Composition for semiconductor photoresist and method for forming pattern using the same

Abstract

To provide a semiconductor photoresist composition with improved storage stability and coating properties, and a method for forming patterns using the semiconductor photoresist composition.SOLUTION: A semiconductor photoresist composition includes an organotin compound represented by Chemical Formula 1 and a solvent.SELECTED DRAWING: Figure 5

Description

[Technical field]

[0001] The present invention relates to a semiconductor photoresist composition and a pattern forming method using the same. [Background technology]

[0002] EUV (extreme ultraviolet) lithography is attracting attention as one of the elemental technologies for manufacturing next-generation semiconductor devices. EUV lithography is a pattern formation technology that uses EUV light with a wavelength of 13.5 nm as the exposure light source. It has been demonstrated that EUV lithography can form extremely fine patterns (e.g., 20 nm or less) during the exposure step in the semiconductor device manufacturing process.

[0003] The realization of extreme ultraviolet (EUV) lithography requires the development of compatible photoresists capable of performing spatial resolution below 16 nm. Currently, traditional chemically amplified (CA) photoresists are being continuously developed to meet the specifications for resolution, photospeed, and feature roughness (feature roughness) and line edge roughness (line edge roughness or LER) for next generation devices.

[0004] These chemically amplified photoresists, which generally contain organic polymers, have an inherent image blur caused by acid-catalyzed reactions that limit resolution at small feature sizes, a fact that has long been known in electron beam (e-beam) lithography. Chemically amplified (CA) photoresists were designed for high sensitivity, but their typical elemental composition reduces the absorbance of the photoresist at 13.5 nm wavelengths, resulting in lower sensitivity and in part creating additional difficulties under EUV exposure.

[0005] CA photoresists can also suffer from roughness issues at small feature sizes, and experiments have shown that line edge roughness (LER) increases as the light speed decreases, due in part to the nature of the acid catalyzed process. Due to the shortcomings and problems of CA photoresists, there is a demand in the semiconductor industry for a new class of high performance photoresists.

[0006] In order to overcome the problems of the chemically amplified organic photoresists described above, inorganic photosensitive compositions have been researched. Inorganic photosensitive compositions are mainly used for negative tone patterning, which is chemically modified by a non-chemically amplified mechanism and is resistant to removal by a developer composition. Inorganic photosensitive compositions contain inorganic elements with higher EUV absorption than hydrocarbons, and are known to ensure sensitivity even with a non-chemically amplified mechanism, to be less sensitive to stochastic variations, and to have less line edge roughness and number of defects.

[0007] Inorganic photoresists based on peroxopolyacids of tungsten and tungsten mixed with niobium, titanium, and / or tantalum have been reported for patterning radiation sensitive materials (Patent Document 1 and Non-Patent Document 1).

[0008] These materials have been effective in patterning large features in a bilayer configuration with deep UV, x-ray, and electron beam sources. More recently, impressive performance has been reported when using cationic hafnium metal oxide sulfate (HfSOx) materials with peroxo complexing agents to develop 15 nm half pitches by projection EUV exposure (Patent Document 2 and Non-Patent Document 2). This system shows top of the line performance of non-CA photoresists and has a light speed approaching the requirements for a viable EUV photoresist. However, hafnium metal oxide sulfate materials with peroxo complexing agents have some practical drawbacks. First, the material is coated with a highly corrosive sulfuric acid / hydrogen peroxide mixture and has poor storage stability. Second, as a complex mixture, it is not easy to modify the structure for performance improvement. Third, it must be developed with an extremely high concentration of TMAH (tetramethylammonium hydroxide) solution, such as 25% by weight.

[0009] Recently, active research has been conducted on molecules containing tin, as it has been discovered that they have excellent extreme ultraviolet absorption. One of these, organotin polymers, enables negative tone patterning that is not removed by organic developers through crosslinking with surrounding polymer chains by oxo bonds as organic ligands are dissociated by light absorption or secondary electrons generated by the absorption. Such organotin polymers have been shown to dramatically improve sensitivity while maintaining resolution and line edge roughness, but further improvement of the above patterning characteristics is required for commercialization. [Prior art documents] [Patent documents]

[0010] [Patent Document 1] U.S. Pat. No. 5,061,599 [Patent Document 2] US Patent Application Publication No. 2011 / 0045406 [Non-patent literature]

[0011] [Non-Patent Document 1] H. Okamoto, T. Iwayanagi, K. Mochiji, H. Umezaki, T. Kudo, Applied Physics Letters, 49(5), 298-300, 1986 [Non-Patent Document 2] JKStowers, A.Telecky, M.Kocsis, BLClark, DAKEszler, A.Grenville, CNAnderson, PPNaulleau, Proc.SPIE, 7969, 796915, 2011 Summary of the Invention [Problem to be solved by the invention]

[0012] An object of the present invention is to provide a semiconductor photoresist composition having improved storage stability and coating properties.

[0013] Another object of the present invention is to provide a pattern forming method using the above semiconductor photoresist composition. [Means for solving the problem]

[0014] The composition for semiconductor photoresist according to the present invention comprises an organotin compound represented by the following Chemical Formula 1 and a solvent.

