Optical Devices

Abstract

This optical device comprises a slab layer (102) formed on a lower cladding layer (101), a core (103) formed on the slab layer (102), and a first metal layer (104a) and a second metal layer (104b). The optical device further comprises a first adhesion layer (105a) and a second adhesion layer (105b), which are respectively formed between the slab layer (102) on both sides of the core (103) and the first metal layer (104a) and the second metal layer (104b). The first metal layer (104a) and the second metal layer (104b) are formed apart from the core (103).

Description

[Technical field]

[0001] The present invention relates to an optical device using an electro-optic material. [Background technology]

[0002] Optical waveguide-type high-speed phase shifters are being researched and developed as key devices for Tbit / s-class ultrafast optical communications and various applications using millimeter and terahertz waves. Among these high-speed phase shifters, there is a plasmonic optical waveguide-type phase shifter that uses electro-optic (EO) materials as the optical waveguide core.

[0003] Among optical waveguide-type high-speed phase shifters, the plasmonic optical waveguide-type phase shifter operates on the principle of dielectric response due to an external modulated electric field to produce a change in refractive index, has a large mode overlap between the modulated high-frequency signal and the light propagating through the waveguide, and can have an extremely short element length. Therefore, the above-mentioned technology can realize an ultra-compact, ultra-low-capacitance phase shifter that can be regarded as a lumped constant element for the modulated high-frequency signal, and has the characteristic of being able to realize an optical modulator capable of high-speed operation.

[0004] In the above-mentioned plasmonic optical waveguide phase shifter, the metal outer conductor of the plasmonic optical waveguide is formed, and finally, an organic material, EO polymer, is applied to fill the minute gaps between the metal outer conductors with the EO material, thereby forming a core made of the EO material.

[0005] However, the EO materials constituting the above-mentioned core are limited to those that can be formed to fill the minute gap in the back-end process.On the other hand, inorganic materials that have been widely used as EO materials can be obtained as high-quality materials by crystal growth technology under special environments such as high temperatures, but as mentioned above, it is difficult to form high-quality crystals to fill the minute gap after forming the metal outer conductor.

[0006] Due to the above-mentioned problems, when using an inorganic EO material, a technique can be applied in which a core is formed first, and then a metal outer conductor is formed, as described below (Non-Patent Document 1). In this technique, first, as shown in Fig. 3A, a wafer is prepared having a Si layer 302 on a SiO2 layer 301 that will become the lower cladding. Next, the Si layer 302 is patterned to form a rib-shaped core 303, as shown in Fig. 3B.

[0007] Next, as shown in Fig. 3C, an Al layer 304 is formed on the Si layer 302 on which the core 303 has been formed, covering the core 303. Thereafter, the Al layer 304 on the upper surface of the core 303 is removed by selectively thinning the Al layer 304, to expose the upper surface of the core 303, as shown in Fig. 3D. As a result, a plasmonic optical waveguide is fabricated that includes the core 303 formed to fill the minute gap between the Al layers 304a and 304b that serve as the metallic outer conductor. [Prior art documents] [Non-patent literature]

[0008] [Non-Patent Document 1] H. Nishi et al., "High-speed Si plasmonic photodetector based on internal photoemission and two-photon absorption", Conference on Lasers and Electro-Optics, 18024143, 2018. Summary of the Invention [Problem to be solved by the invention]

[0009] In this type of plasmonic optical waveguide, the metal outer conductor is generally made of Au in order to reduce loss. However, Au has low adhesion to the EO material layer that constitutes the rib-type waveguide, so an adhesion layer is introduced between them. However, if an adhesion layer exists between the outer conductor made of Au and the core, the characteristics of the plasmonic optical waveguide are significantly affected by the adhesion layer, which is a major problem in that it is difficult to achieve the inherent low loss expected from using Au.

[0010] The present invention has been made to solve the above problems, and has as its object to achieve low loss even when an adhesive layer is introduced between a layer of electro-optic material and a metal outer conductor. [Means for solving the problem]

[0011] The optical device according to the present invention comprises a slab layer made of an electro-optical material having an electro-optical effect, a core made of the same electro-optical material as the slab layer and formed on the slab layer, a first metal layer and a second metal layer formed in contact with both side surfaces of the core, and a metal layer formed between the slab layer and the first metal layer and the second metal layer on both sides of the core to improve adhesion between the slab layer and the first metal layer and the second metal layer. No. 1 Adhesion Layer , second adhesive layer With The first adhesive layer and the second adhesive layer are formed apart from the core, The electro-optical material is an inorganic material, the first metal layer and the second metal layer are made of a precious metal, and the core, the first metal layer, and the second metal layer form a plasmonic optical waveguide. Effect of the Invention

