Photoresist development with organic vapors.

Abstract

Resist development is useful, for example, for forming patterning masks in high-resolution patterning applications. Development can be achieved using an organic vapor, such as a carboxylic acid. In some embodiments, the organic vapor is trifluoroacetic acid. In some embodiments, the organic vapor is hexafluoroacetylacetone. Metal-containing resist films, such as EUV-sensitive organometallic oxides, can be deposited on semiconductor substrates using dry or wet deposition techniques. Metal-containing resist films on semiconductor substrates can be developed using organic vapors, or residues of metal-containing resist materials formed on process chamber surfaces can be removed using organic vapors.

Description

[Technical field]

[0001] Incorporation by Reference A PCT application is being filed contemporaneously herewith as a part of this application, and each application identified in that contemporaneously filed PCT application to which this application claims benefit or priority is hereby incorporated by reference in its entirety for all purposes. [Background technology]

[0002] Fabrication of semiconductor devices, such as integrated circuits, is a multi-step process that involves photolithography. In general, the process involves deposition of material on a wafer and patterning the material by lithographic techniques to form structural features (e.g., transistors and circuits) of the semiconductor device. Typical photolithography process steps known in the art include preparing a substrate on which a photoresist is applied, such as by spin coating, exposing the photoresist to light in a desired pattern to render the exposed areas of the photoresist somewhat soluble in a developer, developing by applying a developer to remove either the exposed or unexposed areas of the photoresist, and subsequent processing, such as by etching or material deposition, to form features on the areas of the substrate from which the photoresist was removed.

[0003] The evolution of semiconductor design is driven by the need for, and ability to, form ever smaller features on semiconductor substrate materials. This technological advance is characterized in "Moore's Law" as the doubling of transistor density in high-density integrated circuits every two years. In fact, chip design and manufacturing have advanced such that modern microprocessors can contain billions of transistors and other circuit features on a single chip. Individual features on such chips can be on the order of 22 nanometers (nm) or less, and in some cases less than 10 nm.

[0004] One challenge in fabricating devices with such small features is the ability to reliably and reproducibly form photolithography masks with sufficient resolution. Current photolithography processes typically use 193 nm ultraviolet (UV) light to expose photoresist. The fact that the light has a wavelength significantly longer than the desired size of the features to be created on the semiconductor substrate creates inherent problems. Achieving feature sizes smaller than the wavelength of the light requires the use of complex resolution enhancement techniques such as multi-patterning. Thus, there has been great interest and research effort in developing photolithography techniques that use short wavelength light, such as extreme ultraviolet (EUV) light, with wavelengths of 10 nm to 15 nm, e.g., 13.5 nm.

[0005] However, EUV photolithography processes can have challenges such as reduced power and loss of light during patterning. Conventional organic chemically amplified resists (CARs), similar to those used in 193 nm UV lithography, have potential drawbacks when used in EUV lithography because they have low absorption coefficients, especially in the EUV region, and diffusion of photoactivated chemical species can result in blurring or line edge roughness. Furthermore, to provide the etch resistance required to pattern underlying device layers, small features patterned with conventional CAR materials can result in high aspect ratios with risk of pattern collapse. Thus, there remains a need for improved EUV photoresist materials with properties such as reduced thickness, greater absorbance, and greater etch resistance.

[0006] The background description provided herein is intended to provide a general overview of the present technology. Work by the currently named inventors within the scope of what is described in this Background section, as well as aspects of the description that may not otherwise be considered prior art at the time of filing, are not admitted, expressly or impliedly, as prior art against the present technology. Summary of the Invention

[0007] Provided herein is a method of developing a photo-patterned metal-containing resist, the method including providing a photo-patterned metal-containing resist on a surface of a semiconductor substrate in a process chamber, and dry developing the resist by selectively removing portions of the photo-patterned metal-containing resist by exposure to a developing chemistry that includes an organic vapor to form a resist mask.

[0008] In some embodiments, the organic vapor comprises a carboxylic acid. In some embodiments, the organic vapor comprises trifluoroacetic acid. In some embodiments, the organic vapor comprises trifluoroacetic anhydride, acetic anhydride, trichloroacetic acid, monofluoroacetic acid, difluoroacetic acid, chlorodifluoroacetic acid, thioacetic acid, or thioglycolic acid. In some embodiments, the organic vapor comprises hexafluoroacetylacetone. In some embodiments, the developing chemical comprises a gas phase mixture of a halogenated carboxylic acid and a hydrogen halide. In some embodiments, dry developing the photo-patterned metal-containing resist comprises reacting an organic vapor with the photo-patterned metal-containing resist to form a volatile compound at a temperature less than about 200° C. In some embodiments, dry developing the photo-patterned metal-containing resist comprises exposing to at least an organic vapor in a plasma-free thermal process. In some embodiments, the photo-patterned metal-containing resist is a photo-patterned metal-containing EUV resist, and the photo-patterned metal-containing EUV resist is an organometallic oxide or an organometallic film. In some embodiments, dry developing the photopatterned metal-containing resist includes using a developer chemistry to selectively remove the EUV unexposed portions of the resist relative to the EUV exposed portions to form a resist mask.

[0009] A method of removing residue from one or more surfaces of a process chamber is also provided, the method including depositing a metal-containing resist material on a surface of a semiconductor substrate in a process chamber, where a portion of the metal-containing resist material forms a residue on the one or more surfaces of the process chamber, and introducing a dry etchant comprising an organic vapor into the process chamber, where the dry etchant at least partially removes the residue on the one or more surfaces of the process chamber.

[0010] In some embodiments, the organic vapor comprises a carboxylic acid. In some embodiments, the organic vapor comprises trifluoroacetic acid. In some embodiments, the organic vapor comprises trifluoroacetic anhydride, acetic anhydride, trichloroacetic acid, monofluoroacetic acid, difluoroacetic acid, chlorodifluoroacetic acid, thioacetic acid, or thioglycolic acid. In some embodiments, the organic vapor comprises hexafluoroacetylacetone. In some embodiments, the dry etchant comprises a gas phase mixture of a halogenated carboxylic acid and a hydrogen halide. In some embodiments, the at least partial removal of the residue comprises reacting the organic vapor with the metal-containing resist material to form a volatile compound at a temperature less than about 200° C. In some embodiments, the at least partial removal of the residue comprises exposing the organic vapor to at least a plasma-free thermal process. In some embodiments, the metal-containing resist material is an organometallic oxide or an organometallic-containing film. In some embodiments, the method further includes purging the process chamber after introducing the dry etchant to remove residual dry etchant from the process chamber, and conditioning one or more surfaces of the process chamber by forming a protective coating of a metal-containing resist material on the one or more surfaces of the process chamber. [Brief description of the drawings]

[0011] [Figure 1] FIG. 1 is a flow diagram of an exemplary method for depositing and developing photoresist, according to some embodiments.

[0012] [Diagram 2] FIG. 2 is a flow diagram of an exemplary method for dry developing a metal-containing resist, according to some embodiments.

[0013] [Figure 3A] FIG. 3A is a cross-sectional schematic diagram of various processing stages of dry development, according to some embodiments. [Figure 3B] FIG. 3B is a cross-sectional schematic diagram of various processing stages of dry development, according to some embodiments. [Figure 3C] 3A-3C are cross-sectional schematic diagrams of various processing stages of dry development, according to some embodiments.

[0014] [Figure 4A] FIG. 4A is a cross-sectional schematic diagram of dry development without application of an inert gas plasma, according to some embodiments.

[0015] [Figure 4B] FIG. 4B is a cross-sectional schematic diagram of a dry development cycle inert gas plasma for descumming, according to some embodiments.

[0016] [Diagram 5] FIG. 5 is a flow diagram of an exemplary method for dry chamber cleaning, according to some embodiments.

[0017] [Figure 6A] FIG. 6A is a cross-sectional schematic diagram of various process stages of dry chamber cleaning, according to some embodiments. [Figure 6B] 6A-6B are cross-sectional schematic diagrams of various processing stages of dry chamber cleaning, according to some embodiments. [Figure 6C] 6A-6C are cross-sectional schematic diagrams of various processing stages of dry chamber cleaning according to some embodiments. [Figure 6D]6A-6D are cross-sectional schematic diagrams of various processing stages of dry chamber cleaning according to some embodiments.

[0018] [Figure 7] FIG. 7 is a schematic diagram of an exemplary process station suitable for performing dry development, cleaning, rework, descum, and smoothing operations according to some embodiments.

[0019] [Figure 8] FIG. 8 is a schematic diagram of an exemplary multi-station processing tool suitable for performing the various dry development, cleaning, rework, descum, and smoothing operations described herein.

[0020] [Figure 9] FIG. 9 is a cross-sectional schematic diagram of an exemplary inductively coupled plasma apparatus for carrying out certain embodiments and operations described herein.

[0021] [Figure 10] FIG. 10 illustrates a semiconductor process cluster tool architecture having a vacuum integrated deposition and patterning module interfaced with a vacuum transfer module suitable for carrying out the processes described herein.

[0022] [Figure 11A] FIG. 11A is a cross-sectional schematic diagram of an example dry deposition apparatus, according to some embodiments.

[0023] [Figure 11B] FIG. 11B illustrates a detailed cross-sectional side view and a plan view of a portion of a top plate, substrate, and edge ring of a dry deposition apparatus, according to some embodiments. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] The present disclosure generally relates to the field of semiconductor processing. In certain aspects, the present disclosure is directed to processes and apparatus for developing photoresists (e.g., EUV-sensitive metal and / or metal oxide-containing photoresists) using organic vapors, such as organic acids, to form patterning masks, for example, in EUV patterning or other wavelength patterning situations. Although the following description focuses on EUV photoresists, it will be apparent that the photoresists described herein may also be suitable for use with other wavelengths of radiation, and the techniques and apparatus described herein are not limited to only the production of EUV photoresists.

[0025] Reference will be made in detail herein to certain embodiments of the present disclosure. Examples of certain embodiments are illustrated in the accompanying drawings. Although the present disclosure will be described in conjunction with these specific embodiments, it will be understood that it is not intended to limit the present disclosure to such specific embodiments. On the contrary, it is intended to cover alternatives, modifications, and equivalents that may be included within the spirit and scope of the present disclosure. In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present disclosure. The present disclosure may be practiced without some or all of these specific details. In other instances, well-known process operations have not been described in detail so as not to unnecessarily obscure the present disclosure.

[0026] Introduction Patterning of thin films in semiconductor processing is often a critical step in the manufacture of semiconductors. Patterning involves lithography. In traditional photolithography, such as 193 nm photolithography, a pattern is printed by emitting photons from a photon source onto a mask and printing the pattern onto a light-sensitive photoresist, thereby causing a chemical reaction within the photoresist that, after development, removes certain portions of the photoresist to form the pattern.

[0027] Advanced technology nodes (as defined by the International Technology Roadmap for Semiconductors) include the 22 nm, 16 nm, and beyond. For example, at the 16 nm node, a typical via or line width in a damascene structure is typically about 30 nm or less. The scaling of features on advanced semiconductor integrated circuits (ICs) and other devices drives lithography to improve resolution.

[0028] Extreme ultraviolet (EUV) lithography can extend lithography techniques by moving to shorter imaging source wavelengths than are achievable with traditional photolithography methods. EUV sources with wavelengths of approximately 10-20 nm, or 11-14 nm, for example 13.5 nm, can be used for state-of-the-art lithography tools, also called scanners. EUV radiation is strongly absorbed by a wide range of solid and fluid materials, including quartz and water vapor, and therefore operates in a vacuum.

[0029] EUV lithography utilizes an EUV resist that is patterned to form a mask for use in etching the underlying layer. The EUV resist may be a polymer-based chemically amplified resist (CAR) obtained by a liquid-based spin-on technique. An alternative to CAR is a directly photopatternable metal oxide-containing film, such as those available from Inpria, Corvallis, Oregon, and described in, for example, US Patent Application Publication No. 2017 / 0102612, US Patent Application Publication No. 2016 / 021660, and US Patent Application Publication No. 2016 / 0116839, which are incorporated herein by reference at least for their disclosure of photopatternable metal oxide-containing films. Such films may be provided by spin-on techniques or dry vapor deposition. Metal oxide-containing films can be patterned directly (i.e., without the use of a separate photoresist) by EUV exposure in a vacuum atmosphere providing patterning resolution of less than 30 nm, as described, for example, in U.S. Patent No. 9,996,004, issued June 12, 2018, and entitled EUV PHOTOPATTERNING OF VAPOR-DEPOSITED METAL OXIDE-CONTAINING HARDMASKS, and / or International Patent Application No. PCT / US2019 / 31618, filed May 9, 2019, and entitled METHODS FOR MAKING EUV PATTERNABLE HARD MASKS, the disclosures above relating at least to the composition, deposition, and patterning of directly photopatternable metal oxide films to form EUV resist masks are incorporated herein by reference. In general, patterning involves exposing an EUV resist to EUV radiation to form a photopattern in the resist, followed by development to remove portions of the resist according to the photopattern to form a mask.

[0030] It should also be understood that the present disclosure relates to lithographic patterning techniques and materials exemplified by EUV lithography, but is also applicable to other next-generation lithographic techniques. In addition to EUV, including the standard 13.5 nm EUV wavelength currently in use and being developed, the most relevant radiation sources for such lithography are DUV (deep UV), which generally refers to the use of 248 nm or 193 nm excimer laser sources, X-ray, formally including EUV in the lower energy range of the X-ray range, and e-beam, which can cover a wide energy range. The particular method may depend on the particular materials and applications used in the semiconductor substrate and the final semiconductor device. Thus, the methods described in this application are merely exemplary of the methods and materials that may be used in the present technology.

[0031] Directly photopatternable EUV resists may consist of or contain metals and / or metal oxides mixed within an organic component. Metals / metal oxides hold great promise in that they can enhance the absorption of EUV photons, generate secondary electrons, and / or exhibit high etch selectivity to the underlying film stack and device layers. To date, these resists have been developed using wet (solvent) approaches, which require the wafer to travel on a track where it is exposed to a developing solvent, dried, and baked. Wet development not only limits productivity, but can also cause line collapse due to surface tension effects and / or delamination.

[0032] Dry development techniques have been proposed to overcome these problems by eliminating substrate delamination and interfacial defects. Dry development can improve performance at narrower line widths (e.g., by preventing surface tension line collapse and delamination seen in wet development) and potentially increase throughput (e.g., by avoiding the need for wet development tracks). Other advantages may include the elimination of the use of organic solvent developers, reduced sensitivity to underlayer adhesion, and elimination of limitations based on solubility. Dry development offers further tunability and is also capable of critical dimension (CD) control and scum removal.

[0033] Dry development has its own challenges including etch selectivity between unexposed and EUV-exposed resist materials, which can result in higher dose to size requirements for effective resist exposure when compared to wet development. Suboptimal selectivity can also lead to rounded PR corners due to reduced contrast at the feature edges, which can increase line CD variability in the subsequent transfer etch step.

[0034] Dry removal of metal-containing resist According to various aspects of the present disclosure, the photopatterned metal-containing photoresist is developed by exposure to a vapor of an organic acid or other gas-phase precursor. An EUV-sensitive metal or metal oxide-containing film, such as an organotin oxide, is disposed on a semiconductor substrate. The EUV-sensitive metal or metal oxide-containing film is directly patterned by EUV exposure in a vacuum atmosphere. The pattern is then developed using a development chemistry to form a resist mask. In some embodiments, the development chemistry is a dry development chemistry. In some embodiments, the dry development chemistry includes an organic vapor, such as trifluoroacetic acid. Such dry development techniques can be performed using either a gentle plasma (high pressure, low power) or non-plasma thermal process while flowing the organic vapor. Additionally or alternatively, the present disclosure provides for dry chamber cleaning of EUV resist material or metal-containing resist material from the interior surfaces of a process chamber by exposure to an organic acid or other gas-phase precursor. In some embodiments, the organic vapor is trifluoroacetic acid. The dry cleaning can be a non-plasma thermal based cleaning operation. The dry chamber clean can be performed in any process chamber used for deposition, bevel edge, and / or backside cleaning, bake, develop, or etch operations.

[0035] Various embodiments of the present disclosure can include combining all dry operations with vapor deposition, EUV lithography patterning, and dry development. Various other embodiments include a combination of wet and dry processing operations, for example, spin-on EUV photoresist (wet process) can be combined with dry development or other wet or dry processes as described herein. Also described are various post-deposition (or post-application) processes such as bevel and backside cleaning, chamber cleaning, descumming, smoothing, curing to modify and enhance film properties, and photoresist rework processes.

[0036] FIG. 1 illustrates a flow diagram of an exemplary method for depositing and developing photoresist, according to some embodiments. The operations of process 100 may be performed in a different order and / or with a different, fewer, or additional number of operations. Aspects of process 100 may be described with reference to FIGS. 2, 3A-3C, 4A-4B, 5, and 6A-6D. One or more operations of process 100 may be performed using an apparatus described in any one of FIGS. 7-11B. In some embodiments, the operations of process 100 may be implemented, at least in part, according to software stored in one or more non-transitory computer-readable media. In some embodiments, a dry chamber clean may be performed after deposition, backside clean and bevel edge clean, post-apply bake, post-exposure bake, or dry develop.

[0037] In block 102 of process 100, a layer of photoresist is deposited. This can be either a dry deposition process, such as a vapor deposition process, or a wet process, such as a spin-on deposition process.

[0038] The photoresist may be a metal-containing EUV resist. The EUV-sensitive metal or metal oxide-containing film may be deposited on the semiconductor substrate by any suitable technique, including wet (e.g., spin-on) or dry (e.g., CVD) deposition techniques. For example, the described process is demonstrated for organotin oxide-based EUV photoresist compositions, and is applicable to both commercially available spin-coatable formulations (e.g., formulations available from Inpria Corp, Corvallis, Oregon) and formulations applied using dry vacuum deposition techniques, as further described below.

