TWC catalysts for gasoline exhaust applications with improved thermal durability.

Abstract

To provide a catalyst article exhibiting high thermal durability while maintaining a high level of three-way catalyst performance, and an exhaust system for internal combustion engines based thereon.SOLUTION: The catalyst article comprises: a substrate; and a catalytic region on the substrate. The catalytic region comprises a first platinum group metal (PGM) component, an oxygen storage component (OSC) material, a rare earth metal oxide, and an inorganic oxide. The rare earth metal oxide has an average diameter (d50) of more than 100 nm.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to catalytic articles useful for treating exhaust gas emissions from gasoline engines. [Background technology]

[0002] In internal combustion engines, hydrocarbons (HC), carbon monoxide (CO), and nitrogen oxides (NO x In gasoline engines, exhaust gases containing various pollutants such as benzene, benzene, and benzene are produced. Emissions control systems that include exhaust gas catalysts are widely used to reduce the amount of these pollutants emitted into the atmosphere. The catalyst typically used in gasoline engine applications is the three-way catalyst (TWC). The TWC serves three main functions: (1) the oxidation of carbon monoxide (CO), (2) the oxidation of unburned hydrocarbons, and (3) the oxidation of NO. x is reduced to N2.

[0003] TWC catalysts require careful engine management techniques to ensure that the engine operates at or near stoichiometric conditions (air / fuel ratio λ=1). However, for technical reasons, the engine needs to operate on either side of λ=1 at various stages during the operating cycle. When the engine is running rich, e.g., during acceleration, the overall exhaust gas composition is reducing in nature and it is more difficult to perform oxidation reactions on the catalyst surface. For this reason, TWCs have been developed to incorporate components that store oxygen during lean periods of the operating cycle and release oxygen during rich periods of the operating cycle, thereby extending the effective operating period. For such purposes, ceria-based (e.g., ceria-zirconia mixed oxide) materials are used as oxygen storage components (OSCs) in the majority of current commercially available TWCs.

[0004] It is well known that exposure of such catalysts to high temperatures, e.g., above 800 °C, can lead to sintering of both the OSC material and the active precious metal, thus degrading the overall performance of the catalyst. For this reason, much effort has been devoted to enhancing the thermal stability of OSC materials. One approach is to introduce other rare earth ions into the OSC material, which is usually done by using soluble rare earth metal precursor solutions as dopants.

[0005] Despite advances in TWC technology, there remains a need for improved catalytic converters for certain engine platforms that provide high conversion rates with improved thermal stability. The present invention addresses these needs, among others. Summary of the Invention

[0006] One aspect of the disclosure is a catalytic article for treating exhaust gases, comprising a substrate and a catalytic region on the substrate, the catalytic region comprising a first platinum group metal (PGM) component, an oxygen storage component (OSC) material, a rare earth metal oxide, and an inorganic oxide, the rare earth metal oxide having an average diameter (d 50 )

[0007] The present invention also includes an exhaust system for an internal combustion engine which includes the three-way catalyst component of the present invention.

[0008] The present invention also encompasses the treatment of exhaust gases from internal combustion engines, particularly gasoline engines, which method comprises contacting the exhaust gases with a three-way catalyst component of the present invention.

[0009] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, the specific surface area of ​​the composition being increased by at least 15% compared to the ceria-zirconia mixed oxide after calcination in air at 1000° C. for 10 hours, the rare earth metal oxide being selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0010] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, wherein the specific surface area of ​​the composition is increased by at least 35% after calcination in air at 1000° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0011] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, wherein the specific surface area of ​​the composition is increased by at least 5% compared to the ceria-zirconia mixed oxide after calcination in air at 1100° C. for 10 hours, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0012] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, wherein the specific surface area of ​​the composition is increased by at least 20% after calcination in air at 1100° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0013] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, wherein the specific surface area of ​​the composition is increased by at least 10% compared to the ceria-zirconia mixed oxide after calcination at 1000° C. for 10 hours under redox conditions, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0014] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, wherein the specific surface area of ​​the composition is increased by at least 10% after calcination at 1000° C. for 10 hours under redox conditions compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0015] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, wherein the specific surface area of ​​the composition is increased by at least 10% compared to the ceria-zirconia mixed oxide after calcination at 1100° C. for 10 hours under redox conditions, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0016] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, wherein the specific surface area of ​​the composition is increased by at least 10% after calcination at 1100° C. for 10 hours under redox conditions compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0017] The present invention relates to the catalytic treatment of combustion exhaust gases, such as those produced by gasoline and other engines, and related catalyst articles and systems. More specifically, the present invention relates to a method for reducing NOx in vehicle exhaust systems. x Surprisingly, the inventors have found that the average diameter (d 50 It has been found that by incorporating a rare earth metal oxide having a TWC ratio of 0.1 to 0.5 in the catalyst, the catalyst of the present invention exhibits high thermal durability while maintaining a high level of TWC performance.

[0018] One aspect of the disclosure is a catalytic article for treating exhaust gases, comprising a substrate and a catalytic region on the substrate, the catalytic region comprising a first platinum group metal (PGM) component, an oxygen storage component (OSC) material, a rare earth metal oxide, and an inorganic oxide, the rare earth metal oxide having an average diameter (d 50 )

[0019] The first PGM is preferably selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof. Particularly preferably, the first PGM is palladium.

[0020] The catalyst zone preferably comprises from 0.03 to 10 wt% of the first PGM, more preferably from 0.03 to 7 wt% of the first PGM, most preferably from 0.03 to 4 wt% of the first PGM, based on the total weight of the catalyst zone.

[0021] In embodiments where the first PGM is palladium, the catalyst zone preferably comprises from 0.03 to 10 wt% palladium, more preferably from 0.03 to 7 wt% palladium, and most preferably from 0.03 to 4 wt% palladium, based on the total weight of the catalyst zone.

[0022] The OSC material is preferably selected from the group consisting of cerium oxide, ceria-zirconia mixed oxide, and alumina-ceria-zirconia mixed oxide. Preferably, the OSC material is ceria-zirconia mixed oxide. The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of 9:1 to 1:9, preferably 8:2 to 2:8, more preferably 7:3 to 3:7.

[0023] The OSC material (eg, ceria-zirconia mixed oxide) may range from 20 to 80 wt % based on the total weight of the catalyst region.

[0024] The rare earth metal oxide may range from 2 to 20 wt %, preferably from 5 to 15 wt %, and more preferably from 8 to 12 wt % of the weight of the OSC material.

[0025] Rare earth metal oxides are La2O3, Pr6O 11 , Nd2O3, Y2O3, and mixtures thereof. Preferably, the rare earth metal oxide is selected from the group consisting of Pr6O 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0026] The average diameter of the rare earth metal oxide in the catalytic region may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the catalytic region may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the catalytic region may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the catalytic region may be at least 8 μm or greater.

[0027] The inorganic oxide is preferably an oxide of an element of group 2, group 3, group 4, group 5, group 13, or group 14. The inorganic oxide is preferably selected from the group consisting of alumina, lanthanide-stabilized alumina, alkaline earth-stabilized alumina, silica, aluminosilicate, magnesia / alumina composite oxide, titania, niobia, tantalum oxide, neodymium oxide, yttrium oxide, lanthanides, and mixed or composite oxides thereof. Particularly preferably, the inorganic oxide is alumina, lanthanide-stabilized alumina, or magnesia / alumina composite oxide. One particularly preferred inorganic oxide is alumina or lanthanide-stabilized alumina.

[0028] The inorganic oxide is preferably 10 to 1500 m 2 / g, pore volume in the range of 0.1 to 4 mL / g, and pore diameter of about 10 to 1000 Å. 2High surface area inorganic oxides, such as high surface area alumina, having a surface area of ​​more than 1000 nm / g are particularly preferred. Other preferred inorganic oxides include magnesia / alumina composite oxides, which optionally further include a cerium-containing component, such as ceria. In such cases, the ceria may be present on the surface of the magnesia / alumina composite oxide, for example as a coating.

[0029] Alternatively, the OSC material and the inorganic oxide may have a weight ratio of 10:1 to 1:10, preferably 8:1 to 1:8 or 5:1 to 1:5, more preferably 4:1 to 1:4 or 3:1 to 1:3, and most preferably 2:1 to 1:2.

