Capacitor with conductive adhesive layer

Abstract

To provide a capacitor with improved mechanical and electrical stability, a manufacturing method for the same, and a medical device including the capacitor.SOLUTION: A capacitor, particularly an electrolytic capacitor, having a metal current collector 1, a conductive adhesive layer 2 adhered to the metal current collector, an electrode active layer 3 adhered to the conductive adhesive layer, an anode 5 consisting of or comprising an oxide-forming metal, and a separator 4 for preventing direct electrical contact between the anode and the electrode active layer. The conductive adhesive layer 2 contains a conductive non-carbide metal compound, particularly a metal oxide or metal nitride.SELECTED DRAWING: Figure 1

Description

[Technical Field]

[0001] The present invention relates to a capacitor with a stabilized conductive adhesive layer and a method for making the same. [Background technology]

[0002] In aqueous electrolytic capacitors in particular, electrode active coatings on current collectors with binders exhibit mechanical and electrical instability when applied directly to the current collector. Electrical contact resistance increases over time, while mechanical stability decreases. Furthermore, the electrolyte can penetrate the porous electrode active coating and passivate the metal surface. Summary of the Invention [Problem to be solved by the invention]

[0003] Based on the above, it is an object of the present invention to provide a capacitor with improved mechanical and electrical stability. [Means for solving the problem]

[0004] This object is achieved by a capacitor having the features set forth in claim 1. Suitable embodiments thereof are set forth in the dependent claims and the following description.

[0005] Generally, the present invention provides an electrode for a capacitor, particularly an electrolytic capacitor, or for an electrochemical cell, which basically comprises a metal current collector, a conductive adhesive layer deposited on the metal current collector, and an electrode active layer deposited on the adhesive layer.

[0006] In one preferred embodiment, the electrode of the present invention functions as a cathode in, for example, a capacitor or electrochemical cell, preferably using an aqueous electrolyte.In particular, when the electrode of the present invention is used as a cathode in a capacitor, an anodic state may occur at the cathode during discharge, which may cause the cathode to be passivated.Advantageously, the conductive adhesive layer can protect the electrode (functioning as a cathode) from such passivation.

[0007] Suitable embodiments of the conductive adhesive layer, electrode active layer, and non-carbide metal compound are described below.

[0008] According to one embodiment of the present invention, there is provided a capacitor, particularly an electrolytic capacitor, comprising a metal current collector, a conductive adhesive layer deposited on the metal current collector, and an electrode active layer deposited on the adhesive layer.

[0009] It is specifically contemplated in accordance with the present invention that the conductive adhesive layer comprises a conductive non-carbide metal compound.

[0010] The term "non-carbide metal compound" refers specifically to ionic or polar metal compounds of metals and non-metals that do not contain carbides.

[0011] The term "electrode active layer" refers specifically to a layer or coating that can function as an electrode or that can include an electrode active material that can function as an electrode. Examples of electrode active materials include, but are not limited to, activated carbon, graphite, graphene, carbon nanotubes, and conductive polymers, among others.

[0012] Advantageously, the conductive adhesive layer of the present invention allows for safe and stable bonding or adhesion of the electrode active layer to the metal current collector. At the same time, the conductive adhesive layer is mechanically, chemically, and electrically stable, thereby reliably protecting the metal current collector from passivation, for example, by the electrolyte. Furthermore, the adhesive layer of the present invention can be formed at a lower temperature than metal carbide layers, the production of which requires high temperatures (e.g., above 700°C). For example, a precursor of the adhesive layer, such as a solution or suspension of a non-carbide metal compound, can be applied to the metal current collector and tempered, for example, at temperatures below 700°C.

[0013] Preferably, the metal current collector together with the conductive adhesive layer and electrode active layer can act as the cathode, or as the cathode surface if the capacitor is an electrolytic capacitor in which the electrolyte forms or acts as the cathode. In either case, the cathode potential is preferably on the metal current collector.

[0014] According to one embodiment of the capacitor of the present invention, the non-carbide metal compound comprises a transition metal, hi one embodiment, the transition metal is selected from ruthenium, niobium, iridium, manganese, zinc, titanium, zirconium, hafnium, vanadium, tantalum, molybdenum, or tungsten.

[0015] According to a further embodiment, the capacitor of the present invention further comprises an anode consisting essentially of or comprising a valve metal, in particular selected from tantalum, niobium, or aluminum.

[0016] According to a further embodiment, the capacitor further comprises an aqueous electrolyte. In one embodiment, the electrolyte comprises ethylene glycol and, optionally, an acid (particularly boric acid or acetic acid), particularly when the anode is formed of aluminum or tantalum. In one embodiment, the electrolyte comprises ethylene glycol, acetic acid, and ammonium acetate. In one embodiment, the electrolyte comprises dimethylformamide, dimethylacetamide, and / or γ-butyrolactone. In one embodiment, the electrolyte comprises tetracyanoquinodimethane, polypyrrole, or poly(3,4-ethylenedioxythiophene).