[0039] The semiconductor substrate may include any material structure suitable for photolithography processing, particularly for the production of integrated circuits and other semiconductor devices. In some implementations, the semiconductor substrate is a silicon wafer. The semiconductor substrate may be a silicon wafer on which features with irregular surface topography ("underlying features") are formed. As referred to herein, the "surface" is the surface on which the film of the present disclosure is deposited or the surface that is exposed to EUV during processing. The underlying features may include areas where material has been removed (e.g., by etching) or where material has been added (e.g., by deposition) during processing prior to performing the method of the present disclosure. Such pre-processing may include the method of the present disclosure or other processing methods in an iterative process in which two or more layers of features are formed on the substrate.

[0040] EUV-sensitive thin films can be deposited on semiconductor substrates, and such films can act as resists for subsequent EUV lithography and processing. Such EUV-sensitive thin films include materials that, upon exposure to EUV, undergo changes such as loss of bulky pendant substituents bonded to metal atoms in low-density M-OH-rich materials, allowing crosslinking to higher-density MOM-bonded metal oxide materials. Through EUV patterning, regions of the film are formed that have altered physical or chemical properties compared to unexposed regions. These properties can be exploited in subsequent processing, such as to dissolve either the unexposed or exposed regions, or to selectively deposit material in either the exposed or unexposed regions. In some implementations, the unexposed film has a more hydrophobic surface than the exposed film under the conditions in which such subsequent processing is performed. For example, removal of material may be performed by exploiting differences in the chemical composition, density, and crosslinking of the film. Removal can be performed by wet or dry processing, as further described below.

[0041] In various embodiments, the thin film is an organometallic material, such as an organotin material including tin oxide, or other metal oxide material / moiety. The organometallic compound can be made by gas phase reaction of an organometallic precursor and a reverse reactant. In various embodiments, the organometallic compound is formed by mixing a specific combination of organometallic precursors having bulky alkyl or fluoroalkyl groups with a reverse reactant and polymerizing the mixture in the gas phase to generate a low density EUV sensitive material that is deposited on the semiconductor substrate.

[0042] In various embodiments, the organometallic precursors include at least one alkyl group on each metal atom that can survive the gas phase reaction, but other ligands or ions coordinated to the metal atom can be replaced by counter reactants. The organometallic precursors include those of the formula: M a R b L c (Formula 1)

[0043] where M is an element having a high patterning radiation absorption cross section and R is C n H 2n+1 and the like, preferably n=1-6, L is a ligand, ion, or other moiety that reacts with the reverse reactant, and a≧1, b≧1, and c≧1. In various embodiments, M is 1×10 7 cm 2 M may be, for example, selected from the group consisting of tin, hafnium, tellurium, bismuth, indium, antimony, iodine, germanium, and combinations thereof. In some embodiments, M is tin. R may be, for example, a compound of the formula C n F x H (2n+1)In various embodiments, R has at least one beta hydrogen or beta fluorine. For example, R can be selected from the group consisting of methyl, ethyl, i-propyl, n-propyl, t-butyl, i-butyl, n-butyl, sec-butyl, n-pentyl, i-pentyl, t-pentyl, sec-pentyl, and mixtures thereof. L can be any moiety that is readily displaced by a reverse reactant to produce an M-OH moiety, such as a moiety selected from the group consisting of amines (dialkylamino, monoalkylamino, etc.), alkoxy, carboxylate, halogen, and mixtures thereof.

[0044] The organometallic precursor may be any of a wide variety of candidate metal organic precursors. For example, when M is tin, such precursors include t-butyltris(dimethylamino)tin, i-butyltris(dimethylamino)tin, n-butyltris(dimethylamino)tin, sec-butyltris(dimethylamino)tin, i-propyl(tris)dimethylaminotin, n-propyltris(dimethylamino)tin, ethyltris(dimethylamino)tin, and similar alkyl(tris)(t-butoxy)tin compounds, such as t-butyltris(t-butoxy)tin. In some embodiments, the organometallic precursor is partially fluorinated.

[0045] The reverse reactant has the ability to replace a reactive moiety, ligand, or ion (e.g., L in Formula 1 above) to link at least two metal atoms via a chemical bond. The reverse reactant may include water, peroxides (e.g., hydrogen peroxide), dihydroxy or polyhydroxy alcohols, fluorinated dihydroxy or polyhydroxy alcohols, fluorinated glycols, and other sources of hydroxyl moieties. In various embodiments, the reverse reactant reacts with the organometallic precursor by forming an oxygen bridge between adjacent metal atoms. Other potential reverse reactants include hydrogen sulfide and hydrogen disulfide, which can bridge metal atoms via sulfur bridges.

[0046] The thin films may include optional materials in addition to the organometallic precursors and back reactants to modify the chemical or physical properties of the film, such as modifying the film's sensitivity to EUV or enhancing its etch resistance. Such optional materials may be introduced, such as by doping during vapor phase formation, before deposition on the semiconductor substrate, after deposition of the thin film, or both. In some implementations, mild remote H 2 By introducing plasma, some Sn-L bonds can be replaced with Sn-H bonds, which can increase the reactivity of the resist under EUV.

[0047] In various embodiments, the EUV patternable film is prepared and deposited on the semiconductor substrate using vapor deposition equipment and processes known in the art.In such processes, polymerized organometallic materials are formed in vapor phase or in situ on the surface of the semiconductor substrate.Suitable processes include, for example, chemical vapor deposition (CVD), atomic layer deposition (ALD), and ALD using CVD components, such as discontinuous ALD-like processes in which metal precursors and counter-reactants are separated in either time or space.

[0048] In general, the method includes mixing a vapor flow of an organometallic precursor with a vapor flow of a reverse reactant to form a polymerized organometallic material and depositing the organometallic material onto a surface of a semiconductor substrate. In some embodiments, multiple organometallic precursors are included in the vapor flow. In some embodiments, multiple reverse reactants are included in the vapor flow. As will be appreciated by those skilled in the art, the mixing and deposition aspects of the process can occur simultaneously in a substantially continuous process.

[0049] In an exemplary continuous CVD process, two or more gas streams of a source of organometallic precursor and a reverse reactant are introduced in separate inlet paths into a deposition chamber of a CVD apparatus where they mix and react in the gas phase to form a coagulated polymeric material (e.g., via metal-oxygen-metal bond formation). The gas streams can be introduced, for example, using separate injection inlets or a dual plenum showerhead. The apparatus is configured so that the flows of organometallic precursor and reverse reactant are mixed in the chamber, thereby allowing the organometallic precursor and reverse reactant to react to form a polymerized organometallic material. Without limiting the mechanism, function, or utility of the present technology, it is believed that the products from such gas phase reactions become heavier in molecular weight as metal atoms are crosslinked by the reverse reactant, and are then condensed or, in some cases, deposited onto a semiconductor substrate. In various embodiments, the steric hindrance of the bulky alkyl groups prevents the formation of a densely packed network, generating a smooth, amorphous, low-density film.

[0050] CVD processes are typically performed at reduced pressures, such as between 10 milliTorr and 10 Torr. In some embodiments, the processes are performed at between 0.5 and 2 Torr. In some embodiments, the temperature of the semiconductor substrate is equal to or less than the temperature of the reactant stream. For example, the substrate temperature can be between 0° C. and 250° C., or between ambient temperature (e.g., 23° C.) and 150° C. In various processes, deposition of the polymerized organometallic material onto the substrate occurs at a rate that is inversely proportional to the surface temperature.

[0051] In some embodiments, the EUV patternable film is prepared and deposited on the semiconductor substrate using wet deposition equipment and processes known in the art, for example, the organometallic material is formed by spin coating on the surface of the semiconductor substrate.

[0052] The thickness of the EUV patternable film formed on the surface of the semiconductor substrate may vary according to the surface characteristics, the materials used, and the processing conditions. In various embodiments, the film thickness may range from 0.5 nm to 100 nm and may be thick enough to absorb a majority of the EUV light under the conditions of EUV patterning. The EUV patternable film may accommodate 30% or more absorption, which results in significantly fewer EUV photons available towards the bottom of the EUV patternable film. Higher EUV absorption results in more crosslinking and densification near the top of the EUV exposed film compared to the bottom of the EUV exposed film. Insufficient crosslinking may cause the resist to be susceptible to lift-off or collapse in wet development, whereas such a risk does not exist in dry development. An all-dry lithography approach may facilitate more efficient utilization of EUV photons with a more opaque resist film. It will be appreciated that efficient utilization of EUV photons may occur with EUV patternable films with higher overall absorption, but in some cases, the EUV patternable film may be less than about 30%. For comparison, most other resist films have a maximum overall absorption of less than 30% (e.g., 10% or less, or 5% or less), so that the resist material at the bottom of the resist film is fully exposed. In some embodiments, the film thickness is 10 nm to 40 nm, or 10 nm to 20 nm. Without limiting the mechanism, function, or utility of the present disclosure, the process of the present disclosure has few limitations on the surface adhesion properties of the substrate and thus can be applied to a wide variety of substrates. Furthermore, as discussed above, the deposited film can closely conform to surface features without "filling" or planarizing such features, which can provide advantages in forming a mask over a substrate, such as a substrate having underlying features.

[0053] In addition to depositing a metal-containing EUV resist thin film on a semiconductor substrate in block 102 of process 100, some metal-containing EUV resist material may form as a residue on the interior surfaces of the process chamber. The interior surfaces may include the chamber walls, floor, and ceiling of the process chamber. Other interior surfaces may include the showerhead, nozzle, and substrate support surface. The metal-containing EUV resist material may form as a result of a dry deposition process, such as a CVD or ALD process. The thickness of the metal-containing EUV resist material residue may increase over time as a result of additional processing (e.g., deposition) operations performed in the process chamber. The residue tends to flake off, shed particles, or peel off from the interior surfaces of the process chamber, causing contamination in downstream processes.

[0054] In block 150 of process 100, a dry chamber clean is performed after deposition of the metal-containing EUV resist film in block 102 of process 100. This allows deposition and dry clean to be performed in the same process chamber. However, it will be understood that the dry chamber clean may be performed in a different process chamber than the deposition operation in some implementations. Indeed, a dry chamber clean may be performed after a bevel edge and / or backside clean, bake, develop, or etch operation since residues may also form in the chamber in which any of these operations are performed, which may or may not be the same as the deposition chamber.

[0055] The dry-deposited EUV resist materials that are removed are typically composed of Sn, O, and C, but the same cleaning techniques can be extended to films of other metal oxide resists and materials. Additionally, the technique can be used for film stripping and photoresist rework.

[0056] At block 104, an optional cleaning process is performed to clean the backside and / or bevel edge of the semiconductor substrate. The backside and / or bevel edge cleaning can non-selectively etch the EUV resist film and evenly remove films with various levels of oxidation or crosslinking on the substrate backside and bevel edge. During application of the EUV patternable film by wet or dry deposition processes, unintended deposition of resist material on the bevel edge and / or backside of the substrate may occur. The unintended deposition may later result in unwanted particles migrating to the top side of the semiconductor substrate and becoming particle defects. Furthermore, this bevel edge and backside deposition may also cause downstream processing issues, including contamination of patterning (scanner) and development tools. Traditionally, this bevel edge removal and backside deposition is performed by wet cleaning techniques. For spin-coated photoresist materials, this process is called edge bead removal (EBR) and is performed by directing a flow of solvent from above and below the bevel edge while the substrate is spinning. The same process can be applied to soluble organic tin oxide based resists deposited by vapor deposition techniques.

[0057] The bevel edge and / or backside cleaning of the substrate may be a dry cleaning process. In some embodiments, the dry cleaning process may be performed using the following gases: HBr, HCl, BCl 3 , SOCl 2 , Cl 2 , BBr 3 , H 2 , O 2 , PCl 3 , C.H. 4 , Methanol, Ammonia, Formic Acid, NF 3, HF. In some embodiments, the dry cleaning process may use the same chemistries as the dry development process described herein. For example, an organic acid such as trifluoroacetic acid or other organic vapors may be used for bevel edge and / or backside cleaning. For bevel edge and / or backside cleaning processes, the vapor and / or plasma must be confined to specific areas of the substrate to ensure that only the backside and bevel are removed without degrading the film on the front side of the substrate.

[0058] Process conditions can be optimized for bevel edge and / or backside cleaning. In some embodiments, higher temperatures, higher pressures, and / or higher reactant flow rates can increase the etch rate. Suitable process conditions for dry bevel edge and backside cleaning can be as follows: reactant flow rates of 100-10,000 sccm (e.g., 500 sccm HCl, HBr, HI, or H) depending on the photoresist film and composition and properties. 2 and Cl 2 Or Br 2 , BCl 3 Or H 2 or other halogen-containing compounds), a temperature of 20-140°C (e.g., 80°C), a pressure of 20-1000 mTorr (e.g., 100 mTorr), or a pressure of 50-765 Torr (e.g., 760 Torr), a plasma power of 0-500 W at a high frequency (e.g., 13.56 MHz), and a time of about 10-20 seconds. Bevel and / or backside cleaning can be accomplished using a Coronus® tool available from Lam Research, Inc., Fremont, Calif., although a wider range of process conditions can be used depending on the capabilities of the processing reactor.

[0059] The bevel edge and / or backside cleaning may alternatively be extended to a complete photoresist removal or photoresist “rework” in which the applied EUV photoresist is removed and the semiconductor substrate is prepared for reapplication of photoresist, such as when the original photoresist is damaged or otherwise defective. Photoresist rework should be accomplished without damaging the underlying semiconductor substrate, and therefore oxygen-based etches should be avoided. Instead, variations of organic vapor chemistries or halogen-containing chemistries as described herein may be used. It will be understood that the photoresist rework operation may be applied at any stage during the process 100. Thus, the photoresist rework operation may be applied after deposition, after bevel edge and / or backside cleaning, after PAB processing, after EUV exposure, after PEB processing, after development, or after a hard bake. In some implementations, the photoresist rework may be performed to non-selectively remove exposed and unexposed areas of the photoresist, but selectively to the underlying layers.

[0060] In some embodiments, the photoresist rework process involves vapors and / or plasmas having one or more of the following gases: HBr, HCl, HI, BCl 3 , Cl 2 , BBr 3 , H 2 , PCl 3 , C.H. 4 , Methanol, Ammonia, Formic Acid, NF 3 HF. In some embodiments, photoresist rework can use the same chemistries as the dry development process described herein. For example, photoresist rework can use organic acids such as trifluoroacetic acid or other organic vapors.

[0061] Process conditions can be optimized for photoresist rework. In some embodiments, higher temperatures, higher pressures, and / or higher reactant flow rates can increase the etch rate. Suitable process conditions for photoresist rework can be as follows: reactant flow rates of 100-500 sccm (e.g., 500 sccm of HCl, HBr, HI, BCl) depending on the photoresist film and composition and properties. 3 or H 2 and Cl 2 or Br 2 ), a temperature of 20 to 140 °C (e.g., 80 °C), a pressure of 20 to 1000 mTorr (e.g., 300 mTorr) or a pressure of 50 to 765 Torr (e.g., 760 Torr), a plasma power of 0 to 800 W (e.g., 500 W) at high frequency (e.g., 13.56 MHz), and a voltage of 0 to 200 V. b (the harder the underlying substrate material, the higher the bias may be used), and a time of about 20 seconds to 3 minutes, sufficient to completely remove the EUV photoresist. These conditions are suitable for some processing reactors, e.g., Kiyo etch tools available from Lam Research, Inc., Fremont, Calif., but it should be understood that a wider range of process conditions may be used depending on the capabilities of the processing reactor.

[0062] In block 150 of process 100, a dry chamber clean operation may be performed after the bevel edge and / or backside clean in block 104 of process 100. This allows the bevel edge and / or backside clean and the dry chamber clean to be performed in the same process chamber. However, it will be understood that the dry chamber clean may be performed in a different process chamber than the bevel edge and / or backside clean in some implementations.

[0063] In block 106 of process 100, an optional post-apply bake (PAB) is performed after deposition of the metal-containing EUV resist film and before EUV exposure. The PAB process can involve a combination of thermal treatment, exposure to chemicals, and moisture to increase the EUV sensitivity of the metal-containing EUV resist film, thereby reducing the EUV dose to develop a pattern in the metal-containing EUV resist film. The PAB process temperature can be adjusted and optimized to increase the sensitivity of the metal-containing EUV resist film. For example, the process temperature can be about 90° C. to about 200° C., or about 150° C. to about 190° C. In some embodiments, the PAB process can be performed at a pressure between atmospheric pressure and vacuum for a process period of about 1 to 15 minutes, for example about 2 minutes. In some embodiments, the PAB process is performed at a temperature of about 100° C. to 230° C. for about 1 to 2 minutes.

[0064] At block 150 of process 100, a dry chamber clean operation may be performed after the PAB treatment at block 106 of process 100. This allows the bake and dry chamber clean to be performed in the same process chamber. However, it will be understood that the dry chamber clean may be performed in a different process chamber than the PAB treatment in some implementations.

[0065] In block 108 of process 100, the metal-containing EUV resist film is exposed to EUV radiation to develop the pattern. Generally speaking, the EUV exposure causes changes in chemical composition and crosslinking in the metal-containing EUV resist film, resulting in an etch selectivity contrast that can be exploited in subsequent development.

[0066] The metal-containing EUV resist film can then be patterned by exposing regions of the film to EUV light, typically under a relatively high vacuum. EUV devices and imaging methods useful herein include those known in the art. In particular, as described above, exposed regions of the film are formed by EUV patterning with altered physical or chemical properties compared to unexposed regions. For example, in exposed regions, cleavage of metal-carbon bonds can occur through the elimination of beta hydrides, leaving reactive and accessible metal hydride functional groups that can be converted to hydroxides and bridging metal oxide moieties via metal-oxygen bridges during a subsequent post-exposure bake (PEB) step. This process can be used to create chemical contrast for development as a negative resist. In general, the higher the number of beta Hs in the alkyl group, the more sensitive the film will be. This can also be described as weaker Sn-C bonds with more branching. Following exposure, baking the metal-containing EUV resist film can result in further crosslinking of the metal oxide film. The difference in properties between the exposed and unexposed regions can be exploited in subsequent processing, such as dissolving the unexposed regions or depositing material in the exposed regions. For example, the pattern can be developed using dry methods to form a metal oxide-containing mask.