[0030] The catalytic region may further comprise an alkali metal or an alkaline earth metal. In some embodiments, the alkali metal or alkaline earth metal may be deposited on the OSC material. Alternatively, or in addition, the alkali metal or alkaline earth metal may be deposited on the inorganic oxide. That is, in some embodiments, the alkali metal or alkaline earth metal may be deposited on, or present on, both the OSC material and the inorganic oxide.

[0031] The alkali metal or alkaline earth metal is generally in contact with an inorganic oxide. Preferably, the alkali metal or alkaline earth metal is supported on an inorganic oxide. In addition to or instead of being in contact with the inorganic oxide, the alkali metal or alkaline earth metal may be in contact with the OSC material.

[0032] The alkali or alkaline earth metal is preferably barium or strontium. More preferably, barium, if present, is less than 30% by weight, most preferably less than 20% by weight, based on the total weight of the catalyst region.

[0033] The total washcoat loading in the catalyst area is 0.1-5 g / in 3 , preferably 0.5 to 4 g / in 3 , more preferably 1 to 3 g / in3 , and most preferably 1.5 to 2.5 g / in 3 may be also possible.

[0034] The catalyst region may further comprise a second PGM component.

[0035] The second PGM is preferably selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof. It is particularly preferred that when the first PGM component is palladium, the second PGM component is rhodium.

[0036] In some embodiments, the palladium component and the rhodium component have a weight ratio of 200:1 to 1:200. Preferably, the palladium component and the rhodium component have a weight ratio of 100:1 to 1:100. More preferably, the palladium component and the rhodium component have a weight ratio of 50:1 to 1:50.

[0037] In certain embodiments, the catalytic region is essentially free of PGM metals other than the palladium component.

[0038] The catalytic region of the present invention may contain further components known to those skilled in the art. For example, the composition of the present invention may further comprise at least one binder and / or at least one surfactant. When a binder is present, a dispersible alumina binder is preferred.

[0039] The substrate may be a metal or ceramic substrate. Preferably, the substrate is a flow-through monolith or a filter monolith.

[0040] The monolith substrate acts as a support to hold the catalytic material. Suitable materials for forming the monolith substrate include ceramic-like materials such as cordierite, silicon carbide, silicon nitride, zirconia, mullite, spodumene, alumina-silica magnesia or zirconium silicate, or porous refractory metals. Such materials and their use in the manufacture of porous monolith substrates are well known in the art.

[0041] When the monolith is a filtering monolith, the filtering monolith is preferably a wall-flow filter. In a wall-flow filter, each inlet channel is alternately separated from an outlet channel by a wall of porous structure, and vice versa. The inlet and outlet channels are preferably arranged in a honeycomb arrangement. If a honeycomb arrangement is present, the channels vertically and laterally adjacent to the inlet channel are preferably plugged at their upstream ends, and vice versa (i.e. the channels vertically and laterally adjacent to the outlet channel are plugged at their downstream ends). When viewed from either end, the alternating plugged and open ends of the channels take on the appearance of a chessboard.

[0042] The substrate may be an electrically heatable substrate (i.e., an electrically heatable substrate is a substrate that heats electrically during use). When the substrate is an electrically heatable substrate, the catalytic article of the present invention includes a power connection, preferably at least two power connections, more preferably only two power connections. Each power connection may be electrically connected to the electrically heatable substrate and to a power source. The catalytic article may be heated by Joule heating, where a current through a resistor converts electrical energy into thermal energy.

[0043] Generally, the electrically heatable substrate comprises a metal, which may be electrically connected to a power connection or connections.

[0044] Typically, the electrically heatable substrate is an electrically heatable honeycomb substrate. The electrically heatable substrate may be a honeycomb substrate that, in use, heats electrically.

[0045] The electrically heatable substrate may include an electrically heatable substrate monolith (e.g., a metal monolith). The monolith may include a corrugated metal sheet or foil. The corrugated metal sheet or foil may be rolled, wound, or stacked. If the corrugated metal sheet is rolled or wound, it may be rolled or wound into a coil, a spiral shape, or a concentric pattern.

[0046] The metal, metal monolith and / or corrugated metal sheet or foil of the electrically heatable substrate may comprise an aluminium ferritic steel, such as Fecralloy™.

[0047] The catalyst of the present invention can be prepared by any suitable means. For example, the catalyst can be prepared by mixing the first PGM, the optional first alkali or alkaline earth metal or second PGM, the inorganic oxide, the OSC material, and the rare earth metal oxide in any order. The method and order of addition is not considered to be particularly important. For example, each component of the catalyst may be added simultaneously to any other component or components, or may be added sequentially in any order. Each component of the catalyst may be added to any other component of the catalyst by impregnation, adsorption, ion exchange, incipient wetness, precipitation, etc., or by any other means commonly known in the art.

[0048] Preferably, the rare earth metal oxide is incorporated into the catalyst region by physical blending, rather than as a dopant.

[0049] The rare earth metal oxide may be added as the last major component to the mixture.

[0050] Preferably, the above catalyst is prepared by depositing the catalyst on a substrate using a washcoating procedure. A representative process for preparing the catalyst using a washcoating procedure is described below. It will be understood that the following process may be modified according to different embodiments of the present invention.

[0051] Washcoating is preferably carried out by first slurrying finely divided particles of the components of the catalyst defined above in a suitable solvent, preferably water, to form a slurry. The slurry preferably contains a solids content of 5-70% by weight, more preferably 10-50% by weight. Preferably, the particles are milled or subjected to another grinding process to ensure that substantially all solid particles have a particle size of less than 20 μm in average diameter before forming the slurry. Additional components such as stabilizers, binders, surfactants, or promoters may also be incorporated into the slurry as a mixture of water-soluble or water-dispersible compounds or complexes.

[0052] The substrate can then be coated with the slurry one or more times to deposit a desired loading of catalyst on the substrate.

[0053] Alternatively, the catalytic article of the present invention may further comprise a second catalytic region, such as a second catalytic region described below. The above catalytic region is hereinafter referred to as a first catalytic region. Thus, the catalytic article comprises a first catalytic region and a second catalytic region. For the avoidance of doubt, the first catalytic region is different (i.e., compositionally different) from the second catalytic region.

[0054] In the first arrangement, the first catalyst region is a first catalyst layer and the second catalyst region is a second catalyst layer. The first catalyst layer may be disposed or supported (e.g., directly disposed or supported) on the second catalyst layer. Alternatively, the second catalyst layer may be disposed or supported (e.g., directly disposed or supported) on the first catalyst layer. It is preferred that the second catalyst layer is disposed or supported (e.g., directly disposed or supported) on the first catalyst layer.

[0055] The first catalyst layer typically extends along the entire length (ie, substantially the entire length) of the substrate, and in particular along the entire length of the channels of the substrate monolith.

[0056] The second catalyst layer typically extends along the entire length (ie, substantially the entire length) of the substrate, and in particular along the entire length of the channels of the substrate monolith.

[0057] In the second configuration, the first catalytic region is a first catalytic zone and the second catalytic region is a second catalytic zone. The first catalytic zone may be disposed upstream of the second catalytic zone. Alternatively, the second catalytic zone may be disposed upstream of the first catalytic zone. Preferably, the first catalytic zone is disposed upstream of the second catalytic zone.

[0058] The first catalytic zone may be adjacent to the second catalytic zone, or there may be a gap (e.g., space) between the first and second catalytic zones. Preferably, the first catalytic zone is in contact with the second catalytic zone. When the first catalytic zone is adjacent and / or in contact with the second catalytic zone, the combination of the first catalytic zone and the second catalytic zone may be disposed or supported as a layer on a substrate. Thus, when the first and second catalytic zones are adjacent or in contact with each other, a layer may be formed on the substrate. Such an arrangement can avoid problems due to back pressure.

[0059] The first catalytic zone typically has a length of 10 to 90% of the length of the substrate, preferably 15 to 75% of the length of the substrate, more preferably 20 to 70% of the length of the substrate, and even more preferably 25 to 65% of the length of the substrate.

