiber material, but the different long staple yarns do not necessarily contain the same type of fiber material. Furthermore, two or more different types of fiber materials may be blended into a single long staple yarn, where each long staple yarn in a fabric contains the same fiber blend, or the blended yarns may be present with long staple yarns of a single material and / or with long staple yarns containing different fiber blends. For example, in one embodiment, a fabric may be formed of two different types of long staple yarns, one type formed of 100% of one material (e.g., aramid long staple fiber) and one type formed of a blend of long staple fibers (e.g., aramid and PBI long staple fiber). In any event, the long staple yarns in the fabric may all be formed of the same material, or at least a portion of the long staple yarns in the fabric may be formed of a different material as compared to other long staple yarns in the fabric. For example, different long staple yarns in the fabric may comprise different fiber blends based on the type of fiber materials in the blend or based on the ratio of fiber materials in the blend.

[0033] In some embodiments, the end of the long staple yarn may be formed by a single long staple yarn. In other embodiments, the end of the long staple yarn may be combined, coupled, or covered (i.e., plied, ply twisted, wrapped, coresheath, coverspun, etc.) with one or more other yarns, such as a filament yarn or another long staple yarn. Alternatively, the long staple yarn may be combined, coupled, or covered with one or more short staple yarns. However, in other embodiments, the long staple yarn is not combined, coupled, or covered with a short staple yarn. Furthermore, in some embodiments, the fabric does not include (i.e., the fabric is devoid of) short staple yarns and / or fibers. In some embodiments, the long staple yarn has an English cotton count (or equivalent denier for plied or twisted yarn) ranging from 7 / 1 to 20 / 1. For example, the English cotton count of plied long staple yarn may range from 14 / 2 to 40 / 2.

[0034] The filament yarns may be monofilament or multifilament yarns of 200-1200 denier (inclusive), 200-800 denier (inclusive), 200-600 denier (inclusive). As described above with respect to the long staple yarns, the ends of the filament yarns may be formed of only one or more filaments or may be combined, bonded, or coated with one or more other yarns. The filament yarns may be formed from inherently FR fibers or fibers that have been treated to be flame retardant. Materials useful as filament yarns in the fabrics of the invention include, but are not limited to, the same fibers described above for use in the long staple yarns. The long staple and filament yarns may include any combination of FR / non-FR materials so long as the entire fabric is flame retardant and / or meets the applicable or desired criteria for flame retardant fabrics. As an example, the fabric may be a protective fabric suitable for use in firefighting apparel (such as the outer shell of a firefighter's outfit), and preferably meets heat, flame, and fire performance and safety standards (e.g., heat shrink, vertical flammability, and char length requirements), such as those set forth in NFPA 1971. However, the flame resistant fabrics contemplated herein may be used in any suitable application and are not limited to use solely in the firefighting industry.

[0035] In some embodiments, at least some or all of the long staple yarns are formed of long staple fibers formed of a single type of material, such as PBI or aramid (meta- or para-aramid) long staple fibers. In some embodiments, at least some or all of the long staple yarns are formed of a blend of at least a first long staple fiber and a second long staple fiber made of a different material (or materials) than the first long staple fiber. In some embodiments, the first long staple fiber constitutes 30% to 65% of the fiber blend of the long staple yarn and the second long staple fiber constitutes 35% to 70% of the fiber blend of the long staple yarn. In some embodiments, the first long staple fiber constitutes 30% to 45% of the fiber blend of the long staple yarn and the second long staple fiber constitutes 55% to 70% of the fiber blend of the long staple yarn. In some embodiments, the first long staple fiber is an aramid fiber (e.g., para-aramid) that constitutes 30% to 65% (or 30% to 45%) of the fiber blend of the long staple yarn, and the second long staple fiber is a PBI fiber that constitutes 40% to 70% (or 55% to 70%) of the fiber blend. In some embodiments, the long staple yarn comprises PBI long staple fiber. In some embodiments, the PBI material is present only in the long staple yarn and / or not in the filament yarn. In some embodiments, the total weight percent of PBI in the fabric is 30% to 60% (inclusive); 35% to 55% (inclusive); or 40% to 50% (inclusive). In some embodiments, the total weight percent of PBI in the fabric is at least 30%, at least 35%, or at least 40%. In some embodiments, at least some or all of the filament yarns are formed from aramid fibers, more specifically para-aramid fibers. In some embodiments, the long staple yarns, filament yarns and / or fabric are formed entirely from essentially FR materials.

