Coating Method

Abstract

The present invention provides a coating method characterized by having: a step for supplying a coating agent to the surface of a lens substrate; a spreading step for spreading the coating agent supplied to the surface by rotating the lens substrate; a first removal step which follows the spreading step and which is for removing, by the rotation of the lens substrate, at least a portion of the liquid residue of the coating agent generated on the peripheral edge section and / or the side surface section of the lens substrate; and a second removal step which follows the first removal step and which is for bringing a suction member into contact with at least the side surface of the lens substrate and removing the liquid residue remaining on the peripheral edge section and / or the side surface section of the lens substrate.　According to the present invention, it is possible to provided a coating method with which when a coating layer is formed by using the coating agent on the substrate surface by a spin coating, the liquid residue of the coating agent generated on the peripheral edge section and / or the side surface section of the lens substrate is reduced, and thus, a substrate having a coating layer excellent in uniformity in the film thickness can be obtained.

Description

[Technical field]

[0001] The present invention relates to a coating method for forming a coating layer on the surface of a lens substrate. [Background technology]

[0002] As a method for forming a coating layer on the surface of a substrate such as a lens substrate, a method called spin coating is known in which a coating agent is supplied onto the lens substrate and the substrate is rotated to spread the coating agent over the surface of the lens substrate to form a coating layer. Spin coating makes it possible to form a relatively thin and uniform coating layer on the surface of the substrate, and is used in various industrial fields.

[0003] However, in a coating method in which the coating agent is spread on the surface of the lens substrate by rotating the lens substrate, a problem may occur in which the coating agent pools on the peripheral and / or side surfaces of the lens substrate when the coating agent is spread. If pools of liquid are formed during spreading, the thickness of the coating layer formed on the peripheral portion becomes thicker than other portions, and the thickness of the coating layer formed cannot be made uniform over the entire surface. In addition, pools of liquid are formed on the side surfaces, which causes a problem of poor appearance of the lens. When a coating layer is formed on a lens substrate, a portion of the coating layer with an uneven thickness cannot be used as a lens, and a problem occurs in that the effective area that can be used as a lens after the coating layer is formed.

[0004] Conventional techniques for dealing with the problem of the coating layer formed on the periphery and / or side surfaces becoming thick include the use of a lens substrate having a flange portion that is removed after the coating layer is formed (see Patent Document 1). However, such techniques have the drawback of being time-consuming to manufacture, as the shape of the lens substrate used for coating becomes complex and a process of removing the flange portion is required after the coating layer is formed.

[0005] As a conventional technique for dealing with the same problem, a technique has been proposed in which a spatula or ring is used to remove puddles that form on the periphery and / or side of the substrate when the coating agent is spread (see Patent Document 2). However, with this technique, if there is a slight change in the contact state of the spatula with the puddle or in the shape of the minute gap formed between the tip of the spatula and the periphery of the substrate, the puddle cannot be properly removed. This necessitates the replacement of the spatula or adjustment of the spatula's position in response to changes in the shape of the lens substrate, which results in problems such as the need to adjust the manufacturing equipment and the fact that the removal of the puddle is easily unstable due to the influence of variations in the holding position of the rotating lens substrate.

[0006] Furthermore, as a conventional technique for dealing with a similar problem, a technique has been proposed in which puddles formed on the periphery and / or sides of the substrate when the coating agent is spread are removed by suction (see Patent Document 3). However, with this technique, the removal of puddles may not be stable depending on the shape of the lens substrate used, and the suction pressure may adversely affect the uniformity of the coating liquid on the surface of the lens substrate. [Prior art documents] [Patent documents]

[0007] [Patent Document 1] JP 2013-054096 A [Patent Document 2] JP 2004-050108 A [Patent Document 3] JP 2016-180806 A [Patent Document 4] JP 2005-246267 A [Patent Document 5] International Publication No. WO2008-093613 Brochure Summary of the Invention [Problem to be solved by the invention]

[0008] In addition, the removal of puddles with an adsorbent such as a sponge has also been considered (see Patent Documents 4 and 5). Patent Document 4 describes a method in which a coating agent is guided to the side surface (edge ​​surface) of a lens substrate using a spatula while being removed with a sponge to make the surface smooth. Furthermore, Patent Documents 4 and 5 also describe scattering the coating agent by rotating the lens substrate.

[0009] However, Patent Documents 4 and 5 do not specify what state of the lens substrate the sponge is brought into contact with to remove pooled liquid. In particular, the embodiment in which the sponge is used in Patent Document 5 is the embodiment in Patent Document 4, which corresponds to the prior art of Patent Document 5, and the invention of Patent Document 5 itself is not a method of removing pooled liquid with a sponge.

[0010] Therefore, in the method of applying a coating agent to a lens substrate by spin coating to produce a lens having a coating layer (hereinafter sometimes simply referred to as a "coated lens"), there has been a demand for the development of a simpler method that allows for high-level adjustment of the thickness and appearance of the peripheral portion of the lens substrate.

[0011] The present invention has been made in view of the above problems, and provides a coating method capable of effectively removing liquid pools formed on the periphery and / or side of a substrate when a coating agent is spread. Furthermore, the present invention provides a method for manufacturing a photochromic lens using the coating method. [Means for solving the problem]

[0012] The present inventors have conducted extensive research to solve the above problems. They have focused on using an adsorption member as a method for relatively stably removing puddles from the peripheral edge and / or periphery of the lens substrate. As a result, they have found that it is important to prevent the puddle from becoming as large as possible before the adsorption member is applied. They have found that the following method can be used to easily remove puddles while still using an adsorption member to produce a high-quality coated lens, and have completed the present invention.

[0013] That is, the first aspect of the present invention is providing a coating agent to a surface of the lens substrate; a spreading step of spreading the coating agent supplied to the surface by rotating the lens substrate; a first removing step of removing at least a portion of the pool of the coating agent generated on the peripheral edge and / or side surface of the lens substrate after the spreading step by rotating the lens substrate; and a second removal step of removing the liquid pool remaining on the peripheral edge and / or side surface of the lens substrate by contacting an adsorption member with at least the side surface of the lens substrate after the first removal step; The coating method is characterized by comprising the steps of:

[0014] In the first aspect of the present invention, in order to produce a higher quality coated lens, it is preferable that the adsorption member contains an organic solvent. By having the adsorption member contain an organic solvent, it is possible to further reduce liquid pools, and it is possible to produce a high quality coated lens. It is preferable that the adsorption member is brought into contact with the side surface of the lens substrate. By bringing the adsorption member into contact with the side surface, it is possible to easily remove liquid pools on the peripheral edge and / or side surface of the lens substrate.

[0015] The second invention relates to a method for producing a coated lens, utilizing the first invention. Effect of the Invention

[0016] The present invention solves the problem of liquid pooling on the periphery and / or sides of the lens substrate that occurs during spin coating by a first removal step in which the lens substrate itself is rotated to remove the pooling, and then a second removal step in which any remaining pooling is removed with an adsorption member, making it possible to produce high-quality coated lenses using a simple method.

[0017] If a sponge is used as the adsorption member, the sponge itself is flexible and can be easily deformed. Therefore, it can easily contact the peripheral portion of the lens substrate, especially the side, and the liquid pool can be removed. In addition, when the foamed resin, especially the sponge, is used, it is easy to absorb the organic solvent. By using an adsorption member containing an organic solvent, when combined with the first removal step, the liquid pool can be removed more effectively, and a high-quality coated lens can be produced. [Brief description of the drawings]

[0018] [Figure 1] FIG. 2 is a diagram showing a typical embodiment using an adsorption member according to the present invention. [Diagram 2] FIG. 11 is a diagram showing another example in which the adsorption member according to the present invention is used. [Diagram 3] FIG. 4 is a schematic diagram showing a method of contacting an adsorption member when a primer composition is used. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0019] The coating method of the present invention comprises the steps of: providing a coating agent to a surface of the lens substrate; a spreading step of spreading the coating agent supplied to the surface by rotating the lens substrate; a first removing step of removing at least a portion of the pool of the coating agent generated on the peripheral edge and / or side surface of the lens substrate after the spreading step by rotating the lens substrate; and a second removal step of removing the liquid pool remaining on the peripheral edge and / or side surface of the lens substrate by contacting an adsorption member with at least the side surface of the lens substrate after the first removal step; It has the following characteristics.

[0020] The liquid pools may occur only on the periphery of the lens substrate, only on the side of the lens substrate, or on both the periphery and the side of the lens substrate. In any case, the method of the present invention can remove the liquid pools and produce a high-quality coated lens.

[0021] The present invention will be described in detail below with reference to specific embodiments.

[0022] (Lens substrate) The lens substrate in the present invention is not particularly limited, and lens substrates of various shapes can be used. For example, it may be a finished lens with an optical power formed, or a semi-finished lens other than a finished lens.

[0023] Among them, the method of the present invention is preferably applicable to finished lenses. Semi-finished lenses used for spectacle lenses are polished on the back surface and processed for power in the subsequent processing step, so that coating defects on the back surface may be negligible. On the other hand, when a finished lens is used, after forming a coating layer, hard coat and anti-reflection coating processing are directly performed. Therefore, the appearance at the time when the coating layer is formed is particularly important. And, particularly when these lens substrates are used, it is desired that the difference in thickness of the peripheral part is small and the appearance including the side part is better at the time when the coating layer is formed. In addition, when used for normal spectacle lenses, it is a circle with a diameter of 30 to 200 mm, preferably 50 to 100 mm, a thickness at the center is 0.5 to 30 mm, preferably 0.5 to 20 mm, and a thickness (width) of the side (edge ​​surface) of the lens substrate is 0.5 to 30 mm, preferably 0.5 to 20 mm. In addition, the base curve of the surface of the lens substrate is preferably 20 or less, more preferably 15 or less. The lower limit of the curvature is not particularly limited, but is 0.5.

[0024] The material of the lens substrate is not particularly limited, and may be a glass lens or a plastic lens. Examples of the plastic lens include lenses made of (meth)acrylic resins, polycarbonate resins, allyl resins, thiourethane resins, urethane resins, and thioepoxy resins. The plastic lens may be subjected to a chemical treatment using an alkaline solution, an acid solution, or a physical treatment such as corona discharge, plasma discharge, or polishing in order to improve the adhesion of the resulting coating layer.

[0025] In addition, the lens substrate may or may not have a coating layer on its surface. A lens substrate having a primer coating layer, a protective layer, or a hard coating layer on its surface can also be used in the present invention. The primer coating layer or the protective layer is formed as an adhesive layer that enhances the adhesion between the lens substrate and other coating layers. In addition, for another purpose, the primer coating layer, the protective layer, or the hard coating layer is formed as a protective layer that protects the lens substrate from the coating layer formed thereon. As a method for forming the primer coating layer, the protective layer, or the hard coating layer, a known method such as a spin coating method or a dipping method is adopted. The coating material used (material for forming the primer coating layer, the protective layer, or the hard coating layer) is not particularly limited, but examples thereof include urethane-based resins, epoxy-based resins, acrylic-based resins, and silicone-based resins in which metal oxide particles such as silica formed by a sol-gel method are dispersed.

[0026] The method of the present invention is not particularly limited to the coating agent used, as long as it is a method of manufacturing a coated lens by supplying a coating agent to the surface of a lens substrate and forming a coating layer on the surface of the lens substrate.Therefore, the method of the present invention can be suitably adopted even when the coating layer that the lens substrate already has is formed on the surface of the lens substrate by spin coating.That is, the present invention can be suitably adopted even when the method of spreading the primer composition that forms a primer coating layer on the surface of the lens substrate by rotating the lens substrate (spin coating method) is adopted.

