Fullerene structure and method for producing same

Abstract

Provided is a fullerene structure that includes a columnar-shaped portion and a fin portion protruding from the columnar-shaped portion, both the columnar-shaped portion and the fin portion being fullerenes. Provided is a method for producing a fullerene structure that includes heating a fullerene raw material to or above the sublimable temperature in the presence of a non-oxidizing gas and cooling the heated atmosphere of the fullerene raw material. In one example, the method includes supplying the non-oxidizing gas in one direction, and heating the fullerene raw material to or above the sublimable temperature on the upstream side and cooling the heated atmosphere of the fullerene raw material on the downstream side, with respect to the non-oxidizing gas supply direction.

Description

[Technical field]

[0001] The present invention relates to a fullerene structure, a method for producing the same, and an apparatus for producing the same. [Background technology]

[0002] Fullerenes are small spherical molecules that exhibit various excellent properties when used alone, but in the industrial field, they are widely used as fullerene aggregates, complexes, etc. For example, in organic solar cells, complexes containing fullerenes are used as acceptor materials, and in organic transistors, fullerenes are formed in the form of thin films on substrates and used. In such applications, fullerenes, which are spherical molecules, are in the form of fine powder, so particulate fullerenes are supported on a support and used. In order to improve the handling of fullerenes alone, it is desirable to form microscale structures of fullerenes. In addition, in microscale structures, it is desirable for fullerenes to have high crystallinity in order to obtain excellent properties when used alone.

[0003] There is a material called fullerene nanowhiskers, which are fullerenes linked together in a fibrous form. This structure is formed via a liquid-liquid interface formation method (Non-Patent Document 1: K. Miyazawa et al., Surf. Interface Anal. 35, 117 (2003).), so the formation speed is very slow, which is a bottleneck in industrial applications.

[0004] Patent Document 1 proposes a method for producing hollow hexagonal columnar fullerene microstructures by mixing an isopropyl alcohol solution containing a metal peroxide with a toluene solution containing fullerenes under low temperature conditions. In the method disclosed in Patent Document 1, the reaction is carried out in a solution at a low temperature, and therefore requires 10 hours or more.

[0005] Patent Document 2 proposes a method for producing fullerene nanowhiskers / nanofiber nanotubes carrying a metal catalyst by holding an isopropyl alcohol solution containing a platinum catalyst and / or a ruthenium catalyst and a toluene solution containing fullerene at -10 to 30°C while forming a liquid phase interface. In the method disclosed in Patent Document 2, the reaction is carried out at a liquid phase interface at a low temperature, and therefore requires 0.5 to 20 days.

[0006] Patent Document 3 proposes a method for producing fullerene nanowhiskers by creating two or more interfaces between a saturated solution of carbon fullerenes and a second solvent and precipitating aggregates of fullerene nanowhiskers at each interface. The method disclosed in Patent Document 3 aims to shorten the time required for forming fullerene nanowhiskers and improve the uniformity and control of the length of the structure, but the growth rate of fullerene nanowhiskers is about 1 μm / min.

[0007] Patent Document 4 proposes a carbon structure in which silver ion particles are formed on the surface of a thin wire made of fullerene molecules, and the thin wire forms a hexahedral shape. Patent Document 4 also proposes producing a carbon structure by incubating a silver ion solution in 1-butanol, adding the silver ion solution to the fullerene solution, forming a liquid-liquid interface between the fullerene solution and the silver ion solution, and precipitating a fullerene structure. In the examples of Patent Document 4, incubation of the silver ion solution takes 8 to 20 days, and precipitation of the fullerene structure takes 20 to 40 hours.

[0008] Patent Document 5 proposes a method for producing two-component fullerene nanowhiskers of the desired length and diameter by pouring a poor solvent into a mixed solution containing C60 powder and C70 powder to form a liquid-liquid interface and leaving the solution in which crystal nuclei are generated at 15°C for two days. [Prior art documents] [Patent documents]

[0009] [Patent Document 1] JP 2004-043245 A [Patent Document 2] JP 2006-083050 A [Patent Document 3] JP 2008-100874 A [Patent Document 4] JP 2011-219282 A [Patent Document 5] JP 2014-088305 A [Non-patent literature]

[0010] [Non-Patent Document 1] K. Miyazawa et al, Surf. Interface Anal. 35, 117 (2003) Summary of the Invention [Problem to be solved by the invention]

[0011] The methods for producing a fullerene structure disclosed in Patent Documents 1 to 5 all use a liquid-liquid interface, and the rate at which the fullerene structure is formed tends to be slow. In Patent Document 3, an attempt is made to shorten the formation time in a method using a liquid-liquid interface, but the method still requires a lot of time, making mass production difficult. Patent Documents 4 and 5 attempt to provide a fullerene structure having functionality, but do not achieve a sufficient reduction in the formation time.