[0017] According to a further embodiment of the capacitor of the present invention, the non-carbide metal compound is a metal oxide, hi one embodiment, the adhesion layer comprises ruthenium oxide, niobium oxide, iridium oxide, manganese oxide, zinc oxide, and mixtures thereof.

[0018] According to a further embodiment of the capacitor of the present invention, the non-carbide metal compound is a metal nitride, hi one embodiment, the adhesion layer comprises titanium nitride, zirconium nitride, hafnium nitride, vanadium nitride, niobium nitride, tantalum nitride, molybdenum nitride, tungsten nitride, or a mixture thereof.

[0019] Preferably, the adhesive layer is structured, in particular in the nanometer range, ie it comprises spherical or rod-shaped particles, for example with a size in the range of 10 nm to 100 nm.

[0020] In one embodiment, the metal oxide is a metal dioxide (MO), particularly a transition metal. Preferred metal oxides are capable of forming nanostructures, such as titanium oxide (TiO), ruthenium oxide (RuO), iridium oxide (IrO), niobium oxide (NbO), or manganese oxide (MnO).

[0021] According to a further embodiment of the capacitor of the present invention, the adhesion layer is characterized by a thickness in the range of 10 nm to 5 μm, hi one embodiment, the adhesion layer is characterized by a thickness in the range of 40 nm to 0.4 μm.

[0022] According to a further embodiment of the capacitor of the invention, the electrode active layer comprises a conductive material selected from carbon, in particular activated carbon, graphite, graphene, carbon nanotubes, and / or conductive polymers.

[0023] According to a further embodiment of the capacitor of the present invention, the conductive layer comprises a binder selected from polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), carbomethyl cellulose (CMC), or rubber, in particular acrylic rubber, nitrile butadiene rubber, styrene butadiene rubber (SBR), or butyl rubber.

[0024] According to a further embodiment of the capacitor of the present invention, the metal current collector comprises or consists essentially of titanium or a titanium alloy.

[0025] According to a further embodiment, the electrolytic capacitor comprises a metal housing, at least a portion of which forms a metal current collector. Advantageously, a cathode potential is present on the metal housing, whereby the cathode is accessible from outside the capacitor through the housing. Preferably, the metal housing, and thus the metal current collector, consists essentially of or comprises titanium or a titanium alloy.

[0026] According to a further embodiment, the capacitor of the present invention further comprises at least one separator element. Such separator element is specifically configured to provide mechanical separation of the electrodes. In one embodiment, the at least one separator element is disposed between the positive electrode and the current collector. In one embodiment, the at least one separator element is designed to be at least semi-permeable to charge carriers, such as those of the electrolyte. In one embodiment, the at least one separator element is formed from foamed or porous polytetrafluoroethylene, polypropylene, polyethylene, or a mixture of polypropylene and polyethylene.

[0027] According to one embodiment of the present invention, there is provided a method for manufacturing a capacitor, and in particular a method for manufacturing a capacitor of the present invention, comprising the steps of depositing a conductive adhesive layer on a metal current collector and depositing an electrode active layer on the conductive adhesive layer.

[0028] In accordance with the present invention, it is specifically envisaged that the conductive adhesive layer comprises a conductive non-carbide metal compound, particularly a metal oxide or a metal nitride.

[0029] Suitable non-carbide metal compounds are described in the above embodiments of the capacitor of the present invention.

[0030] According to one embodiment of the manufacturing method of the present invention, the conductive adhesive layer is applied to the metal current collector in the form of a solution or suspension, the solution or suspension including a non-carbide metal compound and an organic solvent, and after the application of the adhesive layer, the metal current collector together with the adhesive layer is tempered. In one embodiment, the metal current collector together with the adhesive layer is tempered at a temperature below 700°C, particularly at a temperature in the range of 360°C to 550°C.

[0031] Advantageously, the conductive adhesive layer can be formed at lower temperatures compared to those required for the formation of the carbide layer, while providing a stable, porous or nanostructured conductive adhesive layer that protects the metal current collector from passivation and promotes reliable adhesion of the subsequently deposited electrode active layer.

[0032] According to a further embodiment of the manufacturing method of the present invention, the electrode active layer is applied in the form of a composition comprising a conductive material, in particular carbon, in particular activated carbon, graphite, graphene, carbon nanotubes, and / or a conductive polymer, and optionally a binder, and after applying the electrode active layer, the metal current collector is tempered together with the conductive adhesive layer and electrode active layer. In one embodiment, the metal current collector together with the conductive adhesive layer and electrode active layer is tempered after applying the electrode active layer at a temperature below 700°C, in particular at a temperature in the range of 80°C to 240°C.