[0027] The present invention can be adopted when the coating layer and other functional coating layers are formed by a spin coating method (a method in which a coating agent is spread by rotating a lens substrate). Next, specific examples of forming these coating layers will be described.

[0028] (Process for supplying coating agent) In the present invention, a spin coater equipped with a lens substrate rotating means, a coating agent supplying means, and an adsorption means using an adsorption member is used, and the lens substrate is first placed in the spin coater, and then the coating agent is supplied to the surface of the lens substrate. The lens substrate is then rotated at a predetermined rotation speed to spread the coating agent supplied onto the lens substrate. During this process, a pool of the coating agent is formed on the periphery and / or side of the lens substrate.

[0029] (Spreading step, first removal step, and second removal step; when using a coating agent consisting of a primer composition) (Composition of primer composition, etc.) When the primer composition is used as a coating agent, it is preferable to use the following composition and to achieve the following thickness, although there are no particular limitations. Specifically, it is preferable to satisfy the following ranges of composition and viscosity, because it is easy to obtain a primer coating layer of uniform thickness in the thickness range of 1 to 10 microns. Specifically, the solid content concentration of the primer composition is preferably 10 to 50 mass %. The viscosity at 25°C is preferably adjusted to a range of 1 to 20 mPa·s, more preferably to a range of 4 to 10 mPa·s, and particularly preferably to a range of 4 to 7 mPa·s.

[0030] The viscosity can be adjusted by changing the type and amount of the dispersion medium. Specifically, the primer compositions described in WO2011 / 096304, JP2011-219619, WO2004 / 078476, WO2017 / 039019, etc. are preferably used. The primer composition is not particularly limited, but in order to ensure excellent adhesion, it is preferable to use a primer composition containing polyurethane and an organic solvent, or a primer composition containing moisture-curing urethane. In particular, the primer composition containing moisture-curing urethane is considered to be partially cured even when it is spread on the surface of the lens substrate, and the method of the present invention can be suitably applied.

[0031] The moisture-curing urethane is a polyurethane resin that cures with moisture (humidity) in the air. The polyurethane resin is designed so that isocyanate groups remain in the polyurethane molecule, and some of the isocyanate groups present in the molecule react with moisture in the air to generate carbamic acid, which is then decarbonated to generate an amine, and the amine reacts with the remaining isocyanate groups to generate a urea bond, thereby crosslinking and curing the compound.

[0032] (Spreading step and first removal step; when a primer composition is used) In the coating method of the present invention, after the step of supplying a coating agent to the surface of the lens substrate, a spreading step is carried out in which the coating agent supplied to the surface is spread by rotating the lens substrate. In the present invention, when a primer composition is used as a coating agent, it is preferable to rotate the lens substrate at 10 to 500 rpm to spread the coating agent, although this is not particularly limited. As described above, the viscosity of the primer composition (coating agent) is relatively low. Therefore, in order to form a more stable and smoother primer coat layer, it is more preferable to rotate the lens substrate at 30 to 300 rpm. The time for rotating the lens substrate to spread the coating agent may be appropriately determined depending on the composition and viscosity of the primer composition, the size of the lens substrate, etc., but is usually preferably 1 to 60 seconds (sec.).

[0033] After the spreading step, a first removal step is carried out in which at least a portion of the pool of the coating agent generated on the peripheral edge and / or side surface of the lens substrate is removed by rotating the lens substrate. When the primer composition is used, it is preferable to rotate the lens substrate at 500 to 3000 rpm to remove at least a part of the liquid pools formed on the peripheral edge and / or side surface of the lens substrate (first removal step). In the first removal step, it is preferable to set the rotation speed of the lens substrate higher than the rotation speed of the lens substrate in the spreading step described above, and from this viewpoint, it is more preferable that the rotation speed of the lens substrate in the first removal step is more than 500 rpm and 3000 rpm or less. By rotating the lens substrate within the above range, it is possible to efficiently remove at least a part of the liquid pools while forming a smooth primer coating layer. In order to further enhance this effect, it is more preferable to rotate the lens substrate at 800 to 2000 rpm. In particular, by rotating the lens substrate under these conditions to remove the liquid pools, more stable production can be performed and the yield can be further improved. The time for rotating the lens substrate to remove at least a portion of the liquid puddle may be appropriately determined depending on the composition of the primer composition, the viscosity, the desired thickness of the primer coating layer, the size of the lens substrate, etc., but is usually preferably 1 to 60 seconds (sec.), more preferably 1 to 30 seconds (sec.), and even more preferably 1 to 10 seconds (sec.).

[0034] (Second Removal Step: When a Primer Composition is Used) In the present invention, when the primer composition is used as a coating agent, it is preferable to remove at least a part of the liquid pool by the first removal step described above. In the present invention, after the first removal step is performed, a second removal step is then performed in which an adsorption member is brought into contact with at least the side surface of the lens substrate to remove the liquid pool remaining on the peripheral edge and / or side surface of the lens substrate.

[0035] (Second Removal Step: When Adsorbent / Primer Composition is Used) The adsorption member used in the second removal step is for further removing the liquid pool remaining on the periphery and / or side of the lens substrate. The material of the adsorption member is not particularly limited as long as it has the property of being able to adsorb the coating agent. Among them, it is preferable to use a material that does not swell (is difficult to swell) in the solvent described in detail below. Examples include polyurethane, polyvinyl alcohol, polyolefin, fluororesin, melamine resin, polyamide resin, etc. And, from the viewpoints of the adsorption ability of the coating liquid, durability in repeated adsorption and removal, ease of availability, and ease of processing, it is preferable to use an adsorption member made of a foamed resin. Therefore, it is preferable to use a foamed resin made of polyurethane, melamine resin, polyolefin resin, or polyamide resin. Among them, as described in detail below, the adsorption member preferably contains an organic solvent, and in this case, from the viewpoint of solvent resistance, it is particularly preferable to use an adsorption member made of melamine resin, polyolefin resin, or polyamide resin. Among them, by using an adsorption member made of melamine resin, the abrasion resistance is good, and even if the adsorption member contains an organic solvent, it does not change in shape due to swelling, and can be used stably.

[0036] In addition, it is preferable to use a material having a hardness of 100N to 500N for the suction member. Although a hardness of less than 100N is excellent in the suction ability of the coating agent, the contact area when contacting the lens substrate may be too large, so that the coating liquid is excessively absorbed, and the uniformity of the coating surface tends to decrease (crease defects in the liquid pool at the periphery, which will be described later, tend to occur easily). In addition, a hardness of more than 500N may not be able to come into sufficient contact with the lens substrate, and the coating agent may not be sufficiently absorbed. For these reasons, the hardness of the suction member used is preferably 150N to 400N, and more preferably 200N to 350N. The hardness of the suction member is a value measured in accordance with JIS K6400-2 (A method).

[0037] In addition, the material forming the adsorption member is preferably a foamed resin, and in particular, a foamed resin (foam material) with open cells is preferable. Compared with open cells, a foamed material with closed cells has a lower adsorption capacity and may not be able to adequately adsorb and remove. Therefore, it is preferable to use a so-called sponge as a foamed resin having open cells, which is typical of an adsorption member. In addition, as described in detail below, the use of a sponge makes it easier to use an organic solvent.

[0038] The density of the adsorption material is 5 to 20 kg / m 3 In order to more efficiently remove liquid pools and impregnate the organic solvent, the density is preferably 5 to 15 kg / m 3 It is preferable to use a sponge as the adsorption member having such a density range. The density can be adjusted by the material of the sponge, the pore size of the sponge, etc. The pore size of the sponge is not particularly limited, but in order to achieve particularly excellent effects, it is preferable that it is within the following range. Specifically, when observed with an optical microscope, the maximum diameter is preferably in the range of 1 to 1000 μm, and more preferably in the range of 10 to 800 μm. Such sponges can be commercially available. For example, the "Basotect" (registered trademark) series sold by Inoac Corporation can be mentioned.

[0039] (Second Removal Step: When an Adsorbent / Primer Composition Containing an Organic Solvent is Used) In the present invention, the use of the adsorption member makes it possible to easily and stably remove the liquid pool. In particular, in consideration of more stable production of the product (improvement of yield), it is preferable to use the adsorption member, particularly the sponge containing an organic solvent.

[0040] When using an organic solvent, it is preferable that the primer composition is mixed with the material before it is cured. For example, if the primer composition contains moisture-curable urethane, it is preferable that the primer composition is mixed with the urethane monomer (oligomer) before it is cured, or that the urethane monomer (oligomer) can be dispersed in the organic solvent. Specifically, alcohol solvents, ketone solvents, aromatic solvents, halogen solvents, ester solvents, etc. can be mentioned. Among them, in consideration of ease of handling, effects on the human body, removal effect of liquid pools, etc., it is preferable to use a ketone solvent, and it is most preferable to use acetone, methyl ethyl ketone, and methyl isobutyl ketone. In particular, when the organic solvent is a ketone-based solvent and the material forming the adsorption member is a foamed resin, or when the organic solvent is a ketone-based solvent and the material forming the adsorption member is a melamine resin, the effect of removing liquid pools is further improved, which is preferable.

[0041] When the adsorption member contains an organic solvent, the amount of the organic solvent contained in the adsorption member is not particularly limited, but is preferably about 1 cm 3 It is preferable to adjust the amount of organic solvent to 0.1 to 2 g per volume. By containing an organic solvent in this range, liquid pools can be removed efficiently and stably, and a high-quality coated lens can be obtained. In particular, when a primer composition containing a moisture-curing urethane resin is used, in addition to removing liquid pools, some polymer-like deposits may adhere to the periphery and sides of the lens substrate. By keeping the amount of organic solvent within the above range, these deposits can also be removed, and high-quality coated lenses can be produced with good yield. On the other hand, when the sponge contains an excessive amount of organic solvent (for example, when the sponge is 1 cm 3 If the organic solvent exceeds 2 g per volume, the organic solvent will seep into the coating layer and will tend to remove excess liquid puddles and become eroded, which may result in wrinkle defects.

[0042] (Second Removal Step / Shape of Adsorption Member, Conditions for Removing Liquid Pool; When a Primer Composition is Used) In the present invention, the shape of the suction member is not particularly limited. In particular, when removing the liquid pool with the suction member, it is preferable to bring the suction member into contact with at least the side surface of the lens substrate while rotating the lens substrate. By bringing the suction member into contact with the side surface, the liquid pool on the peripheral edge of the lens substrate can be easily removed.

[0043] (Suitable arrangement of the adsorbent member; when a primer composition is used) The primer coat layer formed on the surface of the lens substrate is often a relatively thin film compared to other functional layers. Therefore, compared to other functional layers, the thickness unevenness and appearance problems at the periphery of the lens substrate can be easily adjusted by carrying out the first removal step. However, when forming a thin film (when spin-coating), the primer composition containing an organic solvent may increase in viscosity (drying) as the organic solvent evaporates, and its fluidity may easily decrease. And, even before the curing step (the step of turning the applied primer composition into a primer coat layer) described in detail below, the primer composition tends to dry and harden in part. Therefore, when a primer composition is used, it is preferable to remove the liquid pool in this second removal step and to remove the hardened product formed on the side in part. In particular, when a composition containing polyurethane containing an organic solvent, particularly a moisture-curable urethane containing an organic solvent, is used as the primer composition, the hardened product on the side is easily generated, so it is preferable to use the following method.