[0036] The flame retardant fabrics described herein may include long staple yarns and filament yarns in any combination or orientation. For example, in some examples of the present invention, the fabric may be a woven fabric including a warp direction and a weft direction. In such fabrics, long staple yarns may be included only in the warp direction, only in the weft direction, or in both the warp and weft directions. Similarly, filament yarns may be included only in the warp direction, only in the weft direction, or in both the warp and weft directions in the fabric. In some embodiments, the fabric includes a plurality of long staple yarns in both the warp and weft directions, and a plurality of filament yarns interwoven with a plurality of long staple yarns in both the warp and weft directions. In yet other embodiments, the fabric includes long staple yarns and filament yarns in one direction and only one of long staple yarns or filament yarns in the other direction.

[0037] In other exemplary embodiments, the long staple and / or filament yarns are woven or knitted into a fabric in a grid or stripe (e.g., horizontal or vertical) pattern. Any desired woven (e.g., plain, twill) or knit (e.g., single, double, plain, interlock) pattern may be used.

[0038] The long staple yarns can be arranged in a fabric in any desired ratio to the filament yarns. The ratio of long staple yarns to filament yarns can be the same or different (1) within one direction of the fabric and / or (2) in different directions of the fabric. The ratio is calculated by counting the ends of the yarns. For example, when considering a ply yarn (e.g., a long staple yarn plyed with another long staple yarn), each long staple yarn is not considered individually for purposes of determining the ratio, but rather the two plyed yarns together are considered as one end. For example, consider a fabric woven in a repeating pattern of two yarns (each formed by plying two long staple yarns together) followed by one filament yarn (monofilament or multifilament). In such a fabric, the ratio of filament yarns to long staple yarns is 1:2 based on the ends of each yarn.

[0039] The ratio of filament yarns to long staple yarns in the fabric may be from about 40:1 to about 1:40, or from about 30:1 to about 1:30, or from about 25:1 to about 1:25, or from about 20:1 to about 1:20, or from about 15:1 to about 1:15, or from about 10:1 to about 1:10, or 9:1, or 8:1, or 7:1, or 6:1, or 5:1, or 4:1, or 3:1, or 2:1, or 1:1, or 1:2, or 1:3, or 1:4, or 1:5, or 1:6, or 1:7, or 1:8, or 1:9, or from about 2:3 or 3:2 to about 1:3. In some embodiments, the ratio of filament yarns to long staple yarns in the fabric is from 1:1 to 6:1, or any intermediate ratio within that range. In certain embodiments, the ratio of filament yarns to long staple yarns in the fabric is from 1:2 to 1:8, from 1:3 to 1:7, or from 1:4 to 1:6, or any intermediate ratio therein.

[0040] The frequency of filament yarn presence and the number of filament yarns provided for each such presence may depend on the desired strength properties of the fabric as well as the size of the filament yarn. When larger size filament yarns are used, only one such yarn inserted at every nth end and / or pick may provide sufficient strength to the fabric. Conversely, when smaller filament yarns are used, two or more adjacent warps or picks of such yarns may be desirable.

[0041] In some embodiments, the fabrics disclosed herein have a weight of 2 to 12 ounces per square yard ("osy") (inclusive); 3 to 10 osy (inclusive); 3 to 9 osy (inclusive); 3 to 8.5 osy (inclusive); 4 to 8 osy (inclusive); 4 to 7.5 osy (inclusive); 4 to 7 osy (inclusive); 4.5 to 6.5 osy (inclusive); 5 to 7 osy; 5 to 6.5 osy (inclusive). In some embodiments, the weight of the fabric is 5 to 6 osy (inclusive) and / or is 6.5 osy or less and / or 6 osy or less.

