Metal-resin composite molded product, metal component processing method, and manufacturing method for metal-resin composite molded product

Abstract

An embodiment of the present invention is a metal-resin composite molded product in which a metal member and a thermoplastic resin are joined together. This metal-resin composite molded product has projections and recesses formed on a joined face, of one face of the metal member, where the metal member is joined to the thermoplastic resin. Substantially spherical clusters are formed on a joined surface part, and the arithmetic mean curvature of peaks of the cluster is 2500-5000 (1 / mm).

Description

[Technical field]

[0001] The present invention relates to a technique for joining a metal member and a thermoplastic resin. [Background technology]

[0002] By combining materials with different properties, such as electrically conductive materials such as metals and electrically insulating materials such as resins, parts that are lighter in weight, stronger, or more functional are used in various fields. For example, metal-resin composite molded products in which metal members and thermoplastic resins are bonded together are used in automobile interior parts such as console boxes around instrument panels, engine-related parts, interior parts, housings, interface connections, power terminals, etc. of electronic devices such as digital cameras and mobile phones.

[0003] Generally, bonding and screwing are known as methods for joining different materials such as metal and resin, but these methods are not preferable because they increase the number of steps and parts. Therefore, various methods for joining metal and resin materials have been proposed.

[0004] For example, Japanese Patent No. 4020957 describes a method of performing laser processing on the surface of a metal material in a certain scanning direction, and then performing laser processing in another scanning direction crossing the aforementioned scanning direction, and joining a different material to the surface. Japanese Patent Application Laid-Open No. 2020-116806 describes a method of improving the joining strength when joining a resin molded product to the surface by setting the undercut rate of the unevenness to a predetermined range when forming unevenness on the surface of a metal plate. Japanese Patent Application Laid-Open No. 2013-71312 describes a composite molded body of metal and resin in which a crater-shaped depression is formed in the metal by a laser beam or the like, and granular spatter is formed on the ridge-shaped protuberance where the metal surface is melted and scattered. Patent No. 6819798 describes a composite structure formed by bonding a surface-roughened metal member and a PPS member, in which when any five points on the surface of the surface-roughened metal member are measured using a confocal microscope in accordance with ISO 25178, the number average developed area ratio (Sdr) of the interface is in the range of 5 or more, and the melt viscosity of the PPS resin is in the range of 15 to 500 [Pa s]. Summary of the Invention [Problem to be solved by the invention]

[0005] However, conventional methods for joining metal materials and resin materials are unable to ensure sufficient airtightness at the joint between the metal material and the resin material, and there is a demand for improvement in this regard. SUMMARY OF THE PRESENT DISCLOSURE An object of the present invention is to improve the airtightness of a joint when a metal member and a resin member are joined together. [Means for solving the problem]

[0006] A first aspect of the present invention is a metal resin composite molded product in which a metal member and a thermoplastic resin are bonded together. In this metal resin composite molded product, the surface quality of a surface portion of one surface of the metal member that is bonded to the thermoplastic resin is such that the arithmetic mean curvature of the apex is 3701 ~5000(1 / mm).

[0007] A second aspect of the present invention is a method for processing a metal member. In this processing method, a high-energy beam is irradiated onto a surface of the metal member, so that the arithmetic mean curvature of the apex of the surface is 3701 The surface texture shall be ~5000 (1 / mm).

[0008] A third aspect of the present invention is a method for producing a metal resin composite molded product in which a metal member and a thermoplastic resin are bonded together. In this method, the surface of the metal member is irradiated with a high-energy beam, so that the arithmetic mean curvature of the apex of the surface of the metal member is 3701 The metal member is then inserted into a mold and a thermoplastic resin is injection molded to bond the thermoplastic resin to the surface of the metal member. Effect of the Invention

[0009] According to one aspect of the present invention, when a metal member and a resin member are joined, the airtightness of the joint can be improved. [Brief description of the drawings]

