Membrane carrier for test kit and test kit

Abstract

To provide a film carrier for inspection kit capable of obtaining an inspection kit with improved detection sensitivity, and an inspection kit with improved detection sensitivity.SOLUTION: There is provided a film carrier for inspection kit for detecting a substance to be detected in a liquid sample, the film carrier for inspection kit comprises: a channel having a detection zone. The channel has a rugged structure A having a protrusion part. In at least the detection zone, on a surface of the protrusion part, a fine rugged structure B is formed. On a surface of the fine rugged structure B, a silane coupling agent is adhered. A maximum peak height Rp of a roughness curve of the protrusion part on which the fine rugged structure B is formed, measured using a three-dimensional roughness analysis scanning electron microscope in accordance with JIS B 0601:2013, is 0.005 μm or more and 10 μm or less, and an average length RSm of a roughness curve element is 0.01 μm or more and 15 μm or less.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a membrane carrier for a test kit and a test kit. [Background technology]

[0002] In recent years, point-of-care testing (POCT) reagents that use antigen-antibody reactions to measure infectious disease, pregnancy, blood sugar levels, etc., have been attracting attention. POCT reagents are, for example, reagents for testing performed next to the subject or by the subject themselves, and have the characteristics of being able to determine results in a short time, being simple to use, and being inexpensive. Due to these characteristics, they are often used for examinations when symptoms are at a mild stage or for regular examinations, and are also important examination tools in home medical care, which is expected to increase in the future.

[0003] In many POCT reagents, a liquid sample such as blood is introduced into a test kit, and a judgment is made by detecting a specific target substance contained therein. Immunochromatography is often used as a method for detecting a specific target substance from a liquid sample. In immunochromatography, a liquid dropped onto a membrane carrier of a test kit moves on the membrane carrier, where the target substance and a labeling substance bind to each other, and these then specifically bind to a substance immobilized in the test kit (hereinafter referred to as a detection substance), and the resulting changes in color, mass, etc. are detected. The detection substance may also be called a reagent.

[0004] Nitrocellulose membranes are often used as membrane carriers for moving liquid samples (Patent Document 1). Nitrocellulose membranes have many fine pores with diameters of about several μm, through which liquid samples move by capillary force.

[0005] However, since nitrocellulose membranes are derived from natural products and the pore size and the way the pores are connected to each other are not uniform, the flow rate of the liquid sample varies with each membrane. If there is a difference in the flow rate, the time it takes to detect the target substance also changes, and as a result, it may be erroneously determined that the target substance is not detected before it binds to the target substance.

[0006] To solve the above problems, a liquid sample testing kit with an artificially created microchannel has been devised (Patent Document 2). Patent Document 2 uses synthetic materials to create a membrane carrier with a uniform structure, reducing the possibility of erroneously determining that a substance to be detected is undetectable before it binds to the substance.

[0007] When using synthetic materials, in order to improve detection sensitivity, it is necessary to increase the affinity between the detection substance and the material, and it is considered effective to perform various surface treatments on the material in advance (Patent Documents 3-4). Patent Document 5 discloses a membrane carrier for a test kit for detecting a target substance in a liquid sample, which has at least one flow path capable of transporting the liquid sample, and a microstructure that generates a capillary action for transporting the liquid sample is provided on the bottom surface of the flow path. [Prior art documents] [Patent documents]

[0008] [Patent Document 1] JP 2014-062820 A [Patent Document 2] Patent No. 5799395 [Patent Document 3] JP 2013-113633 A [Patent Document 4] US Patent Application Publication No. 2011 / 0284110 [Patent Document 5] International Publication No. 2016 / 098740 Summary of the Invention [Problem to be solved by the invention]

[0009] There is a demand for further improvement in the detection sensitivity of such test kits.

[0010] The present invention has been made in consideration of the above circumstances, and provides a membrane carrier for a test kit that enables a test kit with improved detection sensitivity to be obtained, and a test kit with improved detection sensitivity. [Means for solving the problem]

[0011] The present inventors have conducted extensive research to achieve the above object. As a result, they have found that the detection sensitivity of a substance to be detected in a liquid sample can be improved by providing a channel of a membrane carrier with a concave-convex structure having protrusions to which a silane coupling agent is attached, while the maximum peak height Rp of the roughness curve and the average length RSm of the roughness curve element are within a specific range, and have arrived at the present invention.

[0012] That is, according to the present invention, there are provided the following membrane carrier for a test kit and the test kit.

[0013] [1] A membrane carrier for a test kit for detecting a target substance in a liquid sample, comprising: a flow path having a detection zone; The flow channel has a concave-convex structure A having a protrusion, A fine relief structure B is formed on the surface of the protrusion at least in the detection zone, A silane coupling agent is attached to the surface of the microrelief structure B, A membrane carrier for a test kit, in which the maximum peak height Rp of the roughness curve of the protrusion portion on which the micro-convex and concave structure B is formed is 0.005 μm or more and 10 μm or less, and the average length RSm of the roughness curve element is 0.01 μm or more and 15 μm or less, as measured using a three-dimensional roughness analysis scanning electron microscope in accordance with JIS B0601:2013. [2] In the membrane carrier for the test kit according to the above [1], The membrane carrier for the test kit, wherein the silane coupling agent is at least one selected from a silane coupling agent having an amino group, a silane coupling agent having a mercapto group, a silane coupling agent having an epoxy group, a silane coupling agent having an acrylic group, a silane coupling agent having a methacryl group, a silane coupling agent having a vinyl group, and a silane coupling agent having an isocyanate group. [3] In the membrane carrier for a test kit according to the above [1] or [2], A membrane carrier for a test kit, in which a crosslinking agent is further attached to the surface of the above-mentioned fine uneven structure B. [4] In the membrane carrier for the test kit according to the above [3], A membrane carrier for a test kit, wherein the crosslinking agent comprises at least one selected from glutaraldehyde, dextran, 1,4-phenyl diisocyanate, toluene-2,4 diisocyanate, polyethyleneimine, 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide, N-succinimidyl 4-(N-maleimidomethyl)cyclohexane-1-carboxylate and N-hydroxysuccinimide. [5] In the membrane carrier for a test kit according to any one of the above [1] to [4], The uneven structure A is a membrane carrier for a test kit containing a thermoplastic resin. [6] In the membrane carrier for the test kit according to the above [5], The above thermoplastic resin is a membrane carrier for a test kit, which contains at least one selected from polyester-based resins, polyolefin-based resins, polystyrene-based resins, polycarbonate-based resins, fluorine-based resins, and (meth)acrylic resins. [7] In the membrane carrier for a test kit according to any one of the above [1] to [6], A membrane carrier for a test kit, wherein the average height of the protrusions is 5 μm or more and 1000 μm or less. [8] In the membrane carrier for a test kit according to any one of the above [1] to [7], A membrane carrier for a test kit, wherein the average distance between adjacent protrusions in the uneven structure A is 500 μm or less. [9] In the membrane carrier for a test kit according to any one of the above [1] to [8], A membrane carrier for a test kit, wherein the average diameter of the bottom surface of the protrusions is 5 μm or more and 1000 μm or less.