[0015] [ka]

[0016] In the above chemical formula 1, X 1 ~X 6 are each independently O or S; L 1 ~L 3each independently represents a single bond, a substituted or unsubstituted divalent saturated aliphatic hydrocarbon group having 1 to 20 carbon atoms, a substituted or unsubstituted divalent saturated or unsaturated alicyclic hydrocarbon group having 3 to 20 carbon atoms, a substituted or unsubstituted divalent unsaturated aliphatic hydrocarbon group having 2 to 20 carbon atoms containing one or more double bonds or triple bonds, a substituted or unsubstituted divalent aromatic hydrocarbon group having 6 to 20 carbon atoms, -C(=O)-, or a combination thereof; R a , R b , R c , R d , R e , R f and R 1 ~R 3 each independently represents a hydrogen atom, a halogen atom, a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkenyl group having 3 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkynyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof; R 4 is a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkenyl group having 3 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkynyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof.

[0017] R in the above Chemical Formula 1 4 may be a substituted or unsubstituted branched alkyl group having 3 to 20 carbon atoms.

[0018] R in the above Chemical Formula 1 1 ~R 3may each independently be a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof.

[0019] R in the above Chemical Formula 1 1 ~R 3 may each independently be n-propyl, n-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, n-nonyl, n-decyl, iso-propyl, iso-butyl, iso-pentyl, iso-hexyl, iso-heptyl, iso-octyl, iso-nonyl, iso-decyl, sec-butyl, sec-pentyl, sec-hexyl, sec-heptyl, sec-octyl, tert-butyl, tert-pentyl, tert-hexyl, tert-heptyl, tert-octyl, tert-nonyl, or tert-decyl.

[0020] L in the above chemical formula 1 1 ~L 3 may each independently be a single bond, or a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms.

[0021] R in the above Chemical Formula 1 a , R b , R c , R d , R e and R f may each independently be a hydrogen atom, a halogen atom, or a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms.

[0022] X in the above chemical formula 1 2 , X 4 and X 6 may each be O.

[0023] X in the above chemical formula 1 1 ~X 6may each be O.

[0024] The organotin compound in the above Chemical Formula 1 may be one of the compounds selected from the group of compounds listed in Group 1 below.

[0025] [ka]

[0026] The content of the organotin compound may be 1% by mass to 30% by mass, based on 100% by mass of the total mass of the composition for semiconductor photoresist.

[0027] The semiconductor photoresist composition may further include additives such as a surfactant, a crosslinking agent, a leveling agent, or a combination thereof.

[0028] According to another embodiment, a method for forming a pattern includes forming a film to be etched on a substrate, applying the above-described semiconductor photoresist composition on the film to be etched to form a photoresist film, patterning the photoresist film to form a photoresist pattern, and etching the film to be etched using the photoresist pattern as an etching mask.

[0029] The step of forming the photoresist pattern may use light having a wavelength of 5 nm to 150 nm.

[0030] The method of forming a pattern may further include forming a resist underlayer film between the substrate and the photoresist film.

[0031] The photoresist pattern may have a width of 5 nm to 100 nm. Effect of the Invention

[0032] A semiconductor photoresist composition according to an embodiment of the present invention can provide a photoresist pattern having improved sensitivity while maintaining line edge roughness. [Brief description of the drawings]

[0033] [Figure 1] 1 is a schematic cross-sectional view illustrating a method for forming a pattern using a semiconductor photoresist composition according to an embodiment of the present invention. [Diagram 2] 1 is a schematic cross-sectional view illustrating a method for forming a pattern using a semiconductor photoresist composition according to an embodiment of the present invention. [Diagram 3] 1 is a schematic cross-sectional view illustrating a method for forming a pattern using a semiconductor photoresist composition according to an embodiment of the present invention. [Figure 4] 1 is a schematic cross-sectional view illustrating a method for forming a pattern using a semiconductor photoresist composition according to an embodiment of the present invention. [Diagram 5] 1 is a schematic cross-sectional view illustrating a method for forming a pattern using a semiconductor photoresist composition according to an embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0034] Hereinafter, an embodiment of the present invention will be described in detail with reference to the accompanying drawings. However, in describing the present invention, a description of already known functions or configurations will be omitted in order to clarify the gist of the present invention.

[0035] In order to clearly explain the present invention, parts unnecessary for the description will be omitted, and the same or similar components will be given the same reference numerals throughout the specification. In addition, the size and thickness of each component shown in the drawings are arbitrarily shown for the convenience of explanation, and the present invention is not necessarily limited to those shown in the drawings.

[0036] In the drawings, the thickness of various layers and regions is exaggerated to clearly show them. Also, in the drawings, the thickness of some layers and regions is exaggerated for the convenience of explanation. When a layer, film, region, plate, or other part is said to be "on" or "on" another part, this includes not only the case where it is "directly on" another part, but also the case where there is another part therebetween.

[0037] In the present invention, "substituted" means that a hydrogen atom is replaced by a deuterium atom, a halogen atom, a hydroxy group, a cyano group, a nitro group, -NRR' (wherein R and R' are each independently a hydrogen atom, a substituted or unsubstituted saturated or unsaturated aliphatic hydrocarbon group having 1 to 30 carbon atoms, a substituted or unsubstituted saturated or unsaturated alicyclic hydrocarbon group having 3 to 30 carbon atoms, or a substituted or unsubstituted aromatic hydrocarbon group having 6 to 30 carbon atoms), -SiRR'R" (wherein R, R', and R" are each independently a hydrogen atom). "Unsubstituted" means that the hydrogen atom is not substituted with any other substituent, and is preferably substituted with a substituted or unsubstituted alkyl group having 1 to 30 carbon atoms, a substituted or unsubstituted saturated or unsaturated aliphatic hydrocarbon group having 1 to 30 carbon atoms, a substituted or unsubstituted saturated or unsaturated alicyclic hydrocarbon group having 3 to 30 carbon atoms, or a substituted or unsubstituted aromatic hydrocarbon group having 6 to 30 carbon atoms), an alkyl group having 1 to 30 carbon atoms, a haloalkyl group having 1 to 10 carbon atoms, an alkylsilyl group having 1 to 10 carbon atoms, a cycloalkyl group having 3 to 30 carbon atoms, an aryl group having 6 to 30 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, or a combination thereof. "Unsubstituted" means that the hydrogen atom remains as a hydrogen atom without being substituted with another substituent.