[0067] In particular, in various embodiments, hydrocarbyl-terminated tin oxide present on the surface is converted to hydrogen-terminated tin oxide in the exposed areas of the imaging layer, especially when the exposure is carried out in a vacuum using EUV. However, removing the exposed imaging layer from vacuum into air or by exposure to oxygen, ozone, H 2 O 2 By the controlled introduction of fluorine, fluorine-containing fluoride, or water, surface Sn-H can be oxidized to Sn-OH. The difference in properties between the exposed and unexposed regions can be exploited in subsequent processing, for example, by reacting the irradiated regions, the unirradiated regions, or both, with one or more reagents to selectively add or remove material from the imaging layer.

[0068] Without limiting the mechanism, function, or utility of the present technology, for example, 2 ~100mJ / cm 2 EUV exposure at doses of 1000 nm leads to the cleavage of Sn-C bonds, which results in the loss of alkyl substituents and relieves steric hindrance, thus allowing the low-density film to collapse. In addition, the reactive metal-H bonds generated in the beta hydride elimination reaction can react with neighboring active groups, such as hydroxyls, in the film, which can lead to further cross-linking and densification, creating a chemical contrast between exposed and unexposed regions.

[0069] After exposing the metal-containing EUV resist film to EUV light, a photopatterned metal-containing EUV resist is provided, which includes EUV exposed areas and EUV unexposed areas.

[0070] At block 110 of process 100, an optional post-exposure bake (PEB) is performed to further enhance the etch selectivity contrast of the photopatterned metal-containing EUV resist. The photopatterned metal-containing EUV resist can be heat treated in the presence of various chemical species to promote crosslinking of the EUV exposed regions, or can simply be baked on a hotplate in ambient air, for example, at 100° C.-250° C. for 1-5 minutes (e.g., 190° C. for 2 minutes).

[0071] In various embodiments, the bake strategy involves careful control of the bake atmosphere, introduction of reactive gases, and / or careful control of the rate of increase of the bake temperature. Examples of useful reactive gases include, for example, air, H 2 O, H 2 O 2 Steam, CO 2 , C.O., O 2 , O 3 , C.H. 4 , C.H. 3 OH, N 2 , H 2 , N.H. 3 , N 2The PEB treatment can be used to (1) drive complete evaporation of organic fragments generated during EUV exposure, (2) oxidize any Sn-H, Sn-Sn, or Sn radical species generated by EUV exposure to metal hydroxides, and (3) promote cross-linking between adjacent Sn-OH groups, resulting in more densely cross-linked SnO. 2 The bake temperature is carefully selected to achieve optimal EUV lithography performance. Too low a PEB temperature may result in insufficient crosslinking, resulting in reduced chemical contrast for development at a given dose. Too high a PEB temperature may also result in adverse effects such as severe oxidation and film shrinkage in unexposed areas (areas removed by development of the patterned film to form the mask in this example), as well as undesirable interdiffusion at the interface between the photopatterned metal-containing EUV resist and the underlayer, both of which may contribute to loss of chemical contrast due to insoluble scum and increased defect density. The PEB treatment temperature may be from about 100°C to about 300°C, from about 170°C to about 290°C, or from about 200°C to about 240°C. In some embodiments, the PEB treatment may be performed at a pressure between atmospheric pressure and vacuum for a treatment period of about 1 to 15 minutes, for example about 2 minutes. In some embodiments, the PEB thermal treatment may be repeated to further increase etch selectivity.

[0072] In block 150 of process 100, a dry chamber clean operation may be performed after the PEB process in block 110 of process 100. This allows the bake and dry chamber clean to be performed in the same process chamber. However, it will be understood that the dry chamber clean may be performed in a different process chamber than the PEB process in some implementations.

[0073] At block 112 of process 100, the photopatterned metal-containing EUV resist is developed to form a resist mask. In various embodiments, the exposed areas are removed (positive tone) or the unexposed areas are removed (negative tone). In some embodiments, the development may include selective deposition of the photopatterned metal-containing EUV resist on either the exposed or unexposed areas, followed by an etching operation. In some embodiments, the development may be performed by exposure to one or more organic vapors (e.g., trifluoroacetic acid). The development may be performed without striking a plasma in some embodiments. Alternatively, the development may be performed by a flow of one or more organic vapors (e.g., trifluoroacetic acid) activated in a remote plasma source or activated by exposure to remote UV radiation. The photoresist for development may include an element selected from the group consisting of tin, hafnium, tellurium, bismuth, indium, antimony, iodine, and germanium. The element may have a high patterning radiation absorption cross section. In some embodiments, the element may have a high EUV absorption cross section. In some embodiments, the metal-containing EUV resist can have an overall absorptivity of greater than 30%, which in an all-dry lithography process allows for more efficient utilization of EUV photons and allows for the development of thicker and more EUV-opaque resists.

[0074] An example of a development process includes subjecting an organotin oxide-containing EUV-sensitive photoresist thin film (e.g., 10-30 nm thick, e.g., 20 nm) to an EUV exposure dose and a post-exposure bake, followed by development. The photoresist film may be deposited based on a gas-phase reaction of an organotin precursor, such as isopropyl(tris)(dimethylamino)tin, with water vapor, or may be a spin-on film containing tin clusters in an organic matrix.

[0075] At block 150 of process 100, a dry chamber clean may be performed after the dry development at block 112 of process 100. This allows the dry development and the dry chamber clean to be performed in the same process chamber. However, it will be understood that the dry chamber clean may be performed in a different process chamber than the dry development in some implementations. Furthermore, it will be understood that the dry chamber clean may be performed in the same process chamber as the etching operation or in a different process chamber. The etching operation may be applied to etch an underlying substrate layer of the semiconductor substrate.

[0076] In block 114 of process 100, the semiconductor substrate optionally undergoes a hard bake. During the hard bake, the semiconductor substrate is exposed to an elevated temperature. For example, the semiconductor substrate may be exposed to an elevated temperature of about 50° C. or higher, about 100° C. to about 300° C., or about 170° C. to about 290° C. The hard bake can remove residual solvent or etching gases from the development.

[0077] FIG. 2 shows a flow diagram of an exemplary method for dry developing a metal-containing resist, according to some embodiments. The operations of process 200 may be performed in a different order and / or with a different, fewer, or additional number of operations. Aspects of process 200 may be described with reference to FIGS. 3A-3C and 4A-4B. One or more operations of process 200 may be performed using an apparatus described in any one of FIGS. 7-11B. In some embodiments, operations of process 200 may be implemented, at least in part, in accordance with software stored on one or more non-transitory computer-readable media.

[0078] In block 202 of process 200, a photo-patterned metal-containing resist is provided on a surface of a semiconductor substrate in a process chamber. The metal-containing resist may be deposited on the surface of the semiconductor substrate. The metal-containing resist may be exposed to UV radiation (e.g., EUV radiation) by a scanner or an EUV lithography tool to form a photo-patterned metal-containing resist. In some implementations, the photo-patterned metal-containing resist is a photo-patterned metal-containing EUV resist. For example, the photo-patterned metal-containing EUV resist is an organometallic oxide or organometallic containing film. The semiconductor substrate may be provided in the process chamber after processing in the scanner and / or PEB processing chamber.

[0079] In block 204 of process 200, the photo-patterned metal-containing resist is dry developed by exposing it to a developing chemical that includes an organic vapor to selectively remove portions of the resist to form a resist mask. Dry developing the photo-patterned metal-containing resist includes using a developing chemical to selectively remove the EUV-unexposed portions of the resist relative to the EUV-exposed portions to form a resist mask. Typically, development is performed using wet developing chemicals. Wet development using solvents generates undesirable waste streams. Wet development generally involves moisture and / or oxygen, which more easily leads to the formation of scum. Wet development is limited by solubility and cluster size, whereas dry development is not limited by solubility and cluster size. Wet development is more prone to pattern collapse and delamination issues that dry development avoids. Development in the present disclosure is performed in the gas phase using dry developing chemicals instead of wet developing chemicals.

[0080] Development using dry development chemistries is usually done using boron trichloride (BCl 3 ) vapor, chlorine gas (Cl 2 ) or bromine gas (Br 2 ) and hydrogen gas (H 2), or vapors of hydrogen halides such as hydrogen bromide (HBr), hydrogen chloride (HCl), or hydrogen fluoride (HF). However, such vapors can leave residues or scum after development. The residues can include residual etch by-products adsorbed on the surface of the semiconductor substrate and possibly on the chamber walls. For example, halogen vapors can react with moisture or oxygen to form residual etch by-products that are difficult to remove. In some cases, the residual etch by-products include bromides, which are sticky and difficult to remove. The accumulation of residual etch by-products can cause process drift, resulting in dangerous precautions in the process chamber. Additionally, the residues adsorbed on the semiconductor substrate can desorb from the semiconductor substrate and contaminate downstream processing tools. In some cases, the residues can include high concentrations of metal or metal oxide clusters that can contaminate downstream processing tools. Also, the residual etch by-products are difficult to remove and do not volatilize easily, which may require a separate plasma step, or a separate chamber with plasma capabilities. In their absence, high temperature swings are implemented that volatilize the residues, which is often undesirable for the semiconductor substrate and process chamber.

[0081] The developing chemical of the present disclosure is an organic vapor. The organic vapor may be an organic acid. In some embodiments, the organic acid comprises a carboxylic acid. In some embodiments, the organic acid comprises trifluoroacetic acid (CF 3 COOH). The organic vapor may be halogenated or at least fluorinated. In some embodiments, the organic vapor includes hexafluoroacetylacetone (CF 3 C O CH 2 C O CF 3 In some embodiments, the organic vapor comprises trifluoroacetic anhydride ((CF 3 CO) 2 O), acetic anhydride ((CH 3 CO) 2 O), trichloroacetic acid (CCl 3COOH), monofluoroacetic acid (CFH 2 COOH), difluoroacetic acid (CF 2 HCOOH), mixed halide acetic acids such as chlorodifluoroacetic acid, sulfur-containing analogs of acetic acid, and thioacetic acid (CH 3 COSH), or thioglycolic acid (HSCH 2 CO 2 H). In some embodiments, the developing chemicals include a mixture of carboxylic acids and hydrogen halides in the vapor phase. For example, the developing chemicals include a mixture of acetic acid or formic acid and hydrogen chloride or hydrogen bromide. In some embodiments, the organic vapors include helium (He), neon (Ne), argon (Ar), xenon (Xe), and nitrogen (N 2 ) may be flowed with or without an inert / carrier gas.

[0082] Organic vapors may react with metal-containing resists to form by-products that are more volatile than etch by-products formed from halogen vapors. As an example, etch by-products of tin bromide can have a boiling point of about 200° C. or higher. However, etch by-products of tin fluoroacetate can be less than about 200° C. For example, hexatin(II)-di-μ-oxy-octakis-μ-trifluoroacetic acid (1F) is volatile at 191° C. at 1 Torr, and tetrakis(trifluoroacetate)tin(IV) (2F) is volatile at 84° C. at 1 Torr. Both 1F and 2F provide high thermal stability and volatility. Etch by-products formed from organic vapors reacting with metal-containing resists may have superior volatility. In particular, etch by-products formed from trifluoroacetic acid reacting with EUV non-exposed organometallic resists may have superior volatility. Without being limited by any theory, trifluoroacetic acid or other fluorinated derivatives of organic acids may increase the volatility of etch by-products due to their electron-withdrawing effect. Trifluoroacetic acid or other fluorinated derivatives of organic acids can be strong organic acids.

[0083] The organic vapor of the present disclosure may be a strong organic acid. As used herein, a strong organic acid may have a pKa value of about 3.8 or less. The strength of the organic acid may be increased by halogenation. In some embodiments, the strength of the organic acid may be significantly increased by fluorination. For example, formic acid or acetic acid may be capable of etching metal-containing resist materials, such as organometallic resist materials, while trifluoroacetic acid may more effectively etch such metal-containing resist materials. Less strong organic acids (e.g., acetic acid) may be plasma-assisted for selective removal of metal-containing resist materials, while stronger organic acids may selectively remove metal-containing resist materials without the assistance of plasma. Thus, in the present disclosure, dry development of metal-containing resists may be performed without the assistance of plasma. However, as described below, plasma may be optionally used for desorption, descum, or smoothing operations after dry development. This plasma-based desorption, descum, or smoothing operation may be unnecessary if the etch by-products of the organic vapor are volatilized.

[0084] The organic vapors of the present disclosure can perform dry development in a plasma-free thermal process. This means that dry development can be performed in a process chamber without plasma capabilities. In some implementations, dry development may be performed without a subsequent plasma-based descum or smoothing operation. By eliminating exposure to plasma, plasma damage to the semiconductor substrate can be avoided, significantly reducing costs and increasing throughput. Furthermore, the interior surface of the process chamber does not need to be resistant to plasma and can be made of a material that is resistant to halogen vapors, such as hydrogen halides. The surfaces of chamber components, such as the chamber walls, ceiling, and showerhead, may be susceptible to corrosion in the presence of moisture and halogen vapors. As a result, the interior surface of the process chamber is typically composed of a material that is stable in plasma, halogen vapor, and water vapor. However, for the dry development chemistries of the present disclosure, such as trifluoroacetic acid, the interior surface of the process chamber of the present disclosure may be composed of a material that does not necessarily meet the aforementioned requirements. In some implementations, the chamber walls of the process chamber may include aluminum oxide, anodized aluminum, or plastic.

[0085] By applying plasma-free thermal techniques, multiple wafers can be batch developed simultaneously in a low-cost thermal vacuum chamber / oven, greatly improving productivity. However, in some embodiments, the thermal dry development process may be followed by exposure to a plasma. Subsequent exposure to plasma may be performed for desorption, descumming, smoothing, or other processing operations.

[0086] Dry development of the photopatterned metal-containing resist can be combined with other dry processing operations, such as dry deposition (e.g., CVD) of the metal-containing resist. In some implementations, processing of the semiconductor substrate may combine all dry steps, including film formation by vapor deposition, EUV lithography patterning, and dry development. The bake operation, bevel edge and / or backside cleaning operation, and chamber cleaning operation may also be dry operations. Such processing operations may avoid material and production costs associated with wet processing operations, such as wet development. Furthermore, dry processing provides more tunability, provides more critical dimension (CD) control, and allows scum removal. In general, wet processing involves moisture and / or oxygen, which more easily causes scum formation. Wet development is limited by solubility and cluster size, whereas dry development is not limited by solubility and cluster size. Wet development is more prone to pattern collapse and delamination problems that dry development avoids. In addition, the use of all dry processing operations can facilitate integration in interconnected vacuum processing chambers without exposure to and contamination by ambient air or trace contaminants contained therein. For example, the PEB heat treatment in which the exposed regions undergo further crosslinking may occur in the same chamber as development, although it will be appreciated that the PEB heat treatment may also be performed in a separate chamber.

[0087] In some embodiments, dry development can be performed by using a thermal process in conjunction with flowing organic vapors such as trifluoroacetic acid. For example, dry development can be performed in a thermal processing chamber. In some embodiments, the organic vapors such as trifluoroacetic acid can rapidly remove the unexposed portions of the photopatterned metal-containing resist relative to the exposed portions of the photopatterned metal-containing resist, leaving a pattern of the exposed film that can be transferred to an underlying layer of a semiconductor substrate by an etching process.

[0088] In some implementations, the semiconductor substrate can be exposed to a dry developing chemical, such as a strong organic acid, in a thermal treatment chamber, such as an oven. The thermal treatment chamber can include a developing chemical line for delivering an organic vapor to the thermal treatment chamber. In some implementations, the thermal treatment chamber can include one or more heating elements for temperature control, such as a heating element coupled to a heating assembly facing the semiconductor substrate in the process chamber for substrate temperature control. In some implementations, the one or more heating elements can be one or more LEDs. The one or more heaters can heat the semiconductor substrate to a high temperature during dry development to promote volatilization of etch by-products.

[0089] In a thermal dry development process, the photopatterned metal-containing resist is exposed to a development chemistry optimized for etch selectivity between exposed and unexposed regions. In general, lower temperatures can increase the contrast in etch selectivity, while higher temperatures can decrease the contrast in etch selectivity. Higher temperatures can increase volatilization of etch byproducts and limit the formation of residues on the semiconductor substrate. In some embodiments, the temperature can be less than about 200°C, about 20°C to about 190°C, about 40°C to about 120°C, or about 50°C to about 100°C. Volatile compounds are formed at temperatures less than about 200°C by reacting the photopatterned metal-containing resist with organic vapors.

[0090] The chamber pressure can be adjusted and can affect the etch selectivity between exposed and unexposed regions during thermal dry development. In some embodiments, the chamber pressure can be relatively low and without dilution, and the chamber pressure can be about 0.1 mTorr to about 1000 mTorr, about 0.2 mTorr to about 300 mTorr, or about 0.5 mTorr to about 100 mTorr. In some embodiments, the chamber pressure can be about 20 mTorr to about 2000 mTorr, or about 20 mTorr to about 1000 mTorr, such as about 300 mTorr. In some embodiments, the chamber pressure can be relatively high with high flow rates and with dilution, and the chamber pressure can be about 100 Torr to about 765 Torr, or about 200 Torr to about 760 Torr.

