Sample supporting body and method for manufacturing sample supporting body

Abstract

To provide a sample supporting body and a method for manufacturing the sample supporting body which can effectively improve the sensitivity of detecting a component of a sample.SOLUTION: A sample supporting body 1 includes a sample supporting body for ionizing a sample Sa. The sample supporting body 1 includes a substrate 2 having a first surface 2a, a second surface 2b on the opposite side to the side where the first surface 2a is formed, and an irregular porous structure 3 at least having an opening in the first surface 2a. The porous structure 3 is formed of a plurality of particles 31 connected to one another. A particle 31A forming the first surface 2a of the plurality of particles 31 has a rough surface 31a where an uneven structure 4 is formed on the first surface 2a side and a non-rough surface 31b where the uneven structure 4 is not formed in the second surface 2b side.SELECTED DRAWING: Figure 2

Description

[Technical field]

[0001] The present disclosure relates to a sample support and a method for manufacturing the sample support. [Background technology]

[0002] Desorption electrospray ionization (DESI) is known as a method for ionizing a sample such as a biological sample. As a sample support suitable for such desorption electrospray ionization, a sample support is known that includes a substrate having a first surface, a second surface opposite to the first surface, and an irregular porous structure that opens at least to the first surface (see, for example, Patent Document 1). In the above sample support, for example, a sample transferred onto the first surface is irradiated with charged droplets, thereby desorbing and ionizing the sample. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] JP 2022-43571 A Summary of the Invention [Problem to be solved by the invention]

[0004] In the above-mentioned sample support, there is a demand for improved detection sensitivity of sample components in mass spectrometry and the like using an ionization method such as the above-mentioned desorption electrospray ionization method.

[0005] An object of the present disclosure is to provide a sample support capable of effectively improving the detection sensitivity of sample components, and a method for manufacturing the sample support. [Means for solving the problem]

[0006] The present disclosure includes the following sample supports [1] to [7] and a method for producing a sample support [8].

[0007] [1] A sample support for ionization of a sample, comprising: a substrate having a first surface, a second surface opposite the first surface, and an irregular porous structure opening to the first surface; the porous structure is formed by a plurality of first particles connected to each other; A sample support, wherein an outermost first particle among the plurality of first particles constituting the first surface has a rough surface on the first surface side on which a concave-convex structure is formed, and a non-rough surface on the second surface side on which the concave-convex structure is not formed.

[0008] In the sample support of [1] above, the outermost first particles (i.e., the first particles located in the outermost layer on the first surface side) constituting the first surface among the plurality of first particles constituting the porous structure have a rough surface on the first surface side where a concave-convex structure is formed. By providing such a concave-convex structure, the sample to be measured can be suitably retained on the rough surface. On the other hand, the surface opposite to the rough surface of the outermost first particles is a non-rough surface on which a concave-convex structure is not formed. This allows excess liquid components contained in the sample to suitably permeate from the first surface side to the second surface side. As a result, it is possible to suppress the measurement (ionization of the sample components remaining on the first surface) being hindered by the excess liquid components overflowing onto the first surface. Therefore, according to the sample support of [1] above, it is possible to efficiently ionize the sample components remaining on the first surface, and therefore it is possible to effectively improve the detection sensitivity of the sample components.

[0009] [2] the porous structure further comprises a plurality of second particles, each of the second particles having a smaller diameter than the first particles; The sample support according to [1], wherein at least a portion of the plurality of second particles are held by being sandwiched between two or more of the outermost first particles.

[0010] In the above configuration [2], the porous structure is configured to include not only a plurality of first particles, but also second particles sandwiched and held between two or more outermost first particles. This makes it possible to reduce the gaps of the sample support on the first surface (i.e., spaces where no particles constituting the porous structure exist) when the sample support is viewed from a position facing the first surface. Also, on the first surface, not only the joints between the first particles but also the joints between the first particles and the second particles and the joints between the second particles are added. This makes it possible to more effectively retain the sample to be measured on the first surface (especially on the joints described above). As a result, it is possible to more effectively improve the detection sensitivity of the components of the sample.

[0011] [3] The sample support of [2], wherein an outermost second particle among the plurality of second particles constituting the first surface has a rough surface on the first surface side on which the unevenness structure is formed, and a non-rough surface on the second surface side on which the unevenness structure is not formed.

[0012] According to the above configuration [3], not only the outermost first particles but also the surfaces on the first surface side of the outermost second particles located between two or more outermost first particles are configured as rough surfaces, so that the sample to be measured can be more suitably retained on the first surface, and as a result, the detection sensitivity of the sample components can be more effectively improved.

[0013] [4] The sample support of [2], wherein the uneven structure is not formed on either the face on the first surface side or the face on the second surface side of the outermost second particle that constitutes the first surface among the plurality of second particles.

[0014] The above-mentioned configuration [3] can be obtained, for example, by carrying out the same treatment as the surface roughening treatment on the surface of the first particle on the surface of the second particle (the surface on the first surface side) that is smaller than the first particle. Here, since the second particle is smaller and more brittle than the first particle, there is a risk that the second particle will be crushed in the above-mentioned surface roughening treatment. As a result, there is a risk that the effect of the above-mentioned [2] will be reduced. In contrast, according to the above-mentioned configuration [4], the surface roughening treatment is carried out only on the surface of the first particle, so that the above-mentioned problems can be avoided.

[0015] [5] The substrate is a first layer including the first surface and including a plurality of the first particles and a plurality of the second particles; The sample support according to any one of [2] to [4], further comprising: a second layer located closer to the second surface than the first layer, the second layer being made of a plurality of the first particles and not containing the second particles.

[0016] In the configuration of [5] above, a first layer containing a mixture of first and second particles is provided to facilitate retention of the sample on the first surface, while a second layer that does not contain second particles and thus allows liquid to pass through more easily than the first layer is provided below the first layer (on the second surface side). This makes it possible to prevent the overflow of excess liquid components onto the first surface, which would otherwise interfere with the measurement (ionization of the sample components remaining on the first surface), when a sample to be measured that contains liquid components is transferred or dropped onto the first surface of the sample support.

[0017] [6] The sample support according to any one of [1] to [5], wherein the particles constituting the second surface among the plurality of first particles have a rough surface on the second surface side on which a concave-convex structure is formed, and a non-rough surface on the first surface side on which no concave-convex structure is formed.

[0018] According to the configuration of [6] above, it becomes possible to use both the first surface and the second surface as a measurement surface (i.e., a surface supporting a sample to be measured) that exerts the effect of [1] above. This improves convenience because a user (measurer) of the sample support does not need to specify which surface of the sample support is the measurement surface when transferring or dropping a sample to be measured onto the sample support.

[0019] [7] The sample support according to any one of [1] to [6], further comprising a conductive layer that does not block the openings of the porous structure on the first surface and covers the first surface along the surface shape of the uneven structure of the outermost first particle.

