Lightweight linerboard for corrugated packaging

Abstract

The present invention relates to a method for producing linerboard that exhibits high bending resistance and high compressive strength, which provides high resistance to inter-flute buckling and sagging in the corrugated board so formed. This is achieved by an inventive combination of optimized fiber refining levels of the furnish in each layer of the linerboard, separate formation of the top layer, and formation of two plies through the use of a multi-layer headbox. Furthermore, linerboard produced by the present invention provides good printing properties, particularly in flexographic printing, in the corrugated board so formed, without adversely affecting the fluting structure.

Description

[Technical field]

[0001] The present invention relates to a method for producing a linerboard for corrugated board, to a linerboard, to uses of said linerboard and to a corrugated board comprising said linerboard. [Background technology]

[0002] Corrugated board is a packaging material that can be converted into solutions for different types of packaging. It is a fibrous material that includes a corrugated medium (fluting) and at least one facing or linerboard bonded to the surface of the corrugated medium, thus forming a sandwich structure. The central paper layer, called the corrugation medium, is formed into a corrugated shape using heat, moisture, and pressure using a corrugator. One or two facings, called liners, are glued to the apex of the corrugation medium. The sandwich can be formed in different ways such as double-sided, double-sided, and triple-sided as described in Kirwan M., J., Paper and Paperboard. Packaging Technology, Blackwell Publishing 2005.

[0003] There are different types of corrugated board grades, which may contain different types of liners and corrugations. Examples of different types of liners are kraft liner, white top kraft liner, and test liner. Kraft liners are typically made from kraft pulp, which may be bleached or unbleached, and may contain one or more plies, but often the top layer / ply is optimized to give a good printing surface and good moisture resistance. Test liners are primarily made from salvaged old corrugated board and are mostly two-ply. Kraft liners are often used in corrugated packaging where strength properties are highly desired.

[0004] Environmental concerns have increased the demand for lighter weight and less raw material consuming linerboards. However, the reduction in linerboard basis weight can negatively impact strength properties. It is important that linerboards exhibit high bending resistance as well as high compressive strength to avoid inter-flute buckling and sagging problems. Inter-flute buckling problems occur when the liner plies of the corrugated structure bend under load, thus weakening the structural strength. Sagging is the result of deformation of the bottom of the corrugated package under load. Furthermore, linerboards with lower basis weights can be more prone to washboarding and printability problems. "Washboarding" or the "washboard effect" is an undesirable effect resulting from the corrugated board manufacturing process that can become even more evident after surface printing. The washboard effect is usually associated with the spreading / absorption of glue at the interface and shrinkage of the glue between the liner and the flutes during drying. As the glue dries, the liner can take on the contours of the flutes, causing the washboard appearance.

[0005] Another challenge associated with the use of light-weight linerboard and fluting is maintaining the fluting structure intact while achieving good flexographic printing characteristics on the board so produced. Summary of the Invention

[0006] It is an object of the present invention to provide a lightweight linerboard that exhibits high strength properties and eliminates or mitigates at least some of the disadvantages of the use of prior art lightweight linerboard in corrugated board. More specific objects are to provide a linerboard and corrugated board that has higher resistance to inter-flute buckling and washboarding and also provides good printing properties when printed using flexographic, inkjet and offset printing.

[0007] The invention is defined by the accompanying independent claims. Embodiments are set out in the accompanying dependent claims and in the following description.

[0008] In a first aspect, the present invention provides a method of making linerboard comprising the steps of: - forming a top ply including a first layer by feeding a first furnish onto a first forming fabric of a boardmaking machine, the first furnish being discharged from a first headbox; - forming a bi-ply including a second layer and a third layer by feeding the second and third furnishes onto a second forming fabric, the second and third furnishes being discharged from a multi-layer headbox; - coating said top ply and said second ply together such that said second ply is disposed between said first ply and said third ply to form a multi-ply web; - dewatering and drying said multi-ply web Including, The present invention relates to a method, wherein the first and third furnishes exhibit a first SR value according to ISO 5267-1 of 22 to 80, preferably 24 to 50, and the second furnish exhibits a second SR value according to ISO 5267-1 of less than 30, preferably less than 25, the first SR value being at least 2 units higher than the second SR value.

