Printed nonwoven web with microdot bonded pattern

Abstract

The present invention relates to a printed nonwoven web that includes a pattern of fused embossed bonds and that is printed on the web. The present invention further relates to a method of making such a nonwoven web and uses of such a nonwoven web.

Description

[Technical field]

[0001] The present invention relates to a nonwoven web comprising a pattern of fused embossed bonds on at least one surface thereof and printed on the same surface. The present invention further relates to a method of making such a nonwoven web and uses of such a nonwoven web. [Background technology]

[0002] In the hygiene industry, nonwoven webs are used extensively as materials for making products such as baby diapers or adult incontinence products. Webs that include or consist of spunbond nonwoven materials and are joined by calendar embossing have become the industry standard for many applications. Not only do these webs have desirable product properties, but they can also be produced economically on high speed lines. Some applications require that the material be printed with text, graphic patterns, or images. Most typically, the printing of these materials is facilitated by flexographic ink printing, where the nonwoven web is fed at high speed into a flexographic printing unit and ink is transferred directly from a printing roll to the web surface. However, image quality is limited when ink printing calender-bonded nonwoven webs that contain a pattern of fused embossed bonds on the print surface because the bonds have a darker color and contrast than the rest of the fabric, causing the print to appear pixelated and uneven. Summary of the Invention

[0003] SUMMARY OF THE PRESENT EMBODIMENT An object of the present invention is to improve the image quality of prints on calender-bonded nonwoven webs without compromising production efficiency and economy. Against this background, the present invention provides a printed nonwoven web comprising a pattern of fused embossed bonds, the nonwoven web being ink printed on a surface exhibiting a pattern of bonds, the pattern of bonds satisfying the following conditions: (a) the number of bonds on the surface is less than 70 / cm 2 More than 75 / cm2 (b) the average area size of each individual junction is 1.5 mm 2 Smaller, preferably 1.35mm 2 and (c) the average center-to-center distance between bonds is less than 1.5 mm, preferably less than 1.3 mm. The bond pattern is preferably uniform across the entire surface of the fabric. This condition is representative of the use of more and smaller bond points than was used in the prior art. Smaller bond points result in a surface with a more uniform appearance. This is particularly advantageous for subsequent printing, as it makes the print appear more uniform. The reason is that if a portion of a printed design contains bond points, that portion will appear a slightly different color than the unbonded printed surface due to differences in smoothness and opacity. Smaller bond points and a denser bond pattern make this phenomenon less noticeable, resulting in a cleaner looking printed design.

[0004] In one embodiment, the bond area, defined as the percentage of the total surface area occupied by the bond points, is less than 18%, preferably less than 15%, more preferably less than 12%, and even more preferably less than 11%. The smaller the total bond area, the smaller the total area with slightly different coloring. Thus, a smaller overall bond area also contributes to improved print quality. Each printed nonwoven web can be produced by a process in which a nonwoven web is bonded by calendar embossing to form a nonwoven web containing on at least one surface thereof a pattern of fused embossed bond points satisfying the above criteria, and the nonwoven web is ink printed on the surface exhibiting the pattern of bond points. Preferably, the ink printing is flexographic ink printing. In a flexographic ink printing unit, the nonwoven web is usually passed over the surface of a printing roll. The printing roll includes an exchangeable cylindrical sleeve folded around a core cylinder. The sleeve contains a mirrored master of the image required as a 3D positive relief. Ink is transferred from an ink reservoir to the printing roll from an anilox roll, which has surface cells to distribute the ink in appropriate amounts. A doctor blade scrapes off excess ink from outside the cells. The printing roll contains a mirrored master of the image required as a 3D positive relief.

[0005] Alternatively, the ink printing can be inkjet printing. This printing method may not offer the line speeds of flexography, but it is more flexible in terms of personalization and modification. Digital printing can be achieved with inkjet printing. The ink can be water-based or solvent-based, and the surface can be dried after application of the ink. Alternatively, the ink can be a UV-curable ink that includes reactive monomers and / or oligomers, pigments, and photoinitiators, and in this case the surface can be irradiated with UV light after application of the ink. UV-curable inks are advantageous in terms of improving adhesion and reducing VOC emissions. The bond pattern formed by the present invention can be manipulated over a wide range of printing resolutions. Specifically, the contact areas on the printing roller are typically in the form of dots, and the dots are arranged in lines. The line screen is expressed in lines per cm and is representative of the printing resolution. In one embodiment, the line screen may be from 15 L / cm to 50 L / cm. To obtain good printing quality, a printing resolution of about 30 L / cm or more may be used.