[0020] According to the configuration [7] above, it becomes possible to use the sample support for laser desorption ionization etc., without impairing the effect of [1] above. More specifically, when using laser desorption ionization etc., that is, when it is necessary to apply a voltage to the first surface to guide the components of the sample ionized on the first surface to the ion detector (ground electrode), it becomes possible to apply a voltage appropriately via the conductive layer.

[0021] [8] A method for producing a sample support according to any one of [1] to [7], a sintering step of sintering the plurality of first particles to obtain a sintered body having substantially the same outer shape as the substrate; and a roughening step of performing a roughening treatment on a surface of the sintered body corresponding to the first surface to form a plurality of the outermost first particles, each of which has a rough surface formed on the first surface side.

[0022] According to the manufacturing method [8] above, by sequentially carrying out a sintering treatment and a surface roughening treatment on a plurality of first particles, a sample support having the effect [1] above can be easily and stably obtained. Effect of the Invention

[0023] According to the present disclosure, it is possible to provide a sample support that can effectively improve the detection sensitivity of sample components, and a method for manufacturing the sample support. [Brief description of the drawings]

[0024] [Figure 1] FIG. 2 is a perspective view showing an embodiment of a sample support. [Diagram 2] 2 is an SEM image of region A shown in FIG. 1. [Diagram 3] FIG. 2 is a diagram showing a schematic view of a portion of the sample support in FIG. 1 that includes outermost particles. [Figure 4] 2 is an SEM image showing a cross section of the sample support of FIG. 1. [Diagram 5] FIG. 5 is an enlarged view of a portion of the SEM image shown in FIG. [Figure 6] FIG. 2 is a diagram showing a second step in the mass spectrometry method using the sample support of FIG. [Figure 7] FIG. 2 is a diagram showing an example of the configuration of a mass spectrometer for carrying out the above-described mass spectrometry method. [Figure 8] FIG. 2 is a diagram showing an example of an irradiation area of ​​microdroplets in an example and a comparative example. [Figure 9] FIG. 13 is a diagram showing measurement results of detection sensitivity per irradiation region in an example and a comparative example. [Figure 10] 13 is an SEM image of a part of the sample support according to the first modified example, viewed from a position facing the first surface. [Figure 11] FIG. 13 is a diagram showing a schematic example of an arrangement of particles constituting a first surface of a first modified example. [Figure 12] FIG. 4 is a diagram showing a schematic layer structure of a sample support according to a first modified example. [Figure 13] FIG. 13 is a diagram showing a schematic example of an arrangement of particles constituting a first surface of a second modified example. [Figure 14] FIG. 13 is a diagram showing a schematic layer structure of a sample support according to a third modified example. [Figure 15] FIG. 13 is a diagram showing a schematic view of a portion including an outermost particle of a sample support according to a third modified example. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0025] Hereinafter, embodiments of the present disclosure will be described in detail with reference to the drawings. In each drawing, the same or corresponding parts are denoted by the same reference numerals, and duplicated explanations will be omitted.

[0026] [Sample support] As shown in FIG. 1, the sample support 1 includes a substrate 2. As an example, the substrate 2 is formed in a rectangular plate shape. The substrate 2 has a first surface 2a and a second surface 2b opposite to the first surface 2a. The first surface 2a is insulating (electrically insulating). In this embodiment, the substrate 2 is an insulating member. Therefore, not only the first surface 2a but the entire substrate 2 is insulating. The first surface 2a functions as a measurement surface onto which a sample to be measured is transferred or dropped. The thickness of the substrate 2 (the distance from the first surface 2a to the second surface 2b) is, for example, about 100 μm to 1500 μm.

[0027] FIG. 2 is an SEM image obtained by imaging the sample support 1 (substrate 2 having a porous structure 3) from a direction facing the first surface 2a. As shown in FIG. 2, an irregular porous structure 3 that opens to the first surface 2a is formed in the substrate 2. In this embodiment, the entire substrate 2 is formed by the porous structure 3. Here, the "irregular porous structure" is, for example, a structure in which voids (pores) extend in irregular directions and are irregularly distributed in three dimensions. For example, the irregular porous structure includes a structure in which the substrate 2 enters from one inlet (opening) on ​​the first surface 2a side and branches into multiple paths, or a structure in which the substrate 2 enters from multiple inlets (openings) on the first surface 2a side and merges into one path. On the other hand, a structure in which, for example, a plurality of pores extending from the first surface 2a to the second surface 2b along the thickness direction of the substrate 2 (i.e., the direction D1 in which the first surface 2a and the second surface 2b face each other) are provided as the main pores (i.e., a regular structure composed of pores mainly extending in one direction) is not included in the irregular porous structure.

[0028] The porous structure 3 is formed by an aggregate of a plurality of particles 31 (first particles). The aggregate of a plurality of particles 31 is a structure in which the plurality of particles 31 are gathered so as to be in contact with each other. That is, the porous structure 3 is formed by a plurality of particles 31 connected to each other. An example of an aggregate of a plurality of particles 31 is a structure in which the plurality of particles 31 are bonded or adhered to each other. That is, in order to configure a structure in which the plurality of particles 31 are fixed in a state in which they are in contact with each other, the plurality of particles 31 may be directly connected to each other by fusion or the like, or may be indirectly connected to each other via another member. In this embodiment, the plurality of particles 31 are bonded to each other by fusion. In this embodiment, the particles 31 are formed of an insulating material. For example, the particles 31 are formed of glass. In this embodiment, soda glass, which has a relatively low melting point among glasses, is used as the material of the particles 31 from the viewpoint of facilitating the manufacture of the aggregate structure. In addition, the particles 31 are formed in a spherical shape. An example of such spherical particles 31 is glass beads.

[0029] As shown in Fig. 3, among the multiple particles 31, particles 31A (outermost first particles) constituting the first surface 2a have a rough surface 31a on the first surface 2a side (upper side in Fig. 3) and a non-rough surface 31b on the second surface 2b side (lower side in Fig. 3). The particles 31A constituting the first surface 2a are particles 31 located in the outermost layer on the first surface 2a side.

[0030] The rough surface 31a of the particle 31A is the surface that is seen when the substrate 2 is viewed from a position facing the first surface 2a of the substrate 2 along the direction D1 (i.e., the surface of the particle 31A shown in the SEM image of FIG. 2). A fine uneven structure 4 is formed on the rough surface 31a. The uneven structure 4 is composed of a plurality of (pointed) convex portions 4a that protrude outward and a plurality of concave portions 4b that are recessed inward. The plurality of convex portions 4a and the plurality of concave portions 4b may be formed regularly or irregularly. For example, the rough surface 31a can be formed by various known roughening treatments for roughening the surface of the particle 31A. Examples of the roughening treatment include sandblasting, laser processing, etching (dry etching), and forming using a mold. As an example, the rough surfaces 31a of the plurality of particles 31A are formed at the same time by performing a sandblasting process on the first surface 2a of the substrate 2 (i.e., the upper surfaces of the plurality of particles 31A) before the rough surfaces 31a are formed on the respective particles 31A. In this case, a concavo-convex structure 4 in which a plurality of protrusions 4a and a plurality of recesses 4b are irregularly formed is obtained.