[0012] An object of the present invention is to provide a fullerene structure having high crystallinity, and another object of the present invention is to provide a fullerene structure in a short time and easily. [Means for solving the problem]

[0013] The present invention relates to the following configuration. [1] A fullerene structure comprising a columnar portion and a fin portion protruding from the columnar portion, the columnar portion and the fin portion each being a fullerene. [2] The fullerene structure according to [1], wherein the fin portion is formed on at least one side surface of the columnar portion. [3] The fullerene structure according to [1] or [2], wherein the columnar portion and the fin portion are each a crystalline fullerene.

[0014] [4] A method for producing a fullerene structure, comprising heating a fullerene raw material in a non-oxidizing gas to a sublimation temperature or higher, and cooling the atmosphere in which the fullerene raw material is heated. [5] A method for producing a fullerene structure according to [4], comprising: supplying a non-oxidizing gas in one direction; heating the fullerene raw material to a sublimation temperature or higher on the upstream side of the supply direction of the non-oxidizing gas; and cooling the atmosphere in which the fullerene raw material is heated on the downstream side.

[0015] [6] An apparatus for producing a fullerene structure, comprising: a reaction vessel having a first compartment and a second compartment; a raw material input section disposed in the first compartment; a product recovery section disposed in the second compartment; a heater for heating the first compartment in the reaction vessel; a temperature control means for controlling the temperature of the second compartment in the reaction vessel to a lower temperature than that of the first compartment; and a gas supplying device for supplying a non-oxidizing gas to the reaction vessel. [7] The apparatus for producing a fullerene structure according to [6], wherein the reaction vessel is a reaction tube, the gas supplier supplies a non-oxidizing gas into the reaction tube from one end side in an axial direction of the reaction tube, and the first compartment is disposed on the upstream side and the second compartment is disposed on the downstream side with respect to a supply direction of the non-oxidizing gas. [8] The apparatus for producing a fullerene structure according to [6] or [7], wherein the heater heats the first section from an outer periphery of the reaction vessel. [9] The apparatus for producing a fullerene structure according to [6] or [7], wherein the heater is installed inside the reaction vessel.

[10] The apparatus for producing a fullerene structure according to any one of [6] to [9], further comprising a gas discharger for discharging gas from within the reaction vessel.

[11] The apparatus for producing a fullerene structure according to any one of [6] to

[10] , further comprising a cooler for cooling the second compartment in the reaction vessel.

[12] The apparatus for producing a fullerene structure according to any one of [6] to

[11] , further comprising a control unit for controlling the heater and the gas supplier, wherein the control unit controls the heater so that the temperature of the first compartment is equal to or higher than the sublimation temperature of the raw material, and controls the gas supplier to supply a non-oxidizing gas from the gas supplier so that the temperature of the second compartment is lower than that of the first compartment. Effect of the Invention

[0016] According to the present invention, a fullerene structure having high crystallinity can be provided. Also, according to the present invention, a fullerene structure can be provided easily in a short time. [Brief description of the drawings]

[0017] [Figure 1] FIG. 1 is a schematic explanatory diagram for explaining an example of a method for producing a fullerene structure. [Diagram 2] FIG. 2 is a schematic perspective view for explaining an example of a manufacturing apparatus for the fullerene structure. [Diagram 3] FIG. 3 is a schematic perspective view for explaining another example of the manufacturing apparatus for the fullerene structure. [Figure 4] FIG. 4 shows photographs of the fullerene structures recovered in Examples 1 to 4, with (a) to (d) showing photographs of Examples 1 to 4, respectively. [Diagram 5] FIG. 5 is a scanning electron microscope (SEM) photograph of the fullerene structure obtained in Example 1. [Figure 6] FIG. 6 is a scanning electron microscope (SEM) photograph of the fullerene structure obtained in Example 2. [Figure 7] FIG. 7 is a scanning electron microscope (SEM) photograph of the fullerene structure obtained in Example 3. [Figure 8] FIG. 8 shows the results of measuring the Raman spectrum of the fullerene structure obtained in Example 1. [Figure 9] FIG. 9 shows the results of measuring the XRD spectrum of the fullerene structure obtained in Example 1. [Figure 10] FIG. 10 is a scanning electron microscope (SEM) photograph of the fullerene structure obtained in Example 5. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0018] Hereinafter, one embodiment of the present invention will be described, but the present invention is not limited to the examples in the following embodiment.

[0019] (Fullerene structure) The fullerene structure according to the present embodiment includes a columnar portion and a fin portion protruding from the columnar portion, and the columnar portion and the fin portion are each made of fullerene. This makes it possible to provide a fullerene structure with high crystallinity.

