Electrode assembly and manufacturing method thereof

Abstract

An electrode assembly according to an embodiment of the present invention includes a negative electrode; a positive electrode; and a separator located between the negative electrode and the positive electrode, and the negative electrode, the positive electrode, and the separator are wound together to form a jelly roll structure. The negative electrode includes a negative electrode current collector and a negative electrode active material part formed by coating a negative electrode active material on the negative electrode current collector. The positive electrode includes a positive electrode current collector and a positive electrode active material part formed by coating a positive electrode active material on the positive electrode current collector. A negative electrode uncoated part in the negative electrode current collector where the negative electrode active material is not coated extends in a first direction, and a positive electrode uncoated part in the positive electrode current collector where the positive electrode active material is not coated extends in a second direction opposite to the first direction. The positive electrode active material part includes a loading reduction part having a smaller loading amount of the positive electrode active material than an adjacent area, and the loading reduction part is located at one end of the positive electrode in the first direction.

Description

[Technical field]

[0001] Cross-reference to related applications This application claims the benefit of priority based on Korean Patent Application No. 10-2021-0012400 filed on January 28, 2021, and Korean Patent Application No. 10-2022-0012250 filed on January 27, 2022, and all contents disclosed in the documents of said Korean patent applications are incorporated herein by reference.

[0002] The present invention relates to an electrode assembly and a manufacturing method thereof, and more particularly, to an electrode assembly having improved energy density and a manufacturing method thereof. [Background technology]

[0003] In recent years, the demand for portable electronic products such as notebook computers, video cameras, mobile phones, etc. has increased dramatically, and the development of electric vehicles, energy storage batteries, robots, satellites, etc. has progressed in earnest. As a result, much research has been conducted on secondary batteries to be used as the driving power source for these products.

[0004] Secondary batteries include, for example, nickel-cadmium batteries, nickel-metal hydride batteries, nickel-zinc batteries, lithium secondary batteries, etc. Among these, lithium secondary batteries have almost no memory effect compared to nickel-based secondary batteries, allowing them to be freely charged and discharged, and they are widely used in the field of cutting-edge electronic devices due to their advantages of having a very low self-discharge rate, high operating voltage, and high energy density per unit weight.

[0005] Secondary batteries are classified according to the shape of the battery case into cylindrical batteries in which the electrode assembly is housed in a cylindrical metal case, prismatic batteries in which the electrode assembly is housed in a prismatic metal case, and pouch batteries in which the electrode assembly is housed in a pouch case made of an aluminum laminate sheet. Among these, cylindrical batteries have the advantages of being relatively large in capacity and structurally stable.

[0006] The electrode assembly built into the battery case is a chargeable and dischargeable power generating element having a laminated structure of a positive electrode, a separator, and a negative electrode, and is classified into a jelly roll type, a stack type, and a stack / folding type. The jelly roll type is a long sheet type positive electrode and a negative electrode coated with an active material, which are wound with a separator interposed between them, the stack type is a type in which a plurality of positive electrodes and a negative electrodes of a predetermined size are stacked in sequence with a separator interposed therebetween, and the stack / folding type is a composite structure of the jelly roll type and the stack type. Among them, the jelly roll type electrode assembly has the advantages of being easy to manufacture and having a high energy density per weight.

[0007] Recently, developments are being made to increase the size of battery cells to achieve high energy density and reduce costs. As energy increases according to the size of the battery cell, the resistance per battery cell must decrease. To decrease resistance, a method of using the electrode collector as an electrode tab, rather than attaching an electrode tab to the electrode, can be used. At this time, due to the characteristics of the electrode manufacturing process in which electrode slurry is applied to the electrode collector, a portion where the loading amount decreases occurs at the boundary between the negative electrode active material portion where the negative electrode slurry is applied and the negative electrode current collector. When considering the N / P ratio, there is a risk that metallic lithium will be deposited on the positive electrode active material portion facing the portion where the loading amount decreases. Here, the N / P ratio is the value obtained by dividing the negative electrode capacity calculated considering the negative electrode capacity per area and mass by the positive electrode capacity calculated considering the positive electrode capacity per area and mass, and is generally 1 or more. In other words, the negative electrode capacity is increased. For reference, if the N / P ratio is not 1, metallic lithium is likely to precipitate during charging and discharging, which will cause a rapid deterioration in battery safety during high-rate charging and discharging. In other words, the N / P ratio has a significant impact on the safety and capacity of the battery.

[0008] As described above, the positive electrode active material part cannot be located in the positive electrode part facing the negative electrode part where the loading amount is reduced due to the risk of precipitation of metallic lithium, which makes it difficult to increase the energy density of the battery cell. Summary of the Invention [Problem to be solved by the invention]

[0009] An object of the present invention is to provide an electrode assembly having improved energy density by increasing the number of sections of a positive electrode active material portion, and a manufacturing method thereof.

[0010] However, the problems to be solved by the embodiments of the present invention are not limited to the above problems, and can be variously expanded within the scope of the technical ideas included in the present invention. [Means for solving the problem]

[0011] An electrode assembly according to an embodiment of the present invention includes a negative electrode; a positive electrode; and a separator located between the negative electrode and the positive electrode, and the negative electrode, the positive electrode, and the separator are wound together to form a jelly roll structure. The negative electrode includes a negative electrode current collector and a negative electrode active material part formed by coating a negative electrode active material on the negative electrode current collector. The positive electrode includes a positive electrode current collector and a positive electrode active material part formed by coating a positive electrode active material on the positive electrode current collector. A negative electrode uncoated part in the negative electrode current collector where the negative electrode active material is not coated extends in a first direction, and a positive electrode uncoated part in the positive electrode current collector where the positive electrode active material is not coated extends in a second direction opposite to the first direction. The positive electrode active material part includes a loading reduction part having a smaller loading amount of the positive electrode active material than an adjacent area, and the loading reduction part is located at one end of the positive electrode in the first direction.

[0012] The negative electrode active material portion may be disposed in a portion corresponding to the loading reduction portion in a direction perpendicular to the first direction.

[0013] The negative electrode active material part may include a negative electrode boundary part forming a boundary between the negative electrode active material part and the negative electrode uncoated part, and the negative electrode boundary part may be disposed in a portion corresponding to the loading reduction part in a direction perpendicular to the first direction.

[0014] The loading amount of the positive active material gradually decreases in the loading decreasing portion in the first direction.

[0015] The first direction and the second direction may be parallel to a height direction of the jelly roll structure.

[0016] The negative electrode uncoated portion may extend beyond the separator in the first direction, and the positive electrode uncoated portion may extend beyond the separator in the second direction.

[0017] The electrode assembly may further include an insulating layer formed on at least one of the negative electrode or the positive electrode, The insulating layer formed on the negative electrode may cover the negative electrode uncoated portion and at least a portion of the negative electrode active material portion, and the insulating layer formed on the positive electrode may cover the positive electrode uncoated portion and at least a portion of the positive electrode active material portion.

[0018] The insulating layer formed on the negative electrode may be formed to cover an end of the negative electrode active material part in the first direction and a portion of the negative electrode uncoated part adjacent thereto, and the insulating layer formed on the positive electrode may be formed to cover an end of the positive electrode active material part in the second direction and a portion of the positive electrode uncoated part adjacent thereto.

[0019] The insulating layer formed on the negative electrode may be disposed at a location not overlapping with a loading reduction portion in a direction perpendicular to the first direction.