[0031] The non-rough surface 31b of the particle 31A is a surface that is not visible when the substrate 2 is viewed in the direction D1 from a position facing the first surface 2a of the substrate 2 (i.e., the surface behind the rough surface 31a). The fine uneven structure 4 formed on the rough surface 31a is not formed on the non-rough surface 31b. In other words, the non-rough surface 31b is a smoother surface than the rough surface 31a. The non-rough surface 31b is not affected by the roughening treatment performed from the side facing the first surface 2a as described above, and has the original smooth surface shape (curved shape, hemispherical shape) of the particle 31A.

[0032] The surfaces of the particles 31 that do not constitute the first surface 2a (i.e., the particles 31 that are present further inside the substrate 2 (porous structure 3) than the particles 31A that constitute the outermost layer) are constituted by the above-mentioned non-rough surface 31b on both the first surface 2a side and the second surface 2b side. That is, the surfaces of the particles 31 that are present inside the substrate 2, like the back surface of the particles 31A (the surface on the second surface 2b side), are not affected by the above-mentioned roughening treatment and have the original smooth surface shape (curved shape, spherical shape) of the particles 31.

[0033] FIG. 4 is an SEM image showing a cross section of the sample support 1. FIG. 5 is an enlarged view of a part of the SEM image of FIG. 4. As shown in FIG. 2, FIG. 4, and FIG. 5, although there is some variation in shape and size for each particle, each of the multiple particles 31 constituting the porous structure 3 has a substantially uniform size (diameter). In addition, from the SEM images of FIG. 2 and FIG. 5, it can be seen that the upper surface of the outermost particle 31A constituting the first surface 2a is configured as a rough surface 31a having a fine uneven structure 4. In addition, from the SEM image of FIG. 5, it can be seen that the lower surface of the particle 31A is configured as a non-rough surface 31b having a smooth curved shape (hemispherical shape) that does not include the uneven structure 4. In addition, from the SEM image of FIG. 4, it can be seen that the surfaces (upper and lower surfaces) of the particles 31 present inside the substrate 2 are configured as a non-rough surface 31b similar to the lower surface of the particle 31A.

[0034] [Method of manufacturing the sample support] The sample support 1 (porous structure 3) is manufactured, for example, as follows. First, a sintered body is obtained by sintering a plurality of particles 31 (sintering step). Specifically, the plurality of particles 31 are compressed by a press or the like and heated at a high temperature below the melting point of the particles 31, so that the surfaces of the plurality of particles 31 are fused and bonded to each other, and a sintered body made of the plurality of particles 31 is obtained. The sintered body has approximately the same outer shape as the substrate 2 that is finally obtained. Next, the surface of the sintered body that corresponds to the first surface 2a (i.e., the surface that is to eventually become the first surface 2a) is subjected to the above-mentioned roughening treatment (roughening step). This allows the upper surface of each of the plurality of particles 31A to be a rough surface 31a. As a result, the above-mentioned porous structure 3 is obtained.

[0035] [Ionization method and mass spectrometry method] The ionization method and mass spectrometry method using the sample support 1 will be described. First, the above-mentioned sample support 1 is prepared as a sample support for ionizing a sample (first step). The sample support 1 may be prepared by being manufactured by the practitioner of the ionization method and mass spectrometry method, or may be prepared by being transferred from the manufacturer or seller of the sample support 1.

[0036] Subsequently, as shown in Fig. 6, the sample Sa is transferred to the first surface 2a of the substrate 2 (second step). In the example of Fig. 6, the sample Sa is a slice of fruit (lemon). For example, the sample Sa is pressed against the first surface 2a of the substrate 2 to cause a part of the sample Sa to adhere onto the first surface 2a.

[0037] 7, the slide glass 6 and the sample support 1 are placed on the stage 41 in the ionization chamber 40 of the mass spectrometer 10. Then, the component Sa1 on the first surface 2a of the substrate 2 is irradiated with the charged microdroplets I to a region (hereinafter referred to as the "target region") including the region where the transferred sample Sa exists, and the component Sa1 is ionized and the sample ion Sa2, which is the ionized component, is attracted (third step). In this embodiment, for example, the stage 41 is moved in the X-axis direction and the Y-axis direction to move the irradiation region I1 of the charged microdroplets I relative to the target region (that is, the charged microdroplets I are scanned relative to the target region). The above first step, second step, and third step correspond to the ionization method using the sample support 1 (in this embodiment, desorption electrospray ionization method).

[0038] In the ionization chamber 40, charged microdroplets I are sprayed from the nozzle 42, and sample ions Sa2 are sucked in from the suction port of the ion transport tube 43. The nozzle 42 has a double-cylinder structure. A solvent is guided into the inner cylinder of the nozzle 42 while a high voltage is applied. As a result, a one-sided charge is imparted to the solvent that has reached the tip of the nozzle 42. A nebulizing gas is guided into the outer cylinder of the nozzle 42. As a result, the solvent is sprayed as microdroplets, and solvent ions generated in the process of vaporizing the solvent are ejected as charged microdroplets I.

[0039] The sample ions Sa2 sucked in through the suction port of the ion transport tube 43 are transported into the mass spectrometry chamber 50 by the ion transport tube 43. The inside of the mass spectrometry chamber 50 is a high vacuum atmosphere (vacuum degree 10 -4The sample ions Sa2 are focused by the ion optical system 51 and introduced into the quadrupole mass filter 52 to which a radio frequency voltage is applied. When the sample ions Sa2 are introduced into the quadrupole mass filter 52 to which a radio frequency voltage is applied, ions having a mass number determined by the frequency of the radio frequency voltage are selectively passed, and the passed ions are detected by the detector 53 (fourth step). By scanning the frequency of the radio frequency voltage applied to the quadrupole mass filter 52, the mass number of the ions reaching the detector 53 is sequentially changed to obtain a mass spectrum in a predetermined mass range. In this embodiment, the detector 53 detects ions corresponding to the position of the irradiation region I1 of the charged microdroplet I, and an image of the two-dimensional distribution of the molecules constituting the sample Sa is obtained. The above first, second, third and fourth steps correspond to a mass analysis method using the sample support 1.