[10] A test kit comprising the membrane carrier for a test kit according to any one of [1] to [9] above. Effect of the Invention

[0014] According to the present invention, it is possible to provide a membrane carrier for a test kit which makes it possible to obtain a test kit with improved detection sensitivity, and a test kit with improved detection sensitivity. [Brief description of the drawings]

[0015] [Figure 1] FIG. 1 is a schematic top view of a test kit, which is an example of an embodiment according to the present invention. [Diagram 2] FIG. 2 is a schematic top view of a membrane carrier, which is an example of an embodiment according to the present invention. [Diagram 3] FIG. 1A is an example of an embodiment according to the present invention, and is an overhead view (top view) of a concave-convex structure A, and FIG. 1B is a perspective view of protrusions constituting the concave-convex structure A shown in FIG. [Figure 4] FIG. 1A is an example of an embodiment according to the present invention, and is an overhead view (top view) of a concave-convex structure A, and FIG. 1B is a perspective view of protrusions constituting the concave-convex structure A shown in FIG. [Diagram 5] FIG. 1A is an example of an embodiment according to the present invention, and is an overhead view (top view) of a concave-convex structure A, and FIG. 1B is a perspective view of protrusions constituting the concave-convex structure A shown in FIG. [Figure 6] FIG. 1A is an example of an embodiment according to the present invention, and is an overhead view (top view) of a concave-convex structure A, and FIG. 1B is a perspective view of protrusions constituting the concave-convex structure A shown in FIG. [Figure 7]FIG. 2 is a schematic top view of a concave-convex structure A, which is an example of an embodiment according to the present invention. [Figure 8] FIG. 1 is a schematic diagram of a surface treatment according to an embodiment of the present invention. [Figure 9] FIG. 2 is an example of an embodiment of the present invention, showing an electron microscope photograph illustrating an enlarged view of a protrusion portion on which a fine concave-convex structure B is formed. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0016] DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described with reference to the drawings. The drawings are schematic diagrams and are not to scale.

[0017] 1. Membrane carrier The membrane carrier for a test kit according to this embodiment (also simply referred to as "membrane carrier 3") is a membrane carrier for a test kit for detecting a substance to be detected in a liquid sample, and is provided with a flow path capable of transporting the liquid sample and having a detection zone, and the flow path is capable of generating capillary action for transporting the liquid sample and has an uneven structure A with protrusions. In the membrane carrier for the test kit according to this embodiment, at least in the detection zone, a fine uneven structure B is formed on the surface of the protrusion, a silane coupling agent is attached to the surface of the fine uneven structure B, and the maximum peak height Rp of the roughness curve of the protrusion on which the fine uneven structure B is formed is 0.005 μm or more and 10 μm or less, and the average length RSm of the roughness curve element is 0.01 μm or more and 15 μm or less, as measured using a three-dimensional roughness analysis scanning electron microscope in accordance with JIS B0601:2013. Moreover, the fine concave-convex structure B formed on the surface of the protrusion according to this embodiment has, for example, as shown in FIG. 9, a striped or streaky shape on a macroscopic scale.

[0018] In the membrane carrier for the test kit of this embodiment, at least in the detection zone, Rp and RSm are within the above ranges, and a fine uneven structure B to which a silane coupling agent is attached is formed, making it possible to increase the amount of detection substance carried in the detection zone, and as a result, the detection sensitivity of the substance to be detected in the liquid sample can be improved. The reason why the amount of detection substance carried in the detection zone can be increased is not clear, but the following reasons are considered. First, the maximum peak height Rp of the roughness curve is a value indicating the maximum height of the convex parts in the fine concave-convex structure B, and the average length RSm of the roughness curve element indicates the average value of the concave-convex period in the fine concave-convex structure B. Therefore, the above Rp and RSm are indices that indicate the balance between the formation interval of the concave-convex structure B and the height of the concave-convex structure. Therefore, at least in the detection zone, the fine uneven structure B in which Rp and RSm are within the above range is considered to have a structure having a space suitable for carrying the detection substance. Therefore, the membrane carrier for the test kit according to this embodiment has the fine uneven structure B in which Rp and RSm are within the above range at least in the detection zone, and therefore it is considered possible to increase the amount of the detection substance carried in the detection zone. Furthermore, by attaching a silane coupling agent to the fine uneven structure B, it is believed that it becomes possible to support detection substances that cannot be well adsorbed on the surface of the fine uneven structure B due to steric hindrance, etc. From the above, it is considered that the membrane carrier for the test kit of this embodiment can increase the amount of detection substance carried in the detection zone due to the synergistic effect of the fine uneven structure B, whose Rp and RSm are within the above ranges, and the silane coupling agent.

[0019] In the membrane carrier for the test kit according to this embodiment, a silane coupling agent is attached to the surface of the fine uneven structure B. Here, the silane coupling agent may be physically adsorbed to the surface of the fine uneven structure B, may be chemically adsorbed, or may be directly bonded to the functional group present on the surface of the fine uneven structure B. Examples of the silane coupling agent according to the present embodiment include a silane coupling agent having an amino group, a silane coupling agent having a mercapto group, a silane coupling agent having an epoxy group, a silane coupling agent having an acrylic group, a silane coupling agent having a methacryl group, a silane coupling agent having a vinyl group, and a silane coupling agent having an isocyanate group. Examples of silane coupling agents having an amino group include 3-aminopropyltriethoxysilane, 3-aminopropyltrimethoxysilane, 3-(2-aminoethyl)aminopropyltriethoxysilane, and 3-(2-aminoethyl)aminopropyltrimethoxysilane. Examples of silane coupling agents having a mercapto group include 3-mercaptopropyltrimethoxysilane, 3-mercaptopropyltriethoxysilane, 2-mercaptoethyltrimethoxysilane, and 2-mercaptoethyltriethoxysilane. Examples of silane coupling agents having an epoxy group include 3-glycidoxypropyltrimethoxysilane, 5,6-epoxyhexyltriethoxysilane, 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, and 3-glycidoxypropyltriethoxysilane. Examples of silane coupling agents having an acrylic group include 3-acryloxypropyltrimethoxysilane, 3-acryloxypropylmethyldimethoxysilane, 3-acryloxypropylmethyldiethoxysilane, and 3-acryloxypropyltriethoxysilane. Examples of silane coupling agents having a methacryl group include 3-methacryloxypropylmethyldimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-methacryloxypropylmethyldiethoxysilane, 3-methacryloxypropyltriethoxysilane, γ-(methacryloyloxypropyl)trimethoxysilane, and γ-(methacryloyloxypropylmethyl)dimethoxysilane. Examples of the silane coupling agent having a vinyl group include vinyltriethoxysilane and vinyltrimethoxysilane. Examples of silane coupling agents having an isocyanate group include trimethoxysilylmethyl isocyanate, triethoxysilylmethyl isocyanate, tripropoxysilylmethyl isocyanate, 2-trimethoxysilylethyl isocyanate, 2-triethoxysilylethyl isocyanate, 2-trippropoxysilylethyl isocyanate, 3-trimethoxysilylpropyl isocyanate, 3-triethoxysilylpropyl isocyanate, 3-trippropoxysilylpropyl isocyanate, 4-trimethoxysilylbutyl isocyanate, 4-triethoxysilylbutyl isocyanate, and 4-trippropoxysilylbutyl isocyanate. These silane coupling agents may be used alone or in combination of two or more. Among these, at least one selected from the group consisting of silane coupling agents having an amino group and silane coupling agents having an epoxy group is preferred, since it is possible to further increase the amount of detection substance carried in the detection zone.

[0020] The amount of the silane coupling agent attached is, for example, 1 m of the surface area of ​​the membrane carrier 3. 2 The range is between 0.1 mg and 10 g per serving.