[0042] The physical and thermal properties of fabrics formed in accordance with embodiments of the present invention ("inventive fabrics") were tested and compared to a control fabric. The fabrics were as follows: Control fabric 1 : A 7osy twill fabric made from two different ply yarns: 1 Sold by TenCate Protective Fabrics under the name KOMBAT FLEX.) Ply A: 2 short staple yarns - each 50% PBI / 50% Kevlar (20 / 2 cotton count) · Ply-twisted yarn B: One short staple yarn (P50%PBI / 50%Kevlar, 20 / 1 cotton count) is plyed with a para-aramid monofilament yarn (400 denier). The ratio of yarn B to yarn A was 1:2 in both the warp and weft directions (ie, BAABAABAA, etc.). Inventive Fabric 1: A 5.6 osy twill fabric woven with long staple (stretch-broken) yarns and filament yarns in both the warp and weft directions. The long staple yarns were formed from a blend of PBI (48%) and para-aramid (52%) long staple fibers. Each end of the long staple yarn was formed by twisting together two long staple yarns to give an English cotton count of 29 / 2. The filament yarns were 400 denier, 100% para-aramid multifilament yarns. The fabric was woven in a pattern of six ends of long staple yarns followed by one end of filament yarns in each of the warp and weft directions (i.e., a filament:long staple yarn ratio of 1:6). Inventive Fabric 2: A 5.6 osy twill fabric woven with long staple (stretch-broken) yarn and filament yarn in both the warp and weft directions. The long staple yarn was formed from a blend of PBI (63%) and para-aramid (37%) long staple fibers. Each end of the long staple yarn was formed by twisting together two long staple yarns to give an English cotton count of 29 / 2. The filament yarn was a 400 denier, 100% para-aramid multifilament yarn. The fabric was woven in a pattern of two ends of long staple yarn followed by one end of filament yarn in each of the warp and weft directions (i.e., a 1:2 ratio of filament yarn:long staple yarn). Inventive Fabric 3: A 5.6 osy twill fabric woven with long staple and filament yarns in both warp and weft directions. Two different types of long staple yarns (LSY) were used in the fabric. The first long staple yarn (LSY1) was formed of 100% para-aramid long staple fiber (i.e., para-aramid stretch-broken yarn). The second long staple yarn (LSY2) was formed of a blend of PBI (63%) and para-aramid (37%) long staple fiber. Each end of both types of long staple yarns was formed by plying two identical long staple yarns together to have an English cotton count of 29 / 2. Specifically, each end of the LSY1 yarn was formed by plying two LSY1 yarns together and each end of the LSY2 yarn was formed by plying two LSY2 yarns together. The filament yarn was a 400 denier, 100% para-aramid multifilament yarn. The fabric was woven in a pattern where each filament yarn was followed by five ends of long staple yarns (i.e., a filament to long staple yarn ratio of 1:5) in each of the warp and weft directions. More specifically, each filament yarn was followed by a long staple yarn end in the following order: LSY2, LSY2, LSY1, LSY2, LSY2. The total percentage of PBI in the fabric was about 40%.

[0043] The performance results of these fabrics are shown in Table 1. [Table 1] *Fabrics were washed according to AATCC 135, 1, V, Ai.

[0044] The fabrics described above were incorporated as outer shell fabrics into conventional material layups for firefighter garments conforming to NFPA 1971 to form garment composites (i.e., fabric composites including outer shell, moisture barrier, and thermal liner) for the equipment suits. More specifically, the fabrics were incorporated into the garment composites shown in Table 2. [Table 2]

[0045] The definitions of the terms used in Table 2 are as follows: "CROSSTECH BLACK®" refers to a capped ePTFE layer laminated to a meta-aramid fabric layer. This moisture barrier is flame retardant, air impermeable, vapor permeable, and waterproof. CROSSTECH BLACK® is available from Gore®. · The term "1.5osy spunlace" refers to a non-apertured, flame retardant spunlace fabric made of 67% meta-aramid fibers / 33% para-aramid fibers having a weight of approximately 1.5osy. The term "2.3 osy spunlace" refers to a non-apertured, flame retardant spunlace fabric made of 67% meta-aramid fibers / 33% para-aramid fibers having a weight of approximately 2.3 osy. The term "Caldura® Facecloth" refers to a flame retardant fabric woven with spun yarns made of a blend of 65% rayon fiber, 25% para-aramid fiber, and 10% nylon in the warp direction and 100% para-aramid fiber yarns in the weft direction. The fabric weighs approximately 3.5 osy and is available from TenCate®.

[0046] The thermal liner was placed within a garment composite such that the top layer of the thermal liner (the 2.3 osy spunlace layer) was positioned adjacent to the moisture barrier. The garment composite was tested for TPP performance per ISO 17492 (modified by NFPA 1971) and THL performance per ASTM F1868 (modified by NFPA 1971) and the results are shown in Table 3 below. [Table 3]

[0047] Long staple yarns can impart higher strength to a fabric compared to short staple yarns. Thus, a fabric containing long staple yarns is stronger than a fabric that differs only by including short staple yarns instead of long staple yarns. Also, using long staple yarns instead of weaker short staple yarns can reduce the overall weight of the fabric while maintaining or improving the strength of the fabric. This is shown in the results above, where inventive fabrics 1, 2 and 3 exhibited similar or increased strength properties to the control fabric, despite weighing 20% ​​less than the control fabric.