[0038] In this specification, unless otherwise specified, the term "alkyl group" refers to a straight-chain or branched aliphatic hydrocarbon group. The alkyl group may be a "saturated alkyl group" that does not contain any double bonds or triple bonds.

[0039] The alkyl group may be an alkyl group having 1 to 10 carbon atoms. For example, the alkyl group may be an alkyl group having 1 to 8 carbon atoms, an alkyl group having 1 to 7 carbon atoms, an alkyl group having 1 to 6 carbon atoms, an alkyl group having 1 to 5 carbon atoms, or an alkyl group having 1 to 4 carbon atoms. For example, the alkyl group having 1 to 5 carbon atoms may be a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an iso-butyl group, a sec-butyl group, a tert-butyl group, or a 2,2-dimethylpropyl group.

[0040] In the present invention, unless otherwise defined, the term "cycloalkyl group" refers to a monovalent cyclic aliphatic hydrocarbon group.

[0041] The cycloalkyl group may be a cycloalkyl group having 3 to 10 carbon atoms, for example, a cycloalkyl group having 3 to 8 carbon atoms, a cycloalkyl group having 3 to 7 carbon atoms, a cycloalkyl group having 3 to 6 carbon atoms, a cycloalkyl group having 3 to 5 carbon atoms, or a cycloalkyl group having 3 to 4 carbon atoms. For example, the cycloalkyl group may be a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, or a cyclohexyl group, but is not limited thereto.

[0042] As used herein, an "aryl group" refers to a cyclic substituent in which all elements of the substituent have p-orbitals and these p-orbitals form conjugation, including monocyclic or fused polycyclic (i.e., rings which share adjacent pairs of carbon atoms) functional groups.

[0043] As used herein, unless otherwise defined, the term "alkenyl group" refers to a straight-chain or branched aliphatic hydrocarbon group and an aliphatic unsaturated alkenyl group containing one or more double bonds.

[0044] As used herein, unless otherwise defined, the term "alkynyl group" refers to a straight-chain or branched aliphatic hydrocarbon group and an aliphatic unsaturated alkynyl group containing one or more triple bonds.

[0045] In the formulae described herein, t-Bu or tert-Bu refers to a tert-butyl group.

[0046] Hereinafter, a semiconductor photoresist composition according to one embodiment of the present invention will be described.

[0047] A composition for semiconductor photoresist according to one embodiment of the present invention includes an organotin compound represented by the following Formula 1 and a solvent.

[0048] [ka]

[0049] In the above chemical formula 1, X 1 ~X 6 are each independently O or S; L 1 ~L 3 each independently represents a single bond, a substituted or unsubstituted divalent saturated aliphatic hydrocarbon group having 1 to 20 carbon atoms, a substituted or unsubstituted divalent saturated or unsaturated alicyclic hydrocarbon group having 3 to 20 carbon atoms, a substituted or unsubstituted divalent unsaturated aliphatic hydrocarbon group having 2 to 20 carbon atoms containing one or more double bonds or triple bonds, a substituted or unsubstituted divalent aromatic hydrocarbon group having 6 to 20 carbon atoms, -C(=O)-, or a combination thereof; R a , R b , R c , R d , R e , R f and R 1 ~R 3each independently represents a hydrogen atom, a halogen atom, a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkenyl group having 3 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkynyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof; R 4 is a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkenyl group having 3 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkynyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof.

[0050] The above-mentioned organotin compounds have two or more coordinate bond sites in addition to the O or S that is directly bonded to Sn. Therefore, the unshared electron pairs of O or S induce not only intermolecular bonds but also intramolecular coordinate bonds, which is advantageous for the formation of an amorphous matrix.

[0051] In particular, compared to the tetravalently coordinated cluster form, the coordination number of Sn is filled by additional coordination bonds, resulting in a structure in which the Sn atom is hidden, improving stability against moisture, preventing aggregation caused by nucleation induced by oxygen contained in the cluster, and increasing long-term storage stability. This effectively reduces defects during the coating process, which also affects coating stability.

[0052] In addition, compared to a monomolecular form, the strength of adhesion to the substrate is improved due to the strengthening of intermolecular or intramolecular bonds, and the stability of the thin film can be improved.

[0053] In addition, since the aggregation phenomenon due to nucleation is prevented, the material is coated in an amorphous form without the use of additives during spin coating, thereby improving sensitivity and coatability.

[0054] As an example, R 4 may be a substituted or unsubstituted branched alkyl group having 3 to 20 carbon atoms.