[0020] The fullerene structure according to the present embodiment has a columnar shape and a fin portion made of fullerene, and therefore can exhibit its function without being supported by other substances. This fullerene structure can have a microscale or even a milliscale structure. A microscale fullerene structure is also advantageous in terms of handling. Nanoscale fine powder tends to be difficult to handle. In addition, the fullerene structure according to the present embodiment has high crystallinity and is densely packed with fullerenes, and therefore can exhibit superiority in terms of electrical conductivity and the like. In addition, fullerenes are promising as n-type conductive materials, and the fullerene structure according to the present embodiment is expected to have a wider range of applications. In addition, the fullerene structure according to the present embodiment has a structure in which the columnar shape portion extends in one direction, and is expected to be applied to electrical wiring and the like. The fullerene structure according to the present embodiment has the advantage that electrical contact is easy to make. In the fullerene structure according to the present embodiment, the columnar shape portion and the fin portion are preferably crystalline fullerenes. By using crystalline fullerenes for the columnar shape portion and the fin portion, the crystallinity is increased, and these advantages can be more effectively exhibited.

[0021] The fullerene structure according to this embodiment can be formed by vapor phase growth as described below, and can therefore be grown to the microscale or even millimeter scale in a short time. In contrast, conventional fullerene nanowhisker materials are formed at a liquid-liquid interface, and the formation speed is very slow. The method for producing a fullerene structure according to this embodiment can achieve a formation speed 100 times faster than conventional methods.

[0022] The fullerene structure according to one embodiment preferably has a shape including a columnar shape portion and a fin portion protruding from the columnar shape portion.Furthermore, the fullerene structure preferably has a shape including a columnar shape portion and a fin portion protruding from at least one side surface of the columnar shape portion.

[0023] In the fullerene structure, the columnar shape has a minor axis and a major axis, and may have a general outer shape of a circular cylinder, an elliptical cylinder, a polygonal cylinder, or the like. The polygonal cylinder shape may be a triangular cylinder, a quadrangular cylinder, a pentagonal cylinder, a hexagonal cylinder, or the like. The columnar shape may have a general outer shape of a column, and may have a groove, a protrusion, or the like formed along the major axis direction of the columnar shape. The columnar shape is preferably a solid shape. The columnar shape may have a substantially uniform cross-sectional shape in a direction perpendicular to the long axis over the entire length of the long axis, or may have a different cross-sectional shape, for example, a tapered shape having a large cross-sectional shape at one end and a thin cross-sectional shape at the other end. In the case of a columnar shape, a crystal may grow in one direction along the long axis from the crystal nucleus as a starting point after the crystal nucleus is generated. In this state, the columnar shape often becomes tapered, with one end being thicker and the other end being thinner.

[0024] The fins are formed to protrude from the columnar shape, and because the fins are integrally formed with the columnar shape, they can maintain their shape during a certain degree of mixing, dispersion, and the like. It is believed that the fin portion is formed in order to ensure a stable crystal shape due to the high crystallinity of the fullerene structure, and that the planar area of ​​the fin portion increases when the stable surface of the crystal becomes dominant. The shape of the fin is not particularly limited, but it is preferable that the fin protrudes from the side surface of the columnar shape and has at least one flat area. More preferably, the fin protrudes from the side surface of the columnar shape by a length that is 0.5 times or more, more preferably 0.8 times or more, the minor axis of the cross section of the columnar shape at the portion where the fin protrudes. The shape of the fin is not particularly limited, but it is preferable that the length (a) parallel to the long axis of the columnar part is longer than the maximum length (b) in the direction perpendicular to the long axis of the columnar part. For example, it is more preferable that a / b is 1.1 times or more, and further more preferable that a / b is 1.2 times or more. The shape of the fin is not particularly limited, and may be formed over the entire length of the major axis of the columnar part, or may be formed partially. For example, the length (a) of one fin part relative to the major axis (c) of the columnar part is preferably a / c 0.1 to 0.8, more preferably a / c 0.2 to 0.5, and more preferably a / c 0.2 to 0.4.

[0025] One embodiment of a fullerene structure is shown in Figure 5. In Figure 5, x is the columnar feature and y is the fin feature.

[0026] In one fullerene structure, one or more fin portions may be formed on the columnar portion. In this case, one or more fin portions may be formed on one side surface of the columnar portion, or one or more fin portions may be formed on each of two or more side surfaces of the columnar portion.

[0027] The size of the fullerene structure is not particularly limited, but the minor axis is preferably 1 μm or more, may be 10 μm or more, or may be 50 μm or more. The aspect ratio of the minor axis to the major axis is not particularly limited, but is preferably 1:1.1 or more, more preferably 1:1.5 or more, and may be 1:2 or more. Here, the minor axis and major axis of the fullerene structure are values ​​determined from the size of the overall external shape including the columnar portion and the fin portion.

[0028] The fullerene structure may be any of various fullerenes, such as C60, C70, C76, and C80. The fullerene structure may be a fullerene derived from a fullerene raw material, such as a fullerene derivative or a functional fullerene modified with an organic molecule. These may be used alone or in combination of two or more. It is preferable that the fullerene structure exhibits crystallinity as a whole, and specifically, it is preferable that the columnar portion and the fin portion are each made of crystalline fullerene. It is preferable that the fullerene structure has a face-centered cubic lattice.