[0009] The linerboard produced by the method of the present invention exhibits high bending resistance and high compression strength, which gives the so-formed corrugated board a high resistance to inter-flute buckling and sagging. This is achieved by the inventive combination of optimized fiber refining levels of the furnish in each layer of the linerboard, separate formation of the top layer, and formation of a two-ply backply by using a multi-layer headbox. Furthermore, the linerboard produced by the present invention provides good printing properties, especially in flexographic printing, in the so-formed corrugated board without adversely affecting the fluting structure. The bulky middle layer generates high compressibility, whereby the undesirable effects of dot gain and stress on the fluting will be mitigated during the printing process. The structure further reduces the surface roughness, which further increases the printing properties.

[0010] In a second aspect, the present invention provides a linerboard comprising a top ply comprising a first ply and a two-ply ply comprising a second and a third ply, the first and third layers are produced from a furnish exhibiting an SR value according to ISO 5267-1 of 22 to 80, preferably 24 to 50; the second layer is produced from a furnish exhibiting an SR value according to ISO 5267-1 of less than 30, preferably less than 25, the first SR value being at least 2 units higher than the second SR value, - a two-ply ply including a second and a third ply is formed by using a multi-layer headbox; a second layer is located between the first and third layers, wherein: - the linerboard has a SCT index (CD) according to ISO 9895 of at least 20 Nm / g, preferably at least 23 Nm / g and a tensile strength (SCT) index (SCT) according to ISO 9895 of at least 7 Nm 6 / kg 3 The linerboards have a bending resistance index GM according to ISO 2493-1.

[0011] In a third aspect, the present invention relates to a corrugated board comprising fluting and a linerboard according to the linerboard of the second aspect.

[0012] The invention further relates to the use of the linerboard of the second aspect in the manufacture of corrugated board to reduce the tendency for inter-flute buckling.

[0013] Measurement and evaluation methods The following methods and assessment methods are referred to in the specification and claims.

[0014] The Shopper Rigler (°SR) value is measured according to ISO 5267-1. SR is measured on the fiber furnish after refining for never-dried pulp and refined pulp.

[0015] The SCT index (CD) is measured according to ISO 9895.

[0016] The bending resistance index is measured using the Lorentzen & Wettre apparatus according to ISO 2493-1 at an angle of 15°. The bending resistance index is measured in MD and CD. The bending resistance index geometric mean (GM) is calculated as the square root of the product of the bending resistance index in CD and MD.

[0017] Scott Bond is measured according to Tappi T569.

[0018] The burst strength is measured according to ISO 2758.

[0019] Density is measured according to ISO 534:2005.

[0020] Bendtsen roughness is measured according to ISO 8791-2.

[0021] Basis weight or grammage is grams per square meter, gsm or g / m 2 gsm refers to weight expressed as grams per cubic metre and measured according to ISO 536. In this specification, gsm and g / m 2 may be used interchangeably.

[0022] Tensile stiffness index is measured according to ISO 1924-3. The tensile stiffness index geometric mean (GM) is calculated as the square root of the product of the tensile stiffness index in MD and CD.

[0023] All measurements are performed under conditions according to ISO 187 unless otherwise specified. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] As used herein, "multilayer headbox" defines a headbox that contains several (at least two) separate CD distribution channels. The headbox nozzle is equipped with separating flights that prevent the layers from intermixing. The headbox is preferably a hydraulic type headbox.

[0025] "Furnishing" as used herein defines a furnish that includes cellulosic fibers and potentially fillers and additives conventionally used in linerboard manufacture.

[0026] "Fillers" as used herein is intended to define inorganic fillers preferably made from natural minerals, including, but not limited to, ground calcium carbonate (GCC), kaolin, precipitated calcium carbonate (PCC), talc, and titanium dioxide.

