METHOD FOR JOINING FLEXIBLE FILMS AND DEVICE FOR IMPLEMENTING THEM

Description

[0001] The present invention refers to a process for bonding flexible films by converting the surface of a first film into a softened state before contacting the softened surface with a second film, and to a device for carrying out the inventive process.

[0002] Methods for bonding flexible films are known to the person skilled in the art, covering a wide variety of different embodiments and adhesives. In most cases, bonding the films to one another requires a substantial amount of adhesive to ensure that the films are completely bonded and delamination is avoided. However, in light of the ongoing discussion of sustainability and conserving natural resources, attempts have been made to reduce the amount of adhesive needed in laminating flexible films.

[0003] US 5,250,610 discloses a composite which is produced by a process which includes applying an aqueous polyurethane dispersion based on a high molecular weight polyhydroxyl component containing carboxylic acid groups and an organic polyisocyanate to the surface of a material or workpiece and contacting said surface with the surface of another material or workpiece. By using the special aqueous polyurethane dispersion, the amount of adhesive can be reduced to 1.5 g / m 2< .

[0004] WO 97 / 03821 describes a process for preparing a laminate wherein a fluid adhesive, the curing of which is accelerated by a catalyst, is applied to a first solid film, whereupon a secondary solid or fluid film, consisting totally or partially of plastic material, is contacted herewith, the latter film containing the catalyst for accelerating the curing of the adhesive. The amount of adhesive applied is 1.5 g / m 2< .

[0005] However, by reducing the amount of adhesive, apart from risking delamination, the risk that air bubbles are trapped during the process increases. Such trapped air bubbles can be visually perceptible in the resulting composite body, especially in cases where transparent films are used, thereby negatively affecting the optical and mechanical performance of the obtained product. Further, in most cases the adhesive not only acts as a bond between the substrates but also compensates any irregularities in the surfaces of the substrates to be bonded. If the amount of adhesive is reduced, it is therefore necessary to find alternative ways of smoothing the surfaces of the substrates before bonding. One way to smooth the surface of a given substrate is to heat said surface in order to smooth out any irregularities.

[0006] US 2015 / 0140307 discloses a method for adhesively bonding two substrates, the method comprising applying an adhesive onto a first substrate, bringing the first substrate with the applied adhesive together with a second substrate made of a thermoplastic and converting the surface of the second substrate into a softened state by heating, wherein the substrates are adhesively bonded to one another before, during and / or immediately after heating by means of pressure. The adhesive is applied in a coating weight of 2 g / m 2< or less.

[0007] However, although the surface is smoothed, heating is usually accompanied by deformation of the heated substrate, in particular stretching, so that the resulting composite body is twisted and distorted.

[0008] US 2017 / 0203543 addresses the above problem by providing a method for adhesively bonding two substrates, the method comprising (i) transporting a first film-shaped substrate containing at least one thermoplastic on at least one supporting conveyer belt through a heating zone in which the substrate is heated so that the surface of the first substrate is transformed into a softened state; (ii) bringing the first substrate together with a second substrate, wherein the surface of the second substrate has been coated with an adhesive at a coating weight of 0.01 to 4 g / m 2< , during and / or immediately after the heating; and (iii) adhesively bonding the two substrates by pressure.

[0009] The process described in the prior art employing a supporting conveyer belt in order to minimize deformation of the heated substrate film still suffers from the drawback that special care has to be taken with regard to the speed with which the conveyer belt is operated. Further, although deformation in a longitudinal direction may be reduced, the problem of deformation in a transversal direction has not been addressed.

[0010] It is therefore the object of the present invention to provide a process which allows lamination of flexible film without risking deformation of the films during lamination.

[0011] It was surprisingly found that the above object is solved by a process wherein the heating of the film is effected by a heating device including at least one heatable roller.

[0012] A first object of the present invention is therefore a process for laminating flexible films, the process comprising: i) providing at least one lamination roller and a heating device, the lamination roller being arranged behind the heating device along a process direction, ii) providing a first film having a thermoplastic surface, iii) providing a second film, iv) bringing the first film and the second film together by means of pressure wherein the thermoplastic surface of the first film is converted into a softened state by means of heating before being brought together with the second film; wherein heating of the surface of the first film is effected by the heating device, which heating device includes at least one heatable roller, wherein the means for bringing the first film into contact with the second film comprises the lamination roller, and wherein the surface of the second film is coated with an adhesive, wherein the adhesive is applied to the second film at a coating weight of less than 2 g / m2.