[0006] In one embodiment, the nonwoven web is a spunbond or spunmelt nonwoven material. Preferably, the material is formed from polyolefin fibers. Suitable polyolefins include, for example, polypropylene (PP), polyethylene (PP) or copolymers including propylene or ethylene-based copolymers (co-PP; co-PE). Spunbond nonwoven materials can be further combined with the same or different spunbond (S) layers and / or meltblown (M) layers to obtain SS, SMS or similar types of multi-layer webs. During bonding, the material runs over the surface of a calender roll having embossing projections on its surface that meet the above criteria. In a preferred embodiment, bonding involves ultrasonic bonding, where ultrasonic vibrations are introduced into the embossing projections and the fibers are fused by ultrasonic welding. Another embodiment uses thermal bonding, where the embossing projections are heated and the fibers are fused by thermal welding. For optimal production efficiency, the steps of the method, on the one hand, the laying and bonding of the fibers to form the nonwoven material, and on the other hand, the printing of the nonwoven, are preferably carried out inline, or, for greater flexibility, an offline setup can be used in which a pre-manufactured nonwoven material is printed separately.

[0007] Generally, the line speed for forming and printing the nonwoven material, whether together in an in-line setting or separately in an off-line setting, is preferably at least 100 meters per minute, more preferably greater than 150 meters per minute, and even more preferably greater than 200 meters per minute. The printed nonwoven webs of the present invention can be used in hygiene products such as baby diapers, sanitary napkins, or adult incontinence products. Alternatively, the nonwoven webs can be used in medical applications such as gowns, face masks, nursing pads, or bed sheets. Additionally, the nonwoven webs can be used in household products such as wipes and cleaning towels. By reducing the distance between the bond points, the bond pattern becomes less noticeable, so the print quality is much closer to what can be achieved with other nonwoven types that are bonded without creating bond points, such as air-through carded ones. The bond dots are so small that they do not interfere with the quality of the print. At the same time, production efficiency and product quality remain high. Specifically, calendar-bonded nonwovens have better physical properties than nonwovens bonded by other methods, such as air-through bonding. Further details and advantages of the invention emerge from the figures and examples described below. [Brief description of the drawings]

[0008] [Figure 1] FIG. 1 shows a schematic configuration of a production line for making a printed nonwoven web according to the present invention. [Diagram 2] FIG. 1 is an explanatory diagram showing the principle of flexographic ink printing. [Diagram 3] FIG. 1 is a schematic diagram of a typical flexographic ink printing layout used for printing nonwoven fabrics. [Figure 4] FIG. 1 illustrates a bonding pattern used in the prior art. [Diagram 5] FIG. 2 illustrates a bonding pattern according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0009] An exemplary machine configuration for making a printed nonwoven web 10 according to the present invention is shown in FIG. The setup includes a conveyor belt and two spunbond machines 20, 22 arranged side-by-side on the conveyor belt. In each spunbond machine, molten thermoplastic polymer is extruded through holes in a die. The extruded fiber strands are then cooled and drawn / stretched to form endless fibers, which are then laid down on the conveyor belt or, in the case of a second layer, on top of a first web previously deposited on the conveyor belt. Each of the spunbond machines 20, 22 is provided with a pair of precompression rollers 21, 23 for precompressing the respective webs. The pre-compressed web is then bonded at bonding unit 25 by calendar embossing, which involves running the fabric over the surface of a calendar roll having a pattern of embossing protrusions on its surface. A heat or ultrasonic energy source introduces heat or ultrasonic energy to the protrusions, fusing the web at each location to provide a pattern of bond points that correspond to the pattern of protrusions on the calendar roll surface. Following splicing, a printing process takes place in a printing unit 30, which will be described in more detail below. The product web is finally wound onto a product roll 40. FIG. 2 shows a flexographic printing unit 31 including a manifold for transferring ink onto the surface of anilox roll 34. The manifold includes an ink reservoir 32 and a doctor blade acting as a retaining blade and a scraper blade. The surface of anilox roll 34 includes cells that allow for the proper distribution of ink to be transferred to a printing roll 36. The surface of printing roll 36 includes a mirrored master of the required image as a 3D positive relief. Printing roll 36 transfers ink to the nonwoven web 10 while the nonwoven web 10 is pressed against the printing roll 36 by a counter-rotating impression cylinder 37.

