Abstract

The composite web (1) comprises a mass (2) of meltblown fibers (3) containing an elastomer and a hydrophilic additive melted and blown together, and a particulate material (4) dispersed among the fibers and at least partially adhered thereto.

Description

[Technical field]

[0001] FIELD OF THEINVENTION This invention relates to composite webs, and more particularly to composite webs containing melt-blown fibers and particulate materials, such as absorbent or superabsorbent materials. [Background technology]

[0002] Known in the prior art are composite webs that include molten, blown fibers, known as "meltblown" fibers, and spunbonds in which particulate material is entrapped, for example in the form of discrete particles.

[0003] The particulate material may for example be an absorbent or superabsorbent polymer material, examples of composite webs containing meltblown fibres and discrete particles being described and illustrated in documents US6494974 and EP0156160.

[0004] By absorbent (or superabsorbent) material is meant a material that can retain any liquid or filter a fluid (liquid or gas) that contains foreign matter (solid, liquid, or gas).

[0005] With respect to composite webs comprising meltblown fibers having entrapped therein discrete particles of liquid-absorbent material, a need is felt to improve the liquid absorption capacity when the same amount of discrete particles of absorbent or superabsorbent material is present, i.e., to reduce the amount of discrete particles of superabsorbent material used without reducing the amount of liquid absorbed. Summary of the Invention

[0006] In this context, the object is to propose a composite web comprising meltblown fibres in which are entrapped discrete particles, in particular discrete particles of absorbent or superabsorbent material, which is able to meet the abovementioned needs.

[0007] More specifically, the present invention aims to provide a composite web comprising meltblown fibers and discrete particles, such as discrete particles of absorbent or superabsorbent materials, in which the amount of discrete particles dispersed and entrapped within the fibers is optimized according to the expected performance of the composite web.

[0008] This object is achieved by a composite web comprising the technical features set forth in one or more of the appended claims. The dependent claims correspond to the possible various embodiments of the invention.

[0009] According to one aspect, the present invention relates to a composite web comprising a mass of meltblown fibers comprising a molten and blown first thermoplastic material and a particulate material dispersed among and at least partially adhered to the fibers.

[0010] According to one aspect of the present disclosure, the first thermoplastic material is an elastomer or an elastomeric material.

[0011] In practice, the composite web is a meltblown web formed from at least one thermoplastic elastomeric material.

[0012] In one embodiment, the composite web may include a hydrophilic additive melt-sprayed along with the first thermoplastic material to render the composite web hydrophilic.

[0013] Additives for rendering the composite web hydrophilic can be advantageously used, especially where the particulate material includes absorbent or superabsorbent materials.

[0014] In such applications, the hydrophilicity of the fibers allows liquid that must be absorbed into the web to effectively reach the absorbent or superabsorbent materials, such as superabsorbent polymers (SAPs), dispersed among the fibers.

[0015] The elastomer makes the fiber suitably elastic, i.e., flexible enough to accommodate the SAP as it absorbs and expands, while at the same time retaining it within the fiber matrix to prevent it from being lost.

[0016] Thus, for example, when a composite web according to the present disclosure is used to manufacture an absorbent pad for an absorbent product for sanitary applications (diapers), inter alia, the integrity of the pad is advantageously improved.

[0017] Furthermore, due to their elastomeric properties, the fibers are able to deform more and therefore expand freely, absorbing more liquid than if the fibers were restrained, and therefore less SAP is needed to absorb the same amount of liquid.

[0018] According to one aspect of the present disclosure, a properly reduced diameter of the fiber contributes to providing sufficient elasticity to follow the expansion of the SAP.

[0019] According to one aspect of the present disclosure, a proper density of fibers, i.e., the number of fibers present in the composite web, allows the web to better accommodate the expansion of the SAP. In fact, the SAP particles can expand more freely the fewer fibers dispersed around them.

[0020] According to one aspect of the present disclosure, the composite web includes a second thermoplastic material within the fibers.

[0021] According to one aspect of the present disclosure, a composite web includes a secondary web bonded to a mass of meltblown fibers having particulate material dispersed therein.

[0022] Advantageously, the elastomer present in the fibers allows the bonding of the auxiliary web and the mass of meltblown fibers without the use of glues or adhesives. In fact, the elastomer provides tack and allows the fibers to adhere to the auxiliary web, especially during extrusion and blowing.

[0023] In the case of superabsorbent materials dispersed within the fibers, generally speaking, the auxiliary web helps to hold together the mass of fibers incorporating the superabsorbent material and the pad.