[0060] The second catalytic zone typically has a length of 10 to 90% of the length of the substrate, preferably 15 to 75% of the length of the substrate, more preferably 20 to 70% of the length of the substrate, and even more preferably 25 to 65% of the length of the substrate.

[0061] The first catalytic zone and the second catalytic zone may be disposed or supported on (eg, directly disposed or supported on) a substrate.

[0062] In a third configuration, the second catalytic region is disposed or supported (eg, directly disposed or supported) on the first catalytic region.

[0063] The first catalytic region may be disposed or supported on (eg, directly disposed or supported on) a substrate.

[0064] The entire length (e.g., all) of the second catalytic region may be disposed or supported (e.g., directly disposed or supported) on the first catalytic region. Alternatively, only a portion or part of the length of the second catalytic region may be disposed or supported (e.g., directly disposed or supported) on the first catalytic region. Only a portion or part of the length of the second catalytic region (e.g., the remaining portion or part) may be disposed or supported (e.g., directly disposed or supported) on the substrate.

[0065] The second catalytic region may be a second catalytic layer and the first catalytic region may be a first catalytic zone. The entire length of the second catalytic zone is preferably disposed or supported on the first catalytic layer. The first catalytic layer may be disposed or supported (e.g., directly disposed or supported) on a substrate.

[0066] The first catalyst layer typically extends along the entire length (ie, substantially the entire length) of the substrate, and in particular along the entire length of the channels of the substrate monolith.

[0067] The second catalytic zone typically has a length of 10 to 90% of the length of the substrate, preferably 15 to 75% of the length of the substrate, more preferably 20 to 70% of the length of the substrate, and even more preferably 25 to 65% of the length of the substrate.

[0068] The second catalytic zone may be disposed at or near the inlet end of the substrate. The second catalytic zone may be disposed at or near the outlet end of the substrate. Preferably, the second catalytic zone is disposed at or near the outlet end of the substrate.

[0069] In an alternative third arrangement, the second catalytic region is a second catalytic zone and the first catalytic region is a first catalytic zone or a first catalytic layer, the second catalytic zone or second catalytic layer being disposed or supported (e.g., directly disposed or supported) on the first catalytic zone.

[0070] The first catalytic zone typically has a length of 10 to 90% of the length of the substrate, preferably 15 to 75% of the length of the substrate, more preferably 20 to 70% of the length of the substrate, and even more preferably 25 to 65% of the length of the substrate.

[0071] The second catalytic zone may be disposed at or near the outlet end of the substrate. The second catalytic zone may be disposed at or near the inlet end of the substrate. Preferably, the second catalytic zone is disposed at or near the outlet end of the substrate.

[0072] In addition to being disposed or supported on the first catalytic zone, the second catalytic zone or second catalytic layer may be disposed or supported (e.g., directly disposed or supported) on a substrate. Thus, a portion or portion of the length of the second catalytic zone or second catalytic layer may be disposed or supported (e.g., directly disposed or supported) on the first catalytic zone, and a portion or portion of the length of the second catalytic zone or second catalytic layer (e.g., the remaining portion or portion) may be disposed or supported (e.g., directly disposed or supported) on a substrate.

[0073] In the alternative third arrangement, when the first catalytic region is a first catalytic zone, the first catalytic zone typically has a length of from 10 to 90% of the length of the substrate, preferably from 15 to 75% of the length of the substrate, more preferably from 20 to 70% of the length of the substrate, and even more preferably from 25 to 65%.

[0074] The first catalytic zone may be disposed at or near the inlet end of the substrate. The first catalytic zone may be disposed at or near the outlet end of the substrate. Preferably, the first catalytic zone is disposed at or near the inlet end of the substrate.

[0075] In a third alternative arrangement, when the first catalytic region is a first catalytic layer, the first catalytic layer typically extends the entire length (i.e., substantially the entire length) of the substrate, particularly the entire length of the channels of the substrate monolith. When the first catalytic region is a first catalytic layer, preferably the second catalytic zone is disposed at or near the outlet end of the substrate.

[0076] In a fourth configuration, the first catalytic region is disposed or supported on the second catalytic region.

[0077] The second catalytic region may be disposed or supported on (eg, directly disposed or supported on) a substrate.

[0078] The entire length (e.g., all) of the first catalytic region may be disposed or supported (e.g., directly disposed or supported) on the second catalytic region. Alternatively, only a portion or part of the length of the first catalytic region may be disposed or supported (e.g., directly disposed or supported) on the second catalytic region. Only a portion or part of the length of the first catalytic region (e.g., the remaining portion or part) may be disposed or supported (e.g., directly disposed or supported) on the substrate.

[0079] The first catalytic region may be a first catalytic layer and the second catalytic region may be a second catalytic zone, with the entire length of the first catalytic zone preferably disposed or supported on the second catalytic layer.

[0080] The second catalyst layer typically extends along the entire length (ie, substantially the entire length) of the substrate, and in particular along the entire length of the channels of the substrate monolith.

[0081] The first catalytic zone typically has a length of 10 to 90% of the length of the substrate, preferably 15 to 75% of the length of the substrate, more preferably 20 to 70% of the length of the substrate, and even more preferably 25 to 65% of the length of the substrate.

[0082] The first catalytic zone may be disposed at or near the inlet end of the substrate. The first catalytic zone may be disposed at or near the outlet end of the substrate. Preferably, the first catalytic zone is disposed at or near the inlet end of the substrate.

[0083] In an alternative fourth configuration, the first catalytic region is a first catalytic zone and the second catalytic region is a second catalytic zone or a second catalytic layer, the first catalytic zone or first catalytic layer being disposed or supported (e.g., directly disposed or supported) on the second catalytic zone.

[0084] The second catalytic zone typically has a length of 10 to 90% of the length of the substrate, preferably 15 to 75% of the length of the substrate, more preferably 20 to 70% of the length of the substrate, and even more preferably 25 to 65% of the length of the substrate.

[0085] The entire length (eg, all) of the second catalytic zone may be disposed or supported (eg, directly disposed or supported) on a substrate.

[0086] The second catalytic zone may be disposed at or near the outlet end of the substrate. The second catalytic zone may be disposed at or near the inlet end of the substrate. Preferably, the second catalytic zone is disposed at or near the outlet end of the substrate.

[0087] In addition to being disposed or supported on the second catalytic zone, the first catalytic zone or first catalytic layer may be disposed or supported (e.g., directly disposed or supported) on a substrate. Thus, a portion or portion of the length of the first catalytic zone or first catalytic layer may be disposed or supported (e.g., directly disposed or supported) on the second catalytic zone, and a portion or portion of the length of the first catalytic zone or first catalytic layer (e.g., the remaining portion or portion) may be disposed or supported (e.g., directly disposed or supported) on a substrate.

[0088] In the alternative fourth configuration, when the first catalytic region is a first catalytic zone, the first catalytic zone typically has a length of from 10 to 90% of the length of the substrate, preferably from 15 to 75% of the length of the substrate, more preferably from 20 to 70% of the length of the substrate, and even more preferably from 25 to 65%.

[0089] The first catalytic zone may be disposed at or near the inlet end of the substrate. The first catalytic zone may be disposed at or near the outlet end of the substrate. The second catalytic zone is preferably disposed at or near the inlet end of the substrate.

[0090] In an alternative fourth arrangement, when the first catalytic region is a first catalytic layer, the first catalytic layer typically extends the entire length (i.e., substantially the entire length) of the substrate, particularly the entire length of the channels of the substrate monolith. When the first catalytic region is a first catalytic layer, preferably the second catalytic zone is disposed at or near the outlet end of the substrate.

[0091] The second catalytic region may include a precious metal component, a second OSC material, and a second inorganic oxide.

[0092] The precious metal component is preferably selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof. It is particularly preferred that the precious metal component is rhodium.

[0093] The second catalyst region preferably contains 0.03 to 1.5 wt % of the precious metal component, more preferably 0.03 to 1 wt %, and most preferably 0.03 to 0.5 wt %, of the precious metal component, based on the total weight of the second catalyst region.

[0094] In embodiments in which the precious metal is rhodium, the second catalyst region preferably comprises from 0.03 to 1.5 wt. % rhodium, more preferably from 0.03 to 1 wt. % rhodium, and most preferably from 0.03 to 0.5 wt. % rhodium, based on the total weight of the second catalyst region.