[0055] The branched alkyl group refers to a group in which the carbon atom bonded to the metal is a secondary carbon, a tertiary carbon or a quaternary carbon, and may be, for example, an iso-propyl group, an iso-butyl group, an iso-pentyl group, an iso-hexyl group, an iso-heptyl group, an iso-octyl group, an iso-nonyl group, an iso-decyl group, a sec-butyl group, a sec-pentyl group, a sec-hexyl group, a sec-heptyl group, a sec-octyl group, a tert-butyl group, a tert-pentyl group, a tert-hexyl group, a tert-heptyl group, a tert-octyl group, a tert-nonyl group or a tert-decyl group.

[0056] As an example, R 1 ~R 3 may each independently be a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof.

[0057] As a specific example, R 1 ~R 3may each independently be n-propyl, n-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, n-nonyl, n-decyl, iso-propyl, iso-butyl, iso-pentyl, iso-hexyl, iso-heptyl, iso-octyl, iso-nonyl, iso-decyl, sec-butyl, sec-pentyl, sec-hexyl, sec-heptyl, sec-octyl, tert-butyl, tert-pentyl, tert-hexyl, tert-heptyl, tert-octyl, tert-nonyl, or tert-decyl.

[0058] As an example, L in the above formula 1 1 ~L 3 may each independently be a single bond, or a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms.

[0059] As a specific example, L in the above formula 1 1 ~L 3 may each independently be a single bond, or a substituted or unsubstituted alkylene group having 1 to 10 carbon atoms.

[0060] For example, L in the above formula 1 1 ~L 3 may each independently be a single bond, or a substituted or unsubstituted alkylene group having 1 to 5 carbon atoms.

[0061] In one embodiment of the present invention, L in the above formula 1 1 ~L 3 may each independently be a single bond, a substituted or unsubstituted methylene group, a substituted or unsubstituted ethylene group, a substituted or unsubstituted trimethylene group, or a substituted or unsubstituted propylene group.

[0062] As an example, R a , R b , R c , R d , R e and Rf may each independently be a hydrogen atom, a halogen atom, or a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms.

[0063] As a specific example, R a , R b , R c , R d , R e and R f may each independently be a hydrogen atom, or a substituted or unsubstituted alkyl group having 1 to 5 carbon atoms.

[0064] For example, R in the above formula 1 a , R b , R c , R d , R e and R f may each independently be a hydrogen atom, a methyl group, an ethyl group, an n-propyl group, or an n-butyl group.

[0065] As an example, X in the above formula 1 2 , X 4 and X 6 may each be O.

[0066] As an example, X in the above formula 1 1 ~X 6 may each be O.

[0067] More specific examples of the organotin compound include the compounds listed in Group 1 below.

[0068] [ka]

[0069] The above organotin compound strongly absorbs extreme ultraviolet light with a wavelength of 13.5 nm and has excellent sensitivity to light having high energy.

[0070] In the semiconductor photoresist composition according to one embodiment of the present invention, the organotin compound may be contained in an amount of 1% by mass to 30% by mass, for example, 1% by mass to 25% by mass, for example, 1% by mass to 20% by mass, for example, 1% by mass to 15% by mass, for example, 1% by mass to 10% by mass, for example, 1% by mass to 5% by mass, based on the total mass of the semiconductor photoresist composition being 100% by mass, but is not limited thereto. When the organotin compound is contained in an amount within the above range, the storage stability and etching resistance of the semiconductor photoresist composition are improved, and the resolution characteristics are improved.

[0071] The composition for semiconductor photoresist according to one embodiment of the present invention contains the above-mentioned organotin compound, so that it is possible to provide a composition for semiconductor photoresist having excellent sensitivity and pattern formability.

[0072] The above-mentioned organotin compounds can be synthesized by appropriately referring to conventionally known synthesis methods. More specifically, those skilled in the art can easily synthesize them by referring to the synthesis methods described in the Examples.

[0073] The solvent contained in the semiconductor photoresist composition according to one embodiment of the present invention may be an organic solvent, and examples thereof include, but are not limited to, aromatic compounds (e.g., xylene, toluene, etc.), alcohols (e.g., 4-methyl-2-pentanol, 4-methyl-2-propanol, 1-butanol, methanol, isopropyl alcohol, 1-propanol, etc.), ethers (e.g., anisole, tetrahydrofuran, etc.), esters (n-butyl acetate, propylene glycol monomethyl ether acetate, ethyl acetate, ethyl lactate, etc.), ketones (e.g., methyl ethyl ketone, 2-heptanone, etc.), and mixtures thereof.

[0074] In one embodiment of the present invention, the composition for semiconductor photoresist may further include a resin in addition to the organotin compound and the solvent.

[0075] The resin may be a phenolic resin that contains at least one of the aromatic moieties listed in Group 2 below.

[0076] [ka]

[0077] The resin may have a weight average molecular weight of 500 to 20,000. The weight average molecular weight of the resin can be measured by gel permeation chromatography (GPC).

[0078] The resin may be contained in an amount of 0.1% by mass to 50% by mass relative to the total mass of the semiconductor resist composition.

[0079] When the resin is contained within the above content range, excellent etching resistance and heat resistance can be obtained.

[0080] Meanwhile, the semiconductor resist composition according to one embodiment of the present invention preferably comprises the above-mentioned organotin compound, solvent, and resin. However, the semiconductor resist composition according to the above-mentioned embodiment may further include additives, if necessary. Examples of the additives include a surfactant, a crosslinking agent, a leveling agent, an organic acid, a quencher, or a combination thereof.