[0020] At least a portion of the negative electrode uncoated portion and the positive electrode uncoated portion may be processed into a plurality of segmented pieces that can be bent independently of each other.

[0021] A method for manufacturing an electrode assembly according to an embodiment of the present invention includes the steps of: manufacturing a negative electrode sheet such that a negative electrode active material portion coated with a negative electrode active material and a negative electrode uncoated portion not coated with the negative electrode active material are alternately arranged on a negative electrode current collector; manufacturing a positive electrode sheet such that a positive electrode active material portion coated with a positive electrode active material and a positive electrode uncoated portion not coated with the positive electrode active material are alternately arranged on a positive electrode current collector; manufacturing a negative electrode by slitting the negative electrode uncoated portion and the negative electrode active material portion; manufacturing a positive electrode by slitting the positive electrode uncoated portion and the positive electrode active material portion; and winding the negative electrode and the positive electrode together with a separator to form a jelly roll structure. The positive electrode sheet includes a loading reduction region in which the loading amount of the positive electrode active material is less than that of an adjacent region, and the loading reduction region is slit in the step of manufacturing the positive electrode. The slit loading reduction region forms a loading reduction portion in the jelly roll structure in which the loading amount of the positive electrode active material is less than that of an adjacent region.

[0022] In the jelly roll structure, the negative electrode uncoated portion may extend in a first direction, and the positive electrode uncoated portion may extend in a second direction opposite to the first direction.

[0023] The loading reducer may be disposed at one end of the positive electrode in the first direction.

[0024] The loading amount of the positive active material gradually decreases in the loading decreasing portion in the first direction.

[0025] In the jelly roll structure, the negative active material portion may be disposed in a portion corresponding to the loading reduction portion in a direction perpendicular to the first direction.

[0026] The negative electrode active material part may include a negative electrode boundary part forming a boundary between the negative electrode active material part and the negative electrode uncoated part, and the negative electrode boundary part may be disposed in a portion of the jelly roll structure corresponding to the loading reduction part in a direction perpendicular to the first direction.

[0027] The loading amount of the positive electrode active material gradually decreases toward the center of the loading reduction region, and the loading reduction region may be provided by slitting the center of the loading reduction region during the manufacturing of the positive electrode. Effect of the Invention

[0028] According to an embodiment of the present invention, a loading reduction portion having a smaller loading amount of a positive electrode active material than an adjacent region is provided in a positive electrode, so that the section of the positive electrode active material portion can be increased without the risk of lithium precipitation, thereby improving the energy density of the electrode assembly.

[0029] The effects of the present invention are not limited to those mentioned above, and other effects not mentioned will be clearly understood by those skilled in the art from the description of the claims. [Brief description of the drawings]

[0030] [Figure 1] 1 illustrates an electrode assembly according to an embodiment of the present invention. [Diagram 2] 2 is a cross-sectional view showing a cross section taken along the line AA' in FIG. 1. [Diagram 3] 1A to 1C are diagrams illustrating a process for manufacturing a negative electrode according to an embodiment of the present invention. [Figure 4] 1A to 1C are diagrams illustrating a process for manufacturing a negative electrode according to an embodiment of the present invention. [Diagram 5] FIG. 2 is a perspective view showing a negative electrode according to one embodiment of the present invention. [Figure 6] 1A to 1C are diagrams illustrating a process for producing a positive electrode according to an embodiment of the present invention. [Figure 7]1A to 1C are diagrams illustrating a process for producing a positive electrode according to an embodiment of the present invention. [Figure 8] FIG. 2 is a perspective view showing a positive electrode according to one embodiment of the present invention. [Figure 9] FIG. 13 is a diagram illustrating an electrode assembly according to a comparative example of the present invention. [Figure 10] 10 is a cross-sectional view showing a cross section taken along the line BB' in FIG. 9. [Figure 11] FIG. 4 is a diagram showing a process for producing a negative electrode according to a comparative example of the present invention. [Figure 12] FIG. 2 is a diagram showing a process for producing a positive electrode according to a comparative example of the present invention. [Figure 13] 4 is a cross-sectional view showing an anode, a cathode and a separator according to another embodiment of the present invention. [Figure 14] 4 is a cross-sectional view showing an anode, a cathode and a separator according to another embodiment of the present invention. [Figure 15] 11 is a perspective view showing an electrode assembly according to another embodiment of the present invention; FIG. [Figure 16] 4 is a cross-sectional view showing an anode, a cathode and a separator according to another embodiment of the present invention. [Figure 17] 4 is a cross-sectional view showing an anode, a cathode and a separator according to another embodiment of the present invention. [Figure 18] 4 is a cross-sectional view showing an anode, a cathode and a separator according to another embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0031] DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention may, however, be embodied in various different forms and should not be construed as limited to the embodiments set forth herein.

[0032] In order to clearly explain the present invention, parts that are not necessary for the explanation will be omitted, and the same reference numerals will be used throughout the specification to refer to the same or similar components.

[0033] In addition, the size and thickness of each component shown in the drawings are arbitrarily shown for convenience of explanation, and the present invention is not necessarily limited to those shown in the drawings. In the drawings, the thicknesses of various layers and regions are exaggerated to clearly express the layers and regions. In the drawings, the thicknesses of some layers and regions are exaggerated to facilitate explanation.

[0034] Furthermore, when a part such as a layer, film, region, or plate is said to be "on" or "above" another part, this includes not only the case where it is "directly on" another part, but also the case where there is another part in between. Conversely, when a part is said to be "directly on" another part, it means that there is no other part in between. Furthermore, being "on" or "above" a reference part means being located above or below the reference part, and does not necessarily mean being located "on" or "above" the direction against gravity.

[0035] Additionally, throughout the specification, when a part is said to "comprise" a certain element, this means that it may further include other elements, but not excluding other elements, unless specifically stated to the contrary.

[0036] Also, throughout the specification, the term "in a plane" means when the subject part is viewed from above, and the term "in cross section" means when the subject part is cut vertically and viewed from the side.

[0037] FIG. 1 is a view showing an electrode assembly according to an embodiment of the present invention, and FIG. 2 is a cross-sectional view showing a cross section taken along line AA' of FIG.

[0038] 1 and 2, an electrode assembly 100 according to an embodiment of the present invention includes an anode 200, a cathode 300, and a separator 400. The separator 400 is located between the anode 200 and the cathode 300. The anode 200, the cathode 300, and the separator 400 are wound together to form a jelly roll structure 100S. Here, the jelly roll structure 100S refers to a structure formed by winding the anode 200, the cathode 300, and the separator 400. In addition, when the jelly roll structure 100S is formed, it is preferable that a separator 400 is additionally disposed on the outside to prevent the anode 200 and the cathode 300 from contacting each other.

[0039] The negative electrode 200 includes a negative electrode current collector 210 and a negative electrode active material part 220 formed by applying a negative electrode active material on the negative electrode current collector 210. In particular, as shown in the figure, the negative electrode active material is applied to both sides of the negative electrode current collector 210 to form the negative electrode active material part 220. In addition, a negative electrode uncoated part 230, where the negative electrode active material is not applied, in the negative electrode current collector 210 extends in a first direction d1. The negative electrode uncoated part 230 continues along one end of the negative electrode 200 to be wound. In addition, the negative electrode uncoated part 230 extends from the separator 400 in the first direction d1. As a result, the negative electrode uncoated part 230 is exposed at one end of the jelly roll structure 100S in the first direction.