[0021] In the membrane carrier for the test kit according to this embodiment, it is preferable that a crosslinker is further attached to the surface of the fine uneven structure B. By further attaching a crosslinker to the surface of the fine uneven structure B, the detection substance can be stably supported on the surface of the fine uneven structure B. This makes it possible to further increase the amount of detection substance supported in the detection zone. In addition, by using a crosslinking agent, it becomes possible to support detection substances that cannot be properly adsorbed onto the surface of the above-mentioned micro-relief structure B due to steric hindrance, etc., thereby further increasing the amount of detection substance supported. Here, the crosslinking agent may be physically adsorbed or chemically adsorbed on the surface of the fine concave-convex structure B, or may be directly bonded to a functional group present on the surface of the fine concave-convex structure B. In addition, the crosslinking agent may be physically adsorbed or chemically adsorbed on the surface of the layer containing the silane coupling agent, or may be directly bonded to the silane coupling agent.

[0022] Examples of the crosslinking agent according to the present embodiment include formaldehyde, glutaraldehyde, dextran, 1,4-phenyl diisocyanate, toluene-2,4 diisocyanate, polyethyleneimine, hexamethylene diisocyanate, hexamethylene diisothiocyanate, N,N'-polymethylene bisiodoacetamide, N,N'-ethylene bismaleimide, ethylene glycol bissuccinimidyl succinate, bisdiazobenzidine, 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide, succinimidyl 3-(2-pyridyldithio)propionate, N-succinimidyl 4-(N-maleimidomethyl)cyclohexane-1 -carboxylate, N-hydroxysuccinimide, N-sulfosuccinimidyl 4-(N-maleimidomethyl)cyclohexane-1-carboxylate, N-succinimidyl (4-iodoacetyl)aminobenzoate, N-succinimidyl 4-(1-maleimidophenyl)butyrate, N-(ε-maleimidocaproyloxy)succinimide, iminothiolane, S-acetylmercaptosuccinic anhydride, methyl-3-(4'-dithiopyridyl)propionimidate, methyl-4-mercaptobutyrylimidate, methyl-3-mercaptopropionimidate, N-succinimidyl-S-acetylmercaptoacetate, and the like. These crosslinking agents may be used alone or in combination of two or more. Among these, at least one crosslinking agent selected from glutaraldehyde, dextran, 1,4-phenyl diisocyanate, toluene-2,4 diisocyanate, polyethyleneimine, 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide, N-succinimidyl 4-(N-maleimidomethyl)cyclohexane-1-carboxylate, and N-hydroxysuccinimide is preferred, as it is capable of further increasing the amount of detection substance carried in the detection zone.

[0023] The amount of the crosslinking agent attached is, for example, 1 m of the surface area of ​​the membrane carrier 3. 2 The range is between 0.1 mg and 10 g per serving.

[0024] Here, the substance to be detected is not limited in any way, and may be any substance capable of undergoing an antigen-antibody reaction with an antibody, such as various pathogens and various clinical markers. Specific examples of the substance to be detected include virus antigens such as influenza virus, norovirus, adenovirus, RS virus, HAV, HBs, and HIV, bacterial antigens such as MRSA, group A streptococcus, group B streptococcus, and Legionella, toxins produced by bacteria, hormones such as mycoplasma, chlamydia trachomatis, and human chorionic gonadotropin, C-reactive protein, myoglobin, cardiac troponin, various tumor markers, agricultural chemicals, and environmental hormones, but are not limited thereto. The usefulness of the substance to be detected is particularly great when it is an item that requires urgent detection and treatment, such as influenza virus, norovirus, C-reactive protein, myoglobin, and cardiac troponin. The substance to be detected may be an antigen that can induce an immune reaction by itself, or a hapten that cannot induce an immune reaction by itself but can bind to an antibody through an antigen-antibody reaction. The substance to be detected is usually in a state of being suspended or dissolved in a liquid sample. The liquid sample may be, for example, a sample in which the substance to be detected is suspended or dissolved in a buffer solution.

[0025] The liquid sample test kit according to this embodiment (hereinafter, also simply referred to as "test kit 18") has a membrane carrier for a test kit according to this embodiment, and detects a target substance in a liquid sample. FIG. 1 is a schematic top view of the test kit. For example, as shown in FIG. 1, the test kit 18 includes a membrane carrier 3 and a housing 18a that houses the membrane carrier 3. The membrane carrier 3 has, on its surface, a drip zone 3x where a liquid sample is dripped, and a detection zone 3y for detecting a target substance in the liquid sample. The drip zone 3x is exposed at a first opening 18b of the housing 18a. The detection zone 3y is exposed at a second opening 18c of the housing 18a.

[0026] FIG. 2 is a schematic top view of the membrane carrier 3. As shown in FIG. 2, the membrane carrier 3 has at least one flow path 2 for transporting a liquid sample. The bottom surface of the flow path 2 is provided with a concave-convex structure A (not shown, details will be described later). The concave-convex structure A is located at least between the drip zone 3x and the detection zone 3y. The concave-convex structure A may be provided over the entire surface of the membrane carrier 3. The entire surface of the membrane carrier 3 may be the flow path 2 for the liquid sample. The concave-convex structure A generates a capillary action. Due to the capillary action of the concave-convex structure A, the liquid sample is transported from the drip zone 3x to the detection zone 3y (along the transport direction d) through the concave-convex structure A. When a substance to be detected in the liquid sample is detected in the detection zone 3y, the color of the detection zone 3y changes.

[0027] The overall shape of the membrane carrier 3 is not particularly limited, and may be, for example, a polygon such as a rectangle, a circle, or an ellipse. When the membrane carrier 3 is a rectangle, the vertical width (length in the short direction) L1 of the membrane carrier 3 may be, for example, 2 mm to 100 mm, and the horizontal width (length in the long direction) L2 of the membrane carrier 3 may be, for example, 2 mm to 100 mm. The thickness of the membrane carrier excluding the height of the uneven structure A may be, for example, 0.1 mm to 10 mm.

[0028] 3 to 6 show an example of the uneven structure A provided on the bottom surface of the flow path and the protrusions (also called convex parts) constituting the uneven structure A in this embodiment. In FIG. 3 to 6, (a) is a bird's-eye view (top view) of the uneven structure A, and (b) is a perspective view of the protrusions constituting the uneven structure A shown in (a). As shown in FIG. 3 to 6, the uneven structure A (7) is a total of the protrusions 8. That is, the membrane carrier 3 has a flat part 9 corresponding to the bottom surface of the flow path 2 for the liquid sample, and a plurality of protrusions 8 protruding from the flat part 9. By capillary action, the spaces between the plurality of protrusions 8 function as the flow path 2 that transports the liquid sample along the surface of the membrane carrier 3. In other words, by capillary action, the voids in the uneven structure A (7) function as the flow path 2 that transports the liquid sample along the surface of the membrane carrier 3. The plurality of protrusions 8 may be arranged regularly or translationally symmetrically on the surface of the membrane carrier 3.