[0033] Suitable conductive materials and binders are described in the above embodiments of the electrolytic capacitor of the present invention.

[0034] Preferably, the composition containing the conductive material is applied in the form of a paste, which can be more easily applied to the surface of the metal current collector or adhesive layer, respectively.

[0035] According to one embodiment of the present invention, there is provided a medical device, particularly an implantable medical device, comprising a capacitor of the present invention or a capacitor obtained by the manufacturing method of the present invention. In one embodiment, the medical device is a pacemaker, a cardioverter / defibrillator, a loop recorder, or a sensor.

[0036] Further advantages, configurations and embodiments of the present invention are described with reference to the following drawings. [Brief explanation of the drawings]

[0037] [Figure 1] 1 shows a schematic diagram of a current collector of a capacitor of the present invention. [Figure 2] Scanning electron microscope image of a surface coated with nanostructured ruthenium oxide. [Figure 3] Scanning electron microscope image of a surface coated with nanostructured ruthenium oxide. [Figure 4]Scanning electron microscope image of a surface coated with nanostructured iridium oxide. [Figure 5] Cyclic voltammograms of titanium substrates coated with nanoporous ruthenium oxide, nanoporous iridium oxide, and uncoated titanium substrates. DETAILED DESCRIPTION OF THE INVENTION

[0038] Example In a preferred embodiment of the present invention, a conductive metal oxide is deposited between the cathode current collector (housing) (e.g., of a capacitor) and an additional electrode active coating or layer. This intermediate layer increases the adhesion of the electrode active coating or layer to the metal current collector and protects the metal current collector from passivation. In particular, the conductive metal oxide deposited as an intermediate layer acts as an adhesion promoter for the electrode active layer, especially due to its nanostructured surface, and prevents passivation of the current collector due to its mechanical and chemical stability.

[0039] Thus, the present invention provides a mechanically, electrically, and chemically stable active layer or coating for a high capacitance cathode, which protects the substrate (e.g., titanium housing) that serves as the current collector from passivation and enables reliable, long-term, stable adhesion of the electrode active layer or coating to the substrate. Advantageously, such active layer or coating can be produced without elevated temperatures (e.g., above 700°C), which are disadvantageous in terms of cost and component failure (warping of the substrate, housing, cover, etc., grain growth, large grains that can compromise the mechanical stability and hermeticity of welded components (e.g., housing and cover)).

[0040] FIG. 1 shows the basic structure of one embodiment of a capacitor of the present invention. The capacitor includes a titanium housing 1, which functions as a current collector. The inner surface of the housing 1 is coated with a metal oxide layer 2 (e.g., ruthenium oxide or iridium oxide) and is further coated with an electrode active layer 3 (e.g., activated carbon with a suitable binder). The capacitor further includes an anode consisting essentially of or including an oxide-forming metal 5. Such metals can be valve metals such as tantalum, aluminum, or niobium. The capacitor further includes a separator 4 to prevent direct electrical contact between the anode 5 and the electrode active layer. Furthermore, an electrolyte fills the space between the anode and the coated titanium housing, thereby establishing electrical contact. In particular, the separator is immersed in the electrolyte.

[0041] For its fabrication, a titanium housing 1 is coated with a conductive metal oxide 2 (e.g., ruthenium oxide or iridium oxide), followed by the deposition of an electrode active layer 3 comprising activated carbon with a suitable binder (PVDF). The graphite electrode thus fabricated is mechanically and electrically stable for long periods in aqueous electrolytes. The long-term stability has been investigated and confirmed at high temperatures.

[0042] The ruthenium oxide layer was fabricated using a coating solution consisting of metal salts dissolved or dispersed in an organic solvent. After coating, the precursor material was converted at temperatures between 360°C and 500°C. The resulting RuOx layer had a thickness ranging from 0.04 μm to 0.4 μm, was fully crystallized, electrically conductive, and mechanically very stable. In a second step, a paste containing activated carbon and a suitable binder was applied to the metal oxide-coated titanium surface, followed by tempering.

[0043] In this example, the ruthenium oxide layer was prepared using a 10 mmol / L to 200 mmol / L solution of ruthenium(III) chloride hydrate in methanol. After coating, the precursor was converted and annealed in a furnace at temperatures between 360 and 500 °C. The resulting RuOx layer had a thickness ranging from 0.04 μm to 0.4 μm, was fully crystallized, conductive, and mechanically very stable. In a second step, a coating of activated carbon and PVDF in an organic solvent was applied to the metal oxide-coated titanium surface and annealed at a temperature of 200 °C.

