Immunosuppressive materials and related methods

Abstract

Zwitterionic phosphatidylserine (ZPS) monomers, ZPS polymers, and ZPS copolymers, methods for making the ZPS monomers, ZPS polymers, and ZPS copolymers, compositions and materials comprising the ZPS polymers and ZPS copolymers, and methods of using the ZPS monomers, ZPS polymers, and ZPS copolymers.

Description

[0001] This application is a divisional application of the PCT international application PCT / US2019 / 023921 filed on March 25, 2019, which entered the Chinese national phase on November 20, 2020, with application number 201980033942.0 and invention name “Immunosuppressive Materials and Related Methods”.

[0002] CROSS-REFERENCE TO RELATED APPLICATIONS

[0003] This application claims the benefit of U.S. Application No. 62 / 647,534, filed on March 23, 2018, the entire contents of which are expressly incorporated herein by reference.

[0004] Government Licensing Statement

[0005] This invention was made with government support under Grant No. HDTRA1-13-1-0044 awarded by the Defense Threat Reduction Agency and under Grant No. DMR-1708436 awarded by the National Science Foundation. The government has certain rights in this invention. Background of the Invention

[0007] When considering biomaterials for in vivo applications, the first and most important requirement is biocompatibility with the human body. In addition to inert biomaterials, functional biomaterials that can actively control and modulate immune responses are another approach. It was found that apoptotic cells can direct immune cells such as macrophages and dendritic cells to an immunosuppressive phenotype through externalized phosphatidylserine (PS) on their surface, thereby inducing immune tolerance even in areas of inflammatory activation.

[0008] There exists a need to develop improved non-fouling polymers and compositions and materials comprising these polymers having advantageous non-fouling properties. The present invention seeks to meet this need and provides further related advantages. SUMMARY OF THE INVENTION

[0010] The present invention provides zwitterionic phosphatidylserine (ZPS) monomers, ZPS polymers and ZPS copolymers, methods for preparing ZPS monomers, ZPS polymers and ZPS copolymers, compositions and materials comprising ZPS polymers and ZPS copolymers, and methods of using ZPS monomers, ZPS polymers and ZPS copolymers.

[0011] The present invention also provides non-zwitterionic (neutral) phosphatidylserine (NZPS) monomers, polymers, copolymers, compositions and materials containing the same, and methods of making and using the same.

[0012] On the one hand, the invention provides particles comprising one or more zwitterionic phosphatidylserine polymers, wherein the polymer is coupled to the particles. In one embodiment, the particles have micron or nanometer size and comprise one or more zwitterionic phosphatidylserine polymers coupled to the particles. In certain embodiments, the polymer is covalently coupled to the particles. In other embodiments, the polymer is physically adsorbed to the particles. As used herein, the term "micrometer size" refers to particles having a diameter of about 1 μm or more. As used herein, the term "nanometer size" refers to particles having a diameter less than 1 μm.

[0013] In certain embodiments, the particle is a biomolecule, and the biomolecule modified to include the polymer is a bioconjugate. Representative biomolecules that can be used in the present invention include proteins, nucleic acids, glycoproteins, lipids, and proteoglycans. Representative proteins include enzymes, signaling proteins (e.g., hormones, cytokines, regulatory proteins, insulin, PD-1 / PD-L1 / 2 inhibitors), hemostatic or thrombotic proteins, vaccines, complement system proteins, and antibodies or functional fragments or characteristic portions thereof. In certain embodiments, the biomolecule is a previously modified biomolecule, such as a PEGylated biomolecule (e.g., a protein modified to include one or more poly(ethylene glycol)s.

[0014] In other embodiments, the biomolecule is a small molecule therapeutic agent (a carbon-based therapeutic agent having a molecular weight less than about 1000 g / mol, preferably less than about 800 g / mol).

[0015] In further embodiments, the particle is a drug delivery vehicle. Representative drug delivery vehicles include micelles, liposomes, and polymersomes (eg, containing one or more therapeutic and / or diagnostic agents).

[0016] In certain embodiments, the particle is a cell, virus, or bacteria.

[0017] In other embodiments, the particle is a hydrogel, such as a microgel or a nanogel.

[0018] In further embodiments, the particle is a metal, a metal oxide, a ceramic, a synthetic polymer, a natural polymer, a crystal, a semiconductor material, graphene, graphene oxide, iron oxide or silicon dioxide, or a quantum dot.

[0019] In certain embodiments, the particle has one or more zwitterionic phosphatidylserine polymers grafted from the particle. In other embodiments, the particle has one or more zwitterionic phosphatidylserine polymers grafted to the particle.

[0020] In certain embodiments, the particles comprise one or more zwitterionic phosphatidylserine polymers having repeating units of the formula:

[0021]

[0022] in

[0023] * indicates the point of attachment of a repeating unit in a polymer or copolymer to other repeating units, or the end group of a polymer or copolymer;

[0024] B is the polymer main chain;

[0025] L 2 is a linking group selected from the following: -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is an integer independently selected from 1 to 20;

[0026] R 2 and R 3 are independently selected from hydrogen, C 1 -C 20 Alkyl and C 6 -C 12 Aryl;

[0027] m is an integer from 1 to 20;

[0028] p is an integer from 1 to 20; and

[0029] n is an integer from about 10 to about 500.

[0030] In other embodiments, the particles comprise one or more zwitterionic phosphatidylserine polymers having repeating units of the formula:

[0031]

[0032] in

[0033] * indicates the point of attachment of a repeating unit in a polymer or copolymer to other repeating units, or the end group of a polymer or copolymer;

[0034] R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl and C 6 -C 12 Aryl,

[0035] R 2 and R 3 are independently selected from hydrogen, C 1 -C 20 Alkyl and C 6 -C 12 Aryl, or R 2 and R 3 Together with nitrogen, it forms a ring;

[0036] R 4 and R 5 is a polymerizable residue of a polymerizable functional group;

[0037] L is C or Si;

[0038] L 2 is a linking group selected from the following: -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is an integer independently selected from 1 to 20;

[0039] L 3 and L 4 Independently selected from -(CH 2 ) x -、-C(=O)NH(CH 2 )x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is an integer independently selected from 0 to 20;

[0040] m is an integer from 1 to 20;

[0041] p is an integer from 1 to 20; and

[0042] n is an integer from about 10 to about 500.

[0043] In further embodiments, the particles comprise one or more zwitterionic phosphatidylserine polymers having repeating units of the formula:

[0044]

[0045] in

[0046] * indicates the point of attachment of a repeating unit in a polymer or copolymer to other repeating units, or the end group of a polymer or copolymer;

[0047] R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl and C 6 -C 12 Aryl;

[0048] R 2 and R 3 are independently selected from hydrogen and C 1 -C 6 Alkyl, or R 2 and R 3 Together with nitrogen, it forms a ring;

[0049] X is O or NH,

[0050] n is an integer from 1 to 20;

[0051] m is an integer from 1 to 20;

[0052] p is an integer from 1 to 20; and

[0053] a is an integer from about 10 to about 500.

[0054] In another aspect, the invention provides a method of rendering a particle immunosuppressive. In one embodiment, the method comprises covalently coupling one or more zwitterionic phosphatidylserine polymers to the particle.

[0055] In another aspect, the present invention provides a substrate surface having one or more zwitterionic phosphatidylserine polymers covalently coupled thereto.

[0056] In other aspects, the present invention also provides: particles having micrometer or nanometer dimensions, comprising one or more neutral (non-zwitterionic) phosphatidylserine polymers covalently coupled to the particles; a method for making the particles immunosuppressive, comprising covalently coupling one or more neutral (non-zwitterionic) phosphatidylserine polymers to the particles; and a substrate surface having one or more neutral (non-zwitterionic) phosphatidylserine polymers covalently coupled thereto.

[0057] In another aspect, the invention provides ZPS monomers. In these embodiments, the monomer comprises a polymerizable moiety covalently coupled to a zwitterionic phosphatidylserine moiety.

[0058] In one embodiment, the ZPS monomer has the formula:

[0059]

[0060] in

[0061] R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl and C 6 -C 12 Aryl;

[0062] R 2 and R 3 are independently selected from hydrogen, C 1 -C 20 Alkyl and C 6 -C 12 Aryl, or R 2 and R 3 Together with nitrogen, it forms a ring;

[0063] R 4 and R 5 independently selected from functional groups suitable for polymerization by addition, condensation or free radical polymerization;

[0064] L is C or Si;

[0065] L 2Independently selected from -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -, wherein x is an integer from 1 to 20;

[0066] L 3 and L 4 Independently selected from -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is an integer independently selected from 0 to 20;

[0067] m is an integer from 1 to 20; and

[0068] p is an integer of 1 to 20.

[0069] In another embodiment, the ZPS monomer has the formula:

[0070]

[0071] in,

[0072] R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl and C 6 -C 12 Aryl,

[0073] R 2 and R 3 are independently selected from hydrogen and C 1 -C 6 Alkyl, or R 2 and R 3 Together with nitrogen, it forms a ring,

[0074] X is O or NH,

[0075] n is an integer from 1 to 20,

[0076] m is an integer from 1 to 20, and

[0077] p is an integer of 1 to 20.

[0078] On the other hand, the invention provides ZPS polymers and copolymers. In these embodiments, the ZPS polymer or copolymer has a repeating unit, wherein one or more repeating units include a zwitterionic phosphatidylserine moiety. In certain embodiments, the zwitterionic phosphatidylserine moiety is a side group from a polymer backbone. In other embodiments, the zwitterionic phosphatidylserine moiety is a component of the polymer backbone (e.g., a portion of the zwitterionic phosphatidylserine moiety is in the polymer backbone).

[0079] In certain embodiments, the ZPS polymer or copolymer comprises repeating units having the formula:

[0080]

[0081] in

[0082] * indicates the point of attachment of a repeating unit in a polymer or copolymer to other repeating units, or the end group of a polymer or copolymer;

[0083] B is the polymer main chain;

[0084] L2 is a linking group that connects the ZPS part to the main chain. Representative groups include -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is an integer independently selected from 1 to 20;

[0085] R 2 and R 3 are independently selected from hydrogen, C 1 -C 20 Alkyl and C 6 -C 12Aryl, or R 2 and R 3 Together with nitrogen, it forms a ring;

[0086] m is an integer from 1 to 20;

[0087] p is an integer from 1 to 20; and

[0088] n is an integer from about 10 to about 500.

[0089] In other embodiments, the ZPS polymer or copolymer comprises repeating units having the formula:

[0090]

[0091] in

[0092] * indicates the point of attachment of a repeating unit in a polymer or copolymer to other repeating units, or the end group of a polymer or copolymer;

[0093] R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl and C 6 -C 12 Aryl;

[0094] R 2 and R 3 are independently selected from hydrogen, C 1 -C 20 Alkyl and C 6 -C 12 Aryl, or R 2 and R 3 Together with nitrogen, it forms a ring;

[0095] R 4 and R 5 polymeric residues independently selected from functional groups suitable for polymerizing by addition, condensation or free radical polymerization;

[0096] L is C or Si;

[0097] L 2 Independently selected from -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -, wherein x is an integer from 1 to 20;

[0098] L 3 and L 4 Independently selected from -(CH 2 )x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x -, and -(CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is an integer independently selected from 0 to 20;

[0099] m is an integer from 1 to 20;

[0100] p is an integer from 1 to 20; and

[0101] n is an integer from about 10 to about 500.

[0102] In further embodiments, the ZPS polymer or copolymer comprises repeating units having the formula:

[0103]

[0104] in

[0105] * indicates the point of attachment of a repeating unit in a polymer or copolymer to other repeating units, or the end group of a polymer or copolymer;

[0106] R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl and C 6 -C 12 Aryl;

[0107] R 2 and R 3 are independently selected from hydrogen and C 1 -C 6 Alkyl, or R 2 and R 3 Together with nitrogen, it forms a ring;

[0108] X is O or NH;

[0109] n is an integer from 1 to 20;

[0110] m is an integer from 1 to 20;

[0111] p is an integer from 1 to 20; and

[0112] a is an integer from about 10 to about 500. BRIEF DESCRIPTION OF THE DRAWINGS

[0113] The foregoing aspects of the present invention and many of the attendant advantages will become more readily appreciated as they become better understood by reference to the following detailed description when taken in conjunction with the accompanying drawings.

[0114] Figure 1 The relative fibrinogen adsorption (%) of MPC, NZPS and ZPS hydrogel surfaces relative to the control TCPS as measured by ELSIA was compared.

[0115] Figure 2A The results were compared with those from RAW 264.7 macrophages (10 5 The levels of TNF-α secretion in the supernatant of RAW 264.7 macrophages (10, 25, 50, 100, 200, 1000 μg / ml) treated with various concentrations (10, 25, 50, 100, 200, 1000 μg / ml) of MPC, NZPS or ZPS nanogel solution for 18 h and then stimulated with LPS (100 ng / mL) for 48 h.

[0116] Figure 2B The results were compared with those from RAW 264.7 macrophages (10 5 The levels of TNF-α secretion in the supernatant of RAW 264.7 macrophages (cells / well) were treated with 100 μg / ml of MPC, NZPS or ZPS nanogel solution for 18 h and then stimulated with LPS (100 ng / mL) for 48 h, wherein various concentrations (0, 10, 25, 50, 100, 200 μg / ml) of Annexin V solution were used, and the nanogel solution was pre-incubated for 6 h.

[0117] Figure 2C The results were compared with those from RAW 264.7 macrophages (10 5 The RAW 264.7 macrophages were incubated with FITC-BSA-encapsulated MPC, NZPS and ZPS nanogels for 30, 60, 120 and 180 min, and then the cells were washed and lysed to detect the recovered fluorescence.