[0012] As described above, according to the present invention, adhesion layers are formed between the slab layers on both sides of the core and the first and second metal layers, so that low loss can be achieved even when adhesion layers are introduced between the layer of electro-optical material and the metal outer conductor. [Brief description of the drawings]

[0013] [Figure 1] FIG. 1 is a cross-sectional view showing a configuration of an optical device according to an embodiment of the present invention. [Figure 2A] FIG. 2A is a cross-sectional view showing a state of an optical device in the middle of a process, for illustrating a method of manufacturing an optical device according to an embodiment of the present invention. [Figure 2B] FIG. 2B is a cross-sectional view showing a state of the optical device in the middle of a process for explaining the method of manufacturing the optical device according to the embodiment of the present invention. [Figure 2C] FIG. 2C is a cross-sectional view showing a state of the optical device in the middle of a process for explaining the method of manufacturing the optical device according to the embodiment of the present invention. [Figure 2D] FIG. 2D is a cross-sectional view showing a state of an optical device in the middle of a process for explaining a method of manufacturing an optical device according to an embodiment of the present invention. [Figure 3A] FIG. 3A is a cross-sectional view showing a state of an optical device in the middle of a process for illustrating a method of manufacturing an optical device. [Figure 3B] FIG. 3B is a cross-sectional view showing a state of the optical device in the middle of a process for explaining the method of manufacturing the optical device. [Figure 3C] FIG. 3C is a cross-sectional view showing a state of the optical device in the middle of a process for explaining the method of manufacturing the optical device. [Figure 3D] FIG. 3D is a cross-sectional view showing a state of an optical device in the middle of a process for explaining a method of manufacturing an optical device. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] An optical device according to an embodiment of the present invention will now be described with reference to Fig. 1. This optical device comprises a slab layer 102 formed on a lower cladding layer 101, a core 103 formed on the slab layer 102, a first metal layer 104a, and a second metal layer 104b. The slab layer 102 is made of an electro-optical material having an electro-optical effect, and the core 103 is also made of the same electro-optical material as the slab layer 102.

[0015] The slab layer 102 and the core 103 form a rib-type waveguide with the core 103 as a rib. The slab layer 102 and the core 103 can be formed integrally. The first metal layer 104a and the second metal layer 104b are formed on the slab layer 102 in contact with both side surfaces of the core 103. The first metal layer 104a and the second metal layer 104b are not formed on the upper part of the core 103. The core 103, the first metal layer 104a, and the second metal layer 104b form a plasmonic optical waveguide. An upper cladding layer made of an insulating material can be provided on the core 103, the first metal layer 104a, and the second metal layer 104b. In this example, air is used as the upper cladding.

[0016] Furthermore, this optical device includes a first adhesion layer 105a and a second adhesion layer 105b formed between the slab layer 102 and the first metal layer 104a and the second metal layer 104b on both sides of the core 103. The first adhesion layer 105a and the second adhesion layer 105b are used to improve adhesion between the slab layer 102 and the first metal layer 104a and the second metal layer 104b. The first metal layer 104a and the second metal layer 104b are formed apart from the core 103.

[0017] The lower cladding layer 101 may be made of an insulating material such as SiO2. The electro-optical material constituting the slab layer 102 and the core 103 is an inorganic material, and may be at least one of lithium niobate, lithium tantalate, barium titanate, and potassium tantalate niobate.

[0018] The first metal layer 104a and the second metal layer 104b can be made of a precious metal such as gold (Au) or silver (Ag). By making the first metal layer 104a and the second metal layer 104b from these metals, the loss of the plasmonic optical waveguide can be reduced. The first adhesive layer 105a and the second adhesive layer 105b can be made of Cr or Ti.

[0019] For example, the thickness from the bottom surface of the slab layer 102 to the top surface of the core 103 (total core height) can be 200 nm, and the width of the core 103 in a cross-sectional view can be 50 nm. The thickness of the slab layer 102 can be 100 nm. The first metal layer 104a and the second metal layer 104b can be 80 nm thick. The first adhesion layer 105a and the second adhesion layer 105b can be spaced apart from the side surface of the core 103 by 40 nm.

[0020] According to the above-mentioned embodiment, since the first adhesive layer 105a and the second adhesive layer 105b are provided, peeling of the first metal layer 104a and the second metal layer 104b is suppressed, and contact between the side surface of the core 103 and the first metal layer 104a and the second metal layer 104b is maintained. As is well known, for example, the adhesion between Cr and lithium niobate is good, and the adhesion between Cr and Au is good. Therefore, the first adhesive layer 105a and the second adhesive layer 105b can prevent the peeling of the first metal layer 104a and the second metal layer 104b. Furthermore, since the areas of first adhesion layer 105a and second adhesion layer 105b are sufficiently large compared to the spacing between first adhesion layer 105a, second adhesion layer 105b and the side surfaces of core 103, peeling of first metal layer 104a and second metal layer 104b can be sufficiently prevented although no adhesion layer is formed at the contact points between core 103 and first metal layer 104a and second metal layer 104b.