[0040] [Action and Effects] In the above-mentioned sample support 1, among the multiple particles 31 constituting the porous structure 3, the particles 31A constituting the first surface 2a (i.e., the particles 31 located in the outermost layer on the first surface 2a side) have a rough surface 31a on which an uneven structure 4 is formed on the first surface 2a side. By providing such an uneven structure 4, the sample Sa to be measured can be suitably held on the rough surface 31a. More specifically, the uneven structure 4 has convex parts 4a (see FIG. 5) pointed outward. The sample Sa is easily caught on the edge parts of such convex parts 4a, so that the sample Sa can be suitably held on the rough surface 31a. In addition, for example, when the sample Sa is a biological cell or the like, the convex parts 4a break the cell membrane of the sample Sa, and the component Sa1 of the sample Sa contained therein can be suitably permeated onto the surface of the rough surface 31a. In other words, the transfer efficiency can be improved when the sample Sa is brought into contact with the first surface 2a of the substrate 2 and transferred. Furthermore, the plurality of protrusions 4a and recesses 4b make the rough surface 31a less slippery than the smooth non-rough surface 31b, which results in suppressing lateral slippage of the sample Sa transferred to the rough surface 31a.

[0041] Meanwhile, the surface of the particle 31A opposite to the rough surface 31a is a non-rough surface 31b on which the concave-convex structure 4 is not formed. This allows excess liquid components contained in the sample Sa to permeate suitably from the first surface 2a side to the second surface 2b side. That is, by making the back surface (lower surface) of the particle 31A a smooth curved surface (non-rough surface 31b) that allows the liquid to permeate more smoothly than the rough surface 31a on which the concave-convex structure 4 is formed, the function of permeating the liquid into the inside of the substrate 2 can be improved. As a result, it is possible to prevent the measurement (ionization of the component Sa1 of the sample Sa remaining on the first surface 2a) from being hindered by the excess liquid components overflowing onto the first surface 2a.

[0042] For the reasons described above, the sample support 1 makes it possible to efficiently ionize the component Sa1 of the sample Sa remaining on the first surface 2a, and therefore effectively improves the detection sensitivity of the component Sa1 of the sample Sa. Furthermore, as the sample Sa is more likely to remain on the first surface 2a as described above, the area on the first surface 2a where the sample Sa stains becomes larger and the stains become darker. This improves the visibility of the sample Sa attached to the measurement surface (first surface 2a) of the sample support 1, and also makes it easier to determine the irradiation range of the microdroplets I for ionization.

[0043] The above effects will be supplemented with reference to Figs. 8 and 9. In the example of Figs. 8 and 9, a conductive layer 5 described later is provided, and laser desorption ionization is used in which ionization is performed by irradiating a laser beam instead of the microdroplet I, instead of the desorption electrospray ionization method of the above embodiment. However, Figs. 8A and 8B show the state before the conductive layer 5 is provided in the example and the comparative example. Fig. 8A shows an example of an irradiation area R of a single laser beam in the example (i.e., the sample support 1C having the conductive layer 5 described later). Fig. 8B shows an example of an irradiation area R of a single laser beam in the comparative example. The sample support according to the comparative example has a substrate (porous structure) made up of a plurality of particles 31 as in the example, but is different from the example in that the upper surface of the plurality of particles 31A constituting the first surface 2a is not roughened as the rough surface 31a.

[0044] FIG. 9 shows mass spectra obtained by performing mass analysis (laser desorption ionization) of sample Sa (Angiotensin II as an example) using each of the above-mentioned Examples and Comparative Examples. That is, in FIG. 9, the horizontal axis indicates mass-to-charge ratio (m / z), and the vertical axis indicates signal intensity (arbitrary unit: arb.unit). FIG. 9 shows mass spectrum M1 of the Example and mass spectrum M2 of the Comparative Example. In order to easily compare mass spectrum M1 of the Example with mass spectrum M2 of the Comparative Example, the origin of the signal intensity of mass spectrum M1 of the Example (i.e., the value corresponding to signal intensity "0") is shifted upward (by about +0.37). In addition, mass spectra M1 and M2 are normalized with the peak intensity of sodium citrate in each of the Examples and Comparative Examples as 100% (1.0). As shown in FIG. 9, according to the Examples, a higher signal intensity was obtained at the position corresponding to sample Sa (Angiotensin II) than in the Comparative Example. That is, according to the embodiment, it was confirmed that the component Sa1 of the sample Sa is more likely to remain on the first surface 2a than in the comparative example, and thus the detection sensitivity of the component Sa1 of the sample Sa is significantly improved. As described above, FIG. 9 shows the measurement results when the laser desorption ionization method is performed using a sample support having a conductive layer 5, but it is considered that the same results can be obtained even when the mass analysis by the desorption electrospray ionization method described above (the first to fourth steps described above) is performed using a sample support not having a conductive layer 5. That is, it is considered that the component Sa1 of the sample Sa is more likely to remain on the first surface 2a in the embodiment (sample support 1) than in the comparative example (i.e., a sample support in which the upper surfaces of the multiple particles 31A constituting the first surface 2a are not roughened 31a), and therefore high detection sensitivity can be obtained in the mass analysis by the desorption electrospray ionization method described above (the first to fourth steps described above).

[0045] In the above ionization method, in the third step, the irradiation area I1 of the charged microdroplets I is moved relative to the first surface 2a. In the component Sa1 of the sample Sa remaining on the first surface 2a side of the substrate 2, the position information of the sample Sa (two-dimensional distribution information of the molecules (component Sa1) constituting the sample Sa) is maintained. Therefore, by moving the irradiation area I1 of the charged microdroplets I relative to the first surface 2a (target area), the component Sa1 of the sample Sa can be ionized while maintaining the position information of the sample Sa. As a result, in the later step of detecting the sample ions Sa2, the two-dimensional distribution of the molecules constituting the sample Sa can be imaged. Furthermore, since the nozzle 42 can be brought close to the first surface 2a as described above, the irradiation area I1 of the charged microdroplets I can be suppressed from expanding. As a result, in the later step of detecting the sample ions Sa2, the two-dimensional distribution of the molecules constituting the sample Sa can be imaged with high resolution.

[0046] Furthermore, in the mass spectrometry method using the sample support 1, as described above, the component Sa1 of the sample Sa is preferably ionized by irradiation with the charged microdroplets I, thereby improving the signal intensity when detecting the sample ions Sa2.

[0047] [Variations] The present disclosure is not limited to the above-described embodiment. The material and shape of each component are not limited to the above-described material and shape, and various materials and shapes can be adopted. In addition, some components included in the sample support 1 according to the above embodiment may be omitted or modified as appropriate. For example, in the above embodiment, some characteristic components included in the sample support 1 and some effects exerted by each component have been described, but the sample support according to the present disclosure does not necessarily need to be configured to exert all the effects described in the above embodiment, and may be configured to exert only some of the effects described in the above embodiment. In the latter case, the sample support only needs to have a configuration essential for exerting at least the part of the effect, and the configuration that is not essential for exerting the part of the effect may be omitted or modified as appropriate. Note that, when focusing on one effect, the configuration essential for exerting the one effect should be reasonably understood based on the technical common sense and the description of this specification, with the person skilled in the art as the standard. Below, some modified examples of the sample support of the present disclosure are illustrated.