[0081] The surfactant may be, for example, but is not limited to, an alkylbenzenesulfonate, an alkylpyridinium salt, a polyethylene glycol, a quaternary ammonium salt, or a combination thereof.

[0082] Examples of the crosslinking agent include, but are not limited to, melamine-based crosslinking agents, substituted urea-based crosslinking agents, acrylic-based crosslinking agents, epoxy-based crosslinking agents, or polymer-based crosslinking agents. Crosslinking agents having at least two crosslink-forming substituents, such as methoxymethylated glycoluril, butoxymethylated glycoluril, methoxymethylated melamine, butoxymethylated melamine, methoxymethylated benzoguanamine, butoxymethylated benzoguanamine, 4-hydroxybutyl acrylate, acrylic acid, urethane acrylate, acrylic methacrylate, 1,4-butanediol diglycidyl ether, glycidol, diglycidyl 1,2-cyclohexanedicarboxylate, trimethylpropane triglycidyl ether, 1,3-bis(glycidoxypropyl)tetramethyldisiloxane, methoxymethylated urea, butoxymethylated urea, or methoxymethylated thiourea, can be used.

[0083] The leveling agent is used to improve the coating flatness during printing, and any known leveling agent that is commercially available can be used.

[0084] The organic acid may be, but is not limited to, p-toluenesulfonic acid, benzenesulfonic acid, p-dodecylbenzenesulfonic acid, 1,4-naphthalenedisulfonic acid, methanesulfonic acid, fluorinated sulfonium salts, malonic acid, citric acid, propionic acid, methacrylic acid, oxalic acid, lactic acid, glycolic acid, succinic acid, or combinations thereof.

[0085] The quencher may be diphenyl(p-tolyl)amine, methyldiphenylamine, triphenylamine, phenylenediamine, naphthylamine, diaminonaphthalene, or combinations thereof.

[0086] The amount of these additives used can be easily adjusted depending on the desired physical properties, and they may not be added at all.

[0087] In addition, the semiconductor resist composition may further use a silane coupling agent as an adhesion promoter to improve adhesion to a substrate (for example, to improve adhesion of the semiconductor resist composition to a substrate). Examples of silane coupling agents include, but are not limited to, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltrichlorosilane, vinyltris(β-methoxyethoxy)silane; or 3-methacryloyloxypropyltrimethoxysilane, 3-acryloyloxypropyltrimethoxysilane, p-styryltrimethoxysilane, 3-methacryloyloxypropylmethyldimethoxysilane, 3-methacryloyloxypropylmethyldiethoxysilane; and carbon-carbon unsaturated bond-containing silane compounds such as trimethoxy[3-(phenylamino)propyl]silane.

[0088] The composition for semiconductor photoresist does not cause pattern collapse or hardly occurs even when a pattern having a high aspect ratio is formed. Therefore, for example, in order to form a fine pattern having a width of 5 nm to 100 nm, for example, a fine pattern having a width of 5 nm to 80 nm, for example, a fine pattern having a width of 5 nm to 70 nm, for example, a fine pattern having a width of 5 nm to 50 nm, for example, a fine pattern having a width of 5 nm to 40 nm, for example, a fine pattern having a width of 5 nm to 30 nm, for example, a fine pattern having a width of 5 nm to 20 nm, the composition can be used in a photoresist process using light with a wavelength of 5 nm to 150 nm, for example, a photoresist process using light with a wavelength of 5 nm to 100 nm, for example, a photoresist process using light with a wavelength of 5 nm to 80 nm, for example, a photoresist process using light with a wavelength of 5 nm to 50 nm, for example, a photoresist process using light with a wavelength of 5 nm to 30 nm, for example, a photoresist process using light with a wavelength of 5 nm to 20 nm. Therefore, by using the semiconductor photoresist composition according to one embodiment of the present invention, extreme ultraviolet lithography using an EUV light source with a wavelength of 13.5 nm can be realized.

[0089] Meanwhile, according to another embodiment of the present invention, there may be provided a method for forming a pattern using the above-mentioned semiconductor photoresist composition. For example, the pattern formed may be a photoresist pattern.

[0090] A method for forming a pattern according to an embodiment of the present invention includes the steps of forming a film to be etched on a substrate, applying the above-described semiconductor photoresist composition on the film to be etched to form a photoresist film, patterning the photoresist film to form a photoresist pattern, and etching the film to be etched using the photoresist pattern as an etching mask.

[0091] A method for forming a pattern using the above-mentioned semiconductor photoresist composition will be described below with reference to Figures 1 to 5. Figures 1 to 5 are schematic cross-sectional views for explaining the method for forming a pattern using the semiconductor photoresist composition according to the present invention.

[0092] Referring to FIG. 1, first, an object to be etched is prepared. An example of the object to be etched may be a thin film 102 formed on a semiconductor substrate 100. Hereinafter, only the case where the object to be etched is the thin film 102 will be described. The surface of the thin film 102 is cleaned to remove contaminants remaining on the thin film 102. The thin film 102 may be, for example, a silicon nitride film, a polysilicon film, or a silicon oxide film.

[0093] Next, a composition for forming a resist underlayer film is coated by spin coating on the surface of the cleaned thin film 102 to form a resist underlayer film 104. However, the present invention is not necessarily limited to this, and various known coating methods, such as spray coating, dip coating, knife edge coating, and printing methods such as inkjet printing and screen printing, can also be used.

[0094] The above-mentioned step of coating the resist underlayer film can be omitted, but the following describes the case where the resist underlayer film is coated.