[0095] The second OSC material is preferably selected from the group consisting of cerium oxide, ceria-zirconia mixed oxide, and alumina-ceria-zirconia mixed oxide. Preferably, the second OSC material is a ceria-zirconia mixed oxide. The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of at least 5:5, preferably at least 6:4, more preferably at least 7:3.

[0096] The second OSC material (eg, ceria-zirconia mixed oxide) may be 20-80 wt % based on the total weight of the second catalyst region.

[0097] The second inorganic oxide is preferably 10 to 1500 m 2 / g, pore volume in the range of 0.1 to 4 mL / g, and pore diameter of about 10 to 1000 Å. 2 High surface area inorganic oxides, such as high surface area alumina, having a surface area of ​​more than 1000 nm / g are particularly preferred. Other preferred inorganic oxides include magnesia / alumina composite oxides, which optionally further include a cerium-containing component, such as ceria. In such cases, the ceria may be present on the surface of the magnesia / alumina composite oxide, for example as a coating.

[0098] The second OSC material and the second inorganic oxide may have a weight ratio of 9:1 to 1:9, preferably 8:2 to 2:8, and more preferably 7:3 to 3:7.

[0099] The total washcoat loading of the second catalyst region is 0.2 to 4 g / in 3 , preferably 0.5 to 3 g / in 3 , more preferably 1 to 2 g / in 3 may be also possible.

[0100] The second catalytic region may further include a second precious metal component.

[0101] The second precious metal is preferably selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof. Particularly preferably, when the precious metal component is rhodium, the second precious metal component is palladium.

[0102] In some embodiments, the palladium component and the rhodium component have a weight ratio of 10:1 to 1:10. More preferably, the palladium component and the rhodium component have a weight ratio of 8:1 to 1:8. Most preferably, the palladium component and the rhodium component have a weight ratio of 5:1 to 1:5.

[0103] In certain embodiments, the second catalytic region is essentially free of precious metals other than the rhodium component.

[0104] The second catalytic region of the present invention may contain further components known to those skilled in the art. For example, the composition of the present invention may further contain at least one binder and / or at least one surfactant. When a binder is present, a dispersible alumina binder is preferred.

[0105] The above-described regions, zones, and layers can be prepared using conventional methods for making and applying washcoats on substrates and are known in the art (see, e.g., WO 99 / 47260, WO 2007 / 077462, and WO 2011 / 080525).

[0106] Another aspect of the present disclosure is a method for producing a NO x The present invention relates to a method for treating vehicle exhaust gas containing CO and HC. Catalytic converters equipped with TWCs made according to this method show improved catalytic performance compared to conventional TWCs (see, for example, Examples 15 and 16, and Tables 3 and 4).

[0107] Another aspect of the present disclosure relates to a system for treating vehicle exhaust gases that includes a catalytic article as described herein along with a conduit for transporting the exhaust gases through the system.

[0108] The system may include a second catalyst article. Preferably, the second catalyst article may include a gasoline particulate filter (GPF) or a TWC. More preferably, the second catalyst article is disposed downstream of the first catalyst article.

[0109] The TWC catalyst may be any conventional TWC catalyst.

[0110] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, the specific surface area of ​​the composition being increased by at least 15% compared to the ceria-zirconia mixed oxide after calcination in air at 1000° C. for 10 hours, the rare earth metal oxide being selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0111] Through intensive research, the inventors have found that the addition of rare earth metal oxides incorporated as a physical blend significantly improves the high temperature thermal stability of the composition compared to pristine OSC materials or compared to OSC materials further doped with rare earth metal precursors.

[0112] The composition preferably comprises 2 to 20 wt% of rare earth metal oxide based on the total weight of the composition. More preferably, the composition comprises 5 to 15 wt% of rare earth metal oxide based on the total weight of the composition. Most preferably, the composition may comprise 8 to 12 wt% of rare earth metal oxide based on the total weight of the composition.

[0113] Preferably, the rare earth metal oxide is PrO 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0114] The rare earth metal oxides have an average diameter (d 50). The average diameter of the rare earth metal oxide in the composition may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 8 μm or greater.

[0115] The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of from 9:1 to 1:9, preferably from 8:2 to 2:8, more preferably from 7:3 to 3:7.

[0116] The specific surface area of ​​the composition may increase by at least 20%, or at least 25%, after calcination in air at 1000° C. for 10 hours. In some embodiments, the specific surface area of ​​the composition may increase by at least 30%, or at least 40%, after calcination in air at 1000° C. for 10 hours. In other embodiments, the specific surface area of ​​the composition may increase by at least 45%, or at least 50%, after calcination in air at 1000° C. for 10 hours.

[0117] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, wherein the specific surface area of ​​the composition is increased by at least 5% compared to the ceria-zirconia mixed oxide after calcination in air at 1100° C. for 10 hours, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0118] The composition preferably comprises 2 to 20 wt% of rare earth metal oxide based on the total weight of the composition. More preferably, the composition comprises 5 to 15 wt% of rare earth metal oxide based on the total weight of the composition. Most preferably, the composition may comprise 8 to 12 wt% of rare earth metal oxide based on the total weight of the composition.

[0119] Preferably, the rare earth metal oxide is PrO 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0120] The rare earth metal oxides have an average diameter (d 50 ). The average diameter of the rare earth metal oxide in the composition may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 8 μm or greater.

[0121] The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of from 9:1 to 1:9, preferably from 8:2 to 2:8, more preferably from 7:3 to 3:7.

[0122] The specific surface area of ​​the composition may preferably increase by at least 10%, or at least 15%, after calcination in air at 1100° C. for 10 hours. In some embodiments, the specific surface area of ​​the composition may increase by at least 20%, or at least 25%, after calcination in air at 1100° C. for 10 hours.

[0123] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, wherein the specific surface area of ​​the composition is increased by at least 10% compared to the ceria-zirconia mixed oxide after calcination at 1000° C. for 10 hours under redox conditions, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0124] The composition preferably comprises 2 to 20 wt% of rare earth metal oxide based on the total weight of the composition. More preferably, the composition comprises 5 to 15 wt% of rare earth metal oxide based on the total weight of the composition. Most preferably, the composition may comprise 8 to 12 wt% of rare earth metal oxide based on the total weight of the composition.

[0125] Preferably, the rare earth metal oxide is PrO 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0126] The rare earth metal oxides have an average diameter (d 50 ). The average diameter of the rare earth metal oxide in the composition may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 8 μm or greater.

[0127] The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of from 9:1 to 1:9, preferably from 8:2 to 2:8, more preferably from 7:3 to 3:7.

[0128] The specific surface area of ​​the composition may be increased by at least 15%, or at least 20%, after calcination under redox conditions at 1000° C. for 10 hours. In some embodiments, the specific surface area of ​​the composition may be increased by at least 25%, or at least 30%, after calcination under redox conditions at 1000° C. for 10 hours.

[0129] Another aspect of the present disclosure is a composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, wherein the specific surface area of ​​the composition is increased by at least 10% compared to the ceria-zirconia mixed oxide after calcination at 1100° C. for 10 hours under redox conditions, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0130] The composition preferably comprises 2 to 20 wt% of rare earth metal oxide based on the total weight of the composition. More preferably, the composition comprises 5 to 15 wt% of rare earth metal oxide based on the total weight of the composition. Most preferably, the composition may comprise 8 to 12 wt% of rare earth metal oxide based on the total weight of the composition.

[0131] Preferably, the rare earth metal oxide is PrO 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0132] The rare earth metal oxides have an average diameter (d 50). The average diameter of the rare earth metal oxide in the composition may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 8 μm or greater.

[0133] The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of from 9:1 to 1:9, preferably from 8:2 to 2:8, more preferably from 7:3 to 3:7.

[0134] The specific surface area of ​​the composition may increase by at least 15%, or at least 20%, after calcination under redox conditions at 1100° C. for 10 hours. In some embodiments, the specific surface area of ​​the composition may increase by at least 25%, or at least 30%, after calcination under redox conditions at 1000° C. for 10 hours. In other embodiments, the specific surface area of ​​the composition may increase by at least 35%, or at least 40%, after calcination under redox conditions at 1000° C. for 10 hours.