[0118] Figure 3A CD40 / CD80 of DC 2.4 dendritic cells incubated with native uricase, MPC-uricase conjugate, NZPS-uricase conjugate, and ZPS-uricase conjugate for 72 hours and stained for flow cytometry were compared relative to vehicle control.

[0119] (B) Summary of the percentage of dendritic cells that remain in an immature state (CD40-CD80-). (C) TGF-β secreted into the supernatant was detected by ELISA kit.

[0120] Figure 3B Compared to Figure 3A The percentage of dendritic cells that remain in an immature state (CD40-CD80-) is described in the literature.

[0121] Figure 3C Compared to Figure 3A TGF-β secretion from dendritic cells was measured by ELISA as described in .

[0122] Figure 4A and 4B The circulation time of native uricase, ZPS-uricase, NZPS-uricase, and MPC-uricase conjugate after the first (4A) and third (4B) injection in mice was compared.

[0123] Figure 4C and 4D The detection of IgM (4C) and IgG (4D) specific for uricase or uricase conjugates was compared.Mice were sacrificed on day 21 and their sera were collected for the detection of IgM and IgG specific for uricase or uricase conjugates by ELISA test.

[0124] Figure 4E Comparison of Treg phenotype (Foxp3+) cells in CD4+CD25+ splenocytes of mice treated with native uricase, ZPS-uricase conjugate, NZPS-uricase conjugate and MPC-uricase conjugate for 72 hours and then stained for flow cytometry relative to blank control. Summary of the percentage of Treg phenotype (Foxp3+) cells in CD4+CD25+ splenocytes.

[0125] Figure 4F Compared with Figure 4E Treg % in CD4+CD25+ cells of mice treated as described in. DETAILED DESCRIPTION OF THE INVENTION

[0127] In one aspect, the present invention provides zwitterionic phosphatidylserine (ZPS) monomers, ZPS polymers and ZPS copolymers, methods for preparing ZPS monomers, ZPS polymers and ZPS copolymers, compositions and materials comprising ZPS polymers and ZPS copolymers, and methods of using ZPS monomers, ZPS polymers and ZPS copolymers.

[0128] As used herein, the term "zwitterionic phosphatidylserine monomer" or "ZPS monomer" refers to a zwitterionic phosphatidylserine monomer comprising a phosphatidylserine moiety (NH 2 -CH(-CH 2 OP(=O)(O - ))-CO 2 H and its ionic form) and additional cationic centers (e.g., -N + (R a )(R b )-, where R a and R b are independently H or C 1 -C 3 The monomer or side group of the homopolymer or copolymer is a zwitterionic monomer or side group due to the cationic N center and the anionic phosphate center.

[0129] A representative ZPS monomer has formula (I):

[0130]

[0131] Wherein, in certain embodiments, R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl (preferably C 1 -C 6 Alkyl) and C 6 -C 12 Aryl, R 2 and R 3 are independently selected from hydrogen and C 1 -C 6 Alkyl, or R 2 and R 3 Together with nitrogen to form a ring, X is O or NH, n is an integer from 1 to 20 (e.g., 1, 2, 3, 4, 5 or 6), m is an integer from 1 to 20 (e.g., 1, 2, 3, 4, 5 or 6), and p is an integer from 1 to 20 (e.g., 1, 2, 3, 4, 5 or 6).

[0132] As described above, the term "zwitterionic phosphatidylserine polymer" or "ZPS polymer" refers to a polymer (i.e., a homopolymer or copolymer) having one or more side groups comprising a phosphatidylserine moiety and an additional cationic center. The polymer is zwitterionic due to the cationic N center and the anionic phosphate center in the side groups of the repeating unit.

[0133] ZPS homopolymers are prepared by polymerizing monomers of formula (I), and ZPS copolymers are prepared by copolymerizing monomers of formula (I) with comonomers. These ZPS polymers (homopolymers, random copolymers, block copolymers) contain repeating units with pendant zwitterionic phosphatidylserine (ZPS) moieties as shown below:

[0134]

[0135] Wherein, in certain embodiments, R 1 , R 2 , R 3 , X, n, m and p are as described above for the monomers of formula (I), a is an integer from about 10 to about 500, and * represents the point of attachment of the repeating unit in the polymer or copolymer to other repeating units, or a polymer or copolymer end group.

[0136] As described herein, ZPS monomers can be readily polymerized under standard polymerization conditions to provide ZPS polymers.

[0137] ZPS monomer, ZPS polymer and ZPS copolymer

[0138] In certain aspects, the present invention provides ZPS monomers and ZPS polymers and ZPS copolymers prepared from ZPS monomers.

[0139] The monomers of the present invention include: (a) a ZPS monomer whose backbone is selected from siloxane, fluorinated, peptide, carbamate, urea, imide, carbonate, anhydride, phosphazene, epoxy, sulfone and sulfide backbones, and degradable backbones other than methacrylate and acrylate backbones, (b) a linear ZPS crosslinker, a degradable and non-degradable ZPS-based crosslinker, or (c) a linear ZPS-based monomer that provides a ZPS group in the polymer backbone or a ZPS group in the polymer side chain.

[0140] The polymers and copolymers of the present invention include polymers and copolymers comprising repeating units containing ZPS groups, such as homopolymers, random copolymers, block copolymers, multi-block copolymers, and branched or star polymers, including such polymers prepared by polymerization (or copolymerization) of one or more monomers of the present invention (e.g., ZPS monomers).

[0141] ZPS monomer In one aspect, the present invention provides ZPS monomers. ZPS monomers provide ZPS polymers and ZPS copolymers comprising repeating units containing ZPS. The ZPS groups of the repeating units and polymers can be ZPS pendant groups (ie, polymer side chains).

[0142] In certain embodiments, the ZPS monomer comprises a polymerizable moiety covalently coupled to a zwitterionic phosphatidylserine moiety.

[0143] In certain embodiments, the ZPS monomers include monomers that provide polymers or copolymers with ZPS side groups (polymer side chains). Representative ZPS monomers have formula (I) shown above. Other representative ZPS monomers have formula (III):

[0144]

[0145] in

[0146] R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl and C 6 -C 12 Aryl;

[0147] R 2 and R 3 are independently selected from hydrogen, C 1 -C 20 Alkyl (e.g., C 1 -C 3 Alkyl) and C 6 -C 12 Aryl, or R 2 and R 3 Together with nitrogen, it forms a ring;

[0148] R 4 and R 5 independently selected from functional groups suitable for polymerization by addition, condensation or free radical polymerization;

[0149] L is C or Si;

[0150] L2 is independently selected from -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -, wherein x is an integer from 1 to 20 (e.g., 1, 2, 3, 4, 5 or 6);

[0151] L 3 and L 4 Independently selected from -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x-、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x is independently selected at each occurrence from 0 to 20, preferably an integer from 1 to 20 (in certain embodiments, L 3 and / or L 4 does not exist);

[0152] m is an integer from 1 to 20 (e.g., 1, 2, 3, 4, 5, or 6); and

[0153] p is an integer from 1 to 20 (eg, 1, 2, 3, 4, 5 or 6).

[0154] The preparation of representative ZPS monomers useful in preparing the polymers and copolymers of the present invention is described in Example 1.

[0155] It should be understood that the ZPS polymers and copolymers of the present invention used to prepare the surface coatings, bulk materials, independent materials, hydrogels and conjugates of the present invention can be prepared from the monomers described herein, including methacrylate / methacrylamide ZPS monomers of formula (I) and ZPS monomers of formula (III).

[0156] ZPS polymers and copolymers In other aspects, the present invention provides a ZPS polymer prepared from a ZPS monomer as described herein and comprising a ZPS repeating unit.

[0157] In certain embodiments, ZPS polymer or copolymer has repeating unit, and wherein one or more repeating units comprise zwitterionic phosphatidylserine part.In some schemes of these embodiments, zwitterionic phosphatidylserine part is the side group from polymer backbone.In other schemes of these embodiments, zwitterionic phosphatidylserine part is the component of polymer backbone (for example, a part of zwitterionic phosphatidylserine part is in polymer backbone).

[0158] In certain embodiments of these polymers and copolymers, the polymer and copolymer backbone can be any of a polyester, polypeptide, polyimide, polyphosphazene, polysiloxane, polyepoxy, vinyl polymer, phenolic polymer, polyurethane, polyurea, polycarbonate, polysulfone, or polysulfide.

[0159] The ZPS polymers and copolymers of the present invention include polymers and copolymers prepared from monomers of formula (I) and (III). The polymers can be formed by polymerization of (a) a monomer of formula (I), (b) a monomer of formula (III), or (c) a comonomer of formula (I) and (III). The copolymers can be prepared by copolymerization of (a) a monomer of formula (I) and a second comonomer suitable for copolymerization with the monomer of formula (I), (b) a monomer of formula (III) and a second comonomer suitable for copolymerization with the monomer of formula (II), and (c) a monomer of formula (I) and a monomer of formula (III) suitable for copolymerization with the monomer of formula (I).

[0160] In certain embodiments, the ZPS monomer provides a polymer repeat unit comprising a ZPS moiety that is pendant from the polymer backbone (i.e., forms part of a polymer side chain). Representative polymers having ZPS moieties as pendant groups from the polymer backbone have formula (II) as shown above. Other representative ZPS polymers have formula (IV):

[0161]

[0162] in

[0163] * indicates the point of attachment of a repeating unit in a polymer or copolymer to other repeating units, or the end group of a polymer or copolymer;

[0164] B is a polymer backbone as described above;

[0165] L 2 is a linking group that connects the ZPS moiety to the main chain, representative groups include -(CH 2 ) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is an integer independently selected from 1 to 20;

[0166] R 2 and R 3 are independently selected from hydrogen, C 1 -C20 Alkyl (e.g., C 1 -C 3 Alkyl groups, including cycloalkyl groups, such as C 3 -C 7 Cycloalkyl) and C 6 -C 12 Aryl, or R2 and R3 together with nitrogen form a ring;

[0167] m is an integer from 1 to 20 (e.g., 1, 2, 3, 4, 5 or 6);

[0168] p is an integer from 1 to 20 (e.g., 1, 2, 3, 4, 5 or 6); and

[0169] n is an integer from about 10 to about 500.

[0170] In other embodiments, representative polymers having ZPS moieties as pendant groups from the polymer backbone have Formula (V):

[0171]

[0172] Where R 1 , R 2 , R 3 , R 4 , R 5 ,L,L 2 , L 3 , L 4 , m, p and * are as described above for the monomer of formula (III), wherein it is understood that R in formula (V) 4 and R 5 The functional groups R in formula (III) are 4 and R 5 of a polymerization residue; n is an integer from about 10 to about 500.

[0173] In certain embodiments, the zwitterionic phosphatidylserine moiety of the ZPS polymer is at least partially contained within the polymer backbone.

[0174] In certain of these embodiments, the ZPS polymer has repeating units comprising the formula:

[0175]

[0176] Where L 2 , p and * are as described above for the polymer of formula (IV), wherein it is understood that L 2 The point coupled to B is N + (R 1 ) of nitrogen (i.e., with L 2 covalently coupled atoms in B); and n is an integer from about 10 to about 500.

[0177] In others of these embodiments, the ZPS polymer has repeating units comprising the formula:

[0178]

[0179] Where R 1 , R 4 , R 5 , L 2 , L 3 , L 4 , p and * are as described above for the monomer of formula (III), wherein it is understood that R in formula (VA) 4 and R 5 are the functional groups R in formula (III) 4 and R 5 of a polymerized residue; and n is an integer from about 10 to about 500.

[0180] In certain embodiments, the present invention provides a modified surface comprising a polymer of formula (II), (IV), (IVA), (V) or (VA). The modified surface can be a surface of an artificial nervous system, a neuron regeneration platform, a neural sensor, a cell culture platform, a non-fouling semiconductor, a battery, an organic solar cell, a biofuel cell, a printed electronic circuit, an organic light emitting diode, an actuator, an electrochromic device, a supercapacitor, a chemical sensor, a flexible transparent display, an electromagnetic shield, an antistatic coating, a microwave absorber or a radar absorber.

[0181] In certain embodiments, the present invention provides a bulk construct comprising a polymer of formula (II), (IV), (IVA), (V) or (VA). Representative constructs can be medical, electronic or offshore devices. In certain aspects of these embodiments, the bulk construct is an artificial nervous system, a neuron regeneration platform, a neural sensor, a cell culture platform, a non-scaling semiconductor, a battery, an organic solar cell, a biofuel cell, a printed electronic circuit, an organic light emitting diode, an actuator, an electrochromic device, a supercapacitor, a chemical sensor, a flexible transparent display, an electromagnetic screen, an antistatic coating, a microwave absorbing device or a radar absorbing device.

[0182] ZPS star polymers and copolymers In other aspects, the present invention provides ZPS star polymers and ZPS copolymers comprising ZPS repeating units.

[0183] These polymers include a core and a plurality of ZPS branches covalently coupled to the core. The core of these polymers can be a small molecule, an oligomer, or a polymer having a star shape. In certain embodiments, these polymers can include three, four, five or more ZPS branches. In certain embodiments of these embodiments, one or more of the ZPS branches can themselves be further branched. In certain embodiments, these polymers can also include terminal functional groups bonded to the ends of the plurality of ZPS branches. Representative terminal functional groups are selected from OH, NH, NH 2 SH, N 3 、CH=CH 2 , C≡CH, COOH, CHO, imidate, haloacetyl, hydrazide, alkoxyamine, aryl azide, diaziridine, maleimide, carbodiimide, N-hydroxysuccinimide (NHS), thiazolidine-2-thione, pyridyl disulfide, difluorocyclooctyne, Staudinger reagent pair, isocyanate, isothiocyanate, thioether, sulfhydryl, hydrazine, hydroxymethylphosphine, sulfo-NHS ester, pentafluorophenyl ester, sulfonyl azide and 5H-dibenzo[b,f]azepine and its derivatives.