[0048] (First Modification) A sample support 1A according to a first modified example will be described with reference to Figs. 10 to 12. The sample support 1A differs from the sample support 1 in that it includes a substrate 2A having a porous structure 3A instead of the substrate 2 having a porous structure 3. The porous structure 3A further includes a plurality of small particles 32 (second particles) each having a smaller diameter than the particles 31. At least a portion of the plurality of small particles 32 are sandwiched and held between two or more particles 31A in the outermost layer on the first surface 2a side of the porous structure 3A.

[0049] The porous structure 3A is formed by a plurality of particles 31 (first particles) connected to each other, and a plurality of small particles 32 (second particles) having a smaller diameter than the particles 31. The small particles 32 are formed of the same material as the particles 31. In this embodiment, the particles 31 and the small particles 32 are formed of the same insulating material. For example, the particles 31 and the small particles 32 are formed of glass. In this embodiment, soda glass, which has a relatively low melting point among glasses, is used as the material for the particles 31 and the small particles 32 from the viewpoint of facilitating the production of the aggregate structure. Moreover, both the particles 31 and the small particles 32 are spherical beads (glass beads).

[0050] FIG. 10 is an SEM image obtained by imaging the substrate 2A in a state before the formation of the rough surface 31a of the particle 31A and the rough surface 32a of the small particles 32A (small particles 32 of the outermost layer on the first surface 2a side) described later from the direction facing the first surface 2a. As shown in FIG. 10, although there is some variation in shape and size for each particle, each of the multiple particles constituting the porous structure 3A can be classified into either the particles 31 or the small particles 32 even by visual inspection. That is, the porous structure 3 is composed of particle groups that can be clearly distinguished into two groups in terms of "size". More specifically, each of the multiple particles 31 has some variation in shape and size, but has a diameter larger than the small particles 32 to a degree that can be distinguished from the above SEM image, and can be distinguished from the small particles 32. Similarly, each of the multiple small particles 32 has some variation in shape and size, but has a diameter smaller than that of the particles 31 to an extent that can be discerned from at least the SEM image, and is therefore distinguishable from the particles 31.

[0051] When the first surface 2a is viewed from a position facing the first surface 2a along a direction D1, the average particle size of the particles 31 contained in a unit area of ​​a predetermined size (for example, an area of ​​several hundred μm to 1 mm square) is R1, and the average particle size of the small particles 32 contained in the unit area is R2, the following formula (1) is satisfied. More preferably, the following formula (2) is satisfied. R1×1 / 100≦R2≦R1×1 / 2 (1) R1×1 / 10≦R2≦R1×2 / 5 (2)

[0052] The average particle sizes R1 and R2 can be calculated based on, for example, an SEM image as shown in FIG. 10. For example, first, all spherical objects are extracted by performing known image processing (edge ​​detection, etc.) on the SEM image of FIG. 10. The objects may be extracted by visual inspection instead of the image processing. Next, an object having a maximum diameter is extracted from the extracted objects, and an object having a diameter with an error from the maximum diameter of a certain amount or less (for example, 30% or less of the maximum diameter) is classified as a large particle (particle 31). Next, the remaining objects that are not classified as particles 31 are classified as small particles 32. Next, the average diameter of the objects classified as particles 31 is calculated as the average particle size R1 of the particles 31, and the average diameter of the objects classified as small particles 32 is calculated as the average particle size R2 of the small particles 32. The average particle sizes R1 and R2 can be calculated by the above-mentioned processing. The above-mentioned calculation method is an example, and the average particle sizes R1 and R2 may be calculated by other methods. As an example, the average particle size R1 of the particles 31 is about 50 μm, and the average particle size R2 of the small particles 32 is about 5 μm to 20 μm.

[0053] As shown in FIG. 10, the first surface 2a of the substrate 2A is composed of the surfaces (upper surfaces) of the particles 31A and small particles 32A located on the uppermost surface (outermost layer) when the direction from the second surface 2b toward the first surface 2a is taken as the upward direction. In FIG. 10, the black parts are parts where the particles 31A and small particles 32A constituting the first surface 2a are not present, and correspond to the gaps (openings) between the particles. When the first surface 2a is viewed from a position facing the first surface 2a along the direction D1, it is preferable that the area occupied by the particles 31 is the largest in a unit area of ​​a predetermined size (for example, an area of ​​several hundred μm to 1 mm square), and the area occupied by the small particles 32 is next larger than the area occupied by the gaps (openings) between the particles. The porous structure 3A is opened to the first surface 2a at such openings. A liquid that has permeated into the porous structure 3A from the openings of the first surface 2a can pass through the inside of the porous structure 3A and escape to the outside of the second surface 2b from the openings on the second surface 2b side. That is, in this embodiment, the porous structure 3A is open to both the first surface 2a and the second surface 2b, and the openings of the first surface 2a and the openings of the second surface 2b are connected to each other via the gaps between the particles inside the porous structure 3A.

[0054] As shown in Fig. 10, at least a part of the small particles 32 contained in the porous structure 3A, i.e., the small particles 32A (outermost second particles) constituting the first surface 2a together with the particles 31A, are sandwiched and held between two or more particles 31A. Examples of the form in which the small particles 32A are held by two or more particles 31A include a form in which one small particle 32A is held between two particles 31A as shown in Fig. 11(A), and a form in which multiple (two in this example) small particles 32A that are in contact with each other are held between two particles 31A as shown in Fig. 11(B). However, the form in which the small particles 32A are held by two or more particles 31A is not limited to the above examples. As shown in Figures 10 and 11, the porous structure 3A has a configuration in which one or more small particles 32A are held by two or more particles 31A constituting the first surface 2a, and thereby has, on the first surface 2a, seams J1 between the particles 31A, seams J2 between the particles 31A and the small particles 32A, and seams J3 between the small particles 32A.

[0055] Here, most of the small particles 32 are distributed on the first surface 2a (i.e., between the particles 31A constituting the first surface 2a), and are not present inside the substrate 2 (porous structure 3A) at a certain distance from the first surface 2a to the second surface 2b. That is, as shown in FIG. 12, when the layer structure of the substrate 2A constituted by the porous structure 3A is represented, the substrate 2A has a mixed layer 21 (first layer) and a large particle layer 22 (second layer). The mixed layer 21 is a layer including the first surface 2a, in which a plurality of particles 31 and a plurality of small particles 32 are mixed. The large particle layer 22 is a layer located on the second surface 2b side of the mixed layer 21, which is made of a plurality of particles 31 and does not contain small particles 32.

[0056] The thickness of the mixed layer 21 in the direction D1 is ⅕ or less of the thickness of the large particle layer 22 in the direction D1. In the present embodiment, as an example, the thickness of the mixed layer 21 is about 1 / 10 of the entire thickness of the substrate 2A (porous structure 3A). In other words, the thickness of the mixed layer 21 is about 1 / 9 of the thickness of the large particle layer 22.

[0057] 11A and 11B, in this embodiment, small particles 32A located in the outermost layer and constituting the first surface 2a have a rough surface 32a on the first surface 2a side where the concave-convex structure 4 is formed, and a non-rough surface 32b on the second surface 2b side where the concave-convex structure 4 is not formed. The rough surface 32a and the non-rough surface 32b have the same configurations as the rough surface 31a and the non-rough surface 31b of the particle 31A described above, respectively.