[0010] 3, multiple units 31 including a manifold 33, anvil roll 34 and print roll 36 are arranged around a common impression cylinder 37 for multi-color printing in printing unit 30. A drying or curing unit 38 follows in-line. FIG. 4 shows a pattern of embossing projections on the surface of a calendar roll that has been used in the past to manufacture a common type of web. It includes elliptical embossing projections 26 of varying length d1 and width d2. The bond area is approximately 0.25 mm. 2 The distances a and b between the projections 26 are greater than 1.5 and greater than 2.5, respectively, and are set so that the number of projections per area is about 50 and the bonding area (meaning the proportion of the total surface area occupied by the flat projection surfaces) is about 18%. Figure 5 shows a pattern according to the invention, which is symmetrical and includes circular embossing projections with a diameter d of 0.4 mm. The bonding area is therefore approximately 0.125 mm 2 The pitch between the junctions, a (= b), is 1.12 mm. As a result, the number of junctions per area is 80 / cm 2 , the total bonding area is 10%. EXAMPLES

[0011] The examples compare the print quality of the microdot material of the present invention and a standard bonded nonwoven material. All tests were performed on the same 17 g / m 2 The test was carried out on a standard nonwoven material of polypropylene 3-ply spunbond (SSS). The comparative test samples were bonded using the bond pattern shown in Figure 4. The inventive test samples were bonded using the bond pattern shown in Figure 5. All samples were printed using flexographic ink printing with the exact same print image and under the exact same conditions (screen, sleeve, inks used, press, etc.). The measurement procedure was as follows: In the first step, the exact same parts of the print samples to be compared are glued on white paper and scanned (resolution at least 300 dpi) into a PDF. Then, each PDF is opened in Adobe Photoshop 2023 software, adjusted exactly to the part to be measured, and converted to grayscale. A gradation step is then applied to separate the dark uneven parts from the uniform parts. The pixels after the gradation curve is applied are displayed in black. For this purpose, a certain sensitivity is set so that different tones of luminance values ​​can be measured. The sensitivity setting is determined by the L value of the darkest tone of the part to be measured using a measuring device (X-Rite Exact). The default sensitivity value (input value) for an L value of 75 is 48. If the L value deviates from +1, the sensitivity value decreases by 2. If the L value deviates from -1, the sensitivity value increases by 2.

[0012] Finally, with the help of the histogram, we can read how many deviant black pixels are present in the printed area and compare the values ​​between the two types of materials. In all pressure ranges where the L value is below 85, the inventive material has less deviation than the comparative material. This was found for four different pictures P1 to P4, which are printing designs used in the absorbent hygiene industry. The results are shown in Table 1 below. [Table 1]

[0013] This was seen for a variety of different solid monochrome prints (rectangles), and the corresponding results are shown in Table 2 below. [Table 2]

[0014] [Table 3]

Claims

1. A printed nonwoven web containing a pattern of fused embossed bonds, the nonwoven web being ink printed on a surface exhibiting the pattern of bonds, The junction pattern must be: (a) The number of junctions on the surface is 70 / cm 2 More than 75 / cm 2 It is super (b) The average area size of each individual junction is 1.5 mm 2 Smaller, preferably 1.35 mm 2 Less than, and (c) the average center-to-center distance between bond points is less than 1.5 mm, preferably less than 1.3 mm; The printed nonwoven web satisfies the above.

2. 2. The printed nonwoven web of claim 1, wherein the bond area, defined as the percentage of the total surface area occupied by bond points, is less than 18%, preferably less than 15%, more preferably less than 12%, and even more preferably less than 11%.

3. 3. The printed nonwoven web of claim 1 or 2, wherein the web is a spunbond or spunmelt nonwoven web.

4. 1. A method of making a printed nonwoven web, comprising: a nonwoven web bonded by calendar embossing to form a nonwoven web containing a pattern of fused embossed bonds; and a nonwoven web ink printed on a surface exhibiting the pattern of bonds, comprising: The junction pattern must be: (a) The number of junctions on the surface is 70 / cm 2 More than 75 / cm 2 It is super (b) The average area size of each individual junction is 1.5 mm 2 Smaller, preferably 1.35 mm 2 Less than, and (c) the average center-to-center distance between bond points is less than 1.5 mm, preferably less than 1.3 mm; The above method is characterized in that

5. 5. The method according to claim 4, wherein the bond area, defined as the percentage of the total area of ​​the surface occupied by the bond points, is smaller than 18%, preferably smaller than 15%, more preferably smaller than 12%, even more preferably smaller than 11%.

6. 6. The method according to claim 4 or 5, wherein the ink printing is flexographic ink printing.

7. The method of claim 6, wherein the line screen is from 15 L / cm to 50 L / cm.

8. 6. The method according to claim 4 or 5, wherein the ink printing is inkjet printing.

9. The method of any one of claims 4 to 8, wherein the web is a spunbond nonwoven web.

10. The method of any one of claims 4 to 9, wherein the calendar embossing comprises ultrasonic embossing.

11. Use of the printed nonwoven web according to any of claims 1 to 10 for the production of hygiene articles, preferably for the production of diapers.