[0091] The gas flow rate of the dry development chemistry can be adjusted, and the gas flow can affect the etch selectivity between exposed and unexposed areas during thermal dry development. In some embodiments, the gas flow rate can be about 0.5 SLM to about 30 SLM, about 1 SLM to about 20 SLM, or about 2 SLM to about 15 SLM. The gas flow rate can include the total flow rate of the gases being flowed, including the organic vapor and a carrier gas, such as nitrogen, argon, etc. The organic vapor flow rate can be only a portion of the total flow rate, and the organic vapor flow rate can be about 0.01 SLM to about 1 SLM. For high flow rates, the organic vapor flow rate can be about 1 SLM to about 10 SLM.

[0092] The duration of exposure can be adjusted in the thermal dry development process. The exposure time can depend on, among other factors, the amount of resist desired to be removed, the development chemistry, the amount of crosslinking in the resist, and the composition and properties of the resist. In some embodiments, the duration of exposure can be about 5 seconds to about 5 minutes, about 10 seconds to about 3 minutes, or about 10 seconds to about 1 minute.

[0093] In some embodiments, the photo-patterned metal-containing resist is developed with a plasma-free thermal technique. In an alternative embodiment, the photo-patterned metal-containing resist is developed with a plasma development process. The photo-patterned metal-containing resist is exposed to a development chemistry that includes radicals / ions of one or more gases. The one or more gases may include organic vapors, such as trifluoroacetic acid. The process chamber for processing the semiconductor substrate for dry development may be a plasma generation chamber or may be coupled to a plasma generation chamber remote from the process chamber. The plasma generation chamber may be an inductively coupled plasma (ICP) reactor, a transformer coupled plasma (TCP) reactor, or a capacitively coupled plasma (CCP) reactor, using equipment and techniques known in the art. An electromagnetic field acts on the one or more gases to generate a plasma in the plasma generation chamber. Ions and / or radicals from the remote plasma may interact with the photo-patterned metal-containing resist. The ions and / or radicals may include ions and / or radicals of an organic acid, such as trifluoroacetic acid. In some embodiments, a vacuum line may be coupled to the process chamber for pressure control, and a development chemical line may be coupled to the plasma generation chamber for delivering one or more gases to the plasma generation chamber. The process chamber may include one or more heaters for temperature control, such as a heater coupled to a heating assembly facing the substrate for substrate temperature control. In some embodiments, the development of the photopatterned metal-containing resist is exposed to conditions optimized to generate a gentle plasma characterized by high pressure and low power. In some embodiments, the RF power level may be adjusted, and the RF power may be about 1000W or less, about 800W or less, or about 500W or less.

[0094] In addition to or instead of plasma activation, activation of one or more gases in the dry development process may occur by photoactivation. In some implementations, photoactivation may be achieved by exposure to ultraviolet (UV) radiation. For example, the process chamber may include a lamp, such as a UV lamp, configured to generate UV radiation. Exposing one or more gases to UV radiation may generate radicals of one or more gases that can be used for dry development of the photopatterned metal-containing resist. Exposure of one or more gases to UV radiation may occur without exposing the photopatterned metal-containing resist to UV radiation. In other words, the photopatterned metal-containing resist is not visible to the UV lamp.

[0095] It will be understood that the aforementioned methods of thermal development, plasma development, and light-activated development may be combined with each other. Such development methods can be applied simultaneously or sequentially. One or more development methods can be applied while flowing dry development chemicals in the gas phase. Development can result in a positive tone or a negative tone, where the dry development chemicals selectively remove either the unexposed or exposed material, leaving the exposed or unexposed counterpart as a mask.

[0096] As mentioned above, the etch selectivity during dry development is adjustable by controlling process conditions such as temperature, pressure, gas flow, gas composition, and plasma power, among other adjustable process conditions. The etch selectivity can be adjusted in a single step or multiple steps to achieve the desired patterned characteristics. In some embodiments, the etch selectivity during dry development is adjusted over one or more steps, thereby affecting the resist profile. More specifically, the amount of taper or re-entrant angle in the resist profile can be controlled by applying dry development chemicals of different etch selectivities over one or more steps. Descum, photoresist rework, hardening, smoothing, and cleaning operations can also be adjusted according to the adjustable etch selectivity.

[0097] 3A-3C show cross-sectional schematic views of various processing stages of dry development according to some embodiments. The examples shown in FIGS. 3A-3C show negative tone dry development. As shown in FIG. 3A, a wafer 300 includes a substrate 302 and a substrate layer 304 to be etched. In some embodiments, the substrate layer 304 includes an ashable hard mask such as spin-on carbon (SoC) or other materials, such as silicon, silicon oxide, silicon nitride, silicon carbide, etc. In some embodiments, the substrate layer 304 can be a layer stack disposed on the substrate 302. The wafer 300 further includes a photo-patterned metal-containing EUV resist film 306. For example, the photo-patterned metal-containing EUV resist film 306 can be an organic metal-containing layer disposed on the substrate layer 304 to be etched. The photo-patterned metal-containing EUV resist film 306 can have a thickness of about 5 nm to about 50 nm, or about 10 nm to about 30 nm. The photo-patterned metal-containing EUV resist film 306 may be provided in a process chamber after photo-patterning in an EUV scanner and / or after the PEB treatment described above. The photo-patterned metal-containing EUV resist film 306 includes non-EUV exposed regions 306a and EUV exposed regions 306b. As shown in FIG. 3B, the non-EUV exposed regions 306a of the photo-patterned metal-containing EUV resist film 306 may be removed in a dry development process by exposing it to a flow of dry development chemicals without applying a plasma. The dry development chemicals may include organic vapors such as organic acids. The organic acids may include halogenated or fluorinated carboxylic acids. Examples of organic acids include, but are not limited to, trifluoroacetic acid, hexafluoroacetylacetone, trichloroacetic acid, monofluoroacetic acid, and difluoroacetic acid. Other examples of organic acids include mixed halide acetic acids such as chlorodifluoroacetic acid, sulfur-containing analogs of acetic acid, thioacetic acid, and thioglycolic acid. The non-EUV exposed regions 306a are removed after development to form a resist mask 308. The substrate layer 304 to be etched can then be etched using the resist mask 308 to provide the structure illustrated in FIG.

[0098] The organometallic oxide film may have a tetrahedrally coordinated structure. The exposed regions have a higher level of Sn-O-Sn cross-linking, resulting in higher density and lower / slower reactivity with halogenated carboxylic acids. The unexposed regions show lower density due to the presence of bulky alkyl substituents that block the approach and condensation of Sn-OH moieties. In the unexposed regions, an acid such as trifluoroacetic acid more readily protonates the more "basic" and accessible oxygen lone pairs characteristic of the more tetrahedrally coordinated organotin oxide hydroxides. A volatile by-product of trifluoroacetate is generated and removed from the unexposed regions. Without being limited by any theory, it is believed that trifluoroacetic acid selectively protonates the oxygen lone pairs to form a volatile by-product. If the alkyl group is isopropyl, then at a typical EUV patterning dose, at least two of the three isopropyl substituents are removed, which causes the exposed regions to condense after the PEB step to form denser SnO. 2 The formation of a tin-like material, which is less reactive with trifluoroacetic acid due to the adoption of a more hexacoordinated tin structure that is less accessible to oxygen atoms, and as a result, its reactivity with trifluoroacetic acid is very slow.

[0099] In some cases, residue or scum may remain after development. Residue may result from slow etching components in less homogeneous EUV resist formulations, including those applied by spin-coating techniques. Such scum may contain high concentrations of metals, which may be problematic during subsequent pattern transfer.

[0100] Additionally or alternatively, after development, roughness may form on the sidewalls of features etched with the developed pattern, some of which may be due to stochastic or non-optimal Gaussian distribution of light resulting in partially or fully exposed material in areas where the resist should remain unexposed, or vice versa.

[0101] In some embodiments, the dry development may be accompanied by a descum / smoothing operation. In some embodiments, the descum and smoothing operation may be an inert gas plasma desorption operation. For example, the inert gas plasma desorption operation may be a helium plasma desorption operation. The inert gas plasma desorption operation may be performed after the dry development or may be performed repeatedly with the dry development.

[0102] FIG. 4A shows a cross-sectional schematic diagram of dry development without application of inert gas plasma, according to some embodiments. The photopatterned metal-containing EUV resist film includes exposed and unexposed regions. As shown in FIG. 4A, metal oxide (e.g., SnO x ) particles or clusters may occupy the non-exposed areas. As dry development progresses, the metal oxide clusters become more concentrated. The metal oxide clusters are generally difficult to remove. Development may be selective with respect to the removal of organic material. After removing the non-exposed areas, the metal oxide clusters may remain on the surface of the substrate as scum. The metal oxide clusters remaining on the sidewalls of the exposed areas may cause roughness.

[0103] FIG. 4B shows a cross-sectional schematic of a dry development cycle inert gas plasma for descumming, according to some embodiments. The first stage involves dry development to remove a substantial portion of the unexposed regions of the photopatterned metal-containing EUV resist film. The dry development chemistry may include, for example, organic acids and / or hydrogen halides. A substantial portion may represent at least more than 70 volume percent of the unexposed regions, more than 80 volume percent of the unexposed regions, or more than 90 volume percent of the unexposed regions. Metal oxide clusters are concentrated at the surface of the remaining unexposed regions of the EUV resist film. The second stage involves applying an inert gas plasma, such as helium plasma, at low power and high ion energy for a short period of time. The helium plasma removes the metal oxide clusters. In addition, the helium plasma removes the clusters from the sidewalls and smoothes the sidewalls. The helium plasma treatment may also help solidify or harden the patterned EUV resist film to form a denser metal oxide like hardmask. After the helium plasma treatment, a low selectivity dry etch step can be used to remove any residue remaining in the unexposed areas of the EUV resist film.

[0104] In some embodiments, dry development may be repeated with helium plasma treatment for one or more cycles until the unexposed areas of the EUV resist film are removed. Helium plasma descumming / smoothing can be repeated with dry development to improve results, as described above. In this way, for example, most of the organic components in the unexposed areas of the pattern can be removed by dry development, and then a short helium plasma operation can remove some of the concentrated metal at the surface, thereby allowing access to the remaining underlying organic material, which can be removed in a subsequent dry development operation / cycle. Another cycle of helium plasma can be used to remove the remaining metal, leaving a clean and smooth feature surface. This cycling can continue until all or substantially all of the scum and roughness residues have been removed, leaving a clean and smooth feature surface.

[0105] The process conditions for the descum and smoothing operations may be controlled during or after development. In some embodiments, the flow of reactants may be about 50 sccm to about 1000 sccm, or about 100 sccm to about 500 sccm, such as about 500 sccm He. In some embodiments, the temperature may be about -60°C to about 120°C, about -20°C to about 60°C, or about 20°C to about 40°C, such as about 20°C. In some embodiments, the chamber pressure may be about 1 mTorr to about 300 mTorr, about 5 mTorr to about 100 mTorr, about 5 mTorr to about 20 mTorr, such as about 10 mTorr. The plasma power may be relatively low when the ion energy is high. In some embodiments, the plasma power may be about 50 W to about 1000 W, about 100 W to about 500 W, or about 100 W to about 300 W, such as about 300 W. In some embodiments, the wafer bias is about 10 V to about 500 V, about 50 V to about 300 V, for example about 200 V. The plasma may be generated using a high RF frequency. In some embodiments, the RF frequency is 13.56 MHz. The duration of exposure to the inert gas plasma may be relatively short to avoid excessive exposure to UV radiation during plasma exposure. In some embodiments, the duration of exposure is about 0.5 seconds to about 5 seconds, about 1 second to about 3 seconds, for example about 2 seconds.

[0106] The inert gas plasma treatment for descumming and cleaning of unexposed resist residue has the concomitant benefit of hardening and solidifying the exposed resist, thereby enhancing its hardmask function in the subsequent operation of etching the underlying substrate. This resist solidification is accomplished by exposing the EUV-exposed resist to UV radiation produced by the inert gas plasma, which may continue after the bias is turned off and descumming / smoothing is completed. If descumming / smoothing is not required or performed, an inert gas plasma cure may be performed instead.

[0107] Not only can the organic vapors of the present disclosure be used in dry development processes, but organic vapors such as trifluoroacetic acid can also be used in dry chamber cleaning or other processing operations for dry removal of metal-containing resists.

[0108] FIG. 5 shows a flow diagram of an exemplary method of dry chamber cleaning, according to some embodiments. The dry chamber cleaning may be performed after deposition, bevel and / or backside cleaning, baking, developing, or etching. In some embodiments, the dry chamber cleaning may be performed after deposition of a resist material in the same process chamber as deposition of the resist material. The operations of process 500 may be performed in a different order and / or with a different, fewer, or additional number of operations. Aspects of process 500 may be described with reference to FIGS. 6A-6D. Process 500 One or more of the operations of process 500 may be performed using an apparatus as described in any one of Figures 7-11B. In some implementations, the operations of process 500 may be implemented, at least in part, in accordance with software stored on one or more non-transitory computer-readable media.

[0109] At block 502 of process 500, a metal-containing resist material is deposited on a surface of a semiconductor substrate in a process chamber, with a portion of the metal-containing resist material forming a residue on one or more surfaces of the process chamber. The composition and deposition of such metal-containing resist materials may be described, for example, in International Patent Application No. PCT / US2019 / 31618, filed May 9, 2019, which is incorporated herein by reference for its disclosure of methods and materials applicable to the present disclosure. The method includes generating a polymerized organometallic material in the gas phase and depositing it on a semiconductor substrate. In some embodiments, the metal-containing resist material is a metal oxide-containing EUV resist material. For example, the elements in the metal-containing resist material are selected from the group consisting of tin, hafnium, tellurium, bismuth, indium, antimony, iodine, germanium, and combinations thereof. In some embodiments, the metal-containing resist material includes an organometallic oxide, such as an organotin oxide.

[0110] In some implementations, the process chamber in which the semiconductor substrate is disposed may be a dry deposition chamber. In other implementations, the process chamber in which the semiconductor substrate is disposed may be a bevel edge and / or backside cleaning chamber, a PAB processing chamber, a PEB processing chamber, a development chamber, or an etch chamber. Any of the aforementioned chambers may accumulate metal-containing resist material on the interior surfaces over time. As the number of semiconductor substrates processed in the processing chamber increases, the unintentional metal-containing resist material may build up on the interior surfaces as residue. Periodic cleaning is required to remove the unintentional deposits of metal-containing resist material. Cleaning can be performed "in situ," where the dry chamber cleaning is performed in the same process chamber in which the unintentional metal-containing resist material is formed.

[0111] The residue may form on one or more surfaces of the process chamber, which may include one or more of the chamber walls, ceiling, floor, showerhead surface, nozzle surface, and substrate support surface. In some implementations, the residue may form as a result of a dry deposition process, such as a CVD or ALD process. The thickness of the residue on the one or more surfaces may increase over time as a result of additional processing (e.g., deposition) operations performed in the process chamber. In some implementations, the average thickness of the residue is about 2 nm or more, about 3 nm or more, about 5 nm or more, or about 10 nm or more. Metal-containing resist materials tend to flake, shed, or peel from one or more surfaces, thereby contaminating subsequent semiconductor substrates during processing.

[0112] FIG. 6A shows a cross-sectional schematic view of a metal-containing EUV resist material 602 formed on a chamber wall 604 of a process chamber. The metal-containing EUV resist material 602 may include metal oxide 606 particles or clusters. The metal oxide 606 particles or clusters may be difficult to remove. In some implementations, the metal-containing EUV resist material 602 is formed by a vapor deposition method such as CVD or ALD. Over time, the metal-containing EUV resist material 602 may thickly build up on the chamber wall 604 of the process chamber. The metal-containing EUV resist material 602 may be an organotin oxide. The metal oxide 606 particles or clusters may include tin oxide.

[0113] Returning to FIG. 5, at block 504 of process 500, a dry etchant comprising an organic vapor is introduced into the process chamber, where the dry etchant at least partially removes residues on one or more surfaces of the process chamber. In some embodiments, the organic vapor is an organic acid. The organic acid may be a strong organic acid having a pKa of about 3.8 or less. In some embodiments, the organic acid comprises a carboxylic acid. In some embodiments, the organic acid comprises trifluoroacetic acid. The organic vapor may be halogenated or at least fluorinated. In some embodiments, the organic vapor comprises hexafluoroacetylacetone. In some embodiments, the organic vapor comprises mixed halide acetic acid such as trifluoroacetic anhydride, acetic anhydride, trichloroacetic acid, monofluoroacetic acid, difluoroacetic acid, chlorodifluoroacetic acid, sulfur-containing analogs of acetic acid, thioacetic acid, or thioglycolic acid. In some embodiments, the dry etchant comprises a mixture of a carboxylic acid and a hydrogen halide in the gas phase. For example, the dry etchant comprises a mixture of acetic acid or formic acid and hydrogen chloride or hydrogen bromide. In some embodiments, the organic vapor may be flowed with or without an inert / carrier gas, such as helium, neon, argon, xenon, and nitrogen.

[0114] In some embodiments, the at least partial removal of the residue comprises reacting an organic vapor with the metal-containing resist material to form a volatile compound at a temperature less than about 200° C. In some embodiments, the at least partial removal comprises substantial removal of the residue, where “substantial removal” refers to sufficient removal of the residue such that at least a portion of one or more surfaces are exposed after removal.

[0115] In some embodiments, the process chamber can be prepared at the desired conditions for dry chamber cleaning before introducing the dry etchant. The preparation of the process chamber can achieve a particular pressure condition, level of loose particles or film impurities, moisture level, temperature condition, or protection of surfaces or components (e.g., substrate support) in the process chamber from the dry etchant. In some embodiments, preparing the process chamber can include purging and / or pumping the process chamber to remove unwanted particles. To facilitate removal of unwanted particles in the process chamber, a purge gas can be flowed into the process chamber. Purging the organometallic precursor can be useful to avoid undesired by-products and ensure sufficient removal of the organometallic precursor before the dry chamber cleaning.