[0058] The sample support 1A (porous structure 3A) is manufactured, for example, as follows. First, a sintered body is obtained by sintering a plurality of particles 31 (first sintering step). Specifically, the plurality of particles 31 are compressed by a press or the like and heated at a high temperature below the melting point of the particles 31, so that the surfaces of the plurality of particles 31 are fused and bonded to each other, and a sintered body consisting of only the plurality of particles 31 is obtained. The sintered body has approximately the same external shape as the substrate 2A to be finally obtained. Next, a plurality of small particles 32 are added to the surface of the sintered body corresponding to the first surface 2a (i.e., the surface that will eventually become the first surface 2a) (addition step). For example, the plurality of small particles 32 are sprinkled on the surface of the sintered body. Next, the sintered body and the plurality of small particles 32 added to the sintered body are sintered (resintered) in a mixed state, and a second sintered body is obtained in which the surfaces of the plurality of particles 31 and the plurality of small particles 32 are fused and bonded to each other (second sintering step). Next, the second sintered body is subjected to a surface roughening step similar to the above-mentioned manufacturing method of the sample support 1. This makes it possible to make the upper surfaces of the plurality of particles 31A and the plurality of small particles 32A into rough surfaces 31a, 32a. As a result, the above-mentioned porous structure 3A is obtained.

[0059] In addition to the effects of the sample support 1 described above, the sample support 1A has the following effects. That is, in the sample support 1A, the porous structure 3A is configured to include not only a plurality of particles 31 but also small particles 32A sandwiched and held between two or more particles 31A. This makes it possible to reduce the gaps in the sample support 1A on the first surface 2a (i.e., spaces where no particles constituting the porous structure 3A exist) when the sample support 1A is viewed from a position facing the first surface 2a. That is, as can be seen from the SEM image of FIG. 10, the small particles 32A are held between the plurality of particles 31A in the outermost layer, thereby filling the gaps between the particles 31A in the outermost layer. Also, as shown in FIG. 10 and FIG. 11, in the first surface 2a, not only the joints J1 between the particles 31A, but also the joints J2 between the particles 31A and the small particles 32A and the joints J3 between the small particles 32A are added. The sample Sa transferred or dropped onto the first surface 2a is particularly likely to remain on such joints J1, J2, and J3. That is, by increasing the number of such joints J1, J2, and J3, the sample Sa to be measured can be suitably retained on the first surface 2a (particularly on the joints J1, J2, and J3 described above). Therefore, according to the sample support 1A, it is possible to efficiently ionize the component Sa1 of the sample Sa retained on the first surface 2a, and therefore the detection sensitivity of the component Sa1 of the sample Sa (i.e., the detection sensitivity of the sample ions Sa2) in the mass analysis using the sample support 1A (for example, the first to fourth steps in the above embodiment) can be improved more effectively. Furthermore, by making it easier for the sample Sa to remain on the first surface 2a as described above, the area on the first surface 2a where the sample Sa is stained becomes larger and the stain becomes darker. This improves the visibility of the sample Sa attached to the measurement surface (first surface 2a) of the sample support 1A, and also has the effect of facilitating the task of determining the irradiation range of the microdroplets I for ionization.

[0060] As shown in (A) and (B) of Fig. 11, in the sample support 1A, the small particle 32A has a rough surface 32a on the first surface 2a side and a non-rough surface 32b on the second surface 2b side. According to the above configuration, not only the particle 31A but also the surface on the first surface 2a side of the small particle 32A held between two or more particles 31A is configured as a rough surface 32a, so that the sample Sa to be measured can be more suitably retained on the first surface 2a. As a result, the detection sensitivity of the component Sa1 of the sample Sa can be more effectively improved.

[0061] In the sample support 1A, the small particles 32 are formed of the same material as the particles 31. If the particles 31 and the small particles 32 were formed of different materials, there is a risk that a signal caused by a material (the material of the small particles 32) different from the base material (the material of the particles 31) may be generated as noise during ionization (in this embodiment, during ionization of the component Sa1 by irradiation with the microdroplets I). In contrast, by forming the particles 31 and the small particles 32 from the same material as in this embodiment, the occurrence of the above-mentioned problems can be avoided. In addition, since the melting points and thermal expansion coefficients of the particles 31 and the small particles 32 are equal, the above-mentioned second sintering step can be easily performed (i.e., it can be performed under the same temperature conditions as the first sintering step), and therefore the substrate 2A (porous structure 3A) can be manufactured easily and with stable quality.

[0062] In the sample support 1A, the particles 31 and the small particles 32 are made of an insulating material. According to the above configuration, the substrate 2A in which the plurality of particles 31 and the plurality of small particles 32 are integrated can be manufactured by a simple method such as sintering. Furthermore, since the substrate 2A can be made insulating, the sample support 1A suitable for the above-mentioned desorption electrospray ionization method can be realized. Furthermore, in this embodiment, the particles 31 and the small particles 32 are made of glass. According to the above configuration, by forming the particles 31 and the small particles 32 from glass having a relatively low melting point, the heating temperature required for the above-mentioned first sintering step and second sintering step can be relatively low, so that the substrate 2A having the porous structure 3A can be obtained suitably and inexpensively.

[0063] In the sample support 1A, the sizes of the particles 31 and the small particles 32 contained in the porous structure 3A are adjusted so as to satisfy the above formula (1) (i.e., "R1×1 / 100≦R2≦R1×1 / 2"). With the above configuration, it is possible to preferably realize a configuration in which one or more small particles 32 are sandwiched and held between two or more particles 31 constituting the first surface 2a. As a result, it is possible to preferably obtain the effect of improving the detection sensitivity as described above. Note that, from the viewpoint of more preferably realizing a configuration in which the small particles 32 are held between the particles 31 as described above, it is more preferable to satisfy the above formula (2) (i.e., "R1×1 / 10≦R2≦R1×2 / 5").

[0064] In the sample support 1A, the substrate 2A has a mixed layer 21 including the first surface 2a, and a large particle layer 22 located on the second surface 2b side of the mixed layer 21. That is, in the sample support 1A, the mixed layer 21 containing particles 31 and small particles 32 is provided to make it easier for the sample Sa to remain on the first surface 2a, while the large particle layer 22, which does not contain small particles 32 and thus allows liquid to pass through more easily than the mixed layer 21, is provided below the mixed layer 21 (on the second surface 2b side). This allows the liquid component to escape appropriately from the mixed layer 21 to the large particle layer 22 when the sample Sa to be measured, which contains a liquid component, is transferred or dropped onto the first surface 2a of the sample support 1A. As a result, it is possible to prevent excess liquid components from overflowing onto the first surface 2a, and to prevent the measurement (i.e., ionization of the component Sa1 of the sample Sa remaining on the first surface 2a) from being hindered by the generation of such excess liquid components.