[0184] ZPS copolymers: hydrophobic and hydrophilic building blocks In a further aspect, the present invention provides a ZPS copolymer comprising a ZPS repeating unit and a hydrophobic and / or hydrophilic structural unit.

[0185] In certain embodiments, the copolymer is a random, diblock, or hyperbranched copolymer comprising ZPS repeating units (eg, poly(ZPS)).

[0186] Representative block copolymers include at least one ZPS component block (A); and at least one hydrophobic block (B). In certain embodiments, the copolymer further comprises a hydrophilic block (C) or a second hydrophobic block (C). The block copolymers of the present invention include AB diblock copolymers, ABC triblock copolymers, ABA triblock copolymers, BAB triblock copolymers, linear or star multiblock (AB) n Copolymers, Miktoarm block copolymers (AB n or A n B) and mixtures thereof. In certain embodiments, the copolymer further comprises neutral hydrophilic repeating units (eg, alkylene oxide repeating units, such as ethylene oxide repeating units).

[0187] In certain embodiments, the copolymer comprises a ZPS component comprising repeating units derived from a ZPS monomer (e.g., a ZPS monomer of the invention having formula (I) or (III)) and a hydrophobic component comprising repeating units derived from a hydrophobic monomer.

[0188] Representative hydrophobic repeating units may be derived from acrylic acid and esters, alkyl acrylic acid and esters, acrylamides, alkyl acrylamides, polysiloxane repeating units, polyester repeating units, polyurethane repeating units, polystyrene repeating units, and fluorinated derivatives thereof.

[0189] In certain embodiments, the copolymer comprises a ZPS component, a hydrophilic component, and an optional hydrophobic component, wherein the ZPS component comprises repeating units derived from a ZPS monomer (e.g., a ZPS monomer of the invention having formula (I) or (III)), the hydrophilic component comprises repeating units derived from a hydrophilic monomer, and the hydrophobic component comprises repeating units derived from a hydrophilic monomer. In certain of these embodiments, the hydrophilic repeating unit comprises a ZPS moiety. In other embodiments, the hydrophilic repeating unit can be polyhydroxyethyl methacrylate (PHEMA), polyethylene glycol (PEG), polycarboxybetaine (PCB), polysulfobetaine (PSB), polyphosphobetaine (PPB), polyphosphorylcholine (PPC), polyacrylamide (PAA), poly(2,3-dihydroxypropyl methacrylate) (PDHPM), poly(N-isopropylacrylamide) (PNIPAM), polyacrylamide (PAM), poly(2-oxazoline), poly(acrylic acid), polymethacrylate (PMA), polyvinyl alcohol (PVA), poly(vinyl pyrrolidone) (PVP), polyelectrolytes, polysaccharides, polyamides and other hydrophilic polymers, peptide-based materials, and copolymers of two or more hydrophilic monomers.

[0190] ZPS polymer surface coating, bulk material and stand-alone material

[0191] In other aspects, the present invention provides ZPS polymer surface coatings, ZPS polymer bulk materials and ZPS polymer stand-alone materials. In certain embodiments, ZPS polymer surface coatings, bulk materials and stand-alone materials are prepared from ZPS monomers and polymers and copolymers prepared from ZPS monomers.

[0192] ZPS polymers can be attached to surfaces (e.g., medical devices, sensors, membranes, ships, and offshore structures) by a "grafting from" or "grafting to" method to make the surface non-fouling. ZPS polymers can also be blended with or blended into bulk materials (e.g., siloxanes). Surface coatings can be on flat surfaces or on nanoparticle / microparticle surfaces. ZPS polymers can also be prepared into stand-alone low-fouling and high-strength materials and devices for medical and offshore applications by (i) unique backbones, such as siloxanes, fluororesins, urethanes, imides, amides, and (ii) strong interactions, such as multiple hydrogen bonds, and (iii) interpenetrating networks.

[0193] ZPS polymer surface coatingThe present invention provides ZPS polymer surface coatings. In certain embodiments, the surface coating comprises a ZPS polymer (oligomer) or ZPS copolymer of the present invention as described herein (e.g., a polymer of formula (II), (IV), (IVA), (V) or (VA)).

[0194] Surfaces coated with ZPS polymers and copolymers have non-fouling properties. The non-fouling properties of the surface can be evaluated by fibrinogen adsorption and cell adhesion. In certain embodiments, the surfaces of the present invention have a surface area of ​​less than about 200 ng / cm 2 In other embodiments, the surfaces of the present invention have a fibrinogen adsorption of less than about 100 ng / cm 2 In other embodiments, the surfaces of the present invention have a fibrinogen adsorption of less than about 50 ng / cm 2 In other embodiments, the surfaces of the present invention have a fibrinogen adsorption of less than about 30 ng / cm 2 In other embodiments, the surfaces of the present invention have a fibrinogen adsorption of less than about 20 ng / cm 2 In other embodiments, the surfaces of the present invention have a fibrinogen adsorption of less than about 10 ng / cm 2 In certain embodiments, the surfaces of the present invention have a fibrinogen adsorption of less than about 5 ng / cm 2 Fibrinogen adsorption.

[0195] In certain embodiments, the surface is coated with a ZPS polymer or copolymer prepared from one or more ZPS monomers selected from a polymerizable group including, but not limited to, ZPS acrylates, ZPS acrylamides, ZPS methacrylates, ZPS methacrylamides, ZPS vinyl compounds, ZPS epoxides, and mixtures thereof. Representative ZPS monomers include those described herein, including ZPS monomers of formula (I) and (III).

[0196] In certain embodiments, the ZPS polymer or copolymer is a random, multi-block or hyperbranched copolymer comprising poly(ZPS). In other embodiments, the ZPS polymer or copolymer is an interpenetrating ZPS polymer network.

[0197] In certain embodiments, the ZPS polymer or copolymer has surface adhesion groups (eg, DOPA, thiol, silane, click chemistry, hydrophobic, hydrophilic, and charged groups).

[0198] Surfaces coated with ZPS polymers and copolymers can be prepared by attaching the ZPS polymers or copolymers to the substrate surface through covalent interactions, physical hydrophobic-hydrophobic, charge-charge and hydrogel bonding interactions, or a combination of chemical and physical interactions.

[0199] A surface coated with a ZPS polymer or copolymer can be prepared by grafting a ZPS polymer from a substrate surface ("grafted from") (e.g., preparing a polymer surface by polymerizing suitable monomers in the presence of a substrate to form a polymer or copolymer), or can be prepared by grafting a ZPS polymer onto a substrate surface ("grafted onto") (e.g., preparing a polymer surface by coupling a preformed polymer or copolymer to a substrate).

[0200] In certain embodiments, ZPS polymers and copolymers are grafted from a substrate by a polymerization method such as atom transfer radical polymerization (ATRP), reversible addition-fragmentation chain transfer polymerization (RAFT), or photoinferterpolymerization.

[0201] In certain embodiments, ZPS polymers and copolymers are grafted to substrates via conjugation methods such as click chemistry, DOPA conjugation chemistry, or self-assembled monolayers (SAMs) through thiols or silanes.

[0202] The ZPS polymer surface coating can be applied to a variety of substrates (e.g., substrate surface). In certain embodiments, the surface is all or part of a biomedical device. Representative biomedical devices include catheters, ear canal drainage tubes, feeding tubes, glaucoma drainage tubes, hydrocephalus shunts, corneal prostheses, nerve guide tubes, tissue adhesives, X-ray guides, artificial joints, artificial heart valves, artificial blood vessels, pacemakers, left ventricular assist devices (LVAD), arterial grafts, vascular grafts, stents, intravascular stents, heart valves, joint replacements, vascular prostheses, skin repair devices, cochlear replacements, contact lenses, artificial ligaments and tendons, dental implants, and tissue scaffolds for regenerative tissue engineering. In certain embodiments, the device is a contact lens.

[0203] In certain embodiments, the surface is all or part of a particle. Representative particles include metals, metal oxides, ceramics, synthetic polymers, natural polymers, silicon dioxide, crystals, and semiconductor material particles. In certain embodiments, the particle is a biomolecule, such as a protein (e.g., an enzyme) or a nucleic acid (e.g., DNA or RNA). In other embodiments, the particle is a cell.

[0204] In certain embodiments, the surface is all or part of a membrane or bioseparation membrane. Representative membranes include membranes used for protein purification, wastewater treatment, bioreactors, desalination, and water / oil purification.

[0205] In certain embodiments, the surface is on, or forms the entirety of, a drug delivery vehicle, such as a gene delivery vehicle, an RNA delivery vehicle, or a protein delivery vehicle.

[0206] In certain embodiments, the surface is on, or forms all or part of, an implantable or subcutaneous sensor.

[0207] In certain embodiments, the surface is on a tissue scaffold, or forms all or part of a tissue scaffold.

[0208] ZPS polymer body material . The present invention provides ZPS polymer bulk materials. In certain embodiments, the bulk material comprises a ZPS polymer (oligomer) or ZPS copolymer of the present invention as described herein (e.g., a polymer of formula (II), (IV), (IVA), (V) or (VA)). In certain embodiments, the material is prepared by a polymerization or copolymerization process using a monomer of the present invention as described herein (e.g., a monomer of formula (I) or (III)).

[0209] In certain embodiments, the bulk material is obtained by blending one or more ZPS polymers or copolymers with one or more other polymers, such as polyesters, polycarbonates, polyurethanes, polyureas, polysulfides, polysulfones, polyimides, polyepoxies, aromatic polyesters, celluloses, fluoropolymers, polyacrylic polymers, polyamides, polyanhydrides, polyethers, vinyl polymers, phenolic resins, elastomers, and other addition polymers.

[0210] In other embodiments, the bulk material comprises an interpenetrating ZPS polymer network and one or more other polymers, such as polyesters, polycarbonates, polyurethanes, polyureas, polysulfides, polysulfones, polyimides, polyepoxies, aromatic polyesters, celluloses, fluoropolymers, polyacrylic polymers, polyamides, polyanhydrides, polyethers, vinyl polymers, phenolic resins, elastomers, and other addition polymers.

[0211] ZPS polymer independent material . The present invention provides ZPS polymer stand-alone materials. In certain embodiments, the material comprises a ZPS polymer (oligomer) or ZPS copolymer of the present invention as described herein (e.g., a polymer of formula (II), (IV), (IVA), (V) or (VA)). In certain embodiments, the material is prepared by a polymerization or copolymerization process using a monomer of the present invention as described herein (e.g., a monomer of formula (I) or (III)).

[0212] In certain embodiments, the ZPS polymer stand-alone material is a non-fouling material and has high mechanical strength. In certain embodiments of these embodiments, the stand-alone material has a protein adsorption of less than about 30, less than about 50, or less than about 100 ng / cm 2 , non-scaling materials with tensile / compressive strength greater than about 0.2, greater than about 0.5 or greater than about 1.0 MPa.

[0213] In certain embodiments, the ZPS polymer stand-alone material is a ZPS polymer network, which is formed by introducing (a) dipole-dipole interactions, such as cyano groups (C≡N) and (b) hydrogen donors / acceptors, such as amide groups ((NH)-(C=O)-), polyamide groups (-(NH)-(C=O)-) n (n=1-5)), carbamate group ((NH)-(C=O)-O-), polycarbamate group ((-(NH)-(C=O)-O-) n (n=1-5)), urea group (-(NH)-(C=O)-(NH)-), polyurea group (-(NH)-(C=O)-(NH)-) n (n=1-5)) and their combinations. These groups can be derived from ZPS monomers and ZPS (random or block) copolymers. These groups can be in the polymer backbone or in the polymer side groups.

[0214] The ZPS polymer network can be reinforced with a backbone in a ZPS monomer or ZPS polymer, such as polyacrylate, polymethacrylate, polyacrylamide, polymethacrylamide, polyamide, polydimethylsiloxane, polyethylene, polypropylene, polystyrene, polytetrafluoroethylene, polyisobutylene, polyester, polycarbonate, polyurethane, polyurea, polysulfide, polysulfone, polyimide, polyepoxide, polyanhydride, polyether and other condensation / addition polymers. In certain embodiments, the ZPS polymer network is reinforced by any combination of the above.

[0215] In certain embodiments, ZPS polymers can form copolymers with other polymers or composite materials, such as polyesters, polycarbonates, polyurethanes, polyureas, polysulfides, polysulfones, polyimides, polyepoxides, aromatic polyesters, celluloses, fluoropolymers, polyacrylic acids, polyamides, polyanhydrides, polyethers, vinyl polymers, phenolic resins, elastomers, and other addition polymers. Fibers, clays, nanotubes, and other inorganic objects can be added to improve the mechanical properties of these materials.

[0216] The ZPS independent material of the present invention can be formed into an object by various methods, such as injection molding, blow molding, extrusion molding, calendaring molding, cast molding, compression molding, prevarication molding, and 3D printing.

[0217] The ZPS stand-alone materials of the present invention can be used in biomedical / biotechnology, consumer products, engineering / marine, therapeutic / diagnostic applications, such as catheters, ear canal drainage tubes, feeding tubes, glaucoma drainage tubes, hydrocephalus shunts, corneal prostheses, nerve guides, tissue adhesives, X-ray guides, artificial joints, artificial heart valves, artificial blood vessels, pacemakers, left ventricular assist devices (LVADs), arterial grafts, vascular grafts, stents, intravascular stents, heart valves, joint replacements, vascular prostheses, skin repair devices, cochlear replacements, contact lenses, artificial ligaments and tendons, dental implants and tissue scaffolds for regenerative tissue engineering, drug delivery, gene delivery, RNA delivery, protein delivery, marine and engineering devices / objects (e.g., membranes, tubes, pipes, containers or plates).