[0116] In some embodiments, the chamber walls and other components can be heated to release unreacted precursors. The heat can additionally or alternatively facilitate the removal of moisture in the process chamber. Without being limited by any theory, the presence of moisture may slow the reaction between the dry etchant and the metal-containing resist material to remove the metal-containing resist material. In addition, an increased temperature in the process chamber increases the etch rate in removing the metal-containing resist material. One or more heaters in the process chamber can heat one or more surfaces to an elevated temperature. In some embodiments, the elevated temperature can be from about 20° C. to about 180° C., from about 40° C. to about 160° C., or from about 80° C. to about 140° C.

[0117] In some implementations, preparing the process chamber may include providing a dummy substrate on a substrate support in the process chamber. Thus, the semiconductor substrate having the metal-containing resist material deposited thereon may be transferred out of the process chamber prior to the dry chamber cleaning. In this manner, the semiconductor substrate is not exposed to the dry etchant during removal of residues of the metal-containing resist material from one or more surfaces of the process chamber. The dummy substrate may be provided on the substrate support to protect the substrate support (e.g., an electrostatic chuck) from exposure to the dry etchant during the dry chamber cleaning. Alternatively, protection of the substrate support may be performed by providing a protective cover over the substrate support during the dry chamber cleaning.

[0118] The dry etchant may be introduced through a showerhead coupled to the process chamber or a separate chamber inlet. The dry etchant may flow into the process chamber and react with the residue of the metal-containing resist material to form volatile products. Without being limited by any theory, the organometallic oxide resist material may have a tetrahedral coordination structure, and the organic vapor, such as trifluoroacetic acid, may protonate the oxygen lone pair to form volatile by-products. After the volatile by-products are formed, the process chamber may be pumped and purged to remove the volatile by-products. Additionally, the process chamber may be pumped and purged to remove residual dry etchant. Such residual dry etchant may cause undesired etching of the subsequent semiconductor substrate.

[0119] Dry chamber cleaning can be optimized for low etch selectivity or high etch rate of the resist material deposited in the process chamber. In this way, unwanted resist material can be removed quickly and efficiently. In some embodiments, higher temperatures and / or higher pressures can reduce the etch selectivity and increase the etch rate of the dry etchant. For example, the resist material can be removed at an etch rate of up to 1 nm / sec. During exposure to the dry etchant, the metal-containing resist material residue on one or more surfaces can be exposed to an elevated temperature. The elevated temperature can be from about 20° C. to about 180° C., from about 40° C. to about 160° C., or from about 80° C. to about 140° C. In some embodiments, the metal-containing resist material residue reacts with an organic vapor to form a volatile compound at a temperature less than about 200° C. During exposure to the dry etchant, the pressure in the process chamber can be elevated. In some embodiments, the chamber pressure is from about 0.01 Torr to 765 Torr, from about 0.1 Torr to 100 Torr, or from about 0.1 Torr to about 6 Torr. In some embodiments, the chamber pressure is cycled between high and low pressure during exposure to the dry etchant. The flow rate of the organic vapor can also be adjusted to control the etch selectivity. In some embodiments, the flow rate of the organic vapor is about 0.05 SLM to about 10 SLM, or about 0.1 SLM to about 5 SLM.

[0120] As described above with respect to dry development, dry chamber cleaning is performed using an organic vapor, such as an organic acid, instead of a halogen vapor. A halogen vapor, such as a hydrogen halide vapor, tends to leave residual etching by-products after removal of the metal-containing resist material. However, an organic vapor, such as trifluoroacetic acid, forms more volatile etching by-products that are less difficult to remove from the process chamber. An organic vapor, such as trifluoroacetic acid, may be used for dry chamber cleaning in plasma-free thermal processes. In other words, the residue of the metal-containing resist material is removed without striking the plasma. Residual carbon, contaminants, or other remaining materials may or may not be removed by exposure to the plasma. In some implementations, following the introduction of the dry etchant, one or more surfaces are exposed to oxygen (O 2 ), ozone (O 3 ), carbon dioxide (CO 2 ), or may be exposed to oxidizing gases such as carbon monoxide (CO).

[0121] Because it is possible to clean as-thermally deposited films (unexposed or uncrosslinked) without the need for the use of plasma, the techniques described herein can also go beyond the process chamber to clean downstream and upstream components of the tool (e.g., exhaust lines from the process chamber to the vacuum pump).More generally, this dry cleaning method can be used to clean other contaminated parts and components with a similar composition of metals with volatile by-products from organic vapors.

[0122] In some embodiments, the interior surface of the process chamber is compatible with the organic vapors of the present disclosure. Rather than the interior surface of the process chamber being resistant to plasma and resistant to vapors of halogens, such as hydrogen halides, the interior surface may comprise any material that is simply resistant to the organic vapors of the present disclosure. In some embodiments, the chamber walls of the process chamber may comprise aluminum oxide, anodized aluminum, or plastic.

[0123] In some implementations, the process chamber may include a chamber component temperature control coupled to one or more surfaces (e.g., chamber walls) to control the temperature. In some implementations, the process chamber may include a gas inlet other than the showerhead for delivering the dry etchant. The gas inlet may be positioned in an area of ​​the process chamber where the concentration of metal-containing resist material is higher. The gas inlet may be positioned in an area of ​​the process chamber where the dry etchant is less likely to be reached by being delivered through the showerhead. In some implementations, the gas inlet may be positioned below the substrate support, in a wall of the process chamber, and / or near the exhaust of the process chamber. It is also possible to deliver the dry etchant to the process chamber using multiple gas inlets. This can ensure that the entire process chamber is dry cleaned. In various implementations, the dry etchant can be delivered to the process chamber through one or more gas inlets separate from the showerhead, and the deposition gas can be delivered to the process chamber through the showerhead. In some implementations, the showerhead can deliver separate gases by keeping the gases largely isolated within the showerhead. The showerhead can include multiple plenum volumes. The use of multiple exhaust lines can ensure separation of gases downstream of the process chamber. Switches can be operably coupled to the multiple exhaust lines to allow separation of dry etchant chemistry from deposition gases / precursors.

[0124] To protect the showerhead, a pressure differential can be used to prevent the dry etchant from entering (e.g., backflowing) into the showerhead. In some implementations, the dry etchant can clean the inner surface of the showerhead by flowing the dry etchant through the showerhead. However, residual organic vapor or moisture may be retained within the channels of the showerhead. In some implementations, the showerhead can be made of a transparent material and heated with a suitable light source. For example, a radiation source tuned to a suitable wavelength (e.g., IR or blue wavelength) can directly heat the residual organic vapor and / or moisture and remove the residual organic vapor and / or moisture. Alternatively, the residual organic vapor and / or moisture can be removed by gas purging.

[0125] FIG. 6B shows a cross-sectional schematic view of the chamber walls 604 after the dry etchant has removed the metal-containing EUV resist material 602 from the chamber walls 604. The dry etchant may include an organic vapor, such as an organic acid, which may include trifluoroacetic acid. The chamber walls 604 may be heated to an elevated temperature to promote low etch selectivity. The process chamber may be at an elevated pressure to promote low etch selectivity. The removal of the metal-containing EUV resist material 602 may be performed without the use of a plasma. Residual particles or clusters of metal oxide 606 may remain on the chamber walls 604 after exposure to the dry etchant. Additionally, residual dry etchant 608 may remain in the process chamber.

[0126] Returning to FIG. 5, in block 506 of process 500, the process chamber is optionally purged to remove residual dry etchant from the process chamber. The purging operation may include flowing a purge gas into the process chamber or a combination of flowing a purge gas and pumping the process chamber to a desired chamber pressure. The purge gas may be an inert gas and / or a reactive gas. The reactive gas may react with the residual dry etchant and facilitate its removal. The reactive gas may be, for example, a tin-based precursor, such as an organotin precursor. The inert gas may be argon, helium, xenon, or nitrogen. The chamber pressure may be from about 0.1 Torr to about 6 Torr.

[0127] In some embodiments, the purging operation may proceed at an elevated temperature. The elevated temperature may facilitate removal of organic vapors from the process chamber. In one example, one or more heaters coupled to one or more surfaces of the process chamber may heat the process chamber to an elevated temperature. In another example, one or more IR sources or LEDs may be installed within the process chamber to heat the process chamber to an elevated temperature. The elevated temperature may be from about 20° C. to about 180° C., or from about 80° C. to about 140° C.

[0128] In some embodiments, a plasma-based treatment, direct or remote, is useful for facilitating the removal of residual dry etchant, which may coat the interior surfaces of the process chamber after dry chamber cleaning. In other embodiments, a non-plasma treatment may be useful for accelerating the removal of residual dry etchant. The residual dry etchant may be oxidized by introducing an oxidizing gas. Thus, the non-plasma treatment may include delivering a flow of ozone and / or oxygen gas.

[0129] FIG. 6C shows a cross-sectional schematic view of the chamber walls 604 after removing the residual dry etchant 608 from the process chamber. A pumping / purging operation can be performed to evacuate the residual dry etchant 608 from the process chamber. In some implementations, the chamber walls 604 or other components of the process chamber can be heated to facilitate the release of the residual dry etchant 608. In some implementations, a direct or remote plasma-based process can be applied to remove the residual dry etchant 608, and such plasma-based process can include a fluorine-based plasma process, an oxygen-based plasma process, or a combination thereof. In some other implementations, a non-plasma process can be applied to remove the residual dry etchant 608. Particles or clusters of metal oxide 606 may remain on the chamber walls 604.

[0130] Returning to FIG. 5, in block 508 of process 500, one or more surfaces of the process chamber are optionally conditioned by forming a protective coating of a metal-containing resist material on the one or more surfaces of the process chamber. The average thickness of the protective coating may be less than the average thickness of the residue of the metal-containing resist material. In some implementations, the average thickness of the protective coating is about 1 nm or more, about 2 nm or more, about 3 nm or more, or about 1 nm to about 5 nm. Alternatively, the one or more surfaces are optionally conditioned by forming a protective coating made of a material different from the metal-containing resist material. Such a protective coating may be a variation of an organotin oxide. After exposure to the dry etchant, the one or more surfaces remain exposed. Exposed surfaces in the process chamber may be particularly vulnerable to attack by halogen-based species. The conditioning operation may protect the one or more surfaces. In addition, the conditioning operation may cover any residual particles or clusters of metal oxide attached to the one or more surfaces. In this manner, the metal oxide particles or clusters are less likely to contaminate the wafer during subsequent processing.

[0131] The conditioning of one or more surfaces of the process chamber can be performed by a gas-phase based deposition technique, such as a CVD or ALD technique. The organometallic material is obtained in the gas phase and deposited on one or more surfaces of the process chamber. The organometallic material can be deposited based on a gas-phase reaction of an organotin precursor, such as isopropyl(tris)(dimethylamino)tin, with water vapor, for example. The flow of water vapor can be relatively small. During conditioning, the substrate support can be protected or covered by a dummy wafer or other protective cover. Protective coatings may be formed on the chamber walls, floor, ceiling, or chamber components such as gas inlets, showerhead, and exhaust lines. Deposition of a protective coating of a metal-containing resist material may be followed by a pumping / purging operation to remove excess precursors and / or back reactants. Conditioning one or more surfaces of the process chamber can trap residual particles of metal oxides and limit particle contamination.

[0132] FIG. 6D shows a cross-sectional schematic view of a metal-containing resist material 610 formed on a chamber wall 604 of a process chamber. The metal-containing EUV resist material 610 can be redeposited in a conditioning operation to protect the chamber walls 604 during processing and trap metal oxide 606 particles or clusters from wafer contamination. This may also be referred to as chamber seasoning. The metal-containing EUV resist material 610 is formed by a vapor deposition method such as CVD or ALD. In some implementations, the metal-containing EUV resist material 610 may be an organotin oxide. Conditioning / seasoning the chamber walls 604 and other interior surfaces of the process chamber reduces undesirable first wafer effects when resuming deposition operations on a semiconductor substrate.

[0133] Although this disclosure frequently refers to the removal of exposed and / or developed EUV-sensitive films, the removal processes described may also be used to remove EUV-sensitive films of similar composition (e.g., other MO x R yThe method can be extended to other films containing metal oxides where metals may form volatile by-products with organic vapors, including non-exposed EUV resist films, such as non-exposed EUV resist films. In some embodiments, films other than EUV resists, such as hard masks, UV resists, or films of similar composition having other uses, can be removed by this method, and in this respect the removal process described relates to the chemical composition of the film, not its function.

[0134] Device The apparatus of the present disclosure is configured to dry strip EUV resist. The apparatus may be configured to perform dry development or dry chamber cleaning. The apparatus may be configured for other processing operations such as deposition, bevel and backside cleaning, post-apply bake, EUV scanning, post-exposure bake, photoresist rework, descum, smoothing, curing, and other operations. In some implementations, the apparatus is configured to perform all drying operations. In some implementations, the apparatus is configured to perform a combination of wet and dry operations. The apparatus may include a single wafer chamber or multiple stations in the same process chamber. When there are multiple stations in the same process chamber, various processing operations as described in this disclosure may be performed in different stations in the same process chamber. In one example, a PEB thermal treatment may be performed in one station and development may be performed in another station.

[0135] An apparatus configured to dry remove EUV resist includes a process chamber having a substrate support. The apparatus can include a dry etch line coupled to the process chamber for delivering an etch gas. In some implementations, the etch gas includes an organic vapor, such as trifluoroacetic acid. The apparatus can include one or more heaters for temperature control. Such heaters can be provided in the process chamber and / or the substrate support. In some implementations, multiple gas inlets can be positioned in the process chamber to flow etch gas near areas prone to unintentional EUV resist formation. The apparatus can further include one or more sensors for sensing particle count, wafer count, thickness count, or other parameters for triggering a dry chamber clean and / or for triggering an end point of the dry chamber clean.

[0136] In some implementations, the process chamber is made of an inexpensive material such as plastic, hi other implementations, the process chamber is made of a metal such as anodized aluminum, or a ceramic such as aluminum oxide.

[0137] FIG. 7 illustrates a schematic diagram of an exemplary process station suitable for performing dry develop, clean, rework, descum, and smooth operations according to some embodiments. Multiple process stations 700 may be included in a common low pressure process tool environment. For example, FIG. 8 illustrates one embodiment of a multi-station processing tool 800, such as a VECTOR® processing tool available from Lam Research, Inc., Fremont, Calif. In some embodiments, one or more hardware parameters of the process tool 800 (including those described in detail below) may be programmatically adjusted by one or more computer controllers 850.

[0138] The process stations can be configured as modules within a cluster tool. Figure 10 illustrates a semiconductor process cluster tool architecture having a vacuum integrated deposition and patterning module suitable for carrying out the embodiments described herein. Such a cluster process tool architecture can include resist deposition, resist exposure (EUV scanner), resist development, and etching modules, as described above and further below with reference to Figures 9 and 10.

[0139] In some embodiments, certain processing functions can be performed sequentially in the same module, such as dry development and etching or dry deposition and dry chamber cleaning. Also, embodiments of the present disclosure are directed to methods and apparatus for receiving a wafer including an EUV resist thin film layer disposed on a layer or layer stack to be etched, following photopatterning in an EUV scanner, dry developing the photopatterned EUV resist thin film layer, and then etching the underlying layer using the patterned EUV resist as a mask, as described herein.

[0140] Returning to Figure 7, the process station 700 is in fluid communication with a reactant delivery system 701 for delivering process gases to a distribution showerhead 706. The reactant delivery system 701 includes a mixing vessel 704 for blending and / or adjusting the process gases delivered to the showerhead 706. One or more mixing vessel inlet valves 720 can control the introduction of process gases to the mixing vessel 704. If plasma exposure is used, the plasma can also be delivered to the showerhead 706 or can be generated at the process station 700. As noted above, in at least some embodiments, non-plasma thermal exposure is preferred.

[0141] 7 includes an optional vaporization point 703 for vaporizing the liquid reactant provided to the mixing vessel 704. In some implementations, a liquid flow controller (LFC) can be provided upstream of the vaporization point 703 to control the mass flow rate of the liquid that is vaporized and delivered to the process station 700. For example, the LFC can include a thermal mass flow meter (MFM) located downstream of the LFC. A plunger valve of the LFC can then be adjusted in response to a feedback control signal provided by a proportional-integral-derivative (PID) controller in electrical communication with the MFM.

[0142] The showerhead 706 distributes process gases toward the substrate 712. In the embodiment illustrated in Figure 7, the substrate 712 is shown positioned below the showerhead 706 and resting on a pedestal 708. The showerhead 706 may have any suitable shape and may have any suitable number and arrangement of ports for distributing process gases to the substrate 712.

[0143] In some implementations, the pedestal 708 can be raised or lowered to expose the substrate 712 to the volume 707 between the substrate 712 and the showerhead 706. It will be appreciated that in some implementations, the height of the pedestal can be programmatically adjusted by a suitable computer controller 750. In some implementations, the showerhead 706 can have multiple plenum volumes with multiple temperature controls.

[0144] In some embodiments, the pedestal 708 may be temperature controlled via a heater 710. In some embodiments, the pedestal 708 may be heated to a temperature of greater than 0° C. to 300° C. or greater, such as 40° C. to 160° C., such as about 80° C. to 140° C., during non-plasma thermal exposure of the photopatterned resist to an organic vapor developing chemistry, such as trifluoroacetic acid, as described in disclosed embodiments. In some embodiments, the heater 710 of the pedestal 708 may include multiple independently controllable temperature control zones.

[0145] Additionally, in some embodiments, pressure control for the process station 700 may be provided by a butterfly valve 718. As shown in the embodiment of Figure 7, the butterfly valve 718 throttles the vacuum provided by a downstream vacuum pump (not shown). However, in some embodiments, pressure control for the process station 700 may also be adjusted by varying the flow rate of one or more gases introduced to the process station 700.