[0065] In the sample support 1A, the thickness of the mixed layer 21 in the direction D1 is ⅕ or less of the thickness of the large particle layer 22 in the direction D1. According to the above configuration, by ensuring a sufficient thickness of the large particle layer 22 relative to the mixed layer 21, the above-mentioned effect (i.e., the effect of allowing liquid components that may hinder measurement to escape from the mixed layer 21 to the large particle layer 22) can be suitably obtained.

[0066] (Second Modification) A sample support 1B according to a second modified example will be described with reference to Fig. 13. The sample support 1B differs from the sample support 1A in that the uneven structure 4 is not formed on either the first surface 2a side or the second surface 2b side of the small particles 32A constituting the first surface 2a. That is, as shown in Fig. 13(A) and (B), in the sample support 1B, the entire surface of the small particles 32A is configured as a non-rough surface 32b.

[0067] The sample support 1B is manufactured, for example, as follows. First, the above-mentioned manufacturing method of the sample support 1 is carried out to obtain the sample support 1. Then, a plurality of small particles 32 are added to the first surface 2a of the sample support 1 (adding step). For example, the plurality of small particles 32 are sprinkled on the above-mentioned surface of the sintered body. Then, the sample support 1 and the plurality of small particles 32 are sintered (resintered) in a mixed state (second sintering step). As a result, the porous structure of the above-mentioned second modified example is obtained. Thus, in the manufacturing method of the sample support 1B, only the particles 31A are roughened, and the small particles 32A are not roughened.

[0068] According to the sample support 1B, in addition to the joint J1, the joints J2 and J3 are increased, so that the sample Sa to be measured can be suitably held on the first surface 2a (particularly on the joints J1, J2, and J3) in the same manner as the sample support 1A. The sample support 1A (porous structure 3A) according to the first modified example described above is obtained by carrying out a treatment similar to the surface roughening treatment on the surface of the particles 31A on the surface (the surface on the first surface 2a side) of the small particles 32A having a smaller diameter than the particles 31A. Here, since the small particles 32A are smaller and more brittle than the particles 31A, there is a risk that the small particles 32A will be crushed and penetrate into the porous structure 3A in the surface roughening treatment. As a result, there is a risk that the effect of the sample support 1A described above (i.e., the effect of the small particles 32A being held between two or more particles 31A) will be reduced. In contrast, with the sample support 1B, only the surfaces of the particles 31A are roughened, and the small particles 32A are not roughened, so that the above-mentioned problems can be avoided.

[0069] (Third Modification) A sample support 1C according to the third modified example will be described with reference to Figures 14 and 15. The sample support 1C differs from the sample support 1 in that it includes a conductive layer 5. The presence of the conductive layer 5 makes it possible for the sample support 1C to be used in an ionization method (such as laser desorption ionization) that requires application of a voltage on the first surface 2a to detect a component Sa1 of an ionized sample Sa.

[0070] The conductive layer 5 covers the first surface 2a so as not to block the openings of the porous structure 3 on the first surface 2a. In other words, the conductive layer 5 is provided so as not to completely block the openings (gaps between particles) of the porous structure 3 on the first surface 2a. This allows the liquid components contained in the sample Sa transferred or dropped onto the first surface 2a (strictly speaking, onto the conductive layer 5 formed on the first surface 2a) to permeate into the porous structure 3 in the sample support 1C as well.

[0071] Moreover, the conductive layer 5 covers the first surface 2a along the surface shape of the uneven structure 4 of the particle 31A. That is, the thickness of the conductive layer 5 is made very thin compared to the size (diameter) of the particle 31A. As a result, the shape of the outer surface of the conductive layer 5 formed on the surface of the particle 31A follows the surface shape (uneven shape) of the uneven structure 4. Therefore, as shown in FIG. 15, even after the conductive layer 5 is formed, the uneven shape of the first surface 2a (i.e., the uneven shape of the rough surface 31a of each particle 31A) is maintained.

[0072] The conductive layer 5 is made of a conductive material. The material of the conductive layer 5 is preferably a metal having low affinity (reactivity) with the sample Sa and high conductivity. From this viewpoint, the material of the conductive layer 5 is preferably, for example, Au (gold), Pt (platinum), etc. The conductive layer 5 is formed to a thickness of about 1 nm to 350 nm by, for example, a plating method, an atomic layer deposition method (ALD: atomic layer deposition), a vapor deposition method, a sputtering method, etc. Note that the material of the conductive layer 5 may be, for example, Cr (chromium), Ni (nickel), Ti (titanium), etc.

[0073] 15, the conductive layer 5 is formed by performing, for example, the above-mentioned deposition method, sputtering method, or the like from the first surface 2a side, so as to cover the rough surface 31a exposed on the first surface 2a side among the surfaces of the particles 31A constituting the first surface 2a. On the other hand, when the conductive layer 5 is formed by ALD, the conductive layer 5 can be formed not only on the surface exposed on the first surface 2a side, but also on the surface (non-rough surface 31b) facing the second surface 2b side of the particles 31A and the surface (non-rough surface 31b) of the particles 31 present inside the porous structure 3 by penetrating into the gaps of the porous structure 3. That is, the conductive layer 5 is only required to be formed so as to cover at least the surface (rough surface 31a) exposed on the first surface 2a side of the particles 31A constituting the first surface 2a, and may also be formed on the surfaces of the particles 31 other than the first surface 2a.

[0074] The sample support 1C makes it possible to use the sample support 1C for laser desorption ionization and the like while making it possible to obtain the same effect as the sample support 1 (i.e., without impeding the effect of the sample support 1 due to the presence of the conductive layer 5). More specifically, when using the laser desorption ionization and the like, that is, when it is necessary to apply a voltage to the first surface 2a in order to guide the component Sa1 of the sample Sa ionized on the first surface 2a to the ion detector (ground electrode side), it becomes possible to apply a voltage appropriately via the conductive layer 5.

[0075] (Fourth Modification) In the sample support 1, the particles 31 constituting the second surface 2b among the plurality of particles 31 may have a rough surface 31a on the second surface 2b side on which the concave-convex structure 4 is formed, and a non-rough surface 31b on the first surface 2a side on which the concave-convex structure 4 is not formed. That is, the sample support 1 may have a symmetrical structure in the direction D1. In other words, the portion on the first surface 2a side and the portion on the second surface 2b side may have the same configuration.

[0076] According to the above-mentioned fourth modified example, it becomes possible to use both the first surface 2a and the second surface 2b as measurement surfaces (i.e., surfaces supporting the sample Sa to be measured) that exhibit the above-mentioned effects of the sample support 1. This improves convenience because the user (measurer) of the sample support 1 does not need to specify which surface of the sample support 1 is the measurement surface when transferring or dropping the sample Sa to be measured onto the sample support 1.