[0029] (Method of manufacturing fullerene structure) An example of a method for producing the fullerene structure according to the present embodiment will be described below. Note that the fullerene structure according to the present embodiment is not limited to the one produced by the following production method. The method for producing a fullerene structure according to the present embodiment is characterized by including heating a fullerene raw material in a non-oxidizing gas to a sublimation temperature or higher, and cooling the atmosphere in which the fullerene raw material is heated. According to this method, a fullerene structure can be provided easily in a short time, and a fullerene structure having high crystallinity can be provided. According to this manufacturing method, a fullerene structure can be provided by a relatively simple technique of heat treatment. Also, according to this manufacturing method, a fullerene structure can be provided without using a liquid phase or a catalyst, and a high-purity fullerene structure can be provided.

[0030] In the step of heating the fullerene raw material, the heating temperature is preferably equal to or higher than the sublimation temperature of the fullerene. Sublimation temperature refers to the temperature at which the fullerenes begin to at least partially sublime. Specifically, the heating temperature is preferably 700° C. or higher, more preferably 800° C. or higher, and even more preferably 900° C. or higher. By heating at 700° C. or higher, fullerenes begin to partially sublimate. Although it depends on reaction conditions such as the size and shape of the reaction vessel and heating time, by heating at 800° C. or higher, more fullerenes are sublimated. The heating temperature is sufficient as long as the fullerene is partially sublimated. By heating to the sublimation temperature of the fullerene or higher, the time required for the fullerene to sublime can be shortened and the reaction can be carried out efficiently. From this viewpoint, the heating temperature is preferably 1200°C or less, more preferably 1000°C or less, and even more preferably 950°C or less. For example, the heating temperature is preferably 700 to 1200°C, more preferably 800 to 1000°C, and even more preferably 900 to 950°C.

[0031] In the step of heating the fullerene raw material, the atmosphere is preferably non-oxidizing, and more preferably inert, so that the generation of by-products due to oxidation reactions can be prevented. Examples of the non-oxidizing gas include inert gases such as argon gas, nitrogen gas, and helium gas, and may be a mixed gas of these gases. The inside of the reaction vessel may be a vacuum atmosphere. In the step of heating the fullerene raw material, it is preferable to make the inside of the reaction vessel a non-oxidizing gas in a temperature range equal to or higher than the sublimation temperature. For example, in order to increase the cleanliness of the inside of the reaction vessel, the inside of the reaction vessel may be replaced with a non-oxidizing gas before starting heating of the fullerene raw material. In the process of heating the fullerene raw material, the non-oxidizing gas may be filled in the reaction vessel. For example, the reaction vessel is filled with the non-oxidizing gas, and then the reaction vessel is heated. The heated atmosphere is transported to the non-heated region by air convection, whereby the heated atmosphere is cooled and the fullerene structure is precipitated. As will be described later in detail, the non-oxidizing gas may be continuously supplied into the reaction vessel to generate a unidirectional air flow in the reaction tube, so that the heated atmosphere is transported to the non-heated region.

[0032] In addition, in the step of cooling the atmosphere in which the fullerene raw material is heated, it is preferable to make the inside of the reaction vessel a non-oxidizing gas in a temperature range of the sublimation temperature or higher. For example, it is more preferable to make the inside of the reaction vessel a non-oxidizing gas in a temperature range of 300°C or higher in the cooling step, and the inside of the reaction vessel may be a non-oxidizing gas during cooling to room temperature.

[0033] In the step of heating the fullerene raw material, the heating time is appropriately adjusted depending on reaction conditions such as the mass of the raw material to be charged, the size of the reaction vessel, the heating temperature, etc. The heating time is the time from when a predetermined heating temperature is reached to when the temperature is cooled below that temperature. For example, the heating time is preferably 10 minutes or more, more preferably 30 minutes or more, and even more preferably 1 hour or more, which can further promote the sublimation of the fullerene raw material and precipitate the fullerene structure. The heating time is preferably 10 hours or less, more preferably 5 hours or less, and may be 2 hours or less. In the method according to one embodiment, the fullerene structure can be precipitated even in a short heat treatment, so that the reaction can be carried out for a shorter time within this range. The size of the obtained fullerene structure tends to be large due to a high heating temperature, a long heating time, etc. Therefore, the heating temperature and the heating time may be appropriately adjusted according to the desired size. For example, as the heating time is longer, the precipitated fullerene structure tends to be longer in the long axis direction. Therefore, in order to obtain a structure longer in the long axis direction, it is recommended to extend the heating time.

[0034] In the step of heating the fullerene raw material, the rate of temperature rise depends on the heating method, the size of the reaction vessel, etc., but is preferably 10 to 100° C. / min, and more preferably 20 to 30° C. / min, for example. In the step of heating the fullerene raw material, the pressure is not particularly limited, and the reaction can be carried out under atmospheric pressure.

[0035] In the step of heating the fullerene raw material, the amount of the fullerene raw material to be added can be appropriately set according to the production conditions such as the size of the reaction vessel, etc. The fullerene raw material may be batch-processed or continuously added.