[0218] In certain embodiments, the stand-alone materials may be used in offshore products such as offshore hulls, offshore structures, bridges, propellers, heat exchangers, periscopes, sensors, fish nets, cables, pipes / pipes, containers, membranes, and oil booms.

[0219] In certain embodiments, the independent material can be combined with a biomaterial. Representative biomaterials include nucleic acids (e.g., genes, DNA, RNA), proteins (e.g., enzymes, antibodies, or functional fragments thereof), peptides, lipids, cells or microorganisms, solid nanoparticles (iron oxide, silicon dioxide, quantum dots, or gold nanoparticles), or are used to prevent surfactants from dehydrating the skin.

[0220] ZPS polymer hydrogel

[0221] The present invention provides ZPS polymer hydrogels. In certain embodiments, the hydrogel comprises a cross-linked ZPS polymer (oligomer) or ZPS copolymer of the present invention as described herein (e.g., a polymer of formula (II), (IV), (IVA), (V) or (VA)). In certain embodiments, the hydrogel is prepared by a polymerization or copolymerization method using a monomer of the present invention as described herein (e.g., a monomer of formula (I) or (III)).

[0222] ZPS polymer hydrogel can be produced by ZPS monomer and various cross-linking agents, including degradable or non-degradable ZPS cross-linking agents. ZPS star polymers can be prepared by forming hydrogels (e.g., by click chemistry). These hydrogels can be in the form of bulk hydrogels or granular hydrogels. These hydrogels can be used as implantable materials and devices to reduce capsule formation and as a medium for protecting, amplifying, preserving and differentiating various cells (e.g., stem cells, immune cells, pancreatic islets, platelets, and cardiomyocytes) in a controlled manner. Granular and star-shaped hydrogels can be injected together with biological products (e.g., various cells and tumors for tumor vaccines).

[0223] In certain embodiments, the ZPS hydrogel is a cross-linked hydrogel prepared from one or more ZPS monomers (eg, monomers of formula (I) or (II)) using one or more cross-linking agents.

[0224] In others of these embodiments, the cross-linking agent is a multifunctional zwitterionic cross-linking agent that includes a carboxybetaine, sulfobetaine, or phosphobetaine moiety.

[0225] In further aspects of these embodiments, the cross-linking agent is a multifunctional cross-linking agent, such as N,N'-methylenebisacrylamide (MBAA), polyethylene glycol (PEG) diacrylate or bisacrylamide, or PEG dimethacrylate or dimethylacrylamide.

[0226] In certain embodiments, a bifunctional ZPS cross-linker is used to prepare the hydrogel. In other embodiments, a degradable or non-degradable cross-linker is used to prepare the hydrogel. In further embodiments, a degradable zwitterionic disulfide cross-linker is used to prepare the hydrogel. In other embodiments, a peptide-based cross-linker that can be degraded by an enzyme or a suitable reagent is used to prepare the hydrogel.

[0227] The ZPS hydrogels of the present invention can be prepared by free radical mediated polymerization techniques, such as thermal, photo or redox.

[0228] The preparation of a representative ZPS hydrogel of the present invention is described in Example 4. Protein adsorption and cell adhesion of a representative ZPS hydrogel are described in Example 4.

[0229] The ZPS hydrogels of the present invention can be used in biosensors and biomedical devices, vascular grafts, intravascular stents, heart valves, joint replacements, cell preservation / expansion / differentiation, drug delivery platforms, hulls, offshore structures / devices, and other materials and devices that come into contact with physiological environments.

[0230] In certain embodiments, the ZPS hydrogel is a star-shaped hydrogel. The star-shaped hydrogel can be prepared from a polymer having a core and a plurality of ZPS groups or zwitterionic branches covalently coupled to the core. A representative core includes one of a star-shaped small molecule, oligomer or polymer having three, four, five or more branches.

[0231] In certain embodiments, the hydrogel is cross-linked by a degradable cross-linking agent that can selectively (i.e., under specific conditions) degrade. The degradable cross-linking agent can be selected from a peptide cross-linking agent, a polysaccharide cross-linking agent, an anhydride cross-linking agent, a disulfide cross-linking agent, and a polyester cross-linking agent. For certain of these embodiments, the hydrogel can be enzymatically hydrolyzed or digested.

[0232] In certain embodiments, the star-shaped hydrogel branched polymer comprises terminal functional groups bound to the ends of the branches (e.g., the ends of multiple ZPS or zwitterionic branches). Representative terminal functional groups include OH, NH, NH 2 SH, N 3 、CH=CH 2 , C≡CH, COOH, CHO, imidate, haloacetyl, hydrazide, alkoxyamine, aryl azide, diaziridine, maleimide, carbodiimide, N-hydroxysuccinimide (NHS), thiazolidine-2-thione, pyridyl disulfide, difluorocyclooctyne, Staudinger reagent pair, isocyanate, isothiocyanate, thioether, sulfhydryl, hydrazine, hydroxymethylphosphine, sulfo-NHS ester, pentafluorophenyl ester, sulfonyl azide and 5H-dibenzo[b,f]azepine.

[0233] In certain embodiments, the hydrogel comprises a first polymer / copolymer (first star-shaped hydrogel) bound to one or more second polymers / copolymers (second star-shaped hydrogel). The hydrogel can be used as an injectable hydrogel. In certain embodiments of these embodiments, the first polymer is bound to the one or more second polymers via a terminal functional group.

[0234] Star-shaped hydrogels can be combined with zwitterionic hydrogels and formed into pellets of various sizes in specific templates or by mechanical reduction (e.g., blenders). These granular hydrogels can be used as injectable hydrogels with or without biological content.

[0235] The ZPS star hydrogel of the present invention can be prepared by: (a) synthesizing ZPS or zwitterionic branches by ATRP, RAFT, ROP, condensation, Michael addition, branch generation / growth reaction, and (b) reacting ZPS or zwitterionic branches with cores to provide star polymers. In certain embodiments, the method further comprises functionalizing the ends of ZPS or zwitterionic branches by a "click" reaction, a thiol exchange reaction, or a reduction reaction.

[0236] In certain embodiments, the ZPS hydrogel is a microgel. The microgels of the present invention are micrometer-sized, cross-linked hydrogels with a size of about 1 micron (10 -6 m) to 1mm(10 -2 m), composed of ZPS-based monomers and supported by arbitrary cross-linking chemicals.

[0237] The microgels of the present invention can be prepared using functionalized ZPS monomers, oligomers or polymers by a variety of methods, including:

[0238] (a) one of the reaction pairs selected from azide and alkyne, azide and olefin, thiol and maleimide, thiol and olefin, thiol and disulfide, or any other "click", bioorthogonal or other reaction pair;

[0239] (b) located at the end of the polymer structure(s) or along the main chain;

[0240] (c) Incorporation of peptides, nucleic acids, proteins, antibodies, nanoparticles, microparticles, micelles, liposomes, polymersomes, drugs, prodrugs or other therapeutic substances or drug delivery formats for surgical applications, therapeutic applications, wound healing applications, drug delivery formulations, cell storage and preservation or regenerative medicine.

[0241] In certain embodiments, the microgel comprises a mixture of ZPS monomers or polymers with other types of ionic or nonionic non-fouling monomers or polymers, or a copolymer of a ZPS-based polymer with other types of ionic or nonionic monomers.

[0242] For microgels, crosslinking is achieved using any combination of physical and / or chemical mechanisms, which in certain embodiments include:

[0243] (a) Chemical crosslinkers of any structure that copolymerize with the monomers via free radical mediated reactions, including commercially available crosslinkers based on polyethylene glycol (PEG), oligoethylene glycol (OEG) or other structures or groups, terminated with two or more acrylates, methacrylates, acrylamides, maleimides or similar reactive groups, or custom synthesized crosslinkers containing any functional, reactive or degradable groups. The optional degradable groups may be selected from disulfide bonds, esters, anhydrides, enzymatically cleavable peptides (e.g., GPQGIWCG motifs), or chemicals that respond to external stimuli.

[0244] (b) bioorthogonal cross-linking chemistries and “click” chemistries, such as azide / alkyne (including SPAAC) and thiol-ene chemistry, by inclusion as functional groups in the main polymer chain(s) or structure or as separate cross-linking molecules;

[0245] (c) any type of physical interaction, including ionic interactions, hydrogen bonds, hydrophobic interactions, interactions with biomolecules or nanoparticles of natural or synthetic origin, or any other reversible or irreversible physical interaction; and

[0246] (d) Any combination of the above cross-linking mechanisms.

[0247] In certain embodiments, microgels are prepared using bifunctional ZPS cross-linking molecules, oligomers or polymers comprising one or more ZPS moieties, or mixtures of these molecules.

[0248] In certain embodiments, microgels are prepared using zwitterionic (carboxybetaine, sulfobetaine or phosphobetaine) cross-linked molecules, oligomers or polymers comprising one or more zwitterionic moieties, or mixtures of these molecules. These cross-linkers may contain degradable groups, such as disulfide bonds, esters, or stimuli-responsive groups or degradable peptides.

[0249] In certain embodiments, as described above, the present invention provides materials formed from two or more assembled microgels, wherein the interactions between each discrete microgel produce a bulk material with unique properties. These materials may include other components, such as small molecule drugs, peptides, biomolecules, nanoparticles, cells or tissues.

[0250] In certain embodiments, the microgels and assemblies described above are prepared from microgels that have a finite size due to a polymerization process such as miniemulsion polymerization.

[0251] In other embodiments, the microgel is derived from the above-described (bulk) hydrogel or the above-described star hydrogel, and after polymerization, is further sized to a finite size using any processing step that grinds, extrude, mince, cut or granulate the hydrogel into discrete units of finite size.

[0252] The microgels and assemblies described above can be dried or lyophilized (freeze dried) into dehydrated powders for storage, transportation, use or sterilization. The microgel powders can be rehydrated with any aqueous fluid, including water, saline or ionic solutions, cell growth or preservation media with or without cells, or any other physiologically relevant solution that can contain therapeutic drugs, therapeutic proteins, therapeutic nucleic acids, cells, nanoparticles or microparticles.

[0253] ZPS star-shaped hydrogels and microgels and their assemblies and / or their partially or completely dried or rehydrated compositions have the following uses:

[0254] (a) Materials with non-Newtonian behavior (e.g., exhibiting viscoelastic, thixotropic, shear thickening (dilatant), shear thinning (pseudoplastic), and / or Bingham plastic properties);

[0255] (b) self-healing materials and / or shape memory materials, or similar classes of “smart” materials that can repair damage or restore their properties following injury or external stimulation; and

[0256] (c) Anti-fouling materials or surface coatings that prevent non-specific adsorption of proteins or other biomolecules, such as for offshore applications, drug delivery platforms, biosensors and other medical devices, vascular grafts, intravascular stents, heart valves, joint replacements, and other materials and devices that come into contact with the physiological environment.

[0257] ZPS star hydrogels and microgels and their assemblies can be used as injectable or spreadable materials for biomedical applications, especially in applications requiring non-Newtonian fluid properties and high biocompatibility:

[0258] (a) Injectable or spreadable materials capable of mechanical support, such as those used in cosmetic or reconstructive surgery, vascular prostheses, skin repair devices, cochlear replacements, injectable vitreous substances, artificial cartilage, artificial fat, collagen mimics and other soft tissue mimics or supports;

[0259] (b) injectable or spreadable materials that have a desired or specific biological interaction with a surface or tissue, particularly when non-specific interactions are to be avoided or a desired balance of non-specific / specific interactions has to be achieved; and

[0260] (c) Injectable or spreadable carriers for delivery and / or protection or shielding of drugs, biomolecules (e.g., nucleic acids, peptides, proteins, polysaccharides), cells (e.g., pancreatic islets, cardiovascular cells, stem cells, T cells, blood cells), nanoparticles or microparticles (e.g., PLGA / drug preparations), micelles, liposomes, polymer vesicles or other therapeutic substances or drug delivery forms for surgical applications, therapeutic applications, wound healing and drug delivery preparations.

[0261] ZPS star hydrogels and microgels and their assemblies can be used as scaffolds, matrices or substrates for the growth, maintenance or expansion of cells and tissues, wherein the cells and microgel constructs can be grown using any culture method or device, including any type of bioreactor, and can be derived from the following lineages, including:

[0262] (a) Pluripotent and multipotent stem and progenitor cells, including:

[0263] (i) embryonic stem cells (ESCs), tissue-derived stem cells (e.g., from the skin, blood, or eye), hematopoietic stem and progenitor cells (HSPCs) derived or purified from umbilical cord blood or bone marrow, mesenchymal stem cells, or induced pluripotent stem cells (iPSCs),

[0264] (ii) genetically modified or transfected stem and progenitor cells, and

[0265] (iii) cancer stem cells (CSC);

[0266] (b) Hematopoietic cells that normally circulate in human blood, including erythrocytes (red blood cells), leukocytes (white blood cells) and platelets (thrombocytes);

[0267] (c) immune cells and progenitor cells or their differentiated lineages, including:

[0268] (i) T cells expressing the CD8 surface glycoprotein, particularly including naive cytotoxic T lymphocytes (CTLs) and their differentiated or activated lineages, including central memory T cells,

[0269] (ii) T cells expressing the CD4 surface glycoprotein, particularly including naive helper T lymphocytes, and their differentiated or activated lineages, including TH1, TH2, TH9, TH17, TFH, Treg and central memory (TCM) T cells,

[0270] (iii) Regulatory T cells (TREG) from any source, natural Treg or induced Treg,

[0271] (iv) Natural killer T cells (NKT),

[0272] (v) Chimeric antigen receptor T cells (CAR-T),

[0273] (vi) genetically modified T cells;

[0274] (d) B cells, dendritic cells and other antigen presenting cells (APCs) or immune cells not specifically listed above;

[0275] (e) Pancreatic islets or other insulin-producing cells and beta cells that can be used to treat and manage diabetes;

[0276] (f) nervous system cells and progenitor cells;

[0277] (g) Cardiovascular system cells and progenitor cells; and

[0278] (h) Cells that can be used in the fields of immunotherapy, regenerative medicine, blood disorders or malignancies, or cancer vaccines or treatments.