[0077] (Other variations) The configurations of the above-mentioned embodiment and the first to fourth modified examples may be appropriately combined. For example, the first modified example may be combined with the third modified example. In this case, the conductive layer 5 is provided on each of the upper surfaces (rough surface 31a) of the particles 31A and the upper surfaces (rough surface 32a) of the small particles 32A of the sample support 1A (see FIG. 11). The second modified example may be combined with the third modified example. In this case, the conductive layer 5 is provided on each of the upper surfaces (rough surface 31a) of the particles 31A and the upper surfaces (non-rough surface 32b) of the small particles 32A of the sample support 1B (see FIG. 13). The first modified example or the second modified example may be combined with the fourth modified example. In this case, a third layer similar to the mixed layer 21 (i.e., a layer in which the particles 31 and the small particles 32 are mixed) is also formed on the second surface 2b side. In this case, the large particle layer 22 in the sample support 1A, 1B is located between the mixed layer 21 on the first surface 2a side and the third layer.

[0078] Furthermore, in the first and second modified examples, the porous structure 3A is configured such that a plurality of particles 31 and a plurality of small particles 32 are fused to each other, thereby realizing a configuration in which the small particles 32A are sandwiched and held between two or more particles 31A constituting the first surface 2a, but the small particles 32A do not necessarily have to be fused to adjacent particles 31A.

[0079] In the above embodiment, the sample support 1 is configured to include only the substrate 2, but the sample support 1 may include a member other than the substrate 2. For example, a support member (such as a frame) for supporting the substrate 2 may be provided on a part of the substrate 2 (such as a corner).

[0080] Moreover, the sample Sa is not limited to the slice of fruit (lemon) exemplified in the above embodiment. The sample Sa may have a flat surface or an uneven surface. The sample Sa may be something other than fruit, for example, a leaf of a plant. In this case, by transferring the components of the surface of the leaf, which is the sample Sa, to the first surface 2a, it becomes possible to perform imaging mass spectrometry of the surface (veins) of the leaf.

[0081] In the above embodiment, the entire substrate 2 is constituted by the porous structure 3, but the porous structure 3 may be formed in a part of the substrate 2. For example, the porous structure 3 may be formed only in a central region (a part of the first surface 2a) of the substrate 2 that is determined as a measurement region for transferring or dropping the sample Sa. In this case, the porous structure 3 may not be formed in other parts of the substrate 2. In addition, the porous structure 3 may not be formed over the entire region from the first surface 2a to the second surface 2b. That is, the porous structure 3 only needs to be open at least to the first surface 2a, and may not be open to the second surface 2b. For example, the substrate 2 may be constituted by a flat plate including the second surface 2b and the porous structure 3 provided on the surface of the plate opposite to the second surface 2b. As an example, the substrate 2 may be constituted by a glass plate and a sintered body (porous structure 3) of glass beads provided on the glass plate.

[0082] In the above embodiment, the first surface 2a has insulating properties so that the sample support 1 can be used in desorption electrospray ionization. More specifically, the substrate 2 (porous structure 3) itself is formed of an insulating material, so that the first surface 2a has insulating properties. However, the sample support 1 can be configured to be used in desorption electrospray ionization by a configuration other than the above. For example, the substrate 2 (porous structure 3) may be formed of a conductive material. In this case, an insulating coating may be applied to the first surface 2a of the substrate 2, so that the first surface 2a has insulating properties. By applying such an insulating coating, the first surface 2a of the substrate 2 can be made insulating, so that the substrate 2 formed of a conductive material can be used. For example, in this case, the porous structure 3 may be formed of an aggregate of a plurality of particles 31 made of a metal. In this way, when an insulating coating is provided, the freedom of selection of the substrate material (i.e., the material of the particles 31) can be improved.

[0083] Furthermore, as the material of the above-mentioned particles 31, 32, in addition to the insulating material exemplified in the above embodiment (glass (soda glass) as an example in the above embodiment), a metal oxide (e.g., alumina, etc.) or an insulating coated metal may be used. Furthermore, the shape of the particles 31, 32 is not limited to a spherical shape and may have a shape other than a spherical shape. In the latter case, the diameters (average particle sizes R1, R2) of the particles 31, 32 described in the above embodiment may be read as the effective diameter of the particle observed when viewing the substrate 2 along the direction D1 from a position facing the first surface 2a (i.e., the maximum diameter of a virtual cylinder that fits within the area occupied by the particle). [Explanation of symbols]

[0084] 1, 1A, 1B, 1C...sample support, 2, 2A...substrate, 2a...first surface, 2b...second surface, 3, 3A...porous structure, 4...rough structure, 5...conductive layer, 21...mixed layer (first layer), 22...large particle layer (second layer), 31...particle (first particle), 31a...rough surface, 31b...non-rough surface, 31A...particle (outermost first particle), 32...small particle (second particle), 32a...rough surface, 32b...non-rough surface, 32A...small particle (outermost second particle), Sa...sample, Sa1...component, Sa2...sample ion (ionized component).

Claims

1. A sample support for ionization of a sample, comprising: a substrate having a first surface, a second surface opposite the first surface, and an irregular porous structure opening to the first surface; the porous structure is formed by a plurality of first particles connected to each other; an outermost first particle constituting the first surface among the plurality of first particles has a rough surface on the first surface side on which a concave-convex structure is formed, and a non-rough surface on the second surface side on which the concave-convex structure is not formed; Sample support.

2. the porous structure further comprises a plurality of second particles each having a smaller diameter than the first particles; 2. The sample support of claim 1, wherein at least a portion of the plurality of second particles are sandwiched and held between two or more of the outermost first particles.

3. 3. The sample support according to claim 2, wherein an outermost second particle among the plurality of second particles constituting the first surface has a rough surface on the first surface side on which the unevenness structure is formed, and a non-rough surface on the second surface side on which the unevenness structure is not formed.

4. The sample support according to claim 2, wherein the uneven structure is not formed on either the first surface side or the second surface side of the outermost second particle among the plurality of second particles that constitutes the first surface.

5. The substrate is a first layer including the first surface and including a plurality of the first particles and a plurality of the second particles; The sample support according to any one of claims 2 to 4, further comprising: a second layer located closer to the second surface than the first layer, the second layer consisting of a plurality of the first particles and not including the second particles.

6. 2. The sample support according to claim 1, wherein the particles constituting the second surface among the plurality of first particles have a rough surface on which a concave-convex structure is formed on the second surface side, and a non-rough surface on which no concave-convex structure is formed on the first surface side.

7. The sample support according to claim 1 , further comprising a conductive layer that does not block the openings of the porous structure in the first surface and covers the first surface along the surface shape of the uneven structure of the outermost first particle.

8. 2. A method for producing a sample support according to claim 1, comprising the steps of: a sintering step of sintering the plurality of first particles to obtain a sintered body having substantially the same outer shape as the substrate; and a roughening step of performing a roughening treatment on a surface of the sintered body corresponding to the first surface to form a plurality of the outermost first particles, each of which has a rough surface formed on the first surface side.