[0013] By effecting the heating of the surface of the film by means of at least one heatable roller, complicated heating by means of radiators or hot air is avoided. Further, it was surprisingly found that heating efficiency is much more enhanced by directly contacting the thermoplastic surface of the film with a heating roller. In addition, an additional smoothing of the surface was observed, believed to be caused by the direct contact of the thermoplastic film with the surface of the roller. Also, by including the means for heating the surface into the transportation system of the film, the speed with which the film is transported could be increased without risk of longitudinal and transversal deformation of the film.

[0014] In a preferred embodiment, the heating of the thermoplastic surface of the first film is effected by a heating device including an assembly of heatable rollers, the assembly preferably including 1 to 10, especially 1 to 5, heatable rollers which are preferably arranged in horizontal succession relative to the process direction. The thermoplastic surface of the first film is converted into a softened state by means of the heating device. However, care should be taken that the surface is not overheated in order to avoid damage to the film. In this regard, it is desirable to control the input of energy during heating without interrupting the process. It was surprisingly found that the energy input may be controlled by adjusting the distance between the heatable rollers and the first film. In a preferred embodiment, each of the at least one heatable roller is therefore individually controllable, allowing to adjust the distance of the heatable rollers and the first film by, for example, removing one or more of the heatable rollers from contact with the first film. It was surprisingly found that this procedure allows for individual and easy adjustment during heating of the thermoplastic surface. The temperature of the at least one heatable roller may adjusted in accordance with the softening point of the thermoplastic surface of the first film. The softening point of any given thermoplastic material may be determined according to a number of methods, for example by heat deflection (ASTM D648) or according to the method of ring & ball (ISO 4625). The softening temperature of commonly used thermoplastics is summarized in pertinent tables. In a preferred embodiment, the at least one heatable roller has a temperature of 80 to 300 °C, preferably 110 to 200 °C. In embodiments where more than one heatable roller is used, the temperature of each heatable roller may be controlled individually. This way, the temperatures of the heatable rollers may differ from each other. Therefore, in a preferred embodiment, each of the heatable rollers has the same or a different temperature.

[0015] Further, the diameter of the at least one heatable roller may be chosen according to need. In a preferred embodiment, the at least one heatable roller has a diameter of 10 to 250 cm, preferably 50 to 100 cm.

[0016] In the course of the present invention, it was surprisingly found that deformation of the heated film can be avoided without the need for cooling. Rather, the temperature of the film can be controlled by individually adjusting the temperature of each heatable roller, resulting in an improved balance of energy. Further, by adjusting the speed of the heatable rollers individually, additional means of control are provided. In a preferred embodiment, each of the heatable rollers is therefore actively driven. Further preferred is an embodiment wherein each of the heatable rollers is actively driven and addressed individually.

[0017] In a preferred embodiment of the inventive process, the first film is led through a series of rollers which are arranged on both sides of the film wherein each roller is individually adjustable in order to bring the surface of the roller into contact with the film. Preferably, the set of rollers is operated in a way that neighboring rollers have opposite direction of rotation. At least the rollers facing the thermoplastic surface of the first film are heatable rollers to transfer the thermoplastic surface of the film into a softened state. It was found that by individually adjusting the rollers, the contact area between the rollers and the film may be adapted according to need, allowing a precise adjustment of the energy input of the thermoplastic surface. The rollers are preferably adjustable in a linear and / or non-linear way.

[0018] The inventive process is especially designed for bonding flexible films which may, for example be used in the production of food packaging. In a preferred embodiment, the first film comprises or is made of a material selected from polyolefins such as polyethylene and polypropylene, polyvinyl chloride, ethylene copolymers such as ethylene-vinyl-acetate, ethylene-acrylate copolymers, ethylene-methyl methacrylate copolymer and ethylene-acrylic acid copolymer, polyesters, polylactides, polyamides and ionomers. In an especially preferred embodiment, the first film comprises or is made of polyethylene, polypropylene or mixtures thereof.

[0019] In a preferred embodiment, the second film comprises or is made of a material selected from metals such as aluminum, iron, and zinc, metal alloys such as bronze and aluminum alloys, thermosetting or thermoplastic plastics such as polyethylene, polypropylene, polyvinyl chloride, polystyrene, acrylonitrile-butadiene-styrene copolymers, polyesters and polyamides, organic polymers such as cellophane, paper and cardboard, textiles and non-woven materials.