[0279] ZPS star-shaped hydrogels and microgels and their assemblies can be used as biocompatible materials, scaffolds, formulation components or contact materials for any method of preserving cells or tissues or retaining their biological functions for clinical or military use, particularly for cell types that are difficult to preserve for long periods of time using conventional methods, such as blood cells (e.g., platelets and red blood cells), at room temperature or low temperatures, in whole blood or preservation solutions, and in the presence or absence of DMSO, glycerol, glycine betaine or other permeabilizing agents or cryoprotectants.

[0280] ZPS star-shaped hydrogels and microgels and their assemblies can be used in objects, devices and components, such as implantable biosensors; wound care devices, glues and sealants, contact lenses; dental implants; orthopedic devices, such as artificial joints, artificial bones, artificial ligaments and artificial tendons; cardiovascular devices, such as catheters, artificial valves, artificial blood vessels, artificial stents, LVAD or cardiac rhythm management devices; gastroenterology devices, such as feeding tubes, digestive tract clamps, gastrointestinal sleeves or gastric balloons; OB / Gyn devices, such as implantable birth control devices or vaginal slings; nephrology devices, such as anastomotic connectors or subcutaneous ports; neurosurgery devices, such as nerve guides, cerebrospinal fluid drainage tubes or shunts; dermatological devices, such as skin prosthetic devices; ophthalmic devices, such as shunts; otolaryngological devices, such as stents, cochlear implants, tubes, shunts, or dilators; intraocular lenses; aesthetic implants, such as breast implants, nasal implants, and cheek implants; neurological implants, such as neurostimulation devices, cochlear implants, and nerve catheters; hormone control implants, such as blood glucose sensors and insulin pumps; implantable biosensors; access port devices; and tissue scaffolds; pulmonary devices, such as valves or artificial lungs for the management of COPD; radiological devices, such as radiopaque or sound-opaque markers; or urological devices, such as catheters or artificial urethras.

[0281] In other aspects, the present invention provides a substrate coated with a ZPS star-shaped hydrogel or microgel or microgel assembly. Representative substrates include objects, devices and components, such as implantable biosensors; wound care devices, glues and sealants, contact lenses; dental implants; orthopedic devices, such as artificial joints, artificial bones, artificial ligaments and artificial tendons; cardiovascular devices, such as catheters, artificial valves, artificial blood vessels, artificial stents, LVADs and / or cardiac rhythm management devices; gastroenterology devices, such as feeding tubes, digestive tract clamps, gastrointestinal sleeves or gastric balloons; OB / Gyn devices, such as implantable birth control devices or vaginal slings; nephrology devices, such as anastomotic connectors or subcutaneous ports; neurosurgery devices, such as nerve guides, cerebrospinal fluid drainage tubes or shunts. devices; dermatological devices, such as skin repair devices; ophthalmic devices, such as shunts; otolaryngological devices, such as stents, cochlear implants, tubes, shunts, or dilators; intraocular lenses; aesthetic implants, such as breast implants, nasal implants, and cheek implants; neurological implants, such as neurostimulation devices, cochlear implants, and nerve catheters; hormone control implants, such as blood glucose sensors and insulin pumps; implanted biosensors; access port devices; and tissue scaffolds; pulmonary devices, such as valves or artificial lungs for the management of COPD; radiological devices, such as radiopaque or sound-opaque markers; or urological devices, such as catheters or artificial urethras.

[0282] ZPS polymer nanoparticles and microparticles

[0283] In another aspect, the present invention provides nano- and micro-particles comprising the ZPS polymers and copolymers of the present invention. The ZPS polymers and copolymers of the present invention can be used to form nano- and micro-particles in the form of nano- and micro-gels, micelles, liposomes and polymer vesicles. They can also be used to coat solid particles, such as quantum dots, iron oxide, silicon dioxide and gold, for treatment or diagnosis. The ZPS polymers and copolymers of the present invention can be associated with nano- and micro-particles by covalent and non-covalent attachment.

[0284] In certain embodiments, particles having nanoscale dimensions are provided. The particles have a core, the surface of which has a plurality of ZPS polymers or copolymers grafted to or from the core. Representative particle cores include metals, metal oxides, ceramics, synthetic polymers, natural polymers, crystals, semiconductor materials, graphene, graphene oxide, iron oxide, silicon dioxide, quantum dots, hydrogels, liposomes, micelles, carbon-based materials, or biomolecules.

[0285] ZPS polymer and copolymer conjugates

[0286] In another aspect, the present invention provides ZPS polymer and copolymer conjugates. ZPS polymers can be attached to biomolecules (eg, proteins / peptides, nucleic acids, and sugars), other macromolecules, and cells by grafting to or from methods to provide a variety of conjugates.

[0287] In certain embodiments, the ZPS polymer conjugate or copolymer conjugate is a ZPS polymer bioconjugate comprising one or more ZPS polymers coupled to a biomolecule. Suitable biomolecules include proteins, nucleic acids, glycoproteins, proteoglycans, and lipids. Suitable biomolecules include small molecule therapeutic agents (i.e., carbon-based therapeutic agents having a molecular weight of less than about 1000 g / mol, preferably less than about 800 g / mol).

[0288] Representative proteins include enzymes, signaling proteins, hemostatic and thrombotic proteins, vaccines, complement system proteins and antibodies, their functional fragments or characteristic parts. Representative signaling proteins include hormones, cytokines, regulatory proteins, insulin and PD-1 / PD-L1 / 2 inhibitors.

[0289] In certain aspects of these embodiments, the ZPS polymer conjugate or copolymer conjugate is a bioconjugate of a ZPS polymer or copolymer comprising one or more ZPS polymers or copolymers coupled to a modified biomolecule, such as a polymer-modified biomolecule. Exemplary polymer-modified biomolecules include biomolecules that have been modified with polyethylene glycol (PEG) polymers (e.g., the PEG portion of these PEG-modified biomolecules can be in the polymer backbone or in a side group from the polymer backbone). Representative polymer-modified biomolecules are described in Example 5, which are further modified by coupling one or more ZPS polymers or copolymers thereto.

[0290] In other embodiments, the ZPS polymer conjugate or copolymer conjugate is a bioconjugate of a ZPS polymer or copolymer comprising one or more ZPS polymers coupled to a cell, virus, or bacteria.

[0291] The ZPS polymer conjugate or copolymer conjugate can be a delivery vehicle. Representative delivery vehicles include micelles, liposomes or polymer vesicles for therapeutic or diagnostic applications.

[0292] In certain embodiments, the present invention provides micelles, liposomes, polymersomes, or particles self-assembled from copolymers or conjugated lipids of the present invention comprising one or more ZPS polymers or copolymers.

[0293] In additional embodiments, the present invention provides compositions comprising a ZPS polymer or copolymer conjugate and a pharmaceutically acceptable carrier or diluent. In certain embodiments, the ZPS polymers and copolymers of the present invention can be used as a carrier or diluent for the composition.

[0294] The preparation and immunogenicity of representative ZPS polymer protein conjugates are described in Example 7.

[0295] ZPS polymer nanogels and nanocages

[0296] In another aspect, the present invention provides ZPS polymer nanogels and nanocages. ZPS polymers can be used to provide nanogels that chemically entrap one or more other substances, and nanocages that physically entrap one or more other substances.

[0297] In certain embodiments, the present invention provides nanogels for chemically encapsulating cargo comprising one or more ZPS polymers or one or more ZPS copolymers.

[0298] In other embodiments, the present invention provides nanocages for physically encapsulating cargo comprising one or more ZPS polymers or one or more ZPS copolymers.

[0299] Suitable cargo (e.g., substances) that can be chemically captured by the nanogel or physically captured by the nanocage include biomolecules such as proteins, lipids, glycoproteins, cells, viruses, bacteria, and small molecules (e.g., therapeutic agents having a molecular weight of less than about 1000 g / mol, preferably 800 g / mol) or other biomolecules described herein.

[0300] In certain embodiments, the nanogel or nanocage comprises a ZPS polymer or copolymer and one or more therapeutic agents.

[0301] In other embodiments, the nanogel or nanocage comprises a ZPS polymer or copolymer and one or more diagnostic agents.

[0302] In additional embodiments, the nanogel or nanocage comprises a ZPS polymer or copolymer, one or more therapeutic agents, and one or more diagnostic agents.

[0303] Non-zwitterionic phosphatidylserine monomers, polymers, copolymers, compositions, surfaces, and methods of making and using the same Law

[0304] It should be understood that neutral phosphatidylserine (NPS) monomers, polymers and copolymers, also referred to herein as non-zwitterionic phosphatidylserine (NZPS) monomers, polymers and copolymers, are also within the scope of the present invention. Therefore, in additional aspects, the present invention provides non-zwitterionic phosphatidylserine (NZPS) monomers, NZPS polymers and NZPS copolymers, methods for preparing NZPS monomers, NZPS polymers and NZPS copolymers, compositions and materials comprising NZPS polymers and NZPS copolymers, and methods of using NZPS monomers, NZPS polymers and NZPS copolymers.

[0305] As used herein, the term "non-zwitterionic phosphatidylserine monomer" or "NZPS monomer" refers to a monomer comprising a phosphatidylserine moiety (NH2 -CH(-CH 2 OP(=O)(O-))-CO 2 H and its ionic form) of a polymerizable monomer or homopolymer or copolymer.

[0306] A representative NZPS monomer has formula (VI):

[0307]

[0308] Wherein, in certain embodiments, R 1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C 1 -C 20 Alkyl (preferably C 1 -C 6 Alkyl) and C 6 -C 12 Aryl, X is O or NH, n is an integer from 1 to 20 (eg, 1, 2, 3, 4, 5, or 6), and p is an integer from 1 to 20 (eg, 1, 2, 3, 4, 5, or 6).

[0309] The term "non-zwitterionic phosphatidylserine polymer" or "NZPS polymer" refers to a polymer (ie, a homopolymer or a copolymer) having one or more pendant groups comprising a phosphatidylserine moiety as described above.

[0310] NZPS polymers are prepared by polymerizing monomers of formula (VI), and NZPS copolymers are prepared by copolymerizing monomers of formula (VI) with comonomers. These NZPS polymers (homopolymers, random copolymers, block copolymers) include repeating units with pendant phosphatidylserine (PS) moieties as shown below:

[0311]

[0312] Wherein, in certain embodiments, R 1 , X, n and p are as described above for the monomer of formula (VI), a is an integer from about 10 to about 500, and * represents the point of attachment of the repeating unit to other repeating units in the polymer or copolymer, or a polymer end group.

[0313] NZPS monomers can be readily polymerized under standard polymerization conditions to provide NZPS polymers.

[0314] Thus, it should be understood that the entire description herein of ZPS monomers, ZPS polymers, ZPS copolymers, compositions comprising ZPS polymers, surfaces comprising ZPS polymers, and methods of using ZPS monomers, polymers and compositions also applies to NZPS monomers, polymers, compositions, surfaces and methods.

[0315] Example 2 describes the preparation and characterization of a representative NZPS of the present invention.

[0316] The preparation and immunogenicity of representative NZPS polymer protein conjugates are described in Example 7.

[0317] This article describes monomers of PS-mimicking polymerizable (NZPS), polymers derived from the monomers, and polymers attached to biomolecules, macromolecules, small molecules, particles, implants, devices, surfaces, coatings, and hydrogels. Biocompatible immunosuppressive biomaterials include NZPS polymers and their derivatives and precursors for use with peptides, proteins, lipids, glycoproteins, biomacromolecules (e.g., cells, viruses, bacteria), nanoparticles, microparticles, small molecule drugs, any of which can be used for human administration, including use with medical devices, prostheses, implant materials (including dental), and organ transplants.

[0318] In one aspect, the polymerizable NZPS monomers and derivatives or precursors have the formula (VIII) shown below:

[0319]

[0320] in

[0321] A, G, and I are functional groups that render the monomer polymerizable in certain embodiments and are independently selected from H, F, Cl, Br, I, SH, protected thiols, NH 2 , -NH-(secondary amine), N=C=O, protected NCO, N=C=S, COOH, activated ester, aldehyde, COSH, C(=S)SH, OCOOH, OCOSH, OC(=S)OH, SC(=O)SH, SC(=S)SH, N(C=O)NH 2 、N(C=NH)NH 2 、N(C=S)NH 2 , δ-valerolactone, ε-caprolactone, CH 2 =CH-C(=O)-O-, CH 2 =CH-C(=O)-NH-, CH 2 =CH-C(=O)-S-, CN, CH 2 =C(CH 3 )-C(=O)-O-, CH 2 =C(CH 3 )-C(=O)-NH-, OH, azide, alkyne, C 6 -C 10 Aryl, cyclic groups (isobornyl, cyclohexyl, cyclopentyl), fluorine (perfluorobutyl, perfluoroethyl) derivatives or blank (absent);

[0322] B, F and H are independently selected from -(CH 2 ) x -, where x is an integer from 0 to 20;

[0323] C is selected from C, N, Si or blank (absent); and

[0324] D is selected from C(=O)(CH 2 ) x 、-(CH 2 ) x -, wherein x is an integer from 1 to 20;

[0325] Also provided are methods of preparing these monomers, polymers prepared from these monomers, and methods of using these polymers to attach them to or from nanoparticles, surfaces, coatings, and hydrogels, and their use to impart an immunosuppressive effect to these nanoparticles, surfaces, coatings, and hydrogels.