[0027] "Microfibrillated cellulose (MFC)" as used herein is meant to define nanoscale cellulose particle fibers or fibrils with at least one dimension less than 1000 nm. MFC comprises partially or wholly fibrillated cellulose or lignocellulosic fibers. The liberated fibrils have a diameter less than 1000 nm, but the actual fibril diameter or particle size distribution and / or aspect ratio (length / width) depends on the source and manufacturing method. There are different acronyms for MFC, such as cellulose microfibril, fibrillated cellulose, nanofibrillated cellulose, fibril aggregate, nanoscale cellulose fibril, cellulose nanofiber, cellulose nanofibril, cellulose microfiber, cellulose fibril, microfibrillar cellulose, microfibril aggregate, and cellulose microfibril aggregate. The present invention discloses a method for manufacturing a linerboard comprising a top ply and a two-ply ply. The linerboard of the present invention is preferably produced on a conventional Fourdrinier machine having two forming units and first and second headboxes, the second headbox being a multi-layer headbox.

[0028] A top ply is formed from the first furnish, according to the present invention, by discharging the first furnish from a first headbox onto a first forming fiber. The consistency of the furnish in the first headbox may be less than 0.35%, preferably approximately 0.1-0.2%.

[0029] In a second step, a two-ply ply including a second and a third ply is formed from the second and third furnishes by discharging the second and third furnishes from a multi-layer headbox onto a second forming wire. The two-ply ply is preferably formed by discharging the furnish from the multi-layer headbox such that the third ply is formed on the second forming wire and the second ply is formed on the third ply. The consistency of the furnish in the multi-layer headbox may be less than 0.45%, preferably between about 0.2 and 0.35%.

[0030] The top ply and the second ply are then coated together to form a multi-ply web such that the second ply is disposed between the first and third plies. The top ply and the second ply may preferably be dewatered to a solids content of greater than 7% by weight, such as 10-15% by weight, prior to coating.

[0031] After coating, the multi-ply web may enter a press section, which removes additional water, typically to a solids content of about 37-42% by weight. The press section may include at least one shoe press unit, preferably two or three shoe press units. The multi-ply web may be further dried by use of conventional drying techniques. The speed of the paperboard making machine used in connection with the present invention may be up to 1300 m / s at the wet end.

[0032] The method of the present invention is further characterized in that the first and third furnishes forming the first and third plies exhibit a first SR value according to ISO 5267-1 of 22 to 80, preferably 24 to 50, most preferably 24 to 30 or 22 to 26 or 24 to 26. The second furnish forming the second ply (middle ply) exhibits a second SR value according to ISO 5267-1 of less than 30, preferably less than 25, or less than 23 or less than 21, such as 15 to 23 or 17 to 22. According to the present invention, the first SR value is at least 2 units higher than the second SR value, preferably at least 5 units higher or at least 7 units higher. The present invention further discloses a linerboard produced according to the method and a corrugated board comprising said linerboard.

[0033] The separate formation of a two-ply comprising a top ply and second and third plies according to the present invention prevents the finer material of the top ply from mixing with the coarser material of the second ply of the two-ply. In this way, the surface roughness of the linerboard is reduced, improving the printability of the board. The inventors of the present invention have further found that in order to reduce the tendency of inter-flute buckling in the corrugated board so formed, the linerboard needs to exhibit both high bending resistance and high SCT index (CD) values. The linerboard of the present invention has a strength of at least 7 Nm 6 / kg 3 , preferably at least 9 Nm 6 / kg 3 , most preferably at least 10 Nm 6 / kg 3 The linerboard may have a bending resistance index (GM) according to ISO 2493-1 of at least 20 Nm / g, preferably at least 23 Nm / g, most preferably at least 24 Nm / g. The SCT index (CD) may be, for example, from 20 to 40 Nm / g or from 24 to 30 Nm / g. The bending resistance index (GM) may be, for example, from 7 to 20 Nm / g. 6 / kg 3 Or 9 to 20 Nm 6 / kg 3 The bending resistance index MD is preferably at least 12 Nm 6 / kg 3 , or at least 13.5 Nm 6 / kg 3 , or at least 15 Nm 6 / kg 3 The bending resistance index CD is preferably at least 5 Nm 6 / kg 3 , or at least 6 Nm 6 / kg 3 , or at least 7 Nm 6 / kg 3 The linerboard may further exhibit a tensile stiffness index GM of at least 5.8 kNm / g, preferably at least 6 kNm / g, most preferably at least 6.1 kNm / g.