[0024] According to one aspect, the present disclosure relates to an absorbent article, such as a diaper, having an absorbent pad comprising a piece of a composite web made according to the present disclosure. [Brief description of the drawings]

[0025] Further features and advantages of the present invention will become more apparent in the following illustrative, and therefore non-limiting, description of preferred but non-exclusive embodiments of composite webs comprising meltblown fibers and particulate material.

[0026] The present specification will now be described with reference to the accompanying drawings, which are provided for illustrative purposes only, without limiting the scope of the invention. [Figure 1] FIG. 1 shows a schematic side view of a composite web including meltblown fibers and particulate material dispersed therein. [Diagram 2] 1 shows a microscope image of a composite web including meltblown fibers and particulate material dispersed therein in a first operating state. [Diagram 3] 2 illustrates the composite web of FIG. 1 in a second operating condition. [Figure 4] 1 shows a schematic plan view of an absorbent article comprising a composite web including meltblown fibers and particulate material dispersed therein. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0027] Referring to the accompanying drawings, the numeral 1 designates a composite web according to the present disclosure.

[0028] The web 1 is of the type known as meltblown or spunbond, that is to say obtained by extrusion-spraying a thermoplastic material.

[0029] The web 1 comprises a mass or bulk or matrix 2 of meltblown fibers 3 .

[0030] In a preferred embodiment, the diameter of the fibers 3 is between 0.1 microns and 30 microns, preferably between 0.5 microns and 10 microns.

[0031] In a preferred embodiment, the gram weight of the fiber 3 is between 0.1 gsm and 300 gsm, preferably between 1 gsm and 20 gsm.

[0032] The fibers 3 include at least one meltblown thermoplastic material, ie, the thermoplastic material that is fed into an extruder to make the web 1 .

[0033] In a preferred embodiment, the thermoplastic material is preferably a polymer, for example polypropylene (PP) or polyethylene (PE), and is present in the fibres 3 in a proportion preferably between 70% and 95% by weight.

[0034] The thermoplastic material has a melt flow rate between 1 and 2000, preferably 1200.

[0035] According to the invention, the fibres 3 comprise an elastomer, ie a substance capable of reducing the elasticity of the fibres 3 in the sense of reducing their resistance to deformation under mechanical stress.

[0036] The elastomer may be melted and blown individually (thus constituting all of the thermoplastic material), may be melted and blown together with another thermoplastic material, or may be melted and blown together with two or more thermoplastic materials (i.e., the elastomer is fed into an extruder to create the meltblown web 1).

[0037] Generally speaking, the thermoplastic material is a thermoplastic material suitable for being melted and blown. Preferably, the thermoplastic material or materials may be selected from the following group of materials, by way of non-exhaustive example: polypropylene and derivatives, polyethylene and derivatives, polylactic acid and derivatives, polyhydroxyalkanoates and derivatives, cellulose and derivatives, cellulose acetate and derivatives, starch and derivatives, polyesters (e.g. polyethylene terephthalate), polyurethanes, polyamides, polycarbonates, thermoplastic biopolymers in general, polyoxymethylene and derivatives, polysulfones and derivatives, methacrylates and derivatives.

[0038] The elastomer, when extruded together with at least one other thermoplastic material, i.e. when it constitutes a thermoplastic material in itself, serves in particular to reduce the elasticity of the fibres 3, i.e. to make the fibres 3 softer and easier to mould.

[0039] In a preferred embodiment, the fibre 3 may be made entirely from an elastic thermoplastic material, for example Vistamaxx®, so as to be particularly elastic, as mentioned above.

[0040] In other words, in a preferred embodiment, the elastomer itself constitutes the first thermoplastic material, ie the mass 2 may be made substantially entirely of the elastomer.

[0041] In one embodiment, the elastomer is present in the fibers in a proportion between 5% and 30% by weight and is combined with at least one other thermoplastic material.

[0042] The web 1 comprises particulate material 4 dispersed among and at least partially attached to the fibres 3 .

[0043] The particulate material is present within the composite web 1 at a gram weight of between 8 and 990 gsm, preferably between 50 and 700 gsm.

[0044] In a preferred embodiment, the granular material 4 comprises an absorbent or superabsorbent material essentially intended to absorb liquids, for example a SAP such as Saviva B3.

[0045] Advantageously, the elastomer present in the fibers 3 or constituting the fibers themselves makes the fibers particularly tacky, especially during meltblowing.

[0046] In this way, the particulate material 4 adheres better to and is held by the fibers.

[0047] The gram weight and diameter of the fibers 3 at least partially determine their dispersion which contributes to the retention of particulate material.

[0048] In a preferred embodiment, the fibers 3 include a hydrophilic additive that renders the fibers hydrophilic.