[0326] In another aspect, NZPS polymers and copolymers are provided. These polymers and copolymers comprise repeating units. In certain embodiments, the repeating units of these polymers and copolymers have the formula (IX) shown below (less R 2 and R 3 )(The repeating unit will not include R 2 and R 3 ; however, macromers may also include polymers and copolymers):

[0327]

[0328] It has n repeating units - M 1 -(K 1 -ZK 2 ) j -M 2 -M 1 -(K 3 -XK 4 ) j -M 2 -, which contains j repeating units -K 1 -ZK 2 - and j repeating units -K 3 -XK 4 -.

[0329] In the above formula,

[0330] K 1 , K 2 , K 3 and K 4 Independently selected from -(CH 2) x -、-(CH(CN)) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is independently selected from an integer from 0 to 20, a combination thereof, or blank (when the substituent is absent);

[0331] R 2 and R 3 independently selected from H, F, Cl, Br, I, OH, SH, protected thiols, NH 2 , -NH-(Secondary amine), N=C=O, N=C=S, COOH, COSH, C(=S)SH, OCOOH, OCOSH, OC(=S)OH, SC(=O)SH, SC(=S)SH, N(C=O)NH 2 、N(C=NH)NH 2 、N(C=S)NH 2 ,δ-valerolactone part,ε-caprolactone part,CH 2 =CH-C(=O)-O-, CH 2 =CH-C(=O)-NH-, CH 2 =CH-C(=O)-S-, CN, CH 2 =C(CH 3 )-C(=O)-O-, CH 2 =C(CH 3 )-C(=O)-NH- or blank (when the substituent is absent);

[0332] n is an integer from 5 to about 10,000.

[0333] j is an integer from 1 to about 1000 at each occurrence.

[0334] M 1 and M 2 Independently selected from -O-(CH 2 ) n -、-S-(CH 2 )n -、-C(=O)-(CH 2 ) n -、-C(=S)-(CH 2 ) n -、-C(=NH)-(CH 2 ) n - and -NH-(CH 2 ) n -, wherein n is an integer from 1 to 20; -(CH 2 ) x -、-(CH(CN)) x -、-C(=O)NH(CH 2 ) x -、-C(=O)O(CH 2 ) x -、-C(=O)OC(=O)O(CH 2 ) x -、-(CH 2 ) x -O-(CH 2 ) x - and - (CH 2 ) x -SS-(CH 2 ) x -, wherein x at each occurrence is independently selected from an integer from 0 to 20, combinations thereof, or blank (when the substituent is absent); and

[0335] Z and X are independently selected from the following formulae:

[0336]

[0337] wherein L is independently selected from F, Cl, Br, I, SH, protected thiol, NH 2 , -NH-(secondary amine), N=C=O, protected NCO, N=C=S, COOH, COSH, C(=S)SH, OCOOH, OCOSH, OC(=S)OH, SC(=O)SH, SC(=S)SH, N(C=O)NH 2 、N(C=NH)NH 2 、N(C=S)NH 2 , δ-valerolactone, ε-caprolactone, CH 2 =CH-C(=O)-O-, CH 2 =CH-C(=O)-NH-, CH 2 =CH-C(=O)-S-, CN, CH 2 =C(CH 3 )-C(=O)-O-, CH 2 =C(CH3 )-C(=O)-NH-, OH, azide, alkyne, C 6 -C 10 Aryl, cyclic group (isobornyl, cyclohexyl, cyclopentyl), fluorine (perfluorobutyl, perfluoroethyl) derivatives or blank;

[0338] K is independently selected from -(CH 2 ) x -, wherein x is an integer from 0 to 20;

[0339] J is selected from C(=O)(CH 2 ) x ,-(CH 2 ) x -, wherein x is an integer from 1 to 20; and

[0340] * is the same as shown in the above formula and K 1 , K 2 , K 3 and K 4 connection point.

[0341] As used herein, the term "about" refers to ±5% of a stated value.

[0342] The following examples are provided to illustrate but not to limit the present invention. Example

[0343] Example 1

[0344] Preparation and characterization of representative ZPS monomers

[0345] In this example, the synthesis and purification of a representative polymerizable zwitterionic (ZPS) monomer is described.

[0346] An illustrative method for synthesizing the polymerizable ZPS monomers of the present invention is shown below.

[0347]

[0348] 3-(tert-butyloxy)-2-((tert-butyl)-2-(2-((2-(methacryloyloxy)ethyl)dimethylammonio)ethyl)phosphite Synthesis of (2-(2-(2-oxycarbonyl)amino)-3-oxopropyl ester (Compound 3). N-Boc-Ser-OtBu (1.0 g, 3.82 mmol) was dissolved in 30 ml of anhydrous benzene, and the solution was cooled to 0 ° C. Next, triethylamine (0.62 mL, 4.6 mmol) was added, and then a 10 mL anhydrous benzene solution of 2-chloro-2-oxo-1,3,2-dioxaphospholane 1 (0.42 mL, 4.6 mmol) was added dropwise over 30 minutes, and the reaction contents were stirred at room temperature for another 3 hours. After the reaction was completed, ether was poured into the reaction mixture, and the precipitated trimethylamine hydrochloride was filtered out. The filtrate was then concentrated under reduced pressure to obtain compound 2 as an oil, which was used in the next step without further purification. Compound 2 was redissolved in 30 mL of anhydrous acetonitrile, and 2-(dimethylamino)ethyl methacrylate (1.45 mL, 8.8 mmol) was added. The reaction mixture was then stirred at 55 ° C for 24 hours. The reaction contents were then concentrated under vacuum and purified by flash column chromatography to afford compound 3 in 42% yield. 1 H NMR (300 MHz, CDCl 3 )δ6.18(s, 1H), 5.67(s, 1H), 4.63-4.54(m, 2H), 4.35-4.14(m, 3H), 4.10-3.99(m, 2H), 3 .83-3.76 (m, 2H), 3.40-3.27 (m, 2H), 2.82 (s, 6H), 1.97 (s, 3H), 1.46 (d, J=11.7Hz, 18H).

[0349] Synthesis of a representative ZPS monomer (compound 4) Compound 3 (0.84 g, 1.6 mmol) was dissolved in 5 mL of dichloromethane and 30 mL of trifluoroacetic acid was added. The reaction contents were stirred for 5 hours. After the reaction was completed, the reaction mixture was concentrated under vacuum to obtain a viscous liquid. The crude product was then crystallized from MeOH: diethyl ether (1: 15) to obtain the desired compound 4 as a white powder. 1 H NMR (300 MHz, D 2 O) δ6.08 (s, 1H), 5.69 (s, 1H), 4.47-4.41 (m, 2H), 4.26-4.23 (m, 2H), 4.05-4.00 (m, 1H ), 3.87-3.84(m, 2H), 3.69-3.67(m, 2H), 3.50-3.45(m, 2H), 2.88(s, 6H), 1.84(s, 3H).

[0350] Example 2

[0351] Preparation and characterization of representative neutral PS monomers

[0352] In this example, the synthesis and purification of a representative polymerizable neutral PS (NZPS) monomer is described. An illustrative method for synthesizing NZPS monomers is shown below.

[0353]

[0354] Synthesis of compound 5 . N-Boc-Ser-OtBu (1.0 g, 3.82 mmol) was dissolved in 30 ml of anhydrous benzene, and the solution was cooled to 0 ° C. Next, triethylamine (0.62 mL, 4.6 mmol) was added, and then a 10 mL anhydrous benzene solution of 2-chloro-2-oxo-1,3,2-dioxaphospholane 1 (0.42 mL, 4.6 mmol) was added dropwise over 30 minutes, and then the reaction contents were stirred at room temperature for another 3 hours. After the reaction was completed, ether was poured into the reaction mixture, and the precipitated trimethylamine hydrochloride was filtered out. The filtrate was then concentrated under reduced pressure to obtain compound 2 as an oil, which was used in the next step without further purification. Compound 2 was redissolved in 30 mL of anhydrous acetonitrile, and sodium methacrylate (0.62 gm, 5.7 mmol) and 18-crown-6 ether (0.14 g, 0.53 mmol) were added thereto. The reaction mixture was then stirred at 55 ° C for 72 hours. After the reaction, the reaction contents were filtered, concentrated in vacuo, and purified by flash column chromatography to obtain compound 5 in a yield of 71%. 1 H NMR (300 MHz, CDCl 3 ) 66.15 (s, 1H), 5.57 (s, 1H), 4.41-4.27 (m, 2H), 4.24-4.04 (m, 4H), 3.86-3.78 (m, 1H), 1.95 (s, 3H), 1.46 (d, J=5.4Hz, 18H).

[0355] Synthesis of a representative neutral PS monomer (Compound 6) Compound 5 (1.2 g, 2.65 mmol) was dissolved in 5 mL of dichloromethane, and 30 mL of trifluoroacetic acid was added thereto. The reaction contents were stirred for 5 hours. After the reaction was completed, the reaction mixture was concentrated under vacuum to obtain a viscous liquid. The crude product was then crystallized with MeOH: diethyl ether (1: 20) to obtain the desired compound 6 as a white powder. 1 H NMR (300 MHz, D 2 O) δ6.11 (s, 1H), 5.66 (s, 1H), 4.34-4.15 (m, 5H), 4.10-3.97 (m, 2H), 1.85 (s, 3H).

[0356] Example 3

[0357] Non-fouling properties of representative NZPS and ZPS hydrogels

[0358] In this example, the non-fouling properties of representative NZPS and ZPS hydrogels are described.

[0359] Preparation of ZPS hydrogel

[0360] ZPS hydrogels were prepared by bulk photopolymerization of an aqueous hydrogel solution containing ZPS monomer (0.67 g Milli-Q water, 330 mg), a crosslinker N,N′methylenebis(acrylamide) (1 wt %, 3.3 mg) and a photoinitiator 2-hydroxy-2-methylphenylacetone (0.33 mg). The aqueous hydrogel solution was placed between two glass slides separated by a 0.5 mm thick polytetrafluoroethylene spacer and then photopolymerized at room temperature for 30 minutes. After polymerization, the hydrogel was removed from the mold and soaked in PBS for three days to remove unreacted chemicals and achieve a fully hydrated hydrogel network. The phosphate-buffered saline was replaced every 12 hours. Following the same protocol, MPC and NZPS hydrogels with the same crosslink density were prepared.

[0361] Fibrinogen adsorption test

[0362] The MPC, NZPS and ZPS hydrogels of hydration were perforated to form a 5 mm diameter disk using a biopsy sampler. The hydrogel disk was placed in a 24-well plate and incubated for 1 hour with 1 mL of 1 mg / mL fibrinogen in PBS buffer solution, then washed 5 times with pure PBS buffer. The hydrogel disk was then transferred to a new hole and incubated for 1 hour with 1 mL of PBS buffer solution of anti-fibrinogen (1 μg / mL) conjugated with 1 mL horseradish peroxidase (HRP). After washing 5 times with pure PBS buffer, all hydrogel disks were transferred to a new hole. Then, 1 mL of 1 mg / mL o-phenylenediamine (OPD), 0.1 M citric acid phosphate pH 5.0 solution containing 0.03% hydrogen peroxide were added. After incubation for 15 minutes, the enzymatic reaction was terminated by adding an equal volume of 1 M HCl. The same steps were performed as a control on a tissue culture polystyrene (TCPS) disk with the same surface area. The absorbance values ​​at 492 nm were recorded using a microplate reader and normalized to the absorbance value of the TCPS sample. Average data were obtained from three samples.

[0363] After incubation in a highly concentrated fibrinogen solution (10 mg / mL) for 1 h, the ZPS hydrogel disks exhibited excellent non-fouling properties by reducing the adsorbed fibrinogen by 84.4% relative to the TCPS disks. In contrast, the NZPS hydrogel disks only reduced the adsorbed fibrinogen by 41% relative to the TCPS disks ( Figure 1 ).

[0364] Example 4

[0365] Immunosuppressive effects of representative NZPS and ZPS nanogels

[0366] In this example, the immunosuppressive effects of representative NZPS and ZPS nanogels are described.

[0367] Preparation of MPC, NZPS and ZPS nanogels

[0368] AOT (sodium bis(2-ethylhexyl)sulfosuccinate, 237 mg) and Brij 30 (poly(ethylene glycol) dodecyl ether, 459 mg) were added to a 20 mL glass vial, and a stirring bar was added thereto. The vial was sealed with a polytetrafluoroethylene-lined septum cap and purged with dry nitrogen for 10 minutes. Nitrogen-deoxygenated hexane (10 mL) was then added to the vial under vigorous stirring. For the aqueous phase, the monomers (MPC, NZPS, ZPS) and the crosslinker (MBA) were dissolved in PBS buffer (pH 7.4, 250 μL) at a molar ratio of 95%:5%. Dry nitrogen was bubbled through the monomer solution for 2 minutes, and then the aqueous phase was slowly added dropwise to the organic continuous phase. The vial was sonicated to form a stable nanoemulsion. Dry nitrogen was bubbled through the monomer solution for 2 minutes, and then the aqueous phase was slowly added dropwise to the organic continuous phase. The vial was sonicated to form a stable nanoemulsion. Then a 20% (w / v) solution of ammonium persulfate in deionized water (10 μL) was added to the emulsion. After 5 minutes, polymerization was initiated by adding tetramethylethylenediamine (TEMED, 6 μL) and maintained at 4°C under rapid magnetic stirring. After 2 hours of reaction, the organic solvent was removed by rotary evaporator, the nanogel was precipitated, and washed 3 times with THF. The nanogel was resuspended in PBS buffer and purified with a centrifugal filter with a molecular weight cutoff of 100 KDa to remove unreacted monomers and crosslinking agents.