[0034] It has further been shown that by use of the present invention it is possible to produce low density linerboard and still achieve high strength properties, in particular high bending resistance and high SCT index (CD) values. The density of the linerboard of the present invention is 900 kg / m 3 Less than 850 kg / m 3 less than 800 kg / m 3 The basis weight of the linerboard of the present invention is preferably in the range of 80 to 225 gsm.

[0035] Linerboard made according to the present invention has a compressive strength of at least 220 J / m 2 , preferably at least 250 J / m 2 , or at least 270 J / m 2 Scott Bond according to TAPPI T569 and / or at least 4.5kPam 2 / g, preferably at least 4.8 kPam 2 / g, most preferably 5kPam 2 It may further exhibit a burst strength according to ISO 2758 of 1 / g.

[0036] According to one embodiment, the linerboard produced by the process of the present invention comprises less than 5% by weight of filler, preferably less than 4% by weight, or less than 3% by weight, calculated on the total weight of said linerboard. In one embodiment, the linerboard does not comprise any filler.

[0037] The method of manufacturing a linerboard may further comprise the step of applying an adhesive to the top ply prior to coating the top ply and the second ply of the two-ply ply such that the adhesive is located between the top ply and the second ply of the two-ply ply. Preferably, the adhesive comprises starch and optionally microfibrillated cellulose (MFC). In this manner, the z-direction tensile strength and the interlaminar peel strength are increased. The adhesive may be applied using a non-impact method such as spraying or curtain coating. The adhesive may comprise starch in an amount of 50-100% by weight, preferably 70-99% by weight, calculated on the total dry weight of the adhesive. In one embodiment, the adhesive also comprises microfibrillated cellulose (MFC) in an amount of 1-100% by weight dry weight, preferably 1-30% by weight. The use of MFC between the plies allows for less interlaminar mixing, which increases stiffness properties. In one embodiment, the adhesive further comprises a pulp fraction comprising cellulose and fine fibers, the pulp fraction exhibiting an SR value of 60-90, preferably 70-90. The adhesive may comprise the pulp fraction in an amount of 1-100% by weight, or in an amount of 1-30% by weight. The use of a pulp fraction with this particular SR value prevents interlayer mixing, yet it does not form a too stiff film that may induce cracks upon drying of the board. The fine fiber fraction may be, for example, a reject fraction received from the fractionation of the pulp. The pulp may be fractionated into a coarser and a finer fraction, the coarser fraction of which may be used for the middle layer in paperboard (such as linerboard) production, and the finer fraction exhibiting an SR value of 60-90 may be used in the adhesive between the paperboard plies.

[0038] In one embodiment, the multi-ply web is calendered in a calender section including at least one nip formed between a heated calender roll and a backing roll or belt, which nip forms the highest line load of the calender section, the highest line load being less than 100 kN / m, preferably less than 50 kN / m. As used in this context, "highest line load" means the highest line load used in any of the nips of the calender section.

[0039] The calender section may include a soft nip calender and / or a wide nip calender, such as a belt calender or an extra soft nip calender. The calender section may include several nips, such as two or three nips, and may be online or offline.

[0040] The linerboard construction of the present invention allows for the use of lower line loads in calendering and still achieves low surface roughness. In this way, bulk and bending resistance are still maintained at a high level even in embodiments where no or only small amounts of CTMP are used in the second layer. To further improve surface roughness, elevated temperatures can be used in calendering. The temperature of the heated calender rolls can be in the range of 80-250°C, preferably in the range of 100-200°C.

[0041] In embodiments where the linerboard has a basis weight of 80 to 135 gsm, the linerboard may have a Bendtsen roughness according to ISO 8791-2 of less than 700 ml / min, preferably less than 650 ml / min.

[0042] In embodiments where the linerboard has a basis weight greater than 135 gsm, such as from 135 to 225 gsm, the linerboard may have a Bendtsen roughness according to ISO 8791-2 of less than 900 ml / min, preferably less than 800 ml / min.