[0040] The positive electrode 300 includes a positive electrode current collector 310 and a positive electrode active material part 320 formed by applying a positive electrode active material on the positive electrode current collector 310. In particular, as shown in the figure, the positive electrode active material may be applied to both sides of the positive electrode current collector 310 to form the positive electrode active material part 320. In addition, a positive electrode uncoated part 330 in the positive electrode current collector 310, where the positive electrode active material is not applied, extends in the second direction d2. The positive electrode uncoated part 330 continues along one end of the positive electrode 300 to be wound. In addition, the positive electrode uncoated part 330 extends from the separator 400 in the second direction d2. As a result, the positive electrode uncoated part 330 is exposed at one end of the jelly roll structure 100S in the second direction.

[0041] Here, the first direction d1 and the second direction d2 are opposite to each other, and may be parallel to the height direction of the jelly roll structure 100S.

[0042] The electrode assembly 100 according to the present embodiment does not have a separate electrode tab attached, but rather uses the negative electrode uncoated portion 230 of the negative electrode collector 210 and the positive electrode uncoated portion 330 of the positive electrode collector 310 as electrode tabs in order to reduce resistance. That is, the electrode assembly 100 according to the present embodiment has a tab-less structure, and the negative electrode uncoated portion 230 and the positive electrode uncoated portion 330 can be defined as electrode tabs in themselves.

[0043] In this case, the positive electrode active material part 320 according to the present embodiment includes a loading reducing part 300D having a smaller loading amount of the positive electrode active material than an adjacent area, and the loading reducing part 300D is located at one end of the positive electrode 300 in the first direction d1. More specifically, the loading amount of the positive electrode active material in the loading reducing part 300D gradually decreases in the first direction d1.

[0044] Here, the loading amount means the amount of active material applied per unit area. In a portion with a large loading amount, a large amount of anode active material or cathode active material may be applied per unit area, resulting in a relatively thick anode active material portion or cathode active material portion. In a portion with a small loading amount, a small amount of anode active material or cathode active material may be applied per unit area, resulting in a relatively thin anode active material portion or cathode active material portion.

[0045] The active material portion can be formed by applying a slurry containing an active material, and in this process, a boundary portion where the loading amount gradually decreases can be formed between the uncoated portion and the active material portion.

[0046] Specifically, the negative electrode active material part 220 may include a negative electrode boundary part 220B that forms a boundary between the negative electrode active material part 220 and the negative electrode uncoated part 230. The negative electrode boundary part 220B has a reduced loading amount in a direction toward which the negative electrode uncoated part 230 is located.

[0047] Similarly, the positive electrode active material part 320 may include a positive electrode boundary part 320B that forms a boundary between the positive electrode active material part 320 and the positive electrode uncoated part 330. The positive electrode boundary part 320B has a reduced loading amount in the direction toward which the positive electrode uncoated part 330 is located.

[0048] The negative electrode boundary portion 220B and the positive electrode boundary portion 320B, in which the loading amount is gradually reduced as described above, are naturally generated during the process of applying the slurry containing the active material to the negative electrode current collector 210 and the positive electrode current collector 310.

[0049] Specifically, the negative electrode boundary portion 220B and the positive electrode boundary portion 320B may be regions where a sliding phenomenon occurs. The sliding phenomenon refers to a phenomenon in which less electrode active material is applied at the boundary region of the slurry application due to the spread of the slurry containing the active material, and the slurry at the application boundary region has a generally inclined shape. Here, if the electrode is entirely dried, the solvent contained in the slurry evaporates and the slurry volume decreases, and the sliding phenomenon may become more severe near the boundary between the region where the active material is applied and the region where it is not applied.

[0050] In this case, the amount of the positive active material may be less than the amount of the negative active material in the region corresponding to the positive boundary portion 320B in the direction perpendicular to the second direction d2. Even if this is the case, the N / P ratio is greater than 1, so that no problem such as the precipitation of metallic lithium occurs.

[0051] The problem is the region corresponding to the negative electrode boundary 220B. In the region corresponding to the negative electrode boundary 220B, the amount of the negative electrode active material may be less than the amount of the positive electrode active material in the direction perpendicular to the first direction d1. In this case, the N / P ratio is less than 1, which may cause a problem of metallic lithium precipitation.

[0052] Therefore, in this embodiment, a loading reduction portion 300D is provided in the positive electrode 300, and the negative electrode active material portion 220 may be disposed at a portion corresponding to the loading reduction portion 300D in a direction perpendicular to the first direction d1. More specifically, the negative electrode boundary portion 220B may be disposed at a portion corresponding to the loading reduction portion 300D in a direction perpendicular to the first direction d1.

[0053] By providing a loading reduction portion 300D in which the loading amount of the positive active material is less than that of the adjacent area at a position corresponding to the negative electrode boundary portion 220B in which the loading amount is gradually reduced, the area in which the positive active material is applied can be increased without the risk of lithium precipitation. In particular, the loading reduction portion 300D may have a shape in which the loading amount of the positive active material gradually decreases as it moves in the first direction d1, corresponding to the shape of the negative electrode boundary portion 220B in which the loading amount gradually decreases as it moves toward the direction in which the negative electrode uncoated portion 230 is located. Therefore, the N / P ratio of the negative electrode 200 and the positive electrode 300 in the region in which the negative electrode boundary portion 220B is formed can be maintained high, and lithium precipitation can be prevented. More detailed information will be described later through a comparison with the comparative examples of FIGS. 9 to 12.

[0054] Hereinafter, a method for manufacturing an electrode assembly according to an embodiment of the present invention will be described in detail with reference to FIGS.

[0055] 3 and 4 are diagrams illustrating a process for manufacturing a negative electrode according to an embodiment of the present invention. Specifically, Fig. 3 is a plan view of a negative electrode sheet as viewed from above, and Fig. 4 is a front view of the negative electrode sheet of Fig. 3 as viewed from the front.

[0056] 3 and 4, a method for manufacturing an electrode assembly according to an embodiment of the present invention includes a step of manufacturing a negative electrode sheet 200S such that a negative electrode active material portion 220 coated with a negative electrode active material and a negative electrode uncoated portion 230 not coated with a negative electrode active material are alternately arranged on a negative electrode current collector 210.

[0057] Specifically, the negative electrode active material may be continuously applied along a third direction d3 to form the negative electrode active material part 220, and a plurality of the negative electrode active material parts 220 may be spaced apart from each other along a fourth direction d4 perpendicular to the third direction d3. That is, the negative electrode uncoated part 230 may be positioned between the plurality of negative electrode active material parts 220.

[0058] Here, the third direction d3 and the fourth direction d4 are directions for explanation based on the negative electrode sheet 200S, and are directions unrelated to the first direction d1 and the second direction d2 in the above-mentioned jelly roll structure 100S.

[0059] Then, the negative electrode uncoated portion 230 and the negative electrode active material portion 220 are slit to manufacture the negative electrode 200. Figure 5 is a perspective view showing a negative electrode according to an embodiment of the present invention.

[0060] 3 to 5, as shown by dotted lines in Figs. 3 and 4, the negative electrode uncoated portion 230 and the negative electrode active material portion 220 may each be slit in a direction parallel to the third direction d3. As a result, a plurality of negative electrodes 200 as shown in Fig. 5 may be manufactured from the negative electrode sheet 200S. That is, the negative electrode 200 in Fig. 5 corresponds to one of a plurality of negative electrodes manufactured by slitting the negative electrode sheet 200S in Figs. 3 and 4. By slitting the negative electrode uncoated portion 230 and the negative electrode active material portion 220 in the negative electrode sheet 200S, a negative electrode 200 having the negative electrode uncoated portion 230 extended to one side may be manufactured.