[0036] The step of cooling the atmosphere in which the fullerene raw material is heated is carried out in order to cool the atmosphere containing the sublimated fullerene raw material after the step of heating the fullerene raw material. As a result, fullerene crystal nuclei are precipitated from the atmosphere containing the sublimated fullerene raw material, and crystalline fullerenes are deposited in the reaction vessel, for example, on the bottom surface of the reaction vessel. Since the deposited fullerenes are maintained at a relatively high temperature, it is believed that they remain active and crystal growth proceeds slowly. Finally, a fullerene structure having a columnar shape with fins can be formed.

[0037] In the step of cooling the atmosphere in which the fullerene raw material is heated, the cooling is preferably performed to a temperature lower than the sublimation temperature of fullerene, and more preferably to a temperature lower than the temperature at which fullerene crystal nuclei begin to precipitate. The cooling may be performed by leaving the material in air, by forcibly cooling the material using a cooler, or by cooling the material at a slow cooling rate.

[0038] The fullerene raw material is not particularly limited and may be various types of fullerene, for example, C60, C70, C76, C80, etc. As the fullerene raw material, a fullerene derivative, a functional fullerene modified with an organic molecule, or the like may be used. The fullerene raw material may be in any form such as powder, granules, or lumps. The fullerene raw materials may be used alone or in combination of two or more kinds.

[0039] A preferred example of a method for producing a fullerene structure includes supplying a non-oxidizing gas in one direction, heating a fullerene raw material to a sublimation temperature or higher on the upstream side of the supply direction of the non-oxidizing gas, and cooling the atmosphere in which the fullerene raw material is heated on the downstream side. In this method, the fullerene raw material can be heated and cooled more easily.

[0040] By supplying the non-oxidizing gas in one direction, a one-way airflow is generated in the reaction system. By heating the fullerene raw material upstream of the supply direction of the non-oxidizing gas to a sublimation temperature or higher, the fullerene raw material is heated on the upstream side, and an atmosphere containing the fullerene raw material can be formed. Then, this atmosphere is transported downstream along the one-way airflow, and during the process of being transported to the non-heated area on the downstream side, the atmosphere containing the fullerene raw material is exposed to an area with a lower temperature. In this way, the atmosphere containing the fullerene raw material is cooled, and nuclei of fullerene crystals are formed, and the fullerene structure is precipitated. At this time, the fullerene structure is precipitated and deposited at a location downstream of the one-way airflow where the cooling temperature is appropriate. In such a reaction system, the heating temperature of the fullerene raw material, the supply rate of the non-oxidizing gas, etc. can be controlled to keep the temperature gradient constant throughout the reaction system, thereby making it possible to almost fix the position where the fullerene structure precipitates and accumulates.

[0041] The supply rate of the non-oxidizing gas is preferably 0.1 to 2 L / min, and more preferably 0.2 to 1 L / min. The non-oxidizing gas may be discharged into the atmosphere through a gas exhaust pipe, or may be forcibly discharged using a fan or the like.

[0042] A schematic diagram for explaining this method is shown in Fig. 1. Fig. 1 is a diagram showing a schematic cross section of a reaction tube, in which 31 is the reaction tube, 32 is a raw material input section, 33 is a product recovery section, 34 is a heater, 38 is a sample stage on which the fullerene raw material is placed, and X indicates the supply direction of the non-oxidizing gas. The fullerene raw material is placed on the raw material input section 32 on the sample stage 38 in the reaction tube 31, and the heating region is heated from the outside of the reaction tube 1 by the heater 34. 3 By heating 1a, the fullerene raw material is heated to a sublimation temperature or higher and sublimes. Then, the atmosphere containing the fullerene raw material is carried to the non-heated region 31b downstream in the supply direction X by the airflow of the non-oxidizing gas. Then, nuclei of fullerene crystals are formed in the product recovery section 33 downstream in the supply direction X, and the fullerene structure is precipitated.

[0043] (Production equipment for fullerene structures) An example of a manufacturing apparatus for the fullerene structure according to the present embodiment will be described below. Note that the fullerene structure according to the present embodiment is not limited to one manufactured by the manufacturing apparatus described below. Also, the manufacturing method for the fullerene structure according to the present embodiment is not limited to a method using the manufacturing apparatus described below.

[0044] The fullerene structure manufacturing apparatus according to this embodiment is characterized by comprising a reaction vessel having a first compartment and a second compartment, a raw material input section disposed in the first compartment, a product recovery section disposed in the second compartment, a heater for heating the first compartment in the reaction vessel, a temperature control means for controlling the temperature of the second compartment in the reaction vessel to a lower temperature than the first compartment, and a gas supplier for supplying a non-oxidizing gas to the reaction vessel. According to this method, a fullerene structure can be provided easily in a short time, and a fullerene structure having high crystallinity can be provided. According to this manufacturing apparatus, a fullerene structure can be provided by a relatively simple method of heat treatment. Also, according to this manufacturing apparatus, a fullerene structure can be provided without using a liquid phase or a catalyst, and a high purity fullerene structure can be provided.