[0044] That is, the suction member is arranged so that the uppermost position of the suction member is located at a position 3 to 30% of the length (k) of the side surface from the upper end edge of the side surface of the lens substrate. It is preferable that the suction member always contacts the side surface from the same position as the uppermost position of the suction member and below. By setting the uppermost position of the suction member within the above range, not only can the liquid pool be removed, but the cured product can also be removed efficiently. In consideration of the removal of the liquid pool and the cured product, it is preferable that the uppermost position of the suction member is located at a position 5 to 20% of the length (k) of the side surface from the upper end edge of the side surface of the lens substrate.

[0045] In addition, if the top of the suction member is placed less than 3% of the side length (k) from the top edge of the lens substrate side surface, the following defects tend to occur. Specifically, if it is placed at a too high position, especially when the suction member contains an organic solvent, the organic solvent may seep into the coating layer (coating film) on the lens substrate surface from the peripheral portion of the lens substrate. Alternatively, if it is placed at a too high position, the suction member itself may bend and cover the peripheral surface of the lens substrate, and there is a risk of removing too much of the primer composition applied to the lens surface. For these reasons, it is preferable to place the suction member so that the top of the suction member is located at a position that is 3% or more of the side length (k) from the top edge. If too much primer composition is removed, it is easy to cause wrinkle defects in the peripheral portion described below.

[0046] On the other hand, if the uppermost part of the adsorption member is located at a position that is more than 30% below the length k, the effect of removing liquid pools and hardened material tends to decrease.

[0047] (Suitable shape and contact conditions of the adsorption member; when a primer composition is used) The suction member is preferably brought into contact with the side surface of the lens substrate at the above-mentioned position, and in this case, it is preferable to bring the suction member into contact with the side surface while rotating the lens substrate. In addition, it is preferable to have a structure in which the suction member in contact rotates in the opposite direction to the rotation of the lens substrate. Therefore, the suction member in contact is preferably cylindrical, and the cylindrical side wall surface is preferably the abutting portion. In particular, it is preferable to have a structure in which the suction member can rotate freely around a cylindrical core axis (the central axis of the cylinder). In order to improve operability, it is preferable to use a roller in which the suction member is covered around the rotating shaft (a roller in which a rotating shaft is installed in the hollow part of the suction member that has become hollow). In this case, the diameter of the rotating shaft is preferably 10 to 50 mm, and the thickness of the suction member is preferably 2 to 50 mm (the thickness of the suction member covering the rotating shaft), more preferably 2 to 45 mm, and particularly preferably 5 to 30 mm. In this case, the height of the suction member is sufficient if it is the length from the uppermost part to the lowermost edge of the side surface, but specifically, it is preferably 5 to 50 mm, and more preferably 10 to 40 mm.

[0048] In addition, the adsorption member of this shape can be used to remove liquid pools from multiple lens substrates. It can be used repeatedly multiple times as long as the quality of the resulting coated lens can be maintained. However, in order to obtain a stable, high-quality coated lens, it is preferable to adjust the adsorption member to be in the same state each time. The same state means that there is no change in the dimensions and shape of the adsorption member, and in particular, there is no dirt on the surface of the adsorption member that contacts the side surface of the lens substrate. The following methods can be mentioned as cleaning methods for cleaning the adsorption member for this purpose. Specifically, the adsorption member containing the primer composition or the like is periodically immersed in the organic solvent, and then the organic solvent contained in the adsorption member is sucked or squeezed out to clean it. Among them, solvent removal by suction is a preferred method because it is less likely to cause a change in the shape of the adsorption member.

[0049] (Preferable embodiment of the adsorption member: when a primer composition is used) The adsorption member used is not particularly limited, and any adsorption member made of the above-mentioned material and having the above-mentioned characteristics can be used. Among them, it is preferable to use the above-mentioned sponge, and it is further preferable that the sponge contains an organic solvent. In particular, when a primer composition containing a moisture-curing urethane resin is used, it is preferable to use a sponge containing an organic solvent. Among them, when an organic solvent is used, it is preferable to use a ketone-based solvent, and the amount of the solvent is, as described above, about 1000 g / cm of sponge. 3 It is preferable that the amount of the sponge is 0.1 to 2 g per 1 cm of the sponge. In particular, when a primer composition containing a moisture-curing urethane resin is used, it is preferable that the amount of the sponge is 0.1 to 2 g per 1 cm of the sponge. 3 The amount of the organic solvent is preferably 0.2 to 1.5 g, and more preferably 0.3 to 1 g.

[0050] When using an adsorption member containing an organic solvent, it is possible to treat multiple lens substrates if the amount of organic solvent is within the above range. However, in order to obtain coated lenses of higher quality, it is recommended to use an amount of organic solvent within the above range each time (1 cm of sponge). 3 The amount of organic solvent is preferably 0.1 to 2 g, more preferably 0.2 to 1.5 g, and more preferably 0.3 to 1 g per unit volume.) It is preferable to automatically supply the organic solvent and adjust the content so that the organic solvent falls within a suitable content range.

[0051] (Suitable contact conditions for the adsorption member: when a primer composition is used) As described above, it is preferable that the adsorption member contacts the side surface of the lens substrate in a rotated state. In particular, when a primer composition is used, it is preferable to contact the adsorption member to the side surface under the following conditions. Specifically, in order to stably remove liquid pools and hardened products, the pressing load (hereinafter, sometimes referred to as the contact force) is preferably 20 to 200 g, and more preferably 30 to 150 g. As a method for adjusting this load, a method of pressing the adsorption member against the side surface of the lens substrate using a means having a spring can be adopted. Specifically, a method of appropriately adjusting the coefficient of the "spring" attached to the base part (in FIG. 2) of the adsorption member (for example, a cylindrical sponge) can be adopted.

[0052] The rotation speed of the lens substrate during contact is preferably 30 to 200 rpm, and more preferably 50 to 100 rpm for more stable removal of accumulated liquid and cured products. The contact time may be appropriately determined, but is usually preferably 1 to 60 seconds (sec), more preferably 1 to 30 seconds (sec), and even more preferably 1 to 20 seconds (sec).

[0053] When a primer composition is used, it is preferable to carry out treatment according to the above-mentioned method. Next, a method for curing the coating agent applied to the surface of the lens substrate when a primer composition is used will be described.

[0054] (Coat layer, method of forming coat layer: When a primer composition is used) After removing the liquid pool by the above method, the lens substrate to which the coating agent has been applied can be treated by a known method to form a primer coating layer on the surface of the lens substrate. In other words, a curing method appropriate for each material contained in the primer composition can be adopted.

[0055] For example, in the case where a polymerizable monomer (including an oligomer) and a thermal polymerization initiator and / or a photopolymerization initiator are contained, the polymerizable monomer may be cured under conditions where the polymerizable monomer undergoes thermal polymerization and / or photopolymerization. In the case where a primer composition contains a polymer and an organic solvent, the primer composition may be cured under conditions where the organic solvent is dried. In the case where a primer composition containing a moisture-curing urethane is used, it is preferable to cure the primer composition by humidification and, if necessary, heating. Specifically, it is preferable to cure the primer composition containing a moisture-curing urethane under conditions of humidity of 10 to 80% and temperature of 20 to 120°C.

[0056] In the resulting coated lens, the thickness of the primer coating layer is not particularly limited, but is preferably 0.1 to 10 μm, and more preferably 1 to 10 μm.

[0057] In the case of a primer coat layer having such a thickness, it may be difficult to distinguish the difference between the evaluation of the width of the liquid pool and the evaluation of the wrinkles of the liquid pool, which will be described in detail below. The wrinkles of the liquid pool are considered to be defects that occur when the organic solvent contained in the adsorption member penetrates into the coating layer, or when the adsorption member is pushed into the surface of the lens substrate, causing the coating film (coating film) at the peripheral portion to be removed (eroded). In addition, when forming a primer coat layer, a cured product may adhere to the side surface. In particular, when a primer composition containing a moisture-curing urethane is used, the adhesion of such a cured product may be a problem. In particular, in the case of a finished lens that immediately proceeds to the next process, this is a major problem in terms of appearance. This cured product can be removed by treating the side surface (for example, polishing, etc.), but this is not a preferred operation because it increases the number of steps. In the present invention, as described in detail below, the evaluation was performed based on the yield results when a primer coat layer was laminated on 20 lens substrates.

[0058] In the present invention, a lens substrate having a primer coating layer on its surface (hereinafter, sometimes simply referred to as a "primer-coated lens substrate") can be manufactured by the above-mentioned method. In the present invention, this primer-coated lens can be used as a lens substrate, and a functional layer can be further coated thereon. The functional layer is not particularly limited, and may be a layer containing various dyes and ultraviolet absorbers. In particular, the method of the present invention can be suitably employed when using a coating agent consisting of a photochromic curable composition containing a photochromic compound and a polymerizable monomer.

[0059] That is, in the present invention, it is possible to form a coating layer multiple times on the surface of the lens substrate, and after coating the lens substrate with a primer composition to form a primer coating layer as described above, a photochromic curable composition can be coated on the primer layer to form a photochromic coating layer.

[0060] In other words, the above-mentioned coating agent supplying step, spreading step, first removing step, and second removing step can be repeated in this order.For example, a coating agent made of a primer composition is supplied onto a lens substrate, and a spreading step, a first removing step, and a second removing step are carried out to form a primer coating layer, and then a photochromic curable composition described later is supplied onto the primer coating layer, and a spreading step, a first removing step, and a second removing step are carried out to form a photochromic coating layer.In this way, a primer coating layer and a photochromic coating layer can be formed on a lens substrate to manufacture a photochromic lens.

[0061] Next, the case where a coating agent comprising the photochromic curable composition is used will be described.

[0062] (Lens substrate; when forming a functional layer) In the present invention, even when a functional layer containing a photochromic compound is formed, the same lens substrate as that explained above in (Lens Substrate) can be used.

[0063] Among them, the above-mentioned primer-coated lens substrate can be preferably used. Among them, the method of the present invention can be preferably adopted when the thickness of the primer coat layer in the primer-coated lens substrate is 1 to 10 μm, more preferably 3 to 10 μm. As described above, if the thickness of the primer coat layer is about 10 μm, it is a relatively thin film, so the thickness and wrinkles of the peripheral part of the primer-coated lens substrate itself may not be a big problem. However, when a primer coat layer exists and a functional layer is formed on the layer, the problems of the thickness and wrinkles of the peripheral part are considered important. The present invention can efficiently solve the problems of the thickness and wrinkles when a functional layer is formed on the primer coat layer of such a primer-coated lens substrate. In particular, the method of the present invention can be preferably adopted when using a primer-coated lens substrate having a primer coat layer on a finished lens.

[0064] (Process for supplying coating agent) In the present invention, as described above, the functional layer can be laminated using a spin coater equipped with a lens substrate rotating means, a coating agent supplying means, and an adsorption means using an adsorption member. A known method can be used to supply the coating agent. The reason why the liquid pools are formed is as described above.

[0065] (Spreading step, first removal step, and second removal step; when using a coating agent that will become a functional layer) (Composition of the coating agent that forms the functional layer) When forming a functional layer, a coating agent with a relatively high viscosity is often used to form a thick coating layer, which can cause problems with the thickness and wrinkles at the periphery, especially in the coating of finished lenses.