[0135] Another aspect of the invention is a composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, wherein the specific surface area of ​​the composition is increased by at least 35% after calcination in air at 1000° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0136] The composition preferably comprises 2 to 20 wt% of rare earth metal oxide based on the total weight of the composition. More preferably, the composition comprises 5 to 15 wt% of rare earth metal oxide based on the total weight of the composition. Most preferably, the composition may comprise 8 to 12 wt% of rare earth metal oxide based on the total weight of the composition.

[0137] Preferably, the rare earth metal oxide is PrO 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0138] The rare earth metal oxides have an average diameter (d 50 ). The average diameter of the rare earth metal oxide in the composition may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 8 μm or greater.

[0139] The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of from 9:1 to 1:9, preferably from 8:2 to 2:8, more preferably from 7:3 to 3:7.

[0140] The PGMs are preferably selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof. Particularly preferably, the PGM is palladium.

[0141] Preferably the composition comprises from 0.03 to 10 wt% PGM, more preferably from 0.03 to 7 wt% PGM, most preferably from 0.03 to 4 wt% PGM, based on the weight of the composition.

[0142] In embodiments where the PGM is palladium, the composition preferably comprises from 0.03 to 10 wt% palladium, more preferably from 0.03 to 7 wt% palladium, and most preferably from 0.03 to 4 wt% palladium, based on the weight of the composition.

[0143] The specific surface area of ​​the composition may increase by at least 40%, or at least 50%, after calcination in air at 1000° C. for 10 hours. In some embodiments, the specific surface area of ​​the composition may increase by at least 60%, or at least 70%, after calcination in air at 1000° C. for 10 hours. In other embodiments, the specific surface area of ​​the composition may increase by at least 80%, at least 90%, at least 100%, or at least 105%, after calcination in air at 1000° C. for 10 hours.

[0144] Another aspect of the invention is a composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, wherein the specific surface area of ​​the composition is increased by at least 20% after calcination in air at 1100° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0145] The composition preferably comprises 2 to 20 wt% of rare earth metal oxide based on the total weight of the composition. More preferably, the composition comprises 5 to 15 wt% of rare earth metal oxide based on the total weight of the composition. Most preferably, the composition may comprise 8 to 12 wt% of rare earth metal oxide based on the total weight of the composition.

[0146] Preferably, the rare earth metal oxide is PrO 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0147] The rare earth metal oxides have an average diameter (d 50 ). The average diameter of the rare earth metal oxide in the composition may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 8 μm or greater.

[0148] The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of from 9:1 to 1:9, preferably from 8:2 to 2:8, more preferably from 7:3 to 3:7.

[0149] The PGMs are preferably selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof. Particularly preferably, the PGM is palladium.

[0150] Preferably the composition comprises from 0.03 to 10 wt% PGM, more preferably from 0.03 to 7 wt% PGM, most preferably from 0.03 to 4 wt% PGM, based on the weight of the composition.

[0151] In embodiments where the PGM is palladium, the composition preferably comprises from 0.03 to 10 wt% palladium, more preferably from 0.03 to 7 wt% palladium, and most preferably from 0.03 to 4 wt% palladium, based on the weight of the composition.

[0152] The specific surface area of ​​the composition may increase by at least 40%, or at least 50%, after calcination in air at 1100° C. for 10 hours. In some embodiments, the specific surface area of ​​the composition may increase by at least 60%, or at least 70%, after calcination in air at 1100° C. for 10 hours. In other embodiments, the specific surface area of ​​the composition may increase by at least 80%, at least 90%, at least 100%, or at least 110%, after calcination in air at 1100° C. for 10 hours.

[0153] Another aspect of the invention is a composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, wherein the specific surface area of ​​the composition is increased by at least 10% after calcination at 1000° C. for 10 hours under redox conditions compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, and the rare earth metal oxide is selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0154] The composition preferably comprises 2 to 20 wt% of rare earth metal oxide based on the total weight of the composition. More preferably, the composition comprises 5 to 15 wt% of rare earth metal oxide based on the total weight of the composition. Most preferably, the composition may comprise 8 to 12 wt% of rare earth metal oxide based on the total weight of the composition.

[0155] Preferably, the rare earth metal oxide is PrO 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0156] The rare earth metal oxides have an average diameter (d 50). The average diameter of the rare earth metal oxide in the composition may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 8 μm or greater.

[0157] The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of from 9:1 to 1:9, preferably from 8:2 to 2:8, more preferably from 7:3 to 3:7.

[0158] The PGMs are preferably selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof. Particularly preferably, the PGM is palladium.

[0159] Preferably the composition comprises from 0.03 to 10 wt% PGM, more preferably from 0.03 to 7 wt% PGM, most preferably from 0.03 to 4 wt% PGM, based on the weight of the composition.

[0160] In embodiments where the PGM is palladium, the composition preferably comprises from 0.03 to 10 wt% palladium, more preferably from 0.03 to 7 wt% palladium, and most preferably from 0.03 to 4 wt% palladium, based on the weight of the composition.

[0161] The specific surface area of ​​the composition may be increased by at least 20%, or at least 30%, after calcination under redox conditions at 1000° C. for 10 hours. In some embodiments, the specific surface area of ​​the composition may be increased by at least 40%, or at least 50%, after calcination under redox conditions at 1000° C. for 10 hours. In other embodiments, the specific surface area of ​​the composition may be increased by at least 60%, or at least 70%, after calcination under redox conditions at 1000° C. for 10 hours.

[0162] Another aspect of the invention is a composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, the specific surface area of ​​the composition being increased by at least 10% after calcination at 1100° C. for 10 hours under redox conditions compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, the rare earth metal oxide being selected from the group consisting of La2O3, Nd2O3, YO3, Pr6O 11 or a mixture thereof.

[0163] The composition preferably comprises 2 to 20 wt% of rare earth metal oxide based on the total weight of the composition. More preferably, the composition comprises 5 to 15 wt% of rare earth metal oxide based on the total weight of the composition. Most preferably, the composition may comprise 8 to 12 wt% of rare earth metal oxide based on the total weight of the composition.

[0164] Preferably, the rare earth metal oxide is PrO 11 , Nd2O3, Y2O3, and mixtures thereof. More preferably, the rare earth metal oxide is Nd2O3, Y2O3, or mixtures thereof. Most preferably, the rare earth metal oxide is Nd2O3.

[0165] The rare earth metal oxides have an average diameter (d 50 ). The average diameter of the rare earth metal oxide in the composition may be at least 500 nm or greater. In some embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 1 μm or greater, at least 2 μm or greater, at least 3 μm or greater, at least 4 μm or greater, at least 5 μm or greater, or at least 6 μm or greater. In other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 7 μm or greater. In yet other embodiments, the average diameter of the rare earth metal oxide in the composition may be at least 8 μm or greater.

[0166] The ceria-zirconia mixed oxide may have a molar ratio of zirconia to ceria of from 9:1 to 1:9, preferably from 8:2 to 2:8, more preferably from 7:3 to 3:7.

[0167] The PGMs are preferably selected from the group consisting of palladium, platinum, rhodium, and mixtures thereof. Particularly preferably, the PGM is palladium.

[0168] Preferably the composition comprises from 0.03 to 10 wt% PGM, more preferably from 0.03 to 7 wt% PGM, most preferably from 0.03 to 4 wt% PGM, based on the weight of the composition.

[0169] In embodiments where the PGM is palladium, the composition preferably contains from 0.03 to 10 wt% palladium, more preferably from 0.03 to 7 wt% palladium, and most preferably from 0.03 to 4 wt% palladium, based on the weight of the composition.

[0170] The specific surface area of ​​the composition may be increased by at least 20%, or at least 30%, after calcination under redox conditions at 1100° C. for 10 hours. In some embodiments, the specific surface area of ​​the composition may be increased by at least 40%, or at least 50%, after calcination under redox conditions at 1100° C. for 10 hours. In other embodiments, the specific surface area of ​​the composition may be increased by at least 60%, or at least 70%, after calcination under redox conditions at 1100° C. for 10 hours.