[0061] When forming the negative electrode active material part 220, a slurry including a negative electrode active material may be applied onto the negative electrode current collector 210. During this slurry application process, a negative electrode boundary part 220B may be formed at the boundary between the negative electrode active material part 220 and the negative electrode uncoated part 230, where the loading amount decreases toward the position of the negative electrode uncoated part 230.

[0062] 6 and 7 are diagrams showing a process for producing a positive electrode according to an embodiment of the present invention. Specifically, Fig. 6 is a plan view of a positive electrode sheet seen from above, and Fig. 7 is a front view of the positive electrode sheet of Fig. 6 seen from the front.

[0063] 6 and 7, a method for manufacturing an electrode assembly according to an embodiment of the present invention includes a step of manufacturing a positive electrode sheet 300S such that positive electrode active material parts 320 coated with a positive electrode active material and positive electrode uncoated parts 330 not coated with a positive electrode active material are alternately arranged on a positive electrode current collector 310.

[0064] Specifically, the positive electrode active material may be continuously applied along a third direction d3 to form the positive electrode active material part 320, and a plurality of the positive electrode active material parts 320 may be spaced apart from each other along a fourth direction d4 perpendicular to the third direction d3. That is, the positive electrode uncoated part 330 may be positioned between the plurality of positive electrode active material parts 320.

[0065] Here, the third direction d3 and the fourth direction d4 are directions for explanation based on the positive electrode sheet 300S, and are directions unrelated to the first direction d1 and the second direction d2 in the above-mentioned jelly roll structure 100S.

[0066] Then, the positive electrode uncoated portion 330 and the positive electrode active material portion 320 are slit to manufacture the positive electrode 300. Figure 8 is a perspective view showing a negative electrode according to an embodiment of the present invention.

[0067] 6 to 8, as shown by dotted lines in Figs. 6 and 7, the positive electrode uncoated portion 330 and the positive electrode active material portion 320 can be slit in a direction parallel to the third direction d3. As a result, a plurality of positive electrodes 300 as shown in Fig. 8 can be manufactured from the positive electrode sheet 300S. That is, the positive electrode 300 in Fig. 8 corresponds to one of a plurality of positive electrodes manufactured by slitting the positive electrode sheet 300S in Figs. 6 and 7. By slitting the positive electrode uncoated portion 330 and the positive electrode active material portion 320 in the positive electrode sheet 300S, a positive electrode 300 having the positive electrode uncoated portion 330 extended to one side can be manufactured.

[0068] When forming the positive electrode active material part 320, a slurry containing a positive electrode active material may be applied onto the positive electrode current collector 310. During this slurry application process, a positive electrode boundary part 320B may be formed at the boundary between the positive electrode active material part 320 and the positive electrode uncoated part 330, in which the loading amount decreases toward the positive electrode uncoated part 330.

[0069] 1, 5 and 8, the manufactured anode 200 and cathode 300 are wound together with the separator 400 to form a jelly roll structure 100S. In this case, in the jelly roll structure 100S, the anode uncoated portion 230 extends from the separator 400 in a first direction d1, and the cathode uncoated portion 330 extends from the separator 400 in a second direction d2 opposite to the first direction d1.

[0070] 6 to 8, in a method for manufacturing an electrode assembly according to an embodiment of the present invention, a positive electrode sheet 300S includes a reduced loading region 300DA in which the loading amount of the positive electrode active material is less than that of an adjacent region. There is no particular limitation on the method for forming the reduced loading region 300DA, and for example, the reduced loading region 300DA may be formed by adjusting the degree of application of a slurry.

[0071] In the step of manufacturing the positive electrode 300, the loading reduction region 300DA in the positive electrode active material part 320 is slit. The slit loading reduction region 300DA corresponds to the loading reduction part 300D in which the loading amount of the positive electrode active material is less than that of the adjacent region in the jelly roll structure 100S shown in FIGS. 1 and 2.

[0072] Specifically, a loading reduction region 300DA, in which the loading amount of the positive active material is less than that of adjacent regions, is formed in a positive active material part 320 formed in a positive electrode sheet 300S. As shown in Fig. 7, the loading reduction region 300DA may be formed in the center of the positive active material part 320. Meanwhile, the loading reduction region 300DA may be configured such that the loading amount of the positive active material gradually decreases toward a central portion 300C of the loading reduction region 300DA, and the loading reduction portion 300D according to this embodiment may be provided by slitting the central portion 300C of the loading reduction region 300DA during the manufacturing of the positive electrode 300.

[0073] That is, the loading reduction region 300DA is formed by applying a slurry containing a positive electrode active material, and the central portion 300C of the loading reduction region 300DA is slit, so that a plurality of positive electrodes 300 each having the loading reduction portion 300D formed thereon can be manufactured.

[0074] Referring to FIG. 8, a loading reduction portion 300D may be provided at one end of the manufactured positive electrode 300, and a positive electrode uncoated portion 330 may be provided at the other end of the positive electrode 300 opposite the one end.

[0075] 1 and 2, when such a positive electrode 300 is wound to form a jelly roll structure 100S, the loading reduction portion 300D may be located at one end of the positive electrode 300 in a first direction d1, and the positive electrode uncoated portion 330 may be located at one end of the positive electrode 300 in a second direction d2.

[0076] In addition, by slitting the central portion 300C of the loading reduction region 300DA, the loading amount of the positive active material in the loading reduction portion 300D gradually decreases in the first direction d1.

[0077] In addition, the negative electrode active material part 220 may be disposed in a portion of the jelly roll structure 100S corresponding to the loading reduction part 300D in a direction perpendicular to the first direction d1. More specifically, the negative electrode boundary part 220B may be disposed in a portion of the jelly roll structure 100S corresponding to the loading reduction part 300D in a direction perpendicular to the first direction d1.

[0078] The corresponding positional relationship between the loading reduction portion 300D and the negative electrode boundary portion 220B is omitted since it is the same as that described above.

[0079] Hereinafter, an electrode assembly according to a comparative example of the present invention will be described with reference to FIGS. 9 to 12, and advantages of the electrode assembly according to this embodiment compared to the electrode assembly according to the comparative example will be described.

[0080] 9 is a view showing an electrode assembly according to a comparative example of the present invention, and FIG 10 is a cross-sectional view showing a cross section taken along line BB' in FIG 9.

[0081] 9 and 10, the electrode assembly 10 according to the comparative example of the present invention includes an anode 20, a cathode 30, and a separator 40, and the anode 20, the cathode 30, and the separator 40 are wound to form a jelly roll structure 10S.

[0082] The negative electrode 20 may include a negative electrode current collector 21, a negative electrode active material part 22, and a negative electrode uncoated part 23. In addition, the negative electrode uncoated part 23 may extend in a first direction d1, and the negative electrode active material part 22 may include a negative electrode boundary part 22B that forms a boundary between the negative electrode active material part 22 and the negative electrode uncoated part 23 and in which the loading amount gradually decreases.

[0083] 11 is a diagram illustrating a process for manufacturing a negative electrode according to a comparative example of the present invention, specifically, a diagram for explaining a process for manufacturing the negative electrode 20 included in the electrode assembly 10 of FIGS.