[0045] In a preferred example of the fullerene structure manufacturing apparatus according to this embodiment, the reaction vessel is a reaction tube, the gas supplier supplies a non-oxidizing gas into the reaction tube from one end side in the axial direction of the reaction tube, and the first compartment is arranged on the upstream side and the second compartment is arranged on the downstream side with respect to the supply direction of the non-oxidizing gas. In this device, the temperature adjustment means controls the flow of non-oxidizing gas and heating by a heater, making it possible to adjust the temperature of the second compartment in the reaction vessel to a lower temperature than the first compartment. The method of adjusting the second compartment in the reaction vessel to a lower temperature than the first compartment is not limited to this, and a temperature gradient may be generated within the reaction vessel by heating one location within the reaction vessel and utilizing air convection.

[0046] FIG. 2 shows an example of an apparatus for producing a fullerene structure according to an embodiment. In the fullerene structure manufacturing apparatus 100 shown in Fig. 2, 1 is a reaction tube, 2 is a raw material input section, 3 is a product recovery section, 4 is a heater, 5 is a gas supplying section, 6 is a gas supply pipe, 7 is a gas exhaust pipe, and 8 is a sample stage. The heater 4 and the gas regulating valve 6a of the gas supplying pipe 6 are connected to a control section 10 and can be controlled. In the figure, X indicates the gas supply direction. As another example of the manufacturing apparatus, a control unit for controlling the heater 4 and a control unit for controlling the gas regulating valve 6a of the gas supply pipe 6 may be provided separately.

[0047] The reaction tube 1 is divided into a non-heating region 1c, a heating region 1a as a first section, and a non-heating region 1b as a second section, in that order from the upstream side in the gas supply direction X. The reaction tube 1 is preferably made of a material that is resistant to heating temperatures and does not allow impurities to be mixed into the tube at high temperatures, such as quartz glass, ceramics, and the like. The reaction tube 1 is preferably cylindrical in order to distribute the pressure load uniformly within the reaction tube and to prevent damage to the reaction tube.

[0048] The heater 4 is a coil heater, and is installed in the heating region 1a by being wound around the outer circumferential surface of the reaction tube 1. The coil heater of the heater 4 is connected to a power source (not shown), and generates heat when a current flows through it, and the temperature can be controlled by the amount of current. This temperature control can be performed by the control unit 10. The heater 4 is not limited to a coil heater, and various heaters such as a panel heater, a radiant heater, etc. Depending on the type and size of the reaction vessel, a heater may be provided inside the reaction vessel.

[0049] A sample stage 8 can be placed inside the reaction tube 1. The sample stage 8 is capable of loading fullerene raw materials and depositing fullerene structures after the reaction, allowing them to be collected. The sample stage 8 is placed inside the reaction tube 1 so that its height can be adjusted. The sample stage 8 is preferably made of a material that is heat resistant and has low reactivity even at high temperatures, such as a quartz substrate or a silicon (Si) substrate. Although the sample stage 8 does not have to be used, taking into consideration cleaning of the inside of the reaction tube 1, using the sample stage 8 enables the reaction to be carried out continuously and smoothly.

[0050] The gas supplier 5 is filled with a non-oxidizing gas and can supply the non-oxidizing gas to the reaction tube 1 through a gas supply pipe 6. The gas supplier 5 is connected to one end of the reaction tube 1 and can supply the non-oxidizing gas from the one end of the reaction tube 1. A gas control valve 6a is installed between the gas supplier 5 and the reaction tube 1, and the supply amount of the non-oxidizing gas can be controlled by the control unit 10.

[0051] A gas exhaust pipe 7 as a gas exhauster is connected to the other end of the reaction tube 1, and is capable of exhausting gas from the other end of the reaction tube 1. The exhausted gas may be exhausted by opening to the atmosphere. Alternatively, the exhausted gas may be forcibly exhausted using a fan or the like. The exhausted gas may be treated by an exhaust treatment device (not shown).

[0052] The raw material input section 2 is disposed in the heating region 1a in the reaction tube 1. The fullerene raw material may be input and placed in the region where the coil heater of the heater 4 is wound. The product recovery section 3 is disposed in the non-heated region 1b in the reaction tube 1. This position corresponds to the region where the coil of the heater 4 is not wound. More specifically, the position of the product recovery section 3 corresponds to the position where the atmosphere containing the fullerene raw material heated and sublimated in the heating region 1a is transported downstream in the gas supply direction X and cooled to an appropriate temperature in the non-heated region 1b. This position can be fixed by controlling the size and shape of the reaction tube, the supply rate of the non-oxidizing gas, the heating temperature, etc.