[0066] The coating agent for forming the functional layer is not particularly limited. In particular, when the coating thickness of the functional layer is 10 to 100 microns, the viscosity (25°C) is preferably 20 to 5000 mPa·s, more preferably 50 to 1000 mPa·s, even more preferably 70 to 500 mPa·s or less, and particularly preferably 100 to 300 mPa·s. In particular, when a coating agent made of a photochromic curable composition containing a photochromic compound and a polymerizable monomer is used, it is preferable that the viscosity is satisfied. When the coating agent contains a photochromic compound, the thickness of the coating layer can be relatively thickened by satisfying the above viscosity range. Since a thick film is formed, the method of the present invention can be suitably adopted. Next, this photochromic curable composition will be described.

[0067] (Composition of the coating agent made of the photochromic curable composition) The photochromic curable composition (hereinafter, sometimes simply referred to as "photochromic liquid") contains a photochromic compound and a polymerizable monomer, and preferably contains (a) a photochromic compound, (b) a polymerizable monomer, and (c) a photopolymerization initiator as components.

[0068] (Photochromic Compound) As the photochromic compound (a), any known photochromic compound can be used without any limitation, for example, a fulgimide compound, a spirooxazine compound, a chromene compound, or the like.

[0069] Among these photochromic compounds, chromene-based photochromic compounds are particularly suitable for use because they have higher durability of photochromic properties than other photochromic compounds and are particularly superior to other photochromic compounds in terms of color development density and fading speed of the photochromic properties.

[0070] Specific examples of chromene-based photochromic compounds that can be suitably used in the present invention include the following compounds.

[0071] [ka]

[0072] [ka]

[0073] [ka]

[0074] The (a) photochromic compound may be used in a suitable mixture of a plurality of types in order to obtain a desired color tone.

[0075] The amount of the (a) photochromic compound blended is preferably 0.01 to 20 parts by mass, more preferably 0.05 to 15 parts by mass, and most preferably 0.1 to 10 parts by mass, relative to 100 parts by mass of the (b) polymerizable monomer blended in the photochromic liquid. By setting the amount within this range, it becomes easy to obtain a sufficient color density and to dissolve the photochromic compound uniformly in the polymerizable monomer, and therefore it becomes easy to obtain a sufficient and uniform color density.

[0076] (Polymerizable monomer) As the (b) polymerizable monomer, any known radical polymerizable monomer can be used without any limitation depending on the purpose, such as improving the surface hardness, improving the impact resistance, and further improving the adhesion to a hard coat layer or an antireflection layer provided as an outer layer.

[0077] (Radical polymerizable monomer) Specific examples of such radical polymerizable monomers include trimethylolpropane trimethacrylate, trimethylolpropane triacrylate, tetramethylolmethane trimethacrylate, tetramethylolmethane triacrylate, tetramethylolmethane tetramethacrylate, tetramethylolmethane tetraacrylate, trimethylolpropane triethylene glycol trimethacrylate, trimethylolpropane triethylene glycol triacrylate, ditrimethylolpropane tetramethacrylate, ditrimethylolpropane tetraacrylate, dipentaerythritol hexaacrylate, bisphenol A dimethacrylate, 2,2-bis(4-methacryloyloxyethoxyphenyl)propane, 2,2-bis(4-methacryloyloxypolyethylene glycol phenyl)propane having an average molecular weight of 628, 2,2-bis(4-methacryloyloxypolyethylene glycol phenyl)propane having an average molecular weight of 804, 2,2-bis(4-methacryloyloxypolyethylene glycol phenyl)propane having an average molecular weight of 776, and 2,2-bis(4-methacryloyloxyethoxyphenyl)propane having an average molecular weight of 805.2-bis(4-acryloyloxypolyethylene glycol phenyl)propane, methoxypolyethylene glycol methacrylate having an average molecular weight of 468, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, pentaethylene glycol dimethacrylate, pentapropylene glycol dimethacrylate, diethylene glycol diacrylate, triethylene glycol diacrylate, tetraethylene glycol diacrylate, pentaethylene glycol diacrylate, tripropylene glycol diacrylate, tetrapropylene glycol diacrylate, pentapropylene glycol diacrylate, polyethylene glycol dimethacrylate having an average molecular weight of 330, polyethylene glycol dimethacrylate having an average molecular weight of 536, polytetramethylene glycol dimethacrylate having an average molecular weight of 736, tripropylene glycol dimethacrylate, Examples of the silsesquioxane include tetrapropylene glycol dimethacrylate, polypropylene glycol dimethacrylate having an average molecular weight of 536, polyethylene glycol diacrylate having an average molecular weight of 258, polyethylene glycol diacrylate having an average molecular weight of 308, polyethylene glycol diacrylate having an average molecular weight of 508, polyethylene glycol diacrylate having an average molecular weight of 708, polycarbonate di(meth)acrylate which is a reaction product of polycarbonate diol and (meth)acrylic acid, polyfunctional urethane (meth)acrylates such as urethane oligomer tetraacrylate, urethane oligomer hexamethacrylate, and urethane oligomer hexaacrylate, polyfunctional polyester (meth)acrylates such as polyester oligomer hexaacrylate, silsesquioxane monomers having (meth)acrylic groups and various structures such as cage-shaped, ladder-shaped, and random, and 2-isocyanatoethyl methacrylate.

[0078] The radical polymerizable monomers may be used in a suitable mixture of two or more kinds, taking into consideration the properties of the cured product, such as solvent resistance, hardness, and heat resistance, after curing of the coating agent.

[0079] In addition to the above, the radical polymerizable monomer may also include a radical polymerizable monomer having at least one epoxy group and at least one radical polymerizable group in the molecule (hereinafter, may be simply referred to as an epoxy-based monomer).

[0080] By using an epoxy monomer as a component of the radically polymerizable monomer, the adhesion between the coating layer and the lens substrate is improved.

[0081] As such an epoxy monomer, any known compound can be used without any limitation, but a compound having a (meth)acryloyloxy group as a radical polymerizable group is preferred.

[0082] Specific examples of the epoxy monomer include glycidyl acrylate, glycidyl methacrylate, β-methylglycidyl methacrylate, bisphenol A-monoglycidyl ether-methacrylate, 4-glycidyloxy methacrylate, 3-(glycidyl-2-oxyethoxy)-2-hydroxypropyl methacrylate, 3-(glycidyloxy-1-isopropyloxy)-2-hydroxypropyl acrylate, 3-(glycidyloxy-2-hydroxypropyloxy)-2-hydroxypropyl acrylate, glycidyloxy polyethylene glycol methacrylate having an average molecular weight of 540 (main component is in the range of molecular weight 390 to 660), etc. Among these, glycidyl acrylate, glycidyl methacrylate, and glycidyloxy polyethylene glycol methacrylate having an average molecular weight of 540 (main component is in the range of molecular weight 390 to 660) are particularly preferred.

[0083] When these epoxy monomers are contained, the blending ratio is preferably 0.01 to 30% by mass, particularly preferably 0.1 to 20% by mass, in the radical polymerizable monomers.

[0084] In addition to the above, the radical polymerizable monomer may also include a radical polymerizable monomer having a silanol group (≡Si-OH) or a group that generates a silanol group upon hydrolysis (hereinafter, sometimes referred to as a silyl monomer) or a radical polymerizable monomer having an isocyanate group (hereinafter, sometimes referred to as an isocyanate monomer). By using a silyl monomer or an isocyanate monomer as a component of the radical polymerizable monomer, it is possible to further increase the adhesion between the coating layer and the lens substrate, particularly when the lens substrate is a plastic lens, and it is also possible to increase the adhesion with the hard coat layer when a hard coat layer is provided as an outer layer.

[0085] Specific examples of the silyl monomer include γ-methacryloyloxypropyltrimethoxysilane, γ-methacryloyloxypropyltriethoxysilane, γ-methacryloyloxypropylmethyldimethoxysilane, (3-acryloxypropyl)dimethylmethoxysilane, (3-acryloxypropyl)methyldimethoxysilane, (3-acryloxypropyl)trimethoxysilane, 3-(N-allylamino)propyltrimethoxysilane, allyldimethoxysilane, allyltriethoxysilane, allyltrimethoxysilane, 3-aminophenoxydimethylvinylsilane, 4-aminophenoxydimethylvinylsilane, 3-(3-aminopropoxy)-3,3-dimethyl-1-propenyltrimethoxysilane, butenyltriethoxysilane, Silane, 2-(chloromethyl)allyltrimethoxysilane, diethoxyvinylsilane, 1,3-divinyltetraethoxydisiloxane, docosenyltriethoxysilane, O-(methacryloxyethyl)-N-(triethoxysilylpropyl)urethane, N-(3-methacryloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane, methacryloxyethoxytrimethylsilane, (methacryloxymethyl)dimethylethoxysilane, methacryloxymethyltriethoxysilane, methacryloxymethyltrimethoxysilane, methacryloxypropyldimethylethoxysilane, methacryloxypropyldimethylmethoxysilane, methacryloxypropyltris(methoxyethoxy)silane, 7-octenyltrimethoxysilane, 1,Examples of the silane include 3-bis(methacryloxy)-2-trimethylsiloxypropane, tetrakis(2-methacryloxyethoxy)silane, trivinylethoxysilane, trivinylmethoxysilane, vinyldimethylethoxysilane, vinyldiphenylethoxysilane, vinylmethyldiacetoxysilane, vinylmethyldiethoxysilane, vinylmethyldimethoxysilane, O-(vinyloxyethyl)-N-(triethoxysilylpropyl)urethane, vinyloxytrimethylsilane, vinylphenyldiethoxysilane, vinylphenylmethylmethoxysilane, vinyltriacetoxysilane, vinyltri-t-butoxysilane, vinyltriethoxysilane, vinyltriisopropenoxysilane, vinyltriisopropoxysilane, vinyltrimethoxysilane, vinyltriphenoxysilane, and vinyltris(2-methoxyethoxy)silane.

[0086] Among these, γ-methacryloyloxypropyltrimethoxysilane, γ-methacryloyloxypropyltriethoxysilane, γ-methacryloyloxypropylmethyldimethoxysilane, (3-acryloxypropyl)dimethylmethoxysilane, (3-acryloxypropyl)methyldimethoxysilane, (3-acryloxypropyl)trimethoxysilane, (methacryloxymethyl)dimethylethoxysilane, methacryloxymethyltriethoxysilane, methacryloxymethyltrimethoxysilane, methacryloxypropyldimethylethoxysilane, and methacryloxypropyldimethylmethoxysilane can be particularly preferably used.

[0087] Specific examples of isocyanate monomers that can be suitably used include 2-isocyanatoethoxy methacrylate, 4-(2-isocyanatoisopropyl)styrene, and the like.

[0088] When a silyl monomer or an isocyanate monomer is contained in the photochromic liquid, the blending amount is not particularly limited, but in order to improve adhesion to the lens substrate and the hard coat layer and to improve scratch resistance when a hard coat layer is provided, the blending amount is preferably 0.5 to 20 mass %, and more preferably 1 to 10 mass %, in terms of the ratio in the radical polymerizable monomer.

[0089] Moreover, these silyl monomers or isocyanate monomers can be used alone or in combination, and it is also possible to use a mixture of a silyl monomer and an isocyanate monomer.

[0090] (Other ingredients: amine compounds) The photochromic liquid may contain an amine compound in addition to the radical polymerizable monomer. By using a photochromic liquid containing an amine compound, the adhesion between the coating layer formed by curing and the lens substrate can be improved.