[0084] Referring to FIG. 11, after the negative electrode sheet 20S is manufactured such that the negative electrode active material parts 22 and the negative electrode uncoated parts 23 are alternately positioned along the fourth direction d4, the negative electrode uncoated parts 23 and the negative electrode active material parts 22 are slit to manufacture a plurality of negative electrodes 20.

[0085] 9 and 10, the positive electrode 30 may include a positive electrode current collector 31, a positive electrode active material part 32, and a positive electrode uncoated part 33. In addition, the positive electrode uncoated part 33 may extend in a second direction d2 opposite to the first direction d1, and the positive electrode active material part 32 may include a positive electrode boundary part 32B that forms a boundary between the positive electrode active material part 32 and the positive electrode uncoated part 33 and in which the loading amount gradually decreases.

[0086] 12 is a diagram illustrating a process for manufacturing a positive electrode according to a comparative example of the present invention, specifically, a diagram for explaining a process for manufacturing the positive electrode 30 included in the electrode assembly 10 of FIGS.

[0087] Referring to FIG. 12, a positive electrode sheet 30S is manufactured such that the positive electrode active material parts 32 and the positive electrode uncoated parts 33 are alternately positioned along a fourth direction d4, and then the positive electrode uncoated parts 33 and the positive electrode active material parts 32 are slit to manufacture a plurality of positive electrodes 30.

[0088] Then, the manufactured anode 20 and cathode 30 are wound together with the separator 40 to manufacture the electrode assembly 10 according to the comparative example of the present invention.

[0089] That is, the electrode assembly 10 according to the comparative example of the present invention may have a similar structure to the electrode assembly 100 according to the present embodiment, except that the loading reduction portion 300D (see FIG. 2) is formed.

[0090] 9 and 10, in the case of the electrode assembly 10 according to the comparative example, the positive electrode active material part 32 cannot be disposed in a portion corresponding to the negative electrode boundary part 22B with respect to a direction perpendicular to the first direction d1. If the positive electrode active material part 32 is extended to a portion corresponding to the negative electrode boundary part 22B, the portion has a low N / P ratio value, and is highly likely to deposit metallic lithium. Therefore, in order to prevent lithium deposition, the length of the positive electrode active material part 32 must be limited. That is, the positive electrode active material part 32 can be formed only in the region B1 shown in the drawings, and the positive electrode active material part 32 cannot be formed in the region B2. This results in the length of the positive electrode active material part 32 being reduced by the negative electrode boundary part 22B.

[0091] 1 and 2, in the case of the electrode assembly 100 according to the present embodiment, the positive electrode active material part 320, particularly the loading reduction part 300D, may be disposed in a portion corresponding to the negative electrode boundary part 220B with respect to a direction perpendicular to the first direction d1. Since the loading reduction part 300D, which has a smaller amount of positive electrode active material loaded than the adjacent area, is provided in a position corresponding to the negative electrode boundary part 220B, the N / P ratio in the corresponding portion may be maintained high, and lithium deposition may be prevented. As a result, the positive electrode active material part 320 may be formed only in the region A1, and the region A2 in which the positive electrode active material part 320 cannot be formed may be reduced. For example, the height width of the positive electrode 300 may be increased to 98% or more of the height width of the negative electrode 200.

[0092] Comparing the area A1 in FIGS. 1 and 2 with the area B1 in FIGS. 9 and 10, the electrode assembly 100 according to this embodiment can have a higher energy density in a limited space than the electrode assembly 10 according to the comparative example because the length of the positive electrode active material portion can be increased by the loading reduction portion 300D.

[0093] Hereinafter, an electrode assembly according to another embodiment of the present invention will be described in detail with reference to Figures 13 and 14. Since the embodiment of Figures 13 and 14 is similar to the embodiment of Figure 2 described above, redundant description of configurations that are substantially the same as or similar to the previous embodiment will be omitted, and the description will focus on differences from the previous embodiment.

[0094] 13 and 14 are cross-sectional views showing an anode, a cathode, and a separator according to another embodiment of the present invention, respectively.

[0095] 13 and 14, the electrode assembly according to the present embodiment includes an anode 200, a cathode 300, and a separator 400, which are wound together to form a jelly roll structure.

[0096] The negative electrode 200 includes a negative electrode current collector 210 and a negative electrode active material part 220, and a negative electrode uncoated part 230 extends from a separator 400 in a first direction d1. The positive electrode 300 includes a positive electrode current collector 310 and a positive electrode active material part 320, and a positive electrode uncoated part 330 extends from the separator 400 in a second direction d2.

[0097] Meanwhile, in the height direction of the jelly roll structure, the length Lp of the positive electrode active material part 320 may be shorter than the length Ln of the negative electrode active material part 220. In addition, the positive electrode active material part 320 may be disposed on the inner side in the height direction than the negative electrode active material part 220. For example, the length Ln in the height direction of the negative electrode active material part 220 may be formed to be larger than the length Lp in the height direction of the positive electrode active material part 320.

[0098] Furthermore, the height Lp of the positive electrode active material part 320 may be shorter than the height of a region excluding the negative electrode boundary part 220B in the negative electrode active material part 220. This structure is intended to prevent the N / P ratio from decreasing to 1 or less, causing lithium metal to be precipitated.

[0099] Meanwhile, the anode active material unit 220 and the cathode active material unit 320 may not protrude further in the height direction than the separator 400. If the anode active material unit 220 and the cathode active material unit 320 protrude further in the height direction than the separator 400, the anode 200 and the cathode 300 may be more likely to come into contact with each other. If this happens, an internal short circuit may occur in the contact area, increasing the risk of fire. Therefore, it is important that the anode active material unit 220 and the cathode active material unit 320 do not protrude further in the height direction than the separator 400. That is, the anode active material unit 220 and the cathode active material unit 320 are preferably located inside the separator 400.

[0100] Meanwhile, the electrode assembly according to the present embodiment may further include an insulating layer 500n, 500p formed on at least one of the negative electrode 200 or the positive electrode 300. In order to minimize the possibility of contact between the negative electrode 200 or the positive electrode 300, the electrode assembly according to the present invention may further include an insulating layer 500n, 500p formed on at least one of the negative electrode 200 or the positive electrode 300.

[0101] 13 shows an insulating layer 500p formed on the positive electrode 300. The insulating layer 500p formed on the positive electrode 300 may cover at least a portion of the positive electrode uncoated portion 330 and the positive electrode active material portion 320.

[0102] The insulating layer 500p can effectively prevent electrical contact between the negative electrode 200 and the positive electrode 300. More specifically, the insulating layer 500p can effectively prevent electrical contact between the positive electrode uncoated portion 330 and the negative electrode active material portion 220.

[0103] The insulating layer 500p may be provided on at least one side of the positive electrode 300. For example, the insulating layer 500p may be provided on both sides of the positive electrode 300. Although not shown in FIG 13, another part of the wound negative electrode 200 is located to the left of the separator 400 located on the left side in the jelly roll structure. Therefore, in order to prevent electrical contact with the negative electrodes 200 located on the left and right sides, it is preferable that the insulating layer 500p is provided on both sides of the positive electrode 300.