[0171] definition As used herein, the term "region" refers to a location on a substrate that is typically obtained by drying and / or firing a washcoat. A "region" may be disposed or carried on the substrate as, for example, a "layer" or a "zone." The location or placement on the substrate is generally controlled during the process of applying the washcoat to the substrate. A "region" typically has a distinct boundary or edge (i.e., it is possible to distinguish one region from another using conventional analytical techniques).

[0172] Typically, a "region" has a substantially uniform length. Reference in this context to a "substantially uniform length" refers to a length that does not deviate from its average value by more than 10% (e.g., the difference between the maximum length and the minimum length), preferably does not deviate by more than 5%, and more preferably does not deviate by more than 1%.

[0173] Each "region" preferably has a substantially uniform composition (i.e., there is no substantial difference in the composition of the washcoat when comparing one portion of the region to another portion of the region). Substantially uniform composition in this context refers to a material (e.g., region) that has a composition difference of 5% or less, usually 2.5% or less, and most usually 1% or less, when comparing one portion of the region to another portion of the region.

[0174] As used herein, the term "zone" refers to a region having a length that is less than the entire length of the substrate, such as ≦75% of the entire length of the substrate. A "zone" typically has a length (i.e., a substantially uniform length) that is at least 5% (e.g., ≧5%) of the entire length of the substrate.

[0175] The overall length of a substrate is the distance between its inlet end and its outlet end (eg, between the ends of the substrate).

[0176] Any reference to a "zone disposed at the inlet end of a substrate" as used herein refers to a zone disposed on or supported by a substrate, the location of which is closer to the inlet end of the substrate than to the outlet end of the substrate. Thus, the midpoint of the zone (i.e., a point at half its length) is closer to the inlet end of the substrate than to the outlet end of the substrate. Similarly, any reference to a "zone disposed at the outlet end of a substrate" as used herein refers to a zone disposed on or supported by a substrate, the location of which is closer to the inlet end of the substrate than to the outlet end of the substrate. Thus, the midpoint of the zone (i.e., a point at half its length) is closer to the outlet end of the substrate than to the inlet end of the substrate.

[0177] When the substrate is a wall-flow filter, generally any reference to a "zone disposed at the inlet end of the substrate" refers to a zone disposed on or supported by the substrate, (a) closer to the inlet end (e.g., open end) of the inlet channel of the substrate than to the closed end (e.g., blocked or plugged end) of the inlet channel; and / or (b) closer to the closed end (e.g., blocked or plugged end) of the outlet channel of the substrate than to the outlet end (e.g., open end) of the outlet channel. Thus, the midpoint (i.e., the point at half its length) of the zone is (a) closer to the inlet end of the inlet channel of the substrate than to the closed end of the inlet channel, and / or (b) closer to the closed end of the outlet channel of the substrate than to the outlet end of the outlet channel.

[0178] Similarly, if the substrate is a wall-flow filter, any reference to a "zone disposed at the outlet end of the substrate" refers to a zone disposed on or supported by the substrate, (a) closer to the outlet end (e.g., open end) of the outlet channel of the substrate than to the closed end (e.g., blocked or plugged end) of the outlet channel; and / or (b) closer to the closed end (e.g., blocked or plugged end) of the inlet channel of the substrate than to the inlet end (e.g., open end) of the inlet channel. Thus, the midpoint (i.e., the point at half its length) of the zone is (a) closer to the outlet end of the outlet channel of the substrate than to the closed end of the outlet channel, and / or (b) closer to the closed end of the inlet channel of the substrate than to the inlet end of the inlet channel.

[0179] If the washcoat is present on the wall of the wall-flow filter (ie, the zone is intra-wall), then both (a) and (b) can be satisfied.

[0180] The term "washcoat" is known in the art and refers to an adherent coating that is usually applied to a substrate during the manufacture of a catalyst.

[0181] As used herein, the acronym "PGM" refers to "platinum group metals." The term "platinum group metals" generally refers to metals selected from the group consisting of Ru, Rh, Pd, Os, Ir, and Pt, preferably metals selected from the group consisting of Ru, Rh, Pd, Ir, and Pt. Generally, the term "PGM" preferably refers to metals selected from the group consisting of Rh, Pt, and Pd.

[0182] As used herein, the term "mixed oxide" generally refers to a mixture of oxides in a single phase, as is conventionally known in the art. As used herein, the term "complex oxide" generally refers to a composition of oxides having two or more phases, as is conventionally known in the art.

[0183] As used herein, the phrase "consisting essentially of" limits the scope of a feature to include the specified materials, and any other materials or steps that do not materially affect the essential properties of the feature, such as trace impurities. The phrase "consisting essentially of" encompasses the phrase "consisting of."

[0184] As used herein with respect to a material, the term "substantially free" typically means that the material is present in a small amount, e.g., ≦5% by weight, preferably ≦2% by weight, more preferably ≦1% by weight, in relation to the contents of a region, layer, or zone. The term "substantially free" encompasses the term "free."

[0185] The term "essentially free" as used herein with respect to a material typically means that the material is present in trace amounts, e.g., ≦1 wt.%, preferably ≦0.5 wt.%, more preferably ≦0.1 wt.%, in the context of the contents of a region, layer, or zone. The term "essentially free" encompasses the term "free".

[0186] As used herein, any reference to an amount of dopant expressed as weight percent, particularly a total amount, refers to the weight of the support material or refractory metal oxide thereof.

[0187] As used herein, the term "loading" refers to g / ft2 on a metal weight basis. 3 Refers to the measurement in units of .

[0188] As used herein, the term "redox" refers to a gas mixture that alternates between a reducing and an oxidizing atmosphere.

[0189] The following examples are merely illustrative of the present invention, and those skilled in the art will recognize many variations that are within the spirit and scope of the claims. EXAMPLES

[0190] Example 1 (Comparative): Catalyst 1 is a CeZr mixed oxide with a molar ratio of Ce to Zr of 1:1.

[0191] Example 2 (Comparative Example): Catalyst 2 was prepared by flooding Nd(NO3)3 solution onto the CeZr mixed oxide of catalyst 1. The Nd loading was 10 wt% (calculated as Nd2O3) based on the total weight of catalyst 2.

[0192] Example 3: Catalyst 3 is a physical mixture of the CeZr mixed oxide of Catalyst 1 and Nd2O3. The particle size of both materials is 50 The weight ratio of the two materials was 90:10.

[0193] Example 4: Catalyst 4 is a physical mixture of the CeZr mixed oxide of Catalyst 1 and Y2O3. The particle size of both materials is 50 The weight ratio of the two materials is 90:10.

[0194] Example 5: The powder samples of Examples 1-4 were placed in a muffle furnace and treated in air at 1000° C. or 1100° C. for 10 hours. The BET surface areas of the treated samples were measured and are reported in Table 1.

[0195] Example 6: Powder samples from Examples 1-4 were placed in a tube furnace. The feed gas was alternated between lean and rich conditions every 5 minutes. The lean gas mixture contained 1% O2, 10% H2O, 20 ppm SO2, balance air. The rich gas mixture contained 0.5% CO, 10% H2O, 20 ppm SO, balance air. The samples were treated at 1000°C or 1100°C for 10 hours. The BET surface area of ​​the treated samples was measured and is also reported in Table 1.

[0196] [Table 1]

[0197] Example 7 (Comparative): Pd nitrate was loaded onto the CeZr mixed oxide of Example 1. The sample was dried and the final powder was calcined at 500° C. for 2 hours. The Pd loading was 1 wt %.

[0198] Example 8 (Comparative): Pd nitrate was loaded onto the powder sample of Example 2. The sample was dried and the final powder was calcined at 500° C. for 2 hours. The Pd loading was 1 wt %.

[0199] Example 9: Pd nitrate was added to the physical mixture of Example 3 to form a slurry. The slurry was dried and the final powder was calcined at 500° C. for 2 hours. The Pd loading was 1 wt %.

[0200] Example 10: Pd nitrate was added to the physical mixture of Example 4 to form a slurry. The slurry was dried and the final powder was calcined at 500° C. for 2 hours. The Pd loading was 1 wt %.

[0201] Example 11: Powder samples of Examples 7-10 were subjected to the same treatments as described in Examples 5 and 6. The BET surface areas of the treated samples were measured and are reported in Table 2.