[0053] Another example of the manufacturing apparatus for a fullerene structure according to an embodiment is shown in Fig. 3. In Fig. 3, the same reference numerals are used for the members common to Fig. 2, and the portions not specifically described are the same as those in Fig. 2. In FIG. 3, the manufacturing apparatus 100 for producing a fullerene structure includes a raw material introduction pipe 9. The raw material introduction tube 9 has a heat-resistant tubular structure, and is inserted so that it penetrates the reaction tube 1 in the non-heated region 1c and its opening is positioned near the raw material introduction section 2 inside the reaction tube 1. This makes it possible to introduce the fullerene raw material into the raw material introduction section 2 inside the reaction tube 1 from outside the reaction tube 1. By using this device, the raw material can be continuously introduced and the reaction can be carried out while maintaining the atmosphere inside the reaction tube 1 constant and heating by the heater 4. A lid may be provided on the opening of the raw material introduction tube 9 on the side where the raw material is introduced. By covering the opening of the raw material introduction tube 9 while the raw material is not being introduced from the raw material introduction tube 9, the atmosphere and temperature in the reaction tube 1 can be kept more uniform.

[0054] The fullerene structure according to the present embodiment can be applied as a carbon material in the fields of batteries, organic electronics, etc. Specifically, it can be applied to organic transistors, electrode materials for fuel cells, electrode materials for organic solar cells, catalyst support materials, n-type carbon materials, etc. EXAMPLES

[0055] The present invention will be described in more detail below with reference to examples, but the present invention is not limited to these.

[0056] (Production Example 1) A fullerene structure was produced from the fullerene raw material according to the following procedure. The fullerene raw material is fullerene-C 60 (Sigma-Aldrich, 98%) was used. The heating device used was a small cylindrical uniform temperature heat treatment device. A schematic diagram of this device is shown in Figure 2. In the experiment, two silicon substrates were placed on the sample stage 8, one in the fullerene raw material input section 2 and the other in the product recovery section 3. First, fullerene raw material was placed on a silicon (Si) substrate, which was then placed in the reaction tube 1, and the portion where the fullerene raw material was placed was adjusted to be located in the heated region 1a. A silicon substrate for recovery was also placed in the non-heated region 1b in the reaction tube 1. Next, argon gas was supplied from one end of the reaction tube 1 at 0.5 L per minute and discharged from the other end, filling the reaction tube 1 with argon gas. Next, the heating region 1a of the reaction tube 1 was heated by the coil heater 4 while argon gas was being supplied at 0.5 L per minute. The heating rate was 20 to 30°C / min, and after the heating temperature was reached, the material was held for 1 hour and then air-cooled. After the material was cooled to 300°C or less, the supply of argon was stopped. The heating temperature was as shown in Table 1.

[0057] By heating the heating region 1a of the reaction tube 1, the fullerene raw material is sublimated, and the atmosphere containing the fullerene raw material is transported by argon gas to the downstream non-heated region 1b, where fullerene crystals precipitate at a certain location and are deposited on a silicon substrate for recovery.

[0058] The reaction tube had an inner diameter of φ36 mm, an axial major axis of 500 mm, and was made of quartz glass. The silicon substrate (fullerene raw material input portion) was 2 mm x 2 mm. The silicon substrate (product collection section) was 1 mm x 3 mm. The dosage of the fullerene raw material was set to 0.1 to 0.3 g.

[0059] The amount of fullerene crystals produced relative to the amount of fullerene raw material supplied was observed, and the precipitation of fullerene crystals was evaluated according to the following criteria. The results are shown in Table 1. A: The formation of fullerene crystals was confirmed. B: The generation of fullerene crystals was confirmed, but the amount of fullerene crystals generated was less than that of A above. C: The formation of fullerene crystals was not confirmed.

[0060] [Table 1]

[0061] As shown in the table, C 60 In the case of fullerenes, the generation of fullerene crystals could be confirmed by controlling the heating temperature to above 700°C. When heated to 800° C. or higher, a large amount of the fullerene raw material was sublimated, and a large amount of fullerene crystals were precipitated in the cooling portion of the non-heated region 1b. When heated to 700°C, the amount of sublimation of the fullerene raw material decreased slightly, and the amount of fullerene crystals produced in the cooling section also decreased slightly. At 650° C., almost the entire amount of the fullerene raw material remained in the heating region 1a, and no generation of fullerene crystals was observed in the cooling region. Photographs of fullerene crystals deposited on a silicon substrate for collection in the non-heated region 1b are shown in FIG. 4. In the figure, (a) to (d) show photographs of Examples 1 to 4, respectively. In the figures, the black parts are the silicon substrates. Granular fullerene crystals were observed on the silicon substrate in Examples 1 to 3, but no fullerene crystals were observed in Example 4.

[0062] The obtained fullerene structure was observed with a scanning electron microscope (SEM). Figure 5 shows an SEM photograph of Example 1, Figure 6 shows an SEM photograph of Example 2, and Figure 7 shows an SEM photograph of Example 3. The white lines at the bottom of the SEM photographs indicate a 100 μm scale bar in Figures 5 and 6, and a 10 μm scale bar in Figure 7. From these figures, it was confirmed that the fullerene structures of Examples 1 to 3 have a structure with a fin portion on a columnar portion. In Example 1, which was treated at a higher temperature, the crystallinity was good, and a clean columnar portion and a large fin portion were confirmed. This is thought to be because, in the high-temperature heating, energetically stable plane orientations were preferentially formed, the number of plane orientations was reduced, and the fin portion grew large. In Example 2, an irregular structure was observed in some parts. In Example 3, it was confirmed that the shape of the fin portion formed on the columnar portion was small, and the fin portion had various plane orientations. This is thought to be due to the decrease in crystallinity due to the low-temperature treatment.