[0010] [Figure 1] 1A to 1C are diagrams illustrating a method for processing a metal member according to an embodiment of the present invention. [Diagram 2] 1A and 1B are images of exemplary clusters formed in laser-irradiated portions of a metal member. [Diagram 3] 1 is a diagram for explaining the state of the interface between a metal member and a resin member according to the size of Spc on the surface of the resin member in a metal-resin composite molded product according to one embodiment. FIG. [Figure 4] FIG. 2 is a diagram showing the shape of a test piece used in an airtightness test. [Diagram 5] FIG. 1 is a diagram showing a schematic configuration of a test device for an airtightness test. [Figure 6] FIG. 6 is a diagram plotting the relationship between the Spc of the surface of the resin member and the pressure detected by the testing device of FIG. 5, based on the test results of the airtightness tests of the examples and comparative examples. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] Hereinafter, a metal-resin composite molded product according to one embodiment of the present invention will be described. A metal resin composite molded product according to one embodiment is a product in which a metal member and a thermoplastic resin are bonded to each other. In this metal resin composite molded product, one surface of the metal member that is bonded to the thermoplastic resin has an uneven surface. In one embodiment, the unevenness of the bonding surface is formed by substantially spherical clusters. The term "substantially spherical" does not necessarily mean that the individual shapes constituting the clusters are spheres, but also includes ellipsoids, spheres or ellipsoids with a portion missing, and the like. The substantially spherical clusters can be formed by, for example, irradiating the surface of the metal member with a laser under predetermined irradiation conditions. As a result of intensive research, the inventors of the present application have found that by making the surface roughness of the joining surface of one side of a metal member that is joined to a thermoplastic resin desired, the airtightness of the joining surface of the metal and resin of a metal-resin composite molded product can be improved more than ever before. In the following embodiment, a case where the desired surface roughness is achieved by forming substantially spherical clusters on the joining surface of the metal member and the thermoplastic resin will be described, but this is not the only option. As long as the desired surface roughness can be achieved on the joining surface of the metal member and the thermoplastic resin, the surface treatment method for this purpose is not limited. The shape of the metal-resin composite molded product is not particularly limited, and the present invention can be applied to metal-resin composite molded products of any shape.

[0012] The metal members contained in the metal-resin composite molded product are not limited to, but may be, for example, aluminum, copper, silver, gold, iron, titanium, nickel, magnesium, zinc, and alloys thereof such as carbon steel and stainless steel. The surface of the metal material may be subjected to a surface treatment such as anodizing or painting. Aluminum, magnesium, copper, and titanium are preferred from the viewpoint of light weight and strength, and aluminum and copper are more preferred, and copper is particularly preferred, in applications requiring electrical conductivity such as terminals. Magnesium and titanium are preferred, and titanium is particularly preferred, in applications requiring thin-walled rigidity.

[0013] The resin contained in the metal-resin composite molded product is preferably a thermoplastic resin that is easy to process by injection molding. Examples of suitable thermoplastic resins include polyacetal (POM), polyamide (PA), polybutylene terephthalate (PBT), polyethylene terephthalate (PET), polycarbonate (PC), polyphenylene sulfide (PPS), liquid crystal polymer (LCP), polyether ether ketone (PEEK), styrene-based resins, acrylic-based resins, and the like.

[0014] The method for joining the metal member and the resin is not limited, but the metal member and the resin can be joined by injection molding. For example, the metal member and the resin can be joined by insert molding using a metal material as an insert member.

[0015] FIG. 1 is a schematic diagram showing a method for processing a metal member according to one embodiment. As shown in Fig. 1, when a metal member is irradiated with a laser, the metal on the surface of the metal member is melted by the high-energy beam of the laser, pushed out to the outside of the irradiated area, and then solidified into a spherical shape due to surface tension, forming unevenness on the surface of the metal member. In one embodiment, the surface of the metal member is scanned with a laser at a fine pitch, generating spherical objects that overlap to form clusters. Alternatively, the metal member is sublimated, and the scattered liquid metal particles solidify (re-adhere) and accumulate, forming spherical clusters. Fig. 2 shows an image of an exemplary cluster formed in the laser irradiated area when a metal member is irradiated with a laser. Here, when the laser output (energy per unit time) is low, the metal on the metal surface does not melt, and sublimation or scattering of liquid metal particles does not occur, so the laser output for forming spherical clusters is appropriately determined according to the metal material used for the metal member. In addition, in order to make the molten metal extruded outside the laser irradiation area into a minute sphere, the laser scanning pitch is preferably 30 μm or less, more preferably 20 μm or less, and even more preferably 10 μm or less. In addition, the laser output and irradiation speed determine the energy given to the metal surface per unit area per unit time, so in addition to the laser output, the irradiation speed is also a factor in forming spherical clusters. The laser output and irradiation speed cause a localized temperature rise on the metal surface in an extremely short period of time, which results in the formation of spherical clusters.