[0049] The hydrophilic additive may be added in the extruder or may be sprayed onto the mass 2 after the meltblowing process, for example.

[0050] If the hydrophilic additive is added in an extruder, the hydrophilic additive may be aqueous or non-aqueous.

[0051] Preferably, the hydrophilic additive is extruded with the thermoplastic material and the elastomer.

[0052] The hydrophilic additive is present in the fibres 3 in a proportion between 1% and 10% by weight, preferably between 3% and 6% by weight.

[0053] The composite web 1 as a whole preferably has a gram weight of between 50 and 1500 gsm.

[0054] In an exemplary embodiment, the fibers 3 include a polymeric material, a hydrophilic additive, and an elastomer, and the particulate material includes an absorbent or superabsorbent material. Web 1 defines a composite meltblown absorbent web, for example, as shown in Figures 2 and 3, which show a dry state and a wet state after absorbing liquid, respectively.

[0055] The composite web 1 thus produced can be used, for example, to produce absorbent sanitary articles and also absorbent pads for food-related or medical applications.

[0056] Advantageously, as mentioned above, the fibers 3 may alternatively be produced by meltblowing only an elastomer.

[0057] The elastomers present in the fibers 3, and therefore their elasticity, gram weight and diameter, contribute to holding the absorbent material together as it swells, thus optimizing what is called wet integrity, which can reach values ​​well above 100, for example, compared to values ​​between 10 and 80 for conventional cellulose pads.

[0058] The reduction in elasticity and / or fiber diameter and / or fiber density contributes to maximizing the proportion of active SAP and reducing the constraints on it, allowing it to expand freely without losses during absorption of liquid.

[0059] As explained below, the reduced constraints on SAP have been confirmed by applicant by measuring what is known as a higher "free absorption" and "centrifuge retention capacity" (CRC) compared to prior art solutions, and thus demonstrating improved SAP usage in percentage terms.

[0060] Thus, advantageously, the absorbent capacity of the composite web 1 is improved over the same amount of absorbent material in conventional absorbent webs.

[0061] SAP losses are also very limited, ie, dry integrity is significantly improved to less than 1%.

[0062] In fact, compared to prior art solutions, SAP loss (dry integrity), SAP usage capacity and wet integrity are all very limited in a single product.

[0063] Additives used to make the web hydrophilic may be sprayed onto the meltblown web instead of being added during extrusion. If the particulate material is a superabsorbent material such as SAP, the additive must be non-aqueous so as not to interact with the superabsorbent material itself.

[0064] As shown by the dashed lines in FIG. 1, in a preferred embodiment, the composite web 1 may include at least one auxiliary web 5 and / or 6 bonded to the mass of meltblown fibers 2 having the particulate material 4 dispersed therein.

[0065] In embodiments in which the composite web 1 includes both auxiliary webs 5 and 6, these may form what is known as a "core cover," particularly when the composite web 1 is of an absorbent type, preferably of an absorbent type as described above.

[0066] In such cases, webs 5 and 6 contribute to holding the particulate material 4 and to the strength of the composite web 1 .

[0067] Preferably, auxiliary webs 5 and / or 6 comprise a nonwoven web 7, for example meltblown or spunbond, the nonwoven web 7 preferably having a gram weight between 1 gsm and 20 gsm.

[0068] In one embodiment, the composite web 1 includes at least one auxiliary web 5 or 6, including, for example, an absorbent distribution layer (ADL) or web 8 of high loft type nonwoven.

[0069] Preferably, the nonwoven web 8 has a gram weight between 10 gsm and 300 gsm and can retain SAP to enhance the strength and flexibility of the composite web 1 and to serve to distribute absorbed liquids.

[0070] Advantageously, in one embodiment, the auxiliary webs 5 and / or 6, i.e. the nonwoven webs 7, 8, and the mass 2 of fibres 3 are joined without adhesive.

[0071] More specifically, the elastomer present in the fibers 3 makes it possible to bond the mass 2 to the auxiliary webs 5 and / or 6 .

[0072] Preferably, in such a case, when the fibers 3 are melted and blown, the fibers 3 are deposited directly onto an auxiliary web 5 or 6 to define a support layer that functions, for example, as a surface layer or an absorbent layer in an absorbent pad including the composite web 1.

[0073] In one embodiment, the auxiliary webs 5 and / or 6 comprise cellulose.

[0074] Listed below are three examples of composite webs according to the present disclosure, preferably intended for making absorbent pads or cores.

[0075] For each example, a summary of the features applicants have detected and associated performance characteristics is provided.