[0029] The shape of the multiple protrusions 8 constituting the above-mentioned concave-convex structure A (7) can be freely selected. Examples of the shape of the protrusions 8 include a cone, a polygonal pyramid, a truncated cone, a truncated polygonal pyramid, a cylinder, a polygonal prism, a hemisphere, and a semi-ellipsoid. Examples of the bottom surface of the concave-convex structure A include a circle or a polygon (for example, a square, a rhombus, a rectangle, a triangle, or a hexagon). For example, as shown in FIG. 3, the shape of the protrusion 8a may be a cone. For example, as shown in FIG. 4, the shape of the protrusion 8b may be a quadrangular pyramid. For example, as shown in FIG. 5, the shape of the protrusion 8c may be a hexagonal pyramid. For example, as shown in FIG. 6, the shape of the protrusion 8d may be a quadrangular prism (a line-and-space structure in which the protrusion 8d is in a line shape). Among these, pyramidal structures such as cones and polygonal pyramids are suitable for the shape of the protrusions 8, because the entire surface of the membrane carrier 3 can be seen when the uneven structure A(7) is viewed from above (from above), and the color change occurring when the target substance is detected can be easily confirmed by optical techniques. Among the pyramidal structures, a cone is preferable.

[0030] The shape of the protrusions 8 constituting the uneven structure A(7) does not need to be a geometrically precise shape, and may be a shape with rounded corners or a shape with fine unevenness on the surface.

[0031] The diameter 4 (average diameter) of the bottom surface 10 of the protrusions 8 constituting the above uneven structure A(7) is preferably 5 μm or more and 1000 μm or less, more preferably 10 μm or more and 500 μm or less. When the diameter 4 of the bottom surface 10 of the protrusions 8 is equal to or more than the above lower limit, the precision of the microfabrication can be kept low, and the cost for forming the uneven structure A(7) tends to be low. When the diameter 4 of the bottom surface 10 of the protrusions 8 is equal to or less than the above upper limit, the number of protrusions 8 in one test kit increases, making it easier to develop a liquid sample. Here, the diameter 4 of the bottom surface 10 of the protrusion 8 can be determined, for example, by arbitrarily selecting five protrusions 8 from the uneven structure A(7) and taking the average value of the diameters of the bottom surface 10 of the five selected protrusions 8.

[0032] The diameter 4 of the bottom surface 10 of the protrusion 8 is defined as the characteristic length of the bottom surface 10 of the protrusion 8. The characteristic length of the bottom surface 10 is the diameter when the shape of the bottom surface 10 is a circle, the length of the shortest side when the shape of the bottom surface 10 is a triangle or a rectangle, the length of the longest diagonal when the shape of the bottom surface 10 is a polygon with pentagons or more sides, and the maximum length of the bottom surface 10 when the shape is other than that.

[0033] As shown in FIG. 3, when the shape of the protrusion 8a is a cone, the diameter 4a of the bottom surface 10a of the protrusion 8a is the diameter of the bottom surface (circle) of the cone. As shown in FIG. 4, when the shape of the protrusion 8b is a regular square pyramid, the diameter 4b of the bottom surface 10b of the protrusion 8b is the length of the side of the bottom surface (regular square) 10b. As shown in FIG. 5, when the shape of the protrusion 8c is a regular hexagonal pyramid, the diameter 4c of the bottom surface 10c of the protrusion 8c is the length of the diagonal line passing through the center of the bottom surface (regular hexagon) 10c (the length of the longest diagonal line). As shown in FIG. 6, when the protrusion 8d is a rectangle, the diameter 4d of the bottom surface 10d of the protrusion 8d is the length of the shortest side of the bottom surface (rectangle) 10d (in FIG. 6, the length in the direction perpendicular to the transport direction d of the liquid sample).

[0034] The height 6 (average height) of the protrusions 8 constituting the above-mentioned concave-convex structure A(7) is preferably 5 μm to 1000 μm, and more preferably 10 μm to 500 μm. When the height 6 of the protrusions 8 is equal to or greater than the above-mentioned lower limit, the volume of the flow channel 2 increases, and the liquid sample can be developed in a shorter time. When the height 6 of the protrusions 8 is equal to or less than the above-mentioned upper limit, the time and cost required to fabricate the concave-convex structure A(7) can be reduced, and fabrication of the concave-convex structure A(7) becomes easier. Here, the height 6 of the protrusions 8 can be determined by, for example, arbitrarily selecting five protrusions 8 from the concave-convex structure A(7) and then averaging the heights of the five selected protrusions 8.

[0035] The height 6 of the protrusion 8 is defined as the maximum length of the protrusion 8 in a direction perpendicular to the flat portion 9. As shown in FIG. 3, when the shape of the protrusion 8a is a cone, the height 6a of the protrusion 8a is the maximum length of the protrusion 8a in a direction perpendicular to the flat portion 9 (the height of the cone). As shown in FIG. 4, when the shape of the protrusion 8b is a quadrangular pyramid, the height 6b of the protrusion 8b is the maximum length of the protrusion 8b in a direction perpendicular to the flat portion 9 (the height of the quadrangular pyramid). As shown in FIG. 5, when the shape of the protrusion 8c is a hexagonal pyramid, the height 6c of the protrusion 8c is the maximum length of the protrusion 8c in a direction perpendicular to the flat portion 9 (the height of the hexagonal pyramid). As shown in FIG. 6, when the shape of the protrusion 8d is a quadrangular prism, the height 6d of the protrusion 8d is the maximum length of the protrusion 8d in a direction perpendicular to the flat portion 9 (the height of the quadrangular prism).

[0036] The distance 5 (average distance) between adjacent protrusions in the concave-convex structure A (7), i.e., the closest distance between the protrusions 8, is preferably 0 to 500 μm. It is preferably 500 μm or less, and more preferably 2 μm or more and 100 μm or less. The distance 5 between adjacent protrusions cannot be smaller than 0 μm, and if it is equal to or less than the upper limit, the contact area between the liquid sample and the flow channel 2 increases, thereby increasing the capillary force and making it easier to move the liquid sample. Here, the "distance between adjacent protrusions" refers to the closest distance between a pair of adjacent protrusions 8. Here, the distance 5 between adjacent protrusions can be determined, for example, by selecting any five distances between adjacent protrusions from the uneven structure A(7) and adopting the average value of the distances between the five selected adjacent protrusions.

[0037] The aspect ratio of the protrusions 8 constituting the above-mentioned concave-convex structure A (7) is preferably 0.1 to 10, and more preferably 0.1 to 2.0. The aspect ratio referred to here is the value (Lh / Lv) obtained by dividing the height 6 (Lh) of the protrusions 8 by the representative length (diameter 4) (Lv) of the bottom surface 10 of the protrusions 8. When the aspect ratio is equal to or greater than the above-mentioned lower limit, the contact area between the liquid sample and the flow channel 2 increases, which increases the capillary force and makes it easier to move the liquid sample. When the aspect ratio is equal to or less than the above-mentioned upper limit, the production of the concave-convex structure A becomes easier.

[0038] The uneven structure A (7) and the membrane carrier 3 of the test kit 18 according to this embodiment include, for example, a thermoplastic resin. In other words, the membrane carrier 3 having the uneven structure A (7) can be produced by processing a film-shaped base material made of a thermoplastic resin.

[0039] Examples of processing methods include thermal imprinting, UV imprinting, injection molding, etching, photolithography, mechanical cutting, laser processing, etc. Among these, thermal imprinting for thermoplastic resins is suitable as a method for performing precise processing at low cost. Examples of the thermoplastic resin include polyester resin, polyolefin resin, polystyrene resin, polycarbonate resin, fluorine resin, and (meth)acrylic resin, and specifically, various types of resins can be used, such as polyethylene terephthalate (PET), cycloolefin polymer (COP), polypropylene (PP), polystyrene (PS), polycarbonate (PC), polyvinylidene fluoride (PVDF), polymethyl methacrylate (PMMA), polyethylene (PE), etc. These thermoplastic resins may be used alone or in combination of two or more.