[0016] In order to ensure sufficient airtightness when bonded to resin, it is preferable to form spherical clusters on the entire surface of the bonding surface of the metal member with the resin. To achieve this, it is preferable to set the laser scanning pitch smaller than the laser irradiation diameter.

[0017] In this disclosure, a "high energy beam" means a beam with energy per unit time high enough to form spherical clusters on the surface of a metal member. The high energy beam is typically, but not necessarily, a laser, and may be a beam generated by an electron gun.

[0018] In one embodiment, a method for manufacturing a metal-resin composite molded product is a method for forming irregularities on the surface of a metal member by irradiating the surface of the metal member with a high-energy beam such as a laser, and then melt-bonding the metal member with the irregularities on its surface to a thermoplastic resin. In one embodiment, substantially spherical clusters are formed on the surface (bonding surface) of the metal member. By forming spherical clusters on the joint surface of the metal member with the resin, when the metal member and the thermoplastic resin are insert molded, the molten resin penetrates into the spherical clusters, increasing the adhesion between the metal and the resin during the molding stage. Therefore, the produced metal-resin composite molded product achieves higher airtightness at the joint surface of the metal member than ever before.

[0019] The area where the spherical clusters are formed on the surface of the metal member is preferably the entire surface of the joint surface of the metal member with the resin, but is not limited to this. For example, if the spherical clusters are formed on most of the joint surface, for example, 70 to 80% or more of the joint surface, a sufficiently high level of airtightness can be ensured on the joint surface of the metal member. For example, when the entire joint surface of the metal member with the resin is irradiated with the laser, if the scanning pitch of the laser is larger than the irradiation diameter of the laser, there will be areas on the joint surface that are not irradiated with the laser. Even in this case, if the areas on the joint surface that are not irradiated with the laser are relatively small, a sufficiently high airtightness is ensured on the joint surface of the metal member.

[0020] The inventors of the present application further focused on the shape of the spherical clusters formed on the surface of the metal member, and conducted research into the relationship between various surface roughness parameters of the metal member surface and the airtightness of the joint surface of the metal member with the resin. As a result, they found that the Spc (peak value of the peak) of the apex of the spherical clusters is arithmetic It was found that airtightness can be improved significantly by setting the mean curvature (Spc) within a certain range. arithmetic The mean curvature (mean curvature) is a parameter of surface quality defined in ISO 25178, and represents the average of the principal curvatures of the peaks formed on the surface being evaluated.

[0021] The reason why the airtightness of the joint surface of the metal member with the resin is improved by setting the Spc of the apex of the spherical cluster within a predetermined range is presumed to be as follows, with reference to FIG. FIG. 3 is a schematic diagram showing the joint surface between the metal member and the resin when the Spc of the apex of the spherical cluster formed on the surface of the metal member is large ("Spc large"), medium ("Spc medium"), and small ("Spc small"). When Spc is large, the apex of the spherical cluster becomes sharp, and when the thermoplastic resin cools, a sink mark (shrinkage) occurs. However, since the apex of the cluster is sharp, a gap is likely to occur between the resin and the metal at the joint surface of the apex, which is disadvantageous in terms of airtightness. On the other hand, when Spc is small, the spherical cluster has a surface property that changes gradually as a whole, so the surface area of ​​the joint is small and the adhesion between the metal and the resin is not high in the molding stage. Therefore, when Spc is medium, it is presumed that the molten resin will penetrate sufficiently into the spherical cluster part on the surface of the metal member, and the adhesion between the metal and the resin will be extremely high in the molding stage.