[0076] What is known as the "SAP usage" was estimated as the ratio, expressed as a percentage, between the centrifuge retention capacity (CRC) of the composite web and the CRC of pure SAP, and / or the ratio, expressed as a percentage, between the free absorption obtained by the composite web and the free absorption of pure SAP.

[0077] Centrifuge retention capacity was measured according to Edana standard method NWSP 2410R2 and free absorption was measured according to Edana standard method NWSP 2400R2. The table below shows the amount of SAP used calculated as CRC of web / CRC of pure SAP.

[0078] Tensile strength was measured by Edana standard method 110.4.R0.

[0079] Wet integrity was tested according to in-house methods using Philip Hardy equipment well known in the industry, as there is no standard laboratory method for testing the integrity of absorbent cores.

[0080] In this case, each specimen was weighed and 50 ml of sodium chloride (NaCl) was poured onto it and then allowed to sit for 15 minutes. The specimens were then hung in a testing apparatus and the time of failure of the absorbent structure and the onset of failure were recorded.

[0081] Drying integrity was also tested using Applicant's in-house method to measure SAP loss in the dry product.

[0082] Test specimens or samples were cut from the composite web 1 and weighed.

[0083] The specimen was shaken three times and the amount of SAP that fell off was measured. The SAP loss was calculated as the ratio of the SAP that fell off to the total weight of the specimen.

[0084] Advantageously, composite webs according to the present disclosure provided excellent results with respect to both wet integrity and dry integrity.

[0085] TIFF0007667179000001.tif89123

[0086] TIFF0007667179000002.tif88124

[0087] TIFF0007667179000003.tif92123

[0088] Referring to FIG. 4, numeral 100 indicates an absorbent article (eg, a diaper) according to the present disclosure, which will be described only to the extent necessary for an understanding of the present invention.

[0089] The absorbent article 100 includes an absorbent portion or pad 101 and a frame 102 on which the absorbent pad 101 is disposed.

[0090] The pad 101 includes a piece 103 of the composite web 1 described above.

[0091] More specifically, strip 103 includes at least one elastomer within a mass of fibers and superabsorbent material in the form of a particulate material dispersed within the fibers. [Prior art documents] [Patent documents]

[0092] [Patent Document 1] US6494974 [Patent Document 2] EP0156160

Claims

1. A composite web comprising: a mass (2) of meltblown fibers (3) comprising at least a melt-blown first thermoplastic material and a melt-blown hydrophilic additive melt-blown with said first thermoplastic material; and a particulate material (4) dispersed among and at least partially attached to said fibers, A composite web, wherein said first thermoplastic material is an elastomer and said particulate material (4) comprises an absorbent or superabsorbent material.

2. 10. The composite web of claim 1, wherein the elastomer is present in the fibers in an amount between 5% and 30% by weight.

3. 3. The composite web of claim 1 or 2, wherein the hydrophilic additive is present in a proportion between 1% and 10% by weight.

4. 4. The composite web of claim 1, 2 or 3, wherein the particulate material is present at a gram weight of between 8 and 990 gsm.

5. 5. The composite web according to any one of claims 1 to 4, wherein the mass (2) of meltblown fibers (3) comprises a second thermoplastic material present in a proportion between 70% and 95% by weight.

6. The composite web of claim 5 , wherein the second thermoplastic material has a melt flow rate of between 1 and 2000.

7. The composite web of claim 1 , wherein the first thermoplastic material has a melt flow rate of between 1 and 2000.

8. 8. The composite web of any one of claims 1 to 7, wherein the fibers have a diameter between 0.1 microns and 30 microns.

9. 9. The composite web of claim 1, wherein the gram weight of the fibers is between 0.1 gsm and 300 gsm.

10. 10. The composite web of claim 1, wherein the gram weight of the composite web is between 50 and 1500 gsm.

11. 11. A composite web according to any one of claims 1 to 10, wherein the particulate material (4) comprises at least one auxiliary web (5, 6) bonded to the mass (2) of dispersed meltblown fibres (3).

12. 12. The composite web of claim 11, wherein the auxiliary webs (5, 6) comprise a first web of nonwoven fabric (7), the gram weight of the first web of nonwoven fabric (7) being between 1 gsm and 20 gsm.

13. 13. A composite web according to claim 11 or 12, wherein the auxiliary webs (5, 6) comprise a second web (8) of nonwoven fabric, the gram weight of said second web (8) of nonwoven fabric being between 10 gsm and 300 gsm.

14. 14. The composite web according to any one of claims 11 to 13, wherein the auxiliary webs (5, 6) and the mass (2) of meltblown fibers (3) are bonded together without any adhesive material.

15. An absorbent article comprising a piece (103) of a composite web according to any one of claims 1 to 14.