[0040] In the case of a processing method using a mold such as imprinting or injection molding, since the top of the cone is narrower than the bottom, the volume to be cut out during mold production is smaller than that required for producing a columnar body with the same bottom, and the mold can be produced at low cost. In this case, it becomes possible to detect the target substance in a liquid sample at low cost.

[0041] As described above, the membrane carrier 3 includes the uneven structure A(7) provided on one surface of the membrane carrier 3, the flow path 2 for transporting a liquid sample formed by the uneven structure A(7), and a detection zone (detection section) 3y for detecting a target substance in a liquid sample. The membrane carrier 3 may be a membrane carrier 3 for a test kit 18 for detecting a target substance in a liquid sample.

[0042] The maximum peak height Rp of the roughness curve of the protrusions on which the microrelief structure B is formed, measured using a three-dimensional roughness analysis scanning electron microscope in accordance with JIS B0601:2013, is 0.005 μm or more and 10 μm or less. The maximum peak height Rp is preferably 0.010 μm or more, more preferably 0.050 μm or more, even more preferably 0.10 μm or more, and even more preferably 0.15 μm or more. The maximum peak height Rp is preferably 8.0 μm or less, more preferably 5.0 μm or less, even more preferably 3.0 μm or less, and even more preferably 1.0 μm or less.

[0043] The average value of the maximum peak height Rp of the roughness curve of the protrusions on which the microrelief structure B is formed, measured using a three-dimensional roughness analysis scanning electron microscope in accordance with JIS B0601:2013, is preferably 0.005 μm or more and 10 μm or less. The average value of the maximum peak height Rp is preferably 0.010 μm or more, more preferably 0.050 μm or more, even more preferably 0.10 μm or more, and even more preferably 0.15 μm or more. The average value of the maximum peak height Rp is preferably 8.0 μm or less, more preferably 5.0 μm or less, even more preferably 3.0 μm or less, and even more preferably 1.0 μm or less. The average value of the maximum peak height Rp can be determined by arbitrarily selecting three protrusions 8 on which the fine uneven structure B is formed and averaging the maximum peak heights Rp of the three selected protrusions 8.

[0044] In the membrane carrier 3, the maximum peak height Rp of the roughness curve of the flat portion 9 may be 0.005 μm or more and 10 μm or less. The maximum peak height Rp of the roughness curve of the flat portion 9 is preferably 0.010 μm or more, more preferably 0.050 μm or more, even more preferably 0.10 μm or more, and even more preferably 0.15 μm or more. The maximum peak height Rp of the roughness curve of the flat portion 9 is preferably 8.0 μm or less, more preferably 5.0 μm or less, even more preferably 3.0 μm or less, and even more preferably 1.0 μm or less.

[0045] The average length RSm of the roughness curve elements of the protrusions on which the microrelief structure B is formed, as measured using a three-dimensional roughness analysis scanning electron microscope in accordance with JIS B0601:2013, is 0.01 μm or more and 15 μm or less. The average length RSm is preferably 0.03 μm or more, more preferably 0.05 μm or more, even more preferably 0.08 μm or more, and even more preferably 0.10 μm or more. The average length RSm is preferably 10 μm or less, more preferably 5.0 μm or less, and even more preferably 3.0 μm or less.

[0046] The average value of the average length RSm of the roughness curve elements of the protrusions on which the microrelief structure B is formed, measured using a three-dimensional roughness analysis scanning electron microscope in accordance with JIS B0601:2013, is preferably 0.01 μm or more and 15 μm or less. The average value of the average length RSm is preferably 0.03 μm or more, more preferably 0.05 μm or more, even more preferably 0.08 μm or more, and even more preferably 0.10 μm or more. The average value of the average length RSm is preferably 10 μm or less, more preferably 5.0 μm or less, and even more preferably 3.0 μm or less. The average value of the average length RSm of the roughness curve elements can be determined by arbitrarily selecting three protrusions 8 on which the fine uneven structure B is formed, and averaging the average lengths RSm of the roughness curve elements of the three selected protrusions 8.

[0047] In the membrane carrier 3, the average length RSm of the roughness curve elements of the flat portion 9 may be 0.01 μm or more and 15 μm or less. The average length RSm of the roughness curve elements of the flat portion 9 is preferably 0.03 μm or more, more preferably 0.05 μm or more, even more preferably 0.08 μm or more, and even more preferably 0.10 μm or more. The average length RSm of the roughness curve elements of the flat portion 9 is preferably 10 μm or less, more preferably 5.0 μm or less, and even more preferably 3.0 μm or less.

[0048] FIG. 7 is a diagram for explaining a method for measuring Rp and RSm of the protrusion 8 in the concave-convex structure A(7) on which the fine concave-convex structure B is formed. Using a three-dimensional roughness analysis scanning electron microscope, the unevenness profile is measured along the surface of the protrusion 8 (along the straight line 20 when viewed from the top), with the apex center of the protrusion 8 (for example, the center 19 of the protrusion) as the center point. The straight line 20 is an arbitrary straight line with a length 20d and a center point at the apex center (for example, the center 19 of the protrusion). The length 20d is the same length as the diameter of the bottom surface of the protrusion 8. When the straight line 20 is a straight line on the same plane (for example, when both ends and the center are on the same plane), that is, when the protrusion 8 is in the shape of a truncated cone, a truncated polygonal pyramid, a cylinder, a polygonal prism, or the like, the maximum peak height Rp of the roughness curve and the average length RSm of the roughness curve element specified in JIS B0601:2013 are calculated from the unevenness profile. If the straight line 20 is not a straight line on the same plane, that is, if the protrusion 8 is in the shape of a cone, a polygonal pyramid, a hemisphere, a semi-ellipsoid, or the like, a tilt correction is applied from the unevenness profile, and the maximum peak height Rp and the average length RSm of the roughness curve element as a plane are calculated as specified in JIS B0601:2013.

[0049] When preparing a membrane carrier 3 having a concave-convex structure A (7) by thermal imprinting, the Rp and RSm of the protrusions 8 on which the fine concave-convex structure B is formed can be adjusted within the above-mentioned numerical ranges by, for example, etching, photolithography, mechanical cutting, laser processing, etc. In particular, it is preferable to adjust the Rp and RSm of the protrusions 8 on which the fine concave-convex structure B is formed by setting the Rp and RSm of the surface of a die (mold) used for thermal imprinting to a predetermined value. For example, it is preferable to adjust the Rp and RSm of the protrusions 8 on which the fine concave-convex structure B is formed by etching, photolithography, mechanical cutting, polishing, laser processing, etc. of the surface of the die (mold). Examples of polishing include cutting by dicing, sandblasting, etc. In laser processing, the Rp and RSm can be adjusted by controlling the laser output.

[0050] That is, the manufacturing method of the test kit 18 according to this embodiment preferably includes a step of producing a membrane carrier 3 having a concave-convex structure A (7) by thermal imprinting (thermal imprinting step). In the thermal imprinting step, the surface of a metal mold on which a plurality of concaves are formed is applied to a substrate (e.g., a film-like substrate) made of, for example, a thermoplastic resin, and the substrate is heated to form a membrane carrier 3 having a concave-convex structure A (7) (a plurality of protrusions 8) corresponding to the shape of the concaves and a flat portion 9.