[0022] Specifically, the Spc of the apex of the spherical cluster on the surface of the metal component is preferably in the range of 2500 to 5000 (1 / mm), more preferably in the range of 3000 to 5000 (1 / mm), and most preferably in the range of 3500 to 5000 (1 / mm). In order to adjust this Spc to be within a desired range, the energy given by the laser irradiation to the joint surface of the metal member with the resin is controlled. When a pulsed laser is used as the laser, the energy E per pulse is expressed as P / f when the average output is P and the frequency is f, so the energy given to the joint surface of the metal member with the resin can be controlled by adjusting the average output P (so-called laser output) and / or the frequency f. For example, if the frequency of the pulsed laser is increased, the amount of energy per pulse given to the surface of the metal member becomes smaller, so Spc tends to decrease. Conversely, if the frequency of the pulsed laser is decreased, the amount of energy per pulse given to the surface of the metal member becomes larger, so Spc tends to increase, but when the amount of energy becomes sufficiently large, Spc becomes saturated. In addition, even under the same laser irradiation conditions, Spc may change depending on the environmental conditions (for example, it is considered that Spc may decrease when the environmental temperature is low), so it is confirmed whether Spc is within the desired range after laser irradiation. EXAMPLES

[0023] Examples of metal-resin composite molded products will be described below. In the examples, a metal resin composite molded article 10 (hereinafter referred to as "test piece 10") having a shape shown in FIG. 4 was prepared as a test piece. As shown in Fig. 4, the test piece 10 is composed of a circular metal member 11 having an inner hole in the center, and a resin molded product 12 placed in the inner hole of the metal member 11. The metal member 11 has an outer diameter of φ50 mm, an inner hole diameter of φ20 mm, and a thickness of 1 mm. The resin molded product 12 has an outer diameter of φ30 mm and a thickness of 3 mm.

[0024] The following materials were used for the metal member 11 and the resin molded part 12. Metallic materials: Aluminum A5052, Copper C1100 ·Thermoplastic resin: Polyphenylene sulfide (PPS) (Durafide (registered trademark) 1140A6 (manufactured by Polyplastics Co., Ltd.)) Polybutylene terephthalate (PBT) (DURANEX (registered trademark) 930MA (manufactured by Polyplastics Co., Ltd.)) Polyphenylene sulfide (PPS) (Durafide (registered trademark) 6150T73 (manufactured by Polyplastics Co., Ltd.))

[0025] Before bonding to the resin molded product 12, a laser processing was performed concentrically on the surface of the metal member 11 within a range of φ20 mm to φ26 mm (the bonding surface with the resin molded product 12) using a laser processing machine (ML-7350DL manufactured by Amada Weld Tech). Table 1 below shows the laser irradiation conditions for Examples 1 to 6. Tables 2 and 3 below show the laser irradiation conditions for Comparative Examples 1 to 11. Although not shown in the table, the laser irradiation pitch was 10 μm and the irradiation diameter was 58 μm for all Examples and Comparative Examples. The pitch is the distance between concentric circles scanned by the laser. Because the pitch is smaller than the irradiation diameter, the entire joining surface is irradiated with the laser.

[0026] In all the examples and comparative examples, the surface of the metal member 11 was observed with a SEM (scanning electron microscope) and it was confirmed that spherical clusters were formed over the entire surface. Furthermore, the Spc of the apex of the spherical cluster formed on the surface of the metal member 11 was measured using a laser microscope VK-X3000 manufactured by Keyence Corporation (see Tables 1 to 3). It can be seen that in Comparative Examples 1, 7, and 8, the laser output is relatively low and the frequency is high, so that the amount of energy per pulse applied to the surface of the metal member 11 is small, and the Spc is low.

[0027] After performing laser processing on the metal member 11, the metal member 11 was joined by insert molding using the metal member 11 as an insert member under the following conditions, thereby forming the test piece 10 shown in FIG. Injection molding machine: Sodick TR100EH Cylinder temperature: 320℃ (for 1140A6, 6150T73), 260℃ (for 930MA) Mold temperature: 150℃ ·Injection speed: 15mm / s - Holding pressure: 50MPa

[0028] Next, an airtightness test was carried out on the test pieces 10 molded as the example and the comparative example. The configuration of a test device for the airtightness test (helium leak test, vacuum method) is shown in FIG. As shown in FIG. 5, the jig 2 and the test piece 10 are placed in the chamber 3 which is sealed from the outside. The jig 2 is in the shape of a rectangular parallelepiped with a bottom, and by placing the test piece 10 on the top, the inside of the jig 2 is sealed from the rest of the chamber 3. With the valve 6 in the open state, the inside of the jig 2 is evacuated by the vacuum pump 5, and then with the valve 6 in the closed state, the chamber 3 is filled with helium gas by the helium cylinder 4. Helium gas leaking from the joint of the test piece 10 in the chamber 3 is detected by the helium detector 7. The control device 8 displays the helium gas detection result. As the helium detector 7, a helium leak tester G-FINE manufactured by Cosmo Instruments Co., Ltd. and an L300i manufactured by Inficon Co., Ltd. were used.