[0095] Thereafter, drying and baking steps are performed to form a resist underlayer film 104 on the thin film 102. The baking process is performed at 100 to 500°C, for example, 100 to 300°C.

[0096] The resist underlayer film 104 can be formed between the substrate 100 and the photoresist film 106 to prevent radiation reflected from the interface between the substrate 100 and the photoresist film 106 or from the hard mask between the layers from scattering into unintended photoresist regions, resulting in non-uniformity of the photoresist linewidth and disruption of pattern formability.

[0097] 2, the above-mentioned semiconductor photoresist composition is coated on a resist underlayer film 104 to form a photoresist film 106. The photoresist film 106 may be in a form in which the above-mentioned semiconductor photoresist composition is coated on a thin film 102 formed on a substrate 100 and then cured by a heat treatment process.

[0098] More specifically, the step of forming a pattern using the semiconductor photoresist composition may include a step of applying the above-mentioned semiconductor resist composition onto the substrate 100 on which the thin film 102 is formed by a method such as spin coating, slit coating, inkjet printing, etc., and a step of drying the applied semiconductor photoresist composition to form a photoresist film 106.

[0099] The semiconductor photoresist composition has already been described in detail, so a duplicated description will be omitted.

[0100] Next, a first baking step is performed to heat the substrate 100 on which the photoresist film 106 is formed. The first baking step can be performed at a temperature of 80°C to 120°C.

[0101] Referring to FIG. 3, the photoresist film 106 is selectively exposed to light.

[0102] As an example, examples of light that can be used in the exposure process include light with short wavelengths such as i-line (wavelength 365 nm), KrF excimer laser (wavelength 248 nm), and ArF excimer laser (wavelength 193 nm), as well as light with high energy wavelengths such as EUV (Extreme UltraViolet; wavelength 13.5 nm) and E-Beam (electron beam).

[0103] More specifically, the light for exposure according to one embodiment of the present invention may be short-wavelength light having a wavelength range of 5 nm to 150 nm, or may be light having a high-energy wavelength such as EUV (Extreme UltraViolet; wavelength 13.5 nm) or E-Beam (electron beam).

[0104] The exposed regions 106b of the photoresist film 106 form a polymer through a crosslinking reaction such as condensation between organometallic compounds, and thus have a different solubility from the unexposed regions 106a of the photoresist film 106.

[0105] Next, a second baking step is performed on the substrate 100. The second baking step can be performed at a temperature of 90° C. to 200° C. By performing the second baking step, the exposed region 106b of the photoresist film 106 becomes less soluble in a developer.

[0106] 4 shows a photoresist pattern 108 formed by dissolving and removing the photoresist film 106a corresponding to the unexposed region using a developer. Specifically, the photoresist film 106a corresponding to the unexposed region is dissolved and then removed using an organic solvent such as 2-heptanone, thereby completing the photoresist pattern 108 corresponding to a negative tone image.

[0107] As described above, the developer used in the pattern formation method according to one embodiment of the present invention may be an organic solvent. Examples of the organic solvent used in the pattern formation method according to one embodiment of the present invention include ketones such as methyl ethyl ketone, acetone, cyclohexanone, and 2-heptanone, alcohols such as 4-methyl-2-propanol, 1-butanol, isopropanol, 1-propanol, and methanol, esters such as propylene glycol monomethyl ether acetate, ethyl acetate, ethyl lactate, n-butyl acetate, and γ-butyrolactone, aromatic compounds such as benzene, xylene, and toluene, or combinations thereof.

[0108] However, the photoresist pattern according to the present invention is not necessarily limited to being formed as a negative tone image, and may be formed to have a positive tone image. In this case, the developer that can be used to form a positive tone image includes a quaternary ammonium hydroxide composition such as tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, or a combination thereof.

[0109] As described above, the photoresist pattern 108 formed by exposure to light having a wavelength such as i-line (wavelength 365 nm), KrF excimer laser (wavelength 248 nm), ArF excimer laser (wavelength 193 nm), as well as high-energy light such as EUV (Extreme UltraViolet; wavelength 13.5 nm) and E-Beam (electron beam) can have a width of 5 nm to 100 nm. As an example, the photoresist pattern 108 can be formed to a width of 5 nm to 90 nm, 5 nm to 80 nm, 5 nm to 70 nm, 5 nm to 60 nm, 5 nm to 50 nm, 5 nm to 40 nm, 5 nm to 30 nm, or 5 nm to 20 nm.

[0110] On the other hand, the photoresist pattern 108 may have a half pitch of 50 nm or less, such as 40 nm or less, such as 30 nm or less, such as 20 nm or less, such as 15 nm or less, and a line width roughness of 10 nm or less, 5 nm or less, 3 nm or less, 2 nm or less.

[0111] Next, the resist underlayer film 104 is etched using the photoresist pattern as an etching mask. Through the above etching process, an organic layer pattern 112 is formed. The formed organic layer pattern 112 may also have a width corresponding to the photoresist pattern .

[0112] 5, the photoresist pattern 108 is used as an etching mask to etch the exposed thin film 102. As a result, the thin film 102 is formed as a thin film pattern 114.

[0113] The thin film 102 can be etched by dry etching using an etching gas such as CHF3, CF4, Cl2, BCl3, or a mixture thereof.