[0051] In one embodiment, carbon and / or nitrogen atoms and oxygen atoms may be present on the surface of the sensing zone.

[0052] The ratio of the number of oxygen atoms to the total number of atoms of each atom (oxygen atoms / (number of carbon atoms+number of nitrogen atoms+number of oxygen atoms)) is 0.01 to 0.50. In one embodiment of the membrane carrier, the ratio of the number of oxygen atoms on the surface of the detection zone (oxygen atoms / (number of carbon atoms+number of nitrogen atoms+number of oxygen atoms)) is 0.01 or more, preferably 0.05 or more, more preferably 0.10 or more, and even more preferably 0.20 or more. In one embodiment of the membrane carrier, the ratio of the number of oxygen atoms on the surface of the detection zone (oxygen atoms / (number of carbon atoms+number of nitrogen atoms+number of oxygen atoms)) is 0.50 or less, preferably 0.40 or less, more preferably 0.38 or less, even more preferably 0.36 or less, even more preferably 0.30 or less, and even more preferably 0.10 or less. The higher the ratio of the number of oxygen atoms on the surface of the detection zone, the easier it is for the detection substance to be fixed to the surface. By the detection substance being fixed to the surface, the detection substance that is washed away when the liquid sample is developed is reduced, enabling highly sensitive testing. When the oxygen atomic ratio on the surface of the detection zone is equal to or less than the above upper limit, the occurrence of erroneous detection due to reaction between the labeling substance and the detection substance when a solution not containing the substance to be detected is developed is further suppressed.

[0053] The oxygen atom number ratio on the surface of the detection zone is calculated by X-ray photoelectron spectroscopy (XPS). The calculation of the oxygen atom number ratio by XPS is described below. The binding energy correction of the spectrum obtained by measurement is performed using the C-C bond in the C1s spectrum. The background (BG) is subtracted from each peak of the C1s spectrum, N1s spectrum, and O1s spectrum of the spectrum that has been subjected to binding energy correction. The peak area (signal intensity) of each atom calculated by subtracting the BG from each peak is divided by a correction factor (relative sensitivity coefficient, transmission function, and kinetic energy correction), and the total area after correction is calculated to be 100. The obtained values ​​are the number of carbon atoms, the number of nitrogen atoms, and the number of oxygen atoms, respectively, and the oxygen atom number ratio (oxygen atom number / (number of carbon atoms + number of nitrogen atoms + number of oxygen atoms)) is calculated.

[0054] The oxygen atomic ratio on the surface of the detection zone can be adjusted to fall within the above range by subjecting the surface of the detection zone to a surface treatment. The method of surface treatment is not limited, and various techniques can be used, such as surface modification by various plasma treatments, corona treatments, UV irradiation, and UV / ozone treatments.

[0055] It is preferable to perform the surface treatment only on the detection zone. By performing the surface treatment only on the detection zone, the detection substance does not adhere to the non-detection zone (area other than the detection zone) in the flow channel, and the detection substance can be adhered with high efficiency only to the detection zone. As a result, the detection signal can be easily recognized in the detection zone (higher S / N ratio).

[0056] As a method for selectively treating the surface of the detection zone to modify the surface of the detection zone, there is a method in which the area other than the detection zone is covered with a mask (shielding material) capable of shielding, and the exposed detection zone is subjected to surface treatment. FIG. 8 is a diagram for explaining the method for selectively treating the surface of the detection zone. A shielding material 14 having a void portion is placed on the membrane carrier 3 to expose the detection zone (surface-treated area). The part of the membrane carrier 3 covered with the shielding material 14 becomes an untreated area (non-detection zone) 15. A metal plate is preferable as the shielding material 14. By surface-treating the exposed area, a membrane carrier 3 is obtained in which the oxygen atomic ratio of the surface of the detection zone is within the above-mentioned range.

[0057] In the above embodiment, as the material of the membrane carrier, it is preferable to use a resin having a surface oxygen atom ratio (oxygen atom number / (carbon atom number+nitrogen atom number+oxygen atom number)) of less than 0.01, and more preferably a resin having 0.005 or less. The resin having a surface oxygen atom ratio of less than 0.01 is a resin that does not contain oxygen atoms in the structural formula of the main component, and may be a resin that contains carbon atoms and does not contain nitrogen atoms and oxygen atoms, such as polyolefin resin, polystyrene resin, and fluorine resin. Specific examples of such resins include polyethylene (PE), cycloolefin polymer (COP), polypropylene (PP), polystyrene (PS), and polyvinylidene fluoride (PVDF). The resin having a surface oxygen atom ratio of less than 0.01 may be a resin that contains carbon atoms and nitrogen atoms and does not contain oxygen atoms, such as polyimide resin. When a resin containing carbon atoms and no nitrogen or oxygen atoms is used, the oxygen atom number ratio in the detection zone (number of oxygen atoms / (number of carbon atoms+number of nitrogen atoms+number of oxygen atoms)) becomes substantially equal to the value of number of oxygen atoms / (number of carbon atoms+number of oxygen atoms).

[0058] When the surface oxygen atomic ratio is 0.005 or less, the adhesion of the labeling substance to the non-detection zone is further suppressed when a membrane carrier is prepared, a test kit is prepared using the prepared membrane carrier, and a liquid sample is developed. If the labeling substance adheres to the non-detection zone, it becomes difficult to recognize a signal of the same intensity in the detection zone (the S / N ratio becomes low).

[0059] When the surface oxygen atomic ratio is 0.005 or less, the adhesion of the labeling substance to the non-detection zone is further suppressed when a membrane carrier is prepared, a test kit is prepared using the prepared membrane carrier, and a liquid sample is developed. If the labeling substance adheres to the non-detection zone, it becomes difficult to recognize a signal of the same intensity in the detection zone (the S / N ratio becomes low).

[0060] In the test kit 18 according to this embodiment, the detection zone 3y of the membrane carrier 3 exhibits a color change when a target substance is detected. The color change may be a color change that can be confirmed by an optical method.

[0061] The optical methods mentioned above mainly include visual judgment and a method of measuring fluorescence and luminescence intensity. When judging by visual judgment, it is preferable that a color change occurs such that the color difference between the two color stimuli (ΔE described in JIS Z8781-4:2013) is 0.5 or more when the colors before and after detection are measured in the color space of CIE1976L*a*b*. If this color difference is 0.5 or more, it becomes easy to visually confirm the color difference. When judging by measuring fluorescence and luminescence intensity, it is preferable that a color change occurs such that the ratio (Fl1 / Fl2) between the fluorescence and luminescence intensity in the detection zone 3y (Fl1) and the fluorescence and luminescence intensity in the upstream and downstream areas adjacent to the detection zone 3y is 10 / 1 or more. If this ratio is 10 / 1 or more, it becomes easy to separate the signal from the noise.

[0062] In one embodiment, in order to prepare the detection zone 3y in the test kit 18 of this embodiment, a detection substance is immobilized in at least a portion of the flow path 2. That is, a detection substance that detects a target substance is immobilized in the detection zone 3y. The color change in the detection zone 3y occurs when the target substance is held in the detection zone 3y by the detection substance (by reacting with the detection substance).