[0146] In some implementations, the position of the showerhead 706 can be adjusted relative to the pedestal 708 to vary the volume 707 between the substrate 712 and the showerhead 706. Further, it will be understood that the vertical position of the pedestal 708 and / or the showerhead 706 may be varied by any suitable mechanism within the scope of the present disclosure. In some implementations, the pedestal 708 may include a rotation axis for rotating the orientation of the substrate 712. It will be understood that in some implementations, one or more of these exemplary adjustments can be implemented programmatically by one or more suitable computer controllers.

[0147] Where a plasma may be used, for example in a descum or smoothing operation, the showerhead 706 and pedestal 708 are in electrical communication with a radio frequency (RF) power source 714 and matching network 716 to power the plasma. In some implementations, the plasma energy can be controlled by controlling one or more of the process station pressure, gas concentration, RF source power, RF source frequency, and plasma power pulse timing. For example, the RF power source 714 and matching network 716 can be operated at any suitable power to form a plasma having a desired composition of radical species. An example of a suitable power is up to about 500 W.

[0148] In some implementations, instructions for the controller 750 may be provided via input / output control (IOC) sequence instructions. In one example, instructions for setting conditions for a process step may be included in a corresponding recipe step of a process recipe. In some cases, a process recipe step may be arranged in sequence such that all instructions for a process step are executed simultaneously with that process step. In some implementations, instructions for setting one or more reactor parameters may be included in a recipe step. For example, a recipe step may include instructions for setting a flow rate of a dry development chemical reactant gas, such as trifluoroacetic acid, and a time delay instruction for the recipe step. In some implementations, the controller 750 may include any of the features described below with respect to the system controller 850 of FIG. 8.

[0149] As mentioned above, one or more process stations can be included in a multi-station processing tool. FIG. 8 shows a schematic diagram of one embodiment of a multi-station processing tool 800 with an inbound load lock 802 and an outbound load lock 804, either or both of which may include a remote plasma source. A robot 806 is configured to move a wafer from a cassette loaded via a pod 808 at atmospheric pressure to the inbound load lock 802 via an atmospheric pressure port 810. The wafer is placed by the robot 806 on a pedestal 812 of the inbound load lock 802, the atmospheric pressure port 810 is closed, and the load lock is pumped down. If the inbound load lock 802 includes a remote plasma source, the wafer may be subjected to a remote plasma treatment to treat the substrate surface within the load lock before being introduced to the processing chamber 814. Additionally, the wafer may also be heated in the inbound load lock 802 to remove, for example, moisture and absorbed gases. A chamber transfer port 816 to the processing chamber 814 is then opened and another robot (not shown) places the wafer into the reactor on the pedestal of the first station shown in the reactor for processing. Although the embodiment shown in Figure 8 includes a load lock, it will be understood that in some embodiments the wafer may enter the process station directly.

[0150] The illustrated processing chamber 814 includes four process stations, numbered 1 through 4 in the embodiment shown in FIG. 8. Each station has a heated pedestal (shown at 818 for station 1) and a gas line inlet. It will be appreciated that in some embodiments, each process station may have a different purpose or multiple purposes. For example, in some embodiments, the process stations may be switchable between a dry development mode and an etch process mode. Additionally or alternatively, in some embodiments, the processing chamber 814 may include one or more corresponding pairs of dry development and etch process stations. Although the illustrated processing chamber 814 includes four stations, it will be appreciated that a processing chamber according to the present disclosure may have any suitable number of stations. For example, in some embodiments, the processing chamber may have five or more stations, while in other embodiments, the processing chamber may have three or fewer stations.

[0151] FIG. 8 illustrates one embodiment of a wafer handling system 890 for transferring wafers within the processing chamber 814. In some embodiments, the wafer handling system 890 can transfer wafers between various process stations and / or between process stations and load locks. It will be understood that any suitable wafer handling system may be used. Non-limiting examples include a wafer carousel and a wafer handling robot. FIG. 8 also illustrates one embodiment of a system controller 850 used to control the process conditions and hardware states of the process tool 800. The system controller 850 can include one or more memory devices 856, one or more mass storage devices 854, and one or more processors 852. The processor 852 can include a CPU or computer, analog and / or digital input / output connections, stepper motor controller boards, etc.

[0152] In some implementations, the system controller 850 controls all of the activity of the process tool 800. The system controller 850 executes system control software 858 that is stored in the mass storage device 854, loaded into the memory device 856, and executed by the processor 852. Alternatively, the control logic may be hard-coded into the controller 850. Application specific integrated circuits, programmable logic devices (e.g., field programmable gate arrays, or FPGAs), and the like may be used for these purposes. In the following description, wherever "software" or "code" is used, functionally equivalent hard-coded logic may be used instead. The system control software 858 may include instructions for controlling the timing, mixture of gases, gas flow rates, chamber and / or station pressures, chamber and / or station temperatures, wafer temperatures, target power levels, RF power levels, substrate pedestal, chuck and / or susceptor positions, and other parameters of a particular process performed by the process tool 800. The system control software 858 may be configured in any suitable manner. For example, various process tool component subroutines or control objects may be written to control the operation of the process tool components used to perform the various process tool processes. The system control software 858 may be coded in any suitable computer readable programming language.

[0153] In some implementations, the system control software 858 may include input / output control (IOC) sequence instructions for controlling the various parameters described above. In some implementations, other computer software and / or programs stored on the mass storage device 854 and / or memory device 856 associated with the system controller 850 may be used. Examples of programs or sections of programs for this purpose include a substrate positioning program, a process gas control program, a pressure control program, a heater control program, and a plasma control program.

[0154] The substrate positioning program may include program code for process tool components used to load the substrate onto the pedestal 818 and control the spacing between the substrate and other parts of the process tool 800.

[0155] The process gas control program may include code for controlling organic vapor composition (e.g., trifluoroacetic acid as described herein) and flow rates to stabilize the pressure of the process station, and optionally code for flowing gases to one or more process stations prior to deposition. The pressure control program may include code for controlling the pressure of the process station, for example, by adjusting a throttle valve in the exhaust system of the process station, gas flow to the process station, etc.

[0156] The heater control program may include code for controlling the current to a heating unit used to heat the substrate, or the heater control program may control the delivery of a heat transfer gas (such as helium) to the substrate.

[0157] The plasma control program can include code for setting RF power levels applied to process electrodes in one or more process stations in accordance with embodiments herein.

[0158] The pressure control program can include code for maintaining pressure in the reaction chamber according to embodiments herein.

[0159] In some implementations, there may be a user interface associated with the system controller 850. The user interface may include a display screen, a graphical software display of equipment and / or process conditions, and user input devices such as a pointing device, keyboard, touch screen, microphone, etc.

[0160] In some implementations, the parameters adjusted by the system controller 850 may relate to process conditions. Non-limiting examples include process gas composition and flow rates, temperature, pressure, plasma conditions (such as RF bias power levels), etc. These parameters may be provided to a user in the form of a recipe or may be entered using a user interface.

[0161] Signals for monitoring the process may be provided by analog and / or digital input connections of the system controller 850 from various process tool sensors. Signals for controlling the process can be output at analog and digital output connections of the process tool 800. Non-limiting examples of process tool sensors that can be monitored include mass flow controllers, pressure sensors (such as pressure gauges), thermocouples, etc. Appropriately programmed feedback and control algorithms can be used with data from these sensors to maintain process conditions.

[0162] The system controller 850 can provide program instructions for carrying out the deposition process described above. The program instructions can control various process parameters such as DC power levels, RF bias power levels, pressure, temperature, etc. The instructions can control parameters for operating development, cleaning, and / or etching processes according to various embodiments described herein.

[0163] System controller 850 typically includes one or more memory devices and one or more processors configured to execute instructions such that the apparatus performs methods according to the disclosed embodiments. Machine-readable media containing instructions for controlling process operations according to the disclosed embodiments may be coupled to system controller 850.

[0164] In some implementations, the system controller 850 is part of a system, such a system may be part of the examples described above. Such a system may include semiconductor processing equipment, including one or more processing tools, one or more chambers, one or more processing platforms, and / or specific processing components (wafer pedestals, gas flow systems, etc.). These systems may be integrated with electronics for controlling system operations before, during, and after processing of a semiconductor wafer or substrate. Such electronics may be referred to as a "controller" and may control various components or subparts of one or more systems. The system controller 850 may be programmed to control any of the processes disclosed herein depending on the processing conditions and / or type of system. Such processes may include delivery of process gases, temperature settings (e.g., heating and / or cooling), pressure settings, vacuum settings, power settings, radio frequency (RF) generator settings, RF matching circuit settings, frequency settings, flow rate settings, fluid delivery settings, position and motion settings, wafer loading and unloading to and from tools and other transfer tools connected or interlocked with the particular system, and / or wafer loading and unloading to and from load locks.

[0165] Broadly, the system controller 850 may be defined as electronic equipment having various integrated circuits, logic, memory, and / or software that receive instructions, issue instructions, control operations, enable cleaning operations, enable endpoint measurements, etc. The integrated circuits may include chips in the form of firmware that store program instructions, digital signal processors (DSPs), chips defined as application specific integrated circuits (ASICs), and / or one or more microprocessors, i.e., microcontrollers that execute program instructions (e.g., software). The program instructions may be instructions communicated to the system controller 850 in the form of various individual settings (or program files) that define operational parameters for performing a particular process on or for a semiconductor wafer or for a system. The operational parameters may, in some implementations, be part of a recipe defined by a process engineer to accomplish one or more processing steps in the fabrication of one or more layers, materials, metals, oxides, silicon, silicon dioxide, surfaces, circuits, and / or wafer dies.

[0166] The system controller 850 may in some embodiments be part of, coupled to, or a combination of a computer that is integrated or coupled with the system or otherwise networked to the system. For example, the system controller 850 may be in the "cloud" or may be all or part of a fab host computer system. This allows for remote access of wafer processing. The computer may allow remote access to the system to monitor the current progress of a fabrication operation, review the history of past fabrication operations, review trends or performance criteria from multiple fabrication operations, modify parameters of a current process, set processing steps following a current process, or start a new process. In some examples, a remote computer (e.g., a server) may provide a process recipe to the system over a network. Such a network may include a local network or the Internet. The remote computer may include a user interface that allows entry or programming of parameters and / or settings, which are then communicated from the remote computer to the system. In some examples, the system controller 850 receives instructions in the form of data. Such data identifies parameters for each processing step performed during one or more operations. It should be understood that the parameters may be specific to the type of process being performed and the type of tool that the system controller 850 is configured to interface with or control. Thus, as described above, the system controller 850 may be distributed, for example, by including one or more individual controllers that are networked together and cooperate toward a common purpose (such as the processes and controls described herein).An example of a distributed controller for such purposes would include one or more integrated circuits on the chamber that communicate with one or more integrated circuits located remotely (e.g., at the platform level or as part of a remote computer) and coupled to control the process in the chamber.

[0167] Exemplary systems may include, but are not limited to, a plasma etch chamber or module, a deposition chamber or module, a spin rinse chamber or module, a metal plating chamber or module, a cleaning chamber or module, a bevel edge etch chamber or module, a physical vapor deposition (PVD) chamber or module, a chemical vapor deposition (CVD) chamber or module, an ALD chamber or module, an atomic layer etch (ALE) chamber or module, an ion implantation chamber or module, a tracking chamber or module, an EUV lithography chamber (scanner) or module, a development chamber or module, and any other semiconductor processing system that may be associated with or used in the fabrication and / or manufacturing of semiconductor wafers.

[0168] As described above, depending on the process step or steps being performed by the tool, system controller 850 may communicate with one or more other tool circuits or modules, other tool components, cluster tools, other tool interfaces, adjacent tools, nearby tools, tools located throughout the factory, a main computer, another controller, or tools used for material transport to and from tool locations and / or load ports within a semiconductor manufacturing factory.

[0169] In certain embodiments, an ICP reactor is described herein that may be suitable for etching operations suitable for carrying out some embodiments. Although an ICP reactor is described herein, it should be understood that in some embodiments, a capacitively coupled plasma reactor may also be used.

[0170] 9 illustrates generally a cross-sectional view of an inductively coupled plasma apparatus 900 suitable for performing certain embodiments or aspects of embodiments, such as dry developing, cleaning, and / or etching, an example of which is the Kiyo® reactor manufactured by Lam Research, Inc. of Fremont, Calif. In other embodiments, other tools or tool types capable of performing the dry developing, cleaning, and / or etching processes described herein may be used.

[0171] The inductively coupled plasma apparatus 900 includes an overall process chamber 924 structurally defined by a chamber wall 901 and a window 911. The chamber wall 901 can be fabricated from stainless steel, aluminum, or plastic. The window 911 can be fabricated from quartz or other dielectric materials. An optional internal plasma grid 950 divides the overall process chamber into an upper sub-chamber 902 and a lower sub-chamber 903. In many implementations, the plasma grid 950 can be removed, thereby utilizing the chamber space consisting of the sub-chambers 902 and 903. A chuck 917 is positioned within the lower sub-chamber 903 near the bottom inner surface. The chuck 917 is configured to receive and hold a semiconductor wafer 919 on which etching and deposition processes are performed. The chuck 917, if present, can be an electrostatic chuck for supporting the wafer 919. In some implementations, an edge ring (not shown) surrounds the chuck 917 and, if present on the chuck 917, has an upper surface that is approximately planar with an upper surface of the wafer 919. The chuck 917 also includes an electrostatic electrode for chucking and dechucking the wafer 919. For this purpose, a filter and DC clamp power supply (not shown) may be provided. Other control systems for lifting the wafer 919 from the chuck 917 may also be provided. The chuck 917 may be charged using an RF power supply 923. The RF power supply 923 is connected to a matching circuit 921 through a connection 927. The matching circuit 921 is connected to the chuck 917 through a connection 925. In this manner, the RF power supply 923 is connected to the chuck 917. In various embodiments, the bias power of the electrostatic chuck may be set to about 50V or may be set to a different bias power depending on the process to be performed according to the disclosed embodiments. For example, the bias power may be about 20V to about 100V, or about 30V to about 150V.

[0172] The elements for plasma generation are 、 Positioned above window 911 Coil 933 included9 includes three turns. A cross section of the coil 933 is shown symbolically with the coils having an "X" rotating into the page while the coils having a "●" rotating out of the page. The elements for plasma generation also include an RF power source 941 configured to provide RF power to the coil 933. Generally, the RF power source 941 is connected to a matching circuit 939 through a connection 945. The matching circuit 939 is connected to the coil 933 through a connection 943. In this manner, the RF power source 941 is connected to the coil 933. An optional Faraday shield 949 is positioned between the coil 933 and the window 911. The Faraday shield 949 may be maintained in a spaced apart relationship relative to the coil 933. In some embodiments, the Faraday shield 949 is disposed directly above the window 911. In some embodiments, the Faraday shield 949 is between the window 911 and the chuck 917. In some embodiments, the Faraday shield 949 is not maintained in a spaced apart relationship to the coil 933. For example, the Faraday shield 949 may be directly below the window 911 with no gap. The coil 933, the Faraday shield 949, and the window 911 are each configured to be substantially parallel to one another. The Faraday shield 949 may prevent metals or other species from depositing on the window 911 of the process chamber 924.

[0173] Process gases can flow into the process chamber via one or more main gas inlets 960 and / or one or more side gas inlets 970 positioned in the upper subchamber 902. Similarly, although not explicitly shown, similar gas inlets can be used to supply process gases to the capacitively coupled plasma processing chamber. A vacuum pump, e.g., a one or two stage mechanical dry pump and / or turbomolecular pump 940, can be used to draw process gases from the process chamber 924 and maintain pressure within the process chamber 924. For example, the vacuum pump can be used to evacuate the lower subchamber 903 during a purge operation. A valve controlled conduit can be used to fluidly connect the vacuum pump to the process chamber 924 to selectively control application of the vacuum environment provided by the vacuum pump. This can be done with a closed loop controlled flow restriction device, such as a throttle valve (not shown) or a pendulum valve (not shown), during plasma processing operations. Similarly, a vacuum pump and a valve controlled fluid connection to the capacitively coupled plasma processing chamber can also be used.

[0174] During operation of the apparatus 900, one or more process gases may be supplied through the gas inlets 960 and / or 970. In certain implementations, the process gases may be supplied only through the main gas inlet 960 or only through the side gas inlet 970. In some cases, the gas inlets shown in the figure may be replaced with more complex gas inlets, such as one or more showerheads. The Faraday shield 949 and / or optional grid 950 may include internal channels and holes that allow delivery of process gases 924 to the process chamber. Either or both of the Faraday shield 949 and optional grid 950 may function as showerheads for delivering process gases. In some implementations, a liquid vaporization and delivery system may be located upstream of the process chamber 924, whereby once the liquid reactants or precursors are vaporized, the vaporized reactants or precursors are introduced into the process chamber 924 via the gas inlets 960 and / or 970.

[0175] Radio frequency power is supplied from an RF power supply 941 to the coil 933, causing an RF current to flow through the coil 933. The RF current flowing through the coil 933 generates an electromagnetic field around the coil 933. The electromagnetic field generates an induced current in the upper subchamber 902. Physical and chemical interactions of the various generated ions and radicals with the wafer 919 etch features in the wafer 919 and selectively deposit layers on the wafer 919.

[0176] When a plasma grid 950 is used such that both an upper subchamber 902 and a lower subchamber 903 are present, induced currents act on the gas present in the upper subchamber 902 to generate an electron-ion plasma in the upper subchamber 902. The optional internal plasma grid 950 limits the number of thermal electrons in the lower subchamber 903. In some embodiments, the apparatus 900 is designed and operated such that the plasma present in the lower subchamber 903 is an ion-ion plasma.