[0104] The insulating layer 500p may be provided in a region of the positive electrode 300 that may face the negative electrode active material part 220. For example, the second direction d2 end of the insulating layer 500p may be disposed at the same height as the second direction d2 end of the separator 400 or outside the second direction d2 end of the separator 400. More specifically, referring to FIG. 13 as an example, the second direction d2 end of the insulating layer 500p may be disposed at the same height as the second direction d2 end of the separator 400. Since the separator 400 protrudes in the height direction between the positive electrode 300 and the negative electrode 200, electrical contact between the positive electrode 300 and the negative electrode 200 can be prevented to some extent. However, since a flow such as a slanting of the positive electrode 300 or the negative electrode 200 may occur inside a secondary battery including the electrode assembly, the possibility that the negative electrode 200 is located near the end of the separator 400 cannot be excluded. Therefore, if the negative electrode 200 is positioned at the end of the separator 400 or if the negative electrode 200 protrudes outward beyond the end of the separator 400 due to the occurrence of a flow such as oblique movement, electrical contact between the positive electrode 300 and the negative electrode 200 cannot be avoided. Also, if the separator 400 is damaged for any reason, electrical contact between the positive electrode 300 and the negative electrode 200 cannot be avoided.

[0105] Therefore, in order to prevent electrical contact between the positive electrode 300 and the negative electrode 200 even if such a case occurs, it is preferable that the insulating layer 500p provided on the positive electrode 300 extends at least to the same height as the end of the separator 400 in the second direction d2 or to the outside of the end of the separator 400 in the second direction d2.

[0106] However, if the insulating layer 500p covers the entire positive electrode uncoated portion 330, the positive electrode uncoated portion 330 will not be able to function as an electrode tab, so it is preferable that the insulating layer 500p cover a portion of the positive electrode uncoated portion 330. That is, the positive electrode uncoated portion 330 may have a shape that further protrudes outward from the insulating layer 500p.

[0107] The insulating layer 500p may be an insulating coating layer or an insulating tape provided on the boundary region between the positive electrode uncoated portion 330 and the positive electrode active material portion 320. However, the form of the insulating layer 500p is not limited thereto, and any form in which the insulating layer 500p can be attached to the positive electrode 300 while ensuring insulating performance can be adopted in the present invention. Meanwhile, the insulating layer 500p may contain, for example, an oil-based SBR binder and an alumina oxide to ensure insulating performance.

[0108] The insulating layer 500p may simultaneously cover at least a portion of the positive electrode uncoated portion 330 and at least a portion of the positive electrode active material portion 320. For example, the insulating layer 500p may be provided on a boundary region between the positive electrode active material portion 320 and the positive electrode uncoated portion 330. For example, the insulating layer 500p may cover at least a portion of the positive electrode boundary portion 320B. For example, the insulating layer 500p may extend from the boundary between the positive electrode uncoated portion 330 and the positive electrode active material portion 320 to a point approximately 0.3 to 5 mm, more preferably approximately 1.5 to 3 mm, within the entire region of the positive electrode uncoated portion 330.

[0109] If the insulating layer 500p were not present, contact between the positive electrode 300 and the negative electrode 200 could cause an internal short circuit, so it is preferable that the insulating layer 500p extend to a position where electrical contact between the positive electrode 300 and the negative electrode 200 does not occur.

[0110] Meanwhile, the insulating layer 500p may extend from the boundary between the positive electrode uncoated portion 330 and the positive electrode active material portion 320 within the entire area of ​​the positive electrode active material portion 320 to a position about 0.1 to 3 mm, more preferably about 0.2 to 0.5 mm.

[0111] If the insulating layer 500p covers a portion of the positive electrode active material part 320, a capacity loss of the battery occurs, so it is necessary to minimize the length of the insulating layer 500p covering the support part. However, since the positive electrode active material part 320 may come into contact with the negative electrode 200, it is preferable that the insulating layer 500p covers at least a portion of the positive electrode active material part 320 to prevent this.

[0112] Meanwhile, referring to FIG. 13, the separation membrane 400 may protrude outward beyond the end of the positive electrode 300 in the first direction d1 and may protrude outward beyond the end of the negative electrode 200 in the second direction d2.

[0113] Meanwhile, the separator 400 does not protrude beyond the end of the negative electrode 200 in the first direction d1. This is because the negative electrode uncoated portion 230 functions as an electrode tab. Similarly, the separator 400 does not protrude beyond the end of the positive electrode 300 in the second direction d2. This is because the positive electrode uncoated portion 330 functions as an electrode tab.

[0114] Meanwhile, one end of the negative electrode 200 facing the insulating layer 500p across the separator 400 may not protrude beyond one end of the separator 400. For example, referring to FIG 13, the positive electrode 300 is provided with the insulating layer 500p, and one end of the negative electrode 200 facing the insulating layer 500p may be disposed inside the separator 400. Therefore, even if the positive electrode uncoated portion 330 protrudes beyond the separator 400, since one end of the negative electrode 200 is located inside the separator 400, the possibility of contact between the positive electrode 300 and the negative electrode 200 is significantly reduced.

[0115] FIG. 14 shows an insulating layer 500p formed on the positive electrode 300 as well as an insulating layer 500n formed on the negative electrode 200. Of course, as another embodiment, although not shown, the present invention also includes an insulating layer formed only on the negative electrode 200. The insulating layer 500n formed on the negative electrode 200 may cover at least a portion of the negative electrode uncoated portion 230 and the negative electrode active material portion 220. The insulating layer 500n may simultaneously cover at least a portion of the negative electrode uncoated portion 230 and at least a portion of the negative electrode active material portion 220. For example, the insulating layer 500n may be provided on a boundary region between the negative electrode active material portion 220 and the negative electrode uncoated portion 230. For example, the insulating layer 500n may cover at least a portion of the negative electrode boundary portion 220B.

[0116] The insulating layer 500n formed on the negative electrode may have a similar structure to the insulating layer 500p formed on the positive electrode 300. Hereinafter, the same description will be omitted and differences from the above-described embodiment will be mainly described.

[0117] The insulating layer 500n formed on the negative electrode 200 may be disposed in a position that does not overlap with the loading reduction portion 300D of the positive electrode 300 based on the direction perpendicular to the first direction d1. The portion where the insulating layer 500n is formed based on the direction perpendicular to the first direction d1 is an unreacted region. Therefore, if the insulating layer 500n is positioned in a position where it overlaps with the loading reduction portion 300D based on the direction perpendicular to the first direction d1, the capacity loss of the battery occurs accordingly, and there is no reason to provide the loading reduction portion 300D. Therefore, as shown in FIG. 14, the insulating layer 500n that covers at least a part of the negative electrode boundary portion 220B is positioned so as not to overlap with the loading reduction portion 300D based on the direction perpendicular to the first direction d1, thereby preventing the capacity loss of the battery.

[0118] Hereinafter, an electrode assembly according to another embodiment of the present invention will be described in detail with reference to FIGS.

[0119] Fig. 15 is a perspective view showing an electrode assembly according to another embodiment of the present invention, and Figs. 16 to 18 are cross-sectional views showing a negative electrode, a positive electrode, and a separator according to another embodiment of the present invention, respectively.

[0120] First, referring to FIGS. 15 and 16, an electrode assembly 100 according to another embodiment of the present invention may have a structure in which at least a portion of a positive electrode uncoated portion 330 or a negative electrode uncoated portion 230 is bent toward the winding center of the jelly roll structure.