[0063] FIG. 8 shows the results of measuring the Raman spectrum of the fullerene structure obtained in Example 1. From this figure, the fullerene structure of Example 1 is C 60 It was confirmed that it was a fullerene.

[0064] FIG. 9 shows the results of measuring the XRD spectrum of the fullerene structure obtained in Example 1. From this figure, it was confirmed that the fullerene structure of Example 1 was a face-centered cubic lattice (fcc). Since the fullerene structure of Example 1 exhibited a neat face-centered cubic lattice, it is believed that the flat surface of the fin portion formed in the columnar shape portion became larger in the SEM photograph shown in FIG.

[0065] (Production Example 2) A fullerene structure of Example 5 was produced in the same manner as in Example 1 of the above Production Example 1, except that the heating time was changed to 10 minutes. The results of scanning electron microscope (SEM) observation of the obtained fullerene structure are shown in Figure 10. The white line at the bottom of the SEM image indicates a 100 μm scale bar. From this figure, it was observed that columnar crystals with fins were formed even with a heating time as short as 10 minutes. Comparing the SEM photographs of Example 1 and Example 5, it can be confirmed that the longer heating time, 1 hour, leads to more advanced crystal growth and larger fins formed in the columnar crystals. [Explanation of symbols]

[0066] 1 reaction tube, 2 raw material input section, 3 product recovery section, 4 heater, 5 gas supply, 6 gas supply pipe, 7 gas exhaust pipe, 8 sample stage, 9 raw material input pipe, 10 control section, 100 apparatus, 31 reaction tube, 32 raw material input section, 33 product recovery section, 34 heater, 38 sample stage

Claims

1. A fullerene structure comprising a columnar portion and a fin portion protruding from the columnar portion, the columnar portion and the fin portion each being a fullerene.

2. The fullerene structure according to claim 1 , wherein the fin portion is formed on at least one side surface of the columnar portion.

3. 3. The fullerene structure according to claim 1, wherein the columnar portion and the fin portion are each a crystalline fullerene.

4. The fullerene structure according to claim 1 , which is a microscale fullerene structure.

5. The fullerene structure according to claim 1 , which is a millimeter-scale fullerene structure.

6. The fullerene structure according to claim 1 , wherein the short diameter of the fullerene structure is 1 μm or more.

7. The fullerene structure according to claim 6 , wherein the short diameter of the fullerene structure is 50 μm or more.

8. 8. The fullerene structure according to claim 1, which is a crystalline fullerene having a face-centered cubic lattice.

9. A method for producing a fullerene structure, comprising: heating a fullerene raw material under a non-oxidizing gas to a temperature at which the fullerene raw material can be sublimated or higher; and cooling the atmosphere in which the fullerene raw material is heated, wherein the cooling is performed by cooling the atmosphere containing the fullerene raw material to a temperature below a temperature at which fullerene crystal nuclei begin to precipitate, and the cooling is performed by allowing the fullerene raw material to cool in air.

10. A method for producing a fullerene structure, comprising: heating a fullerene raw material under a non-oxidizing gas to a temperature at or above the sublimation temperature; and cooling the atmosphere in which the fullerene raw material is heated, the cooling being performed by cooling the atmosphere containing the fullerene raw material to a temperature below a temperature at which fullerene crystal nuclei begin to precipitate, and the cooling being performed by forced cooling using a cooler.

11. 11. The method for producing a fullerene structure according to claim 9 or 10, comprising: supplying a non-oxidizing gas in one direction, heating the fullerene raw material to a sublimation temperature or higher on the upstream side with respect to the supply direction of the non-oxidizing gas, and cooling the atmosphere in which the fullerene raw material is heated on the downstream side.

12. The method for producing a fullerene structure according to claim 9 , wherein the fullerene raw material is heated at 800° C. or higher.

13. The method for producing a fullerene structure according to claim 12, wherein the fullerene raw material is heated at 900° C. or higher.

14. The method for producing a fullerene structure according to claim 9 , wherein the heating time of the fullerene raw material is 10 hours or less.

15. The method includes heating a fullerene raw material in a non-oxidizing gas to a sublimation temperature or higher, and cooling the atmosphere in which the fullerene raw material is heated, The heating and cooling are performed by supplying a non-oxidizing gas in one direction, heating the fullerene raw material to a sublimation temperature or higher on the upstream side with respect to the supply direction of the non-oxidizing gas, and cooling the atmosphere in which the fullerene raw material is heated on the downstream side, The cooling is performed by cooling the atmosphere containing the fullerene raw material in air to a temperature below the temperature at which fullerene crystal nuclei start to precipitate.