[0048] Table 4 below shows the ratios of strength properties (from Table 1) to weight for the control fabric and inventive fabrics 1-3. [Table 4] In all reported cases, the ratio of strength to weight properties was greater for the inventive fabrics than for the control fabrics.

[0049] In some embodiments, the trap tear strength (BW) to weight ratio in at least one of the warp or weft fabric directions, or in both the warp and weft fabric directions, is at least 12; at least 13; at least 14; at least 15; at least 16; at least 17; at least 18; at least 19; at least 20; at least 21; or at least 22. In some embodiments, the trap tear strength (BW) to weight ratio in at least one of the warp or weft fabric directions, or in both the warp and weft fabric directions, is 12 to 24, inclusive; 13 to 22, inclusive; 14 to 20, inclusive; 13 to 17, inclusive; or 14 to 17, inclusive.

[0050] In some embodiments, the trap tear strength (5X) to weight ratio in at least one of the warp or weft fabric directions, or in both the warp and weft fabric directions, is at least 8; at least 9; at least 10; at least 11; at least 12; at least 13; at least 14; at least 15; at least 16; at least 17; at least 18; at least 19; at least 20; at least 21; or at least 22. In some embodiments, the trap tear strength (BW) to weight ratio in at least one of the warp or weft fabric directions, or in both the warp and weft fabric directions, is 8 to 24, inclusive; 9 to 22, inclusive; 12 to 20, inclusive; 13 to 17, inclusive; 13 to 15, inclusive; or 14 to 16, inclusive.

[0051] In some embodiments, the tensile strength (BW) to weight ratio in at least one of the warp or weft fabric directions, or in both the warp and weft fabric directions, is at least 45; at least 50; at least 55; at least 60; or at least 65. In some embodiments, the tensile strength (BW) to weight ratio in at least one of the warp or weft fabric directions, or in both the warp and weft fabric directions, is 50-70 (inclusive); 50-60 (inclusive); 55-70 (inclusive); 55-65 (inclusive); or 60-70 (inclusive).

[0052] In some embodiments, the ratio of tensile strength (10X) to weight in at least one of the warp or weft fabric directions, or in both the warp and weft fabric directions, is at least 45; at least 50; or at least 55. In some embodiments, the ratio of tensile strength (10X) to weight in at least one of the warp or weft fabric directions, or in both the warp and weft fabric directions, is from 40 to 60, inclusive; from 45 to 60, inclusive; or from 50 to 60, inclusive.

[0053] example Provided below is a collection of exemplary embodiments, including at least some explicitly listed as "Examples," that provide further illustration of various exemplary types consistent with the concepts described herein. These examples are not intended to be mutually exclusive, exhaustive, or limiting. Additionally, the present invention is not limited to these illustrative examples, but rather includes all possible modifications and variations within the scope of the issued claims and their equivalents.

[0054] Example 1. A flame retardant fabric comprising: a plurality of long staple yarns comprising a plurality of long staple fibers comprising a flame retardant material; and a plurality of filament yarns comprising a flame retardant material, and no short staple yarns.

[0055] Example 2. The flame resistant fabric of any preceding or subsequent example or combination of examples, wherein at least a portion of the plurality of long staple yarns comprises a fiber blend including first long staple fibers comprising a first type of flame resistant material and second long staple fibers comprising a second type of flame resistant material different from the first type of flame resistant material.

[0056] Example 3. The flame retardant fabric of any preceding or following example or combination of examples, wherein the first type of flame retardant material is aramid and the second type of flame retardant material is PBI.

[0057] Example 4. The flame retardant fabric of any preceding or following example or combination of examples, wherein the first long staple fiber comprises 30-45% of the fiber blend and the second long staple fiber comprises 55-70% of the fiber blend.

[0058] Example 5. The flame retardant fabric of any preceding or following example or combination of examples, wherein the first type of flame retardant material is an aramid and the second type of flame retardant material is a polybenzimidazole.