[0202] [Table 2]

[0203] Experimental Results Example 12 (Comparative): Catalyst 12 is a commercial ternary (Pd-Rh) catalyst with a dual layer structure. The bottom layer consists of Pd supported on a washcoat of a first CeZr mixed oxide, La stabilized alumina, Ba promoter, and boehmite binder. The washcoat loading is about 1.6 g / in 3 The Pd loading was 1 g / ft 3 The top layer consisted of Rh supported on a washcoat of a second CeZr mixed oxide and La-stabilized alumina. The washcoat loading of the top layer was about 1.4 g / in 3 The Rh loading was 2 g / ft 3 The total catalyst loading was about 3.0 g / in 3 It was decided.

[0204] Example 13: Catalyst 13 was prepared similarly to catalyst 12, except that Nd2O3 oxide powder with D50 particle size of about 7 μm was also added to the slurry of Pd nitrate, first CeZr mixed oxide, La stabilized alumina, Ba promoter and boehmite binder. The amount of Nd2O3 added was about 10% by weight of CeZr mixed oxide.

[0205] Example 14: Catalysts 12 and 13 were coated on substrates of the same type, cpsi, and size and aged using a gasoline engine under standard lean, rich, stoichiometric cycling TWC aging conditions. Catalysts 12 and 13 were then performance tested for gasoline engine light-off temperature and evaluated over repeated FTP-75 cycles in a gasoline vehicle.

[0206] Example 15: HC, CO, and NO for Catalyst 12 and Catalyst 13 x T 50 The light-off temperatures are shown in Table 3. The data shows that the increased thermal durability of Catalyst 13 results in significantly improved light-off performance over the standard TWC example of Catalyst 12.

[0207] [Table 3]

[0208] Example 16: HC, CO, and NO averaged over repeated FTP cycles x The conversion performance of Catalyst 13 is shown in Table 4. The data shows that the improved thermal durability of Catalyst 13 results in significantly improved emissions over the standard TWC example of Catalyst 12.

[0209] [Table 4] The disclosure of this specification may include the following aspects. (Aspect 1) 1. A catalytic article for treating exhaust gas, comprising: A substrate; a catalytic region on the substrate; the catalytic region comprises a first platinum group metal (PGM) component, an oxygen storage component (OSC) material, a rare earth metal oxide, and an inorganic oxide; The rare earth metal oxide has an average diameter (d 50 ). (Aspect 2) 2. The catalytic article of embodiment 1, wherein the first PGM component is selected from the group consisting of platinum, palladium, rhodium, and mixtures thereof. (Aspect 3) 3. The catalytic article of any one of the preceding claims, wherein the first PGM component is palladium. (Aspect 4) 4. The catalyst article of claim 3, wherein the palladium loading is in the range of 0.03 to 10 wt %, based on the total weight of the catalyst region. (Aspect 5) 5. The catalytic article of any one of the preceding claims, wherein the OSC material is selected from the group consisting of cerium oxide, ceria-zirconia mixed oxide, and alumina-ceria-zirconia mixed oxide. (Aspect 6) 6. The catalytic article of embodiment 5, wherein the OSC material is a ceria-zirconia mixed oxide. (Aspect 7) 7. The catalyst article of any one of the preceding claims, wherein the inorganic oxide is selected from the group consisting of alumina, lanthanide-stabilized alumina, alkaline earth-stabilized alumina, silica, aluminosilicates, magnesia / alumina composite oxides, titania, niobia, tantalum oxide, neodymium oxide, yttrium oxide, lanthanides, and mixed or composite oxides thereof. (Aspect 8) 8. The catalytic article of claim 7, wherein the inorganic oxide is alumina, a lanthanide-stabilized alumina, or a magnesia / alumina composite oxide. (Aspect 9) 9. The catalytic article of any one of the preceding claims, wherein the catalytic region comprises 2-20 wt. % of the rare earth metal oxide, based on the OSC material. (Aspect 10) The rare earth metal oxide is La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 10. The catalyst article of any one of the preceding claims, wherein the catalyst is selected from the group consisting of: (Aspect 11) The rare earth metal oxide is Pr 6 O 11 , Nd 2 O 3 、Y 2 O 3 or a mixture thereof. (Aspect 12) The rare earth metal oxide is Nd 2 O 3 12. The catalyst article of any one of embodiments 1 to 11, wherein (Aspect 13) 13. The catalytic article of any one of the preceding claims, wherein the rare earth metal oxide is incorporated into the catalytic region as the rare earth metal oxide by physical blending. (Aspect 14) 14. The catalytic article of any one of the preceding claims, wherein the catalytic region further comprises an alkaline or alkaline earth material. (Aspect 15) 15. The catalytic article of embodiment 14, wherein the alkali metal or alkaline earth metal is barium. (Aspect 16) 16. The catalytic article of any one of the preceding claims, wherein the catalytic region further comprises a second PGM component. (Aspect 17) 17. The catalytic article of embodiment 16, wherein the second PGM component is selected from the group consisting of platinum, palladium, rhodium, and mixtures thereof. (Aspect 18) 18. The catalytic article of embodiment 17, wherein the first PGM component is palladium and the second PGM component is rhodium. (Aspect 19) 19. The catalytic article of embodiment 18, wherein the palladium component and the rhodium component have a weight ratio of from 200:1 to 1:200. (Aspect 20) 20. The catalytic article of any one of the preceding aspects, wherein the catalytic region is essentially free of PGM metals other than the palladium component. (Aspect 21) 21. The catalyst article of any one of aspects 1-20, wherein the substrate is a flow-through monolith or a wall-flow filter. (Aspect 22) 22. The catalytic article of any one of the preceding claims, further comprising a second catalytic region. (Aspect 23) An emission treatment system for treating a combustion exhaust gas stream comprising the catalytic article of any one of embodiments 1-22. (Aspect 24) A method for treating an exhaust gas from an internal combustion engine, comprising contacting the exhaust gas with the catalytic article of any one of aspects 1-22. (Aspect 25) A method of treating exhaust gas from an internal combustion engine, comprising contacting the exhaust gas with the emission treatment system of embodiment 23. (Aspect 26) A composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, the specific surface area of ​​the composition being increased by at least 15% compared to the ceria-zirconia mixed oxide after calcination in air at 1000° C. for 10 hours, the rare earth metal oxide being La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 or a mixture thereof. (Aspect 27) 27. The composition of embodiment 26, comprising 2 to 20 wt. % of the rare earth metal oxide, based on the weight of the composition. (Aspect 28) The rare earth metal oxide has an average diameter (d 50 28. The composition of claim 26 or 27, wherein (Aspect 29) 29. The composition according to any one of aspects 26 to 28, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of from 1:9 to 9:1. (Aspect 30) The rare earth metal oxide is Nd 2 O 3 Or Y 2 O 3 30. The composition according to any one of aspects 26 to 29, wherein (Aspect 31) A composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, the specific surface area of ​​the composition being increased by at least 35% after calcination in air at 1000° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, the rare earth metal oxide being selected from the group consisting of La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 or a mixture thereof. (Aspect 32) 32. The composition of embodiment 31, comprising 2 to 20 wt. % of the rare earth metal oxide, based on the weight of the composition. (Aspect 33) The rare earth metal oxide has an average diameter (d50 33. The composition of claim 31 or 32, wherein (Aspect 34) 34. The composition according to any one of aspects 31 to 33, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of from 1:9 to 9:1. (Aspect 35) Aspect 35. The composition of any one of aspects 31-34, wherein the PGM component is palladium. (Aspect 36) The composition of embodiment 35, comprising at least 0.03% by weight of palladium, based on the composition. (Aspect 37) The rare earth metal oxide is Nd 2 O 3 Or Y 2 O 3 The composition according to any one of aspects 31 to 36, wherein (Aspect 38) A composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, the specific surface area of ​​the composition being increased by at least 5% compared to the ceria-zirconia mixed oxide after calcination in air at 1100° C. for 10 hours, the rare earth metal oxide being La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 or a mixture thereof. (Aspect 39) 39. The composition of embodiment 38, comprising 2 to 20 wt. % of the rare earth metal oxide, based on the weight of the composition. (Aspect 40) The rare earth metal oxide has an average diameter (d 50 40. The composition of claim 38 or 39, wherein (Aspect 41) 41. The composition according to any one of aspects 38 to 40, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of from 1:9 to 9:1. (Aspect 42) The rare earth metal oxide is Nd 2 O 3 Or Y 2 O 3 The composition according to any one of embodiments 38 to 41, wherein (Aspect 43) A composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, the specific surface area of ​​the composition being increased by at least 20% after calcination in air at 1100° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, the rare earth metal oxide being selected from the group consisting of La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 or a mixture thereof. (Aspect 44) 44. The composition of embodiment 43, comprising 2 to 20 wt. % of the rare earth metal oxide, based on the weight of the composition. (Aspect 45) The rare earth metal oxide has an average diameter (d 50 45. The composition of claim 43 or 44, having the formula: (Aspect 46) 46. ​​The composition according to any one of aspects 43 to 45, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of from 1:9 to 9:1. (Aspect 47) 47. The composition of any one of aspects 43-46, wherein the PGM component is palladium. (Aspect 48) The composition of embodiment 47, comprising at least 0.03% by weight of palladium, based on the composition. (Aspect 49) The rare earth metal oxide is Nd 2 O 3 Or Y 2 O 3 The composition of any one of aspects 43 to 48, wherein (Aspect 50) A composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, the specific surface area of ​​which is increased by at least 10% compared to the ceria-zirconia mixed oxide after calcination at 1000° C. for 10 hours under redox conditions, the rare earth metal oxide being La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 or a mixture thereof. (Aspect 51) 51. The composition of embodiment 50, comprising 2 to 20 wt. % of the rare earth metal oxide, based on the weight of the composition. (Aspect 52) The rare earth metal oxide has an average diameter (d 50 52. The composition of any one of claims 50 to 51, wherein (Aspect 53) 53. The composition according to any one of aspects 50 to 52, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of 1:9 to 9:1. (Aspect 54) The rare earth metal oxide is Nd 2 O 3 Or Y 2 O 3 54. The composition according to any one of embodiments 50 to 53, wherein (Aspect 55) A composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, the specific surface area of ​​the composition being increased by at least 10% after calcination at 1000° C. for 10 hours under redox conditions compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, the rare earth metal oxide being selected from the group consisting of La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 or a mixture thereof. (Aspect 56) 56. The composition of embodiment 55, comprising 2 to 20 wt. % of the rare earth metal oxide, based on the weight of the composition. (Aspect 57) The rare earth metal oxide has an average diameter (d 50 57. The composition of claim 55 or 56, having the formula: (Aspect 58) 58. The composition according to any one of aspects 55 to 57, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of from 1:9 to 9:1. (Aspect 59) 59. The composition of any one of aspects 55-58, wherein the PGM component is palladium. (Aspect 60) 60. The composition of embodiment 59, comprising at least 0.03% by weight of palladium, based on the composition. (Aspect 61) The rare earth metal oxide is Nd 2 O 3 Or Y 2 O 3 The composition according to any one of embodiments 55 to 60, wherein (Aspect 62) A composition comprising a ceria-zirconia mixed oxide and a rare earth metal oxide, the specific surface area of ​​the composition being increased by at least 10% compared to the ceria-zirconia mixed oxide after calcination at 1100° C. for 10 hours under redox conditions, the rare earth metal oxide being La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 or a mixture thereof. (Aspect 63) 63. The composition of embodiment 62, comprising 2 to 20 wt. % of the rare earth metal oxide, based on the weight of the composition. (Aspect 64) The rare earth metal oxide has an average diameter (d 50 64. The composition of claim 62 or 63, wherein (Aspect 65) 65. The composition according to any one of aspects 62 to 64, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of from 1:9 to 9:1. (Aspect 66) The rare earth metal oxide is Nd 2 O 3 Or Y 2 O 3 66. The composition of any one of embodiments 62 to 65, wherein (Aspect 67) A composition comprising a ceria-zirconia mixed oxide, a rare earth metal oxide, and a platinum group metal (PGM) component, the specific surface area of ​​the composition being increased by at least 10% after calcination at 1100° C. for 10 hours under redox conditions compared to a mixture of the ceria-zirconia mixed oxide and the PGM component, the rare earth metal oxide being selected from the group consisting of La 2 O 3 , Nd 2 O 3 、Y 2 O 3 、Pr 6 O 11 or a mixture thereof. (Aspect 68) 68. The composition of embodiment 67, comprising 2 to 20 wt. % of the rare earth metal oxide, based on the weight of the composition. (Aspect 69) The rare earth metal oxide has an average diameter (d 50 69. The composition of claim 67 or 68, having the formula: (Aspect 70) 70. The composition of any one of aspects 67 to 69, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of from 1:9 to 9:1. (Aspect 71) Aspect 71. The composition of any one of aspects 67-70, wherein the PGM component is palladium. (Aspect 72) 72. The composition of embodiment 71, comprising at least 0.03% by weight of palladium, based on the composition. (Aspect 73) The rare earth metal oxide is Nd 2 O 3 Or Y 2 O 3 The composition of any one of embodiments 67-72, wherein