[0020] The surface of the second film is coated with an adhesive to further increase the bond strength between the first film and the second film. Due to the inventive heating of the first film, the amount of adhesive necessary for bonding the films can be significantly reduced. The adhesive is applied to the surface of the second film at a coating weight of less than 2 g / m 2< , preferably less than 1 g / m 2< , especially 0.01 to 0.7 g / m 2< . It was surprisingly found that although reduced amounts of adhesive were used, no delamination of the product was observed. In contrast, the bonded films showed an excellent bond strength making them suitable for a wide variety of applications. Any suitable adhesive may be used in the inventive process. However, in a preferred embodiment, the adhesive employed in the inventive process is selected from thermoplastic adhesives or cross-linkable adhesives in solvent-containing, aqueous or solvent-free form. Further preferred is an embodiment wherein the adhesive is based on thermoplastic polymers such as polyurethanes, ethylene-vinyl-acetate, solvent-containing adhesives such as acrylate adhesives, one- or two-component polyurethane adhesives, silane-crosslinking adhesives, reactive adhesives such as one-component polyurethane adhesives, solvent-free one- or two-component polyurethane adhesives, silane systems or radiation cross-linkable systems.

[0021] Another object the present invention is a device for carrying out the process according to the invention. The device according to the invention includes a) a feeding device for supplying a first film having a thermoplastic surface; b) a feeding device for supplying a second film, wherein the surface of the second film is coated with an adhesive and wherein the adhesive is applied to the second film at a coating weight of less than 2 g / m2; c) a heating device for heating the thermoplastic surface of the first film to transform the thermoplastic surface into a softened state; d) at least one lamination roller for contacting the first film and second film; and e) an output device for dispensing the joint first and second films wherein the heating device includes at least one heatable roller and each of the heatable rollers included in the heating device is individually controllable wherein the rollers are individually adjustable, preferably in a linear and / or non-linear way, wherein the or each lamination roller is arranged behind the heating device along a process direction.

[0022] The set-up of the inventive device allows for an individual adjustment of the speed with which the film is transported. In a preferred embodiment, the rollers are therefore actively driven.

[0023] It was surprisingly found that deformation of the heated film can be avoided by carefully controlling the energy input during the heating process. In a preferred embodiment, the at least one heatable roller included in the inventive device is therefore individually controllable.

[0024] In a preferred embodiment of the inventive device, the device comprises a series of rollers which are arranged on both sides of the film wherein each roller is individually adjustable in order to bring the surface of the roller into contact with the film. Preferably, the set of rollers is operated in way that neighboring rollers have opposite direction of rotation. At least the rollers facing the thermoplastic surface of the first film are heatable rollers to transfer the thermoplastic surface of the film into a softened state. It was found that by individually adjusting the rollers, the contact area between the rollers and the film may be adapted according to need, allowing a precise adjustment of the energy input of the thermoplastic surface and eliminating the need for additional cooling. The rollers are preferably adjustable in a linear and / or non-linear way.

[0025] In a preferred embodiment, the inventive device further includes means for coating the surface of the second film with an adhesive.

[0026] The inventive device includes means for contacting the first film having a thermoplastic surface, the surface being in a softened state, and the second film. The means for contacting the first and second films includes at least one lamination roller for pressing the second film against the softened surface of the first film.

[0027] The lamination roller is arranged behind the heating device along the process direction. In a particular preferred embodiment, the lamination roller is arranged in close proximity to the at least one heatable roller. In a preferred embodiment contacting of the first and the second film is realized by leading the films between the at least one heatable roller and the lamination roller.

[0028] Any of the components of the inventive device may be operated in a way that ensures fast and efficient production. In a preferred embodiment, the first film is transported with 0.5 to 1.5 times, preferably 0.9 to 1.1 times the speed of the second film. Further, the speed of the at least one heatable roller may be adapted relative to the speed of the first and / or second film according to need.

[0029] The inventive process and the inventive device are especially designed for laminating flexible films. A further object of the present disclosure, however not within the scope of the claimed invention, is a composite body obtained by the process according to the invention or the device according to the invention. In case the inventive process is carried out using an adhesive, the composite body is especially distinguished by the thin layer of adhesive between the films. The adhesive layer preferably has a thickness of less 5 µm, preferably less than 2 µm and especially less than 1 µm.