[0091] As such an amine compound, a compound having an amino group can be used without any restrictions.Specific examples of amine compounds that can be suitably used include non-polymerizable low molecular weight amine compounds such as triethanolamine, N-methyldiethanolamine, triisopropanolamine, 4,4-dimethylaminobenzophenone, and diazabicyclooctane; amine compounds having a polymerizable group such as N,N-dimethylaminoethyl methacrylate and N,N-diethylaminoethyl methacrylate; and amine compounds having a silyl group such as n-(hydroxyethyl)-N-methylaminopropyltrimethoxysilane, dimethoxyphenyl-2-piperidinoethoxysilane, N,N-diethylaminomethyltrimethylsilane, and (N,N-diethyl-3-aminopropyl)trimethoxysilane.

[0092] These amine compounds can be used alone or in combination. The amount of these amine compounds to be added is preferably 0.1 to 20 parts by mass, more preferably 0.5 to 10 parts by mass, and even more preferably 1 to 10 parts by mass, relative to 100 parts by mass of the radical polymerizable monomer contained in the photochromic liquid. By adjusting the amount to this range, high adhesion can be obtained.

[0093] (Polymerization initiator) The (c) photopolymerization initiator can be used without any limitation as long as it can be decomposed by irradiation with light or the like and can cure the (b) polymerizable monomer.

[0094] Specific examples of the photopolymerization initiator include monoacylphosphine oxide compounds such as 2,6-dimethylbenzoyldiphenylphosphine oxide, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, 2,6-dichlorobenzoyldiphenylphosphine oxide, and 2,6-dimethoxybenzoyldiphenylphosphine oxide; bis(2,6-dimethoxybenzoyl)-2,4,4-trimethylpentylphosphine oxide; bis(2,6-dimethylbenzoyl)-2,4,4-trimethylpentylphosphine oxide; bis(2,4,6-trimethylbenzoyl)-2,4,4-trimethylpentylphosphine oxide, bis(2,6-dichlorobenzoyl)-2,4,4-trimethylpentylphosphine oxide, bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide, bis(2,4,6-trimethoxybenzoyl)-phenylphosphine oxide and other bisacylphosphine oxide compounds;Benzophenol, acetophenone, 4,4'-dichlorobenzophenone, methylphenyl glyoxylate, thioxanthone, 2,4-dimethylthioxanthone, 2-methylthioxanthone, 2-chlorothioxanthone, diisopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone, 2-isopropylthioxanthone, 3,3',4,4'-tetra(t-butylperoxycarbonyl)benzophenone, camphorquinone, dibenzosuberone, 2-ethyla Anthraquinone, 4',4"-diethylisophthalophenone, 9,10-phenanthrenequinone, 1-phenyl-1,2-propanedione-2(O-ethoxycarbonyl)oxime, benzophenone, methyl orthobenzoylbenzoate, orthobenzoylbenzoic acid, 4-benzoyl-4'-methyldiphenylsulfide, 2,2-dimethoxy-1,2-diphenylethan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1, 2-methyl-1-[4-(methyl 1-[4-(2-hydroxyethoxy)phenyl]-2-hydroxy-2-methyl-1-propan-1-one, 1-hydroxy-cyclohexyl-phenyl-ketone, 1-[4-(2-hydroxyethoxy)-phenyl]-2-hydroxy-2-methyl-1-propan-1-one, 2-hydroxy-2-methyl-1-phenyl-propan-1-one, 4-phenylbenzophenone, hydroxybenzophenone, 3,3'-dimethyl-4-methoxybenzophenone, benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin iso Propyl ether, benzoin isobutyl ether, 4-phenoxydichloroacetophenone, 4-t-butyl-dichloroacetophenone, 4-t-butyl-trichloroacetophenone, diethoxyacetophenone, 1-(4-isopropylphenyl)-2-hydroxy-2-methylpropan-1-one, 1-(4-dodecylphenyl)-2-hydroxy-2-methylpropan-1-one, 4-(2-hydroxyethoxy)-phenyl(2-hydroxy-2-propyl)ketone, and the like.

[0095] These photopolymerization initiators are generally used in the range of 0.001 to 5 parts by mass per 100 parts by mass of the (b) radical polymerizable monomer. The above photopolymerization initiators may be used alone or in combination of two or more kinds.

[0096] The photochromic liquid may contain a thermal polymerization initiator in addition to the photopolymerization initiator, and this allows the liquid to be cured by heating after or simultaneously with irradiation with light or the like.

[0097] The thermal polymerization initiator is not particularly limited, and known ones can be used. Representative examples include diacyl peroxides such as benzoyl peroxide, p-chlorobenzoyl peroxide, decanoyl peroxide, lauroyl peroxide, and acetyl peroxide; peroxy esters such as t-butyl peroxy-2-ethylhexanoate, t-butyl peroxydicarbonate, cumyl peroxyneodecanate, and t-butyl peroxybenzoate; percarbonates such as diisopropyl peroxydicarbonate, di-2-ethylhexyl peroxydicarbonate, and di-sec-butyloxycarbonate; and azo compounds such as 2,2'-azobisisobutyronitrile, 2,2'-azobis(4-dimethylvaleronitrile), 2,2'-azobis(2-methylbutyronitrile), and 1,1'-azobis(cyclohexane-1-carbonitrile).

[0098] The amount of the thermal polymerization initiator used varies depending on the curing conditions, the type of initiator, and the type and composition of the radical polymerizable monomer, and cannot be generally limited, but it is generally preferable to use the thermal polymerization initiator in the range of 0.01 to 10 parts by mass per 100 parts by mass of the radical polymerizable monomer (b). The thermal polymerization initiators may be used alone or in combination of two or more kinds.

[0099] (Other added ingredients) To the photochromic liquid, additives such as surfactants, antioxidants, radical scavengers, ultraviolet stabilizers, ultraviolet absorbers, release agents, coloring inhibitors, antistatic agents, fluorescent dyes, dyes, pigments, fragrances, plasticizers, etc. may be added in order to prevent yellowing of the coating layer (coat layer) and improve formability, and further to improve the durability of the photochromic compound when added, improve the color development speed, and improve the fading speed, etc., within a range that does not impair the effects of the present invention.

[0100] For example, any of nonionic, anionic, and cationic surfactants can be used as the surfactant, but it is preferable to use a nonionic surfactant because of its solubility in radical polymerizable monomers. Specific examples of nonionic surfactants that can be suitably used include sorbitan fatty acid esters, glycerin fatty acid esters, decaglycerin fatty acid esters, propylene glycol-pentaerythritol fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbit fatty acid esters, polyoxyethylene glycerin fatty acid esters, polyethylene glycol fatty acid esters, polyoxyethylene alkyl ethers, polyoxyethylene phytosterol-phytostanol, polyoxyethylene polyoxypropylene alkyl ethers, polyoxyethylene alkylphenyl ethers, polyoxyethylene castor oil-hydrogenated castor oil, polyoxyethylene lanolin-lanolin alcohol-beeswax derivatives, polyoxyethylene alkylamine-fatty acid amides, polyoxyethylene alkylphenyl formaldehyde condensates, and single-chain polyoxyethylene alkyl ethers. When using surfactants, two or more types may be mixed together. The amount of the surfactant added is preferably within a range of 0.1 to 20 parts by mass relative to 100 parts by mass of the (b) radically polymerizable monomer.

[0101] As the antioxidant, radical scavenger, ultraviolet stabilizer, and ultraviolet absorber, a hindered amine light stabilizer, a hindered phenol antioxidant, a phenol radical scavenger, a sulfur antioxidant, a benzotriazole compound, a benzophenone compound, and the like can be suitably used. These antioxidants, radical scavengers, ultraviolet stabilizers, and ultraviolet absorbers may be used in combination of two or more. Furthermore, when using these non-polymerizable compounds, a surfactant may be used in combination with an antioxidant, a radical scavenger, an ultraviolet stabilizer, and an ultraviolet absorber. The amount of these antioxidants, radical scavengers, ultraviolet stabilizers, and ultraviolet absorbers added is preferably in the range of 0.001 to 20 parts by mass, respectively, relative to 100 parts by mass of the (b) polymerizable monomer.

[0102] In the present invention, the photochromic curable composition is adjusted to have a viscosity (25°C) of preferably 20 to 5000 mPa·s, more preferably 50 to 1000 mPa·s, further preferably 70 to 500 mPa·s or less, and particularly preferably 100 to 300 mPa·s, by blending and mixing the components exemplified above.

[0103] (Spreading step and first removal step; when a coating agent that serves as a functional layer is used) In the present invention, the coating agent constituting the functional layer is supplied to the surface of the lens substrate and spread by a known method, i.e., by using a spin coating method. In particular, when a coating agent consisting of a photochromic curable composition is used, the following method can be adopted.

[0104] First, the photochromic curable composition is supplied to the center of the primer coating layer of the primer-coated lens substrate, and the lens substrate is rotated at a rotation speed of 10 to 500 rpm, more preferably at a rotation speed of 30 to 300 rpm, and even more preferably at a rotation speed of 50 to 200 rpm. At this time, the photochromic curable composition can be spread using a coating liquid spreading assistant mechanism made of a resin film such as polypropylene or polyethylene terephthalate. The spreading time may be appropriately determined in consideration of the rotation speed of the lens substrate, the size of the lens substrate, and the like. In particular, in consideration of operability, the thickness of the obtained photochromic layer, and the like, the spreading time is preferably 5 to 120 seconds (sec.), and more preferably 10 to 60 seconds (sec.).

[0105] Next, it is preferable to carry out a first removal step (a step of removing at least a part of the liquid pool generated by spreading by rotating the lens substrate). In the first removal step, it is preferable to set the rotation speed of the lens substrate to more than 500 rpm and not more than 2000 rpm to remove at least a part of the liquid pool. In consideration of operability and efficiency of removing the liquid pool, it is preferable to carry out the first removal step at a rotation speed of the lens substrate to more than 500 rpm and not more than 1500 rpm, and it is further preferable to carry out the first removal step at a rotation speed of the lens substrate of 600 to 1300 rpm. The time for carrying out the first removal step is not particularly limited, but in order to efficiently remove the liquid pool, it is preferably 1 to 60 seconds (sec.), more preferably 1 to 30 seconds (sec.), and even more preferably 1 to 10 seconds (sec.).

[0106] When a coating agent for forming a functional layer is used, the first removal step can be performed, followed by the second removal step. After the first removal step, a spatula can be brought into contact with the side surface of the lens substrate to further remove excess liquid pools, and then the second removal step can be performed. By providing a step of bringing the spatula into contact, it becomes easier to form a coating layer (manufacture a coated lens) on a lens substrate having a large base curve, on which it is difficult to form a high-quality coating layer when forming a functional layer. In particular, when forming a coating layer on a lens substrate having a base curve of 4 or more, it is preferable to provide a step of bringing the spatula into contact. The step of bringing the spatula into contact (spatula contact step) after the first removal step will be described.

[0107] <Spatula contact process; especially when forming a functional layer> As described above, when forming a functional layer, a spatula can be brought into contact with the side surface of the lens substrate in the latter half of the first removal step or after the first removal step (preferably after the first removal step) to further remove excess liquid pools. This spatula contact step is not essential, but can be suitably employed particularly when forming a coating layer having a base curve on the surface of the lens substrate of 4 or more, preferably 5 or more, and more preferably 5 to 15. That is, it is desirable to remove excess coating liquid with a spatula before carrying out the contact process with the adsorption member.