[0043] The linerboard of the present invention may comprise unbleached or bleached chemical pulp, chemi-thermomechanical pulp (CTMP), and / or unbleached or bleached pulp from hardwood or softwood, including reclaimed pulp, for example from OCC. In one embodiment, the first and third furnishes forming the first and third plies of the linerboard comprise unbleached kraft pulp and the second furnish forming the second ply of the linerboard comprises unbleached kraft pulp and / or chemi-thermomechanical pulp (CTMP) and / or reclaimed fibers. The second ply may further comprise broke. In a preferred embodiment, the first and third furnishes forming the first and third plies comprise 100% by weight unbleached kraft pulp. The second ply may preferably comprise unbleached kraft pulp in an amount of 50-100% by weight and CTMP in an amount of 50-0% by weight. Preferably, the pulp used in all plies is made from virgin fibers, most preferably from never-dried pulp.

[0044] In one embodiment, the second furnish forming the second layer of the linerboard comprises less than 40% by weight CTMP or less than 30% by weight CTMP or less than 20% by weight CTMP, preferably less than 10% by weight, or less than 5% by weight, or even less than 1% by weight CTMP. In one embodiment, the linerboard does not comprise any CTMP. As a result of the method of the present invention, a linerboard exhibiting both low surface roughness and good stiffness properties can be achieved even when no or only small amounts of extender fiber (CTMP) are used.

[0045] Preferably, a first ply of linerboard forms the top ply which provides the printing surface, and a third ply forms the back ply adapted to bond to the medium. The second ply preferably forms the middle ply.

[0046] The present invention further discloses a linerboard manufactured according to the method of the first aspect of the invention. The linerboard may be further characterized by the same features as the method.

[0047] The present invention further discloses a corrugated board comprising fluting and the linerboard of the present invention. The corrugated board preferably comprises at least two liners and at least one medium, at least one of the liners being made from the linerboard of the present invention. The corrugated board may also comprise two or more mediums and three or more liners. The liners are adhesively bonded to at least one surface of the medium. The linerboard of the present invention is intended to be used as a lightweight replacement for kraft liners and therefore for use in high quality corrugated board.

[0048] The present invention further discloses the use of linerboard in the manufacture of corrugated cardboard to reduce the tendency for inter-flute buckling.

Claims

1. 1. A method of manufacturing linerboard comprising the steps of: forming a top ply including a first layer by feeding a first furnish onto a first forming fabric of a paperboard making machine, the first furnish being discharged from a first headbox; forming a bi-ply ply including a second layer and a third layer by feeding the second and third furnishes onto a second forming fabric, the second and third furnishes being discharged from a multi-layer headbox; coating said top ply and said second ply together such that said second ply is disposed between said first ply and said third ply, thereby forming a multi-ply web; dewatering and drying the multi-ply web; and calendering the multi-ply web in a calender section including at least one nip formed between a heated calender roll and a backing roll or belt; the nip providing the highest line load in the calender section, said highest line load being less than 100 kN / m; The method of claim 1, wherein the first and third furnishes exhibit a first Shopper Rigler value (SR value) according to ISO 5267-1 of 22 to 80, and the second furnish exhibits a second Shopper Rigler value (SR value) according to ISO 5267-1 of less than 30, the first SR value being at least 2 units higher than the second SR value.

2. The bending resistance index GM of the linerboard according to ISO 2493-1 is at least 7 Nm ６ / kg ３ and / or the linerboard has an SCT index (CD) according to ISO 9895 of at least 20 Nm / g.

3. The linerboard has a strength of at least 220 J / m ２ Scott Bond according to TAPPI T569 and / or at least 4.5 kPam ２ The method according to claim 1 or 2, wherein the composition exhibits a burst strength ratio according to ISO 2758 of 1 / g.

4. 3. The method according to claim 1 or 2, wherein the density of the linerboard is less than 900 kg / m 3 .

5. 3. The method of claim 1 or 2, wherein the linerboard comprises fillers in an amount of less than 5% by weight, calculated on the total weight of the linerboard.