[0177] Both the upper electron-ion plasma and the lower ion-ion plasma can contain positive and negative ions, but the ion-ion plasma has a greater ratio of negative ions to positive ions. Volatile etch and / or deposition byproducts can be removed from the lower subchamber 903 through port 922. The chuck 917 disclosed herein can operate at elevated temperatures ranging from about 10° C. to about 250° C. The temperature depends on the process operation and the particular recipe.

[0178] The apparatus 900 may be coupled to equipment (not shown) when installed in a clean room or fabrication facility. The equipment includes plumbing to provide process gases, vacuum, temperature control, and environmental particle control. These equipment will be coupled to the apparatus 900 when installed in the intended fabrication facility. Additionally, the apparatus 900 may be coupled to a transfer chamber that allows a robot to move semiconductor wafers in and out of the apparatus 900 using typical automated operations.

[0179] In some implementations, a system controller 930 (which may include one or more physical or logical controllers) controls some or all of the operation of the process chamber 924. The system controller 930 may include one or more memory devices and one or more processors. In some implementations, the apparatus 900 includes a switching system for controlling the flow rates and duration when the disclosed implementations are performed. In some implementations, the apparatus 900 may have a switching time of up to about 500 ms, or up to about 750 ms. The switching time may depend on the flowing chemistry, the selected recipe, the reactor architecture, and other factors.

[0180] In some implementations, the system controller 930 is part of a system, such a system may be part of the examples described above. Such a system may include semiconductor processing equipment, including one or more processing tools, one or more chambers, one or more processing platforms, and / or specific processing components (wafer pedestals, gas flow systems, etc.). These systems may be integrated with electronics for controlling system operations before, during, and after processing of a semiconductor wafer or substrate. Such electronics may be integrated into the system controller 930 and control various components or subcomponents of the system or systems. The system controller 930 may be programmed to control any of the processes disclosed herein depending on the processing parameters and / or type of system. Such processes may include delivery of process gases, temperature settings (e.g., heating and / or cooling), pressure settings, vacuum settings, power settings, radio frequency (RF) generator settings, RF matching circuit settings, frequency settings, flow rate settings, fluid delivery settings, position and motion settings, wafer loading and unloading from tools and other transfer tools connected or interlocked with the particular system, and / or wafer loading and unloading from load locks.

[0181] Broadly, the system controller 930 may be defined as electronic equipment having various integrated circuits, logic, memory, and / or software that receive instructions, issue instructions, control operations, enable cleaning operations, enable endpoint measurements, etc. The integrated circuits may include chips in the form of firmware that store program instructions, digital signal processors (DSPs), chips defined as application specific integrated circuits (ASICs), and / or one or more microprocessors, i.e., microcontrollers that execute program instructions (e.g., software). The program instructions may be instructions communicated to the controller in the form of various individual settings (or program files) that define operational parameters for performing a particular process on or for a semiconductor wafer or for a system. The operational parameters may, in some implementations, be part of a recipe defined by a process engineer to accomplish one or more processing steps in the fabrication or removal of one or more layers, materials, metals, oxides, silicon, silicon dioxide, surfaces, circuits, and / or wafer dies.

[0182] The system controller 930 may, in some embodiments, be part of, or coupled to, a computer that is integrated or coupled with the system or otherwise networked to the system, or a combination thereof. For example, the controller may be in the "cloud" or all or part of a fab host computer system. This allows for remote access of wafer processing. The computer may allow remote access to the system to monitor the current progress of a fabrication operation, review the history of past fabrication operations, review trends or performance criteria from multiple fabrication operations, modify parameters of a current process, set processing steps following a current process, or start a new process. In some examples, a remote computer (e.g., a server) may provide process recipes to the system over a network. Such a network may include a local network or the Internet. The remote computer may include a user interface that allows entry or programming of parameters and / or settings, which are then communicated from the remote computer to the system. In some examples, the system controller 930 receives instructions in the form of data. Such data identifies parameters for each processing step performed during one or more operations. It should be understood that the parameters may be specific to the type of process being performed and the type of tool that the controller is configured to interface with or control. Thus, as described above, the system controller 930 may be distributed, for example, by including one or more individual controllers that are networked together and cooperate toward a common purpose (such as the processes and controls described herein).An example of a distributed controller for such purposes would include one or more integrated circuits on the chamber that communicate with one or more integrated circuits located remotely (e.g., at the platform level or as part of a remote computer) and coupled to control the process in the chamber.

[0183] Exemplary systems may include, but are not limited to, a plasma etch chamber or module, a deposition chamber or module, a spin rinse chamber or module, a metal plating chamber or module, a cleaning chamber or module, a bevel edge etch chamber or module, a physical vapor deposition (PVD) chamber or module, a chemical vapor deposition (CVD) chamber or module, an ALD chamber or module, an ALE chamber or module, an ion implantation chamber or module, a tracking chamber or module, an EUV lithography chamber (scanner) or module, a dry development chamber or module, and any other semiconductor processing system that may be associated with or used in the fabrication and / or manufacturing of semiconductor wafers.

[0184] As described above, depending on the process step or steps being performed by the tool, the controller may communicate with one or more other tool circuits or modules, other tool components, cluster tools, other tool interfaces, adjacent tools, nearby tools, tools located throughout the factory, a main computer, another controller, or tools used for material transport to and from tool locations and / or load ports within a semiconductor manufacturing factory.

[0185] EUVL patterning can be performed using any suitable tool, often referred to as a scanner, such as the TWINSCAN NXE:3300B® platform supplied by ASML, Veldhoven, The Netherlands. 。The EUVL patterning tool may be a stand-alone device from which substrates are loaded and unloaded for deposition and etching as described herein. Or, as described below, the EUVL patterning tool may be a module on a larger multi-component tool. Figure 10 illustrates a semiconductor process cluster tool architecture having a vacuum integrated deposition, EUV patterning, and dry develop / etch module interfaced with a vacuum transfer module suitable for carrying out the processes described herein. Although the processes can be carried out without such vacuum integrated equipment, such equipment may be advantageous in some embodiments.

[0186] FIG. 10 illustrates a semiconductor process cluster tool architecture having a vacuum integrated deposition and patterning module interfaced with a vacuum transfer module suitable for carrying out the processes described herein. The arrangement of transfer modules to "transfer" wafers between multiple storage facilities and processing modules is sometimes referred to as a "cluster tool architecture" system. The deposition and patterning modules are vacuum integrated according to the requirements of the particular process. Other modules, such as for etching, can also be included in the cluster.

[0187] A vacuum transport module (VTM) 1038 interfaces with four processing modules 1020a-1020d, which can be individually optimized to perform various fabrication processes. By way of example, the processing modules 1020a-1020d can be implemented to perform deposition, evaporation, ELD, dry develop, clean, etch, strip, and / or other semiconductor processes. For example, module 1020a can be an ALD reactor that can be operated to perform non-plasma thermal atomic layer deposition as described herein, such as a Vector tool available from Lam Research, Inc. of Fremont, Calif., and module 1020b can be a PECVD tool, such as a Lam Vector®. It should be understood that the figures are not necessarily drawn to scale.

[0188] Airlocks 1042 and 1046, also known as loadlocks or transfer modules, interface with the VTM 1038 and the patterning module 1040. For example, as noted above, a suitable patterning module may be a TWINSCAN NXE:3300B® platform supplied by ASML of Veldhoven, The Netherlands. 。 This tool architecture allows workpieces such as semiconductor substrates or wafers to be transferred under vacuum so that they do not react before exposure. The integration of the deposition module with the lithography tool allows H 2 O, O 2 This is facilitated by the fact that EUVL also requires significantly reduced pressures, given the strong optical absorption of incident photons by surrounding gases such as

[0189] As mentioned above, this integrated architecture is only one possible implementation of a tool for carrying out the described process. The process can also be carried out with more conventional standalone EUVL scanners and as a module, a deposition reactor such as a Lam Vector tool, e.g., as described with reference to FIG. 10 but without an integrated patterning module, either standalone or integrated in a cluster architecture with other tools such as etch, strip, etc. (e.g., Lam Kiyo or Gamma tools).

[0190] Airlock 1042 may be an "out" load lock, referring to the transfer of substrates from the VTM 1038 servicing deposition module 1020a to the patterning module 1040, and airlock 1046 may be an "in" load lock, referring to the transfer of substrates from the patterning module 1040 back to the VTM 1038. The in load lock 1046 may also provide an interface to the outside of the tool for access and egress of substrates. Each process module has a facet that interfaces the module to the VTM 1038. For example, deposition process module 1020a has facet 1036. Within each facet, sensors, such as sensors 1-18 shown, are used to detect the passage of wafer 1026 as it moves between the respective stations. Patterning module 1040 and airlocks 1042 and 1046 may similarly include additional facets and sensors not shown.

[0191] The main VTM robot 1022 transfers wafers 1026 between modules including airlocks 1042 and 1046. In one embodiment, the robot 1022 has one arm, and in another embodiment, the robot 1022 has two arms, each arm having an end effector 1024 that lifts a wafer such as wafer 1026 for transfer. A front-end robot 1044 is used therein to transfer wafers 1026 from the exit airlock 1042 to the patterning module 1040 and from the patterning module 1040 to the entry airlock 1046. The front-end robot 1044 can also transfer wafers 1026 between the entry loadlock and the exterior of the tool for substrate access and egress. Because the entry airlock module 1046 has the ability to adapt the environment between atmospheric pressure and vacuum, the wafers 1026 can move between the two pressure environments without being damaged.

[0192] It should be noted that EUVL tools typically operate at a higher vacuum than deposition tools. In this case, it is desirable to increase the vacuum environment of the substrate during transfer between the deposition and EUVL tools to allow for outgassing of the substrate before entering the patterning tool. The unloading airlock 1042 can provide this function by holding the transferred wafer at a low pressure, no higher than the pressure in the patterning module 1040 for a period of time, and venting the off-gassing, so that the optics of the patterning module 1040 are not contaminated by off-gassing from the substrate. A suitable pressure for the venting off-gas airlock is 1E-8 Torr or less.

[0193] In some implementations, a system controller 1050 (which may include one or more physical or logical controllers) controls some or all of the operations of the cluster tool and / or its separate modules. Note that the controller may be local to the cluster architecture, or may be located outside the cluster architecture on the manufacturing floor, or may be located at a remote location and connected to the cluster architecture via a network. The system controller 1050 may include one or more memory devices and one or more processors. The processor may include a central processing unit (CPU) or computer, analog and / or digital input / output connections, stepper motor controller boards, and other similar components. Instructions are executed on the processor to perform appropriate control operations. These instructions may be stored in a memory device associated with the controller or provided over a network. In certain implementations, the system controller executes system control software.

[0194] The system control software may include instructions for controlling the timing of application and / or magnitude of any aspect of tool or module operation. The system control software may be configured in any suitable manner. For example, various process tool component subroutines or control objects may be written to control the operation of process tool components necessary to perform various process tool processes. The system control software may be coded in any suitable computer readable programming language. In some embodiments, the system control software includes input / output control (IOC) sequence instructions for controlling the various parameters described above. For example, each stage of a semiconductor fabrication process may include one or more instructions executed by the system controller. For example, instructions for setting process conditions for condensation, deposition, evaporation, patterning, and / or etching stages may be included in the corresponding recipe stage.

[0195] In various embodiments, an apparatus for forming a negative pattern mask is provided. The apparatus can include process chambers for patterning, deposition, and etching, and a controller including instructions for forming a negative pattern mask. The instructions include a controller for controlling a chemical amplification reaction on a semiconductor substrate by EUV exposure in the process chamber. Resist (CAR) The photoresist may include code for patterning features in the photoresist to expose a surface of the substrate, developing the photopatterned resist, and etching an underlying layer or layer stack using the patterned resist as a mask. Development may be performed using an organic vapor, such as an organic acid.

[0196] It should be noted that the computer controlling the movement of the wafers may be local to the cluster architecture, or may be located outside the cluster architecture on the manufacturing floor, or may be located at a remote location and connected to the cluster architecture via a network. The controller described above with respect to any of Figures 7, 8, or 9 may be implemented using the tool of Figure 10.

[0197] FIG. 11A illustrates an example of a deposition chamber for vapor-based deposition of metal-containing resist materials, according to some embodiments. As can be seen, an apparatus 1100 is illustrated having a process chamber 1102 including a lid 1108. The process chamber 1102 can include a wafer transfer passage 1104 through one of the walls of the process chamber 1102, the wafer transfer passage 1104 being sized to allow a substrate 1122 to pass through and enter the interior of the process chamber 1102, where the substrate 1122 can be placed on a wafer support 1124. The wafer transfer passage 1104 can have a gate valve 1106 or similar door mechanism operable to seal or open the wafer transfer passage 1104, thereby allowing the environment within the process chamber 1102 to be isolated from the environment on the other side of the gate valve 1106. For example, the process chamber 1102 can be provided with a substrate 1122 via a wafer handling robot located in an adjacent transfer chamber. Such a transfer chamber may, for example, have multiple process chambers 1102 arranged around its periphery, with each such process chamber 1102 connected to the transfer chamber via a corresponding gate valve 1106 .

[0198] The wafer support 1124 can include, for example, an electrostatic chuck (ESC) 1126 that can be used to provide a wafer support surface for supporting the substrate 1122. The ESC 1126 can include, for example, a base plate 1134 bonded to a top plate 1128 that rests on the base plate 1134. The top plate 1128 can be made of, for example, a ceramic material and can have several other components embedded therein. In the illustrated example, the top plate 1128 has two separate electrical systems embedded therein. One such system is an electrostatic clamping electrode system, which can have one or more clamping electrodes 1132 that can be used to generate a charge in the substrate 1122, causing the substrate 1122 to be attracted against the wafer support surface of the top plate 1128. In the embodiment of FIG. 11A, there are two clamping electrodes 1132 providing a bipolar electrostatic clamping system, although in some embodiments, only a single clamping electrode 1132 can be used to provide a monopolar electrostatic clamping system.

[0199] Another system is a thermal control system that can be used to control the temperature of the substrate 1122 during processing conditions. In FIG. 11A, the thermal control system is a multi-zone thermal control system featuring four annular resistive heater traces 1130a, 1130b, 1130c, and 1130d that are concentric with one another and positioned under a clamping electrode 1132. The central resistive heater trace 1130a may fill a generally circular area in some embodiments, and each resistive heater trace 1130a / b / c / d may follow a generally serpentine or serpentine path within a corresponding annular area. Each resistive heater trace 1130a / b / c / d may be individually controlled to provide a variety of radial heating profiles to the top plate 1128, and such a four-zone heating system may be controlled to maintain the substrate 1122 with, for example, a temperature uniformity of ±0.5° C. in some cases. Although the device 1100 of FIG. 11A features a four-zone heating system within the ESC 1126, in other embodiments, a single-zone or multi-zone heating system having more or less than four zones can be used.

[0200] For example, in some implementations of the temperature control mechanisms described above, a heat pump may be used in place of the resistive heating traces. For example, in some implementations, the resistive heater traces may be replaced or augmented by Peltier junctions or other similar devices that can be controlled to "pump" heat from one side to the other. Such a mechanism may be used, for example, to draw heat from the top plate 1128 (and thus the substrate 1122) and direct the heat to the base plate 1134 and heat exchange passages 1136, thereby allowing the substrate 1122 to be cooled more quickly and more effectively, as desired.

[0201] The ESC 1126 may also include a base plate 1134, which may be used, for example, to provide structural support to the underside of the top plate 1128 and may also act as a heat distribution system. For example, the base plate 1134 may include one or more heat exchange passages 1136 arranged generally distributed throughout the base plate 1134, for example, the heat exchange passages 1136 may follow a serpentine, circular switchback, or spiral pattern around the center of the base plate 1134. During use, a heat exchange medium, for example, water or an inert fluorinated liquid, may be circulated through the heat exchange passages 1136. The flow rate and temperature of the heat exchange medium may be externally controlled to result in specific heating or cooling behavior within the base plate 1134.

[0202] The ESC 1126 may be supported, for example, by a wafer support housing 1142 connected to and supported by wafer support columns 1144. The wafer support columns 1144 may include routing passages 1148 for routing, for example, cabling, fluid flow conduits, and other equipment to the underside of the base plate 1134 and / or top plate 1128. or 11A , the cabling for supplying power to the resistive heater traces 1130a / b / c / d may be routed through the routing passages 1148, as may the cabling for supplying power to the clamp electrodes 1132. Other cables, for example, cables for temperature sensors, may also be routed through the routing passages 1148 to locations internal to the wafer support 1124. In embodiments having a temperature-controllable base plate 1134, conduits for transporting heat exchange medium between the base plates 1134 may also be routed through the routing passages 1148. To avoid excessive clutter, such cables and conduits are not shown in FIG. 11A , but it should be understood that they are present nonetheless.

[0203] 11A also includes a wafer support Z actuator 1146 that can provide movable support to the wafer support column 1144. The wafer support Z actuator 1146 can be actuated to move the wafer support column 1144, and the wafer support 1124 supported thereby, vertically up or down, for example, by up to several inches, within the reaction volume 1120 of the process chamber 1102. In doing so, the gap distance X between the substrate 1122 and the underside of the showerhead 1110 can be adjusted in response to various process conditions.

[0204] The wafer support 1124 may also include one or more edge rings, which in some implementations may be used to control and / or fine-tune various process conditions. In FIG. 11A, an upper edge ring 1138 is provided, for example, above the lower edge rings 1140a and 1140b, which are supported by a wafer support housing 1142 and a third lower edge ring 1140c. The upper edge ring 1138 may, for example, generally be subjected to the same processing environment as the substrate 1122, while the lower edge rings 1140a / b / c may generally be shielded from the processing environment. Due to the increased exposure of the upper edge ring 1138, the upper edge ring 1138 may have a limited life span and require more frequent replacement or cleaning compared to the lower edge rings 1140a / b / c.