[0369] Preparation of MPC, NZPS and ZPS nanogels encapsulating FITC-BSA

[0370] AOT (sodium bis(2-ethylhexyl)sulfosuccinate, 237 mg) and Brij 30 (poly(ethylene glycol) dodecyl ether, 459 mg) were added to a 20 mL glass vial, and a stirring bar was added thereto. The vial was sealed with a polytetrafluoroethylene-lined septum cap and purged with dry nitrogen for 10 minutes. Nitrogen-deoxygenated hexane (10 mL) was then added to the vial under vigorous stirring. For the aqueous phase, FITC-BSA, monomers (MPC, NZPS, ZPS) and crosslinkers (MBA) were dissolved in PBS buffer (pH 7.4, 250 μL) at a molar ratio of 95%:5%. Dry nitrogen was bubbled through the monomer solution for 2 minutes, and then the aqueous phase was slowly added dropwise to the organic continuous phase. The vial was ultrasonically treated to form a stable nanoemulsion. A 20% (w / v) solution of ammonium persulfate in deionized water (10 μL) was then added to the emulsion. After 5 minutes, polymerization was initiated by adding tetramethylethylenediamine (TEMED, 6 μL) and maintained at 4 ° C under rapid magnetic stirring. After 2 hours of reaction, the organic solvent was removed by rotary evaporator, the nanogel was precipitated, and washed 3 times with THF. The nanogel was resuspended in PBS buffer and purified with a centrifugal filter with a molecular weight cutoff of 100 KDa to remove free FITC-BSA, unreacted monomers and cross-linking agents.

[0371] Immunosuppressive effects

[0372] RAW 264.7 cells (10 5 Cells were exposed to various concentrations (10, 25, 50, 100, 200, 1000 μg / ml) of MPC, NZPS or ZPS nanogel solutions for 18 h. Then, the cells were stimulated for another 48 h by LPS solution (100 ng / mL), and then the cells were centrifuged at 300 g for 10 min, and the supernatant medium was collected for cytokine (TNF-α) analysis by ELISA. Figure 2A As shown, although the effects of NZPS and ZPS on TNF-α levels were both dose-dependent, NZPS began to exhibit its inhibitory effect on TNF-α at a relatively low concentration, indicating that it has a stronger immunosuppressive effect than ZPS.

[0373] Annexin V blocking

[0374] To confirm that the immunosuppressive effects of NZPS and ZPS were derived from the eat-me signal mediated by their PS head groups, nanogel solutions (100 μg / ml) of MPC, NZPS, or ZPS were preincubated with various concentrations (0, 10, 25, 50, 100, 200 μg / ml) of annexin V (a protein with high affinity for PS groups and can block eat-me signaling) for 6 h. 5 The cells were treated with 100 ng / mL LPS (100 ng / mL) for 18 hours and then stimulated with LPS (100 ng / mL) for 48 hours. The secretion level of TNF-a in the supernatant was determined using an ELISA kit. Figure 2B As shown, the effects of NZPS and ZPS nanogels in reducing TNF-α secretion weakened with increasing concentrations of annexin V, showing effective blocking of its immunosuppressive effects. It is worth noting that ZPS nanogels were less sensitive to the blocking effect of annexin V, which may be because the non-fouling properties of ZPS may reduce the affinity of the PS functional groups in ZPS to its receptors to some extent. This also explains why the immunosuppressive effect of ZPS is weaker than that of NZPS.

[0375] Cellular uptake

[0376] RAW 264.7 macrophages (10 5 Cells were incubated with FITC-BSA-encapsulated MPC, NZPS, and ZPS nanogels for 30, 60, 120, and 180 min, and then the cells were washed and lysed to detect the recovered fluorescence. Figure 2C As shown, MPC showed minimal cellular uptake due to its excellent non-fouling properties, while NZPS nanogels were rapidly taken up by macrophages due to their mediation of eat-me signals. Compared with NZPS, the uptake of ZPS was slowed due to its non-fouling properties and reduced affinity to the receptor. These results suggest that the unique zwitterionic structure of ZPS can achieve both effective immunosuppression and good non-fouling properties.

[0377] Example 5

[0378] Representative bioconjugates containing poly(ZPS) and poly(NZPS)

[0379] In this example, representative bioconjugates of the invention are described. In certain embodiments, the representative bioconjugates comprise a ZPS polymer component. In other embodiments, the representative bioconjugates comprise a NZPS polymer component.

[0380] In this embodiment, the bioconjugate is an enzyme conjugate. A representative enzyme is uricase. The polymer is covalently coupled to the enzyme directly or through a linker suitable for connecting the polymer to the enzyme.

[0381] In the representative bioconjugates shown below, the bioconjugates also include a poly(ethylene glycol) (PEG) moiety. In certain embodiments, these bioconjugates include PEG in the linker between the enzyme and the PS polymer. In other embodiments, these bioconjugates include PEG as a side group from the polymer backbone (e.g., derived from polymerization of PEGMA).

[0382] Preparation and Characterization of Bioconjugates Containing Representative Poly(ZPS)-block-Poly(PEGMA) Block Copolymers

[0383] Synthesis of Thiol-Terminated Poly(ZPS)-block-Poly(PEGMA) Block Copolymers . Reversible addition-fragmentation chain transfer (RAFT) polymerization was used to prepare the block copolymer. Typically, the polymerization reaction of ZPS monomer (6.7 g) was initiated by azobisisobutyronitrile (AIBN, 18 mg) in the presence of 2-(dodecylthiothiocarbonylthio)-2-methylpropionic acid (100 mg) as a chain transfer agent (CTA). After 12 hours of reaction, the polymerization was stopped and the resulting polymer, poly(ZPS)-CTA, was purified by dialysis. Then, poly(ZPS)-CTA was used as a macromolecular CTA for the polymerization of PEGMA monomers (molar ratio: CTA / PEGMA=1 / 50). After precipitation in excess ether, the poly(ZPS)-block-poly(PEGMA)-CTA block copolymer was further purified by dialysis and lyophilization. Then, the CTA moieties on the block copolymer were converted into thiol groups by using a mixed solution of hexylamine and triethylamine.

[0384] Preparation of poly(ZPS)-block-poly(PEGMA)-uricase conjugate

[0385] First, the amine groups on the uricase were converted to maleimido groups by the bifunctional crosslinker BMPS (N-maleimidopropyl-oxysuccinimide ester). The activated uricase (10 mg) was then mixed with 4 ml of PBS solution of thiol-terminated poly(ZPS)-block-poly(PEGMA) copolymer (300 mg). The poly(ZPS)-block-poly(PEGMA)-uricase conjugate was purified by diafiltration to remove excess polymer and unreacted uricase.

[0386] Preparation and Characterization of Bioconjugates Containing Representative Poly(ZPS) and Poly(PEGMA) Polymers

[0387] Synthesis of Thiol-Terminated Poly(ZPS). Reversible addition-fragmentation chain transfer (RAFT) polymerization was used to prepare the block copolymer. Typically, the polymerization reaction of ZPS monomer (6.7 g) was initiated by azobisisobutyronitrile (AIBN, 18 mg) in the presence of 2-(dodecylthiothiocarbonylthio)-2-methylpropionic acid (100 mg) as CTA. After 12 hours of reaction, the polymerization was stopped and the resulting polymer, poly(ZPS)-CTA, was purified by dialysis. Then, the CTA moiety on poly(ZPS)-CTA was converted into thiol groups by using a mixed solution of hexylamine and triethylamine.

[0388] Synthesis of Thiol-Terminated Poly(PEGMA) The polymerization of PEGMA (5 g) was initiated by azobisisobutyronitrile (AIBN, 18 mg) in the presence of 2-(dodecylthiothiocarbonylthio)-2-methylpropionic acid (100 mg) as a chain transfer agent (CTA). After 12 hours of reaction, the polymerization was stopped and the resulting polymer, poly(PEGMA)-CTA, was purified by dialysis. Then, the CTA moiety on poly(PEGMA)-CTA was converted into thiol groups by using a mixed solution of hexylamine and triethylamine.

[0389] Preparation of Bioconjugates Containing Poly(ZPS) and Poly(PEGMA) .

[0390] First, the amine groups on the uricase were converted to maleimido groups by the bifunctional crosslinker BMPS (N-maleimidopropyl-oxysuccinimide ester). The activated uricase (10 mg) was then mixed with 4 ml of PBS solution of sulfhydryl-terminated poly (ZPS) (100 mg). The poly (ZPS)-uricase conjugate was purified by diafiltration to remove excess polymer and unreacted uricase. The second conjugation step was performed by mixing sulfhydryl-terminated poly (PEGMA) with poly (ZPS)-uricase. The poly (ZPS) and poly (PEGMA) modified uricases were purified by diafiltration to remove excess polymer.

[0391] The representative bioconjugate described in this example has the following structure:

[0392]

[0393]

[0394]

[0395] Example 6

[0396] Immunogenicity of representative neutral PS-PEG bioconjugates

[0397] In this example, the immunogenicity of a representative neutral PS-PEG bioconjugate was compared to that of a representative PEG-uricase.

[0398] PEG-uricase and PS-simulated polymer-PEG-uricase of 25U / kg body weight dose were intravenously administered to rats via the tail vein. The administration of the uricase sample was repeated five times, with a time interval of one week between each immunization. At the end of the fifth week (the 35th day), all rats were euthanized. Rats were killed and the rat blood collected by cardiac puncture was processed to perform direct ELISA tests. For ELISA tests, although the detection of anti-uricase antibodies uses coated uricase as an antigen, the detection of anti-PEG antibodies requires BSA-PEG conjugates.

[0399] As the first step of direct ELISA test, 100 μL antigen solution (protein concentration of 10 μg / mL) prepared in coating buffer (0.1M sodium carbonate buffer, pH 10.5) was used to coat each well of a 96-well plate. After overnight coating at 4°C, the plate was washed five times with PBS buffer (pH 7.4) to remove the antigen solution, and then filled with blocking buffer (0.1M Tris buffer solution of 1% BSA, pH 8.0), incubated at room temperature for 1 hour, and then the blocking buffer was removed. All wells were then washed five times with PBS buffer. Subsequently, serial dilutions of rat serum in PBS buffer containing 1% BSA were added to the plate (100 μL / well), incubated for 1 hour at 37°C, then rat serum was removed, and all wells were washed 5 times with PBS buffer. Next, goat anti-rat IgM or IgG (HRP conjugated, Bethyl Laboratories) was added to each well as a secondary antibody and incubated for another 1 hour at 37°C. Subsequently, all wells were washed five times with PBS buffer, and then 100 μL / well of HRP substrate 3,3′,5,5′-tetramethylbenzidine (TMB; Bethyl Laboratories) was added. The plate was shaken for 15 minutes, and 100 μL of stop solution (0.2 MH 2 SO 4 ) was added to each well. The absorbance at 450 nm (signal) and 570 nm (background) was recorded using a microplate reader. Rat serum that was not given a uricase sample was used as a negative control for all ELISA tests.

[0400] The spleen of rats was harvested and passed through a 100 μm cell strainer (Fisherbrand TM ) to isolate spleen cells. Splenocytes from rats in each group were stained with anti-rat Abs against MHCII and CD86 (eBioscience) and then analyzed by flow cytometry. To test T cell activation, splenocytes from rats in each group were cultured in 12-well plates (10 6The cells were cultured in two wells with PEG-uricase and PS-mimetic polymer-PEG-uricase (1 mg / ml). After 72 hours, the cell culture medium from each well was collected using an IL-4 rat ELISA kit (Life Technologies) for quantification of IL-4.

[0401] Example 7

[0402] Immunogenicity of representative ZPS, neutral PS, and PC bioconjugates

[0403] In this example, the immunogenicity of representative bioconjugates is described. The bioconjugate is a uricase conjugate. The uricase conjugate is prepared by covalently coupling (a) a zwitterionic PS (ZPS) polymer, (b) a neutral non-zwitterionic (NZPS) polymer, or (c) a phosphatidylcholine (PC) (MPC) polymer to the surface of uricase.

[0404] Briefly, AOT (120 mg) and Brij 30 (230 mg) were added to a 20 mL glass vial, and a stirring bar was added thereto. The vial was sealed with a polytetrafluoroethylene-lined septum cap and purged with dry nitrogen for 10 min. Then nitrogen-deoxygenated hexane (5 mL) was added to the vial under vigorous stirring. For the aqueous phase, uricase (1 mg) was dissolved in HEPES buffer (pH 8.5, 125 μL), to which ZPS monomer (50 mg) was added and dissolved. Dry nitrogen was bubbled through the monomer / protein solution for 2 min, and then the aqueous phase was slowly added dropwise to the organic continuous phase. phase. The vial was sonicated to form a stable microemulsion. A 20% (w / v) solution of APS in Milli-Q water (10 μL) was then added to the emulsion. After 5 minutes, polymerization was initiated by adding TEMED (6 μL) and maintained at 4 °C under rapid magnetic stirring. After 2 hours of reaction, the organic solvent was removed by a rotary evaporator, and the ZPS-uricase conjugate was precipitated and washed 3 times with THF. The ZPS-uricase conjugate was resuspended in PBS buffer and purified by high-resolution size exclusion chromatography (Sephacryl S-500HR) to remove free uricase. Finally, the conjugate was washed and concentrated 3 times with PBS (pH 7.4) using a centrifugal filter with a molecular weight cutoff of 100 kDa.