[0021] Furthermore, since the first adhesion layer 105a and the second adhesion layer 105b are spaced apart from the side surfaces of the core 103, the characteristics of the plasmonic optical waveguide are not affected by the first adhesion layer 105a and the second adhesion layer 105b. Thus, according to the embodiment, even if the first adhesion layer 105a and the second adhesion layer 105b are introduced between the slab layer 102 and the first metal layer 104a and the second metal layer 104b, low loss can be achieved.

[0022] Next, the fabrication of the optical device according to the embodiment of the present invention will be described with reference to FIGS. 2A to 2D.

[0023] First, as shown in Fig. 2A, a wafer is prepared having an LN film 121 made of lithium niobate on a lower cladding layer 101 made of SiO2. Next, the LN film 121 is patterned by dry etching using a hard mask formed by electron beam lithography technology to form a rib-shaped core 103 on the slab layer 102 as shown in Fig. 1B.

[0024] Next, as shown in FIG. 1C, a first adhesive layer 105a and a second adhesive layer 105b made of Cr are formed on the slab layer 102 on both sides of the core 103. The first adhesive layer 105a and the second adhesive layer 105b are formed 40 nm away from the side (bottom) of the core 103. For example, first, a lift-off mask that covers the core 103 is formed by electron beam lithography. Next, Cr is deposited on the lift-off mask by electron beam evaporation or the like. Thereafter, the lift-off mask is removed (lifted off) to form the first adhesive layer 105a and the second adhesive layer 105b.

[0025] Next, as shown in FIG. 2D, the Au layer 104 is formed covering the core 103, the first adhesive layer 105a, and the second adhesive layer 105b. After that, the Au layer 104 on the upper surface of the core 103 is removed by selectively thinning the Au layer 104, and the upper surface of the core 103 is exposed as shown in FIG. 1. For example, first, the step on the upper surface of the Au layer 104 due to the core 103 is flattened by a resist film formed by applying a resist made of an organic material. Next, etch-back is performed from the flattened surface of the resist film to expose the convex portion on the upper surface of the Au layer 104 due to the core 103. After that, the Au layer 104 on the upper part of the core 103 is removed by a predetermined dry etching technique, and the upper surface of the core 103 can be exposed.

[0026] As described above, according to the present invention, adhesion layers are formed between the slab layers on both sides of the core and the first and second metal layers, making it possible to achieve low loss even when adhesion layers are introduced between the layer of electro-optical material and the metal outer conductor.

[0027] According to the present invention, even if the metallic outer conductor is made of a noble metal such as Au, which has a small value of the imaginary part of the complex dielectric constant among metals having a negative real part of the complex dielectric constant and is expected to realize a low-loss plasmonic optical waveguide, the problem of adhesion with the layer of the electro-optic material can be solved. Furthermore, the problem of peeling of the metallic outer conductor can be solved not only in the case of reducing the loss of the plasmonic optical waveguide but also in the case of combining materials from the viewpoints of increasing the speed and efficiency of the plasmonic optical waveguide modulator.

[0028] It should be noted that the present invention is not limited to the above-described embodiments, and it is apparent that many modifications and combinations can be made by a person having ordinary knowledge in the art within the technical concept of the present invention. [Explanation of symbols]

[0029] 101...lower clad layer, 102...slab layer, 103...core, 104a...first metal layer, 104b...second metal layer, 105a...first adhesive layer, 105b...second adhesive layer.

Claims

1. A slab layer made of an electro-optic material having an electro-optic effect; a core formed on the slab layer and made of the same electro-optic material as the slab layer; a first metal layer and a second metal layer formed on both side surfaces of the core, a first adhesive layer and a second adhesive layer formed between the slab layer and the first metal layer and between the slab layer and the second metal layer on both sides of the core, the first adhesive layer and the second adhesive layer being adapted to improve adhesion between the slab layer and the first metal layer and the second metal layer; Equipped with the first adhesive layer and the second adhesive layer are formed apart from the core, the electro-optical material is an inorganic material; the first metal layer and the second metal layer are made of a precious metal, The core, the first metal layer, and the second metal layer form a plasmonic optical waveguide. An optical device comprising:

2. 2. The optical device according to claim 1, An optical device, wherein the electro-optical material is at least one of lithium niobate, lithium tantalate, barium titanate, and potassium tantalate niobate.

3. 3. The optical device according to claim 1, 1. An optical device according to claim 1, wherein the first metal layer and the second metal layer are made of Au or Ag.

4. The optical device according to any one of claims 1 to 3, 13. An optical device comprising: the first adhesive layer and the second adhesive layer each made of Cr or Ti.

5. The optical device according to any one of claims 1 to 4, An optical device, wherein the slab layer and the core are integrally formed.