[0121] At least a portion of the negative electrode uncoated portion 230 and the positive electrode uncoated portion 330 may be processed into a plurality of segment pieces that can be bent independently of each other. FIGS. 15 and 16 show that at least a portion of the positive electrode uncoated portion 330 is processed into a plurality of segment pieces 330F that can be bent independently of each other. Here, the plurality of segment pieces 330F may have a structure in which they are folded toward the winding center and overlap each other in multiple layers. For example, the plurality of segment pieces 330F may be notched by a laser. The segment pieces 330F may be formed by a known metal foil cutting process such as ultrasonic cutting or punching.

[0122] Although the following description will be given based on the segment piece 330F of the positive electrode uncoated part 330, the negative electrode uncoated part 230 may have the same or similar structure.

[0123] In order to prevent the active material layer and / or insulating layer 500a from being damaged when the positive electrode uncoated portion 330 is bent, it is preferable to provide a certain gap between the lower end of the cutting line between the segment pieces 330F and the active material layer. This is because stress is concentrated near the lower end of the cutting line when the positive electrode uncoated portion 330 is bent. Such a gap is preferably 0.2 to 4 mm. If the gap is adjusted to this numerical range, it is possible to prevent the active material layer and / or insulating layer 500a near the lower end of the cutting line from being damaged by stress generated when the positive electrode uncoated portion 330 is bent. In addition, the gap can prevent damage to the active material layer and / or insulating layer 500a due to tolerances when the segment pieces are notched or cut.

[0124] The positive electrode uncoated part 330 may be folded toward the winding center of the jelly roll structure. When the positive electrode uncoated part 330 is folded in this manner, the vertical space occupied by the positive electrode uncoated part 330 is reduced, thereby improving the energy density. In addition, the bonding area between the positive electrode uncoated part 330 and a current collector plate (not shown) is increased, thereby improving the bonding strength and reducing resistance.

[0125] 15 and 16 show a state where the segment 330F of the positive electrode uncoated portion 330 is bent in one direction. As described above, the one direction may be the direction toward the winding center of the jelly roll structure.

[0126] The positive electrode uncoated part 330 may be adjacent to the negative electrode 200 side beyond the separator 400. Therefore, it is preferable that the insulating layer 500a is extended to an end of the positive electrode uncoated part 330 on the surface facing the winding center among both sides of the positive electrode uncoated part 330. With this structure, even if the positive electrode uncoated part 330 is bent toward the winding center and is adjacent to the negative electrode 200 side beyond the separator 400, electrical contact between the positive electrode 300 and the negative electrode 200 can be prevented. Therefore, an internal short circuit of the secondary battery can be effectively prevented.

[0127] Meanwhile, the insulating layer 500a may be provided only in a partial region of the surface of the positive electrode uncoated portion 330 opposite to the surface facing the winding center. That is, the positive electrode uncoated portion 330 may be exposed to the outside in the remaining partial region of the surface of the positive electrode uncoated portion 330 opposite to the surface facing the winding center. This allows electrical contact with an adjacent current collector plate (not shown). That is, the positive electrode uncoated portion 330 is exposed in a region not covered by the insulating layer 500a in the entire region of the positive electrode uncoated portion 330, and can be electrically connected to the current collector plate. Furthermore, the positive electrode uncoated portion 330 may be connected to the current collector plate by welding in a region not covered by the insulating layer 500a in the entire region of the positive electrode uncoated portion 330. The welding may be, for example, laser welding. The laser welding may be performed by partially melting the base material of the current collector plate, or may be performed with solder for welding between the current collector plate and the positive electrode uncoated portion 330. In this case, it is preferable that the solder has a lower melting point than the current collector plate and the positive electrode uncoated portion 330. Meanwhile, in addition to laser welding, resistance welding, ultrasonic welding, etc. may be used, but the welding method is not limited thereto.

[0128] 17, the insulating layer 500b may have a shape surrounding an end of the positive electrode uncoated portion 330. Specifically, the insulating layer 500b may have a structure surrounding an end surface of the positive electrode uncoated portion 330. For example, if the length of the folded segment 330F of the positive electrode uncoated portion 330 is long, the possibility of contacting the negative electrode 200 increases. Furthermore, the folded segment 330F may be further folded due to flow or external pressure. In this case, the possibility of the end surface of the positive electrode uncoated portion 330 coming into contact with the negative electrode 200 increases. However, according to the above-mentioned structure of the present invention, even if the positive electrode uncoated portion 330 is further folded or deformed, the insulating layer 500b covers the end surface of the positive electrode uncoated portion 330, so that electrical contact between the positive electrode 300 and the negative electrode 200 can be prevented.

[0129] 18, the insulating layer 500c may extend to a folding point of the positive electrode uncoated portion 330 on the side opposite to the side facing the winding center among both sides of the positive electrode uncoated portion 330. Although not shown in FIG. 18, another part of the wound negative electrode 200 is located on the left side of the separator 400 located on the left side of the jelly roll structure. That is, the positive electrode 300 may be in electrical contact with not only the negative electrode 200 located on the right side of the positive electrode 300, but also the negative electrode 200 located on the left side of the positive electrode 300. However, according to the above-mentioned structure of the present invention, electrical contact with the negative electrodes 200 located on both sides of the positive electrode 300 can be reliably prevented.

[0130] Meanwhile, the electrode assembly according to the present embodiment may be housed in a battery can having one side open. The material of the battery can may be aluminum. Such a battery can may be electrically connected to the electrode assembly. The battery can may be electrically connected to one of the positive electrode 300 and the negative electrode 200. For example, the battery can may be electrically connected to the negative electrode 200 of the electrode assembly. In this case, the battery can may have the same polarity as the negative electrode 200. The negative electrode uncoated portion 230 of the negative electrode 200 may be electrically connected to the current collector plate and finally electrically connected to the battery can.

[0131] Meanwhile, a terminal is provided penetrating the center of the closed end formed on the battery can, and the terminal can be electrically connected to the other one of the positive electrode 300 and the negative electrode 200. For example, the terminal can be electrically connected to the positive electrode 300. In this case, the terminal can have the same polarity as the positive electrode 300. The positive electrode uncoated portion 330 of the positive electrode 300 can be electrically connected to the current collector plate and finally electrically connected to the terminal.

[0132] In addition, the battery can and the terminal are electrically insulated from each other. The electrical insulation between the terminal and the battery can can be achieved in various ways. For example, the insulation can be achieved by interposing an insulating gasket between the terminal and the battery can.

[0133] Meanwhile, a secondary battery cell including an electrode assembly according to this embodiment may be, for example, a secondary battery cell having a form factor ratio (defined as the value obtained by dividing the diameter of the secondary battery cell by the height, i.e., the ratio of the diameter (Φ) to the height (H)) of greater than approximately 0.4.

[0134] Here, the form factor refers to a value indicating the diameter and height of a secondary battery cell. The secondary battery cell according to an embodiment of the present invention may be, for example, a 46110 cell, a 48750 cell, a 48110 cell, a 48800 cell, or a 46800 cell. In the numerical value indicating the form factor, the first two digits indicate the diameter of the cell, the next two digits indicate the height of the cell, and the last digit 0 indicates that the cross section of the cell is circular.

[0135] The secondary battery cell according to an embodiment of the present invention may be a cylindrical battery cell having a roughly cylindrical shape with a diameter of roughly 46 mm, a height of roughly 110 mm, and a form factor ratio of roughly 0.418.

[0136] The secondary battery cell according to another embodiment may be a cylindrical battery cell having a roughly cylindrical shape, a diameter of roughly 48 mm, a height of roughly 75 mm, and a form factor ratio of roughly 0.640.