[0405] The structure of the conjugate is schematically illustrated below.

[0406]

[0407] For in vitro immunogenicity studies, DC 2.4 dendritic cells (10 5Each well (cells / well) was incubated with PBS (blank control), native uricase, ZPS-uricase, NZPS-uricase, MPC uricase conjugate (2 mU / mL) for 72 hours. At the end of the incubation period, the cells were centrifuged at 300 g for 10 minutes, and the supernatant medium was collected for cytokine (TGF-β) analysis by ELISA. The cells were harvested and washed twice with ice-cold sterile phosphate-buffered saline. The cells were labeled with anti-CD40-FITC or anti-CD80-PE and analyzed using flow cytometry. Figure 3A and 3B As shown, exposure to native uricase resulted in increased expression of the co-stimulatory markers CD40 and CD80 ( Figure 3A ), thereby reducing the number of immature dendritic cells ( Figure 3B ). In contrast, MPC-uricase, NZPS-uricase, and ZPS-uricase showed diminished effects in stimulating activation of dendritic cells, with NZPS-uricase having the least effect, followed by ZPS-uricase. Measurements of TGF-β, a typical immunosuppressive cytokine marker ( Figure 3C ) showed that although MPC-uricase did not affect the level of TGF-β, both NZPS-uricase and ZPS-uricase had a significant effect on upregulating TGF-β secretion.

[0408] For in vivo immunogenicity studies, 25 U / kg body weight of ZPS-uricase, NZPS-uricase, MPC-uricase conjugates were intravenously administered to mice via the tail vein. The administration of uricase samples was repeated three times, with a one-week interval between each immunization. Blood was collected from mice at different time points (0, 6 h, 24 h, 48 h, 72 h) and immunized with Amplex TM The uric acid / uricase kit measures enzyme activity to estimate the uricase retained in the blood. At the end of the third week (day 21), all mice were euthanized. Mice were sacrificed and their blood was collected by cardiac puncture for direct ELISA testing.

[0409] As the first step of direct ELISA test, 100 μL antigen solution (protein concentration of 10 μg / mL) prepared in coating buffer (0.1M sodium carbonate buffer, pH 10.5) was used to coat each well of a 96-well plate. After overnight coating at 4°C, the plate was washed five times with PBS buffer (pH 7.4) to remove the antigen solution, and then filled with blocking buffer (0.1M Tris buffer solution of 1% BSA, pH 8.0), incubated at room temperature for 1 hour, and then the blocking buffer was removed. All wells were then washed five times with PBS buffer. Subsequently, serial dilutions of mouse serum in PBS buffer containing 1% BSA were added to the plate (100 μL / well), incubated for 1 hour at 37°C, then the mouse serum was removed, and all wells were washed 5 times with PBS buffer. Next, goat anti-rat IgM or IgG (HRP conjugated, Bethyl Laboratories) was added to each well as a secondary antibody and incubated for another 1 hour at 37°C. All wells were then washed five times with PBS buffer before adding 100 μL / well of the HRP substrate 3,3′,5,5′-tetramethylbenzidine (TMB; Bethyl Laboratories). The plate was shaken for 15 min and 100 μL of stop solution (0.2 MH 2 SO 4 ) was added to each well. The absorbance at 450nm (signal) and 570nm (background) was recorded with a microplate reader. The mouse serum without uricase sample was used as a negative control for all ELISA tests. In addition, the mouse spleen was harvested on day 21 and filtered through a 100 μm cell strainer (Fisherbrand TM ) Splenocytes were isolated from mice in each group. Splenocytes from mice in each group were cultured in the presence of native uricase, MPC-uricase, NZPS-uricase, or ZPS-uricase for 72 h and then stained with anti-CD4-PE, anti-CD25-FITC, and anti-Foxp3-Percep antibodies for analysis by flow cytometry.

[0410] like Figure 4A and 4B As shown in Table 1, uricase conjugated to MPC, an inert zwitterionic polymer, suffered accelerated blood clearance (ABC) after three doses.

[0411] Table 1. Pharmacokinetic parameters after repeated injections.

[0412]

[0413] Production of anti-uricase or anti-conjugate antibodies ( Figure 4C and 4D) is the cause of the ABC phenomenon that occurs with native uricase and MPC-uricase conjugates. In contrast, both zwitterionic PS (ZPS) polymers and non-zwitterionic PS (NZPS) polymers can suppress the potential immune response caused by the immunogenic protein carrier (uricase). This immunosuppression leads to the absence of anti-conjugate antibodies ( Figure 4C and 4D ), thus maintaining the circulation time of the uricase conjugate after repeated administration (Table 1). The circulation time of NZPS-uricase was much shorter than that of ZPS-uricase, suggesting that the "eat-me" signal of the PS head group in NZPS may lead to rapid clearance, which is not conducive to increasing the retention time of the protein in vivo. In contrast, the circulation time of ZPS-uricase was comparable to that of MPC-uricase, indicating that ZPS, like other zwitterionic substances, prolongs the circulation time of the protein while retaining the immunosuppressive effect of PS, thereby suppressing the immunogenicity of the protein. This unique property of ZPS makes it particularly suitable for nanoparticles (such as protein conjugates, liposomes, micelles, and solid nanoparticles such as gold, quantum dots, silica, and iron oxide nanoparticles) because it achieves both long circulation and low immunogenicity. In addition, characterization of mouse spleen cells confirmed that NZPS-uricase and ZPS-uricase conjugates can upregulate the expression of T-rege cells ( Figure 4E and 4F ), because they avoid undesirable immune responses.

[0414] While illustrative embodiments have been shown and described, it will be appreciated that various changes can be made therein without departing from the spirit and scope of the invention.

Claims

1. A particle having micrometer or nanometer dimensions comprising one or more zwitterionic phosphatidylserine polymers coupled to the particle.

2. The particle of claim 1, wherein the particle has a micrometer size.

3. The particle of claim 1, wherein the particle has nanoscale dimensions.

4. The particle of any one of claims 1-3, wherein the particle is a biomolecule.

5. The particle of claim 4, wherein the biomolecule is a protein, a nucleic acid, a glycoprotein, a lipid, or a proteoglycan.

6. The particle of claim 4, wherein the biomolecule is a protein selected from the group consisting of an enzyme, a signaling protein, a hemostatic or thrombotic protein, a vaccine, a complement system protein, or an antibody or a functional fragment or characteristic portion thereof.

7. The particle of claim 4, wherein the biomolecule is a small molecule therapeutic agent.

8. The particle of any one of claims 1-3, wherein the particle is a drug delivery vehicle.

9. The particle of claim 8, wherein the drug delivery vehicle is a micelle, a liposome, or a polymer vesicle.

10. The particle of any one of claims 1-3, wherein the particle is a cell, a virus, or a bacterium.

11. The particle of any one of claims 1-3, wherein the particle is a hydrogel.

12. The particle of claim 11, wherein the hydrogel is a microgel or a nanogel.

13. The particle of any one of claims 1-3, wherein the particle is a metal, a metal oxide, a ceramic, a synthetic polymer, a natural polymer, a crystal, a semiconductor material, graphene, graphene oxide, iron oxide or silicon dioxide, or a quantum dot.

14. The particle of any one of claims 1-13, wherein the one or more zwitterionic phosphatidylserine polymers are grafted from the particle.

15. The particle of any one of claims 1-13, wherein the one or more zwitterionic phosphatidylserine polymers are grafted to the particle.

16. The particle of any one of claims 1-13, wherein the one or more zwitterionic phosphatidylserine polymers have repeating units of the formula: in * indicates the point of attachment of a repeating unit to other repeating units in a polymer or copolymer, or the end group of a polymer or copolymer; B is the polymer main chain; L2 is a linking group selected from the following: -(CH2) x -、-C(=O)NH(CH2) x -、-C(=O)O(CH2) x -、-C(=O)OC(=O)O(CH2) x -、-(CH2) x -O-(CH2) x - and -(CH2) x -SS-(CH2) x -, wherein x at each occurrence is an integer independently selected from 1 to 20; R2 and R3 are independently selected from hydrogen, C1-C 20 Alkyl and C6-C 12 Aryl; m is an integer from 1 to 20; p is an integer from 1 to 20; and n is an integer from about 10 to about 500.

17. The particle of any one of claims 1-13, wherein the one or more zwitterionic phosphatidylserine polymers have repeating units of the formula: in * indicates the point of attachment of a repeating unit to other repeating units in a polymer or copolymer, or the end group of a polymer or copolymer; R1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C1-C 20 Alkyl and C6-C 12 Aryl; R2 and R3 are independently selected from hydrogen, C1-C 20 Alkyl and C6-C 12 Aryl; R4 and R5 are polymerizable residues of polymerizable functional groups; L is C or Si; L2 is a linking group selected from the following: -(CH2) x -、-C(=O)NH(CH2) x -、-C(=O)O(CH2) x -、-C(=O)OC(=O)O(CH2) x -、-(CH2) x -O-(CH2) x - and -(CH2) x -SS-(CH2) x -, wherein x at each occurrence is an integer independently selected from 1 to 20; L3 and L4 are independently selected from -(CH2)x -、-C(=O)NH(CH2) x -、-C(=O)O(CH2) x -、-C(=O)OC(=O)O(CH2) x -、-(CH2) x -O-(CH2) x - and -(CH2) x -SS-(CH2) x -, wherein x at each occurrence is an integer independently selected from 0 to 20; m is an integer from 1 to 20; p is an integer from 1 to 20; and n is an integer from about 10 to about 500.

18. A method of rendering a particle immunosuppressive comprising covalently coupling one or more zwitterionic phosphatidylserine polymers to the particle.

19. A substrate surface having one or more zwitterionic phosphatidylserine polymers covalently coupled thereto.

20. A particle having micrometer or nanometer dimensions comprising one or more neutral (non-zwitterionic) phosphatidylserine polymers covalently coupled to the particle.

21. A method of rendering a particle immunosuppressive comprising covalently coupling one or more neutral (non-zwitterionic) phosphatidylserine polymers to the particle.

22. A substrate surface having covalently coupled thereto one or more neutral (non-zwitterionic) phosphatidylserine polymers.

23. A ZPS monomer comprising a polymerizable moiety covalently coupled to a zwitterionic phosphatidylserine moiety.

24. A ZPS monomer having the formula: in R1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C1-C 20 Alkyl and C6-C 12 Aryl; R2 and R3 are independently selected from hydrogen, C1-C 20 Alkyl and C6-C 12 Aryl; R4 and R5 are independently selected from functional groups suitable for polymerization by addition, condensation or free radical polymerization; L is C or Si; L2 is independently selected from -(CH2) x -、-C(=O)NH(CH2) x -、-C(=O)O(CH2)x -, wherein x is an integer from 1 to 20; L3 and L4 are independently selected from -(CH2) x -、-C(=O)NH(CH2) x -、-C(=O)O(CH2) x -、-C(=O)OC(=O)O(CH2) x -、-(CH2) x -O-(CH2) x - and -(CH2) x -SS-(CH2) x -, wherein x at each occurrence is an integer independently selected from 0 to 20; m is an integer from 1 to 20; and p is an integer of 1 to 20.

25. A ZPS polymer or copolymer having repeating units, wherein one or more of the repeating units comprises a zwitterionic phosphatidylserine moiety.

26. A ZPS polymer or copolymer having repeating units of the formula: in * indicates the point of attachment of a repeating unit to other repeating units in a polymer or copolymer, or the end group of a polymer or copolymer; B is the polymer main chain; L2 is a linking group that connects the ZPS part to the main chain, and representative groups include -(CH2) x -、-C(=O)NH(CH2) x -、-C(=O)O(CH2) x -、-C(=O)OC(=O)O(CH2) x -、-(CH2) x -O-(CH2) x - and -(CH2) x -SS-(CH2) x -, wherein x at each occurrence is an integer independently selected from 1 to 20; R2 and R3 are independently selected from hydrogen, C1-C 20 Alkyl and C6-C 12 Aryl; m is an integer from 1 to 20; p is an integer from 1 to 20; and n is an integer from about 10 to about 500.

27. A ZPS polymer or copolymer having repeating units of the formula: in * indicates the point of attachment of a repeating unit to other repeating units in a polymer or copolymer, or the end group of a polymer or copolymer; R1 is selected from hydrogen, fluorine, trifluoromethyl, cyano, C1-C 20 Alkyl and C6-C 12 Aryl; R2 and R3 are independently selected from hydrogen, C1-C 20 Alkyl and C6-C 12 Aryl; R4 and R5 are independently selected from the polymeric residues of functional groups suitable for polymerizing by addition, condensation or free radical polymerization; L is C or Si; L2 is independently selected from -(CH2) x -、-C(=O)NH(CH2) x -、-C(=O)O(CH2) x -, wherein x is an integer from 1 to 20; L3 and L4 are independently selected from -(CH2) x -、-C(=O)NH(CH2) x -、-C(=O)O(CH2) x -、-C(=O)OC(=O)O(CH2) x -、-(CH2) x -O-(CH2) x - and -(CH2) x -SS-(CH2) x -, wherein x at each occurrence is an integer independently selected from 0 to 20; m is an integer from 1 to 20; p is an integer from 1 to 20; and n is an integer from about 10 to about 500.

Images