[0114] The thin film pattern 114 formed using the photoresist pattern 108 formed in the exposure process performed using the EUV light source may have a width corresponding to the photoresist pattern 108. As an example, it may have a width of 5 nm to 100 nm, similar to the photoresist pattern 108. For example, the thin film pattern 114 formed by the exposure process performed using the EUV light source may have a width of 5 nm to 90 nm, 5 nm to 80 nm, 5 nm to 70 nm, 5 nm to 60 nm, 5 nm to 50 nm, 5 nm to 40 nm, 5 nm to 30 nm, or 5 nm to 20 nm, similar to the photoresist pattern 108, and more specifically, may be formed to a width of 20 nm or less. EXAMPLES

[0115] The present invention will be described in more detail with reference to the following examples of preparing the above-mentioned semiconductor photoresist composition, but the technical features of the present invention are not limited to the following examples.

[0116] (Synthesis of organotin compounds) (Synthesis Example 1) In a 250mL two-neck round-bottom flask, 320g (64.7mmol) of tert-BuSn[N(CH3)2] was dissolved in 200ml of toluene, and the temperature was lowered to -20℃ using a dry ice bath. Then, 14.8g (200.0mmol) of 2-methoxyethanol was gradually added dropwise, and the temperature was gradually raised to room temperature. After that, the mixture was refluxed at 120℃ for 6 hours to obtain the compound tert-BuSn(O(CH2)2OCH3)3 represented by the following chemical formula 1a.

[0117] [ka]

[0118] (Synthesis Example 2) The same procedure as in Synthesis Example 1 was carried out, except that 18 g (200.0 mmol) of 1-methoxypropanol was used instead of 2-methoxyethanol, to obtain a compound represented by the following chemical formula 2a, tert-BuSn(O(iPr)OCH3)3.

[0119] [ka]

[0120] (Synthesis Example 3) The same procedure as in Synthesis Example 1 was repeated, except that 18 g (200.0 mmol) of 3-methoxypropanol was used instead of 2-methoxyethanol, to obtain a compound represented by the following formula 3a, tert-BuSn(O(CH2)3OCH3)3.

[0121] [ka]

[0122] (Comparative Synthesis Example 1) In a 250mL two-neck round-bottom flask, 20g (51.9mmol) of Ph3SnCl was dissolved in 70ml of THF, and the temperature was lowered to 0°C in an ice bath. Then, 1M THF solution (62.3mmol) of tert-butyl magnesium chloride (tert-BuMgCl) was slowly added dropwise. After the addition was completed, the mixture was stirred at 25°C for 12 hours to obtain the BuSnPh3 compound.

[0123] Then, BuSnPh3 (10 g, 24.6 mmol) was dissolved in 50 mL of CH2Cl2, and 3 equivalents of 2 M HCl diethyl ether solution (73.7 mmol) was slowly added dropwise for 30 minutes at -78 ° C. After stirring for 12 hours at 25 ° C, the solvent was concentrated and vacuum distilled to obtain the BuSnCl3 compound.

[0124] Then, 25 mL of propionic acid was gradually added dropwise to 10 g (25.6 mmol) of the compound at 25° C., and the mixture was heated under reflux for 12 hours. After raising the temperature to 25° C., acetic acid was distilled off under vacuum to finally obtain the tert-BuSn(OCOC2H5)3 compound.

[0125] (Comparative Synthesis Example 2) In a 250mL two-neck round-bottom flask, 20g (77mmol) of SnCl4 was dissolved in 100ml of toluene, and the temperature was lowered to -30℃ using a dry ice bath. Then, 77mmol of tert-BuLi (1.7M pentane solution) was gradually added dropwise, and the temperature was gradually raised to room temperature. Then, the temperature was lowered again to -30℃ using a dry ice bath, and 17.4g (220mmol) of lithium diethylamide weighed in a glove box in an argon atmosphere was dissolved in THF, and then decantation was gradually performed using a cannula made of PTFE material. After stirring for 3 hours while gradually raising the temperature to room temperature, filtration was performed using a glass filter (G4) in an Ar atmosphere. The solvent was removed using a vacuum, and the compound tert-BuSn[N(C2H5)2]3 was obtained.

[0126] (Comparative Synthesis Example 3) The compound tert-BuSn(OC2H5)3 was obtained in the same manner as in Synthesis Example 1, except that 9.214 g (200.0 mmol) of ethanol was used instead of 2-methoxyethanol.

[0127] (Examples 1 to 5 and Comparative Examples 1 to 3: Production of Semiconductor Photoresist Compositions) The compounds obtained in Synthesis Examples 1 to 3 and Comparative Synthesis Examples 1 to 3 were dissolved in 1-methyl-2-propyl acetate at a concentration of 3 mass% in the mass ratios shown in Table 1 below, and filtered through a 0.1 μm PTFE (polytetrafluoroethylene) syringe filter to produce semiconductor photoresist compositions.

[0128] [Table 1]

[0129] (Photoresist film formation) An 8-inch circular silicon wafer having a native oxide film surface was used as a substrate for thin film deposition, and the wafer was treated in a UV ozone cleaning system for 10 minutes before the thin film was deposited. The semiconductor photoresist compositions according to Examples 1 to 5 and Comparative Examples 1 to 3 were spin-coated on the treated substrate at 1500 rpm for 30 seconds, and baked at 160° C. for 60 seconds (post-bake, PAB) to form a thin film.

[0130] The thickness of the film after coating and baking was then measured by ellipsometry to be 25 nm.