[0137] Furthermore, the secondary battery cell according to another embodiment may be a cylindrical battery cell having a substantially cylindrical shape with a diameter of approximately 48 mm, a height of approximately 110 mm, and a form factor ratio of approximately 0.418.

[0138] Furthermore, the secondary battery cell according to another embodiment may be a cylindrical battery cell having a substantially cylindrical shape, a diameter of approximately 48 mm, a height of approximately 80 mm, and a form factor ratio of approximately 0.600.

[0139] Furthermore, the secondary battery cell according to another embodiment may be a cylindrical battery cell having a substantially cylindrical shape, a diameter of approximately 46 mm, a height of approximately 80 mm, and a form factor ratio of approximately 0.575.

[0140] Conventionally, secondary battery cells with a form factor ratio of approximately 0.4 or less have been used. That is, conventionally, for example, 18650 cells, 21700 cells, etc. have been used. In the case of an 18650 cell, its diameter is approximately 18 mm, its height is approximately 65 mm, and its form factor ratio is approximately 0.277. In the case of a 21700 cell, its diameter is approximately 21 mm, its height is approximately 70 mm, and its form factor ratio is approximately 0.300.

[0141] In this embodiment, terms indicating directions such as front, back, left, right, up, and down are used, but these terms are merely for convenience of explanation and may change depending on the position of the target object, the position of the observer, etc.

[0142] The electrode assembly according to the present embodiment may be housed in a battery can to form a battery cell, as described above. A plurality of such battery cells may be assembled to form a battery module, and the battery module may be mounted with various control and protection systems, such as a Battery Management System (BMS) and a cooling system, to form a battery pack.

[0143] The battery cell, the battery module, or the battery pack may be applied to various devices, particularly, to transportation means such as electric bicycles, electric cars, and hybrid vehicles, but is not limited thereto, and may be applied to various devices that can use secondary batteries.

[0144] Although the preferred embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improvements made by those skilled in the art using the basic concept of the present invention defined in the following claims also fall within the scope of the present invention. [Explanation of symbols]

[0145] 100: Electrode assembly 200: Negative electrode 300: Positive electrode 400: Separation membrane 300D: Loading reduction section

Claims

1. negative electrode, Positive electrode, and A separator disposed between the negative electrode and the positive electrode. Including, the negative electrode, the positive electrode, and the separator are wound together to form a jelly roll structure; the negative electrode includes a negative electrode current collector and a negative electrode active material portion formed by applying a negative electrode active material onto the negative electrode current collector, the positive electrode includes a positive electrode current collector and a positive electrode active material portion formed by applying a positive electrode active material onto the positive electrode current collector, a negative electrode uncoated portion of the negative electrode current collector, on which the negative electrode active material is not coated, extends in a first direction; a positive electrode uncoated portion of the positive electrode current collector, on which the positive electrode active material is not coated, extends in a second direction opposite to the first direction; the positive active material portion includes a loading reduction portion having a loading amount of the positive active material less than that of an adjacent region, The loading reduction portion is located at one end of the positive electrode in the first direction, an amount of the positive active material loaded in the loading reduction portion is less than an amount of the negative active material loaded in the negative active material portion corresponding to the loading reduction portion;

2. The electrode assembly of claim 1 , wherein the negative active material portion is located at a portion corresponding to the loading reduction portion in a direction perpendicular to the first direction.

3. the negative electrode active material part includes a negative electrode boundary part that forms a boundary between the negative electrode active material part and the negative electrode uncoated part, The electrode assembly of claim 1 , wherein the negative electrode boundary portion is located in a portion corresponding to the loading reduction portion in a direction perpendicular to the first direction.

4. The electrode assembly of claim 1 , wherein the loading reducing portion is configured such that the loading amount of the positive active material gradually decreases in the first direction.

5. The electrode assembly of claim 1 , wherein the first direction and the second direction are parallel to a height direction of the jelly roll structure.

6. the negative electrode uncoated portion extends beyond the separator in the first direction, The electrode assembly of claim 1 , wherein the positive electrode uncoated portion extends beyond the separator in the second direction.

7. The negative electrode or the positive electrode further includes an insulating layer formed on at least one of the positive electrode and the negative electrode; the insulating layer formed on the negative electrode covers the negative electrode uncoated portion and at least a portion of the negative electrode active material portion, The electrode assembly of claim 1 , wherein the insulating layer formed on the positive electrode covers the positive electrode uncoated portion and at least a portion of the positive electrode active material portion.

8. the insulating layer formed on the negative electrode is formed to cover an end of the negative electrode active material part in the first direction and a part of the negative electrode uncoated part adjacent thereto, 8. The electrode assembly of claim 7, wherein the insulating layer formed on the positive electrode is formed to cover an end of the positive electrode active material portion in the second direction and a portion of the positive electrode uncoated portion adjacent thereto.

9. The electrode assembly of claim 7 , wherein the insulating layer formed on the negative electrode is located at a position that does not overlap a loading reduction portion in a direction perpendicular to the first direction.

10. The electrode assembly of claim 1 , wherein at least a portion of the negative electrode uncoated portion and the positive electrode uncoated portion are processed into a plurality of segmented pieces that can be bent independently of each other.

11. preparing a negative electrode sheet such that a negative electrode active material portion, on which a negative electrode active material is coated, and a negative electrode uncoated portion, on which the negative electrode active material is not coated, are alternately arranged on a negative electrode current collector; preparing a positive electrode sheet on a positive electrode current collector such that a positive electrode active material portion coated with a positive electrode active material and a positive electrode uncoated portion not coated with the positive electrode active material are alternately arranged; slitting the negative electrode uncoated portion and the negative electrode active material portion to manufacture a negative electrode; manufacturing a positive electrode by slitting the positive electrode uncoated portion and the positive electrode active material portion; and and winding the negative electrode and the positive electrode together with a separator to form a jelly roll structure. the positive electrode sheet includes a reduced loading region having a lower loading amount of the positive electrode active material than an adjacent region, In the step of preparing the positive electrode, the loading reduction region is slit; the slit reduced loading region forms a reduced loading portion in the jelly roll structure, the reduced loading portion having a smaller amount of the positive active material than an adjacent region; In the jelly roll structure, the negative electrode uncoated portion extends in a first direction, and the positive electrode uncoated portion extends in a second direction opposite to the first direction, The loading reduction portion is located at one end of the positive electrode in the first direction, A method for manufacturing an electrode assembly, wherein a loading amount of the positive active material in the loading reduction portion is less than a loading amount of the negative active material in the negative active material portion corresponding to the loading reduction portion.

12. The method of claim 11, wherein the loading amount of the positive active material in the loading reducing portion gradually decreases in the first direction.

13. The method of claim 11 , wherein the negative active material portion is located in a portion of the jelly roll structure corresponding to the loading reduction portion in a direction perpendicular to the first direction.

14. the negative electrode active material part includes a negative electrode boundary part that forms a boundary between the negative electrode active material part and the negative electrode uncoated part, The method of claim 11 , wherein the negative electrode boundary portion is located at a portion of the jelly roll structure corresponding to the loading reduction portion in a direction perpendicular to the first direction.

15. The loading amount of the positive active material gradually decreases toward the center of the loading reduction region, The method of claim 11, wherein in the step of manufacturing the positive electrode, the loading reduction portion is provided by slitting the central portion of the loading reduction region.