6. 3. The method of claim 1 or 2, further comprising the step of applying an adhesive to the top ply prior to coating the top ply and the two-ply ply such that the adhesive is located between the top ply and the second layer of the two-ply ply, the adhesive comprising starch and optionally microfibrillated cellulose (MFC).

7. The method of claim 6, wherein the adhesive further comprises a pulp fraction comprising cellulose fibers and fines, the pulp fraction exhibiting an SR value of 60-90.

8. 3. The method of claim 1 or 2, wherein the step of dewatering the multi-ply web comprises pressing the web in a press section comprising two shoe presses.

9. The method of claim 8, wherein the temperature of the heated calender rolls ranges from 80 to 250°C.

10. 3. The method according to claim 1 or 2, wherein the linerboard has a basis weight in the range of from 80 to 135 gsm and the linerboard has a Bendtsen roughness according to ISO 8791-2 of less than 700 ml / min.

11. 3. The method according to claim 1 or 2, wherein the linerboard has a basis weight in the range of from above 135 to below 225 gsm and the linerboard has a Bendtsen roughness according to ISO 8791-2 of less than 900 ml / min.

12. 3. The method of claim 1 or 2, wherein the first and third furnishes forming the first and third plies comprise unbleached kraft pulp and the second furnish forming the second ply of the linerboard comprises unbleached kraft pulp and / or chemi-thermomechanical pulp (CTMP) and / or recycled fibers.

13. 11. The method of claim 10, wherein the second furnish forming the second ply of the linerboard comprises less than 20% by weight CTMP.

14. A linerboard comprising a top ply and a two-ply, the top ply comprising a first ply and the two-ply comprising a second ply and a third ply; the first and third layers are made from a furnish exhibiting a first SR value according to ISO 5267-1 of 22 to 80; the second layer is made from a furnish exhibiting a second SR value according to ISO 5267-1 of less than 30; a two-ply ply including a second ply and a third ply is formed by use of a multi-layer headbox, the first SR value being at least 2 units higher than the second SR value; a top ply is formed on a first forming fabric and a second ply is formed on a second forming fabric, the top ply and the second ply being coated together such that the second ply is positioned between the first and third plies; and the linerboard is subjected to calendering in a calender section including at least one nip formed between a heated calender roll and a backing roll or belt, the nip providing the highest line load in the calender section, the highest nip load being less than 100 kN / m; The linerboard has an SCT index (CD) according to ISO 9895 of at least 20 Nm / g and a ６ / kg ３ A linerboard exhibiting a bending resistance index GM according to ISO 2493-1.

15. The linerboard has a strength of at least 220 J / m ２ 15. The linerboard of claim 14, which exhibits a Scott Bond according to TAPPI T569 of at least 4.5 kPam2 / g and / or a burst index according to ISO 2758 of at least 4.5 kPam2 / g.

16. A linerboard according to claim 14 or 15, wherein the density of the linerboard is less than 900 kg / m3.

17. 16. The linerboard of claim 14 or 15, wherein the linerboard comprises an adhesive comprising starch and optionally an MFC applied between the first layer of top ply and the second layer of two-ply ply.

18. The linerboard of claim 17, wherein the adhesive further comprises a pulp fraction comprising cellulose fibers and fines, the fines fraction exhibiting an SR value of 60-90.

19. A linerboard as claimed in claim 14 or 15, wherein the temperature of the heated calender rolls is in the range of 80 to 250°C.

20. A linerboard as claimed in claim 14 or 15, wherein the grammage of the linerboard is in the range of ≥ 80 to ≤ 135 gsm and wherein the linerboard has a Bendtsen roughness according to ISO 8791-2 of less than 700 ml / min.

21. A linerboard according to claim 14 or 15, wherein the grammage of the linerboard is in the range from >135 to <225 gsm and wherein the linerboard has a Bendtsen roughness according to ISO 8791-2 of less than 900 ml / min.

22. 16. A corrugated board comprising fluting and the linerboard of claim 14 or 15.

23. 16. Use of a linerboard according to claim 14 or 15 in the manufacture of corrugated board to reduce the tendency for inter-flute buckling.