[0063] In other words, the method for producing the test kit 18 includes a step of immobilizing a detection substance, which causes a color change by retaining a detection target substance in the detection zone 3y, in the detection zone 3y. In order to more efficiently immobilize the detection substance (reagent) in the detection zone 3y, the membrane carrier 3 may be subjected to a surface treatment in advance at a location where the detection zone 3y is to be provided. As the method for the surface treatment, the methods exemplified above can be used.

[0064] In this embodiment, the detection substance (reagent) may be, for example, an antibody. The antibody is an antibody that undergoes an antigen-antibody reaction with the detection target substance, and may be a polyclonal antibody or a monoclonal antibody.

[0065] The color change in the detection zone 3y may be caused by a label having an antibody or an antigen-binding fragment thereof that specifically reacts with a substance to be detected in a liquid sample. The color change occurs, for example, when the label is retained in the detection zone 3y by the substance to be detected (by reacting (binding) with the substance to be detected) and changes color.

[0066] The label may be, for example, a labeled antibody such as a fluorescently labeled antibody, a chemiluminescently labeled antibody, or an enzyme-labeled antibody, or may be a particle such as a colloid particle or latex particle to which the antibody or its antigen-binding fragment is bound. The antigen-binding fragment refers to a fragment that can specifically bind to a substance to be detected, for example, an antigen-binding fragment of an antibody. The label can bind to a substance to be detected via an antibody or its antigen-binding fragment. The particle may be magnetic or fluorescent. Examples of colloid particles include metal colloid particles such as gold colloid particles and platinum colloid particles. The particle is preferably a latex particle in terms of particle size control, dispersion stability, and ease of binding. The material of the latex particle is not particularly limited, but polystyrene is preferred.

[0067] In terms of visibility, the particles are preferably colored particles or fluorescent particles, and more preferably colored particles. The colored particles may be any particles whose color can be detected by the naked eye. The fluorescent particles may contain a fluorescent substance. The particles may be colored latex particles or fluorescent latex particles. When the particles are colored latex particles, the above-mentioned color change is preferably determined by visual inspection. When the particles are fluorescent latex particles, the above-mentioned color change is preferably determined by measuring the fluorescence intensity.

[0068] The label as described above is provided in at least a part of the test kit 18 so as to react with the target substance in the dropped liquid sample. The label may be provided, for example, in a member in the test kit 18, or in at least a part of the flow path 2 of the membrane carrier 3 (upstream of the detection zone 3y). The label that reacted (bound) with the target substance is then held in the detection zone 3y by the detection substance (by the detection substance reacting (binding) with the target substance). This causes a color change (coloring by the label) in the detection zone 3y.

[0069] A liquid sample testing method according to one aspect of the present embodiment is a testing method that uses a test kit 18.

[0070] A method for testing a liquid sample using test kit 18 may include the steps of preparing a mixed liquid sample (mixed liquid sample) by mixing the liquid sample with a label that specifically binds to a substance to be detected in the liquid sample, and binding the substance to be detected and the label to each other, dripping the mixed liquid sample into a drip zone 3x provided on membrane carrier 3, transporting the mixed liquid sample from the drip zone 3x to a detection zone 3y by uneven structure A (7), and detecting a color change (coloration of the label) in the detection zone 3y.

[0071] Furthermore, for example, the above-mentioned testing method may include the steps of: dropping a liquid sample onto a dropping zone 3x on the surface of the membrane carrier 3; transporting the liquid sample from the dropping zone 3x to a detection zone 3y through the uneven structure A(7) (multiple protrusions 8) formed on the surface of the membrane carrier 3 by capillary action exerted by the uneven structure A(7); and binding the substance to be detected in the liquid sample to a label via the above-mentioned antibody or an antigen-binding fragment thereof during the transport process, and further binding the substance to be detected to a reagent fixed to the detection zone 3y, and detecting a color change in the detection zone 3y (optically determining the presence or absence of a color change).

[0072] In the step of binding the analyte and the label in the above-mentioned testing method, the method of mixing the liquid sample and the label is not particularly limited. For example, the liquid sample may be added to a container containing the label, or the liquid containing the label may be mixed with the liquid sample. In addition, for example, a filter may be placed at the drip opening of a container containing the liquid sample, and the label may be immobilized in the filter.

[0073] Although the embodiments of the present invention have been described above with reference to the drawings, these are merely examples of the present invention, and various configurations other than those described above can also be adopted. EXAMPLES

[0074] The present embodiment will be specifically described below with reference to examples and comparative examples, but the present embodiment is not limited to these examples.

[0075] [Example 1] <Preparation of membrane carrier> A cycloolefin polymer sheet (Zeon Corporation, Zeonor ZF-14, film thickness 200 μm) was subjected to thermal imprinting to produce a membrane carrier in which cone-shaped protrusions 8 having a diameter of the bottom surface of the uneven structure A (protrusion) (hereinafter sometimes referred to as "diameter of protrusion" or "diameter") of 30 μm and a height of the uneven structure A (protrusion) (hereinafter sometimes referred to as "height") of 30 μm were arranged in a triangular array as shown in Figure 3 with an average distance between the protrusions of 50 μm. Here, when performing thermal imprinting, an etched mold was used to form a fine uneven structure B on the surface of the uneven structure A (protrusion), and the maximum peak height Rp of the roughness curve and the average length RSm of the roughness curve elements of the protrusion 8 on which the fine uneven structure B was formed were adjusted to the values ​​shown in Table 1. The type of mold used and the etching conditions are as follows: A nickel mold with conical holes, each with an entrance diameter of 30 μm and a depth of 30 μm, arranged in a triangular arrangement with an average distance between holes of 50 μm, was immersed in a 40% by mass etching solution (ferric chloride solution) for 10 minutes, and the immersion time was adjusted to obtain the mold.

[0076] A three-dimensional roughness analysis electron microscope (ERA-600 manufactured by Elionix Corporation) was used to measure the maximum peak height Rp of the roughness curve and the average length RSm of the roughness curve elements (see FIG. 7). Three cone-shaped protrusions 8 were randomly selected. The three protrusions 8 were observed at 10,000 times magnification using a three-dimensional roughness analysis electron microscope to obtain a roughness-enhanced secondary electron image. Next, the roughness profile of a straight line 20 with a length 20d of 30 μm and centered at the apex center of the protrusion 8 (center point 19 of the protrusion) was measured. The roughness profile of the three straight lines 20 was subjected to inclination correction (long wavelength components (waviness components) were separated using a spline high-pass filter to obtain a cross-sectional curve), and the maximum peak height Rp and average length RSm of the roughness curve element as a plane, as specified in JIS B0601:2013, were calculated. The average value of the three obtained data was used as the evaluation value.

[0077] <Preparation of detection zone (detection part)> The surface of the obtained membrane carrier was coated with O 2 Plasma output: 100 W, irradiation time: 120 seconds, pressure: 6 x 10 -2 The surface-treated membrane carrier 3 was thus obtained.

[0078] <Silane coupling agent treatment> A silane coupling agent treatment solution of methanol:distilled water:3-aminopropyltriethoxysilane (manufactured by Tokyo Ohka Kogyo Co., Ltd., also called APTES) = 92:5:3 (mass ratio) was prepared. Next, the surface-treated membrane carrier 3 was immersed in a silane coupling agent treatment solution at room temperature for 4 hours to adhere the silane coupling agent to the surface of the membrane carrier 3. Next, the membrane carrier 3 was rinsed with methanol and then dried at 120°C for 5 minutes to obtain a membrane carrier 3 with the silane coupling agent adhered thereto.