[0205] The apparatus 1100 may also include a system for removing process gases from the process chamber 1102 during and after processing. For example, the process chamber 1102 may include an annular plenum 1156 that surrounds the wafer support column 1144. The annular plenum 1156 may then be fluidly connected to a vacuum foreline 1152 that may be connected to a vacuum pump, such as one that may be located under a subfloor below the apparatus 1100. A control valve 1154 may be provided between the vacuum foreline 1152 and the process chamber 1102 and may be actuated to control flow to the vacuum foreline 1152. In some implementations, a baffle 1150, e.g., an annular plate or other structure, may be provided that may function to distribute the flow into the annular plenum 1156 more evenly around the circumference of the wafer support column 1144, reducing the possibility of flow non-uniformities in the reactants flowing across the substrate 1122.

[0206] The showerhead 1110, as shown, is a dual plenum showerhead 1110 and includes a first plenum 1112 to which process gas is supplied via a first inlet 1116 and a second plenum 1114 to which process gas is supplied via a second inlet 1118. Generally, two plenums can be used to maintain separation between the precursors and the counter reactant prior to release of the precursors and the counter reactant. The showerhead 1110 may have more than two plenums in some implementations. In some cases, a single plenum can be used to release the precursors. process The plenums feed into the reaction space 1120 of the chamber 1102. Each plenum can have a corresponding set of gas distribution ports that fluidly connect the respective plenum to the reaction space 1120 through the faceplate of the showerhead 1110 (the faceplate is the portion of the showerhead 1110 interposed between the bottom plenum and the reaction space 1120).

[0207] The first inlet 1116 and the second inlet 1118 of the showerhead 1110 may be supplied with process gases via a gas supply system, which may be configured to supply one or more precursors and / or counter reactants as described herein. The illustrated apparatus 1100 is configured to supply multiple precursors and multiple counter reactants. For example, a first valve manifold 1168a may be configured to supply a precursor to the first inlet 1116, and a second valve manifold 1168b may be configured to supply another precursor or another counter reactant to the second inlet 1118.

[0208] A first valve manifold 1168a may be configured to supply one or more precursors to the first inlet 1116, and a second valve manifold 1168b may be configured to supply other precursors or other reactants to the second inlet 1118. In this example, the first valve manifold 1168a includes, for example, multiple valves A1-A5. Valve A2 may be, for example, a three-way valve having one port fluidly connected to a first vaporizer 1172a, another port fluidly connected to a bypass line 1170a, and a third port fluidly connected to a port on another three-way valve A3. Similarly, valve A4 may be another three-way valve having one port fluidly connected to a second vaporizer 1172b, another port fluidly connected to a bypass line 1170a, and a third port fluidly connected to a port on another three-way valve A5. One of the other ports on valve A5 may be fluidly connected to the first inlet 1116, and the remaining port on valve A5 may be fluidly connected to one of the remaining ports on valve A3. The remaining port on valve A3 may then be fluidly connected to valve A1, which may be fluidly interposed between valve A3 and a purge gas source 1174, e.g., nitrogen, argon, or other suitable inert gas (for the precursor and / or back reactant). In some embodiments, only the first valve manifold is used.

[0209] For purposes of this disclosure, the term "fluidically connected" is used in reference to volumes, plenums, holes, etc. that may be connected to one another to form a fluid connection, similar to how the term "electrically connected" is used in reference to components that are connected to one another to form an electrical connection. The term "fluidically interposed", when used, may be used to refer to a component, volume, plenum, or hole that is fluidly connected to at least two other components, volumes, plenums, or holes, such that fluid flowing from one of those other components, volumes, plenums, or holes to the other of those components, volumes, plenums, or holes will first flow through the "fluidically interposed" component before reaching the other of those other components, volumes, plenums, or holes. For example, if a pump is fluidly interposed between a reservoir and an outlet, fluid flowing from the reservoir to the outlet will first flow through the pump before reaching the outlet.

[0210] The first valve manifold 1168a may be controllable to, for example, flow vapor from one or both of the vaporizers 1172a and 1172b to the process chamber 1102 or through a first bypass line 1170a to the vacuum foreline 1152. The first valve manifold 1168a may also be controllable to flow purge gas from a purge gas source 1174 to the first inlet 1116.

[0211] For example, to flow vapor from the first vaporizer 1172a to the reaction space 1120, the valve A2 can be actuated to flow the vapor from the first vaporizer 1172a first to the first bypass line 1170a. This flow can be maintained for a period of time sufficient to allow the flow of vapor to reach a steady state flow condition. After a sufficient time has elapsed (or after a flow meter, if used, indicates that the flow rate is stable), the valves A2, A3, and A5 can be actuated to direct the vapor flow from the first vaporizer 1172a to the first inlet. Similar operations with the valves A4 and A5 can be performed to deliver the vapor from the second vaporizer 1172b to the first inlet 1116. In some cases, it may be desirable to purge one of the vapors from the first plenum 1112 by actuating the valves A1, A3, and A5 to allow purge gas from the purge gas source 1174 to flow into the first inlet 1116. In some additional embodiments, it may be desirable to simultaneously flow vapor from one of the vaporizers 1172a or 1172b in parallel with flowing gas from the purge gas into the first inlet 1116. Such an embodiment can be used to dilute the concentration of reactants contained in such vapor.

[0212] It will be appreciated that the second valve manifold 1168b can be controlled in a similar manner, for example by controlling valves B1-B5, to supply vapor from the vaporizers 1172c and 1172d to the second inlet 1118 or to the second bypass line 1170b. Additionally, it will be appreciated that different manifold arrangements can be utilized as well, including a single integrated manifold that includes valves to control the flow of precursors, back reactants, or other reactants to the first inlet 1116 and second inlet 1118.

[0213] As previously mentioned, some devices 1100 may feature a fewer number of vapor sources, e.g., only two vaporizers 1172, in which case it may be possible to modify the valve manifold 1168 to have a fewer number of valves, e.g., only valves A1-A3. 。

[0214] As described above, an apparatus such as the apparatus 1100 that may be used to perform dry deposition of a film may be configured to maintain a particular temperature profile within the process chamber 1102. In particular, such an apparatus 1100 may be configured to maintain the substrate 1122 at a lower temperature, e.g., at least 25° C. to 50° C. lower, than most of the equipment of the apparatus 1100 that is in direct contact with the precursors and / or reverse reactants. In addition, the temperature of the equipment of the apparatus 1100 that is in direct contact with the precursors and / or reverse reactants may be maintained at an elevated temperature level that is high enough to prevent condensation of vaporized reactants on the surfaces of such equipment. At the same time, the temperature of the substrate 1122 may be controlled to a level that promotes condensation, or at least deposition, of the reactants on the substrate 1122.

[0215] To provide such temperature control, various heating systems may be included in the apparatus 1100. For example, the process chamber 1102 may have a receptacle for receiving a cartridge heater 1158; for example, for a process chamber 1102 having a generally cylindrical interior volume, but with a square or rectangular exterior, vertical holes may be drilled in the four corners of the housing of the chamber 1102 to receive the cartridge heater 1158. In some implementations, the showerhead 1110 may be covered with a heater blanket 1160, which may be used to apply heat to the entire exposed top surface of the showerhead 1110 and keep the temperature of the showerhead high. It may also be beneficial to heat the various gas lines used to direct vaporized reactants from the vaporizer 1172 to the showerhead 1110. For example, resistive heater tape may be wrapped around such gas lines and used to heat the gas lines to a high temperature. 11A, all gas lines through which precursors and / or counter reactants may flow are shown as being heated, including the bypass line 1170. The only exceptions are the gas lines from the valve manifold 1168 to the first inlet 1116 and the second inlet 1118, which are very short and can be indirectly heated by the showerhead 1110. Of course, these gas lines can also be actively heated, if desired. In some implementations, heat can also be provided to the gate valve 1106 by providing a heater in close proximity to the gate valve.

[0216] The various operating systems of the apparatus 1100 can be controlled by a controller 1184, which may include one or more processors 1186 and one or more memory devices 1188 operably connected to each other and communicatively connected to the various systems and subsystems of the apparatus 1100 to provide control functions for these systems. For example, the controller 1184 may be configured to control valves A1-A5 and B1-B5, the various heaters 1158, 1160, the vaporizer 1172, the regulator valve 1154, the gate valve 1106, the wafer support Z actuator, etc.

[0217] Another feature that the apparatus 1100 may include is shown in FIG. 11B, which illustrates an enlarged cross-sectional side view and plan view of a portion of the substrate 1122, top plate 1128, and upper edge ring 1138 of FIG. 11A. As can be seen, in some implementations, the substrate 1122 may be elevated from the majority of the top plate 1128 by a number of small mesas 1176, which may be shallow bosses that project from the nominal upper surface of the top plate 1128 by a small distance to provide a backside gap 1178 between the underside of the substrate 1122 and the majority of the top plate 1128. A peripheral wall feature 1177 may be provided on the periphery of the top plate 1128. The peripheral wall feature 1177 may extend around the entire periphery of the top plate 1128 and may be nominally the same height as the mesas 1176. During processing operations, a generally inert gas, such as helium, can flow into the back gap 1178 via one or more gas ports 1182. The gas can then flow radially outward before encountering the peripheral wall feature 1177, which then restricts such radially outward flow and traps a high pressure region of gas between the substrate 1122 and the top plate 1128. Any inert gas that leaks beyond the peripheral wall 1177 can eventually exit through the radial gap 1180 between the outer edge of the substrate 1122 and a portion of the upper edge ring 1138. Such gas can function to protect the underside of the substrate from undesirable effects of the processing operations being performed by acting to prevent gases released by the showerhead 1110 from reaching the underside of the substrate 1122. At the same time, the gas released in the region of the back gap 1178 can also act to increase thermal coupling between the substrate 1122 and the top plate 1128, thereby allowing the top plate 1128 to more effectively heat or cool the substrate 1122. Due to the high pressure provided by the peripheral walls, the gas in the area of ​​the back gap 1178 can also be denser than the gas in the remainder of the chamber, thus providing a more effective thermal coupling between the substrate 1122 and the top plate 1128.

[0218] The controller 1184 can be configured, for example, through the execution of computer-executable instructions, to cause the apparatus 1100 to perform various operations consistent with the above disclosure.

[0219] Once the metal-containing resist film has been deposited on the substrate 1122, the substrate 1122 may be transferred to one or more subsequent process chambers or tools for additional operations (e.g., any of those described herein), as described above. Additional deposition apparatus are described in International Patent Application No. PCT / US2020 / 038968, filed June 22, 2020, and entitled "APPARATUS FOR PHOTORESIST DRY DEPOSITION," which is incorporated herein by reference in its entirety.

[0220] conclusion A process and apparatus are disclosed for dry development of metal and / or metal oxide photoresists, for example to form patterning masks in EUV patterning scenarios.

[0221] It will be understood that the examples and embodiments described herein are for illustrative purposes only, and various modifications or changes will be suggested to those skilled in the art in light thereof. Various details have been omitted for clarity, but various design alternatives can be implemented. Thus, the examples are to be considered as illustrative rather than restrictive, and the disclosure is not to be limited to the details given herein, but can be modified within the scope of the disclosure. The present invention can be realized, for example, in the following manner. Application example 1: 1. A method comprising: Providing a photopatterned metal-containing resist on a surface of a semiconductor substrate in a process chamber; dry developing the photo-patterned metal-containing resist by selectively removing portions of the photo-patterned metal-containing resist by exposure to a developing chemistry that includes an organic vapor to form a resist mask; A method comprising: Application example 2: The method according to Application Example 1, The method of claim 1, wherein the organic vapor comprises a carboxylic acid. Application example 3: The method according to Application Example 2, The method of claim 1, wherein the organic vapor comprises trifluoroacetic acid. Application example 4: The method according to Application Example 1, The method, wherein the organic vapor comprises trifluoroacetic anhydride, acetic anhydride, trichloroacetic acid, monofluoroacetic acid, difluoroacetic acid, chlorodifluoroacetic acid, thioacetic acid, or thioglycolic acid. Application example 5: The method according to Application Example 1, The method of claim 1, wherein the organic vapor comprises hexafluoroacetylacetone. Application example 6: The method according to any one of application examples 1 to 5, The method wherein said developing chemistry comprises a vapor phase mixture of a halogenated carboxylic acid and a hydrogen halide. Example 7: The method according to any one of application examples 1 to 5, The method, wherein dry developing the photo-patterned metal-containing resist comprises reacting the organic vapor with the photo-patterned metal-containing resist to form a volatile compound at a temperature less than about 200° C. Application example 8: The method according to any one of application examples 1 to 5, The method, wherein dry developing the photopatterned metal-containing resist comprises exposing to at least the organic vapor in a plasma-free thermal process. Example 9: The method according to any one of application examples 1 to 5, The method, wherein the photopatterned metal-containing resist is a photopatterned metal-containing EUV resist, and the photopatterned metal-containing EUV resist is an organometallic oxide or organometallic containing film. Example 10: The method according to any one of application examples 1 to 5, dry developing the photo-patterned metal-containing resist includes using the developing chemistry to selectively remove EUV unexposed portions of the photo-patterned metal-containing resist relative to EUV exposed portions to form the resist mask. Example 11: 1. A method comprising: depositing a metal-containing resist material on a surface of a semiconductor substrate in a process chamber, a portion of the metal-containing resist material forming a residue on one or more surfaces of the process chamber; introducing a dry etchant comprising an organic vapor into the process chamber, the dry etchant at least partially removing the residue on the one or more surfaces of the process chamber; A method comprising: Application example 12: The method according to Application Example 11, The method of claim 1, wherein the organic vapor comprises a carboxylic acid. Application example 13: The method according to Application Example 12, The method of claim 1, wherein the organic vapor comprises trifluoroacetic acid. Example 14: The method according to Application Example 11, The method, wherein the organic vapor comprises trifluoroacetic anhydride, acetic anhydride, trichloroacetic acid, monofluoroacetic acid, difluoroacetic acid, chlorodifluoroacetic acid, thioacetic acid, or thioglycolic acid. Example 15: The method according to Application Example 11, The method of claim 1, wherein the organic vapor comprises hexafluoroacetylacetone. Application example 16: 16. The method according to any one of application examples 11 to 15, The method, wherein the dry etchant comprises a vapor phase mixture of a halogenated carboxylic acid and a hydrogen halide. Example 17: 16. The method according to any one of application examples 11 to 15, The method, wherein at least partially removing the residue comprises reacting the organic vapor with the metal-containing resist material to form a volatile compound at a temperature less than about 200°C. Application example 18: 16. The method according to any one of application examples 11 to 15, The method, wherein at least partial removal of the residue comprises exposing to at least the organic vapor in a plasma-free thermal process. Example 19: 16. The method according to any one of application examples 11 to 15, The method, wherein the metal-containing resist material is an organometallic oxide or an organometallic-containing film. Example 20: 16. The method according to any one of application examples 11 to 15, purging the process chamber after introducing the dry etchant to remove residual dry etchant from the process chamber; conditioning the one or more surfaces of the process chamber by forming a protective coating of the metal-containing resist material on the one or more surfaces of the process chamber; The method further comprising:

Claims

1. 1. A method of developing a resist, comprising the steps of: Providing a photopatterned metal-containing resist on a surface of a semiconductor substrate in a process chamber; dry developing the photo-patterned metal-containing resist by selectively removing portions of the photo-patterned metal-containing resist by exposure to a developing chemistry that includes an organic vapor to form a resist mask; Including, The method of claim 1, wherein the organic vapor comprises a carboxylic acid.

2. 2. The method of claim 1 , The method of claim 1, wherein the organic vapor comprises trifluoroacetic acid.

3. 1. A method of developing a resist, comprising the steps of: Providing a photopatterned metal-containing resist on a surface of a semiconductor substrate in a process chamber; dry developing the photo-patterned metal-containing resist by selectively removing portions of the photo-patterned metal-containing resist by exposure to a developing chemistry that includes an organic vapor to form a resist mask; Including, The method, wherein the organic vapor comprises trifluoroacetic anhydride, acetic anhydride, trichloroacetic acid, monofluoroacetic acid, difluoroacetic acid, chlorodifluoroacetic acid, thioacetic acid, or thioglycolic acid.

4. 1. A method of developing a resist, comprising the steps of: Providing a photopatterned metal-containing resist on a surface of a semiconductor substrate in a process chamber; dry developing the photo-patterned metal-containing resist by selectively removing portions of the photo-patterned metal-containing resist by exposure to a developing chemistry that includes an organic vapor to form a resist mask; Including, The method of claim 1, wherein the organic vapor comprises hexafluoroacetylacetone.

5. 1. A method of developing a resist, comprising the steps of: Providing a photopatterned metal-containing resist on a surface of a semiconductor substrate in a process chamber; dry developing the photo-patterned metal-containing resist by selectively removing portions of the photo-patterned metal-containing resist by exposure to a developing chemistry that includes an organic vapor to form a resist mask; Including, The method wherein said developing chemistry comprises a vapor phase mixture of a halogenated carboxylic acid and a hydrogen halide.

6. 6. The method according to any one of claims 1 and 2 to 5, The method, wherein dry developing the photo-patterned metal-containing resist comprises reacting the organic vapor with the photo-patterned metal-containing resist to form a volatile compound at a temperature less than about 200° C.

7. 6. The method according to any one of claims 1 and 2 to 5, The method, wherein dry developing the photopatterned metal-containing resist comprises exposing to at least the organic vapor in a plasma-free thermal process.

8. 6. The method according to any one of claims 1 and 2 to 5, The method, wherein the photopatterned metal-containing resist is a photopatterned metal-containing EUV resist, and the photopatterned metal-containing EUV resist is an organometallic oxide or organometallic containing film.

9. 6. The method according to any one of claims 1 and 2 to 5, dry developing the photo-patterned metal-containing resist includes selectively removing EUV non-exposed portions of the photo-patterned metal-containing resist relative to EUV exposed portions using the developing chemistry to form the resist mask.

Images