[0108] The material and shape of the spatula used are not particularly limited, but for example, spatulas made of metal, plastic such as polyethylene terephthalate (PTFE), or rubber such as silicone can be used. The shape is sufficient as long as it can come into close contact with the side surface of the lens substrate, and preferably the part that comes into contact with the side surface of the lens substrate is linear. Needless to say, the spatula contact step can produce high-quality coated lenses even when applied to lenses with a base curve of less than 4.

[0109] When the thickness of the spatula (thickness of the spatula tip) that contacts the side surface of the lens substrate is large (when the contact area is large), the shape of the liquid pool in the peripheral area may become large. In particular, in the case of a lens substrate with a high curve and a thin side surface, the liquid pool tends to become large. This tendency is particularly strong when the base curve of the surface of the lens substrate is 5 or more. In order to efficiently remove excess coating liquid and reduce liquid pools in the peripheral area, the thickness of the spatula tip that contacts the side surface of the lens substrate is preferably within the following range. That is, the thickness of the spatula tip that contacts the side surface of the lens substrate is preferably 0.05 to 2 mm, and more preferably 0.1 to 1 mm.

[0110] In addition, the tip of the spatula is preferably linear, but the shape of the tip of the spatula is preferably acute. That is, when the spatula is viewed on a surface perpendicular to the side surface of the lens substrate, the angle between the tip of the spatula and both side surfaces of the spatula (vertex angle; hereinafter, sometimes referred to as "tip angle") is preferably 5° or more and less than 90°. When the thickness of the spatula tip is within the above range and the tip angle satisfies this range, particularly excellent effects are exhibited. In order to form a coating layer of higher quality, the tip angle is preferably 10° or more and 45° or less, more preferably 10° or more and 30° or less, and even more preferably 10° or more and 25° or less.

[0111] The spatula used in the present invention preferably has a tip thickness and a cutting edge angle that fall within the above ranges, but preferably has a portion where the spatula side faces face each other (parallel) in a portion that does not form an acute angle (a portion that is not the tip). The thickness of this portion where the spatula side faces are parallel is not particularly limited, but is preferably about 2 mm to 5 mm in consideration of the workability of the spatula tip and the strength of the spatula.

[0112] It is preferable to use a spatula having the above-mentioned shape, particularly a tip, and to position the spatula so that the tip comes into contact with the entire surface of the side surface of the lens substrate.

[0113] When the spatula is applied, it is preferable to apply the spatula to the side surface of the lens substrate in a rotated state. In particular, when forming a functional layer, particularly when a photochromic curable composition is used, it is preferable to apply the tip of the spatula to the side surface under the following conditions. Specifically, in order to stably remove the liquid pool, the pressing load (contact force) is preferably 5 to 200 g, and more preferably 30 to 150 g. By applying a contact force in this range, the liquid pool can be efficiently removed by the spatula. When the spatula is applied, the force of the spring may be used as described in (Preferable contact conditions of the adsorption member; when a primer composition is used).

[0114] The rotation speed of the lens substrate when the spatula is brought into contact is preferably 5 rpm to 500 rpm. By making it 5 rpm or more, the manufacturing efficiency is not reduced. By making it 500 rpm or less, the efficiency of removing the coating agent from the peripheral portion of the lens substrate is stabilized, and a uniform coating film is obtained. In order to further enhance such effects, the rotation speed is preferably 10 to 100 rpm, and in order to more stably remove the liquid pool, it is preferably 20 to 70 rpm. The time for which the spatula is brought into contact is preferably 0.5 to 30 sec, and more preferably 1 to 10 sec. If the time for which the spatula is brought into contact is too short, the liquid pool may not be sufficiently removed, and if the time for which the spatula is brought into contact is too long, a new liquid pool may be formed during adsorption, and the manufacturing efficiency is also reduced. Then, a second removal step is carried out.

[0115] (Second Removal Step; When a Coating Agent is Used to Form a Functional Layer) In the present invention, even when forming a functional layer, the second removal step is carried out following the first removal step. Basically, the same operation as that described above (second removal step; when a primer composition is used) may be carried out. However, there are cases where the preferred conditions are different, and the following description will focus on this.

[0116] (Second Removal Step: When a Coating Agent for Forming Adsorption Member / Functional Layer is Used) In the present invention, even when a functional layer is formed, the adsorption member described above (Second Removal Step: When an Adsorption Member / Primer Composition is Used) can be used without any restrictions. That is, one having the same material and characteristics (hardness) as those described above can be used. Among them, it is preferable to use a sponge, as in the case of forming a primer coat layer. It is also preferable to use a sponge with the same density and pore size characteristics as those described above. Therefore, an example of such a sponge is the "Basotect" (registered trademark) series sold by Inoac Corporation.

[0117] When forming a functional layer, particularly when using a coating agent made of a photochromic curable composition, it is preferable to use a sponge containing an organic solvent. Next, the adsorption member (sponge) that absorbs the organic solvent will be described.

[0118] (Second Removal Step: When a Coating Agent for Forming an Adsorption Member / Functional Layer Containing an Organic Solvent is Used) In the present invention, when forming a functional layer, particularly when using a coating agent made of a photochromic curable composition, it is preferable to use the adsorption member, particularly a sponge containing an organic solvent.

[0119] The type of organic solvent used is preferably one that can be mixed with the coating agent. Specifically, it is preferable to use the same ones as above, and examples thereof include alcohol solvents, ketone solvents, aromatic solvents, halogen solvents, and ester solvents. Among them, in consideration of ease of handling, effects on the human body, and removal effect of liquid pools, it is preferable to use ketone solvents, and it is most preferable to use acetone, methyl ethyl ketone, and methyl isobutyl ketone.

[0120] When forming a functional layer, the curing method is often different from that of the primer composition, and the viscosity is also different, so when an organic solvent is used, it is preferable to set the amount of the organic solvent in the following range. Specifically, the amount of the organic solvent to be contained in the sponge is set to 1 cm 3 It is preferable to adjust the amount of organic solvent to 0.1 to 2 g per volume. By containing an organic solvent in this range, liquid pools can be removed efficiently and stably.

[0121] Even when a functional layer is formed, the shape of the adsorption member is not particularly limited, and the removal of the liquid pool with the adsorption member is preferably performed by bringing the adsorption member into contact with at least the side surface (edge ​​surface) of the lens substrate while rotating the lens substrate. By bringing the adsorption member into contact with the side surface, the liquid pool on the peripheral edge of the lens substrate can be easily removed.

[0122] (Optimal arrangement of the adsorption member; when a coating agent is used to form a functional layer) When forming a functional layer, the thickness is often thicker than the primer coat layer. Therefore, it is preferable to place an adsorption member at the following position to remove liquid pools. In particular, when a photochromic curable composition is used as the coating agent, it is preferable to place an adsorption member at the following position.

[0123] Specifically, it is preferable to arrange the adsorption member (sponge) so that it contacts the entire surface of the side surface of the lens substrate. It is also preferable that the length of the surface that the adsorption member (sponge) contacts is longer in the vertical direction than the length of the side surface of the lens substrate. When forming a functional layer, particularly a photochromic coating layer, in order to efficiently remove liquid pools, a sponge that is larger in the vertical direction than the side surface of the lens substrate is brought into contact with the lens substrate to efficiently remove liquid pools.

[0124] (Suitable shape and contact conditions of the adsorption member; when a coating agent is used to form a functional layer) Even when forming a functional layer, it is preferable that the suction member is brought into contact with the side surface of the lens substrate while rotating, that is, it is preferable that the suction member is cylindrical, and it is preferable that the cylindrical side wall surface is the abutting portion. Since the size of the lens substrate is the same as that when a primer coat layer is formed, it is preferable that the shape of this suitable suction member is the same as that of the lens substrate. Specifically, it is preferable that the suction member is structured to be rotatable around a cylindrical core axis (the central axis of the cylinder), and that the roller is a roller in which the suction member is covered around the rotating shaft (a roller in which a rotating shaft is installed in the hollow part of the suction member that has become hollow). Furthermore, in this case, it is preferable that the diameter of the rotating shaft is 10 to 50 mm, and the thickness of the suction member is preferably 2 to 50 mm (the thickness of the suction member covering the rotating shaft), more preferably 2 to 45 mm, and particularly preferably 5 to 30 mm. In addition, in this case, the height of the suction member is specifically preferably 5 to 50 mm, more preferably 10 to 40 mm, and it is preferable that the suction member is present above and below the side surface of the lens substrate.

[0125] In addition, an adsorption member of this shape can be used to remove liquid pools from multiple lens substrates. It can be used repeatedly multiple times as long as the quality of the resulting coated lens can be maintained. However, in order to stably obtain high-quality coated lenses, it is preferable to adjust the adsorption member to be in the same state each time. The same adjustment method as described above in (Preferred embodiment of adsorption member: When a primer composition is used) can be used.

[0126] (Preferable embodiment of the adsorption member: When a coating agent is used to form a functional layer) Even when a functional layer is formed, it is preferable to use the sponge described above, and it is further preferable that the sponge contains an organic solvent. In particular, when a coating agent made of a photochromic curable composition is used, it is preferable to use a sponge containing an organic solvent. In particular, when an organic solvent is used, it is preferable to use a ketone-based solvent, and the amount of the ketone-based solvent is, as described above, about 1 cm 2 of the sponge. 3The amount is preferably 0.1 to 2 g, more preferably 0.1 to 1 g, and even more preferably 0.2 to 0.7 g per unit.

[0127] Incidentally, even when forming a functional layer, multiple lens substrates can be treated so long as the amount of organic solvent is within the above-mentioned range. However, in order to obtain coated lenses of higher quality, it is preferable to adjust the amount of organic solvent each time to be within the above-mentioned range.

[0128] (Optimal contact conditions for the adsorption member; when a coating agent is used to form a functional layer) As described above, it is preferable that the suction member contacts the side surface of the lens substrate in a rotated state. In particular, when forming a functional layer, particularly when a photochromic curable composition is used, it is preferable to contact the suction member to the side surface under the following conditions. Specifically, in order to stably remove liquid pools, the pressing load (contact force) is preferably 5 to 200 g, and more preferably 5 to 100 g. It is presumed that by setting the contact force within this range, the sponge is in close contact with the side surface, and the sponges are present above and below the side surface, and therefore liquid pools on the periphery of the lens substrate can be efficiently removed.

[0129] In addition, the rotation speed of the lens substrate when it is brought into contact is preferably 5 rpm to 500 rpm. By making it 5 rpm or more, it is not necessary to take time for adsorption and removal, and the manufacturing efficiency is not reduced. In addition, by making it 500 rpm or less, the efficiency of removing the coating agent from the peripheral portion of the lens substrate is stabilized, and a uniform coating film is obtained. In order to further enhance such effects, the rotation speed is preferably 10 to 100 rpm, and in order to more stably remove the liquid pool, it is preferably 20 to 70 rpm. The time of contact is preferably 0.5 to 30 sec, and more preferably 1 to 10 sec. If the adsorption time is too short, there is a risk that the liquid pool cannot be sufficiently removed, and if the adsorption time is too long, there is a risk that a new liquid pool will be formed during adsorption, and the manufacturing efficiency will also be reduced.

[0130] When the suction member is brought into contact with the side surface of the lens substrate, the spatula can be brought into contact at the same time. However, in order to form a more stable and high-quality coating layer, it is preferable to bring only the suction member into contact. Therefore, it is preferable to carry out the first removal step and the second removal step without bringing the spatula into contact. Furthermore, when forming a coating layer on a lens substrate having a large base curve on which it is difficult to form a high-quality coating layer, for example, a lens substrate having a base curve of 4 or more, it is preferable to remove the liquid pool in the following order: the first removal step, contact of the spatula under the above conditions, and the second removal step (without contact of the spatula).