[0059] Example 6. The flame resistant fabric of any of the preceding or following examples or combinations of examples, wherein at least a portion of the long staple fibers of the plurality of long staple yarns comprise a single type of flame resistant material.

[0060] Example 7. The flame resistant fabric of any preceding or following example or combination of examples, wherein the long staple fibers of others of the plurality of long staple yarns comprise a single type of flame resistant material, and the single type of flame resistant material is the same as the first type of flame resistant material.

[0061] Example 8. The flame retardant fabric of any of the preceding or following examples or combinations of examples, wherein the first type of flame retardant material comprises para-aramid.

[0062] Example 9. The flame retardant fabric of any of the preceding or following examples or combinations of examples, wherein at least a portion of the plurality of long staple yarns are twisted with other yarns.

[0063] Example 10. The flame retardant fabric of any preceding or subsequent example or combination of examples, wherein the flame retardant material of at least some of the plurality of filament yarns comprises aramid.

[0064] Example 11. A flame retardant fabric of any preceding or following example or combination of examples, comprising 1 to 6 long staple yarn ends for every filament yarn end extending in at least one direction of the fabric.

[0065] Example 12. A flame retardant fabric of any preceding or following example or combination of examples, including a warp direction and a weft direction, wherein a plurality of long staple yarns and filament yarns are provided in both the warp direction and the weft direction.

[0066] Example 13. A flame retardant fabric of any preceding or following example or combination of examples, having at least three and less than eight long staple yarn ends between adjacent filament yarn ends in at least one of the warp or weft directions.

[0067] Example 14. A flame-retardant fabric of any of the preceding or succeeding examples or combinations of examples containing a weight of 4 to 7 ounces per square yard.

[0068] Example 15. A flame retardant woven fabric having a warp direction and a weft direction, the flame retardant woven fabric comprising: a plurality of flame retardant long staple yarns extending in both the warp direction and the weft direction, at least a portion of the plurality of long staple yarns comprising a fiber blend comprising a plurality of first long staple fibers comprising a first type of material and a plurality of second long staple fibers comprising a second type of material different from the first type of material; and a plurality of flame retardant filament yarns interwoven with the plurality of long staple yarns in both the warp direction and the weft direction.

[0069] Example 16. The flame retardant woven fabric of any of the preceding or following examples or combinations of examples, wherein at least other of the plurality of flame retardant long staple yarns comprises a single type of material.

[0070] Example 17. A flame retardant woven fabric of any preceding or following example or combination of examples, in which the single type of material and the first type of material are the same.

[0071] Example 18. A flame resistant woven fabric having a warp direction and a weft direction, comprising: flame resistant first long staple yarns extending in both the warp direction and the weft direction, each first long staple yarn comprising a fiber blend including a plurality of first long staple fibers comprising a first type of material and a plurality of second long staple fibers comprising a second type of material different from the first type of material; flame resistant second long staple yarns extending in both the warp direction and the weft direction, each second long staple yarn being formed of a single type of material; and 1. A flame retardant woven fabric comprising: a flame retardant filament yarn interwoven with first and second long staple yarns in both the warp and weft directions, each end of the first long staple yarn comprising at least two first long staple yarns twisted together, each end of the second long staple yarn comprising at least two second long staple yarns twisted together, and wherein there are greater than three and less than eight first long staple yarn ends and second long staple yarn ends collectively between adjacent filament yarn ends in at least one of the warp or weft directions.

[0072] Example 19. A flame retardant woven fabric of any preceding or following example or combination of examples, wherein the single type of material and the first type of material are the same.

[0073] Example 20. The flame retardant woven fabric of any preceding or following example or combination of examples, wherein the first type of material comprises para-aramid and the second type of material comprises polybenzimidazole.

