Novel glass material

Abstract

The invention discloses a novel glass material. According to a technical scheme, the novel glass material is prepared from the following components in parts by weight: 70-80 parts of quartz sand, 5-8parts of sodium carbonate, 40-50 parts of carbon black, 6-8 parts of calcite, 7-10 parts of ceramic micro powder, 7-10 parts of iron oxide, 5-9 parts of limestone, 1-3 parts of a boron compound, 2-5 parts of barium carbonate and 3-6 parts of a dispersing agent. The prepared glass directly has the sun-shading, light-shading and ultraviolet-proof effects; the traditional method of coating a glass surface with a shading layer is directly replaced; the prepared glass directly has the effect of shading layer coating; meanwhile, the durability, the aging degree and the like can be greatly improved when the glass is used outdoors, so that the glass cannot become yellow and fall off, the shading effect of the glass is improved, and meanwhile, the strength of the prepared glass is higher than thatof common glass through mutual matching and debugging of the carbon black, the ceramic micro powder and the iron oxide powder.

Description

technical field

[0001] The invention relates to the technical field of glass manufacturing, in particular to a novel glass material. Background technique

[0002] Glass is an amorphous inorganic non-metallic material. It is generally made of a variety of inorganic minerals as the main raw material and a small amount of auxiliary raw materials. Its main components are silicon dioxide and other oxides. It is widely used in buildings to insulate It is a mixture of wind and light, and there are also colored glass mixed with certain metal oxides or salts to show color, and tempered glass made by physical or chemical methods. Sometimes some transparent plastics are also called glass. For plexiglass.

[0003] As an industrial material, glass is widely used in construction and other facilities. Existing glass is mostly divided into different types of glass, tempered glass, curved glass, optical glass, etc., and some glass in buildings is mostly transparent, and it is exposed to dir...

Examples

Embodiment

[0019] A new type of new glass material, specifically according to the following steps:

[0020] Step 1: Prepare the carbon black solution, add an appropriate amount of organic solvent dropwise to the reaction kettle, then slowly put 40 parts of carbon black into the reaction kettle, and raise the temperature in the reaction kettle to 65 degrees Celsius, and the carbon black will be within ten minutes After putting in, start the stirring device and stir the carbon black solution for 5 minutes, then add 4 parts of dispersant in the reactor, the addition of the dispersant will drop in 7 minutes, then start the stirring device again, stir the carbon black solution, and Heat the mixed solution to 60 degrees Celsius, wait for 15 minutes, observe the liquid level of the mixed solution, if the mixed solution contains a lot of floc or sediment, slowly drop 2 parts of dispersant into the reaction kettle, and then start stirring again Stir the equipment for 5 minutes, wait for 10 minute...

technical field

[0001] The invention relates to the technical field of glass manufacturing, in particular to a novel glass material. Background technique

[0002] Glass is an amorphous inorganic non-metallic material. It is generally made of a variety of inorganic minerals as the main raw material and a small amount of auxiliary raw materials. Its main components are silicon dioxide and other oxides. It is widely used in buildings to insulate It is a mixture of wind and light, and there are also colored glass mixed with certain metal oxides or salts to show color, and tempered glass made by physical or chemical methods. Sometimes some transparent plastics are also called glass. For plexiglass.

[0003] As an industrial material, glass is widely used in construction and other facilities. Existing glass is mostly divided into different types of glass, tempered glass, curved glass, optical glass, etc., and some glass in buildings is mostly transparent, and it is exposed to dir...

Examples

Embodiment

[0019] A new type of new glass material, specifically according to the following steps:

[0020] Step 1: Prepare the carbon black solution, add an appropriate amount of organic solvent dropwise to the reaction kettle, then slowly put 40 parts of carbon black into the reaction kettle, and raise the temperature in the reaction kettle to 65 degrees Celsius, and the carbon black will be within ten minutes After putting in, start the stirring device and stir the carbon black solution for 5 minutes, then add 4 parts of dispersant in the reactor, the addition of the dispersant will drop in 7 minutes, then start the stirring device again, stir the carbon black solution, and Heat the mixed solution to 60 degrees Celsius, wait for 15 minutes, observe the liquid level of the mixed solution, if the mixed solution contains a lot of floc or sediment, slowly drop 2 parts of dispersant into the reaction kettle, and then start stirring again Stir the equipment for 5 minutes, wait for 10 minute...