[0131] (Coating layer, coating layer formation method: When using a coating agent that forms a functional layer) In the present invention, when a functional layer is formed, particularly when a photochromic curable composition is used, it is preferable to form a photochromic coating layer by the following method: That is, after the above steps, the lens substrate from which pools of liquid have been removed from the periphery of the lens substrate is usually irradiated with light such as ultraviolet light and / or heated for a predetermined period of time in a nitrogen atmosphere to cure the spread coating agent, thereby forming a coating layer.

[0132] When a photopolymerization initiator is blended as a radical polymerization initiator in a coating agent, for example, a photochromic curable composition, curing can be performed by irradiation with ultraviolet rays, α rays, β rays, γ rays, etc., or by a combination of the above irradiation and heating. When curing is performed by irradiation with ultraviolet rays, a super-high pressure mercury lamp, a high pressure mercury lamp, a low pressure mercury lamp, a xenon lamp, a carbon arc, a germicidal lamp, a metal halide lamp, an electrodeless lamp, an LED lamp, etc. can be used as a light source. Among them, when an LED lamp is used, if a polymerizable monomer is included, there is little excess heat generation, so the viscosity during curing does not become too high, and the formation of liquid pools may become more noticeable. The present invention can also be suitably applied when such an LED lamp is used.

[0133] As described above, the coating method of the present invention includes the above-mentioned coating agent supplying step, spreading step, first removal step, and second removal step, and therefore can effectively remove liquid pools that form on the peripheral edge and / or side surface of the lens substrate during spreading. EXAMPLES

[0134] The present invention will be described in more detail below with reference to examples, but the present invention is not limited to these examples. Although Fig. 1, Fig. 2, and Fig. 3 show schematic diagrams of an apparatus that can be used in the method of the present invention, the scales of these diagrams do not necessarily match the actual ones. Fig. 1, Fig. 2, and Fig. 3 are merely schematic diagrams for explaining the present invention, and do not faithfully reproduce the size.

[0135] (Evaluation of puddle width) In both cases where a coating agent made of a primer composition and a photochromic curable composition was used, the following evaluation was performed. The obtained lens was cut using a diamond cutter along a plane that passed through the center of the lens surface and was perpendicular to the lens surface, and the cross section of the primer coat layer or photochromic coat layer was observed with a video microscope. The thickness of the primer coat layer or photochromic coat layer near the center of the lens was measured from the observed image, while the thickness of the primer coat layer or photochromic coat layer at the lens periphery was similarly measured, and the distance from the boundary where the difference in thickness of the lens periphery relative to the thickness of the lens center was 10% or more to the lens end was defined as the width of the liquid pool remaining part with an uneven thickness. If the width of the remaining part was 2 mm or less, it was considered good, and if it was 3 mm or more, it was considered bad.

[0136] (Evaluation of wrinkles caused by liquid pooling) The following evaluations were carried out in both cases where a coating agent made of a primer composition and a photochromic curable composition was used. The obtained lens (lens having a coating layer) was exposed to fluorescent light in a black box, and the occurrence of wrinkles due to uneven shrinkage at the periphery of the lens was visually confirmed. When uneven shrinkage occurred, wrinkle-like defects occurred at the periphery. Those that did not generate wrinkles were rated as good, and those that generated wrinkles were rated as bad.

[0137] (Confirmation of yield) In both cases where a coating agent made of a primer composition and a photochromic curable composition was used, the following evaluations were also performed. 20 lenses were coated. The side surfaces of the obtained lenses were checked to see if a cured product was present near the side surfaces, and the yield of lenses without a cured product was calculated.

[0138] (Ingredients of the coating agent (hereinafter also called photochromic liquid) that forms the functional layer) (a) Photochromic Compound Photochromic compound PC1: 2 parts by weight

[0139] [ka]

[0140] (b) Polymerizable monomer (radical polymerizable monomer) Trimethylolpropane trimethacrylate: 30 parts by weight 2,2-bis[4-(methacryloxy-polyethoxy)phenyl]propane (the average chain length of the ethylene glycol chain is 10 and the average molecular weight is 804): 45 parts by weight Polyethylene glycol diacrylate (average chain length of ethylene glycol chain is 9, average molecular weight is 508, (meth)acrylic equivalent is 254): 18 parts by mass Polyethylene glycol dimethacrylate (average chain length of ethylene glycol chain is 14, average molecular weight is 736): 5 parts by weight Glycidyl methacrylate: 1 part by weight (c) Photopolymerization initiator Phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide (trade name: Irgacure 819, manufactured by BASF): 0.3 parts by mass, (d) Other ingredients Stabilizer Bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate (molecular weight 508): 5 parts by mass Ethylene bis(oxyethylene) bis[3-(5-tert-butyl-4-hydroxy-m-tolyl)propionate] (manufactured by Ciba Specialty Chemicals, Irganox 245): 3 parts by mass Silane Coupling Agent 3-Trimethoxysilylpropyl methacrylate: 6 parts by weight Leveling Agent - Toray Dow Corning L7001: 0.1 parts by weight (Preparation of photochromic liquid) The above components were mixed and stirred at 70°C for 30 minutes to obtain a photochromic liquid. The kinetic viscosity of this photochromic liquid was measured using a Cannon-Fenske viscometer. The kinetic viscosity was measured at 25°C in accordance with JIS K2283. The viscosity of the sample was calculated from the obtained kinetic viscosity and the specific gravity of the sample measured in advance using the formula [viscosity (mPa s) = kinetic viscosity (cSt) x specific gravity (g / cm3)], which was 110 mPa s.

[0141] Coating agent comprising a primer composition · Moisture-curing primer composition 1 (product name: TR-SC-P, manufactured by Tokuyama Corporation); a primer composition containing moisture-curing urethane. Moisture-curing primer composition 2: A primer composition containing 25% by mass (solid content) of moisture-curing urethane and 75% by mass of ethyl acetate.

[0142] Example 1 The moisture-curable primer composition 1 was applied by spin coating to the surface of a thiourethane plastic lens (diameter 70 mm, surface base curve: 5.00) with a refractive index of 1.60 at a rotation speed of 250 rpm for 6 seconds, followed by 1500 rpm for 5 seconds, and then dried at room temperature for 10 minutes to obtain a lens substrate having a primer coating layer. The thickness of the obtained primer coating layer was adjusted to 6.5 to 7.5 μm. The lens substrate used in the next step was selected from those having no cured product attached to the side surface.

[0143] Next, 2 g of the photochromic liquid obtained above was applied onto the lens substrate on which the primer coating layer was formed, and the lens substrate was rotated and held at 100 rpm for 30 seconds to spread the photochromic liquid. The lens substrate was then rotated and held at 900 rpm for 6 seconds, and excess photochromic liquid was shaken off.

[0144] Next, the rotation speed was reduced to 50 rpm, and while maintaining the rotation, a cylindrical adsorption member with a diameter of 3 cm and a length of 7 cm was brought into close contact with the peripheral edge of the lens substrate, and the photochromic liquid was adsorbed and removed for 5 seconds. The material of the adsorption member used here was an open-cell type polyurethane foam with a hardness of 320 N. The atmospheric temperature during spin coating of the photochromic liquid and during adsorption and removal was approximately 22°C.

[0145] The lens substrate with the photochromic liquid spread on its surface was then exposed to a nitrogen atmosphere at an output of 200 mW / cm 2 The lens was irradiated with light for 90 seconds using a metal halide lamp to harden the photochromic liquid. It was then heated at 90°C for an additional hour to obtain a lens with a coating layer. The width of the remaining liquid pool on the obtained lens was 1.5 mm, which was satisfactory, and no wrinkles were generated due to uneven shrinkage caused by hardening.

[0146] Example 2 Light curing light source with output of 400mW / cm 2A lens having a coating layer was produced by carrying out the same process as in Example 1, except that light was irradiated for 40 seconds using an LED lamp (peak wavelength 385 nm, emission peak half width 10 nm). The width of the remaining liquid pool on the obtained lens was 1.5 mm, which was favorable, and no wrinkles were generated due to uneven shrinkage caused by curing.

[0147] Comparative Example 1 A lens having a coating layer was produced in the same manner as in Example 1, except that the photochromic liquid was not removed by adsorption using an adsorption member after spin coating. The width of the remaining liquid pool on the obtained lens was 3.5 mm, which was unsatisfactory, but no wrinkles were generated due to uneven shrinkage caused by curing.

[0148] Comparative Example 2 A lens having a coating layer was produced in the same manner as in Example 2, except that the photochromic liquid was not removed by adsorption using an adsorption member after spin coating. The width of the remaining liquid pool in the obtained lens was 3.5 mm, which was unsatisfactory, and wrinkles were generated on the periphery.

[0149] Thus, in the examples, the area of ​​uneven thickness formed at the peripheral edge of the lens was narrowed, and it was confirmed that a lens having a more uniform coating layer can be formed by a coating method that performs suction and removal using an adsorption member.

[0150] Example 3 Moisture-curable primer composition 2 was applied to the surface of a thiourethane-based plastic lens substrate (finished lens having a diameter of 70 mm, a surface base curve of 1.0, and a side width (side thickness) of 8.9 mm) with a refractive index of 1.60, and then the moisture-curable primer composition 2 was spread by spin coating at a rotation speed of 250 rpm for 6 seconds.

[0151] (First removal process) Subsequently, coating was performed at 1500 rpm for 5 seconds, and at least a part of the liquid pool was removed.

[0152] (Second removal process) Made of melamine resin, density 9.2kg / m 3 A sponge (adsorption member) with a pore size of 50 to 400 μm was prepared. Specifically, a roller with a thickness of 20 mm and a height of 30 mm was prepared around a freely rotatable shaft (a hollow sponge was prepared with the cylindrical center serving as the shaft). The volume of the hollow sponge was 38 cm. 3 The hardness of this sponge was 320N. 3 The sample was impregnated with acetone so that the weight was 0.7 g per sample.

[0153] The sponge was placed so that the top of the sponge was in contact with a position 1.5 mm below the top of the side of the lens substrate obtained through the first removal step (the sponge was in contact with the entire side surface below the position where the top of the sponge was in contact. See Figure 3.) A schematic diagram of the second removal step when forming a primer coat layer is shown in Figure 2.

[0154] While a sponge containing acetone was brought into contact with the side surface in this state with a contact force of 60 g, the lens substrate to which the primer composition had been applied was rotated at 80 rpm for 5 seconds to remove pools of liquid and cured material.

[0155] The spreading of the moisture-curable primer composition 2, the first removal step, and the second removal step were carried out at a humidity of 60% RH and a temperature of 23°C.

[0156] (Formation and hardening of primer coat layer) The lens substrate obtained through the second removal step was dried at room temperature for 10 minutes to obtain a lens substrate having a primer coating layer. The thickness of the obtained primer coating layer was adjusted to be 6.5 to 7.5 μm.

[0157] The above steps were carried out under the same conditions to prepare 20 lens substrates having a primer coating layer, and the yield was confirmed. The condition of the peripheral portion of the lens substrate was also evaluated according to (evaluation of the width of the liquid pool) and (evaluation of the liquid pool wrinkles). The conditions are summarized in Table 1, and the evaluation results are summarized in Table 2.

[0158] Examples 4 to 21 Lens substrates having a primer coating layer were prepared using the same method as in Example 3, except that the types of lens substrates and the conditions for the second removal step shown in Table 1 were used. The conditions are summarized in Table 1, and the evaluation results are summarized in Table 2.