Claims

1. A catalytic composition comprising a physical mixture of a ceria-zirconia mixed oxide and a rare earth metal oxide, a platinum group metal (PGM) component, and an inorganic oxide, the rare earth metal oxide is in the range of 2 to 20% by weight of the ceria-zirconia mixed oxide; The content of the platinum group metal is 0.03 to 10 wt % based on the total weight of the catalyst composition; The weight ratio of the ceria-zirconia mixed oxide to the inorganic oxide is 10:1 to 1:10; The rare earth metal oxide is Nd ２ O ３ and the platinum group metal (PGM) component is palladium; The inorganic oxide is La-stabilized alumina, (i) the specific surface area of ​​the catalyst composition is increased by at least 35% when calcined in air at 1000° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component; (ii) the specific surface area of ​​the catalyst composition is increased by at least 20% when calcined in air at 1100° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component; (iii) the specific surface area of ​​the catalyst composition is increased by at least 10% when calcined under redox conditions at 1000° C. for 10 hours compared to a mixture of the ceria-zirconia mixed oxide and the PGM component; or (iv) A catalytic composition, the specific surface area of ​​which is increased by at least 10% when calcined under redox conditions at 1100° C. for 10 hours, compared to a mixture of said ceria-zirconia mixed oxide and said PGM component.

2. A catalytic composition comprising a physical mixture of a ceria-zirconia mixed oxide and a rare earth metal oxide, a platinum group metal (PGM) component, and an inorganic oxide, the rare earth metal oxide is in the range of 2 to 20% by weight of the ceria-zirconia mixed oxide; The content of the platinum group metal is 0.03 to 10 wt % based on the total weight of the catalyst composition; The weight ratio of the ceria-zirconia mixed oxide to the inorganic oxide is 10:1 to 1:10; The rare earth metal oxide is Nd ２ O ３ and the platinum group metal (PGM) component is palladium; The inorganic oxide is La-stabilized alumina, (i) the specific surface area of ​​the catalyst composition is increased by at least 15% compared to the ceria-zirconia mixed oxide when calcined in air at 1000° C. for 10 hours; (ii) the specific surface area of ​​the catalyst composition is increased by at least 5% compared to the ceria-zirconia mixed oxide when calcined in air at 1100° C. for 10 hours; (iii) the specific surface area of ​​the catalytic composition is increased by at least 10% compared to the ceria-zirconia mixed oxide when calcined under redox conditions at 1000° C. for 10 hours; or (iv) A catalytic composition, the specific surface area of ​​which is increased by at least 10% when calcined under redox conditions at 1100° C. for 10 hours, compared to the ceria-zirconia mixed oxide.

3. 3. The catalyst composition according to claim 1, comprising 2 to 20% by weight of said rare earth metal oxide, based on the weight of said catalyst composition.

4. 4. The catalyst composition according to claim 1, comprising at least 0.03% by weight of palladium, based on the catalyst composition.

5. The rare earth metal oxide has an average diameter (d ５０ The catalyst composition according to any one of claims 1 to 4, wherein

6. 6. The catalyst composition according to claim 1, wherein the ceria-zirconia mixed oxide has a molar ratio of zirconia to ceria of 1:9 to 9:1.