[0029] The helium pressure in the chamber 3 was set to 400 kPa, and the vacuum pressure in the jig 2 was set to 100 kPa. If the joint between the metal member 11 and the resin molded product 12 of the test piece 10 is not airtight, the helium gas in the chamber 3 flows into the jig 2 and is detected by the helium detector 7. In this test, the helium pressure detected by the helium detector 7 (detection pressure) was 1.0×10 -7 (=1.0E-7) Pa m 3 If the value is more than 1.0 x 10 / s, the airtightness is judged to be NG. -7 (=1.0E-7) Pa m 3 If the value was less than / s, the airtightness was determined to be OK. Regarding the detection pressure of the air tightness test on the test pieces, Table 1 shows the results of Examples 1 to 6, and Tables 2 and 3 show the results of Comparative Examples 1 to 11.

[0030] [Table 1] [Table 2] [Table 3]

[0031] FIG. 6 is a plot of the relationship between the detection pressure in the airtightness test and the Spc of the apex of the spherical cluster formed on the surface of the metal member 11 for Examples 1 to 6 and Comparative Examples 1 to 11. From Fig. 6, it was confirmed that when the Spc of the apex of the cluster is 2500 to 5000 (1 / mm), the airtightness of the joint between the metal member and the resin is high (i.e., the detection pressure is low). When the Spc of the apex of the cluster is 3000 to 5000 (1 / mm), the detection pressure of the airtight test is even lower, which is preferable. When the Spc of the apex of the cluster is 3500 to 5000 (1 / mm), the detection pressure of the airtight test is even lower, which is even more preferable.

[0032] Although the embodiment of the present invention has been described in detail above, the present invention is not limited to the above embodiment. Furthermore, the above embodiment can be improved or modified in various ways without departing from the spirit of the present invention.

[0033] The present invention is related to patent application No. 2022-178512 filed with the Japan Patent Office on November 8, 2022, the entire contents of which are incorporated by reference into the specification of this application.

Claims

1. A metal resin composite molded product in which a metal member and a thermoplastic resin are bonded, The arithmetic mean curvature of the apex of a surface portion of one side of the metal member that is joined to the thermoplastic resin is 3701 to 5000 (1 / mm); Metal-resin composite molded product.

2. The surface portion has substantially spherical clusters formed thereon, and the arithmetic mean curvature of the apex of the cluster is 3701 to 5000 (1 / mm).

2. A metal-resin composite molded product according to claim 1.

3. A method for processing a metal member, comprising the steps of: By irradiating a surface of a metal member with a high-energy beam, the arithmetic mean curvature of the vertex of the surface is set to 3701 to 5000 (1 / mm); A method for processing metal components.

4. A method for processing a metal member, comprising the steps of: Irradiating a surface of a metal member with a high-energy beam to form substantially spherical clusters on the surface, the clusters having an arithmetic mean curvature of apexes of 3701 to 5000 (1 / mm); A method for processing metal components.

5. A method for producing a metal resin composite molded product in which a metal member and a thermoplastic resin are bonded, comprising the steps of: A metal member having an arithmetic mean curvature of a vertex of the surface of the metal member set to 3701 to 5000 (1 / mm) by irradiating the surface of the metal member with a high-energy beam is inserted into a mold, and a thermoplastic resin is injection molded to bond the thermoplastic resin to the surface of the metal member. A manufacturing method for metal-resin composite molded products.

6. A method for producing a metal resin composite molded product in which a metal member and a thermoplastic resin are bonded, comprising the steps of: a high-energy beam is irradiated onto a surface of a metal member to form substantially spherical clusters on the surface, the clusters having an arithmetic mean curvature of apexes of 3701 to 5000 (1 / mm); the metal member on whose surface the substantially spherical clusters have been formed is inserted into a mold; and a thermoplastic resin is injection-molded to bond the thermoplastic resin to the surface of the metal member; A manufacturing method for metal-resin composite molded products.

Images