[0131] (Evaluation 1: Coating property evaluation) The surface roughness (Rq value) of the photoresist films prepared by the coating method according to Examples 1 to 5 and Comparative Examples 1 to 3 was measured using an atomic force microscope (AFM), and the results are shown in Table 2 below.

[0132] (Evaluation 2: Sensitivity and Line Edge Roughness (LER) Evaluation) EUV light was projected onto a wafer coated with the photoresist compositions of Examples 1 to 5 and Comparative Examples 1 to 3 using a Lawrence Berkeley National Laboratory Micro Exposure Tool (MET) in a linear array of 50 circular pads with a diameter of 500 μm. Pad exposure time was adjusted so that an increased EUV dose was applied to each pad.

[0133] The resist and substrate were then post-exposure baked (PEB) on a hotplate at 160°C for 120 seconds. The baked films were then immersed in a developer (2-heptanone) for 30 seconds each, and then washed in the same developer for an additional 10 seconds to produce a negative tone image, i.e., to remove the unexposed coating parts. A final hotplate bake at 150°C for 2 minutes completed the process.

[0134] The thickness of the remaining resist film on the exposed pads was measured using ellipsometry. The remaining thickness was measured against the exposure dose and graphed as a function of the exposure dose. Dg (energy level at which development is complete, sensitivity) was measured for each type of resist and is shown in Table 2 below.

[0135] In addition, the line edge roughness (LER) of the formed lines, as confirmed from images taken with a field emission scanning electron microscope (FE-SEM), was measured, and the results are shown in Table 2 below.

[0136] (Evaluation 3: Storage stability evaluation) For the semiconductor photoresist compositions prepared in Examples 1 to 5 and Comparative Examples 1 to 3, the initial sensitivity value and the sensitivity value after leaving the composition at room temperature (25°C) for 4 weeks were measured, and the storage stability was evaluated according to the following formula. The lower the value of Formula 1 below, the better the storage stability.

[0137]

number

[0138] [Table 2]

[0139] From the results in Table 2, it can be seen that the semiconductor photoresist compositions of Examples 1 to 5 have excellent coating properties and storage stability, and the patterns formed from these semiconductor photoresist compositions have excellent sensitivity without a significant increase in line edge roughness compared to Comparative Examples 1 to 3.

[0140] Although specific embodiments of the present invention have been described and illustrated above, the present invention is not limited to the described embodiments, and it is obvious to those skilled in the art that various modifications and variations can be made without departing from the spirit and scope of the present invention. Therefore, such modifications or variations should not be understood individually from the technical spirit and perspective of the present invention, and the modified embodiments should be considered to belong to the scope of the claims of the present invention. [Explanation of symbols]

[0141] 100 Substrates 102 Thin Film 104 Resist underlayer film 106 Photoresist film 106a Unexposed Area 106b Exposed area 108 Photoresist pattern 112 Organic film pattern 110 Patterned hard mask 114 Thin film pattern

Claims

1. An organotin compound represented by the following chemical formula 1: solvent A composition for a semiconductor photoresist comprising: 【Chemistry 1】 In the above chemical formula 1, X １ ~X ６ is O, L １ ~L ３ each independently represents a substituted or unsubstituted alkylene group having 1 to 5 carbon atoms, R ａ , R ｂ , R ｃ , R ｄ , R ｅ and R f is a hydrogen atom; R 1 to R 3 each independently represent a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms; R ４ is a substituted or unsubstituted branched alkyl group having 3 to 20 carbon atoms.

2. The semiconductor photoresist composition according to claim 1, wherein R 4 in Chemical Formula 1 is a tert-butyl group.

3. R in Formula 1 １ ~R ３ are each independently an n-propyl group, an n-butyl group, an n-pentyl group, an n-hexyl group, an n-heptyl group, an n-octyl group, an n-nonyl group, an n-decyl group, an isopropyl group, an isobutyl group, an isopentyl group, an isohexyl group, an isoheptyl group, an isooctyl group, an isononyl group, an isodecyl group, a sec-butyl group, a sec-pentyl group, a sec-hexyl group, a sec-heptyl group, a sec-octyl group, a tert-butyl group, a tert-pentyl group, a tert-hexyl group, a tert-heptyl group, a tert-octyl group, a tert-nonyl group, or a tert-decyl group.

4. 2. The semiconductor photoresist composition according to claim 1, wherein the organotin compound is one selected from the group of compounds listed in Group 1 below. 【Chemistry 2】

5. 2. The semiconductor photoresist composition according to claim 1, wherein the content of the organotin compound is 1% by mass to 30% by mass, based on 100% by mass of the total mass of the semiconductor photoresist composition.

6. 10. The semiconductor photoresist composition of claim 1, further comprising an additive of a surfactant, a crosslinking agent, a leveling agent, or a combination thereof.

7. forming a film to be etched on a substrate; A step of forming a photoresist film by applying the composition for a semiconductor photoresist according to any one of claims 1 to 6 onto the film to be etched; patterning the photoresist film to form a photoresist pattern; and The method of forming a pattern includes etching the layer to be etched using the photoresist pattern as an etching mask.

8. 8. The method of claim 7, wherein the step of forming the photoresist pattern uses light having a wavelength of 5 nm to 150 nm.

9. The pattern forming method according to claim 7 , further comprising the step of forming a resist underlayer film between the substrate and the photoresist film.

10. 8. The pattern forming method according to claim 7, wherein the photoresist pattern has a width of 5 nm to 100 nm.