[0079] <Measurement of antibody loading amount> An anti-CRP antibody solution was prepared by diluting a fluorescently labeled anti-CRP antibody in PBS (phosphate buffered saline) and applied to the membrane 3. After drying at 45°C for 1 hour, the membrane was ultrasonically cleaned in PBS containing 2 (v / v)% Triton X-100 (trade name). The fluorescence intensity of the remaining antibody was evaluated using a fluorescence microscope (Keyence BZ-X710).

[0080] [Examples 2 to 6] An experiment similar to that of Example 1 was conducted, except that the maximum peak height Rp of the roughness curve and the average length RSm of the roughness curve elements of the protrusion 8 having the fine uneven structure B formed thereon were adjusted to the values ​​shown in Table 1 by adjusting the etching treatment conditions for the mold (specifically, the concentration of the etching solution and the immersion time). The results obtained are shown in Table 1.

[0081] [Examples 7 to 12] By adjusting the etching treatment conditions for the mold, the maximum peak height Rp of the roughness curve and the average length RSm of the roughness curve elements of the protrusion 8 on which the fine uneven structure B is formed were adjusted to the values ​​shown in Table 1, and experiments similar to those in Example 1 were performed except that 3-glycidoxypropyltrimethoxysilane (also called GOPTS) was used instead of 3-aminopropyltriethoxysilane (also called APTES). The results obtained are shown in Table 1.

[0082] [Examples 13 to 18] By adjusting the etching treatment conditions for the mold, the maximum peak height Rp of the roughness curve and the average length RSm of the roughness curve elements of the protrusion 8 on which the fine uneven structure B was formed were adjusted to the values ​​shown in Table 2, and experiments similar to those in Example 1 were performed except that the following crosslinking agent treatment was further performed. The results obtained are shown in Table 2. (Crosslinking agent treatment) A glutaraldehyde solution was prepared by adding 2.5% glutaraldehyde to PBS. Next, the membrane carrier 3 treated with the silane coupling agent was immersed in a glutaraldehyde solution at room temperature for 1 hour to adhere glutaraldehyde (also called GA) to the surface of the membrane carrier 3. Next, the membrane carrier 3 was rinsed with ultrapure water and then dried at 45°C for 30 minutes to obtain a membrane carrier 3 with glutaraldehyde adhered thereto.

[0083] [Comparative Example 1] An experiment similar to that of Example 1 was carried out, except that the treatment with the silane coupling agent was not carried out. The results obtained are shown in Table 2.

[0084] [Comparative Example 2] An experiment similar to that of Example 1 was conducted, except that the etching treatment conditions for the mold were adjusted to adjust the maximum peak height Rp of the roughness curve and the average length RSm of the roughness curve elements of the protrusion 8 having the fine uneven structure B formed thereon to the values ​​shown in Table 2. The results obtained are shown in Table 2.

[0085] [Comparative Example 3] An experiment was carried out in the same manner as in Example 1, except that a mold that had not been subjected to an etching treatment was used and that the treatment with a silane coupling agent was not carried out. The results are shown in Table 2.

[0086] [Comparative Example 4] An experiment was carried out in the same manner as in Example 1, except that a mold that had not been etched was used. The results are shown in Table 2.

[0087] [Comparative Example 5] An experiment similar to that of Example 13 was carried out, except that the treatment with a silane coupling agent was not carried out. The results obtained are shown in Table 2.

[0088] [Table 1]

[0089] [Table 2]

[0090] The results in Tables 1 and 2 show that the membrane carrier for the test kit of this embodiment has Rp and RSm each within a specific range at the protrusions of the uneven surface structure A, and a fine uneven surface structure B to which a silane coupling agent is attached is formed, thereby increasing the amount of antibody, which is the detection substance, carried and enabling the detection of the substance to be detected with high sensitivity.

[0091] This application claims priority based on Japanese Patent Application No. 2018-179125, filed on September 25, 2018, the disclosure of which is incorporated herein in its entirety. [Explanation of symbols]

[0092] 2 Flow Path 3. Membrane carriers 3x drip zone 3y Detection zone (detection part) 4, 4a, 4b, 4c, 4d: characteristic length at the base of the protrusion (diameter at the base of the protrusion) 5 Distance between adjacent protrusions 6,6a,6b,6c,6d Height of protrusion 7,7a,7b,7c,7d Uneven structure A 8,8a,8b,8c,8d Protrusion 9 Flat area 10, 10a, 10b, 10c, 10d Bottom surface of protrusion 13y Detection Zone 14 Shielding section 15 Unprocessed 18 Test Kits 18a Case 18b First opening 18c Second opening 19 Center of protrusion 20 Straight line passing through the center of the protrusion 20d Length of the straight line passing through the center of the protrusion d Flow direction of the liquid sample (transport direction)

Claims

1. A membrane carrier for a test kit for detecting a target substance in a liquid sample, comprising: a flow path having a detection zone; The flow path has a concave-convex structure A having a protrusion, A fine relief structure B is formed on the surface of the protrusion at least in the detection zone, A silane coupling agent is attached to the surface of the fine uneven structure B, A membrane carrier for a test kit, in which the maximum peak height Rp of the roughness curve of the protrusion portion on which the fine uneven structure B is formed is 0.005 μm or more and 10 μm or less, and the average length RSm of the roughness curve element is 0.01 μm or more and 15 μm or less, as measured in accordance with JIS B0601:2013 using a three-dimensional roughness analysis scanning electron microscope.

2. In the membrane carrier for the test kit according to claim 1, The membrane carrier for a test kit, wherein the silane coupling agent comprises at least one selected from a silane coupling agent having an amino group, a silane coupling agent having a mercapto group, a silane coupling agent having an epoxy group, a silane coupling agent having an acrylic group, a silane coupling agent having a methacryl group, a silane coupling agent having a vinyl group, and a silane coupling agent having an isocyanate group.

3. The membrane carrier for a test kit according to claim 1 or 2, A membrane carrier for a test kit, further comprising a crosslinking agent attached to the surface of the micro-relief structure B.

4. In the membrane carrier for the test kit according to claim 3, The crosslinking agent is at least one selected from glutaraldehyde, dextran, 1,4-phenyl diisocyanate, toluene-2,4 diisocyanate, polyethyleneimine, 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide, N-succinimidyl 4-(N-maleimidomethyl) cyclohexane-1-carboxylate, and N-hydroxysuccinimide.

5. A membrane carrier for a test kit according to any one of claims 1 to 4, The uneven structure A is a membrane carrier for a test kit containing a thermoplastic resin.

6. The membrane carrier for a test kit according to claim 5, The membrane carrier for a test kit, wherein the thermoplastic resin comprises at least one selected from polyester-based resins, polyolefin-based resins, polystyrene-based resins, polycarbonate-based resins, fluorine-based resins, and (meth)acrylic resins.

7. The membrane carrier for a test kit according to any one of claims 1 to 6, A membrane carrier for a test kit, wherein the average height of the protrusions is 5 μm or more and 1000 μm or less.

8. The membrane carrier for a test kit according to any one of claims 1 to 7, A membrane carrier for a test kit, wherein the average distance between adjacent protrusions in the uneven structure A is 500 μm or less.

9. The membrane carrier for a test kit according to any one of claims 1 to 8, A membrane carrier for a test kit, wherein the average diameter of the bottom surface of the protrusions is 5 μm or more and 1000 μm or less.

10. A test kit having a membrane carrier for a test kit described in any one of claims 1 to 9.