[0074] Alternative arrangements of the above components, as well as components not shown or described, may be used. Also, some features and subcombinations are possible. bcombination) is useful and refers to other features and subcombinations. The embodiments of the present invention are described by way of illustration and not by way of limitation. Alternative embodiments will be apparent to the reader of this patent. The invention is not limited to the embodiments described above or illustrated in the drawings, but may be embodied in various embodiments and Modifications may be made without departing from the scope of the invention. <Additional Notes> Item 1 (a) a plurality of long staple yarns comprising a plurality of long staple fibers comprising a flame retardant material; and (b) a multifilament yarn containing a flame retardant material; Including, A flame retardant fabric that does not contain short staple yarns. Section 2 Item 2. The flame resistant fabric of item 1, wherein at least a portion of the plurality of long staple yarns comprises a fiber blend comprising a first long staple fiber comprising a first type of flame resistant material and a second long staple fiber comprising a second type of flame resistant material different from the first type of flame resistant material. Section 3 Item 3. The flame retardant fabric according to item 2, wherein the first type of flame retardant material is aramid and the second type of flame retardant material is PBI. Section 4 Item 3. The flame retardant fabric according to item 2, wherein the first long staple fiber comprises 30-45% of the fiber blend, and the second long staple fiber comprises 55-70% of the fiber blend. Section 5 Item 5. The flame retardant fabric according to item 4, wherein the first type of flame retardant material is aramid and the second type of flame retardant material is polybenzimidazole. Section 6 Item 2. The flame resistant fabric of item 1, wherein at least a portion of the long staple fibers of the plurality of long staple yarns comprise a single type of flame resistant material. Section 7 Item 3. The flame resistant fabric of item 2, wherein the long staple fibers of other of the plurality of long staple yarns comprise a single type of flame resistant material, and the single type of flame resistant material is the same as the first type of flame resistant material. Section 8 Item 8. The flame retardant fabric of item 7, wherein the first type of flame retardant material comprises para-aramid. Section 9 Item 2. The flame-retardant fabric according to item 1, wherein at least a portion of the plurality of long staple yarns is twisted with other yarns. Item 10 Item 1. The flame retardant fabric according to item 1, wherein the flame retardant material of at least a portion of the plurality of filament yarns comprises aramid. Section 11 Item 1. The flame-retardant fabric of item 1, comprising 1 to 6 long staple yarn ends for every filament yarn end extending in at least one direction of the fabric. Item 12 Item 1. A flame retardant fabric according to item 1, having a warp direction and a weft direction, wherein the plurality of long staple yarns and filament yarns are provided in both the warp direction and the weft direction. Item 13 Item 13. The flame retardant fabric of item 12, wherein there are at least three and less than eight long staple yarn ends between adjacent filament yarn ends in at least one of the warp direction or the weft direction. Item 14 Item 1. A flame-retardant fabric according to item 1, having a weight of 4 to 7 ounces per square yard, inclusive. Item 15 A flame retardant woven fabric having a warp direction and a weft direction, (a) a plurality of flame retardant long staple yarns extending in both the warp and weft directions, at least a portion of the plurality of long staple yarns comprising a fiber blend including a plurality of first long staple fibers comprising a first type of material and a plurality of second long staple fibers comprising a second type of material different from the first type of material; and (b) a plurality of flame-retardant filament yarns interwoven with said plurality of long staple yarns in both the warp and weft directions; A flame retardant woven fabric comprising: Section 16 16. The flame resistant woven fabric of claim 15, wherein at least others of the plurality of flame resistant long staple yarns comprise a single type of material. Section 17 Item 17. The flame retardant woven fabric according to item 16, wherein the single type of material and the first type of material are the same. Section 18 A flame retardant woven fabric having a warp direction and a weft direction, (a) flame-retardant first long staple yarns extending in both the warp and weft directions, each first long staple yarn comprising a fiber blend including a plurality of first long staple fibers comprising a first type of material and a plurality of second long staple fibers comprising a second type of material different from the first type of material; (b) flame-retardant second long staple yarns extending in both the warp and weft directions, each second long staple yarn being formed of a single type of material; and (c) a flame-retardant filament yarn interwoven with said first and second long staple yarns in both the warp and weft directions. Including, - each end of said first long staple yarn comprises at least two first long staple yarns twisted together; - each end of said second long staple yarn comprises at least two second long staple yarns twisted together; and a total of more than three and less than eight first long staple yarn ends and second long staple yarn ends between adjacent filament yarn ends in at least one of the warp direction or the weft direction. Section 19 Item 19. The flame retardant woven fabric according to item 18, wherein the single type of material and the first type of material are the same. Item 20 20. The flame retardant woven fabric of claim 19, wherein the first type of material comprises para-aramid and the second type of material comprises polybenzimidazole.

Claims

1. (a) a plurality of long staple yarns comprising a flame retardant material and including a plurality of long staple fibers having a length of greater than 2 inches (51 mm) to 40 inches (1016 mm); and (b) a plurality of filament yarns including a flame retardant material; Including, A flame retardant fabric that does not contain short staple yarns that contain short staple fibers having a length of 2 inches (51 mm) or less.