[0044] Figures 2 and 3 show scanning electron microscope images of surfaces coated with nanostructured ruthenium oxide. In Figure 2, the surface shows spherical and cylindrical structures or particles roughly 10 nm in size. As seen in Figure 3, a different process control in which a thicker ruthenium oxide layer was deposited resulted in the formation of nanowires greater than 50 nm in size. These structures are similarly porous.

[0045] Figure 4 shows cyclic voltammograms of titanium substrates coated with ruthenium oxide or iridium oxide and uncoated substrates. The uncoated titanium substrate becomes passivated upon anodic polarization and does not conduct current even at higher depolarizations, whereas the ruthenium oxide and iridium oxide coated substrates remain active, and the current density remains stable without passivation. Voltammograms were obtained using a test electrolyte containing 120:80:30 (volume fraction) ethylene glycol, water, and acetic acid with 12 weight fractions of ammonium acetate and 10 mmol / L KCl. The voltage was determined relative to a Ag / AgCl reference electrode.

Claims

1. A metal current collector (1), a conductive adhesive layer (2) attached onto the metal current collector (1); An electrode active layer (3) attached on the conductive adhesive layer (2); A capacitor, particularly an electrolytic capacitor, comprising: A capacitor characterized in that the adhesive layer (2) comprises an electrically conductive non-carbide metal compound, in particular a metal oxide or a metal nitride.

2. 2. The capacitor of claim 1, wherein the non-carbide metal compound comprises a transition metal selected in particular from ruthenium, niobium, iridium, manganese, zinc, titanium, zirconium, hafnium, vanadium, tantalum, molybdenum, or tungsten.

3. 3. Capacitor according to claim 1 or 2, further comprising an anode (5) consisting essentially of or comprising a valve metal, in particular tantalum, aluminum or niobium.

4. The capacitor of any one of claims 1 to 3, further comprising an aqueous electrolyte.

5. 5. Capacitor according to any one of claims 1 to 4, characterized in that the conductive adhesive layer (2) comprises a metal oxide, in particular ruthenium oxide, niobium oxide, iridium oxide, manganese oxide, zinc oxide, or a mixture thereof, and / or a metal nitride, in particular titanium nitride, zirconium nitride, hafnium nitride, vanadium nitride, niobium nitride, tantalum nitride, molybdenum nitride, tungsten nitride, or a mixture thereof.

6. Capacitor according to any one of claims 1 to 5, characterized in that the conductive adhesive layer (2) has a thickness in the range of 1 nm to 5 μm, in particular in the range of 40 nm to 0.4 μm.

7. 7. Capacitor according to any one of claims 1 to 6, characterized in that the electrode active layer (3) comprises a conductive material selected from carbon, in particular activated carbon, graphite, graphene, carbon nanotubes and / or conductive polymers.

8. Capacitor according to any one of claims 1 to 5, characterized in that the electrode active layer (3) comprises a binder.

9. 9. Capacitor according to claim 8, characterized in that the binder is selected from polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), carbomethyl cellulose (CMC) or rubber, in particular acrylic rubber, nitrile butadiene rubber (NBR), styrene butadiene rubber (SBR) or butyl rubber.

10. Capacitor according to any one of claims 1 to 9, characterized in that the metal current collector (1) comprises or consists essentially of titanium or a titanium alloy.

11. The capacitor according to any one of claims 1 to 10, further comprising a metal housing (1), at least a part of said metal housing (1) forming said metal current collector (1).

12. A method for producing a capacitor, in particular a capacitor according to any one of claims 1 to 11, comprising the steps of: Depositing a conductive adhesive layer (2) on a metal current collector (1); Depositing an electrode active layer (3) on the conductive adhesive layer (2); A method comprising:

10. A method according to claim 9, wherein said conductive adhesive layer (2) comprises a non-carbide conductive metal compound, in particular a metal oxide or a metal nitride.

13. 13. The method according to claim 12, characterized in that the conductive adhesive layer (2) is applied onto the metal current collector (1) in the form of a solution or suspension, the solution or suspension comprising the non-carbide metal compound and an organic solvent, and that after application of the conductive adhesive layer the metal current collector is tempered, in particular at a temperature below 700°C, more particularly in the range of 360°C to 550°C.

14. 14. The method according to claim 12 or 13, characterized in that the electrode active layer (3) is applied in the form of a composition, in particular a paste, comprising an electrically conductive material, in particular carbon, in particular activated carbon, graphite, graphene, carbon nanotubes and / or an electrically conductive polymer, and optionally a binder, and that after applying the electrode layer the metal current collector is tempered, in particular at a temperature below 400°C, more particularly at a temperature in the range of 80°C to 240°C.

15. A medical device, in particular an implantable medical device, comprising a capacitor according to any one of claims 1 to 11 or a capacitor produced by the method according to any one of claims 12 to 14.