[0030] The present invention is described in more detail by reference to the following figures which are by no means to be understood as limiting the scope of the invention. Figures 1 and 2 show an embodiment of the present invention wherein a set of rollers is adjustable in a linear way is arranged in either side of the first film. Figure 1 shows an embodiment wherein the inventive device is in an idle state and Figure 2 shows the inventive device in a working state. A film (9) having a thermoplastic surface is led through a series of rollers (1,2) in which at least one of the rollers is a heatable roller to transfer the thermoplastic surface of the film into a softened state. Contact of the rollers (1,2) to the film is established by adjusting the rollers along an axis (5). This allows the contact area between the film and the rollers to be adapted according to need. After being led through the series of rollers, the first film (9) is brought into contact with the second film (10) in a way that the surface of the second film (10) is contacted with the thermoplastic surface of the first (9) which is in a softened state. Contacting is performed by way of lamination roller (7) to obtain the laminated product (11).

[0031] Figures 3 and 4 show an embodiment of the present invention wherein a set of rollers is adjustable in a non-linear way, Figure 3 showing the inventive device in an idle state while Figure 4 shows the inventive device in a working state. A film (9) having a thermoplastic surface is led through a series of rollers (1,2) in which at least one of the rollers is a heatable roller to transfer the thermoplastic surface of the film into a softened state. Contact of the rollers (1,2) to the film is established by adjusting the rollers along an axis (5). This allows the contact area between the film and the rollers to be maximized for achieving a high degree of efficiency. After being led through the series of rollers, the first film (9) is brought into contact with the second film (10) in a way that the surface of the second film (10) is contacted with the thermoplastic surface of the first (9) which is in a softened state. Contacting is performed by way of lamination roller (7) to obtain the laminated product (11).List of reference signs:

[0032] 1 upper roller 2 lower roller 3 contact area 4 direction of rotation 5 movement of axis 6 front pulley 7 lamination roller 8 axis 9 first film 10 second film 11 laminate

Claims

1. Process for laminating flexible films, the process comprising: i) providing at least one lamination roller and a heating device, the lamination roller (7) being arranged behind the heating device along a process direction, ii) providing a first film (9) having a thermoplastic surface, iii) providing a second film (10), iv) bringing the first film and the second film together by means of pressure wherein the thermoplastic surface of the first film is converted into a softened state by means of heating before being brought together with the second film; wherein heating of the surface of the first film is effected by the heating device, which heating device includes at least one heatable roller (1, 2), wherein the means for bringing the first film into contact with the second film comprises the lamination roller, and wherein the surface of the second film (10) is coated with an adhesive, wherein the adhesive is applied to the second film at a coating weight of less than 2 g / m2.

2. Process according to claim 1, characterized in that heating of the thermoplastic surface of the first film is effected by a heating device including an assembly of 1 to 10, preferably 1 to 5, heatable rollers (1, 2).

3. Process according to any of the forgoing claims characterized in that each of the at least one heatable roller (1, 2) is individually controllable.

4. Process according to any of the forgoing claims characterized in that the first film (9) comprises or is made of a material selected from polyolefins, polyvinyl chloride, ethylene copolymers, polyesters, polylactides, polyamides and ionomers.

5. Process according to any of the forgoing claims characterized in that the second film (10) comprises or is made of a material selected from metals, metal alloys, thermosetting or thermoplastic plastics, organic polymers, textiles and non-woven materials.

6. Process according to claim 1, characterized in that the adhesive is applied to the second film at a coating weight less than 1 g / m2, especially 0.01 to 0.7 g / m2.

7. Device, wherein the device comprises a) a feeding device for supplying a first film (9) having a thermoplastic surface; b) a feeding device for supplying a second film (10), wherein the surface of the second film is (10) is coated with an adhesive and wherein the adhesive is applied to the second film at a coating weight of less than 2 g / m2; c) a heating device for heating the thermoplastic surface of the first film (9) to transform the thermoplastic surface into a softened state; d) at least one lamination roller (7) for contacting the first film (9) and second film (10); and e) an output device for dispensing the joint first and second films wherein the heating device includes at least one heatable roller (1, 2) and each of the the heatable rollers (1, 2) included in the heating device is individually controllable wherein the rollers (1,2) are individually adjustable, preferably in a linear and / or non-linear way, and wherein the or each lamination roller is arranged behind the heating device along a process direction.

8. Device according to any of the claims 7 characterized in that each roller (1,2) is actively driven.

9. Device according to any of the claims 7 or 8 characterized in that the at least one lamination roller is arranged in close proximity to the at least one heatable roller (1,2).