2. 2. The flame resistant fabric of claim 1, wherein at least a portion of the plurality of long staple yarns comprises a fiber blend including first long staple fibers comprising a first flame resistant material and second long staple fibers comprising a second flame resistant material different from the first flame resistant material.

3. 3. The flame retardant fabric of claim 2, wherein the first flame retardant material is an aramid and the second flame retardant material is PBI.

4. 3. The flame resistant fabric of claim 2, wherein said first long staple fibers are 30-45% of said fiber blend and said second long staple fibers are 55-70% of said fiber blend.

5. 5. The flame retardant fabric of claim 4, wherein the first flame retardant material is an aramid and the second flame retardant material is a polybenzimidazole.

6. 10. The flame resistant fabric of claim 1, wherein at least a portion of said plurality of long staple yarns are formed of long staple fibers formed of a single flame resistant material.

7. 3. The flame resistant fabric of claim 2, wherein others of the plurality of long staple yarns are formed of long staple fibers formed of a single flame resistant material, the single flame resistant material being the same as the first flame resistant material.

8. 8. The flame resistant fabric of claim 7, wherein the first flame resistant material is a para-aramid.

9. 10. The flame resistant fabric of claim 1, wherein at least a portion of the plurality of long staple yarns are intertwined with other yarns.

10. 10. The flame resistant fabric of claim 1, wherein the flame resistant material of at least some of the plurality of filament yarns comprises aramid.

11. 10. The flame resistant fabric of claim 1, which is a flame resistant woven fabric comprising 1 to 6 long staple yarn ends for every filament yarn end extending in at least one direction of the fabric.

12. The flame retardant fabric of claim 1, wherein the fabric is a flame retardant woven fabric having a warp direction and a weft direction, and the plurality of long staple yarns and filament yarns are provided in both the warp direction and the weft direction.

13. 13. The flame resistant fabric of claim 12, comprising at least three and no more than eight long staple yarn ends between adjacent filament yarn ends in at least one of the warp direction or the weft direction.

14. 10. The flame resistant fabric of claim 1 having a weight of 4 to 7 ounces per square yard, inclusive.

15. A flame retardant woven fabric having a warp direction and a weft direction, (a) a plurality of flame retardant long staple yarns extending in both the warp and weft directions, at least a portion of the plurality of long staple yarns comprising a fiber blend including: (i) a plurality of first long staple fibers comprising a first material and having a length of greater than 2 inches (51 mm) to 40 inches (1016 mm); and (ii) a plurality of second long staple fibers comprising a second material different from the first material and having a length of greater than 2 inches (51 mm) to 40 inches (1016 mm); and (b) a plurality of flame-retardant filament yarns interwoven with said plurality of long staple yarns in both the warp and weft directions. A flame retardant woven fabric comprising:

16. 16. The flame resistant woven fabric of claim 15, wherein at least other of said plurality of flame resistant long staple yarns are formed of a single material.

17. 17. The flame resistant woven fabric of claim 16, wherein the single material and the first material are the same.

18. A flame retardant woven fabric having a warp direction and a weft direction, (a) flame resistant first long staple yarns extending in both the warp and weft directions, each first long staple yarn comprising a fiber blend including: (i) a plurality of first long staple fibers comprising a first material and having a length of greater than 2 inches (51 mm) to 40 inches (1016 mm); and (ii) a plurality of second long staple fibers comprising a second material different from the first material and having a length of greater than 2 inches (51 mm) to 40 inches (1016 mm); (b) flame-retardant second long staple yarns extending in both the warp and weft directions, each second long staple yarn being formed of a single material and formed of a third long staple fiber having a length of greater than 2 inches (51 mm) to 40 inches (1016 mm); and (c) a flame retardant filament yarn interwoven with said first and second long staple yarns in both the warp and weft directions. Including, - each end of said first long staple thread comprises at least two first long staple threads twisted together; - each end of said second long staple yarn comprises at least two second long staple yarns twisted together; and - a total of more than three and less than eight first long staple yarn ends and second long staple yarn ends are provided between adjacent filament yarn ends in at least one of the warp direction or the weft direction.

19. 20. The flame resistant woven fabric of claim 18, wherein the single material and the first material are the same.

20. 20. The flame resistant woven fabric of claim 19, wherein the first material is a para-aramid and the second material comprises polybenzimidazole.