[0159] Comparative Example 3 Except for not carrying out the second removal step, a lens substrate having a primer coating layer was prepared in the same manner as in Example 3. The conditions are summarized in Table 1, and the evaluation results are summarized in Table 2.

[0160] [Table 1]

[0161] [Table 2]

[0162] Example 22 (Formation of photochromic coating layer) The lens substrate having a primer coating layer on its surface, obtained in Example 3, was used. 2 g of the photochromic liquid obtained above was supplied onto the primer coating layer of the lens substrate, and the photochromic liquid was spread by rotating and maintaining the rotation speed of 100 rpm for 30 seconds.

[0163] (First removal process) Subsequently, the lens substrate was rotated and held at 900 rpm for 6 seconds to shake off at least a portion of the excess photochromic liquid.

[0164] (Second removal process) Made of melamine resin, density 9.2kg / m3 A sponge (adsorption member) with a pore size of 50 to 400 μm was prepared. Specifically, a roller with a thickness of 20 mm and a height of 30 mm was prepared around a freely rotatable shaft (a hollow sponge was prepared with the cylindrical center serving as the shaft). The volume of the hollow sponge was 38 cm. 3 The hardness of this sponge was 320N. 3 The material was impregnated with acetone so that the weight was 0.4 g per unit area.

[0165] The sponge was positioned so that it was in contact with the entire surface of the side surface of the lens substrate obtained through the first removal step (the topmost point of the sponge was 0.5 mm above the topmost point of the side surface of the lens substrate, and the bottommost point of the sponge was 1.6 mm below the bottommost point of the side surface).

[0166] While a sponge containing acetone was brought into contact with the side surface in this state with a contact force of 25 g, the lens substrate on which the photochromic liquid had been applied was rotated at 30 rpm for 2 seconds to remove pools of liquid.

[0167] The spreading of the photochromic liquid, the first removal step, and the second removal step were carried out in an atmosphere with a humidity of 60% RH and a temperature of 23°C.

[0168] (Formation and hardening of photochromic coating layer) Light curing light source with output of 400mW / cm 2 A lens having a coating layer was produced by carrying out the same treatment as in Example 1, except that light was irradiated for 40 seconds using an LED lamp (peak wavelength 385 nm, emission peak half width 10 nm). The thickness of the photochromic coating layer was 40 μm.

[0169] The width of the remaining liquid pool in the obtained lens was less than 1 mm, which was satisfactory, and there was no occurrence of wrinkles due to uneven shrinkage caused by curing. In addition, there was no adhesion of the cured material to the side surface.

[0170] The above steps were carried out under the same conditions to produce 20 lenses with a photochromic coating layer. The average width of the residual liquid pool for the 20 lenses is shown in Table 4. The number of lenses with wrinkles is also shown in Table 4. None of the 20 lenses had any hardened material adhering to the side surface.

[0171] The above conditions are summarized in Table 3, and the results are summarized in Table 4.

[0172] Examples 23 to 36 Lens substrates having a photochromic coating layer were prepared in the same manner as in Example 22, except that the types of lens substrates having a primer coating layer on their surfaces and the conditions for the second removal step shown in Table 3 were used. The results are shown in Table 4. In the evaluation of wrinkles (wrinkles) caused by liquid pooling in Example 36, some lenses were found to be defective, but 90% (18 lenses) were found to be good products, and 10% (2 lenses) were found to be slightly defective. The width of the liquid pooling is the average value of the 18 good lenses.

[0173] Comparative Examples 4 and 5 A lens substrate having a primer coating layer on its surface as shown in Table 3 was used (in Comparative Example 5, only a lens substrate having a non-defective side surface was used). A lens substrate having a photochromic coating layer was produced using the same method as in Example 22, except that the second removal step was not carried out in Example 22, and the results are shown in Table 4.

[0174] [Table 3]

[0175] [Table 4]

[0176] Example 37 (Including spatula contact process) The lens substrate having a primer coating layer on its surface, obtained in Example 3, was used. 2 g of the photochromic liquid obtained above was supplied onto the primer coating layer of the lens substrate, and the photochromic liquid was spread by rotating and maintaining the rotation speed of 100 rpm for 30 seconds.

[0177] (First removal process) Subsequently, the lens substrate was rotated and held at 900 rpm for 6 seconds to shake off at least a portion of the excess photochromic liquid.

[0178] <Spatula contact process> Next, a stainless steel metal spatula with a blade angle of 15° and a blade thickness (thickness of the tip of the spatula that contacts the side surface of the lens substrate) of 0.2 mm was prepared, and the metal spatula was positioned so that the tip of the metal spatula was in contact with the entire surface of the side surface of the obtained lens substrate. While the metal spatula was in contact with the side surface with a contact force of 70 g, the lens substrate on which the photochromic liquid had been applied was rotated at 30 rpm for 2 seconds to remove excess photochromic liquid from the lens side surface.

[0179] (Second removal process) Next, a melamine resin with a density of 9.2 kg / m 3 A sponge (adsorption member) with a pore size of 50 to 400 μm was prepared. Specifically, a roller with a thickness of 20 mm and a height of 30 mm was prepared around a freely rotatable shaft (a hollow sponge was prepared with the cylindrical center serving as the shaft). The volume of the hollow sponge was 38 cm. 3 The hardness of this sponge was 320N. 3 The material was impregnated with acetone so that the weight was 0.4 g per unit area.

[0180] The sponge was positioned so that it was in contact with the entire surface of the side surface of the lens substrate obtained through the first removal step (the topmost point of the sponge was 0.5 mm above the topmost point of the side surface, and the bottommost point of the sponge was 1.6 mm below the bottommost point of the side surface).

[0181] While a sponge containing acetone was placed against the side surface with a contact force of 25 g, the lens substrate coated with the photochromic liquid was rotated at 30 rpm for 2 seconds to remove the pool of liquid. The spreading of the photochromic liquid, the first removal step, and the second removal step were performed in an atmosphere with a humidity of 60% RH and a temperature of 23°C.

[0182] (Formation and hardening of photochromic coating layer) Light curing light source with output of 400mW / cm 2 A lens having a coating layer was produced by carrying out the same treatment as in Example 1, except that light was irradiated for 40 seconds using an LED lamp (peak wavelength 385 nm, emission peak half width 10 nm). The thickness of the photochromic coating layer was 40 μm.

[0183] The width of the remaining liquid pool in the obtained lens was less than 1 mm, which was satisfactory, and there was no occurrence of wrinkles due to uneven shrinkage caused by curing. In addition, there was no adhesion of the cured material to the side surface.

[0184] The above steps were carried out under the same conditions to produce 20 lenses with a photochromic coating layer. The average width of the residual liquid pool for the 20 lenses is shown in Table 7. The number of lenses with wrinkles is also shown in Table 7. None of the 20 lenses had any cured material attached to the side.

[0185] The lens substrates used are summarized in Table 5, the above conditions are summarized in Table 6, and the results are summarized in Table 7. Examples 38 to 44 Lens substrates having a photochromic coating layer were produced in the same manner as in Example 37, except that the types of lens substrates having a primer coating layer on their surface shown in Table 5 and the conditions for the spatula contact step and the second removal step shown in Table 6 were used. The results are shown in Table 7.

[0186] [Table 5]

[0187]

Table 6

[0188]

Table 7

Claims

1. A method for manufacturing a coated lens having a lens substrate and a coating layer provided on a surface of the lens substrate, comprising the steps of: applying a coating material to the surface of the lens substrate; spreading the coating agent applied to the surface by rotating the lens substrate; removing at least a portion of a pool of the coating agent that is generated on at least one of the peripheral portion and the side portion of the lens substrate after the coating agent is spread by rotating the lens substrate; and removing the liquid pool remaining on at least one of the peripheral portion and the side portion of the lens substrate by contacting an adsorption member with at least the side surface of the lens substrate rotating at a speed of 30 to 200 rpm; a rotation speed of the lens substrate during spreading of the coating agent by rotation of the lens substrate is 10 to 500 rpm, and a rotation speed of the lens substrate during removal of the puddle by rotation of the lens substrate is more than 500 rpm and not more than 3000 rpm.

2. The method for producing a coated lens according to claim 1 , wherein the adsorption member contains an organic solvent.

3. The adsorption member 1 cm ３ The method for producing a coated lens according to claim 2, wherein the content of the organic solvent is 0.1 to 2 g per unit weight.

4. The method for producing a coated lens according to claim 2 or 3, wherein the organic solvent includes a ketone-based solvent.

5. The density of the adsorption member is 5 to 20 kg / m ３ The method for producing a coated lens according to any one of claims 1 to 4, wherein

6. The method for manufacturing a coated lens according to any one of claims 1 to 5, wherein the suction member has a hardness in accordance with JIS K6400-2 (A method) of 100N to 500N.

7. The method for manufacturing a coated lens according to any one of claims 1 to 6, wherein the adsorption member includes a foamed resin.

8. The method for manufacturing a coated lens according to any one of claims 1 to 7, wherein the adsorption member contains at least one of a melamine resin and a polyurethane.

9. 9. The method for manufacturing a coated lens according to claim 1, wherein the rotation speed of the lens substrate when removing the puddle by rotating the lens substrate is more than 500 rpm and not more than 2000 rpm.

10. 10. The method for manufacturing a coated lens according to claim 1, wherein the pressure load of the suction member against the lens substrate is 5 to 200 g.

11. 11. The method for manufacturing a coated lens according to claim 1, further comprising contacting a spatula with at least a side surface of the lens substrate before removing the puddle of coating agent remaining on at least one of a peripheral portion and a side portion of the lens substrate by contacting the suction member with at least a side surface of the lens substrate rotating at a speed of 30 to 200 rpm after the puddle of coating agent has been removed by rotating the lens substrate.

12. The method for producing a coated lens according to any one of claims 1 to 11, wherein the coating agent is a photochromic curable composition containing a photochromic compound and a polymerizable monomer.

13. The method for producing a coated lens according to any one of claims 1 to 12, wherein the coating agent is a primer composition containing polyurethane and an organic solvent, or a primer composition containing moisture-curing urethane.

14. forming a first coating film from which the liquid pools have been removed by the method according to any one of claims 1 to 13 using a primer composition containing polyurethane and an organic solvent or a primer composition containing moisture-curable urethane as the coating agent; forming a second coating film from which the liquid pool has been removed by the method according to any one of claims 1 to 13 on the first coating film using a photochromic curable composition containing a photochromic compound and a polymerizable monomer as the coating agent; A method for producing the coated lens according to any one of claims 1 to 13, comprising:

15. The method for producing a coated lens according to any one of claims 1 to 14, wherein the coating layer has a thickness of 1 to 100 µm.

16. providing a coating material to a surface of a lens substrate; spreading the coating agent applied to the surface by rotating the lens substrate; removing at least a portion of the puddle of the coating agent generated on at least one of the peripheral portion and the side portion of the lens substrate after the spreading by rotating the lens substrate; removing the liquid pool remaining on at least one of the peripheral portion and the side portion of the lens substrate by contacting an adsorption member with at least the side surface of the lens substrate rotating at a speed of 30 to 200 rpm; Including, a rotation speed of the lens substrate during spreading of the coating agent by rotation of the lens substrate is 10 to 500 rpm, and a rotation speed of the lens substrate during removal of the puddle by rotation of the lens substrate is more than 500 rpm and not more than 3000 rpm.